JP2016138349A - フマル酸含有繊維、フマル酸含有繊維集合体および吸収体 - Google Patents
フマル酸含有繊維、フマル酸含有繊維集合体および吸収体 Download PDFInfo
- Publication number
- JP2016138349A JP2016138349A JP2015014018A JP2015014018A JP2016138349A JP 2016138349 A JP2016138349 A JP 2016138349A JP 2015014018 A JP2015014018 A JP 2015014018A JP 2015014018 A JP2015014018 A JP 2015014018A JP 2016138349 A JP2016138349 A JP 2016138349A
- Authority
- JP
- Japan
- Prior art keywords
- fumaric acid
- fiber
- mass
- water
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】フマル酸含有繊維は、基材繊維とフマル酸とを有し、前記基材繊維が吸水性繊維を含有し、前記フマル酸が前記吸水性繊維とフマル酸含有水溶液とを接触させた後、水を除去することにより付与されたものであり、前記フマル酸の付与量が吸水性繊維100質量部に対して、0.0001〜0.15質量部の範囲で、細菌増殖による発熱量の推移により、細菌増殖を抑制できることが示される。
【選択図】図1
Description
本発明のフマル酸含有繊維は、基材繊維とフマル酸とを有する。そして、前記基材繊維が吸水性繊維を含有し、前記フマル酸が前記基材繊維とフマル酸含有水溶液とを接触させた後、水を除去することにより付与されたものである。吸水性繊維とフマル酸含有水溶液とを接触させると、吸水性繊維が水を吸収するとともに溶解したフマル酸分子も取り込むこととなり、水を除去すると吸水性繊維の内部にフマル酸分子が存在することとなる。このように吸水性繊維の内部に存在するフマル酸は、体液等によって流されることがないため、長期にわたって防臭、抗菌効果を発揮できる。
本発明には、前記フマル酸含有繊維を含有するフマル酸含有繊維集合体も含まれる。繊維集合体としては、不織布、織物、編み物などの繊維シートや、基材繊維同士が意図的に固着、絡合されていないものなどが挙げられる。
本発明の吸収体は、吸水性材料として、前記フマル酸含有繊維と吸水性樹脂粉末とを含有する。前記吸水性樹脂粉末としては、従来吸収性物品に使用されているものが使用できる。前記吸水性樹脂粉末には、抗菌剤、酸化防止剤、紫外線吸収剤、着色剤、芳香剤、消臭剤、無機質粉末及び有機質繊維状物などの添加剤を含むことができる。前記吸収体は、前記吸水性材料として、前記フマル酸含有繊維以外の吸水性繊維を含有してもよい。
薬剤含有繊維No.1(フマル酸0.000010質量部)
水に、キサンタンガム水溶液にフマル酸30質量%を分散させたフマル酸分散液(第一製網社製、フマル酸分散液「DF−30」、フマル酸100質量部に対するキサンタンガム含有量は0.01質量部〜5質量部)を溶解させて、フマル酸濃度5.0×10−7質量%の薬剤含有水溶液を調製した。この薬剤含有水溶液20gを、セルロース繊維(木材パルプ)100gに対して吹き付け、乾燥機(設定温度50℃)で24時間乾燥させた。得られた薬剤含有繊維No.1は、セルロース繊維100質量部に対するフマル酸含有量は0.000010質量部である。
薬剤含有水溶液のフマル酸濃度を5.0×10−6質量%に変更したこと以外は、前記薬剤含有繊維No.1の作製と同様にして、薬剤含有繊維No.2を得た。得られた薬剤含有繊維No.2は、セルロース繊維100質量部に対するフマル酸含有量は0.00010質量部である。
薬剤含有水溶液のフマル酸濃度を7.5×10−6質量%に変更したこと以外は、前記薬剤含有繊維No.1の作製と同様にして、薬剤含有繊維No.3を得た。得られた薬剤含有繊維No.3は、セルロース繊維100質量部に対するフマル酸含有量は0.00015質量部である。
薬剤含有水溶液のフマル酸濃度を2.5×10−3質量%に変更したこと以外は、前記薬剤含有繊維No.1の作製と同様にして、薬剤含有繊維No.4を得た。得られた薬剤含有繊維No.4は、セルロース繊維100質量部に対するフマル酸含有量は0.05質量部である。
薬剤含有水溶液のフマル酸濃度を7.5×10−3質量%に変更したこと以外は、前記薬剤含有繊維No.1の作製と同様にして、薬剤含有繊維No.5を得た。得られた薬剤含有繊維No.5は、セルロース繊維100質量部に対するフマル酸含有量は0.15質量部である。
クエン酸を水20gに溶解させ、濃度7.5×10−3質量%のクエン酸水溶液を調製した。このクエン酸水溶液を木材パルプ(セルロース繊維)100gに対して吹き付け、乾燥機(設定温度50℃)で24時間乾燥させた。得られた薬剤含有繊維No.6は、セルロース繊維100質量部に対するクエン酸含有量は0.15質量部である。
乳酸を水20gに溶解させ、濃度7.5×10−3質量%の乳酸水溶液を調製した。この乳酸水溶液を木材パルプ(セルロース繊維)100gに対して吹き付け、乾燥機(設定温度50℃)で24時間乾燥させた。得られた薬剤含有繊維No.7は、セルロース繊維100質量部に対する乳酸含有量は0.15質量部である。
木材パルプ(セルロース繊維)100gに対して、水50gを吹き付け、乾燥機(設定温度50℃)で24時間乾燥させ比較繊維を得た。
透液性不織布(縦12cm、横12cm)、ティッシュペーパー(目付け15g/m2、縦10cm、横10cm)、ポリエチレンフィルム(縦12cm、横12cm)を準備した。前記薬剤含有繊維No.1〜7または比較繊維を2g量りとり、これを縦10cm、横10cmの大きさに成形した。この成形物を、2枚のティッシュペーパーで挟んで積層体を得た。前記ポリエチレンフィルム上にホットメルト接着剤を塗布し、前記積層体を重ねた。さらに積層体上にホットメルト接着剤を塗布し、前記透液性不織布を重ね、繊維内包シートを得た。
<臭気強度の評価基準>
○:無臭、または、何とか感知できる程度の臭い。
△:何の臭いであるか理解できる。
×:強烈に臭う。
水に、キサンタンガム水溶液にフマル酸30質量%を分散させたフマル酸分散液(第一製網社製、フマル酸分散液「DF−30」、フマル酸100質量部に対するキサンタンガム含有量は0.01質量部〜5質量部)を溶解させて、フマル酸濃度0.15質量%の薬剤含有水溶液を調製した。木材パルプ(セルロース繊維)0.3gに対して、上記薬剤含有水溶液0.3gを、吹き付け、乾燥機(設定温度50℃)で24時間乾燥させた。得られた薬剤含有繊維No.8は、セルロース繊維100質量部に対するフマル酸含有量は0.15質量部である。
クエン酸、リンゴ酸または乳酸を水に溶解させ、濃度0.15質量%の薬剤水溶液を調製した。この薬剤水溶液0.3gを、木材パルプ(セルロース繊維)0.3gに対して吹き付け、乾燥機(設定温度50℃)で24時間乾燥させた。得られた薬剤含有繊維No.9〜11は、セルロース繊維100質量部に対する薬剤含有量は0.15質量部である。
木材パルプに対する薬剤含有水溶液の吹き付け量を3.0gに変更したこと以外は、薬剤含有繊維No.8〜11の作製と同様にして、薬剤含有繊維No.12〜15を得た。得られた薬剤含有繊維No.12〜15は、セルロース繊維100質量部に対する薬剤含有量は1.5質量部である。
ガラスバイアルに薬剤含有繊維0.3gを入れ、大腸菌を接種した培地を添加し、試験サンプルとした。微小熱量計を用いて、37℃での微生物の増殖を測定した。なお、比較のため、薬剤を付与していない無加工パルプ、および、薬剤を付与せず、菌接種をしていない無加工パルプについても試験を行った。微小熱量計は、微生物が増殖する際に発する熱をとらえて、微生物の増殖を継時的に測定する。薬剤に増殖抑制効果があれば、増殖サーモグラフのピークの出現時間が遅くなる。薬剤に増殖阻止効果があれば、増殖サーモグラフにピークが出現しない。結果を図1に示した。
木材パルプ(セルロース繊維)4gと、吸水性樹脂粉末(SDPグローバル社製、サンウェット(登録商標))2gとを混合し、吸水性材料を作製した。前記吸水性材料6gを、これを縦10cm、横10cmの大きさに成形した。この成形物を、2枚のティッシュペーパー(セルロース繊維、目付け15g/m2、縦10cm、横10cm)で挟んで吸収体コアを作製した。ポリエチレンフィルム(縦12cm、横12cm)上にホットメルト接着剤を塗布し、前記吸収体コアを重ねた。さらに吸収体コア上にホットメルト接着剤を塗布し、透液性不織布(縦12cm、横12cm)を重ね、比較吸収体を得た。
水に、キサンタンガム水溶液にフマル酸30質量%を分散させたフマル酸分散液(第一製網社製、フマル酸分散液「DF−30」、フマル酸100質量部に対するキサンタンガム含有量は0.01質量部〜5質量部)を溶解させて、フマル酸濃度0.15質量%の薬剤含有水溶液を調製した。この薬剤含有水溶液0.6gを、前記比較吸収体に塗布し、室温(20℃)で1週間乾燥させて吸収体No.1を得た。
薬剤含有水溶液のフマル酸濃度を1.5質量%に変更したこと以外は、吸収体No.1の作製と同様にして、吸収体No.2を得た。
比較吸収体への薬剤含有水溶液の塗布量を6.0gに変更したこと以外は、吸収体No.2の作製と同様にして、吸収体No.3を得た。
乳酸を水に溶解させ、濃度1.5質量%の乳酸水溶液を調製した。この薬剤含有水溶液6gを、前記比較吸収体に塗布し、室温(20℃)で1週間乾燥させて吸収体No.4を得た。
薬剤をクエン酸に変更したこと以外は、吸収体No.4の作製と同様にして、吸収体No.5を得た。
薬剤をリンゴ酸に変更したこと以外は、吸収体No.4の作製と同様にして、吸収体No.6を得た。
銀イオン担持化合物(シナネンゼオミック社製、ゼオミック(登録商標)水分散体)を水に溶解させ、濃度1.5質量%の銀イオン担持化合物の水分散液を調製した。この分散液0.6gを、前記比較吸収体に塗布し、室温(20℃)で1週間乾燥させて吸収体No.7を得た。
塩化ベンザルコニウムを水に溶解させ、濃度1.5質量%の水溶液を調製した。この薬剤含有水溶液0.6gを、前記比較吸収体に塗布し、室温(20℃)で1週間乾燥させて吸収体No.8を得た。
吸収体に人尿40mlを吸収させ、恒温槽(40℃)で保管し、吸収直後、10分後、1時間後、3時間後、6時間後の臭気強度を下記の6段階で評価した。評価は、9名の試験者で行い、平均値を評価とした。結果を表2、図2に示した。
0:無臭。
1:何とか感知できる程度の臭い。
2:何の臭いであるか理解できるが、弱い臭い。
3:容易に感知できる臭い。
4:強く臭う。
5:強烈に臭う。
水に、キサンタンガム水溶液にフマル酸30質量%を分散させたフマル酸分散液(第一製網社製、フマル酸分散液「DF−30」、フマル酸100質量部に対するキサンタンガム含有量は0.01質量部〜5質量部)を溶解させて、フマル酸濃度0.15質量%の薬剤含有水溶液を調製した。この薬剤含有水溶液0.03gに水を追加して、全量が1.5gとなるように調整した。木材パルプ60質量%と、吸水性樹脂粉末40質量%とを含有する吸水性材料0.3gに、前記薬剤含有水溶液の希釈液を全て吹き付け、乾燥機(設定温度45℃)で4時間乾燥させた。得られた吸収体No.9は、吸水性材料100質量部に対する薬剤含有量は0.015質量部である。
薬剤含有水溶液の使用量を0.15gに変更したこと以外は、前記吸収体No.9の作製と同様にして、吸収体No.10を得た。得られた吸収体No.10は、吸水性材料100質量部に対する薬剤含有量は0.075質量部である。
銀イオン担持化合物(シナネンゼオミック社製、ゼオミック水分散体)を水に溶解させ、濃度0.15質量%の銀イオン担持化合物の水分散液を調製した。この薬剤含有水溶液0.03gに水を追加して、全量が1.5gとなるように調整した。木材パルプ60質量%と、吸水性樹脂粉末40質量%とを含有する吸水性材料0.3gに、前記薬剤含有水溶液の希釈液を全て吹き付け、乾燥機(設定温度45℃)で4時間乾燥させた。得られた吸収体No.11は、吸水性材料100質量部に対する銀イオン含有量は0.015質量部である。
薬剤含有水溶液の使用量を0.15gに変更したこと以外は、前記吸収体No.11の作製と同様にして、吸収体No.12を得た。得られた吸収体No.12は、吸水性材料100質量部に対する銀イオン含有量は0.075質量部である。
塩化ベンザルコニウムを水に溶解させ、濃度0.15質量%の水溶液を調製した。この薬剤含有水溶液0.03gに水を追加して、全量が1.5gとなるように調整した。木材パルプ60質量%と、吸水性樹脂粉末40質量%とを含有する吸水性材料0.3gに、前記薬剤含有水溶液の希釈液を全て吹き付け、乾燥機(設定温度45℃)で4時間乾燥させた。得られた吸収体No.13は、吸水性材料100質量部に対する薬剤含有量は0.015質量部である。
薬剤含有水溶液の使用量を0.15gに変更したこと以外は、前記吸収体No.13の作製と同様にして、吸収体No.14を得た。得られた吸収体No.14は、吸水性材料100質量部に対する薬剤含有量は0.075質量部である。
ガラスバイアルに薬剤を付与した吸水性材料0.3gを入れ、大腸菌を接種した培地を添加し、試験サンプルとした。微小熱量計を用いて、37℃での微生物の増殖を測定した。結果を図3に示した。なお、比較のため、薬剤を付与していない無加工パルプ、および、薬剤を付与せず、菌接種をしていない無加工パルプについても試験を行った。
Claims (7)
- 基材繊維と、フマル酸とを有し、
前記基材繊維が、吸水性繊維を含有し、
前記フマル酸が、前記基材繊維とフマル酸含有水溶液とを接触させた後、水を除去することにより付与されたものであり、
前記フマル酸の付与量が、吸水性繊維100質量部に対して、0.0001質量部〜0.15質量部であることを特徴とするフマル酸含有繊維。 - 前記吸水性繊維が、セルロース繊維である請求項1に記載のフマル酸含有繊維。
- 前記吸水性繊維が、天然セルロース繊維および/または再生セルロース繊維である請求項1または2に記載のフマル酸含有繊維。
- 前記基材繊維が、セルロース繊維と合成繊維を含有する請求項2または3に記載のフマル酸含有繊維。
- 請求項1〜4のいずれか一項に記載のフマル酸含有繊維を含有することを特徴とするフマル酸含有繊維集合体。
- 不織布、織布、編み物である請求項5に記載のフマル酸含有繊維集合体。
- 吸水性材料として、請求項1〜4のいずれか一項に記載のフマル酸含有繊維と吸水性樹脂粉末とを含有することを特徴とする吸収体。