JP2012036332A - Light-diffusing resin composition, ink using the resin composition, adhesive, sheet, and molded product - Google Patents
Light-diffusing resin composition, ink using the resin composition, adhesive, sheet, and molded product Download PDFInfo
- Publication number
- JP2012036332A JP2012036332A JP2010179562A JP2010179562A JP2012036332A JP 2012036332 A JP2012036332 A JP 2012036332A JP 2010179562 A JP2010179562 A JP 2010179562A JP 2010179562 A JP2010179562 A JP 2010179562A JP 2012036332 A JP2012036332 A JP 2012036332A
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- light diffusing
- light
- resin
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、光拡散性樹脂組成物、ならびにそれを用いたインキ、接着剤、シート及び成形品に関する。より詳しくは、印刷用光拡散性樹脂組成物と、それを用いたインキ、塗料、接着剤等に関し、また、携帯電話、携帯情報端末、電子リモコン、電卓などの電子機器の操作部の加飾、照明に関する。 The present invention relates to a light diffusing resin composition, and an ink, an adhesive, a sheet, and a molded article using the same. More specifically, it relates to a light diffusing resin composition for printing and inks, paints, adhesives and the like using the composition, and decoration of an operation unit of an electronic device such as a mobile phone, a portable information terminal, an electronic remote control, and a calculator. , Regarding lighting.
近年、携帯電話等の電子機器は、小型化、薄型化が進み、光源として発光ダイオード(LED)が広く用いられるようになっている。また一方で、これら電子機器のボタン操作がしやすいよう、ボタン等の操作部を加飾でき、照明できる材料が望まれている。 In recent years, electronic devices such as mobile phones have been reduced in size and thickness, and light emitting diodes (LEDs) have been widely used as light sources. On the other hand, a material that can decorate and illuminate an operation unit such as a button is desired so that the buttons of these electronic devices can be easily operated.
特許文献1には、蛍光性粒子からなる光拡散剤を透明性樹脂に分散させた光拡散性樹脂組成物が記載されている。
また電子装置の操作部を照明する技術として、例えば、特許文献2記載のものがある。特許文献2には、光拡散素子を含むフィルムを用い、発光ダイオードの光源からフィルムに光を入射し、入射された光が光拡散素子によって拡散して、キーパット部を照明することが開示されている。また、光源は、フィルムの側部および下に設けられることが開示されている。
As a technique for illuminating the operation unit of the electronic device, for example, there is one described in
しかしながら、特許文献1記載のように、これまで光拡散剤のそのものの改良は検討されているものの、従来技術よりも高い照明が求められており、上記特許文献1記載の技術でもなお改善の余地があった。また、特許文献2記載の技術では、光源をフィルムの側面に設けた場合、電子機器の操作部が光源から離れるほど十分な照明が得られないといった問題が生じ、一方、光源をフィルムの下に設けた場合、電子機器の薄型化を実現することが困難であった。
However, as described in
本発明者らは、かかる問題点に鑑み鋭意検討を行った結果、ルチル型の白色針状または白色柱状酸化チタンからなる光拡散剤を含有する光拡散樹脂組成物を用いることにより、光拡散性などの光学特性が良好になり、耐候性の良い光拡散樹脂組成物によって形成された印刷パターンにおいて光源から離れた場合であっても、良好な輝度が得られるなど十分な照明効果を奏することを見出し、本発明を完成するに至った。 As a result of intensive studies in view of such problems, the present inventors have found that light diffusibility is obtained by using a light diffusing resin composition containing a light diffusing agent made of rutile white needle-like or white columnar titanium oxide. Even if it is a case where it is a case where it is away from a light source in a printing pattern formed by a light diffusion resin composition having good weather resistance and good weather resistance, it has a sufficient illumination effect such as obtaining good luminance. The headline and the present invention were completed.
すなわち、本発明によれば、(A)樹脂バインダー、(B)ルチル型の白色針状または白色柱状酸化チタンからなる光拡散剤を含み印刷用途であることを特徴とする光拡散性樹脂組成物、並びにこれを用いたインキ、及び接着剤が提供される。また、透明基材と、前記透明基材の表面にパターン形成された着色層と、を備え、前記着色層が上記光拡散性樹脂組成物から構成されることを特徴とするシート、及びこれを用いた成形品が提供される。 That is, according to the present invention, the light diffusing resin composition is characterized in that it is used for printing, comprising (A) a resin binder and (B) a light diffusing agent comprising rutile-type white needle-like or white columnar titanium oxide. And an ink and an adhesive using the same. Further, a sheet comprising: a transparent base material; and a colored layer patterned on the surface of the transparent base material, wherein the colored layer is composed of the light diffusing resin composition, and The molded product used is provided.
本発明によれば、光学特性が良好な光拡散性樹脂組成物を提供できる。 According to the present invention, a light diffusing resin composition having good optical properties can be provided.
以下、本実施形態について説明する。 Hereinafter, this embodiment will be described.
[光拡散性樹脂組成物]
本発明の光拡散性樹脂組成物は、所望のパターンを形成するための印刷用途であればとくに限定されないが、特にシルクスクリーン印刷用が好ましい。以下、光拡散性樹脂組成物に含まれる各成分について、説明する。
[Light diffusing resin composition]
The light diffusing resin composition of the present invention is not particularly limited as long as it is a printing application for forming a desired pattern, but silk screen printing is particularly preferable. Hereinafter, each component contained in the light diffusing resin composition will be described.
(A)樹脂バインダー
本発明における樹脂バインダーとしては、例えば、アクリルウレタン樹脂、ポリエステル樹脂、ポリウレタン樹脂、アクリル樹脂、塩化ビニル酢酸ビニル共重合樹脂、セルロース誘導体樹脂、ポリカーボネート樹脂、ポリビニルブチラール樹脂、ポリアミド樹脂、エポキシ樹脂、光重合反応性樹脂、紫外線硬化型樹脂等が挙げられる。また、これらは1種または2種以上を用いることができる。
(A) Resin binder Examples of the resin binder in the present invention include acrylic urethane resin, polyester resin, polyurethane resin, acrylic resin, vinyl chloride vinyl acetate copolymer resin, cellulose derivative resin, polycarbonate resin, polyvinyl butyral resin, polyamide resin, Examples thereof include an epoxy resin, a photopolymerization reactive resin, and an ultraviolet curable resin. Moreover, these can use 1 type (s) or 2 or more types.
また、樹脂バインダーの含有量は、光拡散剤100重量部に対し、35重量部以上が好ましく、60重量部以上がより好ましい。これにより、密着性の良い光拡散性樹脂組成物ができる。一方、光拡散性能の観点から、樹脂バインダーの含有量は、光拡散剤100重量部に対し、300重量部以下が好ましく、200重量部以下がより好ましい。 Moreover, 35 weight part or more is preferable with respect to 100 weight part of light-diffusion agents, and, as for content of a resin binder, 60 weight part or more is more preferable. Thereby, the light diffusable resin composition with good adhesiveness can be obtained. On the other hand, from the viewpoint of light diffusion performance, the resin binder content is preferably 300 parts by weight or less, more preferably 200 parts by weight or less, with respect to 100 parts by weight of the light diffusion agent.
(B)光拡散剤
本発明における光拡散剤は、ルチル型の白色針状または白色柱状酸化チタンである。これにより光拡散性および耐候性のバランスに優れた光拡散性樹脂組成物が得られる。
(B) Light diffusing agent The light diffusing agent in the present invention is a rutile-type white needle-like or white columnar titanium oxide. Thereby, a light diffusing resin composition having an excellent balance between light diffusibility and weather resistance is obtained.
光拡散剤の形状は、ルチル型の白色針状または白色柱状酸化チタンを用いることができる。この中でも、光拡散性能の観点から、光拡散剤のアスペクト比(繊維長/繊維径)7〜100が好ましく、10〜29がより好ましい。 As the shape of the light diffusing agent, rutile white needle-shaped or white columnar titanium oxide can be used. Among these, from the viewpoint of light diffusion performance, the aspect ratio (fiber length / fiber diameter) of the light diffusing agent is preferably 7 to 100, and more preferably 10 to 29.
光拡散剤の繊維長は、0.1μm以上が好ましく、0.5μm以上がより好ましい。これにより、光拡散性能の効果を発揮できる。一方、印刷適正の観点から、光拡散剤の平均粒径は、40μm以下が好ましく、10μm以下がより好ましい。 The fiber length of the light diffusing agent is preferably 0.1 μm or more, and more preferably 0.5 μm or more. Thereby, the effect of light diffusion performance can be exhibited. On the other hand, from the viewpoint of printing suitability, the average particle diameter of the light diffusing agent is preferably 40 μm or less, and more preferably 10 μm or less.
本発明の光拡散性樹脂組成物には、その特性を損なわない範囲で、種々の顔料、添加剤等を加えることができる。 Various pigments, additives and the like can be added to the light diffusing resin composition of the present invention as long as the characteristics are not impaired.
本発明の光拡散樹脂組成物は、蛍光顔料または蛍光染料の他に必要により、他の有機顔料、無機顔料および体質顔料などを添加することができる。例えば、塗料原料便覧1970年度版(日本塗料工業会編)に記載されている体質顔料、白顔料、黒顔料、灰色顔料、赤色顔料、茶色顔料、緑色顔料、青顔料、紫顔料、金属粉顔料、発光顔料、真珠色顔料等の有機顔料や無機顔料、さらにはプラスチック顔料等が挙げられる。 The light diffusing resin composition of the present invention may contain other organic pigments, inorganic pigments, extender pigments, and the like as necessary in addition to the fluorescent pigment or fluorescent dye. For example, extender pigments, white pigments, black pigments, gray pigments, red pigments, brown pigments, green pigments, blue pigments, purple pigments, and metal powder pigments described in the paint material manual 1970 edition (edited by Japan Paint Industry Association) And organic pigments such as luminescent pigments and pearlescent pigments, inorganic pigments, and plastic pigments.
有機顔料としては、例えば、ベンジジンイエロー、ハンザイエロー、レーキレッド4R等の如き、各種の不溶性アゾ顔料;レーキレッドC、カーミン6B、ボルドー10等の如き溶性アゾ顔料;フタロシアニンブルー、フタロシアニングリーン等の如き、各種の(銅)フタロシアニン系顔料;ローダミンレーキ、メチルバイオレットレーキ等の如き、各種の塩素性染め付けレーキ;キノリンレーキ、ファストスカイブルー等の如き、各種の媒染染料系顔料;アンスラキノン系顔料、チオインジゴ系顔料、ペリノン系顔料等の如き、各種の建染染料系顔料;シンカシアレッドB等の如き、各種のキナクリドン系顔料;ジオキサジンバイオレット等の如き、各種のジオキサジン系顔料;クロモフタール等の如き、各種の縮合アゾ顔料;アニリンブラック等が挙げられる。 Examples of organic pigments include various insoluble azo pigments such as benzidine yellow, Hansa yellow, and Lake Red 4R; soluble azo pigments such as Lake Red C, Carmine 6B, and Bordeaux 10; and phthalocyanine blue and phthalocyanine green. Various (copper) phthalocyanine pigments; various chlorinated dyeing lakes such as rhodamine lakes and methyl violet lakes; various mordant dye pigments such as quinoline lakes and fast sky blues; anthraquinone pigments and thioindigo Various vat dyes such as pigments and perinone pigments; various quinacridone pigments such as Cyncacia Red B; various dioxazine pigments such as dioxazine violet and the like; Various condensed azo pigments; aniline Click, and the like.
無機顔料としては、例えば、黄鉛、ジンククロメート、モリブデートオレンジ等の如き、各種のクロム酸塩;紺青等の如き、各種のフェロシアン化合物;酸化チタン、亜鉛華、チタンイエロー、酸化鉄、ベンガラ、酸化クロームグリーン等の如き、各種の金属酸化物;カドミウムイエロー、カドミウムレッド、硫化水銀等の如き、各種の硫化物ないしはセレン化物;硫酸バリウム、硫酸鉛等の如き、各種の硫酸塩;ケイ酸カルシウム、群青等の如き、各種のケイ酸塩;炭酸カルシウム、炭酸マグネシウム等の如き、各種の炭酸塩;コバルトバイオレット、マンガン紫の如き、各種の燐酸塩;アルミニウム粉、金粉、銀粉、銅粉、ブロンズ粉、真鍮粉等の如き、各種の金属粉末顔料;これら金属のフレーク顔料、マイカ・フレーク顔料;金属酸化物を被覆した形のマイカ・フレーク顔料、雲母状酸化鉄顔料等の如き、メタリック顔料やパール顔料;黒鉛、カーボンブラック等が挙げられる。 Examples of inorganic pigments include various chromates such as chrome lead, zinc chromate, and molybdate orange; various ferrocyan compounds such as bitumen; titanium oxide, zinc white, titanium yellow, iron oxide, and bengara. And various metal oxides such as chrome green oxide; various sulfides or selenides such as cadmium yellow, cadmium red, and mercury sulfide; various sulfates such as barium sulfate and lead sulfate; silicic acid Various silicates such as calcium and ultramarine; various carbonates such as calcium carbonate and magnesium carbonate; various phosphates such as cobalt violet and manganese purple; aluminum powder, gold powder, silver powder, copper powder, Various metal powder pigments such as bronze powder and brass powder; flake pigments of these metals, mica flake pigments; metal acids Form of mica flake pigment coated objects, such as such as micaceous iron oxide pigments, metallic pigments and pearl pigments; graphite, carbon black and the like.
体質顔料としては、例えば、沈降性硫酸バリウム、胡粉、沈降炭酸カルシウム、重炭酸カルシウム、寒水石、アルミナ白、シリカ、含水微粉珪素、超微粉無水シリカ(アエロジル)、珪砂、タルク、沈降性炭酸マグネシウム、ベントナイト、クレー、カオリン、黄土等が挙げられる。 Examples of extender pigments include, for example, precipitated barium sulfate, pepper, precipitated calcium carbonate, calcium bicarbonate, cryolite, alumina white, silica, hydrous finely divided silicon, ultrafine anhydrous silica (Aerosil), silica sand, talc, and precipitated magnesium carbonate. , Bentonite, clay, kaolin, ocher and the like.
本発明の光拡散性樹脂組成物に用いられる溶剤としては、樹脂バインダーを溶解するもの、またその溶液を希釈するものであればよい。例えば、エステル類、エーテル類、ケトン類、アルコール類、多価アルコール誘導体類、芳香族炭化水素類、ハロゲン化炭化水素類、炭化水素類等を挙げることができる。 The solvent used in the light diffusing resin composition of the present invention may be any solvent that dissolves the resin binder and can dilute the solution. Examples include esters, ethers, ketones, alcohols, polyhydric alcohol derivatives, aromatic hydrocarbons, halogenated hydrocarbons, hydrocarbons and the like.
本発明の光拡散性樹脂組成物は、紫外線吸収剤、及び光安定化剤を用いることができる。紫外線吸収剤または光安定化剤としては、芳香族単環炭化水素基、縮合多環芳香族炭化水素基、複素単環基、及び縮合複素環基を有する群から選択されるものであって、波長200〜400nmの領域に吸収能を有するものが好ましい。 The light diffusing resin composition of the present invention can use an ultraviolet absorber and a light stabilizer. The ultraviolet absorber or light stabilizer is selected from the group having an aromatic monocyclic hydrocarbon group, a condensed polycyclic aromatic hydrocarbon group, a heterocyclic monocyclic group, and a condensed heterocyclic group, What has an absorptivity in the area | region of wavelength 200-400 nm is preferable.
上記の紫外線吸収剤としては、例えば、エチレン性不飽和結合を有するベンゾトリアゾール骨格を含むベンゾトリアゾール系紫外線吸収剤、ベンゾフェノン骨格を含むベンゾフェノン系紫外線吸収剤、サリチル酸を骨格に含むサリチル酸系紫外線吸収剤、シアノアクリレート骨格を含むシアノアクリレート系紫外線吸収剤、ヒンダードフェノール骨格を含むヒンダードフェノール系紫外線吸収剤、トリアジンを骨格に含むトリアジン系紫外線吸収剤を挙げることができる。これらは1種または2種以上を用いることができる。 Examples of the ultraviolet absorber include, for example, a benzotriazole ultraviolet absorber containing a benzotriazole skeleton having an ethylenically unsaturated bond, a benzophenone ultraviolet absorber containing a benzophenone skeleton, a salicylic acid ultraviolet absorber containing salicylic acid, Examples thereof include a cyanoacrylate ultraviolet absorber containing a cyanoacrylate skeleton, a hindered phenol ultraviolet absorber containing a hindered phenol skeleton, and a triazine ultraviolet absorber containing a triazine in the skeleton. These can use 1 type (s) or 2 or more types.
上記の光安定化剤としては、例えば、ヒンダードアミンを骨格に含むヒンダードアミン系光安定化剤、ベンゾエートを骨格に含むベンゾエート系光安定化剤を挙げることができる。これらは1種または2種以上を用いることができる。 Examples of the light stabilizer include a hindered amine light stabilizer containing a hindered amine in the skeleton and a benzoate light stabilizer containing benzoate in the skeleton. These can use 1 type (s) or 2 or more types.
本発明の光拡散性樹脂組成物には、必要に応じて、酸化防止剤等の安定剤、レベリング剤、消泡剤、増粘剤、沈降防止剤、顔料分散剤、帯電防止剤、防曇剤等の界面活性剤類、ワックス、スリップ剤、カップリング剤、シランカップリング剤、近赤外線吸収剤等の各種添加剤を、適宜配合してもよい。 If necessary, the light diffusing resin composition of the present invention includes a stabilizer such as an antioxidant, a leveling agent, an antifoaming agent, a thickening agent, an anti-settling agent, a pigment dispersant, an antistatic agent, and an antifogging agent. Various additives such as surfactants such as an agent, wax, slip agent, coupling agent, silane coupling agent, near infrared absorber, and the like may be appropriately blended.
[インキ、接着剤]
本発明の光拡散性樹脂組成物は、シルクスクリーン印刷や他の一般印刷用としてのインキ、塗料、接着剤等として用いることができる。インキ、塗料、接着剤には、その他必要に応じて、各種添加剤を含有してもよい。インキの調整方法は、特に限定されないが、例えば、樹脂バインダーに有機溶媒を混合、撹拌して、溶解または分散させ、そこに光拡散剤を加えて、さらに分散させて、インキを得ることができる。
[Ink, adhesive]
The light diffusing resin composition of the present invention can be used as an ink, paint, adhesive or the like for silk screen printing or other general printing. The ink, paint, and adhesive may contain various additives as necessary. The ink adjustment method is not particularly limited. For example, an organic solvent is mixed and stirred in a resin binder, dissolved or dispersed, a light diffusing agent is added thereto, and further dispersed to obtain an ink. .
[シート]
本発明のシートは、透明基材と、透明基材の表面にパターン形成された着色層と、を備える。また、本発明のシートは、着色層を覆う透明樹脂層と、黒色または有色樹脂層と、をさらに積層した構造であってもよい。
[Sheet]
The sheet of the present invention comprises a transparent substrate and a colored layer patterned on the surface of the transparent substrate. The sheet of the present invention may have a structure in which a transparent resin layer covering a colored layer and a black or colored resin layer are further laminated.
この着色層は、本発明の光拡散性樹脂組成物を用いたインキを透明基材上に印刷することによってパターン形成されたものである。印刷方法は、一般的に公知の方法が使用でき、例えば、オフセット印刷、グラビア印刷、スクリーン印刷、樹脂凸版印刷、インクジェット印刷等が挙げられる。この中でも、装飾性を良好にする観点から、スクリーン印刷が好ましい。 This colored layer is formed by patterning an ink using the light diffusing resin composition of the present invention on a transparent substrate. As the printing method, generally known methods can be used, and examples thereof include offset printing, gravure printing, screen printing, resin letterpress printing, and ink jet printing. Among these, screen printing is preferable from the viewpoint of improving decorativeness.
シートの透明基材としては、透明又は半透明なプラスチック材料が好ましく、例えば、ポリプロピレン、ポリエチレン、ポリエチレンテレフタレート(PET)、ポリカーボネート、アクリル、塩化ビニル、ガラスが挙げられる。 The transparent base material of the sheet is preferably a transparent or translucent plastic material, and examples thereof include polypropylene, polyethylene, polyethylene terephthalate (PET), polycarbonate, acrylic, vinyl chloride, and glass.
本発明のシートは、例えば、次のようにして製造できる。
図1(a)に示すように、透明基材1を用意する。続けて、透明基材1上に、本発明の光拡散性樹脂組成物を用いたインキを用いて所望のパターンを印刷する。これにより、透明基材1の表面にパターン形成された着色層2が形成される(図1(b))。続けて、着色層2を覆うように、透明樹脂層3を形成し、(図1(c))、さらに黒色樹脂層4を形成する。このようにして、図1(d)に示すようなシート10が得られる。
The sheet | seat of this invention can be manufactured as follows, for example.
As shown to Fig.1 (a), the
[成形品]
本発明の成形品は、上記のシートを用いて得られるものである。成形品としては、例えば、携帯電話、携帯情報端末、電子リモコン、電卓などの電子機器の操作ボタンなどが挙げられる。
[Molding]
The molded product of the present invention is obtained using the above-described sheet. Examples of the molded product include operation buttons of electronic devices such as a mobile phone, a portable information terminal, an electronic remote control, and a calculator.
なお、本発明は前述の実施形態に限定されるものではなく、本発明の目的を達成できる範囲での変形、改良等は本発明に含まれるものである。 It should be noted that the present invention is not limited to the above-described embodiments, and modifications, improvements, and the like within the scope that can achieve the object of the present invention are included in the present invention.
次に、本発明の実施例及び比較例について説明する。ただし、本発明はこれらの実施例により限定されるものではない。 Next, examples and comparative examples of the present invention will be described. However, the present invention is not limited to these examples.
(実施例1)
繊維長が1.68μm、繊維径が0.13μm、アスペクト比が12.9でルチル型の白色針状または白色柱状酸化チタン100重量部に対して、飽和ポリエステル樹脂を112重量部、イソホロンを115重量部、シクヘキサノンを100重量部、消泡剤を6重量部混合して光拡散インキを作製した。
得られた光拡散インキを用いて、透明ポリカーボネートフィルムにスクリーン印刷によって、拡散層を形成して、続けて、着色層を覆うように、株式会社セイコーアドバンス製UV 5510 で透明樹脂層を形成し、さらに株式会社セイコーアドバンス製SG740 710で黒色樹脂層を形成し、拡散シートを作製した。
このようにして、得られた拡散シートは、極めて高度の光拡散性能と耐候性を有していた。また、光拡散インキによるスクリーン印刷も良好に行うことが出来た。
Example 1
The fiber length is 1.68 μm, the fiber diameter is 0.13 μm, the aspect ratio is 12.9, and 100 parts by weight of rutile white needle-like or white columnar titanium oxide is 112 parts by weight of saturated polyester resin and 115 parts of isophorone. A light diffusing ink was prepared by mixing 100 parts by weight of hexhexanone and 6 parts by weight of an antifoaming agent.
Using the obtained light diffusing ink, forming a diffusion layer by screen printing on a transparent polycarbonate film, and subsequently forming a transparent resin layer with UV 5510 manufactured by Seiko Advance Co., Ltd. so as to cover the colored layer, Further, a black resin layer was formed with SG740 710 manufactured by Seiko Advance Co., Ltd., and a diffusion sheet was produced.
Thus, the obtained diffusion sheet had extremely high light diffusion performance and weather resistance. Also, screen printing with light diffusing ink could be performed well.
(実施例2)
繊維長が2.86μm、繊維径が0.21μm、アスペクト比が13.6でルチル型の白色針状または白色柱状酸化チタン100重量部に対して、飽和ポリエステル樹脂を112重量部、イソホロンを115重量部、シクヘキサノンを100重量部、消泡剤を6重量部混合して光拡散インキを作製した。
得られた光拡散インキを用いて、透明ポリカーボネートフィルムにスクリーン印刷によって、拡散層を形成して、続けて、着色層を覆うように、株式会社セイコーアドバンス製UV 5510 で透明樹脂層を形成し、さらに株式会社セイコーアドバンス製SG740 710で黒色樹脂層を形成し、拡散シートを作製した。
このようにして、得られた拡散シートは極めて高度の光拡散性能と耐候性を有していた。また、光拡散インキによるスクリーン印刷も良好に行うことが出来た。
(Example 2)
The fiber length is 2.86 μm, the fiber diameter is 0.21 μm, the aspect ratio is 13.6, and 100 parts by weight of rutile white needle-like or white columnar titanium oxide is 112 parts by weight of saturated polyester resin and 115 parts of isophorone. A light diffusing ink was prepared by mixing 100 parts by weight of hexhexanone and 6 parts by weight of an antifoaming agent.
Using the obtained light diffusing ink, forming a diffusion layer by screen printing on a transparent polycarbonate film, and subsequently forming a transparent resin layer with UV 5510 manufactured by Seiko Advance Co., Ltd. so as to cover the colored layer, Further, a black resin layer was formed with SG740 710 manufactured by Seiko Advance Co., Ltd., and a diffusion sheet was produced.
Thus, the obtained diffusion sheet had extremely high light diffusion performance and weather resistance. Also, screen printing with light diffusing ink could be performed well.
(実施例3)
繊維長が5.15μm、繊維径が0.27μm、アスペクト比が19.1でルチル型の白色針状または白色柱状酸化チタン100重量部に対して、飽和ポリエステル樹脂を112重量部、イソホロンを115重量部、シクヘキサノンを100重量部、消泡剤を6重量部混合して光拡散インキを作製した。得られた光拡散インキを用いて、透明ポリカーボネートフィルムにスクリーン印刷によって、拡散層を形成して、続けて、着色層を覆うように、株式会社セイコーアドバンス製UV 5510 で透明樹脂層を形成し、さらに株式会社セイコーアドバンス製SG740 710で黒色樹脂層を形成し、拡散シートを作製した。
このようにして、得られた拡散シートは極めて高度の光拡散性能と耐候性を有していた。また、光拡散インキによるスクリーン印刷も良好に行うことが出来た。
(Example 3)
The fiber length is 5.15 μm, the fiber diameter is 0.27 μm, the aspect ratio is 19.1, and 100 parts by weight of rutile white needle-like or white columnar titanium oxide is 112 parts by weight of saturated polyester resin and 115 parts of isophorone. A light diffusing ink was prepared by mixing 100 parts by weight of hexhexanone and 6 parts by weight of an antifoaming agent. Using the obtained light diffusing ink, forming a diffusion layer by screen printing on a transparent polycarbonate film, and subsequently forming a transparent resin layer with UV 5510 manufactured by Seiko Advance Co., Ltd. so as to cover the colored layer, Further, a black resin layer was formed with SG740 710 manufactured by Seiko Advance Co., Ltd., and a diffusion sheet was produced.
Thus, the obtained diffusion sheet had extremely high light diffusion performance and weather resistance. Also, screen printing with light diffusing ink could be performed well.
(比較例1)
繊維長が15μm、繊維径が0.45μm、アスペクト比が33.3で白色針状結晶の八チタン酸カリウム繊維100重量部に対して、飽和ポリエステル樹脂を112重量部、イソホロンを115重量部、シクヘキサノンを100重量部、消泡剤を6重量部混合して光拡散インキを作製した。得られた光拡散インキを用いて、透明ポリカーボネートフィルムにスクリーン印刷によって、拡散層を形成して、続けて、着色層を覆うように、株式会社セイコーアドバンス製UV 5510で透明樹脂層を形成し、さらに株式会社セイコーアドバンス製SG740 710で黒色樹脂層を形成し、拡散シートを作製した。
このようにして、得られた拡散シートは光拡散性能を有していなかった。また、光拡散インキによるスクリーン印刷は良好に行うことが出来なかった。
(Comparative Example 1)
112 parts by weight of saturated polyester resin and 115 parts by weight of isophorone with respect to 100 parts by weight of white needle-like crystal potassium octatitanate fibers having a fiber length of 15 μm, a fiber diameter of 0.45 μm, and an aspect ratio of 33.3, A light diffusing ink was prepared by mixing 100 parts by weight of hexhexanone and 6 parts by weight of an antifoaming agent. Using the obtained light diffusing ink, a transparent resin film is formed by screen printing on a transparent polycarbonate film, and then a transparent resin layer is formed with UV 5510 manufactured by Seiko Advance Co., Ltd. so as to cover the colored layer. Further, a black resin layer was formed with SG740 710 manufactured by Seiko Advance Co., Ltd., and a diffusion sheet was produced.
Thus, the obtained diffusion sheet did not have light diffusion performance. Also, screen printing with light diffusing ink could not be performed satisfactorily.
(比較例2)
平均粒子径が3.0μm、屈折率1.55のアクリル酸エステル共重合物100重量部に対して、飽和ポリエステル樹脂を112重量部、イソホロンを115重量部、シクヘキサノンを100重量部、消泡剤を6重量部混合して光拡散インキを作製した。得られた光拡散インキを用いて、透明ポリカーボネートフィルムにスクリーン印刷によって、拡散層を形成して、続けて、着色層を覆うように、株式会社セイコーアドバンス製UV 5510で透明樹脂層を形成し、さらに株式会社セイコーアドバンス製SG740 710で黒色樹脂層を形成し、拡散シートを作製した。
このようにして、得られた拡散シートは光拡散性能を有するが十分な効果を発揮しなかった。また、光拡散インキによるスクリーン印刷は良好に行うことが出来た。
(Comparative Example 2)
112 parts by weight of saturated polyester resin, 115 parts by weight of isophorone, 100 parts by weight of sikuhexanone, 100 parts by weight, with respect to 100 parts by weight of acrylic acid ester copolymer having an average particle size of 3.0 μm and a refractive index of 1.55 A light diffusing ink was prepared by mixing 6 parts by weight of the agent. Using the obtained light diffusing ink, a transparent resin film is formed by screen printing on a transparent polycarbonate film, and then a transparent resin layer is formed with UV 5510 manufactured by Seiko Advance Co., Ltd. so as to cover the colored layer. Further, a black resin layer was formed with SG740 710 manufactured by Seiko Advance Co., Ltd., and a diffusion sheet was produced.
Thus, although the obtained diffusion sheet had light-diffusion performance, it did not exhibit sufficient effects. Moreover, the screen printing with the light diffusing ink was successfully performed.
(比較例3)
蛍光顔料100重量部に対して、飽和ポリエステル樹脂を112重量部、イソホロンを115重量部、シクヘキサノンを100重量部、消泡剤を6重量部混合して光拡散インキを作製した。得られた光拡散インキを用いて、透明ポリカーボネートフィルムにスクリーン印刷によって、拡散層を形成して、続けて、着色層を覆うように、株式会社セイコーアドバンス製UV 5510で透明樹脂層を形成し、さらに株式会社セイコーアドバンス製SG740 710で黒色樹脂層を形成し、拡散シートを作製した。
このようにして、得られた拡散シートは光拡散性能を有するが耐候性が悪く実用性がなかった。また、光拡散インキによるスクリーン印刷は良好に行うことが出来た。
(Comparative Example 3)
A light-diffusing ink was prepared by mixing 112 parts by weight of a saturated polyester resin, 115 parts by weight of isophorone, 100 parts by weight of cyclohexanone, and 6 parts by weight of an antifoaming agent with respect to 100 parts by weight of the fluorescent pigment. Using the obtained light diffusing ink, a transparent resin film is formed by screen printing on a transparent polycarbonate film, and then a transparent resin layer is formed with UV 5510 manufactured by Seiko Advance Co., Ltd. so as to cover the colored layer. Further, a black resin layer was formed with SG740 710 manufactured by Seiko Advance Co., Ltd., and a diffusion sheet was produced.
Thus, although the obtained diffusion sheet had light-diffusion performance, its weather resistance was bad and was not practical. Moreover, the screen printing with the light diffusing ink was successfully performed.
(比較例4)
平均粒子径が0.21μm、ルチル型酸化チタン100重量部に対して、飽和ポリエステル樹脂を112重量部、イソホロンを115重量部、シクヘキサノンを100重量部、消泡剤を6重量部混合して光拡散インキを作製した。得られた光拡散インキを用いて、透明ポリカーボネートフィルムにスクリーン印刷によって、拡散層を形成して、続けて、着色層を覆うように、株式会社セイコーアドバンス製UV 5510で透明樹脂層を形成し、さらに株式会社セイコーアドバンス製SG740 710で黒色樹脂層を形成し、拡散シートを作製した。
このようにして、得られた拡散シートは、良好な耐候性は得られたが、光拡散性能を有しなかった。また、光拡散インキによるスクリーン印刷は良好に行うことが出来た。
(Comparative Example 4)
An average particle size of 0.21 μm and rutile-type titanium oxide of 100 parts by weight were mixed with 112 parts by weight of saturated polyester resin, 115 parts by weight of isophorone, 100 parts by weight of cyclohexanone, and 6 parts by weight of antifoaming agent. A light diffusing ink was prepared. Using the obtained light diffusing ink, a transparent resin film is formed by screen printing on a transparent polycarbonate film, and then a transparent resin layer is formed with UV 5510 manufactured by Seiko Advance Co., Ltd. so as to cover the colored layer. Further, a black resin layer was formed with SG740 710 manufactured by Seiko Advance Co., Ltd., and a diffusion sheet was produced.
Thus, although the obtained diffusion sheet had favorable weather resistance, it did not have light diffusion performance. Moreover, the screen printing with the light diffusing ink was successfully performed.
1 透明基材
2 着色層
3 透明樹脂層
4 黒色樹脂層
10 シート
DESCRIPTION OF
Claims (10)
(B)ルチル型の白色針状または白色柱状酸化チタンからなる光拡散剤
を含み、印刷用途であることを特徴とする光拡散性樹脂組成物。 (A) Resin binder (B) A light diffusing resin composition comprising a light diffusing agent composed of rutile-type white needle-like or white columnar titanium oxide and being used for printing.
(B)光拡散剤100重量部に対し、(A)樹脂バインダーを35重量部〜300重量部を含むことを特徴とする光拡散性樹脂組成物。 The light diffusing resin composition according to claim 1,
(B) A light diffusing resin composition comprising 35 to 300 parts by weight of (A) a resin binder with respect to 100 parts by weight of a light diffusing agent.
(B)光拡散剤のアスペクト比(繊維長/繊維径)が7〜100であることを特徴とする光拡散性樹脂組成物。 In the light diffusable resin composition of Claim 1 or 2,
(B) The light diffusing resin composition, wherein the light diffusing agent has an aspect ratio (fiber length / fiber diameter) of 7 to 100.
(B)光拡散剤の繊維長が、0.1〜40μmであることを特徴とする光拡散性樹脂組成物。 In the light diffusable resin composition of Claim 1 or 2,
(B) The light diffusing resin composition is characterized in that the fiber length of the light diffusing agent is 0.1 to 40 μm.
前記着色層が請求項1乃至4いずれか一項に記載の光拡散性樹脂組成物から構成されることを特徴とするシート。 A transparent base material, and a colored layer patterned on the surface of the transparent base material,
The said colored layer is comprised from the light diffusable resin composition as described in any one of Claims 1 thru | or 4.
前記着色層上に、前記着色層を覆う透明樹脂層をさらに備えたことを特徴とするシート。 The sheet according to claim 7,
A sheet further comprising a transparent resin layer covering the colored layer on the colored layer.
前記透明樹脂層上に、黒色または有色樹脂層が形成されたことを特徴とするシート。 The sheet according to claim 8,
A sheet in which a black or colored resin layer is formed on the transparent resin layer.