JP2015088487A - Composition for lithium secondary battery electrode - Google Patents
Composition for lithium secondary battery electrode Download PDFInfo
- Publication number
- JP2015088487A JP2015088487A JP2014195669A JP2014195669A JP2015088487A JP 2015088487 A JP2015088487 A JP 2015088487A JP 2014195669 A JP2014195669 A JP 2014195669A JP 2014195669 A JP2014195669 A JP 2014195669A JP 2015088487 A JP2015088487 A JP 2015088487A
- Authority
- JP
- Japan
- Prior art keywords
- secondary battery
- lithium secondary
- composition
- polyvinyl acetal
- acetal resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、活物質の分散性、接着性、イオン伝導性に優れ、バインダーの添加量が少ない場合でも高容量のリチウム二次電池を作製することが可能なリチウム二次電池電極用組成物に関する。 The present invention relates to a composition for a lithium secondary battery electrode that is excellent in dispersibility, adhesiveness, and ion conductivity of an active material, and that can produce a high-capacity lithium secondary battery even when the amount of binder added is small. .
近年、携帯型ビデオカメラや携帯型パソコン等の携帯型電子機器の普及に伴い、移動用電源としての二次電池の需要が急増している。また、このような二次電池に対する小型化、軽量化、高エネルギー密度化の要求は非常に高い。
このように、繰り返し充放電が可能な二次電池としては、従来、鉛電池、ニッケル−カドミウム電池等の水溶系電池が主流であるが、これらの水溶系電池は、充放電特性は優れているが、電池重量やエネルギー密度の点では、携帯型電子機器の移動用電源として充分満足できる特性を有しているとはいえない。
In recent years, with the widespread use of portable electronic devices such as portable video cameras and portable personal computers, the demand for secondary batteries as mobile power sources has increased rapidly. In addition, there are very high demands for such secondary batteries to be reduced in size, weight, and energy density.
Thus, as secondary batteries that can be repeatedly charged and discharged, conventionally, water-based batteries such as lead batteries and nickel-cadmium batteries have been mainstream, but these water-based batteries have excellent charge / discharge characteristics. However, in terms of battery weight and energy density, it cannot be said that the battery has sufficient characteristics as a power source for moving portable electronic devices.
そこで、二次電池として、リチウム又はリチウム合金を負極電極に用いたリチウム二次電池の研究開発が盛んに行われている。このリチウム二次電池は、高エネルギー密度を有し、自己放電も少なく、軽量であるという優れた特徴を有している。
リチウム二次電池の電極は、通常、活物質とバインダーを溶媒と共に混練し、活物質を分散させてスラリーとした後、このスラリーをドクターブレード法等によって集電体上に塗布し乾燥して薄膜化することにより形成されている。
Therefore, research and development of lithium secondary batteries using lithium or a lithium alloy as a negative electrode as a secondary battery has been actively conducted. This lithium secondary battery has excellent characteristics such as high energy density, low self-discharge, and light weight.
An electrode of a lithium secondary battery is usually a thin film obtained by kneading an active material and a binder together with a solvent, dispersing the active material into a slurry, applying the slurry on a current collector by a doctor blade method or the like, and drying the slurry. It is formed by forming.
現在、特に、リチウム二次電池の電極（負極）用のバインダーとして最も広範に用いられているのが、ポリフッ化ビニリデン（ＰＶＤＦ）に代表されるフッ素系樹脂である。
しかしながら、フッ素系樹脂をバインダーとして用いた場合、可撓性を有する負極薄膜を作製可能な一方で、集電体と負極活物質の結着性が劣るため、電池製造工程時に負極活物質の一部又は全部が集電体から剥離、脱落する恐れがあった。また、電池の充放電が行われる際、負極活物質内ではリチウムイオンの挿入、放出が繰り返され、それに伴い、集電体から負極活物質の剥離、脱落の問題が起こり得るという問題もあった。
このような問題を解決するため、バインダーを過剰に添加することも試みられているが、それに伴って、負極活物質の添加量が相対的に低下し、電池の容量が低下するという問題が新たに生じていた。
Currently, in particular, fluorine-based resins represented by polyvinylidene fluoride (PVDF) are most widely used as binders for electrodes (negative electrodes) of lithium secondary batteries.
However, when a fluororesin is used as a binder, a flexible negative electrode thin film can be produced, but the binding property between the current collector and the negative electrode active material is inferior. There was a risk that some or all of the part would peel off or fall off from the current collector. In addition, when the battery is charged / discharged, lithium ions are repeatedly inserted and released in the negative electrode active material, and there is a problem that the negative electrode active material may be peeled off or dropped off from the current collector. .
In order to solve such a problem, an attempt has been made to add an excessive amount of a binder. However, along with this, the amount of the negative electrode active material added is relatively reduced, and the problem that the battery capacity is reduced is newly introduced. Had occurred.
これに対して、特許文献１には、正極、負極に使用するバインダーとして、電解液に不溶なポリマーと、電解液に可溶なポリマーとの混合物を用いる技術が開示されている。
しかしながら、このような技術では、電解液に可溶なポリマーを用いることによって、バインダーの電解液への流出が起こり、結局、集電体から負極活物質の剥離、脱落を抑制することはできなかった。
On the other hand, Patent Document 1 discloses a technique using a mixture of a polymer insoluble in an electrolytic solution and a polymer soluble in the electrolytic solution as a binder used for a positive electrode and a negative electrode.
However, in such a technique, by using a polymer that is soluble in the electrolytic solution, the binder flows out to the electrolytic solution, and eventually, peeling and dropping of the negative electrode active material from the current collector cannot be suppressed. It was.
本発明は、活物質の分散性、接着性、イオン伝導性に優れ、バインダーの添加量が少ない場合でも高容量のリチウム二次電池を作製することが可能なリチウム二次電池電極用組成物を提供することを目的とする。 The present invention provides a composition for a lithium secondary battery electrode that is excellent in dispersibility, adhesiveness, and ion conductivity of an active material and that can produce a high-capacity lithium secondary battery even when the amount of binder added is small. The purpose is to provide.
本発明は、活物質、バインダー及び有機溶媒を含有するリチウム二次電池電極用組成物であって、前記バインダーは、ポリビニルアセタール樹脂を含有し、前記ポリビニルアセタール樹脂は、下記式（１）で表される水酸基を有する構成単位、下記式（２）で表されるアセチル基を有する構成単位、下記式（３）で表されるアセタール基を有する構成単位、及び、下記式（４）で表される構成単位を有するリチウム二次電池電極用組成物である。
以下に本発明を詳述する。
The present invention is a composition for a lithium secondary battery electrode containing an active material, a binder, and an organic solvent, wherein the binder contains a polyvinyl acetal resin, and the polyvinyl acetal resin is represented by the following formula (1). The structural unit having a hydroxyl group, the structural unit having an acetyl group represented by the following formula (2), the structural unit having an acetal group represented by the following formula (3), and the following formula (4) It is a composition for lithium secondary battery electrodes which has a structural unit.
The present invention is described in detail below.
本発明者らは、鋭意検討の結果、リチウム二次電池電極形成用のバインダーとして、所定の構成単位を有するポリビニルアセタール樹脂を用いることで、活物質の分散性、接着性、イオン伝導性に優れ、バインダーの添加量が少ない場合でも高容量のリチウム二次電池を作製できることを見出し、本発明を完成させるに至った。 As a result of intensive studies, the present inventors use a polyvinyl acetal resin having a predetermined structural unit as a binder for forming a lithium secondary battery electrode, thereby being excellent in dispersibility, adhesiveness, and ion conductivity of the active material. The inventors have found that a high-capacity lithium secondary battery can be produced even when the amount of binder added is small, and have completed the present invention.
本発明のリチウム二次電池電極用組成物は、活物質を含有する。
本発明のリチウム二次電池電極用組成物は、正極、負極のいずれの電極に使用してもよく、また、正極および負極の両方に使用してもよい。従って、活物質としては、正極活物質、負極活物質がある。
The composition for a lithium secondary battery electrode of the present invention contains an active material.
The composition for a lithium secondary battery electrode of the present invention may be used for either a positive electrode or a negative electrode, or may be used for both a positive electrode and a negative electrode. Accordingly, the active material includes a positive electrode active material and a negative electrode active material.
上記正極活物質としては、リチウムを吸蔵および放出可能な遷移金属元素を含むリチウム含有遷移金属酸化物が好ましい。
上記リチウム含有遷移金属化合物の代表的な例としては、例えば、一般式ＬｉｘＭ１（１−ｙ−ｚ）Ｍ２ｙＭ３ｚＯ２（０．９≦ｘ≦１．１、０≦ｙ≦１．０、０≦ｚ≦１．０、Ｍ１とＭ２とＭ３はＣｏ、Ｎｉ、Ｍｎ、Ｆｅ、Ｔｉ等）が挙げられる。具体的には、ＬｉＣｏＯ２、ＬｉＮｉ１／２Ｍｎ１／２Ｏ２、ＬｉＮｉ１／２Ｃｏ１／２Ｏ２、ＬｉＮｉＯ２、ＬｉＮｉ１／３Ｍｎ１／３Ｃｏ１／３Ｏ２、ＬｉＮｉ１／２Ｆｅ１／２Ｏ２、ＬｉＭｎＯ２等が挙げられる。
また、層状構造のリチウム過剰活物質である一般式Ｌｉ［（Ｎｉ０．５Ｍｎ０．５）ａＣｏｂ（Ｌｉ１／３Ｍｎ１／３）ｃ］Ｏ２（ただし、ａ＋ｂ＋ｃ＝１、ｃ＞０）またはＬｉαＮｉβＭｎγＯ２（αが１．１以上でβ：γ＝１：１）であってもよい。具体的には、Ｌｉ１．２Ｎｉ０．４Ｍｎ０．４Ｏ２、Ｌｉ［（Ｎｉ０．５Ｍｎ０．５）５／１２Ｃｏ１／４（Ｌｉ１／３Ｍｎ２／３）１／３］Ｏ２等が挙げられる。また、スピネル構造、オリビン構造であってもよい。具体的にはＬｉＭｎ２Ｏ４、ＬｉＦｅＰＯ４、ＬｉＣｏＰＯ４、ＬｉＭｎＰＯ４等が挙げられ、Ａｌ等を含んでいてもよい。正極活物質は１種のみを単独で用いてもよく、２種以上を組み合わせて用いてもよい。
As the positive electrode active material, a lithium-containing transition metal oxide containing a transition metal element capable of occluding and releasing lithium is preferable.
As a typical example of the lithium-containing transition metal compound, for example, a general formula Li x M1 (1-yz) M2 y M3 z O 2 (0.9 ≦ x ≦ 1.1, 0 ≦ y ≦ 1) 0.0, 0 ≦ z ≦ 1.0, M1, M2, and M3 include Co, Ni, Mn, Fe, Ti, and the like. Specifically, LiCoO 2 , LiNi 1/2 Mn 1/2 O 2 , LiNi 1/2 Co 1/2 O 2 , LiNiO 2 , LiNi 1/3 Mn 1/3 Co 1/3 O 2 , LiNi 1 / 2 Fe 1/2 O 2, LiMnO 2 , and the like.
Further, a lithium-excess active material having a layered structure is represented by the general formula Li [(Ni 0.5 Mn 0.5 ) a Co b (Li 1/3 Mn 1/3 ) c ] O 2 (where a + b + c = 1, c > 0) or Li α Ni β Mn γ O 2 (α is 1.1 or more and β: γ = 1: 1). Specifically, Li 1.2 Ni 0.4 Mn 0.4 O 2 , Li [(Ni 0.5 Mn 0.5 ) 5/12 Co 1/4 (Li 1/3 Mn 2/3 ) 1 / 3 ] O 2 and the like. Moreover, a spinel structure and an olivine structure may be sufficient. Specifically, LiMn 2 O 4 , LiFePO 4 , LiCoPO 4 , LiMnPO 4, etc. may be mentioned, and Al or the like may be included. Only one type of positive electrode active material may be used alone, or two or more types may be used in combination.
上記負極活物質としては、例えば、従来からリチウム二次電池の負極活物質として用いられている材料を用いることができ、例えば、天然黒鉛（鱗片状黒鉛等）、人造黒鉛等の黒鉛類、アセチレンブラック、ケッチェンブラック、チャンネルブラック、ファーネスブラック、ランプブラック、サーマルブラック等のカーボンブラック類、炭素繊維、金属繊維、合金、リチウム金属、錫化合物、珪化物、および窒化物を用いることができる。これらの材料は、単独で用いてもよいし、２種以上を紹み合わせて用いてもよい。 As the negative electrode active material, for example, a material conventionally used as a negative electrode active material of a lithium secondary battery can be used. For example, natural graphite (such as flake graphite), graphite such as artificial graphite, acetylene, etc. Carbon blacks such as black, ketjen black, channel black, furnace black, lamp black, and thermal black, carbon fibers, metal fibers, alloys, lithium metals, tin compounds, silicides, and nitrides can be used. These materials may be used alone or in combination of two or more.
本発明のリチウム二次電池電極用組成物は、導電付与剤を含有してもよい。
上記導電付与剤としては、例えば、黒鉛、アセチレンブラック、カーボンブラック、ケッチェンブラック、気相成長炭素繊維などの炭素材料が挙げられる。特に、正極用の導電付与剤としては、アセチレンブラック、カーボンブラックが好ましく、負極用の導電付与剤としては、アセチレンブラック、鱗片状黒鉛が好ましい。
The composition for a lithium secondary battery electrode of the present invention may contain a conductivity-imparting agent.
Examples of the conductivity-imparting agent include carbon materials such as graphite, acetylene black, carbon black, ketjen black, and vapor grown carbon fiber. In particular, acetylene black and carbon black are preferable as the conductivity imparting agent for the positive electrode, and acetylene black and scaly graphite are preferable as the conductivity imparting agent for the negative electrode.
本発明のリチウム二次電池電極用組成物は、ポリビニルアセタール樹脂を含有する。本発明では、バインダー（結着剤）としてポリビニルアセタール樹脂を正極用として用いた場合、ポリビニルアセタール樹脂の水酸基と正極活物質の酸素原子間に引力的相互作用が働き、正極活物質をポリビニルアセタール樹脂が取り囲む構造をとる。また、同一分子内の別の水酸基が導電付与剤とも引力的相互作用を及ぼし、活物質、導電付与剤間距離をある一定範囲にとどめることが出来る。このように活物質と導電付与剤を程よい距離に特徴的な構造をとることで、活物質の分散性が大幅に改善される。また、ＰＶＤＦ等の樹脂を用いる場合と比較して、集電体との接着性を向上させることができる。更に、溶剤溶解性に優れ、溶剤の選択の範囲が広がるという利点が得られる。 The composition for a lithium secondary battery electrode of the present invention contains a polyvinyl acetal resin. In the present invention, when a polyvinyl acetal resin is used as a binder (binder) for a positive electrode, an attractive interaction acts between a hydroxyl group of the polyvinyl acetal resin and an oxygen atom of the positive electrode active material, and the positive electrode active material is converted into a polyvinyl acetal resin. Takes a structure that surrounds. Further, another hydroxyl group in the same molecule exerts an attractive interaction with the conductivity-imparting agent, so that the distance between the active material and the conductivity-imparting agent can be kept within a certain range. Thus, the dispersibility of an active material is improved significantly by taking a characteristic structure in a moderate distance between an active material and a conductivity-imparting agent. Moreover, compared with the case where resin, such as PVDF, is used, adhesiveness with a collector can be improved. Furthermore, there is an advantage that the solvent solubility is excellent and the range of solvent selection is widened.
上記ポリビニルアセタール樹脂は、上記式（１）で表される水酸基を有する構成単位、上記式（２）で表されるアセチル基を有する構成単位、上記式（３）で表されるアセタール基を有する構成単位、及び、上記式（４）で表される構成単位を有する。
上記ポリビニルアセタール樹脂は、これらの構成単位を有することで、優れた電解液への耐性、集電体との接着性、またイオン伝導性を有することができ、バインダーの添加量を減らした場合でも高容量のリチウムイオン電池を製造できるという利点がある。
The polyvinyl acetal resin has a structural unit having a hydroxyl group represented by the above formula (1), a structural unit having an acetyl group represented by the above formula (2), and an acetal group represented by the above formula (3). It has a structural unit and a structural unit represented by the above formula (4).
By having these structural units, the polyvinyl acetal resin can have excellent resistance to an electrolytic solution, adhesion with a current collector, and ion conductivity, even when the amount of binder added is reduced. There is an advantage that a high capacity lithium ion battery can be manufactured.
上記ポリビニルアセタール樹脂は、上記式（１）で表される水酸基を有する構成単位を有する。
上記ポリビニルアセタール樹脂における上記式（１）で表される水酸基を有する構成単位の含有量（水酸基量）の好ましい下限は４０モル％、好ましい上限は６５モル％である。上記水酸基量が４０モル％未満であると、電解液に対する耐性が不充分となり、電極を電解液中に浸した際、樹脂成分が電解液中に溶出してしまうことがあり、６５モル％を超えると、工業的に合成が困難であるばかりか、溶液粘度が高くなり、活物質を充分に分散させることが困難となることがある。
上記水酸基量のより好ましい下限は４５モル％であり、より好ましい上限は６０モル％である。
The polyvinyl acetal resin has a structural unit having a hydroxyl group represented by the formula (1).
The minimum with preferable content (hydroxyl group amount) of the structural unit which has a hydroxyl group represented by the said Formula (1) in the said polyvinyl acetal resin is 40 mol%, and a preferable upper limit is 65 mol%. When the amount of the hydroxyl group is less than 40 mol%, the resistance to the electrolytic solution becomes insufficient, and when the electrode is immersed in the electrolytic solution, the resin component may be eluted in the electrolytic solution. If it exceeds, not only industrial synthesis is difficult, but also the solution viscosity becomes high and it may be difficult to sufficiently disperse the active material.
A more preferred lower limit of the hydroxyl group content is 45 mol%, and a more preferred upper limit is 60 mol%.
上記ポリビニルアセタール樹脂は、上記式（２）で表されるアセチル基を有する構成単位を有する。
上記ポリビニルアセタール樹脂における上記式（２）で表されるアセチル基を有する構成単位の含有量（アセチル基量）の好ましい下限は１モル％、好ましい上限は２０モル％である。上記アセチル基量が１モル％未満であると、樹脂の柔軟性が不足し、集電体への接着力が不充分となることがあり、上記アセチル基量が２０モル％を超えると、電解液への耐性が著しく低下し、電解液へ溶出し短絡する原因となることがある。上記アセチル基量のより好ましい下限は３モル％、より好ましい上限は１０モル％である。
The polyvinyl acetal resin has a structural unit having an acetyl group represented by the above formula (2).
The minimum with preferable content (acetyl group amount) of the structural unit which has an acetyl group represented by the said Formula (2) in the said polyvinyl acetal resin is 1 mol%, and a preferable upper limit is 20 mol%. If the amount of acetyl groups is less than 1 mol%, the flexibility of the resin may be insufficient, and the adhesive strength to the current collector may be insufficient. If the amount of acetyl groups exceeds 20 mol%, electrolysis will occur. Resistance to the liquid may be significantly reduced, and it may cause elution into the electrolyte and cause a short circuit. The more preferable lower limit of the acetyl group amount is 3 mol%, and the more preferable upper limit is 10 mol%.
上記ポリビニルアセタール樹脂は、上記式（３）で表されるアセタール基を有する構成単位を有する。
上記ポリビニルアセタール樹脂における上記式（３）で表されるアセタール基を有する構成単位の含有量（アセタール化度）は４０〜６５モル％であることが好ましい。上記アセタール化度が４０モル％未満であると、溶媒への溶解性が低下するため組成物への使用が困難となる。上記アセタール化度が６５モル％を超えると、電解液に対する耐性が不充分となり、電極を電解液中に浸漬した際、樹脂成分が電解液中に溶出してしまうことがある。より好ましくは４５〜６０モル％である。
なお、本明細書において、アセタール化度とは、ポリビニルアルコールの水酸基数のうち、ブチルアルデヒドでアセタール化された水酸基数の割合のことであり、アセタール化度の計算方法としては、ポリビニルアセタール樹脂のアセタール基が２個の水酸基からアセタール化されて形成されていることから、アセタール化された２個の水酸基を数える方法を採用してアセタール化度のモル％を算出する。
The polyvinyl acetal resin has a structural unit having an acetal group represented by the above formula (3).
It is preferable that content (acetalization degree) of the structural unit which has an acetal group represented by the said Formula (3) in the said polyvinyl acetal resin is 40-65 mol%. When the degree of acetalization is less than 40 mol%, the solubility in a solvent is lowered, so that it is difficult to use the composition. When the degree of acetalization exceeds 65 mol%, the resistance to the electrolytic solution becomes insufficient, and the resin component may be eluted in the electrolytic solution when the electrode is immersed in the electrolytic solution. More preferably, it is 45-60 mol%.
In this specification, the degree of acetalization is the ratio of the number of hydroxyl groups acetalized with butyraldehyde in the number of hydroxyl groups of polyvinyl alcohol, and the calculation method of the degree of acetalization is as follows. Since the acetal group is formed by acetalization from two hydroxyl groups, a method of counting the two acetal hydroxyl groups is employed to calculate the mol% of the degree of acetalization.
上記式（３）中、Ｒ１は、水素原子又は炭素数１〜２０のアルキル基であるが、特に、炭素数１のアルキル基、炭素数３のアルキル基であることが好ましい。
上記Ｒ１が、炭素数１のアルキル基、炭素数３のアルキル基であるポリビニルアセタール樹脂は、アセトアルデヒド及びブチルアルデヒドでアセタール化することで得られる。
上記ポリビニルアセタール樹脂は、アセトアルデヒドでアセタール化された部分とブチルアルデヒドでアセタール化された部分との割合が０／１００〜５０／５０であることが好ましい。これにより、ポリビニルアセタール樹脂が柔軟になり、集電体への接着力が良好になる。より好ましくは、アセトアルデヒドでアセタール化された部分とブチルアルデヒドでアセタール化された部分の割合が０／１００〜２０／８０である。
In the above formula (3), R 1 is a hydrogen atom or an alkyl group having 1 to 20 carbon atoms, and particularly preferably an alkyl group having 1 carbon atom or an alkyl group having 3 carbon atoms.
The polyvinyl acetal resin in which R 1 is an alkyl group having 1 carbon atom or an alkyl group having 3 carbon atoms can be obtained by acetalization with acetaldehyde and butyraldehyde.
In the polyvinyl acetal resin, the ratio of the portion acetalized with acetaldehyde and the portion acetalized with butyraldehyde is preferably 0/100 to 50/50. Thereby, a polyvinyl acetal resin becomes flexible and the adhesive force to a collector becomes favorable. More preferably, the ratio of the portion acetalized with acetaldehyde and the portion acetalized with butyraldehyde is 0/100 to 20/80.
上記ポリビニルアセタール樹脂は、下記式（４）で表される構成単位を有する。
下記式（４）で表される構成単位を有することで、エチレンオキサイド基の酸素原子が効率的にリチウムイオンと配位し、効率的にリチウムイオンの流れを形成することが出来る。そのためポリビニルアセタール樹脂はイオン伝導性を有することができ、リチウムイオン電池の高容量化が可能に出来るという利点がある。
このイオン伝導性を高めるにはリチウムと更に、下記式（４）で表される構成単位は嵩高い構造をしており、分子間距離が拡がることでガラス転移点が下がり、柔軟な特性を持つようになるため、集電体への接着力が著しく向上するという利点もある。
The said polyvinyl acetal resin has a structural unit represented by following formula (4).
By having the structural unit represented by the following formula (4), the oxygen atom of the ethylene oxide group can efficiently coordinate with the lithium ion, and the flow of the lithium ion can be efficiently formed. Therefore, the polyvinyl acetal resin can have ion conductivity and has an advantage that the capacity of the lithium ion battery can be increased.
In order to increase the ion conductivity, lithium and the structural unit represented by the following formula (4) have a bulky structure, and the glass transition point is lowered and the flexibility is increased by increasing the intermolecular distance. Therefore, there is also an advantage that the adhesive force to the current collector is remarkably improved.
上記式（４）で表される構成単位としては、例えば、ポリエチレングリコール等の複数のエチレンオキサイド基を構成単位内に有するもの、またエチレングリコール単位を単独で構成単位内に有するもの、また非連続的に複数個のエチレングリコール単位やポリエチレングリコール単位に有するもの等が挙げられる。
上記式（４）で表される構成単位は、下記式（５）で表されるエチレンオキサイド基を有する構成単位であることが好ましい。上記エチレンオキサイド基を有することで、エチレンオキサイド基の酸素原子とリチウムイオンが効率的に配位し、高いイオン伝導性を有することが出来るという利点がある。
なお、上記イオン伝導性をより高めるためには、ポリビニルアセタール樹脂と活物質の重量比（ポリビニルアセタール樹脂の重量／活物質の重量）が、０．００２〜０．２であることが好ましい。上記範囲内にあることで、活物質表面に吸着するポリビニルアセタール樹脂層が厚くなりすぎず、また活物質中のリチウムイオン原子と、ポリビニルアセタール樹脂中のエチレンオキサイド中の酸素原子が効率よく配意することが出来る比率となり、イオン伝導性を高めることが可能になる。
Examples of the structural unit represented by the above formula (4) include those having a plurality of ethylene oxide groups such as polyethylene glycol in the structural unit, those having an ethylene glycol unit alone in the structural unit, and discontinuous. In particular, those having a plurality of ethylene glycol units or polyethylene glycol units may be mentioned.
The structural unit represented by the above formula (4) is preferably a structural unit having an ethylene oxide group represented by the following formula (5). By having the ethylene oxide group, there is an advantage that the oxygen atom of the ethylene oxide group and lithium ions can be coordinated efficiently and have high ionic conductivity.
In order to further enhance the ion conductivity, the weight ratio of the polyvinyl acetal resin to the active material (the weight of the polyvinyl acetal resin / the weight of the active material) is preferably 0.002 to 0.2. By being in the above range, the polyvinyl acetal resin layer adsorbed on the active material surface does not become too thick, and the lithium ion atoms in the active material and the oxygen atoms in ethylene oxide in the polyvinyl acetal resin are efficiently provided. Therefore, the ionic conductivity can be increased.
上記Ｒ３は、Ｃ、Ｈ及びＯからなる群より選択される少なくとも１種を有する連結基又は単結合である。上記Ｒ３は炭素数が１〜１０のアルキレン基、もしくはカルボニル基が好ましい。上記Ｒ３の炭素数が上記範囲内であることで、エチレンオキサイド構成単位が主鎖から大きく離れることがなく、水酸基とエチレンオキサイド単位の酸素原子が相互作用を及ぼすため、効果的にエチレンオキサイドが拡がることが出来る。上記範囲を外れるとエチレンオキサイド間の相互作用が強く働き、エチレンオキサイド単位が拡がることが出来ず、効率よくイオン伝導性を高めることが出来ない。上記Ｒ３としては、例えば、メチレン基、エチレン基、カルボニル基、エーテル基等が挙げられる。また、上記Ｒ３は単結合であってもよい。上記Ｒ４は、Ｃ、Ｈ及びＯからなる群より選択される少なくとも１種を有する連結基又は単結合である。上記Ｒ４は炭素数が１〜１０のアルキレン基、もしくはカルボニル基が好ましい。上記Ｒ４としては、例えば、メチレン基、エチレン基、プロピレン基、カルボニル基、エーテル基等が挙げられる。また、上記Ｒ４は単結合であってもよい。
更に、エチレンオキサイドの繰り返し数である整数ｎは特に限定されないが、２〜５０が好ましく、５〜２０がより好ましい。エチレンオキサイドの繰り返し数が上記範囲内であることで、単一分子内でリチウムイオンを保持できなくなるため、効率よくリチウムイオンを伝導することが可能となる。
R 3 is a linking group or a single bond having at least one selected from the group consisting of C, H and O. R 3 is preferably an alkylene group having 1 to 10 carbon atoms or a carbonyl group. When the number of carbon atoms of R 3 is within the above range, the ethylene oxide structural unit is not greatly separated from the main chain, and the hydroxyl group and the oxygen atom of the ethylene oxide unit interact with each other. It can be expanded. If it is out of the above range, the interaction between ethylene oxide works strongly, the ethylene oxide unit cannot be expanded, and the ionic conductivity cannot be increased efficiently. Examples of R 3 include a methylene group, an ethylene group, a carbonyl group, and an ether group. R 3 may be a single bond. R 4 is a linking group or a single bond having at least one selected from the group consisting of C, H and O. R 4 is preferably an alkylene group having 1 to 10 carbon atoms or a carbonyl group. Examples of R 4 include a methylene group, an ethylene group, a propylene group, a carbonyl group, and an ether group. R 4 may be a single bond.
Furthermore, although the integer n which is the repeating number of ethylene oxide is not specifically limited, 2-50 are preferable and 5-20 are more preferable. When the number of ethylene oxide repeats is within the above range, lithium ions cannot be held in a single molecule, and thus lithium ions can be efficiently conducted.
上記ポリビニルアセタール樹脂における上記式（４）で表される構成単位の含有量の好ましい下限は１モル％、好ましい上限は２０モル％である。上記含有量が１モル％未満であると、充分なイオン伝導性が得られないことがあり、上記含有量が２０モル％を超えると、電解液への耐性を保持することが困難になることがある。上記含有量のより好ましい下限は３モル％、より好ましい上限は１０モル％である。 The minimum with preferable content of the structural unit represented by the said Formula (4) in the said polyvinyl acetal resin is 1 mol%, and a preferable upper limit is 20 mol%. If the content is less than 1 mol%, sufficient ion conductivity may not be obtained, and if the content exceeds 20 mol%, it may be difficult to maintain resistance to the electrolytic solution. There is. The more preferable lower limit of the content is 3 mol%, and the more preferable upper limit is 10 mol%.
上記ポリビニルアセタール樹脂における上記式（１）で表される水酸基を有する構成単位の含有量と、上記式（４）で表される構成単位の含有量のモル％比［式（４）/式（１）比］は０．０１〜０．５であることが好ましい。上記範囲内とすることで、エチレンオキサイドが自由に動くことが出来、効率よくリチウムイオンを伝導することができる。
上記式（４）/式（１）比が０．０１未満であると、エチレンオキサイドの酸素原子と水酸基の相互作用が強く働き過ぎてしまい、上記式（４）で表される構成単位が自由に動くことが出来ずリチウムイオンと効率的に配位することができない。また、上記式（４）/式（１）比が０．５を超えると、上記式（４）で表される構成単位の酸素原子間の相互作用が強く働き過ぎでしまい、リチウムイオンと効率的に配意することが出来ないため、充分なイオン伝導性が得られないことがある。上記式（４）/式（１）比は、０．０２〜０．４であることがより好ましい。
The mol% ratio of the content of the structural unit having a hydroxyl group represented by the formula (1) in the polyvinyl acetal resin and the content of the structural unit represented by the formula (4) [formula (4) / formula ( 1) Ratio] is preferably 0.01 to 0.5. By setting it within the above range, ethylene oxide can freely move and lithium ions can be efficiently conducted.
When the ratio of the above formula (4) / formula (1) is less than 0.01, the interaction between the oxygen atom and the hydroxyl group of ethylene oxide is too strong and the structural unit represented by the above formula (4) is free. Cannot move efficiently with lithium ions. Moreover, when the ratio of the above formula (4) / formula (1) exceeds 0.5, the interaction between the oxygen atoms of the structural unit represented by the above formula (4) works too strongly, and the lithium ion and the efficiency In some cases, sufficient ionic conductivity may not be obtained. The ratio of the above formula (4) / formula (1) is more preferably 0.02 to 0.4.
上記ポリビニルアセタール樹脂の重合度の好ましい下限は２５０、好ましい上限は４０００である。上記重合度が２５０未満であると、工業的に入手が難しくなることがある。上記重合度が４０００を超えると、溶液粘度が高くなり、活物質を充分に分散させることが困難となることがある。上記重合度のより好ましい下限は２８０、より好ましい上限は８００である。 The minimum with a preferable polymerization degree of the said polyvinyl acetal resin is 250, and a preferable upper limit is 4000. If the degree of polymerization is less than 250, it may be difficult to obtain industrially. When the polymerization degree exceeds 4000, the solution viscosity becomes high and it may be difficult to sufficiently disperse the active material. The more preferable lower limit of the degree of polymerization is 280, and the more preferable upper limit is 800.
上記ポリビニルアセタール樹脂は、アニオン性基を有することが好ましい。
上記アニオン性基を有することで、ポリビニルアセタール樹脂が活物質の表面に付着しやすくなり、活物質の分散性を高めることができる。
The polyvinyl acetal resin preferably has an anionic group.
By having the anionic group, the polyvinyl acetal resin easily adheres to the surface of the active material, and the dispersibility of the active material can be improved.
本発明のリチウム二次電池電極用組成物中の上記ポリビニルアセタール樹脂の含有量は特に限定されないが、好ましい下限は０．２重量％、好ましい上限は５重量％である。上記ポリビニルアセタール樹脂の含有量が０．２重量％未満であると、集電体への接着力が不足してしまうことがあり、５重量％を超えると、リチウム二次電池の放電容量が低下してしまうことがある。より好ましくは、０．５〜３重量％である。 Although content of the said polyvinyl acetal resin in the composition for lithium secondary battery electrodes of this invention is not specifically limited, A preferable minimum is 0.2 weight% and a preferable upper limit is 5 weight%. When the content of the polyvinyl acetal resin is less than 0.2% by weight, the adhesive force to the current collector may be insufficient. When the content exceeds 5% by weight, the discharge capacity of the lithium secondary battery decreases. May end up. More preferably, it is 0.5 to 3% by weight.
上記ポリビニルアセタール樹脂は、ポリビニルアルコールをアルデヒドでアセタール化してなるものである。
特に、上記ポリビニルアセタール樹脂を製造する方法としては、上記式（４）で表される構成単位を予め有するポリビニルアルコールを用意し、その後アセタール化する方法、上記式（４）で表される構成単位を有しないポリビニルアルコールをアセタール化した後、上記式（４）で表される構成単位のＲ２に相当する部分を付加する方法等が挙げられる。
The polyvinyl acetal resin is obtained by acetalizing polyvinyl alcohol with an aldehyde.
In particular, as a method for producing the polyvinyl acetal resin, a method of preparing polyvinyl alcohol having a structural unit represented by the above formula (4) in advance and then acetalizing it, a structural unit represented by the above formula (4) And a method of adding a portion corresponding to R 2 of the structural unit represented by the above formula (4) after acetalizing polyvinyl alcohol having no benzene.
上記式（４）で表される構成単位を有するポリビニルアルコールを作製する方法としては、例えば、オキシアルキレン基を含有するヒドロキシアルキルビニルエーテルと酢酸ビニルとを共重合した後、得られた共重合体のアルコール溶液に酸またはアルカリを添加してケン化する方法等が挙げられる。また、上記ヒドロキシアルキルビニルエーテルのほか、ジエチレングリコールビニルエーテル、トリエチレングリコールモノビニルエーテル等のポリ（エチレングリコール）ビニルエーテルを使用してもよい。
また、上記式（４）で表される構成単位のＲ２に相当する部分を付加する方法としては、例えば、上記アルキルビニルエーテルの種類を変更する方法等が挙げられる。
As a method for producing polyvinyl alcohol having the structural unit represented by the above formula (4), for example, after copolymerizing hydroxyalkyl vinyl ether containing oxyalkylene group and vinyl acetate, Examples thereof include a method for saponifying an alcohol solution by adding an acid or an alkali. In addition to the above hydroxyalkyl vinyl ether, poly (ethylene glycol) vinyl ethers such as diethylene glycol vinyl ether and triethylene glycol monovinyl ether may be used.
Moreover, as a method of adding the part corresponding to R 2 of the structural unit represented by the above formula (4), for example, a method of changing the kind of the alkyl vinyl ether can be mentioned.
上記式（４）で表される構成単位を有しないポリビニルアルコール（以下、単にポリビニルアルコールともいう）は、例えば、ビニルエステルとエチレンの共重合体をケン化することにより得ることができる。上記ビニルエステルとしては、例えば、蟻酸ビニル、酢酸ビニル、プロピオン酸ビニル、ピバリン酸ビニル等が挙げられる。なかでも、経済性の観点から酢酸ビニルが好適である。 Polyvinyl alcohol not having the structural unit represented by the above formula (4) (hereinafter also simply referred to as polyvinyl alcohol) can be obtained, for example, by saponifying a copolymer of vinyl ester and ethylene. Examples of the vinyl ester include vinyl formate, vinyl acetate, vinyl propionate, vinyl pivalate and the like. Of these, vinyl acetate is preferred from the viewpoint of economy.
上記ポリビニルアルコールは、本発明の効果を損なわない範囲で、エチレン性不飽和単量体を共重合したものであってもよい。上記エチレン性不飽和単量体としては特に限定されず、例えば、アクリル酸、メタクリル酸、（無水）フタル酸、（無水）マレイン酸、（無水）イタコン酸、アクリロニトリルメタクリロニトリル、アクリルアミド、メタクリルアミド、トリメチル−（３−アクリルアミド−３−ジメチルプロピル）−アンモニウムクロリド、アクリルアミド−２−メチルプロパンスルホン酸、及びそのナトリウム塩、エチルビニルエーテル、ブチルビニルエーテル、Ｎ−ビニルピロリドン、塩化ビニル、臭化ビニル、フッ化ビニル、塩化ビニリデン、フッ化ビニリデン、テトラフルオロエチレン、ビニルスルホン酸ナトリウム、アリルスルホン酸ナトリウム等が挙げられる。また、チオール酢酸、メルカプトプロピオン酸等のチオール化合物の存在下で、酢酸ビニル等のビニルエステル系単量体とエチレンを共重合し、それをケン化することによって得られる末端変性ポリビニルアルコールも用いることができる。 The polyvinyl alcohol may be a copolymer of an ethylenically unsaturated monomer as long as the effects of the present invention are not impaired. The ethylenically unsaturated monomer is not particularly limited, and examples thereof include acrylic acid, methacrylic acid, (anhydrous) phthalic acid, (anhydrous) maleic acid, (anhydrous) itaconic acid, acrylonitrile methacrylonitrile, acrylamide, and methacrylamide. , Trimethyl- (3-acrylamido-3-dimethylpropyl) -ammonium chloride, acrylamido-2-methylpropanesulfonic acid and its sodium salt, ethyl vinyl ether, butyl vinyl ether, N-vinyl pyrrolidone, vinyl chloride, vinyl bromide, fluorine Vinyl chloride, vinylidene chloride, vinylidene fluoride, tetrafluoroethylene, sodium vinyl sulfonate, sodium allyl sulfonate and the like. Also use terminal-modified polyvinyl alcohol obtained by copolymerizing vinyl ester monomer such as vinyl acetate with ethylene in the presence of thiol compounds such as thiol acetic acid and mercaptopropionic acid, and saponifying it. Can do.
上記ポリビニルアルコールは、上記ビニルエステルとα−オレフィンとを共重合した共重合体をケン化したものであってもよい。また、更に上記エチレン性不飽和単量体を共重合させ、エチレン性不飽和単量体に由来する成分を含有するポリビニルアルコールとしてもよい。また、チオール酢酸、メルカプトプロピオン酸等のチオール化合物の存在下で、酢酸ビニル等のビニルエステル系単量体とα−オレフィンを共重合し、それをケン化することによって得られる末端ポリビニルアルコールも用いることができる。上記α−オレフィンとしては特に限定されず、例えば、メチレン、エチレン、プロピレン、イソプロピレン、ブチレン、イソブチレン、ペンチレン、へキシレン、シクロヘキシレン、シクロヘキシルエチレン、シクロヘキシルプロピレン等が挙げられる。 The polyvinyl alcohol may be a saponified copolymer obtained by copolymerizing the vinyl ester and an α-olefin. Furthermore, it is good also as polyvinyl alcohol which copolymerizes the said ethylenically unsaturated monomer and contains the component originating in an ethylenically unsaturated monomer. Also used is a terminal polyvinyl alcohol obtained by copolymerizing a vinyl ester monomer such as vinyl acetate with an α-olefin in the presence of a thiol compound such as thiol acetic acid or mercaptopropionic acid, and saponifying it. be able to. The α-olefin is not particularly limited, and examples thereof include methylene, ethylene, propylene, isopropylene, butylene, isobutylene, pentylene, hexylene, cyclohexylene, cyclohexylethylene, and cyclohexylpropylene.
本発明のリチウム二次電池電極用組成物は、上記ポリビニルアセタール樹脂に加えて、ポリフッ化ビニリデン樹脂を含有していてもよい。
上記ポリフッ化ビニリデン樹脂を併用することで、電解液への耐性が更に向上し、放電容量を向上させることが出来る。
In addition to the said polyvinyl acetal resin, the composition for lithium secondary battery electrodes of this invention may contain the polyvinylidene fluoride resin.
By using the polyvinylidene fluoride resin in combination, the resistance to the electrolytic solution can be further improved, and the discharge capacity can be improved.
上記ポリフッ化ビニリデン樹脂を含有する場合、上記ポリビニルアセタール樹脂とポリフッ化ビニリデン樹脂との重量比は、０．５：９．５〜７：３であることが好ましい。
このような範囲内とすることで、ポリフッ化ビニリデンに著しく不足している集電体への接着力を有しながら、電解液への耐性を付与することが出来る。
より好ましい上記ポリビニルアセタール樹脂とポリフッ化ビニリデン樹脂との重量比は１：９〜４：６である。
When the polyvinylidene fluoride resin is contained, the weight ratio of the polyvinyl acetal resin to the polyvinylidene fluoride resin is preferably 0.5: 9.5 to 7: 3.
By setting it within such a range, it is possible to impart resistance to the electrolytic solution while having adhesive force to the current collector that is significantly insufficient for polyvinylidene fluoride.
A more preferred weight ratio of the polyvinyl acetal resin to the polyvinylidene fluoride resin is 1: 9 to 4: 6.
本発明のリチウム二次電池電極用組成物中のバインダー全体の含有量は特に限定されないが、好ましい下限は１重量％、好ましい上限は２０重量％である。上記バインダーの含有量が１重量％未満であると、集電体への接着力が不足してしまうことがあり、２０重量％を超えると、リチウム二次電池の放電容量が低下してしまうことがある。 Although content of the whole binder in the composition for lithium secondary battery electrodes of this invention is not specifically limited, A preferable minimum is 1 weight% and a preferable upper limit is 20 weight%. If the content of the binder is less than 1% by weight, the adhesive force to the current collector may be insufficient, and if it exceeds 20% by weight, the discharge capacity of the lithium secondary battery may be reduced. There is.
本発明のリチウム二次電池電極用組成物は、有機溶媒を含有する。
上記有機溶媒としては、上記ポリビニルアセタール樹脂を溶解させることができるものであれば特に限定されず、例えば、シクロヘキサノン、メチルエチルケトン、メチルイソブチルケトン、テトラヒドロフラン、トルエン、イソプロピルアルコール、Ｎ−メチルピロリドン、エタノール、蒸留水等が挙げられる。なかでも、Ｎ−メチルピロリドンが好ましい。
上記有機溶媒は単独で用いてもよく、２種以上を併用してもよい。
The composition for a lithium secondary battery electrode of the present invention contains an organic solvent.
The organic solvent is not particularly limited as long as it can dissolve the polyvinyl acetal resin. For example, cyclohexanone, methyl ethyl ketone, methyl isobutyl ketone, tetrahydrofuran, toluene, isopropyl alcohol, N-methylpyrrolidone, ethanol, distillation Water etc. are mentioned. Of these, N-methylpyrrolidone is preferable.
The said organic solvent may be used independently and may use 2 or more types together.
本発明のリチウム二次電池電極用組成物中の有機溶媒の含有量は特に限定されないが、好ましい下限は２０重量％、好ましい上限は５０重量％である。上記有機溶媒の含有量が２０重量％未満であると、粘度が高いため、ペーストの塗工が困難になることがあり、５０重量％を超えると、溶剤乾燥時にムラができてしまうことがある。より好ましい下限は２５重量％、より好ましい上限は４０重量％である。 Although content of the organic solvent in the composition for lithium secondary battery electrodes of this invention is not specifically limited, A preferable minimum is 20 weight% and a preferable upper limit is 50 weight%. If the content of the organic solvent is less than 20% by weight, the viscosity may be high, so that paste coating may be difficult. If the content exceeds 50% by weight, unevenness may occur when the solvent is dried. . A more preferred lower limit is 25% by weight, and a more preferred upper limit is 40% by weight.
本発明のリチウム二次電池電極用組成物には、上述した活物質、ポリビニルアセタール樹脂、溶媒以外にも、必要に応じて、難燃助剤、増粘剤、消泡剤、レベリング剤、密着性付与剤のような添加剤を添加してもよい。 In addition to the above-described active material, polyvinyl acetal resin, and solvent, the composition for a lithium secondary battery electrode of the present invention includes a flame retardant aid, a thickener, an antifoaming agent, a leveling agent, and an adhesion as necessary. An additive such as a property-imparting agent may be added.
本発明のリチウム二次電池電極用組成物を製造する方法としては、特に限定されず、例えば、上記活物質、ポリビニルアセタール樹脂、溶媒及び必要に応じて添加する各種添加剤をボールミル、ブレンダーミル、３本ロール等の各種混合機を用いて混合する方法が挙げられる。 The method for producing the composition for a lithium secondary battery electrode of the present invention is not particularly limited. For example, the active material, the polyvinyl acetal resin, the solvent, and various additives to be added as necessary may be a ball mill, a blender mill, The method of mixing using various mixers, such as a 3 roll, is mentioned.
本発明のリチウム二次電池電極用組成物は、例えば、導電性基体上に塗布し、乾燥する工程を経ることで、電極が形成される。
本発明のリチウム二次電池電極用組成物を用いてなるリチウム二次電池もまた本発明の一つである。
本発明のリチウム二次電池電極用組成物を導電性基体に塗布する際の塗布方法としては、例えば、押出しコーター、リバースローラー、ドクターブレード、アプリケーターなどをはじめ、各種の塗布方法を採用することができる。
The electrode for lithium secondary battery electrode composition of the present invention is formed, for example, through a process of coating on a conductive substrate and drying.
A lithium secondary battery using the composition for a lithium secondary battery electrode of the present invention is also one aspect of the present invention.
As a coating method when the composition for a lithium secondary battery electrode of the present invention is applied to a conductive substrate, various coating methods such as an extrusion coater, a reverse roller, a doctor blade, an applicator and the like can be adopted. it can.
本発明によれば、活物質の分散性、接着性、イオン伝導性に優れ、バインダーの添加量が少ない場合でも高容量のリチウム二次電池を作製することが可能なリチウム二次電池電極用組成物を提供できる。 ADVANTAGE OF THE INVENTION According to this invention, the composition for lithium secondary battery electrodes which is excellent in the dispersibility of an active material, adhesiveness, and ionic conductivity, and can produce a high capacity | capacitance lithium secondary battery even when there is little addition amount of a binder. Can provide things.
以下に実施例を掲げて本発明を更に詳しく説明するが、本発明はこれら実施例のみに限定されるものではない。 Hereinafter, the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these examples.
（ポリビニルアルコール（ａ）〜（ｊ）の合成）
攪拌機、温度計、滴下ロートおよび還流冷却器を付したフラスコ中に、酢酸ビニル１０００重量部、式（５）で表される化学式のＲ３がエチレン基であり、ｎ＝１０であるポリ（オキシエチレン）ビニルエーテル３２０重量部及びメタノール３００重量部を添加し、系内の窒素置換を行った後、温度を６０℃まで昇温した。この系に２，２−アゾビスイソブチロニトリル１．１重量部を添加し、重合を開始した。重合開始から５時間で重合を停止した。重合停止時の系内の固形分濃度は５３重量％であり、全モノマーに対する重合収率は６５重量％であった。減圧下に未反応のモノマーを除去した後、共重合体の４５重量％メタノール溶液を得た。得られた共重合体は酢酸ビニル単位９４モル％、エチレンオキサイドを含有するアルキルビニルエーテル単位６モル％を含有することが未反応のモノマーの定量より確認された。
(Synthesis of polyvinyl alcohol (a) to (j))
In a flask equipped with a stirrer, a thermometer, a dropping funnel and a reflux condenser, 1000 parts by weight of vinyl acetate, R 3 of the chemical formula represented by the formula (5) is an ethylene group, and n = 10 After adding 320 parts by weight of ethylene) vinyl ether and 300 parts by weight of methanol and performing nitrogen substitution in the system, the temperature was raised to 60 ° C. To this system, 1.1 parts by weight of 2,2-azobisisobutyronitrile was added to initiate polymerization. The polymerization was stopped in 5 hours from the start of polymerization. When the polymerization was stopped, the solid content concentration in the system was 53% by weight, and the polymerization yield based on all monomers was 65% by weight. After removing unreacted monomers under reduced pressure, a 45 wt% methanol solution of the copolymer was obtained. It was confirmed by quantitative determination of unreacted monomers that the obtained copolymer contained 94 mol% of vinyl acetate units and 6 mol% of alkyl vinyl ether units containing ethylene oxide.
この共重合体のメタノール溶液１００重量部を４０℃で攪拌しながら、３％のＮａＯＨメタノール溶液２５重量部を添加して、よく混合した後に放置した。３０分後、固化したポリマーを粉砕機で粉砕し、メタノールで洗浄後、乾燥してポリマー粉末を得た（以下、これをポリビニルアルコール（ａ）と称する）。
ポリビニルアルコール（ａ）のケン化度は９９モル％、重合度は１２００であった。
また表１に記載した以外は、ポリビニルアルコール（ａ）と同様にしてポリビニルアルコール（ｂ）〜（ｊ）を得た。
While stirring 100 parts by weight of the methanol solution of the copolymer at 40 ° C., 25 parts by weight of 3% NaOH methanol solution was added and mixed well, and then allowed to stand. After 30 minutes, the solidified polymer was pulverized with a pulverizer, washed with methanol, and dried to obtain a polymer powder (hereinafter referred to as polyvinyl alcohol (a)).
Polyvinyl alcohol (a) had a saponification degree of 99 mol% and a polymerization degree of 1200.
Moreover, polyvinyl alcohol (b)-(j) was obtained like polyvinyl alcohol (a) except having described in Table 1.
（ポリビニルアセタール樹脂（Ａ）〜（Ｊ）の合成）
ポリビニルアルコール（ａ）３５０重量部を純水３０００重量部に加え、９０℃の温度で約２時間攪拌し溶解させた。この溶液を４０℃に冷却し、これに濃度３５重量％の塩酸２３０重量部を添加した後、液温を２０℃に下げてｎ−ブチルアルデヒド１５５重量部を添加しこの温度を保持してアセタール化反応を行い、反応生成物を析出させた。その後、液温を５０℃、３時間保持して反応を完了させ、常法により中和、水洗及び乾燥を経て、ポリビニルアセタール樹脂の白色粉末を得た。得られたポリビニルアセタール樹脂をＤＭＳＯ−ｄ６（ジメチルスルホキサシド）に溶解し、１３Ｃ−ＮＭＲ（核磁気共鳴スペクトル）を用いて上記式（１）で表される構成単位の含有量［水酸基量］、上記式（２）で表される構成単位の含有量［アセチル基量］、上記式（３）で表される構成単位の含有量［アセタール化度］、及び、上記式（４）で表される構成単位の含有量［式（４）単位量］を測定したところ、水酸基量は５０モル％、アセチル基量は１モル％、アセタール化度（ブチラール化度）は４４モル％、式（４）単位量は５モル％であった。
なお、上記式（４）で表される構成単位は、上記式（５）で表される構造（Ｒ３＝エチレン基、ｎ＝１０）であった。
また、表２に示す条件（使用ポリビニルアルコール、ｎ−ブチルアルデヒド使用量）とした以外は、ポリビニルアセタール樹脂（Ａ）と同様にして、ポリビニルアセタール樹脂（Ｂ）〜（Ｊ）を合成した。
(Synthesis of polyvinyl acetal resins (A) to (J))
350 parts by weight of polyvinyl alcohol (a) was added to 3000 parts by weight of pure water, and stirred at a temperature of 90 ° C. for about 2 hours for dissolution. The solution was cooled to 40 ° C., and 230 parts by weight of hydrochloric acid having a concentration of 35% by weight was added thereto, the liquid temperature was lowered to 20 ° C., and 155 parts by weight of n-butyraldehyde was added to maintain the temperature, and the acetal was maintained. The reaction product was precipitated by the reaction. Thereafter, the liquid temperature was maintained at 50 ° C. for 3 hours to complete the reaction, and neutralized, washed with water and dried by a conventional method to obtain a white powder of polyvinyl acetal resin. The obtained polyvinyl acetal resin is dissolved in DMSO-d 6 (dimethylsulfoxaside), and the content of the structural unit represented by the above formula (1) using 13 C-NMR (nuclear magnetic resonance spectrum) [hydroxyl group] Amount], the content of the structural unit represented by the above formula (2) [acetyl group amount], the content of the structural unit represented by the above formula (3) [degree of acetalization], and the above formula (4). When the content of the structural unit represented by the formula (4), the amount of hydroxyl groups is 50 mol%, the amount of acetyl groups is 1 mol%, the degree of acetalization (degree of butyralization) is 44 mol%, The unit amount of the formula (4) was 5 mol%.
The structural unit represented by the above formula (4) was a structure represented by the above formula (5) (R 3 = ethylene group, n = 10).
Moreover, polyvinyl acetal resin (B)-(J) was synthesize | combined like polyvinyl acetal resin (A) except having set it as the conditions shown in Table 2 (use polyvinyl alcohol, n-butyraldehyde usage-amount).
（実施例１）
（リチウム二次電池正極用組成物の調製）
バインダーとして得られたポリビニルアセタール樹脂（Ａ）１０重量部に、Ｎ−メチルピロリドン９０重量部を加えて、ポリビニルアセタール樹脂の１０重量％溶液を調製した。この溶液３２．５重量部に対して、正極活物質としてマンガン酸リチウム（日本化学工業社製、セルシードＣ−５Ｈ）５５重量部、導電付与剤としてアセチレンブラック（電気化学工業社製、デンカブラック）を６．５重量部、溶媒としてＮ−メチルピロリドン６重量部を加えて混合し、リチウム二次電池正極用組成物を得た。
Example 1
(Preparation of composition for positive electrode of lithium secondary battery)
90 parts by weight of N-methylpyrrolidone was added to 10 parts by weight of the polyvinyl acetal resin (A) obtained as a binder to prepare a 10% by weight solution of the polyvinyl acetal resin. With respect to 32.5 parts by weight of this solution, 55 parts by weight of lithium manganate (manufactured by Nippon Chemical Industry Co., Ltd., Cell Seed C-5H) as the positive electrode active material, and acetylene black (manufactured by Denki Kagaku Kogyo Co., Ltd., Denka Black) Was added and mixed with 6 parts by weight of N-methylpyrrolidone as a solvent to obtain a composition for a positive electrode of a lithium secondary battery.
（実施例２〜９）
表３に示すポリビニルアセタール樹脂を用い、Ｎ−メチルピロリドンの添加量を変更した以外は実施例１と同様にして、リチウム二次電池正極用組成物を得た。
(Examples 2-9)
A composition for a positive electrode of a lithium secondary battery was obtained in the same manner as in Example 1 except that the polyvinyl acetal resin shown in Table 3 was used and the addition amount of N-methylpyrrolidone was changed.
（実施例１０）
（リチウム二次電池負極用組成物の調製）
バインダーとして得られたポリビニルアセタール樹脂（Ａ）４重量部に、Ｎ−メチルピロリドン９６重量部を加えて、ポリビニルアセタール樹脂の４重量％溶液を調製した。この溶液１００重量部に対して、負極活物質として球状天然黒鉛（日本黒鉛工業社製、ＣＧＢ−１０）４３重量部を加えて混合し、リチウム二次電池負極用組成物を得た。
(Example 10)
(Preparation of composition for negative electrode of lithium secondary battery)
96 parts by weight of N-methylpyrrolidone was added to 4 parts by weight of the polyvinyl acetal resin (A) obtained as a binder to prepare a 4% by weight solution of the polyvinyl acetal resin. With respect to 100 parts by weight of this solution, 43 parts by weight of spherical natural graphite (manufactured by Nippon Graphite Industry Co., Ltd., CGB-10) as a negative electrode active material was added and mixed to obtain a composition for a negative electrode of a lithium secondary battery.
（実施例１１〜１７）
表３に示すポリビニルアセタール樹脂を用い、Ｎ−メチルピロリドンの添加量を変更した以外は実施例１０と同様にして、リチウム二次電池負極用組成物を得た。
(Examples 11 to 17)
A composition for a lithium secondary battery negative electrode was obtained in the same manner as in Example 10 except that the polyvinyl acetal resin shown in Table 3 was used and the addition amount of N-methylpyrrolidone was changed.
（実施例１８）
負極活物質として球状天然黒鉛（日本黒鉛工業社製、ＣＧＢ−１０）４３重量部に代えて、人造グラファイト（日本黒鉛工業社製、ＰＡＧ−５）４３重量部を使用し、表３に示すポリビニルアセタール樹脂を用い、Ｎ−メチルピロリドンの添加量を変更した以外は実施例１０と同様にして、リチウム二次電池負極用組成物を得た。
(Example 18)
Polyvinyl chloride shown in Table 3 was used instead of 43 parts by weight of spherical natural graphite (manufactured by Nippon Graphite Industry Co., Ltd., CGB-10) as a negative electrode active material, and 43 parts by weight of artificial graphite (manufactured by Nippon Graphite Industry Co., Ltd., PAG-5). A composition for a negative electrode of a lithium secondary battery was obtained in the same manner as in Example 10 except that the amount of N-methylpyrrolidone was changed using an acetal resin.
（比較例１〜３）
表３に示すポリビニルアセタール樹脂を用い、Ｎ−メチルピロリドンの添加量を変更した以外は実施例１と同様にして、リチウム二次電池正極用組成物を得た。
(Comparative Examples 1-3)
A composition for a positive electrode of a lithium secondary battery was obtained in the same manner as in Example 1 except that the polyvinyl acetal resin shown in Table 3 was used and the addition amount of N-methylpyrrolidone was changed.
（比較例４）
ポリビニルアセタール樹脂（Ａ）に代えて、ポリフッ化ビニリデン（ＰＶＤＦ、クレハ社製、＃１１００）を用いた以外は実施例１と同様にして、リチウム二次電池正極用組成物を得た。
(Comparative Example 4)
A lithium secondary battery positive electrode composition was obtained in the same manner as in Example 1 except that polyvinylidene fluoride (PVDF, manufactured by Kureha, # 1100) was used instead of the polyvinyl acetal resin (A).
（比較例５〜７）
表３に示すポリビニルアセタール樹脂を用い、Ｎ−メチルピロリドンの添加量を変更した以外は実施例１０と同様にして、リチウム二次電池負極用組成物を得た。
(Comparative Examples 5-7)
A composition for a lithium secondary battery negative electrode was obtained in the same manner as in Example 10 except that the polyvinyl acetal resin shown in Table 3 was used and the addition amount of N-methylpyrrolidone was changed.
（比較例８）
ポリビニルアセタール樹脂（Ａ）に代えて、ポリフッ化ビニリデン（ＰＶＤＦ、クレハ社製、＃１１００）を用いた以外は実施例１０と同様にして、リチウム二次電池負極用組成物を得た。
(Comparative Example 8)
A lithium secondary battery negative electrode composition was obtained in the same manner as in Example 10 except that polyvinylidene fluoride (PVDF, manufactured by Kureha Corporation, # 1100) was used instead of the polyvinyl acetal resin (A).
＜評価＞
実施例及び比較例で得られたリチウム二次電池電極用組成物（正極用、負極用）について以下の評価を行った。結果を表３に示した。
<Evaluation>
The following evaluation was performed about the composition for lithium secondary battery electrodes (for positive electrodes and negative electrodes) obtained by the Example and the comparative example. The results are shown in Table 3.
（１）接着性
実施例１〜９、比較例１〜４で得られたリチウム二次電池正極用組成物については、アルミ箔に対する接着性を評価し、実施例１０〜１８、比較例５〜８で得られたリチウム二次電池負極用組成物については、銅箔に対する接着性を評価した。
(1) Adhesiveness About the compositions for lithium secondary battery positive electrodes obtained in Examples 1 to 9 and Comparative Examples 1 to 4, the adhesiveness to aluminum foil was evaluated, and Examples 10 to 18 and Comparative Examples 5 to 5 were evaluated. About the composition for lithium secondary battery negative electrodes obtained by 8, adhesiveness with respect to copper foil was evaluated.
（１−１）実施例１〜９、比較例１〜４
アルミ箔（厚み２０μｍ）の上に、乾燥後の膜厚が２０μｍとなるように電極用組成物を塗工、乾燥し、アルミ箔上に電極がシート状に形成された試験片を得た。
このサンプルを縦１ｃｍ、横２ｃｍに切り出し、ＡＵＴＯＧＲＡＰＨ（島津製作所社製、「ＡＧＳ−Ｊ」）を用い、試験片を固定しながら電極シートを引き上げ、アルミ箔から完全に電極シートが剥離するまでに要する剥離力(Ｎ)を計測した。
(1-1) Examples 1 to 9 and Comparative Examples 1 to 4
On the aluminum foil (thickness 20 μm), the electrode composition was applied and dried so that the film thickness after drying was 20 μm, to obtain a test piece in which the electrode was formed in a sheet shape on the aluminum foil.
This sample was cut into a length of 1 cm and a width of 2 cm, and the electrode sheet was pulled up while fixing the test piece using AUTOGRAPH (manufactured by Shimadzu Corporation, “AGS-J”) until the electrode sheet was completely peeled from the aluminum foil. The required peel force (N) was measured.
（１−２）実施例１０〜１８、比較例５〜８
上記（１−１）において、アルミ箔を銅箔（厚み２０μｍ）に変更した以外は全く同じ方法にて剥離力を計測した。
(1-2) Examples 10 to 18 and Comparative Examples 5 to 8
In the above (1-1), the peel force was measured in exactly the same manner except that the aluminum foil was changed to a copper foil (thickness 20 μm).
（２）分散性
得られたリチウム二次電池電極用組成物１０重量部とＮ−メチルピロリドン９０重量部を混合、希釈した後、超音波分散機（エスエヌディ社製、「ＵＳ−３０３」）にて１０分間撹拌した。その後レーザー回折式粒度分布計（堀場製作所社製、ＬＡ−９１０）を用いて粒度分布測定を行い、平均粒径を測定した。
(2) Dispersibility After mixing and diluting 10 parts by weight of the obtained composition for a lithium secondary battery electrode and 90 parts by weight of N-methylpyrrolidone, an ultrasonic disperser (manufactured by SNDI, “US-303”) was used. And stirred for 10 minutes. Thereafter, the particle size distribution was measured using a laser diffraction particle size distribution meter (LA-910, manufactured by Horiba, Ltd.), and the average particle size was measured.
（３）溶媒溶解性
（電極シートの作製）
離型処理されたポリエチレンテレフタレート（ＰＥＴ）フィルム上に、乾燥後の膜厚が２０μｍとなるように実施例及び比較例で得られたリチウム二次電池電極用組成物を塗工、乾燥して電極シートを作製した。
その電極シートを２ｃｍ角に切り出し、電極シート試験片を作製した。
(3) Solvent solubility (production of electrode sheet)
On the polyethylene terephthalate (PET) film subjected to the release treatment, the lithium secondary battery electrode compositions obtained in Examples and Comparative Examples were applied and dried so that the film thickness after drying was 20 μm. A sheet was produced.
The electrode sheet was cut into a 2 cm square to prepare an electrode sheet test piece.
（溶出評価）
得られた試験片の重量を正確に計量し、シートに含まれる成分重量比から試験片に含まれる樹脂の重量を算出した。その後、試験片を袋状のメッシュに入れ、メッシュ袋と試験片の合計重量を正確に計測した。
次いで、試験片の入っているメッシュ袋を電解液であるジエチルカーボネートに浸し、室温にて１晩放置した。放置後メッシュ袋を取り出し、１５０℃、８時間の条件で乾燥させ、完全に溶剤を乾燥させた。
乾燥機から取り出した後、室温にて１時間放置し、重量を計測した。試験前後の重量変化から樹脂の溶出量を算出し、その溶出量とあらかじめ算出しておいた樹脂の重量の比から樹脂の溶出率を算出し、以下の基準で評価した。なお、溶出率の値が高いほど、電解液中へ樹脂が溶出しやすいことを意味する。
(Elution evaluation)
The weight of the obtained test piece was accurately measured, and the weight of the resin contained in the test piece was calculated from the component weight ratio contained in the sheet. Thereafter, the test piece was put in a bag-like mesh, and the total weight of the mesh bag and the test piece was accurately measured.
Next, the mesh bag containing the test piece was immersed in diethyl carbonate, which is an electrolytic solution, and left overnight at room temperature. After standing, the mesh bag was taken out and dried under conditions of 150 ° C. and 8 hours to completely dry the solvent.
After taking out from the dryer, it was left at room temperature for 1 hour and weighed. The elution amount of the resin was calculated from the weight change before and after the test, and the elution rate of the resin was calculated from the ratio between the elution amount and the weight of the resin calculated in advance, and evaluated according to the following criteria. In addition, it means that resin is easy to elute in electrolyte solution, so that the value of elution rate is high.
（４）イオン伝導性
アルミ箔（厚み２０μｍ）の上に、乾燥後の膜厚が２０μｍとなるようにリチウム二次電池電極用組成物を塗工、乾燥し、アルミ箔上に電極がシート状に形成された試験片を得た。
得られた試験片をグローブボックス内で減圧乾燥しながら、リード線を取り付け、インピーダンスアナライザー（東陽テクニカ社製）を用いてイオン伝導率を測定した。
(4) A composition for a lithium secondary battery electrode is coated on an ion conductive aluminum foil (thickness 20 μm) so that the film thickness after drying is 20 μm, and the electrode is formed into a sheet on the aluminum foil. A test piece formed in the above was obtained.
While the obtained test piece was dried under reduced pressure in a glove box, a lead wire was attached, and ion conductivity was measured using an impedance analyzer (manufactured by Toyo Technica).
（５）電池性能評価
（ａ）コイン電池の作製
実施例１で得られたリチウム二次電池正極用組成物をアルミ箔に塗布、乾燥し、厚さ０．２ｍｍとし、これをφ１２ｍｍに打ち抜いて正極層を得た。
また、実施例１０で得られたリチウム二次電池負極用組成物を銅箔に塗布、乾燥し、厚さ０．２ｍｍとし、これをφ１２ｍｍに打ち抜いて負極層を得た。
電解液としてＬｉＰＦ６（１Ｍ）を含有するエチレンカーボネートとの混合溶媒を用い、該電解液を正極層に含浸させた後、この正極層を正極集電体上に置き、さらにその上に電解液を含浸させた厚さ２５ｍｍの多孔質ＰＰ膜（セパレータ）を置いた。
更に、この上に負極層となるリチウム金属板を置き、この上に絶縁パッキンで被覆された負極集電体を重ね合わせた。この積層体を、かしめ機により圧力を加え、密閉型のコイン電池を得た。
(5) Battery performance evaluation (a) Preparation of coin battery The lithium secondary battery positive electrode composition obtained in Example 1 was applied to an aluminum foil, dried to a thickness of 0.2 mm, and punched out to φ12 mm. A positive electrode layer was obtained.
Moreover, the composition for lithium secondary battery negative electrodes obtained in Example 10 was applied to a copper foil and dried to a thickness of 0.2 mm, which was punched into φ12 mm to obtain a negative electrode layer.
A mixed solvent with ethylene carbonate containing LiPF 6 (1M) was used as the electrolytic solution, and after impregnating the electrolytic solution into the positive electrode layer, the positive electrode layer was placed on the positive electrode current collector, and further on the electrolytic solution A porous PP membrane (separator) having a thickness of 25 mm impregnated with was placed.
Further, a lithium metal plate serving as a negative electrode layer was placed thereon, and a negative electrode current collector covered with insulating packing was placed thereon. Pressure was applied to the laminate with a caulking machine to obtain a sealed coin battery.
（ｂ）放電容量評価、及び、充放電サイクル評価
得られたコイン電池について、（宝泉社製、充放電試験装置）を用いて放電容量評価、及び、充放電サイクル評価を行った。
この放電容量評価、充放電サイクル評価は電圧範囲３．０〜４．４Ｖ、評価温度は２０℃で行った。
(B) Evaluation of discharge capacity and evaluation of charge / discharge cycle The obtained coin battery was subjected to a discharge capacity evaluation and a charge / discharge cycle evaluation using a charge / discharge test apparatus manufactured by Hosen Co., Ltd.
This discharge capacity evaluation and charge / discharge cycle evaluation were performed at a voltage range of 3.0 to 4.4 V and an evaluation temperature of 20 ° C.
本発明によれば、活物質の分散性、接着性、イオン伝導性に優れ、バインダーの添加量が少ない場合でも高容量のリチウム二次電池を作製することが可能なリチウム二次電池電極用組成物を提供できる。 ADVANTAGE OF THE INVENTION According to this invention, the composition for lithium secondary battery electrodes which is excellent in the dispersibility of an active material, adhesiveness, and ionic conductivity, and can produce a high capacity | capacitance lithium secondary battery even when there is little addition amount of a binder. Can provide things.
Claims (7)
前記バインダーは、ポリビニルアセタール樹脂を含有し、
前記ポリビニルアセタール樹脂は、下記式（１）で表される水酸基を有する構成単位、下記式（２）で表されるアセチル基を有する構成単位、下記式（３）で表されるアセタール基を有する構成単位、及び、下記式（４）で表される構成単位を有する
ことを特徴とするリチウム二次電池電極用組成物。
The binder contains a polyvinyl acetal resin,
The polyvinyl acetal resin has a structural unit having a hydroxyl group represented by the following formula (1), a structural unit having an acetyl group represented by the following formula (2), and an acetal group represented by the following formula (3). It has a structural unit and a structural unit represented by following formula (4), The composition for lithium secondary battery electrodes characterized by the above-mentioned.