JP2017170534A - Cleaner for removing water scale - Google Patents
Cleaner for removing water scale Download PDFInfo
- Publication number
- JP2017170534A JP2017170534A JP2016055927A JP2016055927A JP2017170534A JP 2017170534 A JP2017170534 A JP 2017170534A JP 2016055927 A JP2016055927 A JP 2016055927A JP 2016055927 A JP2016055927 A JP 2016055927A JP 2017170534 A JP2017170534 A JP 2017170534A
- Authority
- JP
- Japan
- Prior art keywords
- cleaner
- abrasive grains
- scale
- descaling
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、浴室、洗面所、キッチン等における水垢除去に好適な、水垢除去用クリーナーに関する。 The present invention relates to a scale removing cleaner that is suitable for removing scale in bathrooms, bathrooms, kitchens, and the like.
水垢は浴室の鏡、蛇口、シャワーヘッド等の表面に付着しやすく、美観を損ねるため、従来から水垢除去性能をうたった様々なクリーナーが販売されている。 Since water stains easily adhere to the surfaces of bathroom mirrors, faucets, showerheads, etc., and detracts from the beauty, various cleaners that have been known for their water removal performance have been sold.
例えば、特許文献１には、独立気泡スポンジの表面に研磨布紙シートを貼着し、一体化させたクリーニング用具が開示されている。また、特許文献２には、ガラス表面の水垢、油膜などの汚れ落としを目的として、微粉の酸化セリウム粒子をバインダーとなる樹脂と共に造粒成形し、この造粒粒子を基材に単層に密に固着させたことを特徴とするパッドが開示されている。また、特許文献３には、太径繊維及び研磨粒子を含む掻き取り層と、パルプ繊維を含む吸水層とが積層された清掃用シートが開示されている。
For example, Patent Document 1 discloses a cleaning tool in which an abrasive cloth paper sheet is attached to the surface of a closed cell sponge and integrated. In
従来のクリーナーは、水垢除去性能が高い製品では、鏡、蛇口等の表面を傷つけてしまう場合があり、傷がつきにくい製品では、水垢除去性能が不十分であった。 Conventional cleaners may damage the surface of mirrors, faucets and the like in products with high scale removal performance, and scale removal performance is insufficient in products that are difficult to scratch.
また、水回りには蛇口等の細かな曲面及び凹凸を有する部材があるため、これらの曲面及び凹凸に追従でき、狭いスペースを簡単にクリーニング可能な、水垢除去用クリーナーが望まれている。 Further, since there are members having fine curved surfaces and irregularities such as faucets around the water, descaling cleaners that can follow these curved surfaces and irregularities and can easily clean a narrow space are desired.
本発明の一側面は、布基材と、砥粒及び結合剤を含む複数の立体要素と、布基材の一方面側に配置され、布基材と立体要素とを接合する接着層と、を備える、水垢除去用クリーナーに関する。 One aspect of the present invention is a fabric base, a plurality of three-dimensional elements including abrasive grains and a binder, an adhesive layer that is disposed on one side of the cloth base and joins the cloth base and the three-dimensional element, The present invention relates to a descaling cleaner.
一態様において、砥粒は、酸化アルミニウム粒子を含有していてよい。 In one embodiment, the abrasive grains may contain aluminum oxide particles.
一態様において、砥粒の平均粒径は０．２〜５μｍであってよい。 In one embodiment, the average grain size of the abrasive grains may be 0.2-5 μm.
一態様において、布基材の少なくとも一部は接着層に埋め込まれていてよい。 In one aspect, at least a portion of the fabric substrate may be embedded in the adhesive layer.
一態様において、布基材は、他方面側にループ状の係止部を有していてよい。 In one aspect, the fabric base material may have a loop-shaped locking portion on the other surface side.
本発明の他の一側面は、上記水垢除去用クリーナーと、水垢除去用クリーナーを支持する支持手段を有するホルダーと、を備える、水垢除去用キットに関する。 Another aspect of the present invention relates to a descaling kit comprising the descaling cleaner and a holder having support means for supporting the descaling cleaner.
本発明の更に他の一側面は、布基材がループ状の係止部を有している水垢除去用クリーナーと、ループ状の係止部と係合するフック状の係止部を有するホルダーと、を備える、水垢除去用キットに関する。 Still another aspect of the present invention is a scale removing cleaner in which the cloth base has a loop-shaped locking portion, and a holder having a hook-shaped locking portion that engages with the loop-shaped locking portion. And a descaling kit.
本発明によれば、水垢除去性能と傷付き防止性能とを両立した水垢除去用クリーナーが提供される。また、本発明によれば、曲面及び凹凸への追従性に優れ、蛇口等の狭いスペースを簡単にクリーニング可能な、水垢除去用クリーナーが提供される。 ADVANTAGE OF THE INVENTION According to this invention, the cleaner for scale removal which is compatible with scale removal performance and damage prevention performance is provided. Further, according to the present invention, there is provided a descaling cleaner that is excellent in followability to curved surfaces and unevenness and can easily clean a narrow space such as a faucet.
以下、図面を参照しつつ、本発明の好適な実施形態について説明する。なお、図面は理解を容易にするため一部を誇張して描いており、寸法比率等は図面に記載のものに限定されるものではない。 Hereinafter, preferred embodiments of the present invention will be described with reference to the drawings. Note that the drawings are partially exaggerated for easy understanding, and dimensional ratios and the like are not limited to those described in the drawings.
（水垢除去用クリーナー）
本実施形態に係る水垢除去用クリーナーは、布基材と、砥粒及び結合剤を含む複数の立体要素と、布基材と立体要素とを接合する接着層と、を備えている。複数の立体要素及び接着層は、布基材の一方面側に配置されており、複数の立体要素が水垢除去用クリーナーの研磨面を形成している。
(Descaler cleaner)
The cleaner for removing scale according to the present embodiment includes a cloth base, a plurality of three-dimensional elements including abrasive grains and a binder, and an adhesive layer that joins the cloth base and the three-dimensional element. The plurality of three-dimensional elements and the adhesive layer are arranged on one surface side of the cloth base material, and the plurality of three-dimensional elements form the polishing surface of the descaling cleaner.
本実施形態に係る水垢除去用クリーナーは、砥粒及び結合剤を含む複数の立体要素が研磨面を形成しているため、結合剤で立体要素中に保持された砥粒によって、効果的に水垢を除去することができる。 In the cleaner for removing scale according to the present embodiment, since a plurality of three-dimensional elements including abrasive grains and a binder form a polished surface, the scale is effectively scaled by the abrasive grains held in the three-dimensional element by the binder. Can be removed.
また、本実施形態では、立体要素から脱落した砥粒は、立体要素間の空隙に入り込むことため、脱落した砥粒による擦過跡の形成が避けられ、良好な傷付き防止性能が得られる。 Moreover, in this embodiment, since the abrasive grains dropped from the three-dimensional elements enter the gaps between the three-dimensional elements, formation of scratches by the dropped abrasive grains can be avoided, and good scratch prevention performance can be obtained.
また、本実施形態では、立体要素中に砥粒が分散していてよく、このとき、使用中に立体要素が徐々に削れることで、研磨面に常に新しい砥粒が表出する。このため、水垢除去性能が長時間維持され、作業時の力加減の変化による処理面の傷付きも避けることができる。 In the present embodiment, the abrasive grains may be dispersed in the three-dimensional element. At this time, the three-dimensional elements are gradually scraped during use, so that new abrasive grains are always exposed on the polished surface. For this reason, the scale removal performance is maintained for a long time, and scratches on the treated surface due to changes in force during work can be avoided.
さらに、本実施形態では、研磨面が複数の立体要素から形成され、且つ、基材が布基材であるため、研磨面及び基材が柔軟性に優れており、曲面及び凹凸への追従性に優れる。 Furthermore, in this embodiment, since the polishing surface is formed from a plurality of three-dimensional elements and the base material is a cloth base material, the polishing surface and the base material are excellent in flexibility, and followability to curved surfaces and irregularities. Excellent.
布基材は、例えば、編布、織布、不織布が挙げられる。具体的には、例えば、編布としては、平形編機、円形編機等で編成したよこ編みの編布、トリコット編機、ラッシェル編機等の経編機で編成したたて編みの編布などが挙げられる。織布としては、平織布、朱子織布、斜文織布等が挙げられる。不織布としては、エアレイド不織布、スパンレース不織布、ケミカルボンド不織布、サーマルボンド不織布、スパンボンド不織布、ニードルパンチ不織布、メルトブローン不織布等が挙げられる。 Examples of the cloth base material include a knitted fabric, a woven fabric, and a non-woven fabric. Specifically, for example, as a knitted fabric, weft knitted fabric knitted by a flat knitting machine, a circular knitting machine, etc., a warp knitted fabric knitted by a warp knitting machine such as a tricot knitting machine, a Raschel knitting machine, etc. Etc. Examples of the woven cloth include plain woven cloth, satin woven cloth, and oblique woven cloth. Examples of the nonwoven fabric include airlaid nonwoven fabric, spunlace nonwoven fabric, chemical bond nonwoven fabric, thermal bond nonwoven fabric, spunbond nonwoven fabric, needle punched nonwoven fabric, and melt blown nonwoven fabric.
布基材の材質は特に限定されず、例えば、ポリエステル、ナイロン、ポリアクリロニトリル、ビニロン、ビニリデン、ポリ塩化ビニル、ポリウレタン、ポリエチレン、ポリプロピレン、ポリブテン、ポリクラール、アセテート、トリアセテート、キュブラ、ポリノジック、レーヨン、プロミックス等の合成樹脂であってよく、綿、麻、毛、絹、パルプ等の天然素材であってもよい。 The material of the cloth substrate is not particularly limited. For example, polyester, nylon, polyacrylonitrile, vinylon, vinylidene, polyvinyl chloride, polyurethane, polyethylene, polypropylene, polybutene, polyclar, acetate, triacetate, cuvula, polynosic, rayon, promix Or a natural material such as cotton, hemp, hair, silk, or pulp.
布基材の坪量は、例えば６ｇ／ｍ２以上であってよく、１０ｇ／ｍ２以上であることが好ましい。これにより、クリーナー用途としての好適な柔軟性及び強度が得られ易くなる。また、布基材の坪量は、例えば１０００ｇ／ｍ２以下であってよく、７００ｇ／ｍ２以下であることが好ましい。これにより、曲面及び凹凸への追従性がより良好になり、蛇口等の狭いスペースをより磨きやすくなる。 The basis weight of the cloth base material may be, for example, 6 g / m 2 or more, and is preferably 10 g / m 2 or more. Thereby, it becomes easy to obtain suitable flexibility and strength as a cleaner application. Further, the basis weight of the cloth base material may be, for example, 1000 g / m 2 or less, and preferably 700 g / m 2 or less. Thereby, followability to a curved surface and unevenness becomes better, and it becomes easier to polish a narrow space such as a faucet.
布基材は、スティフネス値が４０ｇ／１２．７ｍｍ以下であることが好ましく、２５ｇ／１２．７ｍｍ以下であることがより好ましい。これにより、水垢除去用クリーナーに適度な柔軟性が付与され、曲面及び凹凸への追従性がより良好になる。また、布基材のスティフネス値は、機械的強度及び耐久性を確保しやすい観点からは、０．０１ｇ／１２．７ｍｍ以上であってよく、０．０５ｇ／１２．７ｍｍ以上であってもよい。 The fabric base material preferably has a stiffness value of 40 g / 12.7 mm or less, and more preferably 25 g / 12.7 mm or less. Thereby, moderate softness | flexibility is provided to the cleaner for scale removal, and the followable | trackability to a curved surface and an unevenness | corrugation becomes more favorable. In addition, the stiffness value of the cloth base material may be 0.01 g / 12.7 mm or more, or 0.05 g / 12.7 mm or more from the viewpoint of easily ensuring mechanical strength and durability. .
なお、本明細書中、スティフネス値は、ループステフネステスタ（（株）東洋精機製作所）を用いて、幅１２．７ｍｍ、長さ６０ｍｍのループ状試料の頂部を圧子で押し込み、ループの頂部側と基部側とが接したときの負荷荷重の値を示す。具体的には、以下の手順で測定される。
（１）測定試料を幅１２．７ｍｍ、長さ１５０ｍｍの短冊状にカットする。
（２）９０ｍｍ離間して対向する２つのマグネットチャック（厚さ１５ｍｍ）間に、カットした試料を固定する。
（３）マグネットチャック間の距離を０にして、試料を長さ６０ｍｍのループ状に形成する。
（４）ループの頂部に円盤状の圧子を押し当ててループを圧縮し、押し当てに要した荷重を測定する。押し込み速度は３．３ｍｍ／秒とし、押し込んだ距離と荷重との関係をグラフ化する。
（５）ループの頂部側と基部側とが接触を開始した際、グラフに変曲点が観察される。同じ測定を３回行い、この変曲点における荷重の平均値を、スティフネス値とする。
In the present specification, the stiffness value is calculated by using a loop stiffness tester (Toyo Seiki Seisakusho Co., Ltd.) to push the top of a loop-shaped sample having a width of 12.7 mm and a length of 60 mm with an indenter. It shows the value of the load applied when the base and the base are in contact. Specifically, it is measured by the following procedure.
(1) The measurement sample is cut into a strip shape having a width of 12.7 mm and a length of 150 mm.
(2) The cut sample is fixed between two magnet chucks (thickness 15 mm) facing each other with a distance of 90 mm.
(3) The distance between the magnet chucks is set to 0, and the sample is formed in a loop shape having a length of 60 mm.
(4) A disc-shaped indenter is pressed against the top of the loop to compress the loop, and the load required for pressing is measured. The indentation speed is 3.3 mm / sec, and the relationship between the indentation distance and the load is graphed.
(5) When the top side and the base side of the loop start to contact, an inflection point is observed in the graph. The same measurement is performed three times, and the average value of the load at this inflection point is taken as the stiffness value.
布基材の一方面側には接着層が設けられている。布基材の一方面側の一部は、接着層に埋設されていてよい。換言すると、接着層は布基材の一方面側に含浸していてよい。 An adhesive layer is provided on one side of the fabric substrate. A part of one side of the cloth base material may be embedded in the adhesive layer. In other words, the adhesive layer may be impregnated on one side of the cloth base material.
布基材の他方面側には、例えば、ホルダーとの固定手段が設けられていてよい。これにより、曲面及び凹凸のある部材を磨く場合は水垢除去用クリーナーを単独で使用し、鏡面等の平面を磨く場合は水垢除去用クリーナーをホルダーに支持させて使用することができる。 For example, a fixing means with a holder may be provided on the other surface side of the cloth base material. Accordingly, when polishing a member having a curved surface and unevenness, a descaling cleaner can be used alone, and when polishing a flat surface such as a mirror surface, the descaling cleaner can be supported by a holder.
ホルダーとの固定手段は、例えば、面ファスナーであってよい。より具体的には、例えば、布基材は、他方面側にループ状の係止部を有していてよい。これにより、フック状の係止部を有するホルダーに容易に着脱することができる。また、布基材は、他方面側にフック状の係止部を有していてよい。これにより、ループ状の係止部を有するホルダーに容易に着脱することができる。 The fixing means with the holder may be, for example, a hook-and-loop fastener. More specifically, for example, the cloth base material may have a loop-shaped locking portion on the other surface side. Thereby, it can attach or detach easily to the holder which has a hook-shaped latching | locking part. Moreover, the cloth base material may have a hook-shaped locking part on the other surface side. Thereby, it can attach or detach easily to the holder which has a loop-shaped latching | locking part.
接着層は、布基材の一方面側に配置され、布基材と複数の立体要素とを接合する層である。接着層は、例えば、粘着剤から構成される層であってよく、接着剤の硬化物から構成される層であってもよい。 An adhesion layer is a layer which is arrange | positioned at the one surface side of a fabric base material, and joins a fabric base material and a some three-dimensional element. For example, the adhesive layer may be a layer composed of a pressure-sensitive adhesive, or may be a layer composed of a cured product of the adhesive.
接着層が粘着剤から構成される層であるとき、当該粘着剤は、例えば、アクリル系粘着剤、ゴム系粘着剤、シリコーン系粘着剤、ウレタン系粘着剤、ポリエステル系粘着剤であってよく、これらのうちアクリル系粘着剤が好ましい。 When the adhesive layer is a layer composed of an adhesive, the adhesive may be, for example, an acrylic adhesive, a rubber adhesive, a silicone adhesive, a urethane adhesive, a polyester adhesive, Of these, acrylic adhesives are preferred.
接着層が接着剤の硬化物から構成される層であるとき、当該接着剤は、例えば、アクリル系接着剤、ゴム系接着剤、ウレタン系接着剤、ポリエステル系接着剤、エポキシ系接着剤、シリコーン系接着剤等であってよい。 When the adhesive layer is a layer composed of a cured product of an adhesive, the adhesive is, for example, an acrylic adhesive, a rubber adhesive, a urethane adhesive, a polyester adhesive, an epoxy adhesive, silicone It may be a system adhesive or the like.
好適な一態様において、接着層は、アクリル系樹脂を含有することが好ましく、アクリル系粘着剤又はアクリル系接着剤の硬化物から構成される層であることが好ましい。 In a preferred embodiment, the adhesive layer preferably contains an acrylic resin, and is preferably a layer composed of an acrylic pressure-sensitive adhesive or a cured product of an acrylic adhesive.
接着層は、２５℃における弾性率が１×１０４〜１×１０９（Ｐａ）であってよい。このような接着層によれば、曲面及び凹凸に対する追従性に優れるとともに、ホルダーに取付けて平面を磨いたときの形状保持性にも優れる水垢除去用クリーナーが得られる。なお、接着層の２５℃における弾性率は、接着層が粘着剤から構成される層である場合には、粘弾性測定装置（Ｒｈｅｏｍｅｔｒｉｃ Ｓｃｉｅｎｔｉｆｉｃ社 Ａｄｖａｎｃｅｄ Ｒｈｅｏｍｅｔｒｉｃ Ｅｘｐａｎｓｉｏｎ Ｓｙｓｔｅｍ（ＡＲＥＳ））により、周波数１．０Ｈｚの条件で測定され、接着層が接着剤の硬化物から構成される層である場合には、粘弾性測定装置（Ｒｈｅｏｍｅｔｒｉｃ Ｓｃｉｅｎｔｉｆｉｃ社 ＲＳＡ３）により、周波数１．０Ｈｚの条件で測定される。 The adhesive layer may have an elastic modulus at 25 ° C. of 1 × 10 4 to 1 × 10 9 (Pa). According to such an adhesive layer, it is possible to obtain a descaling cleaner that has excellent followability to curved surfaces and irregularities and also has excellent shape retention when attached to a holder and polished on a flat surface. It should be noted that the elastic modulus at 25 ° C. of the adhesive layer is a frequency of 1.0 Hz by a viscoelasticity measuring device (Rheometric Scientific Advanced Rheometric Expansion System (ARES)) when the adhesive layer is a layer composed of an adhesive. When the adhesive layer is a layer composed of a cured product of an adhesive, it is measured under a condition of a frequency of 1.0 Hz by a viscoelasticity measuring device (Rheometric Scientific RSA3).
接着層の厚さは、曲面及び凹凸に対する追従性が十分に得られる範囲で適宜調整してよい。例えば、接着層の厚さは、１ｍｍ以下であってよく、０．５ｍｍ以下であることが好ましい。これにより、水垢除去用クリーナーの柔軟性がより向上し、曲面及び凹凸への追従性が一層向上する。また、接着層の厚さは、１０μｍ以上であってよく、２０μｍ以上であることが好ましい。 The thickness of the adhesive layer may be appropriately adjusted within a range in which followability with respect to curved surfaces and unevenness can be sufficiently obtained. For example, the thickness of the adhesive layer may be 1 mm or less, and is preferably 0.5 mm or less. Thereby, the softness | flexibility of the cleaner for scale removal improves more, and the followable | trackability to a curved surface and an unevenness | corrugation improves further. Further, the thickness of the adhesive layer may be 10 μm or more, and preferably 20 μm or more.
立体要素は、複数の砥粒と該砥粒を結着する結合剤とを含んでいる。立体要素は、布基材の一方面側において、布基材と反対側に凸となるように立体的に成形されている。立体要素は、布基材の一方面側に設けられた接着層によって、布基材上に接着されている。換言すると、立体要素は、接着層の、布基材と反対側の面上に設けられている。 The three-dimensional element includes a plurality of abrasive grains and a binder that binds the abrasive grains. The three-dimensional element is three-dimensionally shaped so as to protrude toward the opposite side of the cloth base on one side of the cloth base. The three-dimensional element is bonded onto the cloth base material by an adhesive layer provided on one side of the cloth base material. In other words, the three-dimensional element is provided on the surface of the adhesive layer opposite to the cloth substrate.
砥粒は、水垢を除去可能な強度を有するものであればよい。砥粒は、例えば、ダイヤモンド、酸化アルミニウム、酸化ケイ素、酸化セリウム、酸化ジルコニウム、酸化クロム、酸化鉄、炭化ケイ素、炭化タングステン、ケイ酸ジルコニウム、ガーネット、フリント、エメリー、トパズ、ジルコニア、窒化ケイ素、窒化ホウ素、珪藻土、軽石等の砥粒であってよい。これらのうち、砥粒は、ダイヤモンド砥粒又は酸化アルミニウム砥粒であることが好ましい。砥粒がダイヤモンド砥粒であると、例えばガラス面に対して、傷付きを十分に抑えつつ、より優れた水垢除去性能が得られる。また、砥粒が酸化アルミニウム砥粒であると、ガラス面のみならず、クロムメッキ面に対する傷付きも顕著に抑制しつつ、十分な水垢除去性能が得られる。 The abrasive grains only need to have a strength capable of removing scale. Abrasive grains are, for example, diamond, aluminum oxide, silicon oxide, cerium oxide, zirconium oxide, chromium oxide, iron oxide, silicon carbide, tungsten carbide, zirconium silicate, garnet, flint, emery, topaz, zirconia, silicon nitride, nitride Abrasive grains such as boron, diatomaceous earth, and pumice may be used. Of these, the abrasive grains are preferably diamond abrasive grains or aluminum oxide abrasive grains. When the abrasive grains are diamond abrasive grains, for example, it is possible to obtain more excellent scale removal performance while sufficiently suppressing scratches on the glass surface. Further, when the abrasive grains are aluminum oxide abrasive grains, not only the glass surface but also the chromium plating surface can be markedly suppressed, and sufficient scale removal performance can be obtained.
砥粒の平均粒径は、例えば、０．２〜５μｍであることが好ましく、０．５〜３μｍであることがより好ましい。平均粒径を上記上限値より小さくすることで、磨き面への傷付きが一層抑制され、平均粒径を上記下限値より大きくすることで水垢除去性能が一層向上する傾向がある。なお、砥粒の平均粒径は、レーザ回折／散乱式粒度分布測定装置（堀場製作所ＬＡ―９２０）により測定される。 The average particle size of the abrasive grains is preferably 0.2 to 5 μm, for example, and more preferably 0.5 to 3 μm. By making the average particle size smaller than the above upper limit value, scratches on the polished surface are further suppressed, and by making the average particle size larger than the above lower limit value, the scale removal performance tends to be further improved. The average particle size of the abrasive grains is measured by a laser diffraction / scattering type particle size distribution measuring device (Horiba, Ltd. LA-920).
結合剤は、複数の砥粒を結着して立体要素を形作る成分であり、複数の砥粒を分散させるマトリックスということもできる。結合剤は、例えば、アクリル系樹脂、フェノール樹脂、エポキシ樹脂、ウレタン樹脂、ポリエステル樹脂等の樹脂を含有していてよい。これらのうち、結合剤はアクリル系樹脂を含有することが好ましい。結合剤は、例えば、アクリルモノマー及び重合開始剤を含有する硬化性組成物の硬化物であってよい。 The binder is a component that binds a plurality of abrasive grains to form a three-dimensional element, and can also be referred to as a matrix that disperses the plurality of abrasive grains. The binder may contain, for example, a resin such as an acrylic resin, a phenol resin, an epoxy resin, a urethane resin, or a polyester resin. Of these, the binder preferably contains an acrylic resin. The binder may be, for example, a cured product of a curable composition containing an acrylic monomer and a polymerization initiator.
結合剤の強度は、３ＭＰａ以上であることが好ましく、５ＭＰａ以上であることがより好ましい。これにより、砥粒の結着力が向上し、水垢除去性能がより向上する傾向がある。また、結合剤の強度は、３００ＭＰａ以下であることが好ましく、２００ＭＰａ以下であることがより好ましい。これにより、過度な負荷がかかった場合に砥粒が脱落しやすくなり、処理面の傷付きが一層顕著に防止される。なお、結合剤の強度は、引張試験にて測定される値を示す。 The strength of the binder is preferably 3 MPa or more, and more preferably 5 MPa or more. Thereby, the binding force of the abrasive grains is improved, and the scale removal performance tends to be further improved. Further, the strength of the binder is preferably 300 MPa or less, and more preferably 200 MPa or less. Thereby, when an excessive load is applied, the abrasive grains easily fall off, and the processing surface is more significantly prevented from being damaged. In addition, the intensity | strength of a binder shows the value measured by a tension test.
立体要素は、その全体に砥粒が分散されていてよい。また、立体要素は、土台となる第一層と、第一層上に設けられた砥粒を含有する第二層と、を含む多層構造であってもよい。このとき、第一層は必ずしも砥粒を含まなくてよい。第一層及び第二層はいずれも結合剤を含有していてよい。 The three-dimensional element may have abrasive grains dispersed throughout. Further, the three-dimensional element may have a multilayer structure including a first layer serving as a base and a second layer containing abrasive grains provided on the first layer. At this time, the first layer does not necessarily include abrasive grains. Both the first layer and the second layer may contain a binder.
一態様において、立体要素は、底面で接着層と接する錐台構造を有していてよい。このとき、錐台構造の上面が研磨面を形成する。このような立体要素では、錐台構造の上面に表出した砥粒により、水垢が除去される。立体要素は、使用時に徐々に削れ、その都度、錐体構造の上面に新たな砥粒が表出する。このため、本実施形態に係る水垢除去用クリーナーは、均一な水垢性能を長時間維持できる。錐台構造は、三角錐台であっても、四角錐台であっても、多角錐台であっても、円錐台であってもよい。 In one aspect, the three-dimensional element may have a frustum structure in contact with the adhesive layer on the bottom surface. At this time, the upper surface of the frustum structure forms a polished surface. In such a three-dimensional element, scale is removed by the abrasive grains exposed on the upper surface of the frustum structure. The three-dimensional element is gradually scraped during use, and new abrasive grains appear on the upper surface of the cone structure each time. For this reason, the scale removal cleaner according to the present embodiment can maintain uniform scale performance for a long time. The frustum structure may be a triangular frustum, a square frustum, a polygonal frustum, or a frustum.
一態様において、立体要素は、底面で接着層と接する錐体構造を有していてよい。このとき、錐体構造の頂点が研磨面を形成する。このような立体要素は、使用時に徐々に頂点が削れて、立体要素が錐台構造を成すようになる。錐台構造の上面には、立体要素中に分散された砥粒が表出し、当該砥粒によって水垢が除去される。錐体構造は、三角錐であっても、四角錐であっても、多角錐であっても、円錐であってもよい。 In one embodiment, the three-dimensional element may have a cone structure that contacts the adhesive layer on the bottom surface. At this time, the apex of the cone structure forms a polished surface. When such a three-dimensional element is used, the apexes are gradually scraped, and the three-dimensional element has a frustum structure. On the upper surface of the frustum structure, abrasive grains dispersed in the three-dimensional element are exposed, and the scale is removed by the abrasive grains. The cone structure may be a triangular pyramid, a quadrangular pyramid, a polygonal pyramid, or a cone.
一態様において、立体要素は、一方の底面で接着層と接する柱状構造を有していてよい。このとき、柱状構造の他方の底面（以下、柱状構造の上面という。）が研磨面を形成する。このような立体要素では、柱状構造の上面に表出した砥粒により、水垢が除去される。立体要素は、使用時に徐々に削れ、その都度、柱状構造の上面に新たな砥粒が表出する。柱状構造は、三角柱であっても、四角柱であっても、多角柱であっても、円柱であってもよい。 In one embodiment, the three-dimensional element may have a columnar structure in contact with the adhesive layer on one bottom surface. At this time, the other bottom surface of the columnar structure (hereinafter referred to as the top surface of the columnar structure) forms a polished surface. In such a three-dimensional element, the scale is removed by the abrasive grains exposed on the upper surface of the columnar structure. The three-dimensional element is gradually scraped during use, and new abrasive grains appear on the upper surface of the columnar structure each time. The columnar structure may be a triangular column, a quadrangular column, a polygonal column, or a cylinder.
一態様において、立体要素は、柱体（例えば三角柱）が横倒しになった構造、すなわち、一側面で接着層と接する柱体構造を有していてよい。このとき、接着層と接する側面に対向する側辺又は側面が、研磨面を形成する。柱体構造は、その底面側に向かう両方向に延びていてよく、例えば、接着層の端部まで延びていてよい。柱体構造の底面側の端部形状は、特に限定されず、例えば、側面に垂直な面を形成していてよく、寄棟状に成形されていてもよい。 In one embodiment, the three-dimensional element may have a structure in which a pillar (eg, a triangular prism) is laid down, that is, a pillar structure that is in contact with the adhesive layer on one side surface. At this time, the side or side opposite to the side contacting the adhesive layer forms a polished surface. The columnar structure may extend in both directions toward the bottom surface side, and may extend to the end of the adhesive layer, for example. The shape of the end portion on the bottom surface side of the columnar structure is not particularly limited, and for example, a surface perpendicular to the side surface may be formed, or may be formed in a dormitory shape.
立体要素の高さ（接着層と接する面から、研磨面を成す頂部までの高さ）は特に限定されないが、例えば１０〜１０００μｍであってよく、１５〜５００μｍであることが好ましい。 The height of the three-dimensional element (the height from the surface in contact with the adhesive layer to the top forming the polished surface) is not particularly limited, but may be, for example, 10 to 1000 μm, and preferably 15 to 500 μm.
本実施形態において、接着層上には複数の立体要素が形成されている。本実施形態では、脱落した砥粒、微細なゴミ等が各立体要素間の空隙に入り込むことができるため、これらによる擦過跡の形成が避けられ、良好な傷付き防止性が得られる。また、本実施形態に係る水垢除去用クリーナーは、研磨面を形成する立体要素が複数に分かれていることから、柔軟性に優れ、曲面及び凹凸への追従性に優れる。 In the present embodiment, a plurality of three-dimensional elements are formed on the adhesive layer. In the present embodiment, dropped abrasive grains, fine dust, and the like can enter the gaps between the three-dimensional elements, so that the formation of scratches due to these can be avoided, and good scratch resistance can be obtained. Moreover, since the three-dimensional element which forms a grinding | polishing surface is divided into several, the scale removal cleaner which concerns on this embodiment is excellent in a softness | flexibility, and is excellent in the followable | trackability to a curved surface and an unevenness | corrugation.
水垢除去用クリーナーのスティフネス値は、４５ｇ／１２．７ｍｍ以下であることが好ましく、３０ｇ／１２．７ｍｍ以下であることがより好ましい。これにより、曲面及び凹凸への追従性がより良好になる。また、水垢除去用クリーナーのスティフネス値は、０．０５ｇ／１２．７ｍｍ以上であることが好ましく、０．１ｇ／１２．７ｍｍ以上であることがより好ましい。これにより、水垢除去作業に適した程よい柔軟性が得られる、ホルダーへの脱着が容易となる等の効果が奏される。なお、本明細書中、水垢除去用クリーナーのスティフネス値は、布基材のスティフネス値と同じ方法で測定される。 The stiffness value of the descaling cleaner is preferably 45 g / 12.7 mm or less, and more preferably 30 g / 12.7 mm or less. Thereby, the followability to a curved surface and unevenness becomes better. Further, the stiffness value of the descaling cleaner is preferably 0.05 g / 12.7 mm or more, and more preferably 0.1 g / 12.7 mm or more. Thereby, moderate flexibility suitable for scale removal work is obtained, and effects such as easy attachment / detachment to / from the holder are exhibited. In the present specification, the stiffness value of the descaling cleaner is measured by the same method as the stiffness value of the cloth substrate.
本実施形態では、複数の立体要素により研磨面が形成されているため、優れた水垢除去性能を維持しつつ、上述の好適なスティフネス値を達成しやすい。水垢除去用クリーナーのスティフネス値は、例えば、布基材及び接着層の剛性・柔軟性を変更することで適宜調整できる。布基材及び接着層は、水垢除去用クリーナーのスティフネス値が上述の好適な範囲となるように、その組成等を選択してよい。 In this embodiment, since the polishing surface is formed by a plurality of three-dimensional elements, it is easy to achieve the above-mentioned preferred stiffness value while maintaining excellent scale removal performance. The stiffness value of the descaling cleaner can be adjusted as appropriate by, for example, changing the rigidity and flexibility of the cloth substrate and the adhesive layer. The composition and the like of the cloth base material and the adhesive layer may be selected so that the stiffness value of the descaling cleaner is within the above-described preferable range.
（水垢除去用キット）
本実施形態に係る水垢除去用キットは、上述した水垢除去用クリーナーと、水垢除去用クリーナーを支持する支持手段を有するホルダーと、を備えている。このような水垢除去用キットによれば、例えば鏡面等の平面を磨く際に、ホルダーで水垢除去用クリーナーを支持することで効率良く作業を行うことができる。
(Scale removal kit)
The scale removal kit according to the present embodiment includes the scale removal cleaner described above and a holder having support means for supporting the scale removal cleaner. According to such a descaling kit, for example, when polishing a flat surface such as a mirror surface, the descaling cleaner is supported by the holder so that the work can be efficiently performed.
ホルダーは、作業者が手で把持する把持部を有していてよい。把持部の形状は、その用途等に応じて適宜設計してよい。 The holder may have a gripping part that an operator grips with a hand. You may design the shape of a holding part suitably according to the use.
ホルダーにおける支持手段は、水垢除去作業による負荷に耐え得る手段であればよい。 The support means in the holder may be any means that can withstand the load caused by the descaling operation.
一態様において、水垢除去用クリーナー及びホルダーは、面ファスナーで互いに接着できるものであってよい。すなわち、水垢除去用クリーナーは、布基材の接着層と反対側の面に、面ファスナー用の第一の係止部を有していてよく、ホルダーは、水垢除去用クリーナーが有する第一の係止部と係合する第二の係止部を有していてよい。 In one embodiment, the descaling cleaner and the holder may be capable of being bonded to each other with a hook-and-loop fastener. That is, the descaling cleaner may have a first engaging portion for a hook-and-loop fastener on the surface of the cloth base opposite to the adhesive layer, and the holder may be a first descaling cleaner that the descaling cleaner has. You may have the 2nd latching | locking part engaged with a latching | locking part.
好適な一態様において、水垢除去用クリーナーは、布基材の接着層と反対側の面に、ループ状の係止部を有していてよい。また、ホルダーは、水垢除去用クリーナーが有するループ状係止部と係合する、フック状の係止部を有していてよい。 In a preferred embodiment, the descaling cleaner may have a loop-shaped locking portion on the surface of the fabric base opposite to the adhesive layer. Further, the holder may have a hook-shaped locking portion that engages with a loop-shaped locking portion of the descaling cleaner.
ホルダーの材質は特に限定されないが、水垢除去という用途上、耐水性を有する素材であることが望ましい。 The material of the holder is not particularly limited, but is preferably a water-resistant material for the purpose of removing scale.
以下、図面を参照して、本発明の好適な一実施形態について説明する。 Hereinafter, a preferred embodiment of the present invention will be described with reference to the drawings.
図１は、水垢除去用クリーナーの好適な一態様を示す斜視図であり、図２は図１のＩＩ−ＩＩ線に沿った断面の拡大図を示す図である。 FIG. 1 is a perspective view showing a preferred embodiment of a descaling cleaner, and FIG. 2 is an enlarged view of a cross section taken along line II-II in FIG.
図１に示す水垢除去用クリーナー１は、布基材１０と、複数の立体要素２０と、布基材１０の一方面上に配置され、布基材１０と立体要素２０とを接合する接着層３０と、を備えている。布基材１０の立体要素２０と反対側の面上には、布基材１０を構成する繊維をループ状に起毛させてループ状係止部１１が形成されている。複数の立体要素２０は、それぞれが複数の砥粒２１及びそれを結着する結合剤２２を含有している。また、立体要素２０は、それぞれが独立して接着層３０上に接着されている。
A descaling cleaner 1 shown in FIG. 1 is disposed on one surface of a
図３は、水垢除去用キットの好適な一態様を示す斜視図である。 FIG. 3 is a perspective view showing a preferred embodiment of the scale removal kit.
図３に示す水垢除去用キット３は、水垢除去用クリーナー１と、ホルダー２と、を有している。ホルダー２は、作業者が把持する把持部４０と、水垢除去用クリーナー１を装着する支持部５０とを備えている。支持部５０には、水垢除去用クリーナー１が有するループ状係止部１１と係合するフック状係止部５１が設けられている。
The scale removal kit 3 shown in FIG. 3 includes a scale removal cleaner 1 and a
以上、本発明の好適な実施形態について説明したが、本発明は上記実施形態に限定されるものではない。 The preferred embodiment of the present invention has been described above, but the present invention is not limited to the above embodiment.
以下、実施例により本発明をより具体的に説明するが、本発明は実施例に限定されるものではない。 EXAMPLES Hereinafter, although an Example demonstrates this invention more concretely, this invention is not limited to an Example.
（実施例１）
布基材として、トリコット編みのポリエステルからなるループ素材を準備した。布基材の坪量は６６ｇ／ｍ２、ウェール数は３３／２５．４ｍｍ、コース数は４４／２５．４ｍｍ、スティフネス値は１．１ｇ／１２．７ｍｍであった。また、立体要素の形状が転写されたポリプロピレン製の鋳型フィルムを準備した。
Example 1
A loop material made of tricot knitted polyester was prepared as a fabric substrate. The basis weight of the cloth substrate was 66 g / m 2 , the number of wales was 33 / 25.4 mm, the number of courses was 44 / 25.4 mm, and the stiffness value was 1.1 g / 12.7 mm. Also, a polypropylene mold film to which the shape of the three-dimensional element was transferred was prepared.
まず、表１に記載の各成分を混合し、接着剤成分を準備した。次いで、表２に記載の各成分を混合し、第一の塗布液を調製した。次いで、表３に記載の各成分を混合し、第二の塗布液を調製した。 First, each component described in Table 1 was mixed to prepare an adhesive component. Subsequently, each component described in Table 2 was mixed to prepare a first coating solution. Subsequently, each component described in Table 3 was mixed to prepare a second coating solution.
鋳型フィルムに第一の塗布液を塗布し、鋳型フィルムの凹部に第一の塗布液を充填した。次いで、溶剤を乾燥除去し、紫外線照射を行うことで、第一の塗布液を硬化させ、鋳型フィルムの凹部内に立体要素を形成した。次に、第二の塗布液を鋳型フィルム上に塗布し、更に布基材をラミネートした。布基材をラミネートした状態で紫外線照射及び熱硬化を行い、布基材と立体要素とが接着層で接着された水垢除去用クリーナーを作製した。得られた水垢除去用クリーナーのスティフネス値を測定したところ、９．７ｇ／１２．７ｍｍであった。 The first coating liquid was applied to the mold film, and the first coating liquid was filled in the recesses of the mold film. Subsequently, the solvent was dried and removed, and the first coating solution was cured by irradiating with ultraviolet rays, thereby forming a three-dimensional element in the concave portion of the mold film. Next, the 2nd coating liquid was apply | coated on the casting_mold | template film, and also the cloth base material was laminated. Ultraviolet light irradiation and heat curing were carried out in a state where the cloth base material was laminated, and a descaling cleaner in which the cloth base material and the three-dimensional element were bonded with an adhesive layer was produced. When the stiffness value of the obtained descaling cleaner was measured, it was 9.7 g / 12.7 mm.
（実施例２）
布基材を、坪量６６ｇ／ｍ２、スティフネス値１．２９ｇ／１２．７ｍｍのポリエステルループ素材に変更し、第一の塗布液に配合する砥粒を、酸化アルミニウム（平均粒径２μｍ、ＷＡ＃６０００、フジミインコーポレーテッド社製）に変更したこと以外は、実施例１と同様にして、水垢除去用クリーナーを作製した。得られた水垢除去用クリーナーのスティフネス値は、１５．８ｇ／１２．７ｍｍであった。
(Example 2)
The cloth base material is changed to a polyester loop material having a basis weight of 66 g / m 2 and a stiffness value of 1.29 g / 12.7 mm, and the abrasive grains to be blended in the first coating liquid are aluminum oxide (
（実施例３）
布基材を、坪量６６ｇ／ｍ２、スティフネス値１．２９ｇ／１２．７ｍｍのポリエステルループ素材に変更し、第一の塗布液に配合する砥粒を、ダイヤモンド粒子（平均粒径２μｍ、ＬＳ６００Ｔ １−３（２ｕｍ）、ＬＡＮＤＳ Ｓｕｐｅｒａｂｒａｓｉｖｅｓ社製）に変更したこと以外は、実施例１と同様にして、水垢除去用クリーナーを作製した。得られた水垢除去用クリーナーのスティフネス値は、１５．３ｇ／１２．７ｍｍであった。
(Example 3)
The cloth base material is changed to a polyester loop material having a basis weight of 66 g / m 2 and a stiffness value of 1.29 g / 12.7 mm, and the abrasive grains to be blended in the first coating liquid are diamond particles (
（比較例１）
布基材に代えて厚さ７５μｍのＰＥＴフィルムを用い、第一の塗布液に配合する砥粒を、ダイヤモンド粒子（平均粒径２μｍ、ＬＳ６００Ｔ １−３（２ｕｍ）、ＬＡＮＤＳ Ｓｕｐｅｒａｂｒａｓｉｖｅｓ社製）に変更したこと以外は、実施例１と同様にして、水垢除去用クリーナーを作製した。得られた水垢除去用クリーナーのスティフネス値は、４７．９ｇ／１２．７ｍｍであった。
(Comparative Example 1)
A 75 μm thick PET film is used in place of the cloth base material, and the abrasive grains blended in the first coating solution are changed to diamond particles (
（比較例２）
市販の水垢除去用クリーナーとして、フォーム基材にダイヤモンド砥粒を付着させた製品である、ヒューマンシステム社製「ダイヤモンドパッドＳ」を準備した。
(Comparative Example 2)
As a commercially available descaling cleaner, “Diamond Pad S” manufactured by Human Systems Co., Ltd., which is a product in which diamond abrasive grains are adhered to a foam substrate, was prepared.
（比較例３）
市販の水垢除去用クリーナーとして、シート基材にダイヤモンド砥粒、酸化アルミニウム砥粒及び酸化セリウム砥粒を付着させた製品である、アイセン社製「貼りつく鏡磨き」を準備した。
(Comparative Example 3)
As a commercially available descaling cleaner, “Attach Mirror Polish” manufactured by Aisen Co., Ltd., a product in which diamond abrasive grains, aluminum oxide abrasive grains, and cerium oxide abrasive grains were adhered to a sheet base material, was prepared.
（比較例４）
市販の水垢除去用クリーナーとして、ポリエステルとパルプの複合基材に研磨液を含浸させた製品である、花王社製「ピカッと輝くシート クレンジング成分ｉｎ」を準備した。
(Comparative Example 4)
As a commercially available descaling cleaner, “Pikaka Shining Sheet Cleansing In” manufactured by Kao Corporation, which is a product obtained by impregnating a composite material of polyester and pulp with a polishing liquid, was prepared.
＜水垢除去性能の評価＞
実施例１〜３及び比較例１〜４の水垢除去用クリーナーについて、以下の方法で水垢除去性能を評価した。なお、実施例１〜３及び比較例１の水垢除去用クリーナーは、４ｃｍ×６ｃｍの試験片を切り取り、試験を行った。
<Evaluation of scale removal performance>
About the scale removal cleaner of Examples 1-3 and Comparative Examples 1-4, scale removal performance was evaluated by the following method. In addition, the cleaner for scale removal of Examples 1-3 and the comparative example 1 cut out the test piece of 4 cm x 6 cm, and tested it.
霧吹きを使って鏡に水を散布し、５０℃の乾燥オーブンで約３０分間乾燥させた。このプロセスを３０回繰り返し、水垢汚れを鏡面上に作成した。３ｍｌの水を水垢汚れのついた鏡面上に滴下し、水垢除去用クリーナーで３０往復、２．０ｋｇｆの荷重で擦った。目視にて、水垢汚れの落ち度合いを確認し、水垢が除去された面積が８０％以上である場合を「Ａ」、４０％以上８０％未満である場合を「Ｂ」、４０％未満である場合を「Ｃ」として評価した。評価結果は、表４に示すとおりとなった。 Water was sprayed on the mirror using a spray bottle and dried in a drying oven at 50 ° C. for about 30 minutes. This process was repeated 30 times to create scale stains on the mirror surface. 3 ml of water was dropped onto a mirror surface with scale dirt and rubbed with a scale removing cleaner for 30 reciprocations with a load of 2.0 kgf. The degree of removal of scale dirt is visually confirmed, and when the area from which scale is removed is 80% or more, “A”, when it is 40% or more and less than 80%, “B”, and less than 40%. The case was evaluated as “C”. The evaluation results are as shown in Table 4.
＜スクラッチテスト（鏡面）＞
実施例１〜３及び比較例１〜３の水垢除去用クリーナーで、３０往復、２．０ｋｇｆの荷重で鏡を擦った。目視で鏡面を観測し、キズが確認できなかった場合を「Ａ」、わずかにキズが生じていた場合を「Ｂ」、著しくキズが生じていた場合を「Ｃ」として評価した。評価結果は、表４に示すとおりとなった。
<Scratch test (mirror surface)>
The mirror was rubbed with a load of 2.0 kgf for 30 reciprocations using the scales for cleaners of Examples 1 to 3 and Comparative Examples 1 to 3. The mirror surface was visually observed and evaluated as “A” when no scratch was confirmed, “B” when slightly scratched, and “C” when markedly scratched. The evaluation results are as shown in Table 4.
＜追従試験＞
実施例１〜３及び比較例１〜３の水垢除去用クリーナーについて、０．５〜０．８ｋｇｆの荷重にて手を使って、標準的な蛇口の栓の付け根の凹部に追従するか確認した。また、各水垢除去用クリーナーが、蛇口のパイプの曲面に追従するか確認した。
凹部及び曲面のいずれにも十分に追従し、水垢除去が可能であった場合を「Ａ」、凹部又は曲面のいずれかに追従せず、いずれかで水垢除去が困難であった場合を「Ｂ」、凹部及び曲面のいずれにも追従せず、いずれも水垢除去が困難であった場合を「Ｃ」として評価した。
<Follow-up test>
About the descaling cleaners of Examples 1 to 3 and Comparative Examples 1 to 3, using hands with a load of 0.5 to 0.8 kgf, it was confirmed whether to follow the concave portion at the base of a standard faucet plug. . Also, it was confirmed that each descaling cleaner follows the curved surface of the tap pipe.
“A” indicates that it is possible to sufficiently follow both the concave portion and the curved surface and remove the scale, and “B” indicates that it is difficult to remove the scale due to any of the concave portion and the curved surface. The case where neither the concave portion nor the curved surface was followed and the removal of scale was difficult was evaluated as “C”.
＜スクラッチテスト（クロムメッキ面）＞
実施例１及び比較例１〜３の水垢除去用クリーナーで、３０往復、２．０ｋｇｆの荷重でクロムメッキ面を擦った。目視でクロムメッキ面を観測し、キズが確認できなかった場合を「Ａ」、わずかにキズが生じていた場合を「Ｂ」、著しくキズが生じていた場合を「Ｃ」として評価した。評価結果は、表５に示すとおりとなった。
<Scratch test (chrome plating surface)>
The chromium plating surface was rubbed with a load of 2.0 kgf with 30 reciprocations using the scale remover of Example 1 and Comparative Examples 1 to 3. The chrome-plated surface was visually observed and evaluated as “A” when no scratch was confirmed, “B” when slightly scratched, and “C” when severely scratched. The evaluation results are as shown in Table 5.
１…水垢除去用クリーナー、２…ホルダー、３…水垢除去用キット、１０…布基材、２０…立体要素、３０…接着層、４０…把持部、５０…支持部。 DESCRIPTION OF SYMBOLS 1 ... Descaler removal cleaner, 2 ... Holder, 3 ... Descaler removal kit, 10 ... Cloth base material, 20 ... Solid element, 30 ... Adhesive layer, 40 ... Gripping part, 50 ... Support part.
Claims (7)
砥粒及び結合剤を含む複数の立体要素と、
前記布基材の一方面側に配置され、前記布基材と前記立体要素とを接合する接着層と、
を備える、水垢除去用クリーナー。 A cloth substrate;
A plurality of three-dimensional elements including abrasive grains and a binder;
An adhesive layer that is disposed on one side of the cloth base material and joins the cloth base material and the three-dimensional element;
A cleaner for removing scale.
前記水垢除去用クリーナーを支持する支持手段を有するホルダーと、
を備える、水垢除去用キット。 A descaling cleaner according to any one of claims 1 to 5,
A holder having support means for supporting the descaling cleaner;
A descaling kit with
前記ループ状の係止部と係合するフック状の係止部を有するホルダーと、
を備える、水垢除去用キット。 A cleaner for removing scale according to claim 5;
A holder having a hook-shaped locking portion that engages with the loop-shaped locking portion;
A descaling kit with