JP2017101125A - Ink, and inkjet recording method - Google Patents
Ink, and inkjet recording method Download PDFInfo
- Publication number
- JP2017101125A JP2017101125A JP2015233834A JP2015233834A JP2017101125A JP 2017101125 A JP2017101125 A JP 2017101125A JP 2015233834 A JP2015233834 A JP 2015233834A JP 2015233834 A JP2015233834 A JP 2015233834A JP 2017101125 A JP2017101125 A JP 2017101125A
- Authority
- JP
- Japan
- Prior art keywords
- ink
- mass
- pigment
- general formula
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、インク、及びインクジェット記録方法に関する。 The present invention relates to an ink and an ink jet recording method.
食品、飲料、日用品などの軟包装材料にインクを用いて画像を記録する技術が発展してきている。 2. Description of the Related Art Technology for recording images using ink on flexible packaging materials such as food, beverages, and daily necessities has been developed.
前記軟包装材料としては、ポリプロピレン（ＰＰ）、ポリエチレンテレフタレート（ＰＥＴ）、ナイロン（ＯＮＹ）などのプラスチックフィルムが使用されることが多く、中でも、ポリプロピレン（ＰＰ）は、安価であり、成形性、耐薬品性、耐熱性などに優れているため、最も多く使用されている。
近年、ポリプロピレン用のインクとして紫外線硬化型インクが提案されているが、臭気や安全性の面から用途が限定されている。こうした背景もあり、環境負荷が少なく安全性に優れたポリプロピレン用の水性インクの開発が期待されている。
As the flexible packaging material, plastic films such as polypropylene (PP), polyethylene terephthalate (PET), and nylon (ONY) are often used, and among them, polypropylene (PP) is inexpensive, moldable, and resistant. Mostly used because of its excellent chemical and heat resistance.
In recent years, ultraviolet curable inks have been proposed as polypropylene inks, but their applications are limited in terms of odor and safety. Against this background, the development of water-based inks for polypropylene with low environmental impact and excellent safety is expected.
本発明は、ポリプロピレンフィルムに対するインクの広がり性に優れ且つ、保存安定性が良好なインクを提供することを目的とする。 An object of this invention is to provide the ink which is excellent in the spreading property of the ink with respect to a polypropylene film, and has favorable storage stability.
前記課題を解決するための手段としての本発明のインクは、水、顔料、有機溶剤、界面活性剤、及び樹脂を含み、前記界面活性剤が、下記一般式（１）で表される化合物を含み、前記一般式（１）で表される化合物の含有量が、０．５質量％以上１．５質量％以下である。
〔一般式（１）〕
[General formula (1)]
本発明によれば、ポリプロピレンフィルムに対するインクの広がり性に優れ且つ、保存安定性が良好なインクを提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the ink which is excellent in the spreading property of the ink with respect to a polypropylene film, and has favorable storage stability can be provided.
本発明のインクは、水、顔料、有機溶剤、界面活性剤、及び樹脂を含み、前記界面活性剤が、下記一般式（１）で表される化合物を含み、前記一般式（１）で表される化合物の含有量が、０．５質量％以上１．５質量％以下である。
〔一般式（１）〕
本発明のインクは、従来の水性のインクでは、インクがポリプロピレンフィルム上に濡れ広がり難いため、インクの広がり不良が起こり易いという問題があり、前記問題に対しては、インクの付着量を増やせばインクの広がりが改善するが、その場合、インク消費量の増加に伴うランニングコストの増加や印刷物の乾燥性の低下による生産性の低下又は乾燥コストの増加などが問題となるという知見に基づくものである。
The ink of the present invention includes water, a pigment, an organic solvent, a surfactant, and a resin, and the surfactant includes a compound represented by the following general formula (1), and is represented by the general formula (1). The content of the compound to be produced is 0.5% by mass or more and 1.5% by mass or less.
[General formula (1)]
The ink of the present invention has a problem that the conventional water-based ink is difficult to spread on the polypropylene film, so that there is a problem that the ink spreads easily. The spread of ink is improved, but in that case, it is based on the knowledge that an increase in running cost due to an increase in ink consumption, a decrease in productivity due to a decrease in dryness of printed matter, or an increase in drying cost becomes a problem. is there.
＜インク＞
以下、インクに用いる有機溶剤、水、色材、樹脂、添加剤等について説明する。
<Ink>
Hereinafter, the organic solvent, water, color material, resin, additive, and the like used for the ink will be described.
＜界面活性剤＞
前記界面活性剤としては、下記一般式（１）で表される化合物を含み、更に必要に応じてその他の界面活性剤を含む。
〔一般式（１）〕
前記一般式（１）で表される化合物は、トリシロキサンの側鎖の１個と末端の全てがメチル基であり、残りの側鎖１個がポリエーテル基である界面活性剤である。
<Surfactant>
As said surfactant, the compound represented by following General formula (1) is included, and also other surfactant is included as needed.
[General formula (1)]
The compound represented by the general formula (1) is a surfactant in which one of the side chains and the terminal of trisiloxane are all methyl groups, and the remaining one side chain is a polyether group.
前記ポリエーテル基Ｒとしては、−（Ｃ２Ｈ４Ｏ）ａ（Ｃ３Ｈ６Ｏ）ｂＲ１であることが好ましい。ただし、Ｒ１は、水素原子又はメチル基を表し、ａ、ｂは整数であり、ユニット数を表す。前記ａ及びｂは、同時に０になることはない。
前記ａ、ｂとしては、特に制限はなく、目的に応じて適宜選択することができるが、インクの保存安定性の点から、ａが０以上１３以下であることが好ましく、ｂが１以上１３以下であることが好ましい。
The polyether group R is preferably — (C 2 H 4 O) a (C 3 H 6 O) b R 1 . However, R < 1 > represents a hydrogen atom or a methyl group, a and b are integers and represent the number of units. The a and b are not 0 at the same time.
The a and b are not particularly limited and may be appropriately selected depending on the intended purpose. However, a is preferably 0 or more and 13 or less, and b is 1 or more and 13 from the viewpoint of storage stability of the ink. The following is preferable.
前記一般式（１）で表される化合物としては、合成したものを用いてもよく、市販品を使用してもよい。前記市販品としては、例えば、ＴＥＧＯ（登録商標）Ｗｅｔ２４０（ＥＶＯＮＩＫ ＩＮＤＵＳＴＲＩＥＳ社製）などが挙げられる。 As a compound represented by the said General formula (1), what was synthesize | combined may be used and a commercial item may be used. Examples of the commercially available product include TEGO (registered trademark) Wet240 (manufactured by EVONIK INDUSTRIES).
前記一般式（１）で表される化合物を有することによって、ポリプロピレンフィルムに対するインクの広がり性が特異的に向上する。その理由は不明であるが、恐らく、前記一般式（１）で表される化合物とポリプロピレンとの化学構造が似ていることが要因の１つであると考えられる。 By having the compound represented by the general formula (1), the spread of the ink with respect to the polypropylene film is specifically improved. The reason is unknown, but it is probably one of the factors that the chemical structure of the compound represented by the general formula (1) is similar to that of polypropylene.
前記一般式（１）で表される化合物の含有量としては、インク全量に対して、０．５質量％以上１．５質量％以下である。
前記含有量が、０．５質量％以上であるとインクの広がり性を向上でき、１．５質量％以下であると保存安定性を向上できる。
The content of the compound represented by the general formula (1) is 0.5% by mass or more and 1.5% by mass or less with respect to the total amount of the ink.
When the content is 0.5% by mass or more, ink spreading property can be improved, and when the content is 1.5% by mass or less, storage stability can be improved.
＜有機溶剤＞
本発明に使用する有機溶剤としては特に制限されず、水溶性有機溶剤を用いることができる。例えば、アルコール類、多価アルコールアルキルエーテル類や多価アルコールアリールエーテル類などのエーテル類、含窒素複素環化合物、アミド類、アミン類、含硫黄化合物類が挙げられる。
水溶性有機溶剤の具体例としては、例えば、エチレングリコール、ジエチレングリコール、１，２−プロパンジオール、１，３−プロパンジオール、１，２−ブタンジオール、１，３−ブタンジオール、１，４−ブタンジオール、２，３−ブタンジオール、３−メチル−１，３−ブタンジオール、トリエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、１，２−ペンタンジオール、１，３−ペンタンジオール、１，４−ペンタンジオール、２，４−ペンタンジオール、１，５−ペンタンジオール、１，２−ヘキサンジオール、１，６−ヘキサンジオール、１，３−ヘキサンジオール、２，５−ヘキサンジオール、１，５−ヘキサンジオール、グリセリン、１，２，６−ヘキサントリオール、２−エチル−１，３−ヘキサンジオール、エチル−１，２，４−ブタントリオール、１，２，３−ブタントリオール、２，２，４−トリメチル−１，３−ペンタンジオール、ペトリオール等の多価アルコール類、エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、テトラエチレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル等の多価アルコールアルキルエーテル類、エチレングリコールモノフェニルエーテル、エチレングリコールモノベンジルエーテル等の多価アルコールアリールエーテル類、２−ピロリドン、Ｎ−メチル−２−ピロリドン、Ｎ−ヒドロキシエチル−２−ピロリドン、１，３−ジメチル−２−イミダゾリジノン、ε−カプロラクタム、γ−ブチロラクトン等の含窒素複素環化合物、ホルムアミド、Ｎ−メチルホルムアミド、Ｎ，Ｎ−ジメチルホルムアミド、３−メトキシ−Ｎ，Ｎ-ジメチルプロピオンアミド、３−ブトキシ−Ｎ，Ｎ-ジメチルプロピオンアミド等のアミド類、モノエタノールアミン、ジエタノールアミン、トリエチルアミン等のアミン類、ジメチルスルホキシド、スルホラン、チオジエタノール等の含硫黄化合物、プロピレンカーボネート、炭酸エチレン等が挙げられる。
湿潤剤として機能するだけでなく、良好な乾燥性を得られることから、沸点が２５０℃以下の有機溶剤を用いることが好ましい。
<Organic solvent>
The organic solvent used in the present invention is not particularly limited, and a water-soluble organic solvent can be used. Examples include alcohols, ethers such as polyhydric alcohol alkyl ethers and polyhydric alcohol aryl ethers, nitrogen-containing heterocyclic compounds, amides, amines, and sulfur-containing compounds.
Specific examples of the water-soluble organic solvent include, for example, ethylene glycol, diethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,2-butanediol, 1,3-butanediol, and 1,4-butane. Diol, 2,3-butanediol, 3-methyl-1,3-butanediol, triethylene glycol, polyethylene glycol, polypropylene glycol, 1,2-pentanediol, 1,3-pentanediol, 1,4-pentanediol 2,4-pentanediol, 1,5-pentanediol, 1,2-hexanediol, 1,6-hexanediol, 1,3-hexanediol, 2,5-hexanediol, 1,5-hexanediol, Glycerin, 1,2,6-hexanetriol, 2-ethyl-1,3-he Polyhydric alcohols such as sundiol, ethyl-1,2,4-butanetriol, 1,2,3-butanetriol, 2,2,4-trimethyl-1,3-pentanediol, petriol, ethylene glycol mono Polyhydric alcohol alkyl ethers such as ethyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, tetraethylene glycol monomethyl ether, propylene glycol monoethyl ether, ethylene glycol monophenyl ether, ethylene glycol mono Polyhydric alcohol aryl ethers such as benzyl ether, 2-pyrrolidone, N-methyl-2-pyrrolidone, N-hydroxyethyl- -N-containing heterocyclic compounds such as pyrrolidone, 1,3-dimethyl-2-imidazolidinone, ε-caprolactam, γ-butyrolactone, formamide, N-methylformamide, N, N-dimethylformamide, 3-methoxy-N, Amides such as N-dimethylpropionamide and 3-butoxy-N, N-dimethylpropionamide, amines such as monoethanolamine, diethanolamine and triethylamine, sulfur-containing compounds such as dimethylsulfoxide, sulfolane and thiodiethanol, propylene carbonate, Examples thereof include ethylene carbonate.
In addition to functioning as a wetting agent, it is preferable to use an organic solvent having a boiling point of 250 ° C. or lower because good drying properties can be obtained.
前記有機溶剤としては、３−メトキシ−３−メチル−１−ブタノールを含むことが好ましい。
前記３−メトキシ−３−メチル−１−ブタノールには、親水性物質と疎水性物質の馴染みを良くする作用があるため、前記インクが、３−メトキシ−３−メチル−１−ブタノールを含有することにより、ポリプロピレン（ＰＰ）に対する濡れ広がり性が向上し、インクの広がり性が向上する。
前記３−メトキシ−３−メチル−１−ブタノールの含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、前記親水性物質と前記疎水性物質の馴染みを良くする作用が十分に得られる点で、インク全量に対して、２質量％以上が好ましい。また、乾燥性の点で、１０質量％以下が好ましい。
The organic solvent preferably contains 3-methoxy-3-methyl-1-butanol.
Since the 3-methoxy-3-methyl-1-butanol has an effect of improving the familiarity of the hydrophilic substance and the hydrophobic substance, the ink contains 3-methoxy-3-methyl-1-butanol. As a result, wetting spreadability with respect to polypropylene (PP) is improved and ink spreadability is improved.
The content of 3-methoxy-3-methyl-1-butanol is not particularly limited and may be appropriately selected depending on the intended purpose. However, it has an effect of improving the familiarity between the hydrophilic substance and the hydrophobic substance. Is preferably 2% by mass or more with respect to the total amount of ink. Moreover, 10 mass% or less is preferable at the point of drying property.
有機溶剤のインク中における含有量は、特に制限はなく、目的に応じて適宜選択することができるが、インクの乾燥性及び吐出信頼性の点から、１０質量％以上６０質量％以下が好ましく、２０質量％以上６０質量％以下がより好ましい。 The content of the organic solvent in the ink is not particularly limited and can be appropriately selected according to the purpose, but is preferably 10% by mass or more and 60% by mass or less from the viewpoint of the drying property and ejection reliability of the ink, 20 mass% or more and 60 mass% or less are more preferable.
＜水＞
インクにおける水の含有量は、特に制限はなく、目的に応じて適宜選択することができるが、インクの乾燥性及び吐出信頼性の点から、１０質量％以上９０質量％以下が好ましく、２０質量％〜６０質量％がより好ましい。
<Water>
The water content in the ink is not particularly limited and may be appropriately selected depending on the intended purpose, but is preferably 10% by mass or more and 90% by mass or less, and 20% by mass from the viewpoint of ink drying property and ejection reliability. % To 60% by mass is more preferable.
前記水としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、イオン交換水、限外濾過水、逆浸透水、蒸留水等の純水；超純水などが挙げられる。これらは、１種単独で使用してもよいし、２種以上を併用してもよい。 There is no restriction | limiting in particular as said water, According to the objective, it can select suitably, For example, pure water, such as ion-exchange water, ultrafiltration water, reverse osmosis water, distilled water; Ultrapure water etc. are mentioned. . These may be used individually by 1 type and may use 2 or more types together.
＜色材＞
前記色材としては、顔料を使用可能である。
前記顔料としては、無機顔料又は有機顔料を使用することができる。これらは、１種単独で用いてもよく、２種以上を併用してもよい。また、混晶を使用してもよい。
前記顔料としては、例えば、ブラック顔料、イエロー顔料、マゼンダ顔料、シアン顔料、白色顔料、緑色顔料、橙色顔料、金色や銀色などの光沢色顔料やメタリック顔料などを用いることができる。
前記無機顔料としては、例えば、酸化チタン、酸化鉄、炭酸カルシウム、硫酸バリウム、水酸化アルミニウム、バリウムイエロー、カドミウムレッド、クロムイエローに加え、コンタクト法、ファーネス法、サーマル法などの公知の方法によって製造されたカーボンブラックを使用することができる。
また、前記有機顔料としては、例えば、アゾ顔料、多環式顔料（例えば、フタロシアニン顔料、ペリレン顔料、ペリノン顔料、アントラキノン顔料、キナクリドン顔料、ジオキサジン顔料、インジゴ顔料、チオインジゴ顔料、イソインドリノン顔料、キノフラロン顔料等）、染料キレート（例えば、塩基性染料型キレート、酸性染料型キレート等）、ニトロ顔料、ニトロソ顔料、アニリンブラックなどを使用できる。これらの顔料のうち、溶媒と親和性の良いものが好ましく用いられる。その他、樹脂中空粒子、無機中空粒子の使用も可能である。
<Color material>
A pigment can be used as the color material.
As the pigment, an inorganic pigment or an organic pigment can be used. These may be used alone or in combination of two or more. A mixed crystal may be used.
As the pigment, for example, a black pigment, a yellow pigment, a magenta pigment, a cyan pigment, a white pigment, a green pigment, an orange pigment, a glossy pigment such as gold or silver, a metallic pigment, or the like can be used.
Examples of the inorganic pigment include titanium oxide, iron oxide, calcium carbonate, barium sulfate, aluminum hydroxide, barium yellow, cadmium red, and chrome yellow, as well as a known method such as a contact method, a furnace method, and a thermal method. Carbon black can be used.
Examples of the organic pigment include azo pigments, polycyclic pigments (for example, phthalocyanine pigments, perylene pigments, perinone pigments, anthraquinone pigments, quinacridone pigments, dioxazine pigments, indigo pigments, thioindigo pigments, isoindolinone pigments, and quinofullerone. Pigments, etc.), dye chelates (for example, basic dye chelates, acidic dye chelates, etc.), nitro pigments, nitroso pigments, aniline black, and the like. Of these pigments, those having good affinity with the solvent are preferably used. In addition, resin hollow particles and inorganic hollow particles can also be used.
前記顔料の具体例として、黒色用としては、ファーネスブラック、ランプブラック、アセチレンブラック、チャンネルブラック等のカーボンブラック（Ｃ．Ｉ．ピグメントブラック７）類、または銅、鉄（Ｃ．Ｉ．ピグメントブラック１１）、酸化チタン等の金属類、アニリンブラック（Ｃ．Ｉ．ピグメントブラック１）等の有機顔料が挙げられる。
さらに、カラー用としては、Ｃ．Ｉ．ピグメントイエロー１、３、１２、１３、１４、１７、２４、３４、３５、３７、４２（黄色酸化鉄）、５３、５５、７４、８１、８３、９５、９７、９８、１００、１０１、１０４、１０８、１０９、１１０、１１７、１２０、１３８、１５０、１５３、１５５、１８０、１８５、２１３、Ｃ．Ｉ．ピグメントオレンジ５、１３、１６、１７、３６、４３、５１、Ｃ．Ｉ．ピグメントレッド１、２、３、５、１７、２２、２３、３１、３８、４８：２、４８：２（パーマネントレッド２Ｂ（Ｃａ））、４８：３、４８：４、４９：１、５２：２、５３：１、５７：１（ブリリアントカーミン６Ｂ）、６０：１、６３：１、６３：２、６４：１、８１、８３、８８、１０１（べんがら）、１０４、１０５、１０６、１０８（カドミウムレッド）、１１２、１１４、１２２（キナクリドンマゼンタ）、１２３、１４６、１４９、１６６、１６８、１７０、１７２、１７７、１７８、１７９、１８４、１８５、１９０、１９３、２０２、２０７、２０８、２０９、２１３、２１９、２２４、２５４、２６４、Ｃ．Ｉ．ピグメントバイオレット１（ローダミンレーキ）、３、５：１、１６、１９、２３、３８、Ｃ．Ｉ．ピグメントブルー１、２、１５（フタロシアニンブルー）、１５：１、１５：２、１５：３、１５：４（フタロシアニンブルー）、１６、１７：１、５６、６０、６３、Ｃ．Ｉ．ピグメントグリーン１、４、７、８、１０、１７、１８、３６、等が挙げられる。
Specific examples of the pigment include black for carbon black (CI pigment black 7) such as furnace black, lamp black, acetylene black, channel black, or copper, iron (CI pigment black 11). ), Metals such as titanium oxide, and organic pigments such as aniline black (CI Pigment Black 1).
Further, for color use, C.I. I. Pigment Yellow 1, 3, 12, 13, 14, 17, 24, 34, 35, 37, 42 (yellow iron oxide), 53, 55, 74, 81, 83, 95, 97, 98, 100, 101, 104 , 108, 109, 110, 117, 120, 138, 150, 153, 155, 180, 185, 213, C.I. I. Pigment orange 5, 13, 16, 17, 36, 43, 51, C.I. I. Pigment Red 1, 2, 3, 5, 17, 22, 23, 31, 38, 48: 2, 48: 2 (Permanent Red 2B (Ca)), 48: 3, 48: 4, 49: 1, 52: 2, 53: 1, 57: 1 (Brilliant Carmine 6B), 60: 1, 63: 1, 63: 2, 64: 1, 81, 83, 88, 101 (Bengara), 104, 105, 106, 108 ( Cadmium red), 112, 114, 122 (quinacridone magenta), 123, 146, 149, 166, 168, 170, 172, 177, 178, 179, 184, 185, 190, 193, 202, 207, 208, 209, 213, 219, 224, 254, 264, C.I. I. Pigment violet 1 (rhodamine lake), 3, 5: 1, 16, 19, 23, 38, C.I. I. Pigment Blue 1, 2, 15 (phthalocyanine blue), 15: 1, 15: 2, 15: 3, 15: 4 (phthalocyanine blue), 16, 17: 1, 56, 60, 63, C.I. I. Pigment green 1, 4, 7, 8, 10, 17, 18, 36, and the like.
インク中の色材の含有量は、画像濃度の向上、良好な定着性や吐出安定性の点から、０．１質量％以上１５質量％以下が好ましく、より好ましくは１質量％以上１０質量％以下である。 The content of the color material in the ink is preferably 0.1% by mass or more and 15% by mass or less, more preferably 1% by mass or more and 10% by mass from the viewpoints of improvement in image density, good fixability and ejection stability. It is as follows.
顔料をインク中に分散させるには、顔料に親水性官能基を導入して自己分散性顔料とする方法、顔料の表面を樹脂で被覆して分散させる方法、分散剤を用いて分散させる方法、などが挙げられる。
顔料に親水性官能基を導入して自己分散性顔料とする方法としては、例えば、顔料（例えばカーボン）にスルホン基やカルボキシル基等の官能基を付加し水中に分散可能とした自己分散顔料等が使用できる。
顔料の表面を樹脂で被覆して分散させる方法としては、顔料をマイクロカプセルに包含させ、水中に分散可能なものを用いることができる。これは、樹脂被覆顔料と言い換えることができる。この場合、インクに配合される顔料はすべて樹脂に被覆されている必要はなく、本発明の効果が損なわれない範囲において、被覆されない顔料や、部分的に被覆された顔料がインク中に分散していてもよい。
分散剤を用いて分散させる方法としては、界面活性剤に代表される、公知の低分子型の分散剤、高分子型の分散剤を用いて分散する方法が挙げられる。
分散剤としては、顔料に応じて例えば、アニオン界面活性剤、カチオン界面活性剤、両性界面活性剤、ノニオン界面活性剤等を使用することが可能である。
竹本油脂社製ＲＴ−１００（ノニオン系界面活性剤）や、ナフタレンスルホン酸Ｎａホルマリン縮合物も、分散剤として好適に使用できる。
分散剤は１種を単独で用いても、２種以上を併用してもよい。
In order to disperse the pigment in the ink, a method of introducing a hydrophilic functional group into the pigment to form a self-dispersing pigment, a method of dispersing the pigment surface by coating with a resin, a method of dispersing using a dispersant, Etc.
Examples of a method for introducing a hydrophilic functional group into a pigment to form a self-dispersing pigment include a self-dispersing pigment that can be dispersed in water by adding a functional group such as a sulfone group or a carboxyl group to the pigment (for example, carbon) Can be used.
As a method for coating the surface of the pigment with a resin and dispersing it, a method in which the pigment is included in microcapsules and can be dispersed in water can be used. This can be paraphrased as a resin-coated pigment. In this case, it is not necessary that all pigments blended in the ink are coated with a resin, and within a range where the effects of the present invention are not impaired, uncoated pigments and partially coated pigments are dispersed in the ink. It may be.
Examples of the method of dispersing using a dispersant include a method of dispersing using a known low-molecular type dispersant or high-molecular type dispersant represented by a surfactant.
As the dispersant, for example, an anionic surfactant, a cationic surfactant, an amphoteric surfactant, a nonionic surfactant, or the like can be used depending on the pigment.
RT-100 (nonionic surfactant) manufactured by Takemoto Yushi Co., Ltd. and naphthalenesulfonic acid Na formalin condensate can also be suitably used as a dispersant.
A dispersing agent may be used individually by 1 type, or may use 2 or more types together.
本発明のインクの一態様として、前記色材が、スチレン−アクリル樹脂被覆顔料を含有することが、ポリプロピレンへの密着性の点で好ましい。
ここで、前記スチレン−アクリル樹脂被覆顔料とは、前記顔料の表面全体又は部分的にスチレン−アクリル樹脂を被覆させた顔料を意味する。前記顔料を前記スチレン−アクリル樹脂で被覆することによって、前記顔料を水に安定的に分散可能な状態にすることができる。この場合、前記インクに配合される前記顔料は、全て前記スチレン−アクリル樹脂に被覆されている必要はなく、本発明の効果が損なわれない範囲において、被覆されない顔料や、部分的に被覆された前記顔料が前記インク中に分散していてもよい。
As one aspect of the ink of the present invention, the colorant preferably contains a styrene-acrylic resin-coated pigment from the viewpoint of adhesion to polypropylene.
Here, the styrene-acrylic resin-coated pigment means a pigment that is entirely or partially coated with a styrene-acrylic resin. By coating the pigment with the styrene-acrylic resin, the pigment can be stably dispersed in water. In this case, the pigment blended in the ink does not need to be entirely coated with the styrene-acrylic resin, and is not coated or partially coated as long as the effect of the present invention is not impaired. The pigment may be dispersed in the ink.
−スチレン−アクリル樹脂−
前記スチレン−アクリル樹脂は、スチレン系モノマー及びスチレンマクロマーの少なくともいずれかと、アクリル酸モノマー、メタクリル酸モノマー、アクリル酸エステル系モノマー及びメタクリル酸エステル系モノマーの少なくともいずれかと、更に必要に応じてその他のモノマーとを共重合することにより得ることができ、スチレン系モノマー及びスチレンマクロマーの少なくともいずれか由来の構造単位と、アクリル酸モノマー、メタクリル酸モノマー、アクリル酸エステル系モノマー及びメタクリル酸エステル系モノマーの少なくともいずれか由来の構造単位と、更に必要に応じてその他のモノマー由来の構造単位とを有する共重合体である。
-Styrene-Acrylic resin-
The styrene-acrylic resin is composed of at least one of a styrene monomer and a styrene macromer, at least one of an acrylic acid monomer, a methacrylic acid monomer, an acrylic acid ester monomer, and a methacrylic acid ester monomer, and, if necessary, other monomers. A structural unit derived from at least one of a styrene monomer and a styrene macromer, and at least one of an acrylic acid monomer, a methacrylic acid monomer, an acrylate ester monomer, and a methacrylic ester monomer. It is a copolymer which has a structural unit derived from this, and a structural unit derived from another monomer as needed.
前記スチレン−アクリル樹脂としては、例えば、スチレン−アクリル酸共重合体、スチレン−メタクリル酸共重合体、スチレン−メタクリル酸−アクリル酸エステル共重合体、スチレン−α―メチルスチレン−アクリル酸共重合体、スチレン−α―メチルスチレン−アクリル酸−アクリル酸エステル共重合体などが挙げられる。これらの中でも、スチレン−アクリル酸共重合体が好ましい。
なお、共重合体の形態としては、ランダム共重合体、ブロック共重合体、交互共重合体、グラフト共重合体のいずれの形態でも用いることができる。
Examples of the styrene-acrylic resin include styrene-acrylic acid copolymer, styrene-methacrylic acid copolymer, styrene-methacrylic acid-acrylic acid ester copolymer, and styrene-α-methylstyrene-acrylic acid copolymer. And styrene-α-methylstyrene-acrylic acid-acrylic acid ester copolymer. Among these, a styrene-acrylic acid copolymer is preferable.
In addition, as a form of a copolymer, any form of a random copolymer, a block copolymer, an alternating copolymer, and a graft copolymer can be used.
前記スチレン系モノマーとしては、例えば、スチレン、α−メチルスチレン、ｏ−メチルスチレン、ｍ−メチルスチレン、ｐ−メチルスチレン、ｔｅｒｔ−ブチルスチレンなどが挙げられる。 Examples of the styrene monomer include styrene, α-methyl styrene, o-methyl styrene, m-methyl styrene, p-methyl styrene, tert-butyl styrene, and the like.
前記スチレンマクロマーとしては、片末端に重合性官能基を有するものであれば特に制限はなく、目的に応じて適宜選択することができ、例えば、片末端に重合性官能基を有するスチレン単独重合体及び片末端に重合性官能基を有する前記スチレン系モノマーの少なくともいずれかと、前記その他のモノマーとの共重合体などが挙げられる。
前記重合性官能基としては、アクリロイルオキシ基、メタクリロイルオキシ基が好ましい。
前記スチレンマクロマーの数平均分子量としては、５００以上５０，０００以下が好ましく、１，０００以上１０，０００以下がより好ましい。
The styrene macromer is not particularly limited as long as it has a polymerizable functional group at one end, and can be appropriately selected according to the purpose. For example, a styrene homopolymer having a polymerizable functional group at one end And a copolymer of at least one of the styrenic monomers having a polymerizable functional group at one end and the other monomers.
As the polymerizable functional group, an acryloyloxy group and a methacryloyloxy group are preferable.
The number average molecular weight of the styrene macromer is preferably 500 or more and 50,000 or less, and more preferably 1,000 or more and 10,000 or less.
前記アクリル酸エステル系モノマー及び前記メタクリル酸エステル系モノマーとしては、例えば、アクリル酸メチル、メタクリル酸メチル、アクリル酸−ｎ−ブチル、メタクリル酸−ｎ−ブチル、アクリル酸−２−エチルヘキシル、メタクリル酸−２−エチルヘキシル、アクリル酸−ｎ−オクチル、メタクリル酸−ｎ−オクチル、アクリル酸ドデシル、メタクリル酸ドデシル、アクリル酸オクタデシル、メタクリル酸オクタデシル、アクリル酸シクロヘキシル、メタクリル酸シクロヘキシル、アクリル酸イソボルニル、メタクリル酸イソボルニル、アクリル酸−２−アミノエチル、メタクリル酸−２−アミノエチル等の不飽和脂肪酸エステル類；アクリルアミド、メタクリルアミド、Ｎ−メチルアクリルアミド、Ｎ−メチルメタクリルアミド等の不飽和脂肪酸アミド類；アクリロニトリル、メタクリロニトリル等の不飽和ニトリル類；及びこれらの塩などが挙げられる。 Examples of the acrylic acid ester monomer and the methacrylic acid ester monomer include, for example, methyl acrylate, methyl methacrylate, acrylic acid-n-butyl, methacrylic acid-n-butyl, acrylic acid-2-ethylhexyl, methacrylic acid- 2-ethylhexyl, acrylate-n-octyl, methacrylate-n-octyl, dodecyl acrylate, dodecyl methacrylate, octadecyl acrylate, octadecyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, isobornyl acrylate, isobornyl methacrylate, Unsaturated fatty acid esters such as 2-aminoethyl acrylate and 2-aminoethyl methacrylate; acrylamide, methacrylamide, N-methylacrylamide, N-methylmethacrylamide Unsaturated fatty amides; acrylonitrile, unsaturated nitriles such as methacrylonitrile; and the like, and salts thereof.
前記スチレン−アクリル樹脂の重量平均分子量としては、３，０００以上５０，０００以下が好ましく、５，０００以上３０，０００以下がより好ましい。 The weight average molecular weight of the styrene-acrylic resin is preferably 3,000 or more and 50,000 or less, and more preferably 5,000 or more and 30,000 or less.
前記スチレン−アクリル樹脂としては、合成したものを使用してもよいし、市販品を用いてもよい。前記スチレン−アクリル樹脂の市販品としては、例えば、ジョンクリル６２Ｊ（ＢＡＳＦジャパン株式会社製）などが挙げられる。 As said styrene-acrylic resin, what was synthesize | combined may be used and a commercial item may be used. As a commercial item of the said styrene-acrylic resin, Jonkrill 62J (made by BASF Japan Ltd.) etc. are mentioned, for example.
前記スチレン−アクリル樹脂被覆顔料に、水や有機溶剤などの材料を混合してインクを得ることが可能である。また、前記スチレン−アクリル樹脂被覆顔料を水や分散剤などと混合して前記スチレン−アクリル樹脂被覆顔料分散体としたものに、水や有機溶剤などの材料を混合してインクを製造することも可能である。 An ink can be obtained by mixing a material such as water or an organic solvent with the styrene-acrylic resin-coated pigment. In addition, the styrene-acrylic resin-coated pigment is mixed with water or a dispersant to form the styrene-acrylic resin-coated pigment dispersion, and water or an organic solvent is mixed to produce an ink. Is possible.
前記インク中の前記スチレン−アクリル樹脂被覆顔料の含有量としては、印刷物の画像濃度とインクの保存安定性を考慮すると、１質量％以上１０質量％以下が好ましく、２質量％以上８質量％以下がより好ましい。 The content of the styrene-acrylic resin-coated pigment in the ink is preferably 1% by mass or more and 10% by mass or less, preferably 2% by mass or more and 8% by mass or less, considering the image density of the printed matter and the storage stability of the ink. Is more preferable.
＜樹脂＞
インク中に含有する樹脂の種類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、ウレタン樹脂、ポリエステル樹脂、アクリル系樹脂、酢酸ビニル系樹脂、スチレン系樹脂、ブタジエン系樹脂、スチレン−ブタジエン系樹脂、塩化ビニル系樹脂、アクリルスチレン系樹脂、アクリルシリコーン系樹脂などが挙げられる。
これらの樹脂からなる樹脂粒子を用いても良い。樹脂粒子を、水を分散媒として分散した樹脂エマルションの状態で、色材や有機溶剤などの材料と混合してインクを得ることが可能である。前記樹脂粒子としては、適宜合成したものを使用してもよいし、市販品を使用してもよい。また、これらは、１種を単独で用いても、２種類以上の樹脂粒子を組み合わせて用いてもよい。
<Resin>
The type of resin contained in the ink is not particularly limited and can be appropriately selected according to the purpose. For example, urethane resin, polyester resin, acrylic resin, vinyl acetate resin, styrene resin, butadiene type Examples thereof include resins, styrene-butadiene resins, vinyl chloride resins, acrylic styrene resins, and acrylic silicone resins.
Resin particles made of these resins may be used. An ink can be obtained by mixing resin particles with a material such as a colorant or an organic solvent in a resin emulsion state in which water is dispersed as a dispersion medium. As said resin particle, what was synthesize | combined suitably may be used and a commercial item may be used. Moreover, these may be used individually by 1 type, or may be used in combination of 2 or more types of resin particles.
樹脂粒子の体積平均粒径としては、特に制限はなく、目的に応じて適宜選択することができるが、良好な定着性、高い画像硬度を得る点から、１０ｎｍ以上１，０００ｎｍ以下が好ましく、１０ｎｍ以上２００ｎｍ以下がより好ましく、１０ｎｍ以上１００ｎｍ以下が特に好ましい。
前記体積平均粒径は、例えば、粒度分析装置（ナノトラック Ｗａｖｅ−ＵＴ１５１、マイクロトラック・ベル株式会社製）を用いて測定することができる。
The volume average particle diameter of the resin particles is not particularly limited and may be appropriately selected depending on the intended purpose, but is preferably 10 nm or more and 1,000 nm or less from the viewpoint of obtaining good fixability and high image hardness. It is more preferably 200 nm or less and particularly preferably 10 nm or more and 100 nm or less.
The volume average particle diameter can be measured using, for example, a particle size analyzer (Nanotrack Wave-UT151, manufactured by Microtrack Bell Co., Ltd.).
前記樹脂の含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、基材への定着性とインクの保存安定性を考慮すると、前記顔料１００質量部に対して、１０質量部以上５００質量部以下が好ましく、８０質量部以上１８０質量部以下がより好ましい。 The content of the resin is not particularly limited and can be appropriately selected according to the purpose. However, in consideration of fixability to a substrate and storage stability of ink, with respect to 100 parts by mass of the pigment, 10 parts by mass or more and 500 parts by mass or less are preferable, and 80 parts by mass or more and 180 parts by mass or less are more preferable.
インク中の固形分の粒径については、特に制限はなく、目的に応じて適宜選択することができるが、吐出安定性、画像濃度などの画像品質を高くする点から、最大個数換算で最大頻度が２０ｎｍ以上１０００ｎｍ以下が好ましく、２０ｎｍ以上１５０ｎｍ以下がより好ましい。固形分は樹脂粒子や顔料の粒子等が含まれる。粒径は、粒度分析装置（ナノトラック Ｗａｖｅ−ＵＴ１５１、マイクロトラック・ベル株式会社製）を用いて測定することができる。 The particle size of the solid content in the ink is not particularly limited and can be appropriately selected according to the purpose. From the viewpoint of improving the image quality such as ejection stability and image density, the maximum frequency in terms of the maximum number is converted. Is preferably 20 nm to 1000 nm, and more preferably 20 nm to 150 nm. The solid content includes resin particles, pigment particles, and the like. The particle size can be measured using a particle size analyzer (Nanotrack Wave-UT151, manufactured by Microtrack Bell Co., Ltd.).
＜＜ポリエステル系ウレタン樹脂＞＞
前記樹脂としては、ポリプロピレンへの密着性を考慮すると、ポリエステル系ウレタン樹脂が好ましい。
ここで、前記ポリエステル系ウレタン樹脂とは、ポリエステルポリオールとポリイソシアネートとを反応させて得られるウレタン樹脂を意味する。ポリエステル系ウレタン樹脂は、合成したものを使用してもよいし、市販品を用いてもよい。
前記ポリエステル系ウレタン樹脂の製造方法としては、特に限定なく、目的に応じて適宜選択することができ、例えば、無溶剤又は有機溶剤の存在下で、前記ポリエステルポリオールと前記ポリイソシアネートを、イソシアネート基が過剰になる当量比で反応させて、イソシアネート末端ウレタンプレポリマーを製造し、次いで、前記イソシアネート末端ウレタンプレポリマー中のアニオン性基をアンモニアや有機アミン等の中和剤により中和した後、鎖延長剤と反応させ、最後に系内の有機溶剤を除去することによって得る方法などが挙げられる。
<< Polyester urethane resin >>
As the resin, a polyester urethane resin is preferable in consideration of adhesion to polypropylene.
Here, the said polyester-type urethane resin means the urethane resin obtained by making polyester polyol and polyisocyanate react. As the polyester urethane resin, a synthesized one may be used, or a commercially available product may be used.
The method for producing the polyester-based urethane resin is not particularly limited, and can be appropriately selected according to the purpose. For example, the polyester polyol and the polyisocyanate are mixed in the presence of a solvent-free or organic solvent with an isocyanate group. Reaction is carried out in an equivalent ratio to be excessive to produce an isocyanate-terminated urethane prepolymer, and then the anionic group in the isocyanate-terminated urethane prepolymer is neutralized with a neutralizing agent such as ammonia or organic amine, and then chain extension The method obtained by making it react with an agent and finally removing the organic solvent in a system is mentioned.
−ポリエステルポリオール−
前記ポリエステルポリオールとしては、例えば、低分子量のポリオールとポリカルボン酸とをエステル化反応して得られるもの、ε−カプロラクトン等の環状エステル化合物を開環重合反応して得られるポリエステル、及びこれらの共重合ポリエステルなどが挙げられる。
前記低分子量のポリオールとしては、例えば、エチレングリコール、プロピレングリコールなどが挙げられる。
前記ポリカルボン酸としては、例えば、コハク酸、アジピン酸、セバシン酸、ドデカンジカルボン酸、テレフタル酸、イソフタル酸、フタル酸、及びこれらの無水物又はエステル形成性誘導体などが挙げられる。
-Polyester polyol-
Examples of the polyester polyol include those obtained by esterification of low molecular weight polyols and polycarboxylic acids, polyesters obtained by ring-opening polymerization reaction of cyclic ester compounds such as ε-caprolactone, and co-polymers thereof. Examples thereof include polymerized polyester.
Examples of the low molecular weight polyol include ethylene glycol and propylene glycol.
Examples of the polycarboxylic acid include succinic acid, adipic acid, sebacic acid, dodecanedicarboxylic acid, terephthalic acid, isophthalic acid, phthalic acid, and anhydrides or ester-forming derivatives thereof.
−ポリイソシアネート−
前記ポリイソシアネートとしては、特に制限はなく、目的に応じて適宜選択することができ、例えば、１，３−フェニレンジイソシアネート、１，４−フェニレンジイソシアネート、２，４−トリレンジイソシアネート（ＴＤＩ）、２，６−トリレンジイソシアネート、４，４’−ジフェニレンメタンジイソシアネート（ＭＤＩ）、２，４−ジフェニルメタンジイソシアネート、４，４’−ジイソシアナトビフェニル、３，３’−ジメチル−４，４’−ジイソシアナトビフェニル、３，３’−ジメチル−４，４’−ジイソシアナトジフェニルメタン、１，５−ナフチレンジイソシアネート、ｍ−イソシアナトフェニルスルホニルイソシアネート、ｐ−イソシアナトフェニルスルホニルイソシアネート等の芳香族ポリイソシアネート化合物；エチレンジイソシアネート、テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート（ＨＤＩ）、ドデカメチレンジイソシアネート、１，６，１１−ウンデカントリイソシアネート、２，２，４−トリメチルヘキサメチレンジイソシアネート、リジンジイソシアネート、２，６−ジイソシアナトメチルカプロエート、ビス（２−イソシアナトエチル）フマレート、ビス（２−イソシアナトエチル）カーボネート、２−イソシアナトエチル−２，６−ジイソシアナトヘキサノエート等の脂肪族ポリイソシアネート化合物；イソホロンジイソシアネート（ＩＰＤＩ）、４，４’−ジシクロヘキシルメタンジイソシアネート（水素添加ＭＤＩ）、シクロヘキシレンジイソシアネート、メチルシクロヘキシレンジイソシアネート（水素添加ＴＤＩ）、ビス（２−イソシアナトエチル）−４−ジクロヘキセン−１，２−ジカルボキシレート、２，５−ノルボルナンジイソシアネート、２，６−ノルボルナンジイソシアネーネート等の脂環式ポリシアネート化合物などが挙げられる。
これらの中でも、長期耐候性を持つ塗膜を必要とする点から、脂肪族又は脂環式ジイソシアネートが好ましい。
-Polyisocyanate-
The polyisocyanate is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include 1,3-phenylene diisocyanate, 1,4-phenylene diisocyanate, 2,4-tolylene diisocyanate (TDI), 2 , 6-tolylene diisocyanate, 4,4'-diphenylenemethane diisocyanate (MDI), 2,4-diphenylmethane diisocyanate, 4,4'-diisocyanatobiphenyl, 3,3'-dimethyl-4,4'-di Aromatic polyisocyanates such as isocyanatobiphenyl, 3,3′-dimethyl-4,4′-diisocyanatodiphenylmethane, 1,5-naphthylene diisocyanate, m-isocyanatophenylsulfonyl isocyanate, p-isocyanatophenylsulfonyl isocyanate Compound; ethylene di Socyanate, tetramethylene diisocyanate, hexamethylene diisocyanate (HDI), dodecamethylene diisocyanate, 1,6,11-undecane triisocyanate, 2,2,4-trimethylhexamethylene diisocyanate, lysine diisocyanate, 2,6-diisocyanatomethylcapro Aliphatic polyisocyanate compounds such as acrylate, bis (2-isocyanatoethyl) fumarate, bis (2-isocyanatoethyl) carbonate, 2-isocyanatoethyl-2,6-diisocyanatohexanoate; isophorone diisocyanate (IPDI) ), 4,4′-dicyclohexylmethane diisocyanate (hydrogenated MDI), cyclohexylene diisocyanate, methylcyclohexylene diisocyanate (hydrogenated TDI), Scan (2-isocyanatoethyl) -4-Jikurohekisen 1,2-dicarboxylate, 2,5-norbornane diisocyanate, and alicyclic polycyanate compound such as 2,6-norbornane diisocyanate Natick sulfonates and the like.
Among these, aliphatic or alicyclic diisocyanates are preferable because a coating film having long-term weather resistance is required.
−鎖延長剤−
前記鎖延長剤としては、例えば、ポリアミンやその他の活性水素原子含有化合物などが挙げられる。
前記ポリアミンとしては、例えば、エチレンジアミン、１，２−プロパンジアミン、１，６−ヘキサメチレンジアミン、ピペラジン、２，５−ジメチルピペラジン、イソホロンジアミン、４，４’−ジシクロヘキシルメタンジアミン、１，４−シクロヘキサンジアミン等のジアミン類；ジエチレントリアミン、ジプロピレントリアミン、トリエチレンテトラミン等のポリアミン類；ヒドラジン、Ｎ，Ｎ’−ジメチルヒドラジン、１，６−ヘキサメチレンビスヒドラジン等のヒドラジン類；コハク酸ジヒドラジド、アジピン酸ジヒドラジド、グルタル酸ジヒドラジド、セバシン酸ジヒドラジド、イソフタル酸ジヒドラジド等のジヒドラジド類などが挙げられる。
-Chain extender-
Examples of the chain extender include polyamines and other active hydrogen atom-containing compounds.
Examples of the polyamine include ethylenediamine, 1,2-propanediamine, 1,6-hexamethylenediamine, piperazine, 2,5-dimethylpiperazine, isophoronediamine, 4,4′-dicyclohexylmethanediamine, and 1,4-cyclohexane. Diamines such as diamines; Polyamines such as diethylenetriamine, dipropylenetriamine and triethylenetetramine; Hydrazines such as hydrazine, N, N′-dimethylhydrazine and 1,6-hexamethylenebishydrazine; Succinic dihydrazide, Adipic dihydrazide And dihydrazides such as glutaric acid dihydrazide, sebacic acid dihydrazide, and isophthalic acid dihydrazide.
＜添加剤＞
インクには、必要に応じて、界面活性剤、消泡剤、防腐防黴剤、防錆剤、ｐＨ調整剤等を加えても良い。
<Additives>
If necessary, a surfactant, an antifoaming agent, an antiseptic / antifungal agent, a rust inhibitor, a pH adjuster, and the like may be added to the ink.
＜その他の界面活性剤＞
前記その他の界面活性剤としては、特に制限はなく、目的に応じて前記一般式（１）で表される化合物以外の公知の界面活性剤を適宜選択することができ、例えば、シリコーン系界面活性剤、フッ素系界面活性剤、両性界面活性剤、ノニオン系界面活性剤、アニオン系界面活性剤などが挙げられる。
<Other surfactants>
There is no restriction | limiting in particular as said other surfactant, According to the objective, well-known surfactant other than the compound represented by the said General formula (1) can be selected suitably, for example, silicone type surfactant Agents, fluorine surfactants, amphoteric surfactants, nonionic surfactants, anionic surfactants and the like.
前記シリコーン系界面活性剤には特に制限はなく目的に応じて適宜選択することができる。中でも高ｐＨでも分解しないものが好ましく、例えば、側鎖変性ポリジメチルシロキサン、両末端変性ポリジメチルシロキサン、片末端変性ポリジメチルシロキサン、側鎖両末端変性ポリジメチルシロキサン等が挙げられ、変性基としてポリオキシエチレン基、ポリオキシエチレンポリオキシプロピレン基を有するものが、水系界面活性剤として良好な性質を示すので特に好ましい。また、前記シリコーン系界面活性剤として、ポリエーテル変性シリコーン系界面活性剤を用いることもでき、例えば、ポリアルキレンオキシド構造をジメチルシロキサンのＳｉ部側鎖に導入した化合物等が挙げられる。
前記フッ素系界面活性剤としては、例えば、パーフルオロアルキルスルホン酸化合物、パーフルオロアルキルカルボン酸化合物、パーフルオロアルキルリン酸エステル化合物、パーフルオロアルキルエチレンオキサイド付加物及びパーフルオロアルキルエーテル基を側鎖に有するポリオキシアルキレンエーテルポリマー化合物が、起泡性が小さいので特に好ましい。前記パーフルオロアルキルスルホン酸化合物としては、例えば、パーフルオロアルキルスルホン酸、パーフルオロアルキルスルホン酸塩等が挙げられる。前記パーフルオロアルキルカルボン酸化合物としては、例えば、パーフルオロアルキルカルボン酸、パーフルオロアルキルカルボン酸塩等が挙げられる。前記パーフルオロアルキルエーテル基を側鎖に有するポリオキシアルキレンエーテルポリマー化合物としては、パーフルオロアルキルエーテル基を側鎖に有するポリオキシアルキレンエーテルポリマーの硫酸エステル塩、パーフルオロアルキルエーテル基を側鎖に有するポリオキシアルキレンエーテルポリマーの塩等が挙げられる。これらフッ素系界面活性剤における塩の対イオンとしては、Ｌｉ＋、Ｎａ＋、Ｋ＋、ＮＨ４ ＋、（ＮＨ３ＣＨ２ＣＨ２ＯＨ）＋、ＮＨ２（ＣＨ２ＣＨ２ＯＨ）２ ＋、ＮＨ（ＣＨ２ＣＨ２ＯＨ）３ ＋等が挙げられる。
前記両性界面活性剤としては、例えばラウリルアミノプロピオン酸塩、ラウリルジメチルベタイン、ステアリルジメチルベタイン、ラウリルジヒドロキシエチルベタインなどが挙げられる。
前記ノニオン系界面活性剤としては、例えば、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレンアルキルエステル、ポリオキシエチレンアルキルアミン、ポリオキシエチレンアルキルアミド、ポリオキシエチレンプロピレンブロックポリマー、ソルビタン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、アセチレンアルコールのエチレンオキサイド付加物などが挙げられる。
前記アニオン系界面活性剤としては、例えば、ポリオキシエチレンアルキルエーテル酢酸塩、ドデシルベンゼンスルホン酸塩、ラウリル酸塩、ポリオキシエチレンアルキルエーテルサルフェートの塩、などが挙げられる。
これらは、１種を単独で用いても、２種以上を併用してもよい。
There is no restriction | limiting in particular in the said silicone type surfactant, According to the objective, it can select suitably. Among them, those that do not decompose even at high pH are preferable, and examples thereof include side chain modified polydimethylsiloxane, both terminal modified polydimethylsiloxane, one terminal modified polydimethylsiloxane, and side chain both terminal modified polydimethylsiloxane. Those having an oxyethylene group or a polyoxyethylene polyoxypropylene group are particularly preferred because they exhibit good properties as an aqueous surfactant. In addition, as the silicone surfactant, a polyether-modified silicone surfactant can be used, and examples thereof include a compound in which a polyalkylene oxide structure is introduced into the side chain of the Si portion of dimethylsiloxane.
Examples of the fluorosurfactant include a perfluoroalkyl sulfonic acid compound, a perfluoroalkyl carboxylic acid compound, a perfluoroalkyl phosphate ester compound, a perfluoroalkyl ethylene oxide adduct, and a perfluoroalkyl ether group in the side chain. The polyoxyalkylene ether polymer compound is particularly preferred because of its low foamability. Examples of the perfluoroalkyl sulfonic acid compound include perfluoroalkyl sulfonic acid, perfluoroalkyl sulfonate, and the like. Examples of the perfluoroalkylcarboxylic acid compound include perfluoroalkylcarboxylic acid and perfluoroalkylcarboxylate. Examples of the polyoxyalkylene ether polymer compound having a perfluoroalkyl ether group in the side chain include a sulfate ester salt of a polyoxyalkylene ether polymer having a perfluoroalkyl ether group in the side chain and a perfluoroalkyl ether group in the side chain. Examples thereof include salts of polyoxyalkylene ether polymers. The counter ions of the salts in these fluorosurfactants include Li + , Na + , K + , NH 4 + , (NH 3 CH 2 CH 2 OH) + , NH 2 (CH 2 CH 2 OH) 2 + , NH (CH 2 CH 2 OH) 3 + , and the like.
Examples of the amphoteric surfactant include lauryl aminopropionate, lauryl dimethyl betaine, stearyl dimethyl betaine, and lauryl dihydroxyethyl betaine.
Examples of the nonionic surfactant include polyoxyethylene alkylphenyl ether, polyoxyethylene alkyl ester, polyoxyethylene alkylamine, polyoxyethylene alkylamide, polyoxyethylene propylene block polymer, sorbitan fatty acid ester, polyoxyethylene. Examples include sorbitan fatty acid esters and ethylene oxide adducts of acetylene alcohol.
Examples of the anionic surfactant include polyoxyethylene alkyl ether acetate, dodecylbenzene sulfonate, laurate, polyoxyethylene alkyl ether sulfate salt, and the like.
These may be used alone or in combination of two or more.
＜消泡剤＞
消泡剤としては、特に制限はなく、例えば、シリコーン系消泡剤、ポリエーテル系消泡剤、脂肪酸エステル系消泡剤などが挙げられる。これらは、１種を単独で用いても、２種以上を併用してもよい。これらの中でも、破泡効果に優れる点から、シリコーン系消泡剤が好ましい。
<Antifoaming agent>
There is no restriction | limiting in particular as an antifoamer, For example, a silicone type antifoamer, a polyether type | system | group antifoamer, a fatty-acid ester type | system | group antifoamer etc. are mentioned. These may be used alone or in combination of two or more. Among these, a silicone type antifoaming agent is preferable from the viewpoint of excellent foam breaking effect.
＜防腐防黴剤＞
防腐防黴剤としては、特に制限はなく、例えば、１，２−ベンズイソチアゾリン−３−オンなどが挙げられる。
<Antiseptic and fungicide>
The antiseptic / antifungal agent is not particularly limited, and examples thereof include 1,2-benzisothiazolin-3-one.
＜防錆剤＞
防錆剤としては、特に制限はなく、例えば、酸性亜硫酸塩、チオ硫酸ナトリウムなどが挙げられる。
<Rust preventive>
There is no restriction | limiting in particular as a rust preventive agent, For example, acidic sulfite, sodium thiosulfate, etc. are mentioned.
＜ｐＨ調整剤＞
ｐＨ調整剤としては、ｐＨを７以上に調整することが可能であれば、特に制限はなく、ジエタノールアミン、トリエタノールアミン等のアミンなどが挙げられる。
<PH adjuster>
The pH adjuster is not particularly limited as long as the pH can be adjusted to 7 or more, and examples thereof include amines such as diethanolamine and triethanolamine.
＜インクの製造方法＞
本発明のインクの製造方法としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、前記水、前記色材、前記有機溶剤、前記界面活性剤、及び前記樹脂を水性媒体中に分散乃至溶解し、更に必要に応じて撹拌混合して作製する方法などが挙げられる。前記撹拌混合としては、例えば、通常の撹拌羽を用いた撹拌機、マグネチックスターラー、高速の分散機などが挙げられる。
<Ink production method>
The method for producing the ink of the present invention is not particularly limited and may be appropriately selected depending on the intended purpose. For example, the water, the color material, the organic solvent, the surfactant, and the resin are added to an aqueous medium. Examples thereof include a method of dispersing or dissolving therein, and further stirring and mixing as necessary. Examples of the stirring and mixing include a stirrer using a normal stirring blade, a magnetic stirrer, and a high-speed disperser.
インクの物性としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、粘度、表面張力、ｐＨ等が以下の範囲であることが好ましい。
インクの２５℃での粘度は、印字濃度や文字品位が向上し、また、良好な吐出性が得られる点から、５ｍＰａ・ｓ以上３０ｍＰａ・ｓ以下が好ましく、５ｍＰａ・ｓ以上２５ｍＰａ・ｓ以下がより好ましい。ここで、粘度は、例えば回転式粘度計（東機産業社製ＲＥ−８０Ｌ）を使用することができる。測定条件としては、２５℃で、標準コーンローター（１°３４’×Ｒ２４）、サンプル液量１．２ｍＬ、回転数５０ｒｐｍ、３分間で測定可能である。
インクの表面張力としては、記録媒体上で好適にインクがレベリングされ、インクの乾燥時間が短縮される点から、２５℃で、３５ｍＮ／ｍ以下が好ましく、３２ｍＮ／ｍ以下がより好ましい。
インクのｐＨとしては、接液する金属部材の腐食防止の観点から、７〜１２が好ましく、８〜１１がより好ましい。
There is no restriction | limiting in particular as a physical property of an ink, According to the objective, it can select suitably, For example, it is preferable that a viscosity, surface tension, pH, etc. are the following ranges.
The viscosity at 25 ° C. of the ink is preferably 5 mPa · s or more and 30 mPa · s or less, preferably 5 mPa · s or more and 25 mPa · s or less from the viewpoint of improving the printing density and character quality and obtaining good discharge properties. More preferred. Here, for the viscosity, for example, a rotary viscometer (RE-80L manufactured by Toki Sangyo Co., Ltd.) can be used. Measurement conditions are 25 ° C., standard cone rotor (1 ° 34 ′ × R24), sample liquid amount 1.2 mL, rotation speed 50 rpm, and measurement is possible for 3 minutes.
The surface tension of the ink is preferably 35 mN / m or less and more preferably 32 mN / m or less at 25 ° C. from the viewpoint that the ink is suitably leveled on the recording medium and the drying time of the ink is shortened.
The pH of the ink is preferably 7 to 12 and more preferably 8 to 11 from the viewpoint of preventing corrosion of the metal member in contact with the liquid.
＜記録媒体＞
記録媒体としては特に制限はなく、普通紙、光沢紙、特殊紙、布などを用いることもできるが、非浸透性基材を用いても良好な画像形成が可能である。
前記非浸透性基材とは、水透過性、吸収性が低い表面を有する基材であり、内部に多数の空洞があっても外部に開口していない材質も含まれ、より定量的には、ブリストー（Ｂｒｉｓｔｏｗ）法において接触開始から３０ｍｓｅｃ１／２までの水吸収量が１０ｍＬ／ｍ２以下である基材をいう。
前記非浸透性基材としては、例えば、塩化ビニル樹脂フィルム、ポリエチレンテレフタレート（ＰＥＴ）フィルム、ポリプロピレン、ポリエチレン、ポリカーボネートフィルムなどのプラスチックフィルムを、好適に使用することができる。
<Recording medium>
The recording medium is not particularly limited, and plain paper, glossy paper, special paper, cloth, and the like can be used. Good image formation is possible even with a non-permeable substrate.
The non-permeable base material is a base material having a surface with low water permeability and absorbability, and includes materials that do not open to the outside even if there are many cavities inside, more quantitatively. In the Bristow method, the water absorption amount from the start of contact to 30 msec 1/2 is 10 mL / m 2 or less.
As said non-permeable base material, plastic films, such as a vinyl chloride resin film, a polyethylene terephthalate (PET) film, a polypropylene, polyethylene, a polycarbonate film, can be used conveniently, for example.
前記非浸透性基材の中でも、ポリプロピレンフィルム、ポリエチレンテレフタレートフィルム、ナイロンフィルムが、良好な画像が得られる点で好ましい。
前記ポリプロピレンフィルムの市販品としては、例えば、Ｐ−２００２、Ｐ−２１０２、Ｐ−２１６１、Ｐ−４１６６（以上、東洋紡株式会社製）、ＰＡ−２０、ＰＡ−３０、ＰＡ−２０Ｗ（以上、ＳＵＮＴＯＸ社製）、ＦＯＡ、ＦＯＳ、ＦＯＲ（以上、フタムラ化学株式会社製）などが挙げられる。
前記ポリエチレンテレフタレートフィルムの市販品としては、例えば、Ｅ−５１００、Ｅ−５１０２（以上、東洋紡株式会社製）、Ｐ６０、Ｐ３７５（以上、東レ株式会社製）、Ｇ２、Ｇ２Ｐ２、Ｋ、ＳＬ（以上、帝人デュポンフィルム株式会社製）などが挙げられる。
前記ナイロンフィルムの市販品としては、例えば、ハーデンフィルムＮ−１１００、Ｎ−１１０２、Ｎ−１２００（以上、東洋紡株式会社製）、ＯＮ、ＮＸ、ＭＳ、ＮＫ（以上、ユニチカ株式会社製）などが挙げられる。
Among the non-permeable substrates, a polypropylene film, a polyethylene terephthalate film, and a nylon film are preferable in that a good image can be obtained.
As a commercial item of the said polypropylene film, P-2002, P-2102, P-2161, P-4166 (above, the Toyobo Co., Ltd. make), PA-20, PA-30, PA-20W (above, SUNTOX) Co., Ltd.), FOA, FOS, FOR (manufactured by Phutamura Chemical Co., Ltd.) and the like.
As a commercial item of the said polyethylene terephthalate film, E-5100, E-5102 (above, Toyobo Co., Ltd. product), P60, P375 (above, Toray Co., Ltd. make), G2, G2P2, K, SL (above, Teijin DuPont Films Ltd.).
Examples of commercially available nylon films include Harden films N-1100, N-1102, N-1200 (above, manufactured by Toyobo Co., Ltd.), ON, NX, MS, NK (above, manufactured by Unitika Ltd.). Can be mentioned.
＜記録物＞
本発明のインク記録物は、記録媒体上に、本発明のインクを用いて形成された画像を有してなる。
インクジェット記録装置及びインクジェット記録方法により記録して記録物とすることができる。
<Recorded material>
The ink recorded matter of the present invention has an image formed using the ink of the present invention on a recording medium.
Recording can be performed by recording with an inkjet recording apparatus and an inkjet recording method.
＜記録装置、記録方法＞
本発明のインクは、インクジェット記録方式による各種記録装置、例えば、プリンタ、ファクシミリ装置、複写装置、プリンタ／ファックス／コピア複合機、立体造形装置などに好適に使用することができる。
本発明において、記録装置、記録方法とは、記録媒体に対してインクや各種処理液等を吐出することが可能な装置、当該装置を用いて記録を行う方法である。記録媒体とは、インクや各種処理液が一時的にでも付着可能なものを意味する。
この記録装置には、インクを吐出するヘッド部分だけでなく、記録媒体の給送、搬送、排紙に係わる手段、その他、前処理装置、後処理装置と称される装置などを含むことができる。
記録装置、記録方法は、加熱工程に用いる加熱手段、乾燥工程に用いる乾燥手段を有しても良い。加熱手段、乾燥手段には、例えば、記録媒体の印字面や裏面を加熱、乾燥する手段が含まれる。加熱手段、乾燥手段としては、特に限定されないが、例えば、温風ヒーター、赤外線ヒーターを用いることができる。加熱、乾燥は、印字前、印字中、印字後などに行うことができる。
また、記録装置、記録方法は、インクによって文字、図形等の有意な画像が可視化されるものに限定されるものではない。例えば、幾何学模様などのパターン等を形成するもの、３次元像を造形するものも含まれる。
また、記録装置には、特に限定しない限り、吐出ヘッドを移動させるシリアル型装置、吐出ヘッドを移動させないライン型装置のいずれも含まれる。
更に、この記録装置には、卓上型だけでなく、Ａ０サイズの記録媒体への印刷も可能とする広幅の記録装置や、例えばロール状に巻き取られた連続用紙を記録媒体として用いることが可能な連帳プリンタも含まれる。
記録装置の一例について図１乃至図２を参照して説明する。図１は同装置の斜視説明図である。図２はメインタンクの斜視説明図である。記録装置の一例としての画像形成装置４００は、シリアル型画像形成装置である。画像形成装置４００の外装４０１内に機構部４２０が設けられている。ブラック（Ｋ）、シアン（Ｃ）、マゼンタ（Ｍ）、イエロー（Ｙ）の各色用のメインタンク４１０（４１０ｋ、４１０ｃ、４１０ｍ、４１０ｙ）の各インク収容部４１１は、例えばアルミニウムラミネートフィルム等の包装部材により形成されている。インク収容部４１１は、例えば、プラスチックス製の収容容器ケース４１４内に収容される。これによりメインタンク４１０は、各色のインクカートリッジとして用いられる。
一方、装置本体のカバー４０１ｃを開いたときの開口の奥側にはカートリッジホルダ４０４が設けられている。カートリッジホルダ４０４には、メインタンク４１０が着脱自在に装着される。これにより、各色用の供給チューブ４３６を介して、メインタンク４１０の各インク排出口４１３と各色用の吐出ヘッド４３４とが連通し、吐出ヘッド４３４から記録媒体へインクを吐出可能となる。
<Recording apparatus and recording method>
The ink of the present invention can be suitably used for various recording apparatuses using an ink jet recording method, such as a printer, a facsimile apparatus, a copying apparatus, a printer / fax / copier complex machine, and a three-dimensional modeling apparatus.
In the present invention, the recording apparatus and the recording method are an apparatus capable of ejecting ink, various treatment liquids, and the like to a recording medium, and a method of performing recording using the apparatus. The recording medium means a medium on which ink or various processing liquids can be temporarily attached.
The recording apparatus can include not only a head portion that ejects ink but also means for feeding, transporting, and discharging a recording medium, and other devices called pre-processing devices and post-processing devices. .
The recording apparatus and the recording method may include a heating unit used in the heating step and a drying unit used in the drying step. The heating means and the drying means include, for example, a means for heating and drying the printing surface and the back surface of the recording medium. Although it does not specifically limit as a heating means and a drying means, For example, a warm air heater and an infrared heater can be used. Heating and drying can be performed before printing, during printing, after printing, and the like.
Further, the recording apparatus and the recording method are not limited to those in which significant images such as characters and figures are visualized by ink. For example, what forms patterns, such as a geometric pattern, etc. includes what forms a three-dimensional image.
Further, the recording apparatus includes both a serial type apparatus that moves the ejection head and a line type apparatus that does not move the ejection head, unless otherwise specified.
Furthermore, this recording apparatus can use not only a desktop type but also a wide recording apparatus that can print on an A0 size recording medium, for example, a continuous paper wound up in a roll shape as a recording medium. Also included are continuous paper printers.
An example of the recording apparatus will be described with reference to FIGS. FIG. 1 is a perspective view of the apparatus. FIG. 2 is an explanatory perspective view of the main tank. An image forming apparatus 400 as an example of a recording apparatus is a serial type image forming apparatus. A mechanism unit 420 is provided in the exterior 401 of the image forming apparatus 400. Each ink storage portion 411 of the main tank 410 (410k, 410c, 410m, 410y) for each color of black (K), cyan (C), magenta (M), yellow (Y) is packaged, for example, an aluminum laminate film It is formed by a member. The ink storage unit 411 is stored in, for example, a plastic container case 414. As a result, the main tank 410 is used as an ink cartridge for each color.
On the other hand, a cartridge holder 404 is provided on the inner side of the opening when the cover 401c of the apparatus main body is opened. A main tank 410 is detachably attached to the cartridge holder 404. Thus, the ink discharge ports 413 of the main tank 410 and the discharge heads 434 for the respective colors communicate with each other via the supply tubes 436 for the respective colors, and ink can be discharged from the discharge heads 434 to the recording medium.
この記録装置には、インクを吐出する部分だけでなく、前処理装置、後処理装置と称される装置などを含むことができる。
前処理装置、後処理装置の一態様として、ブラック（Ｋ）、シアン（Ｃ）、マゼンタ（Ｍ）、イエロー（Ｙ）などのインクの場合と同様に、前処理液や、後処理液を有する液体収容部と液体吐出ヘッドを追加し、前処理液や、後処理液をインクジェット記録方式で吐出する態様がある。
前処理装置、後処理装置の他の態様として、インクジェット記録方式以外の、例えば、ブレードコート法、ロールコート法、スプレーコート法による前処理装置、後処理装置を設ける態様がある。
The recording apparatus can include not only a portion that ejects ink but also a device called a pre-processing device or a post-processing device.
As one mode of the pretreatment device and the posttreatment device, as in the case of inks such as black (K), cyan (C), magenta (M), and yellow (Y), a pretreatment liquid and a posttreatment liquid are included. There is a mode in which a liquid container and a liquid discharge head are added, and a pretreatment liquid and a posttreatment liquid are discharged by an ink jet recording method.
As another aspect of the pretreatment apparatus and the posttreatment apparatus, there is an aspect in which, for example, a pretreatment apparatus or a posttreatment apparatus other than the ink jet recording method is provided by a blade coating method, a roll coating method, or a spray coating method.
なお、インクの使用方法としては、インクジェット記録方法に制限されず、広く使用することが可能である。インクジェット記録方法以外にも、例えば、ブレードコート法、グラビアコート法、バーコート法、ロールコート法、ディップコート法、カーテンコート法、スライドコート法、ダイコート法、スプレーコート法などが挙げられる。 The method of using the ink is not limited to the ink jet recording method, and can be widely used. Besides the ink jet recording method, for example, a blade coating method, a gravure coating method, a bar coating method, a roll coating method, a dip coating method, a curtain coating method, a slide coating method, a die coating method, a spray coating method and the like can be mentioned.
本発明のインクは、前記記録媒体としての非浸透性基材に高画質に記録できるが、より一層、高画質で耐擦性や密着性の高い画像を形成するため、及び高速の印字条件にも対応できる点で、印字（例えば、インク飛翔工程）中に前記記録媒体を加熱することが好ましい。また、印字（例えば、インク飛翔工程）後に前記記録媒体を加熱する加熱工程を含むことが好ましい。 The ink of the present invention can be recorded with high image quality on the non-permeable substrate as the recording medium, but in order to form an image with higher image quality and higher abrasion resistance and adhesion, and under high-speed printing conditions. However, it is preferable to heat the recording medium during printing (for example, an ink flying process). Moreover, it is preferable to include a heating step of heating the recording medium after printing (for example, an ink flying step).
前記記録媒体の加熱に使用する加熱装置としては、特に制限はなく、目的に応じて公知の加熱装置を使用することができ、例えば、強制空気加熱、輻射加熱、伝導加熱、高周波乾燥、及びマイクロ波乾燥用の装置などが挙げられる。これらは、１種単独で用いても、２種以上を併用してもよい。前記加熱装置は、既存のインクジェットプリンターに組み込んだものであってもよく、既存のインクジェットプリンターに外付けされたものであってもよい。 The heating device used for heating the recording medium is not particularly limited, and a known heating device can be used according to the purpose. For example, forced air heating, radiation heating, conduction heating, high-frequency drying, and micro-heating can be used. For example, an apparatus for wave drying. These may be used alone or in combination of two or more. The heating device may be incorporated into an existing inkjet printer or may be externally attached to an existing inkjet printer.
前記記録媒体の加熱温度としては、特に制限はなく、目的に応じて適宜選択することができるが、印字中の加熱温度は３０℃以上６０℃以下が好ましい。また、印字後の加熱温度は１１０℃以下で制御することが好ましい。前記加熱温度としては、乾燥性を考慮すると高いことが好ましいが、前記加熱温度が上限値以下であると、前記記録媒体がダメージを受けず、インクヘッドが暖まることによる不吐出を防ぐことができ、均一なインクの記録膜を形成可能である。 There is no restriction | limiting in particular as a heating temperature of the said recording medium, Although it can select suitably according to the objective, The heating temperature during printing has preferable 30 to 60 degreeC. The heating temperature after printing is preferably controlled at 110 ° C. or lower. The heating temperature is preferably high in consideration of drying properties, but if the heating temperature is lower than the upper limit value, the recording medium is not damaged and non-ejection due to warming of the ink head can be prevented. A uniform ink recording film can be formed.
本発明のインクは、ポリプロピレンフィルムに対するインクの広がり性に優れ且つ、保存安定性も良好なインクである。本発明のインクを用いることで、ポリプロピレン上により少量のインクで印刷できるようになるので、インク使用量減によるランニングコスト低減や印刷物の乾燥性向上による生産性向上が可能となる。 The ink of the present invention is an ink having excellent ink spreading properties with respect to a polypropylene film and good storage stability. By using the ink of the present invention, it becomes possible to print with a small amount of ink on polypropylene, so that the running cost can be reduced by reducing the amount of ink used and the productivity can be improved by improving the drying property of the printed matter.
以下、実施例に基づいて本発明をより具体的に説明するが、本発明は以下の実施例に制限されるものではない。 EXAMPLES Hereinafter, although this invention is demonstrated more concretely based on an Example, this invention is not restrict | limited to a following example.
（調製例１）
＜スチレン−アクリル樹脂被覆ブラック顔料分散体の調製＞
スチレン１１．２ｇ、アクリル酸２．８ｇ、ラウリルメタクリレート１２ｇ、ポリエチレングリコールメタクリレート４ｇ、スチレンマクロマー（商品名：ＡＳ−６、東亞合成株式会社製）４ｇ、及びメルカプトエタノール０．４ｇを混合し、６５℃に昇温した。次に、スチレン１００．８ｇ、アクリル酸２５．２ｇ、ラウリルメタクリレート１０８ｇ、ポリエチレングリコールメタクリレート３６ｇ、ヒドロキシルエチルメタクリレート６０ｇ、スチレンマクロマー（商品名：ＡＳ−６、東亞合成株式会社製）３６ｇ、メルカプトエタノール３．６ｇ、アゾビスメチルバレロニトリル２．４ｇ、及びメチルエチルケトン１８ｇの混合溶液を、２．５時間かけてフラスコ内に滴下した。滴下後、アゾビスメチルバレロニトリル０．８ｇ及びメチルエチルケトン１８ｇの混合溶液を０．５時間かけてフラスコ内に滴下した。６５℃で１時間熟成した後、アゾビスメチルバレロニトリル０．８ｇを添加し、さらに１時間熟成した。反応終了後、フラスコ内にメチルエチルケトン３６４ｇを添加し、固形分濃度５０質量％のポリマー溶液Ａを８００ｇ得た。
次いで、ポリマー溶液Ａを２８ｇ、カーボンブラック（Ｂｌａｃｋ Ｐｅａｒｌｓ １０００、Ｃａｂｏｔ Ｃｏｒｐｏｒａｔｉｏｎ社製）４２ｇ、１ｍｏｌ／Ｌの水酸化カリウム水溶液１３．６ｇ、メチルエチルケトン２０ｇ、及び水１３．６ｇを十分に撹拌した後、ロールミルで混練した。得られたペーストを純水２００ｇに入れて充分に撹拌した後、エバポレータでメチルエチルケトンを除去し、平均孔径５μｍのメンブランフィルター（ＰＴＦＥタイプ、メルク社製）で加圧濾過した後、固形分濃度が２０質量％になるように水分量を調整し、固形分濃度２０質量％のスチレン−アクリル樹脂被覆ブラック顔料分散体を得た。
(Preparation Example 1)
<Preparation of styrene-acrylic resin-coated black pigment dispersion>
11.2 g of styrene, 2.8 g of acrylic acid, 12 g of lauryl methacrylate, 4 g of polyethylene glycol methacrylate, 4 g of styrene macromer (trade name: AS-6, manufactured by Toagosei Co., Ltd.) and 0.4 g of mercaptoethanol are mixed at 65 ° C. The temperature was raised to. Next, 100.8 g of styrene, 25.2 g of acrylic acid, 108 g of lauryl methacrylate, 36 g of polyethylene glycol methacrylate, 60 g of hydroxylethyl methacrylate, 36 g of styrene macromer (trade name: AS-6, manufactured by Toagosei Co., Ltd.), mercaptoethanol A mixed solution of 6 g, azobismethylvaleronitrile 2.4 g, and methyl ethyl ketone 18 g was dropped into the flask over 2.5 hours. After dropping, a mixed solution of 0.8 g of azobismethylvaleronitrile and 18 g of methyl ethyl ketone was dropped into the flask over 0.5 hours. After aging at 65 ° C. for 1 hour, 0.8 g of azobismethylvaleronitrile was added, and further aging was performed for 1 hour. After completion of the reaction, 364 g of methyl ethyl ketone was added to the flask to obtain 800 g of polymer solution A having a solid content concentration of 50% by mass.
Next, 28 g of the polymer solution A, 42 g of carbon black (Black Pearls 1000, manufactured by Cabot Corporation), 13.6 g of a 1 mol / L potassium hydroxide aqueous solution, 20 g of methyl ethyl ketone, and 13.6 g of water were sufficiently stirred, and then a roll mill Kneaded. After the obtained paste was put in 200 g of pure water and sufficiently stirred, methyl ethyl ketone was removed by an evaporator, and after pressure filtration with a membrane filter (PTFE type, manufactured by Merck & Co., Inc.) having an average pore size of 5 μm, the solid content concentration was 20 The amount of water was adjusted so as to be mass%, and a styrene-acrylic resin-coated black pigment dispersion having a solid content concentration of 20 mass% was obtained.
（調製例２）
＜スチレン−アクリル樹脂被覆シアン顔料分散体の調製＞
調製例１において、カーボンブラックの代わりにピグメントブルー１５：４（ＳＭＡＲＴ Ｃｙａｎ ３１５４ＢＡ、ＳＥＮＳＩＥＮＴ社製）を使用した以外は、調製例１と同様にして固形分濃度２０質量％のスチレン−アクリル樹脂被覆シアン顔料分散体を得た。
(Preparation Example 2)
<Preparation of styrene-acrylic resin-coated cyan pigment dispersion>
Styrene-acrylic resin-coated cyan with a solid content concentration of 20% by mass in the same manner as in Preparation Example 1, except that Pigment Blue 15: 4 (SMART Cyan 3154BA, manufactured by SENSIENT) was used instead of carbon black. A pigment dispersion was obtained.
（調製例３）
＜スチレン−アクリル樹脂被覆マゼンダ顔料分散体の調製＞
調製例１において、カーボンブラックの代わりにピグメントレッド１２２（Ｐｉｇｍｅｎｔ Ｒｅｄ １２２、Ｓｕｎ Ｃｈｅｍｉｃａｌ社製）を使用した以外は、調製例１と同様にして固形分濃度２０質量％のスチレン−アクリル樹脂被覆マゼンタ顔料分散体を得た。
(Preparation Example 3)
<Preparation of styrene-acrylic resin-coated magenta pigment dispersion>
A styrene-acrylic resin-coated magenta pigment having a solid concentration of 20% by mass in the same manner as in Preparation Example 1 except that Pigment Red 122 (Pigment Red 122, manufactured by Sun Chemical Co.) was used instead of carbon black in Preparation Example 1. A dispersion was obtained.
（調製例４）
＜スチレン−アクリル樹脂被覆イエロー顔料分散体の調製＞
調製例１において、カーボンブラックの代わりにピグメントイエロー７４（ＳＭＡＲＴ Ｙｅｌｌｏｗ ３０７４ＢＡ、ＳＥＮＳＩＥＮＴ社製）を使用した以外は、調製例１と同様にして固形分濃度２０質量％のスチレン−アクリル樹脂被覆イエロー顔料分散体を得た。
(Preparation Example 4)
<Preparation of styrene-acrylic resin-coated yellow pigment dispersion>
Dispersion of styrene-acrylic resin-coated yellow pigment having a solid content concentration of 20% by mass in the same manner as in Preparation Example 1, except that Pigment Yellow 74 (SMART Yellow 3074BA, manufactured by SENSIENT) was used instead of carbon black. Got the body.
（調製例５）
＜自己分散型ブラック顔料分散体の調製＞
Ｃａｂｏｔ Ｃｏｒｐｏｒａｔｉｏｎ社製のカーボンブラック（Ｂｌａｃｋ Ｐｅａｒｌｓ １０００）１００ｇを、２．５Ｎ（規定）の次亜塩素酸ナトリウム溶液３，０００ｍＬに添加し、温度６０℃、速度３００ｒｐｍで撹拌し、１０時間反応させて酸化処理を行い、カーボンブラックの表面にカルボン酸基が付与された顔料を得た。
この反応液を濾過し、濾別したカーボンブラックを水酸化ナトリウム溶液で中和し、限外濾過を行い、顔料分散液を得た。
次いで、該顔料分散体とイオン交換水を用いて透析膜による限外濾過を行い、さらに超音波分散を行った後、固形分濃度が２０質量％になるように水分量を調整し、固形分濃度２０質量％の自己分散型ブラック顔料分散体を得た。
(Preparation Example 5)
<Preparation of self-dispersing black pigment dispersion>
100 g of carbon black (Black Pearls 1000) manufactured by Cabot Corporation is added to 3,000 mL of 2.5N (normal) sodium hypochlorite solution, stirred at a temperature of 60 ° C. and a speed of 300 rpm, and allowed to react for 10 hours. Oxidation treatment was performed to obtain a pigment having a carboxylic acid group added to the surface of carbon black.
This reaction solution was filtered, and the carbon black separated by filtration was neutralized with a sodium hydroxide solution and subjected to ultrafiltration to obtain a pigment dispersion.
Next, ultrafiltration through a dialysis membrane is performed using the pigment dispersion and ion-exchanged water, and after ultrasonic dispersion, the water content is adjusted so that the solid content concentration is 20% by mass, A self-dispersing black pigment dispersion having a concentration of 20% by mass was obtained.
（調製例６）
＜分散剤分散型ブラック顔料分散体の調製＞
Ｃａｂｏｔ Ｃｏｒｐｏｒａｔｉｏｎ社製のカーボンブラック（Ｂｌａｃｋ Ｐｅａｒｌｓ １０００）１００ｇと分散剤としてのナフタレンスルホン酸ナトリウムホルマリン縮合物（パイオニンＡ−４５−ＰＮ、竹本油脂株式会社製）１５ｇとイオン交換水２８０ｇとの混合物をプレミックスした後、ダイノーミル（シンマルエンタープライゼス社製）で直径０．３ｍｍのジルコニアビーズを用いて、回転速度１０ｍ／ｓｅｃ、液温１０℃の条件で３０分間分散した。
次いで、顔料分散体とジルコニアビーズを分離し、平均孔径０．８μｍメンブレンフィルター（セルロースアセテートタイプ、ＡＤＶＡＮＴＥＣ社製））で濾過した後、固形分濃度が２０質量％になるように水分量を調整し、固形分濃度２０質量％の分散剤分散型ブラック顔料分散体を得た。
(Preparation Example 6)
<Preparation of dispersant-dispersed black pigment dispersion>
A mixture of 100 g of carbon black (Black Pearls 1000) manufactured by Cabot Corporation, 15 g of sodium naphthalene sulfonate formalin condensate (Pionin A-45-PN, manufactured by Takemoto Yushi Co., Ltd.) as a dispersant and 280 g of ion-exchanged water is pre-treated. After mixing, the mixture was dispersed with a dyno mill (manufactured by Shinmaru Enterprises Co., Ltd.) using zirconia beads having a diameter of 0.3 mm for 30 minutes at a rotational speed of 10 m / sec and a liquid temperature of 10 ° C.
Next, the pigment dispersion and zirconia beads are separated, filtered through a membrane filter having an average pore size of 0.8 μm (cellulose acetate type, manufactured by ADVANTEC), and the water content is adjusted so that the solid content concentration is 20% by mass. A dispersant-dispersed black pigment dispersion having a solid content concentration of 20% by mass was obtained.
（調製例７）
＜ポリエステル系ウレタン樹脂エマルションの調製＞
撹拌機、還流冷却管及び温度計を挿入した反応容器に、ポリエステルポリオール（ポリライトＯＤ−Ｘ−２４２０、ＤＩＣ株式会社製）１，５００ｇ、２，２−ジメチロールプロピオン酸（ＤＭＰＡ）２２０ｇ、及びＮ−メチルピロリドン（ＮＭＰ）１，３４７ｇを窒素気流下で仕込み、６０℃に加熱してＤＭＰＡを溶解させた。次いで、４，４’−ジシクロヘキシルメタンジイソシアネート１，４４５ｇ、触媒としてのジブチルスズジラウリレート２．６ｇを加えて９０℃まで加熱し、５時間かけてウレタン化反応を行い、イソシアネート末端ウレタンプレポリマーを得た。
この反応混合物を８０℃まで冷却し、これにトリエチルアミン１４９ｇを添加及び混合したものの中から４，３４０ｇを抜き出して、強撹拌下、水５，４００ｇ及びトリエチルアミン１５ｇの混合溶液の中に加えた。次いで、氷１，５００ｇを投入し、３５質量％の２−メチル−１，５−ペンタンジアミン水溶液６２６ｇを加えて鎖延長反応を行った後、水分量を調整し、固形分濃度３０質量％のポリエステル系ウレタン樹脂エマルションを得た。
(Preparation Example 7)
<Preparation of polyester urethane resin emulsion>
In a reaction vessel into which a stirrer, a reflux condenser and a thermometer were inserted, 1,500 g of polyester polyol (Polylite OD-X-2420, manufactured by DIC Corporation), 220 g of 2,2-dimethylolpropionic acid (DMPA), and N -1,347 g of methylpyrrolidone (NMP) was charged in a nitrogen stream and heated to 60 ° C to dissolve DMPA. Next, 1,445 g of 4,4′-dicyclohexylmethane diisocyanate and 2.6 g of dibutyltin dilaurate as a catalyst were added and heated to 90 ° C. to carry out a urethanization reaction for 5 hours to obtain an isocyanate-terminated urethane prepolymer. It was.
The reaction mixture was cooled to 80 ° C., 4,340 g was extracted from the mixture in which 149 g of triethylamine was added and mixed, and added to a mixed solution of 5,400 g of water and 15 g of triethylamine with vigorous stirring. Next, 1,500 g of ice was added, 626 g of a 35% by mass 2-methyl-1,5-pentanediamine aqueous solution was added to carry out a chain extension reaction, the water content was adjusted, and the solid content concentration was 30% by mass. A polyester urethane resin emulsion was obtained.
（調製例８）
＜アクリル樹脂エマルションの調製＞
撹拌機、還流コンデンサー、滴下装置、及び温度計を備えた反応容器に、イオン交換水９００ｇ、及びラウリル硫酸ナトリウム１ｇを仕込み、撹拌下に窒素置換しながら７０℃まで昇温した。内温を７０℃に保ち、重合開始剤として過硫酸カリウム４ｇを添加し、溶解後、予めイオン交換水４５０ｇ、ラウリル硫酸ナトリウム３ｇにアクリルアミド２０ｇにスチレン３６５ｇ、ブチルアクリレート５４５ｇ、及びメタクリル酸１０ｇを撹拌下で加えて作製した乳化物を、反応溶液内に連続的に４時間かけて滴下した。滴下終了後、３時間の熟成を行った。得られた水性エマルションを常温まで冷却し、水酸化ナトリウム水溶液でｐＨ８に調整した後、水分量を調整し、固形分濃度３０質量％のアクリル樹脂エマルションを得た。
(Preparation Example 8)
<Preparation of acrylic resin emulsion>
A reaction vessel equipped with a stirrer, a reflux condenser, a dropping device, and a thermometer was charged with 900 g of ion-exchanged water and 1 g of sodium lauryl sulfate, and the temperature was raised to 70 ° C. while purging with nitrogen under stirring. Maintaining the internal temperature at 70 ° C., adding 4 g of potassium persulfate as a polymerization initiator, dissolving, and previously stirring 450 g of ion exchange water, 3 g of sodium lauryl sulfate, 20 g of acrylamide, 365 g of styrene, 545 g of butyl acrylate, and 10 g of methacrylic acid The emulsion prepared by adding below was continuously dropped into the reaction solution over 4 hours. After completion of the dropwise addition, aging was performed for 3 hours. The obtained aqueous emulsion was cooled to room temperature and adjusted to pH 8 with an aqueous sodium hydroxide solution, and then the water content was adjusted to obtain an acrylic resin emulsion having a solid content concentration of 30% by mass.
（実施例１）
スチレン−アクリル樹脂被覆顔料ブラック分散体２０．０質量％、ポリエステル系ウレタン樹脂エマルション２０．０質量％、３−メトキシ−３−メチル−１−ブタノール４．０質量％、１，２−プロパンジオール２５．０質量％、下記一般式（１）で表される界面活性剤（ＴＥＧＯ（登録商標）Ｗｅｔ２４０、ＥＶＯＮＩＫ ＩＮＤＵＳＴＲＩＥＳ社製）１．０質量％、防腐防黴剤（プロキセルＬＶ、アビシア社製）０．１質量％、及びイオン交換水２９．９質量％（残量）を混合撹拌し、平均孔径０．８μｍメンブレンフィルター（セルロールアセテートタイプ、ＡＤＶＡＮＴＥＣ社製）にて濾過することにより、実施例１のインクを作製した。
Example 1
Styrene-acrylic resin-coated pigment black dispersion 20.0% by mass, polyester-based urethane resin emulsion 20.0% by mass, 3-methoxy-3-methyl-1-butanol 4.0% by mass, 1,2-propanediol 25 0.0% by mass, surfactant represented by the following general formula (1) (TEGO (registered trademark) Wet240, EVONIK INDUSTRIES) 1.0% by mass, antiseptic / antifungal agent (Proxel LV, manufactured by Avicia) 0 Example 1 by mixing and stirring 1% by mass and 29.9% by mass of ion-exchanged water (remaining amount) and filtering with an average pore size 0.8 μm membrane filter (cellulose acetate type, manufactured by ADVANTEC). An ink was prepared.
（実施例２〜１１、及び比較例１〜５）
実施例１において、下記表１−１〜表１−３に記載した処方に変更した以外は、実施例１と同様にして、実施例２〜１１、及び比較例１〜５のインクを作製した。
(Examples 2 to 11 and Comparative Examples 1 to 5)
In Example 1, inks of Examples 2 to 11 and Comparative Examples 1 to 5 were prepared in the same manner as Example 1, except that the formulations described in Table 1-1 to Table 1-3 were changed. .
なお、前記表１−１〜表１−３中、「一般式（１）で表される界面活性剤」としてＴＥＧＯ（登録商標）Ｗｅｔ２４０（ＥＶＯＮＩＫ ＩＮＤＵＳＴＲＩＥＳ社製）を用い、「比較界面活性剤」として、ＴＥＧＯ（登録商標）Ｗｅｔ２７０（ＥＶＯＮＩＫ ＩＮＤＵＳＴＲＩＥＳ社製）を用いた。
ここで、ＴＥＧＯ（登録商標）Ｗｅｔ２４０は、下記一般式（１）で表される通り、トリシロキサンの側鎖の１個と末端の全てがメチル基で、残りの側鎖１個がポリエーテル基の界面活性剤であり、ＴＥＧＯ（登録商標）Ｗｅｔ２７０は、ヘプタシロキサンの側鎖の９個と末端の全てがメチル基で、残りの側鎖１個がポリエーテル基の界面活性剤である。
〔一般式（１）〕
Here, as shown in the following general formula (1), TEGO (registered trademark) Wet240 is one of trisiloxane side chains and all of the terminals are methyl groups, and the remaining one side chain is a polyether group. TEGO (registered trademark) Wet 270 is a surfactant in which nine side chains and all ends of heptasiloxane are methyl groups, and the remaining one side chain is a polyether group.
[General formula (1)]
作製した実施例１〜１１、及び比較例１〜５のインクについて、以下のようにして、「インクの広がり性」、及び「保存安定性」を評価した。結果を下記表２に示す。 For the inks of Examples 1 to 11 and Comparative Examples 1 to 5, the “ink spreadability” and “storage stability” were evaluated as follows. The results are shown in Table 2 below.
＜インクの広がり性評価＞
作製したインクをインクジェットプリンター（株式会社リコー製ＩＰＳｉＯ ＧＸｅ５５００）に充填し、ポリプロピレンフィルム（パイレンＰ２１０２、東洋紡株式会社製）上に通常印刷で使用するインク量の７０質量％のインク量（６ｇ／ｃｍ２）で１０ｃｍ×１０ｃｍのベタ画像を印刷し、８０℃、５分間の条件で乾燥させた。次いで、印刷されたベタ画像をデジタルマイクロスコープ（ＶＨＸ−２００、株式会社キーエンス製）を用いて解析することによりインク付着面積（印刷部分全体に対してインク付着部分が占める割合）を測定し、下記評価基準により評価した。なお、Ａ評価は非常に優れたレベル、Ｂ評価は使用上問題のないレベル、Ｃ評価は実用性が低いレベルである。
［評価基準］
Ａ：インク付着面積が、９７％超
Ｂ：インク付着面積が、９５％超かつ９７％以下
Ｃ：インク付着面積が、９５％以下
<Evaluation of ink spreadability>
The prepared ink is filled in an ink jet printer (IPSiO GXe5500 manufactured by Ricoh Co., Ltd.), and an ink amount (6 g / cm 2 ) of 70% by mass of the ink amount used for normal printing on a polypropylene film (Pyrene P2102, manufactured by Toyobo Co., Ltd.). ) Was printed with a solid image of 10 cm × 10 cm, and dried at 80 ° C. for 5 minutes. Next, by measuring the printed solid image using a digital microscope (VHX-200, manufactured by Keyence Corporation), the ink adhesion area (the ratio of the ink adhesion portion to the entire printing portion) is measured. Evaluation was based on the evaluation criteria. In addition, A evaluation is a very excellent level, B evaluation is a level with no problem in use, and C evaluation is a low practicality level.
[Evaluation criteria]
A: Ink adhesion area exceeds 97% B: Ink adhesion area exceeds 95% and 97% or less C: Ink adhesion area is 95% or less
＜保存安定性評価＞
作製したインクをインクカートリッジに充填して７０℃で３週間保存し、保存前の粘度に対する保存後の粘度の変化率を下記式から求め、下記の評価基準に基づいて、「インクの保存安定性」を評価した。なお、Ａ評価は非常に優れたレベル、Ｂ評価は使用上問題のないレベル、Ｃ評価は実用性が低いレベルである。
［評価基準］
Ａ：保存前後の粘度変化率が、±５％以内である
Ｂ：保存前後の粘度変化率が、±５％超かつ±１０％以内である
Ｃ：保存前後の粘度変化率が、±１０％を超えている
<Storage stability evaluation>
The prepared ink is filled in an ink cartridge, stored at 70 ° C. for 3 weeks, the change rate of the viscosity after storage with respect to the viscosity before storage is obtained from the following formula, and based on the following evaluation criteria, “ink storage stability” Was evaluated. In addition, A evaluation is a very excellent level, B evaluation is a level with no problem in use, and C evaluation is a low practicality level.
[Evaluation criteria]
A: Viscosity change rate before and after storage is within ± 5% B: Viscosity change rate before and after storage is more than ± 5% and within ± 10% C: Viscosity change rate before and after storage is ± 10% Is over
実施例１〜１１のインクは、本発明の特に好ましい例である。実施例８のインクは、一般式（１）で表される化合物の量が少ないためインクの広がり性が他の実施例と比べて劣るが、Ｂ評価なので使用上問題ないレベルである。実施例９のインクは、一般式（１）で表される化合物の量が多いため保存安定性が他の実施例と比べて劣るが、Ｂ評価なので使用上問題のないレベルである。実施例１０のインクは、「３−メトキシ−３−メチル−１−ブタノールの含有量が、２質量％以上」を満たさない例であり、インクの広がり性が他の実施例と比べて劣るが、Ｂ評価なので使用上問題のないレベルである。これらの結果から、本発明のインクは、ポリプロピレン（ＰＰ）フィルムに対するインクの広がり性に優れており、少量のインクで十分なインクの広がり性を示し、保存安定性も良好であることがわかる。 The inks of Examples 1 to 11 are particularly preferred examples of the present invention. The ink of Example 8 is inferior in ink spreadability to other examples because the amount of the compound represented by the general formula (1) is small. The ink of Example 9 is inferior in storage stability to the other examples because of the large amount of the compound represented by the general formula (1), but is at a level that causes no problem in use because of B evaluation. The ink of Example 10 is an example that does not satisfy “the content of 3-methoxy-3-methyl-1-butanol is 2% by mass or more”, and the spreadability of the ink is inferior to other examples. Since it is B evaluation, it is a level with no problem in use. From these results, it can be seen that the ink of the present invention is excellent in the spread of the ink with respect to the polypropylene (PP) film, exhibits a sufficient spread of the ink with a small amount of ink, and has a good storage stability.
比較例１のインクは、一般式（１）で表される化合物の量が０．５質量％未満のインクの例であるが、インクの広がり性がＣ評価のため実用性が低いと言える。比較例２のインクは、一般式（１）で表される化合物の量が１．５質量％を超えるインクの例であるが、保存安定性がＣ評価のため実用性が低いと言える。比較例３〜５のインクは、一般式（１）で表される化合物以外の界面活性剤を使用した場合の例であるが、いずれもインクの広がり性がＣ評価のため実用性が低いと言える。 The ink of Comparative Example 1 is an example of an ink in which the amount of the compound represented by the general formula (1) is less than 0.5% by mass, but it can be said that the ink spreadability is low due to C evaluation. The ink of Comparative Example 2 is an example of an ink in which the amount of the compound represented by the general formula (1) exceeds 1.5% by mass, but it can be said that the storage stability is not practical because of C evaluation. The inks of Comparative Examples 3 to 5 are examples in the case where a surfactant other than the compound represented by the general formula (1) is used. I can say that.
本発明の態様としては、例えば、以下のとおりである。
＜１＞ 水、顔料、有機溶剤、界面活性剤、及び樹脂を含み、
前記界面活性剤が、下記一般式（１）で表される化合物を含み、
前記一般式（１）で表される化合物の含有量が、０．５質量％以上１．５質量％以下であることを特徴とするインクである。
〔一般式（１）〕
＜２＞ 前記有機溶剤が、３−メトキシ−３−メチル−１−ブタノールを含む前記＜１＞に記載のインクである。
＜３＞ 前記３−メトキシ−３−メチル−１−ブタノールの含有量が、２質量％以上である前記＜２＞に記載のインクである。
＜４＞ 前記３−メトキシ−３−メチル−１−ブタノールの含有量が、２質量％以上１０質量％以下である前記＜３＞に記載のインクである。
＜５＞ 前記一般式（１）のポリエーテル基Ｒが、−（Ｃ２Ｈ４Ｏ）ａ（Ｃ３Ｈ６Ｏ）ｂＲ１（ただし、Ｒ１は、水素原子又はメチル基を表し、ａ、ｂは整数を表す。）である前記＜１＞から＜４＞のいずれかに記載のインクである。
＜６＞ 前記ａが０以上１３以下であり、前記ｂが１以上１３以下である前記＜５＞に記載のインクである。
＜７＞ 前記顔料が、顔料の表面全体又は部分的にスチレン−アクリル樹脂を被覆させたスチレン−アクリル樹脂被覆顔料を含有する前記＜１＞から＜６＞のいずれかに記載のインクである。
＜８＞ 前記顔料が、自己分散型顔料を含有する前記＜１＞から＜７＞のいずれかに記載のインクである。
＜９＞ 前記顔料が、分散剤分散型顔料を含有する前記＜１＞から＜８＞のいずれかに記載のインクである。
＜１０＞ 前記有機溶剤の含有量が、２０質量％以上６０質量％以下である前記＜１＞から＜９＞のいずれかに記載のインクである。
＜１１＞ 前記樹脂が、ポリエステル系ウレタン樹脂及びアクリル樹脂の少なくともいずれかを含有する前記＜１＞から＜１０＞のいずれかに記載のインクである。
＜１２＞ 前記＜１＞から＜１１＞のいずれかに記載のインクに刺激を印加し、記録媒体に付与するインク飛翔工程を含むことを特徴とするインクジェット記録方法である。
＜１３＞ 前記インク飛翔工程後に前記記録媒体を加熱する加熱工程を含む前記＜１２＞に記載のインクジェット記録方法である。
＜１４＞ 前記記録媒体が、ポリプロピレンフィルムである前記＜１２＞から＜１３＞のいずれかに記載のインクジェット記録方法である。
＜１５＞ 前記＜１＞から＜１１＞のいずれかに記載のインクと、前記インクに刺激を印加し、記録媒体に付与するインク飛翔手段とを有することを特徴とするインクジェット記録装置である。
＜１６＞ 前記記録媒体を加熱する加熱手段を更に有する前記＜１５＞に記載のインクジェット記録装置である。
＜１７＞ 前記記録媒体が、ポリプロピレンフィルムである前記＜１５＞から＜１６＞のいずれかに記載のインクジェット記録装置である。
＜１８＞ 記録媒体と、前記記録媒体上に、顔料、界面活性剤、及び樹脂を含有する記録層とを有することを特徴とする記録物である。
＜１９＞ 前記記録層が、スチレン−アクリル樹脂を更に含む前記＜１８＞に記載の記録物である。
＜２０＞ 前記記録媒体が、ポリプロピレンフィルムである前記＜１８＞から＜１９＞のいずれかに記載の記録物である。
As an aspect of this invention, it is as follows, for example.
<1> including water, pigment, organic solvent, surfactant, and resin,
The surfactant includes a compound represented by the following general formula (1),
The ink is characterized in that the content of the compound represented by the general formula (1) is 0.5% by mass or more and 1.5% by mass or less.
[General formula (1)]
<2> The ink according to <1>, wherein the organic solvent contains 3-methoxy-3-methyl-1-butanol.
<3> The ink according to <2>, wherein the content of the 3-methoxy-3-methyl-1-butanol is 2% by mass or more.
<4> The ink according to <3>, wherein the content of the 3-methoxy-3-methyl-1-butanol is 2% by mass or more and 10% by mass or less.
<5> The polyether group R of the general formula (1) is — (C 2 H 4 O) a (C 3 H 6 O) b R 1 (where R 1 represents a hydrogen atom or a methyl group, a and b are integers.) The ink according to any one of <1> to <4>.
<6> The ink according to <5>, wherein the a is 0 or more and 13 or less, and the b is 1 or more and 13 or less.
<7> The ink according to any one of <1> to <6>, wherein the pigment contains a styrene-acrylic resin-coated pigment in which a styrene-acrylic resin is partially or entirely coated on the surface of the pigment.
<8> The ink according to any one of <1> to <7>, wherein the pigment contains a self-dispersing pigment.
<9> The ink according to any one of <1> to <8>, wherein the pigment contains a dispersant-dispersed pigment.
<10> The ink according to any one of <1> to <9>, wherein the content of the organic solvent is 20% by mass or more and 60% by mass or less.
<11> The ink according to any one of <1> to <10>, wherein the resin contains at least one of a polyester-based urethane resin and an acrylic resin.
<12> An inkjet recording method comprising an ink flying step of applying a stimulus to the ink according to any one of <1> to <11> and applying the ink to a recording medium.
<13> The inkjet recording method according to <12>, further including a heating step of heating the recording medium after the ink flying step.
<14> The inkjet recording method according to any one of <12> to <13>, wherein the recording medium is a polypropylene film.
<15> An inkjet recording apparatus comprising: the ink according to any one of <1> to <11>; and an ink flying unit that applies a stimulus to the ink and applies the ink to a recording medium.
<16> The inkjet recording apparatus according to <15>, further including a heating unit configured to heat the recording medium.
<17> The inkjet recording apparatus according to any one of <15> to <16>, wherein the recording medium is a polypropylene film.
<18> A recorded matter comprising a recording medium, and a recording layer containing a pigment, a surfactant, and a resin on the recording medium.
<19> The recorded matter according to <18>, wherein the recording layer further includes a styrene-acrylic resin.
<20> The recorded matter according to any one of <18> to <19>, wherein the recording medium is a polypropylene film.
前記＜１＞から＜１１＞のいずれかに記載のインク、前記＜１２＞から＜１４＞のいずれかに記載のインクジェット記録方法、前記＜１５＞から＜１７＞のいずれかに記載のインクジェット記録装置、及び前記＜１８＞から＜２０＞のいずれかに記載の記録物は、従来における前記諸問題を解決し、前記本発明の目的を達成することができる。 The ink according to any one of <1> to <11>, the ink jet recording method according to any one of <12> to <14>, and the ink jet recording according to any one of <15> to <17>. The apparatus and the recorded matter according to any one of <18> to <20> can solve the conventional problems and achieve the object of the present invention.
４００ 画像形成装置
４０１ 画像形成装置の外装
４０１ｃ 装置本体のカバー
４０４ カートリッジホルダ
４１０ メインタンク
４１０ｋ、４１０ｃ、４１０ｍ、４１０ｙ ブラック（Ｋ）、シアン（Ｃ）、マゼンタ（Ｍ）、イエロー（Ｙ）の各色用のメインタンク
４１１ インク収容部
４１３ インク排出口
４１４ 収容容器ケース
４２０ 機構部
４３４ 吐出ヘッド
４３６ 供給チューブ
400 Image forming apparatus 401 Exterior of image forming apparatus 401c Cover of apparatus main body 404 Cartridge holder 410 Main tank 410k, 410c, 410m, 410y For each color of black (K), cyan (C), magenta (M), yellow (Y) Main tank 411 Ink storage section 413 Ink discharge port 414 Storage container case 420 Mechanism section 434 Discharge head 436 Supply tube
Claims (6)
前記界面活性剤が、下記一般式（１）で表される化合物を含み、
前記一般式（１）で表される化合物の含有量が、０．５質量％以上１．５質量％以下であることを特徴とするインク。
〔一般式（１）〕
The surfactant includes a compound represented by the following general formula (1),
The ink according to claim 1, wherein the content of the compound represented by the general formula (1) is 0.5% by mass or more and 1.5% by mass or less.
[General formula (1)]