JP2015036427A - 機械構造用鋼 - Google Patents
機械構造用鋼 Download PDFInfo
- Publication number
- JP2015036427A JP2015036427A JP2013167356A JP2013167356A JP2015036427A JP 2015036427 A JP2015036427 A JP 2015036427A JP 2013167356 A JP2013167356 A JP 2013167356A JP 2013167356 A JP2013167356 A JP 2013167356A JP 2015036427 A JP2015036427 A JP 2015036427A
- Authority
- JP
- Japan
- Prior art keywords
- steel
- content
- comparative example
- cutting
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】機械構造用鋼である。質量%で、C:0.15〜0.25%、Si:0.04〜0.15%、Mn:0.6〜1.0%、P:≦0.030%、S:0.015〜0.030%、Cu:≦0.30%、Ni:≦1.00%、Cr:1.0〜2.0%、Mo:≦1.00%、s−Al:0.010〜0.050%、及び、N:0.005〜0.030%を含み、残部Fe及び不純物からなり、元素Mの質量%を[M]とすると、10.0×[Si]+[Mn]+[Cr]≦3.90、5.44×[Si]+34.6×[S]≧1.06、[Ni]+[Mo]≦1.00%を満たし、主としてフェライト・パーライト組織からなることを特徴とする。
【選択図】なし
Description
Ngo=10×[Si]+[Mn]+[Cr]
である。
Ngo=10×[Si]+[Mn]+[Cr]≦3.90 (式1)
Nvb=5.44×[Si]+34.6×[S]−0.71
である。
Nvb=5.44×[Si]+34.6×[S]−0.71≧0.35 (式2)
つまり、
5.44×[Si]+34.6×[S]≧1.06 (式3)
を満たすことが必要である。
20 旋削試験片
21 試験部
22 チャック部
Claims (1)
- 質量%で、C:0.15〜0.25%、Si:0.04〜0.15%、Mn:0.6〜1.0%、P:≦0.030%、S:0.015〜0.030%、Cu:≦0.30%、Ni:≦1.00%、Cr:1.0〜2.0%、Mo:≦1.00%、s−Al:0.010〜0.050%、及び、N:0.005〜0.030%を含み、残部Fe及び不純物からなり、元素Mの質量%を[M]とすると、
10.0×[Si]+[Mn]+[Cr]≦3.90
5.44×[Si]+34.6×[S]≧1.06
[Ni]+[Mo]≦1.00
を満たし、主としてフェライト・パーライト組織からなることを特徴とする機械構造用鋼。