JP2009025472A

JP2009025472A - Viewing angle control sheet

Info

Publication number: JP2009025472A
Application number: JP2007187211A
Authority: JP
Inventors: Yasuhiko Akojima; 靖彦阿子島; Atsuya Shimizu; 敦也清水
Original assignee: Shin Etsu Polymer Co Ltd; Shin Etsu Chemical Co Ltd
Current assignee: Shin Etsu Polymer Co Ltd; Shin Etsu Chemical Co Ltd
Priority date: 2007-07-18
Filing date: 2007-07-18
Publication date: 2009-02-05

Abstract

<P>PROBLEM TO BE SOLVED: To provide a viewing angle control sheet that has both viewing angle control effect and decoration properties while maintaining visibility in a display screen, and an applied decoration is hardly peeled off. <P>SOLUTION: The viewing angle control sheet 1 includes: a louver layer 10 in which a light-transmission strip 11 and light-shielding strip 12 are alternately arranged; a transparent protective layer 40 provided on the louver layer 10; and a decorative layer 20 formed on a surface 10a of the louver layer between the louver layer 10 and the transparent protective layer 40. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

本発明は、視野角制御シートに関する。 The present invention relates to a viewing angle control sheet.

例えば、携帯電話や携帯情報端末等では、表示画面を側方から覗き見されることを防止するために視野角制御シートが用いられることがある。また、近年、覗き見を防止するだけでなく、アクセサリーとしても使用できるように装飾が施された視野角制御シートが広く用いられている。このような、装飾性を有する制御シートとしては、以下に示すものがある。 For example, in a mobile phone or a portable information terminal, a viewing angle control sheet may be used to prevent the display screen from being looked into from the side. In recent years, viewing angle control sheets that have been decorated so that they can be used as accessories as well as preventing peeping are widely used. Examples of such control sheets having decorative properties include the following.

光透過帯と遮光帯とが交互に配されたルーバー層と、該ルーバー層上に形成された透明保護層とを有し、該透明保護層上に加飾層が形成された視野角制御シート（特許文献１）。この視野角制御シートを用いれば、光透過帯により表示画面の視認性を保ちつつ、遮光帯により側方からの表示画面の視認性のみが低くなり、側方からの覗き見を防ぐことができる。また、装飾性を有する視野角制御シートであるため、アクセサリーとしての付加価値も高い。
特開２００７−１０７１６号公報 A viewing angle control sheet having a louver layer in which light transmission bands and light shielding bands are alternately arranged, and a transparent protective layer formed on the louver layer, and a decorative layer formed on the transparent protective layer (Patent Document 1). If this viewing angle control sheet is used, the visibility of the display screen from the side is lowered by the light shielding band while the visibility of the display screen is maintained by the light transmission band, and the peeping from the side can be prevented. . Moreover, since it is a viewing angle control sheet having decorativeness, the added value as an accessory is also high.
JP 2007-10716 A

しかし、特許文献１の視野角制御シートでは、表面が擦れること等により加飾層が剥がれ落ちてしまうことがあった。そのため、装飾が剥がれ落ちてしまうおそれの少ない視野角制御シートが望まれている。
本発明は、表示画面の視認性を保った状態で、視野角制御効果と装飾性とを兼ね備え、かつ施した装飾が剥がれ落ちてしまうおそれのほとんどない視野角制御シートを目的とする。 However, in the viewing angle control sheet of Patent Document 1, the decorative layer may be peeled off due to the surface being rubbed. Therefore, there is a demand for a viewing angle control sheet that is less likely to cause the decoration to peel off.
An object of the present invention is to provide a viewing angle control sheet that has both a viewing angle control effect and a decorative property while maintaining the visibility of a display screen, and has almost no fear of peeling off the applied decoration.

本発明の視野角制御シートは、光透過帯と遮光帯とが交互に配されたルーバー層と、該ルーバー層上に設けられた透明保護層とを有しており、前記ルーバー層と前記透明保護層との間の、ルーバー層表面に加飾層が形成されている。 The viewing angle control sheet of the present invention has a louver layer in which light transmission bands and light shielding bands are alternately arranged, and a transparent protective layer provided on the louver layer, and the louver layer and the transparent layer A decorative layer is formed on the surface of the louver layer between the protective layer.

また、本発明の視野角制御シートは、前記加飾層が、シリコーン系インキを用いて形成されているのが好ましい。 Moreover, as for the viewing angle control sheet | seat of this invention, it is preferable that the said decoration layer is formed using silicone type ink.

本発明の視野角制御シートは、表示画面の視認性を保った状態で、視野角制御効果と装飾性とを兼ね備えており、施した装飾が剥がれ落ちてしまうおそれがほとんどない。 The viewing angle control sheet of the present invention has both the viewing angle control effect and the decorativeness while maintaining the visibility of the display screen, and there is almost no possibility that the applied decoration will be peeled off.

以下、本発明の視野角制御シートの実施形態の一例について図１〜４に基づいて詳細に説明する。
［視野角制御シート］
本発明の視野角制御シート１は、図１〜３に示すように、ルーバー層１０と、ルーバー層１０上に設けられた透明保護層４０とを有している。また、図３に示すように、ルーバー層１０と透明保護層４０との間の、ルーバー層１０の表面１０ａ（以下、ルーバー層表面１０ａとする。）に加飾層２０が形成されている。また、ルーバー層１０の透明保護層４０が設けられている側と反対側の面１０ｂ（以下、ルーバー層表面１０ｂとする。）には、粘着層５０が設けられている。
以下、図１〜４に示すように、ルーバー層１０の厚さ方向をＺ方向、Ｚ方向に垂直な面内における互いに垂直な２方向をそれぞれＸ方向、Ｙ方向とする。 Hereinafter, an example of an embodiment of the viewing angle control sheet of the present invention will be described in detail based on FIGS.
[Viewing angle control sheet]
The viewing angle control sheet 1 of the present invention has a louver layer 10 and a transparent protective layer 40 provided on the louver layer 10 as shown in FIGS. Moreover, as shown in FIG. 3, the decoration layer 20 is formed in the surface 10a (henceforth louver layer surface 10a) of the louver layer 10 between the louver layer 10 and the transparent protective layer 40. As shown in FIG. An adhesive layer 50 is provided on the surface 10b of the louver layer 10 opposite to the side on which the transparent protective layer 40 is provided (hereinafter referred to as the louver layer surface 10b).
In the following, as shown in FIGS. 1 to 4, the thickness direction of the louver layer 10 is defined as a Z direction, and two directions perpendicular to each other in a plane perpendicular to the Z direction are defined as an X direction and a Y direction, respectively.

Ｘ−Ｙ平面（Ｚ方向に垂直な面）内における視野角制御シート１の平面形状は、適用する表示画面の形状等に合わせて適宜決定すればよく、例えば、図２に示すような矩形が挙げられる。 The planar shape of the viewing angle control sheet 1 in the XY plane (a plane perpendicular to the Z direction) may be appropriately determined according to the shape of the display screen to be applied. For example, a rectangle as shown in FIG. Can be mentioned.

（ルーバー層）
ルーバー層１０は、図１に示すように、Ｘ方向に延びた、複数の帯状の光透過帯１１および遮光帯１２からなる層である。光透過帯１１と遮光帯１２は、Ｙ方向に交互に配されている。ルーバー層１０が有する光透過帯１１は全て、Ｘ方向の長さが一定であり、Ｙ方向の幅も一定である。また、ルーバー層１０が有する遮光帯１２も全て、Ｘ方向の長さが一定であり、Ｙ方向の幅も一定である。
ただし、光透過帯１１および遮光帯１２は、Ｘ方向の長さが視野角制御シート１の形状によっては異なっていてもよい。また、Ｙ方向の幅は、表示画面の視野角を制御できる範囲であれば、たとえば表示画面の周縁部に配される光透過帯１１および遮光帯１２の幅が、表示画面の中央部に配される幅と異なっていてもよい。 (Louvre layer)
As shown in FIG. 1, the louver layer 10 is a layer composed of a plurality of strip-shaped light transmission bands 11 and light shielding bands 12 extending in the X direction. The light transmission bands 11 and the light shielding bands 12 are alternately arranged in the Y direction. All the light transmission bands 11 of the louver layer 10 have a constant length in the X direction and a constant width in the Y direction. Further, all of the light shielding bands 12 included in the louver layer 10 have a constant length in the X direction and a constant width in the Y direction.
However, the light transmission band 11 and the light shielding band 12 may have different lengths in the X direction depending on the shape of the viewing angle control sheet 1. Further, if the width in the Y direction is within a range in which the viewing angle of the display screen can be controlled, for example, the widths of the light transmission band 11 and the light shielding band 12 arranged at the peripheral edge of the display screen are arranged at the center of the display screen. It may be different from the width to be done.

光透過帯１１の材料としては、透明性が高い樹脂が用いられる。具体的には、光透過帯１１のみに対して、図２中のＺ方向に光を透過させたときの光線透過率が７５％以上、好ましくは８５％以上であるような、高い透明性を有する樹脂材料であるのが好ましい。例えば、透明性が高い熱可塑性樹脂や熱硬化性樹脂が用いられ、具体例としては、セルロース系樹脂、ポリオレフィン系樹脂、ポリエステル系樹脂、シリコーン樹脂、ポリスチレン樹脂、ポリ塩化ビニル樹脂、アクリル樹脂、ポリカーボネート樹脂等が挙げられる。なかでもシリコーン樹脂が好ましく、特に耐熱性が高い点から、シリコーンゴムであるのが特に好ましい。 As the material of the light transmission band 11, a highly transparent resin is used. Specifically, high transparency such that the light transmittance when light is transmitted in the Z direction in FIG. 2 is 75% or more, preferably 85% or more, with respect to only the light transmission band 11. It is preferable that it is the resin material which has. For example, highly transparent thermoplastic resins and thermosetting resins are used. Specific examples include cellulose resins, polyolefin resins, polyester resins, silicone resins, polystyrene resins, polyvinyl chloride resins, acrylic resins, polycarbonates. Examples thereof include resins. Of these, silicone resins are preferred, and silicone rubber is particularly preferred from the viewpoint of particularly high heat resistance.

なお、本明細書における「光線透過率」の値は、光源としてＪＩＳＺ８７２０に規定されるＤ_６５を用い、光源から出射された検査光の強度を受光センサーで測定する装置において、前記検査光の光路上に被測定物が無い状態での受光センサーの出力値をＡ、検査光の光路上に被測定物を配置し、被測定物を透過した透過光が受光センサーで受光される状態での出力値をＢとし、下記式（１）により算出される値とする。
（光線透過率（％））＝（Ｂ／Ａ）×１００・・・（１） Note that the value of “light transmittance” in this specification is D ₆₅ defined in JIS Z 8720 as a light source, and in the apparatus for measuring the intensity of inspection light emitted from the light source with a light receiving sensor, the inspection light is used. The output value of the light receiving sensor when there is no object to be measured on the optical path is A, the object to be measured is placed on the optical path of the inspection light, and the light transmitted through the object to be measured is received by the light receiving sensor. Let B be the value calculated by the following equation (1).
(Light transmittance (%)) = (B / A) × 100 (1)

遮光帯１２の材料としては、光透過帯１１の材料として前記に挙げた樹脂を基材とし、これに顔料や染料等の着色剤を添加してなる着色樹脂が好適に用いられる。遮光帯１２の色調は、遮光帯１２における好ましい遮光性が得られればよく、例えば黒、赤、黄、緑、青、水色等とすることができる。遮光帯１２の色調は、着色剤の種類および添加量によって調整できる。具体的には、遮光帯１２のみに対して、図２中のＹ方向に光を透過させたときの光線透過率が４０％以下、好ましくは１０％以下となるような遮光性を有する遮光帯１２であるのが好ましい。また、遮光帯１２の色調は、ルーバー層１０を見たときに認識される色調となるので装飾性も考慮して設計することが好ましい。 As the material of the light-shielding band 12, a colored resin obtained by using the above-described resin as the material of the light-transmitting band 11 as a base material and adding a colorant such as a pigment or a dye thereto is preferably used. The color tone of the light-shielding band 12 is not particularly limited as long as a preferable light-shielding property in the light-shielding band 12 can be obtained. The color tone of the shading band 12 can be adjusted by the type and amount of the colorant. Specifically, a light-shielding band having a light-shielding property with respect to only the light-shielding band 12 so that the light transmittance when light is transmitted in the Y direction in FIG. 12 is preferred. Moreover, since the color tone of the light-shielding band 12 is a color tone recognized when the louver layer 10 is viewed, it is preferable to design in consideration of decorativeness.

着色剤の具体例としては、カーボンブラック、ベンカラ、酸化鉄、酸化チタン、黄色酸化鉄、ジスアゾイエロー、フタロシアニンブルー等の一般的な有機顔料あるいは無機顔料が挙げられる。着色剤は１種のみを用いてもよく、２種以上を用いてもよい。また、黒色顔料を用いない場合は、良好な遮光性を得るために白色顔料を併用することが好ましい。 Specific examples of the colorant include general organic pigments or inorganic pigments such as carbon black, benkara, iron oxide, titanium oxide, yellow iron oxide, disazo yellow, and phthalocyanine blue. Only 1 type may be used for a coloring agent and it may use 2 or more types. Moreover, when not using a black pigment, it is preferable to use a white pigment together in order to obtain favorable light-shielding property.

ルーバー層１０において、光透過帯１１を形成する樹脂材料と、遮光帯１２の基材となる樹脂材料とは同じであってもよく、異なっていてもよい。光透過帯１１と遮光帯１２との接着性の点からは、両者が同じ樹脂材料により形成されているのが好ましい。 In the louver layer 10, the resin material forming the light transmission band 11 and the resin material serving as the base material of the light shielding band 12 may be the same or different. From the viewpoint of adhesiveness between the light transmission band 11 and the light shielding band 12, it is preferable that both are formed of the same resin material.

ルーバー層１０のＹ―Ｚ平面内における視野角θは、図３に示すように、光透過帯１１のＺ方向における厚さＴおよびＹ方向における幅Ｗ１によって決まる。また、Ｙ方向における光透過帯１１の幅Ｗ１と遮光帯１２の幅Ｗ２の比は、Ｚ方向に平行な光線の透過率に影響する。
具体的には、ルーバー層１０における前記視野角θは、３０〜１５０°の範囲内であるのが好ましく、６０〜１２０°の範囲内であるのがより好ましい。
光透過帯１１のＺ方向における厚さＴは、０．１〜２．５ｍｍ程度であるのが好ましく、０．１４〜０．４ｍｍ程度であるのがより好ましい。
光透過帯１１のＹ方向における幅Ｗ１は、５０μｍ〜０．３ｍｍの範囲内であるのが好ましく、７５μｍ〜０．２ｍｍの範囲内であるのがより好ましい。
遮光帯１２のＹ方向における幅Ｗ２は、５μｍ〜５０μｍの範囲内であるのが好ましく、１５μｍ〜３０μｍの範囲内であるのがより好ましい。
遮光帯１２のＺ方向における厚さＴは、光透過帯１１の厚さＴと同じである。 The viewing angle θ in the YZ plane of the louver layer 10 is determined by the thickness T of the light transmission band 11 in the Z direction and the width W1 in the Y direction, as shown in FIG. Further, the ratio between the width W1 of the light transmission band 11 and the width W2 of the light shielding band 12 in the Y direction affects the transmittance of light rays parallel to the Z direction.
Specifically, the viewing angle θ in the louver layer 10 is preferably in the range of 30 to 150 °, and more preferably in the range of 60 to 120 °.
The thickness T in the Z direction of the light transmission band 11 is preferably about 0.1 to 2.5 mm, and more preferably about 0.14 to 0.4 mm.
The width W1 in the Y direction of the light transmission band 11 is preferably in the range of 50 μm to 0.3 mm, and more preferably in the range of 75 μm to 0.2 mm.
The width W2 of the light shielding band 12 in the Y direction is preferably in the range of 5 μm to 50 μm, and more preferably in the range of 15 μm to 30 μm.
The thickness T of the light shielding band 12 in the Z direction is the same as the thickness T of the light transmission band 11.

（透明保護層）
透明保護層４０は、接着剤３１によりルーバー層１０上に設けられる、ルーバー層１０および加飾層２０を保護する層である。
透明保護層４０の材料としては、透明性が高い樹脂が用いられる。具体的には、透明保護層４０のみに対して、図２中のＺ方向に光を透過させたときの光線透過率が７５％以上、好ましくは８５％以上であるような、高い透明性を有する樹脂材料であるのが好ましい。
また、透明保護層４０を構成する樹脂材料は、高透明性であるとともに紫外線吸収性を有することが好ましく、具体的には、ポリエステル系樹脂、アクリル樹脂、およびポリカーボネート樹脂であるのが好ましい。 (Transparent protective layer)
The transparent protective layer 40 is a layer that protects the louver layer 10 and the decorative layer 20 provided on the louver layer 10 by the adhesive 31.
As a material for the transparent protective layer 40, a highly transparent resin is used. Specifically, high transparency such that only the transparent protective layer 40 has a light transmittance of 75% or more, preferably 85% or more when light is transmitted in the Z direction in FIG. It is preferable that it is the resin material which has.
Moreover, it is preferable that the resin material which comprises the transparent protective layer 40 is highly transparent, and has a UV absorptivity, and specifically, it is preferable that they are a polyester-type resin, an acrylic resin, and a polycarbonate resin.

また、透明保護層４０を構成する樹脂に紫外線吸収剤を含有させてもよい。紫外線吸収剤としては透明性を損なわないものが好ましい。具体例としては、酸化セリウム系紫外線吸収剤、酸化亜鉛系紫外線吸収剤、酸化チタン系紫外線吸収剤が挙げられる。これらの紫外線吸収剤は微粒子化されたものが好ましい。
透明保護層４０に含有させる紫外線吸収剤の粒子径および添加量は、透明保護層４０の好ましい光線透過率が得られる範囲で適宜設定することができる。 Moreover, you may make the resin which comprises the transparent protective layer 40 contain an ultraviolet absorber. As the ultraviolet absorber, those which do not impair the transparency are preferable. Specific examples include cerium oxide ultraviolet absorbers, zinc oxide ultraviolet absorbers, and titanium oxide ultraviolet absorbers. These ultraviolet absorbers are preferably finely divided.
The particle diameter and addition amount of the ultraviolet absorber contained in the transparent protective layer 40 can be appropriately set within a range in which a preferable light transmittance of the transparent protective layer 40 is obtained.

透明保護層４０のＺ方向における厚さは、０．０２５〜０．２ｍｍの範囲であるのが好ましく、０．０５〜０．１ｍｍの範囲であるのがより好ましい。透明保護層４０の厚さが０．０２５ｍｍ以上であれば、保護機能および紫外線遮蔽効果が充分に高くなる。また、透明保護層４０の厚さが０．２ｍｍ以下であれば、透明保護層４０の光線透過率が低くなりすぎるのを防げる。 The thickness of the transparent protective layer 40 in the Z direction is preferably in the range of 0.025 to 0.2 mm, and more preferably in the range of 0.05 to 0.1 mm. If the thickness of the transparent protective layer 40 is 0.025 mm or more, the protective function and the ultraviolet shielding effect are sufficiently high. Moreover, if the thickness of the transparent protective layer 40 is 0.2 mm or less, it can prevent that the light transmittance of the transparent protective layer 40 becomes low too much.

接着剤３１は、硬化後における光線透過率が高いものが好ましい。具体的には、硬化後の接着剤３１単独の光線透過率が６５％以上であるものが好ましく、８０％以上であるものがより好ましい。
接着剤３１としては、硬化後に透明性を有する、熱硬化型接着剤、多液反応型接着剤、紫外線硬化型接着剤等が挙げられ、具体的には、エポキシ系接着剤、ウレタン系接着剤、アクリル系接着剤、メラミン系接着剤、ポリエステル系接着剤、シリコーン系接着剤等が好適に用いられる。 The adhesive 31 preferably has a high light transmittance after curing. Specifically, it is preferable that the light transmittance of the cured adhesive 31 alone is 65% or more, and more preferably 80% or more.
Examples of the adhesive 31 include thermosetting adhesives, multi-component reaction adhesives, UV curable adhesives, and the like that have transparency after curing, and specifically, epoxy adhesives and urethane adhesives. An acrylic adhesive, a melamine adhesive, a polyester adhesive, a silicone adhesive, and the like are preferably used.

（加飾層）
加飾層２０は、図３に示すように、ルーバー層１０と透明保護層４０との間の、ルーバー層表面１０ａに形成される。ルーバー層１０は透明保護層４０よりも厚い層であるため、ルーバー層表面１０ａへの加飾層２０の形成は、透明保護層４０への加飾層２０の形成に比べて、インキの乾燥等で加熱した際に反りが生じるおそれが少ない。 (Decoration layer)
As shown in FIG. 3, the decorative layer 20 is formed on the louver layer surface 10 a between the louver layer 10 and the transparent protective layer 40. Since the louver layer 10 is thicker than the transparent protective layer 40, the formation of the decorative layer 20 on the louver layer surface 10 a is more difficult than the formation of the decorative layer 20 on the transparent protective layer 40. There is little risk of warping when heated at.

加飾層２０は、顔料や染料等の着色剤により着色されている。着色剤としては、遮光帯１２に使用できる着色剤と同じものが使用できる。加飾層２０の色調は、ルーバー層１０における遮光帯１２の色調と異なっており、好ましい光線透過率を有するものであればよい。加飾層２０のＸ−Ｙ平面における形状は、所望の絵柄の形状とすることができる。 The decorative layer 20 is colored with a colorant such as a pigment or a dye. As the colorant, the same colorant that can be used for the light shielding band 12 can be used. The color tone of the decorative layer 20 is different from the color tone of the shading band 12 in the louver layer 10 and may have any preferable light transmittance. The shape in the XY plane of the decoration layer 20 can be made into the shape of a desired picture.

加飾層２０は、具体的には、ルーバー層表面１０ａに印刷法により形成することができる。
加飾層２０を形成する印刷法は、特に限定されないが、網点印刷を用いることが好ましく、ルーバー層１０へ網点印刷を行うにはオフセット印刷法またはスクリーン印刷法が特に好ましい。
網点印刷を用いる場合、加飾層２０の好ましい光線透過率と絵柄の良好な視認性を両立させるために、網点面積率（絵柄を構成する面積全体のうち、インキが存在している面積の割合。）が２０〜６０％の範囲内であるのが好ましく、３５〜５０％の範囲内であるのがより好ましい。
加飾層２０の材料としては、例えば、酸化重合型インキ、紫外線硬化型インキ、蒸発乾燥型インキ等の、一般的なオフセット印刷用インキを用いることができる。インキの基材（ビヒクル）の具体例としては、アクリレート系光重合性樹脂、アクリル樹脂、塩化ビニル−酢酸ビニル共重合樹脂、ポリエステル樹脂、ポリウレタン樹脂等が挙げられる。 Specifically, the decorative layer 20 can be formed on the louver layer surface 10a by a printing method.
The printing method for forming the decorative layer 20 is not particularly limited, but halftone printing is preferably used, and the offset printing method or the screen printing method is particularly preferable for performing halftone printing on the louver layer 10.
When halftone printing is used, in order to achieve both favorable light transmittance of the decorative layer 20 and good visibility of the pattern, the halftone dot area ratio (the area where ink is present in the entire area constituting the pattern) Is preferably in the range of 20 to 60%, and more preferably in the range of 35 to 50%.
As a material of the decoration layer 20, for example, a general offset printing ink such as an oxidation polymerization type ink, an ultraviolet curable ink, and an evaporation drying type ink can be used. Specific examples of the ink substrate (vehicle) include acrylate photopolymerizable resins, acrylic resins, vinyl chloride-vinyl acetate copolymer resins, polyester resins, polyurethane resins, and the like.

また、加飾層２０がルーバー層表面１０ａに印刷法により形成される場合は、シリコーン系インキを用いることが好ましい。
ルーバー層１０の形成にはシリコーンゴムが好適に用いられるため、その場合にはルーバー層１０と加飾層２０との親和性が高くなる。また、ルーバー層１０と透明保護層４０とを接着する接着剤３１にはシリコーン系接着剤が好適に用いられることから、接着性が良好となる。
シリコーン系インキとしては、液状シリコーンゴムに顔料・染料等の着色剤を添加したものが挙げられ、特に付加加硫型の液状シリコーンゴム系インクを用いるのが好ましい。 Further, when the decorative layer 20 is formed on the louver layer surface 10a by a printing method, it is preferable to use a silicone-based ink.
Since silicone rubber is suitably used for forming the louver layer 10, in that case, the affinity between the louver layer 10 and the decorative layer 20 is increased. Further, since a silicone-based adhesive is suitably used for the adhesive 31 that bonds the louver layer 10 and the transparent protective layer 40, the adhesiveness is improved.
Examples of the silicone-based ink include those obtained by adding a colorant such as a pigment or a dye to liquid silicone rubber, and it is particularly preferable to use an addition vulcanization-type liquid silicone rubber-based ink.

加飾層２０における光線透過率は、加飾層２０中に存在する染料や顔料の種類および量によって変化する。
加飾層２０における光線透過率が低いほど、加飾層２０で構成される絵柄の視認性が良くなるが、視野角制御シート１を表示画面上に適用した場合、その表示画面の視認性は低下してしまう。
具体的には、加飾層２０の全面積の９０％以上の領域において、加飾層２０単独の光線透過率が６５〜９０％の範囲内であるのが好ましく、７５〜８５％の範囲内であるのがより好ましい。
ただし、加飾層２０単独の光線透過率とは、実質的には、視野角制御シート１において、加飾層２０が存在する領域にＺ方向に光を透過させたときの光線透過率をＣ（％）、加飾層２０が存在しない領域にＺ方向に光を透過させたときの光線透過率をＤ（％）とし、下記式（２）で算出される値とする。
（加飾層２０単独の光線透過率（％））＝（Ｃ／Ｄ）×１００・・・（２） The light transmittance in the decorative layer 20 varies depending on the type and amount of the dye or pigment present in the decorative layer 20.
The lower the light transmittance in the decorative layer 20 is, the better the visibility of the pattern composed of the decorative layer 20 is. However, when the viewing angle control sheet 1 is applied on the display screen, the visibility of the display screen is It will decline.
Specifically, in the region of 90% or more of the total area of the decorative layer 20, the light transmittance of the decorative layer 20 alone is preferably in the range of 65 to 90%, and in the range of 75 to 85%. It is more preferable that
However, the light transmittance of the decorative layer 20 alone is substantially the light transmittance when the light is transmitted in the Z direction in the region where the decorative layer 20 exists in the viewing angle control sheet 1. (%), The light transmittance when light is transmitted in the Z direction to a region where the decorative layer 20 does not exist is defined as D (%), and is a value calculated by the following formula (2).
(Light transmittance (%) of the decorative layer 20 alone) = (C / D) × 100 (2)

加飾層２０の光線透過率を前記範囲内とすることにより、表示画面の良好な視認性と、加飾層２０によって形成される絵柄の良好な視認性を同時に達成することができる。
また、加飾層２０の全体において光線透過率が均一である必要はなく、加飾層２０の各部分によって光線透過率が互いに異なっていてもよい。例えば、表示画面の周縁部など、表示画面の中でも比較的使用頻度が低い領域では、比較的低い光線透過率でも許容される。一方、表示画面の中央部など使用頻度が高い領域では、加飾層２０の光線透過率が高いことが好ましい。 By setting the light transmittance of the decorative layer 20 within the above range, it is possible to simultaneously achieve good visibility of the display screen and good visibility of the pattern formed by the decorative layer 20.
Further, the light transmittance need not be uniform throughout the decorative layer 20, and the light transmittance may be different depending on each part of the decorative layer 20. For example, a relatively low light transmittance is allowed in a region where the frequency of use is relatively low in the display screen, such as a peripheral portion of the display screen. On the other hand, it is preferable that the light transmittance of the decorative layer 20 is high in a region where the usage frequency is high, such as the center portion of the display screen.

また、加飾層２０は、図４に示すような構成としてもよい。図４において、図３と同じ構成要素には同じ符号を付して、その説明を省略する。
加飾層２０は、ルーバー層表面１０ａに、平面形状が所望の絵柄の形状である接着層２１が設けられ、接着層２１上に転写フィルムの転写層２２が転写されることにより形成される。
接着層２１の材料は、透明性を有し、転写層２２をルーバー層表面１０ａに接着一体化する機能を有するものであればよい。また、接着層２１の平面形状は加飾層２０の平面形状と同じであり装飾性が求められる。したがって、微細な形状を精度良く実現できる点で印刷法により接着層２１を形成することが好ましい。特に、転写層２２を転写するには、接着層２１は一定の膜厚を必要とするため、その膜厚を得るには接着層２１をスクリーン印刷法により形成することが好ましい。 Moreover, the decoration layer 20 is good also as a structure as shown in FIG. 4, the same components as those in FIG. 3 are denoted by the same reference numerals, and the description thereof is omitted.
The decorative layer 20 is formed by providing an adhesive layer 21 having a desired plane shape on the louver layer surface 10 a and transferring the transfer layer 22 of the transfer film onto the adhesive layer 21.
The material of the adhesive layer 21 may be any material that is transparent and has a function of bonding and integrating the transfer layer 22 to the louver layer surface 10a. Further, the planar shape of the adhesive layer 21 is the same as the planar shape of the decorative layer 20, and a decorative property is required. Therefore, it is preferable to form the adhesive layer 21 by a printing method in that a fine shape can be realized with high accuracy. In particular, in order to transfer the transfer layer 22, the adhesive layer 21 needs a certain film thickness. Therefore, it is preferable to form the adhesive layer 21 by a screen printing method in order to obtain the film thickness.

接着層２１の好適な材料としては、スクリーン印刷法によりパターン状に塗布可能で、半硬化状態で粘着性（タック性）を有し、かつ硬化後に透明性を有する樹脂を基材とするインキを用いることができる。例えば、熱硬化型インキ、多液反応型インキ、蒸発乾燥型インキ、紫外線硬化型インキ等が挙げられ、インキの基材の具体例としてはエポキシ樹脂、ウレタン樹脂、アクリル樹脂、メラミン樹脂、ポリエステル樹脂、シリコーン樹脂等が挙げられる。なかでも、ルーバー層１０への接着性が高い点からシリコーン樹脂が特に好ましい。 A suitable material for the adhesive layer 21 is an ink based on a resin that can be applied in a pattern by a screen printing method, has a tackiness in a semi-cured state, and has transparency after curing. Can be used. For example, thermosetting ink, multi-component reaction ink, evaporative drying ink, ultraviolet curable ink, and the like. Specific examples of the ink base material are epoxy resin, urethane resin, acrylic resin, melamine resin, polyester resin. And silicone resin. Among these, a silicone resin is particularly preferable because of its high adhesiveness to the louver layer 10.

また、接着層２１の材料には、顔料または染料を含有させることができる。接着層２１の色調は加飾層２０の色調となるので、これにより装飾性を向上させることができる。ただし、接着層２１への顔料または染料の添加量が多いほど加飾層２０における光線透過率が低下するため、添加量は表示画面の視認性を損なわない量に留めることが好ましい。 The material of the adhesive layer 21 can contain a pigment or a dye. Since the color tone of the adhesive layer 21 becomes the color tone of the decorative layer 20, the decorativeness can be improved thereby. However, since the light transmittance in the decorative layer 20 decreases as the amount of the pigment or dye added to the adhesive layer 21 increases, the amount added is preferably limited to an amount that does not impair the visibility of the display screen.

また、接着層２１は、硬化後の硬度が、ＪＩＳＫ５６００に準処する試験方法による鉛筆引掻試験でＨ以上であることが好ましい。接着層２１の硬度を上記の範囲とすることにより、接着層２１上に転写層２２を転写する際に、接着層２１にダレが発生するのを防止できる。 In addition, the adhesive layer 21 preferably has a hardness after curing of H or more in a pencil scratch test by a test method according to JIS K 5600. By setting the hardness of the adhesive layer 21 in the above range, it is possible to prevent the adhesive layer 21 from sagging when the transfer layer 22 is transferred onto the adhesive layer 21.

接着層２１の厚さは、特に限定されないが、加飾層２０における良好な光線透過率および良好な接着性を達成する上で、５〜５０μｍ程度であるのが好ましく、１０〜３０μｍ程度であるのがより好ましい。 Although the thickness of the contact bonding layer 21 is not specifically limited, In order to achieve the favorable light transmittance and the favorable adhesiveness in the decoration layer 20, it is preferable that it is about 5-50 micrometers, and is about 10-30 micrometers. Is more preferable.

転写層２２の構成材料は特に限定されず、各種の装飾用転写フィルムにおける転写層を用いることができる。
転写層２２の構成材料としては、例えば、インキ層、金属薄膜層、樹脂薄膜にホログラムパターンが形成されたホログラム層等が挙げられる。
転写層２２単独の光線透過率は、低いほど、転写層２２による絵柄の視認性が良くなるが、視野角制御シート１を表示画面上に適用した場合の表示画面の視認性は低下する。また、転写層２２における光線透過率は、全体で均一である必要はなく、転写層２２の部分ごとに材料や色調が異なっていてもよい。
また、加飾層２０を接着層２１と転写層２２とからなる構成とした場合についても、加飾層２０における光線透過率は、印刷法により加飾層２０が形成された場合（図３の場合）と同じ範囲であるのが好ましい。 The constituent material of the transfer layer 22 is not particularly limited, and transfer layers in various decorative transfer films can be used.
Examples of the constituent material of the transfer layer 22 include an ink layer, a metal thin film layer, a hologram layer in which a hologram pattern is formed on a resin thin film, and the like.
The lower the light transmittance of the transfer layer 22 alone, the better the visibility of the pattern by the transfer layer 22, but the visibility of the display screen when the viewing angle control sheet 1 is applied on the display screen is lowered. Further, the light transmittance in the transfer layer 22 does not need to be uniform as a whole, and the material and color tone may be different for each portion of the transfer layer 22.
Moreover, also about the case where the decoration layer 20 is set to the structure which consists of the contact bonding layer 21 and the transfer layer 22, the light transmittance in the decoration layer 20 is the case where the decoration layer 20 is formed by the printing method (FIG. 3). In the same range as in the case of (a).

（粘着層）
粘着層５０は、ルーバー層表面１０ｂ上に設けられ、適用する表示画面に再剥離可能に接着される層である。
粘着層５０の材料としては、表示画面に対して再剥離可能に接着できる程度の粘着力を有するものであればよく、透明性が高いものが好ましい。また、表示画面から剥離したときに糊残りが少ないものが好ましい。例えば、粘着層５０は再剥離可能な粘着剤として市販されている材料からなる層や、エラストマー（低架橋密度品のゲル状物質を含む）からなり、表面５０ａ（表示画面との接着面）が鏡面加工された層であることが好ましい。
再剥離可能な粘着剤の具体例としては、アクリル系粘着剤、ウレタン系粘着剤、ゴム系粘着剤等が挙げられる。
エラストマーの具体例としては、シリコーンゴム、シリコーンゲル、ウレタンゴム、ウレタンゲル等が挙げられる。これらの中でも、糊残りが少なく、透明性が高い点でシリコーンゴムが特に好ましい。 (Adhesive layer)
The adhesive layer 50 is a layer that is provided on the louver layer surface 10b and is detachably adhered to a display screen to be applied.
The material of the adhesive layer 50 may be any material as long as it has such an adhesive force that it can be removably adhered to the display screen, and a material having high transparency is preferable. Moreover, the thing with little adhesive residue when peeling from a display screen is preferable. For example, the pressure-sensitive adhesive layer 50 is made of a layer made of a commercially available material as a re-peelable pressure-sensitive adhesive, or made of an elastomer (including a gel material of a low crosslink density product), and has a surface 50a (adhesive surface with a display screen). A mirror-finished layer is preferred.
Specific examples of the removable adhesive include acrylic adhesives, urethane adhesives, rubber adhesives, and the like.
Specific examples of the elastomer include silicone rubber, silicone gel, urethane rubber, and urethane gel. Among these, silicone rubber is particularly preferable because it has little adhesive residue and high transparency.

本発明の視野角制御シート１において、加飾層２０が設けられていない領域の光線透過率、すなわち本実施形態では粘着層５０とルーバー層１０と透明保護層４０とが積層されている部分にＺ方向に光を透過させたときの光線透過率は、６０％以上であることが好ましく、７０％以上であることがより好ましい。この領域の光線透過率の上限は高い方が好ましいが、充分な視野角制御効果を得るためには９０％程度が限界である。 In the viewing angle control sheet 1 of the present invention, the light transmittance of the region where the decorative layer 20 is not provided, that is, in the portion where the adhesive layer 50, the louver layer 10 and the transparent protective layer 40 are laminated in this embodiment. The light transmittance when light is transmitted in the Z direction is preferably 60% or more, and more preferably 70% or more. The upper limit of the light transmittance in this region is preferably high, but about 90% is the limit in order to obtain a sufficient viewing angle control effect.

また、視野角制御シート１において、加飾層２０が設けられている領域の光線透過率、すなわち本実施形態では粘着層５０とルーバー層１０と加飾層２０と透明保護層４０とが積層されている部分に、Ｚ方向に光を透過させたときの光線透過率は、表示画面の視認性を確保しつつ装飾を施すという点から、５０％以上であることが好ましく、６０％以上であることがより好ましい。この領域の光線透過率の上限は、充分な視野角制御効果を得るためには８５％程度であるのが特に好ましい。 Further, in the viewing angle control sheet 1, the light transmittance of the region where the decorative layer 20 is provided, that is, in this embodiment, the adhesive layer 50, the louver layer 10, the decorative layer 20, and the transparent protective layer 40 are laminated. The light transmittance when the light is transmitted in the Z direction is preferably 50% or more and 60% or more from the viewpoint of decorating while ensuring the visibility of the display screen. It is more preferable. The upper limit of the light transmittance in this region is particularly preferably about 85% in order to obtain a sufficient viewing angle control effect.

［製造方法］
以下、図３に示す実施形態例である、本発明の視野角制御シート１の製造方法の例を説明する。
ルーバー層１０は、以下のようにして製造することができる。まず、光透過帯１１の構成材料からなり、厚さが前記Ｗ１である第１のシートを複数枚と、遮光帯１２の構成材料からなり、厚さが前記Ｗ２である第２のシートを複数枚用意し、それらを交互に積層し、加熱および加圧することによりこれらのシートが一体化してなるブロック体を形成する。ついで、該ブロック体をシート表面に垂直な切断面でスライスすることによりルーバー層１０が得られる。スライスする際の厚さ（スライス幅）は前記Ｔとする。 [Production method]
Hereinafter, the example of the manufacturing method of the viewing angle control sheet 1 of this invention which is the embodiment example shown in FIG. 3 is demonstrated.
The louver layer 10 can be manufactured as follows. First, a plurality of first sheets made of the constituent material of the light transmission band 11 and having the thickness W1 and a plurality of second sheets made of the constituent material of the light shielding band 12 and having the thickness W2. A block body in which these sheets are integrated is formed by preparing sheets, laminating them alternately, and heating and pressing. Next, the louver layer 10 is obtained by slicing the block body along a cut surface perpendicular to the sheet surface. The thickness (slice width) when slicing is T.

ついで、オフセット印刷法により、ルーバー層表面１０ａに加飾層２０を形成する。
ルーバー層１０および加飾層２０と、透明保護層４０とを積層一体化させる方法は特に限定されず、公知の手法を適宜用いることができる。
例えば、予め透明保護層４０の片面、および/またはルーバー層表面１０ａと加飾層２０表面に接着剤３１を塗布し、透明保護層４０とルーバー層１０とを、ルーバー層表面１０ａ側が透明保護層４０に接着されるように貼り合わせた後、接着剤３１を硬化させる。
さらに、ルーバー層表面１０ｂに粘着層５０を設けることにより、視野角制御シート１が得られる。 Next, the decorative layer 20 is formed on the louver layer surface 10a by an offset printing method.
The method for laminating and integrating the louver layer 10 and the decorative layer 20 and the transparent protective layer 40 is not particularly limited, and a known method can be appropriately used.
For example, the adhesive 31 is applied in advance to one surface of the transparent protective layer 40 and / or the louver layer surface 10a and the decorative layer 20 surface, so that the transparent protective layer 40 and the louver layer 10 are disposed on the louver layer surface 10a side. After bonding so as to adhere to 40, the adhesive 31 is cured.
Furthermore, the viewing angle control sheet 1 is obtained by providing the adhesive layer 50 on the louver layer surface 10b.

以上説明した、本実施形態例の視野角制御シート１は、加飾層２０がルーバー層１０と透明保護層４０との間に形成されており、加飾層２０が外部と接触することがないため、擦れ等により加飾層２０が剥げ落ちてしまうおそれがほとんどない。また、透明保護層４０の紫外線吸収性が高い場合には加飾層２０に到達する紫外線を低減できるため、加飾層２０の色彩の劣化を防ぐ効果が高くなる。
さらに、視認側のルーバー層表面（ルーバー層表面１０ａ）に加飾層２０が設けられていることから、視野角外からでも加飾部分を視認できるため、広告媒体としても用いることができる。 In the viewing angle control sheet 1 according to this embodiment described above, the decorative layer 20 is formed between the louver layer 10 and the transparent protective layer 40, and the decorative layer 20 does not come into contact with the outside. Therefore, there is almost no possibility that the decorative layer 20 will peel off due to rubbing or the like. Moreover, since the ultraviolet-ray which reaches | attains the decoration layer 20 can be reduced when the ultraviolet-ray absorptivity of the transparent protective layer 40 is high, the effect which prevents the deterioration of the color of the decoration layer 20 becomes high.
Furthermore, since the decoration layer 20 is provided on the louver layer surface (louver layer surface 10a) on the viewing side, the decoration portion can be visually recognized even from outside the viewing angle, and thus can be used as an advertising medium.

［変形例］
本発明の視野角制御シートの実施形態の変形例としては、ルーバー層表面１０ａ側に設けられた透明保護層４０とは別に、ルーバー層表面１０ｂと粘着層５０との間に第２の透明保護層を設けてもよい。第２の透明保護層の好ましい材料、好ましい光線透過率の範囲、形成方法等は、ルーバー層表面１０ａ側に設けた透明保護層４０と同様である。
かかる変形例によれば、ルーバー層表面１０ａ側の透明保護層４０と第２の透明保護層との間にルーバー層１０が挟まれたサンドイッチ構造となるため、構造の対称性が増し、反りが生じ難くなるなど構造安定性が向上する。 [Modification]
As a modification of the embodiment of the viewing angle control sheet of the present invention, a second transparent protection is provided between the louver layer surface 10b and the adhesive layer 50 separately from the transparent protective layer 40 provided on the louver layer surface 10a side. A layer may be provided. The preferred material, preferred light transmittance range, formation method, and the like of the second transparent protective layer are the same as those of the transparent protective layer 40 provided on the louver layer surface 10a side.
According to such a modification, since the louver layer 10 is sandwiched between the transparent protective layer 40 on the louver layer surface 10a side and the second transparent protective layer, the symmetry of the structure is increased and the warp is increased. Structural stability is improved, such as being less likely to occur.

本発明の視野角制御シートは、例えば携帯電話、携帯情報端末（例えばＰＤＡ；ＰｅｒｓｏｎａｌＤｉｄｉｔａｌＡｓｓｉｓｔａｎｔ）等、情報表示体の表示画面に適用して、その表示画面の視野角を制御できる。さらに、航空機のエンターテーメントビデオ用モニターに装着する表示画面における、広告媒体として適用できる。 The viewing angle control sheet of the present invention can be applied to a display screen of an information display body such as a mobile phone or a portable information terminal (for example, PDA; Personal Digital Assistant) to control the viewing angle of the display screen. Furthermore, the present invention can be applied as an advertising medium on a display screen to be mounted on an aircraft entertainment video monitor.

本発明の視野角制御シートの実施形態の一例を示す分解斜視図である。It is a disassembled perspective view which shows an example of embodiment of the viewing angle control sheet | seat of this invention. 本発明の視野角制御シートの実施形態の一例を示す斜視図である。It is a perspective view which shows an example of embodiment of the viewing angle control sheet | seat of this invention. 図２の視野角制御シートをＩ−Ｉ線で切断した断面図である。It is sectional drawing which cut | disconnected the viewing angle control sheet | seat of FIG. 2 by the II line. 本発明の視野角制御シートの他の実施形態例の断面図である。It is sectional drawing of the other embodiment example of the viewing angle control sheet | seat of this invention.

符号の説明Explanation of symbols

１視野角制御シート
１０ルーバー層
１０ａルーバー層表面
１１光透過帯
１２遮光帯
２０加飾層
４０透明保護層 DESCRIPTION OF SYMBOLS 1 View angle control sheet 10 Louver layer 10a Louver layer surface 11 Light transmission band 12 Light shielding band 20 Decoration layer 40 Transparent protective layer

Claims

光透過帯と遮光帯とが交互に配されたルーバー層と、該ルーバー層上に設けられた透明保護層とを有しており、前記ルーバー層と前記透明保護層との間の、ルーバー層表面に加飾層が形成されていることを特徴とする視野角制御シート。 A louver layer having a louver layer in which light transmission bands and light shielding bands are alternately arranged, and a transparent protective layer provided on the louver layer, the louver layer between the louver layer and the transparent protective layer A viewing angle control sheet, wherein a decorative layer is formed on the surface.

前記加飾層が、シリコーン系インキを用いて形成されている請求項１に記載の視野角制御シート。 The viewing angle control sheet according to claim 1, wherein the decorative layer is formed using a silicone-based ink.