JP2015067291A - Delamination container - Google Patents
Delamination container Download PDFInfo
- Publication number
- JP2015067291A JP2015067291A JP2013201558A JP2013201558A JP2015067291A JP 2015067291 A JP2015067291 A JP 2015067291A JP 2013201558 A JP2013201558 A JP 2013201558A JP 2013201558 A JP2013201558 A JP 2013201558A JP 2015067291 A JP2015067291 A JP 2015067291A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- container
- evoh
- barrier
- surface side
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、内容物の減少に伴って内層が外層から剥離し収縮する積層剥離容器に関する。 The present invention relates to a laminated peeling container in which an inner layer peels from an outer layer and shrinks with a decrease in contents.
従来、内容物の減少に伴って内層が外層から剥離し収縮することによって容器の内部に空気が入り込むことを抑制する積層剥離容器が知られている（例えば、特許文献１）。 2. Description of the Related Art Conventionally, there has been known a laminated peeling container that suppresses air from entering the container by peeling and shrinking the inner layer from the outer layer as the contents are reduced (for example, Patent Document 1).
このような積層剥離容器として、外層の最内層がポリプロピレン層であり、内層の最外層がＥＶＯＨ層であるものがある。このような層構成の採用により、ＥＶＯＨ層が優れた酸素バリア性が有していることに加えて、ポリプロピレン層とＥＶＯＨ層の間の剥離性が優れているので、酸素バリア性に優れ且つ内層が容易に剥離して収縮する積層剥離容器が得られる。 As such a delamination container, there is one in which the innermost layer of the outer layer is a polypropylene layer and the outermost layer of the inner layer is an EVOH layer. By adopting such a layer structure, in addition to the EVOH layer having excellent oxygen barrier properties, the peelability between the polypropylene layer and the EVOH layer is excellent, so that the oxygen barrier property is excellent and the inner layer Can be easily peeled and contracted.
しかし、本発明者が検討を行ったところ、積層剥離容器の使用環境によっては、酸素バリア性が低下して内容物が劣化してしまう場合があることに気が付いた。 However, as a result of studies by the present inventor, it has been found that depending on the use environment of the delamination container, the oxygen barrier property may be lowered and the contents may be deteriorated.
本発明はこのような事情に鑑みてなされたものであり、酸素バリア性の低下を抑制することができる積層剥離容器を提供するものである。 This invention is made | formed in view of such a situation, and provides the delamination container which can suppress the fall of oxygen barrier property.
本発明によれば、外層と内層とを備え、内容物の減少に伴って前記内層が前記外層から剥離し収縮する積層剥離容器であって、前記内層は、ＥＶＯＨ層と、前記ＥＶＯＨ層の容器外面側に設けられた外側バリア層と、前記ＥＶＯＨ層の容器内面側に設けられた内側バリア層とを備える、積層剥離容器が提供される。 According to the present invention, there is provided a laminated peeling container comprising an outer layer and an inner layer, wherein the inner layer peels and shrinks from the outer layer as the content decreases, and the inner layer includes an EVOH layer and a container for the EVOH layer. There is provided a delamination container including an outer barrier layer provided on the outer surface side and an inner barrier layer provided on the container inner surface side of the EVOH layer.
本発明者は鋭意検討を行ったところ、ＥＶＯＨ層は水蒸気に曝されると酸素バリア性が低下する場合があり、積層剥離容器においては内層が外層から剥離することによって、内層と外層の間に入り込んだ空気にＥＶＯＨ層が曝されるために、積層剥離容器が高湿度環境で使用された場合にはＥＶＯＨ層の酸素バリア性が低下してその結果、内容物が劣化してしまうことが分かった。
そして、ＥＶＯＨ層の両側にバリア層を設けることによってＥＶＯＨ層の酸素バリア性の低下が抑制され、それによって内容物の劣化が抑制されることを見出し、本発明の完成に到った。
As a result of intensive studies, the present inventors have found that when the EVOH layer is exposed to water vapor, the oxygen barrier property may decrease, and in the delamination container, the inner layer peels from the outer layer, so that the inner layer is separated from the outer layer. Since the EVOH layer is exposed to the air that has entered, it is understood that when the delamination container is used in a high-humidity environment, the oxygen barrier property of the EVOH layer is lowered, and as a result, the contents deteriorate. It was.
And it discovered that the fall of the oxygen barrier property of an EVOH layer was suppressed by providing a barrier layer on both sides of an EVOH layer, and thereby the deterioration of the content was suppressed, and it came to the completion of this invention.
以下、本発明の種々の実施形態を例示する。以下に示す実施形態は互いに組み合わせ可能である。
好ましくは、前記ＥＶＯＨ層は、酸素吸収剤を含有する。
好ましくは、前記外側バリア層の容器外面側に外側ＥＶＯＨ層をさらに備える。
Hereinafter, various embodiments of the present invention will be exemplified. The following embodiments can be combined with each other.
Preferably, the EVOH layer contains an oxygen absorbent.
Preferably, an outer EVOH layer is further provided on the outer surface side of the outer barrier layer.
以下、本発明の実施形態について説明する。以下に示す実施形態中で示した各種特徴事項は、互いに組み合わせ可能である。また、各特徴について独立して発明が成立する。 Hereinafter, embodiments of the present invention will be described. Various characteristic items shown in the following embodiments can be combined with each other. The invention is established independently for each feature.
１．第１実施形態
図１（ａ）〜（ｂ）に示すように、本発明の第１実施形態の積層剥離容器１は、円筒状の胴部と底部とで構成される本体部１ａと、内容物の充填及び排出を行うための口部１ｂとを備える。口部１ｂには、雄ネジ部１ｃが設けられている。雄ネジ部１ｃには、雌ねじを有するキャップやポンプなどが取り付けられる。
1. 1st Embodiment As shown to Fig.1 (a)-(b), the delamination container 1 of 1st Embodiment of this invention is the main-body part 1a comprised by the cylindrical trunk | drum and bottom, and the content And a mouth portion 1b for filling and discharging objects. The mouth portion 1b is provided with a male screw portion 1c. A cap or a pump having a female screw is attached to the male screw portion 1c.
積層剥離容器１は、容器外面側の外層３と、容器内面側の内層５を備える。内層５で囲まれた収容空間７に内容物が充填される。図１（ａ）は、容器内に内容物が満充填されていて外層３と内層５が接触している状態を示し、図１（ｂ）は、内容物が口部１ｂから排出されることによって内層５が外層３から剥離して収容空間７が収縮している状態を示す。外層３と内層５の間の空間９には、本体部１ａ又は口部１ｂの外層３に空気導入孔を設けて、この空気導入孔を通じて空気を導入することができる。尚、空気導入孔に逆止弁を設けて、空間９から外部に空気が排出されないようにしてもよい。 The delamination container 1 includes an outer layer 3 on the container outer surface side and an inner layer 5 on the container inner surface side. The accommodation space 7 surrounded by the inner layer 5 is filled with the contents. FIG. 1A shows a state in which the contents are fully filled in the container and the outer layer 3 and the inner layer 5 are in contact with each other, and FIG. 1B shows that the contents are discharged from the mouth portion 1b. Shows a state in which the inner layer 5 is peeled from the outer layer 3 and the accommodation space 7 is contracted. In the space 9 between the outer layer 3 and the inner layer 5, an air introduction hole is provided in the outer layer 3 of the main body 1a or the mouth 1b, and air can be introduced through the air introduction hole. Note that a check valve may be provided in the air introduction hole so that air is not discharged from the space 9 to the outside.
収容空間７からの内容物の排出は、マヨネーズや醤油などの内容物を収容する絞り出し容器のように外層３を押圧することにより、内層５が共に押しつぶされて口部１ｂから内容物を排出するようにしてもよく、雄ネジ部１ｃにポンプを取り付けて、ポンプを作動させることによって内容物を排出するようにしてもよい。また、空気導入孔に逆止弁が設けられている場合は、外層３を押しつぶしたときに、外層３と内層５との間の空気の内圧が上がることで、内層５を押しつぶして内容物を排出することもできる。 The contents are discharged from the storage space 7 by pressing the outer layer 3 like a squeeze container for storing contents such as mayonnaise and soy sauce, so that the inner layer 5 is crushed together and the contents are discharged from the mouth portion 1b. Alternatively, a pump may be attached to the male screw portion 1c and the contents may be discharged by operating the pump. In addition, when a check valve is provided in the air introduction hole, when the outer layer 3 is crushed, the internal pressure of the air between the outer layer 3 and the inner layer 5 increases, so that the inner layer 5 is crushed and the contents are crushed. It can also be discharged.
外層３と内層５の間の空間９に空気が入り込むと、内層５の最外層は、空気に曝されることになる。ここで、内層５の詳細構成を図２に示す。図２に示すように、内層５は、ＥＶＯＨ層５ａと、ＥＶＯＨ層５ａの容器外面側に設けられた外側バリア層５ｂと、ＥＶＯＨ層５ａの容器内面側に設けられた内側バリア層５ｃと、内側バリア層５ｃの容器内面側に設けられた内面層５ｄを備える。外側バリア層５ｂ及び内側バリア層５ｃは、ＥＶＯＨ層５ａを覆うことによって、ＥＶＯＨ層５ａと空気との接触を低減する機能を有するものであり、本実施形態では、ＥＶＯＨ層５ａの両側にバリア層を設けることによって、ＥＶＯＨ層５ａが空気と接触しないようになっている。これに対して、従来の積層剥離容器１では、ＥＶＯＨ層５ａの容器外面側には外側バリア層５ｂが設けられておらず、外層３と内層５の間の空間９に入り込んだ空気がＥＶＯＨ層５ａに直接接触する構成になっていた。このため、積層剥離容器１が高湿度環境で使用された場合には、空気に含まれる水蒸気によってＥＶＯＨ層５ａが変性されて、その酸素バリア性が低下していた。本実施形態によれば、このような水蒸気によるＥＶＯＨ層５ａの変性が抑制可能である。 When air enters the space 9 between the outer layer 3 and the inner layer 5, the outermost layer of the inner layer 5 is exposed to the air. Here, the detailed structure of the inner layer 5 is shown in FIG. As shown in FIG. 2, the inner layer 5 includes an EVOH layer 5a, an outer barrier layer 5b provided on the container outer surface side of the EVOH layer 5a, an inner barrier layer 5c provided on the container inner surface side of the EVOH layer 5a, An inner surface layer 5d provided on the inner surface side of the inner barrier layer 5c is provided. The outer barrier layer 5b and the inner barrier layer 5c have a function of reducing the contact between the EVOH layer 5a and air by covering the EVOH layer 5a. In this embodiment, the barrier layers are provided on both sides of the EVOH layer 5a. Thus, the EVOH layer 5a is prevented from coming into contact with air. On the other hand, in the conventional delamination container 1, the outer barrier layer 5b is not provided on the outer surface side of the EVOH layer 5a, and the air entering the space 9 between the outer layer 3 and the inner layer 5 is the EVOH layer. It was the structure which contacts 5a directly. For this reason, when the delamination container 1 is used in a high-humidity environment, the EVOH layer 5a is denatured by water vapor contained in the air, and its oxygen barrier property is lowered. According to the present embodiment, such modification of the EVOH layer 5a due to water vapor can be suppressed.
ＥＶＯＨ層５ａは、エチレン−ビニルアルコール共重合体（ＥＶＯＨ）樹脂からなる層であり、エチレンと酢酸ビニル共重合物の加水分解により得られる。ＥＶＯＨ樹脂のエチレン含有量は、例えば２５〜５０ｍｏｌ％であり、酸素バリア性の観点から２５〜３５ｍｏｌ％が好ましい。 The EVOH layer 5a is a layer made of an ethylene-vinyl alcohol copolymer (EVOH) resin, and is obtained by hydrolysis of ethylene and vinyl acetate copolymer. The ethylene content of the EVOH resin is, for example, 25 to 50 mol%, and preferably 25 to 35 mol% from the viewpoint of oxygen barrier properties.
また、ＥＶＯＨ層５ａは、酸素吸収剤を含有することが好ましい。酸素吸収剤をＥＶＯＨ層５ａに含有させることにより、ＥＶＯＨ層５ａの酸素バリア性をさらに向上させることができる。本発明者らの実験によれば、ＥＶＯＨ層５ａに酸素吸収剤を用いた場合、ＥＶＯＨ層５ａが酸素吸収するときの反応によって臭気物質が発生するが、本実施形態のように、ＥＶＯＨ層５ａの両側にバリア層を設けた場合には、この臭気物質の外部放出が抑制される。 The EVOH layer 5a preferably contains an oxygen absorbent. By containing the oxygen absorbent in the EVOH layer 5a, the oxygen barrier property of the EVOH layer 5a can be further improved. According to the experiments by the present inventors, when an oxygen absorbent is used for the EVOH layer 5a, an odorous substance is generated by a reaction when the EVOH layer 5a absorbs oxygen. However, as in the present embodiment, the EVOH layer 5a When barrier layers are provided on both sides of the odorant, the release of the odorous substance to the outside is suppressed.
外側バリア層５ｂ及び内側バリア層５ｃは、ＥＶＯＨ層５ａと空気との接触を阻害するものであればよく、例えば、ポリオレフィンからなる。また、ポリオレフィンのみではＥＶＯＨ層５ａと接着性が十分でない場合には、ポリオレフィンにカルボキシル基を導入した酸変性ポリオレフィン（例：無水マレイン酸変性ポリエチレン）を添加してもよい。ポリオレフィンとしては、低密度ポリエチレン、直鎖状低密度ポリエチレン、高密度ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体及びその混合物などが挙げられる。外側バリア層５ｂの一例は、低密度ポリエチレンと酸変性ポリエチレンの混合物であり、内側バリア層５ｃの一例は、エチレン酢酸ビニル共重合体（EVA）、低密度ポリエチレン、直鎖状低密度ポリエチレン、又は、低密度ポリエチレン又は直鎖状低密度ポリエチレンと、酸変性ポリエチレンの混合物などである。
尚、ＥＶＯＨ層５ａとの接着性、及び、外層３との間の剥離性を考慮すると、外側バリア層５ｂとしてはエチレン酢酸ビニル共重合体（EVA）が好ましい。
The outer barrier layer 5b and the inner barrier layer 5c only need to inhibit contact between the EVOH layer 5a and air, and are made of, for example, polyolefin. In addition, when the polyolefin alone is insufficient in adhesion to the EVOH layer 5a, an acid-modified polyolefin in which a carboxyl group is introduced into the polyolefin (eg, maleic anhydride-modified polyethylene) may be added. Examples of the polyolefin include low density polyethylene, linear low density polyethylene, high density polyethylene, polypropylene, ethylene-propylene copolymer, and mixtures thereof. An example of the outer barrier layer 5b is a mixture of low density polyethylene and acid-modified polyethylene, and an example of the inner barrier layer 5c is ethylene vinyl acetate copolymer (EVA), low density polyethylene, linear low density polyethylene, or , Low density polyethylene or a mixture of linear low density polyethylene and acid-modified polyethylene.
In consideration of adhesiveness with the EVOH layer 5a and releasability with the outer layer 3, the outer barrier layer 5b is preferably an ethylene vinyl acetate copolymer (EVA).
内側バリア層５ｃの容器内面側には内面層５ｄが設けられる。内面層５ｄは、例えば、上述したポリオレフィンからなり、直鎖状低密度ポリエチレンが好ましい。内側バリア層５ｃは、ＥＶＯＨ層５ａと内面層５ｄの間の接着層としても機能する。 An inner surface layer 5d is provided on the inner surface side of the inner barrier layer 5c. The inner surface layer 5d is made of the above-described polyolefin, for example, and linear low density polyethylene is preferable. The inner barrier layer 5c also functions as an adhesive layer between the EVOH layer 5a and the inner surface layer 5d.
外層３は、例えば、上述したポリオレフィンからなり、ポリプロピレンが好ましい。本実施形態では、外層３は、１層構成であるが、外層３は、複数層構成であってもよい。例えば、リプロ層の両側をポリプロピレン層で挟んだ構成であってもよい。ここで、リプロ層とは、容器の成形時にでたバリをリサイクルして使用した層をいう。また、外層３は、復元性を有するように、内層３よりも肉厚に形成される。 The outer layer 3 is made of, for example, the above-described polyolefin, and polypropylene is preferable. In the present embodiment, the outer layer 3 has a single-layer configuration, but the outer layer 3 may have a multi-layer configuration. For example, a configuration in which both sides of the repro layer are sandwiched between polypropylene layers may be employed. Here, the repro layer refers to a layer that is used by recycling burrs produced during the molding of the container. Moreover, the outer layer 3 is formed thicker than the inner layer 3 so as to have resilience.
本実施形態の積層剥離容器１の製造方法は、特に限定されず、例えば、製造すべき容器に対応する積層構造を備えた溶融状態の積層パリソンを押出し、この溶融状態の積層パリソンをブロー成形金型にセットし、ブロー成形法によって所望の容器形状に成形することによって得ることができる。なお、図１では、ピンチオフ部は図示していないが、容器の底部等に適宜設けられる。空気導入孔を形成する場合には、ブロー成形体を金型から取り出した後に、パンチやドリルなどによって形成することができる。 The manufacturing method of the lamination peeling container 1 of this embodiment is not specifically limited, For example, the laminated parison of a molten state provided with the laminated structure corresponding to the container which should be manufactured is extruded, and this laminated parison of a molten state is blow molded metal It can be obtained by setting in a mold and molding into a desired container shape by blow molding. In addition, although the pinch-off part is not illustrated in FIG. 1, it is appropriately provided at the bottom of the container. In the case of forming the air introduction hole, it can be formed by a punch or a drill after the blow molded body is taken out from the mold.
ブロー成形によって得られた積層剥離容器１にはそのまま内容物の充填を行ってもよく、内容物の充填前に予備剥離を行った後に内容物の充填を行ってもよい。本実施形態の積層剥離容器１においては、予備剥離は、例えば、外層３に設けられた空気導入孔から外層３と内層５との間に空気を注入する、又は、外層３と内層５の間の界面Ｐから外層３と内層５の間に空気を強制注入することによって行うことができる。容器口部の界面Pから空気を注入する方法においては、容器の成形時に容器口部の先端から更に延びるように筒状部を一体に形成する。その筒状部の一部を筒状部中心に向かって押しつぶすことにより、筒状部における内層を部分的に剥離させ、剥離させた部分に対応する外層に孔を開け、当該孔から空気を注入する。この際、筒状部の開口端の界面から注入した空気が外部に漏れないように、プラグなどを開口端に押し込んで、開口端における内層と外層を密着させることで開口端の界面を封止してもよい。この予備剥離工程が終わった後、容器に不要な筒状部を切断して図１に示す容器とする。 The laminated peeling container 1 obtained by blow molding may be filled with the contents as it is, or after the preliminary peeling before filling the contents, the contents may be filled. In the laminated peeling container 1 of the present embodiment, the preliminary peeling is performed, for example, by injecting air between the outer layer 3 and the inner layer 5 from an air introduction hole provided in the outer layer 3 or between the outer layer 3 and the inner layer 5. This can be performed by forcibly injecting air between the outer layer 3 and the inner layer 5 from the interface P. In the method of injecting air from the interface P of the container mouth portion, the cylindrical portion is integrally formed so as to extend further from the tip of the container mouth portion when the container is formed. By crushing part of the cylindrical part toward the center of the cylindrical part, the inner layer in the cylindrical part is partially peeled off, a hole is made in the outer layer corresponding to the peeled part, and air is injected from the hole To do. At this time, in order to prevent the air injected from the interface at the opening end of the cylindrical portion from leaking to the outside, the plug or the like is pushed into the opening end and the inner layer and the outer layer at the opening end are brought into close contact to seal the opening end interface May be. After this preliminary peeling step is finished, a cylindrical portion unnecessary for the container is cut into the container shown in FIG.
２．第２実施形態
本発明の第２実施形態は、第１実施形態に類似しているが、内層５の詳細構成が異なっている。以下、差異点を中心に説明を進める。
2. Second Embodiment A second embodiment of the present invention is similar to the first embodiment, but the detailed configuration of the inner layer 5 is different. Hereinafter, the explanation will be focused on the differences.
図３に示すように、本実施形態では、内層５は、第１実施形態の構成に加えて、外側バリア層５ｂの容器外面側に外側ＥＶＯＨ層５ｅを備える。 As shown in FIG. 3, in this embodiment, the inner layer 5 includes an outer EVOH layer 5e on the container outer surface side of the outer barrier layer 5b in addition to the configuration of the first embodiment.
第１実施形態では、外側バリア層５ｂが内層５の最外層に位置しているので、外側バリア層５ｂとＥＶＯＨ層５ａとの間の接着性を高めるために外側バリア層５ｂに酸変性ポリオレフィンを含有させると、外側バリア層５ｂと外層３との間の接着性も高まってしまい、内層５が外層３から剥離しにくくなってしまうという問題が生じる。 In the first embodiment, since the outer barrier layer 5b is located at the outermost layer of the inner layer 5, in order to improve the adhesion between the outer barrier layer 5b and the EVOH layer 5a, acid-modified polyolefin is added to the outer barrier layer 5b. When contained, the adhesion between the outer barrier layer 5b and the outer layer 3 is also increased, and there arises a problem that the inner layer 5 becomes difficult to peel from the outer layer 3.
そこで、本実施形態では、外側バリア層５ｂの容器外面側に外側ＥＶＯＨ層５ｅを設けることによって、外側バリア層５ｂが外層３と接触しないようにして、内層５と外層３の間の剥離性を高めている。また、外側ＥＶＯＨ層５ｅは、ＥＶＯＨ層５ａと同様にエチレン−ビニルアルコール共重合体（ＥＶＯＨ）樹脂からなる層であり、優れた酸素バリア性を有している。このため、外側ＥＶＯＨ層５ｅを設けることによって、ＥＶＯＨ層５ａの劣化がさらに抑制される。外側ＥＶＯＨ層５ｅとＥＶＯＨ層５ａのエチレン含有量は同じであっても異なっていてもよい。例えば、ＥＶＯＨ層５ａのエチレン含有量を外側ＥＶＯＨ層５ｅのエチレン含有量よりも低くすることによって、ＥＶＯＨ層５ａの酸素バリア性を高くできるとともに、外層３との剥離性を高くすることができる。 Therefore, in the present embodiment, the outer EVOH layer 5e is provided on the outer surface side of the outer barrier layer 5b so that the outer barrier layer 5b does not come into contact with the outer layer 3 so that the peelability between the inner layer 5 and the outer layer 3 is improved. It is increasing. The outer EVOH layer 5e is a layer made of an ethylene-vinyl alcohol copolymer (EVOH) resin like the EVOH layer 5a, and has an excellent oxygen barrier property. For this reason, the deterioration of the EVOH layer 5a is further suppressed by providing the outer EVOH layer 5e. The ethylene contents of the outer EVOH layer 5e and the EVOH layer 5a may be the same or different. For example, by making the ethylene content of the EVOH layer 5a lower than the ethylene content of the outer EVOH layer 5e, the oxygen barrier property of the EVOH layer 5a can be enhanced and the peelability from the outer layer 3 can be enhanced.
１：積層剥離容器、３：外層、５：内層、７：収容空間、９：空間 1: Laminated peeling container, 3: outer layer, 5: inner layer, 7: accommodating space, 9: space
Claims (3)
前記内層は、ＥＶＯＨ層と、前記ＥＶＯＨ層の容器外面側に設けられた外側バリア層と、前記ＥＶＯＨ層の容器内面側に設けられた内側バリア層とを備える、積層剥離容器。 A delamination container comprising an outer layer and an inner layer, wherein the inner layer peels and shrinks from the outer layer as the content decreases;
The inner layer includes an EVOH layer, an outer barrier layer provided on the container outer surface side of the EVOH layer, and an inner barrier layer provided on the container inner surface side of the EVOH layer.