JP2019106414A - 軟磁性圧粉磁心の製造方法および軟磁性圧粉磁心 - Google Patents
軟磁性圧粉磁心の製造方法および軟磁性圧粉磁心 Download PDFInfo
- Publication number
- JP2019106414A JP2019106414A JP2017236616A JP2017236616A JP2019106414A JP 2019106414 A JP2019106414 A JP 2019106414A JP 2017236616 A JP2017236616 A JP 2017236616A JP 2017236616 A JP2017236616 A JP 2017236616A JP 2019106414 A JP2019106414 A JP 2019106414A
- Authority
- JP
- Japan
- Prior art keywords
- soft magnetic
- content
- magnetic powder
- magnetic alloy
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
軟磁性合金からなる軟磁性粉末を得る工程および前記軟磁性粉末を成形する工程を有する軟磁性圧粉磁心の製造方法であって、
前記軟磁性粉末を成形する工程における成形温度が400℃以上700℃以下、成形圧力が400MPa以上2000MPa以下であり、
前記軟磁性合金はFeを主成分とし、
前記軟磁性合金の連続した測定範囲における1nm×1nm×1nmの80000個以上のグリッドのFe含有量(原子%)をy軸とし、各グリッドのFe含有量が高い順で求めた累計頻度(%)をx軸とした場合に、累計頻度20〜80%における近似直線の傾き−0.1〜−0.4を有し、
下記式(1)に示す非晶質化率Xが85%以上の非晶質であることを特徴とする。
X=100−(Ic/(Ic+Ia)×100)…(1)
Ic:結晶性散乱積分強度
Ia:非晶性散乱積分強度
前記式(1)に示す非晶質化率Xが95%以上であってもよい。
前記軟磁性合金におけるCの含有量が0.1〜7.0原子%であってもよい。
Fe含有量についての累計頻度95%以上のグリッドにおけるB含有量のバラツキσBが2.8以上であってもよい。
M1がNb,Ti,Zr,Hf,V,Ta,MoおよびPからなる群から選択される1種以上であり、
Fe含有量についての累計頻度95%以上のグリッドにおけるM1含有量のバラツキσM1が2.8以上であってもよい。
M2がNb,Cu,ZrおよびHfからなる群から選択される1種以上であり、
Fe含有量についての累計頻度95%以上のグリッドにおけるM2含有量のバラツキσM2が2.8以上であってもよい。
0.1≦b≦3.0
1.0≦c≦10.0
0.0≦d≦17.5
6.0≦e≦13.0
0.0≦f≦7.0
1.0≦β≦14.1
2.0≦γ≦20.0
0.0≦Ω≦7.0
X=100−(Ic/(Ic+Ia)×100)…(1)
Ic:結晶性散乱積分強度
Ia:非晶性散乱積分強度
表1に示す各試料の組成の母合金が得られるように純金属材料をそれぞれ秤量した。そして、チャンバー内で真空引きした後、高周波加熱にて溶解し母合金を作製した。
得られた薄帯おいて、1辺の長さが40nm×40nm×50nmの直方体を測定範囲とし、連続した測定範囲における1nm×1nm×1nmの80000個のグリッドのFe含有量を3DAPにより測定し、Fe含有量(原子%)をy軸とし、各グリッドのFe含有量が高い順で求めた累計頻度(%)をx軸としたときの、累計頻度20〜80%における近似直線の傾きを算出した。
得られた薄帯に対し、XRDによりX線結晶構造解析を実施し、相の同定を行った。具体的には、結晶化したFe又は化合物のピーク(Ic:結晶性散乱積分強度、Ia:非晶性散乱積分強度)を読み取り、そのピーク強度から結晶化率を割り出し、下記式(1)により非晶質化率Xを算出した。本実施例では、薄帯の、ロール面に接していた面と、接していない面との両方を測定し、その平均値を非晶質化率Xとした。
X=100−(Ic/(Ic+Ia)×100)…(1)
Ic:結晶性散乱積分強度
Ia:非晶性散乱積分強度
実験1の試料No.9の組成を下表2に示す組成に変化させた点以外は同一の条件で試験を行った。結果を下表2に示す。
実験1における軟磁性合金の組成を変化させ、添加剤を変化させ、剥離噴射圧力を0.3MPaとした点以外は同一の条件で試験を行った。リン酸系ガラスは軟化点350℃のものを用いた。ビスマス系ガラスは軟化点480℃のものを用いた。さらに、σBの測定およびσM1またはσM2の測定を行った。結果を下表3および下表4に示す。
得られた薄帯において、1辺の長さが40nm×40nm×50nmの直方体を測定範囲とし、連続した測定範囲における1nm×1nm×1nmの80000個のグリッドのFe含有量について累計頻度(%)を算出し、その累計頻度(%)が95%以上のグリッドにおけるB含有量を測定して、σBを算出した。Fe含有量およびB含有量は3DAPにより測定した。
得られた薄帯において、1辺の長さが40nm×40nm×50nmの直方体を測定範囲とし、連続した測定範囲における1nm×1nm×1nmの80000個のグリッドのFe含有量について累計頻度(%)を算出し、その累計頻度(%)が95%以上のグリッドにおけるM1またはM2の含有量を測定して、σM1またはσM2を算出した。Fe含有量およびM1またはM2の含有量は3DAPにより測定した。
下表5に示す組成の母合金が得られるように純金属材料をそれぞれ秤量した。そして、チャンバー内で真空引きした後、高周波加熱にて溶解し母合金を作製した。
12… 測定範囲
13… グリッド
21… ノズル
22… 溶融金属
23… ロール
24… 薄帯
25… チャンバー
26… 剥離ガス噴射装置
Claims (7)
- 軟磁性合金からなる軟磁性粉末を得る工程および前記軟磁性粉末を成形する工程を有する軟磁性圧粉磁心の製造方法であって、
前記軟磁性粉末を成形する工程における成形温度が400℃以上700℃以下、成形圧力が400MPa以上2000MPa以下であり、
前記軟磁性合金はFeを主成分とし、
前記軟磁性合金の連続した測定範囲における1nm×1nm×1nmの80000個以上のグリッドのFe含有量(原子%)をy軸とし、各グリッドのFe含有量が高い順で求めた累計頻度(%)をx軸とした場合に、累計頻度20〜80%における近似直線の傾き−0.1〜−0.4を有し、
下記式(1)に示す非晶質化率Xが85%以上の非晶質である軟磁性圧粉磁心の製造方法。
X=100−(Ic/(Ic+Ia)×100)…(1)
Ic:結晶性散乱積分強度
Ia:非晶性散乱積分強度 - 前記近似直線の傾きが−0.1〜−0.2を有し、
前記式(1)に示す非晶質化率Xが95%以上である請求項1に記載の軟磁性圧粉磁心の製造方法。 - 前記軟磁性合金がCを有し、
前記軟磁性合金におけるCの含有量が0.1〜7.0原子%である請求項1または2に記載の軟磁性圧粉磁心の製造方法。 - 前記軟磁性合金がBを有し、
Fe含有量についての累計頻度95%以上のグリッドにおけるB含有量のバラツキσBが2.8以上である請求項1〜3のいずれかに記載の軟磁性圧粉磁心の製造方法。 - 前記軟磁性合金がFe−Si−M1−B−Cu−C系の軟磁性合金であり、
M1がNb,Ti,Zr,Hf,V,Ta,MoおよびPからなる群から選択される1種以上であり、
Fe含有量についての累計頻度95%以上のグリッドにおけるM1含有量のバラツキσM1が2.8以上である請求項1〜4のいずれかに記載の軟磁性圧粉磁心の製造方法。 - 前記軟磁性合金がFe−M2−B−C系の軟磁性合金であり、
M2がNb,Cu,ZrおよびHfからなる群から選択される1種以上であり、
Fe含有量についての累計頻度95%以上のグリッドにおけるM2含有量のバラツキσM2が2.8以上である請求項1〜4のいずれかに記載の軟磁性圧粉磁心の製造方法。 - 請求項1〜6のいずれかに記載の製造方法によって得られる軟磁性圧粉磁心であって、相対密度が0.90以上であることを特徴とする軟磁性圧粉磁心。