JP2019131731A - Resin composition having insect-repellent function, and film, wall paper, decorative sheet including the same - Google Patents

Abstract

To provide a resin composition that has an insect-repellent function, suppresses bleeding whitening, has excellent embossing suitability, and suppresses a deterioration of favorable properties such as chemical resistance and contamination resistance of an ethylene-vinyl alcohol copolymer, and a film, wall paper, decorative sheet including the same.SOLUTION: A thermoplastic resin composition contains (A) an ethylene-vinyl alcohol copolymer 100 pts.mass and (B) a pyrethroid compound 0.01-5 pts.mass. The content of an ethylene-derived constitutional unit in the component (A) is preferably 35-60 mol%.SELECTED DRAWING: Figure 1

Description

本発明は、新規な樹脂組成物に関する。更に詳しくは、防虫機能を有する樹脂組成物、及びこれを用いたフィルム並びに壁紙、化粧シートに関する。
The present invention relates to a novel resin composition. More specifically, the present invention relates to a resin composition having an insect repellent function, a film using the same, wallpaper, and a decorative sheet.

エチレン・ビニルアルコール共重合体は耐薬品性、及び耐汚染性などに優れているため、従来から塩化ビニル系樹脂フィルムなどのフィルム基材の表面にエチレン・ビニルアルコール共重合体フィルムが貼合された積層体が、壁紙や化粧シートとして使用されている。近年、蚊の媒介するデング熱などの感染症に対する関心、ヒアリなどの強い毒を有する外来昆虫に対する関心が高まっており、壁紙や化粧シートにも防虫機能を付与することが期待されている。しかし、防虫剤を配合した樹脂組成物のフィルムには、防虫剤がフィルム表面にブリードアウトして白濁した外観を呈するという問題（以下、この問題を「ブリード白化」ということがある。）があった。
Since ethylene / vinyl alcohol copolymer has excellent chemical resistance and stain resistance, an ethylene / vinyl alcohol copolymer film has been conventionally bonded to the surface of a film substrate such as a vinyl chloride resin film. Laminated bodies are used as wallpaper and decorative sheets. In recent years, interest in infectious diseases such as dengue fever mediated by mosquitoes and interest in foreign insects having strong poisons such as fire ants have increased, and it is expected to provide insect repellent functions to wallpaper and decorative sheets. However, a film of a resin composition containing an insect repellent has a problem that the insect repellent bleeds out on the film surface and exhibits a cloudy appearance (hereinafter, this problem may be referred to as “bleed whitening”). It was.

特開２００６‐０９６７１８号公報JP 2006-096718 A 特開２０１１‐１５７５３９号公報JP 2011-157539 A

本発明の課題は、防虫機能を有する樹脂組成物、及びこれを用いたフィルム、並びに壁紙、化粧シートを提供することにある。本発明の更なる課題は、防虫機能を有し、ブリード白化が抑制され、エンボス加工適性に優れ、エチレン・ビニルアルコール共重合体の有する耐薬品性及び耐汚染性などの好ましい特性の低下の抑制された樹脂組成物、及びこれを用いたフィルム、並びに壁紙、化粧シートを提供することにある。
An object of the present invention is to provide a resin composition having an insect repellent function, a film using the same, a wallpaper, and a decorative sheet. Further problems of the present invention include an insect repellent function, suppression of bleed whitening, excellent embossing suitability, and suppression of reduction in preferable properties such as chemical resistance and stain resistance of the ethylene / vinyl alcohol copolymer. Another object of the present invention is to provide a resin composition, a film using the resin composition, a wallpaper, and a decorative sheet.

本発明者は、鋭意研究した結果、特定の樹脂組成物により、上記課題を達成できることを見出した。 As a result of intensive studies, the present inventor has found that the above-described problems can be achieved by a specific resin composition.

すなわち、本発明は、
（Ａ）エチレン・ビニルアルコール共重合体 １００質量部；及び、
（Ｂ）ピレスロイド系化合物 ０．０１〜５質量部；
を含む熱可塑性樹脂組成物である。 That is, the present invention
(A) ethylene / vinyl alcohol copolymer 100 parts by mass; and
(B) 0.01-5 parts by mass of a pyrethroid compound;
Is a thermoplastic resin composition.

第２の発明は、
（Ａ）エチレン・ビニルアルコール共重合体 ８０〜９８質量％；と
（Ｃ）ポリエチレン ２０〜２質量％；からなり、
ここで上記成分（Ａ）エチレン・ビニルアルコール共重合体と上記成分（Ｃ）ポリエチレンとの和は１００質量％である、熱可塑性樹脂混合物 １００質量部；及び、
（Ｂ）ピレスロイド系化合物 ０．０１〜５質量部；
を含む熱可塑性樹脂組成物である。 The second invention is
(A) ethylene-vinyl alcohol copolymer 80-98% by mass; and (C) polyethylene 20-2% by mass;
Here, the sum of the component (A) ethylene / vinyl alcohol copolymer and the component (C) polyethylene is 100% by mass, 100 parts by mass of the thermoplastic resin mixture; and
(B) 0.01-5 parts by mass of a pyrethroid compound;
Is a thermoplastic resin composition.

第３の発明は、上記成分（Ａ）エチレン・ビニルアルコール共重合体のエチレンに由来する構成単位の含有量が３５〜６０モル％である第１の発明又は第２の発明に記載の熱可塑性樹脂組成物である。 3rd invention is thermoplasticity as described in 1st invention or 2nd invention whose content of the structural unit derived from ethylene of the said component (A) ethylene vinyl alcohol copolymer is 35-60 mol%. It is a resin composition.

第４の発明は、第１〜３の発明の何れか１に記載の熱可塑性樹脂組成物からなるフィルムである。 A fourth invention is a film comprising the thermoplastic resin composition according to any one of the first to third inventions.

第５の発明は、第４の発明に記載のフィルムを含む壁紙である。 5th invention is the wallpaper containing the film as described in 4th invention.

第６の発明は、第４の発明に記載のフィルムを含む化粧シートである。
6th invention is a decorative sheet containing the film as described in 4th invention.

本発明の樹脂組成物は防虫機能を有する。本発明の樹脂組成物からなるフィルムは、防虫機能を有し、ブリード白化が抑制され、エンボス加工適性に優れ、エチレン・ビニルアルコール共重合体フィルムの有する耐薬品性及び耐汚染性などの好ましい特性の低下が抑制されている。そのため、壁紙や化粧シートとして好適に用いることができる。
The resin composition of the present invention has an insect repellent function. The film comprising the resin composition of the present invention has an insect-repellent function, bleed whitening is suppressed, has excellent embossing suitability, and preferable characteristics such as chemical resistance and stain resistance of the ethylene / vinyl alcohol copolymer film The decline of the is suppressed. Therefore, it can be suitably used as wallpaper or a decorative sheet.

本明細書において「樹脂」の用語は、２以上の樹脂を含む樹脂混合物や、樹脂以外の成分を含む樹脂組成物をも含む用語として使用する。本明細書において「フィルム」の用語は、「シート」と相互交換的に又は相互置換可能に使用する。また本明細書において、ある層と他の層とを順に積層することは、それらの層を直接積層すること、及び、それらの層の間にアンカーコートなどの別の層を１層以上介在させて積層することの両方を含む。本明細書において、「フィルム」及び「シート」の用語は、工業的にロール状に巻き取ることのできるものに使用する。「板」の用語は、工業的にロール状に巻き取ることのできないものに使用する。 In this specification, the term “resin” is used as a term including a resin mixture containing two or more resins and a resin composition containing components other than the resin. In this specification, the term “film” is used interchangeably or interchangeably with “sheet”. Further, in this specification, laminating a certain layer and another layer in order means laminating those layers directly and interposing one or more other layers such as anchor coats between these layers. Including both lamination. In this specification, the terms “film” and “sheet” are used for what can be rolled up in a roll form industrially. The term “plate” is used for those that cannot be rolled up industrially in roll form.

数値範囲に係る「以上」の用語は、ある数値又はある数値超の意味で使用する。例えば、２０％以上は、２０％又は２０％超を意味する。数値範囲に係る「以下」の用語は、ある数値又はある数値未満の意味で使用する。例えば、２０％以下は、２０％又は２０％未満を意味する。更に数値範囲に係る「〜」の記号は、ある数値、ある数値超かつ他のある数値未満、又は他のある数値の意味で使用する。ここで、他のある数値は、ある数値よりも大きい数値とする。例えば、１０〜９０％は、１０％、１０％超かつ９０％未満、又は９０％を意味する。 The term “more than” relating to a numerical range is used in the sense of a certain numerical value or a certain numerical value. For example, 20% or more means 20% or more than 20%. The term “below” relating to a numerical range is used to mean a certain numerical value or less than a certain numerical value. For example, 20% or less means 20% or less than 20%. Furthermore, the symbol “˜” relating to a numerical range is used to mean a certain numerical value, a certain numerical value and less than a certain other numerical value, or another certain numerical value. Here, it is assumed that some other numerical value is larger than a certain numerical value. For example, 10-90% means 10%, more than 10% and less than 90%, or 90%.

実施例以外において、又は別段に指定されていない限り、本明細書及び特許請求の範囲において使用されるすべての数値は、「約」という用語により修飾されるものとして理解されるべきである。特許請求の範囲に対する均等論の適用を制限しようとすることなく、各数値は、有効数字に照らして、及び通常の丸め手法を適用することにより解釈されるべきである。 Unless otherwise specified, or unless otherwise specified, all numerical values used in the specification and claims are to be understood as being modified by the term “about”. Without attempting to limit the application of the doctrine of equivalents to the claims, each number should be interpreted in the light of significant figures and by applying conventional rounding techniques.

本発明の樹脂組成物は、（Ａ）エチレン・ビニルアルコール共重合体；及び、（Ｂ）ピレスロイド系化合物；を含む。 The resin composition of the present invention includes (A) an ethylene / vinyl alcohol copolymer; and (B) a pyrethroid compound.

（Ａ）エチレン・ビニルアルコール共重合体：
上記成分（Ａ）エチレン・ビニルアルコール共重合体は、エチレンとビニルアルコールとが共重合した構造を有する共重合体である。上記成分（Ａ）は、ビニルアルコールが熱力学的に不安定な化合物であるため、通常は、エチレンとビニルエステルとの共重合体を鹸化して生産される。 (A) Ethylene / vinyl alcohol copolymer:
The component (A) ethylene / vinyl alcohol copolymer is a copolymer having a structure in which ethylene and vinyl alcohol are copolymerized. The component (A) is usually produced by saponifying a copolymer of ethylene and vinyl ester because vinyl alcohol is a thermodynamically unstable compound.

上記ビニルエステルとしては、例えば、酢酸ビニル、プロピオン酸ビニル、酪酸ビニル、及びピバリン酸ビニルなどの脂肪酸ビニルエステルをあげることができる。上記ビニルエステルとしては、これらの１種以上を用いることができる。 Examples of the vinyl ester include fatty acid vinyl esters such as vinyl acetate, vinyl propionate, vinyl butyrate, and vinyl pivalate. One or more of these may be used as the vinyl ester.

上記成分（Ａ）の鹸化度（ビニルエステルに由来する全構成単位を１００モル％としたとき、ビニルエステルに由来する構成単位であって、鹸化によりビニルアルコール構造になっている構成単位の割合。）は、エチレン・ビニルアルコール共重合体フィルムの有する耐薬品性及び耐汚染性などの好ましい特性の低下を抑制する観点から、通常８０モル％以上、好ましくは８５モル％以上、より好ましくは９０モル％以上であってよい。一方、耐水性、ブリード白化の抑制、エンボス加工適性、及び壁紙や化粧シートとして用いる際の施行性の観点から、通常１００モル％以下、好ましくは９９モル％以下、より好ましくは９６モル％以下であってよい。 Degree of saponification of component (A) (the proportion of structural units derived from vinyl ester and having a vinyl alcohol structure by saponification when the total structural units derived from vinyl ester are 100 mol%). ) Is usually 80 mol% or more, preferably 85 mol% or more, more preferably 90 mol, from the viewpoint of suppressing a decrease in preferable properties such as chemical resistance and stain resistance of the ethylene / vinyl alcohol copolymer film. % Or more. On the other hand, from the viewpoint of water resistance, suppression of bleed whitening, suitability for embossing, and enforceability when used as wallpaper or a decorative sheet, it is usually 100 mol% or less, preferably 99 mol% or less, more preferably 96 mol% or less. It may be.

上記成分（Ａ）のエチレンに由来する構成単位の含有量は、全構成モノマーに由来する構成単位の総和を１００モル％としたとき、耐水性、ブリード白化の抑制、エンボス加工適性、及び壁紙や化粧シートとして用いる際の施行性の観点から、通常１０モル％以上、好ましくは２０モル％以上、より好ましくは３０モル％以上、更に好ましくは３５モル％以上、最も好ましくは４０モル％以上であってよい。一方、エチレン・ビニルアルコール共重合体フィルムの有する耐薬品性及び耐汚染性などの好ましい特性の低下を抑制する観点から、通常８０モル％以下、好ましくは７０モル％以下、より好ましくは６５モル％以下、更に好ましくは６０モル％以下、最も好ましくは５５モル％以下であってよい。 The content of the structural unit derived from ethylene of the component (A) is water resistance, suppression of bleed whitening, suitability for embossing, wallpaper, and the like when the sum of structural units derived from all structural monomers is 100 mol%. From the viewpoint of effectiveness when used as a decorative sheet, it is usually at least 10 mol%, preferably at least 20 mol%, more preferably at least 30 mol%, even more preferably at least 35 mol%, most preferably at least 40 mol%. It's okay. On the other hand, from the viewpoint of suppressing a decrease in preferable properties such as chemical resistance and stain resistance of the ethylene / vinyl alcohol copolymer film, it is usually 80 mol% or less, preferably 70 mol% or less, more preferably 65 mol%. Hereinafter, it may be more preferably 60 mol% or less, most preferably 55 mol% or less.

上記成分（Ａ）のＪＩＳ Ｋ７２１０‐１：２０１４に準拠し、２１０℃、２１．１８Ｎの条件で測定したメルトマスフローレートは、フィルム製膜性の観点から、通常１〜３０ｇ／１０分、好ましくは２〜２０ｇ／１０分であってよい。 Based on JIS K7210-1: 2014 of the said component (A), the melt mass flow rate measured on condition of 210 degreeC and 21.18N is 1-30 g / 10min normally from a film-forming viewpoint, Preferably It may be 2-20 g / 10 minutes.

上記成分（Ａ）は、本発明の目的に反しない限度において、所望により、エチレンに由来する構成単位、及びビニルエステルに由来する構成単位以外に、エチレン、ビニルエステルの少なくとも何れかと共重合可能なモノマーに由来する構成単位を含むものであってよい。上記共重合可能なモノマーは、通常、炭素・炭素二重結合を有する化合物であり、典型的にはエチレン性二重結合を有する化合物である。上記共重合可能なモノマーとしては、例えば、プロピレン、１‐ブテン、１‐ヘキセン、及び１‐オクテンなどのα‐オレフィン；マレイン酸、イタコン酸、フマル酸、アクリル酸、及びメタクリル酸などの不飽和カルボン酸；マレイン酸モノエステル、マレイン酸ジエステル、無水マレイン酸、イタコン酸モノエステル、イタコン酸ジエステル、無水イタコン酸、フマル酸モノエステル、フマル酸ジエステル、無水フマル酸、アクリル酸メチル等のアクリル酸アルキル、及びメタクリル酸メチル等のメタクリル酸アルキルなどの不飽和カルボン酸の誘導体；及び、塩化ビニル；などをあげることができる。上記共重合可能なモノマーとしては、これらの１種以上を用いることができる。 The component (A) can be copolymerized with at least one of ethylene and vinyl ester in addition to the structural unit derived from ethylene and the structural unit derived from vinyl ester, as long as it does not contradict the purpose of the present invention. It may contain a structural unit derived from a monomer. The copolymerizable monomer is usually a compound having a carbon / carbon double bond, typically a compound having an ethylenic double bond. Examples of the copolymerizable monomer include α-olefins such as propylene, 1-butene, 1-hexene, and 1-octene; unsaturated compounds such as maleic acid, itaconic acid, fumaric acid, acrylic acid, and methacrylic acid. Carboxylic acid; maleic acid monoester, maleic acid diester, maleic anhydride, itaconic acid monoester, itaconic acid diester, itaconic anhydride, fumaric acid monoester, fumaric acid diester, fumaric anhydride, methyl acrylate and other alkyl acrylates And derivatives of unsaturated carboxylic acids such as alkyl methacrylates such as methyl methacrylate; and vinyl chloride. One or more of these may be used as the copolymerizable monomer.

上記成分（Ａ）のエチレンに由来する構成単位、ビニルエステルに由来する構成単位などの各構成単位の含有量は、^１３Ｃ‐ＮＭＲを使用して求めることができる。ピークの帰属は、「高分子分析ハンドブック（２００８年９月２０日初版第１刷、社団法人日本分析化学会高分子分析研究懇談会編、株式会社朝倉書店）」や「独立行政法人物質・材料研究機構材料情報ステーションのＮＭＲデータベース（ｈｔｔｐ：／／ｐｏｌｙｍｅｒ．ｎｉｍｓ．ｇｏ．ｊｐ／ＮＭＲ／）」を参考に行い、ピーク面積比から上記成分（Ａ）中の各構成単位の含有量を算出することができる。なお^１３Ｃ−ＮＭＲの測定は、株式会社三井化学分析センターなどの分析機関において行うこともできる。 The content of each structural unit such as a structural unit derived from ethylene of the component (A) or a structural unit derived from vinyl ester can be determined using ¹³ C-NMR. The attribution of the peak is “Polymer Analysis Handbook (September 20, 2008, first edition, edited by Japan Analytical Chemistry Society, Polymer Analysis Research Meeting, Asakura Shoten Co., Ltd.)” Calculate the content of each structural unit in the component (A) from the peak area ratio by referring to the NMR database (http://polymer.nims.go.jp/NMR/) of the Research Organization Material Information Station. be able to. In addition, the measurement of ¹³ C-NMR can also be performed in an analysis organization such as Mitsui Chemical Analysis Center.

（Ｂ）ピレスロイド系化合物：
上記成分（Ｂ）ピレスロイド系化合物は、防虫機能を発現させる働きをする。また上記成分（Ａ）との組み合わせにおいて、ブリード白化が起こり難いという特性を有する。 (B) Pyrethroid compound:
The component (B) pyrethroid compound functions to develop an insect repellent function. Moreover, in combination with the said component (A), it has the characteristic that bleeding whitening does not occur easily.

上記成分（Ｂ）としては、例えば、ピレトリン１、ピレトリン２、シネリン１、シネリン２、ジャスモリン１、及びジャスモリン２などの天然ピレスロイド；アレスリン、フタルスリン（Ｄ‐テトラメトリン）、レスメトリン、フラメトリン、フェノトリン、ペルメトリン、シフェノトリン、ベラトリン、シラフルオフェン、及びエトフェンプロックス（２‐（４‐エトキシフェニル）‐２‐メチルプロピル＝３‐フェノキシベンジルエーテル、ＣＡＳ登録番号８０８４４‐０７‐１）などの合成ピレスロイド系化合物；などをあげることができる。これらの中で、虫以外の生物に対する毒性（哺乳類や鳥類などの温血動物に対する毒性、魚に対する毒性など。）の低さ、及び防虫機能の観点から、エトフェンプロックスが好ましい。上記成分（Ｂ）としては、これらの１種又は２種以上の混合物を用いることができる。 Examples of the component (B) include natural pyrethroids such as pyrethrin 1, pyrethrin 2, cineline 1, cinerine 2, jasmorin 1, and jasmolin 2; Synthetic pyrethroid compounds such as ciphenothrin, veratrine, silafluophene, and etofenprox (2- (4-ethoxyphenyl) -2-methylpropyl = 3-phenoxybenzyl ether, CAS Registry Number 80844-07-1); I can give you. Among these, etofenprox is preferable from the viewpoint of low toxicity to organisms other than insects (toxicity to warm-blooded animals such as mammals and birds, toxicity to fish, etc.) and insect-repellent function. As said component (B), these 1 type, or 2 or more types of mixtures can be used.

上記成分（Ｂ）の配合量は、上記成分（Ａ）１００質量部に対して、ブリード白化を抑制する観点から、通常５質量部以下、好ましくは４質量部以下、より好ましくは３質量部以下、更に好ましくは２．５質量部以下、最も好ましくは２質量部以下である。一方、防虫機能、及び防虫機能の持続性の観点から、通常０．０１質量部以上、好ましくは０．１質量部以上、より好ましくは０．５質量部以上である。 The blending amount of the component (B) is usually 5 parts by mass or less, preferably 4 parts by mass or less, more preferably 3 parts by mass or less, from the viewpoint of suppressing bleed whitening with respect to 100 parts by mass of the component (A). More preferably, it is 2.5 parts by mass or less, and most preferably 2 parts by mass or less. On the other hand, from the viewpoint of the insect repellent function and the sustainability of the insect repellent function, it is usually 0.01 parts by mass or more, preferably 0.1 parts by mass or more, more preferably 0.5 parts by mass or more.

（Ｃ）ポリエチレン：
本発明の樹脂組成物は、好ましい態様の１つにおいて、上記成分（Ｃ）ポリエチレンを含むものであってよい。上記成分（Ｃ）は、フィルム製膜性、耐水性、エンボス加工適性、及び壁紙や化粧シートとして用いる際の施行性を高める働きをする。 (C) Polyethylene:
In one of the preferable embodiments, the resin composition of the present invention may contain the component (C) polyethylene. The component (C) functions to enhance film formability, water resistance, embossing suitability, and enforceability when used as a wallpaper or a decorative sheet.

上記成分（Ｃ）は、エチレンに由来する構成単位を主として含む重合体である。上記成分（Ｃ）としては、例えば、低密度ポリエチレン、直鎖状低密度ポリエチレン、超低密度ポリエチレン、高密度ポリエチレン、エチレン単独重合体、エチレンとα−オレフィン（例えば、プロピレン、１−ブテン、１−ヘキセン、及び１−オクテン等の１種又は２種以上）との共重合体などをあげることができる。上記成分（Ｃ）としては、これらの１種又は２種以上の混合物を用いることができる。なお上記成分（Ｃ）として混合物を用いる場合には、混合物として後述する密度やメルトマスフローレートの範囲を有するものが好ましい。 The component (C) is a polymer mainly containing structural units derived from ethylene. Examples of the component (C) include low density polyethylene, linear low density polyethylene, ultra-low density polyethylene, high density polyethylene, ethylene homopolymer, ethylene and α-olefin (for example, propylene, 1-butene, 1 -A copolymer with 1 type, or 2 or more types, such as -hexene and 1-octene, etc. can be mention | raise | lifted. As said component (C), these 1 type, or 2 or more types of mixtures can be used. In addition, when using a mixture as said component (C), what has the range of the density and melt mass flow rate mentioned later as a mixture is preferable.

上記成分（Ｃ）のＪＩＳ Ｋ７１１２：１９９９に準拠し、水中置換法で測定した密度は、透明性の観点から、通常９３０Ｋｇ／ｍ^３以下、好ましくは９１０Ｋｇ／ｍ^３以下、より好ましくは８９０Ｋｇ／ｍ^３以下、更に好ましくは８８０Ｋｇ／ｍ^３以下であってよい。一方、フィルム製膜性の観点から通常８５０Ｋｇ／ｍ^３以上、好ましくは８６０Ｋｇ／ｍ^３以上であってよい。 Based on JIS K7112: 1999 of the said component (C), the density measured by the underwater substitution method is usually 930 Kg / m ³ or less, preferably 910 Kg / m ³ or less, more preferably 890 Kg / m, from the viewpoint of transparency. ³ or less, more preferably it may be at 880 kg / ^{m 3} or less. On the other hand, from the viewpoint of film formability, it may be usually 850 kg / m ³ or more, preferably 860 kg / m ³ or more.

上記成分（Ｃ）のＪＩＳ Ｋ７２１０‐１：２０１４に準拠し、１９０℃、２１．１８Ｎの条件で測定したメルトマスフローレートは、フィルム製膜性の観点から、通常０．１〜３０ｇ／１０分、好ましくは０．５〜１０ｇ／１０分であってよい。 Based on JIS K7210-1: 2014 of the said component (C), the melt mass flow rate measured on condition of 190 degreeC and 21.18N is 0.1-30 g / 10min normally from a film-forming viewpoint, Preferably, it may be 0.5 to 10 g / 10 minutes.

上記成分（Ｃ）の配合量は、任意成分であるから特に制限されない。上記成分（Ｃ）の配合量は、上記成分（Ａ）と上記成分（Ｃ）との和を１００質量％として、フィルム製膜性の観点から、好ましくは２質量％以上、より好ましくは５質量％以上であってよい。一方、透明性の観点から、好ましくは２０質量％以下、より好ましくは１５質量％以下、更に好ましくは１０質量％以下であってよい。 The compounding amount of the component (C) is not particularly limited because it is an optional component. The blending amount of the component (C) is preferably 2% by mass or more, more preferably 5% by mass, from the viewpoint of film formability, with the sum of the component (A) and the component (C) being 100% by mass. % Or more. On the other hand, from the viewpoint of transparency, it may be preferably 20% by mass or less, more preferably 15% by mass or less, and still more preferably 10% by mass or less.

本発明の樹脂組成物には、本発明の目的に反しない限度において、フェノール系、リン系、及び硫黄系などの酸化防止剤；老化防止剤、光安定剤、及び紫外線吸収剤などの耐候剤；酸アミド、脂肪酸、脂肪酸金属塩、ワックス、シリコンオイル、及び変性シリコンオイルなどの滑剤；芳香族リン酸金属塩系、及びゲルオール系などの造核剤；グリセリン脂肪酸エステル系などの帯電防止剤；有機系・無機系の各種難燃剤；無機微粒子、有機微粒子、無機着色剤、及び有機着色剤などの任意成分を１種又は２種以上含ませることができる。これらの任意成分の配合量は、任意成分であるから特に制限されない。これらの任意成分の配合量は、上記成分（Ａ）を１００質量部として、通常０．０１〜１０質量部程度である。 In the resin composition of the present invention, phenolic, phosphorus-based and sulfur-based antioxidants; anti-aging agents, light stabilizers, and weathering agents such as UV absorbers, etc., as long as they do not contradict the purpose of the present invention. Lubricants such as acid amides, fatty acids, fatty acid metal salts, waxes, silicone oils, and modified silicone oils; nucleating agents such as aromatic phosphate metal salts and gelols; antistatic agents such as glycerin fatty acid esters; Various types of organic and inorganic flame retardants; one or more optional components such as inorganic fine particles, organic fine particles, inorganic colorants, and organic colorants can be included. The amount of these optional components is not particularly limited because they are optional components. The compounding quantity of these arbitrary components is about 0.01-10 mass parts normally by making the said component (A) into 100 mass parts.

本発明の樹脂組成物は、上記成分（Ａ）、上記成分（Ｂ）、及びその他の任意成分を用い、公知の溶融混練機を使用して溶融混練することにより得ることができる。上記溶融混練機としては、例えば、加圧ニーダー及びミキサー等のバッチ混練機；同方向回転二軸押出機、異方向回転二軸押出機などの押出混練機；カレンダーロール混練機；及び、これらを任意に組み合わせた装置などをあげることができる。得られた樹脂組成物は、公知の造粒方法を使用して造粒し、ペレット化することができる。上記造粒方法としては、例えば、ホットカット、ストランドカット、及びアンダーウォーターカットなどの方法をあげることができる。 The resin composition of the present invention can be obtained by using the above component (A), the above component (B), and other optional components by melt kneading using a known melt kneader. Examples of the melt kneader include, for example, a batch kneader such as a pressure kneader and a mixer; an extrusion kneader such as a co-rotating twin screw extruder and a different direction rotating twin screw extruder; a calendar roll kneader; Arbitrary combinations of devices can be given. The obtained resin composition can be granulated and pelletized using a known granulation method. Examples of the granulation method include methods such as hot cut, strand cut, and underwater cut.

本発明のフィルムは、本発明の樹脂組成物を含むフィルムである。本発明のフィルムは、好ましくは本発明の樹脂組成物からなるフィルムである。本発明のフィルムは、本発明の樹脂組成物を用い、公知の製膜装置を使用して製膜することにより得ることができる。上記製膜装置としては、例えば、カレンダー圧延ロールと引巻取機を備える装置；押出機、Ｔダイ、及び引巻取機を備える装置；及び、押出機、円筒ダイ、及び引巻取機を備える装置；などをあげることができる。 The film of the present invention is a film containing the resin composition of the present invention. The film of the present invention is preferably a film comprising the resin composition of the present invention. The film of the present invention can be obtained by forming a film using the resin composition of the present invention using a known film forming apparatus. Examples of the film forming apparatus include an apparatus including a calender roll and a winder; an apparatus including an extruder, a T die, and a winder; and an extruder, a cylindrical die, and a winder. And the like.

本発明の壁紙は、本発明のフィルムを含む壁紙である。本発明の壁紙としては、例えば、正面（壁紙が実使用に供される際に、通常視認される側となる面。以下、同じ。）側から順に、本発明のフィルムの層、印刷層、及び着色樹脂シートの層を有するものをあげることができる。 The wallpaper of the present invention is a wallpaper including the film of the present invention. As the wallpaper of the present invention, for example, the film layer of the present invention, the printed layer, in order from the front side (the surface that is normally visible when the wallpaper is put into actual use; the same applies hereinafter) And those having a colored resin sheet layer.

本発明の化粧シートは、本発明のフィルムを含む化粧シートである。本発明の化粧シートとしては、例えば、正面（化粧シートが実使用に供される際に、通常視認される側となる面。以下、同じ。）側から順に、本発明のフィルムの層、印刷層、及び着色樹脂シートの層を有するものをあげることができる。 The decorative sheet of the present invention is a decorative sheet including the film of the present invention. As the decorative sheet of the present invention, for example, the layer of the film of the present invention and the printing in this order from the front side (the surface that is normally visible when the decorative sheet is used for actual use). The thing which has a layer and the layer of a colored resin sheet can be mention | raise | lifted.

本発明のフィルムの層には、意匠性の観点から、所望により、エンボス模様を形成してもよいし、形成しなくてもよい。上記エンボス模様は、例えば、エンボスロールと受けロールとで押圧する機構を備えたエンボス装置を使用し、回転するエンボスロールと受けロールとの間に、本発明のフィルムを供給投入し、押圧することにより；又は、本発明のフィルムの層、印刷層、及び着色樹脂シートの層を有する積層体を、本発明のフィルムの層側の面が上記エンボスロール側となるように供給投入し、押圧することにより；形成することができる。上記エンボスロールは、その表面に凹凸模様の彫刻されたロールである。上記エンボスロールとしては、例えば、金属製、セラミック製、及びシリコンゴム製などのエンボスロールをあげることができる。上記エンボス形状は、特に制限されず、意匠性の観点から、任意の形状を選択することができる。上記エンボス形状としては、例えば、木目柄や皮しぼなどの天然素材を模した形状；金属を加工したかの様なヘアライン模様の形状；格子柄、ストライプ模様、及び水玉模様などの幾何抽象柄の形状；及び、これらの組み合わせをあげることができる。更に上記エンボス模様の凹部には、ワイピング印刷などの方法により、印刷インキを充填してもよいし、充填しなくてもよい。 In the film layer of the present invention, an embossed pattern may or may not be formed as desired from the viewpoint of design. For example, the embossed pattern is formed by using an embossing device having a mechanism for pressing with an embossing roll and a receiving roll, and supplying and pressing the film of the present invention between the rotating embossing roll and the receiving roll. Or, supply and press the laminated body having the layer of the film of the present invention, the printed layer, and the layer of the colored resin sheet so that the surface on the layer side of the film of the present invention is on the embossing roll side. It can be formed. The embossing roll is a roll engraved with an uneven pattern on its surface. Examples of the embossing roll include metal, ceramic and silicon rubber embossing rolls. The emboss shape is not particularly limited, and any shape can be selected from the viewpoint of design. The embossed shape includes, for example, a shape imitating a natural material such as a wood grain pattern or a skin wrinkle; a shape of a hairline pattern as if processing a metal; a geometric abstract pattern such as a lattice pattern, a stripe pattern, and a polka dot pattern Shapes; and combinations thereof. Furthermore, the concave portions of the embossed pattern may be filled with printing ink by a method such as wiping printing, or may not be filled.

上記着色樹脂シートとしては、例えば、芳香族ポリエステル、脂肪族ポリエステルなどのポリエステル系樹脂；アクリル系樹脂；ポリカーボネート系樹脂；ポリ（メタ）アクリルイミド系樹脂；ポリエチレン、ポリプロピレン、及びポリメチルペンテンなどのポリオレフィン系樹脂；セロファン、トリアセチルセルロース、ジアセチルセルロース、及びアセチルセルロースブチレートなどのセルロース系樹脂；ポリスチレン、アクリロニトリル・ブタジエン・スチレン共重合樹脂（ＡＢＳ樹脂）、スチレン・エチレン・プロピレン・スチレン共重合体、スチレン・エチレン・エチレン・プロピレン・スチレン共重合体、及びスチレン・エチレン・ブタジエン・スチレン共重合体などのスチレン系樹脂；ポリ塩化ビニル系樹脂；ポリ塩化ビニリデン系樹脂；ポリフッ化ビニリデンなどの含弗素系樹脂；その他、ポリビニルアルコール、エチレン・ビニルアルコール共重合体、ポリエーテルエーテルケトン、ナイロン、ポリアミド、ポリイミド、ポリウレタン、ポリエーテルイミド、ポリスルフォン、ポリエーテルスルフォン；などの着色樹脂シートをあげることができる。これらのシートは、無延伸シート、一軸延伸シート、二軸延伸シートを包含する。また発泡シートを包含する。更にこれらの１種以上を２層以上積層した積層シートを包含する。 Examples of the colored resin sheet include polyester resins such as aromatic polyesters and aliphatic polyesters; acrylic resins; polycarbonate resins; poly (meth) acrylimide resins; polyolefins such as polyethylene, polypropylene, and polymethylpentene. Cellulosic resin: Cellulosic resin such as cellophane, triacetylcellulose, diacetylcellulose, and acetylcellulose butyrate; polystyrene, acrylonitrile / butadiene / styrene copolymer resin (ABS resin), styrene / ethylene / propylene / styrene copolymer, styrene・ Styrene resins such as ethylene / ethylene / propylene / styrene copolymers and styrene / ethylene / butadiene / styrene copolymers; polyvinyl chloride resins; polyvinyl chloride Fluorine-based resins such as polyvinylidene fluoride; Polyvinyl alcohol, ethylene / vinyl alcohol copolymer, polyetheretherketone, nylon, polyamide, polyimide, polyurethane, polyetherimide, polysulfone, polyethersulfone And the like. These sheets include an unstretched sheet, a uniaxially stretched sheet, and a biaxially stretched sheet. It also includes a foam sheet. Furthermore, the laminated sheet which laminated | stacked these 1 or more types 2 or more layers is included.

上記着色樹脂シートの厚みは、特に制限されないが、通常２０μｍ以上、好ましくは５０μｍ以上、より好ましくは８０μｍ以上であってよい。また物品の薄肉化の要求に応える観点から、通常１５００μｍ以下、好ましくは８００μｍ以下、より好ましくは４００μｍ以下、更に好ましくは２５０μ以下であってよい。 The thickness of the colored resin sheet is not particularly limited, but may be usually 20 μm or more, preferably 50 μm or more, more preferably 80 μm or more. Further, from the viewpoint of meeting the demand for thinner articles, it may be usually 1500 μm or less, preferably 800 μm or less, more preferably 400 μm or less, and even more preferably 250 μm or less.

上記印刷層は、高い意匠性を付与するために設けるものであり、任意の模様を任意のインキと任意の印刷機を使用して印刷することにより形成することができる。 The printing layer is provided for imparting high designability, and can be formed by printing an arbitrary pattern using an arbitrary ink and an arbitrary printing machine.

印刷は、直接又はアンカーコートを介して、本発明のフィルムの正面とは反対側の面の上に、又は／及び上記着色樹脂シートの正面側の面の上に、全面的に又は部分的に、施すことができる。模様としては、ヘアライン等の金属調模様、木目模様、大理石等の岩石の表面を模した石目模様、布目や布状の模様を模した布地模様、タイル貼模様、煉瓦積模様、寄木模様、及びパッチワークなどをあげることができる。印刷インキとしては、バインダーに顔料、溶剤、安定剤、可塑剤、触媒、及び硬化剤等を適宜混合したものを使用することができる。上記バインダーとしては、例えば、ポリウレタン系樹脂、塩化ビニル・酢酸ビニル系共重合体樹脂、塩化ビニル・酢酸ビニル・アクリル系共重合体樹脂、塩素化ポリプロピレン系樹脂、アクリル系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、ブチラール系樹脂、ポリスチレン系樹脂、ニトロセルロース系樹脂、及び酢酸セルロース系樹脂などの樹脂、及びこれらの樹脂組成物を使用することができる。また金属調の意匠を施すため、アルミニウム、錫、チタン、インジウム及びこれらの酸化物などを、直接又はアンカーコートを介して、本発明のフィルムの正面とは反対側の面の上に、又は／及び上記着色樹脂シートの正面側の面の上に、全面的に又は部分的に、公知の方法により蒸着してもよい。 Printing is carried out directly or through an anchor coat on the surface opposite to the front surface of the film of the present invention, and / or on the front surface surface of the colored resin sheet. Can be applied. The patterns include metal-like patterns such as hairlines, wood grain patterns, stone patterns imitating the surface of rocks such as marble, fabric patterns imitating cloth and cloth-like patterns, tiled patterns, brickwork patterns, parquet patterns, And patchwork. As printing ink, what mixed the pigment, the solvent, the stabilizer, the plasticizer, the catalyst, the hardening | curing agent, etc. in the binder suitably can be used. Examples of the binder include polyurethane resins, vinyl chloride / vinyl acetate copolymer resins, vinyl chloride / vinyl acetate / acrylic copolymer resins, chlorinated polypropylene resins, acrylic resins, polyester resins, polyamides. Resins such as resin, butyral resin, polystyrene resin, nitrocellulose resin, and cellulose acetate resin, and these resin compositions can be used. Moreover, in order to give a metallic design, aluminum, tin, titanium, indium and oxides thereof are directly or via an anchor coat on the surface opposite to the front surface of the film of the present invention, or / In addition, it may be vapor-deposited by a known method on the entire front surface of the colored resin sheet or partially.

本発明のフィルムと上記着色樹脂シートとの積層は、特に制限されず、任意の方法で行うことができる。上記方法としては、例えば、公知の接着剤を用いてドライラミネートする方法；及び公知の粘着剤からなる層を形成した後、両者を重ね合せ押圧する方法；などをあげることができる。 Lamination | stacking with the film of this invention and the said colored resin sheet is not restrict | limited in particular, It can carry out by arbitrary methods. Examples of the method include a method of dry laminating using a known adhesive; and a method of forming a layer made of a known pressure-sensitive adhesive and then pressing them together.

図１は本発明の壁紙の一例を示す断面の概念図である。正面側から順に本発明のフィルムの層１、印刷層２、及び着色樹脂シートの層３を有している。また本発明のフィルムの層１にはエンボス模様４が形成されている。
FIG. 1 is a schematic sectional view showing an example of the wallpaper of the present invention. It has the layer 1 of the film of this invention, the printing layer 2, and the layer 3 of the colored resin sheet in order from the front side. An embossed pattern 4 is formed on the layer 1 of the film of the present invention.

以下、本発明を実施例により説明するが、本発明はこれらに限定されるものではない。 EXAMPLES Hereinafter, although an Example demonstrates this invention, this invention is not limited to these.

測定方法
（イ）ヘーズ：
ＪＩＳ Ｋ７１３６：２０００に従い、日本電色工業株式会社の濁度計「ＮＤＨ２０００（商品名）」を用いて測定した。 Measurement method (a) Haze:
According to JIS K7136: 2000, it measured using the turbidimeter "NDH2000 (brand name)" of Nippon Denshoku Industries Co., Ltd.

（ロ）ブリード白化：
温度８０℃、相対湿度５０％の環境下で２４時間処理した後、上記（イ）の方法に従い、ヘーズを測定した。上記（イ）ヘーズの値と比較して、ヘーズの増加が小さいものは、ブリード白化が抑制されていると評価できる。 (B) Bleed whitening:
After being treated for 24 hours in an environment of a temperature of 80 ° C. and a relative humidity of 50%, haze was measured according to the method (a). It can be evaluated that bleed whitening is suppressed when the increase in haze is small compared with the value of (a) haze.

（ハ）防虫機能：
樹脂フィルムに直径６ｃｍ、深さ５ｃｍのポリエチレンテレフタレートカップを仰向けに貼付け、上記カップの底に穴を開け、該穴から１０匹のチカイエカ（メス）を上記カップに入れた後、上記穴を脱脂綿で栓をし、５質量％蔗糖水を餌として綿に含ませた。４８時間経過後のノックダウン数と死虫数の和を計数した。試験は３回繰り返して行い、３回の試験の総和を算出した。 (C) Insect control function:
A polyethylene terephthalate cup with a diameter of 6 cm and a depth of 5 cm is stuck on the resin film, and a hole is made in the bottom of the cup. Ten Chikaeka (female) are put into the cup through the hole, and then the hole is made of absorbent cotton. The stopper was put and 5% by mass sucrose water was included in cotton as a bait. The sum of the number of knockdowns and the number of dead insects after 48 hours was counted. The test was repeated three times and the sum of the three tests was calculated.

（ニ）エンボス加工適性：
壁紙のエンボス形成面を肉眼（矯正視力１．０）で目視観察し、以下の基準で評価した。
◎：少なくとも最適条件では、エンボスが壁紙のエンボス形成面の全体にわたって形成されており、かつ壁紙や防虫フィルムの割れや穴開きもない。
○：最適条件でも、壁紙のエンボス形成面の一部にエンボスの形成されていない部分がある。しかし、少なくとも最適条件では、壁紙や防虫フィルムの割れや穴開きはない。
×：最適条件でも、エンボスがほとんど又は全く形成されていない、又は／及び、壁紙、防虫フィルムに割れや穴開きがある。 (D) Embossing suitability:
The embossed surface of the wallpaper was visually observed with the naked eye (corrected visual acuity 1.0) and evaluated according to the following criteria.
A: At least under the optimum conditions, the emboss is formed over the entire embossed surface of the wallpaper, and there is no cracking or perforation of the wallpaper or insect-proof film.
○: Even under optimum conditions, there is a portion where the emboss is not formed on a part of the emboss formation surface of the wallpaper. However, at least under optimal conditions, there is no cracking or perforation of the wallpaper or insect-proof film.
X: Little or no embossing is formed even under optimum conditions, and / or there are cracks and holes in the wallpaper and the insect-proof film.

（ホ）耐薬品性（耐ストレスクラック性）：
プロクター・アンド・ギャンブル社のオレンジオイル含有アルカリ洗剤「マイスター プロパー（Ｍｅｉｓｔｅｒ Ｐｒｏｐｅｒ）」（商品名）２０ｍｌに対し、マジックペン用（赤）インキを１０滴の割合で混合し試験液とした。次に試験片（壁紙）の防虫フィルム側の面の上に３０ｍｍ×４０ｍｍの大きさにカットした日本製紙クレシア株式会社の紙ワイパー「キムワイプ（商品名）」を広げて置き、スポイトを使用して上記試験液１０滴を上記紙ワイパーの上に均一に滴下した。滴下後、上記紙ワイパーと上記試験片との間の気泡を、ピンセットを使用して抜き、上記紙ワイパーと上記試験片とを密着させたものを温度２３℃、相対湿度５０％の環境下で保管した。保管時間２４時間毎に、上記試験液１０滴を滴下し、気泡を抜いて密着させる操作を繰り返しながら７２時間保管した。所定時間経過後、上記試験片上の上記試験液を含んだ上記紙ワイパーを除去し、上記試験片を上記紙ワイパーに水を染み込ませて水拭きし、更に乾いた上記紙ワイパーで乾拭きし、上記試験片表面に付着した上記試験液を完全に取除いた。上記試験片（壁紙）の防虫フィルム側の面を肉眼（矯正視力１．０）、又はルーペ（拡大倍率２５倍）を用いて目視観察し、以下の基準で評価した。
◎：ルーペを用いて観察してもクラックは認められない
○：肉眼ではクラックは認められない。しかし、ルーペを用いて観察すると軽微なクラックの存在が認められる。
×：肉眼でクラックを認めることができる。 (E) Chemical resistance (stress crack resistance):
An orange oil-containing alkaline detergent “Meister Proper” (trade name) (20 ml) manufactured by Procter & Gamble Co., Ltd. was mixed in a ratio of 10 drops with a magic pen (red) ink to prepare a test solution. Next, spread the paper wiper “Kimwipe (trade name)” of Nippon Paper Crecia Co., Ltd. cut to a size of 30 mm x 40 mm on the surface of the insect repellent film side of the test piece (wallpaper) and use a dropper. Ten drops of the test solution were uniformly dropped on the paper wiper. After dripping, bubbles between the paper wiper and the test piece are removed using tweezers, and the paper wiper and the test piece are brought into close contact with each other in an environment of a temperature of 23 ° C. and a relative humidity of 50%. Stored. It was stored for 72 hours while repeating the operation of dropping 10 drops of the test solution and removing the bubbles to make it come into close contact every 24 hours. After the elapse of a predetermined time, the paper wiper containing the test solution on the test piece is removed, the test piece is dipped in water with the paper wiper, wiped with the dry paper wiper, and then wiped. The test solution adhering to the surface of the test piece was completely removed. The surface of the test piece (wallpaper) on the insect-proof film side was visually observed using the naked eye (corrected visual acuity 1.0) or a magnifying glass (magnification 25 times), and evaluated according to the following criteria.
A: No cracks are observed even when observed with a loupe. B: No cracks are observed with the naked eye. However, when observed with a magnifying glass, the presence of minor cracks is observed.
X: A crack can be recognized with the naked eye.

使用した原材料
（Ａ）エチレン・ビニルアルコール共重合体：
（Ａ−１）株式会社クラレの「エバールＥ１０５Ｂ（商品名）」。エチレンに由来する構成単位の含有量４４モル％。メルトマスフローレート（２１０℃、２１．１８Ｎ）１３ｇ／１０分。
（Ａ−２）株式会社クラレの「エバールＬ１７１Ｂ（商品名）」。エチレンに由来する構成単位の含有量２７モル％。メルトマスフローレート（２１０℃、２１．１８Ｎ）４．０ｇ／１０分。
（Ａ−３）株式会社クラレの「エバールＧ１５６Ｂ（商品名）」。エチレンに由来する構成単位の含有量４８モル％。メルトマスフローレート（２１０℃、２１．１８Ｎ）１５ｇ／１０分。
（Ａ−４）東ソー株式会社の「メルセンＨ‐６０５１（商品名）」。エチレンに由来する構成単位の含有量８１モル％。メルトマスフローレート（２１０℃、２１．１８Ｎ）１４ｇ／１０分。 Raw materials used (A) Ethylene / vinyl alcohol copolymer:
(A-1) “Eval E105B (trade name)” by Kuraray Co., Ltd. 44 mol% content of structural units derived from ethylene. Melt mass flow rate (210 ° C., 21.18 N) 13 g / 10 min.
(A-2) “EVAL L171B (trade name)” of Kuraray Co., Ltd. The content of structural units derived from ethylene is 27 mol%. Melt mass flow rate (210 ° C., 21.18 N) 4.0 g / 10 min.
(A-3) “EVAL G156B (trade name)” of Kuraray Co., Ltd. The content of structural units derived from ethylene is 48 mol%. Melt mass flow rate (210 ° C., 21.18 N) 15 g / 10 min.
(A-4) “Mersen H-6051 (trade name)” by Tosoh Corporation. Content of 81 mol% of structural units derived from ethylene. Melt mass flow rate (210 ° C., 21.18 N) 14 g / 10 min.

（Ａ’−１）株式会社プライムポリマーのポリプロピレン「プライムポリプロＦ‐７３０ＮＶ（商品名）」。 (A′-1) Prime Polymer Co., Ltd. “Prime Polypro F-730NV (trade name)”.

（Ｂ）ピレスロイド系化合物：
（Ｂ−１）三井化学アグロ株式会社のピレスロイド系化合物「エトフェンプロックス（商品名）」。２‐（４‐エトキシフェニル）‐２‐メチルプロピル＝３‐フェノキシベンジルエーテル。 (B) Pyrethroid compound:
(B-1) A pyrethroid compound “Etophenprox (trade name)” of Mitsui Chemicals Agro Co., Ltd. 2- (4-Ethoxyphenyl) -2-methylpropyl = 3-phenoxybenzyl ether.

（Ｃ）ポリエチレン：
（Ｃ−１）ダウエラストマー社の「エンゲージ８１００（商品名）」。密度８７０Ｋｇ／ｍ^３、メルトマスフローレート（１９０℃、２１．１８Ｎ）１ｇ／１０分。 (C) Polyethylene:
(C-1) “Engage 8100 (trade name)” of Dow Elastomer. Density 870 Kg / m ³ , melt mass flow rate (190 ° C., 21.18 N) 1 g / 10 min.

例１
（１）熱可塑性樹脂組成物の作成：
上記成分（Ａ−１）１００質量部、及び上記成分（Ｂ−１）２質量部の混合物を日本製鋼株式会社の２８ｍｍ径、Ｌ／Ｄ＝４２の二軸押出機を使用し、スクリュウ回転数２００ｒｐｍ、ダイス出口樹脂温度２２０℃の条件で溶融混練し、ストランドカット法により、熱可塑性樹脂組成物のペレットを得た。
（２）防虫フィルムの作成：
上記で得たペレットを用い、押出機、Ｔダイ、及びバキュームチャンバ―方式の引巻取機を備えたフィルム製膜装置を使用し、Ｔダイ出口樹脂温度２２０℃、鏡面冷却ロールの表面温度４０℃、及び引取速度２０ｍ／分の条件で、厚み１２μｍの防虫フィルムを得た。
（３）壁紙の作成：
リケンテクノス株式会社の厚み１２０μｍ、白色の着色ポリ塩化ビニル系樹脂フィルム「ＦＣ１８１４（商品名）」の片面の上に、塩化ビニル・酢酸ビニル共重合体系樹脂バインダーの印刷インキを用い、乾燥後の層厚みが２μｍとなるように印刷層を設け、該印刷層の上に上記（２）で得た防虫フィルムを重ね、鏡面ロールと表面の平滑な受けロールとで押圧する機構を備えた装置を使用して温度２５℃で押圧し、積層体を得た。次に、予熱ロール及び木目導管・梨地メッキの金属製エンボスロールＢＲ‐１６を備えたエンボス加工装置を使用し、温度１２０℃に設定した予熱ロールと押圧ロールとの間に、上記積層体を、上記積層体の上記（２）で得た防虫フィルム側の面が予熱ロール側となるように通紙し、挟み込んで予熱した後、そのまま連続的に、温度を１５０℃に設定した上記エンボスロールとゴム表面を持つ平滑ロールとの間に、上記積層体を、上記積層体の上記（２）で得た防虫フィルム側の面がエンボスロール側になるように挟み込んでエンボス加工を行い、表面にエンボス模様を有する壁紙を得た。このとき押圧の圧力は１１Ｋｇ／ｃｍであった。なお上記の加工条件では、エンボスがほとんど又は全く形成されていない場合、あるいは壁紙、防虫フィフィルムに割れや穴開きがある場合は、予熱ロールの温度を１００〜１８０℃の範囲で、エンボスロールの温度を１２０〜２００℃の範囲で適宜調節した。
（４）上記試験（イ）〜（ニ）を行った。結果を表１に示す。 Example 1
(1) Preparation of thermoplastic resin composition:
A mixture of 100 parts by mass of the above component (A-1) and 2 parts by mass of the above component (B-1) was used with a 28 mm diameter, L / D = 42 twin screw extruder manufactured by Nippon Steel Co., Ltd. The mixture was melt-kneaded under conditions of 200 rpm and a die outlet resin temperature of 220 ° C., and pellets of a thermoplastic resin composition were obtained by a strand cut method.
(2) Creation of insect-proof film:
Using the pellets obtained above, using a film-forming apparatus equipped with an extruder, a T-die, and a vacuum chamber type winder, a T-die outlet resin temperature of 220 ° C., a mirror surface cooling roll surface temperature of 40 ° C. An insect-proof film having a thickness of 12 μm was obtained under the conditions of ° C. and a take-up speed of 20 m / min.
(3) Creating wallpaper:
Layer thickness after drying using printing ink of vinyl chloride / vinyl acetate copolymer resin binder on one side of a white colored polyvinyl chloride resin film “FC1814 (trade name)” with a thickness of 120 μm from Riken Technos Co., Ltd. Is provided with a printing layer so as to be 2 μm, the insect repellent film obtained in (2) above is superimposed on the printing layer, and an apparatus having a mechanism for pressing with a mirror surface roll and a smooth receiving roll on the surface is used. And pressed at a temperature of 25 ° C. to obtain a laminate. Next, using the preheating roll and the embossing apparatus provided with the metal embossing roll BR-16 made of wood grain conduit and satin plating, the laminate is placed between the preheating roll set at a temperature of 120 ° C. and the pressing roll. The embossing roll with the temperature set at 150 ° C. continuously after passing through the laminate so that the surface on the insect-protective film side obtained in (2) is on the preheating roll side, and sandwiching and preheating. The laminate is sandwiched between a smooth roll having a rubber surface so that the insect-protective film side surface obtained in (2) above is on the embossing roll side, and embossed on the surface. A wallpaper with a pattern was obtained. At this time, the pressing pressure was 11 kg / cm. In the above processing conditions, when little or no embossing is formed, or when there are cracks or perforations in the wallpaper or insect repellent film, the temperature of the preheating roll is set within the range of 100 to 180 ° C. The temperature was appropriately adjusted in the range of 120 to 200 ° C.
(4) The above tests (a) to (d) were performed. The results are shown in Table 1.

例２〜１０：
熱可塑性樹脂組成物の配合を表１に示すように変更したこと以外は、例１と同様に行った。結果を表１に示す。 Examples 2 to 10 :
The same procedure as in Example 1 was performed except that the composition of the thermoplastic resin composition was changed as shown in Table 1. The results are shown in Table 1.

本発明の樹脂組成物からなるフィルムは、防虫機能を有し、ブリード白化が抑制され、エンボス加工適性に優れている。また透明性や耐薬品性が良好であることから、エチレン・ビニルアルコール共重合体フィルムの有する好ましい特性の低下も抑制されていると評価できる。
The film made of the resin composition of the present invention has an insect repellent function, suppresses bleed whitening, and is excellent in embossing suitability. Moreover, since transparency and chemical resistance are favorable, it can be evaluated that the fall of the preferable characteristic which an ethylene-vinyl alcohol copolymer film has is also suppressed.

本発明の壁紙の一例を示す断面の概念図である。It is a conceptual diagram of the section which shows an example of the wallpaper of the present invention.

１：本発明のフィルムの層
２：印刷層
３：着色樹脂シートの層
４：エンボス模様

1: Layer 2 of the present invention 2: Print layer 3: Colored resin sheet layer 4: Embossed pattern

Claims (6)

（Ａ）エチレン・ビニルアルコール共重合体 １００質量部；及び、
（Ｂ）ピレスロイド系化合物 ０．０１〜５質量部；
を含む熱可塑性樹脂組成物。
(A) ethylene / vinyl alcohol copolymer 100 parts by mass; and
(B) 0.01-5 parts by mass of a pyrethroid compound;
A thermoplastic resin composition comprising:
（Ａ）エチレン・ビニルアルコール共重合体 ８０〜９８質量％；と
（Ｃ）ポリエチレン ２０〜２質量％；
からなり、ここで上記成分（Ａ）エチレン・ビニルアルコール共重合体と上記成分（Ｃ）ポリエチレンとの和は１００質量％である、熱可塑性樹脂混合物 １００質量部；及び、
（Ｂ）ピレスロイド系化合物 ０．０１〜５質量部；
を含む熱可塑性樹脂組成物。
(A) ethylene-vinyl alcohol copolymer 80-98% by mass; and (C) polyethylene 20-2% by mass;
Wherein the sum of the component (A) ethylene vinyl alcohol copolymer and the component (C) polyethylene is 100% by weight, 100 parts by weight of a thermoplastic resin mixture; and
(B) 0.01-5 parts by mass of a pyrethroid compound;
A thermoplastic resin composition comprising:
上記成分（Ａ）エチレン・ビニルアルコール共重合体のエチレンに由来する構成単位の含有量が３５〜６０モル％である請求項１又は２に記載の熱可塑性樹脂組成物。
The thermoplastic resin composition according to claim 1 or 2, wherein the content of the structural unit derived from ethylene of the component (A) ethylene-vinyl alcohol copolymer is 35 to 60 mol%.
請求項１〜３の何れか１項に記載の熱可塑性樹脂組成物からなるフィルム。
The film which consists of a thermoplastic resin composition of any one of Claims 1-3.
請求項４に記載のフィルムを含む壁紙。
A wallpaper comprising the film according to claim 4.
請求項４に記載のフィルムを含む化粧シート。 A decorative sheet comprising the film according to claim 4.