JP2011224856A - Laminate polyester film - Google Patents
Laminate polyester film Download PDFInfo
- Publication number
- JP2011224856A JP2011224856A JP2010096220A JP2010096220A JP2011224856A JP 2011224856 A JP2011224856 A JP 2011224856A JP 2010096220 A JP2010096220 A JP 2010096220A JP 2010096220 A JP2010096220 A JP 2010096220A JP 2011224856 A JP2011224856 A JP 2011224856A
- Authority
- JP
- Japan
- Prior art keywords
- polyester film
- coating layer
- film
- weight
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、積層ポリエステルフィルムに関するものであり、例えば、液晶ディスプレイ、プラズマディスプレイパネル、有機エレクトロルミネッセンス等、外光反射による干渉ムラの軽減が必要な積層ポリエステルフィルムに関するものである。 The present invention relates to a laminated polyester film, for example, a laminated polyester film that needs to reduce interference unevenness due to reflection of external light, such as a liquid crystal display, a plasma display panel, and organic electroluminescence.
近年、ポリエステルフィルムは、各種の光学用フィルムに多く用いられ、液晶やプラズマディスプレイ等の部材であるタッチパネル、反射防止フィルム、プリズムシート、光拡散シート、電磁波シールドフィルム等の用途に用いられている。これらの部材に用いられるベースフィルムには優れた透明性、視認性が要求される。 In recent years, polyester films are frequently used for various optical films, and are used for applications such as touch panels, antireflection films, prism sheets, light diffusion sheets, and electromagnetic wave shielding films, which are members of liquid crystals and plasma displays. The base film used for these members is required to have excellent transparency and visibility.
これらフィルムにはカール防止や傷つき防止、表面硬度等の性能を向上させるために、ハードコート加工されることが多い。また、基材としては、透明性、機械特性に優れたポリエステルフィルムが一般的に使用される。ポリエステルフィルムとハードコート層との密着性を向上させるために、中間層として易接着の塗布層が設けられる場合が一般的である。そのため、ポリエステルフィルム、易接着の塗布層、ハードコート層の3層の屈折率を考慮しないと干渉ムラが発生してしまう。 These films are often hard-coated in order to improve performance such as curling prevention, damage prevention, and surface hardness. Moreover, as a base material, the polyester film excellent in transparency and mechanical characteristics is generally used. In order to improve the adhesion between the polyester film and the hard coat layer, an easily adhesive coating layer is generally provided as an intermediate layer. For this reason, interference unevenness occurs unless the refractive index of the three layers of the polyester film, the easily adhesive coating layer, and the hard coat layer is taken into consideration.
干渉ムラのあるフィルムをタッチパネル等のディスプレイに使用すると、視認性の悪いものになってしまい、使用しづらいものとなってしまう。そのため干渉ムラ対策をすることが求められている。一般的には、干渉ムラを軽減させるための塗布層の屈折率は、基材のポリエステルフィルムの屈折率とハードコート層の屈折率の相乗平均付近と考えられ、この辺りの屈折率に調整することが理想的である。ポリエステルフィルムの屈折率が高いため、一般的には塗布層の屈折率を高く設計する必要がある。 When a film with interference unevenness is used for a display such as a touch panel, the visibility becomes poor and it is difficult to use. Therefore, it is required to take measures against interference unevenness. In general, the refractive index of the coating layer for reducing interference unevenness is considered to be around the geometric mean of the refractive index of the polyester film of the substrate and the refractive index of the hard coat layer, and is adjusted to the refractive index around this. Ideally. Since the refractive index of the polyester film is high, it is generally necessary to design the coating layer with a high refractive index.
塗布層の屈折率を高くして、干渉ムラを改善した例としては、例えば、塗布層中に屈折率の高い金属酸化物を含有させることにより、塗布層中の屈折率を上げる方法がある。この場合は、フィルムの透明性が低下し、各種の光学用として十分な性能を発揮できない場合がある(特許文献1)。また別の例としては、金属キレート化合物と樹脂を組み合わせる方法もある。この場合は、水溶液中での金属キレートの不安定さから、組み合わせによっては塗布液の安定性が十分でない場合があり、長時間の生産を行う場合、液交換作業の増加を招く可能性がある(特許文献2)。また通常用いられる高屈折率材料はハードコート層等の表面機能層との密着性に劣る。そのため高屈折率材料と組み合わせても効果的に密着性を向上することができる塗布層が求められている。 As an example of improving interference unevenness by increasing the refractive index of the coating layer, for example, there is a method of increasing the refractive index in the coating layer by including a metal oxide having a high refractive index in the coating layer. In this case, the transparency of the film is lowered, and there are cases where sufficient performance for various optical applications cannot be exhibited (Patent Document 1). As another example, there is a method of combining a metal chelate compound and a resin. In this case, the stability of the coating solution may not be sufficient depending on the combination due to the instability of the metal chelate in the aqueous solution, which may lead to an increase in the liquid exchange work when producing for a long time. (Patent Document 2). Moreover, the high refractive index material used normally is inferior to adhesiveness with surface functional layers, such as a hard-coat layer. Therefore, a coating layer that can effectively improve adhesion even when combined with a high refractive index material is required.
本発明は、上記実情に鑑みなされたものであって、その解決課題は、外光反射による干渉ムラが軽減され、ハードコート等の各種の表面機能層との密着性に優れた積層ポリエステルフィルムを提供することにある。 The present invention has been made in view of the above circumstances, and the problem to be solved is a laminated polyester film with reduced interference unevenness due to external light reflection and excellent adhesion to various surface functional layers such as hard coats. It is to provide.
本発明者らは、上記実情に鑑み、鋭意検討した結果、特定の構成からなる積層ポリエステルフィルムを用いれば、上述の課題を容易に解決できることを知見し、本発明を完成させるに至った。 As a result of intensive studies in view of the above circumstances, the present inventors have found that the use of a laminated polyester film having a specific configuration can easily solve the above-described problems, and have completed the present invention.
すなわち、本発明の要旨は、ポリエステルフィルムの少なくとも片面に、縮合多環式芳香族を有する化合物、イソシアネート系化合物、および平均粒子径0.15μm以下の粒子を含有する塗布層を有し、当塗布層の絶対反射率が波長400〜800nmの範囲で極小値を1つ有し、当該極小値における絶対反射率が4.0%以上であることを特徴とする積層ポリエステルフィルムに存する。 That is, the gist of the present invention is that at least one surface of a polyester film has a coating layer containing a compound having a condensed polycyclic aromatic, an isocyanate compound, and particles having an average particle size of 0.15 μm or less. The absolute reflectance of the layer has one minimum value in the wavelength range of 400 to 800 nm, and the absolute reflectance at the minimum value is 4.0% or more.
本発明の積層ポリエステルフィルムによれば、ハードコート等の種々の表面機能層を積層した際に外光反射による干渉ムラが少なく、種々の表面機能層との密着性に優れたフィルムを提供することができ、その工業的価値は高い。 According to the laminated polyester film of the present invention, when various surface functional layers such as a hard coat are laminated, there is little interference unevenness due to reflection of external light, and a film excellent in adhesiveness with various surface functional layers is provided. And its industrial value is high.
以下、本発明をさらに詳細に説明する。
本発明における積層ポリエステルフィルムを構成するポリエステルフィルムは単層構成であっても多層構成であってもよく、2層、3層構成以外にも本発明の要旨を越えない限り、4層またはそれ以上の多層であってもよく、特に限定されるものではない。
Hereinafter, the present invention will be described in more detail.
The polyester film constituting the laminated polyester film in the present invention may have a single layer structure or a multilayer structure, and may have four or more layers as long as it does not exceed the gist of the present invention other than a two-layer or three-layer structure. It may be a multilayer, and is not particularly limited.
本発明において使用するポリエステルは、ホモポリエステルであっても共重合ポリエステルであってもよい。ホモポリエステルからなる場合、芳香族ジカルボン酸と脂肪族グリコールとを重縮合させて得られるものが好ましい。芳香族ジカルボン酸としては、テレフタル酸、2,6−ナフタレンジカルボン酸などが挙げられ、脂肪族グリコールとしては、エチレングリコール、ジエチレングリコール、1,4−シクロヘキサンジメタノール等が挙げられる。代表的なポリエステルとしては、ポリエチレンテレフタレート等が例示される。一方、共重合ポリエステルのジカルボン酸成分としては、イソフタル酸、フタル酸、テレフタル酸、2,6−ナフタレンジカルボン酸、アジピン酸、セバシン酸、オキシカルボン酸(例えば、p−オキシ安息香酸など)等の一種または二種以上が挙げられ、グリコール成分として、エチレングリコール、ジエチレングリコール、プロピレングリコール、ブタンジオール、4−シクロヘキサンジメタノール、ネオペンチルグリコール等の一種または二種以上が挙げられる。 The polyester used in the present invention may be a homopolyester or a copolyester. In the case of a homopolyester, those obtained by polycondensation of an aromatic dicarboxylic acid and an aliphatic glycol are preferred. Examples of the aromatic dicarboxylic acid include terephthalic acid and 2,6-naphthalenedicarboxylic acid, and examples of the aliphatic glycol include ethylene glycol, diethylene glycol, and 1,4-cyclohexanedimethanol. Typical polyester includes polyethylene terephthalate and the like. On the other hand, the dicarboxylic acid component of the copolyester includes isophthalic acid, phthalic acid, terephthalic acid, 2,6-naphthalenedicarboxylic acid, adipic acid, sebacic acid, oxycarboxylic acid (for example, p-oxybenzoic acid, etc.), etc. 1 type or 2 types or more are mentioned, As a glycol component, 1 type or 2 types or more, such as ethylene glycol, diethylene glycol, propylene glycol, butanediol, 4-cyclohexane dimethanol, neopentyl glycol, is mentioned.
また、フィルムの耐候性の向上、カラーフィルター等に用いられる色素の劣化防止のために、ポリエステルフィルム中に紫外線吸収剤を含有させてもよい。紫外線吸収剤は、紫外線吸収能を有する化合物で、ポリエステルフィルムの製造工程で付加される熱に耐えうるものであれば特に限定されない。 Moreover, you may contain a ultraviolet absorber in a polyester film in order to improve the weather resistance of a film, and to prevent deterioration of the pigment | dye used for a color filter etc. The ultraviolet absorber is not particularly limited as long as it is a compound having ultraviolet absorbing ability and can withstand the heat applied in the production process of the polyester film.
紫外線吸収剤としては、有機系紫外線吸収剤と無機系紫外線吸収剤があるが、透明性の観点からは有機系紫外線吸収剤が好ましい。有機系紫外線吸収剤としては、特に限定されないが、例えば、環状イミノエステル系、ベンゾトリアゾール系、ベンゾフェノン系などが挙げられる。耐久性の観点からは環状イミノエステル系、ベンゾトリアゾール系がより好ましい。また、紫外線吸収剤を2種類以上併用して用いることも可能である。 As the ultraviolet absorber, there are an organic ultraviolet absorber and an inorganic ultraviolet absorber. From the viewpoint of transparency, an organic ultraviolet absorber is preferable. Although it does not specifically limit as an organic type ultraviolet absorber, For example, a cyclic imino ester type, a benzotriazole type, a benzophenone type etc. are mentioned. From the viewpoint of durability, a cyclic imino ester type and a benzotriazole type are more preferable. It is also possible to use two or more ultraviolet absorbers in combination.
本発明のフィルムのポリエステル層中には、易滑性の付与および各工程での傷発生防止を主たる目的として、粒子を配合することが好ましい。配合する粒子の種類は、易滑性付与可能な粒子であれば特に限定されるものではなく、具体例としては、例えば、シリカ、炭酸カルシウム、炭酸マグネシウム、炭酸バリウム、硫酸カルシウム、リン酸カルシウム、リン酸マグネシウム、カオリン、酸化アルミニウム、酸化チタン等の粒子が挙げられる。また、特公昭59−5216号公報、特開昭59−217755号公報等に記載されている耐熱性有機粒子を用いてもよい。この他の耐熱性有機粒子の例として、熱硬化性尿素樹脂、熱硬化性フェノール樹脂、熱硬化性エポキシ樹脂、ベンゾグアナミン樹脂等が挙げられる。さらに、ポリエステル製造工程中、触媒等の金属化合物の一部を沈殿、微分散させた析出粒子を用いることもできる。 In the polyester layer of the film of the present invention, it is preferable to blend particles mainly for the purpose of imparting slipperiness and preventing scratches in each step. The kind of the particle to be blended is not particularly limited as long as it is a particle capable of imparting slipperiness. Specific examples thereof include silica, calcium carbonate, magnesium carbonate, barium carbonate, calcium sulfate, calcium phosphate, and phosphoric acid. Examples of the particles include magnesium, kaolin, aluminum oxide, and titanium oxide. Further, the heat-resistant organic particles described in JP-B-59-5216, JP-A-59-217755 and the like may be used. Examples of other heat-resistant organic particles include thermosetting urea resins, thermosetting phenol resins, thermosetting epoxy resins, benzoguanamine resins, and the like. Furthermore, precipitated particles obtained by precipitating and finely dispersing a part of a metal compound such as a catalyst during the polyester production process can also be used.
一方、使用する粒子の形状に関しても特に限定されるわけではなく、球状、塊状、棒状、扁平状等のいずれを用いてもよい。また、その硬度、比重、色等についても特に制限はない。これら一連の粒子は、必要に応じて2種類以上を併用してもよい。 On the other hand, the shape of the particles to be used is not particularly limited, and any of a spherical shape, a block shape, a rod shape, a flat shape and the like may be used. Moreover, there is no restriction | limiting in particular about the hardness, specific gravity, a color, etc. These series of particles may be used in combination of two or more as required.
また、用いる粒子の平均粒子径は、通常0.01〜3μm、好ましくは0.01〜2μmの範囲である。平均粒子径が0.01μm未満の場合には、易滑性を十分に付与できなかったり、粒子が凝集して、分散性が不十分となり、フィルムの透明性を低下させたりする場合がある。一方、3μmを超える場合には、フィルムの表面粗度が粗くなりすぎて、後工程において種々の表面機能層を塗設させる場合等に不具合が生じる場合がある。 Moreover, the average particle diameter of the particle | grains to be used is 0.01-3 micrometers normally, Preferably it is the range of 0.01-2 micrometers. When the average particle size is less than 0.01 μm, the slipperiness may not be sufficiently imparted, or the particles may be aggregated, the dispersibility becomes insufficient, and the transparency of the film may be lowered. On the other hand, when the thickness exceeds 3 μm, the surface roughness of the film becomes too rough, and a problem may occur when various surface functional layers are applied in a subsequent process.
さらにポリエステル層中の粒子含有量は、通常0.0001〜5重量%、好ましくは0.0003〜3重量%の範囲である。粒子含有量が0.0001重量%未満の場合には、フィルムの易滑性が不十分な場合があり、一方、5重量%を超えて添加する場合にはフィルムの透明性が不十分な場合がある。 Furthermore, the content of particles in the polyester layer is usually in the range of 0.0001 to 5% by weight, preferably 0.0003 to 3% by weight. When the particle content is less than 0.0001% by weight, the slipperiness of the film may be insufficient. On the other hand, when the content exceeds 5% by weight, the transparency of the film is insufficient. There is.
ポリエステル層中に粒子を添加する方法としては、特に限定されるものではなく、従来公知の方法を採用しうる。例えば、各層を構成するポリエステルを製造する任意の段階において添加することができるが、好ましくはエステル化もしくはエステル交換反応終了後、添加するのが良い。 The method for adding particles to the polyester layer is not particularly limited, and a conventionally known method can be adopted. For example, it can be added at any stage for producing the polyester constituting each layer, but it is preferably added after completion of esterification or transesterification.
また、ベント付き混練押出機を用い、エチレングリコールまたは水などに分散させた粒子のスラリーとポリエステル原料とをブレンドする方法、または、混練押出機を用い、乾燥させた粒子とポリエステル原料とをブレンドする方法などによって行われる。 Also, a method of blending a slurry of particles dispersed in ethylene glycol or water with a vented kneading extruder and a polyester raw material, or a blending of dried particles and a polyester raw material using a kneading extruder. It is done by methods.
なお、本発明におけるポリエステルフィルム中には、上述の粒子以外に必要に応じて従来公知の酸化防止剤、帯電防止剤、熱安定剤、潤滑剤、染料、顔料等を添加することができる。 In addition to the above-mentioned particles, conventionally known antioxidants, antistatic agents, thermal stabilizers, lubricants, dyes, pigments, and the like can be added to the polyester film in the present invention as necessary.
本発明におけるポリエステルフィルムの厚みは、フィルムとして製膜可能な範囲であれば特に限定されるものではないが、通常10〜300μm、好ましくは50〜250μmの範囲である。 Although the thickness of the polyester film in this invention will not be specifically limited if it can be formed into a film as a film, Usually, 10-300 micrometers, Preferably it is the range of 50-250 micrometers.
次に本発明におけるポリエステルフィルムの製造例について具体的に説明するが、以下の製造例に何ら限定されるものではない。すなわち、先に述べたポリエステル原料を使用し、ダイから押し出された溶融シートを冷却ロールで冷却固化して未延伸シートを得る方法が好ましい。この場合、シートの平面性を向上させるためシートと回転冷却ドラムとの密着性を高めることが好ましく、静電印加密着法および/または液体塗布密着法が好ましく採用される。次に得られた未延伸シートは二軸方向に延伸される。その場合、まず、前記の未延伸シートを一方向にロールまたはテンター方式の延伸機により延伸する。延伸温度は、通常70〜120℃、好ましくは80〜110℃であり、延伸倍率は通常2.5〜7倍、好ましくは3.0〜6倍である。次いで、一段目の延伸方向と直交する方向に延伸するが、その場合、延伸温度は通常70〜170℃であり、延伸倍率は通常3.0〜7倍、好ましくは3.5〜6倍である。そして、引き続き180〜270℃の温度で緊張下または30%以内の弛緩下で熱処理を行い、二軸配向フィルムを得る。上記の延伸においては、一方向の延伸を2段階以上で行う方法を採用することもできる。その場合、最終的に二方向の延伸倍率がそれぞれ上記範囲となるように行うのが好ましい。 Next, although the manufacture example of the polyester film in this invention is demonstrated concretely, it is not limited to the following manufacture examples at all. That is, a method of using the polyester raw material described above and cooling and solidifying a molten sheet extruded from a die with a cooling roll to obtain an unstretched sheet is preferable. In this case, in order to improve the flatness of the sheet, it is preferable to improve the adhesion between the sheet and the rotary cooling drum, and an electrostatic application adhesion method and / or a liquid application adhesion method is preferably employed. Next, the obtained unstretched sheet is stretched in the biaxial direction. In that case, first, the unstretched sheet is stretched in one direction by a roll or a tenter type stretching machine. The stretching temperature is usually 70 to 120 ° C., preferably 80 to 110 ° C., and the stretching ratio is usually 2.5 to 7 times, preferably 3.0 to 6 times. Next, the film is stretched in the direction perpendicular to the first stretching direction. In that case, the stretching temperature is usually 70 to 170 ° C., and the stretching ratio is usually 3.0 to 7 times, preferably 3.5 to 6 times. is there. Subsequently, heat treatment is performed at a temperature of 180 to 270 ° C. under tension or under relaxation within 30% to obtain a biaxially oriented film. In the above-described stretching, a method in which stretching in one direction is performed in two or more stages can be employed. In that case, it is preferable to carry out so that the draw ratios in the two directions finally fall within the above ranges.
また、本発明においては積層ポリエステルフィルムを構成するポリエステルフィルム製造に関しては同時二軸延伸法を採用することもできる。同時二軸延伸法は、前記の未延伸シートを通常70〜120℃、好ましくは80〜110℃で温度コントロールされた状態で機械方向および幅方向に同時に延伸し配向させる方法であり、延伸倍率としては、面積倍率で4〜50倍、好ましくは7〜35倍、さらに好ましくは10〜25倍である。そして、引き続き、170〜250℃の温度で緊張下または30%以内の弛緩下で熱処理を行い、延伸配向フィルムを得る。上述の延伸方式を採用する同時二軸延伸装置に関しては、スクリュー方式、パンタグラフ方式、リニアー駆動方式等、従来公知の延伸方式を採用することができる。 In the present invention, the simultaneous biaxial stretching method can be adopted for the production of the polyester film constituting the laminated polyester film. The simultaneous biaxial stretching method is a method in which the above-mentioned unstretched sheet is usually stretched and oriented in the machine direction and the width direction at a temperature controlled normally at 70 to 120 ° C., preferably 80 to 110 ° C. Is 4 to 50 times, preferably 7 to 35 times, and more preferably 10 to 25 times in terms of area magnification. Subsequently, heat treatment is performed at a temperature of 170 to 250 ° C. under tension or under relaxation within 30% to obtain a stretched oriented film. With respect to the simultaneous biaxial stretching apparatus that employs the above-described stretching method, a conventionally known stretching method such as a screw method, a pantograph method, or a linear driving method can be employed.
次に本発明における積層ポリエステルフィルムを構成する塗布層の形成について説明する。塗布層に関しては、ポリエステルフィルムの延伸工程中にフィルム表面を処理する、インラインコーティングにより設けられてもよく、一旦製造したフィルム上に系外で塗布する、オフラインコーティングを採用してもよく、両者を併用してもよい。製膜と同時に塗布が可能であるため、製造が安価に対応可能であり、塗布層の厚みを延伸倍率により変化させることができるという点でインラインコーティングが好ましく用いられる。 Next, formation of the coating layer which comprises the laminated polyester film in this invention is demonstrated. As for the coating layer, it may be provided by in-line coating, which treats the film surface during the stretching process of the polyester film, or may be applied off-system on the film once manufactured, and may employ both offline coating. You may use together. In-line coating is preferably used in that it can be applied at the same time as film formation, and thus can be manufactured at low cost, and the thickness of the coating layer can be changed by the draw ratio.
インラインコーティングについては、以下に限定するものではないが、例えば、逐次二軸延伸においては、特に縦延伸が終了した横延伸前にコーティング処理を施すことができる。インラインコーティングによりポリエステルフィルム上に塗布層が設けられる場合には、製膜と同時に塗布が可能になると共に塗布層を高温で処理することができ、ポリエステルフィルムとして好適なフィルムを製造できる。 The in-line coating is not limited to the following, but for example, in the sequential biaxial stretching, the coating treatment can be performed particularly before the lateral stretching after the longitudinal stretching is finished. When a coating layer is provided on a polyester film by in-line coating, coating can be performed simultaneously with film formation, and the coating layer can be processed at a high temperature, and a film suitable as a polyester film can be produced.
本発明においては、ポリエステルフィルムの少なくとも片面に、縮合多環式芳香族を有する化合物、イソシアネート系化合物、および平均粒子径0.15μm以下の粒子を含有する塗布層を有し、当塗布層の絶対反射率が波長400〜800nmの範囲で極小値を1つ有し、当該極小値における絶対反射率が4.0%以上である塗布層を有することを必須の要件とするものである。 In the present invention, at least one surface of the polyester film has a coating layer containing a compound having a condensed polycyclic aromatic, an isocyanate compound, and particles having an average particle size of 0.15 μm or less. It is an essential requirement to have a coating layer having one minimum value in the wavelength range of 400 to 800 nm and having an absolute reflectance of 4.0% or more at the minimum value.
本発明における縮合多環式芳香族の具体例としては、下記式で示される構造を有する化合物である。 Specific examples of the condensed polycyclic aromatic in the present invention are compounds having a structure represented by the following formula.
ポリエステルフィルム上への塗布性を考慮すると、縮合多環式芳香族を有する化合物は、例えば、ポリエステル樹脂、アクリル樹脂、ウレタン樹脂等の高分子化合物が好ましい。特にポリエステル樹脂にはより多くの縮合多環式芳香族を導入することができるためより好ましい。 In consideration of applicability on the polyester film, the compound having a condensed polycyclic aromatic is preferably a polymer compound such as a polyester resin, an acrylic resin, or a urethane resin. In particular, polyester resins are more preferable because more condensed polycyclic aromatics can be introduced.
縮合多環式芳香族をポリエステル樹脂に組み込む方法としては、例えば、縮合多環式芳香族に置換基として水酸基を2つあるいはそれ以上導入してジオール成分あるいは多価水酸基成分とするか、あるいはカルボン酸基を2つあるいはそれ以上導入してジカルボン酸成分あるいは多価カルボン酸成分として作成する方法がある。 As a method of incorporating the condensed polycyclic aromatic into the polyester resin, for example, two or more hydroxyl groups are introduced into the condensed polycyclic aromatic as a substituent to form a diol component or a polyvalent hydroxyl component, or There is a method in which two or more acid groups are introduced to prepare a dicarboxylic acid component or a polyvalent carboxylic acid component.
積層ポリエステルフィルム製造工程において、着色がしにくいという点で、塗布層に含有する縮合多環式芳香族はナフタレン骨格を有する化合物が好ましい。また、塗布層上に形成される各種表面機能層との密着性や、透明性が良好であるという点で、ポリエステル構成成分としてナフタレン骨格を組み込んだ樹脂が好適に用いられる。当該ナフタレン骨格としては、代表的なものとして、1,5−ナフタレンジカルボン酸および2,6−ナフタレンジカルボン酸、2,7−ナフタレンジカルボン酸が挙げられる。 In the laminated polyester film production process, the condensed polycyclic aromatic contained in the coating layer is preferably a compound having a naphthalene skeleton in that it is difficult to be colored. In addition, a resin in which a naphthalene skeleton is incorporated as a polyester component is suitably used in terms of good adhesion to various surface functional layers formed on the coating layer and transparency. Representative examples of the naphthalene skeleton include 1,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, and 2,7-naphthalenedicarboxylic acid.
なお、縮合多環式芳香族には、水酸基やカルボン酸基以外にも、硫黄元素を含有する置換基、フェニル基等の芳香族置換基、ハロゲン元素基等を導入することにより、屈折率の向上が期待でき、塗布性や密着性の観点から、アルキル基、エステル基、アミド基等の置換基を導入してもよい。 In addition to the hydroxyl group and the carboxylic acid group, the condensed polycyclic aromatic has a refractive index of a refractive index by introducing a substituent containing a sulfur element, an aromatic substituent such as a phenyl group, a halogen element group, and the like. Improvements can be expected, and substituents such as alkyl groups, ester groups, and amide groups may be introduced from the viewpoints of coatability and adhesion.
イソシアネート系化合物とは、イソシアネート、あるいはブロックイソシアネートに代表されるイソシアネート誘導体由来の化合物のことである。イソシアネートとしては、例えば、トリレンジイソシアネート、キシリレンジイソシアネート、メチレンジフェニルジイソシアネート、フェニレンジイソシアネート、ナフタレンジイソシアネート等の芳香族イソシアネート、α,α,α’,α’−テトラメチルキシリレンジイソシアネート等の芳香環を有する脂肪族イソシアネート、メチレンジイソシアネート、プロピレンジイソシアネート、リジンジイソシアネート、トリメチルヘキサメチレンジイソシアネート、ヘキサメチレンジイソシアネート等の脂肪族イソシアネート、シクロヘキサンジイソシアネート、メチルシクロヘキサンジイソシアネート、イソホロンジイソシアネート、メチレンビス(4−シクロヘキシルイソシアネート)、イソプロピリデンジシクロヘキシルジイソシアネート等の脂環族イソシアネート等が例示される。また、これらイソシアネートのビュレット化物、イソシアヌレート化物、ウレトジオン化物、カルボジイミド変性体等の重合体や誘導体も挙げられる。これらは単独で用いても、複数種併用してもよい。上記イソシアネートの中でも、紫外線による黄変を避けるために、芳香族イソシアネートよりも脂肪族イソシアネートまたは脂環族イソシアネートがより好ましい。 An isocyanate compound is a compound derived from an isocyanate derivative typified by isocyanate or blocked isocyanate. Examples of the isocyanate include aromatic isocyanates such as tolylene diisocyanate, xylylene diisocyanate, methylene diphenyl diisocyanate, phenylene diisocyanate, and naphthalene diisocyanate, and aromatic rings such as α, α, α ′, α′-tetramethylxylylene diisocyanate. Aliphatic isocyanates such as aliphatic isocyanate, methylene diisocyanate, propylene diisocyanate, lysine diisocyanate, trimethylhexamethylene diisocyanate, hexamethylene diisocyanate, cyclohexane diisocyanate, methylcyclohexane diisocyanate, isophorone diisocyanate, methylene bis (4-cyclohexyl isocyanate), isopropylidene dicyclohexyl diisocyanate Ne Alicyclic isocyanates such as bets are exemplified. Further, polymers and derivatives such as burettes, isocyanurates, uretdiones, and carbodiimide modified products of these isocyanates are also included. These may be used alone or in combination. Among the above isocyanates, aliphatic isocyanates or alicyclic isocyanates are more preferable than aromatic isocyanates in order to avoid yellowing due to ultraviolet rays.
本発明におけるブロックイソシアネートのブロック剤としては、例えば重亜硫酸塩類、フェノール、クレゾール、エチルフェノールなどのフェノール系化合物、プロピレングリコールモノメチルエーテル、エチレングリコール、ベンジルアルコール、メタノール、エタノールなどのアルコール系化合物、マロン酸ジメチル、マロン酸ジエチル、アセト酢酸メチル、アセト酢酸エチル、アセチルアセトンなどの活性メチレン系化合物、ブチルメルカプタン、ドデシルメルカプタンなどのメルカプタン系化合物、ε‐カプロラクタム、δ‐バレロラクタムなどのラクタム系化合物、ジフェニルアニリン、アニリン、エチレンイミンなどのアミン系化合物、アセトアニリド、酢酸アミドの酸アミド化合物、ホルムアルデヒド、アセトアルドオキシム、アセトンオキシム、メチルエチルケトンオキシム、シクロヘキサノンオキシムなどのオキシム系化合物が挙げられ、これらは単独でも2種以上の併用であってもよい。 Examples of the blocking agent for the blocked isocyanate in the present invention include phenol compounds such as bisulfites, phenol, cresol and ethyl phenol, alcohol compounds such as propylene glycol monomethyl ether, ethylene glycol, benzyl alcohol, methanol and ethanol, and malonic acid. Active methylene compounds such as dimethyl, diethyl malonate, methyl acetoacetate, ethyl acetoacetate, acetylacetone, mercaptan compounds such as butyl mercaptan, dodecyl mercaptan, lactam compounds such as ε-caprolactam, δ-valerolactam, diphenylaniline, Amine compounds such as aniline and ethyleneimine, acetanilide, acid amide compounds of acetic acid amide, formaldehyde, acetoaldoxime, Examples include oxime compounds such as acetone oxime, methyl ethyl ketone oxime, and cyclohexanone oxime, and these may be used alone or in combination of two or more.
また、本発明におけるイソシアネート系化合物は単体で用いても良いし、各種ポリマーとの混合物や結合物として用いても良い。イソシアネート系化合物の分散性や架橋性を向上させるという意味において、ウレタン樹脂やポリエステル樹脂との混合物や結合物を使用することが好ましい。 In addition, the isocyanate compound in the present invention may be used alone, or may be used as a mixture or bond with various polymers. In the sense of improving the dispersibility and crosslinkability of the isocyanate compound, it is preferable to use a mixture or a bond with a urethane resin or a polyester resin.
本発明における積層ポリエステルフィルムにおいて、塗布面状の向上、塗布面上にハードコート層等の種々の表面機能層が積層されたときの干渉ムラの低減、透明性や密着性の向上、塗布面状を良化させる等のために各種のバインダーポリマーを併用することも可能である。 In the laminated polyester film of the present invention, the coated surface is improved, interference unevenness is reduced when various surface functional layers such as a hard coat layer are laminated on the coated surface, transparency and adhesion are improved, and the coated surface is formed. It is also possible to use various binder polymers in combination for improving the quality.
本発明において使用する「バインダーポリマー」とは高分子化合物安全性評価フロースキーム(昭和60年11月 化学物質審議会主催)に準じて、ゲルパーミエーションクロマトグラフィー(GPC)測定による数平均分子量(Mn)が1000以上の高分子化合物で、かつ造膜性を有するものと定義する。 The “binder polymer” used in the present invention is a number average molecular weight (Mn) measured by gel permeation chromatography (GPC) according to a polymer compound safety evaluation flow scheme (hosted by the Chemical Substance Council in November 1985). ) Is a polymer compound having a molecular weight of 1000 or more and having a film-forming property.
バインダーポリマーの具体例としては、ポリエステル樹脂、アクリル樹脂、ウレタン樹脂、ポリビニル(ポリビニルアルコール、ポリ塩化ビニル、塩化ビニル酢酸ビニル共重合体等)、ポリアルキレングリコール、ポリアルキレンイミン、メチルセルロース、ヒドロキシセルロース、でんぷん類等が挙げられる。 Specific examples of the binder polymer include polyester resin, acrylic resin, urethane resin, polyvinyl (polyvinyl alcohol, polyvinyl chloride, vinyl chloride vinyl acetate copolymer, etc.), polyalkylene glycol, polyalkylene imine, methyl cellulose, hydroxy cellulose, and starch. And the like.
さらに塗布層中には本発明の主旨を損なわない範囲において、イソシアネート系化合物以外の架橋剤を併用することも可能である。イソシアネート系化合物以外の架橋剤としては、種々公知の樹脂が使用できるが、例えば、オキサゾリン化合物、メラミン化合物、エポキシ化合物等が挙げられる。 Furthermore, in the coating layer, a crosslinking agent other than the isocyanate compound can be used in combination as long as the gist of the present invention is not impaired. As the crosslinking agent other than the isocyanate compound, various known resins can be used, and examples thereof include an oxazoline compound, a melamine compound, and an epoxy compound.
オキサゾリン化合物とは、分子内にオキサゾリン基を有する化合物である。特にオキサゾリン基を含有する重合体が好ましく、付加重合性オキサゾリン基含有モノマー単独もしくは他のモノマーとの重合によって作成できる。付加重合性オキサゾリン基含有モノマーは、2−ビニル−2−オキサゾリン、2−ビニル−4−メチル−2−オキサゾリン、2−ビニル−5−メチル−2−オキサゾリン、2−イソプロペニル−2−オキサゾリン、2−イソプロペニル−4−メチル−2−オキサゾリン、2−イソプロペニル−5−エチル−2−オキサゾリン等を挙げることができ、これらの1種または2種以上の混合物を使用することができる。これらの中でも2−イソプロペニル−2−オキサゾリンが工業的にも入手しやすく好適である。他のモノマーは、付加重合性オキサゾリン基含有モノマーと共重合可能なモノマーであれば制限なく、例えばアルキル(メタ)アクリレート(アルキル基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、イソブチル基、t−ブチル基、2−エチルヘキシル基、シクロヘキシル基)等の(メタ)アクリル酸エステル類;アクリル酸、メタクリル酸、イタコン酸、マレイン酸、フマール酸、クロトン酸、スチレンスルホン酸およびその塩(ナトリウム塩、カリウム塩、アンモニウム塩、第三級アミン塩等)等の不飽和カルボン酸類;アクリロニトリル、メタクリロニトリル等の不飽和ニトリル類;(メタ)アクリルアミド、N−アルキル(メタ)アクリルアミド、N,N−ジアルキル(メタ)アクリルアミド、(アルキル基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、イソブチル基、t−ブチル基、2−エチルヘキシル基、シクロヘキシル基等)等の不飽和アミド類;酢酸ビニル、プロピオン酸ビニル等のビニルエステル類;メチルビニルエーテル、エチルビニルエーテル等のビニルエーテル類;エチレン、プロピレン等のα−オレフィン類;塩化ビニル、塩化ビニリデン、フッ化ビニル等の含ハロゲンα,β−不飽和モノマー類;スチレン、α−メチルスチレン、等のα,β−不飽和芳香族モノマー等を挙げることができ、これらの1種または2種以上のモノマーを使用することができる。 An oxazoline compound is a compound having an oxazoline group in the molecule. In particular, a polymer containing an oxazoline group is preferable, and it can be prepared by polymerization of an addition polymerizable oxazoline group-containing monomer alone or with another monomer. Addition polymerizable oxazoline group-containing monomers include 2-vinyl-2-oxazoline, 2-vinyl-4-methyl-2-oxazoline, 2-vinyl-5-methyl-2-oxazoline, 2-isopropenyl-2-oxazoline, 2-isopropenyl-4-methyl-2-oxazoline, 2-isopropenyl-5-ethyl-2-oxazoline, and the like can be mentioned, and one or a mixture of two or more thereof can be used. Among these, 2-isopropenyl-2-oxazoline is preferred because it is easily available industrially. The other monomer is not limited as long as it is a monomer copolymerizable with an addition polymerizable oxazoline group-containing monomer. For example, alkyl (meth) acrylate (the alkyl group includes a methyl group, an ethyl group, an n-propyl group, an isopropyl group, (meth) acrylic acid esters such as n-butyl group, isobutyl group, t-butyl group, 2-ethylhexyl group, cyclohexyl group); acrylic acid, methacrylic acid, itaconic acid, maleic acid, fumaric acid, crotonic acid, styrene Unsaturated carboxylic acids such as sulfonic acid and its salts (sodium salt, potassium salt, ammonium salt, tertiary amine salt, etc.); Unsaturated nitriles such as acrylonitrile, methacrylonitrile; (meth) acrylamide, N-alkyl ( (Meth) acrylamide, N, N-dialkyl (meth) acrylamide, As the alkyl group, unsaturated amides such as methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, t-butyl group, 2-ethylhexyl group and cyclohexyl group); vinyl acetate Vinyl esters such as vinyl propionate; vinyl ethers such as methyl vinyl ether and ethyl vinyl ether; α-olefins such as ethylene and propylene; halogen-containing α, β-unsaturated monomers such as vinyl chloride, vinylidene chloride and vinyl fluoride And α, β-unsaturated aromatic monomers such as styrene and α-methylstyrene, and the like, and one or more of these monomers can be used.
メラミン化合物とは、化合物中にメラミン骨格を有する化合物のことである。例えば、アルキロール化メラミン誘導体、アルキロール化メラミン誘導体にアルコールを反応させて部分的あるいは完全にエーテル化した化合物、およびこれらの混合物を用いることができる。エーテル化に用いるアルコールとしては、メチルアルコール、エチルアルコール、イソプロピルアルコール、n−ブタノール、イソブタノール等が好適に用いられる。また、メラミン化合物としては、単量体、あるいは2量体以上の多量体のいずれであってもよく、あるいはこれらの混合物を用いてもよい。さらに、メラミンの一部に尿素等を共縮合したものも使用できるし、メラミン化合物の反応性を上げるために触媒を使用することも可能である。 A melamine compound is a compound having a melamine skeleton in the compound. For example, an alkylolated melamine derivative, a compound partially or completely etherified by reacting an alcohol with an alkylolated melamine derivative, and a mixture thereof can be used. As alcohol used for etherification, methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butanol, isobutanol and the like are preferably used. Moreover, as a melamine compound, either a monomer or a multimer more than a dimer may be sufficient, or a mixture thereof may be used. Further, a product obtained by co-condensing urea or the like with a part of melamine can be used, and a catalyst can be used to increase the reactivity of the melamine compound.
エポキシ化合物としては、例えば、分子内にエポキシ基を含む化合物、そのプレポリマーおよび硬化物が挙げられる。例えば、エピクロロヒドリンとエチレングリコール、ポリエチレングリコール、グリセリン、ポリグリセリン、ビスフェノールA等の水酸基やアミノ基との縮合物が挙げられ、ポリエポキシ化合物、ジエポキシ化合物、モノエポキシ化合物、グリシジルアミン化合物等がある。ポリエポキシ化合物としては、例えば、ソルビトール、ポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、トリグリシジルトリス(2−ヒドロキシエチル)イソシアネート、グリセロールポリグリシジルエーテル、トリメチロールプロパンポリグリシジルエーテル、ジエポキシ化合物としては、例えば、ネオペンチルグリコールジグリシジルエーテル、1,6−ヘキサンジオールジグリシジルエーテル、レゾルシンジグリシジルエーテル、エチレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、プロピレングリコールジグリシジルエーテル、ポリプロピレングリコールジグリシジルエーテル、ポリテトラメチレングリコールジグリシジルエーテル、モノエポキシ化合物としては、例えば、アリルグリシジルエーテル、2−エチルヘキシルグリシジルエーテル、フェニルグリシジルエーテル、グリシジルアミン化合物としてはN,N,N’,N’,−テトラグリシジル−m−キシリレンジアミン、1,3−ビス(N,N−ジグリシジルアミノ)シクロヘキサン等が挙げられる。 As an epoxy compound, the compound containing an epoxy group in a molecule | numerator, its prepolymer, and hardened | cured material are mentioned, for example. Examples include condensates of epichlorohydrin with hydroxyl groups and amino groups such as ethylene glycol, polyethylene glycol, glycerin, polyglycerin, and bisphenol A, and polyepoxy compounds, diepoxy compounds, monoepoxy compounds, glycidylamine compounds, and the like. is there. Examples of the polyepoxy compound include sorbitol, polyglycidyl ether, polyglycerol polyglycidyl ether, pentaerythritol polyglycidyl ether, diglycerol polyglycidyl ether, triglycidyl tris (2-hydroxyethyl) isocyanate, glycerol polyglycidyl ether, trimethylol. Examples of the propane polyglycidyl ether and diepoxy compound include neopentyl glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, resorcin diglycidyl ether, ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, propylene glycol diglycidyl ether. Ether, polypropylene glycol diglycidyl ether, Ritetramethylene glycol diglycidyl ether and monoepoxy compounds include, for example, allyl glycidyl ether, 2-ethylhexyl glycidyl ether, phenyl glycidyl ether, and glycidyl amine compounds such as N, N, N ′, N ′,-tetraglycidyl-m. -Xylylenediamine, 1,3-bis (N, N-diglycidylamino) cyclohexane and the like.
これらの架橋剤は、単独で用いてもよいし、複数種を混合して用いてもよい。さらにインラインコーティングへの適用等を配慮した場合、水溶性または水分散性を有することが好ましい。 These cross-linking agents may be used alone or in combination of two or more. Furthermore, when consideration is given to application to in-line coating, it is preferable to have water solubility or water dispersibility.
また、本発明は、塗布層中に、塗布層の固着性、滑り性改良を目的として粒子を含有するものであるが、その平均粒子径はフィルムの透明性の観点から0.15μm以下の範囲であり、好ましくは0.12μm以下の範囲である。また、固着性および滑り性の観点から、平均粒子径は好ましくは0.03μm以上の範囲、より好ましくは0.05μm以上の範囲である。粒子としては、具体例としてはシリカ、アルミナ、カオリン、炭酸カルシウム、酸化チタン、有機粒子等が挙げられる。 In the present invention, the coating layer contains particles for the purpose of improving adhesion and slipperiness of the coating layer, and the average particle diameter is in the range of 0.15 μm or less from the viewpoint of the transparency of the film. Preferably, it is the range of 0.12 μm or less. Further, from the viewpoints of adhesion and slipperiness, the average particle size is preferably in the range of 0.03 μm or more, more preferably in the range of 0.05 μm or more. Specific examples of the particles include silica, alumina, kaolin, calcium carbonate, titanium oxide, and organic particles.
さらに本発明の主旨を損なわない範囲において、塗布層には必要に応じて消泡剤、塗布性改良剤、増粘剤、有機系潤滑剤、帯電防止剤、紫外線吸収剤、酸化防止剤、発泡剤、染料、顔料等が含有されてもよい。 Furthermore, as long as it does not impair the gist of the present invention, the coating layer has an antifoaming agent, a coating property improving agent, a thickener, an organic lubricant, an antistatic agent, an ultraviolet absorber, an antioxidant, foaming as necessary. Agents, dyes, pigments and the like may be contained.
本発明における積層ポリエステルフィルムを構成する塗布層に用いられる縮合多環式芳香族を有する化合物は、その化合物中で縮合多環式芳香族の占める割合は、好ましくは5〜80重量%の範囲であり、より好ましくは10〜60重量%の範囲である。また、塗布層全体に占める縮合多環式芳香族を有する化合物の割合は、通常10〜99重量%の範囲、好ましくは40〜95重量%の範囲、より好ましくは50〜92重量%の範囲である。これらの範囲より外れる場合は、ハードコート層等の表面機能層を形成後の干渉ムラにより視認性が悪くなる場合がある。なお、縮合多環式芳香族の割合は、例えば、適当な溶剤または温水で塗布層を溶解抽出し、クロマトグラフィーで分取し、NMRやIRで構造を解析、さらに熱分解GC−MS(ガスクロマトグラフィー質量分析)等で解析することにより求めることができる。 In the compound having a condensed polycyclic aromatic used in the coating layer constituting the laminated polyester film in the present invention, the proportion of the condensed polycyclic aromatic in the compound is preferably in the range of 5 to 80% by weight. Yes, more preferably in the range of 10 to 60% by weight. The proportion of the compound having a condensed polycyclic aromatic in the entire coating layer is usually in the range of 10 to 99% by weight, preferably in the range of 40 to 95% by weight, more preferably in the range of 50 to 92% by weight. is there. If it falls outside these ranges, the visibility may deteriorate due to interference unevenness after the surface functional layer such as a hard coat layer is formed. The ratio of the condensed polycyclic aromatic can be determined by, for example, dissolving and extracting the coating layer with an appropriate solvent or warm water, separating by chromatography, analyzing the structure by NMR or IR, and further pyrolyzing GC-MS (gas It can be determined by analyzing with chromatography mass spectrometry.
本発明における積層ポリエステルフィルムを構成する塗布層中のイソシアネート系化合物の割合は、通常1〜80重量%の範囲、好ましくは3〜50重量%の範囲、より好ましくは5〜30重量%の範囲である。これらの範囲より外れる場合は、ハードコート層等の表面機能層との密着性が低下する可能性が懸念される場合や、塗布面状が悪化する場合がある。 The ratio of the isocyanate compound in the coating layer constituting the laminated polyester film in the present invention is usually in the range of 1 to 80% by weight, preferably in the range of 3 to 50% by weight, more preferably in the range of 5 to 30% by weight. is there. When it is out of these ranges, there is a possibility that the adhesion with the surface functional layer such as the hard coat layer may be lowered, or the coated surface state may be deteriorated.
本発明における積層ポリエステルフィルムを構成する塗布層中の平均粒子径0.15μm以下の粒子の割合は、通常1〜30重量%の範囲、より好ましくは1〜15重量%の範囲、さらに好ましくは3〜10重量%の範囲である。これらの範囲より外れる場合は、塗布層の透明性の低下や密着性の低下が懸念される。 The proportion of particles having an average particle size of 0.15 μm or less in the coating layer constituting the laminated polyester film in the present invention is usually in the range of 1 to 30% by weight, more preferably in the range of 1 to 15% by weight, and further preferably 3 It is in the range of -10% by weight. When it is outside these ranges, there is a concern that the transparency and adhesion of the coating layer may be lowered.
本発明のポリエステルフィルムにおいて、上述した塗布層を設けた面と反対側の面にも塗布層を設けることも可能である。例えば、ハードコート層等の表面機能層を形成する反対側にマイクロレンズ層、プリズム層、スティッキング防止層、光拡散層、ハードコート等の機能層を形成する場合に、当該機能層との密着性を向上させることが可能である。反対側の面に形成する塗布層の成分としては、従来公知のものを使用することができる。例えば、ポリエステル樹脂、アクリル樹脂、ウレタン樹脂等のバインダーポリマー、イソシアネート系化合物、オキサゾリン化合物、メラミン化合物、エポキシ化合物等の架橋剤等が挙げられ、これらの材料を単独で用いてもよいし、複数種を併用して用いてもよい。また、上述してきたような縮合多環式芳香族を有する化合物とイソシアネート系化合物を含有する塗布層(ポリエステルフィルムに両面同一の塗布層)であってもよい。 In the polyester film of the present invention, a coating layer can also be provided on the surface opposite to the surface on which the coating layer is provided. For example, when a functional layer such as a microlens layer, a prism layer, a sticking prevention layer, a light diffusion layer, or a hard coat is formed on the opposite side of the surface functional layer such as a hard coat layer, the adhesion to the functional layer It is possible to improve. A conventionally well-known thing can be used as a component of the coating layer formed in the surface on the opposite side. Examples thereof include binder polymers such as polyester resins, acrylic resins and urethane resins, cross-linking agents such as isocyanate compounds, oxazoline compounds, melamine compounds and epoxy compounds. These materials may be used alone or in combination. May be used in combination. Further, it may be a coating layer (coating layer having the same surface on both sides of a polyester film) containing a compound having a condensed polycyclic aromatic and an isocyanate compound as described above.
塗布層中の成分の分析は、例えば、TOF−SIMS等の表面分析によって行うことができる。 Analysis of the components in the coating layer can be performed by surface analysis such as TOF-SIMS.
インラインコーティングによって塗布層を設ける場合は、上述の一連の化合物を水溶液または水分散体として、固形分濃度が0.1〜50重量%程度を目安に調整した塗布液をポリエステルフィルム上に塗布する要領にて積層ポリエステルフィルムを製造するのが好ましい。また、本発明の主旨を損なわない範囲において、水への分散性改良、造膜性改良等を目的として、塗布液中には少量の有機溶剤を含有していてもよい。有機溶剤は1種類のみでもよく、適宜、2種類以上を使用してもよい。 When providing a coating layer by in-line coating, the above-mentioned series of compounds is applied as an aqueous solution or dispersion, and the coating solution adjusted to a solid content concentration of about 0.1 to 50% by weight as a guide is applied onto the polyester film. It is preferable to produce a laminated polyester film. Moreover, in the range which does not impair the main point of this invention, a small amount of organic solvents may be contained in the coating liquid for the purpose of improving dispersibility in water, improving film-forming properties, and the like. Only one type of organic solvent may be used, or two or more types may be used as appropriate.
本発明における積層ポリエステルフィルムに関して、ポリエステルフィルム上に設けられる塗布層の膜厚は、通常0.04〜0.20μm、好ましくは0.07〜0.15μmの範囲である。膜厚が上記範囲より外れる場合は、表面機能層を積層後の干渉ムラにより、視認性が悪化する場合がある。 Regarding the laminated polyester film in the present invention, the thickness of the coating layer provided on the polyester film is usually in the range of 0.04 to 0.20 μm, preferably 0.07 to 0.15 μm. When the film thickness is out of the above range, visibility may deteriorate due to interference unevenness after the surface functional layer is laminated.
本発明において、塗布層を設ける方法はリバースグラビアコート、ダイレクトグラビアコート、ロールコート、ダイコート、バーコート、カーテンコート等、従来公知の塗工方式を用いることができる。 In the present invention, as a method for providing the coating layer, a conventionally known coating method such as reverse gravure coating, direct gravure coating, roll coating, die coating, bar coating, curtain coating or the like can be used.
本発明において、ポリエステルフィルム上に塗布層を形成する際の乾燥および硬化条件に関しては特に限定されるわけではなく、例えば、オフラインコーティングにより塗布層を設ける場合、通常、80〜200℃で3〜40秒間、好ましくは100〜180℃で3〜40秒間を目安として熱処理を行うのが良い。 In the present invention, the drying and curing conditions for forming the coating layer on the polyester film are not particularly limited. For example, when the coating layer is provided by off-line coating, it is usually 3 to 40 at 80 to 200 ° C. The heat treatment may be performed for 2 seconds, preferably 100 to 180 ° C. for 3 to 40 seconds.
一方、インラインコーティングにより塗布層を設ける場合、通常、70〜280℃で3〜200秒間を目安として熱処理を行うのが良い。 On the other hand, when the coating layer is provided by in-line coating, heat treatment is usually performed at 70 to 280 ° C. for 3 to 200 seconds as a guide.
また、オフラインコーティングあるいはインラインコーティングに係わらず、必要に応じて熱処理と紫外線照射等の活性エネルギー線照射とを併用してもよい。本発明における積層ポリエステルフィルムを構成するポリエステルフィルムにはあらかじめ、コロナ処理、プラズマ処理等の表面処理を施してもよい。 Further, irrespective of off-line coating or in-line coating, heat treatment and active energy ray irradiation such as ultraviolet irradiation may be used in combination as required. The polyester film constituting the laminated polyester film in the present invention may be subjected to surface treatment such as corona treatment or plasma treatment in advance.
本発明における塗布層は干渉ムラの発生を抑制するために、屈折率の調整がされたものであり、その屈折率は基材のポリエステルフィルムとハードコート層等の表面機能層の相乗平均付近に設計したものである。塗布層の屈折率と塗布層の反射率は密接な関係がある。本発明の絶対反射率は、横軸に波長、縦軸に反射率を示すグラフを描き、反射率の極小値が波長400〜800nmの範囲に1つである必要があり、その極小値は4.0%以上である。本発明の絶対反射率の範囲においては、その極小値が同じ波長に現れるならば、極小値の反射率は、屈折率が高い場合は高い値となり、屈折率が低い場合は低い値となる。 The coating layer in the present invention has a refractive index adjusted to suppress the occurrence of interference unevenness, and the refractive index is in the vicinity of the geometric mean of the surface functional layer such as the base material polyester film and the hard coat layer. Designed. The refractive index of the coating layer and the reflectance of the coating layer are closely related. For the absolute reflectance of the present invention, a graph showing the wavelength on the horizontal axis and the reflectance on the vertical axis is drawn, and the minimum value of the reflectance needs to be one in the wavelength range of 400 to 800 nm, and the minimum value is 4 0.0% or more. In the range of the absolute reflectance of the present invention, if the minimum value appears at the same wavelength, the reflectance of the minimum value is a high value when the refractive index is high, and a low value when the refractive index is low.
本発明における絶対反射率は、波長400〜800nmの範囲に極小値が1つ存在、より好ましくは波長500〜700nmの範囲に極小値が1つ存在するものである。また、その極小値の値が、好ましくは4.0〜6.5%、より好ましくは4.5〜6.2%の範囲である。波長400〜800nmの範囲にある極小値が1つではない場合、また、極小値の絶対反射率が上記の値を外れる場合は、ハードコート層等の表面機能層を形成後に干渉ムラが発生し、フィルムの視認性が低下する場合がある。
本発明において、上記範囲の絶対反射率は、例えば、用いる縮合多環式芳香族を有する化合物の種類や量、用いるイソシアネート系化合物の種類や量等を適宜選択することによって、得ることができる。
The absolute reflectance in the present invention has one minimum value in the wavelength range of 400 to 800 nm, more preferably one minimum value in the wavelength range of 500 to 700 nm. The minimum value is preferably in the range of 4.0 to 6.5%, more preferably 4.5 to 6.2%. If the minimum value in the wavelength range of 400 to 800 nm is not one, and if the absolute reflectance of the minimum value deviates from the above value, interference unevenness occurs after the surface functional layer such as a hard coat layer is formed. The visibility of the film may be reduced.
In the present invention, the absolute reflectance in the above range can be obtained, for example, by appropriately selecting the type and amount of the compound having a condensed polycyclic aromatic to be used, the type and amount of the isocyanate compound to be used, and the like.
本発明においては、ディスプレイ用等、透明性が要求される用途に使用する場合のために、透明性が高いフィルムがより好まれる。例えば、透明性の1つの指標としてヘーズが挙げられ、その値は、好ましくは1.5%以下の範囲、より好ましくは1.2%以下の範囲、さらに好ましくは1.0%以下の範囲である。ヘーズが高い場合は、フィルムの視認性が低下する場合がある。 In the present invention, a film having high transparency is more preferred for use in applications where transparency is required, such as for displays. For example, haze is mentioned as one index of transparency, and the value is preferably in the range of 1.5% or less, more preferably in the range of 1.2% or less, and further preferably in the range of 1.0% or less. is there. When the haze is high, the visibility of the film may be lowered.
本発明のポリエステルフィルムには、塗布層の上にハードコート層等の表面機能層を設けるのが一般的である。ハードコート層に使用される材料としては、特に限定されないが、例えば、単官能(メタ)アクリレート、多官能(メタ)アクリレート、テトラエトキシシラン等の反応性珪素化合物等の硬化物が挙げられる。これらのうち生産性及び硬度の両立の観点より、紫外線硬化性の多官能(メタ)アクリレートを含む組成物の重合硬化物であることが特に好ましい。 The polyester film of the present invention is generally provided with a surface functional layer such as a hard coat layer on the coating layer. Although it does not specifically limit as a material used for a hard-coat layer, For example, hardened | cured materials, such as reactive silicon compounds, such as monofunctional (meth) acrylate, polyfunctional (meth) acrylate, and tetraethoxysilane, are mentioned. Among these, from the viewpoint of achieving both productivity and hardness, a polymerization cured product of a composition containing an ultraviolet curable polyfunctional (meth) acrylate is particularly preferable.
紫外線硬化性の多官能(メタ)アクリレートを含む組成物としては特に限定されるものでない。例えば、公知の紫外線硬化性の多官能(メタ)アクリレートを一種類以上混合したもの、紫外線硬化性ハードコート材として市販されているもの、或いはこれら以外に本実施形態の目的を損なわない範囲において、その他の成分を更に添加したものを用いることができる。 It does not specifically limit as a composition containing a ultraviolet curable polyfunctional (meth) acrylate. For example, a mixture of one or more known ultraviolet curable polyfunctional (meth) acrylates, those commercially available as ultraviolet curable hard coat materials, or the range that does not impair the purpose of this embodiment other than these, What added the other component further can be used.
紫外線硬化性の多官能(メタ)アクリレートとしては、特に限定されるものではないが、例えばジペンタエリスリトールヘキサ(メタ)アクリレート、テトラメチロールメタンテトラ(メタ)アクリレート、テトラメチロールメタントリ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ) アクリレート、1,6−ビス(3−アクリロイルオキシ−2−ヒドロキシプロピルオキシ)ヘキサン等の多官能アルコールの(メタ)アクリル誘導体や、ポリエチレングリコールジ(メタ)アクリレート、そしてポリウレタン(メタ)アクリレート等が挙げられる。 The UV-curable polyfunctional (meth) acrylate is not particularly limited. For example, dipentaerythritol hexa (meth) acrylate, tetramethylolmethanetetra (meth) acrylate, tetramethylolmethanetri (meth) acrylate, (Meth) acryl derivatives of polyfunctional alcohols such as trimethylolpropane tri (meth) acrylate, 1,6-hexanediol di (meth) acrylate, 1,6-bis (3-acryloyloxy-2-hydroxypropyloxy) hexane And polyethylene glycol di (meth) acrylate and polyurethane (meth) acrylate.
紫外線硬化性の多官能(メタ)アクリレートを含む組成物に含まれるその他の成分は特に限定されるものではない。例えば、無機又は有機の微粒子、重合開始剤、重合禁止剤、酸化防止剤、帯電防止剤、分散剤、界面活性剤、光安定剤及びレベリング剤等が挙げられる。また、ウェットコーティング法において成膜後乾燥させる場合には、任意の量の溶媒を添加することができる。 Other components contained in the composition containing an ultraviolet curable polyfunctional (meth) acrylate are not particularly limited. Examples thereof include inorganic or organic fine particles, polymerization initiators, polymerization inhibitors, antioxidants, antistatic agents, dispersants, surfactants, light stabilizers, and leveling agents. In addition, when the film is dried after film formation in the wet coating method, an arbitrary amount of solvent can be added.
ハードコート層の形成方法は、有機材料を用いた場合にはロールコート法、ダイコート法等の一般的なウェットコート法が採用される。形成されたハードコート層には必要に応じて加熱や紫外線、電子線等の活性エネルギー線照射を施し、硬化反応を行うことができる。 As a method for forming the hard coat layer, when an organic material is used, a general wet coat method such as a roll coat method or a die coat method is employed. The formed hard coat layer can be subjected to a curing reaction by heating, irradiation with active energy rays such as ultraviolet rays and electron beams as necessary.
以下、本発明を実施例によりさらに詳細に説明するが、本発明はその要旨を越えない限り、以下の実施例に限定されるものではない。また、本発明で用いた測定法および評価方法は次のとおりである。 EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited to a following example, unless the summary is exceeded. The measurement method and evaluation method used in the present invention are as follows.
(1)ポリエステルの固有粘度の測定方法
ポリエステルに非相溶な他のポリマー成分および顔料を除去したポリエステル1gを精秤し、フェノール/テトラクロロエタン=50/50(重量比)の混合溶媒100mlを加えて溶解させ、30℃で測定した。
(1) Measuring method of intrinsic viscosity of polyester 1 g of polyester from which other polymer components and pigments incompatible with polyester have been removed are precisely weighed, and 100 ml of a mixed solvent of phenol / tetrachloroethane = 50/50 (weight ratio) is added. And dissolved at 30 ° C.
(2)平均粒子径の測定方法
電子顕微鏡(HITACHI製S−4500)を使用して塗布層の表面を観察し、粒子10個の粒子径の平均値を平均粒子径とした。
(2) Measuring method of average particle diameter The surface of the coating layer was observed using an electron microscope (S-4500 manufactured by HITACHI), and the average value of the particle diameters of 10 particles was defined as the average particle diameter.
(3)塗布層の膜厚測定方法
塗布層の表面をRuO4で染色し、エポキシ樹脂中に包埋した。その後、超薄切片法により作成した切片をRuO4で染色し、塗布層断面をTEM(Hitachi製 H−7650、加速電圧100V)を用いて測定した。
(3) Method for measuring film thickness of coating layer The surface of the coating layer was dyed with RuO 4 and embedded in an epoxy resin. Thereafter, the section prepared by ultramicrotomy stained with RuO 4, a coating layer cross-section was measured by using a TEM (Hitachi Ltd. H-7650, accelerating voltage 100 V).
(4)ポリエステルフィルムにおける塗布層表面からの絶対反射率の評価方法
あらかじめ、ポリエステルフィルムの測定裏面に黒テープ(ニチバン株式会社製ビニールテープVT―50)を貼り、分光光度計(日本分光株式会社製 紫外可視分光光度計 V−570 および自動絶対反射率測定装置 AM−500N)を使用して同期モード、入射角5°、N偏光、レスポンス Fast、データ取区間隔1.0nm、バンド幅10nm、走査速度1000m/minで塗布層面を波長範囲300〜800nmの絶対反射率を測定し、その極小値における波長(ボトム波長)と反射率を評価した。
(4) Evaluation method of absolute reflectance from coating layer surface in polyester film A black tape (vinyl tape VT-50 manufactured by Nichiban Co., Ltd.) was previously applied to the measurement back surface of the polyester film, and a spectrophotometer (manufactured by JASCO Corporation). UV-visible spectrophotometer V-570 and automatic absolute reflectance measuring device AM-500N), synchronous mode, incident angle 5 °, N-polarization, response fast, data collection interval 1.0 nm, bandwidth 10 nm, scanning The absolute reflectance of the coating layer surface in the wavelength range of 300 to 800 nm was measured at a speed of 1000 m / min, and the wavelength (bottom wavelength) and reflectance at the minimum value were evaluated.
(5)ヘーズの測定方法
村上色彩技術研究所製ヘーズメーターHM−150を使用して、JIS K 7136で測定した。
(5) Measuring method of haze It measured by JISK7136 using Murakami Color Research Laboratory make haze meter HM-150.
(6)干渉ムラの評価方法
ポリエステルフィルムの塗布層側に、ジペンタエリスリトールヘキサアクリレート72重量部、2−ヒドロキシ−3−フェノキシプロピルアクリレート18重量部、五酸化アンチモン10重量部、光重合開始剤(商品名:イルガキュア184、チバスペシャルティケミカル製)1重量部、メチルエチルケトン200重量部の混合塗液を乾燥膜厚が5μmになるように塗布し、紫外線を照射して硬化させハードコート層を形成した。得られたフィルムを3波長光域型蛍光灯下で目視にて、干渉ムラを観察し、干渉ムラが確認できないものを◎、薄くまばらな干渉ムラが確認されるものを○、薄いが線状の干渉ムラが確認できるものを△、明瞭な干渉ムラが確認されるものを×とした。
(6) Interference unevenness evaluation method On the polyester film coating layer side, 72 parts by weight of dipentaerythritol hexaacrylate, 18 parts by weight of 2-hydroxy-3-phenoxypropyl acrylate, 10 parts by weight of antimony pentoxide, a photopolymerization initiator ( (Product name: Irgacure 184, manufactured by Ciba Specialty Chemical) 1 part by weight and 200 parts by weight of methyl ethyl ketone were applied so that the dry film thickness was 5 μm and cured by irradiating with ultraviolet rays to form a hard coat layer. The obtained film is visually observed under a three-wavelength fluorescent lamp, and interference unevenness is observed. If the interference unevenness is not confirmed, ◎, thin sparse interference unevenness is confirmed, thin, linear The case where the interference unevenness was confirmed was indicated by Δ, and the case where clear interference unevenness was confirmed was indicated by ×.
(7)密着性の評価方法
より厳しい密着性の評価を行うために、上記(5)の評価で使用したハードコート液から五酸化アンチモンを除いた材料で検討した。すなわち、ジペンタエリスリトールヘキサアクリレート80重量部、2−ヒドロキシ−3−フェノキシプロピルアクリレート20重量部、光重合開始剤(商品名:イルガキュア184、チバスペシャルティケミカル製)5重量部、メチルエチルケトン200重量部の混合塗液を乾燥膜厚が5μmになるように塗布し、紫外線を照射して硬化させハードコート層を形成した。得られたフィルムに対して、初期(密着性1)、および80℃、85%RHの環境下で50時間後(密着性2)、10×10のクロスカットをして、その上に18mm幅のテープ(ニチバン株式会社製セロテープ(登録商標)CT−18)を貼り付け、180度の剥離角度で急激にはがした後の剥離面を観察し、剥離面積が5%未満ならば◎、5%以上20%未満なら○、20%以上50%未満なら△、50%以上ならば×とした。
(7) Adhesive evaluation method In order to evaluate the tighter adhesiveness, it examined by the material remove | excluding antimony pentoxide from the hard-coat liquid used by the evaluation of said (5). That is, 80 parts by weight of dipentaerythritol hexaacrylate, 20 parts by weight of 2-hydroxy-3-phenoxypropyl acrylate, 5 parts by weight of a photopolymerization initiator (trade name: Irgacure 184, manufactured by Ciba Specialty Chemical), and 200 parts by weight of methyl ethyl ketone The coating liquid was applied so as to have a dry film thickness of 5 μm and cured by irradiating with ultraviolet rays to form a hard coat layer. The obtained film was initially (adhesiveness 1), and after 50 hours (adhesiveness 2) in an environment of 80 ° C. and 85% RH (adhesiveness 2), 10 × 10 cross-cut, and 18 mm wide on it. (A Nichiban Co., Ltd. cello tape (registered trademark) CT-18) was applied and the peeled surface was observed after abrupt peeling at a 180 degree peel angle. % If less than 20% and less than 20%, Δ if more than 20% and less than 50%, and x if more than 50%.
(8)滑り性の評価方法
第1塗布層面上を爪でこすったとき、引っかかり感がなく、滑り感がある場合を○、引っかかり感がなく、滑り感がない場合を△、引っかかり感がある場合を×とした。
(8) Evaluation method of slipperiness When the surface of the first coating layer is rubbed with a nail, there is no catching feeling and there is a slipping feeling, ○, there is no catching feeling and there is no slipping feeling, and there is a catching feeling. The case was marked with x.
実施例および比較例において使用したポリエステルは、以下のようにして準備したものである。
<ポリエステル(A)の製造方法>
テレフタル酸ジメチル100重量部とエチレングリコール60重量部とを出発原料とし、触媒として酢酸マグネシウム・四水塩0.09重量部を反応器にとり、反応開始温度を150℃とし、メタノールの留去とともに徐々に反応温度を上昇させ、3時間後に230℃とした。4時間後、実質的にエステル交換反応を終了させた。この反応混合物にエチルアシッドフォスフェート0.04重量部を添加した後、三酸化アンチモン0.04重量部を加えて、4時間重縮合反応を行った。すなわち、温度を230℃から徐々に昇温し280℃とした。一方、圧力は常圧より徐々に減じ、最終的には0.3mmHgとした。反応開始後、反応槽の攪拌動力の変化により、極限粘度0.63に相当する時点で反応を停止し、窒素加圧下ポリマーを吐出させた。得られたポリエステル(A)の極限粘度は0.63であった。
The polyester used in the examples and comparative examples was prepared as follows.
<Method for producing polyester (A)>
Using 100 parts by weight of dimethyl terephthalate and 60 parts by weight of ethylene glycol as starting materials, 0.09 parts by weight of magnesium acetate tetrahydrate as a catalyst is placed in the reactor, the reaction start temperature is set to 150 ° C., and the methanol is distilled off gradually. The reaction temperature was raised to 230 ° C. after 3 hours. After 4 hours, the transesterification reaction was substantially terminated. After adding 0.04 part by weight of ethyl acid phosphate to this reaction mixture, 0.04 part by weight of antimony trioxide was added, and a polycondensation reaction was carried out for 4 hours. That is, the temperature was gradually raised from 230 ° C. to 280 ° C. On the other hand, the pressure was gradually reduced from normal pressure, and finally 0.3 mmHg. After the start of the reaction, the reaction was stopped at a time corresponding to an intrinsic viscosity of 0.63 due to a change in stirring power of the reaction tank, and the polymer was discharged under nitrogen pressure. The intrinsic viscosity of the obtained polyester (A) was 0.63.
<ポリエステル(B)の製造方法>
ポリエステル(A)の製造方法において、エチルアシッドフォスフェート0.04重量部を添加後、平均粒子径1.6μmのエチレングリコールに分散させたシリカ粒子を0.2重量部、三酸化アンチモン0.04重量部を加えて、極限粘度0.65に相当する時点で重縮合反応を停止した以外は、ポリエステル(A)の製造方法と同様の方法を用いてポリエステル(B)を得た。得られたポリエステル(B)は、極限粘度0.65であった。
<Method for producing polyester (B)>
In the method for producing polyester (A), after adding 0.04 part by weight of ethyl acid phosphate, 0.2 part by weight of silica particles dispersed in ethylene glycol having an average particle diameter of 1.6 μm and 0.04 part of antimony trioxide are added. A polyester (B) was obtained using the same method as the production method of the polyester (A) except that the polycondensation reaction was stopped at a time corresponding to the intrinsic viscosity of 0.65 by adding parts by weight. The obtained polyester (B) had an intrinsic viscosity of 0.65.
塗布層を構成する化合物例は以下のとおりである。
(化合物例)
・縮合多環式芳香族を有する化合物:(I)
下記組成で共重合したポリエステル樹脂の水分散体
モノマー組成:(酸成分)2,6−ナフタレンジカルボン酸/5−ソジウムスルホイソフタル酸//(ジオール成分)エチレングリコール/ジエチレングリコール=92/8//80/20(mol%)
Examples of compounds constituting the coating layer are as follows.
(Example compounds)
・ Compounds having condensed polycyclic aromatics: (I)
Water dispersion of polyester resin copolymerized with the following composition: Monomer composition: (acid component) 2,6-naphthalenedicarboxylic acid / 5-sodium sulfoisophthalic acid // (diol component) ethylene glycol / diethylene glycol = 92/8 // 80/20 (mol%)
・ポリエステル樹脂:(II)
下記組成で共重合したポリエステル樹脂の水分散体
モノマー組成:(酸成分)テレフタル酸/イソフタル酸/5−ソジウムスルホイソフタル酸//(ジオール成分)エチレングリコール/1,4−ブタンジオール/ジエチレングリコール=56/40/4//70/20/10(mol%)
・ Polyester resin: (II)
Water dispersion of polyester resin copolymerized with the following composition: Monomer composition: (acid component) terephthalic acid / isophthalic acid / 5-sodium sulfoisophthalic acid // (diol component) ethylene glycol / 1,4-butanediol / diethylene glycol = 56/40/4 // 70/20/10 (mol%)
・ウレタン樹脂(III)
カルボン酸水分散型ポリエステルポリウレタン樹脂である、ハイドランAP−40(大日本インキ化学工業社製)
・ Urethane resin (III)
Hydran AP-40 (manufactured by Dainippon Ink & Chemicals, Inc.), a carboxylic acid water-dispersed polyester polyurethane resin
・イソシアネート系化合物:(IVA)
ビスフェノールAのエチレンオキサイド2モル付加物とマレイン酸とのポリエステル(分子量2000)200重量部に、ヘキサメチレンジイソシアネート33.6重量部を添加し、100℃で2時間反応を行った。次いで系の温度を一旦50℃まで下げ、30%重亜硫酸ナトリウム水溶液73重量部を添加し、45℃で60分間攪拌を行った後、水718重量部で希釈したブロックイソシアネート系化合物。
・イソシアネート系化合物:(IVB)
ヘキサメチレンジイソシアネートトリマー158重量部、メトキシポリエチレングリコール(OH価=81mgKOH/g)26重量部、ジエチルジエチレングリコール27.8重量部、ジオクチルチンラウレート0.001重量部を85℃で反応させた。その後、放冷し、メチルエチルケトンオキシム66重量部を滴下し、反応させた。引き続き、1,6−ヘキサメチレンジオール系ポリカーボネートジオール(OH価=56mgKOH/g)115重量部、トリメチロールプロパン(OH価=1254mgKOH/g)1.2重量部、ジメチロールプロピオン酸(OH価=837mgKOH/g)7.6重量部、ジメチルジプロピレングリコール50重量部を加え、攪拌後、イソホロンジイソシアネート40.3重量部を加え、反応させた。放冷後、ヘキサメチレンジイソシアネートトリマー8.2重量部を添加し、攪拌後、トリエチルアミン5.8重量部を添加し、攪拌した。この混合液に水450重量部を滴下し、15%のジエチレントリアミン水溶液21重量部を滴下・攪拌し得られたブロックイソシアネート系化合物。
・ Isocyanate compounds: (IVA)
33.6 parts by weight of hexamethylene diisocyanate was added to 200 parts by weight of a polyester (molecular weight 2000) of bisphenol A ethylene oxide 2 mol adduct and maleic acid, and reacted at 100 ° C. for 2 hours. Then, the temperature of the system was once lowered to 50 ° C., 73 parts by weight of a 30% aqueous sodium bisulfite solution was added, the mixture was stirred at 45 ° C. for 60 minutes, and then diluted with 718 parts by weight of water.
・ Isocyanate compounds: (IVB)
158 parts by weight of hexamethylene diisocyanate trimer, 26 parts by weight of methoxypolyethylene glycol (OH value = 81 mg KOH / g), 27.8 parts by weight of diethyl diethylene glycol and 0.001 part by weight of dioctyltin laurate were reacted at 85 ° C. Thereafter, the mixture was allowed to cool, and 66 parts by weight of methyl ethyl ketone oxime was added dropwise to react. Subsequently, 115 parts by weight of 1,6-hexamethylenediol-based polycarbonate diol (OH value = 56 mgKOH / g), 1.2 parts by weight of trimethylolpropane (OH value = 1254 mgKOH / g), dimethylolpropionic acid (OH value = 837 mgKOH) / G) 7.6 parts by weight and 50 parts by weight of dimethyldipropylene glycol were added, and after stirring, 40.3 parts by weight of isophorone diisocyanate was added and reacted. After allowing to cool, 8.2 parts by weight of hexamethylene diisocyanate trimer was added, and after stirring, 5.8 parts by weight of triethylamine was added and stirred. A block isocyanate compound obtained by dropping 450 parts by weight of water into this mixed solution and dropping and stirring 21 parts by weight of a 15% aqueous diethylenetriamine solution.
・ヘキサメトキシメチルメラミン(V) ・ Hexamethoxymethylmelamine (V)
・粒子:(VIA) 平均粒子径0.07μmのシリカゾル
・粒子:(VIB) 平均粒子径0.12μmのシリカゾル
・粒子:(VIC) 平均粒子径0.30μmのシリカゾル
・ Particles: (VIA) Silica sol with an average particle size of 0.07 μm ・ Particles: (VIB) Silica sol with an average particle size of 0.12 μm ・ Particles: (VIC) Silica sol with an average particle size of 0.30 μm
実施例1:
ポリエステル(A)、(B)をそれぞれ90%、10%の割合で混合した混合原料を最外層(表層)の原料とし、ポリエステル(A)を中間層の原料として、2台の押出機に各々を供給し、各々285℃で溶融した後、40℃に設定した冷却ロール上に、2種3層(表層/中間層/表層=1:18:1の吐出量)の層構成で共押出し冷却固化させて未延伸シートを得た。次いで、ロール周速差を利用してフィルム温度85℃で縦方向に3.4倍延伸した後、この縦延伸フィルムの両面に、下記表1に示す塗布液1を塗布し、テンターに導き、横方向に120℃で3.9倍延伸し、225℃で熱処理を行った後、横方向に2%弛緩し、膜厚(乾燥後)が0.10μmの塗布層を有する厚さ100μmのポリエステルフィルムを得た。
Example 1:
A mixed raw material in which polyesters (A) and (B) are mixed at a ratio of 90% and 10%, respectively, is used as a raw material for the outermost layer (surface layer), and polyester (A) is used as a raw material for the intermediate layer in each of two extruders. Are melted at 285 ° C. and then coextruded and cooled on a cooling roll set at 40 ° C. in a layer configuration of two types and three layers (surface layer / intermediate layer / surface layer = 1: 18: 1 discharge amount). Solidified to obtain an unstretched sheet. Next, the film was stretched 3.4 times in the longitudinal direction at a film temperature of 85 ° C. using the difference in peripheral speed of the roll, and then the coating liquid 1 shown in Table 1 below was applied to both sides of the longitudinally stretched film, and led to a tenter. Polyester with a thickness of 100 μm having a coating layer with a film thickness (after drying) of 0.10 μm after stretching 3.9 times at 120 ° C. in the transverse direction and heat treatment at 225 ° C. A film was obtained.
得られたポリエステルフィルムの絶対反射率を測定したところ、極小値は610nmで、その反射率は5.1%であった。ハードコート層を積層後のフィルムには干渉ムラは確認できず、また密着性も良好であり、ヘーズも低く透明性も良好であった。このフィルムの特性を下記表2に示す。 When the absolute reflectance of the obtained polyester film was measured, the minimum value was 610 nm, and the reflectance was 5.1%. Interference unevenness could not be confirmed in the film after laminating the hard coat layer, adhesion was good, haze was low, and transparency was good. The properties of this film are shown in Table 2 below.
実施例2〜14:
実施例1において、塗布剤組成を表1に示す塗布剤組成に変更する以外は実施例1と同様にして製造し、ポリエステルフィルムを得た。でき上がったポリエステルフィルムは表2に示すとおり、高い反射率を有し、干渉ムラレベルも良好で、密着性も良好なものであった。
Examples 2-14:
In Example 1, it manufactured similarly to Example 1 except having changed the coating agent composition into the coating agent composition shown in Table 1, and obtained the polyester film. As shown in Table 2, the finished polyester film had high reflectivity, good interference unevenness level, and good adhesion.
比較例1〜5:
実施例1において、塗布剤組成を表1に示す塗布剤組成に変更する以外は実施例1と同様にして製造し、ポリエステルフィルムを得た。でき上がった積層ポリエステルフィルムを評価したところ、表2に示すとおり、明瞭な干渉ムラが観察できる場合、密着性が良くない場合、ヘーズが高い場合や滑り性が悪い場合が見られた。
Comparative Examples 1-5:
In Example 1, it manufactured similarly to Example 1 except having changed the coating agent composition into the coating agent composition shown in Table 1, and obtained the polyester film. When the finished laminated polyester film was evaluated, as shown in Table 2, when clear interference unevenness could be observed, adhesion was not good, haze was high, or slipperiness was poor.
比較例6:
実施例1において、塗布層を設けない以外は実施例1と同様にして製造し、ポリエステルフィルムを得た。でき上がったフィルムを評価したところ、表2に示すとおり、密着性が悪いものであった。
Comparative Example 6:
In Example 1, it manufactured like Example 1 except not providing an application layer, and obtained the polyester film. When the completed film was evaluated, as shown in Table 2, the adhesion was poor.
本発明のフィルムは、例えば、液晶やプラズマディスプレイ等の部材である各種の光学用フィルム等において、ハードコート層等との密着性および視認性を重視する用途に好適に利用することができる。 The film of the present invention can be suitably used for, for example, various optical films that are members of liquid crystal, plasma displays, etc., for applications that place importance on adhesion and visibility with a hard coat layer or the like.
Claims (1)