JP2017082235A - Manufacturing method of conjugated diene rubber - Google Patents
Manufacturing method of conjugated diene rubber Download PDFInfo
- Publication number
- JP2017082235A JP2017082235A JP2016254790A JP2016254790A JP2017082235A JP 2017082235 A JP2017082235 A JP 2017082235A JP 2016254790 A JP2016254790 A JP 2016254790A JP 2016254790 A JP2016254790 A JP 2016254790A JP 2017082235 A JP2017082235 A JP 2017082235A
- Authority
- JP
- Japan
- Prior art keywords
- conjugated diene
- group
- rubber
- weight
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、共役ジエン系ゴムの製造方法に関し、より詳しくは、低発熱性、およびウエットグリップ性に優れたゴム架橋物を与えることのできる共役ジエン系ゴムを製造するための方法に関する。また、本発明は、この製造方法により得られる共役ジエン系ゴム、該共役ジエン系ゴムを含有するゴム組成物およびそのゴム架橋物にも関する。 The present invention relates to a method for producing a conjugated diene rubber, and more particularly to a method for producing a conjugated diene rubber capable of providing a crosslinked rubber product having low heat build-up and excellent wet grip properties. The present invention also relates to a conjugated diene rubber obtained by this production method, a rubber composition containing the conjugated diene rubber, and a rubber cross-linked product thereof.
近年、自動車用のタイヤには、環境問題および資源問題から低燃費性が強く求められる一方で、安全性の面から優れたウエットグリップ性が求められている。充填剤としてシリカを配合したゴム組成物の架橋物は、カーボンブラックを配合したゴム組成物の架橋物に比べて、低発熱性に優れるため、タイヤを構成した場合の転がり抵抗が小さくなる。そのため、シリカを配合したゴム組成物の架橋物を用いてタイヤを構成することにより、低燃費性に優れたタイヤを得ることができる。 In recent years, automobile tires are strongly required to have low fuel consumption due to environmental problems and resource problems, while excellent wet grip properties are required from the viewpoint of safety. A crosslinked product of a rubber composition blended with silica as a filler is superior in low heat build-up compared to a crosslinked composition of a rubber composition blended with carbon black, and therefore rolling resistance when a tire is configured is reduced. Therefore, a tire excellent in fuel efficiency can be obtained by constituting a tire using a crosslinked product of a rubber composition containing silica.
しかし、従来のゴムにシリカを配合しても、ゴムとシリカとの親和性が不十分であるため、これらは分離しやすく、そのため、このことに起因して、架橋前のゴム組成物の加工性が悪く、また、これを架橋して得られるゴム架橋物の低発熱性が不十分となる。 However, even if silica is blended with conventional rubber, since the affinity between rubber and silica is insufficient, they are easily separated. Therefore, due to this, the processing of the rubber composition before crosslinking is performed. Moreover, the low exothermic property of the rubber cross-linked product obtained by cross-linking this is insufficient.
そこで、ゴムとシリカとの親和性を改良すべく、例えば、特許文献１や特許文献２などに開示されるような種々のシランカップリング剤を、ゴム組成物に添加することが提案されている。しかし、シランカップリング剤を扱うには高度な加工技術が必要であり、また、シランカップリング剤が高価なことから配合量が多くなると、タイヤの製造コストが高くなるという問題がある。 Thus, in order to improve the affinity between rubber and silica, it has been proposed to add various silane coupling agents as disclosed in, for example, Patent Document 1 and Patent Document 2 to the rubber composition. . However, in order to handle the silane coupling agent, a high processing technique is required. Further, since the silane coupling agent is expensive, there is a problem that the production cost of the tire increases when the amount is increased.
このような問題を解決するために、例えば、特許文献３や特許文献４などに開示されるように、溶液重合法によりゴム重合体を得る際に、重合体鎖の活性末端に変性剤を反応させることにより、ゴム自体にシリカとの親和性を持たせる技術が検討されている。しかしながら、近年の自動車用のタイヤへの低燃費性およびウエットグリップ性への要求の高まりから、さらに低発熱性に優れ、しかもウエットグリップ性にも優れるゴム架橋物を与えることができるゴムが望まれている。 In order to solve such a problem, for example, as disclosed in Patent Document 3 and Patent Document 4, when a rubber polymer is obtained by a solution polymerization method, a modifier is reacted with an active end of a polymer chain. Thus, a technique for giving rubber itself an affinity for silica has been studied. However, due to the recent increase in demand for low fuel consumption and wet grip properties for automobile tires, a rubber that can provide a rubber cross-linked product that is further excellent in low heat generation and excellent in wet grip properties is desired. ing.
本発明は、このような実状に鑑みてなされたものであり、低発熱性およびウエットグリップ性に優れたゴム架橋物を与えることができる、共役ジエン系ゴムの製造方法を提供することを目的とする。 The present invention has been made in view of such a situation, and an object of the present invention is to provide a method for producing a conjugated diene rubber, which can provide a rubber cross-linked product having low heat build-up and excellent wet grip properties. To do.
本発明者らは、上記目的を達成するために鋭意研究した結果、活性末端を有する共役ジエン系重合体鎖に、変性剤として、シロキサンを反応させ、次いで、シロキサンを反応させた共役ジエン系重合体鎖に、変性剤として、８位が３級アミン構造含有基で置換された１，６−ジオキサ−２−シラシクロオクタン構造を有する化合物を反応させることにより得られ、かつ、共役ジエン単量体単位部分におけるビニル結合含有量が５０重量％以下である共役ジエン系ゴムによれば、これを用いて得られるゴム架橋物が、低発熱性およびウエットグリップ性に優れたものであることを見出し、本発明を完成させるに至った。 As a result of diligent research to achieve the above object, the present inventors have reacted a conjugated diene polymer chain having an active end with a siloxane as a modifier, and then reacted with a siloxane. It is obtained by reacting the compound chain with a compound having a 1,6-dioxa-2-silacyclooctane structure substituted with a tertiary amine structure-containing group at the 8-position as a modifier, and conjugated diene monomer According to the conjugated diene rubber having a vinyl bond content of 50% by weight or less in the body unit part, it has been found that the rubber cross-linked product obtained by using the rubber has excellent low heat buildup and wet grip properties. The present invention has been completed.
すなわち、本発明によれば、不活性溶媒中で、重合開始剤を用いて、共役ジエン化合物を含む単量体を重合し、活性末端を有する共役ジエン系重合体鎖を得る第１工程と、前記活性末端を有する共役ジエン系重合体鎖に、シロキサンを反応させる第２工程と、前記第２工程で得られるシロキサンを反応させた共役ジエン系重合体鎖に、下記一般式（１）で表される化合物を反応させる第３工程とを備える、共役ジエン単量体単位部分におけるビニル結合含有量が５０重量％以下である共役ジエン系ゴムの製造方法が提供される。
本発明の製造方法において、前記シロキサンとして、下記一般式（２）で表されるポリオルガノシロキサンを用いることが好ましい。
本発明の製造方法において、前記重合開始剤として有機アルカリ金属アミド化合物を用いることが好ましい。
本発明の製造方法において、前記有機アルカリ金属アミド化合物が、下記一般式（３）で表される化合物であることが好ましい。
In the production method of the present invention, the organic alkali metal amide compound is preferably a compound represented by the following general formula (3).
本発明の製造方法において、前記第１工程における重合を、前記重合開始剤１モルに対して、０．０１〜１．２モルの極性化合物の存在下で行うことが好ましい。 In the production method of the present invention, the polymerization in the first step is preferably performed in the presence of 0.01 to 1.2 mol of a polar compound with respect to 1 mol of the polymerization initiator.
本発明の製造方法において、前記第１工程が、不活性溶媒中で、イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体を、重合開始剤により重合し、イソプレン単量体単位８０〜１００重量％、および芳香族ビニル単量体単位０〜２０重量％を含む活性末端を有する重合体ブロック（Ａ）を形成させる工程と、前記活性末端を有する重合体ブロック（Ａ）と、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体と、を混合して重合反応を継続させ、１，３−ブタジエン単量体単位５０〜１００重量％および芳香族ビニル単量体単位０〜５０重量％を含む活性末端を有する重合体ブロック（Ｂ）を、重合体ブロック（Ａ）と一続きにして形成させることにより、活性末端を有する共役ジエン系重合体鎖を得る工程とを備えることが好ましい。
また、この際において、前記重合体ブロック（Ｂ）の形成を、前記重合開始剤１モルに対して、０．０１〜１．２モルの極性化合物の存在下で行うことが好ましい。
In the production method of the present invention, the first step is performed by polymerizing a monomer containing isoprene or isoprene and an aromatic vinyl compound in an inert solvent with a polymerization initiator, A step of forming a polymer block (A) having an active terminal containing 100% by weight and an aromatic vinyl monomer unit of 0 to 20% by weight, a polymer block (A) having the active terminal, 3-butadiene or a monomer containing 1,3-butadiene and an aromatic vinyl compound is mixed to continue the polymerization reaction, and 50 to 100% by weight of 1,3-butadiene monomer unit and aromatic vinyl By forming a polymer block (B) having an active end containing 0 to 50% by weight of monomer units in a continuous manner with the polymer block (A), a conjugated dimer having an active end is formed. Preferably comprises the step of obtaining a down polymer chains.
In this case, the polymer block (B) is preferably formed in the presence of 0.01 to 1.2 mol of a polar compound with respect to 1 mol of the polymerization initiator.
また、本発明によれば、上記の製造方法により得られる共役ジエン系ゴムが提供される。
さらに、本発明によれば、上記共役ジエン系ゴムを含むゴム成分１００重量部に対して、シリカ１０〜２００重量部を含有してなるゴム組成物が提供される。
本発明のゴム組成物は、架橋剤をさらに含有してなるものであることが好ましい。
Moreover, according to this invention, the conjugated diene type rubber | gum obtained by said manufacturing method is provided.
Furthermore, according to this invention, the rubber composition formed by containing 10-200 weight part of silica with respect to 100 weight part of rubber components containing the said conjugated diene-type rubber is provided.
The rubber composition of the present invention preferably contains a crosslinking agent.
また、本発明によれば、上記ゴム組成物を架橋してなるゴム架橋物、および該ゴム架橋物を含んでなるタイヤが提供される。 Moreover, according to this invention, the rubber | gum crosslinked material formed by bridge | crosslinking the said rubber composition and the tire containing this rubber | gum crosslinked material are provided.
本発明によれば、低発熱性およびウエットグリップ性に優れたゴム架橋物を与えることのできる共役ジエン系ゴム、該共役ジエン系ゴムを含有するゴム組成物、該ゴム組成物を架橋してなり、低発熱性およびウエットグリップ性に優れたゴム架橋物、および該ゴム架橋物を含んでなるタイヤを提供することができる。 According to the present invention, a conjugated diene rubber capable of providing a rubber cross-linked product excellent in low heat buildup and wet grip, a rubber composition containing the conjugated diene rubber, and the rubber composition are cross-linked. Further, it is possible to provide a rubber cross-linked product excellent in low heat buildup and wet grip properties and a tire comprising the rubber cross-linked product.
＜共役ジエン系ゴムの製造方法＞
本発明の製造方法は、
不活性溶媒中で、重合開始剤を用いて、共役ジエン化合物を含む単量体を重合し、活性末端を有する共役ジエン系重合体鎖を得る第１工程と、
前記活性末端を有する共役ジエン系重合体鎖に、シロキサンを反応させる第２工程と、
前記第２工程で得られるシロキサンを反応させた共役ジエン系重合体鎖に、後述する一般式（１）で表される化合物を反応させる第３工程とを備える、
共役ジエン単量体単位部分におけるビニル結合含有量が５０重量％以下である共役ジエン系ゴムの製造方法である。
<Method for producing conjugated diene rubber>
The production method of the present invention comprises:
A first step of polymerizing a monomer containing a conjugated diene compound using a polymerization initiator in an inert solvent to obtain a conjugated diene polymer chain having an active end;
A second step of reacting siloxane with the conjugated diene polymer chain having an active end;
A third step of reacting the conjugated diene polymer chain obtained by reacting the siloxane obtained in the second step with a compound represented by the following general formula (1),
This is a method for producing a conjugated diene rubber having a vinyl bond content in the conjugated diene monomer unit portion of 50% by weight or less.
＜第１工程＞
本発明の製造方法の第１工程は、不活性溶媒中で、重合開始剤を用いて、共役ジエン化合物を含む単量体を重合し、活性末端を有する共役ジエン系重合体鎖を得る工程である。
<First step>
The first step of the production method of the present invention is a step of polymerizing a monomer containing a conjugated diene compound in an inert solvent using a polymerization initiator to obtain a conjugated diene polymer chain having an active end. is there.
本発明の製造方法の第１工程において、活性末端を有する共役ジエン系重合体鎖を得るために、単量体として用いる共役ジエン化合物としては、特に限定されないが、１，３−ブタジエン、イソプレン、２，３−ジメチル−１，３−ブタジエン、２−フェニル−１，３−ブタジエン、１，３−ペンタジエン、２−メチル−１，３−ペンタジエン、１，３−ヘキサジエン、４，５−ジエチル−１，３−オクタジエン、３−ブチル−１，３−オクタジエンなどを挙げることができる。これらのなかでも、１，３−ブタジエンおよびイソプレンが好ましい。これらの共役ジエン化合物は、１種類を単独で使用しても２種類以上を組合せて用いてもよい。 In the first step of the production method of the present invention, the conjugated diene compound used as a monomer in order to obtain a conjugated diene polymer chain having an active end is not particularly limited, but 1,3-butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, 2-phenyl-1,3-butadiene, 1,3-pentadiene, 2-methyl-1,3-pentadiene, 1,3-hexadiene, 4,5-diethyl- Examples include 1,3-octadiene and 3-butyl-1,3-octadiene. Of these, 1,3-butadiene and isoprene are preferred. These conjugated diene compounds may be used alone or in combination of two or more.
また、本発明の製造方法の第１工程において、重合に用いる単量体として、共役ジエン化合物とともに芳香族ビニル化合物を用いてもよい。単量体として用いる芳香族ビニル化合物としては、スチレン、メチルスチレン、エチルスチレン、ｔ−ブチルスチレン、α−メチルスチレン、α−メチル−ｐ−メチルスチレン、クロルスチレン、ブロモスチレン、メトキシスチレン、ジメチルアミノメチルスチレン、ジメチルアミノエチルスチレン、ジエチルアミノメチルスチレン、ジエチルアミノエチルスチレン、シアノエチルスチレン、ビニルナフタレンなどが挙げられる。これらのなかでも、スチレンが好ましい。本発明の製造方法の第１工程で得られる、活性末端を有する共役ジエン系重合体鎖は、共役ジエン単量体単位５０〜１００重量％を含むものが好ましく、５５〜９５重量％を含むものがより好ましく、また、芳香族ビニル単量体単位０〜５０重量％を含むものが好ましく、５〜４５重量％を含むものがより好ましい。 Moreover, you may use an aromatic vinyl compound with a conjugated diene compound as a monomer used for superposition | polymerization in the 1st process of the manufacturing method of this invention. Aromatic vinyl compounds used as monomers include styrene, methylstyrene, ethylstyrene, t-butylstyrene, α-methylstyrene, α-methyl-p-methylstyrene, chlorostyrene, bromostyrene, methoxystyrene, dimethylamino Examples thereof include methyl styrene, dimethylaminoethyl styrene, diethylaminomethyl styrene, diethylaminoethyl styrene, cyanoethyl styrene and vinyl naphthalene. Of these, styrene is preferred. The conjugated diene polymer chain having an active end obtained in the first step of the production method of the present invention preferably contains 50 to 100% by weight of a conjugated diene monomer unit, and contains 55 to 95% by weight. More preferably, those containing 0 to 50% by weight of aromatic vinyl monomer units are preferred, and those containing 5 to 45% by weight are more preferred.
さらに、本発明の製造方法の第１工程においては、共役ジエン化合物とともに、芳香族ビニル化合物以外の、共役ジエン化合物と共重合可能な化合物を用いてもよい。このような共役ジエン化合物と共重合可能な化合物としては、エチレン、プロピレン、１−ブテンなどの鎖状オレフィン化合物；シクロペンテン、２−ノルボルネンなどの環状オレフィン化合物；１，５−ヘキサジエン、１，６−ヘプタジエン、１，７−オクタジエン、ジシクロペンタジエン、５−エチリデン−２−ノルボルネンなどの非共役ジエン化合物；（メタ）アクリル酸メチル、（メタ）アクリル酸エチル、（メタ）アクリル酸ブチルなどの（メタ）アクリル酸エステル；（メタ）アクリロニトリル、（メタ）アクリルアミドなどのその他の（メタ）アクリル酸誘導体；などが挙げられる。これらの共役ジエン化合物と共重合可能な化合物は、本発明の製造方法の第１工程で得られる、活性末端を有する共役ジエン系重合体鎖中に、単量体単位として、１０重量％以下とするのが好ましく、５重量％以下とするのがより好ましい。 Furthermore, in the 1st process of the manufacturing method of this invention, you may use the compound copolymerizable with a conjugated diene compound other than an aromatic vinyl compound with a conjugated diene compound. Examples of the compound copolymerizable with such a conjugated diene compound include: chain olefin compounds such as ethylene, propylene, and 1-butene; cyclic olefin compounds such as cyclopentene and 2-norbornene; 1,5-hexadiene, 1,6- Non-conjugated diene compounds such as heptadiene, 1,7-octadiene, dicyclopentadiene and 5-ethylidene-2-norbornene; (meth) methacrylates such as methyl (meth) acrylate, ethyl (meth) acrylate and butyl (meth) acrylate ) Acrylic acid ester; (meth) acrylonitrile, other (meth) acrylic acid derivatives such as (meth) acrylamide; and the like. The compound copolymerizable with these conjugated diene compounds is 10% by weight or less as a monomer unit in the conjugated diene polymer chain having an active end obtained in the first step of the production method of the present invention. It is preferable to set it to 5% by weight or less.
重合に用いる不活性溶媒としては、溶液重合において通常使用されるものであり、重合反応を阻害しないものであれば特に限定されない。不活性溶媒の具体例としては、ブタン、ペンタン、ヘキサン、ヘプタンなどの鎖状脂肪族炭化水素；シクロペンタン、シクロヘキサンなどの脂環式炭化水素；ベンゼン、トルエン、キシレンなどの芳香族炭化水素；などが挙げられる。これらの不活性溶媒は、１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。不活性溶媒の使用量は、特に限定されないが、単量体濃度が、たとえば１〜５０重量％となる量であり、好ましくは１０〜４０重量％となる量である。 The inert solvent used for the polymerization is not particularly limited as long as it is one usually used in solution polymerization and does not inhibit the polymerization reaction. Specific examples of the inert solvent include chain aliphatic hydrocarbons such as butane, pentane, hexane, and heptane; alicyclic hydrocarbons such as cyclopentane and cyclohexane; aromatic hydrocarbons such as benzene, toluene, and xylene; Is mentioned. These inert solvents may be used individually by 1 type, and may be used in combination of 2 or more type. Although the usage-amount of an inert solvent is not specifically limited, It is the quantity from which a monomer concentration will be 1 to 50 weight%, for example, Preferably it will be 10 to 40 weight%.
重合に用いる重合開始剤としては、共役ジエン化合物を含む単量体を重合させて、活性末端を有する共役ジエン系重合体鎖を与えることができるものであれば、特に限定されない。その具体例としては、有機アルカリ金属化合物、有機アルカリ土類金属化合物、およびランタン系列金属化合物などを主触媒とする重合開始剤を挙げることができる。有機アルカリ金属化合物としては、たとえば、ｎ−ブチルリチウム、ｓｅｃ−ブチルリチウム、ｔ−ブチルリチウム、ヘキシルリチウム、フェニルリチウム、スチルベンリチウムなどの有機モノリチウム化合物；ジリチオメタン、１，４−ジリチオブタン、１，４−ジリチオ−２−エチルシクロヘキサン、１，３，５−トリリチオベンゼン、１，３，５−トリス（リチオメチル）ベンゼンなどの有機多価リチウム化合物；ナトリウムナフタレンなどの有機ナトリウム化合物；カリウムナフタレンなどの有機カリウム化合物；などが挙げられる。また、有機アルカリ土類金属化合物としては、例えば、ジ−ｎ−ブチルマグネシウム、ジ−ｎ−ヘキシルマグネシウム、ジエトキシカルシウム、ジステアリン酸カルシウム、ジ−ｔ−ブトキシストロンチウム、ジエトキシバリウム、ジイソプロポキシバリウム、ジエチルメルカプトバリウム、ジ−ｔ−ブトキシバリウム、ジフェノキシバリウム、ジエチルアミノバリウム、ジステアリン酸バリウム、ジケチルバリウムなどが挙げられる。ランタン系列金属化合物を主触媒とする重合開始剤としては、たとえば、ランタン、セリウム、プラセオジム、ネオジム、サマリウム、ガドリニウムなどのランタン系列金属と、カルボン酸、およびリン含有有機酸などとからなるランタン系列金属の塩を主触媒とし、これと、アルキルアルミニウム化合物、有機アルミニウムハイドライド化合物、有機アルミニウムハライド化合物などの助触媒とからなる重合開始剤などが挙げられる。これらの重合開始剤の中でも、有機モノリチウム化合物、および有機多価リチウム化合物が好ましく用いられ、有機モノリチウム化合物がより好ましく用いられ、ｎ−ブチルリチウムが特に好ましく用いられる。
なお、有機アルカリ金属化合物は、予め、ジブチルアミン、ジヘキシルアミン、ジベンジルアミン、ピロリジン、ピペリジン、ヘキサメチレンイミン、およびヘプタメチレンイミンなどの２級アミン化合物と反応させて、有機アルカリ金属アミド化合物として使用してもよい。有機アルカリ金属アミド化合物を重合開始剤として用いることにより、得られるゴム架橋物を、より低発熱性およびウエットグリップ性に優れたものとすることができる。これらの重合開始剤は、１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
The polymerization initiator used for the polymerization is not particularly limited as long as it can polymerize a monomer containing a conjugated diene compound to give a conjugated diene polymer chain having an active end. Specific examples thereof include a polymerization initiator having an organic alkali metal compound, an organic alkaline earth metal compound, a lanthanum series metal compound, or the like as a main catalyst. Examples of the organic alkali metal compound include organic monolithium compounds such as n-butyllithium, sec-butyllithium, t-butyllithium, hexyllithium, phenyllithium and stilbenelithium; dilithiomethane, 1,4-dilithiobutane, 1,4 -Organic polyvalent lithium compounds such as dilithio-2-ethylcyclohexane, 1,3,5-trilithiobenzene, 1,3,5-tris (lithiomethyl) benzene; organic sodium compounds such as sodium naphthalene; organic such as potassium naphthalene Potassium compounds; and the like. Examples of the organic alkaline earth metal compound include di-n-butylmagnesium, di-n-hexylmagnesium, diethoxycalcium, calcium distearate, di-t-butoxystrontium, diethoxybarium, and diisopropoxybarium. , Diethyl mercaptobarium, di-t-butoxybarium, diphenoxybarium, diethylaminobarium, barium distearate, diketylbarium and the like. As a polymerization initiator having a lanthanum series metal compound as a main catalyst, for example, a lanthanum series metal comprising a lanthanum series metal such as lanthanum, cerium, praseodymium, neodymium, samarium, gadolinium, a carboxylic acid, and a phosphorus-containing organic acid. And a polymerization initiator composed of this salt and a cocatalyst such as an alkylaluminum compound, an organoaluminum hydride compound, and an organoaluminum halide compound. Among these polymerization initiators, an organic monolithium compound and an organic polyvalent lithium compound are preferably used, an organic monolithium compound is more preferably used, and n-butyllithium is particularly preferably used.
In addition, organic alkali metal compounds are used as organic alkali metal amide compounds by reacting with secondary amine compounds such as dibutylamine, dihexylamine, dibenzylamine, pyrrolidine, piperidine, hexamethyleneimine, and heptamethyleneimine in advance. May be. By using an organic alkali metal amide compound as a polymerization initiator, the obtained rubber cross-linked product can be made more excellent in low exothermic property and wet grip property. These polymerization initiators may be used individually by 1 type, and may be used in combination of 2 or more type.
有機アルカリ金属アミド化合物としては、たとえば、有機アルカリ金属化合物に、２級アミン化合物を反応させたものなどが挙げられ、なかでも、本発明の製造方法においては、下記一般式（３）で表される化合物を好適に用いることができる。
一般式（３）中、Ｍ１はアルカリ金属原子を表し、Ｒ１２、Ｒ１３は、それぞれ独立して、アルキル基、シクロアルキル基、アリール基、アラルキル基、アミノ基の保護基、または加水分解して水酸基を生じうる基を表し、Ｒ１２およびＲ１３は互いに結合して、これらが結合する窒素原子とともに環構造を形成してもよく、該環構造を形成する場合には、これらが結合する窒素原子に加えて、これらが結合する窒素原子以外のヘテロ原子とともに環構造を形成していてもよい。 In General Formula (3), M 1 represents an alkali metal atom, and R 12 and R 13 are each independently an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an amino group protecting group, or a hydrolysis group. R 12 and R 13 may be bonded to each other to form a ring structure together with the nitrogen atom to which they are bonded, and in the case of forming the ring structure, these are bonded In addition to the nitrogen atom to be formed, a ring structure may be formed together with a hetero atom other than the nitrogen atom to which they are bonded.
アルキル基としては、特に限定されないが、炭素数１〜２０のアルキル基が好ましく、炭素数１〜１０のアルキル基がより好ましい。このようなアルキル基としては、たとえば、メチル基、エチル基、ｎ−プロピル基、イソプロピル基、ｎ−ブチル基、イソブチル基、ｓｅｃ−ブチル基、ｔｅｒｔ−ブチル基、ｎ−ペンチル基、ｎ−ヘキシル基、ｎ−ヘプチル基、ｎ−オクチル基、ｎ−デシル基などが挙げられる。 Although it does not specifically limit as an alkyl group, A C1-C20 alkyl group is preferable and a C1-C10 alkyl group is more preferable. Examples of such alkyl groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, and n-hexyl. Group, n-heptyl group, n-octyl group, n-decyl group and the like.
シクロアルキル基としては、特に限定されないが、炭素数３〜２０のシクロアルキル基が好ましく、炭素数３〜１２のシクロアルキル基がより好ましい。このようなシクロアルキル基としては、たとえば、シクロプロピル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基、シクロドデシル基などが挙げられる。 Although it does not specifically limit as a cycloalkyl group, A C3-C20 cycloalkyl group is preferable and a C3-C12 cycloalkyl group is more preferable. Examples of such cycloalkyl groups include a cyclopropyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, and a cyclododecyl group.
アリール基としては、特に限定されないが、炭素数６〜１２のアリール基が好ましく、炭素数６〜１０のアリール基がより好ましい。このようなアリール基としては、たとえば、フェニル基、１−ナフチル基、２−ナフチル基などが挙げられる。 Although it does not specifically limit as an aryl group, A C6-C12 aryl group is preferable and a C6-C10 aryl group is more preferable. Examples of such an aryl group include a phenyl group, a 1-naphthyl group, and a 2-naphthyl group.
アラルキル基としては、特に限定されないが、炭素数７〜１３のアラルキル基が好ましく、炭素数７〜９のアラルキル基がより好ましい。このようなアラルキル基としては、たとえば、ベンジル基、フェネチル基などが挙げられる。 Although it does not specifically limit as an aralkyl group, A C7-C13 aralkyl group is preferable and a C7-C9 aralkyl group is more preferable. Examples of such aralkyl groups include benzyl group and phenethyl group.
アミノ基の保護基としては、特に限定されず、アミノ基の保護基として作用する基であればよいが、たとえば、アルキルシリル基などが挙げられる。このようなアルキルシリル基としては、たとえば、トリメチルシリル基、トリエチルシリル基、トリフェニルシリル基、メチルジフェニルシリル基、エチルメチルフェニルシリル基、ｔｅｒｔ−ブチルジメチルシリル基などが挙げられる。
なお、Ｒ１２、および／またはＲ１３がアミノ基の保護基である場合には、アミノ基の保護基が外れることにより、得られる共役ジエン系ゴムを形成する重合体鎖の一方の末端において、後述する一般式（５）におけるＲ１４、および／またはＲ１５が水素原子である構造を導入することができる。
The amino-protecting group is not particularly limited as long as it is a group that acts as an amino-protecting group, and examples thereof include an alkylsilyl group. Examples of such alkylsilyl groups include trimethylsilyl group, triethylsilyl group, triphenylsilyl group, methyldiphenylsilyl group, ethylmethylphenylsilyl group, tert-butyldimethylsilyl group, and the like.
In the case where R 12 and / or R 13 is an amino group protecting group, the amino group protecting group is removed, so that at one end of the polymer chain forming the resulting conjugated diene rubber, A structure in which R 14 and / or R 15 in the general formula (5) described later is a hydrogen atom can be introduced.
加水分解して水酸基を生じうる基としては、特に限定されず、たとえば、酸などの存在下で加水分解することで、水酸基を生成する基であればよいが、たとえば、アルコキシアルキル基、エポキシ基を含有する基などが挙げられる。
アルコキシアルキル基としては、メトキシメチル基、エトキシメチル基、エトキシエチル基、プロポキシメチル基、ブトキシメチル基、ブトキシエチル基、プロポキシエチル基などが挙げられる。
また、エポキシ基を含有する基としては、たとえば下記一般式（４）で表される基などが挙げられる。
−Ｚ１−Ｚ２−Ｅ１ （４）
一般式（４）中、Ｚ１は炭素数１〜１０のアルキレン基またはアルキルアリーレン基であり、Ｚ２はメチレン基、硫黄原子または酸素原子であり、Ｅ１はグリシジル基である。
The group capable of generating a hydroxyl group by hydrolysis is not particularly limited, and may be any group that generates a hydroxyl group by hydrolysis in the presence of an acid, for example, an alkoxyalkyl group, an epoxy group, and the like. And a group containing
Examples of the alkoxyalkyl group include a methoxymethyl group, an ethoxymethyl group, an ethoxyethyl group, a propoxymethyl group, a butoxymethyl group, a butoxyethyl group, and a propoxyethyl group.
Examples of the group containing an epoxy group include a group represented by the following general formula (4).
-Z 1 -Z 2 -E 1 (4)
In General Formula (4), Z 1 is an alkylene group having 1 to 10 carbon atoms or an alkylarylene group, Z 2 is a methylene group, a sulfur atom or an oxygen atom, and E 1 is a glycidyl group.
また、Ｒ１２およびＲ１３は互いに結合して、これらが結合する窒素原子とともに環構造を形成していてもよく、この場合における、Ｒ１２およびＲ１３と、これと結合する窒素原子とで形成される構造の具体例としては、アゼチジン環（Ｒ１２およびＲ１３が、プロピレン基）、ピロリジン環（Ｒ１２およびＲ１３が、ブチレン基）、ピペリジン環（Ｒ１２およびＲ１３が、ペンチレン基）、ヘキサメチレンイミン環（Ｒ１２およびＲ１３が、ヘキシレン基）などが挙げられる。
Ｒ１２およびＲ１３が互いに結合して、これらが結合する窒素原子とともに環構造を形成する場合、環構造は、４〜８員環構造であることが好ましい。
R 12 and R 13 may be bonded to each other to form a ring structure together with the nitrogen atom to which they are bonded. In this case, R 12 and R 13 are formed from the nitrogen atom that is bonded to this. Specific examples of the structure include azetidine ring (R 12 and R 13 are propylene groups), pyrrolidine ring (R 12 and R 13 are butylene groups), piperidine ring (R 12 and R 13 are pentylene groups) And hexamethyleneimine ring (R 12 and R 13 are hexylene groups).
When R 12 and R 13 are bonded to each other to form a ring structure together with the nitrogen atom to which they are bonded, the ring structure is preferably a 4- to 8-membered ring structure.
また、一般式（３）中、Ｍ１はアルカリ金属原子であり、このようなアルカリ金属原子としては、リチウム原子、ナトリウム原子、カリウム原子などが挙げられるが、これらの中でも、重合活性の観点より、リチウム原子が好ましい。 In general formula (3), M 1 is an alkali metal atom. Examples of such an alkali metal atom include a lithium atom, a sodium atom, and a potassium atom. Among these, from the viewpoint of polymerization activity. A lithium atom is preferable.
本発明の製造方法の第１工程において、重合開始剤として、上記一般式（３）で表される化合物を用いた場合、有機アルカリ金属アミド化合物を形成するアミン構造が、重合体鎖の重合開始末端に結合した状態で残存することとなる。そのため、重合開始剤として、上記一般式（３）で表される化合物を用いると、得られる共役ジエン系ゴムを形成する重合体鎖の一方の末端に、下記一般式（５）で表される構造が導入される。
一般式（５）中、Ｒ１４、Ｒ１５は、それぞれ独立して、水素原子、アルキル基、シクロアルキル基、アリール基、アラルキル基、アミノ基の保護基、または加水分解して水酸基を生じうる基を表し、Ｒ１４およびＲ１５は互いに結合して、これらが結合する窒素原子とともに環構造を形成してもよく、該環構造を形成する場合には、これらが結合する窒素原子に加えて、これらが結合する窒素原子以外のヘテロ原子とともに環構造を形成していてもよい。 In the general formula (5), R 14 and R 15 each independently represent a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, a protective group for an amino group, or a hydroxyl group upon hydrolysis. R 14 and R 15 may be bonded to each other to form a ring structure together with the nitrogen atom to which they are bonded, and in the case of forming the ring structure, in addition to the nitrogen atom to which they are bonded, A ring structure may be formed together with a hetero atom other than the nitrogen atom to which they are bonded.
Ｒ１４、Ｒ１５となりうるアルキル基、シクロアルキル基、アリール基、アラルキル基、アミノ基の保護基、または加水分解して水酸基を生じうる基としては、一般式（３）におけるＲ１２、Ｒ１３と同じものを挙げることができ、また、Ｒ１４およびＲ１５は互いに結合して、これらが結合する窒素原子とともに環構造を形成する場合にも、一般式（３）におけるＲ１２、Ｒ１３と同じものとすることができる。
なお、Ｒ１４、Ｒ１５となりうる水素原子は、アミノ基の保護基が外れることにより、導入される。
Examples of the alkyl group, cycloalkyl group, aryl group, aralkyl group, amino-protecting group, or group capable of hydrolyzing to generate a hydroxyl group that can be R 14 and R 15 include R 12 and R 13 in formula (3). In the case where R 14 and R 15 are bonded to each other to form a ring structure together with the nitrogen atom to which they are bonded, R 12 , R 13 in the general formula (3) and Can be the same.
In addition, the hydrogen atom which can become R 14 and R 15 is introduced when the protecting group of the amino group is removed.
本発明の製造方法において、重合開始剤として、有機アルカリ金属アミド化合物を用いた場合、得られる共役ジエン系ゴムを、一方の末端にアミン構造を有し、かつ、他方の末端に変性剤に由来する特定の構造を有するものとすることができる。その結果、このようなアミン構造の効果により、得られる共役ジエン系ゴムを用いたゴム架橋物は、より低発熱性およびウエットグリップ性に優れたものとなる。 In the production method of the present invention, when an organic alkali metal amide compound is used as a polymerization initiator, the resulting conjugated diene rubber has an amine structure at one end and is derived from a modifier at the other end. It may have a specific structure. As a result, due to the effect of such an amine structure, the resulting rubber cross-linked product using the conjugated diene rubber is more excellent in low heat generation and wet grip properties.
重合開始剤としての有機アルカリ金属アミド化合物を重合系に添加する方法としては、特に限定されず、予め、有機アルカリ金属化合物に、２級アミン化合物を反応させて、有機アルカリ金属アミド化合物を得て、これを共役ジエン化合物を含む単量体と混合して、重合反応を進行させる方法を採用することができる。あるいは、有機アルカリ金属化合物と、２級アミン化合物とを別々に重合系に添加し、これらを共役ジエン化合物を含む単量体と混合することで、重合系において、有機アルカリ金属アミド化合物を生成させることで、重合反応を進行させる方法を採用してもよい。反応温度等の反応条件は、特に限定されるものではなく、たとえば、目的とする重合反応条件に従えばよい。 The method of adding the organic alkali metal amide compound as a polymerization initiator to the polymerization system is not particularly limited, and a secondary amine compound is reacted with the organic alkali metal compound in advance to obtain an organic alkali metal amide compound. A method of mixing this with a monomer containing a conjugated diene compound and allowing the polymerization reaction to proceed can be employed. Alternatively, an organic alkali metal amide compound is generated in the polymerization system by adding the organic alkali metal compound and the secondary amine compound separately to the polymerization system and mixing them with a monomer containing a conjugated diene compound. Thus, a method of advancing the polymerization reaction may be employed. The reaction conditions such as the reaction temperature are not particularly limited, and may be according to the intended polymerization reaction conditions, for example.
２級アミン化合物の使用量は、目的とする重合開始剤の添加量に応じて決定すればよいが、有機アルカリ金属化合物１ミリモル当り、通常０．０１〜１．５ミリモル、好ましくは０．１〜１．２ミリモル、より好ましくは０．５〜１．０ミリモルの範囲である。 The amount of the secondary amine compound used may be determined according to the amount of the target polymerization initiator added, but is usually 0.01 to 1.5 mmol, preferably 0.1 to 1 mmol of the organic alkali metal compound. It is -1.2 mmol, More preferably, it is the range of 0.5-1.0 mmol.
重合開始剤の使用量は、目的とする共役ジエン系重合体鎖の分子量に応じて決定すればよいが、単量体１０００ｇ当り、通常１〜５０ミリモル、好ましくは１．５〜２０ミリモル、より好ましくは２〜１５ミリモルの範囲である。 The amount of the polymerization initiator used may be determined according to the molecular weight of the target conjugated diene polymer chain, but is usually 1 to 50 mmol, preferably 1.5 to 20 mmol, per 1000 g of monomer. Preferably it is the range of 2-15 mmol.
重合温度は、通常−８０〜＋１５０℃、好ましくは０〜１００℃、より好ましくは３０〜９０℃の範囲である。重合様式としては、回分式、連続式などのいずれの様式をも採用できるが、共役ジエン化合物と芳香族ビニル化合物とを共重合させる場合は、共役ジエン単量体単位と芳香族ビニル単量体単位との結合のランダム性を制御しやすい点で、回分式が好ましい。 The polymerization temperature is usually in the range of −80 to + 150 ° C., preferably 0 to 100 ° C., more preferably 30 to 90 ° C. As the polymerization mode, any of batch type and continuous type can be adopted. However, when copolymerizing a conjugated diene compound and an aromatic vinyl compound, a conjugated diene monomer unit and an aromatic vinyl monomer are used. The batch method is preferred because it is easy to control the randomness of the bond with the unit.
また、本発明の製造方法の第１工程においては、共役ジエン化合物を含む単量体を重合するにあたり、極性化合物の存在下で重合を行うことが好ましい。具体的には、重合開始剤１モルに対して、好ましくは０．０１〜１．２モル、より好ましくは０．１〜１．１モル、さらに好ましくは０．１〜１．０モルの極性化合物を使用し、このような極性化合物の存在下で重合を行うことにより、第１工程において得られる共役ジエン系重合体鎖に含まれる共役ジエン単量体単位部分におけるビニル結合含有量を、好適に調節することができる。具体的には、共役ジエン系重合体鎖に含まれる共役ジエン単量体単位部分におけるビニル結合含有量を好ましくは５０重量％以下、より好ましくは４５重量％以下、さらに好ましくは４２重量％以下とすることができる。また、ビニル結合含有量の下限は特に限定されないが、好ましくは５重量％以上である。共役ジエン系重合体鎖に含まれる共役ジエン単量体単位部分におけるビニル結合含有量を上記範囲とすることにより、最終的に得られる共役ジエン系ゴムに含まれる共役ジエン単量体単位部分におけるビニル結合含有量を、５０重量％以下とすることができ、これにより、得られるゴム架橋物を、低発熱性が大きく改善されたものとすることができる。 Moreover, in the 1st process of the manufacturing method of this invention, when superposing | polymerizing the monomer containing a conjugated diene compound, it is preferable to superpose | polymerize in presence of a polar compound. Specifically, the polarity is preferably 0.01 to 1.2 mol, more preferably 0.1 to 1.1 mol, and still more preferably 0.1 to 1.0 mol, with respect to 1 mol of the polymerization initiator. By using the compound and polymerizing in the presence of such a polar compound, the vinyl bond content in the conjugated diene monomer unit portion contained in the conjugated diene polymer chain obtained in the first step is suitably selected. Can be adjusted to. Specifically, the vinyl bond content in the conjugated diene monomer unit portion contained in the conjugated diene polymer chain is preferably 50% by weight or less, more preferably 45% by weight or less, and further preferably 42% by weight or less. can do. The lower limit of the vinyl bond content is not particularly limited, but is preferably 5% by weight or more. By setting the vinyl bond content in the conjugated diene monomer unit part contained in the conjugated diene polymer chain within the above range, the vinyl in the conjugated diene monomer unit part finally contained in the conjugated diene rubber is obtained. The bond content can be set to 50% by weight or less, whereby the obtained rubber cross-linked product can have a greatly improved low exothermic property.
極性化合物の存在下で重合を行う方法としては、特に限定されないが、たとえば、重合に用いる不活性溶媒中に、極性化合物を添加して、重合を行う方法などが挙げられる。また、極性化合物の具体例としては、ジブチルエーテル、テトラヒドロフラン、２，２−ジ（テトラヒドロフリル）プロパンなどのエーテル化合物；テトラメチルエチレンジアミンなどの第三級アミン；アルカリ金属アルコキシド；ホスフィン化合物；などが挙げられる。これらのなかでも、エーテル化合物、および第三級アミンが好ましく、第三級アミンがより好ましく、テトラメチルエチレンジアミンが特に好ましい。これらの極性化合物は、１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。 The method for carrying out the polymerization in the presence of the polar compound is not particularly limited, and examples thereof include a method for carrying out the polymerization by adding the polar compound to an inert solvent used for the polymerization. Specific examples of polar compounds include ether compounds such as dibutyl ether, tetrahydrofuran and 2,2-di (tetrahydrofuryl) propane; tertiary amines such as tetramethylethylenediamine; alkali metal alkoxides; phosphine compounds; It is done. Among these, ether compounds and tertiary amines are preferable, tertiary amines are more preferable, and tetramethylethylenediamine is particularly preferable. These polar compounds may be used individually by 1 type, and may be used in combination of 2 or more type.
本発明の製造方法の第１工程で得られる、活性末端を有する共役ジエン系重合体鎖の重量平均分子量（Ｍｗ）は、特に限定されないが、ポリスチレン換算のゲルパーミエーションクロマトグラフィで測定される値として、１００，０００〜１，０００，０００が好ましく、１５０，０００〜７００，０００がより好ましく、１５０，０００〜５００，０００が特に好ましい。活性末端を有する共役ジエン系重合体鎖の重量平均分子量（Ｍｗ）を上記範囲内とすることにより、得られるゴム架橋物を、ウエットグリップ性と低発熱性とのバランスが良好なものとすることができる。 The weight average molecular weight (Mw) of the conjugated diene polymer chain having an active end obtained in the first step of the production method of the present invention is not particularly limited, but is a value measured by gel permeation chromatography in terms of polystyrene. 100,000 to 1,000,000 are preferred, 150,000 to 700,000 are more preferred, and 150,000 to 500,000 are particularly preferred. By making the weight average molecular weight (Mw) of the conjugated diene polymer chain having an active end within the above range, the resulting rubber cross-linked product has a good balance between wet grip and low heat build-up. Can do.
また、本発明の製造方法の第１工程で得られる、活性末端を有する共役ジエン系重合体鎖の重量平均分子量（Ｍｗ）と数平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）で表わされる分子量分布も、特に限定されないが、好ましくは１．０〜３．０であり、より好ましくは１．０〜２．５である。活性末端を有する共役ジエン系重合体鎖の分子量分布（Ｍｗ／Ｍｎ）が上記範囲内にあると、共役ジエン系ゴムの製造が容易となる。 Moreover, it is represented by the ratio (Mw / Mn) of the weight average molecular weight (Mw) and the number average molecular weight (Mn) of the conjugated diene polymer chain having an active end obtained in the first step of the production method of the present invention. The molecular weight distribution is not particularly limited, but is preferably 1.0 to 3.0, more preferably 1.0 to 2.5. When the molecular weight distribution (Mw / Mn) of the conjugated diene polymer chain having an active end is within the above range, the production of the conjugated diene rubber is facilitated.
また、本発明の製造方法においては、得られるゴム架橋物を、より低発熱性およびウエットグリップ性に優れたものとするためには、第１工程を、次のような工程とすることが好ましい。
すなわち、不活性溶媒中で、イソプレン、またはイソプレンおよび芳香族ビニル化合物を含む単量体を、重合開始剤により重合し、イソプレン単量体単位８０〜１００重量％、および芳香族ビニル単量体単位０〜２０重量％を含む活性末端を有する重合体ブロック（Ａ）を形成させる工程と、
前記活性末端を有する重合体ブロック（Ａ）と、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体と、を混合して重合反応を継続させ、１，３−ブタジエン単量体単位５０〜１００重量％および芳香族ビニル単量体単位０〜５０重量％を含む活性末端を有する重合体ブロック（Ｂ）を、重合体ブロック（Ａ）と一続きにして形成させることにより、活性末端を有する共役ジエン系重合体鎖を得る工程と、を備えるものとすることが好ましい。
In the production method of the present invention, the first step is preferably the following step in order to make the obtained rubber cross-linked product more excellent in low heat generation and wet grip properties. .
That is, isoprene or a monomer containing isoprene and an aromatic vinyl compound is polymerized with a polymerization initiator in an inert solvent, and isoprene monomer units 80 to 100% by weight, and aromatic vinyl monomer units Forming a polymer block (A) having an active end containing 0 to 20% by weight;
The polymer block (A) having an active terminal and 1,3-butadiene, or a monomer containing 1,3-butadiene and an aromatic vinyl compound are mixed to continue the polymerization reaction, and 1,3 -A polymer block (B) having an active end containing 50 to 100% by weight of a butadiene monomer unit and 0 to 50% by weight of an aromatic vinyl monomer unit is formed continuously with the polymer block (A). And obtaining a conjugated diene polymer chain having an active end by making it preferable.
このような工程を採用することにより、第１工程により得られる活性末端を有する共役ジエン系重合体鎖を、イソプレン単量体単位８０〜１００重量％、および芳香族ビニル単量体単位０〜２０重量％を含む重合体ブロック（Ａ）と、１，３−ブタジエン単量体単位５０〜１００重量％および芳香族ビニル単量体単位０〜５０重量％を含む重合体ブロック（Ｂ）とが一続きにして形成されてなるものとすることができる。
以下、このような態様について説明する。
By adopting such a step, the conjugated diene polymer chain having an active terminal obtained in the first step is converted to 80 to 100% by weight of isoprene monomer units and 0 to 20 aromatic vinyl monomer units. The polymer block (A) containing 1% by weight and the polymer block (B) containing 50 to 100% by weight of 1,3-butadiene monomer units and 0 to 50% by weight of aromatic vinyl monomer units are one. It can be formed continuously.
Hereinafter, such an aspect will be described.
［重合体ブロック（Ａ）］
本発明の一態様に係る共役ジエン系重合体鎖中の重合体ブロック（Ａ）は、重合体ブロック（Ａ）中、イソプレン単量体単位８０〜１００重量％および芳香族ビニル単量体単位０〜２０重量％を含むものであればよいが、イソプレン単量体単位８５〜９５重量％および芳香族ビニル単量体単位５〜１５重量％を含むものであることが好ましく、イソプレン単量体単位８９〜９５重量％および芳香族ビニル単量体単位５〜１１重量％を含むものであることがより好ましい。イソプレン単量体単位と芳香族ビニル単量体単位との含有割合が上記範囲内にあると、共役ジエン系ゴムにシリカを配合した場合に、共役ジエン系ゴムとシリカとの親和性が良好となり、これを用いて得られるゴム架橋物の低発熱性およびウエットグリップ性をより向上させることができる。
[Polymer block (A)]
In the polymer block (A), the polymer block (A) in the conjugated diene polymer chain according to one embodiment of the present invention contains 80 to 100% by weight of isoprene monomer units and 0 aromatic vinyl monomer units. However, it is preferable that it contains 85 to 95% by weight of isoprene monomer units and 5 to 15% by weight of aromatic vinyl monomer units, and isoprene monomer units 89 to 89% by weight. More preferably, it contains 95% by weight and 5 to 11% by weight of aromatic vinyl monomer units. When the content ratio of the isoprene monomer unit and the aromatic vinyl monomer unit is within the above range, the affinity between the conjugated diene rubber and the silica is improved when silica is added to the conjugated diene rubber. The low heat build-up and wet grip properties of the rubber cross-linked product obtained by using this can be further improved.
重合体ブロック（Ａ）に含まれる芳香族ビニル単量体単位を構成するために用いられる芳香族ビニル化合物としては、上述した芳香族ビニル化合物と同じものを用いることができ、これらの中でもスチレンが好ましい。なお、これらの芳香族ビニル化合物は、１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。 As the aromatic vinyl compound used for constituting the aromatic vinyl monomer unit contained in the polymer block (A), the same aromatic vinyl compound as described above can be used, and among these, styrene is used. preferable. In addition, these aromatic vinyl compounds may be used individually by 1 type, and may be used in combination of 2 or more type.
重合体ブロック（Ａ）は、イソプレン単量体単位のみ、またはイソプレン単量体単位および芳香族ビニル単量体単位からなるものであることが好ましいが、所望により、イソプレン単量体単位、またはイソプレン単量体単位および芳香族ビニル単量体単位に加えて、その他の単量体単位を含んでいてもよい。その他の単量体単位を構成するために用いられるその他の化合物としては、１，３−ブタジエン、２，３−ジメチル−１，３−ブタジエン、２−クロロ−１，３−ブタジエン、１，３−ペンタジエン、および１，３−ヘキサジエンなどのイソプレン以外の共役ジエン化合物；アクリロニトリル、およびメタクリロニトリルなどのα，β−不飽和ニトリル；アクリル酸、メタクリル酸、および無水マレイン酸などの不飽和力ルボン酸または酸無水物；メタクリル酸メチル、アクリル酸エチル、およびアクリル酸ブチルなどの不飽和カルボン酸エステル；１，５−ヘキサジエン、１，６−ヘプタジエン、１，７−オクタジエン、ジシクロペンタジエン、および５−エチリデン−２−ノルボルネンなどの非共役ジエン；などが挙げられる。これらの中でも、１，３−ブタジエンが好ましい。これらのその他の単量体は、それぞれ単独で、あるいは２種以上を組み合わせて用いることができる。重合体ブロック（Ａ）中における、その他の単量体単位の含有割合は、２０重量％以下であることが好ましく、１０重量％以下であることがより好ましく、６重量％以下であることがさらに好ましい。 The polymer block (A) is preferably composed of only an isoprene monomer unit or an isoprene monomer unit and an aromatic vinyl monomer unit. If desired, the isoprene monomer unit or isoprene is used. In addition to the monomer unit and the aromatic vinyl monomer unit, other monomer units may be included. Other compounds used to constitute other monomer units include 1,3-butadiene, 2,3-dimethyl-1,3-butadiene, 2-chloro-1,3-butadiene, 1,3 Conjugated diene compounds other than isoprene such as pentadiene and 1,3-hexadiene; α, β-unsaturated nitriles such as acrylonitrile and methacrylonitrile; unsaturated power rubons such as acrylic acid, methacrylic acid and maleic anhydride Acids or anhydrides; unsaturated carboxylic esters such as methyl methacrylate, ethyl acrylate, and butyl acrylate; 1,5-hexadiene, 1,6-heptadiene, 1,7-octadiene, dicyclopentadiene, and 5 -Non-conjugated dienes such as ethylidene-2-norbornene; Among these, 1,3-butadiene is preferable. These other monomers can be used alone or in combination of two or more. The content ratio of the other monomer units in the polymer block (A) is preferably 20% by weight or less, more preferably 10% by weight or less, and further preferably 6% by weight or less. preferable.
本発明において、共役ジエン系重合体鎖中の重合体ブロック（Ａ）は、不活性溶媒中、イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体を、重合開始剤により重合することにより形成される。形成された重合体ブロック（Ａ）は、活性末端を有するものとなる。 In the present invention, the polymer block (A) in the conjugated diene polymer chain is obtained by polymerizing a monomer containing isoprene or isoprene and an aromatic vinyl compound with a polymerization initiator in an inert solvent. It is formed. The formed polymer block (A) has an active end.
重合体ブロック（Ａ）を形成するために、イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体の重合に用いられる不活性溶媒としては、上述した不活性溶媒と同じものを用いることができる。不活性溶媒の使用量は、単量体濃度が、好ましくは１〜８０重量％となる量であり、より好ましくは１０〜５０重量％となる量である。 In order to form the polymer block (A), the same inert solvent as described above may be used as the inert solvent used for the polymerization of the monomer containing isoprene or isoprene and an aromatic vinyl compound. it can. The amount of the inert solvent used is such that the monomer concentration is preferably 1 to 80% by weight, more preferably 10 to 50% by weight.
重合体ブロック（Ａ）を形成するために用いられる重合開始剤としては、イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体を重合させて、活性末端を有する重合体鎖を与えることができるものであれば、特に限定されない。その具体例としては、上述した重合開始剤と同じものを挙げることができる。 As a polymerization initiator used to form the polymer block (A), isoprene or a monomer containing isoprene and an aromatic vinyl compound is polymerized to give a polymer chain having an active end. If it can do, it will not specifically limit. Specific examples thereof include the same as the polymerization initiator described above.
重合開始剤の使用量は、目的とする分子量に応じて決定すればよいが、イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体１００ｇ当り、好ましくは４〜２５０ミリモル、より好ましくは６〜２００ミリモル、特に好ましくは１０〜７０ミリモルの範囲である。 The amount of the polymerization initiator used may be determined according to the target molecular weight, but is preferably 4 to 250 mmol, more preferably 6 per 100 g of monomer containing isoprene or isoprene and an aromatic vinyl compound. It is in the range of ˜200 mmol, particularly preferably 10 to 70 mmol.
イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体を重合する際における重合温度は、好ましくは−８０〜＋１５０℃、より好ましくは０〜１００℃、さらに好ましくは２０〜９０℃の範囲である。重合様式としては、回分式、連続式など、いずれの様式をも採用できる。また、結合様式としては、たとえば、ブロック状、テーパー状、およびランダム状などの種々の結合様式とすることができる。 The polymerization temperature when polymerizing isoprene or a monomer containing isoprene and an aromatic vinyl compound is preferably in the range of −80 to + 150 ° C., more preferably 0 to 100 ° C., and still more preferably 20 to 90 ° C. is there. As the polymerization mode, any mode such as batch mode or continuous mode can be adopted. Moreover, as a coupling | bonding mode, it can be set as various coupling | bonding modes, such as block shape, a taper shape, and random shape, for example.
また、本発明の一態様に係る製造方法においては、重合体ブロック（Ａ）を形成するに際し、極性化合物の存在下で、イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体を重合することが好ましい。具体的には、重合開始剤１モルに対して、好ましくは０．０１〜１．０モル、より好ましくは０．０２〜０．５モル、さらに好ましくは０．０５〜０．２モルの極性化合物を使用し、このような極性化合物の存在下で重合を行うことにより、重合体ブロック（Ａ）中における、イソプレン単量体単位部分のビニル結合含有量を好適に調節することができる。重合体ブロック（Ａ）におけるイソプレン単量体単位部分のビニル結合含有量は、好ましくは４０重量％以下であり、より好ましくは２５重量％以下、さらに好ましくは１５重量％以下である。また、ビニル結合含有量の下限は特に限定されないが、好ましくは１重量％以上である。イソプレン単量体単位部分のビニル結合含有量を上記範囲内とすることにより、得られるゴム架橋物の低発熱性をより向上させることができる。なお、イソプレン単量体単位部分のビニル結合は、１，２−ビニル結合、３，４−ビニル結合のいずれであってもよい。 Moreover, in the manufacturing method which concerns on 1 aspect of this invention, when forming a polymer block (A), the monomer containing an isoprene or an isoprene and an aromatic vinyl compound is superposed | polymerized in presence of a polar compound. It is preferable. Specifically, the polarity is preferably 0.01 to 1.0 mol, more preferably 0.02 to 0.5 mol, and still more preferably 0.05 to 0.2 mol with respect to 1 mol of the polymerization initiator. By using the compound and carrying out polymerization in the presence of such a polar compound, the vinyl bond content of the isoprene monomer unit portion in the polymer block (A) can be suitably adjusted. The vinyl bond content of the isoprene monomer unit portion in the polymer block (A) is preferably 40% by weight or less, more preferably 25% by weight or less, and further preferably 15% by weight or less. The lower limit of the vinyl bond content is not particularly limited, but is preferably 1% by weight or more. By setting the vinyl bond content of the isoprene monomer unit portion within the above range, the low exothermic property of the resulting rubber cross-linked product can be further improved. The vinyl bond in the isoprene monomer unit portion may be either a 1,2-vinyl bond or a 3,4-vinyl bond.
極性化合物の存在下で、イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体の重合を行う方法としては、特に限定されないが、たとえば、重合に用いる不活性溶媒中に、極性化合物を添加して、重合を行う方法などが挙げられる。また、極性化合物としては、上述した極性化合物と同じものを用いることができる。 The method for polymerizing isoprene or a monomer containing isoprene and an aromatic vinyl compound in the presence of the polar compound is not particularly limited. For example, the polar compound is added to an inert solvent used for the polymerization. Then, a method of performing polymerization and the like can be mentioned. Moreover, as a polar compound, the same thing as the polar compound mentioned above can be used.
重合体ブロック（Ａ）の重量平均分子量（Ｍｗ）は、ゲルパーミエーションクロマトグラフィによって測定されるポリスチレン換算の値として、５００〜１５，０００であることが好ましく、１，０００〜１２，０００であることがより好ましく、１，５００〜１０，０００であることが特に好ましい。重合体ブロック（Ａ）の重量平均分子量が上記範囲内にあると、得られるゴム架橋物の低発熱性およびウエットグリップ性をより向上させることができる。 The weight average molecular weight (Mw) of the polymer block (A) is preferably from 500 to 15,000, and preferably from 1,000 to 12,000 as a value in terms of polystyrene measured by gel permeation chromatography. Is more preferable and 1,500 to 10,000 is particularly preferable. When the weight average molecular weight of the polymer block (A) is within the above range, the low exothermic property and wet grip property of the resulting rubber cross-linked product can be further improved.
また、重合体ブロック（Ａ）の重量平均分子量（Ｍｗ）と数平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）で表わされる分子量分布は、１.０〜１．５であることが好ましく、１.０〜１．３であることがより好ましい。重合体ブロック（Ａ）の分子量分布の値（Ｍｗ／Ｍｎ）が上記範囲内にあると、共役ジエン系ゴムの製造がより容易となる。 The molecular weight distribution represented by the ratio (Mw / Mn) of the weight average molecular weight (Mw) and the number average molecular weight (Mn) of the polymer block (A) is preferably 1.0 to 1.5, More preferably, it is 1.0 to 1.3. When the value (Mw / Mn) of the molecular weight distribution of the polymer block (A) is within the above range, the production of the conjugated diene rubber becomes easier.
［重合体ブロック（Ｂ）］
本発明の一態様に係る共役ジエン系重合体鎖中の重合体ブロック（Ｂ）は、重合体ブロック（Ｂ）中、１，３−ブタジエン単量体単位５０〜１００重量％および芳香族ビニル単量体単位０〜５０重量％を含むものであればよいが、１，３−ブタジエン単量体単位５５〜９５重量％および芳香族ビニル単量体単位５〜４５重量％を含むものであることが好ましい。１，３−ブタジエン単量体単位と芳香族ビニル単量体単位との含有割合が上記範囲内にあると、共役ジエン系ゴムの製造がより容易となる。
[Polymer block (B)]
The polymer block (B) in the conjugated diene polymer chain according to one embodiment of the present invention comprises 50 to 100% by weight of 1,3-butadiene monomer unit and aromatic vinyl unit in the polymer block (B). It is sufficient if it contains 0 to 50% by weight of the monomer unit, but preferably contains 55 to 95% by weight of 1,3-butadiene monomer unit and 5 to 45% by weight of aromatic vinyl monomer unit. . When the content ratio of the 1,3-butadiene monomer unit and the aromatic vinyl monomer unit is within the above range, the production of the conjugated diene rubber becomes easier.
重合体ブロック（Ｂ）に含まれる芳香族ビニル単量体単位を構成するために用いられる芳香族ビニル化合物としては、上述した芳香族ビニル化合物と同じものを用いることができ、これらの中でも、スチレンが好ましい。 As the aromatic vinyl compound used for constituting the aromatic vinyl monomer unit contained in the polymer block (B), the same aromatic vinyl compound as described above can be used, and among these, styrene Is preferred.
重合体ブロック（Ｂ）は、１，３−ブタジエン単量体単位のみ、または１，３−ブタジエン単量体単位および芳香族ビニル単量体単位からなるものであることが好ましいが、本発明における本質的な特性を損なわない範囲において、所望により、１，３−ブタジエン単量体単位、または１，３−ブタジエン単量体単位および芳香族ビニル単量体単位に加えて、その他の単量体単位を含んでいてもよい。その他の単量体単位を構成するために用いられるその他の単量体としては、上述した重合体ブロック（Ａ）において例示された化合物（ただし、１，３−ブタジエンを除く）と同じものを用いることができる。また、重合体ブロック（Ｂ）においては、その他の単量体としてイソプレンを用いることもできる。重合体ブロック（Ｂ）中における、その他の単量体単位の含有割合は、５０重量％以下であることが好ましく、４０重量％以下であることがより好ましく、３５重量％以下であることがさらに好ましい。 The polymer block (B) is preferably composed only of 1,3-butadiene monomer units or composed of 1,3-butadiene monomer units and aromatic vinyl monomer units. As long as the essential characteristics are not impaired, the 1,3-butadiene monomer unit, or other monomer in addition to the 1,3-butadiene monomer unit and the aromatic vinyl monomer unit, as desired. Units may be included. As other monomers used for constituting other monomer units, the same compounds as those exemplified in the polymer block (A) described above (excluding 1,3-butadiene) are used. be able to. In the polymer block (B), isoprene can be used as another monomer. The content ratio of other monomer units in the polymer block (B) is preferably 50% by weight or less, more preferably 40% by weight or less, and further preferably 35% by weight or less. preferable.
本発明の一態様において、共役ジエン系重合体鎖中の重合体ブロック（Ｂ）は、上述した活性末端を有する重合体ブロック（Ａ）と、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体と、を混合して重合反応を継続させることにより、重合体ブロック（Ａ）と一続きに形成される。形成された重合体ブロック（Ｂ）は、活性末端を有するものとなる。一方、重合体ブロック（Ａ）からは、活性末端が消失する。 In one embodiment of the present invention, the polymer block (B) in the conjugated diene polymer chain includes the above-described polymer block (A) having an active end, 1,3-butadiene, or 1,3-butadiene and The polymer block (A) is formed continuously by mixing the monomer containing the aromatic vinyl compound and continuing the polymerization reaction. The formed polymer block (B) has an active end. On the other hand, the active terminal disappears from the polymer block (A).
重合体ブロック（Ｂ）を形成するために、重合体ブロック（Ａ）と、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体との重合に用いられる不活性溶媒としては、特に限定されず、上述した不活性溶媒と同じものを用いることができる。 Inert used for polymerizing polymer block (A) with monomers comprising 1,3-butadiene or 1,3-butadiene and an aromatic vinyl compound to form polymer block (B) The solvent is not particularly limited, and the same inert solvent as described above can be used.
重合体ブロック（Ｂ）を形成する際における、活性末端を有する重合体ブロック（Ａ）の使用量は、目的とする分子量に応じて決定すればよいが、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体１００ｇ当り、好ましくは０．１〜５ミリモル、より好ましくは０．１５〜２ミリモル、さらに好ましくは０．２〜１．５ミリモルの範囲である。 The amount of the polymer block (A) having an active terminal in forming the polymer block (B) may be determined according to the target molecular weight, but 1,3-butadiene or 1,3 -Preferably it is 0.1-5 mmol, More preferably, it is 0.15-2 mmol, More preferably, it is the range of 0.2-1.5 mmol per 100g of monomers containing a butadiene and an aromatic vinyl compound.
重合体ブロック（Ａ）と１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体との混合方法は、特に限定されず、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体の溶液中に活性末端を有する重合体ブロック（Ａ）を加えてもよいし、活性末端を有する重合体ブロック（Ａ）の溶液中に１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体を加えてもよい。重合の制御の観点より、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体の溶液中に活性末端を有する重合体ブロック（Ａ）を加える方法が好ましい。 The mixing method of the polymer block (A) and 1,3-butadiene, or a monomer containing 1,3-butadiene and an aromatic vinyl compound is not particularly limited, and 1,3-butadiene, or 1,3 -The polymer block (A) having an active end may be added to a solution of a monomer containing butadiene and an aromatic vinyl compound, or 1, 3 in the solution of the polymer block (A) having an active end. A monomer containing butadiene or 1,3-butadiene and an aromatic vinyl compound may be added. From the viewpoint of controlling the polymerization, a method of adding a polymer block (A) having an active end to a solution of 1,3-butadiene or a monomer containing 1,3-butadiene and an aromatic vinyl compound is preferable.
１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体を重合するにおける重合温度は、好ましくは−８０〜＋１５０℃、より好ましくは０〜１００℃、さらに好ましくは２０〜９０℃の範囲である。重合様式としては、回分式、連続式など、いずれの様式をも採用できる。重合体ブロック（Ｂ）を共重合体鎖とする場合には、結合のランダム性を制御しやすい点で、回分式が好ましい。 The polymerization temperature for polymerizing 1,3-butadiene or a monomer containing 1,3-butadiene and an aromatic vinyl compound is preferably -80 to + 150 ° C, more preferably 0 to 100 ° C, and still more preferably 20 It is the range of -90 degreeC. As the polymerization mode, any mode such as batch mode or continuous mode can be adopted. When the polymer block (B) is used as a copolymer chain, a batch system is preferable because the randomness of the bonds can be easily controlled.
重合体ブロック（Ｂ）を共重合体鎖とする場合の各単量体の結合様式は、たとえば、ブロック状、テーパー状、およびランダム状などの種々の結合様式とすることができる。これらの中でも、ランダム状が好ましい。ランダム状にすることにより、得られるゴム架橋物の低発熱性をより向上させることができる。なお、１，３−ブタジエンおよび芳香族ビニル化合物の結合様式をランダム状にする場合、重合系内において、１，３−ブタジエンと芳香族ビニル化合物との合計量に対する芳香族ビニル化合物の比率が高くなりすぎないように、１，３−ブタジエンまたは１，３−ブタジエンと芳香族ビニル化合物とを、連続的または断続的に重合系内に供給して重合することが好ましい。 When the polymer block (B) is used as a copolymer chain, the bonding mode of each monomer may be various bonding modes such as a block shape, a taper shape, and a random shape. Among these, a random shape is preferable. By making it random, the low heat build-up of the resulting rubber cross-linked product can be further improved. When the bonding mode of 1,3-butadiene and aromatic vinyl compound is made random, the ratio of the aromatic vinyl compound to the total amount of 1,3-butadiene and aromatic vinyl compound is high in the polymerization system. In order not to become too much, it is preferable to polymerize by supplying 1,3-butadiene or 1,3-butadiene and an aromatic vinyl compound continuously or intermittently into the polymerization system.
また、本発明の一態様においては、重合体ブロック（Ａ）の形成時と同様に、重合体ブロック（Ｂ）を形成するに際し、極性化合物の存在下で、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体を重合することが好ましい。具体的には、重合開始剤１モルに対して、好ましくは０．０１〜１．２モル、より好ましくは０．１〜１．１モル、さらに好ましくは０．１〜１．０モルの極性化合物を使用し、このような極性化合物の存在下で重合を行うことにより、重合体ブロック（Ｂ）中における、１，３−ブタジエン単量体単位部分のビニル結合含有量を好適に調節することができ、その結果として、最終的に得られる共役ジエン系ゴムに含まれる共役ジエン単量体単位部分におけるビニル結合含有量を好適に調節することができる。重合体ブロック（Ｂ）における１，３−ブタジエン単量体単位部分のビニル結合含有量は、好ましくは５０重量％以下であり、より好ましくは４５重量％以下、さらに好ましくは４２重量％以下である。また、ビニル結合含有量の下限は特に限定されないが、好ましくは５重量％以上である。 In one embodiment of the present invention, as in the formation of the polymer block (A), when forming the polymer block (B), 1,3-butadiene, or 1, It is preferable to polymerize a monomer containing 3-butadiene and an aromatic vinyl compound. Specifically, the polarity is preferably 0.01 to 1.2 mol, more preferably 0.1 to 1.1 mol, and still more preferably 0.1 to 1.0 mol, with respect to 1 mol of the polymerization initiator. The vinyl bond content of the 1,3-butadiene monomer unit portion in the polymer block (B) is suitably adjusted by polymerizing in the presence of such a polar compound. As a result, the vinyl bond content in the conjugated diene monomer unit portion contained in the finally obtained conjugated diene rubber can be suitably adjusted. The vinyl bond content of the 1,3-butadiene monomer unit portion in the polymer block (B) is preferably 50% by weight or less, more preferably 45% by weight or less, and further preferably 42% by weight or less. . The lower limit of the vinyl bond content is not particularly limited, but is preferably 5% by weight or more.
極性化合物の存在下で、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体の重合を行う方法としては、特に限定されないが、たとえば、重合に用いる不活性溶媒中に、極性化合物を添加して、重合を行う方法などが挙げられる。この場合においては、重合体ブロック（Ａ）の形成時に添加した極性化合物の量と、新たに添加する極性化合物の量との合計が上記した範囲となるように、極性化合物の添加を行えばよい。そのため、重合体ブロック（Ａ）の形成時に、重合体ブロック（Ｂ）における１，３−ブタジエン単量体単位部分のビニル結合含有量を調節するのに十分な量の極性化合物を添加している場合は、新たに極性化合物を添加しなくてもよい。また、極性化合物としては、上述した極性化合物と同じものを用いることができる。 A method for polymerizing a monomer containing 1,3-butadiene or 1,3-butadiene and an aromatic vinyl compound in the presence of a polar compound is not particularly limited. For example, an inert solvent used for polymerization Examples thereof include a method of polymerizing by adding a polar compound. In this case, the polar compound may be added so that the sum of the amount of the polar compound added during the formation of the polymer block (A) and the amount of the newly added polar compound falls within the above-described range. . Therefore, when the polymer block (A) is formed, a sufficient amount of polar compound is added to adjust the vinyl bond content of the 1,3-butadiene monomer unit portion in the polymer block (B). In this case, it is not necessary to add a new polar compound. Moreover, as a polar compound, the same thing as the polar compound mentioned above can be used.
このようにして、重合体ブロック（Ａ）および重合体ブロック（Ｂ）を有する、活性末端を有する共役ジエン系重合体鎖を得ることができる。本発明の一態様においては、活性末端を有する共役ジエン系重合体鎖は、生産性の観点より、重合体ブロック（Ａ）−重合体ブロック（Ｂ）で構成され、かつ、重合体ブロック（Ｂ）の末端が活性末端であることが好ましいが、重合体ブロック（Ａ）を複数有するものであってもよいし、その他の重合体ブロックを有するものであってもよい。たとえば、重合体ブロック（Ａ）−重合体ブロック（Ｂ）−重合体ブロック（Ａ）などの、活性末端を有する共役ジエン系重合体鎖が挙げられる。この場合には、重合体ブロック（Ｂ）に続いて形成された重合体ブロック（Ａ）の末端に、活性末端が形成されることとなる。共役ジエン系重合体鎖の活性末端側に重合体ブロック（Ａ）を形成させる場合、イソプレンの使用量は、初めの重合反応（１つ目の重合体ブロック（Ａ）を形成するための重合反応）に使用した重合開始剤１モルに対して、１０〜１００モルであることが好ましく、１５〜７０モルであることがより好ましく、２０〜３５モルであることが特に好ましい。 In this way, a conjugated diene polymer chain having an active terminal and having a polymer block (A) and a polymer block (B) can be obtained. In one embodiment of the present invention, the conjugated diene polymer chain having an active end is composed of a polymer block (A) -polymer block (B) and a polymer block (B ) Is preferably an active end, but may have a plurality of polymer blocks (A) or may have other polymer blocks. Examples thereof include conjugated diene polymer chains having an active end such as polymer block (A) -polymer block (B) -polymer block (A). In this case, an active terminal is formed at the terminal of the polymer block (A) formed subsequent to the polymer block (B). When the polymer block (A) is formed on the active terminal side of the conjugated diene polymer chain, the amount of isoprene used is the initial polymerization reaction (polymerization reaction for forming the first polymer block (A)). ) Is preferably 10 to 100 mol, more preferably 15 to 70 mol, and particularly preferably 20 to 35 mol with respect to 1 mol of the polymerization initiator used in (1).
本発明の一態様において得られる、活性末端を有する共役ジエン系重合体鎖における重合体ブロック（Ａ）と重合体ブロック（Ｂ）との重量比（重合体ブロック（Ａ）、重合体ブロック（Ｂ）が複数存在する場合は、それぞれの合計重量を基準とした重量比）は、（重合体ブロック（Ａ）の重量）／（重合体ブロック（Ｂ）の重量）で、０．００１〜０．１であることが好ましく、０．００３〜０．０７であることがより好ましく、０．００５〜０．０５であることが特に好ましい。重合体ブロック（Ａ）と重合体ブロック（Ｂ）との重量比を上記範囲内とすることにより、得られるゴム架橋物を、ウエットグリップ性と低発熱性とのバランスが良好なものとすることができる。 The weight ratio of the polymer block (A) to the polymer block (B) in the conjugated diene polymer chain having an active end obtained in one embodiment of the present invention (polymer block (A), polymer block (B )), The weight ratio based on the total weight of each of them is (weight of polymer block (A)) / (weight of polymer block (B)). 1 is preferable, 0.003 to 0.07 is more preferable, and 0.005 to 0.05 is particularly preferable. By making the weight ratio of the polymer block (A) and the polymer block (B) within the above range, the resulting rubber cross-linked product should have a good balance between wet grip and low heat build-up. Can do.
重合体ブロック（Ａ）および重合体ブロック（Ｂ）を有する、活性末端を有する共役ジエン系重合体鎖における、イソプレン単量体単位および１，３−ブタジエン単量体単位の合計単量体単位と、芳香族ビニル単量体単位との含有割合は、活性末端を有する共役ジエン系重合体鎖中、イソプレン単量体単位および１，３−ブタジエン単量体単位の合計単量体単位５０〜１００重量％、および芳香族ビニル単量体単位０〜５０重量％であることが好ましく、イソプレン単量体単位および１，３−ブタジエン単量体単位の合計単量体単位５５〜９５重量％、および芳香族ビニル単量体単位５〜４５重量％であることがより好ましい。また、重合体ブロック（Ａ）および重合体ブロック（Ｂ）を有する、活性末端を有する共役ジエン系重合体鎖における、イソプレン単量体単位中および１，３−ブタジエン単量体単位中のビニル結合含有量は、上述した重合体ブロック（Ｂ）における１，３−ブタジエン単量体単位中のビニル結合含有量と同じ範囲にあることが好ましい。 A total monomer unit of an isoprene monomer unit and a 1,3-butadiene monomer unit in a conjugated diene polymer chain having an active end and having a polymer block (A) and a polymer block (B); The content ratio with respect to the aromatic vinyl monomer unit is a total monomer unit of 50 to 100 of the isoprene monomer unit and the 1,3-butadiene monomer unit in the conjugated diene polymer chain having an active end. And 0 to 50% by weight of aromatic vinyl monomer units, 55 to 95% by weight of total monomer units of isoprene monomer units and 1,3-butadiene monomer units, and It is more preferable that it is 5-45 weight% of aromatic vinyl monomer units. In addition, vinyl bonds in the isoprene monomer unit and in the 1,3-butadiene monomer unit in the conjugated diene polymer chain having an active end having the polymer block (A) and the polymer block (B). The content is preferably in the same range as the vinyl bond content in the 1,3-butadiene monomer unit in the polymer block (B) described above.
＜第２工程＞
本発明の製造方法の第２工程は、第１工程にて得られた活性末端を有する共役ジエン系重合体鎖に、シロキサンを反応させる工程である。
<Second step>
The second step of the production method of the present invention is a step of reacting siloxane with the conjugated diene polymer chain having an active end obtained in the first step.
本発明の製造方法の第２工程で用いるシロキサンとしては、シロキサン構造（−Ｓｉ−Ｏ−）を主鎖として有するものであればよく、特に限定されないが、側鎖に有機基を有するオルガノシロキサンが好ましく、下記一般式（２）で表されるポリオルガノシロキサンがより好ましい。
なお、本発明の製造方法の第２工程において、シロキサンは、第１工程にて得られた活性末端を有する共役ジエン系重合体鎖を変性させるための変性剤として作用する。
In the second step of the production method of the present invention, siloxane acts as a modifier for modifying the conjugated diene polymer chain having an active end obtained in the first step.
一般式（２）中、Ｒ４〜Ｒ１１は、炭素数１〜６のアルキル基、または炭素数６〜１２のアリール基であり、これらは互いに同一であっても相違していてもよい。Ｘ２およびＸ５は、炭素数１〜６のアルキル基、炭素数６〜１２のアリール基、炭素数１〜５のアルコキシ基、および、エポキシ基を含有する炭素数４〜１２の基からなる群より選ばれるいずれかの基であり、これらは互いに同一であっても相違していてもよい。Ｘ３は、炭素数１〜５のアルコキシ基、またはエポキシ基を含有する炭素数４〜１２の基であり、Ｘ３が複数あるときは、それらは互いに同一であっても相違していてもよい。Ｘ４は、２〜２０のアルキレングリコールの繰返し単位を含有する基であり、Ｘ４が複数あるときは、それらは互いに同一であっても相違していてもよい。ｍは０〜２００の整数、ｎは０〜２００の整数、ｋは０〜２００の整数であり、ｍ＋ｎ＋ｋは１以上である。 In General Formula (2), R 4 to R 11 are each an alkyl group having 1 to 6 carbon atoms or an aryl group having 6 to 12 carbon atoms, and these may be the same as or different from each other. X 2 and X 5 are composed of a C 4-12 group containing an alkyl group having 1-6 carbon atoms, an aryl group having 6-12 carbon atoms, an alkoxy group having 1-5 carbon atoms, and an epoxy group. Any group selected from the group may be the same or different. X 3 is an alkoxy group having 1 to 5 carbon atoms or a group having 4 to 12 carbon atoms containing an epoxy group, and when there are a plurality of X 3 , they may be the same as or different from each other. Good. X 4 is a group containing 2 to 20 alkylene glycol repeating units, and when there are a plurality of X 4 , they may be the same as or different from each other. m is an integer of 0 to 200, n is an integer of 0 to 200, k is an integer of 0 to 200, and m + n + k is 1 or more.
一般式（２）で表されるポリオルガノシロキサンにおいて、一般式（２）中のＲ４〜Ｒ１１、Ｘ２およびＸ５を構成し得る炭素数１〜６のアルキル基としては、たとえば、メチル基、エチル基、ｎ−プロピル基、イソプロピル基、ブチル基、ペンチル基、ヘキシル基およびシクロヘキシル基などが挙げられる。炭素数６〜１２のアリール基としては、たとえば、フェニル基およびメチルフェニル基などが挙げられる。これらの中でも、ポリオルガノシロキサン自体の製造の容易性の観点から、メチル基およびエチル基が好ましい。 In the polyorganosiloxane represented by the general formula (2), examples of the alkyl group having 1 to 6 carbon atoms that can constitute R 4 to R 11 , X 2 and X 5 in the general formula (2) include methyl Group, ethyl group, n-propyl group, isopropyl group, butyl group, pentyl group, hexyl group and cyclohexyl group. Examples of the aryl group having 6 to 12 carbon atoms include a phenyl group and a methylphenyl group. Among these, a methyl group and an ethyl group are preferable from the viewpoint of ease of production of the polyorganosiloxane itself.
また、一般式（２）で表されるポリオルガノシロキサンにおいて、Ｘ２、Ｘ３およびＸ５を構成し得る炭素数１〜５のアルコキシ基としては、たとえば、メトキシ基、エトキシ基、プロポキシ基、イソプロポキシ基およびブトキシ基などが挙げられる。これらの中でも、ポリオルガノシロキサン自体の製造の容易性の観点から、メトキシ基およびエトキシ基が好ましい。 In the polyorganosiloxane represented by the general formula (2), examples of the alkoxy group having 1 to 5 carbon atoms that can constitute X 2 , X 3 and X 5 include a methoxy group, an ethoxy group, a propoxy group, An isopropoxy group, a butoxy group, etc. are mentioned. Among these, a methoxy group and an ethoxy group are preferable from the viewpoint of ease of production of the polyorganosiloxane itself.
さらに、一般式（２）で表されるポリオルガノシロキサンにおいて、Ｘ２、Ｘ３およびＸ５を構成し得るエポキシ基を含有する炭素数４〜１２の基としては、たとえば、下記一般式（６）で表される基が挙げられる。
−Ｚ３−Ｚ４−Ｅ２ （６）
一般式（６）中、Ｚ３は、炭素数１〜１０のアルキレン基、またはアルキルアリーレン基であり、Ｚ４はメチレン基、硫黄原子、または酸素原子であり、Ｅ２はエポキシ基を有する炭素数２〜１０の炭化水素基である。
Furthermore, in the polyorganosiloxane represented by the general formula (2), examples of the group having 4 to 12 carbon atoms containing an epoxy group that can constitute X 2 , X 3 and X 5 include the following general formula (6 ) Is represented.
-Z 3 -Z 4 -E 2 (6 )
In General Formula (6), Z 3 is an alkylene group having 1 to 10 carbon atoms or an alkylarylene group, Z 4 is a methylene group, a sulfur atom, or an oxygen atom, and E 2 is a carbon having an epoxy group. It is a hydrocarbon group of several 2 to 10.
一般式（６）で表される基としては、Ｚ４が酸素原子であるものが好ましく、Ｚ４が酸素原子であり、かつ、Ｅ２がグリシジル基であるものがより好ましく、Ｚ３が炭素数１〜３のアルキレン基であり、Ｚ４が酸素原子であり、かつ、Ｅ２がグリシジル基であるものが特に好ましい。 The group represented by the general formula (6) is preferably a Z 4 is an oxygen atom, a Z 4 is an oxygen atom, and is more preferably a E 2 is a glycidyl group, Z 3 is carbon Particularly preferred is an alkylene group having a number of 1 to 3, Z 4 is an oxygen atom, and E 2 is a glycidyl group.
また、一般式（２）で表されるポリオルガノシロキサンにおいて、Ｘ２およびＸ５としては、上記の中でも、エポキシ基を含有する炭素数４〜１２の基、または、炭素数１〜６のアルキル基が好ましい。また、Ｘ３としては、上記の中でも、エポキシ基を含有する炭素数４〜１２の基が好ましい。さらに、Ｘ２およびＸ５が炭素数１〜６のアルキル基であり、Ｘ３がエポキシ基を含有する炭素数４〜１２の基であることがより好ましい。 In addition, in the polyorganosiloxane represented by the general formula (2), as X 2 and X 5 , among the above, a group having 4 to 12 carbon atoms containing an epoxy group or an alkyl having 1 to 6 carbon atoms Groups are preferred. X 3 is preferably a group having 4 to 12 carbon atoms containing an epoxy group. Further, an X 2 and X 5 is an alkyl group having 1 to 6 carbon atoms, and more preferably X 3 is a group having 4 to 12 carbon atoms containing an epoxy group.
また、一般式（２）で表されるポリオルガノシロキサンにおいて、Ｘ４、すなわち２〜２０のアルキレングリコールの繰返し単位を含有する基としては、下記一般式（７）で表される基が好ましい。
一般式（２）で表されるポリオルガノシロキサンにおいて、ｍは０〜２００の整数、好ましくは２０〜１５０の整数、より好ましくは３０〜１２０の整数である。ｍが２００以下であると、一般式（２）で表されるポリオルガノシロキサン自体の製造がより容易になると共に、その粘度が高くなりすぎず、取り扱いもより容易となる。 In the polyorganosiloxane represented by the general formula (2), m is an integer of 0 to 200, preferably an integer of 20 to 150, more preferably an integer of 30 to 120. When m is 200 or less, the production of the polyorganosiloxane itself represented by the general formula (2) becomes easier, the viscosity does not become too high, and handling becomes easier.
また、一般式（２）で表されるポリオルガノシロキサンにおいて、ｎは０〜２００の整数、好ましくは０〜１５０の整数、より好ましくは０〜１２０の整数である。ｋは０〜２００の整数、好ましくは０〜１５０の整数、より好ましくは０〜１３０の整数である。ｍ、ｎおよびｋの合計数は１以上であり、１〜４００であることが好ましく、２０〜３００であることがより好ましく、３０〜２５０であることが特に好ましい。ｍ、ｎおよびｋの合計数が１以上であると、一般式（２）で表されるポリオルガノシロキサンと活性末端を有する共役ジエン系重合体鎖との反応が進行し易く、さらに、ｍ、ｎおよびｋの合計数が４００以下であると、一般式（２）で表されるポリオルガノシロキサン自体の製造が容易になると共に、その粘度が高くなりすぎず、取り扱いも容易となる。 Moreover, in the polyorganosiloxane represented by General formula (2), n is an integer of 0-200, Preferably it is an integer of 0-150, More preferably, it is an integer of 0-120. k is an integer of 0-200, preferably an integer of 0-150, more preferably an integer of 0-130. The total number of m, n and k is 1 or more, preferably 1 to 400, more preferably 20 to 300, and particularly preferably 30 to 250. When the total number of m, n and k is 1 or more, the reaction between the polyorganosiloxane represented by the general formula (2) and the conjugated diene polymer chain having an active end easily proceeds, and m, When the total number of n and k is 400 or less, the production of the polyorganosiloxane itself represented by the general formula (2) is facilitated, the viscosity is not excessively increased, and the handling is facilitated.
本発明の製造方法の第２工程における、シロキサンの使用量は、上述した第１工程において重合に使用した重合開始剤１モルに対して、シロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、好ましくは０．１〜１０モル、より好ましくは０．２〜５モルである。シロキサンの使用量が上記範囲内にあると、得られるゴム架橋物の低発熱性をより高めることができる。 The amount of siloxane used in the second step of the production method of the present invention is such that the siloxane structure (—Si—O—) in the siloxane is repeated with respect to 1 mol of the polymerization initiator used in the polymerization in the first step. In terms of the number of units, it is preferably 0.1 to 10 mol, more preferably 0.2 to 5 mol. When the usage-amount of siloxane exists in the said range, the low exothermic property of the rubber crosslinked material obtained can be improved more.
シロキサンと活性末端を有する共役ジエン系重合体鎖とを反応させる方法は、特に限定されないが、これらを、それぞれが溶解可能な溶媒中で、混合する方法などが挙げられる。この際に用いる溶媒としては、上述した第１工程において用いる不活性溶媒として例示したものなどを用いることができる。また、この際においては、活性末端を有する共役ジエン系重合体鎖を得るための重合に用いた重合溶液に、シロキサンを添加する方法が簡便であり好ましい。また、この際においては、シロキサンは、不活性溶媒に溶解して重合系内に添加することが好ましく、その溶液濃度は、１〜５０重量％の範囲とすることが好ましい。反応温度は、特に限定されないが、通常０〜１２０℃であり、反応時間も特に限定されないが、通常１分〜１時間である。 A method of reacting siloxane with a conjugated diene polymer chain having an active end is not particularly limited, and examples thereof include a method of mixing them in a solvent in which each is soluble. As the solvent used in this case, those exemplified as the inert solvent used in the first step described above can be used. In this case, a method of adding siloxane to a polymerization solution used for polymerization for obtaining a conjugated diene polymer chain having an active end is simple and preferable. In this case, the siloxane is preferably dissolved in an inert solvent and added to the polymerization system, and the solution concentration is preferably in the range of 1 to 50% by weight. Although reaction temperature is not specifically limited, Usually, it is 0-120 degreeC, Reaction time is also not specifically limited, Usually, it is 1 minute-1 hour.
活性末端を有する共役ジエン系重合体鎖を含有する溶液に、シロキサンを添加する時期は特に限定されないが、重合反応が完結しておらず、活性末端を有する共役ジエン系重合体鎖を含有する溶液が単量体をも含有している状態、より具体的には、活性末端を有する共役ジエン系重合体鎖を含有する溶液が、１００ｐｐｍ以上、より好ましくは３００〜５０，０００ｐｐｍの単量体を含有している状態で、この溶液にシロキサンを添加することが望ましい。シロキサンの添加をこのように行なうことにより、活性末端を有する共役ジエン系重合体鎖と重合系中に含まれる不純物などとの副反応を抑制して、反応を良好に制御することが可能となる。 The timing of adding siloxane to the solution containing conjugated diene polymer chains having active ends is not particularly limited, but the polymerization reaction is not completed and the solution containing conjugated diene polymer chains having active ends More specifically, a solution containing a conjugated diene polymer chain having an active end is 100 ppm or more, more preferably 300 to 50,000 ppm of monomer. It is desirable to add siloxane to this solution in the contained state. By adding siloxane in this manner, side reactions between the conjugated diene polymer chain having an active terminal and impurities contained in the polymerization system can be suppressed, and the reaction can be controlled well. .
本発明の製造方法の第２工程によれば、上述した第１工程にて得られた活性末端を有する共役ジエン系重合体鎖の活性末端に、変性剤としてのシロキサンを反応させることで、少なくとも一部の共役ジエン系重合体鎖は、シロキサン構造中のケイ素原子と共役ジエン系重合体鎖の活性末端との間に新たな結合を形成し、共役ジエン系重合体鎖の末端に、シロキサン構造が導入されるとともに、シロキサン構造中の酸素原子と、共役ジエン系重合体鎖の活性末端を形成していた金属原子との間で、−Ｏ−Ｍ＋（Ｍは、アルカリ金属原子、アルカリ土類金属原子、または、ランタン系列金属原子）で表される活性末端が形成されることとなる。なお、本発明の製造方法の第２工程により得られる、反応後の共役ジエン系重合体鎖は、重合体鎖末端に、シロキサンによる変性構造が導入されたものを含むものであるが、これ以外にも、シロキサンによる変性がされていない未変性の共役ジエン系重合体鎖を含むものであってもよい。 According to the second step of the production method of the present invention, by reacting siloxane as a modifier with the active end of the conjugated diene polymer chain having the active end obtained in the first step, at least, Some conjugated diene polymer chains form a new bond between the silicon atom in the siloxane structure and the active end of the conjugated diene polymer chain, and the siloxane structure is at the end of the conjugated diene polymer chain. Between the oxygen atom in the siloxane structure and the metal atom forming the active terminal of the conjugated diene polymer chain, -O - M + (M is an alkali metal atom, alkaline earth An active terminal represented by a similar metal atom or a lanthanum series metal atom) is formed. In addition, the conjugated diene polymer chain after the reaction obtained by the second step of the production method of the present invention includes those in which a modified structure by siloxane is introduced at the end of the polymer chain. Further, it may contain an unmodified conjugated diene polymer chain that is not modified with siloxane.
＜第３工程＞
本発明の製造方法の第３工程は、第２工程で得られるシロキサンを反応させた共役ジエン系重合体鎖に、下記一般式（１）で表される化合物を反応させる工程である。
The third step of the production method of the present invention is a step of reacting a compound represented by the following general formula (1) with the conjugated diene polymer chain obtained by reacting the siloxane obtained in the second step.
なお、本発明の製造方法の第３工程において用いる、シロキサンを反応させた共役ジエン系重合体鎖とは、上述した第２工程を経たものであればよく、そのため、このようなシロキサンを反応させた共役ジエン系重合体鎖には、シロキサンによる変性構造が導入された活性末端を有する共役ジエン系重合体鎖を含んでいればよく、シロキサンによる変性がされていない未変性の活性末端を有する共役ジエン系重合体鎖をも含み得るものである。さらには、シロキサンによる変性構造が導入された活性末端を有する共役ジエン系重合体鎖の活性末端が加水分解され、活性末端が水酸基に変換された、シロキサンによる変性構造が導入された共役ジエン系重合体鎖をも含み得るものである。以下、第３工程の説明において、シロキサンを反応させた共役ジエン系重合体鎖を、適宜、「共役ジエン系重合体鎖」と略記する。 In addition, the conjugated diene polymer chain reacted with siloxane used in the third step of the production method of the present invention is not limited as long as it has undergone the above-mentioned second step. It is sufficient that the conjugated diene polymer chain contains a conjugated diene polymer chain having an active end having a modified structure introduced with siloxane, and a conjugate having an unmodified active end not modified with siloxane. A diene polymer chain may also be included. Furthermore, the active end of the conjugated diene polymer chain having an active end introduced with a modified structure by siloxane is hydrolyzed, and the active end is converted to a hydroxyl group. It can also contain coalesced chains. Hereinafter, in the description of the third step, a conjugated diene polymer chain reacted with siloxane is abbreviated as a “conjugated diene polymer chain” as appropriate.
一般式（１）において、Ｘ１はヒドロカルビルオキシ基、ハロゲン基および水酸基から選択される官能基を表す。Ｘ１となりうるヒドロカルビルオキシ基としては、特に限定されないが、メトキシ基、エトキシ基、ｎ−プロポキシ基、イソプロポキシ基、ｎ−ブトキシ基、イソブトキシ基、ｓｅｃ−ブトキシ基、ｔｅｒｔ−ブトキシ基などのアルコキシ基；ビニルオキシ基、アリルオキシ基などのアルケニルオキシ基；フェノキシ基、ナフトキシ基などのアリーロキシ基；ベンジルオキシ基などのアラルキルオキシ基；などが挙げられる。これらのなかでも、アルコキシ基およびアリーロキシ基が好ましく、アルコキシ基がより好ましく、メトキシ基およびエトキシ基が特に好ましい。また、Ｘ１となりうるハロゲン基としては、特に限定されないが、フルオロ基、クロロ基、ブロモ基、ヨード基が挙げられ、これらのなかでも、クロロ基が好ましい。また、Ｘ１は水酸基であってもよく、この水酸基は、ヒドロカルビルオキシ基やハロゲン基であったものが加水分解されて水酸基となったものであってもよい。 In the general formula (1), X 1 represents a functional group selected from a hydrocarbyloxy group, a halogen group and a hydroxyl group. Hydrocarbyloxy group that can be X 1 is not particularly limited, but alkoxy such as methoxy group, ethoxy group, n-propoxy group, isopropoxy group, n-butoxy group, isobutoxy group, sec-butoxy group, and tert-butoxy group. Groups; alkenyloxy groups such as vinyloxy groups and allyloxy groups; aryloxy groups such as phenoxy groups and naphthoxy groups; aralkyloxy groups such as benzyloxy groups; and the like. Among these, an alkoxy group and an aryloxy group are preferable, an alkoxy group is more preferable, and a methoxy group and an ethoxy group are particularly preferable. In addition, the halogen group that can be X 1 is not particularly limited, and examples thereof include a fluoro group, a chloro group, a bromo group, and an iodo group, and among these, a chloro group is preferable. X 1 may be a hydroxyl group, and the hydroxyl group may be a hydrocarbyloxy group or a halogen group that has been hydrolyzed to form a hydroxyl group.
一般式（１）において、ｒ（すなわち、一般式（１）においてＸ１で表される基の数）は、０〜２の整数であり、ｒが２であることが好ましい。一般式（１）におけるｒが２である場合において、一般式（１）で表される化合物１分子中に２個含まれるＸ１で表される基は、同一のものであってもよいし、互いに異なるものであってもよい。 In the general formula (1), r (that is, the number of groups represented by X 1 in the general formula (1)) is an integer of 0 to 2, and r is preferably 2. When r in the general formula (1) is 2, the two groups represented by X 1 contained in one molecule of the compound represented by the general formula (1) may be the same. May be different from each other.
一般式（１）において、Ｒ１は置換基を有していてもよい炭化水素基を表す。Ｒ１となりうる炭化水素基としては、特に限定されないが、メチル基、エチル基、ｎ−プロピル基、イソプロピル基、ｎ−ブチル基、イソブチル基、ｓｅｃ−ブチル基、ｔｅｒｔ−ブチル基などのアルキル基；ビニル基、アリル基などのアルケニル基；エチニル基、プロピニル基などのアルキニル基；フェニル基、ナフチル基などのアリール基；ベンジル基などのアラルキル基；などが挙げられる。これらのなかでも、アルキル基およびアリール基が好ましく、アルキル基がより好ましく、メチル基およびエチル基が特に好ましい。また、Ｒ１で表される炭化水素基は、炭化水素基以外の置換基を有していてもよく、その置換基としては、特に限定されないが、カルボキシル基、酸無水物基、ヒドロカルビルカルボニル基、アルコキシカルボニル基、アシルオキシ基などのカルボニル基含有基や、エポキシ基、オキシ基、シアノ基、アミノ基、ハロゲン基などを挙げることができる。なお、一般式（１）におけるｒが０である場合において、一般式（１）で表される化合物１分子中に２個含まれる、Ｒ１で表される基は、同一のものであってもよいし、互いに異なるものであってもよい。 In the general formula (1), R 1 represents may be substituted hydrocarbon group. The hydrocarbon group that can be R 1 is not particularly limited, but is an alkyl group such as a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a sec-butyl group, or a tert-butyl group. Alkenyl groups such as vinyl group and allyl group; alkynyl groups such as ethynyl group and propynyl group; aryl groups such as phenyl group and naphthyl group; aralkyl groups such as benzyl group; Among these, an alkyl group and an aryl group are preferable, an alkyl group is more preferable, and a methyl group and an ethyl group are particularly preferable. Further, the hydrocarbon group represented by R 1 may have a substituent other than the hydrocarbon group, and the substituent is not particularly limited, but is a carboxyl group, an acid anhydride group, a hydrocarbylcarbonyl group. Carbonyl group-containing groups such as alkoxycarbonyl group and acyloxy group, epoxy group, oxy group, cyano group, amino group, halogen group and the like. When r in the general formula (1) is 0, two groups represented by R 1 contained in one molecule of the compound represented by the general formula (1) are the same. Or they may be different from each other.
一般式（１）において、Ｒ２およびＲ３は、それぞれ独立して、置換基を有していてもよい炭化水素基を表し、Ｒ２およびＲ３は互いに結合して環構造を形成して、これらが結合する窒素原子とともに環構造を形成していてもよい。また、これらが環構造を形成する場合には、これらが結合する窒素原子に加えて、これらが結合する窒素原子以外のヘテロ原子とともに環構造を形成していてもよい。Ｒ２およびＲ３が互いに結合しない場合に、Ｒ２およびＲ３となりうる炭化水素基としては、特に限定されないが、メチル基、エチル基、ｎ−プロピル基、イソプロピル基、ｎ−ブチル基、イソブチル基、ｓｅｃ−ブチル基、ｔｅｒｔ−ブチル基などのアルキル基；ビニル基、アリル基などのアルケニル基；エチニル基、プロピニル基などのアルキニル基；フェニル基、ナフチル基などのアリール基；ベンジル基などのアラルキル基；などが挙げられる。これらのなかでも、アルキル基およびアリール基が好ましく、アルキル基がより好ましく、メチル基およびエチル基が特に好ましい。また、Ｒ２およびＲ３が互いに結合して、これらが結合する窒素原子とともに環構造を形成する場合に、Ｒ２およびＲ３が結合してなる２価の炭化水素基としては、特に限定されないが、ｎ−ブチレン基（一般式（１）において、これらが結合する窒素原子とともに１−ピロリジン基を形成する場合）、ｎ−ペンチレン基（１−ピペリジン基を形成する場合）などのアルキレン基や、ブタジエニレン基（１−ピロール基を形成する場合）などが挙げられる。
なお、Ｒ２およびＲ３が互いに結合して、これらが結合する窒素原子とともに環構造を形成する場合、環構造としては、４〜８員環構造が好ましい。
In the general formula (1), R 2 and R 3 each independently represent a hydrocarbon group which may have a substituent, and R 2 and R 3 are bonded to each other to form a ring structure. , And may form a ring structure together with the nitrogen atom to which they are bonded. When these form a ring structure, in addition to the nitrogen atom to which they are bonded, the ring structure may be formed with a heteroatom other than the nitrogen atom to which they are bonded. When R 2 and R 3 are not bonded to each other, as the hydrocarbon group that can serve as R 2 and R 3, but are not limited to, methyl group, ethyl group, n- propyl group, an isopropyl group, n- butyl group, isobutyl Group, sec-butyl group, alkyl group such as tert-butyl group; alkenyl group such as vinyl group, allyl group; alkynyl group such as ethynyl group, propynyl group; aryl group such as phenyl group, naphthyl group; An aralkyl group; and the like. Among these, an alkyl group and an aryl group are preferable, an alkyl group is more preferable, and a methyl group and an ethyl group are particularly preferable. In addition, when R 2 and R 3 are bonded to each other to form a ring structure together with the nitrogen atom to which they are bonded, the divalent hydrocarbon group formed by bonding R 2 and R 3 is not particularly limited. An alkylene group such as an n-butylene group (when forming a 1-pyrrolidine group together with a nitrogen atom to which they are bonded in the general formula (1)), an n-pentylene group (when forming a 1-piperidine group), And a butadienylene group (when a 1-pyrrole group is formed).
Incidentally, bonded R 2 and R 3 together, when they form a ring structure together with the nitrogen atom to which they are attached, a ring structure, 4-8 membered ring structure are preferred.
また、Ｒ２およびＲ３で表される炭化水素基は、環構造形成の有無に関わらず、炭化水素基以外の置換基を有していてもよく、その置換基としては、特に限定されないが、カルボキシル基、酸無水物基、ヒドロカルビルカルボニル基、アルコキシカルボニル基、アシルオキシ基などのカルボニル基含有基や、エポキシ基、オキシ基、シアノ基、アミノ基、ハロゲン基などを挙げることができる。さらに、Ｒ２およびＲ３は互いに結合して、これらが結合する窒素原子とともに環構造を形成する場合には、その環構造を形成する原子として、炭素原子およびこれらが結合する窒素原子以外のヘテロ原子が含まれていてもよく、そのようなヘテロ原子の例として、窒素原子や酸素原子を挙げることができる。 Further, the hydrocarbon group represented by R 2 and R 3 may have a substituent other than the hydrocarbon group regardless of whether or not a ring structure is formed, and the substituent is not particularly limited. , Carboxyl groups, acid anhydride groups, hydrocarbylcarbonyl groups, alkoxycarbonyl groups, acyloxy groups and other carbonyl group-containing groups, epoxy groups, oxy groups, cyano groups, amino groups, halogen groups, and the like. Further, when R 2 and R 3 are bonded to each other to form a ring structure together with the nitrogen atom to which they are bonded, the atoms forming the ring structure are hetero atoms other than the carbon atom and the nitrogen atom to which they are bonded. An atom may be contained, and examples of such a hetero atom include a nitrogen atom and an oxygen atom.
一般式（１）で表される化合物として、特に好ましいものとして、Ｒ２およびＲ３で表される炭化水素基が互いに結合して、これらが結合する窒素原子とともに、ピペラジン環構造を形成しているものが挙げられる。より具体的には、下記一般式（８）で表される化合物が特に好ましい。一般式（１）で表される化合物として、このような構造を有するものを用いることにより、得られるゴム架橋物を特に低発熱性およびウエットグリップ性に優れたものとすることができる。
一般式（８）におけるＲ１７は、炭化水素基を表す。Ｒ１７となりうる炭化水素基としては、特に限定されないが、メチル基、エチル基、ｎ−プロピル基、イソプロピル基、ｎ−ブチル基、イソブチル基、ｓｅｃ−ブチル基、ｔｅｒｔ−ブチル基などのアルキル基；ビニル基、アリル基などのアルケニル基；エチニル基、プロピニル基などのアルキニル基；フェニル基、ナフチル基などのアリール基；ベンジル基などのアラルキル基；などが挙げられる。これらのなかでも、アルキル基およびアリール基が好ましく、アルキル基がより好ましく、メチル基が特に好ましい。 R 17 in the general formula (8) represents a hydrocarbon group. The hydrocarbon group that can be R 17 is not particularly limited, but is an alkyl group such as a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a sec-butyl group, or a tert-butyl group. Alkenyl groups such as vinyl group and allyl group; alkynyl groups such as ethynyl group and propynyl group; aryl groups such as phenyl group and naphthyl group; aralkyl groups such as benzyl group; Among these, an alkyl group and an aryl group are preferable, an alkyl group is more preferable, and a methyl group is particularly preferable.
一般式（１）で表される化合物の具体例としては、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン、２，２−ジエトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン、２，２−ジメトキシ−８−（Ｎ，Ｎ−ジエチル）メチル−１，６−ジオキサ−２−シラシクロオクタン、２−メトキシ−２−メチル−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタンなどが挙げられる。これら一般式（１）で表される化合物は、１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。 Specific examples of the compound represented by the general formula (1) include 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane, 2,2- Diethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane, 2,2-dimethoxy-8- (N, N-diethyl) methyl-1,6-dioxa-2 -Silacyclooctane, 2-methoxy-2-methyl-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane and the like. These compounds represented by the general formula (1) may be used singly or in combination of two or more.
一般式（１）で表される化合物の使用量は、特に限定されないが、共役ジエン系重合体鎖の活性末端１モルに対する一般式（１）で表される化合物の量として、０．１〜１０．０モルであることが好ましく、０．２〜５．０モルであることがより好ましく、０．３〜２．０モルであることが特に好ましい。このような量で、一般式（１）で表される化合物を用いることにより、得られる共役ジエン系ゴムが、特に低発熱性およびウエットグリップ性に優れたゴム架橋物を与えるものとなる。 Although the usage-amount of the compound represented by General formula (1) is not specifically limited, As a quantity of the compound represented by General formula (1) with respect to 1 mol of active terminals of a conjugated diene type polymer chain, 0.1-0.1 It is preferably 10.0 moles, more preferably 0.2 to 5.0 moles, and particularly preferably 0.3 to 2.0 moles. By using the compound represented by the general formula (1) in such an amount, the resulting conjugated diene rubber gives a rubber cross-linked product particularly excellent in low heat buildup and wet grip properties.
なお、通常、一般式（１）で表される化合物は、共役ジエン系重合体鎖と反応する場合には、次のようにして反応が進行すると考えられる。すなわち、まず、一般式（１）で表される化合物が、活性末端を有する共役ジエン系重合体鎖の活性末端と反応する場合の第１の反応形態を例示すると、１段階目の反応として、一般式（１）で表される化合物中の８員環構造における酸素−ケイ素結合が開裂して、そのケイ素原子が共役ジエン系重合体鎖の活性末端との間に新たに結合を形成し、酸素原子は活性末端の対イオンと塩構造（なお、この塩構造は、重合反応停止時に重合反応停止剤などに由来するプロトンと反応して水酸基を生じるものである）を形成する。さらに、一般式（１）で表される化合物が、ヒドロカルビルオキシ基を有する場合（一般式（１）におけるｒが１または２である場合）には、そのヒドロカルビルオキシ基と共役ジエン系重合体鎖の活性末端が反応して、ヒドロカルビルオキシ基が結合していたケイ素原子から脱離し、さらに、そのケイ素原子と共役ジエン系重合体鎖の活性末端との間に新たに結合が生じる。 In general, when the compound represented by the general formula (1) reacts with the conjugated diene polymer chain, the reaction is considered to proceed as follows. That is, first, when the compound represented by the general formula (1) is reacted with the active end of the conjugated diene polymer chain having an active end, the first reaction is as follows: The oxygen-silicon bond in the 8-membered ring structure in the compound represented by the general formula (1) is cleaved, and the silicon atom forms a new bond with the active end of the conjugated diene polymer chain, The oxygen atom forms a salt structure with a counter ion at the active terminal (note that this salt structure reacts with a proton derived from a polymerization reaction terminator to generate a hydroxyl group when the polymerization reaction is stopped). Further, when the compound represented by the general formula (1) has a hydrocarbyloxy group (when r in the general formula (1) is 1 or 2), the hydrocarbyloxy group and the conjugated diene polymer chain As a result, the active end of each of them reacts to desorb from the silicon atom to which the hydrocarbyloxy group was bonded, and a new bond is formed between the silicon atom and the active end of the conjugated diene polymer chain.
あるいは、第２の反応形態として、１段階目の反応において、一般式（１）で表される化合物中の８員環構造における酸素−ケイ素結合が開裂することなく、ケイ素原子に結合している、Ｘ１が脱離することで、そのケイ素原子が共役ジエン系重合体鎖の活性末端との間に新たに結合を形成する。さらに、一般式（１）で表される化合物が、ヒドロカルビルオキシ基を有する場合（一般式（１）におけるｒが２である場合）には、そのヒドロカルビルオキシ基と共役ジエン系重合体鎖の活性末端が反応して、ヒドロカルビルオキシ基が結合していたケイ素原子から脱離し、さらに、そのケイ素原子と共役ジエン系重合体鎖の活性末端との間に新たに結合が生じる。 Alternatively, as the second reaction form, in the first-stage reaction, the oxygen-silicon bond in the 8-membered ring structure in the compound represented by the general formula (1) is bonded to the silicon atom without cleavage. , X 1 is eliminated, and the silicon atom newly forms a bond with the active end of the conjugated diene polymer chain. Furthermore, when the compound represented by the general formula (1) has a hydrocarbyloxy group (when r in the general formula (1) is 2), the activity of the hydrocarbyloxy group and the conjugated diene polymer chain The terminal is reacted to desorb from the silicon atom to which the hydrocarbyloxy group was bonded, and a new bond is formed between the silicon atom and the active terminal of the conjugated diene polymer chain.
また、一般式（１）で表される化合物が、活性末端が水酸基に変換された、シロキサンによる変性構造が導入された共役ジエン系重合体鎖と反応する場合の反応形態を例示すると、一般式（１）におけるＸ１とシロキサンによる変性構造が導入された共役ジエン重合体鎖の水酸基とが反応して、Ｘ１と水酸基の水素原子とがそれぞれ脱離することで、共役ジエン系重合体鎖と一般式（１）で表される化合物との間に新たに結合が生じる。 Further, when the compound represented by the general formula (1) reacts with a conjugated diene polymer chain in which a modified structure by siloxane having an active terminal converted to a hydroxyl group is introduced, the general formula X 1 in (1) reacts with the hydroxyl group of the conjugated diene polymer chain in which the modified structure by siloxane is introduced, and X 1 and the hydrogen atom of the hydroxyl group are eliminated respectively, thereby conjugated diene polymer chain. And a new bond is formed between the compound represented by formula (1).
一般式（１）で表される化合物と共役ジエン系重合体鎖とを反応させる方法は、特に限定されないが、これらを、それぞれが溶解可能な溶媒中で、混合する方法などが挙げられる。この際に用いる溶媒としては、上述した第１工程および第２工程において用いる不活性溶媒として例示したものなどを用いることができる。また、この際においては、上述した第２工程において、活性末端を有する共役ジエン系重合体鎖に、シロキサンを反応させるために用いた反応溶液に、一般式（１）で表される化合物を添加する方法が簡便であり好ましい。また、この際においては、一般式（１）で表される化合物は、不活性溶媒に溶解して重合系内に添加してもよい。反応温度は、特に限定されないが、通常０〜１２０℃であり、反応時間も特に限定されないが、通常１分〜１時間である。 A method of reacting the compound represented by the general formula (1) with the conjugated diene polymer chain is not particularly limited, and examples thereof include a method of mixing them in a solvent in which each of them can be dissolved. As the solvent used in this case, those exemplified as the inert solvent used in the first step and the second step described above can be used. In this case, the compound represented by the general formula (1) is added to the reaction solution used for reacting the siloxane with the conjugated diene polymer chain having an active end in the second step described above. This method is preferable because it is simple. In this case, the compound represented by the general formula (1) may be dissolved in an inert solvent and added to the polymerization system. Although reaction temperature is not specifically limited, Usually, it is 0-120 degreeC, Reaction time is also not specifically limited, Usually, it is 1 minute-1 hour.
共役ジエン系重合体鎖を含有する溶液に、一般式（１）で表される化合物を添加する時期は、上述した第２工程においてシロキサンを添加した後であれば、特に限定されないが、上述した第２工程と同様に、重合反応が完結しておらず、共役ジエン系重合体鎖を含有する溶液が単量体をも含有している状態、より具体的には、共役ジエン系重合体鎖を含有する溶液が、１００ｐｐｍ以上、より好ましくは３００〜５０，０００ｐｐｍの単量体を含有している状態で、この溶液に一般式（１）で表される化合物を添加することが望ましい。一般式（１）で表される化合物の添加をこのように行なうことにより、共役ジエン系重合体鎖と重合系中に含まれる不純物などとの副反応を抑制して、反応を良好に制御することが可能となる。 The time when the compound represented by the general formula (1) is added to the solution containing the conjugated diene polymer chain is not particularly limited as long as it is after the siloxane is added in the second step described above. As in the second step, the polymerization reaction is not completed and the solution containing the conjugated diene polymer chain also contains the monomer, more specifically, the conjugated diene polymer chain. It is desirable to add the compound represented by the general formula (1) to this solution in a state in which the solution containing contains a monomer of 100 ppm or more, more preferably 300 to 50,000 ppm. By adding the compound represented by the general formula (1) in this way, side reactions between the conjugated diene polymer chain and impurities contained in the polymerization system are suppressed, and the reaction is controlled well. It becomes possible.
なお、本発明の製造方法の第２工程および第３工程において、活性末端を有する共役ジエン系重合体鎖に、シロキサンおよび一般式（１）で表される化合物を反応させる前の状態のとき、シロキサンのみを反応させた後であって、一般式（１）で表される化合物を反応させる前の状態のとき、あるいは、シロキサンおよび一般式（１）で表される化合物のいずれも反応させた後において、活性末端を有する共役ジエン系重合体鎖が残存している状態のときに、本発明の効果を阻害しない範囲で、活性末端を有する共役ジエン系重合体鎖の活性末端の一部を、従来から通常使用されているカップリング剤や変性剤などを重合系内に添加して、カップリングや変性を行ってもよい。 In the second step and the third step of the production method of the present invention, when the conjugated diene polymer chain having an active end is in a state before reacting the siloxane and the compound represented by the general formula (1), After reacting only the siloxane and before reacting the compound represented by the general formula (1), or both the siloxane and the compound represented by the general formula (1) were reacted. Later, when the conjugated diene polymer chain having an active terminus remains, a part of the active terminus of the conjugated diene polymer chain having an active terminus may be used as long as the effect of the present invention is not impaired. The coupling or modification may be carried out by adding a coupling agent or a modifier that has been conventionally used in the polymerization system.
そして、第３工程において、共役ジエン系重合体鎖に、一般式（１）で表される化合物を反応させた後は、メタノールおよびイソプロパノールなどのアルコールまたは水などの、重合停止剤を添加して未反応の活性末端を失活させることが好ましい。 In the third step, after the compound represented by the general formula (1) is reacted with the conjugated diene polymer chain, a polymerization terminator such as alcohol or water such as methanol and isopropanol is added. It is preferable to deactivate the unreacted active terminal.
共役ジエン系重合体鎖の活性末端を失活させた後、所望により、フェノール系安定剤、リン系安定剤、イオウ系安定剤などの老化防止剤、クラム化剤、およびスケール防止剤などを反応溶液に添加し、その後、直接乾燥またはスチームストリッピングなどにより反応溶液から重合溶媒を分離して、共役ジエン系ゴムを回収する。なお、反応溶液から重合溶媒を分離する前に、重合溶液に伸展油を混合し、共役ジエン系ゴムを油展ゴムとして回収してもよい。 After deactivating the active end of the conjugated diene polymer chain, react with anti-aging agents such as phenol-based stabilizers, phosphorus-based stabilizers, sulfur-based stabilizers, crumbs, and scale inhibitors as desired. After adding to the solution, the polymerization solvent is separated from the reaction solution by direct drying or steam stripping, and the conjugated diene rubber is recovered. Before separating the polymerization solvent from the reaction solution, an extending oil may be mixed into the polymerization solution and the conjugated diene rubber may be recovered as an oil-extended rubber.
共役ジエン系ゴムを油展ゴムとして回収する場合に用いる伸展油としては、たとえば、パラフィン系、芳香族系およびナフテン系の石油系軟化剤、植物系軟化剤、ならびに脂肪酸などが挙げられる。石油系軟化剤を用いる場合には、ＩＰ３４６の方法（英国のＴＨＥ ＩＮＳＴＩＴＵＴＥ ＰＥＴＲＯＬＥＵＭの検査方法）により抽出される多環芳香族の含有量が３％未満であることが好ましい。伸展油を使用する場合、その使用量は、共役ジエン系ゴム１００重量部に対して、好ましくは５〜１００重量部、より好ましくは１０〜６０重量部、さらに好ましくは２０〜５０重量部である。 Examples of the extending oil used when recovering the conjugated diene rubber as an oil-extended rubber include paraffinic, aromatic and naphthenic petroleum softeners, plant softeners, and fatty acids. When using a petroleum softener, it is preferable that the content of polycyclic aromatics extracted by the method of IP346 (the inspection method of THE INSTITUTE PETROLEUM in the UK) is less than 3%. When using the extender oil, the amount used is preferably 5 to 100 parts by weight, more preferably 10 to 60 parts by weight, and still more preferably 20 to 50 parts by weight with respect to 100 parts by weight of the conjugated diene rubber. .
このようにして本発明の製造方法により得られる共役ジエン系ゴムは、上述した第２工程において、変性剤として、シロキサンを用いて反応を行い、次いで、上述した第３工程において、変性剤として、一般式（１）で表される化合物を用いて反応を行うことにより、得られるものである。そのため、本発明の製造方法により得られる共役ジエン系ゴムは、重合体鎖末端に、シロキサンによる変性構造および一般式（１）で表される化合物による変性構造が導入されたものを含むものであるが、このようなもの以外にも、重合体鎖末端に、シロキサンによる変性構造のみが導入されたものや、重合体鎖末端に、一般式（１）で表される化合物による変性構造のみが導入されたもの、さらには、いずれの変性構造も導入されていないものなどを含有するものであってもよい。特に、本発明においては、得られるゴム架橋物の低発熱性およびウエットグリップ性をより高めるという観点より、共役ジエン系ゴムを構成する、全重合体中における、シロキサンによる変性構造および一般式（１）で表される化合物による変性構造が導入されたものと、一般式（１）で表される化合物による変性構造のみが導入されたものとの合計の含有割合（すなわち、少なくとも、一般式（１）で表される化合物による変性構造が導入されたものの含有割合）が、１０重量％以上であるものが好ましく、２０重量％以上であるものがより好ましい。なお、上限は、特に限定されない。 Thus, the conjugated diene rubber obtained by the production method of the present invention reacts with siloxane as a modifier in the second step described above, and then as a modifier in the third step described above. It is obtained by carrying out the reaction using the compound represented by the general formula (1). Therefore, the conjugated diene rubber obtained by the production method of the present invention includes those in which a modified structure by siloxane and a modified structure by a compound represented by the general formula (1) are introduced at the polymer chain end. In addition to these, only a modified structure by siloxane was introduced at the polymer chain end, or only a modified structure by the compound represented by the general formula (1) was introduced at the polymer chain end. Further, those containing no modified structure may be included. In particular, in the present invention, from the viewpoint of further improving the low heat build-up and wet grip properties of the resulting rubber cross-linked product, the modified structure by siloxane and the general formula (1) in the entire polymer constituting the conjugated diene rubber. ) In which the modified structure by the compound represented by the formula (1) and the modified structure by the compound represented by the general formula (1) only are introduced (that is, at least the general formula (1) ) Is preferably 10% by weight or more, and more preferably 20% by weight or more. The upper limit is not particularly limited.
本発明の製造方法により得られる共役ジエン系ゴムに含まれる共役ジエン単量体単位部分におけるビニル結合含有量は、５０重量％以下であり、好ましくは４５重量％以下、より好ましくは４２重量％以下である。また、ビニル結合含有量の下限は、特に限定されないが、好ましくは５重量％以上である。ビニル結合含有量を上記範囲とすることにより、得られるゴム架橋物を、低発熱性が特に改善されたものとすることができる。ビニル結合含有量の調節方法としては、特に限定されないが、たとえば、上述した第１工程における重合時において、所定量の極性化合物の存在下で重合を行う方法が挙げられる。ただし、このような方法に特に限定されるものではなく、たとえば、重合反応温度を調節する方法、極性化合物の種類を変える方法、重合開始剤の種類を変える方法によりビニル結合含有量を調節するような態様とすることもできる。なお、ビニル結合含有量は、１Ｈ−ＮＭＲ測定により、共役ジエン系ゴム中の共役ジエン単量体単位の含有量、および、ビニル結合の含有量を測定することにより求めることできる。 The vinyl bond content in the conjugated diene monomer unit portion contained in the conjugated diene rubber obtained by the production method of the present invention is 50% by weight or less, preferably 45% by weight or less, more preferably 42% by weight or less. It is. The lower limit of the vinyl bond content is not particularly limited, but is preferably 5% by weight or more. By setting the vinyl bond content in the above range, the obtained rubber cross-linked product can have a particularly improved low exothermic property. The method for adjusting the vinyl bond content is not particularly limited, and examples thereof include a method of performing polymerization in the presence of a predetermined amount of a polar compound during the polymerization in the first step described above. However, it is not particularly limited to such a method. For example, the vinyl bond content may be adjusted by adjusting the polymerization reaction temperature, changing the type of polar compound, or changing the type of polymerization initiator. It can also be set as this aspect. The vinyl bond content can be determined by measuring the content of the conjugated diene monomer unit in the conjugated diene rubber and the vinyl bond content by 1 H-NMR measurement.
また、本発明の製造方法により得られる共役ジエン系ゴムのカップリング率は、特に限定されないが、好ましくは１０重量％以上、より好ましくは１５重量％以上、特に好ましくは２０重量％以上であり、また、好ましくは８０重量％以下、より好ましくは７５重量％以下、特に好ましくは７０重量％以下である。カップリング率が上記範囲であると、得られるゴム架橋物の機械的強度および耐摩耗性を良好にバランスさせることができる。なお、カップリング率は、シロキサンおよび一般式（１）で表される化合物、ならびに、必要に応じて用いられるカップリング剤やその他の変性剤と反応させる前の活性末端を有する共役ジエン系重合体鎖のピークトップ分子量の１．８倍以上の分子量を有する重合体分子の、最終的に得られた共役ジエン系ゴムの全量に対する重量分率であり、このときの分子量の測定は、ゲルパーミエーションクロマトグラフィによりポリスチレン換算分子量として求めるものとする。 The coupling rate of the conjugated diene rubber obtained by the production method of the present invention is not particularly limited, but is preferably 10% by weight or more, more preferably 15% by weight or more, and particularly preferably 20% by weight or more. Further, it is preferably 80% by weight or less, more preferably 75% by weight or less, and particularly preferably 70% by weight or less. When the coupling ratio is in the above range, the mechanical strength and wear resistance of the resulting rubber cross-linked product can be well balanced. The coupling rate is conjugated diene polymer having an active terminal before reacting with the siloxane and the compound represented by the general formula (1), and a coupling agent or other modifier used as necessary. This is the weight fraction of polymer molecules having a molecular weight of 1.8 times or more of the chain peak top molecular weight with respect to the total amount of the finally obtained conjugated diene rubber, and the molecular weight at this time is measured by gel permeation. It shall obtain | require as a polystyrene conversion molecular weight by chromatography.
また、本発明の製造方法により得られる共役ジエン系ゴムの重量平均分子量（Ｍｗ）は、ポリスチレン換算のゲルパーミエーションクロマトグラフィで測定される値で、好ましくは１００，０００〜３，０００，０００、より好ましくは１５０，０００〜２，０００，０００、特に好ましくは２００，０００〜１，５００，０００である。共役ジエン系ゴムの重量平均分子量を上記範囲内とすることにより、共役ジエン系ゴムへのシリカの配合が容易となり、ゴム組成物の加工性をより高めることができ、さらには、得られるゴム架橋物の低発熱性をより高めることができる。 In addition, the weight average molecular weight (Mw) of the conjugated diene rubber obtained by the production method of the present invention is a value measured by gel permeation chromatography in terms of polystyrene, preferably 100,000 to 3,000,000. Preferably it is 150,000-2,000,000, Most preferably, it is 200,000-1,500,000. By making the weight average molecular weight of the conjugated diene rubber within the above range, it is easy to add silica to the conjugated diene rubber, and the processability of the rubber composition can be further improved. The low exothermic property of a thing can be improved more.
本発明の製造方法により得られる共役ジエン系ゴムの重量平均分子量（Ｍｗ）と数平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）で表わされる分子量分布は、１．１〜３．０であることが好ましく、１．２〜２．５であることがより好ましく、１．２〜２．２であることが特に好ましい。共役ジエン系ゴムの分子量分布（Ｍｗ／Ｍｎ）を上記範囲内とすることにより、得られるゴム架橋物の低発熱性をより向上させることができる。 The molecular weight distribution represented by the ratio (Mw / Mn) of the weight average molecular weight (Mw) and the number average molecular weight (Mn) of the conjugated diene rubber obtained by the production method of the present invention is 1.1 to 3.0. It is preferably 1.2 to 2.5, more preferably 1.2 to 2.2. By setting the molecular weight distribution (Mw / Mn) of the conjugated diene rubber within the above range, the low exothermic property of the resulting rubber cross-linked product can be further improved.
また、本発明の製造方法により得られる共役ジエン系ゴムのムーニー粘度（ＭＬ１＋４，１００℃）は、好ましくは２０〜１００、より好ましくは３０〜９０、特に好ましくは３５〜８０である。なお、共役ジエン系ゴムを油展ゴムとする場合は、その油展ゴムのムーニー粘度を上記の範囲とすることが好ましい。 The Mooney viscosity (ML 1 + 4 , 100 ° C.) of the conjugated diene rubber obtained by the production method of the present invention is preferably 20 to 100, more preferably 30 to 90, and particularly preferably 35 to 80. When the conjugated diene rubber is an oil-extended rubber, the Mooney viscosity of the oil-extended rubber is preferably in the above range.
また、本発明の製造方法により得られる共役ジエン系ゴムのガラス転移温度（Ｔｇ）は、特に限定されないが、好ましくは−１０℃〜−１１０℃であり、より好ましくは−２０℃〜−７０℃である。本発明の製造方法により得られる共役ジエン系ゴムのガラス転移温度は、たとえば、共役ジエン系ゴム中の芳香族ビニル単量体単位含有量、および共役ジエン単量体単位部分におけるビニル結合含有量を調節することによって、調節することができる。 The glass transition temperature (Tg) of the conjugated diene rubber obtained by the production method of the present invention is not particularly limited, but is preferably -10 ° C to -110 ° C, more preferably -20 ° C to -70 ° C. It is. The glass transition temperature of the conjugated diene rubber obtained by the production method of the present invention is, for example, the aromatic vinyl monomer unit content in the conjugated diene rubber and the vinyl bond content in the conjugated diene monomer unit portion. It can be adjusted by adjusting.
このようにして本発明の製造方法により得られる共役ジエン系ゴムは、充填剤および架橋剤などの配合剤を添加した上で、種々の用途に好適に用いることができる。特に、充填剤としてシリカを配合した場合に、低発熱性、およびウエットグリップ性に優れたゴム架橋物を与えることができるゴム組成物を与える。 Thus, the conjugated diene rubber obtained by the production method of the present invention can be suitably used for various applications after adding compounding agents such as a filler and a crosslinking agent. In particular, when silica is blended as a filler, a rubber composition capable of giving a crosslinked rubber product having low heat build-up and excellent wet grip properties is provided.
＜ゴム組成物＞
本発明のゴム組成物は、上述した本発明の製造方法により得られる共役ジエン系ゴムを含むゴム成分１００重量部に対して、シリカ１０〜２００重量部を含有してなる組成物である。
<Rubber composition>
The rubber composition of the present invention is a composition comprising 10 to 200 parts by weight of silica with respect to 100 parts by weight of a rubber component containing the conjugated diene rubber obtained by the production method of the present invention described above.
本発明で用いるシリカとしては、たとえば、乾式法ホワイトカーボン、湿式法ホワイトカーボン、コロイダルシリカ、沈降シリカなどが挙げられる。これらの中でも、含水ケイ酸を主成分とする湿式法ホワイトカーボンが好ましい。また、カーボンブラック表面にシリカを担持させたカーボン−シリカデュアル・フェイズ・フィラーを用いてもよい。これらのシリカは、それぞれ単独で、あるいは２種以上を組み合わせて用いることができる。用いるシリカの窒素吸着比表面積（ＡＳＴＭ Ｄ３０３７−８１に準じＢＥＴ法で測定される）は、好ましくは５０〜３００ｍ２／ｇ、より好ましくは８０〜２２０ｍ２／ｇである。また、シリカのｐＨは、ｐＨ５〜１０であることが好ましい。 Examples of the silica used in the present invention include dry method white carbon, wet method white carbon, colloidal silica, and precipitated silica. Among these, wet method white carbon mainly containing hydrous silicic acid is preferable. Alternatively, a carbon-silica dual phase filler in which silica is supported on the carbon black surface may be used. These silicas can be used alone or in combination of two or more. The nitrogen adsorption specific surface area (measured by the BET method in accordance with ASTM D3037-81) of the silica used is preferably 50 to 300 m 2 / g, more preferably 80 to 220 m 2 / g. Moreover, it is preferable that the pH of a silica is pH 5-10.
本発明のゴム組成物におけるシリカの配合量は、ゴム組成物中のゴム成分１００重量部に対して、１０〜２００重量部であり、好ましくは３０〜１５０重量部、より好ましくは５０〜１００重量部である。シリカの配合量を上記範囲とすることにより、ゴム組成物の加工性が優れたものとなり、得られるゴム架橋物のウエットグリップ性および低発熱性をより向上させることができる。 The compounding quantity of the silica in the rubber composition of this invention is 10-200 weight part with respect to 100 weight part of rubber components in a rubber composition, Preferably it is 30-150 weight part, More preferably, it is 50-100 weight. Part. By setting the blending amount of silica within the above range, the processability of the rubber composition becomes excellent, and the wet grip property and low heat build-up property of the resulting rubber cross-linked product can be further improved.
本発明のゴム組成物には、低発熱性をより向上させるという観点より、さらにシランカップリング剤を配合してもよい。シランカップリング剤としては、特に限定されず、種々のシランカップリング剤を用いることができるが、本発明においては、スルフィド系、メルカプト系、保護化メルカプト系（例えば、カルボニルチオ基を持つもの）、ビニル系、アミノ系、グリシドキシ系、ニトロ系、またはクロロ系のシランカップリング剤を好適に用いることができる。例えば、ビニルトリエトキシシラン、β−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、Ｎ−（β−アミノエチル）−γ−アミノプロピルトリメトキシシラン、３−オクタノイルチオ−１−プロピル−トリエトキシシラン、ビス（３−（トリエトキシシリル）プロピル）ジスルフィド、ビス（３−（トリエトキシシリル）プロピル）テトラスルフィド、γ−トリメトキシシリルプロピルジメチルチオカルバミルテトラスルフィド、およびγ−トリメトキシシリルプロピルベンゾチアジルテトラスルフィドなどを挙げることができる。また、Ｍｏｍｅｎｔｉｖｅ社製のＮＸＴ−Ｚ４５、エポニックデグッサ社製のＶＰ Ｓｉ３６３なども用いることができる。これらのシランカップリング剤は、それぞれ単独で、あるいは２種以上を組み合わせて用いることができる。シランカップリング剤の配合量は、シリカ１００重量部に対して、好ましくは０．１〜３０重量部、より好ましくは１〜１５重量部である。 The rubber composition of the present invention may further contain a silane coupling agent from the viewpoint of further improving the low heat buildup. The silane coupling agent is not particularly limited, and various silane coupling agents can be used. In the present invention, sulfide-based, mercapto-based, and protected mercapto-based (for example, those having a carbonylthio group). Vinyl, amino, glycidoxy, nitro, or chloro silane coupling agents can be suitably used. For example, vinyltriethoxysilane, β- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, N- (β-aminoethyl) -γ-aminopropyltrimethoxysilane, 3-octanoylthio-1-propyl-triethoxysilane Bis (3- (triethoxysilyl) propyl) disulfide, bis (3- (triethoxysilyl) propyl) tetrasulfide, γ-trimethoxysilylpropyldimethylthiocarbamyl tetrasulfide, and γ-trimethoxysilylpropylbenzothia Examples thereof include zirconium tetrasulfide. Also, NXT-Z45 manufactured by Momentive, VP Si363 manufactured by Eponic Degussa, and the like can be used. These silane coupling agents can be used alone or in combination of two or more. The blending amount of the silane coupling agent is preferably 0.1 to 30 parts by weight, more preferably 1 to 15 parts by weight with respect to 100 parts by weight of silica.
また、本発明のゴム組成物には、さらに、ファーネスブラック、アセチレンブラック、サーマルブラック、チャンネルブラック、およびグラファイトなどのカーボンブラックを配合してもよい。これらのなかでも、ファーネスブラックが好ましい。これらのカーボンブラックは、それぞれ単独で、あるいは２種以上を組み合わせて用いることができる。カーボンブラックの配合量は、ゴム組成物中のゴム成分１００重量部に対して、通常、１２０重量部以下である。 The rubber composition of the present invention may further contain carbon black such as furnace black, acetylene black, thermal black, channel black, and graphite. Among these, furnace black is preferable. These carbon blacks can be used alone or in combination of two or more. The compounding amount of carbon black is usually 120 parts by weight or less with respect to 100 parts by weight of the rubber component in the rubber composition.
なお、本発明の製造方法により得られる共役ジエン系ゴムを含むゴム成分に、シリカを添加する方法としては特に限定されず、固形のゴム成分に対して添加して混練する方法（乾式混練法）や共役ジエン系ゴムを含む溶液に対して添加して凝固・乾燥させる方法（湿式混練法）などを適用することができる。 The method of adding silica to the rubber component containing the conjugated diene rubber obtained by the production method of the present invention is not particularly limited, and a method of adding and kneading the solid rubber component (dry kneading method) Alternatively, a method of adding to a solution containing a conjugated diene rubber and solidifying and drying (wet kneading method) can be applied.
また、本発明のゴム組成物は、架橋剤をさらに含有していることが好ましい。架橋剤としては、例えば、硫黄、ハロゲン化硫黄、有機過酸化物、キノンジオキシム類、有機多価アミン化合物、メチロール基を有するアルキルフェノール樹脂などが挙げられる。これらの中でも、硫黄が好ましく使用される。架橋剤の配合量は、ゴム組成物中のゴム成分１００重量部に対して、好ましくは０．１〜１５重量部、より好ましくは０．５〜５重量部、特に好ましくは１〜４重量部である。 Moreover, it is preferable that the rubber composition of the present invention further contains a crosslinking agent. Examples of the crosslinking agent include sulfur, sulfur halides, organic peroxides, quinonedioximes, organic polyvalent amine compounds, and alkylphenol resins having a methylol group. Among these, sulfur is preferably used. The amount of the crosslinking agent is preferably 0.1 to 15 parts by weight, more preferably 0.5 to 5 parts by weight, and particularly preferably 1 to 4 parts by weight with respect to 100 parts by weight of the rubber component in the rubber composition. It is.
さらに、本発明のゴム組成物には、上記成分以外に、常法に従って、架橋促進剤、架橋活性化剤、老化防止剤、充填剤（上記シリカおよびカーボンブラックを除く）、活性剤、プロセス油、可塑剤、滑剤などの配合剤をそれぞれ必要量配合できる。 Further, in addition to the above components, the rubber composition of the present invention includes a crosslinking accelerator, a crosslinking activator, an anti-aging agent, a filler (excluding silica and carbon black), an activator, and a process oil in accordance with conventional methods. The compounding agents such as plasticizers and lubricants can be blended in the required amounts.
架橋剤として、硫黄または含硫黄化合物を用いる場合には、架橋促進剤および架橋活性化剤を併用することが好ましい。架橋促進剤としては、例えば、スルフェンアミド系架橋促進剤；グアニジン系架橋促進剤；チオウレア系架橋促進剤；チアゾール系架橋促進剤；チウラム系架橋促進剤；ジチオカルバミン酸系架橋促進剤；キサントゲン酸系架橋促進剤；などが挙げられる。これらのなかでも、スルフェンアミド系架橋促進剤を含むものが好ましい。これらの架橋促進剤は、それぞれ単独で、あるいは２種以上を組み合わせて用いられる。架橋促進剤の配合量は、ゴム組成物中のゴム成分１００重量部に対して、好ましくは０．１〜１５重量部、より好ましくは０．５〜５重量部、特に好ましくは１〜４重量部である。 When sulfur or a sulfur-containing compound is used as the crosslinking agent, it is preferable to use a crosslinking accelerator and a crosslinking activator in combination. Examples of the crosslinking accelerator include sulfenamide-based crosslinking accelerators; guanidine-based crosslinking accelerators; thiourea-based crosslinking accelerators; thiazole-based crosslinking accelerators; thiuram-based crosslinking accelerators; dithiocarbamic acid-based crosslinking accelerators; A crosslinking accelerator; and the like. Among these, those containing a sulfenamide-based crosslinking accelerator are preferable. These crosslinking accelerators are used alone or in combination of two or more. The blending amount of the crosslinking accelerator is preferably 0.1 to 15 parts by weight, more preferably 0.5 to 5 parts by weight, and particularly preferably 1 to 4 parts by weight with respect to 100 parts by weight of the rubber component in the rubber composition. Part.
架橋活性化剤としては、例えば、ステアリン酸などの高級脂肪酸；酸化亜鉛；などを挙げることができる。これらの架橋活性化剤は、それぞれ単独で、あるいは２種以上を組み合わせて用いられる。架橋活性化剤の配合量は、ゴム組成物中のゴム成分１００重量部に対して、好ましくは０．０５〜２０重量部、特に好ましくは０．５〜１５重量部である。 Examples of the crosslinking activator include higher fatty acids such as stearic acid; zinc oxide. These crosslinking activators are used alone or in combination of two or more. The amount of the crosslinking activator is preferably 0.05 to 20 parts by weight, particularly preferably 0.5 to 15 parts by weight with respect to 100 parts by weight of the rubber component in the rubber composition.
また、本発明のゴム組成物には、上述した本発明の製造方法によって得られる共役ジエン系ゴム以外のその他のゴムを配合してもよい。その他のゴムとしては、例えば、天然ゴム、ポリイソプレンゴム、乳化重合スチレン−ブタジエン共重合ゴム、溶液重合スチレン−ブタジエン共重合ゴム、ポリブタジエンゴム（高シス−ＢＲ、低シスＢＲであってもよい。また、１，２−ポリブタジエン重合体からなる結晶繊維を含むポリブタジエンゴムであってもよい）、スチレン−イソプレン共重合ゴム、ブタジエン−イソプレン共重合ゴム、スチレン−イソプレン−ブタジエン共重合ゴム、アクリロニトリル−ブタジエン共重合ゴム、アクリロニトリル−スチレン−ブタジエン共重合ゴムなどのうち、上述した本発明の製造方法によって得られる共役ジエン系ゴム以外のものをいう。これらのなかでも、天然ゴム、ポリイソプレンゴム、ポリブタジエンゴム、溶液重合スチレン−ブタジエン共重合ゴムが好ましい。これらのゴムは、それぞれ単独で、あるいは２種以上を組み合わせて用いることができる。 Moreover, you may mix | blend rubbers other than the conjugated diene type rubber | gum obtained by the manufacturing method of this invention mentioned above with the rubber composition of this invention. Examples of other rubbers include natural rubber, polyisoprene rubber, emulsion polymerization styrene-butadiene copolymer rubber, solution polymerization styrene-butadiene copolymer rubber, and polybutadiene rubber (high cis-BR and low cis BR may be used. Further, it may be a polybutadiene rubber containing crystal fibers made of 1,2-polybutadiene polymer), styrene-isoprene copolymer rubber, butadiene-isoprene copolymer rubber, styrene-isoprene-butadiene copolymer rubber, acrylonitrile-butadiene. Among copolymer rubbers, acrylonitrile-styrene-butadiene copolymer rubbers and the like, it refers to those other than the conjugated diene rubbers obtained by the production method of the present invention described above. Among these, natural rubber, polyisoprene rubber, polybutadiene rubber, and solution-polymerized styrene-butadiene copolymer rubber are preferable. These rubbers can be used alone or in combination of two or more.
本発明のゴム組成物において、本発明の製造方法により得られる共役ジエン系ゴムは、ゴム組成物中のゴム成分の１０〜１００重量％を占めることが好ましく、５０〜１００重量％を占めることが特に好ましい。このような割合で、本発明の共役ジエン系ゴムをゴム成分中に含めることにより、低発熱性とウエットグリップ性とが向上されたゴム架橋物を得ることができる。 In the rubber composition of the present invention, the conjugated diene rubber obtained by the production method of the present invention preferably accounts for 10 to 100% by weight, preferably 50 to 100% by weight of the rubber component in the rubber composition. Particularly preferred. By including the conjugated diene rubber of the present invention in the rubber component at such a ratio, it is possible to obtain a crosslinked rubber product having improved low heat build-up and wet grip properties.
また、本発明のゴム組成物には、ゴム成分以外に樹脂を配合してもよい。樹脂を配合することにより、ゴム組成物に粘着性を付与させたり、ゴム組成物中の充填剤の分散性を高めることができる。その結果、得られるゴム架橋物のウエットグリップ性や耐摩耗性の向上が期待できる。また、可塑剤と同様な効果として、ゴム組成物の加工性を向上させることもできる。樹脂としては、例えば、Ｃ５系石油樹脂、Ｃ５／Ｃ９系石油樹脂、Ｃ９系石油樹脂、ジシクロペンタジエン系樹脂、テルペン系樹脂、テルペンフェノール樹脂、芳香族変性テルペン樹脂、アルキルフェノール−アセチレン樹脂、ロジン系樹脂、ロジンエステル樹脂、インデン系樹脂、インデンを含有するＣ９系樹脂、α−メチルスチレン・インデン共重合体樹脂、クマロン−インデン樹脂、ファルネセン系樹脂、ポリリモネン樹脂などが挙げられる。これらの樹脂は、変性されていたり、水素添加されていたりするものであってもよい。これらの樹脂は、それぞれ単独で、あるいは２種以上を組み合わせて用いられる。樹脂の配合量は、ゴム組成物中のゴム成分１００重量部に対して、好ましくは２５重量部以下である。 Moreover, you may mix | blend resin with the rubber composition of this invention in addition to a rubber component. By blending the resin, it is possible to impart adhesiveness to the rubber composition or to increase the dispersibility of the filler in the rubber composition. As a result, improvement in wet grip properties and wear resistance of the obtained rubber cross-linked product can be expected. Moreover, the processability of a rubber composition can also be improved as an effect similar to a plasticizer. Examples of the resin include C5 petroleum resins, C5 / C9 petroleum resins, C9 petroleum resins, dicyclopentadiene resins, terpene resins, terpene phenol resins, aromatic modified terpene resins, alkylphenol-acetylene resins, and rosin resins. Examples thereof include resin, rosin ester resin, indene resin, C9 resin containing indene, α-methylstyrene / indene copolymer resin, coumarone-indene resin, farnesene resin, polylimonene resin and the like. These resins may be modified or hydrogenated. These resins are used alone or in combination of two or more. The compounding amount of the resin is preferably 25 parts by weight or less with respect to 100 parts by weight of the rubber component in the rubber composition.
本発明のゴム組成物を得るためには、常法に従って各成分を混練すればよく、たとえば、架橋剤や架橋促進剤などの熱に不安定な成分を除く配合剤と本発明の製造方法により得られる共役ジエン系ゴムを含むゴム成分とを混練後、その混練物に架橋剤や架橋促進剤などの熱に不安定な成分を混合して目的の組成物を得ることができる。熱に不安定な成分を除く配合剤と本発明の製造方法により得られる共役ジエン系ゴムを含むゴム成分との混練温度は、好ましくは８０〜２００℃、より好ましくは１２０〜１８０℃であり、その混練時間は、好ましくは３０秒〜３０分である。また、その混練物と熱に不安定な成分との混合は、通常１００℃以下、好ましくは８０℃以下まで冷却した後に行われる。 In order to obtain the rubber composition of the present invention, each component may be kneaded according to a conventional method. For example, by using a compounding agent excluding thermally unstable components such as a crosslinking agent and a crosslinking accelerator, and the production method of the present invention After kneading the rubber component containing the resulting conjugated diene rubber, the composition can be obtained by mixing the kneaded product with a thermally unstable component such as a crosslinking agent or a crosslinking accelerator. The kneading temperature of the compounding agent excluding the heat labile component and the rubber component containing the conjugated diene rubber obtained by the production method of the present invention is preferably 80 to 200 ° C, more preferably 120 to 180 ° C, The kneading time is preferably 30 seconds to 30 minutes. The kneaded product and the thermally unstable component are usually mixed after cooling to 100 ° C. or lower, preferably 80 ° C. or lower.
＜ゴム架橋物＞
本発明のゴム架橋物は、上述した本発明のゴム組成物を架橋してなるものである。
本発明のゴム架橋物は、本発明のゴム組成物を用い、たとえば、所望の形状に対応した成形機、たとえば、押出機、射出成形機、圧縮機、ロールなどにより成形を行い、加熱することにより架橋反応を行い、架橋物として形状を固定化することにより製造することができる。この場合においては、予め成形した後に架橋しても、成形と同時に架橋を行ってもよい。成形温度は、通常、１０〜２００℃、好ましくは２５〜１２０℃である。架橋温度は、通常、１００〜２００℃、好ましくは１３０〜１９０℃であり、架橋時間は、通常、１分〜２４時間、好ましくは２分〜１２時間、特に好ましくは３分〜６時間である。
<Rubber cross-linked product>
The rubber cross-linked product of the present invention is obtained by cross-linking the rubber composition of the present invention described above.
The rubber cross-linked product of the present invention uses the rubber composition of the present invention, for example, is molded by a molding machine corresponding to a desired shape, for example, an extruder, an injection molding machine, a compressor, a roll, and heated. Can be produced by carrying out a crosslinking reaction and fixing the shape as a crosslinked product. In this case, crosslinking may be performed after molding in advance, or crosslinking may be performed simultaneously with molding. The molding temperature is usually 10 to 200 ° C, preferably 25 to 120 ° C. The crosslinking temperature is usually 100 to 200 ° C, preferably 130 to 190 ° C, and the crosslinking time is usually 1 minute to 24 hours, preferably 2 minutes to 12 hours, particularly preferably 3 minutes to 6 hours. .
また、ゴム架橋物の形状、大きさなどによっては、表面が架橋していても内部まで十分に架橋していない場合があるので、さらに加熱して二次架橋を行ってもよい。 Further, depending on the shape and size of the rubber cross-linked product, even if the surface is cross-linked, it may not be sufficiently cross-linked to the inside. Therefore, secondary cross-linking may be performed by heating.
加熱方法としては、プレス加熱、スチーム加熱、オーブン加熱、熱風加熱などのゴムの架橋に用いられる一般的な方法を適宜選択すればよい。 As a heating method, a general method used for crosslinking of rubber such as press heating, steam heating, oven heating, and hot air heating may be appropriately selected.
このようにして得られる本発明のゴム架橋物は、上述した本発明の製造方法により得られる共役ジエン系ゴムを用いて得られるものであるため、低発熱性およびウエットグリップ性に優れるものである。そして、本発明のゴム架橋物は、このような特性を活かし、たとえば、タイヤにおいて、キャップトレッド、ベーストレッド、カーカス、サイドウォール、ビード部などのタイヤ各部位の材料；ホース、ベルト、マット、防振ゴム、その他の各種工業用品の材料；樹脂の耐衝撃性改良剤；樹脂フィルム緩衝剤；靴底；ゴム靴；ゴルフボール；玩具；などの各種用途に用いることができる。特に、本発明のゴム架橋物は、オールシーズンタイヤ、高性能タイヤ、およびスタッドレスタイヤなどの各種タイヤにおいて、トレッド、カーカス、サイドウォール、およびビード部などのタイヤ各部位に好適に用いることができ、特に低発熱性に優れるので、低燃費タイヤのトレッド用として、特に好適に用いることができる。 The rubber cross-linked product of the present invention thus obtained is obtained by using the conjugated diene rubber obtained by the production method of the present invention described above, and therefore has excellent low heat buildup and wet grip properties. . The rubber cross-linked product of the present invention makes use of such characteristics, and for example, in tires, materials for tire parts such as cap treads, base treads, carcass, sidewalls and bead parts; hoses, belts, mats, It can be used in various applications such as vibration rubber and other various industrial article materials; resin impact resistance improvers; resin film buffers; shoe soles; rubber shoes; golf balls; In particular, the rubber cross-linked product of the present invention can be suitably used in various parts of a tire such as a tread, a carcass, a sidewall, and a bead part in various tires such as an all-season tire, a high-performance tire, and a studless tire, In particular, since it is excellent in low heat generation property, it can be particularly suitably used as a tread for a fuel-efficient tire.
以下、本発明を、さらに詳細な実施例に基づき説明するが、本発明は、これら実施例に限定されない。なお、以下において、「部」は、特に断りのない限り重量基準である。また、試験および評価は下記に従った。 Hereinafter, although this invention is demonstrated based on a more detailed Example, this invention is not limited to these Examples. In the following, “part” is based on weight unless otherwise specified. Moreover, the test and evaluation followed the following.
〔重量平均分子量、分子量分布、カップリング率〕
重量平均分子量（Ｍｗ）、分子量分布（Ｍｗ／Ｍｎ）、およびカップリング率は、ゲルパーミエーションクロマトグラフィによりポリスチレン換算の分子量に基づくチャートを得て、得られたチャートに基づいて求めた。ゲルパーミエーションクロマトグラフィの具体的な測定条件は、以下のとおりとした。
測定機：高速液体クロマトグラフ（東ソー社製、商品名「ＨＬＣ−８２２０」）
カラム：東ソー社製、商品名「ＧＭＨ−ＨＲ−Ｈ」を二本直列に連結した。
検出器：示差屈折計
溶離液：テトラヒドロフラン
カラム温度：４０℃
なお、カップリング率については、上記の条件のゲルパーミエーションクロマトグラフィにより得られた溶出曲線において、全溶出面積に対する、分子量の最も小さいピークが示すピークトップ分子量の１．８倍以上のピークトップ分子量を有するピーク部分の面積比を、共役ジエン系重合体鎖のカップリング率の値とした。
[Weight average molecular weight, molecular weight distribution, coupling rate]
The weight average molecular weight (Mw), molecular weight distribution (Mw / Mn), and coupling rate were determined based on the chart obtained by obtaining a chart based on the molecular weight in terms of polystyrene by gel permeation chromatography. The specific measurement conditions for gel permeation chromatography were as follows.
Measuring instrument: High-performance liquid chromatograph (trade name “HLC-8220” manufactured by Tosoh Corporation)
Column: Tosoh Corporation, product name "GMH-HR-H" was connected in series.
Detector: Differential refractometer Eluent: Tetrahydrofuran Column temperature: 40 ° C
Regarding the coupling rate, in the elution curve obtained by gel permeation chromatography under the above conditions, the peak top molecular weight is 1.8 times or more the peak top molecular weight indicated by the peak with the smallest molecular weight relative to the total elution area. The area ratio of the peak portion was defined as the value of the coupling rate of the conjugated diene polymer chain.
〔芳香族ビニル単量体単位含有量、ビニル結合含有量〕
芳香族ビニル単量体単位含有量、およびビニル結合含有量は、１Ｈ−ＮＭＲにより測定した。
[Aromatic vinyl monomer unit content, vinyl bond content]
The aromatic vinyl monomer unit content and the vinyl bond content were measured by 1 H-NMR.
〔ゴム架橋物の低発熱性〕
低発熱性については、長さ５０ｍｍ、幅１２．７ｍｍ、厚さ２ｍｍの試験片を、レオメトリックス社製ＡＲＥＳを用い、動的歪み２．５％、１０Ｈｚの条件で６０℃におけるｔａｎδを測定することにより評価した。このｔａｎδの値については、比較例１〜４の測定値をそれぞれ１００とする指数で示した。この指数が小さいものほど、低発熱性に優れる。
[Low heat build-up of rubber cross-linked product]
For low heat generation, tan δ at 60 ° C. is measured under the conditions of dynamic strain 2.5% and 10 Hz, using ARES manufactured by Rheometrics Co., Ltd., with a test piece having a length of 50 mm, a width of 12.7 mm, and a thickness of 2 mm. It was evaluated by. About the value of this tan-delta, it showed with the index | exponent which sets the measured value of Comparative Examples 1-4 to 100, respectively. The smaller this index, the better the low heat buildup.
〔ゴム架橋物のウエットグリップ性〕
ウエットグリップ性については、長さ５０ｍｍ、幅１２．７ｍｍ、厚さ２ｍｍの試験片を、レオメトリックス社製ＡＲＥＳを用い、動的歪み０．５％、１０Ｈｚの条件で０℃におけるｔａｎδの値を測定することにより評価した。このｔａｎδの値については、比較例１〜４の測定値をそれぞれ１００とする指数で示した。この指数が大きいものほど、ウエットグリップ性に優れる。
[Wet grip properties of rubber cross-linked products]
For the wet grip property, a test piece having a length of 50 mm, a width of 12.7 mm, and a thickness of 2 mm was used. Evaluation was made by measuring. About the value of this tan-delta, it showed with the index | exponent which sets the measured value of Comparative Examples 1-4 to 100, respectively. The larger this index, the better the wet grip.
〔製造例１〕
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン３．４６ｍｍｏｌ、１，３−ブタジエン４７４ｇ、およびスチレン１２６ｇを仕込んだ後、ｎ−ブチルリチウム７．６９ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．４５モルとなる量）を加え、５０℃で重合を開始した。重合を開始してから１０分経過後、１，３−ブタジエン３７６ｇ、およびスチレン２４ｇを６０分間かけて連続的に添加した。重合反応中の最高温度は７５℃であった。連続添加終了後、さらに１０分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、下記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、２．４４ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）７．６９ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム１を得た。得られた共役ジエン系ゴム１の重量平均分子量（Ｍｗ）は４５８，０００、カップリング率は５７．０％、スチレン単量体単位含有量は１５重量％、ビニル結合含有量は３０重量％であった。
[Production Example 1]
In a nitrogen atmosphere, an autoclave equipped with a stirrer was charged with 4000 g of cyclohexane, 3.46 mmol of tetramethylethylenediamine, 474 g of 1,3-butadiene, and 126 g of styrene, and then 7.69 mmol of n-butyllithium (based on 1 mol of n-butyllithium, The amount of tetramethylethylenediamine as a polar compound was 0.45 mol), and polymerization was started at 50 ° C. Ten minutes after the start of the polymerization, 376 g of 1,3-butadiene and 24 g of styrene were continuously added over 60 minutes. The maximum temperature during the polymerization reaction was 75 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 10 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, a polyorganosiloxane represented by the following formula (9) In the state of a weight percent concentration of xylene solution, 2.44 g (converted to the number of repeating units of siloxane structure (—Si—O—) in polyorganosiloxane, 1.1 times mol of n-butyllithium used) And the reaction was allowed to proceed for 30 minutes. Then, 7.69 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 1. The resulting conjugated diene rubber 1 has a weight average molecular weight (Mw) of 458,000, a coupling rate of 57.0%, a styrene monomer unit content of 15% by weight, and a vinyl bond content of 30% by weight. there were.
〔製造例２〕
窒素置換された８００ｍｌアンプル瓶に、シクロヘキサン７０．０ｇ、およびテトラメチルエチレンジアミン０．７７ｍｍｏｌを添加し、さらに、ｎ−ブチルリチウム７．６９ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．１０モルとなる量）を添加した。次いで、イソプレン２７．９ｇ、およびスチレン２．１ｇをゆっくりと添加し、温度５０℃としたアンプル瓶内で１２０分間反応させることにより、活性末端を有する重合体ブロック（Ａ）を得た。この重合体ブロック（Ａ）の重量平均分子量（Ｍｗ）は６，３００、分子量分布（Ｍｗ／Ｍｎ）は１．１０、スチレン単量体単位含有量は７．０重量％、イソプレン単量体単位含有量は９３．０重量％、およびビニル結合含有量は７．５重量％であった。
[Production Example 2]
To an 800 ml ampoule bottle substituted with nitrogen, 70.0 g of cyclohexane and 0.77 mmol of tetramethylethylenediamine were added, and 7.69 mmol of n-butyllithium (tetramethylethylenediamine as a polar compound with respect to 1 mol of n-butyllithium). In an amount of 0.10 mol). Subsequently, 27.9 g of isoprene and 2.1 g of styrene were slowly added and reacted in an ampoule bottle at a temperature of 50 ° C. for 120 minutes to obtain a polymer block (A) having an active end. The polymer block (A) has a weight average molecular weight (Mw) of 6,300, a molecular weight distribution (Mw / Mn) of 1.10, a styrene monomer unit content of 7.0% by weight, and an isoprene monomer unit. The content was 93.0% by weight, and the vinyl bond content was 7.5% by weight.
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン２．６９ｍｍｏｌ、１，３−ブタジエン４７４ｇ、およびスチレン１２６ｇを仕込んだ後、上記にて得られた活性末端を有する重合体ブロック（Ａ）を全量加え、５０℃で重合を開始した（使用したｎ−ブチルリチウム１モルに対する、反応系中に存在する極性化合物としてのテトラメチルエチレンジアミンの量は０．４５モル）。重合を開始してから１０分経過後、１，３−ブタジエン３７６ｇ、およびスチレン２４ｇを６０分間かけて連続的に添加した。重合反応中の最高温度は７５℃であった。連続添加終了後、さらに１０分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、２．４４ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）７．６９ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム２を得た。得られた共役ジエン系ゴム２の重量平均分子量（Ｍｗ）は４６１，０００、カップリング率は５８．２％、スチレン単量体単位含有量は１５重量％、ビニル結合含有量は３０重量％であった。 In an autoclave equipped with a stirrer, 4000 g of cyclohexane, 2.69 mmol of tetramethylethylenediamine, 474 g of 1,3-butadiene, and 126 g of styrene were charged in a nitrogen atmosphere, and then the polymer block (A) having active ends obtained above was obtained. Was added at a temperature of 50 ° C. (the amount of tetramethylethylenediamine as a polar compound present in the reaction system relative to 1 mol of n-butyllithium used was 0.45 mol). Ten minutes after the start of the polymerization, 376 g of 1,3-butadiene and 24 g of styrene were continuously added over 60 minutes. The maximum temperature during the polymerization reaction was 75 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 10 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) was replaced by 40 In the state of a weight percent concentration of xylene solution, 2.44 g (converted to the number of repeating units of siloxane structure (—Si—O—) in polyorganosiloxane, 1.1 times mol of n-butyllithium used) And the reaction was allowed to proceed for 30 minutes. Then, 7.69 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 2. The resulting conjugated diene rubber 2 has a weight average molecular weight (Mw) of 461,000, a coupling rate of 58.2%, a styrene monomer unit content of 15% by weight, and a vinyl bond content of 30% by weight. there were.
〔製造例３〕
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン３．４６ｍｍｏｌ、ジ−Ｎ−ヘキシルアミン６．９２ｍｍｏｌ、１，３−ブタジエン４７４ｇ、およびスチレン１２６ｇを仕込んだ後、ｎ−ブチルリチウム７．６９ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．４５モルとなる量）を加え、５０℃で重合を開始した。重合を開始してから１０分経過後、１，３−ブタジエン３７６ｇ、およびスチレン２４ｇを６０分間かけて連続的に添加した。重合反応中の最高温度は７５℃であった。連続添加終了後、さらに１０分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、２．４４ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）７．６９ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム３を得た。得られた共役ジエン系ゴム３の重量平均分子量（Ｍｗ）は４６３，０００、カップリング率は５６．５％、スチレン単量体単位含有量は１５重量％、ビニル結合含有量は３０重量％であった。
[Production Example 3]
An autoclave equipped with a stirrer was charged with 4000 g of cyclohexane, 3.46 mmol of tetramethylethylenediamine, 6.92 mmol of di-N-hexylamine, 474 g of 1,3-butadiene, and 126 g of styrene under a nitrogen atmosphere, and then 7. 69 mmol (the amount by which the amount of tetramethylethylenediamine as a polar compound was 0.45 mol with respect to 1 mol of n-butyllithium) was added, and polymerization was started at 50 ° C. Ten minutes after the start of the polymerization, 376 g of 1,3-butadiene and 24 g of styrene were continuously added over 60 minutes. The maximum temperature during the polymerization reaction was 75 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 10 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) was replaced by 40 In the state of a weight percent concentration of xylene solution, 2.44 g (converted to the number of repeating units of siloxane structure (—Si—O—) in polyorganosiloxane, 1.1 times mol of n-butyllithium used) And the reaction was allowed to proceed for 30 minutes. Then, 7.69 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 3. The obtained conjugated diene rubber 3 has a weight average molecular weight (Mw) of 463,000, a coupling rate of 56.5%, a styrene monomer unit content of 15% by weight, and a vinyl bond content of 30% by weight. there were.
〔製造例４〕
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン２．６９ｍｍｏｌ、１，３−ブタジエン４００ｇ、およびスチレン１００ｇを仕込んだ後、ｎ−ブチルリチウム５．９９ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．４５モルとなる量）を加え、５０℃で重合を開始した。重合を開始してから１０分経過後、１，３−ブタジエン４００ｇを６０分間かけて連続的に添加した。重合反応中の最高温度は７０℃であった。連続添加終了後、さらに１０分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、１．９０ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）５．９９ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム４を得た。得られた共役ジエン系ゴム４の重量平均分子量（Ｍｗ）は４８６，０００、カップリング率は５９．５％、スチレン単量体単位含有量は１０重量％、ビニル結合含有量は４０重量％であった。
[Production Example 4]
An autoclave equipped with a stirrer was charged with 4000 g of cyclohexane, 2.69 mmol of tetramethylethylenediamine, 400 g of 1,3-butadiene, and 100 g of styrene under a nitrogen atmosphere, and then 5.99 mmol of n-butyllithium (based on 1 mol of n-butyllithium, The amount of tetramethylethylenediamine as a polar compound was 0.45 mol), and polymerization was started at 50 ° C. Ten minutes after the initiation of polymerization, 400 g of 1,3-butadiene was continuously added over 60 minutes. The maximum temperature during the polymerization reaction was 70 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 10 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) was replaced by 40 1.90 g (in terms of the number of repeating units of siloxane structure (—Si—O—) in polyorganosiloxane) 1.1 times mol of n-butyllithium used in the state of xylene solution of the concentration by weight And the reaction was allowed to proceed for 30 minutes. Then, 2.99 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (a compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 4. The resulting conjugated diene rubber 4 has a weight average molecular weight (Mw) of 486,000, a coupling rate of 59.5%, a styrene monomer unit content of 10% by weight, and a vinyl bond content of 40% by weight. there were.
〔製造例５〕
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン１．００ｍｍｏｌ、１，３−ブタジエン３５０ｇ、およびスチレン２５０ｇを仕込んだ後、ｎ−ブチルリチウム６．６７ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．１５モルとなる量）を加え、５０℃で重合を開始した。重合を開始してから２０分経過後、１，３−ブタジエン４００ｇを６０分間かけて連続的に添加した。重合反応中の最高温度は８０℃であった。連続添加終了後、さらに１０分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、２．１１ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）６．６７ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム５を得た。得られた共役ジエン系ゴム５の重量平均分子量（Ｍｗ）は４５０，０００、カップリング率は５５．８％、スチレン単量体単位含有量は２５重量％、ビニル結合含有量は１２重量％であった。
[Production Example 5]
In a nitrogen atmosphere, an autoclave equipped with a stirrer was charged with 4000 g of cyclohexane, 1.00 mmol of tetramethylethylenediamine, 350 g of 1,3-butadiene, and 250 g of styrene, and then 6.67 mmol of n-butyllithium (based on 1 mol of n-butyllithium, The amount of tetramethylethylenediamine as a polar compound was 0.15 mol), and polymerization was started at 50 ° C. After 20 minutes from the start of polymerization, 400 g of 1,3-butadiene was continuously added over 60 minutes. The maximum temperature during the polymerization reaction was 80 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 10 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) was replaced by 40 In the state of xylene solution with a concentration by weight of 2.11 g (converted to the number of repeating units of siloxane structure (—Si—O—) in polyorganosiloxane, 1.1 times mol of n-butyllithium used) And the reaction was allowed to proceed for 30 minutes. Next, 6.67 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (a compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 5. The resulting conjugated diene rubber 5 has a weight average molecular weight (Mw) of 450,000, a coupling rate of 55.8%, a styrene monomer unit content of 25% by weight, and a vinyl bond content of 12% by weight. there were.
〔製造例６〕
２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン７．６９ｍｍｏｌを添加しなかったこと以外は、製造例１と同様に操作して、固形状の共役ジエン系ゴム６を得た。得られた共役ジエン系ゴム６の重量平均分子量（Ｍｗ）は４５５，０００、カップリング率は５６．５％、スチレン単量体単位含有量は１５重量％、ビニル結合含有量は３０重量％であった。
[Production Example 6]
The same operation as in Production Example 1 was conducted, except that 7.69 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane was not added. A solid conjugated diene rubber 6 was obtained. The resulting conjugated diene rubber 6 has a weight average molecular weight (Mw) of 455,000, a coupling rate of 56.5%, a styrene monomer unit content of 15% by weight, and a vinyl bond content of 30% by weight. there were.
〔製造例７〕
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン４．０５ｍｍｏｌ、１，３−ブタジエン２５２ｇ、およびスチレン３４８ｇを仕込んだ後、ｎ−ブチルリチウム４．７６ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．８５モルとなる量）を加え、５０℃で重合を開始した。重合を開始してから１５分経過後、１，３−ブタジエン３３８ｇ、およびスチレン６２ｇを６０分間かけて連続的に添加した。重合反応中の最高温度は７０℃であった。連続添加終了後、さらに１５分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、１．５１ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）４．７６ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム７を得た。得られた共役ジエン系ゴム７の重量平均分子量（Ｍｗ）は５６０，０００、カップリング率は４４．２％、スチレン単量体単位含有量は４１重量％、ビニル結合含有量は３４重量％であった。
[Production Example 7]
An autoclave equipped with a stirrer was charged with 4000 g of cyclohexane, 4.05 mmol of tetramethylethylenediamine, 252 g of 1,3-butadiene, and 348 g of styrene in a nitrogen atmosphere, and then 4.76 mmol of n-butyllithium (based on 1 mol of n-butyllithium, Polymerization was started at 50 ° C. by adding tetramethylethylenediamine as a polar compound in an amount of 0.85 mol). After 15 minutes from the start of polymerization, 338 g of 1,3-butadiene and 62 g of styrene were continuously added over 60 minutes. The maximum temperature during the polymerization reaction was 70 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 15 minutes, and after confirming that the polymerization conversion was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) In the state of a xylene solution having a concentration by weight, 1.51 g (converted to the number of repeating units of the siloxane structure (—Si—O—) in the polyorganosiloxane, 1.1 times the mol of n-butyllithium used) And the reaction was allowed to proceed for 30 minutes. Then, 2.76 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 7. The resulting conjugated diene rubber 7 has a weight average molecular weight (Mw) of 560,000, a coupling rate of 44.2%, a styrene monomer unit content of 41% by weight and a vinyl bond content of 34% by weight. there were.
〔製造例８〕
窒素置換された８００ｍｌアンプル瓶に、シクロヘキサン７４．３ｇ、およびテトラメチルエチレンジアミン０．４８ｍｍｏｌを添加し、さらに、ｎ−ブチルリチウム４．７６ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．１０モルとなる量）を添加した。次いで、イソプレン１７．３ｇ、およびスチレン１．３ｇをゆっくりと添加し、５０℃のアンプル瓶内で１２０分反応させることにより、活性末端を有する重合体ブロック（Ａ）を得た。この重合体ブロック（Ａ）の重量平均分子量（Ｍｗ）は６，５００、分子量分布（Ｍｗ／Ｍｎ）は１．１２、スチレン単量体単位含有量は７．０％、イソプレン単量体単位含有量は９３．０重量％、およびビニル結合含有量は７．９重量％であった。
[Production Example 8]
To an 800 ml ampoule bottle purged with nitrogen, 74.3 g of cyclohexane and 0.48 mmol of tetramethylethylenediamine were added, and 4.76 mmol of n-butyllithium (tetramethylethylenediamine as a polar compound with respect to 1 mol of n-butyllithium). In an amount of 0.10 mol). Subsequently, 17.3 g of isoprene and 1.3 g of styrene were slowly added and reacted in an ampoule bottle at 50 ° C. for 120 minutes to obtain a polymer block (A) having an active end. This polymer block (A) has a weight average molecular weight (Mw) of 6,500, a molecular weight distribution (Mw / Mn) of 1.12, a styrene monomer unit content of 7.0% and an isoprene monomer unit content. The amount was 93.0% by weight and the vinyl bond content was 7.9% by weight.
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン３．５７ｍｍｏｌ、１，３−ブタジエン２５２ｇ、およびスチレン３４８ｇを仕込んだ後、上記にて得られた活性末端を有する重合体ブロック（Ａ）を全量加え、５０℃で重合を開始した（使用したｎ−ブチルリチウム１モルに対する、反応系中に存在する極性化合物としてのテトラメチルエチレンジアミンの量は０．８５モル）。重合を開始してから１５分経過後、１，３−ブタジエン３３８ｇ、およびスチレン６２ｇを６０分間かけて連続的に添加した。重合反応中の最高温度は７０℃であった。連続添加終了後、さらに１５分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、１．５１ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）４．７６ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム８を得た。得られた共役ジエン系ゴム８の重量平均分子量（Ｍｗ）は５６８，０００、カップリング率は４４．６％、スチレン単量体単位含有量は４１重量％、ビニル結合含有量は３４重量％であった。 In an autoclave equipped with a stirrer, 4000 g of cyclohexane, 3.57 mmol of tetramethylethylenediamine, 252 g of 1,3-butadiene, and 348 g of styrene were charged in a nitrogen atmosphere, and then the polymer block (A) having active ends obtained above was obtained. Was added at a temperature of 50 ° C. (the amount of tetramethylethylenediamine as a polar compound present in the reaction system relative to 1 mol of n-butyllithium used was 0.85 mol). After 15 minutes from the start of polymerization, 338 g of 1,3-butadiene and 62 g of styrene were continuously added over 60 minutes. The maximum temperature during the polymerization reaction was 70 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 15 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) was changed to 40%. In the state of a xylene solution having a concentration by weight, 1.51 g (converted to the number of repeating units of the siloxane structure (—Si—O—) in the polyorganosiloxane, 1.1 times the mol of n-butyllithium used) And the reaction was allowed to proceed for 30 minutes. Then, 2.76 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 8. The resulting conjugated diene rubber 8 has a weight average molecular weight (Mw) of 568,000, a coupling rate of 44.6%, a styrene monomer unit content of 41% by weight, and a vinyl bond content of 34% by weight. there were.
〔製造例９〕
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン４．０５ｍｍｏｌ、ジ−Ｎ−ヘキシルアミン４．２９ｍｍｏｌ、１，３−ブタジエン２５２ｇ、およびスチレン３４８ｇを仕込んだ後、ｎ−ブチルリチウム４．７６ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．８５モルとなる量）を加え、５０℃で重合を開始した。重合を開始してから１５分経過後、１，３−ブタジエン３３８ｇ、およびスチレン６２ｇを６０分間かけて連続的に添加した。重合反応中の最高温度は７０℃であった。連続添加終了後、さらに１５分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、１．５１ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）４．７６ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム９を得た。得られた共役ジエン系ゴム９の重量平均分子量（Ｍｗ）は５６６，０００、カップリング率は４４．０％、スチレン単量体単位含有量は４１重量％、ビニル結合含有量は３４重量％であった。
[Production Example 9]
An autoclave equipped with a stirrer was charged with 4000 g of cyclohexane, 4.05 mmol of tetramethylethylenediamine, 4.29 mmol of di-N-hexylamine, 252 g of 1,3-butadiene, and 348 g of styrene under a nitrogen atmosphere, and then 4. 76 mmol (the amount by which the amount of tetramethylethylenediamine as a polar compound was 0.85 mol with respect to 1 mol of n-butyllithium) was added, and polymerization was started at 50 ° C. After 15 minutes from the start of polymerization, 338 g of 1,3-butadiene and 62 g of styrene were continuously added over 60 minutes. The maximum temperature during the polymerization reaction was 70 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 15 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) was changed to 40%. In the state of a xylene solution having a concentration by weight, 1.51 g (converted to the number of repeating units of the siloxane structure (—Si—O—) in the polyorganosiloxane, 1.1 times the mol of n-butyllithium used) And the reaction was allowed to proceed for 30 minutes. Then, 2.76 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 9. The resulting conjugated diene rubber 9 had a weight average molecular weight (Mw) of 566,000, a coupling rate of 44.0%, a styrene monomer unit content of 41% by weight and a vinyl bond content of 34% by weight. there were.
〔製造例１０〕
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン３．９７ｍｍｏｌ、１，３−ブタジエン３１８ｇ、およびスチレン２８２ｇを仕込んだ後、ｎ−ブチルリチウム４．１８ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．９５モルとなる量）を加え、４０℃で重合を開始した。重合を開始してから２０分経過後、１，３−ブタジエン２９２ｇ、およびスチレン１０８ｇを８０分間かけて連続的に添加した。重合反応中の最高温度は６５℃であった。連続添加終了後、さらに２０分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、１．３３ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）４．１８ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム１０を得た。得られた共役ジエン系ゴム１０の重量平均分子量（Ｍｗ）は６３０，０００、カップリング率は４６．８％、スチレン単量体単位含有量は３９重量％、ビニル結合含有量は４０重量％であった。
[Production Example 10]
An autoclave equipped with a stirrer was charged with 4000 g of cyclohexane, 3.97 mmol of tetramethylethylenediamine, 318 g of 1,3-butadiene, and 282 g of styrene under a nitrogen atmosphere, and then 4.18 mmol of n-butyllithium (based on 1 mol of n-butyllithium, The amount of tetramethylethylenediamine as a polar compound was 0.95 mol) was added, and polymerization was started at 40 ° C. After 20 minutes from the start of polymerization, 292 g of 1,3-butadiene and 108 g of styrene were continuously added over 80 minutes. The maximum temperature during the polymerization reaction was 65 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 20 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) was changed to 40 1.33 g (in terms of the number of repeating units of siloxane structure (—Si—O—) in polyorganosiloxane) in the state of xylene solution with a concentration by weight of 1.1 times mol of n-butyllithium used And the reaction was allowed to proceed for 30 minutes. Next, 4.18 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 10. The resulting conjugated diene rubber 10 has a weight average molecular weight (Mw) of 630,000, a coupling rate of 46.8%, a styrene monomer unit content of 39% by weight, and a vinyl bond content of 40% by weight. there were.
〔製造例１１〕
攪拌機付きオートクレーブに、窒素雰囲気下、シクロヘキサン４０００ｇ、テトラメチルエチレンジアミン２．８０ｍｍｏｌ、１，３−ブタジエン２４０ｇ、およびスチレン３６０ｇを仕込んだ後、ｎ−ブチルリチウム４．００ｍｍｏｌ（ｎ−ブチルリチウム１モルに対する、極性化合物としてのテトラメチルエチレンジアミンの量が０．７０モルとなる量）を加え、４０℃で重合を開始した。重合を開始してから２０分経過後、１，３−ブタジエン３４０ｇ、およびスチレン６０ｇを８０分間かけて連続的に添加した。重合反応中の最高温度は６５℃であった。連続添加終了後、さらに２０分間重合反応を継続し、重合転化率が９５％から１００％の範囲になったことを確認してから、上記式（９）で表されるポリオルガノシロキサンを、４０重量％濃度のキシレン溶液の状態にて、１．２７ｇ（ポリオルガノシロキサン中のシロキサン構造（−Ｓｉ−Ｏ−）の繰り返し単位数に換算して、使用したｎ−ブチルリチウムの１．１倍モルに相当する量）添加し、３０分間反応させた。次いで、２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン（一般式（１）で表される化合物）４．００ｍｍｏｌを添加し、１０分間反応させた。その後、重合停止剤として、使用したｎ−ブチルリチウムの２倍モルに相当する量のメタノールを添加して、共役ジエン系ゴムを含有する溶液を得た。この溶液に、老化防止剤として、イルガノックス１５２０Ｌ（チバスペシャリティーケミカルズ社製）を、共役ジエン系ゴム１００部に対して０．１５部添加した後、スチームストリッピングにより溶媒を除去し、６０℃で２４時間真空乾燥して、固形状の共役ジエン系ゴム１１を得た。得られた共役ジエン系ゴム１１の重量平均分子量（Ｍｗ）は６５５，０００、カップリング率は４２．４％、スチレン単量体単位含有量は４２重量％、ビニル結合含有量は３０重量％であった。
[Production Example 11]
In a nitrogen atmosphere, an autoclave equipped with a stirrer was charged with 4000 g of cyclohexane, 2.80 mmol of tetramethylethylenediamine, 240 g of 1,3-butadiene, and 360 g of styrene, and then 4.00 mmol of n-butyllithium (based on 1 mol of n-butyllithium, The amount of tetramethylethylenediamine as a polar compound was 0.70 mol) was added, and polymerization was started at 40 ° C. After 20 minutes from the start of polymerization, 340 g of 1,3-butadiene and 60 g of styrene were continuously added over 80 minutes. The maximum temperature during the polymerization reaction was 65 ° C. After completion of the continuous addition, the polymerization reaction was continued for another 20 minutes, and after confirming that the polymerization conversion rate was in the range of 95% to 100%, the polyorganosiloxane represented by the above formula (9) was changed to 40%. 1.27 g (in terms of the weight% concentration of xylene solution, converted to the number of repeating units of siloxane structure (—Si—O—) in polyorganosiloxane) 1.1 times mol of n-butyllithium used And the reaction was allowed to proceed for 30 minutes. Next, 4.00 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane (a compound represented by the general formula (1)) was added, The reaction was allowed for 10 minutes. Thereafter, as a polymerization terminator, an amount of methanol corresponding to twice the mole of n-butyllithium used was added to obtain a solution containing a conjugated diene rubber. Irganox 1520L (manufactured by Ciba Specialty Chemicals) as an anti-aging agent was added to this solution in an amount of 0.15 part per 100 parts of conjugated diene rubber, and the solvent was removed by steam stripping. For 24 hours to obtain a solid conjugated diene rubber 11. The resulting conjugated diene rubber 11 has a weight average molecular weight (Mw) of 655,000, a coupling rate of 42.4%, a styrene monomer unit content of 42% by weight, and a vinyl bond content of 30% by weight. there were.
〔製造例１２〕
２，２−ジメトキシ−８−（４−メチルピペラジニル）メチル−１，６−ジオキサ−２−シラシクロオクタン４．７６ｍｍｏｌを添加しなかったこと以外は、製造例７と同様に操作して、固形状の共役ジエン系ゴム１２を得た。得られた共役ジエン系ゴム１２の重量平均分子量（Ｍｗ）は５５１，０００、カップリング率は４３．０％、スチレン単量体単位含有量は４１重量％、ビニル結合含有量は３４重量％であった。
[Production Example 12]
The same operation as in Production Example 7 was conducted except that 4.76 mmol of 2,2-dimethoxy-8- (4-methylpiperazinyl) methyl-1,6-dioxa-2-silacyclooctane was not added. A solid conjugated diene rubber 12 was obtained. The resulting conjugated diene rubber 12 has a weight average molecular weight (Mw) of 551,000, a coupling rate of 43.0%, a styrene monomer unit content of 41% by weight, and a vinyl bond content of 34% by weight. there were.
表１に、製造例１〜１２において得られた共役ジエン系ゴム１〜１２について、まとめて示す。
〔実施例１〕
容量２５０ｍｌのブラベンダータイプミキサー中で、製造例１で得られた共役ジエン系ゴム１ ７０部とブタジエンゴム（日本ゼオン社製、商品名「Ｎｉｐｏｌ ＢＲ１２２０」）３０部とを３０秒素練りし、次いでシリカ（エボニック社製、商品名「Ｕｌｔｒａｓｉｌ ７０００ＧＲ」）６６．７部、プロセスオイル（新日本石油社製、商品名「アロマックス Ｔ−ＤＡＥ」）１１．３部、およびシランカップリング剤：ビス（３−（トリエトキシシリル）プロピル）テトラスルフィド（デグッサ社製、商品名「Ｓｉ６９」）７．２部を添加して、１１０℃を開始温度として１．５分間混練後、シリカ（エボニック社製、商品名「Ｕｌｔｒａｓｉｌ ７０００ＧＲ」）２３．３部、カーボンブラック（東海カーボン社製、商品名「シースト ７ＨＭ」）１０部、プロセスオイル（新日本石油社製、商品名「アロマックス Ｔ−ＤＡＥ」）１０部、酸化亜鉛３部、ステアリン酸２部および老化防止剤：Ｎ−フェニル−Ｎ’−（１，３−ジメチルブチル）−ｐ−フェニレンジアミン（大内新興化学工業社製、商品名「ノクラック６Ｃ」）２部を添加し、更に２．５分間混練し、ミキサーから混練物を排出させた。混練終了時の混練物の温度は１５０℃であった。混練物を、室温まで冷却した後、再度ブラベンダータイプミキサー中で、１１０℃を開始温度として２分間混練した後、ミキサーから混練物を排出させた。次いで、５０℃のオープンロールで、得られた混練物に、硫黄１．７部、架橋促進剤：Ｎ−ｔｅｒｔ−ブチル−２−ベンゾチアゾリルスルフェンアミド（大内新興化学工業社製、商品名「ノクセラーＮＳ−Ｐ」）１．８部、および架橋促進剤：１，３−ジフェニルグアニジン（大内新興化学工業社製、商品名「ノクセラーＤ」）１．７部を加えてこれらを混練した後、シート状のゴム組成物を取り出した。このゴム組成物を、１６０℃で２０分間プレス架橋して、ゴム架橋物の試験片を作製し、この試験片について、低発熱性およびウエットグリップ性の評価を行なった。結果を表２に示す。
[Example 1]
In a Brabender type mixer with a capacity of 250 ml, 70 parts of the conjugated diene rubber 170 obtained in Production Example 1 and 30 parts of butadiene rubber (trade name “Nipol BR1220” manufactured by ZEON Corporation) are kneaded for 30 seconds. Next, 66.7 parts of silica (trade name “Ultrasil 7000GR” manufactured by Evonik), 11.3 parts of process oil (trade name “Aromax T-DAE” manufactured by Nippon Oil Corporation), and silane coupling agent: screw 7.2 parts of (3- (triethoxysilyl) propyl) tetrasulfide (Degussa, trade name “Si69”) was added and kneaded for 1.5 minutes at 110 ° C. as the starting temperature, and then silica (Evonik) , 23.3 parts of the trade name “Ultrasil 7000GR”), carbon black (manufactured by Tokai Carbon Co., Ltd., trade name “SEAST 7HM” ) 10 parts, 10 parts of process oil (trade name “Aromax T-DAE” manufactured by Nippon Oil Corporation), 3 parts of zinc oxide, 2 parts of stearic acid and anti-aging agent: N-phenyl-N ′-(1, 2 parts of 3-dimethylbutyl) -p-phenylenediamine (manufactured by Ouchi Shinsei Chemical Co., Ltd., trade name “NOCRACK 6C”) was added, kneaded for 2.5 minutes, and the kneaded product was discharged from the mixer. The temperature of the kneaded product at the end of kneading was 150 ° C. After the kneaded product was cooled to room temperature, it was kneaded again in a Brabender type mixer at 110 ° C. for 2 minutes, and then the kneaded product was discharged from the mixer. Next, with an open roll at 50 ° C., 1.7 parts of sulfur and a crosslinking accelerator: N-tert-butyl-2-benzothiazolylsulfenamide (manufactured by Ouchi Shinsei Chemical Co., Ltd., commercial product) (Name "Noxeller NS-P") 1.8 parts, and crosslinking accelerator: 1,3-diphenylguanidine (made by Ouchi Shinsei Chemical Co., Ltd., trade name "Noxeller D") 1.7 parts After that, the sheet-like rubber composition was taken out. This rubber composition was press-crosslinked at 160 ° C. for 20 minutes to produce a rubber cross-linked test piece. The test piece was evaluated for low heat build-up and wet grip. The results are shown in Table 2.
〔実施例２〜５、比較例１〕
製造例１で得られた共役ジエン系ゴム１ ７０部に代えて、製造例２で得られた共役ジエン系ゴム２（実施例２）、製造例３で得られた共役ジエン系ゴム３（実施例３）、製造例４で得られた共役ジエン系ゴム４（実施例４）、製造例５で得られた共役ジエン系ゴム５（実施例５）、および製造例６で得られた共役ジエン系ゴム６（比較例１）をそれぞれ７０部使用した以外は、実施例１と同様にして、シート状のゴム組成物およびゴム架橋物の試験片を作製し、同様にして、低発熱性およびウエットグリップ性の評価を行なった。結果を表２に示す。
[Examples 2 to 5, Comparative Example 1]
Instead of 70 parts of the conjugated diene rubber 1 obtained in Production Example 1, the conjugated diene rubber 2 obtained in Production Example 2 (Example 2) and the conjugated diene rubber 3 obtained in Production Example 3 (implementation) Example 3), conjugated diene rubber 4 obtained in Production Example 4 (Example 4), conjugated diene rubber 5 obtained in Production Example 5 (Example 5), and conjugated diene obtained in Production Example 6 Except that 70 parts of each of the rubbers 6 (Comparative Example 1) was used, a sheet-like rubber composition and a cross-linked rubber specimen were prepared in the same manner as in Example 1, and the low exothermic property and The wet grip property was evaluated. The results are shown in Table 2.
〔実施例１〜５、比較例１の評価〕
表２から判るように、本発明の共役ジエン系ゴムの製造方法によって得られる、共役ジエン系ゴム（実施例１〜５）を用いて得られたゴム架橋物は、シロキサンのみで変性させた共役ジエン系ゴム（比較例１）を用いて得られたゴム架橋物よりも、低発熱性およびウエットグリップ性に優れたものであった。
なお、実施例１〜５、比較例１において、低発熱性およびウエットグリップ性の評価結果は、比較例１の結果を１００とする指数で示した。低発熱性についてはその値が小さいほど優れるものと判断でき、また、ウエットグリップ性についてはその値が大きいほど優れるものと判断できる。
[Evaluation of Examples 1 to 5 and Comparative Example 1]
As can be seen from Table 2, the crosslinked rubber obtained by using the conjugated diene rubber (Examples 1 to 5) obtained by the method for producing a conjugated diene rubber of the present invention is a conjugated modified with only siloxane. Compared to a rubber cross-linked product obtained using a diene rubber (Comparative Example 1), it was excellent in low heat generation and wet grip properties.
In Examples 1 to 5 and Comparative Example 1, the evaluation results of low heat build-up and wet grip properties are shown as indices with the result of Comparative Example 1 being 100. It can be determined that the smaller the value of the low heat buildup, the better, and the higher the wet grip property, the better.
〔実施例６〕
ブタジエンゴム（日本ゼオン社製、商品名「Ｎｉｐｏｌ ＢＲ１２２０」）３０部に代えて、天然ゴム（ＳＭＲ ＣＶ−６０）３０部を使用した以外は、実施例１と同様にして、シート状のゴム組成物およびゴム架橋物の試験片を作製し、同様にして、低発熱性およびウエットグリップ性の評価を行なった。結果を表３に示す。
Example 6
A sheet-like rubber composition as in Example 1 except that 30 parts of natural rubber (SMR CV-60) was used instead of 30 parts of butadiene rubber (manufactured by Nippon Zeon Co., Ltd., trade name “Nipol BR1220”). Test pieces of rubber and crosslinked rubber were prepared and evaluated in the same manner for low heat build-up and wet grip. The results are shown in Table 3.
〔比較例２〕
製造例１で得られた共役ジエン系ゴム１ ７０部に代えて、製造例６で得られた共役ジエン系ゴム６ ７０部を使用した以外は、実施例６と同様にして、シート状のゴム組成物およびゴム架橋物の試験片を作製し、同様にして、低発熱性およびウエットグリップ性の評価を行なった。結果を表３に示す。
[Comparative Example 2]
In the same manner as in Example 6, except that 70 parts of conjugated diene rubber 6 obtained in Production Example 6 was used instead of 70 parts of conjugated diene rubber 1 obtained in Production Example 1, a sheet-like rubber Test pieces of the composition and the crosslinked rubber were prepared and evaluated in the same manner for low heat build-up and wet grip. The results are shown in Table 3.
〔実施例６、比較例２の評価〕
表３から判るように、本発明の共役ジエン系ゴムの製造方法によって得られる、共役ジエン系ゴム（実施例６）を用いて得られたゴム架橋物は、ブタジエンゴムに代えて天然ゴムを配合した場合においても、シロキサンのみで変性させた共役ジエン系ゴム（比較例２）を用いて得られたゴム架橋物よりも、低発熱性およびウエットグリップ性に優れたものであった。
なお、実施例６、比較例２において、低発熱性およびウエットグリップ性の評価結果は、比較例２の結果を１００とする指数で示した。低発熱性についてはその値が小さいほど優れるものと判断でき、また、ウエットグリップ性についてはその値が大きいほど優れるものと判断できる。
[Evaluation of Example 6 and Comparative Example 2]
As can be seen from Table 3, the rubber cross-linked product obtained using the conjugated diene rubber (Example 6) obtained by the method for producing a conjugated diene rubber of the present invention contains natural rubber instead of butadiene rubber. Even in this case, it was superior in low exothermic property and wet grip property than the crosslinked rubber obtained using the conjugated diene rubber modified with siloxane alone (Comparative Example 2).
In Example 6 and Comparative Example 2, the evaluation results of low exothermic property and wet grip property are shown as indices with the result of Comparative Example 2 being 100. It can be determined that the smaller the value of the low heat buildup, the better, and the higher the wet grip property, the better.
〔実施例７〕
容量２５０ｍｌのブラベンダータイプミキサー中で、製造例７で得られた共役ジエン系ゴム７ ７０部とブタジエンゴム（日本ゼオン社製、商品名「Ｎｉｐｏｌ ＢＲ１２２０」）３０部とを３０秒素練りし、次いでシリカ（ローディア社製、商品名「Ｚｅｏｓｉｌ １１６５ＭＰ」）５０．０部、プロセスオイル（新日本石油社製、商品名「アロマックス Ｔ−ＤＡＥ」）２７．５部、およびシランカップリング剤：ビス（３−（トリエトキシシリル）プロピル）テトラスルフィド（デグッサ社製、商品名「Ｓｉ６９」）６．０部を添加して、１１０℃を開始温度として１．５分間混練後、シリカ（ローディア社製、商品名「Ｚｅｏｓｉｌ １１６５ＭＰ」）２５．０部、酸化亜鉛３部、ステアリン酸２部および老化防止剤：Ｎ−フェニル−Ｎ’−（１，３−ジメチルブチル）−ｐ−フェニレンジアミン（大内新興化学工業社製、商品名「ノクラック６Ｃ」）２部を添加し、更に２．５分間混練し、ミキサーから混練物を排出させた。混練終了時の混練物の温度は１５０℃であった。混練物を、室温まで冷却した後、再度ブラベンダータイプミキサー中で、１１０℃を開始温度として２分間混練した後、ミキサーから混練物を排出させた。次いで、５０℃のオープンロールで、得られた混練物に、硫黄１．５部、架橋促進剤：Ｎ−ｔｅｒｔ−ブチル−２−ベンゾチアゾリルスルフェンアミド（大内新興化学工業社製、商品名「ノクセラーＮＳ−Ｐ」）１．８部、および架橋促進剤：１，３−ジフェニルグアニジン（大内新興化学工業社製、商品名「ノクセラーＤ」）１．５部を加えてこれらを混練した後、シート状のゴム組成物を取り出した。このゴム組成物を、１６０℃で２０分間プレス架橋して、ゴム架橋物の試験片を作製し、この試験片について、ウエットグリップ性および低発熱性の評価を行なった。結果を表４に示す。
Example 7
In a Brabender type mixer having a capacity of 250 ml, 770 parts of the conjugated diene rubber obtained in Production Example 7 and 30 parts of butadiene rubber (product name “Nipol BR1220” manufactured by Nippon Zeon Co., Ltd.) are kneaded for 30 seconds. Next, 50.0 parts of silica (trade name “Zeosil 1165MP” manufactured by Rhodia), 27.5 parts of process oil (trade name “Aromax T-DAE” manufactured by Nippon Oil Corporation), and silane coupling agent: screw 6.0 parts of (3- (triethoxysilyl) propyl) tetrasulfide (Degussa, trade name “Si69”) was added, kneaded for 1.5 minutes at 110 ° C. as a starting temperature, and then silica (manufactured by Rhodia) , Trade name "Zeosil 1165MP") 25.0 parts, zinc oxide 3 parts, stearic acid 2 parts and anti-aging agent: N-phenyl-N'- 2 parts of 1,3-dimethylbutyl) -p-phenylenediamine (trade name “NOCRACK 6C” manufactured by Ouchi Shinsei Chemical Industry Co., Ltd.) was added, and the mixture was further kneaded for 2.5 minutes, and the kneaded product was discharged from the mixer. . The temperature of the kneaded product at the end of kneading was 150 ° C. After the kneaded product was cooled to room temperature, it was kneaded again in a Brabender type mixer at 110 ° C. for 2 minutes, and then the kneaded product was discharged from the mixer. Subsequently, with an open roll at 50 ° C., 1.5 parts of sulfur and a crosslinking accelerator: N-tert-butyl-2-benzothiazolylsulfenamide (manufactured by Ouchi Shinsei Chemical Co., Ltd., commercial product) 1.8 parts of the name “Noxeller NS-P”) and 1.5 parts of the crosslinking accelerator: 1,3-diphenylguanidine (made by Ouchi Shinsei Chemical Co., Ltd., trade name “Noxeller D”) are added and kneaded. After that, the sheet-like rubber composition was taken out. This rubber composition was press-crosslinked at 160 ° C. for 20 minutes to produce a rubber cross-linked test piece. The test piece was evaluated for wet grip and low heat build-up. The results are shown in Table 4.
〔実施例８〜１１、比較例３〕
製造例７で得られた共役ジエン系ゴム７ ７０部に代えて、製造例８で得られた共役ジエン系ゴム８（実施例８）、製造例９で得られた共役ジエン系ゴム９（実施例９）、製造例１０で得られた共役ジエン系ゴム１０（実施例１０）、製造例１１で得られた共役ジエン系ゴム１１（実施例１１）、および製造例１２で得られた共役ジエン系ゴム１２（比較例３）をそれぞれ７０部使用した以外は、実施例７と同様にして、シート状のゴム組成物およびゴム架橋物の試験片を作製し、同様にして、低発熱性およびウエットグリップ性の評価を行なった。結果を表４に示す。
[Examples 8 to 11, Comparative Example 3]
Instead of 70 parts of the conjugated diene rubber 7 obtained in Production Example 7, the conjugated diene rubber 8 obtained in Production Example 8 (Example 8) and the conjugated diene rubber 9 obtained in Production Example 9 (implementation) Example 9), conjugated diene rubber 10 obtained in Production Example 10 (Example 10), conjugated diene rubber 11 obtained in Production Example 11 (Example 11), and conjugated diene obtained in Production Example 12 Except that 70 parts of each of the rubber system 12 (Comparative Example 3) was used, a sheet-like rubber composition and a test piece of a rubber cross-linked product were prepared in the same manner as in Example 7. The wet grip property was evaluated. The results are shown in Table 4.
〔実施例７〜１１、比較例３の評価〕
表４から判るように、本発明の共役ジエン系ゴムの製造方法によって得られる、共役ジエン系ゴム（実施例７〜１１）を用いて得られたゴム架橋物は、共役ジエン系ゴムのスチレン単量体単位含有量が４０重量％付近である場合においても、シロキサンのみで変性させた共役ジエン系ゴム（比較例３）を用いて得られたゴム架橋物よりも、低発熱性およびウエットグリップ性に優れたものであった。
なお、実施例７〜１１、比較例３において、低発熱性およびウエットグリップ性の評価結果は、比較例３の結果を１００とする指数で示した。低発熱性についてはその値が小さいほど優れるものと判断でき、また、ウエットグリップ性についてはその値が大きいほど優れるものと判断できる。
[Evaluation of Examples 7 to 11 and Comparative Example 3]
As can be seen from Table 4, the crosslinked rubber obtained by using the conjugated diene rubber (Examples 7 to 11) obtained by the method for producing a conjugated diene rubber of the present invention is a styrene dimer of conjugated diene rubber. Even in the case where the monomer unit content is around 40% by weight, the heat build-up property and wet grip property are lower than those of a rubber cross-linked product obtained by using a conjugated diene rubber modified only with siloxane (Comparative Example 3). It was excellent.
In Examples 7 to 11 and Comparative Example 3, the evaluation results of low heat build-up and wet grip properties are shown as indices with the result of Comparative Example 3 being 100. It can be determined that the smaller the value of the low heat buildup, the better, and the higher the wet grip property, the better.
〔実施例１２〕
ブタジエンゴム（日本ゼオン社製、商品名「Ｎｉｐｏｌ ＢＲ１２２０」）３０部に代えて、天然ゴム（ＳＭＲ ＣＶ−６０）３０部を使用した以外は、実施例７と同様にして、シート状のゴム組成物およびゴム架橋物の試験片を作製し、同様にして、低発熱性およびウエットグリップ性の評価を行なった。結果を表５に示す。
Example 12
A sheet-like rubber composition in the same manner as in Example 7 except that 30 parts of natural rubber (SMR CV-60) was used instead of 30 parts of butadiene rubber (manufactured by Zeon Corporation, trade name “Nipol BR1220”). Test pieces of rubber and crosslinked rubber were prepared and evaluated in the same manner for low heat build-up and wet grip. The results are shown in Table 5.
〔比較例４〕
製造例７で得られた共役ジエン系ゴム７ ７０部に代えて、製造例１２で得られた共役ジエン系ゴム１２ ７０部を使用した以外は、実施例１２と同様にして、シート状のゴム組成物およびゴム架橋物の試験片を作製し、同様にして、低発熱性およびウエットグリップ性の評価を行なった。結果を表５に示す。
[Comparative Example 4]
In the same manner as in Example 12, except that 70 parts of the conjugated diene rubber 12 obtained in Production Example 12 was used instead of 70 parts of the conjugated diene rubber 7 obtained in Production Example 7, a sheet-like rubber Test pieces of the composition and the crosslinked rubber were prepared and evaluated in the same manner for low heat build-up and wet grip. The results are shown in Table 5.
〔実施例１２、比較例４の評価〕
表５から判るように、本発明の共役ジエン系ゴムの製造方法によって得られる、共役ジエン系ゴム（実施例１２）を用いて得られたゴム架橋物は、共役ジエン系ゴムのスチレン単量体単位含有量を４０重量％付近とし、かつ、ブタジエンゴムに代えて天然ゴムを配合した場合においても、シロキサンのみで変性させた共役ジエン系ゴム（比較例４）を用いて得られたゴム架橋物よりも、低発熱性およびウエットグリップ性に優れたものであった。
なお、実施例１２、比較例４において、低発熱性およびウエットグリップ性の評価結果は、比較例４の結果を１００とする指数で示した。低発熱性についてはその値が小さいほど優れるものと判断でき、また、ウエットグリップ性についてはその値が大きいほど優れるものと判断できる。
[Evaluation of Example 12 and Comparative Example 4]
As can be seen from Table 5, the crosslinked rubber obtained by using the conjugated diene rubber (Example 12) obtained by the method for producing a conjugated diene rubber of the present invention is a styrene monomer of a conjugated diene rubber. A rubber cross-linked product obtained by using a conjugated diene rubber (Comparative Example 4) modified only with siloxane even when the unit content is around 40% by weight and natural rubber is blended in place of butadiene rubber More excellent in low heat generation and wet grip.
In Example 12 and Comparative Example 4, the evaluation results of low exothermic property and wet grip property are shown as indices with the result of Comparative Example 4 being 100. It can be determined that the smaller the value of the low heat buildup, the better, and the higher the wet grip property, the better.
Claims (12)
前記活性末端を有する共役ジエン系重合体鎖に、シロキサンを反応させる第２工程と、
前記第２工程で得られるシロキサンを反応させた共役ジエン系重合体鎖に、下記一般式（１）で表される化合物を反応させる第３工程とを備える、
共役ジエン単量体単位部分におけるビニル結合含有量が５０重量％以下である共役ジエン系ゴムの製造方法。
A second step of reacting siloxane with the conjugated diene polymer chain having an active end;
A third step of reacting the compound represented by the following general formula (1) with the conjugated diene polymer chain obtained by reacting the siloxane obtained in the second step;
A method for producing a conjugated diene rubber, wherein the vinyl bond content in the conjugated diene monomer unit is 50% by weight or less.
不活性溶媒中で、イソプレン、または、イソプレンおよび芳香族ビニル化合物を含む単量体を、重合開始剤により重合し、イソプレン単量体単位８０〜１００重量％、および芳香族ビニル単量体単位０〜２０重量％を含む活性末端を有する重合体ブロック（Ａ）を形成させる工程と、
前記活性末端を有する重合体ブロック（Ａ）と、１，３−ブタジエン、または１，３−ブタジエンおよび芳香族ビニル化合物を含む単量体と、を混合して重合反応を継続させ、１，３−ブタジエン単量体単位５０〜１００重量％および芳香族ビニル単量体単位０〜５０重量％を含む活性末端を有する重合体ブロック（Ｂ）を、重合体ブロック（Ａ）と一続きにして形成させることにより、活性末端を有する共役ジエン系重合体鎖を得る工程とを備える請求項１〜５のいずれかに記載の共役ジエン系ゴムの製造方法。 The first step includes
In an inert solvent, isoprene or a monomer containing isoprene and an aromatic vinyl compound is polymerized with a polymerization initiator, and isoprene monomer units 80 to 100% by weight, and aromatic vinyl monomer unit 0 Forming a polymer block (A) having active ends comprising ˜20% by weight;
The polymer block (A) having an active terminal and 1,3-butadiene, or a monomer containing 1,3-butadiene and an aromatic vinyl compound are mixed to continue the polymerization reaction, and 1,3 -A polymer block (B) having an active end containing 50 to 100% by weight of a butadiene monomer unit and 0 to 50% by weight of an aromatic vinyl monomer unit is formed continuously with the polymer block (A). A process for producing a conjugated diene rubber according to any one of claims 1 to 5, further comprising a step of obtaining a conjugated diene polymer chain having an active end.