JP2015203117A - バスバー用アルミニウム合金板及びその製造方法 - Google Patents
バスバー用アルミニウム合金板及びその製造方法 Download PDFInfo
- Publication number
- JP2015203117A JP2015203117A JP2014081332A JP2014081332A JP2015203117A JP 2015203117 A JP2015203117 A JP 2015203117A JP 2014081332 A JP2014081332 A JP 2014081332A JP 2014081332 A JP2014081332 A JP 2014081332A JP 2015203117 A JP2015203117 A JP 2015203117A
- Authority
- JP
- Japan
- Prior art keywords
- aluminum alloy
- plate
- less
- alloy plate
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】バスバー用アルミニウム合金板は、Mg:0.3〜0.9%(質量%、以下同じ。)、Si:0.2〜1.2%、Cu:0.2%以下、Fe:0.5%以下を含有し、残部がAl及び不可避的不純物からなる化学成分を有する。また、Al母相中に、Mg及びSiを含有する針状粒子が900〜4000個/μm2存在している。また、Al母相中に存在するFe系粒子は、平均円相当径が5μm以下であり、かつ、2μmを超える円相当径を有する粒子の数が10000個/mm2以下である。
【選択図】図1
Description
Al母相中に、Mg及びSiを含有する針状粒子が900〜4000個/μm2存在し、
上記Al母相中に存在するFe系粒子は、平均円相当径が5μm以下であり、かつ、2μmを超える円相当径を有する粒子の数が10000個/mm2以下であることを特徴とするバスバー用アルミニウム合金板にある。
該板材に溶体化処理を施した後、
1〜10%の圧下率で上記板材にスキンパスを行い、
その後、上記板材に人工時効処理を施すことを特徴とするバスバー用アルミニウム合金板の製造方法にある。
・Mg:0.3〜0.9%
Mg(マグネシウム)は、Siと共存することにより針状粒子を析出させ、析出強化によりアルミニウム合金板の強度を向上させる作用を有する。一方、針状粒子として析出しないMgはAl母相に固溶しているため、Mgの固溶量が過度に多くなると導電率が低下する傾向がある。
Si(シリコン)は、Mgと共存することにより針状粒子を析出させ、アルミニウム合金板の強度を向上させる作用を有する。Siの含有量を0.2〜1.2%の範囲とすることにより、アルミニウム合金板の強度特性及び曲げ加工性を向上させることができる。同じ観点から、Siの含有量を0.25〜1.1%にすることが好ましい。
Cu(銅)は、使用する原料の種類によってある程度混入する可能性がある。Cuは曲げ加工の際にせん断帯の形成を促進する作用を有する。せん断帯が存在すると、曲げ加工の際に生じる微小な割れがせん断帯を伝播して拡大し、アルミニウム合金板に割れが発生し易くなる。それ故、Cuの含有量が過度に多くなると曲げ加工性の低下を招く。また、Cuの含有量が多くなると、導電率が低下する傾向がある。そのため、Cuの含有量を0.2%以下に規制することにより、上述の問題を回避し、アルミニウム合金板の導電性及び曲げ加工性を向上させることができる。同じ観点から、Cuの含有量を0.1%以下に規制することが好ましい。
Fe(鉄)は、Cuと同様に、使用する原料の種類によってある程度混入する可能性がある。Feの含有量が多くなると、Al母相中に粗大なFe系粒子を発生させ易くなる。粗大なFe系粒子は曲げ加工の際に割れの起点となり得るため、Feの含有量が過度に多くなると曲げ加工性の低下を招き、アルミニウム合金板に割れが発生しやすくなる。そのため、Feの含有量を0.5%以下に規制することにより、上述の問題を回避し、アルミニウム合金板の曲げ加工性を向上させることができる。同じ観点から、Feの含有量を0.4%以下に規制することが好ましい。
・針状粒子
Al母相に含まれる第二相粒子のうち、Mg及びSiを含有し、針状を呈する粒子を針状粒子という。針状粒子は、人工時効処理により析出し、析出強化によりアルミニウム合金板の強度を向上させる作用を有する。また、針状粒子が多く析出するほどAl母相中のMg固溶量が相対的に低下するため、針状粒子の数が多いほど導電率が高くなる傾向がある。それ故、針状粒子の数を900個/μm2以上とすることにより、アルミニウム合金板の強度及び導電性を向上させることができる。
Al母相中に含まれる第二相粒子のうち、Al−Fe−Si系、Al−Fe系の晶出物や析出物よりなる粒子をFe系粒子という。Fe系粒子は、アルミニウム合金板にFeが含まれる場合に形成される。Al母相中に粗大なFe系粒子が存在すると、曲げ加工における割れの起点となり、曲げ加工性の低下を招く。従って、曲げ加工性に優れたアルミニウム合金板を得るために、Fe系粒子の平均円相当径を5μm以下に規制し、かつ、2μmを超える円相当径を有する粒子の数を10000個/mm2以下に規制する。なお、アルミニウム合金板は、例えば、Feを含まない化学成分とする等の方法により、Fe系粒子を含まない構成とすることも可能である。Al母相中にFe系粒子が存在しない場合であっても、アルミニウム合金板の強度特性、導電性及び曲げ加工性が低下することはない。
アルミニウム合金板は、170MPa以上の引張強さ及び55%IACS以上の導電率を有することが好ましい。かかる特性を有するアルミニウム合金板は、バスバーに要求される強度特性及び導電性を十分に満足するため、バスバーの素材として好適である。
上記アルミニウム合金板の実施例について、以下に説明する。本例においては、表1に示す化学成分(合金A〜M)を有するアルミニウム合金圧延板(試験材1〜13)を作製し、引張強さ、導電率及び曲げ加工性について評価を行った。
・針状粒子の数の評価
厚み方向における試験材の中心部から、板面に平行な薄片状試料を採取した。透過型電子顕微鏡を用いて、薄片状試料を倍率50000倍で観察した電子顕微鏡像を取得した。得られた電子顕微鏡像の画像解析を行い、視野内に存在する針状粒子の個数を計測した。そして、針状粒子の個数を視野面積で除して単位面積当たりの個数(個/μm2)に換算した。なお、上記の手法は、微細な第二相粒子の観察方法として一般的であるが、上記手法に基づいて針状粒子の粒子径を測定することは困難である。
厚み方向における試験材の中心部に、板面に平行な断面を露出させた。走査型電子顕微鏡を用い、当該断面を倍率500倍で観察した電子顕微鏡像を取得した。得られた電子顕微鏡像の画像解析を行い、視野内に存在するFe系粒子の円相当径を算出し、度数分布を作成した。そして、当該度数分布に基づいてFe系粒子の平均円相当径及び2μmを超える円相当径を有するFe系粒子の数を算出した。
JIS Z 2241に規定された試験方法に準じて引張試験を行い、試験材の引張強さを測定した。なお、引張試験片は、長手方向と圧延方向とが平行となるように採取した。また、引張試験においては、引張強さが170MPa以上の試験材を合格と判定した。
導電率測定器(日本フェルスター社製「SIGMATEST2.069」)を用い、25℃における試験材の導電率を測定した。なお、導電率測定においては、導電率が55%IACS以上の試験材を合格と判定した。
JIS Z 2248に規定された試験方法に準じて、試験材から採取した条材を用いて180度密着曲げ試験を行い、試験後の割れの有無を目視により確認した。なお、180度密着曲げ試験は、予備曲げ時の内側曲げ半径が2.0mmとなるように行った。また、180度密着曲げ試験においては、試験後の割れがない試験材を合格と判定した。
試験材9は、Mgの含有量が多い合金Iを用いたため、針状粒子の数が過多となった。その結果、180度密着曲げ試験において不合格と判定された。また、Mgの含有量が多いため、導電率測定において不合格と判定された。
試験材11は、Siの含有量が多い合金Kを用いたため、針状粒子の数が過多となった。その結果、180度密着曲げ試験において不合格と判定された。
試験材13は、Feの含有量が0.5%を超える合金Mを用いたため、粗大なFe系粒子の数が過多となった。その結果、180度密着曲げ試験において不合格と判定された。
本例は、スキンパスを施す際の圧下率を変更して作製したアルミニウム合金板の例である。本例においては、まず、DC鋳造により、Mg:0.65%、Si:0.40%、Cu:0.02%、Fe:0.25%を含有し、残部がAl及び不可避的不純物からなる化学成分を有し、厚さ500mm、幅500mmの寸法を有する鋳塊を作製した。得られた鋳塊を560℃で10時間加熱して均質化処理を行った後、熱間圧延を行って厚さ4.0mmの粗圧延板を作製した。なお、熱間圧延の開始時における鋳塊の温度は560℃とした。また、熱間圧延終了時の粗圧延板の温度は330℃であった。次いで、表3に示す圧下率で粗圧延板に冷間圧延を行い、板材を準備した。
試験材25は、スキンパスにおける圧下率が10%を超えたため、加工硬化量が過度に大きくなり、180度密着曲げ試験において不合格と判定された。
Claims (3)
- Mg:0.3〜0.9%(質量%、以下同じ。)、Si:0.2〜1.2%、Cu:0.2%以下、Fe:0.5%以下を含有し、残部がAl及び不可避的不純物からなる化学成分を有し、
Al母相中に、Mg及びSiを含有する針状粒子が900〜4000個/μm2存在し、
上記Al母相中に存在するFe系粒子は、平均円相当径が5μm以下であり、かつ、2μmを超える円相当径を有する粒子の数が10000個/mm2以下であることを特徴とするバスバー用アルミニウム合金板。 - 170MPa以上の引張強さ及び55%IACS以上の導電率を有することを特徴とする請求項1に記載のバスバー用アルミニウム合金板。
- Mg:0.3〜0.9%(質量%、以下同じ。)、Si:0.2〜1.2%、Cu:0.2%以下、Fe:0.5%以下を含有し、残部がAl及び不可避的不純物からなる化学成分を有する板材を準備し、
該板材に溶体化処理を施した後、
1〜10%の圧下率で上記板材にスキンパスを行い、
その後、上記板材に人工時効処理を施すことを特徴とするバスバー用アルミニウム合金板の製造方法。