JP2012177133A - ポリイソシアネート組成物 - Google Patents
ポリイソシアネート組成物 Download PDFInfo
- Publication number
- JP2012177133A JP2012177133A JP2012115663A JP2012115663A JP2012177133A JP 2012177133 A JP2012177133 A JP 2012177133A JP 2012115663 A JP2012115663 A JP 2012115663A JP 2012115663 A JP2012115663 A JP 2012115663A JP 2012177133 A JP2012177133 A JP 2012177133A
- Authority
- JP
- Japan
- Prior art keywords
- composition
- isocyanate
- functional groups
- biuret
- units
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】この発明は、組成物及びかかる組成物の製造方法及びイソシアナトアルコキシシランに関係する。ポリイソシアネート組成物は、アミノアルキルシランユニット及びジアミンユニットから選択する3つ以上5つ以下のユニット並びにイソシアネート官能基及びそれらの誘導体から選択する少なくとも1つの官能基を含む少なくとも2つの異なるオリゴマー化合物を含む。この発明は、前述の化合物の一つが少なくとも2つのアミノアルキルシランユニットを含むこと及び他の化合物が少なくとも2つのジアミンユニットを含むことを特徴とする。この発明は、コーティングに適している。
【選択図】なし
Description
>N―R―N<
(式中、Rは、炭化水素基を表し、これは、2つのイソシアネート官能基を無視するなら、イソシアネートモノマーの残基である)。勿論、Rは、イソシアネート官能基のオリゴマー化において造られる如何なる官能基即ちカルバメート、尿素(ビウレットを含む)、アロファネート又はビウレット官能基及びオリゴ縮合(オリゴマー化を含む)の記述において言及されるものをも示さない。−R−の分子量は、多くて200である。Rは、三官能性モノマー例えばLTI、NTI及びUTIの場合には、他の「アミノ」基を含むことができる。
・芳香環の構成員である結合点を有する任意のイソシアネート官能基は、芳香族とみなし;
・sp3混成の炭素である結合点(勿論、窒素の)を有する任意のイソシアネート官能基は、脂肪族とみなす。
− 最も近い環から最大で炭素一つだけ離れている結合点(直接結合が好ましい)を有する任意の脂肪族イソシアネート官能基は、脂環式基とみなされる。
− 第二sp3炭素(即ち、2つの炭素及び1つの水素と結合した炭素)に担われる結合点を有する任意のイソシアネート官能基は、第二官能基とみなされる。
− 第三sp3炭素(即ち、3つの炭素に結合した炭素)に担われる結合点を有する任意のイソシアネート官能基は、第三官能基とみなされる。
− 第三炭素(即ち、最後の結合を考慮しなければ、3つの炭素に結合した炭素)に担われるsp3炭素自体に担われる結合点を有する任意のイソシアネート官能基は、ネオペンチル性とみなされる。
− 環外の及び第三以外のsp3炭素により担われる狭義のメチレン(−CH2−)自体により担われる結合点を有する任意のイソシアネート官能基は、直鎖性官能基とみなされる。
− 「脂肪族」は、すべてのイソシアネート官能基が脂肪族性である任意のモノマーを意味すると理解され;
− 「芳香族」は、すべてのイソシアネート官能基が芳香族性である任意のモノマーを意味すると理解され;
− 「混合した」は、少なくとも一つの官能基が脂肪族性であり且つ少なくとも一つの官能基が芳香族性である任意のモノマーを意味すると理解され;
− 「脂環式」は、すべてのイソシアネート官能基が脂肪族性であり且つ少なくとも一つが脂環式である任意のモノマーを意味すると理解され;
− 「直鎖脂肪族」は、すべてのイソシアネート官能基が脂肪族性であり、それらの何れも脂環式でなく且つ少なくとも一つが直鎖状である任意のモノマー、又は少なくとも一つの回転自由の従って環外のポリメチレン配列(CH2)π(式中、πは、2以上の整数を表す)を示す任意のモノマーを意味すると理解される。
◆ 脂環式及びアリール脂肪族(即ち、芳香族性脂肪族)を含む脂肪族、例えば:
・直鎖(又は単純)脂肪族としての、少なくとも一つの環外ポリメチレン配列(CH2)π(式中、πは、2〜10の整数、有利には、4〜8の整数を表す)を示すポリメチレンジイソシアネートモノマー、及び、特に、ヘキサメチレンジイソシアネート(これらのメチレンの一つは、MPDI(メチルペンタメチレンジイソシアネート)の場合のように、メチル又はエチル基により置換されうる);
・環状脂肪族(即ち脂環式)(部分的に「ネオペンチル」性の脂環式)としての;イソホロンジイソシアネート(IPDI);
・環状脂肪族(脂環式)ジイソシアネートとしての、ノルボルナンからの誘導体又は芳香族イソシアネートの水素化形態(ジアミノ化環の生成後に、例えばホスゲン化によるイソシアネート化にかけた核の水素化);
・芳香族性脂肪族としての、アリーレンジアルキレンジイソシアネート(例えば、OCN−CH2−Φ−CH2−NCO、その一部は、直鎖状脂肪族とみなされる)即ち、芳香核から少なくとも2炭素だけ離れたイソシアネート官能基を有するもの、例えば(OCN−[CH2]t−Φ−[CH2]u−NCO)(t及びuは、1より大きい);
◆ 又は、芳香族、例えばトルイレンジイソシアネート(ここでは、関心ある物質として言及されるが、他方、その水素化形態は、脂環式とみなされ、有利には、例えば、1,3−及び1,4−BIC(ビスイソシアネートメチルシクロヘキサン)である)。
「三量体化」により得られる誘導体、即ち、3つの異なる分子に属する3つのイソシアネート官能基が縮合してイソシアネート官能基を有する3つの基自身を有するイソシアヌル環を形成することにより得られる誘導体。
−NH−CO−N<(式中、開鎖のままの窒素の結合は、水素及び/又は脂肪族基にのみ結合される)。
A−(NCO)z−(Si(R2)m(X−R3)n)y
{ここに、Aは、ビウレット及び/又はアシル尿素構造を含む幹の残基を表し;
zは、0〜30の数を表し;
yは、1〜30の数を表し;
mは、0〜3の閉区間(即ち、境界を含む)内の、有利には2以上の、好ましくは3以上の整数を表し;
nは、0〜3の閉区間(即ち、境界を含む)内の、有利には2以下の整数を表し;
但し、m+n=3であり;
R2は、1〜20炭素原子の、好ましくは1〜12炭素原子の直鎖又は分枝鎖の炭化水素鎖を表し、この炭化水素鎖は、脂肪族(アルアルキルを含む)又は芳香族(適宜、ヘテロ原子で中断される)であってよく、このR2鎖は、この鎖の両端の炭素がケイ素に結合しているならば、アルキレン型であってよく;
R3は、1〜20炭素原子の、好ましくは1〜12炭素原子の直鎖又は分枝鎖の炭化水素鎖を表し、この炭化水素鎖は、脂肪族又は芳香族又はアルアルキルであってよく(適宜、ヘテロ原子で中断される)、このR3鎖は、この鎖の両端の炭素が同じケイ素原子に担われた2つの基Xに結合しているならば、アルキレン型であってよい;
X=O又はS}。
− 以後1〜5と記録されるビウレットユニットを含む構造
− 6〜10と記録されるアシル尿素構造
2〜20ユニットを含むオリゴマー配列を生じる構造1及び/又は構造2のオリゴマー化の生成物。これらの配列は、以下のように図式表示することができ、これらの構造の分布は、鎖に沿ってランダムである。
− R 少なくとも一つのイソシアネート官能基を有するイソシアネート又はポリイソシアネート分子の残基、
− R1 少なくとも一つのシラン官能基を有する分子の残基であって、一般に、2〜20炭素原子の好ましくは3〜12炭素原子の直鎖又は分枝鎖の炭化水素鎖であり、この炭化水素鎖は、脂肪族又は芳香族又はアルアルキルでありえて、適宜、ヘテロ原子に中断されている当該残基、
− R2及びR3 同一であっても異なってもよく、上で定義してあり、
− n 1〜3であり且つn+m=3、
− X = O又はS。
アシル尿素ユニットを含むこれらの構造は、ビウレット構造に関して記述することができるが、但し、このビウレット構造においては、R4−C(=O)−ユニットが、R−NH−C(=O)−ユニットに取って代わる。
− R4は、N−アシル尿素官能基を与えるように反応した少なくとも一つのカルボキシル官能基を有する分子の残基を表す。
二酸(R4−(COOH)2)の場合には、下記のようになる。
アロファネート: −R−N[−C(=O)−NH−R−NCO]−C(=O)−O−R5
カルバメート: −R−NH−C(=O)−O−R5
尿素:−R−NH−C(=O)−NH−R6−又は−R−NH−C(=O)−N−(R6)(R7)
ウレチジンジオン:
Y−NH−R5−Si(R3−X)3-m(R2)m又は
Y−NH−R6−N(−Y)−R5−Si(R3−X)3-m(R2)m又は
R6−[(NH−R5−Si(R3−X)3-m(R2)m)]z
ここに
− Y=H又は、脂肪族又は芳香族又は芳香族性脂肪族であって、適宜、ヘテロ原子により中断されている1〜20炭素原子の直鎖若しくは分枝鎖炭化水素鎖、
− R5 脂肪族又は芳香族又は芳香族性脂肪族であって、適宜、ヘテロ原子により中断されている1〜20炭素原子の直鎖又は分枝鎖炭化水素;R5は、好ましくは、1〜8炭素原子の脂肪族炭化水素鎖である、
− R6 脂肪族又は芳香族又は芳香族性脂肪族であって、適宜、ヘテロ原子により中断されている1〜20炭素原子の直鎖又は分枝鎖炭化水素のアルキレン鎖、
− z=2〜6、好ましくは、z=2。
少なくとも2つのカルボキシル官能基を含む化合物の非制限的例として、アジピン酸、ドデカン二酸、ウンデカン二酸、グルタル酸、及びそれらの分枝同族体を挙げることができる。
− イソシアネート、好ましくはジイソシアネート又はイソシアネートの混合物を、反応器に導入し、
− 適宜、ビウレット化用の触媒例えばカルボン酸又はルイス酸例えばジブチル錫ジラウレートを加え、
− この混合物を110℃に加熱し、
− この混合物に、少なくとも1個の第一又は第二アミン官能基を有し且つ1個のシラン官能基を有する化合物、又はこれらのアミンの混合物を加え、
− 反応媒質を、100〜200℃、好ましくは110〜160℃の温度に、1〜5時間にわたって維持し、
− 未反応のモノマーを、適当な方法例えば薄膜装置における真空蒸留により除去し、
− アルコキシシランユニットを含み且つイソシアネートユニットを含むポリビウレット生成物を回収する。
(Y)2−N−C(=Z)−N(−Y)−R5−Si(R3−X)3-m(R2)m又は
C(=Z)−[(NY−R5−Si(R3−X)3-m(R2)m)]2
ここに、Yは、上で規定した通りであり、Y基の少なくとも1つは、Hに等しく、Yは、適宜置換されたアルキレン鎖でありえ、該鎖は、尿素の2つの窒素を繋ぎ、
A−N(Y)d−C(=Z)−N(Y)−R5−Si(R3−X)3-m(R2)m
ここに、Aは、炭化水素幹の残基を表し、それは、少なくとも1つの第一又は第二アミン官能基を、尿素又はチオ尿素結合に挿入して含み、
ここに、Yは、上で規定した通りであり、Y基の少なくとも1つは、Hに等しく、Yは、適宜置換されたアルキレン鎖でありえて、該鎖は、尿素の2つの窒素を繋ぎ、
Z=O又はSである。
− 出発イソシアネート又は出発ポリイソシアネート混合物に、少なくとも1つのカルボン酸官能基を有する化合物を加え、
− 温度を約100℃±20℃の値に上昇させ、
− この反応媒質に、少なくとも1つの第一又は第二アミン官能基を有し且つ少なくとも1つのシラン官能基を有する化合物又はこれらのアミンの混合物を加え、
− この反応媒質を、100〜200℃の好ましくは110〜160℃の温度に1〜5時間にわたって維持し、
− 未反応モノマーを、適当な方法例えば薄膜デバイス上の真空蒸留により除去し、
− アルコキシシランユニットを含み且つイソシアネートユニットを含むポリアシル尿素ビウレット生成物を回収する。
− 少なくとも1つのビウレット及び/又はアシル尿素結合の存在、
− 及び100gの溶液当たり0〜20重量%好ましくは1〜19重量%のNCO含量、
− 及び珪素(Si)の重量%で表して、0.1〜17.5%の、好ましくは0.5〜13%の、Si−X−R3ユニットの含量及びオリゴマー分布。
− 少なくとも1つのシラン官能基(遊離のイソシアネート官能基を欠く)を含むこの発明の混合された3つのビウレット及び/又は混合された3つのアシル尿素化合物、
− 及び/又は少なくとも1つのシラン官能基及び少なくとも1つの遊離のイソシアネート官能基を含むこの発明の混合された真のビウレット及び/又は混合された真のアシル尿素化合物、
− 及び/又は少なくとも1つのシラン官能基を含む(遊離のイソシアネート官能基を欠く)この発明のポリビウレット及び/又はアシル尿素化合物、
− 及び/又は少なくとも1つのシラン官能基及び少なくとも1つの遊離のイソシアネート官能基を含むこの発明の真のポリビウレット及び/又は真のポリアシル尿素化合物。
− イソシアネート又はイソシアネート及びアルキルカルバメート化合物の出発混合物、
− 及び随意のイソシアネート又はイソシアネート及びアルキルアロファネート化合物の混合物、
− イソシアネートイソシアヌレート化合物、
− ビウレット化合物。
− 求核官能基を含むアルコキシシラン例えばアミノ又はチオアルキルトリアルコキシシラン、
− ヒドロキシアルキルアクリレート、
− 鎖伸長剤例えばジアミン、ジオール又はポリオール、
− 当業者に周知であるイソシアネート官能基を一時的にブロックする薬剤例えばオキシム、ピラゾール、トリアゾール、イミダゾール、ラクタム又はケトエステル(これらのすべての化合物は、少なくとも1つの置換基を有することが可能である)。こうして、非制限的例として、メチルエチルケトキシム、3,5−ジメチルピラゾール、ε−カプロラクタムなどを挙げることができる。
− 様々な特性例えば撥水性を与えるために、ポリオールポリマー例えばセルロース、グアー又は木材のヒドロキシル官能基と反応させるため、
− ポリウレタン及び/又はポリ尿素及び/又はポリチオウレタン及び/又はポリアミドコーティングを得るために、ポリオールの可動性水素を含む官能基例えばポリオールポリマーのヒドロキシル官能基及び/又はポリマーのアミン若しくはチオール若しくはカルボキシル官能基と反応させるために、
− 特定の特性例えば表面張力の低下に寄与するための、コーティング用添加剤、ワニス又は接着剤配合物として、
− 無機化合物例えばシリカ又は二酸化チタン又は酸化ジルコニウムのヒドロキシル又はシラノール官能基と反応するために、
− 少なくとも1つのアルコキシシラン官能基例えばエポキシアルキルトリアルコキシシラン、アルキルトリアルコキシシラン、テトラアルコキシシランなどを有する他のシラン化合物と反応するため
に利用することができる。
− 活性化二重結合を有するモノマー化合物の重合から得られるアクリル酸ポリ(チ)オール、例えば(シクロ)アルキル又はヒドロキシアルキルアクリレート又はメタクリレート、
− アクリル酸ポリアミン、
− 二酸又はジエステル又はカーボネートの、ジオール又はアミノアルコールとの重縮合から生成するポリエステルポリアミン又はポリ(チ)オールポリマー、
− ポリカーボネートポリ(チ)オールポリマー、
− ヒドロキシル及び/又はアミノ及び/又はチオ官能基ポリアミンを有するアルキルユニットを含むポリシロキサン化合物、
− ヒドロキシル及び/又はアミン及び/又はチオール官能基ヒドロキシル官能基を有するポリエーテル、
− ヒドロキシル又はカルボン酸官能基を含むポリプレン化合物、
− アルコキシシラン、
− 又は一時的にブロックされたヒドロキシル、チオール又はアミン官能基を含むポリマー化合物。
これらのブロックされた官能基の例として、イミン、ジオキソラン、アセタールなどを挙げることができる。
可動性水素を含む化合物は、ブロッキング剤と考えられ、直鎖状脂肪族イソシアネート官能基を有する化合物の添加は、180℃以下の放出温度を示す。
約5mモル(評価すべき保護されたブロックされたNCO同等物として)をショット型試験管に入れてマグネチックスターラーで攪拌する。
イソシアネート官能基の「ジブチルアミン」法による定量的測定のために標準化された方法を用いる。定量すべき混合物のイソシアネート官能基との反応により消費されなかったN,N−ジブチルアミンの標準HCl溶液による逆滴定。反応するN,N−ジブチルアミンと導入された量との差は、定量すべき混合物のイソシアネート官能基の含量を測定することを可能にする。
ゲル浸透クロマトグラフィーを、数平均及び重量平均分子量を測定するための方法として使用する。既知分子量のポリスチレン標準を利用して、ゲル浸透カラムを較正する。用いる溶出用溶媒は、標準ポリマー及び分析すべきポリマーに対して良好な溶媒である。それは、ポリマーの検出のための方法(屈折率測定法又は紫外線吸収による分析又は赤外線による分析)により持ち込まれる制約を考慮して選択される。この溶媒は、エーテル例えばテトラヒドロフラン、塩素化誘導体例えばジクロロメタンなどから選択される。
HDI:ヘキサメチレンジイソシアネート
GPC:ゲル浸透クロマトグラフィー
DBA:N,N−ジブチルアミン
APTEO:アミノプロピルトリエトキシシラン
APTMO:アミノプロピルトリメトキシシラン
実施例1:ヘキサメチレンジイソシアネート(HDI)の及びアミノプロピルトリエトキシシラン(APTEO)のビウレット(CMI 1487)
1680gのヘキサメチレンジイソシアネートを、機械式スターラー、滴下漏斗及び還流冷却器を備えた3lの反応器に導入して、窒素で不活性化する。出発NCOの含量は、1.19である。反応媒質の温度は、18.5℃である。次いで、456.5gのアミノプロピルトリエトキシシラン(APTEO)を、1時間にわたって加える。NCO/アミンモル比は、10/1である。反応媒質における発熱ドリフト及び白色沈殿の出現が認められる。発熱反応は、反応媒質の温度を100℃に上昇させる際に利用される。こうして、反応媒質の温度は、徐々に上昇し、添加の10分後には、反応媒質の温度は、25℃であり、30分後には43℃であり、55分後には93℃である。1時間後には、観察された沈殿は、事実上、完全に、その反応媒質に可溶性である。添加の終了時から、反応媒質の温度は、外部エネルギーを与えることによって140℃に上昇する。2時間にわたって、140℃で反応させた後に、反応媒質のイソシアネート官能基の含量は、反応媒質100g当たりNCO0.729モルである。
この手順は、APTMOをAPTEOの代りに用いることを除いては、実施例1のように行なう。
手順は、同じ量の生成物に関しては実施例2のようにするが、操作条件を少し変え;特に、加熱時間は、2時間ではなくて3時間とする。
手順は、モノマーの蒸留の前にバッチを2分割することを除いて、実施例2及び3のように行なう。1010gの生成物を、HDIモノマーの蒸留により精製する。
手順は、NCO/NH2比を7とする以外は、実施例1のようにする。
手順は、NCO/NH2比を10とすることを除いては、実施例1のように行なう。
1010gの実施例4からの組成物を、機械的攪拌機、滴下漏斗及び還流冷却器を備えた3lの反応器に導入して、窒素で不活性化する。反応媒質のNCO含量は、30%である(100g当たり0.716NCO)。この反応媒質を110℃にして、10gのヘキサメチルジシラザン(10重量%)を攪拌しながら導入する。この反応媒質の温度を50分間にわたって140℃にし、この温度で3時間維持する。これらのNCO官能基の反応率を定期的に測定する。それは、次のように変化する:HMDZの添加後1時間の反応の完結時には8.9%であり、1時間30分後には10.6%であり、2時間30分後には14.8%であり、そして3時間後には16.8%である。この反応媒質を100℃まで25分にわたって冷却して、4.6gの1−ブタノールを環状三量体形成反応を停止させるために反応媒質に加える。この反応媒質を、その後、精製して、過剰のモノマーを除去する。実施例1と同じ精製方法を用いる。
100gの実施例1の組成物及び182gの2つのヒドロキシプロピル官能基を含むテレチェリック(telechelic)シリコーン油(Rhodorsil V75)を、反応器に充填する。イソシアネート官能基の含量は、0.129である。
− 2時間40分の反応後に、その含量は、0.113であり(即ち、12.4%のNCO官能基の消費)、
− 4時間の反応後に、その含量は、0.097であり(即ち24.8%のNCO官能基の消費)、
− 80℃で9時間の反応後に、NCO含量は、0.066(2.77%)である(即ち、反応率49%)。
実施例2の化合物のイソシアネート官能基を、対応するメチルカルバメートを得るためにメタノールによりブロックする。
100gの実施例1の組成物を反応器に充填してから、67.3gのアミノプロピルトリメトキシシランを15分間にわたって加える。NCO官能基の含量は、0.218である。
この組成物は、下記の3重架橋システムを構成するシステムに有用な組成物である:
− イソシアネート官能基による、可動性水素を含むポリオール又はポリアミン化合物との架橋、
− 放射技術(UV照射下での架橋又は電子銃)による、他の二重結合を有する架橋可能なモノマーとの架橋、
− 無機物質(シリカ、二酸化チタン、ジルコニア)又はアルコキシシランのシラノール又はヒドロキシル官能基との架橋。
− 2時間30分後に、NCO含量は、0.266(即ち、NCOの反応率16.6%)であり、
− 4時間30分後に、NCO含量は、0.239(即ち、NCOの反応率25.1%)であり、
− 6時間後には、NCO含量は、0.227であり(即ち、NCOの反応率29%)であり、
− 11時間後には、NCO含量は、0.219(即ち、NCOの反応率31.3%)であり、
− 12時間後には、NCO含量は、0.215(即ち、NCOの反応率32.6%)である。
100g当たり0.52モルのNCO官能基含量を有する100gのトロネートHDT(HDI ポリイソシアヌレート、Rhodia社から市販されている)を、実施例1におけるように備えた反応器に導入する。115g(即ち、0.52モル)のアミノプロピルトリエトキシシランを、1時間にわたってランさせる。NCO/NH2比は、1である。
手順は、アミノプロピルトリメトキシシラン(93g)をシランとして用いること以外は比較用実施例1と同様にする。こうして、有機溶媒中で沈殿して溶解度の乏しい化合物が得られる。
この発明の化合物は、下記の4つの応用分野で成功裏に用いられてきている:
− コーティング、ペイント及びワニス:
− 様々な表面におけるシリコーンマスチック及び接着プライマー、
− 重量の重いタイヤ、
− ポリアミド繊維のコーティング。
Claims (12)
- 少なくとも2つの別々のオリゴマー化合物を含むポリイソシアネート組成物であって、
アミノアルキルシランユニット及びジアミノユニットから選択する3つ以上で5つ以下のユニット並びに少なくとも一種のイソシアネート官能基の誘導体からなり、
前記化合物の一つが、少なくとも二つのアミノアルキルシランユニットを含み、及び、
他の化合物が少なくとも二つのジアミノユニットを含み、
前記イソシアネート官能基の誘導体が、カルバメート、ウレチジンジオン、イソシアヌレート、ビウレット、アロファネート、4,6−ジオキソ−2−イミノヘキサヒドロ−1,3,5−トリアジン、イミノオキサジアジンジオン及び2−イミノ−4−オキソ−1,3−ジアゼチジン官能基のいずれかであり、
前記アミノアルキルシランユニットが、下記式Iの化合物の誘導体であることを特徴とする組成物:
(式中、
m及びnは、それぞれ、0、1、2又は3であり;
但し、m+n=3であり;
R1は、2〜20炭素原子の直鎖又は分枝鎖の炭化水素鎖であって、該炭化水素鎖は、脂肪族又は芳香族又はアルアルキルであり、適宜、ヘテロ原子で中断され;
R2は、1〜20炭素原子の直鎖又は分枝鎖の炭化水素鎖を表し;
R3は、1〜20炭素原子の直鎖又は分枝鎖の炭化水素鎖を表し;
X=O又はSである)。 - アミノアルキルシランユニットのジアミノユニットに対する当量比が少なくとも15%である、請求項1に記載の組成物。
- 前記のオリゴマー化合物は、各々、前記組成物の、少なくとも3重量%存在している、請求項1に記載の組成物。
- 前記のオリゴマー化合物が、各々、重量で、組成物の、最大で2/3に相当する、請求項1に記載の組成物。
- 前記の2つの別々のオリゴマー化合物が、いずれもビウレット官能基を含む、請求項1に記載の組成物。
- ビウレット官能基の含量が、前記組成物の5重量%以上である、請求項5に記載の組成物。
- ビウレット官能基の含量が、前記組成物の20重量%以下である、請求項6に記載の組成物。
- 前記組成物の5重量%以上のイソシアネート官能基(遊離の及びブロックされたもの)の含量を示す、請求項1に記載の組成物。
- 前記組成物の5%重量以上の遊離のイソシアネート官能基の含量を示す、請求項1に記載の組成物。
- 前記組成物の5重量%以上のブロックされたイソシアネート官能基の含量を示す、請求項1に記載の組成物。
- NFT 30−029(1980年10月)により測定された粘性が6000mPa・s以下を示す、請求項1に記載の組成物。
- 2重量%以下のイソシアネートモノマーを含む、請求項1に記載の組成物。