JP2012116880A - 屋外用ウレタン接着剤 - Google Patents
屋外用ウレタン接着剤 Download PDFInfo
- Publication number
- JP2012116880A JP2012116880A JP2010265365A JP2010265365A JP2012116880A JP 2012116880 A JP2012116880 A JP 2012116880A JP 2010265365 A JP2010265365 A JP 2010265365A JP 2010265365 A JP2010265365 A JP 2010265365A JP 2012116880 A JP2012116880 A JP 2012116880A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- urethane adhesive
- outdoor
- compound
- solar cell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】(A)イソシアネート化合物(a1)とエステル結合を有するポリオール(a2)が反応して得られるウレタン樹脂及び(B)ヒドロキシフェニルトリアジン系化合物を含み、イソシアネート化合物(a1)は、脂肪族イソシアネート及び脂環式イソシアネートから選択される少なくとも1種を含む、剥離強度が高く、耐候性に優れる屋外用ウレタン接着剤13。
【選択図】図1
Description
(A)イソシアネート化合物(a1)とエステル結合を有するポリオール(a2)が反応して得られるウレタン樹脂及び
(B)ヒドロキシフェニルトリアジン系化合物
を含んで成り、
前記イソシアネート化合物(a1)は、脂肪族イソシアネート及び脂環式イソシアネートから選択される少なくとも1種を含む、屋外用ウレタン接着剤を提供する。
本発明は、他の態様において、シラン化合物を、更に含んで成る屋外用ウレタン接着剤を提供する。
本発明は、更なる態様において、ヒンダーアミン系化合物を、更に含んで成る屋外用ウレタン接着剤を提供する。
本発明は、好ましい要旨において、上記太陽電池バックシートを用いて得られる太陽電池モジュールを提供する。
(A)イソシアネート化合物(a1)とエステル結合を有するポリオール(a2)が反応して得られるウレタン樹脂及び
(B)ヒドロキシフェニルトリアジン系化合物
を含んで成り、
前記イソシアネート化合物(a1)は、脂肪族イソシアネート及び脂環式イソシアネートから選択される少なくとも1種を含むので、
剥離強度及び耐候性の両方の性能が向上して、太陽電池バックシート用接着剤として適する接着剤になる。特に、有機系太陽電池バックシートには着色性及び柔軟性が要求されるので、本発明の屋外用ウレタン接着剤は、有機系太陽電池バックシート用接着剤としてより好ましい。
本発明の屋外用ウレタン接着剤は、更に、ヒンダードフェノール系化合物を含むことで、耐候性がより向上し、太陽電池バックシート用接着剤としてより適切な接着剤となる。
本発明の屋外用ウレタン接着剤は、更に、ヒンダーアミン系化合物を含むことで、ヒドロキシフェニルトリアジンとの相乗効果によって耐候性が向上し、太陽電池バックシート用接着剤としてより好ましく使用することができる。
近年、光吸収層に有機化合物を用いた有機系太陽電池が開発されており、有機系太陽電池に着色性や柔軟性を持たせることが要求されている。従って、有機系太陽電池のバックシートを構成するフィルムが透明化する傾向があるので、色差変化が小さい本発明の太陽電池バックシートは、かかる点からも有用である。
本発明に係る太陽電池モジュールは、上記太陽電池バックシートを用いて得られるので、外観に優れ、更に耐久性能にも優れる。
本発明に係る(A)ウレタン樹脂は、イソシアネート化合物(a1)と、エステル結合を有するポリオール(a2)の反応によって得られるポリマーであって、ウレタン結合を有する。
本発明に係る「イソシアネート化合物(a1)」は、脂肪族イソシアネート及び脂環式イソシアネートのみから構成されることを意味しない。本発明が目的とする屋外用ウレタン接着剤を得られる限り、即ち、本発明の屋外用ウレタン接着剤の剥離強度及び耐候性に悪影響を与えない範囲で、イソシアネート化合物(a1)は、芳香族イソシアネートを含んでもよい。尚、イソシアネート化合物(a1)は、耐候性の観点から、エチレン性二重結合(例えば、エチレン基、ブチレン基等)を含まないことが好ましい。
尚、本明細書では、芳香環は環状の炭化水素鎖に含まれない。
「脂環式イソシアネート」とは、環状の炭化水素鎖を有し、鎖状の炭化水素鎖を有してよい化合物である。イソシアネート基は、環状の炭化水素鎖と直接結合しても、有し得る鎖状の炭化水素鎖と直接結合してもよい。「脂環式イソシアネート」は、芳香環を有してもよいが、その芳香環と、イソシアネート基は、直接結合していない。
従って、例えば、4,4’−ジフェニルメタンジイソシアネート(OCN−C6H4−CH2−C6H4−NCO)は、イソシアネート基が芳香環に直接結合しているので、芳香族イソシアネートに該当する。一方、例えば、キシリレンジイソシアネート(OCN−CH2−C6H4−CH2−NCO)は、芳香環を有するが、イソシアネート基が芳香環に直接結合せず、メチレン基と結合しているので、脂肪族イソシアネートに該当する。
尚、芳香環は、二つ以上のベンゼン環が縮環していてもよい。
脂環式イソシアネートとしては、例えば、5−イソシアナト−1−イソシアナトメチル−1,3,3−トリメチルシクロヘキサン(イソホロンジイソシアネート)、1,3−ビス(イソシアナトメチル)シクロヘキサン(水添キシリレンジイソシアネート)、ビス(4−イソシアナトシクロヘキシル)メタン(水添ジフェニルメタンジイソシアネート)、1,4−ジイソシアナトシクロヘキサン等を例示できる。
これらのイソシアネート化合物は、単独で又は組み合わせて使用することができる。特に、HDI、イソホロンジイソシアネート及びキシリレンジイソシアネートが好ましく、特に、HDIの3量体、イソホロンジイソシアネートの3量体及びキシリレンジイソシアネートの単量体が好ましい。
ポリエステルポリオールは、一般に、低分子ポリオールと、ジカルボン酸及びその無水物との縮合重合反応によって得られる。
カルボン酸無水物として、例えば、無水酢酸、無水プロピオン酸、無水コハク酸、無水マレイン酸、無水フタル酸が挙げられる。これらは、単独で用いても、複数種類を用いても良い。
ジオールとして、例えば、エチレングリコール、1−メチルエチレングリコール、1−エチルエチレングリコール、プロピレングリコール、ブタンジオール、ペンタンジオール、ヘキサンジオール、ヘプタンジオール、オクタンジオール、ノナンジオール、デカンジオール、ネオペンチルグリコール、2−メチル−1,3−プロパンジオール、シクロヘキサンジメタノール、2,4−ジメチル−1,5−ペンタンジオール、2,4−ジブチル−1,5−ペンタンジオール等の低分子量ジオールが含まれる。エチレングリコール、ブタンジオール、ヘキサンジオール、オクタンジオール及びデカンジオールから選択される少なくとも一種が好ましい。
「アクリルポリオール」は、水酸基を有する(メタ)アクリレートの単独重合体でも、「その他の重合性単量体」との共重合体であってもよい。アクリルポリオールの水酸基がイソシアネート基と反応する。
「水酸基を有する(メタ)アクリレート」として、例えば、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、3−ヒドロキシプロピル(メタ)アクリレート、グリセリンモノ(メタ)アクリレート、4−ヒドロキシブチルアクリレート等を例示できる。
本発明では、(C)シラン化合物として、例えば、(メタ)アクリロキシアルキルトリアルコキシシラン類、(メタ)アクリロキシアルキルアルキルアルコキシシラン類、ビニルトリアルコキシシラン類、ビニルアルキルアルコキシシラン類、エポキシシラン類、メルカプトシラン類及びイソシアヌレートシラン類を用いることができるが、これらのシラン化合物のみに限定されることはない。
「(メタ)アクリロキシアルキルアルキルアルコキシシラン類」として、例えば、3−(メタ)アクリロキシプロピルメチルジメトキシシラン、3−(メタ)アクリロキシプロピルメチルジエトキシシラン、3−(メタ)アクリロキシプロピルエチルジエトキシシラン、3−(メタ)アクリロキシエチルメチルジメトキシシラン等を例示できる。
「ビニルトリアルコキシシラン類」として、例えば、ビニルトリメトキシシラン、ビニルトリエトキシシラン、ビニルジメトキシエトキシシラン、ビニルトリ(メトキシエトキシ)シラン、ビニルトリ(エトキシメトキシ)シラン等が例示できる。
「エポキシシラン類」は、例えば、グリシジル系シラン及びエポキシシクロヘキシル系シランに分類できる。「グリシジル系シラン」は、グリシドキシ基を有するもので、具体的には、例えば、3−グリシドキシプロピルメチルジイソプロペノキシシラン、3−グリシドキシプロピルトリメトキシシラン、3−グリシドキシプロピルトリエトキシシラン、3−グリシドキシプロピルジエトキシシラン等を例示できる。
「エポキシシクロヘキシル系シラン」は、3,4−エポキシシクロヘキシル基を有するもので、具体的には、例えば、2−(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン、2−(3,4−エポキシシクロヘキシル)エチルトリエトキシシラン等を例示できる。
「イソシアヌレートシラン類」として、例えば、トリス(3−(トリメトキシシリル)プロピル)イソシアヌレート等を例示できる。
これら(C)シラン化合物は、剥離強度を向上させることに加え、(B)ヒドロキシフェニルトリアジンが含まれた接着剤の耐候性を向上させることができる。本発明では、特に、エポキシシラン類を添加すると、屋外用ウレタン接着剤の性能が著しく向上するので好ましい。
「(D)ヒンダードフェノール系化合物」とは、一般にヒンダードフェノール系化合物とされるものであり、本発明が目的とする屋外用ウレタン接着剤を得られる限り、特に制限されるものではない。
(D)ヒンダードフェノール系化合物は、市販されているものを使用することができる。(D)ヒンダードフェノール系化合物として、例えば、商品名IRGANOX1010、IRGANOX1035、IRGANOX1076、IRGANOX1135、IRGANOX1330及びIRGANOX1520等を使用することができる。ヒンダードフェノール系化合物は、酸化防止剤として接着剤に添加され、例えば、ホスファイト系酸化防止剤、チオエーテル系酸化防止剤、アミン系酸化防止剤等と組み合わせて使用してもよい。
(E)ヒンダードアミン系化合物は、市販されているものを使用することができる。(E)ヒンダードアミン系化合物として、例えば、チヌビン765、チヌビン111FDL、チヌビン123、チヌビン144、チヌビン152、チヌビン292及びチヌビン5100等を使用することができる。ヒンダードアミン系化合物は、光安定剤として接着剤に添加され、例えば、ベンゾトリアゾール系光安定剤、ベンゾエート系光安定剤、ベンゾトリアゾール系光安定剤等と組み合わせて使用することができる。
「その他の成分」を、屋外用ウレタン接着剤に添加する時期は、目的とする屋外用ウレタン樹脂が得られる限り、特に制限されるものではない。その他の成分は、例えば、(A)ウレタン樹脂を合成する際に、イソシアネート化合物(a1)及びポリオール(a2)と一緒に添加しても良く、また、まずイソシアネート化合物(a1)とポリオール(a2)とを反応させて(A)ウレタン樹脂を合成した後、(B)ヒドロキシフェニルトリアジン系化合物を加えるときに、一緒に添加してもよい。
「粘着付与樹脂」として、例えば、スチレン系樹脂、テルペン系樹脂、脂肪族石油樹脂、芳香族石油樹脂、ロジンエステル、アクリル樹脂及びポリエステル樹脂(ポリエステルポリオールを除く)等を例示できる。
「顔料」として、例えば、酸化チタン及びカーボンブラック等を例示できる。
「可塑剤」として、例えば、ジオクチルフタレート、ジブチルフタレート、ジイソノニルアジペート、ジオクチルアジペート及びミネラルスピリット等を例示できる。
「難燃剤」として、例えば、ハロゲン系難燃剤、リン系難燃剤、アンチモン系難燃剤及び、金属水酸化物系難燃剤等を例示できる。
「ワックス」として、パラフィンワックスやマイクロクリスタリンワックス等のワックスが好ましい。
従って、防壁材、屋根材、太陽電池モジュール、窓材、屋外フローリング材、照明保護材、自動車部材、看板等の屋外材料用途として好適である。これらの屋外材料は、複数のフィルムが貼り合わされた積層体を含んでいる。フィルムとしては、プラスチック基材に金属が蒸着されたフィルム(金属蒸着フィルム)、金属が蒸着されていないフィルム(プラスチックフィルム)がある。
太陽電池バックシートを作製する際には、本発明の屋外用ウレタン接着剤をフィルムへ塗布する。塗布方法としては、グラビアコート、ワイヤーバーコート、エアナイフコート、ダイコート、リップコート、コンマコートなどの様々な方法により行うことができる。本発明の屋外用ウレタン接着剤が塗布された複数のフィルムを貼り合わせ、太陽電池バックシートが完成する。
図1は、本発明の太陽電池バックシートの断面図である。太陽電池バックシート10は、2枚のフィルムとその間の屋外用ウレタン接着剤13から形成されており、2枚のフィルム11及び12は、屋外用ウレタン接着剤13によって貼り合わされている。フィルム11及び12は、同一の材料であっても、異なる材料であってもよい。図1では、2枚のフィルム11及び12は、貼り合わされているが、3枚以上のフィルムが貼り合わされていてもよい。
フィルム12として、ポリ塩化ビニル、ポリエステル、フッ素樹脂、アクリル樹脂から成るプラスチックフィルムが用いられるが、耐熱性、耐候性及び剛性、絶縁性等を付与するためにポリエチレンテレフタレートフィルムやポリブチレンテレフタレートフィルムを用いることが特に好ましい。フィルム11及び12は、透明でも、着色されても良い。
フィルム11の蒸着薄膜11aとフィルム12とは、本発明の屋外用ウレタン接着剤13を用いて貼り付けられるが、フィルム11及び12は、ドライラミネート法によって積層されることが多い。
バックシート10は、上述したように、複数のフィルム11及び12の積層体なので、ウレタン接着剤13には、バックシート10が、たとえ長期間屋外に曝されても、フィルム11及び12が剥離しないことが要求される。
1.(A)イソシアネート化合物(a1)とエステル結合を有するポリオール(a2)が反応して得られるウレタン樹脂及び
(B)ヒドロキシフェニルトリアジン系化合物
を含んで成り、
前記イソシアネート化合物(a1)は、脂肪族イソシアネート及び脂環式イソシアネートから選択される少なくとも1種を含む、屋外用ウレタン接着剤。
2.ポリオール(a2)は、ポリエステルポリオール及びアクリルポリオールから選択される少なくとも1種を含んで成る上記1に記載の屋外用ウレタン接着剤。
3.シラン化合物を、更に含んで成る上記1又は2に記載の屋外用ウレタン接着剤。
4.ヒンダードフェノール系化合物を、更に含んで成る上記1〜3のいずれかに記載の屋外用ウレタン接着剤。
5.ヒンダーアミン系化合物を、更に含んで成る上記1〜4のいずれかに記載の屋外用ウレタン接着剤。
6.上記1〜5のいずれかに記載の屋外用ウレタン接着剤を用いて得られる太陽電池バックシート。
7.上記6に記載の太陽電池バックシートを用いて得られる太陽電池モジュール。
実施例及び比較例で使用した屋外用ウレタン接着剤の原料を以下に記載する。
(a1−1)脂肪族イソシアネート:1,6−ジイソシアナトヘキサン(HDI)
(住化バイエルウレタン社製のスミジュールN3300(商品名))
(HDI イソシアヌレート3量体(脂肪族)、NCO%=21.8%)
(a1−2)脂環式イソシアネート:イソホロンジイソシアネート(IPDI)
(エボニックデグサ社製のVESTANATT1890(商品名))
(IPDIイソシアヌレート3量体(脂環式)、NCO%=17.3%)
(a1−3)脂肪族イソシアネート:キシリレンジイソシアネート(XDI)
(三井化学社製のタケネート500(商品名))
(XDI(脂肪族)、NCO%=44.7%)
(a1’−4)4,4’−ジフェニルメタンジイソシアネート(MDI)
(日本ポリウレタン社製のミリオネートMT(商品名))
(MDI(芳香族)、NCO%=33.6%)
(a1’−5)フェニルイソシアネート(東京化成工業社製)
(フェニルイソシアネート(芳香族)、NCO=35.3%)
(a2−1)ポリエステルポリオール
(旭川化学社製のPES229(商品名)のポリオール成分)
(アジピン酸、イソフタル酸、無水フタル酸、ジエチレングリコール、PPG400、トリメチロールプロパンからなるポリエステルポリオール)
(a2−2)ポリエステルポリオール
(旭川化学社製のPES8001(商品名)のポリオール成分)
(セバシン酸、テレフタル酸、ヘキサンジオール、メチルペンタンジオールからなるポリエステルポリオール)
(a2−3)ポリエステルポリオール
(豊国製油社製のHS 2N-226P(商品名))
(無水フタル酸、2,4−ジブチル−1,5−ペンタンジオールからなるポリエステルポリオール)
(a2−4)アクリルポリオール
(綜研化学社製のOG3(商品名))
(n−ブチルメタクリレート、イソブチルメタクリレート、メチルメタクリレート、2−ヒドロキシエチルメタクリレートからなるアクリルポリオール)
(a2−5)アクリルポリオール
(エストロンケミカル社製のイソクリルH270(商品名))
(メチルメタクリレート、ブチルメタクリレート、2−ヒドロキシエチルメタクリレート、メタクル酸からなるアクリルポリオール)
(a2’−6)ポリエーテルポリオール
(第一工業製薬社製のハイフレックスD2000(商品名))
(PPG2000)
尚、成分(a1)と成分(a2)が反応することで、本発明に係る(A)ウレタン樹脂が得られる。
(B1)ヒドロキシフェニルトリアジン
(BASF社製のチヌビン479(商品名))
2−[4−(オクチル−2−メチルエタノエート)オキシ−2−ヒドロキシフェニル]−4,6−[ビス(2,4−ジメチルフェニル)]−1,3,5−トリアジン
(B2)ヒドロキシフェニルトリアジン
(BASF社製のチヌビン400(商品名))
2−[4−(2−ヒドロキシ−3−ドデシロキシ−プロピル)オキシ−2−ヒドロキシフェニル]−4,6−[ビス(2,4−ジメチルフェニル)−1,3,5−トリアジン及び2−[4−(2−ヒドロキシ−3−トリデシロキシ−プロピル)オキシ−2−ヒドロキシフェニル]−4,6−[ビス(2,4−ジメチルフェニル)−1,3,5−トリアジンの混合物
(B3)ヒドロキシフェニルトリアジン
(BASF社製のチヌビン405(商品名))
2−(2,4−ジヒドロキシフェニル)−4,6−ビス−(2,4−ジメチルフェニル)−1,3,5−トリアジンと(2−エチルヘキシル)−グリシド酸エステルの反応生成物
(B4)ヒドロキシフェニルトリアジン
(BASF社製のチヌビン460(商品名))
2,4−ビス[2−ヒドロキシ−4−ブトキシフェニル]−6−(2,4−ジブトキシフェニル)−1,3−5−トリアジン
(B5)ヒドロキシフェニルトリアジン
(BASF社製のチヌビン477(商品名))
トリス[2,4,6−[2−{4−(オクチル−2−メチルエタノエート)オキシ−2−ヒドロキシフェニル}]−1,3,5−トリアジン
(B6’)ベンゾトリアゾール
(BASF社製のチヌビン328(商品名))
2−(3,5−ジ−tert−アミル−2−ヒドロキシフェニル)ベンゾトリアゾール
(B7’)ベンゾトリアゾール
(BASF社製のチヌビン234(商品名))
2−[2−ヒドロキシ−3,5−ビス(α,α−ジメチルベンジル)フェニル]−2H−ベンゾトリアゾール
(B8’)ベンゾトリアゾール
(SHUANG-BANG INDUSTRIAL CO., LTD製のSB-UVA626SP(商品名))
2−(3’−t−ブチル−2’−ヒドロキシ−5’−メチルフェニル)−5−クロロベンゾトリアゾール
(B9’)シュウ酸アニリド
(クラリアントジャパン社製のHostavin PR-25(商品名))
[(4−メトキシフェニル)−メチレン]マロン酸−ジメチルエステル
(B10’)マロン酸エステル
(クラリアントジャパン社製のHostavin B-CAP(商品名))
テトラエチル−2,2’−(1,4−フェニレン−ジメチリデン)−ビスマロネート
(C1)エポキシシラン
(エボニックデグサ社製のダイナシランGLYEO(商品名))
3−グリシドキシプロピルトリエトキシシラン
(C2)エポキシシラン
(エボニックデグサ社製のダイナシランGLYMO(商品名))
3−グリシドキシプロピルトリメトキシシラン
(C3)エポキシシラン
(チッソ社製のサイラエースS530(商品名))
2−(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン
(C4)イソシアヌレートシラン
(モメンティブ社製のSilquest Y−11597(商品名))
トリス(3−(トリメトキシシリル)プロピル)イソシアヌレート
(C5)メルカプトシラン
(チッソ社製のサイラエースS810(商品名))
3−メルカプトプロピルトリメトキシシラン
(D1)ヒンダードフェノール
(BASF社製のイルガノックス1330(商品名))
1,3,5−トリメチル−2,4,6−トリス(3,5−ジ−t−ブチル−4−ヒドロキシベンジル)ベンゼン
(E)光安定剤
(E1)ヒンダードアミン
(BASF社製のチヌビン765(商品名))
セバシン酸ビス(1,2,2,6,6−ペンタメチル−4−ピペリジル)
下記の実施例1〜23及び比較例1〜9の屋外用ウレタン接着剤を、上記成分を用いて製造し、得られた屋外用ウレタン接着剤の性能を、評価した。以下に製造方法及び評価方法を示す。
<屋外用ウレタン接着剤の製造>
表1に示すように、
(a1−1)住化バイエルウレタン社製のスミジュールN3300(商品名)を13.16g、
(a2−1)旭川化学社製のPES229(商品名)を樹脂分として86.84g、
(B1)BASF社製のチヌビン479(商品名)を0.50g、
(D1)BASF社製のイルガノックス1330(商品名)を0.20g
を秤量して混合した後、これら混合物に酢酸エチルを添加して固形分30%の溶液を調製した。この調製液を屋外用ウレタン接着剤とし、以下の試験を行った。
先ず、実施例1の屋外用ウレタン接着剤を透明ポリエチレンテレフタレート(PET)シート(三菱化学ポリエステルフィルム社製のO300EW36(商品名))に固形分重量が10g/m2となるように塗布し、80℃で10分間乾燥させた。
その後、PETシートの接着剤塗布面に、表面処理透明ポリオレフィンフィルム(フタムラ化学社製のリニアローデンシティポリエチレンフィルム LL−XUMN #30(商品名))の表面処理された面を被せ、平面プレス機(神藤金属工業社製のASF−5(商品名))で圧締圧1.0MPa 50℃で30分間、両フィルムをプレスした。プレスしたまま、両フィルムを40℃で1週間養生し、フィルム積層物1とした。
実施例1の屋外用ウレタン接着剤を白色PET(東レ社製のルミラー#100−E20(商品名))に固形分重量が10g/m2となるように塗布し、80℃で10分間乾燥させた。
その後、PETシートの接着剤塗布面に、透明PETフィルム(三菱樹脂社製のテックバリアVグレード(商品名))の表面処理面を被せ、平面プレス機で圧締圧1.0MPa 50℃で30分間、両フィルムをプレスした。プレスしたまま、両フィルムを40℃で1週間養生し、フィルム積層物2とした。
屋外用ウレタン接着剤の評価を以下の方法で行った。
1.UV照射による黄変性の評価
フィルム積層物1のポリオレフィンフィルム側を照射面として、UV照射試験機(岩崎電気社製のアイスーパーUVテスター W13(商品名)))にセットし、照度1000W/m2、60℃50%RHの条件下で15時間の照射を行った。色差計にて照射前後の色差(Δb)を測定し、黄変度を評価した。評価基準は以下のとおりである。
◎:Δbが10未満
○:Δbが10以上 15未満
×:Δbが15以上
フィルム積層物2を、150℃オーブン(シミズ社製のPSFS−50(商品名))に投入し、7日間の静置養生を行った。色差計にて照射前後の色差(Δb)を測定し、黄変度を評価した。評価基準は以下のとおりである。
◎:Δbが13未満
○:Δbが13以上 23未満
×:Δbが23以上
フィルム積層物1を15mm幅に切り出し、引っ張り強度試験機(オリエンテック社製のテンシロンRTM-250(商品名))を用いて、室温環境下、100mm/min、引っ張り速度180°の剥離試験を行った。評価基準は以下のとおりである。
◎:剥離強度が8N/15mm以上
○:剥離強度が6N/15mm以上8N/15mm未満
×:剥離強度が6N/15mm未満
10 バックシート
11 フィルム
11a 蒸着薄膜
12 フィルム
13 接着剤層
20 封止材(EVA)
30 太陽電池セル
40 ガラス板
50 スペーサ
Claims (4)
- (A)イソシアネート化合物(a1)とエステル結合を有するポリオール(a2)が反応して得られるウレタン樹脂及び
(B)ヒドロキシフェニルトリアジン系化合物
を含んで成り、
前記イソシアネート化合物(a1)は、脂肪族イソシアネート及び脂環式イソシアネートから選択される少なくとも1種を含む、屋外用ウレタン接着剤。 - シラン化合物を、更に含んで成る請求項1に記載の屋外用ウレタン接着剤。
- 請求項1又は2に記載の屋外用ウレタン接着剤を用いて得られる太陽電池バックシート。
- 請求項3に記載の太陽電池バックシートを用いて得られる太陽電池モジュール。