JP2013216537A - フェライト粒子の製造方法 - Google Patents
フェライト粒子の製造方法 Download PDFInfo
- Publication number
- JP2013216537A JP2013216537A JP2012088073A JP2012088073A JP2013216537A JP 2013216537 A JP2013216537 A JP 2013216537A JP 2012088073 A JP2012088073 A JP 2012088073A JP 2012088073 A JP2012088073 A JP 2012088073A JP 2013216537 A JP2013216537 A JP 2013216537A
- Authority
- JP
- Japan
- Prior art keywords
- metal carbonate
- range
- carbonate
- raw material
- ferrite particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】MXFe3−XO4で表される組成のフェライト粒子が生成するように成分調整されたFe成分原料とM成分原料とを分散媒中に投入してスラリーを得る工程と、前記スラリーを噴霧乾燥させて造粒物を得る工程と、前記造粒物を焼成して焼成物を得る工程とを有するフェライト粒子の製造方法であって、M成分原料が、低酸素雰囲気下における分解温度が100℃〜600℃の範囲の第1の金属炭酸塩と、当該分解温度が650℃〜1200℃の範囲の第2の金属炭酸塩とを少なくとも含み、第1の金属炭酸塩と第2の金属炭酸塩との割合が重量比で10:1〜100:1の範囲であることを特徴とする。
【選択図】図1
Description
Mnフェライト粒子を下記方法で作製した。出発原料として、Fe2O3(平均粒径:0.6μm)7.0kgと、MnCO3(平均粒径:5.0μm)1.9kgと、Mn3O4(平均粒径:0.9μm)1.3kgと、CaCO3(平均粒径:1μm)60gとを純水3.0kg中に分散し、分散剤としてポリカルボン酸アンモニウム系分散剤を60g添加して混合物とした。この混合物を湿式ボールミル(メディア径2mm)により粉砕処理し、混合スラリーを得た。
得られたフェライト粒子を熱硬化性樹脂中に分散させた後、加熱により樹脂を硬化させた。この硬化物の表面をクロスセクションポリッシャー(日本電子製)を用いて研磨した。研磨した粒子表面を走査電子顕微鏡(日本電子製)を用いて観察し、粒子の断面写真を撮影した。撮影した粒子断面写真を画像解析ソフト「Image-Pro」を使用して粒子部分と空孔部分に分離し、総面積に対する空孔部分の面積比を計測し空孔率とした。この空孔率を100粒子分測定し、その平均値をそれぞれ空孔率とした。
フェライト粒子の見掛け密度はJIS Z 2504に準拠して測定した。
室温専用振動試料型磁力計(VSM)(東英工業社製「VSM−P7」)を用いて、外部磁場を0〜79.58×104A/m(10000エルステッド)の範囲で1サイクル連続的に印加して、飽和磁化、残留磁化、保磁力及び79.58×103A/m(1000エルステッド)の磁場における磁化σ1000(Am2/kg)をそれぞれ測定した。
表面を電解研磨した厚さ2mmの電極としての真鍮板2枚を、距離2mm離して対向するように配置した。電極間にフェライト粒子200mgを装入した後、それぞれの電極の背後に断面積240cm2の磁石(表面磁束密度が1500ガウスのフェライト磁石)を配置して、電極間にフェライト粒子のブリッジを形成させた。そして、1000Vの直流電圧を電極間に印加し、フェライト粒子に流れる電流値を測定し、フェライト粒子の電気抵抗を算出した。
表1に示す出発原料及び配合量、焼成温度で実施例1と同様にしてフェライト粒子を作製した。そして、実施例1と同様にして各物性を測定した。表1に測定結果をまとめて示す。また、図2に比較例1のフェライト粒子の断面SEM写真を示す。
Claims (5)
- MXFe3−XO4(但し、MはMg,Mn,Ca,Ti,Cu,Zn,Sr,Niからなる群より選ばれる少なくとも1種の金属元素,0≦X≦1)で表される組成のフェライト粒子が生成するように成分調整されたFe成分原料とM成分原料とを分散媒中に投入してスラリーを得る工程と、前記スラリーを噴霧乾燥させて造粒物を得る工程と、前記造粒物を焼成して焼成物を得る工程とを有するフェライト粒子の製造方法であって、
M成分原料が、低酸素雰囲気下における分解温度が100℃〜600℃の範囲の第1の金属炭酸塩と、当該分解温度が650℃〜1200℃の範囲の第2の金属炭酸塩とを少なくとも含み、第1の金属炭酸塩と第2の金属炭酸塩との割合が重量比で10:1〜100:1の範囲であることを特徴とするフェライト粒子の製造方法。 - 前記造粒物を焼成して焼成物を得る工程において、300℃〜600℃の範囲の所定温度を5時間以上保持した後、800℃〜1200℃の範囲の所定温度を3時間以上保持する請求項1記載の製造方法。
- 第1の金属炭酸塩と第2の金属炭酸塩との平均粒径の比が1:1〜10:1の範囲である請求項1又は2記載の製造方法。
- 第1の金属炭酸塩が炭酸マンガン又は炭酸マグネシウムである請求項1〜3のいずれかに記載の製造方法。
- 第2の金属炭酸塩が炭酸カルシウム、炭酸バリウム、炭酸ストロンチウムのいずれかである請求項1〜4のいずれかに記載の製造方法。