JP2014189656A - 自動車内装材用粘着剤および自動車内装材用粘着シート - Google Patents
自動車内装材用粘着剤および自動車内装材用粘着シート Download PDFInfo
- Publication number
- JP2014189656A JP2014189656A JP2013066950A JP2013066950A JP2014189656A JP 2014189656 A JP2014189656 A JP 2014189656A JP 2013066950 A JP2013066950 A JP 2013066950A JP 2013066950 A JP2013066950 A JP 2013066950A JP 2014189656 A JP2014189656 A JP 2014189656A
- Authority
- JP
- Japan
- Prior art keywords
- automobile interior
- pressure
- sensitive adhesive
- weight
- rosin ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】本発明は、高温環境での凝集力、および低温環境での低極性被着体との密着性を両立できる自動車内装材用粘着剤および自動車内装材用粘着シートの提供を目的とする。
【解決手段】カルボキシル基および水酸基を有するアクリル系ポリマー(A)と、水酸基価10〜130mgKOH/gの、重合ロジンエステルおよび水素化ロジンエステを含む粘着付与樹脂(B)と、イソシアネート硬化剤(C)とを含む、自動車内装材用粘着剤である。
【選択図】図1
【解決手段】カルボキシル基および水酸基を有するアクリル系ポリマー(A)と、水酸基価10〜130mgKOH/gの、重合ロジンエステルおよび水素化ロジンエステを含む粘着付与樹脂(B)と、イソシアネート硬化剤(C)とを含む、自動車内装材用粘着剤である。
【選択図】図1
Description
本発明は、自動車等の車内に使用する粘着剤に関する。
従来、防音材や車内装飾材等の内装材を自動車に貼り付けるときは接着剤を使用していたが、取り扱いの容易な粘着テープを使用する場合が増えている。しかし、自動車は、夏季は高温環境で使用され、冬季は低温環境で使用されるため内装材に使用する粘着テープにも高温と低温と環境が変わった場合でも浮きや剥がれが生じない性能が要求されていた。
そこで、特許文献1では、アクリル系ポリマーに安定化ロジンエステル樹脂を配合した水性の粘着剤が開示されている。また、特許文献2では、アクリル系ポリマーに安定化ロジンエステル樹脂を配合した水性の粘着剤が開示されている。
しかし、従来の粘着剤は、高温環境で使用すると凝集力が不足し、剥がれが生じるなど耐熱性が不足する問題があった。また、低温環境で粘着シートをポリオレフィンなどの低極性被着体に貼り付けたときに浮き・剥がれが生じる場合あった。
本発明は、高温環境での凝集力、および低温環境での低極性被着体との密着性を両立できる自動車内装材用粘着剤および自動車内装材用粘着シートの提供を目的とする。
本発明は、カルボキシル基および水酸基を有するアクリル系ポリマー(A)と、水酸基価10〜130mgKOH/gの、重合ロジンエステルおよび水素化ロジンエステルから選ばれる1種以上の粘着付与樹脂(B)と、イソシアネート硬化剤(C)とを含む、自動車内装材用粘着剤である。
上記構成の本発明によれば、自動車内装材用粘着剤を加工した粘着シートにおいて、粘着剤層は、アクリル系ポリマー、重合ロジンエステルおよび水素化ロジンエステルは水酸基を有するためのイソシアネート硬化剤による架橋ネットワークに組み込まれるか、極性部位の分子間力により、高温環境で凝集力を維持しつつ、粘着力を得やすい。一方、低温環境では、架橋ネットワークに組み込まれていない重合ロジンエステルおよび水素化ロジンエステルの存在、ならびに重合ロジンエステルおよび水素化ロジンエステルは架橋ネットワークに組み込まれた場合でも適度なモビリティがあるため、粘着剤層は、ポリオレフィン等の低極体に対して密着性を維持しやすい特性が得られた。
本発明により高温環境での凝集力、および低温環境での低極性被着体との密着性を両立できる自動車内装材用粘着剤および自動車内装材用粘着シートを提供できた。
本明細書で(メタ)アクリレートは、アクリレートおよびメタクリレートを含むモノマーをいう。また、本明細書で自動車は、列車、船舶、航空機を含む車体を総称するものである。
本発明の自動車内装材用粘着剤は、アクリル系ポリマー(A)、粘着付与樹脂(B)およびイソシアネート硬化剤(C)を含むものである。この自動車内装材用粘着剤は、両面粘着テープや、キャスト粘着テープに加工した上で、内装材に貼付した上で、自動車に貼り付けて使用することができる。この内装材は、人が乗る自動車車内に使用する内装材のみではなく、エンジンルームやエンジンルームなどで使用する吸音材、緩衝材、カーペット等を含み、広く自動車の車内で使用する部材を意味する。
本発明の自動車内装材用粘着剤をさらに詳しく説明すると前記アクリル系ポリマー(A)は、カルボキシル基含有モノマーと、水酸基含有モノマーとを含むモノマー混合物を共重合したものであり、前記粘着付与樹脂(B)は、水酸基価10〜130mgKOH/gの重合ロジンエステルもしくは水素化ロジンエステルであることが必要である。
そして本発明の自動車内装材用粘着剤は、高温環境下でもハガレやズレが生じにくい。この特性については、後述記載の実施例において、耐熱クリープ性や耐熱保持力に優れていることからも明らかである。
そして本発明の自動車内装材用粘着剤は、高温環境下でもハガレやズレが生じにくい。この特性については、後述記載の実施例において、耐熱クリープ性や耐熱保持力に優れていることからも明らかである。
本発明においてアクリル系ポリマー(A)は、カルボキシル基および水酸基を有するポリマーである。そしてアクリル系モノマーを必須とし、必要に応じてアクリル系モノマー以外のビニル系モノマーを含むモノマーを共重合して得るポリマーである。共重合の方法は、溶液重合、乳化重合、懸濁重合、塊状重合など公知の重合方法を利用できるが、本発明では、反応制御や物性コントロールが容易な溶液重合が好ましい。
前記モノマーは、カルボキシル基含有モノマー、水酸基含有モノマーおよびその他共重合可能なモノマーを使用できる。
前記カルボキシル基含有モノマーは、具体的には、例えばアクリル酸、メタクリル酸、イタコン酸、マレイン酸等が挙げられる。カルボキシル基含有モノマーは、全モノマーのうち0.1〜10重量%用いることが好ましく、1〜8重量%がより好ましい。0.1〜10重量%使用することで、凝集力と密着性を両立しやすくなる。
前記カルボキシル基含有モノマーは、具体的には、例えばアクリル酸、メタクリル酸、イタコン酸、マレイン酸等が挙げられる。カルボキシル基含有モノマーは、全モノマーのうち0.1〜10重量%用いることが好ましく、1〜8重量%がより好ましい。0.1〜10重量%使用することで、凝集力と密着性を両立しやすくなる。
水酸基含有モノマーは、例えば、2−ヒドロキシエチル(メタ)アクリレート、3−ヒドロキシプロピル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、ヒドロキシプロピル(メタ)アクリレート等が挙げられる。水酸基含有モノマーは、全モノマーのうち0.01〜0.2重量%用いることが好ましく、0.05〜0.15重量%がより好ましい。0.01〜0.2重量%用いることでイソシアネート硬化剤との架橋密度をより調整しやすくなり、凝集力と密着性をより両立しやすくなる。
アクリル系ポリマー(A)の合成には、上記以外のモノマーとして、アルキル(メタ)アクリレート、およびその他ビニルモノマーを使用することができる。
アルキル(メタ)アクリレートとしては、例えば、(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸ブチル、(メタ)アクリル酸プロピル、(メタ)アクリル酸ペンチル、(メタ)アクリル酸ヘキシル、(メタ)アクリル酸2−エチルヘキシル、(メタ)アクリル酸オクチル、(メタ)アクリル酸ノニル、(メタ)アクリル酸デシル、(メタ)アクリル酸ドデシル、(メタ)アクリル酸ラウリル、
その他ビニルモノマーは、グリシジル(メタ)アクリレート、N−メチロールアクリルアミド、(メタ)アクリルアミド、酢酸ビニル、アクリルニトリル、スチレン、α―メチルスチレン等が挙げられる。これに限定するものではない。
これらモノマーは、単独または2種以上併用できる。
その他ビニルモノマーは、グリシジル(メタ)アクリレート、N−メチロールアクリルアミド、(メタ)アクリルアミド、酢酸ビニル、アクリルニトリル、スチレン、α―メチルスチレン等が挙げられる。これに限定するものではない。
これらモノマーは、単独または2種以上併用できる。
本発明においてアクリル系ポリマー(A)の重合平均分子量は、30万〜150万が好ましく、50万〜120万がより好ましい。重合平均分子量が30万に満たない場合は、凝集力が低下、すなわち耐熱性が不足するなどの恐れがある。一方、150万を越えると凝集力が高くなり、表面極性の低い被着体に対する密着性が低下、すなわち粘着力や耐熱クリープ性が低下するなどの恐れがある。なお本発明において重量平均分子量とはGPC測定で求めたポリスチレン換算の重量平均分子量であり、GPC測定条件は以下のとおりである。装置:SHIMADZU Prominence((株)島津製作所製)カラム:TOSOH TSK−GEL GMHXL(東ソー(株)製)を使用。溶媒:テトラヒドロフラン、流速:0.5ml/min、温度:40℃、試料濃度:0.1wt%、試料注入量:100μl。
本発明において共重合には、過酸化物系の重合開始剤やアゾビス系の重合開始剤等、従来公知の重合開始剤を使用することができる。有機過酸化物の重合開始剤としては、例えば、ベンゾイルパーオキサイド、ジ−t−ブチルパーオキサイド、クメンハイドロパーオキサイド、t−ブチルパーオキシベンゾエート、t−ブチルパーオキシネオデカノエート、t−ブチルパーオキシ2−エチルヘキサノエート等が挙げられ、アゾ系の重合開始剤としては、2,2’−アゾビスイソブチロニトリル、2,2’−アゾビス(2−アミジノプロパン)ジヒドロクロライド、2,2’−アゾビス[2−(5−メチル−2−イミダゾリン−2−イル)プロパン]ジヒドロクロライド、2,2’−アゾビス(2−メチルプロピオンアミジン)二硫酸塩、2,2’−アゾビス(N,N’−ジメチレンイソブチルアミジン)等が挙げられる。これら重合開始剤は、単独または2種以上併用できる。
本発明において粘着付与樹脂(B)は、水酸基価が10〜130mgKOH/gの重合ロジンエステルもしくは水素化ロジンエステルであることが好ましく、20〜80mgKOH/gがより好ましい。10mgKOH/gに満たない場合は、粘着付与樹脂同士の分子間力等の作用が低下するなどし、凝集力が低下、すなわち耐熱性が不足するなどの恐れがある。130mgKOH/gを超えると、粘着付与樹脂同士の分子間力等の作用が強くなり凝集、アクリル樹脂との相溶性が低下し、凝集力が低下、すなわち耐熱性が不足するなどの恐れがある。
前記粘着付与樹脂(B)は、本発明の課題を解決できる範囲内であれば上記以外の、例えば、テルペン系粘着付与樹脂や石油系粘着付与樹脂などを配合することもできる。
前記粘着付与樹脂(B)は、アクリル系ポリマー(A)100重量部に対し、粘着付与樹脂(B)5〜100重量部用いることが好ましく、15〜60重量部がより好ましい。5重慮部に満たない場合、表面極性の低い被着体に対する密着性が低下、すなわち粘着力や耐熱クリープ性が低下するなどの恐れがある。100重量部を超えると、タックが著しく低下することで被着体に対する密着性が低下、すなわち粘着力や耐熱クリープ性が低下するなどの恐れがある。
また、前記粘着付与樹脂(B)の軟化点は、60〜160℃が好ましい。60℃に満たない場合は、耐熱性が低下する恐れがあり、160℃を超えるとアクリル樹脂との相溶性が低下し、凝集力が低下、すなわち耐熱性が不足するなどの恐れがある。
粘着付与樹脂(B)は、単独または2種以上併用できる。
粘着付与樹脂(B)は、単独または2種以上併用できる。
本発明の自動車内装材用粘着剤は、架橋剤を含むことが好ましい。架橋剤はイソシアネート化合物、エポキシ化合物、金属キレート化合物、アジリジン化合物などが好ましい。
イソシアネート化合物では、例えば、トリレンジイソシアネート、キシレンジイソシアネート、ヘキサメチレンジイソシアネートおよびこれらトリメチロールプロパンなどのポリオールとのアダクト体などが挙げられ、エポキシ系化合物では、エチレングリコールジグリシジルエーテル、トリグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、グリセリンジグリシジルエーテルなどが挙げられる。金属レート化合物では、例えば、アルミニウム、亜鉛、鉄、スズ、チタン、アンチモン、マグネシウム、バナジウムなどの多価金属がアセチルアセトンやアセト酢酸エチルに廃位した化合物が挙げられる。アジリジン系化合物では、例えば、N,N’−トルエン−2,4−ビス(1−アジリジンカルボキサイド)、N,N’−ジフェニルメタン-4,4’−ビス(1−アジリジンカルボキサイド)トリエチレンメラミン、ビスイソプロタロイル−1−(2−メチルアジリジン)、またはトリ−1−アジリジニルホスフィンオキサイドなどが挙げられる。これらの中でもイソシアネート化合物が好ましい。また、上記架橋剤は単独で使用しても、2種類以上を併用してもよい。
イソシアネート化合物では、例えば、トリレンジイソシアネート、キシレンジイソシアネート、ヘキサメチレンジイソシアネートおよびこれらトリメチロールプロパンなどのポリオールとのアダクト体などが挙げられ、エポキシ系化合物では、エチレングリコールジグリシジルエーテル、トリグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、グリセリンジグリシジルエーテルなどが挙げられる。金属レート化合物では、例えば、アルミニウム、亜鉛、鉄、スズ、チタン、アンチモン、マグネシウム、バナジウムなどの多価金属がアセチルアセトンやアセト酢酸エチルに廃位した化合物が挙げられる。アジリジン系化合物では、例えば、N,N’−トルエン−2,4−ビス(1−アジリジンカルボキサイド)、N,N’−ジフェニルメタン-4,4’−ビス(1−アジリジンカルボキサイド)トリエチレンメラミン、ビスイソプロタロイル−1−(2−メチルアジリジン)、またはトリ−1−アジリジニルホスフィンオキサイドなどが挙げられる。これらの中でもイソシアネート化合物が好ましい。また、上記架橋剤は単独で使用しても、2種類以上を併用してもよい。
架橋剤は、アクリル系ポリマー(A)と粘着付与樹脂(B)との合計100重量部に対し、1〜30重量部が好ましく、5〜20重量部がより好ましい。1重量部に満たない場合は、アクリル樹脂や粘着付与樹脂との架橋密度の低下や、分子間力等の作用が低下するなどし、凝集力が低下、すなわち耐熱性が不足するなどの恐れがある。一方、30重量部を超えると、アクリル樹脂や粘着付与樹脂との架橋密度が過剰になり、表面極性の低い被着体に対する密着性が低下し、粘着力や耐熱クリープ性が低下する恐れがある。
本発明の自動車内装材用粘着剤には、必要に応じて公知の粘着剤組成物に配合される充填剤、顔料、染料、希釈剤、老化防止剤、重合禁止剤、紫外線吸収剤、紫外線安定剤、カップリング剤等、各種添加剤を含んでもよい。
本発明の粘着シートは、基材と、上記の粘着剤を塗工することで形成した粘着剤層とを含むことができる。一方、基材を有さず粘着剤層のみからなるキャストシート、または両面粘着シートに加工することも好ましい。なお、粘着シートの取り扱いのため、剥離性シートを粘着剤層に貼り合わせて使用することは言うまでもない。
本発明で基材とは、例えば、ポリエチレン、ポリプロピレン、ポリエステル、ポリスチレン、ポリエチレンテレフタレート(PET)、ポリ塩化ビニル、ポリカーボネート、セロファン等のプラスチック、また、上質紙、クラフト紙、クレープ紙、グラシン紙等の紙、また、織布、不織布等の布、ウレタン発泡体、EPDM発泡体等の発泡体が挙げられるが、特にこれに限定されるものではない。
前記塗工は、剥離性シートに粘着剤を塗工して粘着剤層を形成した後、基材へ粘着剤層を転写する転写法、または基材に直接粘着剤を塗工し粘着剤層を形成する直接塗工法が一般的である。塗工装置としては、例えばリバースロールコーター、エアーナイフコーター、ナイフコータ、コンマコーター、ダイコーター、グラビアコーターなどが用いられるが、特にこれに限定されるものではない。粘着剤層の厚さは、25〜120μmが好ましい。
以下、実施例により、本発明を具体的に説明するが、本発明は以下の例によって限定されるものではない。なお、実施例中の部及び%は、それぞれ重量部および重量%を示している。
<実施例1>
撹拌機、還流冷却管、窒素導入管、温度計、滴下管を備えた反応装置を使用して、窒素雰囲気下で、表1の各モノマーの合計量の50重量%、開始剤としてアゾビスイソブチロニトリルを適量、溶剤として酢酸エチル50部を反応槽に仕込み、残りのモノマーの全量、および酢酸エチル35部、アゾビスイソブチロニトリルを適量添加して混合した溶液を滴下管に仕込んだ。反応槽を加熱し還流を確認後、モノマー混合物を滴下管から約2時間かけて滴下し、その後約80℃にて反応を継続した。反応終了後、冷却、酢酸エチルで希釈し、アクリル系ポリマー溶液を得た。アクリル系ポリマーの不揮発分は54%であった。
得られたアクリル系ポリマー100重量部に対して、表1の粘着付与樹脂30部、イソシアネート硬化剤(トリレンジイソシアネートトリメチロールプロパンアダクト体の不揮発分37.5%酢酸エチル溶液)11.5部、酢酸エチル適量を配合し不揮発分45%の粘着剤を得た。
撹拌機、還流冷却管、窒素導入管、温度計、滴下管を備えた反応装置を使用して、窒素雰囲気下で、表1の各モノマーの合計量の50重量%、開始剤としてアゾビスイソブチロニトリルを適量、溶剤として酢酸エチル50部を反応槽に仕込み、残りのモノマーの全量、および酢酸エチル35部、アゾビスイソブチロニトリルを適量添加して混合した溶液を滴下管に仕込んだ。反応槽を加熱し還流を確認後、モノマー混合物を滴下管から約2時間かけて滴下し、その後約80℃にて反応を継続した。反応終了後、冷却、酢酸エチルで希釈し、アクリル系ポリマー溶液を得た。アクリル系ポリマーの不揮発分は54%であった。
得られたアクリル系ポリマー100重量部に対して、表1の粘着付与樹脂30部、イソシアネート硬化剤(トリレンジイソシアネートトリメチロールプロパンアダクト体の不揮発分37.5%酢酸エチル溶液)11.5部、酢酸エチル適量を配合し不揮発分45%の粘着剤を得た。
<実施例2〜9、比較例1〜8>
表1〜表3に示すように、共重合体溶液の種類、粘着付与樹脂及び硬化剤の種類、配合量を変更した以外は実施例1と同様にして、粘着剤を得た。
表1〜表3に示すように、共重合体溶液の種類、粘着付与樹脂及び硬化剤の種類、配合量を変更した以外は実施例1と同様にして、粘着剤を得た。
表中、単量体の種類を下記の略号で示した。
BA:アクリル酸ブチル
AA:アクリル酸
HEA:2−ヒドロキシエチルアクリレート
D−125:ペンセルD−125(荒川化学)重合ロジンエステル(水酸基価:32)(軟化点:約125℃)
D−135:ペンセルD−135(荒川化学)重合ロジンエステル(水酸基価:32)(軟化点:約135℃)
KE−359:パインクリスタルKE−359(荒川化学)水素化ロジンエステル(水酸基価:42)(軟化点:約100℃)
KE−311:パインクリスタルKE−311(荒川化学)水素化ロジンエステル(水酸基価:10未満) (軟化点:約100℃)
A-125:スーパーエステルA-125(荒川化学)ロジンエステル(水酸基価:10未満) (軟化点:約125℃)
P-100:アルコンP-100(荒川化学)水素化石油樹脂(水酸基価:10未満) (軟化点:約100℃)
FTR6100:FTR6100(三井化学)石油樹脂(水酸基価:10未満) (軟化点:約100℃
TO105:YSレジンTO105(ヤスハラケミカル)テルペン重合体(水酸基価:10未満) (軟化点:約105℃)
BA:アクリル酸ブチル
AA:アクリル酸
HEA:2−ヒドロキシエチルアクリレート
D−125:ペンセルD−125(荒川化学)重合ロジンエステル(水酸基価:32)(軟化点:約125℃)
D−135:ペンセルD−135(荒川化学)重合ロジンエステル(水酸基価:32)(軟化点:約135℃)
KE−359:パインクリスタルKE−359(荒川化学)水素化ロジンエステル(水酸基価:42)(軟化点:約100℃)
KE−311:パインクリスタルKE−311(荒川化学)水素化ロジンエステル(水酸基価:10未満) (軟化点:約100℃)
A-125:スーパーエステルA-125(荒川化学)ロジンエステル(水酸基価:10未満) (軟化点:約125℃)
P-100:アルコンP-100(荒川化学)水素化石油樹脂(水酸基価:10未満) (軟化点:約100℃)
FTR6100:FTR6100(三井化学)石油樹脂(水酸基価:10未満) (軟化点:約100℃
TO105:YSレジンTO105(ヤスハラケミカル)テルペン重合体(水酸基価:10未満) (軟化点:約105℃)
<粘着シートの作成>
得られた粘着剤をコンマコーターを用いて市販の剥離性シート上に粘着剤層の乾燥後の厚さが60μmになるよう塗工し、電気オーブンで100℃−2分、乾燥し溶剤を除去した後に、50μPETフィルムを貼り合せることで粘着シートを得た。得られた粘着シートを用いて以下の物性評価を行った。結果を表に示す。
得られた粘着剤をコンマコーターを用いて市販の剥離性シート上に粘着剤層の乾燥後の厚さが60μmになるよう塗工し、電気オーブンで100℃−2分、乾燥し溶剤を除去した後に、50μPETフィルムを貼り合せることで粘着シートを得た。得られた粘着シートを用いて以下の物性評価を行った。結果を表に示す。
<粘着力>
23℃−50%の雰囲気下で長さ10mm×幅25mmの粘着シートをステンレス板、ポリプロピレン板、へそれぞれ貼着し、2kgロールで1往復圧着し、23℃−50%の雰囲気下で24時間放置した。その後、23℃−50%の雰囲気下でJISZ0237の測定方法に準拠して、引っ張り試験を用いて剥離角180°、剥離速度300mm/minで粘着力を測定した。
23℃−50%の雰囲気下で長さ10mm×幅25mmの粘着シートをステンレス板、ポリプロピレン板、へそれぞれ貼着し、2kgロールで1往復圧着し、23℃−50%の雰囲気下で24時間放置した。その後、23℃−50%の雰囲気下でJISZ0237の測定方法に準拠して、引っ張り試験を用いて剥離角180°、剥離速度300mm/minで粘着力を測定した。
<保持力試験>
23℃−50%の雰囲気下で長さ100mm×幅25mmの粘着シートの長さ25mm×幅25mm分をポリプロピレン板へそれぞれ貼着し、2kgロールで1往復圧着し、23℃−50%の雰囲気下で20分間放置した。その後、80℃の雰囲気下で500gの重りを付け180度の方向に力が加わるようセットし、24時間後に粘着シートが被着体から何ミリずれているか、もしくは完全にずれ落ちた落下秒数を測定した。
23℃−50%の雰囲気下で長さ100mm×幅25mmの粘着シートの長さ25mm×幅25mm分をポリプロピレン板へそれぞれ貼着し、2kgロールで1往復圧着し、23℃−50%の雰囲気下で20分間放置した。その後、80℃の雰囲気下で500gの重りを付け180度の方向に力が加わるようセットし、24時間後に粘着シートが被着体から何ミリずれているか、もしくは完全にずれ落ちた落下秒数を測定した。
<定荷重剥離性>
図1を元に説明する。23℃(湿度50%)の雰囲気下で、長さ100mm×幅25mmの粘着シート(1)を、長さ80mmの部分を被着体板(2)であるステンレス板、ポリプロピレン板、ポリエチレン板にそれぞれ貼着した。そして、2kgロールで1往復圧着し、23℃(湿度50%)の雰囲気下で24時間放置した。その後、80℃の雰囲気下で200gの重り(3)を付け90度の方向に力が加わるようセットし、24時間経過後に粘着シートが被着体から何ミリ剥がれているか、もしくは完全に剥がれ落ちた落下秒数を測定した。なお、剥がれは図1のA−B間の長さである。
図1を元に説明する。23℃(湿度50%)の雰囲気下で、長さ100mm×幅25mmの粘着シート(1)を、長さ80mmの部分を被着体板(2)であるステンレス板、ポリプロピレン板、ポリエチレン板にそれぞれ貼着した。そして、2kgロールで1往復圧着し、23℃(湿度50%)の雰囲気下で24時間放置した。その後、80℃の雰囲気下で200gの重り(3)を付け90度の方向に力が加わるようセットし、24時間経過後に粘着シートが被着体から何ミリ剥がれているか、もしくは完全に剥がれ落ちた落下秒数を測定した。なお、剥がれは図1のA−B間の長さである。
以下に実施例、比較例の詳細と物性を表4〜表6に示す。
Claims (5)
- カルボキシル基および水酸基を有するアクリル系ポリマー(A)と、水酸基価10〜130mgKOH/gの、重合ロジンエステルまたは水素化ロジンエステルを含む粘着付与樹脂(B)と、イソシアネート硬化剤(C)とを含む、自動車内装材用粘着剤。
- 重合ロジンエステルの軟化点が100〜170℃、水素化ロジンエステルの軟化点が80〜140℃である、請求項1記載の自動車内装材用粘着剤。
- アクリル系ポリマー(A)が、カルボキシル基含有モノマー0.1〜10重量%、水酸基含有モノマー0.01〜0.2重量%およびその他共重合可能なモノマーを共重合してなることを特徴とする請求項1または2記載の自動車内装材用粘着剤。
- アクリル系ポリマー(A)100重量部に対して、粘着付与樹脂(B)を5〜100重量部含む、請求項1〜3いずれか1項に記載の自動車内装材用粘着剤。
- 基材と、請求項1〜4いずれか1項に記載の自動車内装材用粘着剤から形成してなる粘着剤層とを備えた自動車内装材用粘着シート。