JP2018124269A - Component for watch and watch - Google Patents
Component for watch and watch Download PDFInfo
- Publication number
- JP2018124269A JP2018124269A JP2017216500A JP2017216500A JP2018124269A JP 2018124269 A JP2018124269 A JP 2018124269A JP 2017216500 A JP2017216500 A JP 2017216500A JP 2017216500 A JP2017216500 A JP 2017216500A JP 2018124269 A JP2018124269 A JP 2018124269A
- Authority
- JP
- Japan
- Prior art keywords
- film
- timepiece
- watch
- toning
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、時計用部品および時計に関する。 The present invention relates to a timepiece component and a timepiece.
時計は、実用品としての機能が求められるとともに、装飾品として優れた審美性(美的外観)が要求される。 A watch is required to have a function as a practical product and to have excellent aesthetics (aesthetic appearance) as a decorative product.
このため、文字板、ケース等の時計用部品には、優れた質感を有する貴金属材料が用いられている(例えば、特許文献1参照)。 For this reason, noble metal materials having excellent texture are used for timepiece parts such as dials and cases (see, for example, Patent Document 1).
しかしながら、貴金属材料は、一般に高価であり、また、埋蔵量等の関係から、過剰な使用を抑制することが求められている。 However, noble metal materials are generally expensive, and it is required to suppress excessive use from the viewpoint of reserves and the like.
本発明の目的は、貴金属を主材料として使用しなくても、優れた外観を有する時計用部品を提供すること、また、前記時計用部品を備えた時計を提供することにある。 An object of the present invention is to provide a timepiece component having an excellent appearance without using a precious metal as a main material, and to provide a timepiece having the timepiece component.
このような目的は、下記の本発明により達成される。
本発明の時計用部品は、Tiの窒化物もしくは炭化物、Crの窒化物もしくは炭化物、または、金属材料を含む第1の材料で構成され、金属光沢を呈する金属光沢部と、
前記金属光沢部の少なくとも一部を被覆し、金属酸化物を含む材料で構成された複数の層を有する積層体で構成され、色調を調整する機能を有する調色膜と、
前記調色膜の前記金属光沢部に対向する面とは反対の面側に設けられ、特定の機能を付与する機能性膜とを備えることを特徴とする。
Such an object is achieved by the present invention described below.
A timepiece component of the present invention is composed of a first material including a nitride or carbide of Ti, a nitride or carbide of Cr, or a metal material, and a metallic luster portion exhibiting a metallic luster,
A toning film that covers at least a part of the metallic luster part, is composed of a laminate having a plurality of layers made of a material containing a metal oxide, and has a function of adjusting the color tone;
It is provided on the surface opposite to the surface facing the metallic luster portion of the toning film, and includes a functional film that imparts a specific function.
これにより、貴金属を主材料として使用しなくても、優れた外観を有する時計用部品を提供することができる。 As a result, it is possible to provide a watch component having an excellent appearance without using a precious metal as a main material.
本発明の時計用部品では、前記機能性膜は、防汚性を向上させる機能を有するものであることが好ましい。 In the timepiece part of the invention, it is preferable that the functional film has a function of improving antifouling properties.
これにより、汚れの付着による審美性の低下をより効果的に防止することができる。また、汚れが付着した場合であっても、より容易に当該汚れを除去することができる。したがって、より長期間にわたって、様々な環境下において、優れた審美性をより好適に保持することができる。また、時計用部品の手触り感も優れたものとなる。 Thereby, the fall of the aesthetics by adhesion of dirt can be prevented more effectively. Moreover, even if dirt is attached, the dirt can be more easily removed. Therefore, excellent aesthetics can be more suitably maintained under various environments for a longer period of time. In addition, the feel of the watch parts is excellent.
本発明の時計用部品では、前記機能性膜は、フッ素含有有機ケイ素化合物を含む材料で構成されたものであることが好ましい。 In the timepiece part of the invention, it is preferable that the functional film is made of a material containing a fluorine-containing organosilicon compound.
これにより、汚れの付着による審美性の低下をさらに効果的に防止することができる。また、汚れが付着した場合であっても、さらに容易に当該汚れを除去することができる。したがって、さらに長期間にわたって、様々な環境下において、優れた審美性をさらに好適に保持することができる。また、機能性膜がフッ素含有有機ケイ素化合物を含む材料で構成されたものであると、防汚性、手触り感だけでなく、防水性、耐擦傷性等も向上する。また、機能性膜の調色膜等に対する密着性をより優れたものとすることができ、時計用部品や当該時計用部品を備える時計の耐久性をより優れたものとすることができる。また、フッ素含有有機ケイ素化合物は、時計用部品全体としての外観に与える影響が小さいため、より確実に時計用部品の審美性を優れたものとすることができる。 Thereby, the fall of the aesthetics by adhesion of dirt can be prevented still more effectively. Moreover, even if dirt is attached, the dirt can be removed more easily. Therefore, excellent aesthetics can be more suitably maintained under various environments for a longer period of time. Further, when the functional film is composed of a material containing a fluorine-containing organosilicon compound, not only antifouling property and touch feeling but also waterproof property, scratch resistance and the like are improved. In addition, the adhesion of the functional film to the toning film and the like can be further improved, and the durability of the timepiece component and the timepiece including the timepiece component can be further improved. In addition, since the fluorine-containing organosilicon compound has a small influence on the appearance of the entire watch part, the aesthetics of the watch part can be more reliably improved.
本発明の時計用部品では、前記機能性膜は、抗菌性を向上させる機能を有するものであることが好ましい。 In the timepiece part of the invention, it is preferable that the functional film has a function of improving antibacterial properties.
時計(特に、腕時計、懐中時計等の携帯時計)は、皮膚に接触して用いられることが多く、また、各種菌との接触が多い屋外で用いられることが多い。したがって、時計用部品は高い抗菌性を有するものであることが好ましいが、機能性膜が抗菌性を向上させる機能を有するものであると、このような要求を好適に満足することができる。 Timepieces (especially portable watches such as wristwatches, pocket watches, etc.) are often used in contact with the skin, and are often used outdoors where there is much contact with various bacteria. Therefore, it is preferable that the timepiece component has a high antibacterial property, but such a requirement can be suitably satisfied when the functional film has a function of improving the antibacterial property.
本発明の時計用部品では、前記機能性膜は、硬度を向上させる機能を有するものであることが好ましい。 In the timepiece part of the invention, it is preferable that the functional film has a function of improving hardness.
これにより、耐擦傷性(傷の付き難さ)、耐打痕性(打痕のつき難さ)等を優れたものとすることができ、時計用部品や当該時計用部品を備える時計全体としての耐久性をより優れたものとすることができる。 As a result, the scratch resistance (hardness of scratching), dent resistance (hardness of scratching), etc. can be improved, and the watch part and the watch as a whole equipped with the watch part can be made. The durability can be made more excellent.
本発明の時計用部品では、前記機能性膜は、窒化ケイ素、窒化アルミニウムの一方を含む材料で構成されたものであることが好ましい。 In the timepiece part of the invention, it is preferable that the functional film is made of a material containing one of silicon nitride and aluminum nitride.
これにより、時計用部品の製造コストを抑制しつつ、時計用部品の審美性をより優れたものとし、かつ、時計用部品の耐擦傷性、耐打痕性等をより優れたものとすることができ、時計用部品や当該時計用部品を備える時計全体としての耐久性をさらに優れたものとすることができる。また、時計用部品の生産性をより優れたものとすることができる。また、窒化ケイ素、窒化アルミニウムは、上記のような優れた特徴を有しつつ、透過性を有する為、下地の外観に与える影響が小さく、より確実に時計用部品の審美性を優れたものとすることができる。 As a result, while suppressing the production cost of watch parts, the watch parts will have better aesthetics, and the watch parts will have better scratch resistance, dent resistance, etc. Thus, it is possible to further improve the durability of the timepiece part and the timepiece having the timepiece part as a whole. In addition, the productivity of timepiece parts can be further improved. In addition, since silicon nitride and aluminum nitride have the above-mentioned excellent characteristics and have transparency, they have a small effect on the appearance of the base, and more reliably improve the aesthetics of watch parts. can do.
本発明の時計用部品では、前記金属光沢部は、前記第1の材料で構成された基材であることが好ましい。 In the timepiece component according to the aspect of the invention, it is preferable that the metallic gloss portion is a base material made of the first material.
これにより、時計用部品の構造をより単純なものとすることができ、時計用部品の生産性をより優れたものとすることができる。 Thereby, the structure of the timepiece part can be made simpler, and the productivity of the timepiece part can be further improved.
本発明の時計用部品では、前記金属光沢部は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料のいずれをも実質的に含まない材料で構成された基材上に設けられた被膜であることが好ましい。 In the timepiece component of the present invention, the metallic luster portion is formed on a base material made of a material substantially free of any of Ti nitride and carbide, Cr nitride and carbide, and metal material. It is preferable that the coating is provided.
これにより、基材の構成材料等の選択の幅が広がり、時計用部品の成形方法の選択の幅、時計における時計用部品の配置部位の選択の幅等をより広いものとすることができる。また、時計用部品全体としての、金属材料の使用量をより少ないものとすることができる。 Thereby, the selection range of the constituent material of the base material is widened, and the selection range of the molding method of the timepiece component, the selection range of the placement part of the timepiece component in the timepiece, and the like can be made wider. In addition, the amount of metal material used as a whole watch component can be reduced.
本発明の時計用部品では、前記調色膜は、Ta2O5、SiO2、TiO2、Al2O3、ZrO2、Nb2O5およびHfO2よりなる群から選択される少なくとも1種を含む材料で構成された層を有するものであることが好ましい。 In the timepiece part of the invention, the toning film is at least one selected from the group consisting of Ta 2 O 5 , SiO 2 , TiO 2 , Al 2 O 3 , ZrO 2 , Nb 2 O 5 and HfO 2. It is preferable to have a layer composed of a material containing
これにより、時計用部品の審美性をより優れたものとすることができるとともに、時計用部品全体として表現することのできる色調の範囲をより広いものとすることができる。また、これらの化合物は、各種の金属酸化物の中でも化学的安定性が特に高い材料であり、時計用部品全体としての外観の安定性、耐久性をより優れたものとすることができる。 Thereby, while being able to make the aesthetics of the timepiece parts more excellent, the range of the color tone that can be expressed as the whole timepiece parts can be made wider. In addition, these compounds are materials having particularly high chemical stability among various metal oxides, and can make the appearance stability and durability of the entire watch part excellent.
本発明の時計用部品では、前記調色膜の厚さは、100nm以上2000nm以下であることが好ましい。 In the timepiece part of the invention, it is preferable that the toning film has a thickness of 100 nm to 2000 nm.
これにより、時計用部品の審美性をより優れたものとすることができ、表現することができる色範囲(色再現域)をより広いものとすることができるとともに、調色膜の不本意な剥離等をより効果的に防止することができ、時計用部品の耐久性、信頼性をより優れたものとすることができ、また、時計用部品の生産性をより優れたものとすることができる。 As a result, the aesthetics of the timepiece component can be made more excellent, the color range (color reproduction range) that can be expressed can be made wider, and the toning film is unwilling. Separation can be prevented more effectively, durability and reliability of watch parts can be improved, and productivity of watch parts can be improved. it can.
本発明の時計用部品では、前記調色膜を構成する各層の厚さは、それぞれ、10nm以上300nm以下であることが好ましい。 In the timepiece component of the present invention, it is preferable that the thickness of each layer constituting the toning film is 10 nm or more and 300 nm or less.
これにより、時計用部品の審美性をより優れたものとすることができ、色再現域をより広いものとすることができるとともに、調色膜の不本意な剥離等をより効果的に防止することができ、時計用部品の耐久性、信頼性をより優れたものとすることができる。 As a result, the aesthetics of the watch parts can be made more excellent, the color reproduction range can be made wider, and unintentional peeling of the toning film can be more effectively prevented. The durability and reliability of the timepiece component can be further improved.
本発明の時計用部品では、前記金属光沢部は、Ti、CrまたはAlを含む材料で構成されたものであることが好ましい。 In the timepiece component according to the aspect of the invention, it is preferable that the metallic gloss portion is made of a material containing Ti, Cr, or Al.
これにより、時計用部品全体として、青みがかった高級感のある金属光沢を好適に得ることができる。 Thereby, as a whole watch component, a bluish and high-grade metallic luster can be suitably obtained.
本発明の時計用部品は、風防ガラス、ケースまたはバンドであることが好ましい。
これらの部品(時計用部品)は、時計全体の外観に大きな影響を与えるものであるため、これらの部品に本発明が適用されることにより、時計全体としての審美性をより優れたものとすることができる。また、これらの部品(時計用部品)は、通常、時計において、外部に露出する部品である。このような部品には、前述したような機能性膜が有することにより発揮される機能が特に強く求められる。したがって、これらの部品に本発明が適用されることにより、本発明による効果がより顕著に発揮される。
The timepiece part of the present invention is preferably a windshield, a case or a band.
Since these parts (parts for watches) have a great influence on the appearance of the entire watch, the present invention is applied to these parts, thereby improving the aesthetics of the watch as a whole. be able to. These parts (timepiece parts) are usually parts exposed to the outside in a timepiece. Such a component is particularly strongly required to have a function exhibited by the functional film as described above. Therefore, when the present invention is applied to these components, the effects of the present invention are more remarkably exhibited.
本発明の時計は、本発明の時計用部品を備えたことを特徴とする。
これにより、貴金属を主材料として使用しなくても、優れた外観を有する時計を提供することができる。
The timepiece of the present invention includes the timepiece component of the present invention.
Accordingly, it is possible to provide a timepiece having an excellent appearance without using a noble metal as a main material.
以下、添付する図面を参照しつつ、好適な実施形態について詳細な説明をする。
《時計用部品》
まず、本発明の時計用部品について説明する。
Hereinafter, preferred embodiments will be described in detail with reference to the accompanying drawings.
《Watch parts》
First, the timepiece part of the present invention will be described.
[第1実施形態]
図1は、本発明の時計用部品の第1実施形態を模式的に示す断面図である。
[First Embodiment]
FIG. 1 is a cross-sectional view schematically showing a first embodiment of a timepiece part of the invention.
時計用部品10は、Tiの窒化物もしくは炭化物、Crの窒化物もしくは炭化物、または、金属材料を含む第1の材料で構成され、金属光沢を呈する金属光沢部1と、金属光沢部1の少なくとも一部を被覆し、金属酸化物を含む材料で構成された複数の層(金属酸化物層51)を有する積層体で構成され、時計用部品10全体としての色調を調整する機能を有する調色膜5と、調色膜5の金属光沢部1に対向する面とは反対の面側に設けられ、特定の機能を付与する機能性膜6とを備えている。
The
なお、本発明において、「窒化物」は、窒素(N)を含む金属化合物のことを指し、炭窒化物等を含む。また、本発明において、「炭化物」は、炭素(C)を含む金属化合物のことを指し、炭窒化物等を含む。 In the present invention, “nitride” refers to a metal compound containing nitrogen (N), and includes carbonitride and the like. In the present invention, “carbide” refers to a metal compound containing carbon (C), and includes carbonitride and the like.
金属光沢部1は、金属光沢感を呈する部位である。
調色膜5は、金属光沢部1の金属光沢感を生かしつつ、時計用部品10全体としての色調を調整する機能を有するものである。
そして、観察者の視点は、図1中の上側(時計用部品10の調色膜5が設けられた面側(時計用部品10の金属光沢部1よりも調色膜5に近い側))である(後述する図2〜図6についても同様)。
The
The
The observer's viewpoint is the upper side in FIG. 1 (the surface side on which the
このような構成により、貴金属を主材料として使用しなくても、優れた外観(金属光沢を呈する外観)、特に高級感を有する時計用部品10を提供することができる。また、貴金属を使用する場合であっても、その使用量を抑制することができる。より具体的には、例えば、貴金属を実質的に含まなくても貴金属材料が呈するような高級感のある外観を得ることができる。また、貴金属は、一般に、傷等が付きやすいという特徴があるが、上記のような構成とすることにより、時計用部品10全体として耐擦傷性等を優れたものとすることができる。特に、時計用部品10では、優れた外観と、優れた耐擦傷性とを両立することができる。また、金属材料だけでは、表現することが困難な青みがかった光沢感のある金属感や、赤みがかった光沢感のある金属感等、様々な色調を表現することができ、単に金属材料(特に、貴金属材料)のみを用いた場合には得ることのできない色調の外観を得ることができる。すなわち、表現することができる色範囲(色再現域)をより広いものとすることができる。また、金属光沢部1が金属材料(例えば、化学的安定性が比較的低く、酸化等の反応が進行しやすい金属材料等)で構成されたものであっても、化学的安定性に優れた酸化物で構成された調色膜5で被覆することにより、時計用部品10全体としての外観の安定性、耐久性が向上する。
また、機能性膜6を有することにより、時計用部品10に特定の機能を付与することができる。これにより、例えば、時計用部品10全体、また、時計用部品10が適用される時計全体として、防汚性、抗菌性、硬度、耐擦傷性、耐打痕性等の機能を向上させることができる。
With such a configuration, it is possible to provide a
In addition, by having the
特に、本実施形態の時計用部品10では、金属光沢部1は、第1の材料で構成された基材2である。言い換えると、本実施形態の時計用部品10は、金属光沢部1として機能する基材2と、調色膜5とを備えている。
In particular, in the
これにより、時計用部品10の構造をより単純なものとすることができ、時計用部品10の生産性をより優れたものとすることができる。
Thereby, the structure of the
≪基材(金属光沢部)≫
本実施形態において、基材2(金属光沢部1)は、Tiの窒化物もしくは炭化物、Crの窒化物もしくは炭化物、または、金属材料を含む第1の材料で構成されたものである。
≪Base material (metallic glossy part) ≫
In the present embodiment, the base material 2 (the metallic luster part 1) is composed of a nitride or carbide of Ti, a nitride or carbide of Cr, or a first material containing a metal material.
金属光沢部1を構成する金属材料としては、貴金属より卑な金属であるのが好ましく、例えば、Al、Ti、V、Cr、Fe、Co、Ni、Cu、Zn、Zr、Nb、Mo、In、Sn、Hf、Ta、W、Bi、Mgや、これらのうち少なくとも1種を含む合金等が挙げられる。なお、少量の貴金属を含むことを妨げるものではない。
The metallic material constituting the
特に、金属光沢部1が、Ti、CrまたはAlを含む材料で構成されたものであると、時計用部品10全体として、青みがかった高級感のある金属光沢を好適に得ることができる。
In particular, when the
また、金属光沢部1が、TiまたはCrの窒化物で構成されたものであると、時計用部品10全体として、高級感のある金色の外観(単体としてのAuに類似した外観)を好適に得ることができる。
Further, when the
また、金属光沢部1が、Tiの炭化物で構成されたものであると、時計用部品10全体として、高級感のある黒味を帯びた色の外観を好適に得ることができる。特に、時計用部品10全体として、従来では、表現が特に困難であった黒味がかった赤色や黒味がかった青色等の外観を得ることができる。
Moreover, when the
金属光沢部1がTiの炭窒化物を含む材料で構成されている場合、例えば、ピンクゴールドに類似の色調を好適に表現することができる。
When the
金属光沢部1は、貴金属元素(Au、Ag、Pt、Pd、Rh、Ir、Ru、Os)の含有率が十分に低いものであるのが好ましく、金属光沢部1中における貴金属元素の含有率(複数種の貴金属元素を含む場合はこれらの含有率の総和)は、1.0質量%以下であるのが好ましく、0.5質量%以下であるのがより好ましく、0.1質量%以下であるのがさらに好ましい。
The
これにより、貴金属を主材料として使用しなくても、優れた外観が得られるという本発明による効果がより顕著に発揮される。 Thereby, even if it uses no noble metal as a main material, the effect by this invention that the outstanding external appearance is acquired is exhibited more notably.
なお、金属光沢部1は、金属光沢感を有するものであれば、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料以外の成分を含むものであってもよい。ただし、金属光沢部1中における前記の材料(Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料)の含有率は、5質量%以下であるのが好ましく、1質量%以下であるのがより好ましい。
The
基材2は、各部位で均一な組成を有するものであってもよいし、組成の異なる部位を有するものであってもよい。
The
金属光沢部1は、30nm以上の厚さを有するものであるのが好ましく、40nm以上の厚さを有するものであるのがより好ましく、50nm以上の厚さを有するものであるのがさらに好ましい。
The
これにより、時計用部品10全体としての光沢感、審美性をより優れたものとすることができる。
Thereby, the glossiness and aesthetics of the
基材2の形状、大きさは、特に限定されず、通常、時計用部品10の形状、大きさに基づいて決定される。また、基材2には、文字、数字、記号、模様等の凹凸パターンが設けられていてもよい。
The shape and size of the
基材2は、例えば、表面に、鏡面加工、スジ目加工、梨地加工等の表面加工が施されたものであってもよい。
For example, the
これにより、時計用部品10の表面の光沢具合にバリエーションを持たせることが可能となり、時計用部品10の審美性をさらに向上させることができる。鏡面加工は、例えば、周知の研磨方法を用いて行うことができ、例えば、バフ(羽布)研磨、バレル研磨、その他の機械研磨等を採用することができる。
Thereby, it becomes possible to give a variation in the glossiness of the surface of the
また、このような表面加工を施した基材2を用いて製造される時計用部品10は、後に詳述する各種の膜に対して表面加工を直接施すことにより得られるものに比べて、ギラツキ等が抑制されたものとなり、特に審美性に優れたものとなる。また、後に詳述する各種の膜は通常比較的薄いものであり、当該膜に対して表面加工を直接施す場合には、当該表面加工を施す際に当該膜にカケ、剥離等の欠陥を生じ易く、時計用部品10の製造の歩留りが著しく低下する場合があるが、基材2に対して表面加工を行うことにより、このような問題の発生も効果的に防止することができ、かつ比較的膜厚が薄い為表面加工の審美性を損なうこともない。また、基材2に対する表面加工は、後に詳述する各種の膜に対する表面加工に比べて、温和な条件で容易に行うことができる。
Moreover, the
≪調色膜≫
調色膜5は、金属酸化物の多層膜で構成されたものである。言い換えると、調色膜5は、複数の金属酸化物層51を備える積層体である。
≪Toning film≫
The
調色膜5(金属酸化物層51)は、金属材料の酸化物で構成されたものであればよいが、調色膜5は、Ta2O5、SiO2、TiO2、Al2O3、ZrO2、Nb2O5およびHfO2よりなる群から選択される少なくとも1種を含む材料で構成された層(金属酸化物層51)を有するものであるのが好ましく、複数の金属酸化物層51として、前記群から選択される互いに異なる材料で構成された層を有するものであるのがより好ましい。
The toning film 5 (metal oxide layer 51) only needs to be composed of an oxide of a metal material. However, the toning
これにより、時計用部品10の審美性をより優れたものとすることができるとともに、時計用部品10全体として表現することのできる色調の範囲をより広いものとすることができる。また、これらの化合物は、各種の金属酸化物の中でも化学的安定性が特に高い材料であり、時計用部品10全体としての外観の安定性、耐久性をより優れたものとすることができる。
Thereby, while being able to make the aesthetics of the
中でも、Al2O3およびHfOは、硬度が特に高い材料であり、化学的な耐久性だけでなく、機械的な力に対しても優れた耐久性を有する。 Among them, Al 2 O 3 and HfO are materials having particularly high hardness, and have excellent durability not only for chemical durability but also for mechanical force.
なお、調色膜5(金属酸化物層51)は、主として金属酸化物で構成されたものであればよく、金属酸化物以外の成分を含むものであってもよい。ただし、調色膜5(金属酸化物層51)中における金属酸化物以外の成分の含有率は、5質量%以下であるのが好ましく、1質量%以下であるのがより好ましい。 In addition, the toning film 5 (metal oxide layer 51) should just be mainly comprised by the metal oxide, and may contain components other than a metal oxide. However, the content of components other than the metal oxide in the toning film 5 (metal oxide layer 51) is preferably 5% by mass or less, and more preferably 1% by mass or less.
また、調色膜5は、金属酸化物層51以外の図示しない層を、例えば金属酸化物層51間に設けられた中間層として有していてもよい。
The
調色膜5の厚さは、100nm以上2000nm以下であるのが好ましく、150nm以上1000nm以下であるのがより好ましく、200nm以上800nm以下であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10の審美性をより優れたものとすることができ、色再現域をより広いものとすることができるとともに、調色膜5の不本意な剥離等をより効果的に防止することができ、時計用部品10の耐久性、信頼性をより優れたものとすることができ、また、時計用部品10の生産性をより優れたものとすることができる。
Thereby, the aesthetics of the
調色膜5を構成する各層(各金属酸化物層51)の厚さは、それぞれ、10nm以上300nm以下であるのが好ましく、15nm以上200nm以下であるのがより好ましく、25nm以上150nm以下であるのがさらに好ましい。
The thickness of each layer (each metal oxide layer 51) constituting the
これにより、時計用部品10の審美性をより優れたものとすることができ、色再現域をより広いものとすることができるとともに、調色膜5の不本意な剥離等をより効果的に防止することができ、時計用部品10の耐久性、信頼性をより優れたものとすることができる。
Thereby, the aesthetics of the
調色膜5を構成する金属酸化物層51の数は、2以上であるのが好ましく、3以上であるのがより好ましい。
The number of metal oxide layers 51 constituting the
これにより、時計用部品10の審美性をより優れたものとすることができ、色再現域をより広いものとすることができるとともに、調色膜5の不本意な剥離等をより効果的に防止することができ、時計用部品10の耐久性、信頼性をより優れたものとすることができる。
Thereby, the aesthetics of the
調色膜5の形成方法は、特に限定されず、例えば、スピンコート、ディッピング、刷毛塗り、噴霧塗装、静電塗装、電着塗装等の塗装、電解めっき、浸漬めっき、無電解めっき等の湿式めっき法や、熱CVD、プラズマCVD、レーザーCVD等の化学蒸着法(CVD)、真空蒸着、スパッタリング、イオンプレーティング、レーザーアブレーション等の乾式めっき法(気相成膜法)、溶射等が挙げられるが、乾式めっき法(気相成膜法)が好ましい。
The method for forming the
調色膜5の形成方法として乾式めっき法(気相成膜法)を適用することにより、均一な膜厚を有し、均質で、かつ、基材2等との密着性が特に優れた調色膜5を確実に形成することができる。その結果、時計用部品10の審美的外観、耐久性を特に優れたものとすることができる。
By applying a dry plating method (vapor phase film forming method) as a method for forming the
また、調色膜5の形成方法として乾式めっき法(気相成膜法)を適用することにより、形成すべき調色膜5を構成する各金属酸化物層51が比較的薄いものであっても、膜厚のばらつきを十分に小さいものとすることができる。このため、時計用部品10の信頼性を向上させる上でも有利である。
Further, by applying a dry plating method (vapor phase film forming method) as a method for forming the
また、調色膜5の形成方法として乾式めっき法(気相成膜法)を適用することにより、調色膜5中の各部位(各金属酸化物層51)における酸素の含有率をより確実に制御することができる。
Further, by applying a dry plating method (vapor phase film forming method) as a method for forming the
上記のような乾式めっき法(気相成膜法)の中でも、イオンプレーティングが特に好ましい。 Among the dry plating methods (vapor phase film forming methods) as described above, ion plating is particularly preferable.
調色膜5の形成方法としてイオンプレーティングを適用することにより、上記のような効果はより顕著なものとなる。すなわち、調色膜5の形成方法としてイオンプレーティングを適用することにより、均一な膜厚を有し、均質で、かつ、基材2等との密着性が特に優れた調色膜5をより確実に形成することができる。その結果、最終的に得られる時計用部品10の審美的外観、耐久性をさらに優れたものとすることができる。
By applying ion plating as a method for forming the
また、調色膜5の形成方法としてイオンプレーティングを適用することにより、形成すべき調色膜5を構成する各金属酸化物層51が比較的薄いものであっても、膜厚のばらつきを特に小さいものとすることができる。
In addition, by applying ion plating as a method for forming the
また、調色膜5の形成方法としてイオンプレーティングを適用することにより、調色膜5中の各部位(各金属酸化物層51)における酸素の含有率をより確実に制御することができる。
In addition, by applying ion plating as a method for forming the
また、調色膜5を乾式めっき法により形成する場合、例えば、ターゲットを複数セットすることにより、基材2を装置内から取り出すことなく、同一装置内で、調色膜5を構成する各金属酸化物層51を引き続いて形成することができる。
When the
これにより、調色膜5を構成する各層間での密着性が特に優れたものとなるとともに、時計用部品10の生産性も向上する。
As a result, the adhesion between the layers constituting the
≪機能性膜≫
調色膜5の金属光沢部1に対向する面とは反対の面側には、特定の機能を付与する機能性膜6が設けられている。
≪Functional membrane≫
A
例えば、機能性膜6は、防汚性を向上させる機能を有するもの(防汚膜)であるのが好ましい。
これにより、汚れの付着による審美性の低下をより効果的に防止することができる。また、汚れが付着した場合であっても、より容易に当該汚れを除去することができる。したがって、より長期間にわたって、様々な環境下において、優れた審美性をより好適に保持することができる。また、時計用部品10の手触り感も優れたものとなる。
For example, the
Thereby, the fall of the aesthetics by adhesion of dirt can be prevented more effectively. Moreover, even if dirt is attached, the dirt can be more easily removed. Therefore, excellent aesthetics can be more suitably maintained under various environments for a longer period of time. In addition, the feel of the
防汚性を有する機能性膜6としては、例えば、フッ素系化合物を含む材料で構成されたもの等が挙げられるが、中でも、フッ素含有有機ケイ素化合物を含む材料で構成されたものであるのが好ましい。
Examples of the
これにより、汚れの付着による審美性の低下をさらに効果的に防止することができる。また、汚れが付着した場合であっても、さらに容易に当該汚れを除去することができる。したがって、さらに長期間にわたって、様々な環境下において、優れた審美性をさらに好適に保持することができる。また、機能性膜6がフッ素含有有機ケイ素化合物を含む材料で構成されたものであると、防汚性、手触り感だけでなく、防水性、耐擦傷性等も向上する。また、機能性膜6の調色膜5等に対する密着性をより優れたものとすることができ、時計用部品10や当該時計用部品10を備える時計の耐久性をより優れたものとすることができる。また、フッ素含有有機ケイ素化合物は、時計用部品10全体としての外観に与える影響が小さいため、より確実に時計用部品10の審美性を優れたものとすることができる。
Thereby, the fall of the aesthetics by adhesion of dirt can be prevented still more effectively. Moreover, even if dirt is attached, the dirt can be removed more easily. Therefore, excellent aesthetics can be more suitably maintained under various environments for a longer period of time. Further, when the
フッ素含有有機ケイ素化合物の具体例としては、CF3(CF2)2C2H4Si(OCH3)3、CF3(CF2)4C2H4Si(OCH3)3、CF3(CF2)6C2H4Si(OCH3)3、CF3(CF2)8C2H4Si(OCH3)3、CF3(CF2)10C2H4Si(OCH3)3、CF3(CF2)12C2H4Si(OCH3)3、CF3(CF2)14C2H4Si(OCH3)3、CF3(CF2)16C2H4Si(OCH3)3、CF3(CF2)18C2H4Si(OCH3)3、CF3(CF2)6C2H4Si(OC2H5)3、CF3(CF2)8C2H4Si(OC2H5)3、CF3(CF2)6C2H4SiCl3、CF3(CF2)8C2H4SiCl3、CF3(CF2)6C3H6Si(OCH3)3、CF3(CF2)8C3H6Si(OCH3)3、CF3(CF2)6C3H6Si(OC2H5)3、CF3(CF2)8C3H6Si(OC2H5)3、CF3(CF2)6C3H6SiCl3、CF3(CF2)8C3H6SiCl3、CF3(CF2)6C4H8Si(OCH3)3、CF3(CF2)8C4H8Si(OCH3)3、CF3(CF2)6C4H8Si(OC2H5)3、CF3(CF2)8C4H8Si(OC2H5)3、CF3(CF2)6C2H4Si(CH3)(OCH3)2、CF3(CF2)8C2H4Si(CH3)(OCH3)2、CF3(CF2)6C2H4Si(CH3)Cl2、CF3(CF2)8C2H4Si(CH3)Cl2、CF3(CF2)6C2H4Si(C2H5)(OC2H5)2、CF3(CF2)8C2H4Si(C2H5)(OC2H5)2等が挙げられる。 Specific examples of the fluorine-containing organosilicon compound include CF 3 (CF 2 ) 2 C 2 H 4 Si (OCH 3 ) 3 , CF 3 (CF 2 ) 4 C 2 H 4 Si (OCH 3 ) 3 , CF 3 ( CF 2) 6 C 2 H 4 Si (OCH 3) 3, CF 3 (CF 2) 8 C 2 H 4 Si (OCH 3) 3, CF 3 (CF 2) 10 C 2 H 4 Si (OCH 3) 3 CF 3 (CF 2 ) 12 C 2 H 4 Si (OCH 3 ) 3 , CF 3 (CF 2 ) 14 C 2 H 4 Si (OCH 3 ) 3 , CF 3 (CF 2 ) 16 C 2 H 4 Si ( OCH 3 ) 3 , CF 3 (CF 2 ) 18 C 2 H 4 Si (OCH 3 ) 3 , CF 3 (CF 2 ) 6 C 2 H 4 Si (OC 2 H 5 ) 3 , CF 3 (CF 2 ) 8 C 2 H 4 Si (OC 2 H 5 ) 3 CF 3 (CF 2 ) 6 C 2 H 4 SiCl 3 , CF 3 (CF 2 ) 8 C 2 H 4 SiCl 3 , CF 3 (CF 2 ) 6 C 3 H 6 Si (OCH 3 ) 3 , CF 3 ( CF 2) 8 C 3 H 6 Si (OCH 3) 3, CF 3 (CF 2) 6 C 3 H 6 Si (OC 2 H 5) 3, CF 3 (CF 2) 8 C 3 H 6 Si (OC 2 H 5 ) 3 , CF 3 (CF 2 ) 6 C 3 H 6 SiCl 3 , CF 3 (CF 2 ) 8 C 3 H 6 SiCl 3 , CF 3 (CF 2 ) 6 C 4 H 8 Si (OCH 3 ) 3 , CF 3 (CF 2) 8 C 4 H 8 Si (OCH 3) 3, CF 3 (CF 2) 6 C 4 H 8 Si (OC 2 H 5) 3, CF 3 (CF 2) 8 C 4 H 8 Si (OC 2 H 5 ) 3 , CF 3 (CF 2 ) 6 C 2 H 4 Si (CH 3 ) (OCH 3 ) 2 , CF 3 (CF 2 ) 8 C 2 H 4 Si (CH 3 ) (OCH 3 ) 2 , CF 3 (CF 2 ) 6 C 2 H 4 Si (CH 3) Cl 2, CF 3 ( CF 2) 8 C 2 H 4 Si (CH 3) Cl 2, CF 3 (CF 2) 6 C 2 H 4 Si (C 2 H 5) (OC 2 H 5) 2, CF 3 (CF 2) 8 C 2 H 4 Si (C 2 H 5) (OC 2 H 5) 2 and the like.
また、フッ素含有有機ケイ素化合物としては、アミノ基を含有する化合物も好適に用いることができる。 Moreover, as a fluorine-containing organosilicon compound, the compound containing an amino group can also be used suitably.
アミノ基を含有するフッ素含有有機ケイ素化合物としては、例えば、C9F19CONH(CH2)3Si(OC2H5)3、C9F19CONH(CH2)3SiCl3、C9F19CONH(CH2)3Si(CH3)Cl2、C9F19CONH(CH2)NH(CH2)Si(OC2H5)3、C9F19CONH(CH2)5CONH(CH2)Si(OC2H5)3、C8F17SO2NH(CH2)5CONH(CH2)Si(OC2H5)3、C3F7O(CF(CF3)CF2O)2−CF(CF3)−CONH(CH2)Si(OC2H5)3、C3F7O(CF(CF3)CF2O)m’−CF(CF3)−CONH(CH2)Si(OCH3)3[ここで、m’は1以上の整数]等が挙げられる。 Examples of the fluorine-containing organosilicon compound containing an amino group include C 9 F 19 CONH (CH 2 ) 3 Si (OC 2 H 5 ) 3 , C 9 F 19 CONH (CH 2 ) 3 SiCl 3 , C 9 F 19 CONH (CH 2 ) 3 Si (CH 3 ) Cl 2 , C 9 F 19 CONH (CH 2 ) NH (CH 2 ) Si (OC 2 H 5 ) 3 , C 9 F 19 CONH (CH 2 ) 5 CONH ( CH 2) Si (OC 2 H 5) 3, C 8 F 17 SO 2 NH (CH 2) 5 CONH (CH 2) Si (OC 2 H 5) 3, C 3 F 7 O (CF (CF 3) CF 2 O) 2 -CF (CF 3 ) -CONH (CH 2) Si (OC 2 H 5) 3, C 3 F 7 O (CF (CF 3) CF 2 O) m '-CF (CF 3) -CONH (CH 2) S (OCH 3) 3 [where, m 'is an integer of 1 or more], and the like.
また、フッ素含有有機ケイ素化合物としては、例えば、Rf'(CH2)2SiCl3、Rf'(CH2)2Si(CH3)Cl2、(Rf'CH2CH2)2SiCl2、Rf'(CH2)2Si(OCH3)3、Rf'CONH(CH2)3Si(OC2H5)3、Rf'CONH(CH2)2NH(CH2)3Si(OC2H5)3、Rf'SO2N(CH3)(CH2)2CONH(CH2)3Si(OC2H5)3、Rf'(CH2)2OCO(CH2)2S(CH2)3Si(OCH3)3、Rf'(CH2)2OCONH(CH2)2Si(OC2H5)3、Rf'COO−Cy(OH)−(CH2)2Si(OCH3)3、Rf'(CH2)2NH(CH2)2Si(OCH3)3、およびRf'(CH2)2NH(CH2)2NH(CH2)2Si(OCH2CH2OCH3)3等を用いてもよい。上記の各式において、Cyはシクロヘキサン残基であり、Rf’は、炭素数4以上16以下のポリフルオロアルキル基である。
Examples of the fluorine-containing organosilicon compound include R f ′ (CH 2 ) 2 SiCl 3 , R f ′ (CH 2 ) 2 Si (CH 3 ) Cl 2 , (R f ′ CH 2 CH 2 ) 2 SiCl. 2, R f '(CH 2 ) 2 Si (OCH 3) 3, R f' CONH (CH 2) 3 Si (OC 2 H 5) 3, R f 'CONH (CH 2) 2 NH (CH 2) 3 Si (OC 2 H 5) 3 , R f 'SO 2 N (CH 3) (CH 2) 2 CONH (CH 2) 3 Si (OC 2 H 5) 3, R f' (CH 2) 2 OCO (
機能性膜6を構成するフッ素含有有機ケイ素化合物としては、特に、下記式(1)または下記式(2)で示される化合物が好ましい。
As the fluorine-containing organosilicon compound constituting the
式(1)中、Rf 1はパーフルオロアルキル基を示す。Xは臭素、ヨウ素または水素を示す。Yは水素または低級アルキル基を示し、Zはフッ素またはトリフルオロメチル基を示す。R1は加水分解可能な基を示し、R2は水素または不活性な1価の炭化水素基を示す。a、b、c、d、eは0または1以上の整数で、かつa+b+c+d+eは少なくとも1以上であり、a、b、c、d、eで括られた各繰り返し単位の存在順序は、式中において限定されない。fは0、1または2である。gは1、2または3である。hは1以上の整数である In formula (1), R f 1 represents a perfluoroalkyl group. X represents bromine, iodine or hydrogen. Y represents hydrogen or a lower alkyl group, and Z represents a fluorine or trifluoromethyl group. R 1 represents a hydrolyzable group, and R 2 represents hydrogen or an inert monovalent hydrocarbon group. a, b, c, d and e are 0 or an integer of 1 or more, a + b + c + d + e is at least 1 and the order of presence of each repeating unit enclosed by a, b, c, d and e is as follows: It is not limited in. f is 0, 1 or 2. g is 1, 2 or 3. h is an integer of 1 or more
式(2)中、Rf 2は式:「−(CkF2k)O−」で示される単位を含み、分岐を有しない直鎖状のパーフルオロポリアルキレンエーテル構造を有する2価の基を示す。なお、式:「−(CkF2k)O−」におけるkは1以上6以下の整数である。R3は炭素原子数1〜8の1価炭化水素基であり、Wは加水分解性基またはハロゲン原子を示す。pは0、1または2であり、nは1以上5以下の整数である。mおよびrは、2または3である。 In formula (2), R f 2 is a divalent group having a linear perfluoropolyalkylene ether structure containing a unit represented by the formula: “— (C k F 2k ) O—” and having no branch. Indicates. Note that k in the formula: “— (C k F 2k ) O—” is an integer of 1 to 6. R 3 is a monovalent hydrocarbon group having 1 to 8 carbon atoms, and W represents a hydrolyzable group or a halogen atom. p is 0, 1 or 2, and n is an integer of 1 to 5. m and r are 2 or 3.
また、機能性膜6は、抗菌性を向上させる機能を有するもの(抗菌膜)であってもよい。
Moreover, the
時計(特に、腕時計、懐中時計等の携帯時計)は、皮膚に接触して用いられることが多く、また、各種菌との接触が多い屋外で用いられることが多い。したがって、時計用部品10は高い抗菌性を有するものであることが好ましいが、機能性膜6が抗菌性を向上させる機能を有するものであると、このような要求を好適に満足することができる。
Timepieces (especially portable watches such as wristwatches, pocket watches, etc.) are often used in contact with the skin, and are often used outdoors where there is much contact with various bacteria. Therefore, it is preferable that the
抗菌性を有する機能性膜6の構成材料としては、例えば、TiO2等の光触媒;2−(4−チアゾリル)ベンズイミダゾール等のイミダゾール誘導体;シクロフルアニド等のN−ハロアルキルチオ系化合物;10,10’−オキシビスフェノキサアルシン等のフェニルエーテル誘導体;セシルジメチルエチルアンモニウムブロミド等の第4級アンモニウム塩;2,3,5,6−テトラコロル−4−(メチルスルホニル)ピリジン等のスルホン誘導体;アミド類;トリアジン誘導体;トリアゾール誘導体;メチロール基含有化合物;活性ハロゲン含有化合物;活性化されたN−S結合含有化合物;イソチアゾロン系化合物;有機ヨウ素系化合物;ベンズイソチアゾロン系化合物;ピリチオン系化合物;ヒノキチオール、キチン、キトサン、ワサビ抽出物、モウソウチク抽出物等の天然物系抗菌剤等が挙げられる。
As a constituent material of the
これにより、時計用部品10の抗菌性をより優れたものとすることができるとともに、機能性膜6の調色膜5等に対する密着性をより優れたものとすることができ、時計用部品10や当該時計用部品10を備える時計の耐久性をより優れたものとすることができる。
As a result, the antibacterial property of the
また、機能性膜6は、硬度を向上させる機能を有するもの(硬質膜)であってもよい。
これにより、耐擦傷性(傷の付き難さ)、耐打痕性(打痕のつき難さ)等を優れたものとすることができ、時計用部品10や当該時計用部品10を備える時計全体としての耐久性をより優れたものとすることができる。
The
As a result, the scratch resistance (hardness to scratch), the dent resistance (hardness to scratch), and the like can be improved, and the
硬度を向上させる機能を有する機能性膜6の構成材料としては、例えば、DLC、ダイヤモンド、カーボンナノチューブ等の炭素系材料、窒化クロム、窒化ケイ素、窒化アルミニウム等の金属窒化物、炭化クロム、炭化ケイ素、炭化アルミニウム、炭化チタン等の金属窒化物、フッ化クロム、フッ化ケイ素、フッ化アルミニウム、フッ化チタン等の金属フッ化物、硫化クロム、硫化ケイ素、硫化アルミニウム、硫化チタン等の金属硫化物等が挙げられるが、硬度を向上させる機能を有する機能性膜6は、窒化ケイ素、窒化アルミニウムの一方を含む材料で構成されたものであるのが好ましい。
Examples of the constituent material of the
これにより、時計用部品10の製造コストを抑制しつつ、時計用部品10の審美性をより優れたものとし、かつ、時計用部品10の耐擦傷性、耐打痕性等をより優れたものとすることができ、時計用部品10や当該時計用部品10を備える時計全体としての耐久性をさらに優れたものとすることができる。また、時計用部品10の生産性をより優れたものとすることができる。また、窒化ケイ素、窒化アルミニウムは、上記のような優れた特徴を有しつつ、透過性を有する為、下地の外観に与える影響が小さく、より確実に時計用部品10の審美性を優れたものとすることができる。
As a result, the manufacturing cost of the
機能性膜6は、各部位で均一な組成を有するものであってもよいし、組成の異なる部位を有するものであってもよい。例えば、機能性膜6は、複数の層を備える積層体であってもよいし、厚さ方向に組成が傾斜的に変化する傾斜材料で構成されたものであってもよい。
なお、機能性膜6は、上述したような機能を有するものに限定されない。
The
The
前述した成分の機能性膜6中における含有率(複数の成分を含む場合には、これらの含有率の和)は、90質量%以上であるのが好ましく、95質量%以上であるのがより好ましく、99質量%以上であるのがさらに好ましい。
これにより、前述したような効果がより顕著に発揮される。
The content of the above-described components in the functional film 6 (in the case where a plurality of components are included) is preferably 90% by mass or more, more preferably 95% by mass or more. Preferably, it is 99 mass% or more.
Thereby, the effects as described above are more remarkably exhibited.
機能性膜6の厚さは、2nm以上1000nm以下であるのが好ましく、3nm以上500nm以下であるのがより好ましく、4nm以上300nm以下であるのがさらに好ましい。
The thickness of the
これにより、機能性膜6の不本意な剥離等を効果的に防止しつつ、前述したような機能性膜6を設けることによる効果をより顕著に発揮させることができる。
Thereby, the effect by providing the
機能性膜6の形成方法は、特に限定されず、例えば、スピンコート、ディッピング、刷毛塗り、噴霧塗装、静電塗装、電着塗装等の塗装、電解めっき、浸漬めっき、無電解めっき等の湿式めっき法や、熱CVD、プラズマCVD、レーザーCVD等の化学蒸着法(CVD)、真空蒸着、スパッタリング、イオンプレーティング法、レーザーアブレーション等の乾式めっき法(気相成膜法)、溶射等が挙げられるが、乾式めっき法(気相成膜法)が好ましい。
The formation method of the
機能性膜6の形成方法として乾式めっき法(気相成膜法)を適用することにより、均一な膜厚を有し、均質で、かつ、調色膜5等との密着性が特に優れた機能性膜6を確実に形成することができる。
By applying a dry plating method (vapor phase film forming method) as a method for forming the
また、機能性膜6の形成方法として乾式めっき法(気相成膜法)を適用することにより、形成すべき機能性膜6が比較的薄いものであっても、膜厚のばらつきを十分に小さいものとすることができる。
In addition, by applying a dry plating method (vapor phase film formation method) as a method for forming the
また、機能性膜6の形成方法として乾式めっき法(気相成膜法)を適用することにより、機能性膜6中の各部位における不本意な組成のばらつきをより効果的に抑制することができる。
In addition, by applying a dry plating method (vapor phase film formation method) as a method for forming the
上記のような乾式めっき法(気相成膜法)の中でも、イオンプレーティングが特に好ましい。 Among the dry plating methods (vapor phase film forming methods) as described above, ion plating is particularly preferable.
機能性膜6の形成方法としてイオンプレーティングを適用することにより、上記のような効果はより顕著なものとなる。すなわち、機能性膜6の形成方法としてイオンプレーティングを適用することにより、均一な膜厚を有し、均質で、かつ、調色膜5等との密着性が特に優れた機能性膜6をより確実に形成することができる。
By applying ion plating as a method for forming the
また、機能性膜6の形成方法としてイオンプレーティングを適用することにより、形成すべき機能性膜6が比較的薄いものであっても、膜厚のばらつきを特に小さいものとすることができる。
Further, by applying ion plating as a method for forming the
また、機能性膜6の形成方法としてイオンプレーティングを適用することにより、機能性膜6中の各部位における不本意な組成のばらつきをより効果的に抑制することができる。
In addition, by applying ion plating as a method for forming the
また、機能性膜6は、調色膜5と同一の成膜方法で形成されたものであるのが好ましい。例えば、調色膜5がイオンプレーティングにより形成されたものである場合、機能性膜6もイオンプレーティングにより形成されたものであるのが好ましい。
The
これにより、例えば、ターゲットや雰囲気ガス(反応ガス)等を変更することにより、基材2を装置内から取り出すことなく、同一装置内で、調色膜5と機能性膜6とを引き続いて形成することができる。これにより、調色膜5と機能性膜6との密着性が特に優れたものとなるとともに、時計用部品10の生産性も向上する。
Thereby, for example, the toning
[第2実施形態]
次に、第2実施形態の時計用部品について説明する。
図2は、本発明の時計用部品の第2実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Second Embodiment]
Next, the timepiece part of the second embodiment will be described.
FIG. 2 is a cross-sectional view schematically showing a second embodiment of the timepiece part of the invention. In the following description, differences from the above-described embodiment will be mainly described, and description of similar matters will be omitted.
本実施形態の時計用部品10は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料のいずれをも実質的に含まない材料で構成された基材2と、第1の材料で構成され基材2を被覆する被膜3と、被膜3を被覆する調色膜5と、調色膜5を被覆する機能性膜6とがこの順で積層されている。言い換えると、本実施形態の時計用部品10では、金属光沢部1は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料のいずれをも実質的に含まない材料で構成された基材2上に設けられた被膜3である。
The
このように、基材2とは異なる部位として、金属光沢部1としての被膜3を設けることにより、基材2の構成材料等の選択の幅が広がる。例えば、ガラス、セラミックス、プラスチック材料等も基材2の構成材料として好適に用いることができ、時計用部品10の成形方法の選択の幅、時計における時計用部品10の配置部位の選択の幅等をより広いものとすることができる。また、時計用部品10全体としての、金属材料の使用量をより少ないものとすることができる。これにより、例えば、時計用部品10の軽量化に寄与することができる。また、時計用部品10の電波透過性を優れたものとすることができ、例えば、時計用部品10を電波時計等に好適に適用することができる。また、基材2として光透過性を有する材料で構成されたものを用い、被膜3の厚さを比較的薄いものとすることにより、時計用部品10全体として、優れた光沢感、審美性を発揮しつつ、十分な光透過性を確保することができる。その結果、時計用部品10を、例えば、風防ガラスやスケルトンタイプの裏蓋のように光透過性が求められる部品に好適に適用することができる。
Thus, by providing the
≪基材≫
本実施形態において、基材2の構成材料としては、例えば、サファイアガラス、ソーダガラス、結晶性ガラス、石英ガラス、鉛ガラス、カリウムガラス、ホウケイ酸ガラス、無アルカリガラス等のガラス材料、アルミナ、チタニア等のセラミックス材料、各種熱可塑性樹脂、各種硬化性樹脂等のプラスチック材料等が挙げられる。
≪Base material≫
In the present embodiment, examples of the constituent material of the
なお、本実施形態において、基材2は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料のいずれをも実質的に含まないものであればよく、少量であれば、例えば、フィラーや不可避成分等として、Tiの窒化物もしくは炭化物、Crの窒化物もしくは炭化物、または、金属材料を含んでいてもよい。例えば、基材2は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料を、これらの含有率の和が5質量%以下の含有率で含んでいてもよい。このような場合、前述したような効果が十分に得られる。
In the present embodiment, the
≪被膜(金属光沢部)≫
本実施形態においては、被膜3が金属光沢部1として機能する。
被膜3の構成材料としては、前述した実施形態での基材2(金属光沢部1)で挙げたものと同様である。すなわち、本実施形態において、被膜3は、第1の材料で構成されている。
≪Coating (metallic glossy part) ≫
In the present embodiment, the
The constituent material of the
被膜3の厚さは、30nm以上5000nm以下であるのが好ましく、40nm以上3000nm以下であるのがより好ましく、50nm以上500nm以下であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10全体としての光沢感、審美性をより優れたものとすることができるとともに、被膜3の不本意な剥離等をより効果的に防止し、時計用部品10の耐久性をより優れたものとすることができるとともに、時計用部品10の生産性をより優れたものとすることができる。
As a result, the glossiness and aesthetics of the
被膜3は、各部位で均一な組成を有するものであってもよいし、組成の異なる部位を有するものであってもよい。例えば、被膜3は、組成が傾斜的に変化する傾斜材料(例えば、厚さ方向に組成が傾斜的に変化する傾斜材料等)で構成されたもの等であってもよい。
The
被膜3の形成方法は、特に限定されず、例えば、スピンコート、ディッピング、刷毛塗り、噴霧塗装、静電塗装、電着塗装等の塗装、電解めっき、浸漬めっき、無電解めっき等の湿式めっき法や、熱CVD、プラズマCVD、レーザーCVD等の化学蒸着法(CVD)、真空蒸着、スパッタリング、イオンプレーティング、レーザーアブレーション等の乾式めっき法(気相成膜法)、溶射等が挙げられるが、乾式めっき法(気相成膜法)が好ましい。
The method for forming the
被膜3の形成方法として乾式めっき法(気相成膜法)を適用することにより、均一な膜厚を有し、均質で、かつ、基材2等との密着性が特に優れた被膜3を確実に形成することができる。その結果、時計用部品10の審美的外観、耐久性を特に優れたものとすることができる。
By applying a dry plating method (vapor phase film forming method) as a method for forming the
また、被膜3の形成方法として乾式めっき法(気相成膜法)を適用することにより、形成すべき被膜3が比較的薄いものであっても、膜厚のばらつきを十分に小さいものとすることができる。このため、時計用部品10の信頼性を向上させる上でも有利である。
Further, by applying a dry plating method (vapor phase film forming method) as a method of forming the
上記のような乾式めっき法(気相成膜法)の中でも、イオンプレーティングが特に好ましい。 Among the dry plating methods (vapor phase film forming methods) as described above, ion plating is particularly preferable.
被膜3の形成方法としてイオンプレーティングを適用することにより、上記のような効果はより顕著なものとなる。すなわち、被膜3の形成方法としてイオンプレーティングを適用することにより、均一な膜厚を有し、均質で、かつ、基材2等との密着性が特に優れた被膜3をより確実に形成することができる。その結果、最終的に得られる時計用部品10の審美的外観、耐久性をさらに優れたものとすることができる。
By applying ion plating as a method for forming the
また、被膜3の形成方法としてイオンプレーティングを適用することにより、形成すべき被膜3が比較的薄いものであっても、膜厚のばらつきを特に小さいものとすることができる。
Further, by applying ion plating as a method for forming the
[第3実施形態]
次に、第3実施形態の時計用部品について説明する。
図3は、本発明の時計用部品の第3実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Third Embodiment]
Next, the timepiece part of the third embodiment will be described.
FIG. 3 is a cross-sectional view schematically showing a third embodiment of the timepiece part of the invention. In the following description, differences from the above-described embodiment will be mainly described, and description of similar matters will be omitted.
本実施形態の時計用部品10では、基材2が光透過性を有するものであり、機能性膜6と、基材2と、調色膜5と、被膜3(金属光沢部1)とがこの順で積層されている。
In the
このように、時計用部品10を構成する各部材の配置は、前述したものと異なるものであってもよい。
Thus, the arrangement of the members constituting the
また、本実施形態のように、機能性膜6と、基材2と、調色膜5と、被膜3(金属光沢部1)とがこの順で積層されていることにより、観察者に、所定の厚みを有し、光透過性を有する機能性膜6および基材2を介して、調色膜5、被膜3(金属光沢部1)を視認させることができるため、時計用部品10の外観に奥行き感を持たせることができる。
In addition, as in the present embodiment, the
基材2および機能性膜6は、いずれも光透過性を有するものであればよいが、基材2および機能性膜6についての可視光の透過率(例えば、波長550nmの光の透過率)は、それぞれ、80%以上であるのが好ましく、85%以上であるのがより好ましく、90%以上であるのがさらに好ましい。
The
これにより、上記のような配置にすることによる効果がより顕著に発揮され、時計用部品10の審美性をより優れたものとすることができる。
Thereby, the effect by making it arrange | positioned as mentioned above is exhibited more notably, and the aesthetics of the
[第4実施形態]
次に、第4実施形態の時計用部品について説明する。
図4は、本発明の時計用部品の第4実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Fourth Embodiment]
Next, the timepiece part of the fourth embodiment will be described.
FIG. 4 is a cross-sectional view schematically showing a fourth embodiment of the timepiece part of the invention. In the following description, differences from the above-described embodiment will be mainly described, and description of similar matters will be omitted.
本実施形態の時計用部品10では、第1の材料で構成された基材2(金属光沢部1の第1の領域11)と、第1の材料で構成された被膜3(金属光沢部1の第2の領域12)と、被膜3を被覆する調色膜5と、機能性膜6とがこの順で積層されており、基材2と被膜3とは、互いに異なる材料で構成されている。言い換えると、本実施形態では、金属光沢部1は、第1の領域11と、第1の領域11よりも調色膜5側に、第1の領域11と重ね合わせて層状に設けられた第2の領域12とを有するものであり、第2の領域12は、第1の領域11とは異なる材料で構成されたものである。
In the
これにより、微妙な色調整を行うことができ、時計用部品10全体としての色再現域をより広いものとすることができ、時計用部品10の審美性をより優れたものとすることができる。また、全体としての金属の使用量をさらに抑制しつつ、時計用部品10の審美性を優れたものとすることができる。
Thereby, delicate color adjustment can be performed, the color reproduction range of the
第1の領域11の厚さは、20nm以上であるのが好ましく、25nm以上であるのがより好ましく、30nm以上であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10全体としての光沢感、審美性をより優れたものとすることができる。
Thereby, the glossiness and aesthetics of the
第2の領域12の厚さは、30nm以下であるのが好ましく、20nm以下であるのがより好ましく、10nm以下であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10の審美性をより優れたものとすることができるとともに、第2の領域12の不本意な剥離等をより効果的に防止することができ、時計用部品10の耐久性、信頼性をより優れたものとすることができ、また、時計用部品10の生産性をより優れたものとすることができる。
Thereby, while being able to make the aesthetics of the
第1の領域11および第2の領域12は、それぞれ、第1の材料で構成されたものであればよく、その材料の組み合わせは特に限定されず、第1の領域11および第2の領域12は、同一の組成を有するものであってもよいし、異なる組成を有するものであってもよいが、第1の領域11がTiNで構成されたものであり、かつ、第2の領域12がTi、Cr、AlまたはFeを含む金属材料で構成されたものであるのが好ましい。
これにより、高級感が特に高い金色を表現することができる。
The
This makes it possible to express a gold color with a particularly high-class feeling.
[第5実施形態]
次に、第5実施形態の時計用部品について説明する。
図5は、本発明の時計用部品の第5実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Fifth Embodiment]
Next, the timepiece part of the fifth embodiment will be described.
FIG. 5 is a sectional view schematically showing a fifth embodiment of the timepiece part of the invention. In the following description, differences from the above-described embodiment will be mainly described, and description of similar matters will be omitted.
本実施形態の時計用部品10では、第1の材料以外の材料で構成された基材2と、第1の材料で構成された被膜3(金属光沢部1)と、被膜3(金属光沢部1)を被覆する調色膜5と、調色膜5を被覆する機能性膜6とがこの順で積層されており、金属光沢部1は、第1の領域11と、第1の領域11よりも調色膜5側に、第1の領域11と重ね合わせて層状に設けられた第2の領域12とを有するものであり、第2の領域12は、第1の領域11とは異なる材料で構成されたものである。すなわち、基材2が金属光沢部1を構成するものではなく、かつ、金属光沢部1としての被膜3が、第1の領域11(第1の層)と、第2の領域12(第2の層)とを有するものであること以外は、前述した第4実施形態と同様である。
In the
第1の領域11が層状に設けられたものであることにより、基材2、第1の領域11の構成材料等の選択の幅が広がり、例えば、鋳造等が困難な材料でも好適に用いることができる。また、時計用部品10全体としての金属材料の使用量をより少ないものとすることができる。
Since the
第1の領域11の厚さは、20nm以上1500nm以下であるのが好ましく、25nm以上1000nm以下であるのがより好ましく、30nm以上500nm以下であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10全体としての光沢感、審美性をより優れたものとすることができるとともに、第1の領域11の不本意な剥離等をより効果的に防止し、時計用部品10の耐久性をより優れたものとすることができるとともに、時計用部品10の生産性をより優れたものとすることができる。
As a result, the glossiness and aesthetics of the
[第6実施形態]
次に、第6実施形態の時計用部品について説明する。
図6は、本発明の時計用部品の第6実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Sixth Embodiment]
Next, the timepiece part of the sixth embodiment will be described.
FIG. 6 is a cross-sectional view schematically showing a sixth embodiment of the timepiece part of the invention. In the following description, differences from the above-described embodiment will be mainly described, and description of similar matters will be omitted.
本実施形態の時計用部品10では、基材2が光透過性を有するものであり、機能性膜6と、基材2と、調色膜5と、第2の領域12および第1の領域11を有する被膜3(金属光沢部1)とがこの順で積層されている。すなわち、本実施形態の時計用部品10は、構成部材の配置が異なること以外は、前記第5実施形態と同様である。また、本実施形態の時計用部品10は、被膜3(金属光沢部1)が異なること以外は、前記第3実施形態と同様である。
In the
時計用部品10は、時計を構成する部品であればいかなるものであってもよいが、時計の使用時において外部から視認しうる部品であるのが好ましく、具体的には、風防ガラス、ケース、ベゼル、裏蓋、バンド(バンドの駒、バンド中留、尾錠、バックル、バンド・バングル着脱機構等を含む)、文字板、時計用針、ローター、りゅうず(例えば、ネジロック式りゅうず等)、ボタン、ダイヤルリング、見切板等が挙げられ、中でも、風防ガラス、ケースまたはバンドであるのが好ましい。
The
これらの部品(時計用部品)は、時計全体の外観に大きな影響を与えるものであるため、これらの部品に本発明が適用されることにより、時計全体としての審美性をより優れたものとすることができる。また、これらの部品(時計用部品)は、通常、時計において、外部に露出する部品である。このような部品には、前述したような機能性膜が有することにより発揮される機能が特に強く求められる。したがって、これらの部品に本発明が適用されることにより、前述したような本発明による効果がより顕著に発揮される。 Since these parts (parts for watches) have a great influence on the appearance of the entire watch, the present invention is applied to these parts, thereby improving the aesthetics of the watch as a whole. be able to. These parts (timepiece parts) are usually parts exposed to the outside in a timepiece. Such a component is particularly strongly required to have a function exhibited by the functional film as described above. Therefore, by applying the present invention to these components, the effects of the present invention as described above are more remarkably exhibited.
《時計》
次に、本発明の時計について説明する。
図7は、本発明の時計(腕時計)の好適な実施形態を模式的に示す部分断面図である。
"clock"
Next, the timepiece of the invention will be described.
FIG. 7 is a partial cross-sectional view schematically showing a preferred embodiment of the timepiece (watch) of the present invention.
本実施形態の腕時計(時計)W10は、胴(ケース)W22と、裏蓋W23と、ベゼル(縁)W24と、ガラス板(風防ガラス)W25とを備えている。また、ケースW22内には、図示しないムーブメント(例えば、文字板、針付きのもの)が収納されている。 The wristwatch (clock) W10 of the present embodiment includes a trunk (case) W22, a back cover W23, a bezel (edge) W24, and a glass plate (windshield) W25. In addition, in the case W22, a movement (not shown) (for example, one with a dial and a needle) is accommodated.
胴W22には巻真パイプW26が嵌入・固定され、この巻真パイプW26内にはりゅうずW27の軸部W271が回転可能に挿入されている。 A winding stem pipe W26 is fitted and fixed to the trunk W22, and a shaft portion W271 of a crown W27 is rotatably inserted into the winding stem pipe W26.
胴W22とベゼルW24とは、プラスチックパッキンW28により固定され、ベゼルW24とガラス板W25とはプラスチックパッキンW29により固定されている。 The body W22 and the bezel W24 are fixed by a plastic packing W28, and the bezel W24 and the glass plate W25 are fixed by a plastic packing W29.
また、胴W22に対し裏蓋W23が嵌合(または螺合)されており、これらの接合部(シール部)W50には、リング状のゴムパッキン(裏蓋パッキン)W40が圧縮状態で介挿されている。この構成によりシール部W50が液密に封止され、防水機能が得られる。 Further, a back cover W23 is fitted (or screwed) to the body W22, and a ring-shaped rubber packing (back cover packing) W40 is inserted in a compressed state at these joint portions (seal portions) W50. Has been. With this configuration, the seal portion W50 is sealed in a liquid-tight manner, and a waterproof function is obtained.
りゅうずW27の軸部W271の途中の外周には溝W272が形成され、この溝W272内にはリング状のゴムパッキン(りゅうずパッキン)W30が嵌合されている。ゴムパッキンW30は巻真パイプW26の内周面に密着し、該内周面と溝W272の内面との間で圧縮される。この構成により、りゅうずW27と巻真パイプW26との間が液密に封止され防水機能が得られる。なお、りゅうずW27を回転操作したとき、ゴムパッキンW30は軸部W271と共に回転し、巻真パイプW26の内周面に密着しながら周方向に摺動する。 A groove W272 is formed on the outer periphery of the shaft W271 of the crown W27, and a ring-shaped rubber packing (crown packing) W30 is fitted in the groove W272. The rubber packing W30 is in close contact with the inner peripheral surface of the winding stem pipe W26 and is compressed between the inner peripheral surface and the inner surface of the groove W272. With this configuration, the space between the crown W27 and the winding stem pipe W26 is sealed in a liquid-tight manner to obtain a waterproof function. When the crown W27 is rotated, the rubber packing W30 rotates together with the shaft portion W271 and slides in the circumferential direction while being in close contact with the inner peripheral surface of the winding stem pipe W26.
本発明の時計としての腕時計W10は、その構成部品のうち少なくとも1つが前述したような本発明の時計用部品で構成されたものである。言い換えると、本発明の時計は、本発明の時計用部品を備えたものである。 The wristwatch W10 as a timepiece of the present invention is constituted by at least one of the constituent parts of the timepiece part of the present invention as described above. In other words, the timepiece of the present invention includes the timepiece component of the present invention.
これにより、貴金属を主材料として使用しなくても、優れた外観(金属光沢を呈する外観)を有する時計W10を提供することができる。 Thereby, even if it uses no precious metal as a main material, the timepiece W10 which has the outstanding external appearance (appearance which exhibits metallic luster) can be provided.
以上、本発明の好適な実施形態について説明したが、本発明は、これらに限定されるものではない。 As mentioned above, although preferred embodiment of this invention was described, this invention is not limited to these.
例えば、本発明の時計用部品、時計では、各部の構成は、同様の機能を発揮する任意の構成のものに置換することができ、また、任意の構成を付加することもできる。
例えば、金属光沢部と調色膜との間や、基材と被膜との間には、少なくとも1層の中間層を有していてもよい。
For example, in the timepiece component and timepiece of the present invention, the configuration of each part can be replaced with any configuration that exhibits the same function, and any configuration can be added.
For example, at least one intermediate layer may be provided between the metallic gloss portion and the toning film, or between the base material and the coating.
また、前述した実施形態では、機能性膜が、時計用部材の外表面を構成する場合について代表的に説明したが、機能性膜は、例えば、金属光沢部と調色膜との間に配置されたものであってもよいし、光透過性を有する基材と調色膜との間に設けられたものであってもよい。 Further, in the above-described embodiment, the case where the functional film constitutes the outer surface of the timepiece member has been described as a representative example. However, the functional film is disposed, for example, between the metallic gloss portion and the toning film. It may be provided, or may be provided between a base material having optical transparency and a toning film.
また、前述した第4、第5、第6実施形態では、金属光沢部は、第1の領域および第2の領域を有するものとして説明したが、さらに、これらとは異なる第3の領域を有していてもよい。 In the fourth, fifth, and sixth embodiments described above, the metallic gloss portion has been described as having the first region and the second region, but further has a third region different from these. You may do it.
また、前述した実施形態では、金属光沢部の一方の面側に調色膜が設けられた構成について代表的に説明したが、金属光沢部の両側の面にそれぞれ調色膜が設けられていてもよい。 Further, in the above-described embodiment, the configuration in which the toning film is provided on one surface side of the metallic glossy portion has been representatively described. However, the toning film is provided on both sides of the metallic glossy portion, respectively. Also good.
また、前述した実施形態では、金属光沢部の一方の面側に機能性膜が設けられた構成について代表的に説明したが、金属光沢部の両側の面にそれぞれ機能性膜が設けられていてもよい。 Further, in the above-described embodiment, the configuration in which the functional film is provided on one surface side of the metallic gloss part has been representatively described. However, the functional film is provided on both sides of the metallic gloss part. Also good.
次に、本発明の具体的実施例について説明する。
[1]時計用部品の製造
(実施例1)
まず、ステンレス鋼(SUS304)を用いて、鋳造により、腕時計ケースの形状を有する基材を作製し、その後、必要箇所を切削、研磨した。
Next, specific examples of the present invention will be described.
[1] Manufacture of watch parts (Example 1)
First, a base material having a watch case shape was produced by casting using stainless steel (SUS304), and then necessary portions were cut and polished.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 Next, this base material was washed. As the cleaning of the substrate, first, alkaline electrolytic degreasing was performed for 30 seconds, then neutralization was performed for 10 seconds, water was washed for 10 seconds, and pure water was washed for 10 seconds.
次に、基材の一部をマスクで被覆した状態で、イオンプレーティングを行うことにより、基材の表面のうち最終的に得られるケース(時計用部品)の外表面(時計としたときに外部に露出する部位)に、金属酸化物の多層膜で構成された調色膜を形成した。 Next, by performing ion plating with a part of the base material covered with a mask, the outer surface of the case (watch part) finally obtained from the surface of the base material (when used as a watch) A toning film composed of a metal oxide multilayer film was formed on a portion exposed to the outside.
調色膜は、基材側から、TiO2層(厚さ47nm)、SiO2層(厚さ110nm)、TiO2層(厚さ66nm)、SiO2層(厚さ45nm)、TiO2層(厚さ20nm)、SiO2層(厚さ108nm)、TiO2層(厚さ78nm)およびSiO2層(厚さ33nm)がこの順に積層されたものとして形成した。 From the base material side, the toning film is composed of a TiO 2 layer (thickness 47 nm), a SiO 2 layer (thickness 110 nm), a TiO 2 layer (thickness 66 nm), a SiO 2 layer (thickness 45 nm), a TiO 2 layer ( A 20 nm thick), SiO 2 layer (108 nm thick), TiO 2 layer (78 nm thick) and SiO 2 layer (33 nm thick) were laminated in this order.
次に、イオンプレーティングにより、調色膜の表面に、SiNで構成された厚さ32nmの機能性膜(硬質膜)を形成し、その後、マスクを除去することにより、時計用部品としての腕時計ケースを得た。 Next, a functional film (hard film) made of SiN and having a thickness of 32 nm is formed on the surface of the toning film by ion plating, and then the mask is removed, whereby the wristwatch as a watch part. Got a case.
(実施例2)
まず、腕時計ケースの形状を有する無機ガラス製の基材を用意した。
(Example 2)
First, an inorganic glass substrate having the shape of a watch case was prepared.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ浸漬脱脂を30秒間行い、その後、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 Next, this base material was washed. As the cleaning of the substrate, first, alkali immersion degreasing was performed for 30 seconds, and then neutralization was performed for 10 seconds, water washing for 10 seconds, and pure water cleaning for 10 seconds.
次に、基材の一部をマスクで被覆した状態で、イオンプレーティングを行うことにより、基材の表面のうち最終的に得られるケース(時計用部品)の外表面(時計としたときに外部に露出する部位)に、TiNで構成された厚さ160nmの被膜(金属光沢部)を形成した。 Next, by performing ion plating with a part of the base material covered with a mask, the outer surface of the case (watch part) finally obtained from the surface of the base material (when used as a watch) A 160 nm-thick film (metallic glossy part) made of TiN was formed on the part exposed to the outside.
引き続き、イオンプレーティングにより、被膜(金属光沢部)の表面に、金属酸化物の多層膜で構成された調色膜を形成した。 Subsequently, a toning film composed of a multilayer film of metal oxide was formed on the surface of the coating (metallic glossy portion) by ion plating.
調色膜は、被膜(金属光沢部)側から、SiO2層(厚さ66nm)、Ta2O5層(厚さ74nm)、SiO2層(厚さ120nm)、Ta2O5層(厚さ71nm)およびSiO2層(厚さ47nm)がこの順に積層されたものとして形成した。 The toning film is composed of a SiO 2 layer (thickness 66 nm), a Ta 2 O 5 layer (thickness 74 nm), a SiO 2 layer (thickness 120 nm), and a Ta 2 O 5 layer (thickness) from the coating (metallic glossy part) side. 71 nm) and a SiO 2 layer (thickness 47 nm) were laminated in this order.
次に、以下のようにして、調色膜の表面に、フッ素含有有機ケイ素化合物で構成された厚さ5nmの機能性膜(防汚膜)を形成し、その後、マスクを除去することにより、時計用部品としての腕時計ケースを得た。
すなわち、まず、フッ素含有有機ケイ素化合物(信越化学工業社製、KY−130(3))をフッ素系溶剤(信越化学工業社製、FRシンナー)で希釈して固形分3質量%となるように調製したものを、スチールウール(日本スチールウール社製、#0、線径0.025mm)0.5gが前もって充填された容器(上方が解放された円筒形の銅製容器、内径16mm×内高さ6mm)に、1.0g充填して、120℃で1時間乾燥した。次に、この銅製容器を、被膜(金属光沢部)および調色膜が形成された基材とともに、真空蒸発装置内に載置し、装置内を0.01Paの圧力とした後、0.6Å/sの膜形成速度(蒸着速度)となるように銅製容器からフッ素含有有機ケイ素化合物を蒸発させた。加熱源としてはモリブデン製抵抗加熱ボートを用いた。
Next, by forming a functional film (antifouling film) having a thickness of 5 nm composed of a fluorine-containing organosilicon compound on the surface of the toning film as follows, and then removing the mask, A watch case was obtained as a watch component.
That is, first, a fluorine-containing organosilicon compound (manufactured by Shin-Etsu Chemical Co., Ltd., KY-130 (3)) is diluted with a fluorine-based solvent (manufactured by Shin-Etsu Chemical Co., Ltd., FR thinner) so as to have a solid content of 3% by mass. The prepared one was pre-filled with 0.5 g of steel wool (manufactured by Nippon Steel Wool Co., # 0, wire diameter 0.025 mm) (cylindrical copper container with open top, inner diameter 16 mm ×
(実施例3)
被膜(金属光沢部)形成時における成膜条件、調色膜形成時における成膜条件、機能性膜の成膜条件を調整することにより、被膜(金属光沢部)、調色膜および機能性膜の構成を表1に示すようにした以外は、前記実施例2と同様にして時計用部品(ケース)を製造した。
(Example 3)
By adjusting the film forming conditions when forming the coating (metallic glossy part), the film forming conditions when forming the toning film, and the film forming conditions of the functional film, the coating (metallic glossing part), the toning film and the functional film A timepiece part (case) was manufactured in the same manner as in Example 2 except that the configuration was changed as shown in Table 1.
(実施例4)
まず、ステンレス鋼(SUS304)を用いて、鋳造により、腕時計ケースの形状を有する基材(金属光沢部の第1の領域)を作製し、その後、必要箇所を切削、研磨した。
Example 4
First, using stainless steel (SUS304), a base material (first region of the metallic luster part) having a watch case shape was produced by casting, and then necessary portions were cut and polished.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 Next, this base material was washed. As the cleaning of the substrate, first, alkaline electrolytic degreasing was performed for 30 seconds, then neutralization was performed for 10 seconds, water was washed for 10 seconds, and pure water was washed for 10 seconds.
次に、基材の一部をマスクで被覆した状態で、イオンプレーティングを行うことにより、基材の表面のうち最終的に得られるケース(時計用部品)の外表面(時計としたときに外部に露出する部位)に、TiNで構成された厚さ160nmの被膜(金属光沢部の第2の領域)を形成した。 Next, by performing ion plating with a part of the base material covered with a mask, the outer surface of the case (watch part) finally obtained from the surface of the base material (when used as a watch) A 160 nm-thick film (second region of the metallic luster part) made of TiN was formed on the part exposed to the outside.
引き続き、イオンプレーティングにより、被膜の表面に、金属酸化物の多層膜で構成された調色膜を形成した。 Subsequently, a toning film composed of a metal oxide multilayer film was formed on the surface of the coating by ion plating.
調色膜は、被膜側から、SiO2層(厚さ82nm)、Ta2O5層(厚さ63nm)およびSiO2層(厚さ91nm)がこの順に積層されたものとして形成した。 Choiromaku from the coating side, is formed as an SiO 2 layer (thickness 82nm), Ta 2 O 5 layer (thickness 63 nm) and SiO 2 layer (thickness 91 nm) are stacked in this order.
次に、イオンプレーティングにより、調色膜の表面に、SiNで構成された厚さ110nmの機能性膜(硬質膜)を形成し、その後、マスクを除去することにより、時計用部品としての腕時計ケースを得た。 Next, a functional film (hard film) made of SiN and having a thickness of 110 nm is formed on the surface of the toning film by ion plating, and then the mask is removed, so that a wristwatch as a watch component is obtained. Got a case.
(実施例5、6)
調色膜形成時における成膜条件、機能性膜形成時における成膜条件を調整することにより、調色膜、機能性膜の構成を表1に示すようにした以外は、前記実施例4と同様にして時計用部品(腕時計ケース)を製造した。
(Examples 5 and 6)
Except that the composition of the toning film and the functional film is as shown in Table 1 by adjusting the film forming conditions at the time of forming the toning film and the film forming conditions at the time of forming the functional film, Similarly, a watch part (watch case) was manufactured.
(実施例7)
まず、腕時計ケースの形状を有する無機ガラス製の基材を用意した。
(Example 7)
First, an inorganic glass substrate having the shape of a watch case was prepared.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ浸漬脱脂を30秒間行い、その後、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 Next, this base material was washed. As the cleaning of the substrate, first, alkali immersion degreasing was performed for 30 seconds, and then neutralization was performed for 10 seconds, water washing for 10 seconds, and pure water cleaning for 10 seconds.
次に、基材の一部をマスクで被覆した状態で、イオンプレーティングを行うことにより、基材の表面のうち最終的に得られるケース(時計用部品)の外表面(時計としたときに外部に露出する部位)に、第1の領域(第1の層)および第2の領域(第2の層)がこの順で積層された積層体としての被膜(金属光沢部)を形成した。 Next, by performing ion plating with a part of the base material covered with a mask, the outer surface of the case (watch part) finally obtained from the surface of the base material (when used as a watch) A coating (metal gloss part) as a laminate in which the first region (first layer) and the second region (second layer) were laminated in this order was formed on the part exposed to the outside.
第1の領域(第1の層)は、TiNで構成されたものであり、厚さが100nmのものであった。また、第2の領域(第2の層)は、Alで構成されたものであり、厚さが5nmのものであった。 The first region (first layer) was made of TiN and had a thickness of 100 nm. The second region (second layer) was made of Al and had a thickness of 5 nm.
引き続き、イオンプレーティングにより、被膜(金属光沢部)の表面に、金属酸化物の多層膜で構成された調色膜を形成した。 Subsequently, a toning film composed of a multilayer film of metal oxide was formed on the surface of the coating (metallic glossy portion) by ion plating.
調色膜は、被膜(金属光沢部)側から、SiO2層(厚さ109nm)、Ta2O5層(厚さ65nm)およびSiO2層(厚さ42nm)がこの順に積層されたものとして形成した。 The toning film is composed of an SiO 2 layer (thickness 109 nm), a Ta 2 O 5 layer (thickness 65 nm), and an SiO 2 layer (thickness 42 nm) laminated in this order from the coating (metallic glossy part) side. Formed.
次に、以下のようにして、調色膜の表面に、フッ素含有有機ケイ素化合物で構成された厚さ5nmの機能性膜(防汚膜)を形成し、その後、マスクを除去することにより、時計用部品としての腕時計ケースを得た。
すなわち、まず、フッ素含有有機ケイ素化合物(信越化学工業社製、KY−130(3))をフッ素系溶剤(信越化学工業社製、FRシンナー)で希釈して固形分3質量%となるように調製したものを、スチールウール(日本スチールウール社製、#0、線径0.025mm)0.5gが前もって充填された容器(上方が解放された円筒形の銅製容器、内径16mm×内高さ6mm)に、1.0g充填して、120℃で1時間乾燥した。次に、この銅製容器を、被膜(金属光沢部)および調色膜が形成された基材とともに、真空蒸発装置内に載置し、装置内を0.01Paの圧力とした後、0.6Å/sの膜形成速度(蒸着速度)となるように銅製容器からフッ素含有有機ケイ素化合物を蒸発させた。加熱源としてはモリブデン製抵抗加熱ボートを用いた。
Next, by forming a functional film (antifouling film) having a thickness of 5 nm composed of a fluorine-containing organosilicon compound on the surface of the toning film as follows, and then removing the mask, A watch case was obtained as a watch component.
That is, first, a fluorine-containing organosilicon compound (manufactured by Shin-Etsu Chemical Co., Ltd., KY-130 (3)) is diluted with a fluorine-based solvent (manufactured by Shin-Etsu Chemical Co., Ltd., FR thinner) so as to have a solid content of 3% by mass. The prepared one was pre-filled with 0.5 g of steel wool (manufactured by Nippon Steel Wool Co., # 0, wire diameter 0.025 mm) (cylindrical copper container with open top, inner diameter 16 mm ×
(実施例8)
まず、ステンレス鋼(SUS304)を用いて、鋳造により、腕時計ケースの形状を有する基材(金属光沢部の第1の領域)を作製し、その後、必要箇所を切削、研磨した。
(Example 8)
First, using stainless steel (SUS304), a base material (first region of the metallic luster part) having a watch case shape was produced by casting, and then necessary portions were cut and polished.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 Next, this base material was washed. As the cleaning of the substrate, first, alkaline electrolytic degreasing was performed for 30 seconds, then neutralization was performed for 10 seconds, water was washed for 10 seconds, and pure water was washed for 10 seconds.
次に、基材の一部をマスクで被覆した状態で、イオンプレーティングを行うことにより、基材の表面のうち最終的に得られるケース(時計用部品)の外表面(時計としたときに外部に露出する部位)に、TiNで構成された厚さ160nmの被膜(金属光沢部の第2の領域)を形成した。 Next, by performing ion plating with a part of the base material covered with a mask, the outer surface of the case (watch part) finally obtained from the surface of the base material (when used as a watch) A 160 nm-thick film (second region of the metallic luster part) made of TiN was formed on the part exposed to the outside.
引き続き、イオンプレーティングにより、被膜の表面に、金属酸化物の多層膜で構成された調色膜を形成した。 Subsequently, a toning film composed of a metal oxide multilayer film was formed on the surface of the coating by ion plating.
調色膜は、被膜側から、SiO2層(厚さ70nm)、Nb2O5層(厚さ60nm)、SiO2層(厚さ130nm)およびNb2O5層(厚さ42nm)がこの順に積層されたものとして形成した。 The toning film is composed of the SiO 2 layer (thickness 70 nm), the Nb 2 O 5 layer (thickness 60 nm), the SiO 2 layer (thickness 130 nm) and the Nb 2 O 5 layer (thickness 42 nm) from the coating side. It formed as what was laminated | stacked in order.
次に、イオンプレーティングにより、調色膜の表面に、SiNで構成された厚さ45nmの機能性膜(硬質膜)を形成し、その後、マスクを除去することにより、時計用部品としての腕時計ケースを得た。 Next, a functional film (hard film) made of SiN and having a thickness of 45 nm is formed on the surface of the toning film by ion plating, and then the mask is removed, so that a wristwatch as a watch component is obtained. Got a case.
(実施例9)
まず、ステンレス鋼(SUS304)を用いて、鋳造により、腕時計ケースの形状を有する基材(金属光沢部の第1の領域)を作製し、その後、必要箇所を切削、研磨した。
Example 9
First, using stainless steel (SUS304), a base material (first region of the metallic luster part) having a watch case shape was produced by casting, and then necessary portions were cut and polished.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 Next, this base material was washed. As the cleaning of the substrate, first, alkaline electrolytic degreasing was performed for 30 seconds, then neutralization was performed for 10 seconds, water was washed for 10 seconds, and pure water was washed for 10 seconds.
次に、基材の一部をマスクで被覆した状態で、イオンプレーティングを行うことにより、基材の表面のうち最終的に得られるケース(時計用部品)の外表面(時計としたときに外部に露出する部位)に、TiNで構成された厚さ160nmの被膜(金属光沢部の第2の領域)を形成した。 Next, by performing ion plating with a part of the base material covered with a mask, the outer surface of the case (watch part) finally obtained from the surface of the base material (when used as a watch) A 160 nm-thick film (second region of the metallic luster part) made of TiN was formed on the part exposed to the outside.
引き続き、イオンプレーティングにより、被膜の表面に、金属酸化物の多層膜で構成された調色膜を形成した。 Subsequently, a toning film composed of a metal oxide multilayer film was formed on the surface of the coating by ion plating.
調色膜は、被膜側から、SiO2層(厚さ65nm)、ZrO2層(厚さ67nm)、SiO2層(厚さ130nm)、ZrO2層(厚さ78nm)、SiO2層(厚さ130nm)、ZrO2層(厚さ94nm)およびSiO2層(厚さ60nm)がこの順に積層されたものとして形成した。 Choiromaku from the coating side, SiO 2 layer (thickness 65 nm), ZrO 2 layer (thickness 67 nm), SiO 2 layer (thickness 130 nm), ZrO 2 layer (thickness 78 nm), SiO 2 layer (thickness 130 nm), a ZrO 2 layer (thickness 94 nm), and a SiO 2 layer (thickness 60 nm) were laminated in this order.
次に、以下のようにして、調色膜の表面に、フッ素含有有機ケイ素化合物で構成された厚さ5nmの機能性膜(防汚膜)を形成し、その後、マスクを除去することにより、時計用部品としての腕時計ケースを得た。
すなわち、まず、フッ素含有有機ケイ素化合物(信越化学工業社製、KY−130(3))をフッ素系溶剤(信越化学工業社製、FRシンナー)で希釈して固形分3質量%となるように調製したものを、スチールウール(日本スチールウール社製、#0、線径0.025mm)0.5gが前もって充填された容器(上方が解放された円筒形の銅製容器、内径16mm×内高さ6mm)に、1.0g充填して、120℃で1時間乾燥した。次に、この銅製容器を、被膜(金属光沢部)および調色膜が形成された基材とともに、真空蒸発装置内に載置し、装置内を0.01Paの圧力とした後、0.6Å/sの膜形成速度(蒸着速度)となるように銅製容器からフッ素含有有機ケイ素化合物を蒸発させた。加熱源としてはモリブデン製抵抗加熱ボートを用いた。
Next, by forming a functional film (antifouling film) having a thickness of 5 nm composed of a fluorine-containing organosilicon compound on the surface of the toning film as follows, and then removing the mask, A watch case was obtained as a watch component.
That is, first, a fluorine-containing organosilicon compound (manufactured by Shin-Etsu Chemical Co., Ltd., KY-130 (3)) is diluted with a fluorine-based solvent (manufactured by Shin-Etsu Chemical Co., Ltd., FR thinner) so as to have a solid content of 3% by mass. The prepared one was pre-filled with 0.5 g of steel wool (manufactured by Nippon Steel Wool Co., # 0, wire diameter 0.025 mm) (cylindrical copper container with open top, inner diameter 16 mm ×
(実施例10)
被膜(金属光沢部の第2の領域)の成膜条件、調色膜の成膜条件、機能性膜の成膜条件を調整することにより、構成を表1に示すようにした以外は、前記実施例9と同様にして時計用部品(腕時計ケース)を製造した。
(Example 10)
Except that the configuration is as shown in Table 1 by adjusting the film formation conditions of the coating film (second region of the metallic luster part), the film formation conditions of the toning film, and the film formation conditions of the functional film, A watch part (watch case) was manufactured in the same manner as in Example 9.
(実施例11、12)
被膜(金属光沢部の第2の領域)の成膜条件、調色膜の成膜条件、機能性膜の成膜方法、成膜条件を調整することにより、構成を表1に示すようにした以外は、前記実施例9と同様にして時計用部品(腕時計ケース)を製造した。
(Examples 11 and 12)
The configuration is shown in Table 1 by adjusting the film forming conditions of the coating (second region of the metallic luster part), the film forming conditions of the toning film, the film forming method of the functional film, and the film forming conditions. A watch part (watch case) was manufactured in the same manner as in Example 9 except for the above.
(実施例13)
まず、文字板形状を有するポリカーボネート製の基材を用意した。
(Example 13)
First, a polycarbonate substrate having a dial shape was prepared.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ浸漬脱脂を30秒間行い、その後、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 Next, this base material was washed. As the cleaning of the substrate, first, alkali immersion degreasing was performed for 30 seconds, and then neutralization was performed for 10 seconds, water washing for 10 seconds, and pure water cleaning for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、金属酸化物の多層膜で構成された調色膜を形成した。 Next, a toning film composed of a multilayer film of metal oxide was formed on one surface of the substrate by ion plating.
調色膜は、基材側から、SiO2層(厚さ212nm)、Al2O3層(厚さ70nm)、SiO2層(厚さ235nm)、Al2O3層(厚さ78nm)、SiO2層(厚さ88nm)、TiO2層(厚さ35nm)、SiO2層(厚さ31nm)、TiO2層(厚さ62nm)、SiO2層(厚さ105nm)およびTiO2層(厚さ50nm)がこの順に積層されたものとして形成した。 From the substrate side, the toning film is composed of SiO 2 layer (thickness 212 nm), Al 2 O 3 layer (thickness 70 nm), SiO 2 layer (thickness 235 nm), Al 2 O 3 layer (thickness 78 nm), SiO 2 layer (thickness 88 nm), TiO 2 layer (thickness 35 nm), SiO 2 layer (thickness 31 nm), TiO 2 layer (thickness 62 nm), SiO 2 layer (thickness 105 nm) and TiO 2 layer (thickness) 50 nm) was laminated in this order.
引き続き、イオンプレーティングにより、調色膜の表面に、CrCで構成された厚さ90nmの被膜(金属光沢部)を形成した。 Subsequently, a 90 nm-thick film (metallic glossy part) made of CrC was formed on the surface of the toning film by ion plating.
その後、基材の他方の面(前記調色膜および被膜(金属光沢部)が形成された面とは反対側の表面)に、イオンプレーティングにより、HfO2層(厚さ12nm)およびSiO2層(厚さ28nm)をこの順に積層し、さらに、引き続いて行ったイオンプレーティングにより、SiO2層(厚さ28nm)の表面に、SiNで構成された厚さ120nmの機能性膜を形成した。 Thereafter, an HfO 2 layer (thickness: 12 nm) and SiO 2 are formed on the other surface of the substrate (the surface opposite to the surface on which the toning film and the coating (metallic glossy portion) are formed) by ion plating. Layers (thickness 28 nm) were laminated in this order, and a functional film having a thickness of 120 nm composed of SiN was formed on the surface of the SiO 2 layer (thickness 28 nm) by subsequent ion plating. .
引き続き、イオンプレーティングにより、機能性膜の表面に、SiO2層(厚さ84nm)を形成した。
これにより、時計用部品としての文字板を得た。
Subsequently, an SiO 2 layer (thickness 84 nm) was formed on the surface of the functional film by ion plating.
Thus, a dial as a watch part was obtained.
(実施例14)
まず、文字板形状を有するポリカーボネート製の基材を用意した。
(Example 14)
First, a polycarbonate substrate having a dial shape was prepared.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ浸漬脱脂を30秒間行い、その後、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 Next, this base material was washed. As the cleaning of the substrate, first, alkali immersion degreasing was performed for 30 seconds, and then neutralization was performed for 10 seconds, water washing for 10 seconds, and pure water cleaning for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、金属酸化物の多層膜で構成された調色膜を形成した。 Next, a toning film composed of a multilayer film of metal oxide was formed on one surface of the substrate by ion plating.
調色膜は、基材側から、HfO2層(厚さ87nm)、SiO2層(厚さ125nm)、TiO2層(厚さ71nm)およびSiO2層(厚さ64nm)がこの順に積層されたものとして形成した。 In the toning film, an HfO 2 layer (thickness 87 nm), a SiO 2 layer (thickness 125 nm), a TiO 2 layer (thickness 71 nm), and a SiO 2 layer (thickness 64 nm) are laminated in this order from the substrate side. Formed as a dish.
引き続き、イオンプレーティングにより、調色膜の表面に、TiNで構成された厚さ160nmの被膜(金属光沢部)を形成した。 Subsequently, a 160 nm-thick film (metallic gloss part) made of TiN was formed on the surface of the toning film by ion plating.
その後、基材の他方の面(前記調色膜および被膜(金属光沢部)が形成された面とは反対側の表面)に、イオンプレーティングにより、SiO2層(厚さ10nm)を形成した。 Thereafter, an SiO 2 layer (thickness: 10 nm) was formed by ion plating on the other surface of the substrate (the surface opposite to the surface on which the toning film and the coating (metallic glossy portion) were formed). .
次に、SiO2層(厚さ10nm)の表面に、以下のようにして、フッ素含有有機ケイ素化合物で構成された厚さ5nmの機能性膜(防汚膜)を形成し、時計用部品としての文字板を得た。
すなわち、まず、フッ素含有有機ケイ素化合物(信越化学工業社製、KY−130(3))をフッ素系溶剤(信越化学工業社製、FRシンナー)で希釈して固形分3質量%となるように調製したものを、スチールウール(日本スチールウール社製、#0、線径0.025mm)0.5gが前もって充填された容器(上方が解放された円筒形の銅製容器、内径16mm×内高さ6mm)に、1.0g充填して、120℃で1時間乾燥した。次に、この銅製容器を、上記の各層が設けられた基材とともに、真空蒸発装置内に載置し、装置内を0.01Paの圧力とした後、0.6Å/sの膜形成速度(蒸着速度)となるように銅製容器からフッ素含有有機ケイ素化合物を蒸発させた。加熱源としてはモリブデン製抵抗加熱ボートを用いた。
Next, a functional film (antifouling film) having a thickness of 5 nm composed of a fluorine-containing organosilicon compound is formed on the surface of the SiO 2 layer (
That is, first, a fluorine-containing organosilicon compound (manufactured by Shin-Etsu Chemical Co., Ltd., KY-130 (3)) is diluted with a fluorine-based solvent (manufactured by Shin-Etsu Chemical Co., Ltd., FR thinner) so as to have a solid content of 3% by mass. The prepared one was pre-filled with 0.5 g of steel wool (manufactured by Nippon Steel Wool Co., # 0, wire diameter 0.025 mm) (cylindrical copper container with open top, inner diameter 16 mm ×
(実施例15)
調色膜および被膜(金属光沢部)の成膜条件を調整することにより、構成を表1に示すようにした以外は、前記実施例14と同様にして時計用部品(文字板)を製造した。
(Example 15)
A watch component (a dial plate) was manufactured in the same manner as in Example 14 except that the film forming conditions of the toning film and the coating film (metallic glossy part) were adjusted, and the configuration was as shown in Table 1. .
(実施例16)
被膜(金属光沢部の第2の領域)形成時における成膜条件、調色膜形成時における成膜条件、機能性膜形成時における成膜条件を調整することにより、調色膜、機能性膜の構成を表1に示すようにした以外は、前記実施例4と同様にして時計用部品(腕時計ケース)を製造した。
(Example 16)
By adjusting the film forming conditions when forming the coating (second region of the metallic luster part), the film forming conditions when forming the toning film, and the film forming conditions when forming the functional film, the toning film and the functional film A watch part (watch case) was manufactured in the same manner as in Example 4 except that the configuration of the watch was as shown in Table 1.
(比較例1)
調色膜を形成しなかった以外は、前記実施例1と同様にして時計用部品(腕時計ケース)を製造した。
(Comparative Example 1)
A watch part (watch case) was manufactured in the same manner as in Example 1 except that the toning film was not formed.
(比較例2)
機能性膜を形成しなかった以外は、前記比較例1と同様にして時計用部品(腕時計ケース)を製造した。
(Comparative Example 2)
A watch part (watch case) was manufactured in the same manner as Comparative Example 1 except that the functional film was not formed.
(比較例3)
鋳造により、Au製の腕時計ケースの形状の部材を作製し、その後、必要箇所を切削、研磨し、腕時計ケース(時計用部品)を得た。すなわち、本比較例の時計用部品は、金無垢の材料で構成されたものである。
(Comparative Example 3)
A member having the shape of a watch case made of Au was produced by casting, and then a necessary portion was cut and polished to obtain a watch case (watch part). That is, the timepiece part of this comparative example is made of a solid gold material.
各実施例および各比較例の時計用部品の構成を表1にまとめて示す。なお、基材を除く各部位の厚さは、括弧書きで示した。また、表中、無機ガラスをG、SUS304をSUSで示した。また、時計用部品を構成する各部位について、表中に示す成分の含有率は、いずれも、99.9質量%以上であった。 Table 1 summarizes the configurations of the timepiece parts of each example and each comparative example. In addition, the thickness of each site | part except a base material was shown in parenthesis writing. In the table, G represents inorganic glass and SUS304 represents SUS. Moreover, the content rate of the component shown in the table | surface about each site | part which comprises the components for timepieces was all 99.9 mass% or more.
また、前記各実施例のうちTiCで構成された層を有するものについては、いずれも、当該層におけるC(炭素)の含有率は、50質量%以上60質量%以下の範囲内の値であった。 In each of the examples having a layer composed of TiC, the C (carbon) content in the layer is a value within the range of 50% by mass to 60% by mass. It was.
また、前記各実施例のうちTiNで構成された層を有するものについては、いずれも、当該層におけるN(窒素)の含有率は、50質量%以上60質量%以下の範囲内の値であった。 In each of the examples having a layer composed of TiN, the content of N (nitrogen) in the layer is a value within a range of 50% by mass or more and 60% by mass or less. It was.
また、前記各実施例のうちTiCNで構成された層を有するものについては、いずれも、当該層におけるC(炭素)の含有率は、5質量%以上15質量%以下の範囲内の値であり、かつ、当該層におけるN(窒素)の含有率は、1質量%以上5質量%以下の範囲内の値であった。 In each of the above examples, the C (carbon) content in each layer having a layer composed of TiCN is a value within the range of 5% by mass to 15% by mass. And the content rate of N (nitrogen) in the said layer was the value within the range of 1 mass% or more and 5 mass% or less.
[2]評価
上記各実施例および各比較例で製造した各時計用部品について、目視による観察を行った。
[2] Evaluation Each watch part manufactured in each of the above Examples and Comparative Examples was visually observed.
その結果、前記各実施例の時計用部品は、いずれも、高級感にあふれる優れた外観を呈していた。特に、実施例2、4、5、6、7、8、9、11、12、14、15の時計用部品は、比較例3と同様に、高級感のある金色を呈しており、実施例1、3、13では、高級感のある青みがかった光沢を呈する優れた外観が得られた。また、金属光沢部が、Tiの炭窒化物で構成されている実施例10の時計用部品では、ピンクゴールドに類似の高級感のある外観が得られた。また、金属光沢部が、Tiの炭化物で構成されている実施例16の時計用部品では、高級感のある青みのある黒色を呈する優れた外観が得られた。 As a result, all of the timepiece parts of the above-described embodiments exhibited an excellent appearance full of luxury. In particular, the watch parts of Examples 2, 4, 5, 6, 7, 8, 9, 11, 12, 14, and 15 exhibit a high-quality gold color as in Comparative Example 3. In 1, 3, and 13, excellent appearances having a high-quality bluish luster were obtained. Moreover, in the timepiece part of Example 10 in which the metallic luster part was composed of Ti carbonitride, a high-grade appearance similar to pink gold was obtained. Moreover, in the timepiece part of Example 16 in which the metallic luster part was composed of Ti carbide, an excellent appearance with a bluish black with a high-class feeling was obtained.
また、各実施例では、それぞれが有する機能性膜に対応した機能が効果的に発揮されたものであった。 Moreover, in each Example, the function corresponding to the functional film which each has was exhibited effectively.
すなわち、SiNまたはAlNで構成された機能性膜(硬質膜)を有する実施例1、3、4、8、13、16の時計用部品では、耐擦傷性(傷の付き難さ)、耐打痕性(打痕のつき難さ)等が特に優れ、耐久性が特に優れたものであった。また、フッ素含有有機ケイ素化合物で構成された機能性膜(防汚膜)を有する実施例2、5、7、9、10、14、15の時計用部品では、汚れの付着による審美性の低下が効果的に防止されており、汚れが付着した場合であっても、容易に当該汚れを除去することができ、手触り感、防水性、耐擦傷性等にも優れており、機能性膜の調色膜に対する密着性に優れ、時計用部品の耐久性に優れていた。また、光触媒層TiO2で構成した実施例5、11、12や、2−(4−チアゾリル)ベンズイミダゾールで構成された機能性膜(抗菌膜)を有する実施例6の時計用部品では、抗菌性に優れていた。また、標準光源D50を用いたときの、実施例1についてのL*は36.8、a*は42.1、b*は−90.1であり、実施例2についてのL*は84.7、a*は13.2、b*は49.3であり、実施例3についてのL*は42.2、a*は38.0、b*は−87.3であり、実施例4についてのL*は85.4、a*は14.2、b*は40.2であり、実施例5についてのL*は87.5、a*は10.1、b*は41.4であり、実施例6についてのL*は87.5、a*は10.1、b*は41.4であり、実施例7についてのL*は87.6、a*は3.5、b*は41.1であり、実施例8についてのL*は88.5、a*は10.6、b*は41.4であり、実施例9についてのL*は83.8、a*は9.3、b*は42.2であり、実施例10についてのL*は84.9、a*は11.6、b*は22.6であり、実施例11についてのL*は89.3、a*は8.6、b*は36.6であり、実施例12についてのL*は89.5、a*は9.4、b*は38.5であり、実施例13についてのL*は38.0、a*は40.4、b*は−86.5であり、実施例14についてのL*は85.4、a*は8.6、b*は42.8であり、実施例15についてのL*は88.0、a*は10.6、b*は36.9であり、実施例16についてのL*は38.7、a*は2.8、b*は−39.7であった。 That is, in the timepiece parts of Examples 1, 3, 4, 8, 13, and 16 having a functional film (hard film) made of SiN or AlN, the scratch resistance (hardness to scratch) and the hit resistance are reduced. The traceability (difficulty of making a dent) was particularly excellent, and the durability was particularly excellent. Further, in the watch parts of Examples 2, 5, 7, 9, 10, 14, and 15 having the functional film (antifouling film) composed of the fluorine-containing organosilicon compound, the aesthetics are deteriorated due to adhesion of dirt. Is effectively prevented, and even when dirt is adhered, the dirt can be easily removed, and it is excellent in touch feeling, waterproofness, scratch resistance, etc. Excellent adhesion to the toning film and excellent durability of watch parts. Moreover, in the timepiece components of Examples 5, 11, and 12 configured with the photocatalytic layer TiO 2 and the functional film (antibacterial film) configured with 2- (4-thiazolyl) benzimidazole, It was excellent in nature. When the standard light source D50 was used, L * for Example 1 was 36.8, a * was 42.1, b * was −90.1, and L * for Example 2 was 84. 7, a * is 13.2, b * is 49.3, L * for Example 3 is 42.2, a * is 38.0, b * is −87.3, Example 4 L * is 85.4, a * is 14.2 and b * is 40.2. L * is 87.5, a * is 10.1, b * is 41.4 for Example 5. L * for Example 6 is 87.5, a * is 10.1, b * is 41.4, L * for Example 7 is 87.6, a * is 3.5, b * is 41.1, L * for Example 8 is 88.5, a * is 10.6, b * is 41.4, L * for Example 9 is 83.8, a * Is 9.3, b * 42.2, L * for Example 10 is 84.9, a * is 11.6, b * is 22.6, L * for Example 11 is 89.3, a * is 8 .6, b * is 36.6, L * for Example 12 is 89.5, a * is 9.4, b * is 38.5, and L * for Example 13 is 38. 0, a * is 40.4, b * is −86.5, L * for Example 14 is 85.4, a * is 8.6, b * is 42.8, and Example 15 L * is 88.0, a * is 10.6, b * is 36.9, L * is 38.7, a * is 2.8, and b * is −39. 7.
これに対し、比較例1では、高級感に劣った外観しか得られなかった。また、比較例2では、高級感に劣った外観しか得られなかっただけでなく、各実施例の時計用部品が有する機能(高硬度、耐擦傷性、耐打痕性、防汚性、抗菌性等)も発揮されなかった。比較例3については、優れた外観を呈していたものの、時計用部品の製造に多量の貴金属を必要とした。 On the other hand, in Comparative Example 1, only an appearance inferior to a high-class feeling was obtained. Moreover, in Comparative Example 2, not only an appearance that was inferior to a high-class feeling was obtained, but also the functions (high hardness, scratch resistance, dent resistance, antifouling properties, antibacterial properties) of the watch parts of each Example Sex etc.) was not exhibited. Although the comparative example 3 had an excellent appearance, a large amount of noble metal was required for the production of the watch part.
なお、各実施例および比較例1については、機能性膜が設けられた側の面から観察を行った。 In addition, about each Example and Comparative Example 1, it observed from the surface by which the functional film was provided.
基材の形状をバンドに変更した以外は、前記各実施例および各比較例と同様にして時計用部品(バンド)を製造して、前記と同様の評価を行ったところ、前記と同様の結果が得られた。 Except that the shape of the base material was changed to a band, a watch part (band) was manufactured in the same manner as in the above Examples and Comparative Examples, and the same evaluation as described above was performed. was gotten.
また、金属光沢部の材料として、SUS304の代わりに、Al、Cr、Tiを用いた以外は、前記実施例1、5〜7、9、10と同様にして時計用部品を製造して、前記と同様の評価を行ったところ、前記と同様の結果が得られた。 Further, a watch part was manufactured in the same manner as in Examples 1, 5 to 7, 9, and 10 except that Al, Cr, and Ti were used instead of SUS304 as the material for the metallic luster part. As a result of the same evaluation, the same result as above was obtained.
また、第2の領域の構成材料として、Alの代わりに、Ti、Cr、Feを用いた以外は、前記実施例8と同様にして時計用部品を製造して、前記と同様の評価を行ったところ、前記と同様の結果が得られた。 A watch part was manufactured in the same manner as in Example 8 except that Ti, Cr, and Fe were used instead of Al as the constituent material for the second region, and the same evaluation as described above was performed. As a result, the same results as described above were obtained.
また、前記各実施例および各比較例で製造した時計用部品を用いて、図7に示すような腕時計を組み立てた。これらの腕時計にて、上記と同様な評価を行ったところ、上記と同様の結果が得られた。 Further, a wristwatch as shown in FIG. 7 was assembled using the timepiece parts manufactured in the respective Examples and Comparative Examples. When these wristwatches were evaluated in the same manner as described above, the same results as described above were obtained.
10…時計用部品、1…金属光沢部、11…第1の領域、12…第2の領域、2…基材、3…被膜、5…調色膜、51…金属酸化物層、6…機能性膜、W10…腕時計(時計)、W22…胴(ケース)、W23…裏蓋、W24…ベゼル(縁)、W25…ガラス板(風防ガラス)、W26…巻真パイプ、W27…りゅうず、W271…軸部、W272…溝、W28…プラスチックパッキン、W29…プラスチックパッキン、W30…ゴムパッキン(りゅうずパッキン)、W40…ゴムパッキン(裏蓋パッキン)、W50…接合部(シール部)
DESCRIPTION OF
Claims (14)
前記金属光沢部の少なくとも一部を被覆し、金属酸化物を含む材料で構成された複数の層を有する積層体で構成され、色調を調整する機能を有する調色膜と、
前記調色膜の前記金属光沢部に対向する面とは反対の面側に設けられ、特定の機能を付与する機能性膜とを備えることを特徴とする時計用部品。 A metallic luster portion made of a first material including a nitride or carbide of Ti, a nitride or carbide of Cr, or a metallic material and exhibiting metallic luster;
A toning film that covers at least a part of the metallic luster part, is composed of a laminate having a plurality of layers made of a material containing a metal oxide, and has a function of adjusting the color tone;
A timepiece component comprising: a functional film that is provided on a surface opposite to a surface facing the metallic gloss portion of the toning film and that imparts a specific function.