JP2012502819A - アルデヒド放出の少ない多層リグノセルロース含有成形体 - Google Patents
アルデヒド放出の少ない多層リグノセルロース含有成形体 Download PDFInfo
- Publication number
- JP2012502819A JP2012502819A JP2011527292A JP2011527292A JP2012502819A JP 2012502819 A JP2012502819 A JP 2012502819A JP 2011527292 A JP2011527292 A JP 2011527292A JP 2011527292 A JP2011527292 A JP 2011527292A JP 2012502819 A JP2012502819 A JP 2012502819A
- Authority
- JP
- Japan
- Prior art keywords
- binder
- monomer
- lignocellulose
- weight
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
及び場合により、次のモノマーから構成されている1種以上のポリマーMを含有する水性分散液としての成分(II):a)少なくとも1個のエポキシド基及び/又は少なくとも1個のヒドロキシアルキル基を含有する少なくとも1種のエチレン系不飽和モノマー(モノマーM1)0〜50質量%、及びb)モノマーM1と異なっている少なくとももう1種のエチレン系不飽和モノマー(モノマーM2)50〜100質量%、及び場合により、成分(III)としての通常の添加剤を含有し、かつ、この際、結合剤(b)は、結合剤(a)がホルムアルデヒド樹脂を含有する場合には、ホルムアルデヒド捕捉体を含有する)。
Description
少量のホルムアルデヒドを用いて製造されたアミノプラスト接着剤の使用、いわゆるホルムアルデヒド捕捉体、例えば、アミン基含有化合物を用いる製造された木質材料の後処理及び木質材料上への被覆層の塗布(この際、被覆層は、ホルムアルデヒド捕捉体として、大量のメラミン及び/又は尿素を添加した接着剤で保持される)。
A)結合剤(a)の使用によって得られる、リグノセルロース含有粒子を含有する1層以上の中間層及び
B)結合剤(b)の使用によって得られる、リグノセルロース含有粒子を含有する1層以上の被覆層
から成る多層リグノセルロース含有成形体によって解明され、
この際、結合剤(a)は、(a1)ホルムアルデヒド樹脂及び(a2)少なくとも2個のイソシアネート基を有する有機イソシアネートを含む群から選択され、
この際、結合剤(b)は、
次の成分を含有する水性成分(I):
(i)次のモノマーから構成されているポリマーA:
a)少なくとも1種のエチレン系不飽和モノカルボン酸及び/又はジカルボン酸(モノマーA1)80〜100質量%及び
b)モノマーA1と異なっている少なくとももう1種のエチレン系不飽和モノマー(モノマーA2)0〜20質量%、
及び場合により
(ii)ヒドロキシ、カルボン酸及びその誘導体、一級、二級及び三級アミン、エポキシ、アルデヒドの群から選択される少なくとも2個の官能基を有する低分子架橋結合剤、
及び場合により、
次のモノマーから構成されている1種以上のポリマーMを含有する水性分散液としての成分(II):
a)少なくとも1個のエポキシド基及び/又は少なくとも1個のヒドロキシアルキル基を含有する少なくとも1種のエチレン系不飽和モノマー(モノマーM1)0〜50質量%、及び
b)モノマーM1と異なっている少なくとももう1種のエチレン系不飽和モノマー(モノマーM2)50〜100質量%、
及び場合により、
成分(III)としての通常の添加剤を含有し、
かつ、この際、結合剤(b)は、結合剤(a)がホルムアルデヒド樹脂を含有する場合には、ホルムアルデヒド捕捉体を含有する。
次の成分を含有する水性成分(I):
(i)次のモノマーから構成されているポリマーA:
a)少なくとも1種のエチレン系不飽和モノカルボン酸及び/又はジカルボン酸(モノマーA1)70〜100質量%及び
b)モノマーA1と異なっている少なくとももう1種のエチレン系不飽和モノマー(モノマーA2)0〜30質量%、
及び場合により
(ii)ヒドロキシ、カルボン酸及びその誘導体、一級、二級及び三級アミン、エポキシ、アルデヒドの群から選択される少なくとも2個の官能基を有する低分子架橋結合剤、
及び場合により、
次のモノマーから構成されている1種以上のポリマーMを含有する水性分散液としての成分(II):
a)少なくとも1個のエポキシド基及び/又は少なくとも1個のヒドロキシアルキル基を含有する少なくとも1種のエチレン系不飽和モノマー(モノマーM1)0〜50質量%、及び
b)モノマーM1と異なっている少なくとももう1種のエチレン系不飽和モノマー(モノマーM2)50〜100質量%、
及び場合により、
成分(III)としての通常の添加剤を含有する。
a)少なくとも1種のエチレン系不飽和モノカルボン酸及び/又はジカルボン酸(モノマーA1)70〜100質量%及び
b)モノマーA1と異なっている、少なくとももう1種のエチレン系不飽和モノマー(モノマーA2)0〜30質量%。
a)少なくとも1個のエポキシド基及び/又は少なくとも1個のヒドロキシアルキル基を有する少なくとも1種のエチレン系不飽和モノマー(モノマーM1)0〜50質量%、及び
b)モノマーM1と異なっている少なくとももう1種のエチレン系不飽和モノマー(モノマーM2)50〜100質量%。
好適な1実施態様で、結合剤(b)は、低分子架橋結合剤(ii)を含有しないが、例えば、次の変法1、変法2及び変法3に記載された、成分(II)を含有する。
1層以上の中間層A)のために、結合剤(a)は、成分(a1)、有利にアミノプラスト樹脂、特に有利にUF樹脂及び/又はMUF樹脂だけを含有する。
1層以上の中間層A)のために、結合剤(a)は、成分(a1)、有利にアミノプラスト、特に有利にUF樹脂及び/又はMUF樹脂、及び成分(a2)、有利にPMDIを、組合せ(a1)及び(a2)について前記で定義した量で含有する。
1層以上の中間層A)のために、結合剤(a)は、成分(a2)、有利にPMDIだけを含有する。
1層以上の中間層A)のために、結合剤(a)は、成分(a1)、有利にアミノプラスト樹脂、特に有利にUF樹脂及び/又はMUF樹脂だけを含有する。
1層以上の中間層A)について、結合剤(a)は、成分(a2)、有利にPMDIだけを含有する。
1層以上の中間層A)のために、結合剤(a)は、成分(a1)、有利にアミノプラスト樹脂、特に有利にUF樹脂及び/又はMUF樹脂及び/又は成分(a2)、有利にPMDIを、組合せ(a1)及び(a2)について前記で定義した量で含有する。
1.成分(I)及び(II)
成分(I)は、アクリル酸70質量%及び無水マレイン酸30質量%の水中ラジカル重合開始溶液重合によって得られる、本発明によるポリマーAの商慣習の水溶液であった。成分(I)は、他の架橋結合剤成分、例えば、多アルカノールアミン、例えば、トリエタノールアミンを含有しなかった。質量平均分子量Mwは、80000g/モルであった。固体含量は45質量%であった。
BM1:1.に記載した成分(I)及び(II)1:1混合で(各々の固体含量に対して)
BM2:atro UF接着剤(この場合、BASF SEのKAURIT(登録商標)KL 347)9%
プラス硝酸アンモニウム硬化剤4質量%(接着剤の固体含量に対して)。
BM3:atro UF接着剤(この場合、BASF SEのKAURIT(登録商標)KL 347)9%
プラス硝酸アンモニウム硬化剤1質量%(接着剤の固体含量に対して)。
BM4:1.に記載した成分(I)、しかし、架橋結合剤(ii)として、トリエタノールアミン((I)100部に対して30部)を含有する。
BM5:Lupranat(登録商標)M20 FB、BASF SEのイソシアネートをベースとする結合剤。
BM6:BM1100質量部及びトリエタノールアミン10質量部を含む混合物。
ホルムアルデヒド放出の測定は、次の方法で木質材料の試験法により行なわれた(Bundesgegesetzblatt 10/91, S. 488/489):CEN prEN 717-1("デシケーター"); DIN EN 120("パーホレーター"); DIN 52368(CEN prEN 717-2;ガス分析又は立方メートル室内値に相応する)。
引剥強度(AF):EN311;屈曲強度(BF)EN310;横引張強度(QZ)EN319;総密度(Rohdichte)EN323;含水量EN322;膨潤厚(D24h)EN317。
4.1 製造
表1に挙げた量のトウヒチップ(20℃で、気湿65%を調湿する)を、相応する量の水性結合剤(表1、結合剤の固体含量欄参照;atro木材に対する結合剤の固体量が挙げられている)とLoedige混合機中で接着させ、湿度を測定する。引き続き、中間層及び被覆層のためのマットが散布され、かつ200℃で、圧縮時間因子10s/ボード厚mmで圧縮させる。
Claims (12)
- A)結合剤(a)の使用によって得られる、リグノセルロース含有粒子を含有する1層以上の中間層及び
B)結合剤(b)の使用によって得られる、リグノセルロース含有粒子を含有する1層以上の被覆層
から成る多層リグノセルロース含有成形体であって、
この際、結合剤(a)は、(a1)ホルムアルデヒド樹脂及び(a2)少なくとも2個のイソシアネート基を有する有機イソシアネートからなる群から選択され、
この際、結合剤(b)は、
次の成分を含有する水性成分(I):
(i)次のモノマーを含有するポリマーA:
a)少なくとも1種のエチレン系不飽和モノカルボン酸及び/又はジカルボン酸(モノマーA1)70〜100質量%及び
b)モノマーA1と異なっている少なくとももう1種のエチレン系不飽和モノマー(モノマーA2)0〜30質量%、
及び場合により
(ii)ヒドロキシ、カルボン酸及びその誘導体、一級、二級及び三級アミン、エポキシ、アルデヒドの群から選択される少なくとも2個の官能基を有する低分子架橋結合剤、
及び場合により、
次のモノマーを含有する1種以上のポリマーMを含有する水性分散液としての成分(II):
a)少なくとも1個のエポキシド基及び/又は少なくとも1個のヒドロキシアルキル基を含有する少なくとも1種のエチレン系不飽和モノマー(モノマーM1)0〜50質量%、及び
b)モノマーM1と異なっている少なくとももう1種のエチレン系不飽和モノマー(モノマーM2)50〜100質量%、
及び場合により、
成分(III)としての通常の添加剤を含有し、
かつ、この際、結合剤(b)は、結合剤(a)がホルムアルデヒド樹脂を含有する場合には、ホルムアルデヒド捕捉体を含有する、多層リグノセルロース含有成形体。 - 結合剤(b)は、低分子架橋結合剤(ii)を含有し、かつ成分(II)を含有しない、請求項1に記載の多層リグノセルロース含有成形体。
- 結合剤(b)は、低分子架橋結合剤(ii)を含有しないが、成分(II)を含有する、請求項1に記載の多層リグノセルロース含有成形体。
- 結合剤(b)は、低分子架橋結合剤(ii)も成分(II)も含有する、請求項1に記載の多層リグノセルロース含有成形体。
- 1つの中間層A)及び2つの被覆層B)を有する3層である、請求項1から4までのいずれか1項に記載の多層リグノセルロース含有成形体。
- 結合剤(a)は、ホルムアルデヒド樹脂(a1)だけである、請求項1から5までのいずれか1項に記載の多層リグノセルロース含有成形体。
- 結合剤(a)は、少なくとも2個のイソシアネート基を有する有機イソシアネート(a1)だけである、請求項1から6までのいずれか1項に記載の多層リグノセルロース含有成形体。
- 結合剤(a)は、各々純粋な非希釈物質の(a1)及び(a2)の合計に対して、成分(a1)を、70〜99.9質量%の範囲で、及び成分(a2)を0.1〜30質量%の範囲で含有する、請求項1から7までのいずれか1項に記載の多層リグノセルロース含有成形体。
- ボードの形の請求項1から8までのいずれか1項に記載の多層リグノセルロース含有成形体。
- 請求項1から9までのいずれか1項に記載の多層リグノセルロース含有成形体を製造する方法であって、リグノセルロース粒子を1層以上の中間層A)のために結合剤(a)と接触させ、リグノセルロース粒子を1層以上の被覆層B)のために結合剤(b)と接触させ、所望の配列により相互に積層させ、かつ高められた温度で圧縮させる前記方法。
- 全ての種類の製品の製造のための及び建築範囲における、請求項1から9までのいずれか1項に記載の多層リグノセルロース含有成形体の使用。
- 家具及び家具部材の、包装材料の製造のための、住宅建築における又は内装における又は自動車両における、請求項1から9までのいずれか1項に記載の多層リグノセルロース含有成形体の使用。