JP2013514190A - 硫酸塩及び/又は硝酸塩を含有する鋳造混合物及びそれらの使用 - Google Patents
硫酸塩及び/又は硝酸塩を含有する鋳造混合物及びそれらの使用 Download PDFInfo
- Publication number
- JP2013514190A JP2013514190A JP2012544504A JP2012544504A JP2013514190A JP 2013514190 A JP2013514190 A JP 2013514190A JP 2012544504 A JP2012544504 A JP 2012544504A JP 2012544504 A JP2012544504 A JP 2012544504A JP 2013514190 A JP2013514190 A JP 2013514190A
- Authority
- JP
- Japan
- Prior art keywords
- mold
- casting
- casting mixture
- mixture
- weight percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
Claims (26)
- 鋳造混合物であって、
(a)鋳造用骨材と、
(b)前記鋳造混合物によって調製される金属鋳物のベイニングを低減する量の、ナトリウム、カリウム、カルシウム、及びマグネシウムの硫酸塩、硝酸塩、並びにそれらの混合物からなる群から選択される無機塩と
を含む、鋳造混合物。 - 赤色酸化鉄、黒色酸化鉄、及びそれらの混合物からなる群から選択される酸化鉄をさらに含む、請求項1に記載の鋳造混合物。
- 酸化鉄が赤色酸化鉄である、請求項2に記載の鋳造混合物。
- 鋳造用骨材がケイ砂を含む、請求項3に記載の鋳造混合物。
- 無機塩が、硫酸ナトリウム、硫酸カリウム、硫酸カルシウム、及び硫酸マグネシウム、並びにそれらの混合物からなる群から選択される、請求項4に記載の鋳造混合物。
- 石膏が、鋳造混合物中で硫酸カルシウム塩源として使用される、請求項5に記載の鋳造混合物。
- 塩が、硝酸ナトリウム、硝酸カリウム、硝酸カルシウム、及び硝酸マグネシウム、並びにそれらの混合物からなる群から選択される、請求項4に記載の鋳造混合物。
- 鋳造混合物がドロマイトをさらに含有する、請求項1に記載の鋳造混合物。
- 硫酸塩及び/又は硝酸塩対赤色酸化鉄の重量比が1:1〜4:1である、請求項5、6及び7のいずれかに記載の鋳造混合物。
- 硫酸塩及び/又は硝酸塩対赤色酸化鉄の重量比が1:1〜2:1である、請求項9に記載の鋳造混合物。
- 鋳造混合物が有機バインダーを含有する、請求項10に記載の鋳造混合物。
- バインダーがフェノールウレタンバインダー又はエポキシアクリレートバインダーである、請求項11に記載の鋳造混合物。
- 鋳造混合物が触媒を含有する、請求項11に記載の鋳造混合物。
- 鋳造混合物中の塩の量が、鋳造用骨材の重量を基準として0.5重量パーセント〜4.0重量パーセントである、請求項11に記載の鋳造混合物。
- 鋳造混合物中の塩の量が、鋳造用骨材の重量を基準として0.5重量パーセント〜4.0重量パーセントである、請求項14に記載の鋳造混合物。
- 鋳造混合物中の塩の量が、鋳造用骨材の重量を基準として0.5重量パーセント〜2.5重量パーセントである、請求項11に記載の鋳造混合物。
- 鋳造混合物中の塩の量が、鋳造用骨材の重量を基準として0.5重量パーセント〜2.5重量パーセントである、請求項16に記載の鋳造混合物。
- (a)請求項11に記載の鋳造混合物を型に導入して鋳型を形成するステップと、
(b)(A)の鋳型を、鋳型を硬化させることができる蒸気硬化触媒と接触させるステップと、
(c)(B)から得られる前記鋳型を、前記鋳型が取り扱い可能になるまで硬化させるステップと、
(d)前記鋳型を型からはずすステップと
を含む、鋳型を調製するためのコールドボックス法。 - (a)請求項18に記載の方法によって調製された鋳型をモールドアセンブリにはめ込むステップと、
(b)金属を液体状態のうちに前記モールドアセンブリへ注ぐステップと、
(c)前記金属を冷却及び固体化させるステップと、
(d)次いで、鋳造した金属部品をモールドアセンブリから引離すステップと
を含む、金属部品の鋳造方法。 - 請求項19に従って調製した金属部品。
- (a)請求項12に記載の鋳造混合物を型に導入して鋳型を形成するステップと、
(b)(A)の前記鋳型を、前記鋳型が取り扱い可能になるまで硬化させるステップと、
(c)前記鋳型を型からはずすステップと
を含む、鋳型を調製するためのノーベーク法。 - (a)請求項21に記載の方法によって調製された鋳型をモールドアセンブリにはめ込むステップと、
(b)金属を液体状態のうちに前記モールドアセンブリへ注ぐステップと、
(c)前記金属を冷却及び固体化させるステップと、
(d)次いで、鋳造した金属部品をモールドアセンブリから引離すステップと
を含む、金属部品の鋳造方法。 - 請求項22に従って調製した金属部品。
- (a)請求項12に記載の鋳造混合物を型に導入して鋳型を形成するステップと、
(b)前記鋳型を150℃〜260℃の温度に加熱するステップと、
(c)(A)の前記鋳型を、前記鋳型が取り扱い可能になるまで硬化させるステップと、
(d)前記鋳型を型からはずすステップと
を含む、鋳型を調製するためのウォームボックス法。 - (a)請求項24に記載の方法によって調製された鋳型をモールドアセンブリにはめ込むステップと、
(b)金属を液体状態のうちに前記モールドアセンブリへ注ぐステップと、
(c)前記金属を冷却及び固体化させるステップと、
(d)次いで、鋳造した金属部品をモールドアセンブリから引離すステップと
を含む、金属部品の鋳造方法。 - 請求項25に従って調製した金属部品。