JP2015020935A - Multiple glass - Google Patents
Multiple glass Download PDFInfo
- Publication number
- JP2015020935A JP2015020935A JP2013151070A JP2013151070A JP2015020935A JP 2015020935 A JP2015020935 A JP 2015020935A JP 2013151070 A JP2013151070 A JP 2013151070A JP 2013151070 A JP2013151070 A JP 2013151070A JP 2015020935 A JP2015020935 A JP 2015020935A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- window
- hollow layer
- existing
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、住宅や建物に設置された既設の窓ガラスをそのまま利用しながら、中空層支持体を介して、新設の後付けガラスを貼り合わせることによって製造される複層ガラスに関する。 The present invention relates to a multi-layer glass produced by bonding a newly installed retrofitted glass through a hollow layer support while using an existing window glass installed in a house or a building as it is.
住宅や建物の省エネルギー性の向上や窓ガラスの結露防止を目的に、開口部に装着される窓ガラスとして、断熱性に優れた複層ガラスが普及してきている。複層ガラスは、2枚のガラスを、その四周において中空層支持体を介して貼り合わせ、中空層支持体と2枚のガラスで囲まれた空間(中空層)に乾燥空気層を封入したもので、単板ガラスに比べて断熱性が向上したガラスである。当然のことながら、複層ガラスの総厚み(2枚のガラスの厚みと中空層支持体の厚みの総和)は、単板ガラスの厚みの2倍以上になってしまう。 For the purpose of improving the energy saving property of houses and buildings and preventing the condensation of the window glass, a multi-layer glass having excellent heat insulation has become widespread as a window glass attached to the opening. The double-glazed glass is made by laminating two sheets of glass through a hollow layer support in the four circumferences, and enclosing a dry air layer in a space (hollow layer) surrounded by the hollow layer support and the two sheets of glass. And it is the glass which heat insulation improved compared with the single plate glass. As a matter of course, the total thickness of the double-glazed glass (the sum of the thicknesses of the two glasses and the thickness of the hollow layer support) is twice or more the thickness of the single glass plate.
複層ガラスの厚みが大きくなってしまう結果として、複層ガラスを装着するサッシ(障子)や窓枠には、単板ガラスのそれに比べて大きなガラス用溝幅が必要になるため、複層ガラス用に製作されたガラス用溝幅の大きい障子や窓枠を使用する必要がある。つまり、既設の障子や窓枠が単板ガラス用に作製されたものである場合、単板ガラスに代わって複層ガラスを装着するためには、ガラスだけではなく障子や窓枠についても、複層ガラス用のものに交換しなければならなかったのである。 As a result of the increase in the thickness of the double-glazed glass, the sash (shoji) and window frame to which the double-glazed glass is attached require a larger glass groove width than that of the single-glazed glass. It is necessary to use a shoji or window frame with a large groove width for glass. In other words, when existing shojis and window frames are made for single glass, in order to install double-glazed glass instead of single-glazed glass, double-glazed glass is used not only for glass but also for shoji and window frames. It had to be exchanged for one.
単板ガラス用の小さなガラス用溝幅の障子や窓枠にそのまま装着できるような構造を有した複層ガラス構造が開示されている(特許文献1)。これは、2枚のガラス板を封着材で貼り合わせただけの構造であって、かつ室内側ガラスを窓枠内周面で保持させたことを特徴とするものである。このような構造の複層ガラスを、工場の複層ガラス製造ラインで製造するのが手間であって、むしろコスト高になると思われる。このような複層窓の取付け構造は、既設の単板ガラスをそのまま利用した複層ガラスではなく、単板ガラス用窓枠に装着することのできる複層窓の取付け構造を開示したものである。 A multi-layer glass structure having a structure that can be directly mounted on a shoji or window frame having a small glass groove width for a single glass sheet is disclosed (Patent Document 1). This is a structure in which two glass plates are simply bonded together with a sealing material, and the indoor side glass is held on the inner peripheral surface of the window frame. It would be troublesome to produce a double-glazed glass having such a structure on a double-glazed glass production line in a factory, and it would be rather expensive. Such a multi-layer window mounting structure discloses a multi-layer window mounting structure that can be attached to a single-panel glass window frame, rather than a multi-layer glass using an existing single-panel glass as it is.
一方、既存のサッシや窓枠を使用したまま単板ガラスを複層ガラス化するものとしては、密封保持材(アダプターと呼ばれる)を介して、複層ガラスを単板ガラス用窓枠に装着する方法が開示されている(例えば、特許文献2)。この方法は、その後広く実用化されている。 On the other hand, as a method of converting a single glass sheet into a double glass while using an existing sash or window frame, there is a method of attaching the double glass to a single glass window frame through a sealing holding material (called an adapter). It is disclosed (for example, Patent Document 2). This method has been widely used since then.
近年になって、既設のビル用単板ガラスを利用したまま、新設のガラスを貼り合わせた複層ガラス及びその製造方法が開示されている。特許文献3は、既設の板ガラスと新設の板ガラスの間に乾燥剤、スペーサー及び低透湿性シール材からなる中空層支持体を介在させて、そして既設の開口部固定部材と新設の板ガラスとの間を非透水性のシール材で固定した複層ガラスとその製造方法を開示している。 In recent years, there has been disclosed a multi-layer glass in which a new glass is pasted while using an existing single glass for a building and a method for producing the same. In Patent Document 3, a hollow layer support made of a desiccant, a spacer and a low moisture-permeable sealing material is interposed between an existing plate glass and a new plate glass, and between the existing opening fixing member and the new plate glass. Discloses a multi-layer glass fixed with a water-impermeable sealing material and a method for producing the same.
特許文献4は、特許文献3で開示された複層ガラスの耐久性を向上させることを目途としてなされたものであって、既設のガラス窓に対して新設のスペーサー付きガラス板を配置し、それらガラス間の四辺周辺部をシール材で封着して得られる複層ガラス及びその製造方法を開示したものであって、シール材が既設のガラス板、新設のスペーサー付きガラス板及びスペーサーのすべてに接着し、スペーサー付きガラス板の、既設のガラス板に面する側の面と小口面との二面がシール材と接着することで耐久性を向上させている。特許文献5は、特許文献3で開示された複層ガラスの組立作業の手間を省き、容易に組み立てることができる複層ガラスの組立方法を開示したものである。なお、特許文献4で開示された複層ガラスと類似した技術は、実用化されている(非特許文献1)。 Patent Document 4 is intended to improve the durability of the multi-layer glass disclosed in Patent Document 3, and a newly installed glass plate with a spacer is disposed on an existing glass window. Disclosed is a multi-layer glass obtained by sealing the periphery of the four sides between glasses with a sealing material and a method for producing the same, and the sealing material is applied to all existing glass plates, newly installed glass plates with spacers, and spacers. The durability is improved by bonding the two surfaces of the glass plate with the spacer, that is, the side facing the existing glass plate and the facet surface to the sealing material. Patent Document 5 discloses a method for assembling a double-glazed glass that can be easily assembled without the trouble of assembling the double-glazed glass disclosed in Patent Document 3. In addition, the technique similar to the multilayer glass disclosed by patent document 4 is put into practical use (nonpatent literature 1).
特許文献1で開示された複層窓の窓板取付け構造は、既設の窓枠を利用したまま、窓枠内周面に支持させながら複層板が取り付けられるものであるが、あらかじめそのような窓板取付け構造とした複層板を製造し、既設の窓枠に取り付けるものであって、既設の窓ガラスをそのまま活かして複層ガラスとするものではない。従って、既設の窓ガラスが装着されている場合は、これを取り外して、新たにそのような窓板取付け構造とした複層板を装着しなければならず、既設の窓ガラスが無駄になる。 In the multi-layer window window plate mounting structure disclosed in Patent Document 1, the multi-layer plate is mounted while being supported on the inner peripheral surface of the window frame while using the existing window frame. A multi-layer plate having a window plate attachment structure is manufactured and attached to an existing window frame, and the existing window glass is not used as it is to form a multi-layer glass. Therefore, when the existing window glass is attached, it is necessary to remove it and newly attach a multilayer board having such a window plate mounting structure, and the existing window glass is wasted.
また、特許文献1で開示された複層窓の窓板取付け構造は実用化されていない。これは、実用化されている一般的な複層ガラス(図1)では、中空層支持体の両側面に塗布等された粘着剤と、中空層支持体の背面側に注入されたシール材によって2枚のガラスを貼り合わせるのに対して(該粘着剤を一次シール、該シール材を二次シールと呼ぶ場合が多い)、特許文献1で開示された複層窓の窓板取付け構造では、2枚のガラスを封止材のみで貼り合わせる構造であって、長期耐久性に乏しいためと考えられる。一次シールがなく、二次シールだけで貼り合わせているためである。 In addition, the multi-window window plate mounting structure disclosed in Patent Document 1 has not been put to practical use. This is because, in general multilayer glass (FIG. 1) in practical use, an adhesive applied on both sides of the hollow layer support and a sealing material injected on the back side of the hollow layer support. In contrast to bonding two sheets of glass (the adhesive is often referred to as a primary seal and the sealant is referred to as a secondary seal), in the window plate mounting structure of a multi-layer window disclosed in Patent Document 1, This is considered to be due to the structure in which two pieces of glass are bonded only with a sealing material, and the long-term durability is poor. This is because there is no primary seal and only the secondary seal is applied.
次に、特許文献2に開示された方法は、既設の障子又は窓枠をそのまま活かすことはできるが、やはり既設の窓ガラスを取り外し、アダプターと呼ばれる密封保持材を利用して新たに複層ガラスを装着するものであって、既設の窓ガラスを取り外して廃棄しなければならない点で、無駄が多い。 Next, the method disclosed in Patent Document 2 can make use of the existing shoji or window frame as it is, but also removes the existing window glass and newly uses a sealing holding material called an adapter to newly create a multilayer glass. This is wasteful in that the existing window glass must be removed and discarded.
ここで、背景技術を正確に理解するため、窓ガラスの取付け構造と部材の関係を図2に示す。図2はいわゆる固定窓(しばしばFIX窓と呼ばれる)の取付け構造を簡略化して示したものであって、窓ガラス10は、建物の壁に施工された窓枠20に直接装着される。窓枠が取り付けられる建物の壁部分は、しばしば額縁30と呼ばれる。特許文献3に開示された技術は、この固定窓を対象として、既設の窓ガラス10に対して中空層支持体40を介して新設の窓ガラス50を並設し、新設の窓ガラスと開口部(サッシ)固定部材(すなわち、窓枠20若しくは額縁30)との間をシール材60で固定した複層ガラスである。 Here, in order to understand the background art accurately, the relationship between the window glass mounting structure and the members is shown in FIG. FIG. 2 shows a simplified structure for mounting a so-called fixed window (often referred to as a FIX window). The window glass 10 is directly attached to a window frame 20 constructed on the wall of a building. The wall part of the building to which the window frame is attached is often called the picture frame 30. In the technique disclosed in Patent Document 3, a new window glass 50 is arranged in parallel with the existing window glass 10 through the hollow layer support 40 for the fixed window, and the new window glass and the opening are provided. (Sash) It is a multi-layer glass in which the space between the fixing member (that is, the window frame 20 or the frame 30) is fixed by the sealing material 60.
一方、図3はいわゆる開閉窓(可動窓とも呼ばれる)の取付け構造である。開閉窓としては引違い窓や上げ下げ窓が一般的である。この場合、室内側の窓ガラス11は室内側の障子15に取り付けられ、室外側の窓ガラス12は、室外側の障子16に取り付けられ、そして、障子15及び16が、建物の壁(額縁30)に取り付けられた窓枠20に取り付けられる。通常、窓枠20に設けられたレール201、202に沿って障子15、16がスライドして動く。障子には、いわゆる戸車151、161が設置され、レールの上を戸車が回転して動くことによって、スムーズな開閉を可能にしている。開閉窓の構造では、窓ガラスは額縁に施工された窓枠にはめ込まれるのではなく障子に取り付けられ、障子が窓枠に取り付けられることになる。従って、このような窓ガラス11、12を複層ガラスにする場合は、可動性を確保するために、額縁や窓枠との間でシールすることはできないのである。 On the other hand, FIG. 3 shows a mounting structure of a so-called opening / closing window (also called a movable window). As the opening / closing window, a sliding window or a raising / lowering window is generally used. In this case, the indoor window glass 11 is attached to the indoor shoji 15, the outdoor window glass 12 is attached to the outdoor shoji 16, and the shoji 15 and 16 are attached to the building wall (picture frame 30). ) Is attached to the window frame 20 attached. Usually, the shojis 15 and 16 slide along the rails 201 and 202 provided on the window frame 20. The shojis are provided with so-called doors 151 and 161, and the doors rotate and move on the rails, thereby enabling smooth opening and closing. In the structure of the open / close window, the window glass is attached to the shoji instead of being fitted into the window frame constructed on the frame, and the shoji is attached to the window frame. Therefore, when such window glass 11 and 12 is made into a multi-layer glass, in order to ensure mobility, it cannot seal between a frame or a window frame.
特許文献3には、既設の板ガラスの室内側開口部に新設の板ガラスを並設した複層ガラスとその製造方法が開示されているが、明細書に添付された図面から明らかなように、新設の板ガラスは、建物のサッシ固定部材との間で、二次シール材によって固定される。従って、既設の板ガラス又は該板ガラスがはめ込まれたサッシは、建物のサッシ固定部材との間で固定されており、動くことができない構造になっている。このことは、特許文献3の特許請求の範囲において、「既存の建築物の引違い及び上げ下げ窓サッシ部を除く」とされていることからも明らかである。 Patent Document 3 discloses a multi-layer glass in which a new plate glass is juxtaposed to an indoor side opening of an existing plate glass and a method for producing the same, but as is apparent from the drawings attached to the specification, The plate glass is fixed by a secondary sealant between the sash fixing member of the building. Therefore, the existing plate glass or the sash fitted with the plate glass is fixed between the sash fixing member of the building and cannot move. This is also clear from the fact that, in the scope of claims of Patent Document 3, “excludes the sliding of existing buildings and the raising and lowering window sash portion”.
特許文献4は、その明細書の記載から、前記特許文献3を先行技術文献として提示し、特許文献3に開示された複層ガラスでは、新規のガラス板の小口面と框との間の隙間にのみシール材を充填しているため耐久性に懸念があるとし、その耐久性を改善することを目途としてなされたものである。従って、特許文献3に開示された技術と同様に、既存の建築物の引違い及び上げ下げ窓のような可動のサッシ部に適用できない技術であることは明らかである。 Patent Document 4 presents Patent Document 3 as a prior art document from the description of the specification, and in the multi-layer glass disclosed in Patent Document 3, a gap between the edge of the novel glass plate and the ridge Since only the sealing material is filled with the seal material, there is a concern about the durability, and the purpose is to improve the durability. Therefore, like the technique disclosed in Patent Document 3, it is obvious that the technique cannot be applied to a movable sash portion such as a sliding door and a raising / lowering window of an existing building.
また、特許文献3及び特許文献4で開示された技術は、既設の窓ガラスを利用したまま一般的な複層ガラス構造を実現するためのものである。そこでは、中空層支持体の基材として略中空矩形の断面を有する、いわゆるアルミスペーサーを用い、その中空空間内に乾燥剤としてシリカゲル若しくはゼオライトが封入され、該アルミスペーサーの側面には粘着剤としてのブチルゴムが塗布される。なお、特許文献3には中空層支持体としてトゥルーシール社のスイグルシールを用いた例が記載されている。スイグルシールの構造は必ずしも明白ではないが、類似のシール材の情報等を考え合わせると、側面にブチルゴムが形成された樹脂製の中空層支持体と考えられる。 In addition, the techniques disclosed in Patent Document 3 and Patent Document 4 are for realizing a general multilayer glass structure while using an existing window glass. In this case, a so-called aluminum spacer having a substantially hollow rectangular cross section is used as a base material for the hollow layer support, silica gel or zeolite is enclosed as a desiccant in the hollow space, and an adhesive is provided on the side of the aluminum spacer. Of butyl rubber is applied. In addition, Patent Document 3 describes an example using a True Seal watergle seal as a hollow layer support. The structure of the water seal is not always clear, but considering information on similar seal materials, it can be considered as a resin hollow layer support having butyl rubber formed on the side surface.
前記粘着剤として用いられているブチルゴムは、非透湿性に優れたものであるが、ガラスとの接着力は十分ではなく、それだけでは重量の重いガラスを保持することができない。そこで、ガラスがアルミスペーサーの粘着剤(ブチルゴム)から剥がれてしまうのを防止するために、必ず2枚のガラスの対面する表面とアルミスペーサーの背面とで形成される空間を二次シール材で封止して強固な接着を確保する必要がある。また、現場での複層ガラスの組立において、ガラスを安全に保持する必要があることからも、二次シール材による封止に際しては、下辺にセッティングブロックやスポンジゴム等を敷いてガラスを支えるのが普通である。 The butyl rubber used as the pressure-sensitive adhesive is excellent in non-moisture permeability, but does not have sufficient adhesive strength with glass and cannot hold heavy glass alone. Therefore, in order to prevent the glass from being peeled off from the adhesive (butyl rubber) of the aluminum spacer, the space formed by the two glass facing surfaces and the back of the aluminum spacer must be sealed with a secondary sealant. It is necessary to stop and ensure strong adhesion. In addition, since it is necessary to hold the glass safely in the assembly of double-glazed glass at the site, when sealing with a secondary sealant, a setting block or sponge rubber is laid on the lower side to support the glass. Is normal.
また、特許文献4で開示された複層ガラスでは、明細書の記載から明らかなように、貼り合わせたスペーサー付きガラスの小口とスポンジゴムやセッティングブロックの隙間から二次シール材を充填しなければならず、手間がかかるし、セッティングブロックのある箇所において、スペーサーと既設ガラスとスペーサー付きガラスで囲まれた空間に、どのように二次シール材が充填されているのか不明である。さらに、スペーサー付きガラスの小口面がセッティングブロック(もしくはスポンジゴム)に当接された構造では、該空間に二次シール材を充填することは不可能とさえ思われる。いずれにしても、特許文献4で開示された複層ガラスでは、その組立に手間が掛かり、二次シール材の充填も容易ではなく、複層ガラスの耐久性が依然として不十分になる懸念がある。特許文献5は、特許文献4とほぼ同一の技術内容であって、施工現場での組立作業を容易にするものであるが、二次シール材の充填に関しては、特許文献4と同様に容易ではなく、依然として耐久性が不十分になる懸念が残されている。 In addition, in the double-layer glass disclosed in Patent Document 4, as is clear from the description of the specification, the secondary sealing material must be filled from the gap between the edge of the glass with a spacer and the sponge rubber or the setting block. However, it takes time and it is unclear how the secondary sealing material is filled in the space surrounded by the spacer, the existing glass, and the glass with the spacer at the place where the setting block is located. Further, in the structure in which the small edge surface of the glass with the spacer is in contact with the setting block (or sponge rubber), it seems even impossible to fill the space with the secondary sealant. In any case, in the multilayer glass disclosed in Patent Document 4, it takes time to assemble, the secondary sealing material is not easily filled, and the durability of the multilayer glass may still be insufficient. . Patent Document 5 has almost the same technical contents as Patent Document 4 and facilitates assembly work at the construction site. However, as with the case of Patent Document 4, filling of the secondary sealing material is not as easy. There is still a concern that durability will be insufficient.
前記従来の課題を解決するために本発明は、既設の窓ガラスに、中空層支持体を介して、新設の後付けガラスを貼り合わせた複層ガラスであって、該中空層支持体が、両側面に接着剤が塗布又は貼付(以下、塗布等という)された基材と、乾燥剤及び酸素吸収剤からなり、該既設の窓ガラスと該新設の後付けガラスとを、該基材を介して、該基材の両側面に塗布等された接着剤で接着することによって互いに貼り合わせ、さらに該新設の後付けガラスの四辺で、その小口面、中空層支持体の背面及び既設の窓ガラス表面との間をシール材で固定したことを特徴とする複層ガラスを開示する。 In order to solve the above-mentioned conventional problems, the present invention is a multi-layer glass obtained by bonding a newly installed rear glass to an existing window glass via a hollow layer support, and the hollow layer support is formed on both sides. A base material having an adhesive applied or affixed to the surface (hereinafter referred to as application), a desiccant and an oxygen absorber, and the existing window glass and the newly installed rear glass through the base material , And bonded to each other with an adhesive applied on both sides of the base material, and further, the four sides of the newly installed retrofitting glass, the small edge surface, the back surface of the hollow layer support, and the existing window glass surface Disclosed is a double-glazed glass characterized in that a gap is fixed with a sealing material.
図4は、本発明の主要部を示したものである。このような構造にすることによって、既設の窓ガラス10をそのまま利用し、かつ建物の既設の額縁30や窓枠20との間を必ずしもシールによって固定する必要がなく、新設の後付けガラス50と既設の窓ガラス10との間でのみシール材60で固定する複層ガラスを得ることができる。既設の建物の額縁や窓枠との間でシールする必要がないことから、後述するように、従来技術を適用することができなかった引違い窓や上げ下げ窓のような開閉窓についても、その可動性を損なうことなく複層ガラスにすることができる。なお、固定窓の場合には、事情が許すなら、図4の60aの空間の少なくとも一部がシールされることは一向に差し支えない。固定窓は開閉されないことから、窓枠や額縁とシールされたとしても問題は生じないからである。 FIG. 4 shows the main part of the present invention. By adopting such a structure, it is not necessary to use the existing window glass 10 as it is and to fix it between the existing frame 30 and the window frame 20 of the building with a seal, and the newly installed rear glass 50 and the existing glass. It is possible to obtain a double-glazed glass that is fixed with the sealing material 60 only between the window glass 10 and the window glass 10. Since it is not necessary to seal between the frame and window frame of an existing building, as will be described later, open / close windows such as sliding windows and raising / lowering windows, to which the conventional technology could not be applied. Double glass can be obtained without impairing mobility. In the case of a fixed window, if circumstances permit, at least a part of the space 60a in FIG. 4 may be sealed. This is because the fixed window is not opened and closed, and no problem occurs even if it is sealed with the window frame or the frame.
中空層支持体40の詳細を図5に示す。図5(A)は中空アルミスペーサー401を基材とするものであるが、その側面には通常の複層ガラスに用いられているブチルゴムのような粘着剤ではなく、接着剤402が塗布等されている。接着剤を用いているので、ガラスの保持力に優れ、セッティングブロックやスポンジゴムのような部材を用いることなく既設の窓ガラスに貼り付けることができる。 Details of the hollow layer support 40 are shown in FIG. In FIG. 5A, the hollow aluminum spacer 401 is used as a base material, but an adhesive 402 is applied to the side surface instead of a pressure-sensitive adhesive such as butyl rubber that is used for ordinary double-layer glass. ing. Since an adhesive is used, the glass has excellent holding power and can be attached to an existing window glass without using a member such as a setting block or sponge rubber.
さらに、本発明の複層ガラスにおいては、従来技術では必要であったセッティングブロックやスポンジゴムを用いないので、それらによってシール材の充填を邪魔されることがなく、新設の後付けガラスの小口面と既設の窓ガラスの表面との間を丁寧にシールすることができ、またシールの出来映えを容易に確認することができることから、補修も容易となり、シールの信頼性を高めることができる。 Furthermore, in the double-glazed glass of the present invention, the setting block and sponge rubber required in the prior art are not used. Since the space between the existing window glass and the surface of the existing window glass can be carefully sealed and the performance of the seal can be easily confirmed, repair can be facilitated and the reliability of the seal can be improved.
アルミスペーサーの中空部403には、通常用いられているシリカゲルやゼオライト等の乾燥剤404に加えて、酸素吸収剤405を封入することが必須である。通気孔406を通して中空層70に存在する水分を吸着するだけでなく、酸素をも吸収するためである。水分を吸収するのは中空層内で結露が発生するのを防止するためであり、中空層内の酸素を吸収するのは中空層内の圧力を低下させることによって、既設の板ガラス及び新設の後付けガラスが大気圧を受け、中空層支持体を強く押さえつけて接着を強化するためである。このようにすることによって、本発明による複層ガラス構造は、必ずしも額縁や窓枠とシール材で固定しなくとも、ガラスの保持を確実にすることができるのである。さらにガラスの保持を強固にするため、窓枠や額縁との間をシール材で固定してもよいし、補助的な倒れ防止部材を用いることは差し支えない。 In addition to the commonly used desiccant 404 such as silica gel and zeolite, it is essential to enclose an oxygen absorbent 405 in the hollow portion 403 of the aluminum spacer. This is because not only the moisture present in the hollow layer 70 is adsorbed through the vent holes 406 but also oxygen. Moisture is absorbed to prevent dew condensation in the hollow layer, and oxygen in the hollow layer is absorbed by lowering the pressure in the hollow layer so that the existing plate glass and a new retrofit can be installed. This is because the glass is subjected to atmospheric pressure and strongly presses the hollow layer support to strengthen the adhesion. By doing so, the multi-layer glass structure according to the present invention can ensure the holding of the glass without necessarily fixing the frame or the window frame with the sealing material. Further, in order to strengthen the holding of the glass, the space between the window frame and the frame may be fixed with a sealing material, or an auxiliary fall prevention member may be used.
中空層支持体の基材としては、前記した一般的なアルミスペーサーの他、アルミニウム板、アクリルシート、ブチルゴム等の樹脂基材、あるいはアクリル系接着剤を含浸させた不織布等を用いることができる。図5(B)は、樹脂基材411に乾燥剤414と酸素吸収剤415が含浸され、両側面には接着剤412が塗布等された構造を有する中空層支持体である。樹脂基材411としてはシリコーンやEPDM等の発泡樹脂が用いることができる。その場合、発泡樹脂を透過して水分が中空層内に拡散するのを防止するため、中間に水分バリヤー416を挿入するのが望ましい。水分バリヤーとしては、アルミフォイルやポリプロピレンフィルム等を用いることができる。 As the substrate for the hollow layer support, in addition to the general aluminum spacer described above, a resin substrate such as an aluminum plate, an acrylic sheet or butyl rubber, or a nonwoven fabric impregnated with an acrylic adhesive can be used. FIG. 5B shows a hollow layer support having a structure in which a resin base material 411 is impregnated with a desiccant 414 and an oxygen absorbent 415 and an adhesive 412 is applied on both side surfaces. As the resin base material 411, a foamed resin such as silicone or EPDM can be used. In that case, it is desirable to insert a moisture barrier 416 in the middle in order to prevent moisture from diffusing into the hollow layer through the foamed resin. As the moisture barrier, aluminum foil, polypropylene film or the like can be used.
本発明においては、中空層支持体の基材としては、一般的なアルミスペーサーよりも樹脂基材や不織布を用いる方が望ましい。本発明は、既設の窓ガラスと新設の後付けガラスとを、中空層支持体の基材を介して、基材側面に塗布等された接着剤で接着することを特徴としているが、ガラスと基材との間の接着剤による接着を引き剥がそうとする力が働いたとき、基材が樹脂や不織布である方が、基材自身が伸縮することにより、その力を逃がすことができるからである。 In the present invention, it is desirable to use a resin base material or a nonwoven fabric as a base material for the hollow layer support rather than a general aluminum spacer. The present invention is characterized in that an existing window glass and a new retrofitted glass are bonded to each other with an adhesive applied to the side surface of the substrate through the substrate of the hollow layer support. When a force is applied to peel off the adhesive bond with the material, the base material is a resin or non-woven fabric, and the base material itself can be expanded and contracted to release the force. is there.
次に、住宅用引違い窓の障子に既設の窓ガラスが装着されているケースにおける、本発明の複層ガラスの構造を図6に示す。住宅用引違い窓では、典型的に、額縁30に窓枠20が設けられ、室内側窓ガラス11は室内側障子15に取り付けられ、室外側窓ガラス12は室外側障子16に取り付けられている。窓枠にはレール201、202が設けられ、障子には戸車151、152が設けられ、レールの上を戸車がスライドすることにより障子が開閉できる構造になっている。障子の幅は20mm程度であり、中央に厚み3〜4mm程度の既設の窓ガラスが装着されているので、窓ガラスの両側で、ガラス表面と障子の最外面との間には高々8mm程度のスペースしかない。そして、既設の窓ガラスを利用したまま複層ガラスとする場合には、新設の後付けガラス51、52の厚みを3〜4mmとすると、中空層支持体41、42の厚さは4mm程度以下にする必要があり、前記した中空層支持体(図5(A)及び(B))を用いることは困難となる。 Next, FIG. 6 shows the structure of the multi-layer glass of the present invention in a case where an existing window glass is attached to a sliding sliding door for a house. In a residential sliding window, a window frame 20 is typically provided on the frame 30, the indoor window glass 11 is attached to the indoor shoji 15, and the outdoor window glass 12 is attached to the outdoor shoji 16. . Rails 201 and 202 are provided on the window frame, and doors 151 and 152 are provided on the shoji, so that the door can be opened and closed by sliding the door on the rail. The width of the shoji is about 20 mm, and an existing window glass with a thickness of about 3 to 4 mm is mounted in the center. Therefore, on both sides of the window glass, there is about 8 mm between the glass surface and the outermost surface of the shoji. There is only space. And when using the existing window glass as a multilayer glass, if the thickness of the new retrofitted glasses 51 and 52 is 3 to 4 mm, the thickness of the hollow layer supports 41 and 42 is about 4 mm or less. Therefore, it is difficult to use the hollow layer support (FIGS. 5A and 5B).
このようなケースでは、図5(C)に示したような、2〜3mm程度の厚さのアクリルシートやアルミニウム板を基材421として、両側面に1〜2mm程度の厚みの接着剤422が塗布等された構造の中空層支持体を用いることができる。接着剤の中に乾燥剤424及び酸素吸収剤425を練り混んでもよいが、図7に示したように、乾燥剤及び酸素吸収剤を中空層の内部に封入してもよい。例えば、乾燥剤及び酸素吸収剤を封入した袋をガラス面や中空層支持体に貼付しておくことにより、既設の窓ガラスと新設の後付けガラスを貼り合わせると同時に、乾燥剤及び酸素吸収剤を中空層に封入することができる。 In such a case, an acrylic sheet or aluminum plate having a thickness of about 2 to 3 mm as shown in FIG. 5C is used as a base material 421, and an adhesive 422 having a thickness of about 1 to 2 mm is formed on both sides. A hollow layer support having a coated structure can be used. The desiccant 424 and the oxygen absorbent 425 may be mixed in the adhesive, but as shown in FIG. 7, the desiccant and the oxygen absorbent may be enclosed in the hollow layer. For example, by attaching a bag containing a desiccant and an oxygen absorbent to a glass surface or a hollow layer support, the existing window glass and a new retrofitted glass are bonded together, and at the same time, the desiccant and the oxygen absorbent are added. It can be enclosed in a hollow layer.
既設窓ガラスが装着された開閉窓の障子の厚さがさらに薄い時には、新設の窓ガラスを装着するためのスペースはさらに限定されることになる。そのような場合には、簡易的に両面接着テープを用いることができる。両面接着テープとしては、アクリルシートや不織布の両面に感圧型接着剤を形成した厚さ2〜4mm程度のものを用いることができる。この場合、既設の窓ガラスに両面接着テープを貼付し、両面接着テープに付いている離型紙を剥がした後、新設の後付けガラスを貼り付けるだけでよい。この場合も、中空層の水分と酸素を吸着し吸収するために、中空層内部に乾燥剤及び酸素吸収剤を封入することは、既に述べた理由により、必須である。 When the thickness of the shoji of the opening / closing window to which the existing window glass is attached is further reduced, the space for installing the new window glass is further limited. In such a case, a double-sided adhesive tape can be used simply. As the double-sided adhesive tape, a tape having a thickness of about 2 to 4 mm in which a pressure-sensitive adhesive is formed on both sides of an acrylic sheet or a nonwoven fabric can be used. In this case, it is only necessary to apply a double-sided adhesive tape to an existing window glass, peel off the release paper attached to the double-sided adhesive tape, and then attach a new post-installation glass. Also in this case, in order to adsorb and absorb the moisture and oxygen in the hollow layer, it is essential to enclose the desiccant and the oxygen absorbent inside the hollow layer for the reasons already described.
前記した種々の構造の中空層支持体に用いることのできる接着剤としては、アクリル系接着剤が望ましい。アクリル系接着剤は接着力が強く、剥がれにくく、耐光性・耐候性にも優れているからである。アクリル系接着剤は、常温においては少なくとも10kg/cm2程度、50℃以上の高温においても1kg/cm2程度の接着力を有している。そして、約1cm幅のアクリル系接着剤を基材に塗布等した中空層支持体をガラスの四周に貼付した場合、四周の長さが約400cm程度の後付けガラスを貼り合わせる場合、400cm2程度の接着面積が確保できることになる。接着力が低下する50℃程度の高温を想定した場合でも、400kgの重量を有するガラスを保持することができることになる。従って、通常のガラスが1m2当たり10kgから20kg程度の重量であることからすると、アクリル系接着剤は後付けガラスを保持するのに十分な接着力を有しているのである。アクリル系以外の接着剤を用いてもよいが、後付けガラスを保持するのに十分な接着力を有していることが必須である。 As an adhesive that can be used for the hollow layer support having various structures described above, an acrylic adhesive is desirable. This is because acrylic adhesives have strong adhesive strength, are difficult to peel off, and are excellent in light resistance and weather resistance. The acrylic adhesive has an adhesive strength of at least about 10 kg / cm 2 at room temperature and about 1 kg / cm 2 even at a high temperature of 50 ° C. or higher. And when the hollow layer support body which apply | coated the acrylic adhesive of about 1 cm width to the base material is affixed on the four circumferences of glass, when pasting glass with a length of the circumference of about 400 cm is pasted, about 400 cm 2 An adhesion area can be secured. Even when a high temperature of about 50 ° C. at which the adhesive strength is reduced is assumed, glass having a weight of 400 kg can be held. Therefore, given that normal glass weighs about 10 kg to 20 kg per m 2 , the acrylic adhesive has sufficient adhesive strength to hold the post-attached glass. Adhesives other than acrylic may be used, but it is essential to have sufficient adhesive strength to hold the retrofitted glass.
接着剤が塗布等された中空層支持体は、新設の後付けガラスもしくは既設の窓ガラスの四周に途切れることなく接着しなければならない。周辺からの水分の侵入を防止し、接着力を低下させないためである。接着幅は、前記したように1cm(10mm)程度あれば十分であるが、5mmから30mm程度の範囲であることが好ましい。接着幅が大きいほど接着力も大きくなるが、窓全体の意匠の面からは30mm程度以下であることが望ましい。 The hollow layer support to which the adhesive has been applied, etc., must be bonded without interruption to the four sides of the newly installed retrofitted glass or existing window glass. This is to prevent moisture from entering from the periphery and not lower the adhesive force. As described above, an adhesive width of about 1 cm (10 mm) is sufficient, but a range of about 5 mm to 30 mm is preferable. The larger the bonding width is, the larger the bonding force is, but it is preferably about 30 mm or less from the design surface of the entire window.
本発明では、図4に示したように、新設の後付けガラスの四辺全てにおいて、後付けガラス50の小口面50a、中空層支持体40の背面40a及び既設の窓ガラス10の表面10aをシール材60で固定する。複層ガラスとしての耐久性の確保及び新設の後付けガラスの既設窓ガラスへの接着性の強化のためである。また、新設の後付けガラスの小口に人が当たって怪我をすることのないよう安全性を高めることにもなる。シール材としては、水分の透湿性が小さく、ガラスとの接着力の大きなものが望ましいが、一般的なポリサルファイド系やシリコーン系のシール材を用いることができる。固定窓の場合には、前記したように、空間60aの部分の少なくとも一部にシール材を注入して額縁や窓枠と固定しても差し支えない。 In the present invention, as shown in FIG. 4, on all four sides of the newly installed retrofitted glass, the small edge surface 50 a of the retrofitted glass 50, the back surface 40 a of the hollow layer support 40, and the surface 10 a of the existing window glass 10 are sealed 60. Secure with. This is to ensure durability as a double-glazed glass and to strengthen the adhesion of newly installed retrofitted glass to the existing window glass. It will also increase safety so that people will not be hurt by hitting the mouthpiece of the new retrofit glass. As the sealing material, a material having a low moisture permeability and a large adhesive force with glass is desirable, but a general polysulfide-based or silicone-based sealing material can be used. In the case of the fixed window, as described above, a sealing material may be injected into at least a part of the space 60a and fixed to the frame or the window frame.
本発明では、特許文献3のように、必ずしも新設の後付けガラスを窓枠若しくは額縁とシール材の固定する必要はなく、また、特許文献4のように新設の後付けガラスと窓枠及び既設窓ガラスとの間にシール材を充填するものでもない。新設の後付けガラス50は、中空層支持体40を介して接着剤で既設の窓ガラス10に接着され、さらにシール材60で固定するだけでよい。そこでは、前記したように、新設の後付けガラスを既設の窓ガラスに対して強く保持するため、中空層70に乾燥剤とともに酸素吸収剤を封入しておくことが必須となる。こうすることによって、中空層内に含まれる酸素ガスの一部が酸素吸収剤に吸収され、中空層が減圧され、新設の後付けガラスが大気圧によって既設の窓ガラスに対して押し付けられる力が働くことになり、保持力が増加することになるからである。 In the present invention, it is not always necessary to fix the newly installed retrofitted glass to the window frame or the frame and the sealing material as in Patent Document 3, and the newly installed retrofitted glass, the window frame and the existing window glass as in Patent Document 4. Neither is it filled with a sealing material. The new retrofitted glass 50 may be bonded to the existing window glass 10 with an adhesive via the hollow layer support 40 and further fixed with the sealing material 60. In this case, as described above, it is essential to enclose the oxygen absorber together with the desiccant in the hollow layer 70 in order to hold the newly installed retrofitted glass strongly against the existing window glass. By doing so, part of the oxygen gas contained in the hollow layer is absorbed by the oxygen absorbent, the hollow layer is depressurized, and the force that the newly installed rear glass is pressed against the existing window glass by atmospheric pressure works. This is because the holding force increases.
酸素吸収剤としては、一般的に用いられている鉄粉やアスコルビン酸等を用いることができる。鉄粉は、水分の作用を受けて徐々に酸化する際に、酸素を吸収する性質を利用するものであって、本発明に用いるのに好都合である(特許文献6及び特許文献7)。従って、鉄粉の作用により、中空層に残存する水分の作用を受けて酸素が吸収され、中空層内の圧力を低下させることができる。その後は、乾燥剤が吸収した水分が放出される際に、徐々に酸素を吸収することになる。従って、鉄粉の酸素吸収作用は短期間に終わることなく、その効果が長く持続し、中空層内の圧力を徐々に低下させることができる。酸素吸収剤は、前記したように、中空アルミスペーサーの中空空間に乾燥剤とともに封入するか、樹脂基材に練り混むか、あるいは乾燥剤とともに通気性のある袋に入れて中空層内に封入して用いることができる。 As the oxygen absorbent, generally used iron powder, ascorbic acid, or the like can be used. Iron powder utilizes the property of absorbing oxygen when it is gradually oxidized under the action of moisture, and is convenient for use in the present invention (Patent Documents 6 and 7). Therefore, by the action of the iron powder, oxygen is absorbed by the action of moisture remaining in the hollow layer, and the pressure in the hollow layer can be reduced. Thereafter, oxygen is gradually absorbed when the moisture absorbed by the desiccant is released. Therefore, the oxygen absorption action of the iron powder does not end in a short period of time, the effect lasts for a long time, and the pressure in the hollow layer can be gradually reduced. As described above, the oxygen absorbent is enclosed in the hollow space of the hollow aluminum spacer together with the desiccant, kneaded into the resin base material, or placed in a breathable bag together with the desiccant and enclosed in the hollow layer. Can be used.
乾燥剤の量は、中空層の容積1リッター当たり5g程度あればよい。中空層内部に残存する水分を除去し、中空層支持体やガラスとの界面を拡散してくる水分を除去するには、この程度の量で十分である。一方、中空層に存在する酸素を徐々に吸収し減圧するための酸素吸収剤の量としても1リッター当たり5g程度を封入すればよい。一般に酸素吸収剤の酸素吸収能は1g当たり20cc程度であり、1リッター当たり5gも封入すれば、最終的に100cc(10%)を吸収することになるが、それまで徐々に酸素を吸収することによって、中空層の減圧効果が持続するからである。 The amount of the desiccant may be about 5 g per liter of the hollow layer volume. This amount is sufficient for removing moisture remaining inside the hollow layer and removing moisture diffusing at the interface with the hollow layer support or glass. On the other hand, the amount of the oxygen absorbent for gradually absorbing and depressurizing the oxygen present in the hollow layer may be about 5 g per liter. In general, the oxygen absorbent capacity of oxygen absorber is about 20cc per gram, and if 5g per liter is sealed, it will eventually absorb 100cc (10%), but gradually absorb oxygen until then. This is because the pressure reducing effect of the hollow layer is maintained.
なお、可動の開閉窓においても後付けガラスの保持力を補強するために、図6における空間61a及び62aの部分の少なくとも一部にシールを注入して障子と固定してもよい。障子からはみ出さないようにシール材を注入する限り、障子の開閉を妨げないからである。あるいは、開閉を妨げない範囲であれば、後付けガラスと障子との間に化粧板を設けてもよい。化粧板は、窓全体の美観を損なわないように、障子と接着によって固定して、新設の後付けガラスの脱落を防止する支えとして利用することができる。化粧板は、新設の後付けガラスの脱落を防止する用に供することができれば、上辺部のみに設けてもよいし、上下辺部に設けてもよいし、左右辺部に設けてもよいが、開閉を妨げるものであってはならない。 In order to reinforce the holding power of the retrofitted glass even in the movable opening / closing window, a seal may be injected into at least part of the spaces 61a and 62a in FIG. This is because as long as the sealing material is injected so as not to protrude from the shoji, opening and closing of the shoji is not hindered. Alternatively, a decorative plate may be provided between the retrofitted glass and the shoji as long as it does not hinder the opening and closing. The decorative board can be used as a support for preventing the fall of the newly installed retrofitted glass by fixing it with a shoji so as not to impair the aesthetic appearance of the entire window. The decorative plate may be provided only on the upper side, may be provided on the upper and lower sides, or may be provided on the left and right sides, as long as it can be used for preventing falling off of the newly installed retrofitted glass. It must not interfere with opening and closing.
本発明によれば、既存の窓ガラスを利用して無駄なく簡便に複層ガラスを得ることができる。新設の後付けガラスは、既設の窓ガラスに接着及びシールするだけで十分であるので、これまで後付けガラスを並設することによって複層ガラス化することができなかった引違い窓や上げ下げ窓のような可動の開閉窓の窓ガラスをも複層ガラス化することができる。施工に際して、緩衝材やセッティングブロックを用いる必要もないので、取り付けが容易である。必ずしも窓枠や額縁との間がシール材で固定する必要がないので、複層ガラスの取替の際には、窓枠や額縁との関係は無関係に、複層ガラスだけを単独で取り外すこともできる。 According to the present invention, a multi-layer glass can be easily obtained without waste using an existing window glass. Newly installed retrofitted glass only needs to be bonded and sealed to the existing window glass, so it has not been possible to convert it to double-glazing by arranging the retrofitted glass side by side. The window glass of a movable movable opening / closing window can also be made into a multi-layer glass. Since it is not necessary to use a cushioning material or a setting block at the time of construction, installation is easy. Since it is not always necessary to fix the window frame and frame with a sealant, when replacing the double-glazed glass, remove the double-glazed glass alone, regardless of the relationship with the window frame or frame. You can also.
また、本発明によれば、複層ガラスの中空層が酸素吸収剤によって減圧されるので、複層ガラスのガラス面が大気圧によって押し付けられることになり、ガラスが剥がれにくくなり、耐久性も向上する。 Further, according to the present invention, since the hollow layer of the multilayer glass is depressurized by the oxygen absorbent, the glass surface of the multilayer glass is pressed by the atmospheric pressure, the glass is hardly peeled off, and the durability is improved. To do.
本発明の実施態様は、既に図4及び図6に示したとおりである。また、本発明に用いることのできる中空層支持体及び乾燥剤と酸素吸収剤の含有態様も図5及び図7に例示したとおりである。以下、実施例を示してさらに本発明を詳述する。 The embodiment of the present invention is as already shown in FIGS. Further, the hollow layer support that can be used in the present invention and the mode of inclusion of the desiccant and the oxygen absorbent are also as illustrated in FIGS. Hereinafter, the present invention will be further described in detail with reference to examples.
幅500mm x 高さ800mm x 厚さ3mmの板ガラス2枚を、図6に示したように、引き違い用単板サッシ(トステム社製デュオSG)の室外側障子及び室内側障子に装着して、既設窓ガラスとした。次に、幅480mm x 高さ780mm x 厚さ3mmの板ガラス2枚を用意し、その四周に、ガラス端から10mmの幅で、両面テープを貼付した。この板ガラスの表面に、酸素吸収剤(三菱ガス化学製パウチ型)6個(約6gに相当する)を貼付し、さらに市販のシリカゲル乾燥剤6g(紙包袋入り3個)も同様に配置し、新設の後付けガラスとした。この新設の後付けガラスを、酸素吸収剤及び乾燥剤が中空層側にくるようにして、それぞれ、室外側障子及び室内側障子に装着された既設の窓ガラスに貼り付けた。両面テープとしては、3M社製の9455番(商品名:ベータテープ)を用いた。アクリル系不織布からなる基材の両側にアクリル系接着剤が塗布されたものであって、厚さ約2mmのものを2枚重ねて用いた。最後に、新設の後付けガラスの小口面(端面)、両面テープの背面及び既設の窓ガラス表面の間を、コーキング用ガンを用いてシリコーン系シール材(信越化学社製KE42)で封止することによって、本発明による複層ガラスを作製した。 As shown in FIG. 6, two flat glass sheets having a width of 500 mm × a height of 800 mm × a thickness of 3 mm are attached to the outdoor shoji and the indoor shoji of a single plate sash for sliding (Tostem Duo SG), The existing window glass was used. Next, two plate glasses having a width of 480 mm × a height of 780 mm × a thickness of 3 mm were prepared, and a double-sided tape was affixed to the four circumferences with a width of 10 mm from the glass edge. Six oxygen absorbers (pouch type made by Mitsubishi Gas Chemical) (corresponding to about 6 g) are affixed to the surface of this plate glass, and 6 g of commercially available silica gel desiccant (3 in a paper bag) are also arranged in the same manner. The newly installed retrofitted glass. This newly installed retrofitted glass was affixed to the existing window glass attached to the outdoor shoji and the indoor shoji, respectively, so that the oxygen absorbent and the desiccant were on the hollow layer side. As the double-sided tape, No. 9455 (trade name: Beta Tape) manufactured by 3M Company was used. An acrylic adhesive was applied on both sides of a base material made of an acrylic nonwoven fabric, and two sheets having a thickness of about 2 mm were used. Finally, seal the gap between the rear face of the newly installed glass (end face), the back of the double-sided tape, and the existing window glass surface with a silicone sealant (KE42 manufactured by Shin-Etsu Chemical Co., Ltd.) using a caulking gun. Thus, a multilayer glass according to the present invention was produced.
本実施例では、単板用サッシに装着された既設窓ガラスの両側には、単板用サッシの最外面(いわゆる、つら面)との間に約7mmの間隔しかないが、本実施例の構成である3mm厚の新設板ガラスと4mm厚の両面テープからなる中空層支持体がちょうど納まる厚みであって、引き違い窓の開閉にはなんら問題は生じなかった。 In this embodiment, there is only an interval of about 7 mm between both sides of the existing window glass mounted on the single plate sash and the outermost surface (so-called icicle surface) of the single plate sash. The thickness was just enough to accommodate the 3 mm-thick new plate glass and the 4 mm-thick double-sided tape, and there was no problem in opening and closing the sliding window.
本実施例の複層ガラス窓は、神奈川県産業技術センター内(海老名市下今泉705−1)で作製した。そして、室内側障子に取り付けられた複層ガラス厚みが時間とともにどのように変化するかを、同センター内にある機械材料技術部・精密測定室において測定した。この精密測定室内は20℃の恒温に保たれていた。厚み測定は、三次元座標測定機UPMC
850 CARAT(東京精密社製)を用いて、複層ガラスの中央部(対角線の交わる点)において、既設窓ガラスの外側表面の座標点と新設窓ガラスの外側表面の座標点を測定することにより行った。既設窓ガラス及び新設の板ガラスの厚み自体は変動しないことから、測定された厚みの変化は、中空層の厚みの変化に対応するものとした。
The double-glazed glass window of this example was produced in the Kanagawa Prefectural Industrial Technology Center (Shimaimazumi 705-1, Ebina City). Then, how the thickness of the double-layer glass attached to the indoor shoji was changed with time was measured in the mechanical material engineering department / precision measurement room in the center. The precision measurement chamber was kept at a constant temperature of 20 ° C. Thickness measurement is 3D coordinate measuring machine UPMC
By using 850 CARAT (manufactured by Tokyo Seimitsu Co., Ltd.), by measuring the coordinate point of the outer surface of the existing window glass and the coordinate point of the outer surface of the new window glass at the center of the multilayer glass (the point where the diagonal lines intersect) went. Since the thicknesses of the existing window glass and the new plate glass themselves do not vary, the measured change in thickness corresponds to the change in the thickness of the hollow layer.
このようにして測定した複層ガラスの厚み変化を表1及び図8に示した。本発明による複層ガラスの作製後、約8日間に渡って厚みの変化を測定した結果、作製後の初期には、中空層に微量含まれていた水分の吸収によると思われる厚みの減少が観察され、その後も酸素吸収剤による酸素ガスの吸収に起因すると考えられる厚みの減少が継続して観察された。最終的に、作製後8日間(11604分)経過した後には、厚みは9.8311mmとなり、作製直後の厚み9.9099mmから0.0788mm減少したことがわかった。これは、中空層厚みが作製直後の4mmから3.9212mmまで約2%減少したことを意味する。このように本発明の複層ガラスにおいては、中空層に乾燥剤だけでなく酸素吸収剤を含有させた結果、中空層の容積が継続して徐々に減少し、複層ガラスを構成する窓ガラスが中空層支持体に向けて、大気圧によって押し付けられていることがわかった。 The thickness change of the multi-layer glass measured in this way is shown in Table 1 and FIG. As a result of measuring the change in thickness over about 8 days after the production of the multi-layer glass according to the present invention, in the initial stage after the production, there was a decrease in thickness that seems to be due to the absorption of a small amount of moisture contained in the hollow layer. Observed, and thereafter continued to observe a decrease in thickness that was attributed to the absorption of oxygen gas by the oxygen absorbent. Finally, after 8 days (11604 minutes) after the production, the thickness became 9.831 mm, and it was found that the thickness was reduced by 0.0788 mm from the thickness of 9.9099 mm immediately after the production. This means that the hollow layer thickness has decreased by about 2% from 4 mm immediately after fabrication to 3.9212 mm. As described above, in the multilayer glass of the present invention, as a result of containing not only the desiccant but also the oxygen absorbent in the hollow layer, the volume of the hollow layer continuously decreases and the window glass constituting the multilayer glass Was pressed by the atmospheric pressure toward the hollow layer support.
1、1‘:一般的な複層ガラスを構成する2枚の板ガラス
4:一般的な複層ガラスを構成するアルミスペーサー
6:一般的な複層ガラスを構成する二次シール材
7:一般的な複層ガラスにおける中空層
8、8‘:一般的な複層ガラスを構成する一次シール材(粘着剤)
9:一般的な複層ガラスを構成する乾燥剤
10、11、12:既設の窓ガラス
15:室内側障子、16:室外側障子、20:窓枠、30:額縁
40、41、42:中空層支持体
50、51、52:新設の後付けガラス
60、61、62:シール材、70:中空層
151、152:戸車、201、202:レール
401、411、421、431:中空層支持体の基材
402、412、422、432:接着剤
403:中空アルミスペーサーの中空部
404、414、424、434:乾燥剤
405、415、425、435:酸素吸収剤
406:通気孔、416:水分バリヤー
1, 1 ': Two sheet glasses constituting a general double-layer glass 4: Aluminum spacer constituting a general double-layer glass 6: Secondary sealing material 7 constituting a general double-layer glass: General Hollow layers 8 and 8 'in a multilayer glass: primary sealing material (adhesive) constituting a general multilayer glass
9: Desiccant constituting general multilayer glass 10, 11, 12: Existing window glass 15: Indoor shoji, 16: Outdoor shoji, 20: Window frame, 30: Frame 40, 41, 42: Hollow Layer supports 50, 51, 52: Newly installed rear glass 60, 61, 62: Sealing material, 70: Hollow layer 151, 152: Door cart, 201, 202: Rail 401, 411, 421, 431: Hollow layer support Substrate 402, 412, 422, 432: Adhesive 403: Hollow part of hollow aluminum spacer 404, 414, 424, 434: Desiccant 405, 415, 425, 435: Oxygen absorber 406: Vent, 416: Moisture barrier
Claims (2)
A multi-layer glass in which a new retrofitted glass is bonded to an existing window glass through a hollow layer support, and the hollow layer support is formed from a base material on which adhesive is applied or pasted on both side surfaces. The existing window glass and the new retrofitted glass are bonded to each other by bonding with an adhesive applied or pasted on both sides of the base material via the base material, and supporting the hollow layer A desiccant and an oxygen absorbent are enclosed in a hollow layer surrounded by a body, the existing window glass, and the new retrofitted glass, and the small side surface of the new retrofitted glass, A double-glazed glass comprising a back surface and a surface of the existing window glass covered with a sealing material.