JP2018203966A - Fluorescent body-containing particle, light-emitting device using the same, and florescent body-containing sheet - Google Patents
Fluorescent body-containing particle, light-emitting device using the same, and florescent body-containing sheet Download PDFInfo
- Publication number
- JP2018203966A JP2018203966A JP2017114475A JP2017114475A JP2018203966A JP 2018203966 A JP2018203966 A JP 2018203966A JP 2017114475 A JP2017114475 A JP 2017114475A JP 2017114475 A JP2017114475 A JP 2017114475A JP 2018203966 A JP2018203966 A JP 2018203966A
- Authority
- JP
- Japan
- Prior art keywords
- phosphor
- resin
- ionic liquid
- semiconductor nanoparticle
- containing particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
以下の開示は、蛍光体含有粒子およびそれを用いた発光装置、蛍光体含有シートに関する。 The following disclosure relates to phosphor-containing particles, a light-emitting device using the same, and a phosphor-containing sheet.
半導体ナノ粒子蛍光体（量子ドットとも呼ばれる）は、量子サイズ効果によりサイズ可変な（ｓｉｚｅ−ｔｕｎｅａｂｌｅ）電子特性から、商業的関心が持たれている。サイズ可変な電子特性は、生体標識、太陽光発電、触媒作用、生体撮像、ＬＥＤ、一般的な空間照明、及び電子発光ディスプレイなどの様々な用途に利用できる。 Semiconductor nanoparticle phosphors (also called quantum dots) are of commercial interest due to their size-tunable electronic properties due to quantum size effects. The variable size electronic properties can be used in a variety of applications such as biomarkers, solar power generation, catalysis, bioimaging, LEDs, general spatial illumination, and electroluminescent displays.
しかしながら、半導体ナノ粒子蛍光体は水分・熱・紫外線に曝露されると発光特性が低下するという弱点を有している。また、半導体ナノ粒子蛍光体をシリコーン樹脂などの封止層に直接組み込むと、凝集が生じ光学特性を低下させる問題もある。 However, semiconductor nanoparticle phosphors have a weak point in that their light emission characteristics deteriorate when exposed to moisture, heat, and ultraviolet rays. Further, when the semiconductor nanoparticle phosphor is directly incorporated into a sealing layer such as a silicone resin, there is a problem that aggregation occurs and optical characteristics are deteriorated.
これらの問題を解決するため、たとえば特表２０１３−５０５３４７号公報（特許文献１）には、各１次粒子が、１次マトリックス材料から構成されており、半導体ナノ粒子の集団を含み、各１次粒子は、表面コーティング材料の層が個別に与えられており、１次粒子がマイクロビーズの形態で与えられており、表面コーティング材料がポリマー材料を含む、コーティングされた複数の１次粒子が開示されている。このようにコーティングされた複数の１次粒子を作製することで、周囲環境および１次粒子作製後の処理工程に対して反応性を小さくすることができる。 In order to solve these problems, for example, Japanese Patent Publication No. 2013-505347 (Patent Document 1) discloses that each primary particle is composed of a primary matrix material, includes a group of semiconductor nanoparticles, and each 1 Secondary particles are provided with a layer of surface coating material individually, primary particles are provided in the form of microbeads, and a plurality of coated primary particles comprising a polymeric material is disclosed. Has been. By producing a plurality of primary particles coated in this way, the reactivity with respect to the surrounding environment and the processing steps after the production of the primary particles can be reduced.
しかしながら特許文献１に開示された従来技術では、１次粒子をコーティングする方法として原子層堆積法（ＡＬＤ：Ａｔｏｍｉｃ Ｌａｙｅｒ Ｄｅｐｏｓｉｔｉｏｎ）が用いられているが、この方法では、１００℃以上４００℃以下というような高い反応温度を必要とする。このため、ビーズ表面保護コーティング時の熱により半導体ナノ粒子蛍光体の発光特性が低下してしまうという問題がある。 However, in the prior art disclosed in Patent Document 1, atomic layer deposition (ALD) is used as a method for coating primary particles. In this method, the temperature is 100 ° C. or more and 400 ° C. or less. High reaction temperature is required. For this reason, there exists a problem that the light emission characteristic of semiconductor nanoparticle fluorescent substance will fall with the heat | fever at the time of bead surface protective coating.
以下の開示は、上記課題を解決するためになされたものであって、その目的とするところは、高い発光効率を有し、かつ、化学安定性が向上された、半導体ナノ粒子蛍光体を用いた新規な蛍光体含有粒子を提供することである。 The following disclosure has been made in order to solve the above-mentioned problems, and the object thereof is to use a semiconductor nanoparticle phosphor having high luminous efficiency and improved chemical stability. And providing a new phosphor-containing particle.
本発明の一態様の蛍光体含有粒子は、半導体ナノ粒子蛍光体が分散された、イオン性液体に由来する構成単位を含む樹脂の粒状物であるコア部と、前記コア部の少なくとも一部を覆う、イオン性液体に由来する構成単位を含む樹脂の層状物であるシェル部とを備えることを特徴とする。 The phosphor-containing particle of one embodiment of the present invention includes a core part that is a resin granular material including a structural unit derived from an ionic liquid in which a semiconductor nanoparticle phosphor is dispersed, and at least a part of the core part. And a shell portion that is a resin layered material including a structural unit derived from an ionic liquid.
本発明の一態様の蛍光体含有粒子において、前記シェル部は半導体ナノ粒子蛍光体を含まないことが好ましい。 In the phosphor-containing particles of one embodiment of the present invention, it is preferable that the shell portion does not contain a semiconductor nanoparticle phosphor.
本発明の一態様の蛍光体含有粒子において、前記シェル部は、前記コア部の全面を覆うことが好ましい。 In the phosphor-containing particles of one embodiment of the present invention, it is preferable that the shell portion covers the entire surface of the core portion.
本発明の一態様の蛍光体含有粒子において、前記コア部における前記樹脂と、前記シェル部における前記樹脂とが同一種類の樹脂であってもよいし、前記コア部における前記樹脂と、前記シェル部における前記樹脂とが互いに異なる種類の樹脂であってもよい。 In the phosphor-containing particles of one embodiment of the present invention, the resin in the core part and the resin in the shell part may be the same type of resin, or the resin in the core part and the shell part. The resin may be a different type of resin.
本発明の一態様の蛍光体含有粒子において、コア部における前記樹脂およびシェル部における前記樹脂のうちの少なくともいずれかが、重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂であることが好ましい。またこの場合、前記コア部における前記樹脂および前記シェル部における前記樹脂が、共に、重合性官能基として（メタ）アクリル酸エステル基を有するイオン性液体に由来する構成単位を含む樹脂であることが好ましい。 In the phosphor-containing particle of one embodiment of the present invention, at least one of the resin in the core portion and the resin in the shell portion is a resin including a structural unit derived from an ionic liquid having a polymerizable functional group. It is preferable. In this case, both the resin in the core part and the resin in the shell part are resins including a structural unit derived from an ionic liquid having a (meth) acrylate group as a polymerizable functional group. preferable.
本発明の一態様の蛍光体含有粒子において、前記シェル部における前記樹脂は、前記コア部における前記樹脂に含まれる架橋剤よりも多い混合比率で架橋剤を含むことが好ましい。この場合、前記シェル部における前記樹脂が含む架橋剤は前記樹脂全体に対し重量比で５０％より多く、前記コア部における前記樹脂が含む架橋剤は前記樹脂全体に対し重量比で５０％以下であることが好ましい。 In the phosphor-containing particles of one embodiment of the present invention, it is preferable that the resin in the shell portion contains a crosslinking agent in a larger mixing ratio than the crosslinking agent contained in the resin in the core portion. In this case, the cross-linking agent contained in the resin in the shell part is more than 50% by weight with respect to the whole resin, and the cross-linking agent contained in the resin in the core part is less than 50% by weight with respect to the whole resin. Preferably there is.
本発明の一態様の蛍光体含有粒子の粒径は１００ｎｍ以上３０μｍ以下であることが好ましい。 The particle size of the phosphor-containing particles of one embodiment of the present invention is preferably 100 nm or more and 30 μm or less.
本発明の一態様の蛍光体含有粒子において、前記シェル部の厚みは０．１μｍ以上５μｍ以下であることが好ましい。 In the phosphor-containing particles of one embodiment of the present invention, the thickness of the shell part is preferably 0.1 μm or more and 5 μm or less.
本発明の一態様はまた、光源と、上述した本発明の一態様の蛍光体含有粒子が透光性を有する媒体中に分散された波長変換部とを備える発光装置についても提供する。 One embodiment of the present invention also provides a light-emitting device including a light source and a wavelength conversion unit in which the phosphor-containing particles of one embodiment of the present invention described above are dispersed in a light-transmitting medium.
本発明の一態様の発光装置は、前記コア部において赤色の蛍光を発する半導体ナノ粒子蛍光体がイオン性液体に由来する構成単位を含む樹脂中に分散された蛍光体含有粒子と、前記コア部において緑色の蛍光を発する半導体ナノ粒子蛍光体がイオン性液体に由来する構成単位を含む樹脂中に分散された蛍光体含有粒子とを含むことが好ましい。 The light-emitting device of one embodiment of the present invention includes a phosphor-containing particle in which a semiconductor nanoparticle phosphor that emits red fluorescence in a core includes a constituent unit derived from an ionic liquid, and the core It is preferable that the semiconductor nanoparticle phosphor emitting green fluorescence contains phosphor-containing particles dispersed in a resin containing a structural unit derived from an ionic liquid.
本発明の一態様はさらに、上述した本発明の一態様の蛍光体含有粒子が、シート状の透光性を有する媒体中に分散された蛍光体含有シートについても提供する。 One embodiment of the present invention further provides a phosphor-containing sheet in which the phosphor-containing particles of one embodiment of the present invention described above are dispersed in a sheet-like medium having translucency.
本発明によれば、半導体ナノ粒子蛍光体が分散された、イオン性液体に由来する構成単位を含む樹脂の粒状物であるコア部と、前記コア部の少なくとも一部を覆う、イオン性液体に由来する構成単位を含む樹脂の層状物であるシェル部とを備える。このような蛍光体含有粒子は、従来のＡＬＲ法のような高い温度での加熱を経ることなく製造することができ、これにより、高い発光効率と、優れた化学安定性とを有し、取扱い性にも優れた蛍光体含有粒子を提供することができる。また、前記コア部は前記シェル部の存在により保護されるため、粒子を作製する際の半導体ナノ粒子蛍光体の凝集を防止でき、高い光学特性を維持することができ、粒子を作製後にも水分と酸素による半導体ナノ粒子蛍光体の劣化を減少させることができるという効果も奏される。また、このようにして得られた蛍光体含有粒子は、現在利用されている蛍光体と同程度の大きさに作製することによって、現在商業利用されている蛍光体と同じような形態で利用することができ、これを利用した発光装置、蛍光体含有シートなどを提供することができる。 According to the present invention, a core part that is a resin granular material including a structural unit derived from an ionic liquid, in which semiconductor nanoparticle phosphors are dispersed, and an ionic liquid that covers at least a part of the core part. And a shell part that is a layered product of resin including the derived structural unit. Such phosphor-containing particles can be manufactured without being heated at a high temperature as in the conventional ALR method, thereby having high luminous efficiency and excellent chemical stability, and handling. It is possible to provide phosphor-containing particles having excellent properties. In addition, since the core part is protected by the presence of the shell part, it is possible to prevent aggregation of the semiconductor nanoparticle phosphor during the production of particles, maintain high optical properties, and maintain moisture after the particles are produced. Further, there is an effect that the deterioration of the semiconductor nanoparticle phosphor due to oxygen can be reduced. In addition, the phosphor-containing particles obtained in this way are used in the same form as phosphors currently used commercially by making them to the same size as phosphors currently used. It is possible to provide a light emitting device, a phosphor-containing sheet, and the like using the same.
本発明の蛍光体含有粒子において、上述のように前記シェル部による保護によって、前記コア部の半導体ナノ粒子蛍光体の劣化を減少させることができるが、前記シェル部にナノ粒子蛍光体を含む粒子（蛍光体含有粒子）とすることも可能である。この場合でも前記コア部の半導体ナノ粒子蛍光体の劣化を減少させることができる。ただし前記シェル部の半導体ナノ粒子蛍光体が劣化すると、励起光を吸収するにも関わらず発光強度が低下するため、蛍光体含有粒子としての発光効率を低下させる原因となりうる。つまり、前記シェル部にナノ粒子蛍光体を含まない粒子（蛍光体含有粒子）とすることで、本発明のさらなる効果を得ることができる。 In the phosphor-containing particles of the present invention, the deterioration of the semiconductor nanoparticle phosphor in the core portion can be reduced by the protection by the shell portion as described above, but the particles containing the nanoparticle phosphor in the shell portion It is also possible to use (phosphor-containing particles). Even in this case, deterioration of the semiconductor nanoparticle phosphor in the core can be reduced. However, when the semiconductor nanoparticle phosphor in the shell portion deteriorates, the emission intensity decreases despite absorbing the excitation light, which may cause a decrease in the luminous efficiency of the phosphor-containing particles. That is, the further effect of this invention can be acquired by setting it as the particle | grains (phosphor containing particle | grains) which do not contain nanoparticle fluorescent substance in the said shell part.
＜蛍光体含有粒子＞
図１は、本発明の一態様の好ましい一例の蛍光体含有粒子（マイクロビーズ）１を模式的に示す図である。本発明の一態様の蛍光体含有粒子１は、半導体ナノ粒子蛍光体３が分散された、イオン性液体に由来する構成単位を含む樹脂４の粒状物であるコア部２と、前記コア部２の少なくとも一部を覆う、イオン性液体に由来する構成単位を含む樹脂の層状物であるシェル部５とを備えることを特徴とする。
<Phosphor-containing particles>
FIG. 1 is a diagram schematically showing a phosphor-containing particle (microbead) 1 as a preferred example of one embodiment of the present invention. The phosphor-containing particle 1 of one embodiment of the present invention includes a
本発明の一態様に用いられる「イオン性液体」とは、常温（たとえば２５℃）でも溶融状態の塩（常温溶融塩）であり、以下の一般式（Ｉ）
Ｘ＋Ｙ− （Ｉ）
で示されるものが好ましい。
The “ionic liquid” used in one embodiment of the present invention is a salt (room temperature molten salt) that is in a molten state even at room temperature (for example, 25 ° C.).
X + Y − (I)
Is preferred.
上記一般式（Ｉ）中、Ｘ＋は、イミダゾリウムイオン、ピリジニウムイオン、ホスホニウムイオン、脂肪族四級アンモニウムイオン、ピロリジニウム、スルホニウムから選択されるカチオンである。これらの中でも、大気中での空気および水分に対する安定性に優れるという理由から、脂肪族四級アンモニウムイオンが特に好ましいカチオンとして挙げられる。 In the general formula (I), X + is a cation selected from an imidazolium ion, a pyridinium ion, a phosphonium ion, an aliphatic quaternary ammonium ion, pyrrolidinium, and sulfonium. Among these, aliphatic quaternary ammonium ions are particularly preferable cations because they are excellent in stability to air and moisture in the atmosphere.
また上記一般式（Ｉ）中、Ｙ−は、テトラフルオロホウ酸イオン、ヘキサフルオロリン酸イオン、ビストリフルオロメチルスルホニルイミド酸イオン、過塩素酸イオン、トリス（トリフルオロメチルスルホニル）炭素酸イオン、トリフルオロメタンスルホン酸イオン、トリフルオロ酢酸イオン、カルボン酸イオン、ハロゲンイオンから選択されるアニオンである。これらの中でも、大気中での空気および水分に対する安定性に優れるという理由から、ビストリフルオロメチルスルホニルイミド酸イオンが特に好ましいアニオンとして挙げられる。 In the general formula (I), Y − represents tetrafluoroborate ion, hexafluorophosphate ion, bistrifluoromethylsulfonylimido ion, perchlorate ion, tris (trifluoromethylsulfonyl) carbonate ion, trifluoro. An anion selected from lomethanesulfonate ion, trifluoroacetate ion, carboxylate ion, and halogen ion. Among these, bistrifluoromethylsulfonylimido ion is mentioned as a particularly preferable anion because it has excellent stability to air and moisture in the atmosphere.
本発明の一態様の蛍光体含有粒子１のコア部２およびシェル部５において用いられるイオン性液体は、少なくともそのいずれかが、重合性官能基を有するものであることが好ましい。このような重合性官能基を有するイオン性液体としては、たとえば、２−（メタクリロイロキシ）−エチルトリメチルアンモニウムビス（トリフルオロメタンスルホニル）イミド（以下、「ＭＯＥ−２００Ｔ」と略記）や、１−（３−アクリロイロキシ−プロピル）−３−メチルイミダゾリウムビス（トリフルオロメタンスルホニル）イミドなどが挙げられる。重合性官能基を有しないイオン性液体としては、たとえば、Ｎ，Ｎ，Ｎ−トリメチル−Ｎ−プロピルアンモニウムビス（トリフルオロメタンスルホニル）イミド、Ｎ，Ｎ−ジメチル−Ｎ−メチル−２−（２−メトキシエチル）アンモニウムビス（トリフルオロメタンスルホニル）イミド（以下、「ＤＥＭＥ−ＴＦＳＩ」と略記）などが挙げられる。重合性官能基を有するイオン性液体を用いることで、半導体ナノ粒子蛍光体の分散液として機能するイオン性液体を、重合性官能基によりそのまま重合させることができる。このように、半導体ナノ粒子蛍光体を分散させた状態で、重合性官能基を有するイオン性液体を重合し、重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂を形成することで、半導体ナノ粒子蛍光体を分散させた樹脂を固体化させる際に起こっていた凝集などを抑制することができる。また、上述のように、半導体ナノ粒子蛍光体を、重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂中に分散させるようにすることで、半導体ナノ粒子蛍光体が静電的に安定化し、半導体ナノ粒子蛍光体を強固に保護することができる。
It is preferable that at least one of the ionic liquids used in the
上述のような重合性官能基を有するイオン性液体は、従来公知の適宜のイオン性液体に、従来公知の適宜の手法で重合性官能基を導入することによって得ることができるが、市販品を用いても勿論よい。 The ionic liquid having a polymerizable functional group as described above can be obtained by introducing a polymerizable functional group into a conventionally known appropriate ionic liquid by a conventionally known appropriate technique. Of course, it may be used.
また、本発明の一態様の蛍光体含有粒子１におけるコア部２を作製するにあたり、半導体ナノ粒子蛍光体を分散させた状態で、重合性官能基を有するイオン性液体を重合させるための温度、時間などの条件は、用いる重合性官能基を有するイオン性液体の種類、量などに応じて好適な条件が適宜選択され、特に制限されるものではない。たとえば、重合性官能基を有するイオン性液体としてＭＯＥ−２００Ｔを用いる場合には、たとえば６０℃以上１００℃以下の温度で１時間以上１０時間以下という条件で好適に重合させることができる。またたとえば重合性官能基を有するイオン性液体として１−（３−アクリロイロキシ−プロピル）−３−メチルイミダゾリウムビス（トリフルオロメタンスルホニル）イミドを用いる場合には、たとえば６０℃以上１５０℃以下の温度で１時間以上１０時間以下という条件で好適に重合させることができる。
Further, in producing the
なお、上記重合に触媒を用いる場合、用いる触媒に特に制限されるものではなく、従来公知のたとえばアゾビスイソブチロニトリル、ジメチル２，２’−アゾビス（２−メチルプロピオナート）などを用いることができる。中でも、重合が速く進むという理由からは、アゾビスイソブチロニトリルを触媒として用いることが好ましい。
When a catalyst is used for the polymerization, the catalyst used is not particularly limited, and conventionally known examples such as azobisisobutyronitrile and
なお、本発明の一態様に用いるイオン性液体は、必ずしも重合性官能基を有していなくともよく、一部、重合性官能基を有さないイオン性液体を含んでいても勿論よい。また、重合性官能基を有さないイオン性液体に、重合を促すジエチレングリコールジメタクリレート、１，１，１−トリメチルオルプロパントリアクリレートなどを添加して重合することで、イオン性液体に由来する構成単位を含む樹脂を有するようにしてもよい。また、本発明の効果を阻害しない範囲で、エポキシ、シリコーンおよび（メタ）アクリレートなどの樹脂成分を含み、イオン性液体に由来する構成単位を含む樹脂を得るようにしてもよい。 Note that the ionic liquid used in one embodiment of the present invention does not necessarily have a polymerizable functional group, and may of course include an ionic liquid that does not have a polymerizable functional group. In addition, a composition derived from an ionic liquid by adding and polymerizing diethylene glycol dimethacrylate, 1,1,1-trimethylolpropane triacrylate, etc. that promote polymerization to an ionic liquid having no polymerizable functional group You may make it have resin containing a unit. Moreover, you may make it obtain resin which contains resin components, such as an epoxy, silicone, and (meth) acrylate, and the structural unit derived from an ionic liquid in the range which does not inhibit the effect of this invention.
本発明の一態様の蛍光体含有粒子１における半導体ナノ粒子蛍光体３は、可視光の散乱がない単一の蛍光体粒子であり、従来公知の適宜の半導体ナノ粒子蛍光体を特に制限なく用いることができる。半導体ナノ粒子蛍光体を用いることで、粒径制御と組成制御による発光波長の制御を精密に行なうことができるという利点がある。 The semiconductor nanoparticle phosphor 3 in the phosphor-containing particle 1 of one embodiment of the present invention is a single phosphor particle that does not scatter visible light, and a conventionally known appropriate semiconductor nanoparticle phosphor is used without particular limitation. be able to. By using the semiconductor nanoparticle phosphor, there is an advantage that the emission wavelength can be precisely controlled by controlling the particle diameter and composition.
半導体ナノ粒子蛍光体の原料としては、特に制限されるものではなく、半導体ナノ粒子蛍光体として従来より用いられるＣｄＳ、ＣｄＳｅ、ＣｄＴｅ、ＺｎＳ、ＺｎＳｅ、ＺｎＴｅ、ＩｎＮ、ＩｎＰ、ＩｎＡｓ、ＩｎＳｂ、ＡｌＰ、ＡｌＳ、ＡｌＡｓ、ＡｌＳｂ、ＧａＮ、ＧａＰ、ＧａＡｓ、ＧａＳｂ、ＰｂＳ、ＰｂＳｅ、Ｓｉ、Ｇｅ、ＭｇＳ、ＭｇＳｅ、ＭｇＴｅから選ばれる少なくともいずれかであってよい。さらに、半導体ナノ粒子蛍光体は、当業者に知られている二成分コア型、三成分コア型、四成分コア型、コアシェル型またはコアマルチシェル型、ドープされた半導体ナノ粒子蛍光体または傾斜した半導体ナノ粒子蛍光体であってよい。図１には、１種類の半導体ナノ粒子蛍光体３を、複数、イオン性液体に由来する構成単位を含む樹脂４中に分散させた場合を示している。 The raw material of the semiconductor nanoparticle phosphor is not particularly limited, and CdS, CdSe, CdTe, ZnS, ZnSe, ZnTe, InN, InP, InAs, InSb, AlP, conventionally used as the semiconductor nanoparticle phosphor. It may be at least one selected from AlS, AlAs, AlSb, GaN, GaP, GaAs, GaSb, PbS, PbSe, Si, Ge, MgS, MgSe, and MgTe. In addition, semiconductor nanoparticle phosphors are known to those skilled in the art two-component core, three-component core, four-component core, core-shell or core multi-shell, doped semiconductor nanoparticle phosphor or tilted It may be a semiconductor nanoparticle phosphor. FIG. 1 shows a case where one kind of semiconductor nanoparticle phosphor 3 is dispersed in a resin 4 containing a plurality of structural units derived from an ionic liquid.
半導体ナノ粒子蛍光体は、その形状については特に制限されないが、球状、ロッド状、ワイヤ状など従来公知の適宜の形状の半導体ナノ粒子蛍光体を特に制限なく用いることができる。特に、形状制御による発光特性の制御の容易さという観点からは、球状の半導体ナノ粒子蛍光体を用いることが好ましい。 The shape of the semiconductor nanoparticle phosphor is not particularly limited, but a semiconductor nanoparticle phosphor having a conventionally known appropriate shape such as a spherical shape, a rod shape, or a wire shape can be used without any particular limitation. In particular, from the viewpoint of easy control of light emission characteristics by shape control, it is preferable to use a spherical semiconductor nanoparticle phosphor.
半導体ナノ粒子蛍光体の粒径は、原料および所望の発光波長に応じて適宜選択することができ、特に制限されないが、１ｎｍ以上２０ｎｍ以下の範囲内であることが好ましく、２ｎｍ以上５ｎｍ以下の範囲内であることがより好ましい。半導体ナノ粒子蛍光体の粒径が１ｎｍ未満である場合には、体積に対する表面積の割合が増えることにより、表面欠陥が支配的となり効果が低下する傾向にあるためであり、また、半導体ナノ粒子蛍光体の粒径が２０ｎｍを超える場合には、分散状態が低下し、凝集・沈降が生じる傾向にあるためである。ここで、半導体ナノ粒子蛍光体の形状が球状である場合には、粒径は、たとえば粒度分布測定装置により測定された平均粒径もしくは電子顕微鏡により観察された粒子の大きさを指す。また半導体ナノ粒子蛍光体の形状がロッド状である場合には、粒径は、たとえば電子顕微鏡により測定された短軸および長軸の大きさを指す。さらに、半導体ナノ粒子蛍光体の形状がワイヤ状である場合には、粒径は、たとえば電子顕微鏡により測定された短軸および長軸の大きさを指す。 The particle size of the semiconductor nanoparticle phosphor can be appropriately selected according to the raw material and the desired emission wavelength, and is not particularly limited, but is preferably in the range of 1 nm to 20 nm, and preferably in the range of 2 nm to 5 nm. More preferably, it is within. This is because when the particle size of the semiconductor nanoparticle phosphor is less than 1 nm, the ratio of the surface area to the volume increases, so that surface defects tend to be dominant and the effect tends to decrease. This is because when the particle size of the body exceeds 20 nm, the dispersed state tends to decrease and aggregation / sedimentation tends to occur. Here, when the shape of the semiconductor nanoparticle phosphor is spherical, the particle size refers to, for example, an average particle size measured by a particle size distribution measuring device or a particle size observed by an electron microscope. Moreover, when the shape of the semiconductor nanoparticle phosphor is rod-shaped, the particle size refers to the size of the short axis and the long axis measured by, for example, an electron microscope. Furthermore, when the shape of the semiconductor nanoparticle phosphor is a wire shape, the particle size refers to the size of the short axis and the long axis measured by, for example, an electron microscope.
半導体ナノ粒子蛍光体の含有量（２種以上の半導体ナノ粒子蛍光体を用いる場合には総量）は、特に制限されないが、コア部２におけるイオン性液体１００重量に対し０．００１重量部以上５０重量部以下の範囲内であることが好ましく、０．０１重量部以上２０重量部以下の範囲内であることがより好ましい。半導体ナノ粒子蛍光体の含有量が、コア部２におけるイオン性液体１００重量部に対し０．００１重量部未満である場合には、半導体ナノ粒子蛍光体からの発光が弱すぎる傾向にあるためであり、また、半導体ナノ粒子蛍光体の含有量が、コア部２におけるイオン性液体１００重量部に対し５０重量部を超える場合には、イオン性液体中で均一に分散することが困難となる傾向にあるためである。
The content of the semiconductor nanoparticle phosphor (total amount when two or more semiconductor nanoparticle phosphors are used) is not particularly limited, but is 0.001 part by weight or more and 50 parts by weight or more with respect to 100 parts by weight of the ionic liquid in the
イオン性液体に由来する構成単位を含む樹脂中に半導体ナノ粒子蛍光体を分散させたもの（ポリマーマトリックス）を粒子状とする方法は特に制限されないが、たとえば、ポリマーマトリックスを物理的に粉砕し、所望のサイズにすることで、好適に製造することができる。 Although there is no particular limitation on the method of making the semiconductor nanoparticle phosphor dispersed in a resin containing a structural unit derived from an ionic liquid (polymer matrix), for example, the polymer matrix is physically pulverized, It can manufacture suitably by making it into a desired size.
本発明の一態様の蛍光体含有粒子１は、コア部２において、半導体ナノ粒子蛍光体の表面にイオン性液体を構成するイオンが配位することで、ナノ粒子を安定化し、これにより高い発光効率が付与される。また、半導体ナノ粒子蛍光体が、酸素、水分の透過率が低いイオン性液体に由来する構成単位を含む樹脂中に分散されていることで、粒子を作製する際の半導体ナノ粒子蛍光体の凝集を防止でき、高い光学特性を維持することができ、粒子を作製後にも水分と酸素による半導体ナノ粒子蛍光体の劣化を減少させることができる。これにより、半導体ナノ粒子蛍光体を励起発光させる際に光酸化が起きにくく、そのため優れた化学的安定性を有する。
The phosphor-containing particle 1 of one embodiment of the present invention stabilizes the nanoparticle by coordinating ions constituting the ionic liquid on the surface of the semiconductor nanoparticle phosphor in the
本発明の一態様における樹脂４の粒状物（コア部２）の形状は、球状物（真球状物、扁球状物、長球状物）、六面体状物、四面体状物など特に制限されない。また、樹脂４の粒状物（コア部２）の粒径も特に制限されるものではないが、０．０１μｍ以上１００μｍ以下の範囲内であることが好ましい。また、白色ＬＥＤなどのＬＥＤデバイスで用いる従来蛍光体と同様の大きさにすることで、従来蛍光体と同様の生産プロセスでＬＥＤデバイスなどに搭載することができるという利点があることから、樹脂４の粒状物は、粒径０．１μｍ以上３０μｍ以下の真球状であることが特に好ましい。また、樹脂４の粒状物が真球状であることで、コア部の形成後に形成するシェル部を形成しやすく、また、透光性を有する媒体中に分散する際に分散しやすいいう利点もある。なお、樹脂４の粒状物の粒径は、光学顕微鏡や走査型顕微鏡（ＳＥＭ）により観察された粒状物の大きさ（長軸および短軸を有する場合には長軸の大きさ）、または、粒度分布測定装置により測定された値を指す。 The shape of the granular material (core portion 2) of the resin 4 in one embodiment of the present invention is not particularly limited, such as a spherical material (true spherical material, oblate spherical material, long spherical material), hexahedral material, tetrahedral material, and the like. Further, the particle size of the granular material (core part 2) of the resin 4 is not particularly limited, but is preferably in the range of 0.01 μm or more and 100 μm or less. Further, since the size of the conventional phosphor used in the LED device such as a white LED is the same as that of the conventional phosphor, there is an advantage that it can be mounted on the LED device or the like in the same production process. The granular material is particularly preferably a true sphere having a particle size of 0.1 μm or more and 30 μm or less. Moreover, since the granular material of the resin 4 is a spherical shape, it is easy to form a shell portion formed after the core portion is formed, and there is an advantage that it is easily dispersed when dispersed in a light-transmitting medium. . In addition, the particle size of the granular material of the resin 4 is the size of the granular material observed by an optical microscope or a scanning microscope (SEM) (the size of the long axis when having a major axis and a minor axis), or The value measured by the particle size distribution measuring device.
本発明の一態様の蛍光体含有粒子１は、上述のような樹脂４の粒状物（コア部２）の少なくとも一部を覆う、イオン性液体に由来する構成単位を含む樹脂の層状物であるシェル部５をさらに備える。本発明の一態様の蛍光体含有粒子１において、シェル部５は、従来の原子層堆積法によるコーティングのような１００℃以上４００℃以下もの高い反応温度への加熱処理を行うことなく樹脂の粒状物（コア部２）をコーティングすることが可能であり、コーティングの際の半導体ナノ粒子蛍光体の特性劣化を防ぎ、高い発光効率を有する蛍光体含有粒子を提供することができるという利点がある。また、シェル部５で樹脂４の粒状物（コア部２）の少なくとも一部を覆うことで、酸素・水分に起因する半導体ナノ粒子蛍光体の劣化を抑制することができ、化学安定性が向上された蛍光体含有粒子を得ることができる。より向上された化学安定性が得られる観点からは、シェル部５は、樹脂４の粒状物（コア部２）の表面の１０％以上を覆うように形成されていることが好ましく、５０％以上を覆うように形成されていることがより好ましく、樹脂の粒状物（コア部２）の全面を覆うように形成されていることが特に好ましい。 The phosphor-containing particle 1 of one embodiment of the present invention is a resinous layered product including a structural unit derived from an ionic liquid that covers at least a part of the granular material (core portion 2) of the resin 4 as described above. A shell portion 5 is further provided. In the phosphor-containing particle 1 of one embodiment of the present invention, the shell portion 5 is a resin granule without performing a heat treatment to a reaction temperature as high as 100 ° C. or higher and 400 ° C. or lower as in the coating by the conventional atomic layer deposition method. It is possible to coat an object (core part 2), and there is an advantage that it is possible to provide phosphor-containing particles having high luminous efficiency by preventing deterioration of characteristics of the semiconductor nanoparticle phosphor during coating. Moreover, by covering at least a part of the granular material (core part 2) of the resin 4 with the shell part 5, deterioration of the semiconductor nanoparticle phosphor caused by oxygen and moisture can be suppressed, and chemical stability is improved. The obtained phosphor-containing particles can be obtained. From the viewpoint of obtaining improved chemical stability, the shell portion 5 is preferably formed so as to cover 10% or more of the surface of the granular material (core portion 2) of the resin 4 and is 50% or more. Is more preferably formed so as to cover the entire surface of the resin granular material (core part 2).
シェル部の厚みも特に制限されるものではないが、０．０１μｍ以上１０μｍ以下の範囲内であることが好ましい。また、コア部の酸素・水分に起因する半導体ナノ粒子蛍光体の劣化を抑制することができ、化学安定性が向上された蛍光体含有粒子を得ることができるという利点があることから、シェル部の厚みは、０．１μｍ以上５μｍ以下で、コア部表面の全面に均一な膜であることが特に好ましい。 The thickness of the shell part is not particularly limited, but is preferably in the range of 0.01 μm or more and 10 μm or less. Moreover, since there is an advantage that phosphor-containing particles with improved chemical stability can be obtained because deterioration of the semiconductor nanoparticle phosphor due to oxygen and moisture in the core portion can be suppressed, the shell portion The thickness of is preferably 0.1 μm or more and 5 μm or less, and is particularly preferably a uniform film over the entire surface of the core part.
なお、本発明の一態様の蛍光体含有粒子１において、コア部２の少なくとも一部を覆うようにシェル部５が形成されていることは、たとえば、任意の光源から蛍光体含有粒子１に光を入射させることで、半導体ナノ粒子蛍光体３が分散されたコア部２が蛍光を発し、半導体ナノ粒子蛍光体を含まないシェル部５については、蛍光体含有粒子の断面を蛍光顕微鏡やＳＥＭ−ＥＤＸなどで観察することで確認することができる。たとえば蛍光顕微鏡で観察した場合、シェル部５からは蛍光を検出できないし、ＳＥＭ−ＥＤＸで観察した場合、シェル部５には蛍光体を形成する元素は検出されない。場合によってはこれらを組み合わせて確認することができる。
In addition, in the phosphor-containing particle 1 of one embodiment of the present invention, the shell portion 5 is formed so as to cover at least a part of the
本発明の一態様の蛍光体含有粒子において、前記シェル部にナノ粒子蛍光体を含む粒子（蛍光体含有粒子）とすることも可能である。この場合でも前記コア部の半導体ナノ粒子蛍光体の劣化を減少させることができるという効果が奏される。ただし、前記シェル部の半導体ナノ粒子蛍光体が劣化すると、励起光を吸収するにも関わらず発光強度が低下するため、蛍光体含有粒子としての発光効率を低下させる原因となりうる。このような観点からは、本発明の一態様の蛍光体含有粒子においては、シェル部が半導体ナノ粒子蛍光体を含まないことが好ましい。 In the phosphor-containing particles of one embodiment of the present invention, the shell portion may include particles containing a nanoparticle phosphor (phosphor-containing particles). Even in this case, there is an effect that the deterioration of the semiconductor nanoparticle phosphor in the core portion can be reduced. However, when the semiconductor nanoparticle phosphor in the shell portion deteriorates, the emission intensity decreases despite absorbing the excitation light, which may cause a decrease in the luminous efficiency of the phosphor-containing particles. From such a viewpoint, in the phosphor-containing particles of one embodiment of the present invention, it is preferable that the shell portion does not contain the semiconductor nanoparticle phosphor.
シェル部５に用いられるイオン性液体に由来する構成単位を含む樹脂は、コア部２に用いられるイオン性液体に由来する構成単位を含む樹脂と同一種類であってもよいし、互いに異なる種類であってもよい。
The resin including the structural unit derived from the ionic liquid used for the shell portion 5 may be the same type as the resin including the structural unit derived from the ionic liquid used for the
シェル部５に用いられるイオン性液体に由来する構成単位を含む樹脂が、コア部２に用いられるイオン性液体に由来する構成単位を含む樹脂と同一種類である場合、たとえば共に、重合性官能基を有するイオン性液体としてＭＯＥ−２００Ｔもしくは１−（３−アクリロイロキシ−プロピル）−３−メチルイミダゾリウムビス（トリフルオロメタンスルホニル）イミドを用いる場合には、同一の材料であるためコア部に対してシェル部の形成が容易で、均一な層状物を形成することができるというような効果が奏される。
When the resin containing the structural unit derived from the ionic liquid used for the shell part 5 is the same type as the resin containing the structural unit derived from the ionic liquid used for the
またシェル部５に用いられる重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂が、コア部２に用いられる重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂と互いに異なる種類である場合、たとえば、耐久性・耐候性の高い方の樹脂をシェル部の形成に用いることで、コア部を形成する樹脂において相対的に耐久性・耐候性が低くとも、高い耐久性・耐候性を有する蛍光体含有粒子を得ることができる。
Further, a resin containing a structural unit derived from an ionic liquid having a polymerizable functional group used for the shell portion 5 is a resin containing a structural unit derived from an ionic liquid having a polymerizable functional group used for the
また、本発明の一態様の蛍光体含有粒子１において、コア部における前記樹脂およびシェル部における前記樹脂のうちの少なくともいずれかが、重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂であることが好ましい。この場合、シェル部５に用いられる重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂が、コア部２に用いられる重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂と同一種類である場合、互いに異なる種類である場合のいずれにおいても、重合性官能基が共に（メタ）アクリル酸エステル基であることが、好ましい。（メタ）アクリル酸エステル基を有するイオン性液体の好適な例としては、上述した２−（メタクリロイロキシ）−エチルトリメチルアンモニウムビス（トリフルオロメタンスルホニル）イミド、１−（３−アクリロイルオキシ−プロピル）−３−メチルイミダゾリウムビス（トリフルオロメタンスルホニル）イミドがある。
Moreover, in the phosphor-containing particle 1 of one embodiment of the present invention, at least one of the resin in the core portion and the resin in the shell portion includes a structural unit derived from an ionic liquid having a polymerizable functional group. A resin is preferred. In this case, the resin including the structural unit derived from the ionic liquid having the polymerizable functional group used for the shell portion 5 includes the structural unit derived from the ionic liquid having the polymerizable functional group used for the
本発明の一態様の蛍光体含有粒子１において、コア部２およびシェル部５に、重合性官能基を有するイオン性液体を用いることで、半導体ナノ粒子蛍光体の分散液として機能するイオン性液体を、重合性官能基によりそのまま重合させることができ、半導体ナノ粒子蛍光体を分散させた樹脂を固体化させる際に起こっていた凝集などを抑制することができる。中でも、コア部２およびシェル部５において、共に重合性官能基として（メタ）アクリル酸エステル基を用いることで、加熱や触媒反応によって重合することができるようになり、液体の状態からそのまま分散状態を維持して固体化することができる。これにより、半導体ナノ粒子蛍光体が静電的に安定化し、強固に保護することができ、空気、水分から半導体ナノ粒子蛍光体の表面を保護することができ、発光効率の高い蛍光体含有粒子を提供することができる。
In the phosphor-containing particle 1 of one embodiment of the present invention, an ionic liquid that functions as a dispersion of a semiconductor nanoparticle phosphor by using an ionic liquid having a polymerizable functional group for the
また、本発明の一態様の蛍光体含有粒子１において、コア部２およびシェル部５に用いられる重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂は、架橋剤が配合されていてもよい。本発明の一態様の蛍光体含有粒子１において、コア部２およびシェル部５に用いられる重合性官能基を有するイオン性液体に由来する構成単位を含む樹脂に架橋剤が配合されていることで、樹脂は架橋構造をとり、より強固な樹脂となる。架橋剤としては、従来公知の適宜の架橋剤を特に制限なく用いることができ、たとえば、ジエチレングリコールジメタクリレート、１，１，１−トリメチルオルプロパントリアクリレートなどが例示される。
In the phosphor-containing particle 1 of one embodiment of the present invention, the resin containing a structural unit derived from an ionic liquid having a polymerizable functional group used for the
本発明の一態様の蛍光体含有粒子１は、前記シェル部における前記樹脂は、前記コア部における前記樹脂に含まれる架橋剤よりも多い混合比率で架橋剤を含むことが好ましい。半導体ナノ粒子蛍光体３を含むコア部２においては、イオン性液体により半導体ナノ粒子蛍光体３が静電的に安定化し、強固に保護することができるため、コア部２においては半導体ナノ粒子蛍光体３を安定化するイオン性液体に由来する構成単位を含む樹脂の混合比率を高くしつつ、シェル部５においては、強度を維持する架橋剤の混合比率を高くすることで、発光効率が高く、空気、水分から保護された蛍光体含有粒子を簡便に得ることができる。具体的には、前記シェル部における前記樹脂が含む架橋剤は前記樹脂全体に対し重量比で５０％より多く（より好ましくは５０％より多く、７５％以下）、前記コア部における前記樹脂が含む架橋剤は前記樹脂全体に対し重量比で５０％以下（より好ましくは１０％以上５０％以下）であることが好適である。
In the phosphor-containing particle 1 of one embodiment of the present invention, it is preferable that the resin in the shell portion contains a crosslinking agent in a larger mixing ratio than the crosslinking agent contained in the resin in the core portion. In the
本発明の一態様の蛍光体含有粒子１は、その粒径については特に制限されるものではないが、白色ＬＥＤなどのＬＥＤデバイスで用いる従来蛍光体と同様の大きさにすれば従来蛍光体と同様の生産プロセスでＬＥＤデバイスなどに搭載することができるという利点があることから、１００ｎｍ以上３０μｍ以下の範囲内であることが好ましく、１μｍ以上２０μｍ以下の範囲内であることがより好ましい。蛍光体含有粒子１の粒径が１００ｎｍ未満である場合には、粒径が小さいことにより凝集などが起こり透光性を有する媒体中に分散させることが困難になるという傾向にあり、また、蛍光体含有粒子１の粒径が３０μｍを超える場合には、従来蛍光体と同様のプロセスで透光性を有する媒体中に分散させることが困難になるという傾向にあるためである。なお、蛍光体含有粒子１の粒径は、光学顕微鏡や走査型顕微鏡（ＳＥＭ）により観察された粒状物の大きさ（長軸および短軸を有する場合には長軸の大きさ）、または、粒度分布測定装置により測定された値を指す。 The phosphor-containing particle 1 of one embodiment of the present invention is not particularly limited in particle size, but if the particle size is the same as that of a conventional phosphor used in an LED device such as a white LED, Since it can be mounted on an LED device or the like in the same production process, it is preferably in the range of 100 nm to 30 μm, and more preferably in the range of 1 μm to 20 μm. When the particle diameter of the phosphor-containing particles 1 is less than 100 nm, aggregation is caused by the small particle diameter, and it tends to be difficult to disperse in a translucent medium. This is because when the particle size of the body-containing particles 1 exceeds 30 μm, it tends to be difficult to disperse them in a light-transmitting medium by the same process as that of the conventional phosphor. In addition, the particle size of the phosphor-containing particles 1 is the size of the granular material observed by an optical microscope or a scanning microscope (SEM) (the size of the major axis when having a major axis and a minor axis), or The value measured by the particle size distribution measuring device.
（蛍光体含有粒子の製造方法）
上述した本発明の一態様の蛍光体含有粒子は、たとえば、半導体ナノ粒子蛍光体が分散された、イオン性液体（好ましくは重合性官能基を有するイオン性液体）に由来する構成単位を含む樹脂の粒状物と、イオン性液体（好ましくは重合性官能基を有するイオン性液体。半導体ナノ粒子蛍光体を含有しないことが好ましい）とを混合し、分散重合させることで、半導体ナノ粒子蛍光体３が分散された、イオン性液体に由来する構成単位を含む樹脂４の粒状物であるコア部２と、前記コア部２の少なくとも一部を覆う、イオン性液体に由来する構成単位を含む樹脂の層状物であるシェル部５とを備え、前記シェル部５は半導体ナノ粒子蛍光体を含まない蛍光体含有粒子を好適に製造することができる。
(Method for producing phosphor-containing particles)
The phosphor-containing particles of one embodiment of the present invention described above include, for example, a resin including a structural unit derived from an ionic liquid (preferably an ionic liquid having a polymerizable functional group) in which a semiconductor nanoparticle phosphor is dispersed. Are mixed with an ionic liquid (preferably an ionic liquid having a polymerizable functional group, preferably not containing a semiconductor nanoparticle phosphor) and subjected to dispersion polymerization, thereby producing a semiconductor nanoparticle phosphor 3. Of the resin containing the
シェル部５を構成する樹脂を形成するための分散重合は、たとえばシェル部５の形成に用いる重合性官能基を有するイオン性液体がＭＯＥ−２００Ｔである場合には、たとえば６０℃以上１００℃以下で１時間以上１０時間以下の条件で行うことができ、また、シェル部５の形成に用いる重合性官能基を有するイオン性液体が１−（３−アクリロイロキシ−プロピル）−３−メチルイミダゾリウムビス（トリフルオロメタンスルホニル）イミドである場合には、たとえば６０℃以上１００℃以下で１時間以上１０時間以下という条件で行うことができる。このように、従来の原子堆積法によるコーティングとは異なり、半導体ナノ粒子蛍光体が熱により特性劣化してしまうことなく、樹脂の粒状物（コア部）の表面に、シェル部５が形成された蛍光体含有粒子を好適に製造することができる。 For example, when the ionic liquid having a polymerizable functional group used for forming the shell portion 5 is MOE-200T, the dispersion polymerization for forming the resin constituting the shell portion 5 is, for example, 60 ° C. or higher and 100 ° C. or lower. The ionic liquid having a polymerizable functional group used for forming the shell portion 5 is 1- (3-acryloyloxy-propyl) -3-methylimidazolium bis. In the case of (trifluoromethanesulfonyl) imide, it can be performed, for example, at 60 ° C. or higher and 100 ° C. or lower for 1 hour or longer and 10 hours or shorter. Thus, unlike the coating by the conventional atomic deposition method, the shell part 5 was formed in the surface of the granular material (core part) of resin, without the characteristic deterioration of the semiconductor nanoparticle fluorescent substance by heat. Phosphor-containing particles can be suitably produced.
＜発光装置＞
図１には、本発明の一態様の蛍光体含有粒子１を用いた好ましい一例の発光装置１１を模式的に示す図である。本発明の一態様は、図１に示すように、光源１２と、上述した本発明の一態様の蛍光体含有粒子１が透光性を有する媒体１３中に分散された波長変換部とを備える発光装置（ＬＥＤパッケージ）１１についても提供する。上述のように、本発明の一態様の蛍光体含有粒子は取扱い性（ハンドリング性）がよく、現在利用されている蛍光体と同程度の大きさに作製することによって、現在商業利用されている蛍光体と同じような形態で、現行のプロセスを変更することなく利用することができる。図１に示す発光装置１１において、蛍光体含有粒子１以外の光源１２、透光性を有する媒体１３、リード線１４、枠体１５などは、従来公知の適宜のものを特に制限なく用いることができる。
<Light emitting device>
FIG. 1 is a diagram schematically showing a preferred example of a
本発明の一態様の発光装置１１において、光源１２としては、特に制限されず、発光ダイオード（ＬＥＤ）、レーザダイオード（ＬＤ）などを用いることができる。
In the light-emitting
本発明の一態様の発光装置１１において、光源１２および蛍光体含有粒子１を封入するための透光性を有する媒体１３としては、特に制限されず、エポキシ、シリコーンおよび（メタ）アクリレート、シリカガラス、シリカゲル、シロキサン、ゾルゲル、ヒドロゲル、アガロース、セルロース、ポリエーテル、ポリエチレン、ポリビニル、ポリジアセチレン、ポリフェニレンビニレン、ポリスチレン、ポリピロール、ポリイミド、ポリイミダゾール、ポリスルホン、ポリチオフェン、ポリホスフェート、ポリ（メタ）アクリレート、ポリアクリルアミド、ポリペプチド、ポリサッカライドなどが挙げられる。これらを複数組み合わせて透光性を有する媒体として用いてもよい。
In the light-emitting
図２は、本発明の好ましい他の例の発光装置２１を模式的に示す図である。なお、図２において、図１に示した例の発光装置１１と同様の構成を有する部分については同一の参照符を付して説明を省略する。図２に示す例の発光装置２１は、コア部において赤色の蛍光を発する半導体ナノ粒子蛍光体がイオン性液体に由来する構成単位を含む樹脂中に分散された蛍光体含有粒子２２と、コア部において緑色の蛍光を発する半導体ナノ粒子蛍光体がイオン性液体に由来する構成単位を含む樹脂中に分散された蛍光体含有粒子２３とを含む点で、図１に示した例の発光装置１１と異なる。
FIG. 2 is a diagram schematically showing a
上述したように、本発明の一態様の蛍光体含有粒子は、取扱い性（ハンドリング性）がよく、現在利用されている蛍光体と同程度の大きさに作製することによって、現在商業利用されている蛍光体と同じような形態で、現行のプロセスを変更することなく利用することができる。図２に示す例の発光装置２１によれば、従来蛍光体と同様のプロセスで発光装置を製造し、さらに、異なる波長を有する半導体ナノ粒子蛍光体を含む蛍光体含有粒子を用いることで所望の発光色を示す発光装置を製造することができる。なお、図２に示す例の発光装置２１のように、コア部において赤色の蛍光を発する半導体ナノ粒子蛍光体がイオン性液体に由来する構成単位を含む樹脂中に分散された蛍光体含有粒子２２と、コア部において緑色の蛍光を発する半導体ナノ粒子蛍光体がイオン性液体に由来する構成単位を含む樹脂中に分散された蛍光体含有粒子２３とを組み合わせて用いる場合には、色再現性の高い白色発光を呈する発光装置を得ることができることから、青色発光する発光ダイオード（ＬＥＤ）、青色発光するレーザダイオード（ＬＤ）などを好適に用いることができる。
As described above, the phosphor-containing particles of one embodiment of the present invention have good handleability (handling properties), and are currently used commercially by making them to the same size as phosphors currently used. It can be used in the same form as existing phosphors without changing the current process. According to the
なお、図２に示した発光装置２１において、コア部において赤色の蛍光を発する半導体ナノ粒子蛍光体がイオン性液体に由来する構成単位を含む樹脂中に分散された蛍光体含有粒子２２と、コア部において緑色の蛍光を発する半導体ナノ粒子蛍光体がイオン性液体に由来する構成単位を含む樹脂中に分散された蛍光体含有粒子２３との混合比率は特に制限されないが、重量比で、蛍光体含有粒子２２を１００とした場合に蛍光体含有粒子２３が１０以上１０００以下の範囲内であることが好ましく、２０以上５００以下の範囲内であることがより好ましい。蛍光体含有粒子２２を１００とした場合に蛍光体含有粒子２３が１０未満である場合には、赤色と緑色の発光強度の差により白色から大きくずれ、赤色に偏った発光色になる傾向にあるためであり、また、蛍光体含有粒子２２を１００とした場合に蛍光体含有粒子２３が１０００を超える場合には、赤色と緑色の発光強度の差により白色から大きくずれ、緑色に偏った発光色になるという傾向にあるためである。
In the
なお、本発明の一態様の発光装置は図１、図２に示した例に制限されるものでは勿論なく、たとえば、３種類以上の半導体ナノ粒子蛍光体を用いてもよい。 Note that the light-emitting device of one embodiment of the present invention is not limited to the example illustrated in FIGS. 1 and 2, and for example, three or more kinds of semiconductor nanoparticle phosphors may be used.
＜蛍光体含有シート＞
図３は、本発明の好ましい例の蛍光体含有シート３１を模式的に示す図である。本発明の一態様は、図３に示すように、本発明の一態様の蛍光体含有粒子１が、シート状の透光性を有する媒体３２中に分散された蛍光体含有シート３１についても提供する。上述したように、本発明の一態様の蛍光体含有粒子は、取扱い性（ハンドリング性）がよく、現在利用されている蛍光体と同程度の大きさに作製することによって、現在商業利用されている蛍光体と同じような形態で、現行のプロセスを変更することなく利用することができる。したがって、図３に示す蛍光体含有シート３１のように、従来の蛍光体の場合と同様の製造プロセスで蛍光体含有シートを製造することができる。このような本発明の一態様の蛍光体含有シートは、従来と同様に、液晶バックライト、白色ＬＥＤデバイスなどの用途に好適に用いることができる。
<Phosphor-containing sheet>
FIG. 3 is a view schematically showing a phosphor-containing
さらに、本発明の一態様の蛍光体含有粒子を用いた蛍光体含有シートによれば、以下の（１）、（２）の理由により、蛍光体含有粒子を分散する媒体の材料の制約が緩和され、媒体の材料の選択の自由度が向上するという利点がある。 Furthermore, according to the phosphor-containing sheet using the phosphor-containing particles of one embodiment of the present invention, the restrictions on the material of the medium in which the phosphor-containing particles are dispersed are relaxed for the following reasons (1) and (2). In addition, there is an advantage that the degree of freedom in selecting the material of the medium is improved.
（１）半導体ナノ粒子蛍光体が剥き出しの状態で樹脂化する従来と比較して、蛍光体含有粒子に含まれ保護された状態で樹脂化すればよいので、製造時の半導体ナノ粒子蛍光体の劣化を気にしなくてよい。 (1) Compared to the conventional case where the semiconductor nanoparticle phosphor is resinated in an exposed state, the resin may be resinized in a state protected and contained in the phosphor-containing particles. You don't have to worry about deterioration.
（２）剥き出しの状態の半導体ナノ粒子蛍光体を媒体が含む従来と比較して、蛍光体含有粒子に保護された状態で使用されるので、使用による半導体ナノ粒子蛍光体の劣化を気にしなくてよい。 (2) Compared to the conventional case where the medium contains a semiconductor nanoparticle phosphor in an exposed state, it is used in a state protected by the phosphor-containing particles, so there is no concern about deterioration of the semiconductor nanoparticle phosphor due to use. It's okay.
また、上述のように使用による半導体ナノ粒子蛍光体の劣化を気にしなくてよいので、シートを保護するための部分が不要であり、省スペース化が可能であるという利点もある。すなわち、剥き出しの状態の半導体ナノ粒子蛍光体の劣化要因である水分、酸素を阻止するために従来必須であった保護のための部分をなくすことで、シートを薄くすることができる。より具体的には、エッジ部分を設ける必要がなく（あるいは少なく）なるため、面方向に関して省スペース化が可能となるとともに、保護のための保護層を設ける必要がなく（あるいは少なく）なるため、厚み方向に関して省スペース化が可能となる。 Moreover, since it is not necessary to worry about deterioration of the semiconductor nanoparticle phosphor due to use as described above, there is an advantage that a portion for protecting the sheet is unnecessary and space saving is possible. That is, the sheet can be made thin by eliminating the protective portion that has been essential in the past in order to prevent moisture and oxygen, which are degradation factors of the exposed semiconductor nanoparticle phosphor. More specifically, since it is not necessary (or less) to provide an edge portion, it is possible to save space in the surface direction, and it is not necessary (or less) to provide a protective layer for protection. Space can be saved in the thickness direction.
本発明の一態様の蛍光体含有シートに用いられる透光性を有する媒体３２としては、本発明の一態様の発光装置において上述した透光性を有する媒体１３と同様のものを好適に用いることができる。また、本発明の一態様の蛍光体含有粒子を分散させた、透光性を有する媒体をシート状に形成する方法としては、従来の蛍光体含有シートを製造するのと同様に、たとえばまず、蛍光体シート形成用の塗布液として蛍光体含有粒子を樹脂に分散した溶液（以下、「シート製造用蛍光体含有粒子分散シリコーン樹脂」とする）を作製する。シート製造用蛍光体含有粒子分散シリコーン樹脂は蛍光体含有粒子と樹脂を混合することにより得られる。付加反応型シリコーン樹脂を用いる場合は、ケイ素原子に結合したアルケニル基を含有する化合物と、ケイ素原子に結合した水素原子を有する化合物を混合すると、室温でも硬化反応が始まることがあるので、さらにアセチレン化合物などのヒドロシリル化反応遅延剤をシート製造用蛍光体含有粒子分散シリコーン樹脂に配合して、ポットライフを延長することも可能である。また、添加材として塗布膜安定化のための分散剤やレベリング剤、シート表面の改質剤としてシランカップリング剤などの接着補助剤などをシート製造用蛍光体含有粒子分散シリコーン樹脂に混合することも可能である。また、蛍光体沈降抑制剤としてアルミナ微粒子、シリカ微粒子、シリコーン微粒子などをシート製造用蛍光体含有粒子分散シリコーン樹脂に混合することも可能である。
As the light-transmitting
流動性を適切にするために必要であれば、溶媒を加えて溶液とすることもできる。溶媒は流動状態の樹脂の粘度を調整できるものであれば、特に限定されない。たとえば、トルエン、メチルエチルケトン、メチルイソブチルケトン、ヘキサン、テルピネオールなどが挙げられる。 If necessary to make fluidity appropriate, a solvent can be added to form a solution. A solvent will not be specifically limited if the viscosity of resin of a fluid state can be adjusted. For example, toluene, methyl ethyl ketone, methyl isobutyl ketone, hexane, terpineol and the like can be mentioned.
これらの成分を所定の組成になるよう調合した後、ホモジナイザー、自公転型攪拌機、３本ローラー、ボールミル、遊星式ボールミル、ビーズミルなどの撹拌・混練機で均質に混合分散することで、シート製造用蛍光体含有粒子分散シリコーン樹脂が得られる。混合分散後、もしくは混合分散の過程で、真空もしくは減圧条件下で脱泡することも好ましく行われる。 After preparing these components to a predetermined composition, they are mixed and dispersed homogeneously with a homogenizer, a revolving stirrer, a three-roller, a ball mill, a planetary ball mill, a bead mill, etc. A phosphor-containing particle-dispersed silicone resin is obtained. Defoaming is preferably carried out under vacuum or reduced pressure conditions after mixing or dispersing.
次に、シート製造用蛍光体含有粒子分散シリコーン樹脂を基材上に塗布し、乾燥させる。塗布は、リバースロールコーター、ブレードコーター、スリットダイコーター、ダイレクトグラビアコーター、オフセットグラビアコーター、キスコーター、ナチュラルロールコーター、エアーナイフコーター、ロールブレードコーター、バリバーロールブレードコーター、トゥーストリームコーター、ロッドコーター、ワイヤーバーコーター、アプリケーター、ディップコーター、カーテンコーター、スピンコーター、ナイフコーターなどにより行うことができる。また、本発明の一態様の蛍光体含有シートはスクリーン印刷やグラビア印刷、平版印刷などの印刷法を用いても作製することもできる。印刷法を用いる場合には、特にスクリーン印刷が好ましく用いられる。 Next, the phosphor-containing particle-dispersed silicone resin for sheet production is applied on the substrate and dried. Application is reverse roll coater, blade coater, slit die coater, direct gravure coater, offset gravure coater, kiss coater, natural roll coater, air knife coater, roll blade coater, varibar roll blade coater, two stream coater, rod coater, wire A bar coater, an applicator, a dip coater, a curtain coater, a spin coater, a knife coater or the like can be used. In addition, the phosphor-containing sheet of one embodiment of the present invention can be manufactured using a printing method such as screen printing, gravure printing, or lithographic printing. When using a printing method, screen printing is particularly preferably used.
シートの乾燥は熱風乾燥機や赤外線乾燥機などの一般的な加熱装置を用いて行うことができる。シートの加熱硬化には、熱風乾燥機や赤外線乾燥機などの一般的な加熱装置が用いられる。この場合、加熱硬化条件は、通常、４０℃以上２５０℃以下で１分間以上５時間以下、好ましくは１００℃以上２００℃以下で２分間以上３時間以下である。 The sheet can be dried using a general heating device such as a hot air dryer or an infrared dryer. For heating and curing the sheet, a general heating device such as a hot air dryer or an infrared dryer is used. In this case, the heat curing conditions are usually 40 ° C. or higher and 250 ° C. or lower for 1 minute or longer and 5 hours or shorter, preferably 100 ° C. or higher and 200 ° C. or lower for 2 minutes or longer and 3 hours or shorter.
なお、図３には、図１に示した第１の実施態様の蛍光体含有粒子１を用いた場合を示したが、これに制限されるものではなく、２種類以上の半導体ナノ粒子蛍光体を含んでいても勿論よい。 FIG. 3 shows the case where the phosphor-containing particles 1 of the first embodiment shown in FIG. 1 are used. However, the present invention is not limited to this, and two or more types of semiconductor nanoparticle phosphors are used. Of course, it may be included.
１ 蛍光体含有粒子、２ コア部、３ 半導体ナノ粒子蛍光体、４ 樹脂、５ シェル部、１１ 発光装置、１２ 光源、１３ 媒体、１４ リード線、１５ 枠体、２１ 発光装置、２２ 蛍光体含有粒子、２３ 蛍光体含有粒子、３１ 蛍光体含有シート、３２ 媒体。 DESCRIPTION OF SYMBOLS 1 Phosphor containing particle | grains, 2 core part, 3 semiconductor nanoparticle fluorescent substance, 4 resin, 5 shell part, 11 light-emitting device, 12 light source, 13 medium, 14 lead wire, 15 frame, 21 light-emitting device, 22 phosphor containing Particles, 23 phosphor-containing particles, 31 phosphor-containing sheet, 32 medium.
Claims (14)
前記コア部の少なくとも一部を覆う、イオン性液体に由来する構成単位を含む樹脂の層状物であるシェル部とを備える、蛍光体含有粒子。 A core part, which is a granular material of a resin containing a structural unit derived from an ionic liquid, in which a semiconductor nanoparticle phosphor is dispersed;
A phosphor-containing particle comprising: a shell portion that is a layered product of a resin including a structural unit derived from an ionic liquid that covers at least a part of the core portion.