JP2011099030A - Extrusion molded product made of aromatic polycarbonate resin composition - Google Patents

Extrusion molded product made of aromatic polycarbonate resin composition Download PDF

Info

Publication number
JP2011099030A
JP2011099030A JP2009254079A JP2009254079A JP2011099030A JP 2011099030 A JP2011099030 A JP 2011099030A JP 2009254079 A JP2009254079 A JP 2009254079A JP 2009254079 A JP2009254079 A JP 2009254079A JP 2011099030 A JP2011099030 A JP 2011099030A
Authority
JP
Japan
Prior art keywords
polycarbonate resin
component
group
tert
bis
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2009254079A
Other languages
Japanese (ja)
Inventor
Yuji Higaki
裕二 檜垣
Takashi Oda
隆司 小田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Teijin Ltd
Original Assignee
Teijin Chemicals Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Teijin Chemicals Ltd filed Critical Teijin Chemicals Ltd
Priority to JP2009254079A priority Critical patent/JP2011099030A/en
Priority to EP10828412.6A priority patent/EP2497800A4/en
Priority to KR1020127011509A priority patent/KR20120114220A/en
Priority to CN2010800501630A priority patent/CN102597111A/en
Priority to US13/505,794 priority patent/US20120217439A1/en
Priority to TW099138073A priority patent/TW201129605A/en
Priority to PCT/JP2010/070156 priority patent/WO2011055854A1/en
Publication of JP2011099030A publication Critical patent/JP2011099030A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide an extrusion molded product made of an aromatic polycarbonate resin composition having excellent transparency, appearance and flame retardancy. <P>SOLUTION: The extrusion molded product is made of the aromatic polycarbonate resin composition containing 0.005 to 5 pts.wt. flame retardant (B) (component B) based on 100 pts.wt. aromatic polycarbonate resin (A) (component A) having a branched structure having 0.70 to 1.50 mol% branched ratio. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

本発明は、芳香族ポリカーボネート樹脂組成物からなる押し出し成形品に関する。さらに詳しくは高い透明性を維持した上で難燃性及び外観に優れる芳香族ポリカーボネート樹脂組成物からなる押し出し成形品に関する。   The present invention relates to an extrusion molded article comprising an aromatic polycarbonate resin composition. More specifically, the present invention relates to an extrusion-molded article comprising an aromatic polycarbonate resin composition having excellent flame retardancy and appearance while maintaining high transparency.

芳香族ポリカーボネート樹脂は射出成形、押し出しシート成形などの簡便で生産性に優れた加工法により、幅広い産業分野で利用されている。とりわけ各種照明カバー、透過型ディスプレイ用の保護カバー等の高い透明性が要求される用途には、芳香族ポリカーボネート樹脂の高い光線透過率と極めて低いヘーズに代表される優れた透明性を生かして幅広く使用されている。また、これらの用途では近年アクリル樹脂のもらい火の問題もあり、火災時の難燃性についても注目されており、上記の特性に加えて高度な難燃性を有する樹脂組成物からなる押し出し成形品が求められている。   Aromatic polycarbonate resins are used in a wide range of industrial fields by simple and highly productive processing methods such as injection molding and extrusion sheet molding. Especially for applications that require high transparency, such as various lighting covers and protective covers for transmissive displays, make use of the high light transmittance of aromatic polycarbonate resin and the excellent transparency represented by extremely low haze. in use. In addition, in these applications, there is also a problem of stagnation of acrylic resin in recent years, and attention has been paid to flame retardancy at the time of fire. Extrusion molding consisting of a resin composition having high flame retardancy in addition to the above characteristics Goods are sought.

芳香族ポリカーボネート樹脂に難燃性を付与する方法としては、従来臭素系化合物やリン系化合物を添加した難燃性芳香族ポリカーボネート樹脂組成物が提案されており、難燃化の要望の強いＯＡ機器、家電製品などに利用されているが、一方でこれらの難燃剤に代わる難燃性芳香族ポリカーボネート樹脂組成物が開発され、上記に挙げた製品などに使用されつつある。かかる難燃剤変更の目的としては、成形時における腐蝕ガスの発生の抑制、または製品のリサイクル性の向上などが挙げられる。上記に挙げた難燃剤に代わる難燃剤としては例えばシリコーン化合物を挙げることができる。シリコーン化合物を芳香族ポリカーボネート樹脂に配合した難燃性樹脂組成物は近年精力的に検討され、種々の提案がされている。例えばポリカーボネート樹脂にパーフルオロアルキルスルホン酸アルカリ（土類）金属塩とアルコキシ基、ビニル基およびフェニル基を有する有機シロキサンを配合する方法（特許文献１参照）、およびポリカーボネート樹脂にパーフルオロアルキルスルホン酸のアルカリ金属塩またはアルカリ土類金属塩と２価炭化水素基を介してケイ素原子に結合したオルガノキシシリル基を含有するオルガノポリシロキサンを配合する方法（特許文献２参照）などが提案されている。また、樹脂成分に特定の石油系重質油類またはピッチ類とシリコーン化合物を配合する方法（特許文献３参照）、および芳香環を有する非シリコーン樹脂に式Ｒ２ＳｉＯ１．０で示される単位とＲＳｉＯ１．５で示される単位（Ｒは炭化水素基）を持ち、重量平均分子量が１０，０００以上２７０，０００以下であるシリコーン樹脂を配合する方法（特許文献４参照）などが提案されている。 As a method for imparting flame retardancy to an aromatic polycarbonate resin, a flame retardant aromatic polycarbonate resin composition to which a bromine-based compound or a phosphorus-based compound has been conventionally proposed has been proposed, and OA equipment has a strong demand for flame retardancy. However, flame retardant aromatic polycarbonate resin compositions that replace these flame retardants have been developed and are being used in the products listed above. Examples of the purpose of changing the flame retardant include suppression of generation of a corrosive gas at the time of molding or improvement of product recyclability. Examples of flame retardants that can replace the flame retardants listed above include silicone compounds. In recent years, a flame retardant resin composition in which a silicone compound is blended with an aromatic polycarbonate resin has been intensively studied and various proposals have been made. For example, a method in which an alkali (earth) metal salt of perfluoroalkyl sulfonate and an organosiloxane having an alkoxy group, a vinyl group, and a phenyl group are blended with a polycarbonate resin (see Patent Document 1), and a perfluoroalkyl sulfonic acid with a polycarbonate resin. A method of blending an organopolysiloxane containing an alkali metal salt or an alkaline earth metal salt and an organoxysilyl group bonded to a silicon atom via a divalent hydrocarbon group has been proposed (see Patent Document 2). Further, a method of blending a specific petroleum heavy oil or pitch and a silicone compound into the resin component (see Patent Document 3), and a unit represented by the formula R 2 SiO 1.0 in a non-silicone resin having an aromatic ring And a method of blending a silicone resin having a unit represented by RSiO 1.5 (R is a hydrocarbon group) and having a weight average molecular weight of 10,000 or more and 270,000 or less (see Patent Document 4). Yes.

しかしながら、上記提案のポリカーボネート樹脂組成物は、例えば薄肉の場合にドリップを生じＵＬ規格９４のＶ−０ランクを達成できない、シリコーンの分散が不十分で成形品に白濁が生じる、あるいは湿熱処理によりシリコーンが凝集して湿熱処理後の透明性が低下するなどの点で透明性、難燃性が十分とはいえないものが多かった。   However, the above-mentioned proposed polycarbonate resin composition has, for example, a drip in the case of a thin wall and cannot achieve the UL standard 94 V-0 rank, the silicone is not sufficiently dispersed and the molded product becomes clouded, or the wet heat treatment There were many cases where transparency and flame retardancy were not sufficient in that they aggregated and the transparency after wet heat treatment decreased.

ドリップを抑制するためにはフィブリル形成能を有するポリテトラフルオロエチレンを使用することが有効である。しかしながらポリテトラフルオロエチレンを芳香族ポリカーボネート樹脂に配合するとポリテトラフルオロエチレンと芳香族ポリカーボネート樹脂が非相溶性であるために押し出し成形品の透明性が低下するという問題がある。   In order to suppress the drip, it is effective to use polytetrafluoroethylene having a fibril forming ability. However, when polytetrafluoroethylene is blended with an aromatic polycarbonate resin, there is a problem that the transparency of the extruded product is lowered because the polytetrafluoroethylene and the aromatic polycarbonate resin are incompatible.

芳香族ポリカーボネート樹脂に有機アルカリ金属塩、およびポリ（メチル水素シロキサン）からなる樹脂組成物についても具体例が記載されている。（特許文献５参照）しかしながらかかる樹脂組成物は樹脂組成物自体が白濁し、さらには成形品表面で剥離などの分散不良が発生し、十分とは言えないものであった。芳香族ポリカーボネート樹脂に有機アルカリ金属塩、およびポリ（フェニルメチル水素シロキサン）からなる樹脂組成物の例が知られている（特許文献６参照）。さらに分岐構造を有するポリカーボネートと有機金属塩からなる樹脂組成物（特許文献７）、分岐構造を有するポリカーボネートと有機金属塩および特定のシロキサン化合物からなる樹脂組成物についても具体的に記載されている（特許文献８、９参照）。   Specific examples are also described for a resin composition comprising an aromatic alkali resin and an organic alkali metal salt and poly (methyl hydrogen siloxane). However, such a resin composition is not sufficient because the resin composition itself becomes cloudy, and further, poor dispersion such as peeling occurs on the surface of the molded product. An example of a resin composition comprising an aromatic polycarbonate resin and an organic alkali metal salt and poly (phenylmethylhydrogensiloxane) is known (see Patent Document 6). Furthermore, a resin composition comprising a polycarbonate having a branched structure and an organic metal salt (Patent Document 7), and a resin composition comprising a polycarbonate having a branched structure, an organic metal salt and a specific siloxane compound are also specifically described ( (See Patent Documents 8 and 9).

これらにより優れた難燃性と透明性を維持する組成物が提供されるが、ポリカーボネート用途の多様化、製品の薄肉化により、さらなる難燃性のアップが求められている。難燃性ポリカーボネート樹脂組成物は用途によってさまざまなものが開発されており、その難燃レベルも様々であるが、それぞれの材料の難燃レベルを少しでもアップすること、例えば電気用途において材料の難燃性指標として広く用いられているＵＬ９４規格に関し、材料の難燃ランクＶ−０を達成できる試験片の最小厚みを０．１ｍｍでも薄くすることができれば、難燃材料としての用途が広がりその効果は非常に大きい。また、難燃レベルは同一であっても、使用される難燃剤などの添加量を少しでも少なくすることができれば、加工時の発生ガス低減、加工性のアップ、品質の安定性、各種物性向上につながる。特に押し出しシートや賦型押し出しシートを押出し成形する場合には、加工時の発生ガスが原因で冷却ロールに付着しそれがシート表面外観を悪化させるという問題があり改善を強く求められている。   Although the composition which maintains the outstanding flame retardance and transparency by these is provided, the further flame retardance improvement is calculated | required by diversification of a polycarbonate use and the thinning of a product. Various flame retardant polycarbonate resin compositions have been developed depending on the application, and the flame retardant level varies, but it is necessary to raise the flame retardant level of each material as much as possible, for example, in the electrical application With regard to the UL94 standard widely used as a flammability index, if the minimum thickness of a specimen that can achieve the flame retardance rank V-0 of the material can be reduced even by 0.1 mm, the use as a flame retardant material will be expanded and its effect Is very big. In addition, even if the flame retardant level is the same, if the amount of flame retardant used can be reduced as much as possible, gas generated during processing is reduced, workability is improved, quality is stable, and various physical properties are improved. Leads to. In particular, when extruding an extruded sheet or a shaped extruded sheet, there is a problem that gas generated during processing adheres to the cooling roll, which deteriorates the sheet surface appearance, and there is a strong demand for improvement.

特開平６−３０６２６５号公報JP-A-6-306265 特開平６−３３６５４７号公報JP-A-6-336547 特開平９−１６９９１４号公報JP-A-9-169914 特開平１０−１３９９６４号公報Japanese Patent Laid-Open No. 10-139964 特公昭６０−３８４１９号公報Japanese Patent Publication No. 60-38419 特開２００３−１４７１９０号公報JP 2003-147190 A 特許３１２９３７４号公報Japanese Patent No. 3129374 特許３１６３５９６号公報Japanese Patent No. 3163596 特開２００７−３１５８３号公報JP 2007-31583 A

本発明の目的は、透明性、外観および難燃性に優れた芳香族ポリカーボネート樹脂組成物からなる押し出し成形品を提供することにある。   An object of the present invention is to provide an extruded product comprising an aromatic polycarbonate resin composition having excellent transparency, appearance and flame retardancy.

本発明者らは、上記目的を達成せんとして鋭意研究を重ねた結果、分岐率が限定された分岐構造を有するポリカーボネート樹脂と難燃剤とを組み合わせることで難燃性に優れ、透明性、外観にも優れる芳香族ポリカーボネート樹脂組成物からなる押し出し成形品が得られることを見出し、本発明に到達した。   As a result of intensive studies to achieve the above object, the present inventors are excellent in flame retardancy by combining a polycarbonate resin having a branched structure with a limited branching rate and a flame retardant, in transparency and appearance. The present inventors have found that an extrusion-molded product comprising an aromatic polycarbonate resin composition that is also excellent can be obtained, and reached the present invention.

すなわち、本発明によれば、（１）（Ａ）分岐率０．７０〜１．５０ｍｏｌ％の分岐構造を有する芳香族ポリカーボネート樹脂（Ａ成分）１００重量部に対して、（Ｂ）難燃剤（Ｂ成分）０．００５〜５重量部を含有する芳香族ポリカーボネート樹脂組成物からなる押し出し成形品が提供される。   That is, according to the present invention, (B) flame retardant (B) with respect to 100 parts by weight of (A) aromatic polycarbonate resin (component A) having a branched structure with a branching ratio of 0.70 to 1.50 mol%. B component) An extruded product comprising an aromatic polycarbonate resin composition containing 0.005 to 5 parts by weight is provided.

本発明のより好適な態様の一つは、（２）Ｂ成分が（Ｂ−１）アルカリ（土類）金属塩（Ｂ−１成分）および（Ｂ−２）芳香族基を有するシリコーン化合物（Ｂ−２成分）からなる群より選択される少なくとも１種の難燃剤である上記構成（１）の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品である。   One of the more preferred embodiments of the present invention is that (2) a silicone compound in which the B component has (B-1) an alkali (earth) metal salt (B-1 component) and (B-2) an aromatic group ( (B-2 component) is an extrusion-molded article comprising an aromatic polycarbonate resin composition having the above constitution (1), which is at least one flame retardant selected from the group consisting of B-2 component).

本発明のより好適な態様の一つは、（３）Ａ成分１００重量部に対して、Ｂ−１成分を０．００５〜１．０重量部含有することを特徴とする上記構成（２）の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品である。   One of the more preferable embodiments of the present invention is (3) the above constitution (2), wherein 0.001 to 1.0 part by weight of the B-1 component is contained with respect to 100 parts by weight of the A component. It is an extrusion-molded article comprising the aromatic polycarbonate resin composition.

本発明のより好適な態様の一つは、（４）Ａ成分１００重量部に対して、Ｂ−２成分を０．０５〜２．０重量部含有することを特徴とする上記構成（２）〜（３）のいずれかの芳香族ポリカーボネート樹脂組成物からなる押し出し成形品である。   One of the more preferable embodiments of the present invention is the above-mentioned constitution (2), wherein 0.05 to 2.0 parts by weight of the B-2 component is contained per 100 parts by weight of the (4) A component. It is an extrusion molded article which consists of an aromatic polycarbonate resin composition in any one of-(3).

本発明のより好適な態様の一つは、（５）Ｂ−１成分がパーフルオロアルキルスルホン酸アルカリ（土類）金属塩、芳香族スルホン酸アルカリ（土類）金属塩、および芳香族系イミドのアルカリ（土類）金属塩からなる群より選択される１種以上の有機アルカリ（土類）金属塩であることを特徴とする上記構成（２）〜（４）のいずれかの芳香族ポリカーボネート樹脂組成物からなる押し出し成形品である。   One of the more preferable embodiments of the present invention is that (5) the component B-1 is an alkali (earth) metal salt of a perfluoroalkyl sulfonate, an alkali (earth) metal salt of an aromatic sulfonate, and an aromatic imide The aromatic polycarbonate according to any one of the above constitutions (2) to (4), wherein the aromatic polycarbonate is one or more organic alkali (earth) metal salts selected from the group consisting of alkali (earth) metal salts of It is an extrusion-molded product made of a resin composition.

本発明のより好適な態様の一つは、（６）Ｂ−２成分が分子中にＳｉ−Ｈ基を含有するシリコーン化合物であることを特徴とする上記構成（２）〜（５）のいずれかの芳香族ポリカーボネート樹脂組成物からなる押し出し成形品である。   One of the more preferable embodiments of the present invention is any one of the above constitutions (2) to (5), wherein (6) the B-2 component is a silicone compound containing a Si—H group in the molecule. It is an extrusion-molded article comprising such an aromatic polycarbonate resin composition.

本発明のより好適な態様の一つは、（７）押し出し成形品が、押し出しシート、押し出し賦型シート、または異型押し出し品である上記構成（１）〜（６）のいずれかの芳香族ポリカーボネート樹脂組成物からなる押し出し成形品である。   One of the more preferable embodiments of the present invention is (7) the aromatic polycarbonate according to any one of the above constitutions (1) to (6), wherein the extruded product is an extruded sheet, an extruded shaped sheet, or a modified extruded product. It is an extrusion-molded product made of a resin composition.

本発明のより好適な態様の一つは、（８）押し出し成形品が、照明用カバーまたは透過型ティスプレイ用カバーである上記構成（１）〜（６）のいずれかの芳香族ポリカーボネート樹脂組成物からなる押し出し成形品である。   One of the more preferable embodiments of the present invention is: (8) The aromatic polycarbonate resin composition according to any one of the above constitutions (1) to (6), wherein the extruded product is a lighting cover or a transmissive display cover. This is an extruded product made of a product.

本発明の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品は、芳香族ポリカーボネート樹脂に有機アルカリ（土類）金属塩と芳香族基を含有するシリコーン化合物を配合させた樹脂組成物において、これまでにないまでに有機アルカリ（土類）金属塩の配合量を狭い範囲に限定することにより、肉厚成形品における透明性を維持した上で優れた難燃性を有するものであり、これらの技術は従来の難燃化技術にはないものである。本発明の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品は、環境負荷が高いとされる臭素系難燃剤やリン系難燃剤を使用せずに高度な難燃性を付与することも可能となり、さらに成形品の肉薄部でも肉厚部でも透明性を維持しているので、照明用カバーまたは透過型ティスプレイ用カバーなどの各種工業用途に極めて有用であり、その奏する工業的効果は極めて大である。   The extrusion molded article comprising the aromatic polycarbonate resin composition of the present invention is a resin composition obtained by blending an aromatic polycarbonate resin with a silicone compound containing an organic alkali (earth) metal salt and an aromatic group. By limiting the blending amount of the organic alkali (earth) metal salt to a narrow range until now, it has excellent flame retardancy while maintaining transparency in the thick molded product. It is not found in conventional flame retardant technology. Extrusion molded products comprising the aromatic polycarbonate resin composition of the present invention can also impart high flame retardancy without using brominated flame retardants and phosphorus-based flame retardants, which are considered to have a high environmental load, Furthermore, since the transparency is maintained in both the thin and thick parts of the molded product, it is extremely useful for various industrial applications such as lighting covers and transmission-type display covers, and the industrial effects exhibited are extremely large. is there.

以下、更に本発明の詳細について説明する。
＜Ａ成分：芳香族ポリカーボネート樹脂＞
本発明のＡ成分として使用される分岐率０．７０〜１．５０ｍｏｌ％の芳香族ポリカーボネート樹脂とは、分岐構造を有する芳香族ポリカーボネート樹脂（Ａ−１成分）、または、Ａ−１成分と直鎖状芳香族ポリカーボネート樹脂（Ａ−２成分）との混合物であり、Ａ成分全体としての分岐率が０．７０〜１．５０ｍｏｌ％を満たしていれば、分岐率が０．７０〜１．５０ｍｏｌ％の範囲を外れる分岐構造を有する芳香族ポリカーボネート樹脂を含んでいてもよい。 Hereinafter, the details of the present invention will be described.
<A component: aromatic polycarbonate resin>
The aromatic polycarbonate resin having a branching ratio of 0.70 to 1.50 mol% used as the A component of the present invention is an aromatic polycarbonate resin having a branched structure (A-1 component) or directly with the A-1 component. If it is a mixture with a chain aromatic polycarbonate resin (component A-2) and the branching rate of the entire component A satisfies 0.70 to 1.50 mol%, the branching rate is 0.70 to 1.50 mol. An aromatic polycarbonate resin having a branched structure outside the range of% may be included.

より優れた難燃性を付与する観点からは、Ａ成分がＡ−１成分を２０重量％〜１００重量％含むことが好ましく、７０重量％〜１００重量％含むことがより好ましく１００重量％含むことがさらに好ましい。Ａ成分全体としての分岐率は０．７０〜１．５０ｍｏｌ％であり、０．７０〜１．３０ｍｏｌ％が好ましく、０．７０〜１．２０ｍｏｌ％がより好ましく、０．７５〜１．００ｍｏｌ％がさらに好ましい。なお、分岐率は樹脂全体に含まれる製造に用いた二価フェノール由来の構造単位の総モル数に対する分岐剤由来の構造単位のモル数（分岐剤由来の構造単位のモル数／二価フェノール由来の構造単位の総モル数×１００（ｍｏｌ％で表す））を意味し、かかる分岐率は１Ｈ−ＮＭＲ測定により実測することができる。 From the viewpoint of imparting more excellent flame retardancy, the A component preferably contains 20% to 100% by weight of the A-1 component, more preferably 70% to 100% by weight, more preferably 100% by weight. Is more preferable. The branching ratio as the whole component A is 0.70 to 1.50 mol%, preferably 0.70 to 1.30 mol%, more preferably 0.70 to 1.20 mol%, and 0.75 to 1.00 mol%. Is more preferable. The branching rate is the number of moles of the structural unit derived from the branching agent to the total number of moles of the structural unit derived from the dihydric phenol used for the production included in the entire resin (the number of moles of the structural unit derived from the branching agent / derived from the dihydric phenol. The total number of moles of structural units × 100 (expressed in mol%)), and the branching ratio can be measured by 1 H-NMR measurement.

分岐率が低いと、満足な分岐特性が得られず溶融張力が低すぎて、組成物に関する難燃性、とくにドリップ防止性が発現しにくくなり、さらに、押出成形が困難になるので好ましくない。一方、分岐率が高いとポリマーが架橋し、ゲルが発生し、ポリマーの耐衝撃性が低下する。さらに分岐率が高すぎると成形品表面にくもりが生じやすくなり、それを解消するためにシリンダー温度を高くしたり射出速度をより細かく調整しなければならなくなるという問題がある。   If the branching ratio is low, satisfactory branching characteristics cannot be obtained, the melt tension is too low, flame retardancy with respect to the composition, in particular, anti-drip property is difficult to be exhibited, and extrusion molding becomes difficult, which is not preferable. On the other hand, if the branching ratio is high, the polymer is crosslinked, a gel is generated, and the impact resistance of the polymer is lowered. Further, if the branching rate is too high, the surface of the molded product is likely to be clouded, and there is a problem that the cylinder temperature must be increased or the injection speed must be adjusted more finely in order to eliminate this.

本発明のＡ成分の分岐率をＺｍｏｌ％とし、２８０℃における溶融張力をＹとした場合、ＺとＹとの関係は３．８Ｚ−２．４ ≦ Ｙ ≦ ３．８Ｚ＋４．５であることが好ましく、より好ましくは３．８Ｚ−１．８ ≦ Ｙ ≦ ３．８Ｚ＋３．９である。Ｙ＜３．８Ｚ−２．４であると、難燃性試験においてドリップが生じやすくなり十分な難燃性が得られなくなる問題があり、さらに、溶融張力が低すぎてドローダウンを生じ易く、押出成形が容易に行えなくなる場合があり好ましくない。また、Ｙ ＞３．８Ｚ＋４．５であると、溶融張力が高すぎて流動性が悪く成形性に劣り、成型品の表面状態が悪くなり好ましくない。なお、溶融張力は 温度２８０℃ 押出温度１０ｍｍ／ｍｉｎ、引張速度１５７ｍｍ／ｓ、オリフィスＬ／Ｄ＝８／２．１で生じる張力として測定できる。   When the branching rate of the A component of the present invention is Z mol% and the melt tension at 280 ° C. is Y, the relationship between Z and Y is 3.8Z−2.4 ≦ Y ≦ 3.8Z + 4.5. More preferably, it is 3.8Z-1.8 <= Y <= 3.8Z + 3.9. If Y <3.8Z-2.4, there is a problem that drip is likely to occur in the flame retardancy test and sufficient flame retardancy cannot be obtained, and the melt tension is too low to easily cause drawdown, It is not preferable because extrusion may not be easily performed. Further, if Y 1> 3.8Z + 4.5, the melt tension is too high, the fluidity is poor and the moldability is poor, and the surface state of the molded product is deteriorated. The melt tension can be measured as a tension generated at a temperature of 280 ° C., an extrusion temperature of 10 mm / min, a tensile speed of 157 mm / s, and an orifice L / D = 8 / 2.1.

本発明のＡ成分の粘度平均分子量は、１０，０００〜５０，０００の範囲が好ましく、１６，０００〜３０，０００がより好ましく、１８，０００〜２８，０００の範囲がさらにより好ましく、１９，０００〜２６，０００の範囲が最も好ましい。分子量が５０，０００を越えると溶融張力が高すぎて成形性に劣る場合があり、分子量が１０，０００未満であると成形片を燃焼した際のドリップ防止効果が不十分となり、すなわち本発明の優れた難燃性が発揮しにくくなることや溶融張力が低くすぎて押出成形が困難になることがある。また、本発明のＡ成分として使用される芳香族ポリカーボネート樹脂は、分子量が前述の好ましい分子量範囲を満たすように、分岐構造を有する芳香族ポリカーボネート樹脂１種あるいは２種以上を混合しても差し支えない。この場合、粘度平均分子量が前述の好ましい分子量範囲外である分岐構造を有するポリカーボネート樹脂を混合することも当然に可能である。なお、本発明でいう粘度平均分子量はまず次式にて算出される比粘度を塩化メチレン１００ｍｌにポリカーボネート樹脂０．７ｇを２０℃で溶解した溶液からオストワルド粘度計を用いて求め、
比粘度（ηＳＰ）＝（ｔ−ｔ０）／ｔ０
［ｔ０は塩化メチレンの落下秒数、ｔは試料溶液の落下秒数］
求められた比粘度を次式にて挿入して粘度平均分子量Ｍを求める。
ηＳＰ／ｃ＝［η］＋０．４５×［η］２ｃ（但し［η］は極限粘度）
［η］＝１．２３×１０−４Ｍ０．８３
ｃ＝０．７ The viscosity average molecular weight of the component A of the present invention is preferably in the range of 10,000 to 50,000, more preferably 16,000 to 30,000, still more preferably in the range of 18,000 to 28,000, A range of 000 to 26,000 is most preferred. If the molecular weight exceeds 50,000, the melt tension may be too high and the moldability may be inferior. If the molecular weight is less than 10,000, the drip prevention effect when the molded piece is burned becomes insufficient. It may be difficult to exhibit excellent flame retardancy, and the melt tension may be too low to make extrusion difficult. In addition, the aromatic polycarbonate resin used as the component A of the present invention may be mixed with one or more aromatic polycarbonate resins having a branched structure so that the molecular weight satisfies the aforementioned preferable molecular weight range. . In this case, it is naturally possible to mix a polycarbonate resin having a branched structure whose viscosity average molecular weight is outside the above preferred molecular weight range. In addition, the viscosity average molecular weight as used in the field of this invention calculates | requires first using the Ostwald viscometer from the solution which melt | dissolved 0.7 g of polycarbonate resins in 20 ml of methylene chloride with the specific viscosity computed by following Formula,
Specific viscosity (η SP ) = (t−t 0 ) / t 0
[T 0 is methylene chloride falling seconds, t is sample solution falling seconds]
The obtained specific viscosity is inserted by the following equation to determine the viscosity average molecular weight M.
η SP /c=[η]+0.45×[η] 2 c (where [η] is the intrinsic viscosity)
[Η] = 1.23 × 10 −4 M 0.83
c = 0.7

本発明のＡ成分は、樹脂中の全Ｎ（窒素）量が好ましくは０〜７ｐｐｍ、より好ましくは０〜５ｐｐｍである。なお、樹脂中の全Ｎ（窒素）量の測定は三菱化学社製ＴＮ−１０型微量窒素分析装置（化学発光法）を用いて測定することが出来る。   In the component A of the present invention, the total N (nitrogen) amount in the resin is preferably 0 to 7 ppm, more preferably 0 to 5 ppm. The total N (nitrogen) content in the resin can be measured using a TN-10 type trace nitrogen analyzer (chemiluminescence method) manufactured by Mitsubishi Chemical Corporation.

また、全Ｃｌ（塩素）量が好ましくは０〜２００ｐｐｍ、より好ましくは０〜１５０ｐｐｍである。分岐構造を有するポリカーボネート樹脂中の全Ｎ量が７ｐｐｍを越えるかまたは全Ｃｌ量が２００ｐｐｍを越えると、熱安定性が悪くなるので好ましくない。   The total Cl (chlorine) amount is preferably 0 to 200 ppm, more preferably 0 to 150 ppm. If the total N amount in the polycarbonate resin having a branched structure exceeds 7 ppm or the total Cl amount exceeds 200 ppm, the thermal stability is deteriorated, which is not preferable.

本発明のＡ−１成分である分岐構造を有する芳香族ポリカーボネート樹脂は、好ましくは分岐率が０．７０〜１．５０ｍｏｌ％であり、より好ましくは０．７０〜１．３０ｍｏｌ％、さらに好ましくは０．７５〜１．１０ｍｏｌ％である。   The aromatic polycarbonate resin having a branched structure which is the A-1 component of the present invention preferably has a branching rate of 0.70 to 1.50 mol%, more preferably 0.70 to 1.30 mol%, and still more preferably. It is 0.75 to 1.10 mol%.

本発明のＡ−１成分である分岐構造を有する芳香族ポリカーボネート樹脂の粘度平均分子量は、１０，０００〜５０，０００の範囲が好ましく、１６，０００〜３０，０００がより好ましく、１８，０００〜２８，０００の範囲がさらにより好ましく、１９，０００〜２６，０００の範囲が最も好ましい。   The viscosity average molecular weight of the aromatic polycarbonate resin having a branched structure which is the A-1 component of the present invention is preferably in the range of 10,000 to 50,000, more preferably 16,000 to 30,000, and 18,000 to A range of 28,000 is even more preferred, with a range of 19,000-26,000 being most preferred.

本発明のＡ−１成分である分岐構造を有するポリカーボネート樹脂は、二価フェノール、分岐剤、一価フェノール類およびホスゲンを用いて有機溶媒の存在下で行う界面重合反応法により得られる。   The polycarbonate resin having a branched structure which is the A-1 component of the present invention can be obtained by an interfacial polymerization reaction method using a dihydric phenol, a branching agent, monohydric phenols and phosgene in the presence of an organic solvent.

本発明の分岐構造を有するポリカーボネート樹脂を得るために使用される二価フェノールの代表的な例は、２，２−ビス（４−ヒドロキシフェニル）プロパン（通称ビスフェノールＡ）、ハイドロキノン、レゾルシノール、４，４’−ビフェノール、１，１−ビス（４ヒドロキシフェニル）エタン、２，２−ビス（４−ヒドロキシ−３−メチルフェニル）プロパン、２，２−ビス（４−ヒドロキシフェニル）ブタン、１，１−ビス（４−ヒドロキシフェニル）−１−フェニルエタン、１，１−ビス（４−ヒドロキシフェニル）シクロヘキサン、１，１−ビス（４−ヒドロキシフェニル）−３，３，５−トリメチルシクロヘキサン、２，２−ビス（４−ヒドロキシフェニル）ペンタン、４，４’−（ｐ−フェニレンジイソプロピリデン）ジフェノール、４，４’−（ｍ−フェニレンジイソプロピリデン）ジフェノール、１，１−ビス（４−ヒドロキシフェニル）−４−イソプロピルシクロヘキサン、ビス（４−ヒドロキシフェニル）オキシド、ビス（４−ヒドロキシフェニル）スルフィド、ビス（４−ヒドロキシフェニル）スルホキシド等が挙げられる。これらは単独で用いても、二種以上併用してもよい。なかでも２，２−ビス（４−ヒドロキシフェニル）プロパンすなわちビスフェノールＡが好ましい。   Representative examples of the dihydric phenol used to obtain the polycarbonate resin having a branched structure of the present invention are 2,2-bis (4-hydroxyphenyl) propane (commonly called bisphenol A), hydroquinone, resorcinol, 4, 4′-biphenol, 1,1-bis (4hydroxyphenyl) ethane, 2,2-bis (4-hydroxy-3-methylphenyl) propane, 2,2-bis (4-hydroxyphenyl) butane, 1,1 -Bis (4-hydroxyphenyl) -1-phenylethane, 1,1-bis (4-hydroxyphenyl) cyclohexane, 1,1-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane, 2, 2-bis (4-hydroxyphenyl) pentane, 4,4 ′-(p-phenylenediisopropylidene) diphe 4,4 ′-(m-phenylenediisopropylidene) diphenol, 1,1-bis (4-hydroxyphenyl) -4-isopropylcyclohexane, bis (4-hydroxyphenyl) oxide, bis (4-hydroxy Phenyl) sulfide, bis (4-hydroxyphenyl) sulfoxide and the like. These may be used alone or in combination of two or more. Of these, 2,2-bis (4-hydroxyphenyl) propane, that is, bisphenol A is preferable.

本発明で使用される三価以上のフェノール（分岐剤）の代表的な例は、１，１，１−トリス（４−ヒドロキシフェニル）エタン、４，６−ジメチル−２，４，６−トリ（４−ヒドロキシフェニル）ヘプテン−２、４，６−ジメチル−２，４，６−トリ（４−ヒドロキシフェニル）ヘプタン、１，３，５−トリ（４−ヒドロキシフェニル）ベンゼン、２，６−ビス（２−ヒドロキシ−５−メチルベンジル）−４−メチルフェノ−ル、テトラ（４−ヒドロキシフェニル）メタン、トリスフェノール、ビス（２，４−ジヒドロキシルフェニル）ケトン、フロログルシン、フロログルシド、イサンチンビスフェノール、１，４−ビス（４，４−ジヒドロキシトリフェニルメチル）ベンゼン、トリメリト酸、ピロメリト酸、が挙げられる。これらは単独で用いても、二種以上併用してもよい。なかでも、１，１，１−トリス（４−ヒドロキシフェニル）エタンが好ましい。   Representative examples of tri- or higher-valent phenols (branching agents) used in the present invention include 1,1,1-tris (4-hydroxyphenyl) ethane, 4,6-dimethyl-2,4,6-tri (4-hydroxyphenyl) heptene-2,4,6-dimethyl-2,4,6-tri (4-hydroxyphenyl) heptane, 1,3,5-tri (4-hydroxyphenyl) benzene, 2,6- Bis (2-hydroxy-5-methylbenzyl) -4-methylphenol, tetra (4-hydroxyphenyl) methane, trisphenol, bis (2,4-dihydroxylphenyl) ketone, phloroglucin, phloroglucid, isantine bisphenol, Examples include 1,4-bis (4,4-dihydroxytriphenylmethyl) benzene, trimellitic acid, and pyromellitic acid. These may be used alone or in combination of two or more. Of these, 1,1,1-tris (4-hydroxyphenyl) ethane is preferable.

本発明のＡ−１成分である分岐構造を有するポリカーボネート樹脂の製造に使用される一価フェノール（末端停止剤）としてはどのような構造でもよく特に制限はない。例えば、ｐ−ｔｅｒｔ−ブチルフェノール、ｐ−ｔｅｒｔ−オクチルフェノール、ｐ−クミルフェノール、４−ヒドロキシベンゾフェノン、フェノール等が挙げられる。これらは単独で用いても、二種以上併用してもよい。なかでも、ｐ−ｔｅｒｔ−ブチルフェノールが好ましい。   The monohydric phenol (terminal terminator) used for the production of the polycarbonate resin having a branched structure which is the A-1 component of the present invention may have any structure and is not particularly limited. For example, p-tert-butylphenol, p-tert-octylphenol, p-cumylphenol, 4-hydroxybenzophenone, phenol and the like can be mentioned. These may be used alone or in combination of two or more. Of these, p-tert-butylphenol is preferable.

すなわち、本発明のＡ−１成分である分岐構造を有するポリカーボネートは、分岐構造部分が１，１，１−トリス（４−ヒドロキシフェニル）エタンから誘導されてなる構造であり、分岐構造部分を除いた直鎖構造部分がビスフェノールＡから誘導されてなる構造であり、末端がｐ−ｔｅｒｔ−ブチルフェノールから誘導されて成る構造であることが好ましい。   That is, the polycarbonate having a branched structure which is the A-1 component of the present invention is a structure in which the branched structure portion is derived from 1,1,1-tris (4-hydroxyphenyl) ethane, and the branched structure portion is excluded. The straight chain structure portion is preferably a structure derived from bisphenol A and the terminal is preferably a structure derived from p-tert-butylphenol.

本発明の分岐状ポリカーボネート樹脂は、好適には下記の方法で製造される。
すなわち、二価フェノール化合物および分岐剤を溶解したアルカリ水溶液に有機溶媒の存在下でホスゲンを吹き込み反応させて、ポリカーボネートオリゴマーを得、これに一価フェノール類を投入し乳化させた後、無攪拌下で重合させることを特徴とする方法である。 The branched polycarbonate resin of the present invention is preferably produced by the following method.
That is, phosgene was blown into an alkaline aqueous solution in which a dihydric phenol compound and a branching agent were dissolved in the presence of an organic solvent to obtain a polycarbonate oligomer. It is the method characterized by making it superpose | polymerize.

また、反応促進のために反応触媒として、例えば、トリエチルアミン、トリブチルアミン、テトラ−ｎ−ブチルアンモニウムブロマイド、テトラ−ｎ−ブチルホスホニウムブロマイド等の第三級アミン、第四級アンモニウム化合物、第四級ホスホニウム化合物等の触媒を使用することも出来る。反応触媒は二価フェノール化合物に対して０．００２モル％以下が好ましく、０．００１モル％以下がより好ましい。特に無触媒で上記反応を行うことが好ましい。０．００２モル％を越える場合は分岐剤量に対し溶融張力が高くなりすぎたり、ゲルが生成したりする。また触媒がクロロホーメート基と反応して熱的に不安定なウレタン結合が多くなると共に、触媒が残存することにより分岐状ポリカーボネート樹脂中の全Ｎ含有量が増大し、耐衝撃性、透明性、耐熱性が低下するので好ましくない。よって上記反応を無触媒で行うことが特に好ましい。その際、反応温度は通常０〜４０℃好ましく、さらに１５〜３８℃が好ましい。反応時間は１０分〜５時間程度、反応中のｐＨは９．０以上に保つのが好ましく、１１．０〜１３．８がさらに好ましい。   Further, as a reaction catalyst for promoting the reaction, for example, tertiary amine such as triethylamine, tributylamine, tetra-n-butylammonium bromide, tetra-n-butylphosphonium bromide, quaternary ammonium compound, quaternary phosphonium A catalyst such as a compound can also be used. The reaction catalyst is preferably 0.002 mol% or less, more preferably 0.001 mol% or less, based on the dihydric phenol compound. In particular, the above reaction is preferably carried out without a catalyst. When it exceeds 0.002 mol%, the melt tension becomes too high with respect to the amount of the branching agent, or a gel is formed. In addition, the catalyst reacts with the chloroformate group to increase the number of thermally unstable urethane bonds, and the remaining catalyst increases the total N content in the branched polycarbonate resin, resulting in impact resistance and transparency. This is not preferable because the heat resistance is lowered. Therefore, it is particularly preferable to carry out the above reaction without a catalyst. At that time, the reaction temperature is usually preferably 0 to 40 ° C, more preferably 15 to 38 ° C. The reaction time is about 10 minutes to 5 hours, and the pH during the reaction is preferably maintained at 9.0 or more, more preferably 11.0 to 13.8.

上記の界面重合反応する際に一価フェノール類を投入後に乳化させる方法としては特に制限はないが、撹拌装置で撹拌する方法、またはアルカリ水溶液を添加する方法等が挙げられ、撹拌装置としては、パドル、プロペラ、タービンまたはカイ型翼等の単純な撹拌装置、ホモジナイザー、ミキサー、ホモミキサー等の高速撹拌機、スタティックミキサー、コロイドミル、オリフィスミキサー、フロージェットミキサー、超音波乳化装置等がある。なかでも無触媒で重合する方法においてはホモミキサー、スタティックミキサー等が好ましく用いられる。   There is no particular limitation on the method of emulsifying the monohydric phenols after adding the above-mentioned interfacial polymerization reaction, but examples include a method of stirring with a stirrer or a method of adding an alkaline aqueous solution. There are simple stirring devices such as paddles, propellers, turbines or chi-type blades, high-speed stirrers such as homogenizers, mixers and homomixers, static mixers, colloid mills, orifice mixers, flow jet mixers, ultrasonic emulsifiers and the like. Of these, homomixers, static mixers and the like are preferably used in the polymerization without catalyst.

次いで、該分岐状ポリカーボネート樹脂有機溶媒溶液を洗浄、造粒、乾燥し、本発明の分岐状ポリカーボネート樹脂（パウダー）を得ることができる。さらに該パウダーを溶融押出してペレット化して本発明の分岐状ポリカーボネート樹脂（ペレット）が得られる。洗浄、造粒、乾燥などは特に制限はなく公知の方法が採用できる。   Next, the branched polycarbonate resin organic solvent solution is washed, granulated, and dried to obtain the branched polycarbonate resin (powder) of the present invention. Further, the powder is melt extruded and pelletized to obtain the branched polycarbonate resin (pellet) of the present invention. Cleaning, granulation, drying and the like are not particularly limited, and known methods can be employed.

また、分岐構造を有するポリカーボネート樹脂中の全Ｃｌ含有量を低下させるには、反応時溶媒として使用されるジクロロメタン（塩化メチレン）、ジクロロエタン、トリクロロエタン、テトラクロロエタン、ペンタクロロエタン、ヘキサクロロエタン、ジクロロエチレン、クロロベンゼン、ジクロロベンゼンなどの塩素化炭化水素溶媒を除去することが必要である。例えば、分岐構造を有するポリカーボネート樹脂パウダーやペレットの乾燥処理を十分に行なうことが挙げられる。   In order to reduce the total Cl content in the polycarbonate resin having a branched structure, dichloromethane (methylene chloride), dichloroethane, trichloroethane, tetrachloroethane, pentachloroethane, hexachloroethane, dichloroethylene, chlorobenzene, used as a solvent during the reaction, It is necessary to remove chlorinated hydrocarbon solvents such as dichlorobenzene. For example, it is possible to sufficiently dry the polycarbonate resin powder and pellets having a branched structure.

本発明の分岐構造を有する芳香族ポリカーボネートは実質的にハロゲン原子を含まないものであることが好ましい。実質的にハロゲン原子を含まないとは、分子中にハロゲン置換二価フェノールなどを含まないことを示し、上記芳香族ポリカーボネートの製造方法において残留する微量の溶媒（ハロゲン化炭化水素）や、カーボネート前駆体までも対象とするものではない。   The aromatic polycarbonate having a branched structure of the present invention is preferably substantially free of halogen atoms. The phrase “substantially free of halogen atoms” means that the molecule does not contain halogen-substituted dihydric phenols, etc., and a trace amount of solvent (halogenated hydrocarbon) remaining in the above aromatic polycarbonate production method or carbonate precursor Not even the body.

Ａ−２成分である直鎖状芳香族ポリカーボネート樹脂は通常二価フェノールとカーボネート前駆体とを界面重縮合法、溶融エステル交換法で反応させて得られたものの他、カーボネートプレポリマーを固相エステル交換法により重合させたもの、または環状カーボネート化合物の開環重合法により重合させて得られるものである。   The linear aromatic polycarbonate resin that is component A-2 is usually obtained by reacting a dihydric phenol and a carbonate precursor by interfacial polycondensation or melt transesterification, as well as a carbonate prepolymer by solid-phase ester. It is obtained by polymerizing by an exchange method or polymerized by a ring-opening polymerization method of a cyclic carbonate compound.

ここで使用される二価フェノールの代表的な例としては、ハイドロキノン、レゾルシノール、４，４’−ジヒドロキシジフェニル、ビス（４−ヒドロキシフェニル）メタン、ビス｛（４−ヒドロキシ−３，５−ジメチル）フェニル｝メタン、１，１−ビス（４−ヒドロキシフェニル）エタン、１，１−ビス（４−ヒドロキシフェニル）−１−フェニルエタン、２，２−ビス（４−ヒドロキシフェニル）プロパン（通称ビスフェノールＡ）、２，２−ビス｛（４−ヒドロキシ−３−メチル）フェニル｝プロパン、２，２−ビス｛（４−ヒドロキシ−３，５−ジメチル）フェニル｝プロパン、２，２−ビス｛（３−イソプロピル−４−ヒドロキシ）フェニル｝プロパン、２，２−ビス｛（４−ヒドロキシ−３−フェニル）フェニル｝プロパン、２，２−ビス（４−ヒドロキシフェニル）ブタン、２，２−ビス（４−ヒドロキシフェニル）−３−メチルブタン、２，２−ビス（４−ヒドロキシフェニル）−３，３−ジメチルブタン、２，４−ビス（４−ヒドロキシフェニル）−２−メチルブタン、２，２−ビス（４−ヒドロキシフェニル）ペンタン、２，２−ビス（４−ヒドロキシフェニル）−４−メチルペンタン、１，１−ビス（４−ヒドロキシフェニル）シクロヘキサン、１，１−ビス（４−ヒドロキシフェニル）−４−イソプロピルシクロヘキサン、１，１−ビス（４−ヒドロキシフェニル）−３，３，５−トリメチルシクロヘキサン、９，９−ビス（４−ヒドロキシフェニル）フルオレン、９，９−ビス｛（４−ヒドロキシ−３−メチル）フェニル｝フルオレン、α，α’−ビス（４−ヒドロキシフェニル）−ｏ−ジイソプロピルベンゼン、α，α’−ビス（４−ヒドロキシフェニル）−ｍ−ジイソプロピルベンゼン、α，α’−ビス（４−ヒドロキシフェニル）−ｐ−ジイソプロピルベンゼン、１，３−ビス（４−ヒドロキシフェニル）−５，７−ジメチルアダマンタン、４，４’−ジヒドロキシジフェニルスルホン、４，４’−ジヒドロキシジフェニルスルホキシド、４，４’−ジヒドロキシジフェニルスルフィド、４，４’−ジヒドロキシジフェニルケトン、４，４’−ジヒドロキシジフェニルエーテルおよび４，４’−ジヒドロキシジフェニルエステル等が挙げられ、これらは単独または２種以上を混合して使用できる。   Representative examples of the dihydric phenol used here include hydroquinone, resorcinol, 4,4′-dihydroxydiphenyl, bis (4-hydroxyphenyl) methane, bis {(4-hydroxy-3,5-dimethyl). Phenyl} methane, 1,1-bis (4-hydroxyphenyl) ethane, 1,1-bis (4-hydroxyphenyl) -1-phenylethane, 2,2-bis (4-hydroxyphenyl) propane (commonly referred to as bisphenol A) ), 2,2-bis {(4-hydroxy-3-methyl) phenyl} propane, 2,2-bis {(4-hydroxy-3,5-dimethyl) phenyl} propane, 2,2-bis {(3 -Isopropyl-4-hydroxy) phenyl} propane, 2,2-bis {(4-hydroxy-3-phenyl) phenyl} propane, 2 2-bis (4-hydroxyphenyl) butane, 2,2-bis (4-hydroxyphenyl) -3-methylbutane, 2,2-bis (4-hydroxyphenyl) -3,3-dimethylbutane, 2,4- Bis (4-hydroxyphenyl) -2-methylbutane, 2,2-bis (4-hydroxyphenyl) pentane, 2,2-bis (4-hydroxyphenyl) -4-methylpentane, 1,1-bis (4- Hydroxyphenyl) cyclohexane, 1,1-bis (4-hydroxyphenyl) -4-isopropylcyclohexane, 1,1-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane, 9,9-bis (4 -Hydroxyphenyl) fluorene, 9,9-bis {(4-hydroxy-3-methyl) phenyl} fluorene, α, α'-bis ( -Hydroxyphenyl) -o-diisopropylbenzene, α, α'-bis (4-hydroxyphenyl) -m-diisopropylbenzene, α, α'-bis (4-hydroxyphenyl) -p-diisopropylbenzene, 1,3- Bis (4-hydroxyphenyl) -5,7-dimethyladamantane, 4,4′-dihydroxydiphenyl sulfone, 4,4′-dihydroxydiphenyl sulfoxide, 4,4′-dihydroxydiphenyl sulfide, 4,4′-dihydroxydiphenyl ketone 4,4′-dihydroxydiphenyl ether, 4,4′-dihydroxydiphenyl ester, etc., and these can be used alone or in admixture of two or more.

なかでもビスフェノールＡ、２，２−ビス｛（４−ヒドロキシ−３−メチル）フェニル｝プロパン、２，２−ビス（４−ヒドロキシフェニル）ブタン、２，２−ビス（４−ヒドロキシフェニル）−３−メチルブタン、２，２−ビス（４−ヒドロキシフェニル）−３，３−ジメチルブタン、２，２−ビス（４−ヒドロキシフェニル）−４−メチルペンタン、１，１−ビス（４−ヒドロキシフェニル）−３，３，５−トリメチルシクロヘキサンおよびα，α’−ビス（４−ヒドロキシフェニル）−ｍ−ジイソプロピルベンゼンからなる群より選ばれた少なくとも１種のビスフェノールより得られる単独重合体または共重合体が好ましく、特に、ビスフェノールＡの単独重合体および１，１−ビス（４−ヒドロキシフェニル）−３，３，５−トリメチルシクロヘキサンとビスフェノールＡ、２，２−ビス｛（４−ヒドロキシ−３−メチル）フェニル｝プロパンまたはα，α’−ビス（４−ヒドロキシフェニル）−ｍ−ジイソプロピルベンゼンとの共重合体が好ましく使用される。そのなかでもさらに２，２−ビス（４−ヒドロキシフェニル）プロパンすなわちビスフェノールＡが好ましい。   Among them, bisphenol A, 2,2-bis {(4-hydroxy-3-methyl) phenyl} propane, 2,2-bis (4-hydroxyphenyl) butane, 2,2-bis (4-hydroxyphenyl) -3 -Methylbutane, 2,2-bis (4-hydroxyphenyl) -3,3-dimethylbutane, 2,2-bis (4-hydroxyphenyl) -4-methylpentane, 1,1-bis (4-hydroxyphenyl) A homopolymer or copolymer obtained from at least one bisphenol selected from the group consisting of 3,3,5-trimethylcyclohexane and α, α′-bis (4-hydroxyphenyl) -m-diisopropylbenzene In particular, a homopolymer of bisphenol A and 1,1-bis (4-hydroxyphenyl) -3,3,5-trimethyl Copolymers of rucyclohexane and bisphenol A, 2,2-bis {(4-hydroxy-3-methyl) phenyl} propane or α, α'-bis (4-hydroxyphenyl) -m-diisopropylbenzene are preferably used. Is done. Among these, 2,2-bis (4-hydroxyphenyl) propane, that is, bisphenol A is more preferable.

カーボネート前駆体としてはカルボニルハライド、カーボネートエステルまたはハロホルメート等が使用され、具体的にはホスゲン、ジフェニルカーボネートまたは二価フェノールのジハロホルメート等が挙げられる。これらのうち、ホスゲンまたはジフェニルカーボネートが工業的に有利である。   As the carbonate precursor, carbonyl halide, carbonate ester, haloformate or the like is used, and specific examples include phosgene, diphenyl carbonate, dihaloformate of dihydric phenol, and the like. Of these, phosgene or diphenyl carbonate is industrially advantageous.

上記二価フェノールとカーボネート前駆体を界面重縮合法または溶融エステル交換法によって反応させてポリカーボネート樹脂を製造するに当っては、必要に応じて触媒、末端停止剤、二価フェノールの酸化防止剤等を使用してもよい。また、得られたポリカーボネート樹脂の２種以上を混合した混合物であってもよい。   In producing polycarbonate resin by reacting the above dihydric phenol and carbonate precursor by interfacial polycondensation method or melt transesterification method, catalyst, terminal terminator, dihydric phenol antioxidant, etc., as necessary May be used. Moreover, the mixture which mixed 2 or more types of the obtained polycarbonate resin may be sufficient.

界面重縮合法による反応は、通常二価フェノールとホスゲンとの反応であり、酸結合剤および有機溶媒の存在下に反応させる。酸結合剤としては、例えば水酸化ナトリウム、水酸化カリウム等のアルカリ金属水酸化物またはピリジン等のアミン化合物が用いられる。有機溶媒としては、例えば塩化メチレン、クロロベンゼン等のハロゲン化炭化水素が用いられる。また、反応促進のために例えばトリエチルアミン、テトラ−ｎ−ブチルアンモニウムブロマイド、テトラ−ｎ−ブチルホスホニウムブロマイド等の第三級アミン、第四級アンモニウム化合物、第四級ホスホニウム化合物等の触媒を用いることもできる。その際、反応温度は通常０〜４０℃、反応時間は１０分〜５時間程度、反応中のｐＨは９以上に保つのが好ましい。また、かかる重合反応において、通常末端停止剤（一価フェノール）が使用される。かかる末端停止剤として単官能フェノール類を使用することができる。単官能フェノール類は末端停止剤として分子量調節のために一般的に使用され、かかる単官能フェノール類としては、一般にはフェノールまたは低級アルキル置換フェノールであって、下記一般式（１）で表される単官能フェノール類を示すことができる。   The reaction by the interfacial polycondensation method is usually a reaction between a dihydric phenol and phosgene, and is reacted in the presence of an acid binder and an organic solvent. As the acid binder, for example, an alkali metal hydroxide such as sodium hydroxide or potassium hydroxide or an amine compound such as pyridine is used. As the organic solvent, for example, halogenated hydrocarbons such as methylene chloride and chlorobenzene are used. In order to accelerate the reaction, a catalyst such as a tertiary amine such as triethylamine, tetra-n-butylammonium bromide or tetra-n-butylphosphonium bromide, a quaternary ammonium compound or a quaternary phosphonium compound may be used. it can. At that time, the reaction temperature is usually 0 to 40 ° C., the reaction time is preferably about 10 minutes to 5 hours, and the pH during the reaction is preferably maintained at 9 or more. In this polymerization reaction, a terminal stopper (monohydric phenol) is usually used. Monofunctional phenols can be used as such end terminators. Monofunctional phenols are generally used as end terminators for molecular weight control. Such monofunctional phenols are generally phenols or lower alkyl-substituted phenols represented by the following general formula (1). Monofunctional phenols can be indicated.

Figure 2011099030
（式中、Ａは水素原子または炭素数１〜９の直鎖または分岐のアルキル基あるいはフェニル基置換アルキル基であり、ｒは１〜５、好ましくは１〜３の整数である。）
Figure 2011099030
 (In the formula, A is a hydrogen atom, a linear or branched alkyl group having 1 to 9 carbon atoms or a phenyl group-substituted alkyl group, and r is an integer of 1 to 5, preferably 1 to 3.)

上記単官能フェノール類の具体例としては、例えばフェノール、ｐ−ｔｅｒｔ−ブチルフェノール、ｐ−クミルフェノールおよびイソオクチルフェノールが挙げられる。
また、他の単官能フェノール類としては、長鎖のアルキル基あるいは脂肪族ポリエステル基を置換基として有するフェノール類または安息香酸クロライド類、もしくは長鎖のアルキルカルボン酸クロライド類も示すことができる。これらのなかでは、下記一般式（２）および（３）で表される長鎖のアルキル基を置換基として有するフェノール類が好ましく使用される。 Specific examples of the monofunctional phenols include phenol, p-tert-butylphenol, p-cumylphenol and isooctylphenol.
In addition, as other monofunctional phenols, phenols or benzoic acid chlorides having a long chain alkyl group or an aliphatic polyester group as a substituent, or long chain alkyl carboxylic acid chlorides can also be shown. Among these, phenols having a long-chain alkyl group represented by the following general formulas (2) and (3) as a substituent are preferably used.

Figure 2011099030
Figure 2011099030
 （式中、Ｘは−Ｒ−Ｏ−、−Ｒ−ＣＯ−Ｏ−または−Ｒ−Ｏ−ＣＯ−である、ここでＲは単結合または炭素数１〜１０、好ましくは１〜５の二価の脂肪族炭化水素基を示し、ｎは１０〜５０の整数を示す。）
Figure 2011099030
Figure 2011099030
 Wherein X is —R—O—, —R—CO—O— or —R—O—CO—, wherein R is a single bond or a carbon number of 1 to 10, preferably 1 to 5; A valent aliphatic hydrocarbon group, and n represents an integer of 10 to 50.)

かかる一般式（２）の置換フェノール類としてはｎが１０〜３０、特に１０〜２６のものが好ましく、その具体例としては例えばデシルフェノール、ドデシルフェノール、テトラデシルフェノール、ヘキサデシルフェノール、オクタデシルフェノール、エイコシルフェノール、ドコシルフェノールおよびトリアコンチルフェノール等を挙げることができる。   As the substituted phenols of the general formula (2), those having n of 10 to 30, particularly 10 to 26 are preferable, and specific examples thereof include decylphenol, dodecylphenol, tetradecylphenol, hexadecylphenol, octadecylphenol, Examples include eicosylphenol, docosylphenol, and triacontylphenol.

また、一般式（３）の置換フェノール類としてはＸが−Ｒ−ＣＯ−Ｏ−であり、Ｒが単結合である化合物が適当であり、ｎが１０〜３０、特に１０〜２６のものが好適であって、その具体例としては例えばヒドロキシ安息香酸デシル、ヒドロキシ安息香酸ドデシル、ヒドロキシ安息香酸テトラデシル、ヒドロキシ安息香酸ヘキサデシル、ヒドロキシ安息香酸エイコシル、ヒドロキシ安息香酸ドコシルおよびヒドロキシ安息香酸トリアコンチルが挙げられる。また、末端停止剤は単独でまたは２種以上混合して使用してもよい。   Further, as the substituted phenols of the general formula (3), those in which X is —R—CO—O— and R is a single bond are suitable, and those in which n is 10 to 30, particularly 10 to 26. Specific examples thereof include, for example, decyl hydroxybenzoate, dodecyl hydroxybenzoate, tetradecyl hydroxybenzoate, hexadecyl hydroxybenzoate, eicosyl hydroxybenzoate, docosyl hydroxybenzoate and triacontyl hydroxybenzoate. Moreover, you may use a terminal terminator individually or in mixture of 2 or more types.

溶融エステル交換法による反応は、通常二価フェノールとカーボネートエステルとのエステル交換反応であり、不活性ガスの存在下に二価フェノールとカーボネートエステルとを加熱しながら混合して、生成するアルコールまたはフェノールを留出させる方法により行われる。反応温度は生成するアルコールまたはフェノールの沸点等により異なるが、通常１２０〜３５０℃の範囲である。反応後期には系を１．３３×１０３〜１３．３Ｐａ程度に減圧して生成するアルコールまたはフェノールの留出を容易にさせる。反応時間は通常１〜４時間程度である。 The reaction by the melt transesterification method is usually a transesterification reaction between a dihydric phenol and a carbonate ester, and the alcohol or phenol produced by mixing the dihydric phenol and the carbonate ester with heating in the presence of an inert gas. Is carried out by distilling the water. The reaction temperature varies depending on the boiling point of the alcohol or phenol produced, but is usually in the range of 120 to 350 ° C. In the latter stage of the reaction, the system is evacuated to about 1.33 × 10 3 to 13.3 Pa to facilitate the distillation of the alcohol or phenol produced. The reaction time is usually about 1 to 4 hours.

カーボネートエステルとしては、置換されていてもよい炭素数６〜１０のアリール基、アラルキル基あるいは炭素数１〜４のアルキル基などのエステルが挙げられる。具体的にはジフェニルカーボネート、ビス（クロロフェニル）カーボネート、ジナフチルカーボネート、ビス（ジフェニル）カーボネート、ジメチルカーボネート、ジエチルカーボネート、ジブチルカーボネートなどが挙げられ、なかでもジフェニルカーボネートが好ましい。   Examples of the carbonate ester include esters such as an optionally substituted aryl group having 6 to 10 carbon atoms, an aralkyl group, or an alkyl group having 1 to 4 carbon atoms. Specific examples include diphenyl carbonate, bis (chlorophenyl) carbonate, dinaphthyl carbonate, bis (diphenyl) carbonate, dimethyl carbonate, diethyl carbonate, and dibutyl carbonate. Among them, diphenyl carbonate is preferable.

また、重合速度を速めるために重合触媒を用いることができ、かかる重合触媒としては、例えば水酸化ナトリウム、水酸化カリウム、二価フェノールのナトリウム塩、カリウム塩等のアルカリ金属化合物、水酸化カルシウム、水酸化バリウム、水酸化マグネシウム等のアルカリ土類金属化合物、テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、トリメチルアミン、トリエチルアミン等の含窒素塩基性化合物、アルカリ金属やアルカリ土類金属のアルコキシド類、アルカリ金属やアルカリ土類金属の有機酸塩類、亜鉛化合物類、ホウ素化合物類、アルミニウム化合物類、珪素化合物類、ゲルマニウム化合物類、有機スズ化合物類、鉛化合物類、オスミウム化合物類、アンチモン化合物類マンガン化合物類、チタン化合物類、ジルコニウム化合物類などの通常エステル化反応、エステル交換反応に使用される触媒を用いることができる。触媒は単独で使用してもよいし、２種以上を組み合わせて使用してもよい。これらの重合触媒の使用量は、原料の二価フェノール１ｍｏｌに対し、好ましくは１×１０−８〜１×１０−３当量、より好ましくは１×１０−７〜５×１０−４当量の範囲で選ばれる。 A polymerization catalyst can be used to increase the polymerization rate. Examples of such polymerization catalyst include sodium hydroxide, potassium hydroxide, sodium salt of dihydric phenol, alkali metal compounds such as potassium salt, calcium hydroxide, Alkaline earth metal compounds such as barium hydroxide and magnesium hydroxide, nitrogen-containing basic compounds such as tetramethylammonium hydroxide, tetraethylammonium hydroxide, trimethylamine and triethylamine, alkoxides of alkali metals and alkaline earth metals, alkali metals And organic earth salts of alkaline earth metals, zinc compounds, boron compounds, aluminum compounds, silicon compounds, germanium compounds, organotin compounds, lead compounds, osmium compounds, antimony compounds manganese compounds, H Emission compounds, usually the esterification reaction, such as zirconium compounds, there can be used a catalyst used in the transesterification reaction. A catalyst may be used independently and may be used in combination of 2 or more type. The amount of these polymerization catalysts used is preferably in the range of 1 × 10 −8 to 1 × 10 −3 equivalent, more preferably 1 × 10 −7 to 5 × 10 −4 equivalent, relative to 1 mol of dihydric phenol as a raw material. Chosen by

また、かかる重合反応において、フェノール性の末端基を減少するために、重縮反応の後期あるいは終了後に、例えばビス（クロロフェニル）カーボネート、ビス（ブロモフェニル）カーボネート、ビス（ニトロフェニル）カーボネート、ビス（フェニルフェニル）カーボネート、クロロフェニルフェニルカーボネート、ブロモフェニルフェニルカーボネート、ニトロフェニルフェニルカーボネート、フェニルフェニルカーボネート、メトキシカルボニルフェニルフェニルカーボネートおよびエトキシカルボニルフェニルフェニルカーボネート等の化合物を加えることができる。なかでも２−クロロフェニルフェニルカーボネート、２−メトキシカルボニルフェニルフェニルカーボネートおよび２−エトキシカルボニルフェニルフェニルカーボネートが好ましく、特に２−メトキシカルボニルフェニルフェニルカーボネートが好ましく使用される。   In the polymerization reaction, in order to reduce phenolic end groups, for example, bis (chlorophenyl) carbonate, bis (bromophenyl) carbonate, bis (nitrophenyl) carbonate, bis ( Compounds such as phenylphenyl) carbonate, chlorophenylphenyl carbonate, bromophenylphenyl carbonate, nitrophenylphenyl carbonate, phenylphenyl carbonate, methoxycarbonylphenylphenyl carbonate and ethoxycarbonylphenylphenyl carbonate can be added. Of these, 2-chlorophenyl phenyl carbonate, 2-methoxycarbonylphenyl phenyl carbonate and 2-ethoxycarbonylphenyl phenyl carbonate are preferable, and 2-methoxycarbonylphenyl phenyl carbonate is particularly preferably used.

さらにかかる重合反応において触媒の活性を中和する失活剤を用いることが好ましい。この失活剤の具体例としては、例えばベンゼンスルホン酸、ｐ−トルエンスルホン酸、ベンゼンスルホン酸メチル、ベンゼンスルホン酸エチル、ベンゼンスルホン酸ブチル、ベンゼンスルホン酸オクチル、ベンゼンスルホン酸フェニル、ｐ−トルエンスルホン酸メチル、ｐ−トルエンスルホン酸エチル、ｐ−トルエンスルホン酸ブチル、ｐ−トルエンスルホン酸オクチル、ｐ−トルエンスルホン酸フェニルなどのスルホン酸エステル；さらに、トリフルオロメタンスルホン酸、ナフタレンスルホン酸、スルホン化ポリスチレン、アクリル酸メチル‐スルホン化スチレン共重合体、ドデシルベンゼンスルホン酸−２−フェニル−２−プロピル、ドデシルベンゼンスルホン酸−２−フェニル−２−ブチル、オクチルスルホン酸テトラブチルホスホニウム塩、デシルスルホン酸テトラブチルホスホニウム塩、ベンゼンスルホン酸テトラブチルホスホニウム塩、ドデシルベンゼンスルホン酸テトラエチルホスホニウム塩、ドデシルベンゼンスルホン酸テトラブチルホスホニウム塩、ドデシルベンゼンスルホン酸テトラヘキシルホスホニウム塩、ドデシルベンゼンスルホン酸テトラオクチルホスホニウム塩、デシルアンモニウムブチルサルフェート、デシルアンモニウムデシルサルフェート、ドデシルアンモニウムメチルサルフェート、ドデシルアンモニウムエチルサルフェート、ドデシルメチルアンモニウムメチルサルフェート、ドデシルジメチルアンモニウムテトラデシルサルフェート、テトラデシルジメチルアンモニウムメチルサルフェート、テトラメチルアンモニウムヘキシルサルフェート、デシルトリメチルアンモニウムヘキサデシルサルフェート、テトラブチルアンモニウムドデシルベンジルサルフェート、テトラエチルアンモニウムドデシルベンジルサルフェート、テトラメチルアンモニウムドデシルベンジルサルフェート等の化合物を挙げることができるが、これらに限定されない。これらの化合物を二種以上併用することもできる。   Furthermore, it is preferable to use a deactivator that neutralizes the activity of the catalyst in such a polymerization reaction. Specific examples of the deactivator include, for example, benzene sulfonic acid, p-toluene sulfonic acid, methyl benzene sulfonate, ethyl benzene sulfonate, butyl benzene sulfonate, octyl benzene sulfonate, phenyl benzene sulfonate, p-toluene sulfone. Sulfonic acid esters such as methyl acid, ethyl p-toluenesulfonate, butyl p-toluenesulfonate, octyl p-toluenesulfonate, phenyl p-toluenesulfonate; trifluoromethanesulfonic acid, naphthalenesulfonic acid, sulfonated polystyrene , Methyl acrylate-sulfonated styrene copolymer, dodecylbenzenesulfonate-2-phenyl-2-propyl, dodecylbenzenesulfonate-2-phenyl-2-butyl, octylsulfonate tetrabutylphospho Salts, tetrabutylphosphonium decylsulfonate, tetrabutylphosphonium benzenesulfonate, tetraethylphosphonium dodecylbenzenesulfonate, tetrabutylphosphonium dodecylbenzenesulfonate, tetrahexylphosphonium dodecylbenzenesulfonate, tetradecylbenzenesulfonate tetra Octyl phosphonium salt, decyl ammonium butyl sulfate, decyl ammonium decyl sulfate, dodecyl ammonium methyl sulfate, dodecyl ammonium ethyl sulfate, dodecyl methyl ammonium methyl sulfate, dodecyl dimethyl ammonium tetradecyl sulfate, tetradecyl dimethyl ammonium methyl sulfate, tetramethyl ammonium hexyl sulfate Over DOO, decyl trimethyl ammonium hexadecyl sulfate, tetrabutylammonium dodecylbenzyl sulfate, tetraethylammonium dodecylbenzyl sulfate, there may be mentioned compounds such as tetramethylammonium dodecylbenzyl sulfate, and the like. Two or more of these compounds can be used in combination.

失活剤の中でもホスホニウム塩もしくはアンモニウム塩型のものが好ましい。かかる失活剤の量としては、残存する触媒１ｍｏｌに対して０．５〜５０ｍｏｌの割合で用いるのが好ましく、また重合後のポリカーボネート樹脂に対し、０．０１〜５００ｐｐｍの割合、より好ましくは０．０１〜３００ｐｐｍ、特に好ましくは０．０１〜１００ｐｐｍの割合で使用する。   Among the quenching agents, those of phosphonium salt or ammonium salt type are preferred. The amount of the deactivator is preferably 0.5 to 50 mol with respect to 1 mol of the remaining catalyst, and 0.01 to 500 ppm, more preferably 0 with respect to the polycarbonate resin after polymerization. 0.01 to 300 ppm, particularly preferably 0.01 to 100 ppm.

Ａ−２成分の直鎖状芳香族ポリカーボネート樹脂の分子量は特定されないが、粘度平均分子量が１０，０００未満であると高温特性等が低下し、５０，０００を超えると成形加工性が低下するようになるので、粘度平均分子量が１０，０００〜５０，０００のものが好ましく、１６，０００〜３０，０００のものがより好ましく、さらに好ましくは１８，０００〜２８，０００、最も好ましくは１９，０００〜２６、０００である。また、直鎖状ポリカーボネート樹脂の２種以上を混合しても差し支えない。この場合、２種以上を混合した混合物の粘度平均分子量が好ましい範囲であれば、粘度平均分子量が上記範囲外であるポリカーボネート樹脂とを混合することも当然に可能である。   The molecular weight of the A-2 component linear aromatic polycarbonate resin is not specified, but if the viscosity average molecular weight is less than 10,000, the high-temperature characteristics and the like deteriorate, and if it exceeds 50,000, the moldability seems to decrease. Therefore, the viscosity average molecular weight is preferably 10,000 to 50,000, more preferably 16,000 to 30,000, still more preferably 18,000 to 28,000, and most preferably 19,000. ~ 26,000. Further, two or more kinds of linear polycarbonate resins may be mixed. In this case, as long as the viscosity average molecular weight of the mixture obtained by mixing two or more kinds is in a preferable range, it is naturally possible to mix with a polycarbonate resin having a viscosity average molecular weight outside the above range.

特に粘度平均分子量が５０，０００を超えるポリカーボネート樹脂との混合物はドリップ防止能が高く、本発明の効果をさらに効率的に発揮するため好ましいものである。より好ましくは粘度平均分子量が８０，０００以上のポリカーボネート樹脂との混合物であり、さらに好ましくは１００，０００以上の粘度平均分子量を有するポリカーボネート樹脂との混合物である。すなわちＧＰＣ（ゲルパーミエーションクロマトグラフィー）などの方法により明らかな２ピークの分布を有するものが好ましく使用できる。   In particular, a mixture with a polycarbonate resin having a viscosity average molecular weight exceeding 50,000 is preferable because it has a high anti-drip ability and exhibits the effect of the present invention more efficiently. More preferred is a mixture with a polycarbonate resin having a viscosity average molecular weight of 80,000 or more, and further preferred is a mixture with a polycarbonate resin having a viscosity average molecular weight of 100,000 or more. That is, those having a clear two-peak distribution by a method such as GPC (gel permeation chromatography) can be preferably used.

本発明のＡ−２成分である直鎖状芳香族ポリカーボネートは、上記芳香族ポリカーボネート樹脂であって、かつ実質的にハロゲン原子を含まないものであることが好ましい。実質的にハロゲン原子を含まないとは、分子中にハロゲン置換二価フェノールなどを含まないことを示し、上記芳香族ポリカーボネートの製造方法において残留する微量の塩素系溶媒、カーボネート前駆体他までも対象とするものではない。   The linear aromatic polycarbonate which is the component A-2 of the present invention is preferably the above aromatic polycarbonate resin and substantially free of halogen atoms. “Substantially free of halogen atoms” means that the molecule does not contain halogen-substituted dihydric phenols, etc., and includes trace amounts of chlorinated solvents, carbonate precursors, etc. remaining in the above aromatic polycarbonate production method. It is not something to do.

＜Ｂ成分：難燃剤＞
本発明のＢ成分として使用される難燃剤としてはリン系難燃剤、有機アルカリ（土類）金属塩等の有機金属塩系難燃剤、シリコーン系難燃剤、ホスファゼン系難燃剤等が例示されるが、その中でも有機アルカリ（土類）金属塩および芳香族基を有するシリコーン化合物からなる群より選択される少なくとも１種の難燃剤が好ましく使用される。Ｂ成分の含有量はＡ成分１００重量部に対して０．００５〜５重量部であり、好ましくは０．０１〜４重量部であり、より好ましくは０．１０〜３．５重量部であり、さらに好ましくは０．１５〜３重量部である。含有量が０．００５未満の場合、十分な難燃性が得られず、５重量部を超える場合十分な機械物性が得られなくなる。 <B component: flame retardant>
Examples of the flame retardant used as the component B of the present invention include phosphorus flame retardants, organic metal salt flame retardants such as organic alkali (earth) metal salts, silicone flame retardants, and phosphazene flame retardants. Of these, at least one flame retardant selected from the group consisting of organic alkali (earth) metal salts and silicone compounds having an aromatic group is preferably used. Content of B component is 0.005-5 weight part with respect to 100 weight part of A component, Preferably it is 0.01-4 weight part, More preferably, it is 0.10-3.5 weight part More preferably, it is 0.15 to 3 parts by weight. When the content is less than 0.005, sufficient flame retardancy cannot be obtained, and when it exceeds 5 parts by weight, sufficient mechanical properties cannot be obtained.

＜Ｂ−１成分：有機アルカリ（土類）金属塩＞
本発明のＢ−１成分として使用される有機アルカリ（土類）金属塩としては、従来ポリカーボネート樹脂を難燃化するのに使用されている各種の金属塩が使用可能であるが、特に有機スルホン酸のアルカリ（土類）金属塩、芳香族系イミドのアルカリ（土類）金属塩、硫酸エステルのアルカリ（土類）金属塩、およびリン酸部分エステルのアルカリ（土類）金属塩を挙げることができる。（ここで、アルカリ（土類）金属塩の表記は、アルカリ金属塩、アルカリ土類金属塩のいずれも含む意味で使用する）これらは単独の使用だけでなく、２種以上を混合して使用することも可能である。なお、有機アルカリ（土類）金属塩を構成する金属は、アルカリ金属あるいはアルカリ土類金属であり、より好適にはアルカリ金属である。アルカリ金属としては、リチウム、ナトリウム、カリウム、ルビジウム、セシウムが挙げられ、アルカリ土類金属としては、ベリリウム、マグネシウム、カルシウム、ストロンチウム、バリウムが挙げられ、特に好ましくはリチウム、ナトリウム、カリウムである。 <B-1 component: Organic alkali (earth) metal salt>
As the organic alkali (earth) metal salt used as the B-1 component of the present invention, various metal salts conventionally used for flame-retarding polycarbonate resins can be used. List alkali (earth) metal salts of acids, alkali (earth) metal salts of aromatic imides, alkali (earth) metal salts of sulfate esters, and alkali (earth) metal salts of phosphoric acid partial esters Can do. (Here, the notation of alkali (earth) metal salt is used to include both alkali metal salts and alkaline earth metal salts). These are not only used alone but also used in combination of two or more. It is also possible to do. The metal constituting the organic alkali (earth) metal salt is an alkali metal or an alkaline earth metal, and more preferably an alkali metal. Examples of the alkali metal include lithium, sodium, potassium, rubidium, and cesium, and examples of the alkaline earth metal include beryllium, magnesium, calcium, strontium, and barium, and lithium, sodium, and potassium are particularly preferable.

前記有機スルホン酸のアルカリ（土類）金属塩としては、脂肪族スルホン酸のアルカリ（土類）金属塩、芳香族スルホン酸のアルカリ（土類）金属塩等が挙げられる。
かかる脂肪族スルホン酸のアルカリ（土類）金属塩の好ましい例としては、アルキルスルホン酸アルカリ（土類）金属塩、かかるアルキルスルホン酸アルカリ（土類）金属塩のアルキル基の一部がフッ素原子で置換したスルホン酸アルカリ（土類）金属塩、およびパーフルオロアルキルスルホン酸アルカリ（土類）金属塩を挙げることができ、これらは１種もしくは２種以上を併用して使用することができる。 Examples of the alkali (earth) metal salt of the organic sulfonic acid include an alkali (earth) metal salt of an aliphatic sulfonic acid and an alkali (earth) metal salt of an aromatic sulfonic acid.
Preferred examples of the alkali (earth) metal salt of the aliphatic sulfonic acid include an alkali (earth) metal salt of an alkyl sulfonate, and a part of the alkyl group of the alkali (earth) metal salt of the alkyl sulfonate is a fluorine atom. And alkali (earth) metal salts of sulfonates substituted with, and alkali (earth) metal salts of perfluoroalkyl sulfonates, and these can be used alone or in combination of two or more.

アルキルスルホン酸アルカリ（土類）金属塩の好ましい例としては、メタンスルホン酸塩、エタンスルホン酸塩、プロパンスルホン酸塩、ブタンスルホン酸塩、メチルブタンスルホン酸塩、ヘキサンスルホン酸塩、へプタンスルホン酸塩、オクタンスルホン酸塩等が挙げられ、これらは１種もしくは２種以上を併用して使用することができる。またかかるアルキル基の一部がフッ素原子で置換した金属塩も挙げることができる。   Preferred examples of the alkali (earth) metal salt of alkyl sulfonate include methane sulfonate, ethane sulfonate, propane sulfonate, butane sulfonate, methyl butane sulfonate, hexane sulfonate, heptane sulfone. Examples thereof include acid salts and octane sulfonates, and these can be used alone or in combination of two or more. In addition, a metal salt in which a part of the alkyl group is substituted with a fluorine atom can also be mentioned.

一方、パーフルオロアルキルスルホン酸アルカリ（土類）金属塩の好ましい例としては、パーフルオロメタンスルホン酸塩、パーフルオロエタンスルホン酸塩、パーフルオロプロパンスルホン酸塩、パーフルオロブタンスルホン酸塩、パーフルオロメチルブタンスルホン酸塩、パーフルオロヘキサンスルホン酸塩、パーフルオロヘプタンスルホン酸塩、パーフルオロオクタンスルホン酸塩等が挙げられ、特に炭素数が１〜８のものが好ましい。これらは１種もしくは２種以上を併用して使用することができる。   On the other hand, preferred examples of alkali (earth) metal salts of perfluoroalkyl sulfonate include perfluoromethane sulfonate, perfluoroethane sulfonate, perfluoropropane sulfonate, perfluorobutane sulfonate, perfluoro Examples include methylbutane sulfonate, perfluorohexane sulfonate, perfluoroheptane sulfonate, and perfluorooctane sulfonate, and those having 1 to 8 carbon atoms are particularly preferable. These can be used alone or in combination of two or more.

この中で最も好ましいのはパーフルオロアルキルスルホン酸アルカリ金属塩である。かかるアルカリ金属の中でも、難燃性の要求がより高い場合にはルビジウムおよびセシウムが好適である一方、これらは汎用的でなくまた精製もし難いことから、結果的にコストの点で不利となる場合がある。一方、コストの点で有利であるがリチウムおよびナトリウムは逆に難燃性の点で不利な場合がある。これらを勘案してパーフルオロアルキルスルホン酸アルカリ金属塩中のアルカリ金属を使い分けることができるが、いずれの点においても特性のバランスに優れたパーフルオロアルキルスルホン酸カリウム塩が最も好適である。かかるカリウム塩と他のアルカリ金属からなるパーフルオロアルキルスルホン酸アルカリ金属塩とを併用することもできる。   Of these, the alkali metal salt of perfluoroalkylsulfonic acid is most preferable. Among these alkali metals, rubidium and cesium are suitable when the demand for flame retardancy is higher, but these are not versatile and difficult to purify, resulting in disadvantages in terms of cost. There is. On the other hand, although it is advantageous in terms of cost, lithium and sodium may be disadvantageous in terms of flame retardancy. In consideration of these, the alkali metal in the perfluoroalkylsulfonic acid alkali metal salt can be properly used, but perfluoroalkylsulfonic acid potassium salt having an excellent balance of properties is most suitable in any respect. Such potassium salts and alkali metal salts of perfluoroalkylsulfonic acid composed of other alkali metals can be used in combination.

パーフルオロアルキルスルホン酸アルカリ金属塩の具体例としては、トリフルオロメタンスルホン酸カリウム、パーフルオロブタンスルホン酸カリウム、パーフルオロヘキサンスルホン酸カリウム、パーフルオロオクタンスルホン酸カリウム、ペンタフルオロエタンスルホン酸ナトリウム、パーフルオロブタンスルホン酸ナトリウム、パーフルオロオクタンスルホン酸ナトリウム、トリフルオロメタンスルホン酸リチウム、パーフルオロブタンスルホン酸リチウム、パーフルオロヘプタンスルホン酸リチウム、トリフルオロメタンスルホン酸セシウム、パーフルオロブタンスルホン酸セシウム、パーフルオロオクタンスルホン酸セシウム、パーフルオロヘキサンスルホン酸セシウム、パーフルオロブタンスルホン酸ルビジウム、およびパーフルオロヘキサンスルホン酸ルビジウム等が挙げられ、これらは１種もしくは２種以上を併用して使用することができる。これらの中で特にパーフルオロブタンスルホン酸カリウムが好ましい。   Specific examples of alkali metal perfluoroalkyl sulfonates include potassium trifluoromethane sulfonate, potassium perfluorobutane sulfonate, potassium perfluorohexane sulfonate, potassium perfluorooctane sulfonate, sodium pentafluoroethane sulfonate, perfluoro Sodium butanesulfonate, sodium perfluorooctanesulfonate, lithium trifluoromethanesulfonate, lithium perfluorobutanesulfonate, lithium perfluoroheptanesulfonate, cesium trifluoromethanesulfonate, cesium perfluorobutanesulfonate, perfluorooctanesulfonate Cesium, cesium perfluorohexane sulfonate, rubidium perfluorobutane sulfonate, and perf Oro hexane sulfonate rubidium, and these may be used in combination of at least one or two. Of these, potassium perfluorobutanesulfonate is particularly preferred.

芳香族スルホン酸アルカリ（土類）金属塩に使用する芳香族スルホン酸としては、モノマー状またはポリマー状の芳香族サルファイドのスルホン酸、芳香族カルボン酸およびエステルのスルホン酸、モノマー状またはポリマー状の芳香族エーテルのスルホン酸、芳香族スルホネートのスルホン酸、モノマー状またはポリマー状の芳香族スルホン酸、モノマー状またはポリマー状の芳香族スルホンスルホン酸、芳香族ケトンのスルホン酸、複素環式スルホン酸、芳香族スルホキサイドのスルホン酸、芳香族スルホン酸のメチレン型結合による縮合体からなる群から選ばれた少なくとも１種の酸を挙げることができ、これらは１種もしくは２種以上を併用して使用することができる。   The aromatic sulfonic acid used in the aromatic (earth) metal salt of aromatic sulfonate includes monomeric or polymeric aromatic sulfide sulfonic acid, aromatic carboxylic acid and ester sulfonic acid, monomeric or polymeric sulfonic acid. Aromatic ether sulfonic acid, aromatic sulfonate sulfonic acid, monomeric or polymeric aromatic sulfonic acid, monomeric or polymeric aromatic sulfonic acid, aromatic ketone sulfonic acid, heterocyclic sulfonic acid, Examples include at least one acid selected from the group consisting of sulfonic acids of aromatic sulfoxides and condensates of methylene type bonds of aromatic sulfonic acids, and these are used alone or in combination of two or more. be able to.

モノマー状またはポリマー状の芳香族サルファイドのスルホン酸アルカリ（土類）金属塩としては、特開昭５０−９８５３９号公報に記載されており、例えば、ジフェニルサルファイド−４，４’−ジスルホン酸ジナトリウム、ジフェニルサルファイド−４，４’−ジスルホン酸ジカリウムなどを挙げることができる。   Monomer or polymer aromatic sulfite alkali (earth) metal salts of aromatic sulfides are described in JP-A-50-98539, for example, disodium diphenyl sulfide-4,4′-disulfonate. And dipotassium diphenyl sulfide-4,4′-disulfonate.

芳香族カルボン酸およびエステルのスルホン酸アルカリ（土類）金属塩としては、特開昭５０−９８５４０号公報に記載されており、例えば５−スルホイソフタル酸カリウム、５−スルホイソフタル酸ナトリウム、ポリエチレンテレフタル酸ポリスルホン酸ポリナトリウムなどを挙げることができる。   Examples of sulfonic acid alkali (earth) metal salts of aromatic carboxylic acids and esters are described in JP-A No. 50-98540, for example, potassium 5-sulfoisophthalate, sodium 5-sulfoisophthalate, polyethylene terephthalate. And polysodium acid polysulfonate.

モノマー状またはポリマー状の芳香族エーテルのスルホン酸アルカリ（土類）金属塩としては、特開昭５０−９８５４２号公報に記載されており、例えば１−メトキシナフタレン−４−スルホン酸カルシウム、４−ドデシルフェニルエーテルジスルホン酸ジナトリウム、ポリ（２，６−ジメチルフェニレンオキシド）ポリスルホン酸ポリナトリウム、ポリ（１，３−フェニレンオキシド）ポリスルホン酸ポリナトリウム、ポリ（１，４−フェニレンオキシド）ポリスルホン酸ポリナトリウム、ポリ（２，６−ジフェニルフェニレンオキシド）ポリスルホン酸ポリカリウム、ポリ（２−フルオロ−６−ブチルフェニレンオキシド）ポリスルホン酸リチウムなどを挙げることができる。   Monomeric or polymeric aromatic ether sulfonate alkali (earth) metal salts are described in JP-A-50-98542, for example, 1-methoxynaphthalene-4-sulfonate calcium, 4- Disodium dodecylphenyl ether disulfonate, polysodium poly (2,6-dimethylphenylene oxide) polysulfonate, polysodium poly (1,3-phenylene oxide) polysulfonate, polysodium poly (1,4-phenylene oxide) polysulfonate And poly (2,6-diphenylphenylene oxide) polypotassium polysulfonate, poly (2-fluoro-6-butylphenylene oxide) lithium polysulfonate, and the like.

芳香族スルホネートのスルホン酸アルカリ（土類）金属塩としては、特開昭５０−９８５４４号公報に記載されており、例えばベンゼンスルホネートのスルホン酸カリウムなどを挙げることができる。   Examples of alkali (earth) metal sulfonates of aromatic sulfonates are described in JP-A No. 50-98544, and examples thereof include potassium sulfonate of benzene sulfonate.

モノマー状またはポリマー状の芳香族スルホン酸アルカリ（土類）金属塩としては、特開昭５０−９８５４６号公報に記載されており、例えばベンゼンスルホン酸ナトリウム、ベンゼンスルホン酸ストロンチウム、ベンゼンスルホン酸マグネシウム、ｐ−ベンゼンジスルホン酸ジカリウム、ナフタレン−２，６−ジスルホン酸ジカリウム、ビフェニル−３，３’−ジスルホン酸カルシウムなどを挙げることができる。   Monomeric or polymeric aromatic (earth) metal sulfonates are described in JP-A No. 50-98546, for example, sodium benzenesulfonate, strontium benzenesulfonate, magnesium benzenesulfonate, Examples include dipotassium p-benzenedisulfonate, dipotassium naphthalene-2,6-disulfonate, and calcium biphenyl-3,3′-disulfonate.

モノマー状またはポリマー状の芳香族スルホンスルホン酸アルカリ（土類）金属塩としては、特開昭５２−５４７４６号公報に記載されており、例えばジフェニルスルホン−３−スルホン酸ナトリウム、ジフェニルスルホン−３−スルホン酸カリウム、ジフェニルスルホン−３，３’−ジスルホン酸ジカリウム、ジフェニルスルホン−３，４’−ジスルホン酸ジカリウムなどを挙げることができる。   Monomeric or polymeric aromatic sulfonesulfonic acid alkali (earth) metal salts are described in JP-A-52-54746, for example, sodium diphenylsulfone-3-sulfonate, diphenylsulfone-3- Examples include potassium sulfonate, dipotassium diphenyl-3,3′-disulfonate, dipotassium diphenylsulfone-3,4′-disulfonate, and the like.

芳香族ケトンのスルホン酸アルカリ（土類）金属塩としては、特開昭５０−９８５４７号公報に記載されており、例えばα，α，α−トリフルオロアセトフェノン−４−スルホン酸ナトリウム、ベンゾフェノン−３，３’−ジスルホン酸ジカリウムなどを挙げることができる。   Examples of alkali sulfonate alkali (earth) metal salts of aromatic ketones are described in JP-A No. 50-98547, for example, α, α, α-trifluoroacetophenone-4-sulfonic acid sodium salt, benzophenone-3 , 3'-disulfonic acid dipotassium.

複素環式スルホン酸アルカリ（土類）金属塩としては、特開昭５０−１１６５４２号公報に記載されており、例えばチオフェン−２，５−ジスルホン酸ジナトリウム、チオフェン−２，５−ジスルホン酸ジカリウム、チオフェン−２，５−ジスルホン酸カルシウム、ベンゾチオフェンスルホン酸ナトリウムなどを挙げることができる。   Heterocyclic sulfonic acid alkali (earth) metal salts are described in JP-A-50-116542, for example, disodium thiophene-2,5-disulfonate, dipotassium thiophene-2,5-disulfonate. Thiophene-2,5-disulfonate calcium, sodium benzothiophenesulfonate, and the like.

芳香族スルホキサイドのスルホン酸アルカリ（土類）金属塩としては、特開昭５２−５４７４５号公報に記載されており、例えばジフェニルスルホキサイド−４−スルホン酸カリウムなどを挙げることができる。   Examples of the alkali (earth) metal sulfonate of aromatic sulfoxide are described in JP-A-52-54745, and examples thereof include potassium diphenyl sulfoxide-4-sulfonate.

芳香族スルホン酸アルカリ（土類）金属塩のメチレン型結合による縮合体としては、ナフタレンスルホン酸ナトリウムのホルマリン縮合物、アントラセンスルホン酸ナトリウムのホルマリン縮合物などを挙げることができる。   Examples of the condensate obtained by methylene bond of alkali (earth) metal salt of aromatic sulfonate include formalin condensate of sodium naphthalene sulfonate and formalin condensate of sodium anthracene sulfonate.

前記、硫酸エステルのアルカリ（土類）金属塩としては、特に一価および／または多価アルコール類の硫酸エステルのアルカリ（土類）金属塩を挙げることができ、かかる一価および／または多価アルコール類の硫酸エステルとしては、メチル硫酸エステル、エチル硫酸エステル、ラウリル硫酸エステル、ヘキサデシル硫酸エステル、ポリオキシエチレンアルキルフェニルエーテルの硫酸エステル、ペンタエリスリトールのモノ、ジ、トリ、テトラ硫酸エステル、ラウリン酸モノグリセライドの硫酸エステル、パルミチン酸モノグリセライドの硫酸エステル、ステアリン酸モノグリセライドの硫酸エステルなどを挙げることができる。これらの硫酸エステルのアルカリ（土類）金属塩として好ましくはラウリル硫酸エステルのアルカリ（土類）金属塩を挙げることができる。   Examples of the alkali (earth) metal salt of the sulfate ester include, in particular, alkali (earth) metal salts of sulfate esters of monovalent and / or polyhydric alcohols. Alcohol sulfates include methyl sulfate, ethyl sulfate, lauryl sulfate, hexadecyl sulfate, polyoxyethylene alkylphenyl ether sulfate, pentaerythritol mono, di, tri, tetrasulfate, and lauric acid monoglyceride. And sulfuric acid ester of palmitic acid monoglyceride, stearic acid monoglyceride sulfate and the like. The alkali (earth) metal salts of these sulfates are preferably alkali (earth) metal salts of lauryl sulfate.

前記リン酸部分エステルのアルカリ（土類）金属塩としては、具体的にビス（２，６−ジブロモ−４−クミルフェニル）リン酸、ビス（４−クミルフェニル）リン酸、ビス（２，４，６−トリブロモフェニル）リン酸ビス（２，４−ジブロモフェニル）リン酸、ビス（４−ブロモフェニル）リン酸、ジフェニルリン酸、ビス（４−ｔｅｒｔ−ブチルフェニル）リン酸等のアルカリ（土類）金属塩を挙げることができる。   Specific examples of the alkali (earth) metal salt of the phosphoric acid partial ester include bis (2,6-dibromo-4-cumylphenyl) phosphoric acid, bis (4-cumylphenyl) phosphoric acid, and bis (2,4,6). Alkali (earth) such as bis (2,4-dibromophenyl) phosphoric acid, bis (4-bromophenyl) phosphoric acid, diphenylphosphoric acid, bis (4-tert-butylphenyl) phosphoric acid ) Metal salts can be mentioned.

前記芳香族系イミドのアルカリ（土類）金属塩としては、例えばサッカリン、Ｎ−（ｐ−トリルスルホニル）−ｐ−トルエンスルホンアミド（言い換えるとジ（ｐ−トルエンスルホン）イミド）、Ｎ−（Ｎ’−ベンジルアミノカルボニル）スルファニルイミド、およびＮ−（フェニルカルボキシル）スルファニルイミド、ビス（ジフェニルリン酸）イミド等のアルカリ（土類）金属塩などが挙げられる。   Examples of the alkali (earth) metal salt of the aromatic imide include saccharin, N- (p-tolylsulfonyl) -p-toluenesulfonamide (in other words, di (p-toluenesulfone) imide), N- (N Examples include '-benzylaminocarbonyl) sulfanilimide, and alkali (earth) metal salts such as N- (phenylcarboxyl) sulfanilimide and bis (diphenylphosphoric acid) imide.

これらの中で好ましい成分としてパーフルオロアルキルスルホン酸アルカリ（土類）金属塩、芳香族スルホン酸アルカリ（土類）金属塩、および芳香族系イミドのアルカリ（土類）金属塩からなる群より選択される１種以上の化合物が挙げられ、その中でもパーフルオロブタンスルホン酸カリウム、パーフルオロブタンスルホン酸ナトリウム、式（４）で示されるジフェニルスルホンのスルホン酸塩、ジ（ｐ−トルエンスルホン）イミドのカリウム塩、および、ジ（ｐ−トルエンスルホン）イミドのナトリウム塩からなる群より選択される１種以上の化合物がより好ましい。さらに最も好ましくはパーフルオロブタンスルホン酸カリウムである。   Among these, preferable components are selected from the group consisting of alkali (earth) metal salts of perfluoroalkyl sulfonates, alkali (earth) metal aromatic sulfonates, and alkali (earth) metal salts of aromatic imides. Among them, potassium perfluorobutanesulfonate, sodium perfluorobutanesulfonate, diphenylsulfone sulfonate represented by the formula (4), di (p-toluenesulfone) imide One or more compounds selected from the group consisting of potassium salt and sodium salt of di (p-toluenesulfone) imide are more preferred. Most preferred is potassium perfluorobutane sulfonate.

Figure 2011099030
［式中、ｎは０〜３を表し、ＭはＫあるいはＮａを表す。］
Figure 2011099030
 [Wherein n represents 0 to 3, and M represents K or Na. ]

本発明の樹脂組成物に含有されるＢ−１成分の量は芳香族ポリカーボネート樹脂（Ａ成分）１００重量部に対して、０．００５〜１．０重量部が好ましく、より好ましくは０．００６〜０．３重量部であり、さらに好ましくは０．００７〜０．１重量部であり、さらにより好ましくは０．００８〜０．０５重量部、最も好ましくは０．０１〜０．０２５重量部である。Ｂ−１成分の含有量が多すぎると本発明の特徴である透明性が損なわれるだけでなく、場合によっては成形時に樹脂が分解して逆に難燃性が低下する方向となる。添加量が少なすぎると難燃性が不十分となり本発明の目的である難燃性が発揮されない。   The amount of the B-1 component contained in the resin composition of the present invention is preferably 0.005 to 1.0 part by weight, more preferably 0.006, per 100 parts by weight of the aromatic polycarbonate resin (component A). To 0.3 parts by weight, more preferably 0.007 to 0.1 parts by weight, even more preferably 0.008 to 0.05 parts by weight, and most preferably 0.01 to 0.025 parts by weight. It is. When there is too much content of B-1 component, not only transparency which is the characteristics of this invention will be impaired, but depending on the case, resin will decompose | disassemble at the time of shaping | molding and it will become the direction where flame retardance conversely falls. If the addition amount is too small, the flame retardancy becomes insufficient and the flame retardancy that is the object of the present invention is not exhibited.

＜Ｂ−２成分：シリコーン化合物＞
本発明のＢ−２成分として使用されるシリコーン化合物は本発明の目的である難燃性や透明性を得ることができれば特に限定されないが、芳香族基を有するシリコーン化合物が好ましく、さらに２５℃における粘度が３００ｃＳｔ以下が好ましい。粘度が高くなると成形品の透明性が低下する。さらにＢ成分のシリコーン化合物が効率的に難燃効果を発揮するためには、燃焼過程における分散状態が重要である。かかる分散状態を決定する重要な因子として粘度が挙げられる。これは、燃焼過程においてシリコーン化合物があまりにも揮発しやすい場合、すなわち、粘度が低すぎるシリコーン化合物の場合には、燃焼時に系内に残っているシリコーンが希薄であるため、燃焼時に均一なシリコーンのストラクチャーを形成することが困難となるためと考えられるかかる観点より、２５℃における粘度は１０〜３００ｃＳｔがより好ましく、さらに好ましくは１５〜２００ｃＳｔ、最も好ましくは２０〜１７０ｃＳｔである。 <B-2 component: silicone compound>
The silicone compound used as the B-2 component of the present invention is not particularly limited as long as the flame retardancy and transparency as the object of the present invention can be obtained, but a silicone compound having an aromatic group is preferable, and further at 25 ° C. The viscosity is preferably 300 cSt or less. As the viscosity increases, the transparency of the molded product decreases. Further, in order for the B component silicone compound to effectively exhibit a flame retardant effect, the dispersed state in the combustion process is important. Viscosity is an important factor that determines the dispersion state. This is because if the silicone compound is too volatile during the combustion process, that is, if the viscosity of the silicone compound is too low, the silicone remaining in the system at the time of combustion is dilute. From this viewpoint considered to be difficult to form a structure, the viscosity at 25 ° C. is more preferably 10 to 300 cSt, still more preferably 15 to 200 cSt, and most preferably 20 to 170 cSt.

Ｂ−２成分が有する芳香族基はシリコーン原子に結合しているものであり、ポリカーボネート樹脂との相溶性を高めたり透明性維持に寄与しており、燃焼時の炭化皮膜形成にも有利であることから難燃効果の発現にも寄与している。芳香族基を有しない場合は成形品の透明性が得られにくく、高度な難燃性を得ることも困難となる傾向がある。   The aromatic group of the B-2 component is bonded to the silicone atom, which improves compatibility with the polycarbonate resin and contributes to maintaining transparency, and is advantageous for forming a carbonized film during combustion. Therefore, it also contributes to the development of flame retardant effect. When it does not have an aromatic group, it tends to be difficult to obtain transparency of the molded product and to obtain high flame retardancy.

本発明のシリコーン化合物は好ましくはＳｉ−Ｈ基を含有するシリコーン化合物である。特に、分子中にＳｉ−Ｈ基および芳香族基を含有するシリコーン化合物であって、
（１）Ｓｉ−Ｈ基が含まれる量（Ｓｉ−Ｈ量）が０．１〜１．２ｍｏｌ／１００ｇ
（２）下記一般式（５）で示される芳香族基が含まれる割合（芳香族基量）が１０〜７０重量％、かつ

Figure 2011099030
（式（５）中、Ｘはそれぞれ独立にＯＨ基、ヘテロ原子含有官能基を有しても良い炭素数１〜２０の炭化水素基を示す。ｎは０〜５の整数を表わす。さらに式（５）中においてｎが２以上の場合はそれぞれ互いに異なる種類のＸを取ることができる。）
（３）平均重合度が３〜１５０
であるシリコーン化合物の中から選択される少なくとも一種以上のシリコーン化合物である。 The silicone compound of the present invention is preferably a silicone compound containing a Si-H group. In particular, a silicone compound containing a Si—H group and an aromatic group in the molecule,
(1) The amount of Si—H group contained (Si—H amount) is 0.1 to 1.2 mol / 100 g.
(2) The ratio (aromatic group amount) in which the aromatic group represented by the following general formula (5) is contained is 10 to 70% by weight, and
Figure 2011099030
 (In formula (5), each X independently represents an OH group or a hydrocarbon group having 1 to 20 carbon atoms which may have a hetero atom-containing functional group. N represents an integer of 0 to 5. (5) In the case where n is 2 or more, different types of X can be taken.
(3) Average polymerization degree is 3 to 150
And at least one silicone compound selected from silicone compounds.

さらに好ましくは、Ｓｉ−Ｈ基含有単位として、下記一般式（６）および（７）で示される構成単位のうち、少なくとも一種以上の式で示される構成単位を含むシリコーン化合物の中から選択される少なくとも一種以上のシリコーン化合物である。   More preferably, the Si—H group-containing unit is selected from silicone compounds containing at least one constituent unit represented by the formula among the constituent units represented by the following general formulas (6) and (7). At least one silicone compound.

Figure 2011099030
Figure 2011099030
 （式（６）および式（７）中、Ｚ１〜Ｚ３はそれぞれ独立に水素原子、ヘテロ原子含有官能基を有しても良い炭素数１〜２０の炭化水素基、または下記一般式（８）で示される化合物を示す。α１〜α３はそれぞれ独立に０または１を表わす。ｍ１は０もしくは１以上の整数を表わす。さらに式（８）中においてｍ１が２以上の場合の繰返し単位はそれぞれ互いに異なる複数の繰返し単位を取ることができる。）
Figure 2011099030
Figure 2011099030
 (In Formula (6) and Formula (7), Z 1 to Z 3 are each independently a hydrogen atom, a hydrocarbon group having 1 to 20 carbon atoms which may have a hetero atom-containing functional group, or the following general formula ( 8) and α1 to α3 each independently represents 0 or 1. m1 represents 0 or an integer of 1 or more, and the repeating unit in the case where m1 is 2 or more in formula (8) (Several different repeating units can be taken.)

Figure 2011099030
（式（８）中、Ｚ４〜Ｚ８はそれぞれ独立に水素原子、ヘテロ原子含有官能基を有しても良い炭素数１〜２０の炭化水素基を示す。α４〜α８はそれぞれ独立に０または１を表わす。ｍ２は０もしくは１以上の整数を表わす。さらに式（８）中においてｍ２が２以上の場合の繰返し単位はそれぞれ互いに異なる複数の繰返し単位を取ることができる。）
Figure 2011099030
 (In formula (8), Z 4 to Z 8 each independently represent a hydrogen atom or a hydrocarbon group having 1 to 20 carbon atoms which may have a hetero atom-containing functional group. Α 4 to α 8 are each independently 0. Or represents 1. m2 represents 0 or an integer greater than or equal to 1. Further, in the formula (8), when m2 is 2 or more, the repeating unit may take a plurality of different repeating units.

より好ましくは、Ｍを１官能性シロキサン単位、Ｄを２官能性シロキサン単位、Ｔを３官能性シロキサン単位とするとき、ＭＤ単位またはＭＤＴ単位からなるシリコーン化合物である。   More preferably, when M is a monofunctional siloxane unit, D is a bifunctional siloxane unit, and T is a trifunctional siloxane unit, the silicone compound is composed of MD units or MDT units.

上記一般式（６）、（７）および（８）で示される構成単位のＺ１〜Ｚ８、および一般式（５）のＸにおけるヘテロ原子含有官能基を有しても良い炭素数１〜２０の炭化水素基としては、メチル基、エチル基、プロピル基、ブチル基、ヘキシル基、デシル基等のアルキル基、シクロヘキシル基等のシクロアルキル基、ビニル基、アリル基等のアルケニル基、フェニル基、トリル基等のアリール基およびアラルキル基を挙げることができ、さらにこれらの基はエポキシ基、カルボキシル基、無水カルボン酸基、アミノ基、およびメルカプト基などの各種官能基を含むものであってもよい。さらに好ましくは炭素数１〜８のアルキル基、アルケニル基またはアリール基であり、特にはメチル基、エチル基、プロピル基等の炭素数１〜４のアルキル基、ビニル基、またはフェニル基が好ましい。 Z 1 to Z 8 of the structural units represented by the general formulas (6), (7) and (8), and a hetero atom-containing functional group in X of the general formula (5) may have 1 to 1 carbon atoms. Examples of the hydrocarbon group 20 include an alkyl group such as a methyl group, an ethyl group, a propyl group, a butyl group, a hexyl group and a decyl group, a cycloalkyl group such as a cyclohexyl group, an alkenyl group such as a vinyl group and an allyl group, and a phenyl group. , Aryl groups such as tolyl groups, and aralkyl groups, and these groups may include various functional groups such as epoxy groups, carboxyl groups, carboxylic anhydride groups, amino groups, and mercapto groups. Good. More preferably, it is a C1-C8 alkyl group, an alkenyl group, or an aryl group, and especially a C1-C4 alkyl group, such as a methyl group, an ethyl group, and a propyl group, a vinyl group, or a phenyl group is preferable.

前記一般式（６）および（７）で示される構成単位のうち、少なくとも一種以上の式で示される構成単位を含むシリコーン化合物において、複数のシロキサン結合の繰返し単位を有する場合は、それらはランダム共重合、ブロック共重合、テーパード共重合のいずれの形態を取ることも可能である。   Among the structural units represented by the general formulas (6) and (7), when the silicone compound containing at least one structural unit represented by the formula has a plurality of repeating units of siloxane bonds, they are randomly shared. Any form of polymerization, block copolymerization and tapered copolymerization can be employed.

本発明においては、Ｂ−２成分で好ましいＳｉ−Ｈ基を含有するシリコーン化合物については、シリコーン化合物中のＳｉ−Ｈ量を０．１〜１．２ｍｏｌ／１００ｇの範囲とすることが好ましい。Ｓｉ−Ｈ量が０．１〜１．２ｍｏｌ／１００ｇの範囲にあることで、燃焼時にシリコーンのストラクチャーの形成が容易となる。さらに好ましくはＳｉ−Ｈ量が０．１〜１．０ｍｏｌ／１００ｇの範囲、最も好ましくは０．２〜０．６ｍｏｌ／１００ｇの範囲にあるシリコーン化合物である。Ｓｉ−Ｈ量が少ないとシリコーンのストラクチャー形成が困難となり、Ｓｉ−Ｈ量が多いと組成物の熱安定性が低下する。なお、ここでシリコーンのストラクチャーとは、シリコーン化合物相互の反応、または樹脂とシリコーンとの反応により生成する網状構造をさす。   In the present invention, it is preferable that the amount of Si—H in the silicone compound be in the range of 0.1 to 1.2 mol / 100 g for the silicone compound containing the Si—H group preferred as the B-2 component. When the Si—H amount is in the range of 0.1 to 1.2 mol / 100 g, formation of a silicone structure is facilitated during combustion. More preferred is a silicone compound having a Si-H amount in the range of 0.1 to 1.0 mol / 100 g, most preferably in the range of 0.2 to 0.6 mol / 100 g. When the amount of Si—H is small, it is difficult to form a silicone structure, and when the amount of Si—H is large, the thermal stability of the composition is lowered. Here, the silicone structure refers to a network structure formed by a reaction between silicone compounds or a reaction between a resin and silicone.

また、ここで言うＳｉ−Ｈ基量とは、シリコーン化合物１００ｇあたりに含まれるＳｉ−Ｈ構造のモル数を言うが、これはアルカリ分解法により、シリコーン化合物の単位重量当たり発生した水素ガスの体積を測定することにより求めることができる。例えば、２５℃においてシリコーン化合物１ｇ当たり１２２ｍｌの水素ガスが発生した場合、下記計算式により、Ｓｉ−Ｈ量は０．５ｍｏｌ／１００ｇとなる。
１２２×２７３／（２７３＋２５）÷２２４００×１００≒０．５ The Si—H group amount referred to here means the number of moles of the Si—H structure contained per 100 g of the silicone compound. This is the volume of hydrogen gas generated per unit weight of the silicone compound by the alkali decomposition method. Can be determined by measuring. For example, when 122 ml of hydrogen gas is generated per 1 g of the silicone compound at 25 ° C., the Si—H amount is 0.5 mol / 100 g according to the following formula.
122 × 273 / (273 + 25) ÷ 22400 × 100≈0.5

一方、芳香族ポリカーボネート樹脂（Ａ成分）にシリコーン化合物を配合した樹脂組成物において、成形品の白濁、あるいは湿熱処理による透明性の低下を抑えるためには、前述したとおり、シリコーン化合物の分散状態が重要である。シリコーン化合物が偏在する場合には、樹脂組成物自体が白濁し、さらには成形品表面で剥離などが生じたり、あるいは湿熱処理時にシリコーン化合物が移行して偏在して透明性が低下するなど、透明性の良好な成形品を得ることが困難となるためである。かかる分散状態を決定する重要な因子としてシリコーン化合物中の芳香族基量、平均重合度が挙げられる。殊に透明性の樹脂組成物において平均重合度は重要である。   On the other hand, in the resin composition in which the silicone compound is blended with the aromatic polycarbonate resin (component A), in order to suppress the white turbidity of the molded product or the decrease in transparency due to the wet heat treatment, as described above, the dispersion state of the silicone compound is is important. When the silicone compound is unevenly distributed, the resin composition itself becomes cloudy, and further, peeling occurs on the surface of the molded product, or the silicone compound migrates during the wet heat treatment and is unevenly distributed to reduce transparency. This is because it is difficult to obtain a molded article having good properties. Important factors that determine the dispersion state include the amount of aromatic groups in the silicone compound and the average degree of polymerization. In particular, the average degree of polymerization is important in a transparent resin composition.

かかる観点より、本発明のシリコーン化合物としては、シリコーン化合物中の芳香族基量は１０〜７０重量％であることが好ましい。さらに好ましくは芳香族基量が１５〜６０重量％の範囲、最も好ましくは２５〜５５重量％の範囲にあるシリコーン化合物である。シリコーン化合物中の芳香族基量が１０重量％より少ないとシリコーン化合物が偏在して分散不良となり、透明性が良好な成形品を得ることが困難となる場合がある。芳香族基量が７０重量％より多いとシリコーン化合物自体の分子の剛直性が高くなるためやはり偏在して分散不良となり、透明性が良好な成形品を得ることが困難となる場合がある。   From this viewpoint, the silicone compound of the present invention preferably has an aromatic group content of 10 to 70% by weight in the silicone compound. More preferred is a silicone compound having an aromatic group content in the range of 15 to 60% by weight, most preferably in the range of 25 to 55% by weight. If the amount of the aromatic group in the silicone compound is less than 10% by weight, the silicone compound is unevenly distributed, resulting in poor dispersion, and it may be difficult to obtain a molded article having good transparency. If the amount of the aromatic group is more than 70% by weight, the molecular rigidity of the silicone compound itself is increased, and therefore it is unevenly distributed and poorly dispersed, and it may be difficult to obtain a molded product with good transparency.

なお、ここで芳香族基量とは、シリコーン化合物において、前述した一般式（５）で示される芳香族基が含まれる割合のことを言い、下記計算式によって求めることができる。
芳香族基量＝〔Ａ／Ｍ〕×１００（重量％）
ここで、上記式におけるＡ、Ｍはそれぞれ以下の数値を表す。
Ａ＝シリコーン化合物１分子中に含まれる、全ての一般式（５）で示される芳香族基部分の合計分子量
Ｍ＝シリコーン化合物の分子量 Here, the amount of the aromatic group means a ratio of the aromatic group represented by the general formula (5) described above in the silicone compound, and can be determined by the following calculation formula.
Aromatic group amount = [A / M] x 100 (wt%)
Here, A and M in the above formula represent the following numerical values, respectively.
A = Total molecular weight of aromatic group moieties represented by the general formula (5) contained in one molecule of the silicone compound M = Molecular weight of the silicone compound

さらに本発明のＢ−２成分として使用されるシリコーン化合物は、２５℃における屈折率が１．４０〜１．６０の範囲にあることが望ましい。さらに好ましくは屈折率が１．４２〜１．５９の範囲であり、最も好ましくは、１．４４〜１．５９の範囲にあるシリコーン化合物である。屈折率が上記範囲内にある場合、芳香族ポリカーボネート中にシリコーン化合物が微分散することで、より白濁の少ない染色性の良好な樹脂組成物が提供される。   Further, the silicone compound used as the B-2 component of the present invention preferably has a refractive index at 25 ° C. in the range of 1.40 to 1.60. More preferred is a silicone compound having a refractive index in the range of 1.42 to 1.59, and most preferred is a range of 1.44 to 1.59. When the refractive index is within the above range, the silicone compound is finely dispersed in the aromatic polycarbonate, thereby providing a resin composition with less white turbidity and good dyeability.

さらに本発明のＢ−２成分として使用されるシリコーン化合物は、１０５℃／３時間における加熱減量法による揮発量が１８％以下であることが好適である。さらに好ましくは揮発量が１０％以下であるシリコーン化合物である。揮発量が１８％より大きいと本発明の樹脂組成物を押出してペレット化を行う際に、樹脂からの揮発物の量が多くなる問題が生じ、さらに、成形品中に生じる気泡が多くなりやすいという問題がある。   Furthermore, the silicone compound used as the B-2 component of the present invention preferably has a volatilization amount of 18% or less by a heat loss method at 105 ° C./3 hours. More preferably, the silicone compound has a volatilization amount of 10% or less. When the volatilization amount is larger than 18%, there is a problem that the amount of the volatile matter from the resin increases when the resin composition of the present invention is extruded and pelletized, and more bubbles are generated in the molded product. There is a problem.

Ｂ−２成分として使用されるシリコーン化合物としては、上記の条件を満たすものであれば直鎖状であっても分岐構造を持つものであっても良く、Ｓｉ−Ｈ基を分子構造中の側鎖、末端、分岐点の何れか、または複数の部位に有する各種の化合物を用いることが可能である。   The silicone compound used as the component B-2 may be linear or branched as long as the above conditions are satisfied, and the Si—H group may be a side in the molecular structure. It is possible to use various compounds having any of a chain, a terminal, a branch point, or a plurality of sites.

一般的に分子中にＳｉ−Ｈ基を含有するシリコーン化合物の構造は、以下に示す４種類のシロキサン単位を任意に組み合わせることによって構成される。
Ｍ単位：（ＣＨ３）３ＳｉＯ１／２、Ｈ（ＣＨ３）２ＳｉＯ１／２、Ｈ２（ＣＨ３）ＳｉＯ１／２、（ＣＨ３）２（ＣＨ２＝ＣＨ）ＳｉＯ１／２、（ＣＨ３）２（Ｃ６Ｈ５）ＳｉＯ１／２、（ＣＨ３）（Ｃ６Ｈ５）（ＣＨ２＝ＣＨ）ＳｉＯ１／２等の１官能性シロキサン単位
Ｄ単位：（ＣＨ３）２ＳｉＯ、Ｈ（ＣＨ３）ＳｉＯ、Ｈ２ＳｉＯ、Ｈ（Ｃ６Ｈ５）ＳｉＯ、（ＣＨ３）（ＣＨ２＝ＣＨ）ＳｉＯ、（Ｃ６Ｈ５）２ＳｉＯ等の２官能性シロキサン単位
Ｔ単位：（ＣＨ３）ＳｉＯ３／２、（Ｃ３Ｈ７）ＳｉＯ３／２、ＨＳｉＯ３／２、（ＣＨ２＝ＣＨ）ＳｉＯ３／２、（Ｃ６Ｈ５）ＳｉＯ３／２等の３官能性シロキサン単位
Ｑ単位：ＳｉＯ２で示される４官能性シロキサン単位 In general, the structure of a silicone compound containing a Si—H group in the molecule is constituted by arbitrarily combining the following four types of siloxane units.
M units: (CH 3 ) 3 SiO 1/2 , H (CH 3 ) 2 SiO 1/2 , H 2 (CH 3 ) SiO 1/2 , (CH 3 ) 2 (CH 2 = CH) SiO 1/2 , (CH 3 ) 2 (C 6 H 5 ) SiO 1/2 , (CH 3 ) (C 6 H 5 ) (CH 2 ═CH) SiO 1/2 and other monofunctional siloxane units D units: (CH 3 ) 2 SiO, H (CH 3 ) SiO, H 2 SiO, H (C 6 H 5 ) SiO, (CH 3 ) (CH 2 ═CH) SiO, (C 6 H 5 ) 2 SiO, etc. Unit T unit: (CH 3 ) SiO 3/2 , (C 3 H 7 ) SiO 3/2 , HSiO 3/2 , (CH 2 ═CH) SiO 3/2 , (C 6 H 5 ) SiO 3/2 trifunctional siloxane units Q units etc: tetrafunctional siloxane represented by SiO 2 Place

本発明において使用されるＳｉ−Ｈ基を含有するシリコーン化合物の構造は、具体的には、示性式としてＤｎ、Ｔｐ、ＭｍＤｎ、ＭｍＴｐ、ＭｍＱｑ、ＭｍＤｎＴｐ、ＭｍＤｎＱｑ、ＭｍＴｐＱｑ、ＭｍＤｎＴｐＱｑ、ＤｎＴｐ、ＤｎＱｑ、ＤｎＴｐＱｑが挙げられる。この中で好ましいシリコーン化合物の構造は、ＭｍＤｎ、ＭｍＴｐ、ＭｍＤｎＴｐ、ＭｍＤｎＱｑであり、さらに好ましい構造は、ＭｍＤｎまたはＭｍＤｎＴｐである。
（上記示性式中の係数ｍ、ｎ、ｐ、ｑは各シロキサン単位の重合度を表す整数である。またｍ、ｎ、ｐ、ｑのいずれかが２以上の数値である場合、その係数の付いたシロキサン単位は、結合する水素原子やヘテロ原子含有官能基を有しても良い炭素数１〜２０の炭化水素基が異なる２種以上のシロキサン単位とすることができる。） Specifically, the structure of the silicone compound containing a Si—H group used in the present invention is expressed as D n , T p , M m D n , M m T p , M m Q q , M m D n T p, M m D n Q q, M m T p Q q, M m D n T p Q q, D n T p, D n Q q, include D n T p Q q. Among these, preferable structures of the silicone compound are M m D n , M m T p , M m D n T p , and M m D n Q q , and more preferable structures are M m D n or M m D n. T p .
(The coefficients m, n, p, q in the above formula are integers representing the degree of polymerization of each siloxane unit. Also, if any of m, n, p, q is a numerical value of 2 or more, the coefficient The siloxane units with can be two or more siloxane units having different hydrocarbon groups having 1 to 20 carbon atoms which may have a hydrogen atom or a hetero atom-containing functional group.

ここで、各示性式における係数の合計がシリコーン化合物の平均重合度となる。本発明においては、この平均重合度を３〜１５０の範囲とすることが好ましく、より好ましくは４〜８０の範囲、さらに好ましくは５〜６０の範囲である。重合度が３より小さい場合、
シリコーン化合物自体の揮発性が高くなるため、このシリコーン化合物を配合した樹脂組成物の加工時において樹脂からの揮発分が多くなりやすいという問題がある。重合度が１５０より大きい場合、このシリコーン化合物を配合した樹脂組成物における難燃性や透明性が不十分となりやすい。
なお、上記のシリコーン化合物は、それぞれ単独で用いてもよく、２種以上を組合せて用いてもよい。 Here, the sum of the coefficients in each characteristic formula is the average degree of polymerization of the silicone compound. In this invention, it is preferable to make this average degree of polymerization into the range of 3-150, More preferably, it is the range of 4-80, More preferably, it is the range of 5-60. If the degree of polymerization is less than 3,
Since the volatility of the silicone compound itself is increased, there is a problem that the volatile component from the resin tends to increase during the processing of the resin composition containing the silicone compound. If the degree of polymerization is greater than 150, the flame retardancy and transparency of the resin composition containing this silicone compound tends to be insufficient.
In addition, said silicone compound may be used independently, respectively and may be used in combination of 2 or more type.

このようなＳｉ−Ｈ結合を有するシリコーン化合物は、それ自体従来公知の方法によって製造することができる。例えば、目的とするシリコーン化合物の構造に従い、相当するオルガノクロロシラン類を共加水分解し、副生する塩酸や低沸分を除去することによって目的物を得ることができる。また、分子中にＳｉ−Ｈ結合や一般式（５）で示される芳香族基、その他のヘテロ原子含有官能基を有しても良い炭素数１〜２０の炭化水素基を有するシリコーンオイル、環状シロキサンやアルコキシシラン類を出発原料とする場合には、塩酸、硫酸、メタンスルホン酸等の酸触媒を使用し、場合によって加水分解のための水を添加して、重合反応を進行させた後、使用した酸触媒や低沸分を同様に除去することによって、目的とするシリコーン化合物を得ることができる。   Such a silicone compound having a Si—H bond can be produced by a method known per se. For example, the target product can be obtained by cohydrolyzing the corresponding organochlorosilanes according to the structure of the target silicone compound and removing by-product hydrochloric acid and low-boiling components. In addition, a silicone oil having a C1-C20 hydrocarbon group that may have an Si-H bond, an aromatic group represented by the general formula (5), or other heteroatom-containing functional group in the molecule, cyclic When using siloxane or alkoxysilane as a starting material, use an acid catalyst such as hydrochloric acid, sulfuric acid, methanesulfonic acid, etc., and optionally add water for hydrolysis to advance the polymerization reaction, The target silicone compound can be obtained by removing the acid catalyst and low-boiling components used in the same manner.

さらに、Ｓｉ−Ｈ基を含有するシリコーン化合物が下記の構造式で示されるシロキサン単位 Ｍ、ＭＨ、Ｄ、ＤＨ 、Ｄφ２、Ｔ、Ｔφ （ただし Ｍ：（ＣＨ３）３ＳｉＯ１／２ＭＨ：Ｈ（ＣＨ３）２ＳｉＯ１／２Ｄ：（ＣＨ３）２ＳｉＯＤＨ：Ｈ（ＣＨ３）ＳｉＯＤφ２：（Ｃ６Ｈ５）２ＳｉＴ：（ＣＨ３）ＳｉＯ３／２Ｔφ：（Ｃ６Ｈ５）ＳｉＯ３／２）を有しており、１分子あたりに有する各シロキサン単位の平均数をそれぞれｍ、ｍｈ、ｄ、ｄｈ、ｄｐ２、ｔ、ｔｐとした場合、下記関係式のすべてを満足することが好ましい。
２ ≦ ｍ＋ｍｈ ≦ ４０
０．３５ ≦ ｄ＋ｄｈ＋ｄｐ２ ≦ １４８
０ ≦ ｔ＋ｔｐ ≦ ３８
０．３５ ≦ ｍｈ＋ｄｈ ≦ １１０ Further, a silicone compound containing a Si-H group is a siloxane unit represented by the following structural formula: M, MH , D, DH , Dφ2 , T, Tφ (where M: (CH 3 ) 3 SiO 1 1 2 MH : H (CH 3 ) 2 SiO 1/2 D: (CH 3 ) 2 SiOD H : H (CH 3 ) SiOD φ 2 : (C 6 H 5 ) 2 SiT: (CH 3 ) SiO 3/2 T φ: (C 6 H 5) has a SiO 3/2), m the average number of the respective siloxane units having per molecule, respectively, m h, d, d h , d p2, t, and t p In this case, it is preferable to satisfy all of the following relational expressions.
2 ≦ m + m h ≦ 40
0.35 ≦ d + d h + d p2 ≦ 148
0 ≦ t + t p ≦ 38
0.35 ≦ m h + d h ≦ 110

この範囲を外れると本発明の樹脂組成物において良好な難燃性と優れた透明性を同時に達成することが困難となり、場合によってはＳｉ−Ｈ基を含有するシリコーン化合物の製造が困難となる。   Outside this range, it becomes difficult to simultaneously achieve good flame retardancy and excellent transparency in the resin composition of the present invention, and in some cases, it becomes difficult to produce a silicone compound containing a Si—H group.

本発明のＢ−２成分として使用されるシリコーン化合物の含有量は芳香族ポリカーボネート樹脂（Ａ成分）１００重量部に対して好ましくは０．０５〜２重量部であり、より好ましくは０．０８〜１．８重量部さらに好ましくは０．１〜１．５重量部、最も好ましくは０．１〜１重量部である。含有量が多すぎると樹脂の耐熱性が低下したり、押し出し加工時に発生するガスにより押し出し成形品の外観が悪化するという問題あり、少なすぎると難燃性が発揮されないという問題がある。   The content of the silicone compound used as the B-2 component of the present invention is preferably 0.05 to 2 parts by weight, more preferably 0.08 to 100 parts by weight with respect to 100 parts by weight of the aromatic polycarbonate resin (component A). It is 1.8 parts by weight, more preferably 0.1 to 1.5 parts by weight, and most preferably 0.1 to 1 part by weight. If the content is too large, there is a problem that the heat resistance of the resin is lowered or the appearance of the extruded product is deteriorated by a gas generated during extrusion processing, and if it is too small, there is a problem that flame retardancy is not exhibited.

＜その他の成分＞
一方、本発明の樹脂組成物には、透明性を損なうことがない限り、他の樹脂や充填剤は配合しても差し支えないが、他の樹脂や充填剤の多くは透明性に支障を来すので、その種類や量の選択は、その点を考慮すべきである。 <Other ingredients>
On the other hand, the resin composition of the present invention may contain other resins and fillers as long as the transparency is not impaired, but many of the other resins and fillers impair transparency. Therefore, the selection of the type and quantity should take that point into consideration.

本発明の樹脂組成物には、透明性を損なうことがない限り、成形品の機械的物性、化学的性質または電気的性質の改良のために、Ａ成分以外の他の熱可塑性樹脂を配合することができる。この他の熱可塑性樹脂の配合量は、その種類および目的によって変わるが、通常、芳香族ポリカーボネート樹脂（Ａ成分）１００重量部当たり、１〜３０重量部が好ましく、より好ましくは２〜２０重量部が適当である。   Unless the transparency is impaired, the resin composition of the present invention is blended with a thermoplastic resin other than the component A in order to improve the mechanical properties, chemical properties or electrical properties of the molded product. be able to. The blending amount of the other thermoplastic resin varies depending on the type and purpose, but is usually preferably 1 to 30 parts by weight, more preferably 2 to 20 parts by weight per 100 parts by weight of the aromatic polycarbonate resin (component A). Is appropriate.

他の熱可塑性樹脂としては、例えば、ポリエチレン樹脂、ポリプロピレン樹脂、ポリアルキルメタクリレート樹脂などに代表される汎用プラスチックス、ポリフェニレンエーテル樹脂、ポリアセタール樹脂、ポリアミド樹脂、環状ポリオレフィン樹脂、ポリアリレート樹脂（非晶性ポリアリレート、液晶性ポリアリレート）等に代表されるエンジニアリングプラスチックス、ポリエーテルエーテルケトン、ポリエーテルイミド、ポリサルフォン、ポリエーテルサルフォン、ポリフェニレンサルファイドなどのいわゆるスーパーエンジニアリングプラスチックスと呼ばれるものを挙げることができる。さらにオレフィン系熱可塑性エラストマー、ポリアミド系熱可塑性エラストマー、ポリウレタン系熱可塑性エラストマーなどの熱可塑性エラストマーも使用することができる。   Other thermoplastic resins include, for example, general-purpose plastics represented by polyethylene resin, polypropylene resin, polyalkyl methacrylate resin, polyphenylene ether resin, polyacetal resin, polyamide resin, cyclic polyolefin resin, polyarylate resin (non-crystalline) And so-called super engineering plastics such as engineering plastics typified by polyarylate and liquid crystalline polyarylate), polyetheretherketone, polyetherimide, polysulfone, polyethersulfone, and polyphenylene sulfide. . Furthermore, thermoplastic elastomers such as olefin-based thermoplastic elastomers, polyamide-based thermoplastic elastomers, and polyurethane-based thermoplastic elastomers can also be used.

本発明の樹脂組成物には、成形品に種々の機能の付与や特性改善のために、それ自体知られた添加物を少割合配合することができる。これら添加物は本発明の目的を損なわない限り、通常の配合量である。   In the resin composition of the present invention, additives known per se can be blended in a small proportion for imparting various functions and improving properties to the molded product. These additives are used in usual amounts as long as the object of the present invention is not impaired.

かかる添加剤としては、ドリップ防止剤（フィブリル形成能を有する含フッ素ポリマーなど）、熱安定剤、紫外線吸収剤、光安定剤、離型剤、滑剤、摺動剤（ＰＴＦＥ粒子など）、着色剤（カーボンブラック、酸化チタンなどの顔料、染料）、蛍光増白剤、蓄光顔料、蛍光染料、帯電防止剤、流動改質剤、結晶核剤、無機および有機の抗菌剤、光触媒系防汚剤（微粒子酸化チタン、微粒子酸化亜鉛など）、グラフトゴムに代表される衝撃改質剤、赤外線吸収剤またはフォトクロミック剤が挙げられる。   Examples of such additives include anti-drip agents (such as fluorine-containing polymers having fibril-forming ability), heat stabilizers, ultraviolet absorbers, light stabilizers, mold release agents, lubricants, sliding agents (such as PTFE particles), and colorants. (Pigments and dyes such as carbon black and titanium oxide), fluorescent whitening agents, phosphorescent pigments, fluorescent dyes, antistatic agents, flow modifiers, crystal nucleating agents, inorganic and organic antibacterial agents, photocatalytic antifouling agents ( Fine particle titanium oxide, fine particle zinc oxide, etc.), impact modifiers typified by graft rubber, infrared absorbers or photochromic agents.

本発明の樹脂組成物の熱安定性、酸化防止性、光安定性（紫外線安定性）および離型性の改良のために、芳香族ポリカーボネート樹脂において、これらの改良に使用されている添加剤が有利に使用される。以下これら添加剤について具体的に説明する。   In order to improve the thermal stability, antioxidant property, light stability (ultraviolet light stability) and releasability of the resin composition of the present invention, the additives used for these improvements in the aromatic polycarbonate resin are as follows. Advantageously used. Hereinafter, these additives will be specifically described.

本発明の樹脂組成物は、熱安定剤としてリン含有安定剤を配合することができる。かかるリン含有安定剤としては、ホスファイト化合物、ホスホナイト化合物、およびホスフェート化合物のいずれも使用可能である。   The resin composition of this invention can mix | blend a phosphorus containing stabilizer as a heat stabilizer. As the phosphorus-containing stabilizer, any of phosphite compounds, phosphonite compounds, and phosphate compounds can be used.

ホスファイト化合物としては、さまざまなものを用いることができる。具体的には例えば下記一般式（９）で表わされるホスファイト化合物、下記一般式（１０）で表わされるホスファイト化合物、および下記一般式（１１）で表わされるホスファイト化合物を挙げることができる。   Various phosphite compounds can be used. Specific examples include phosphite compounds represented by the following general formula (9), phosphite compounds represented by the following general formula (10), and phosphite compounds represented by the following general formula (11).

Figure 2011099030
［式中Ｒ８は、水素原子または炭素数１〜２０のアルキル基、炭素数６〜２０のアリール基ないしアルカリール基、炭素数７〜３０のアラルキル基、またはこれらのハロ、アルキルチオ（アルキル基は炭素数１〜３０）またはヒドロキシ置換基を示し、３個のＲ８は互いに同一または互いに異なるのいずれの場合も選択でき、また２価フェノール類から誘導されることにより環状構造も選択できる。］
Figure 2011099030
 [Wherein R 8 represents a hydrogen atom or an alkyl group having 1 to 20 carbon atoms, an aryl group or an alkaryl group having 6 to 20 carbon atoms, an aralkyl group having 7 to 30 carbon atoms, or a halo or alkylthio thereof (an alkyl group) Represents 1 to 30 carbon atoms) or a hydroxy substituent, and three R 8 can be selected from the same or different from each other, and a cyclic structure can be selected by being derived from dihydric phenols. ]

Figure 2011099030
［式中Ｒ９、Ｒ１０はそれぞれ水素原子、炭素数１〜２０のアルキル基、炭素数６〜２０のアリール基ないしアルキルアリール基、炭素数７〜３０のアラルキル基、炭素数４〜２０のシクロアルキル基、炭素数１５〜２５の２−（４−オキシフェニル）プロピル置換アリール基を示す。なお、シクロアルキル基およびアリール基は、アルキル基で置換されていないもの、またはアルキル基で置換されているもののいずれも選択できる。］
Figure 2011099030
 [Wherein R 9 and R 10 are each a hydrogen atom, an alkyl group having 1 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms or an alkylaryl group, an aralkyl group having 7 to 30 carbon atoms, and an alkyl group having 4 to 20 carbon atoms. A cycloalkyl group, a 2- (4-oxyphenyl) propyl-substituted aryl group having 15 to 25 carbon atoms is shown. The cycloalkyl group and the aryl group can be selected from those not substituted with an alkyl group or those substituted with an alkyl group. ]

Figure 2011099030
［式中Ｒ１１、Ｒ１２は炭素数１２〜１５のアルキル基である。なお、Ｒ１１およびＲ１２は互いに同一または互いに異なるのいずれの場合も選択できる。］で表わされるホスファイト化合物を挙げることができる。
Figure 2011099030
 [Wherein R 11 and R 12 are alkyl groups having 12 to 15 carbon atoms. Note that R 11 and R 12 can be selected to be the same or different from each other. The phosphite compound represented by this can be mentioned.

ホスホナイト化合物としては下記一般式（１２）で表わされるホスホナイト化合物、および下記一般式（１３）で表わされるホスホナイト化合物を挙げることができる。   Examples of the phosphonite compound include a phosphonite compound represented by the following general formula (12) and a phosphonite compound represented by the following general formula (13).

Figure 2011099030
Figure 2011099030
 ［式中、Ａｒ１、Ａｒ２は炭素数６〜２０のアリール基ないしアルキルアリール基、または炭素数１５〜２５の２−（４−オキシフェニル）プロピル置換アリール基を示し、４つのＡｒ１は互いに同一、または互いに異なるいずれも選択できる。または２つのＡｒ２は互いに同一、または互いに異なるいずれも選択できる。］
Figure 2011099030
Figure 2011099030
 [In the formula, Ar 1, Ar 2 represents a 2- (4-oxyphenyl) propyl-substituted aryl group of the aryl group or alkyl aryl group having 6 to 20 carbon atoms, or 15-25 carbon atoms, the four Ar 1 Either the same or different from each other can be selected. Alternatively, two Ar 2 can be selected to be the same or different from each other. ]

上記一般式（９）で表されるホスファイト化合物の好ましい具体例としては、ジフェニルイソオクチルホスファイト、２，２’−メチレンビス（４，６−ジ−ｔｅｒｔ−ブチルフェニル）オクチルホスファイト、ジフェニルモノ（トリデシル）ホスファイト、フェニルジイソデシルホスファイト、フェニルジ（トリデシル）ホスファイトが挙げられる。   Preferable specific examples of the phosphite compound represented by the general formula (9) include diphenylisooctyl phosphite, 2,2′-methylenebis (4,6-di-tert-butylphenyl) octyl phosphite, diphenylmono (Tridecyl) phosphite, phenyl diisodecyl phosphite, phenyl di (tridecyl) phosphite are mentioned.

上記一般式（１０）で表されるホスファイト化合物の好ましい具体例としては、ジステアリルペンタエリスリトールジホスファイト、ビス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）ペンタエリスリトールジホスファイト、ビス（２，６−ジ−ｔｅｒｔ−ブチル−４−メチルフェニル）ペンタエリスリトールジホスファイト、フェニルビスフェノールＡペンタエリスリトールジホスファイト、ジシクロヘキシルペンタエリスリトールジホスファイトなどが挙げられ、好ましくはジステアリルペンタエリスリトールジホスファイト、ビス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）ペンタエリスリトールジホスファイト、ビス（２，６−ジ−ｔｅｒｔ−ブチル−４−メチルフェニル）ペンタエリスリトールジホスファイトを挙げることができる。かかるホスファイト化合物は１種、または２種以上を併用することができる。   Preferred specific examples of the phosphite compound represented by the general formula (10) include distearyl pentaerythritol diphosphite, bis (2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis (2 , 6-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite, phenylbisphenol A pentaerythritol diphosphite, dicyclohexylpentaerythritol diphosphite, etc., preferably distearyl pentaerythritol diphosphite, Bis (2,4-di-tert-butylphenyl) pentaerythritol diphosphite and bis (2,6-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite can be mentioned.Such phosphite compounds can be used alone or in combination of two or more.

上記一般式（１１）で表されるホスファイト化合物の好ましい具体例としては、４，４’−イソプロピリデンジフェノールテトラトリデシルホスファイトを挙げることができる。   Preferable specific examples of the phosphite compound represented by the general formula (11) include 4,4'-isopropylidenediphenol tetratridecyl phosphite.

上記一般式（１２）で表されるホスホナイト化合物の好ましい具体例としては、テトラキス（２，４−ジ−ｉｓｏ−プロピルフェニル）−４，４’−ビフェニレンジホスホナイト、テトラキス（２，４−ジ−ｎ−ブチルフェニル）−４，４’−ビフェニレンジホスホナイト、テトラキス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−４，４’−ビフェニレンジホスホナイト、テトラキス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−４，３’−ビフェニレンジホスホナイト、テトラキス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−３，３’−ビフェニレンジホスホナイト、テトラキス（２，６−ジ−ｉｓｏ−プロピルフェニル）−４，４’−ビフェニレンジホスホナイト、テトラキス（２，６−ジ−ｎ−ブチルフェニル）−４，４’−ビフェニレンジホスホナイト、テトラキス（２，６−ジ−ｔｅｒｔ−ブチルフェニル）−４，４’−ビフェニレンジホスホナイト、テトラキス（２，６−ジ−ｔｅｒｔ−ブチルフェニル）−４，３’−ビフェニレンジホスホナイト、テトラキス（２，６−ジ−ｔｅｒｔ−ブチルフェニル）−３，３’−ビフェニレンジホスホナイト等が挙げられ、テトラキス（ジ−ｔｅｒｔ−ブチルフェニル）−ビフェニレンジホスホナイトが好ましく、テトラキス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−ビフェニレンジホスホナイトがより好ましい。このテトラキス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−ビフェニレンジホスホナイトは、２種以上の混合物が好ましく、具体的にはテトラキス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−４，４’−ビフェニレンジホスホナイト（Ｅ２−１成分）、テトラキス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−４，３’−ビフェニレンジホスホナイト（Ｅ２−２成分）および、テトラキス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−３，３’−ビフェニレンジホスホナイト（Ｅ２−３成分）の１種もしくは２種以上を併用して使用可能であるが、好ましくはかかる３種の混合物である。また、３種の混合物の場合その混合比は、Ｅ２−１成分、Ｅ２−２成分およびＥ２−３成分を重量比で１００：３７〜６４：４〜１４の範囲が好ましく、１００：４０〜６０：５〜１１の範囲がより好ましい。   Preferable specific examples of the phosphonite compound represented by the general formula (12) include tetrakis (2,4-di-iso-propylphenyl) -4,4′-biphenylenediphosphonite, tetrakis (2,4-di). -N-butylphenyl) -4,4'-biphenylenediphosphonite, tetrakis (2,4-di-tert-butylphenyl) -4,4'-biphenylenediphosphonite, tetrakis (2,4-di-tert) -Butylphenyl) -4,3'-biphenylenediphosphonite, tetrakis (2,4-di-tert-butylphenyl) -3,3'-biphenylenediphosphonite, tetrakis (2,6-di-iso-propyl) Phenyl) -4,4′-biphenylenediphosphonite, tetrakis (2,6-di-n-butylphenyl) -4,4′-bifu Nylene diphosphonite, tetrakis (2,6-di-tert-butylphenyl) -4,4′-biphenylenediphosphonite, tetrakis (2,6-di-tert-butylphenyl) -4,3′-biphenylenedi Examples thereof include phosphonite, tetrakis (2,6-di-tert-butylphenyl) -3,3′-biphenylenediphosphonite, tetrakis (di-tert-butylphenyl) -biphenylenediphosphonite is preferred, and tetrakis ( 2,4-di-tert-butylphenyl) -biphenylenediphosphonite is more preferred. The tetrakis (2,4-di-tert-butylphenyl) -biphenylenediphosphonite is preferably a mixture of two or more, specifically tetrakis (2,4-di-tert-butylphenyl) -4,4. '-Biphenylenediphosphonite (E2-1 component), tetrakis (2,4-di-tert-butylphenyl) -4,3'-biphenylenediphosphonite (E2-2 component) and tetrakis (2,4- One kind or two or more kinds of di-tert-butylphenyl) -3,3′-biphenylenediphosphonite (component E2-3) can be used in combination, but these three kinds of mixtures are preferable. In the case of three kinds of mixtures, the mixing ratio is preferably in the range of 100: 37 to 64: 4 to 14 by weight ratio of E2-1 component, E2-2 component and E2-3 component, and 100: 40 to 60 : The range of 5-11 is more preferable.

上記一般式（１３）で表されるホスホナイト化合物の好ましい具体例としては、ビス（２，４−ジ−ｉｓｏ−プロピルフェニル）−４−フェニル−フェニルホスホナイト、ビス（２，４−ジ−ｎ−ブチルフェニル）−３−フェニル−フェニルホスホナイト、ビス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−４−フェニル−フェニルホスホナイト、ビス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−３−フェニル−フェニルホスホナイトビス（２，６−ジ−ｉｓｏ−プロピルフェニル）−４−フェニル−フェニルホスホナイト、ビス（２，６−ジ−ｎ−ブチルフェニル）−３−フェニル−フェニルホスホナイト、ビス（２，６−ジ−ｔｅｒｔ−ブチルフェニル）−４−フェニル−フェニルホスホナイト、ビス（２，６−ジ−ｔｅｒｔ−ブチルフェニル）−３−フェニル−フェニルホスホナイト等が挙げられ、ビス（ジ−ｔｅｒｔ−ブチルフェニル）−フェニル−フェニルホスホナイトが好ましく、ビス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−フェニル−フェニルホスホナイトがより好ましい。このビス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−フェニル−フェニルホスホナイトは、２種以上の混合物が好ましく、具体的にはビス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−４−フェニル−フェニルホスホナイト、およびビス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）−３−フェニル−フェニルホスホナイトの１種もしくは２種を併用して使用可能であるが、好ましくはかかる２種の混合物である。また、２種の混合物の場合その混合比は、重量比で５：１〜４の範囲が好ましく、５：２〜３の範囲がより好ましい。   Preferable specific examples of the phosphonite compound represented by the general formula (13) include bis (2,4-di-iso-propylphenyl) -4-phenyl-phenylphosphonite, bis (2,4-di-n). -Butylphenyl) -3-phenyl-phenylphosphonite, bis (2,4-di-tert-butylphenyl) -4-phenyl-phenylphosphonite, bis (2,4-di-tert-butylphenyl) -3 -Phenyl-phenylphosphonite bis (2,6-di-iso-propylphenyl) -4-phenyl-phenylphosphonite, bis (2,6-di-n-butylphenyl) -3-phenyl-phenylphosphonite, Bis (2,6-di-tert-butylphenyl) -4-phenyl-phenylphosphonite, bis (2,6-di-tert-butyl) Benzyl) -3-phenyl-phenylphosphonite and the like, bis (di-tert-butylphenyl) -phenyl-phenylphosphonite is preferred, bis (2,4-di-tert-butylphenyl) -phenyl-phenyl Phosphonite is more preferred. The bis (2,4-di-tert-butylphenyl) -phenyl-phenylphosphonite is preferably a mixture of two or more, specifically, bis (2,4-di-tert-butylphenyl) -4- One or two of phenyl-phenylphosphonite and bis (2,4-di-tert-butylphenyl) -3-phenyl-phenylphosphonite can be used in combination. It is a mixture. In the case of two kinds of mixtures, the mixing ratio is preferably in the range of 5: 1 to 4 by weight, and more preferably in the range of 5: 2 to 3.

一方、ホスフェート化合物としては、トリブチルホスフェート、トリメチルホスフェート、トリクレジルホスフェート、トリフェニルホスフェート、トリクロルフェニルホスフェート、トリエチルホスフェート、ジフェニルクレジルホスフェート、ジフェニルモノオルソキセニルホスフェート、トリブトキシエチルホスフェート、ジブチルホスフェート、ジオクチルホスフェート、ジイソプロピルホスフェートなどを挙げることができ、好ましくはトリメチルホスフェートである。   On the other hand, as phosphate compounds, tributyl phosphate, trimethyl phosphate, tricresyl phosphate, triphenyl phosphate, trichlorophenyl phosphate, triethyl phosphate, diphenyl cresyl phosphate, diphenyl monoorthoxenyl phosphate, tributoxyethyl phosphate, dibutyl phosphate, dioctyl Examples thereof include phosphate and diisopropyl phosphate, and trimethyl phosphate is preferable.

上記のリン含有熱安定剤の中で、さらに好ましい化合物としては、以下の一般式（１４）および（１５）で表される化合物を挙げることができる。   Among the above phosphorus-containing heat stabilizers, more preferred compounds include compounds represented by the following general formulas (14) and (15).

Figure 2011099030
（式（１４）中、Ｒ１３およびＲ１４は、それぞれ独立して炭素原子数１〜１２のアルキル基、シクロアルキル基、アリール基またはアラルキル基を示す。）
Figure 2011099030
 (In formula (14), R 13 and R 14 each independently represents an alkyl group having 1 to 12 carbon atoms, a cycloalkyl group, an aryl group or an aralkyl group.)

Figure 2011099030
（式（１５）中、Ｒ１５、Ｒ１６、Ｒ１７、Ｒ１８、Ｒ２１、Ｒ２２、およびＲ２３はそれぞれ独立して水素原子、炭素原子数１〜１２のアルキル基、シクロアルキル基、アリール基またはアラルキル基を示し、Ｒ１９は水素原子または炭素原子数１〜４のアルキル基を示し、およびＲ２０は水素原子またはメチル基を示す。）
Figure 2011099030
 (In the formula (15), R 15 , R 16 , R 17 , R 18 , R 21 , R 22 , and R 23 are each independently a hydrogen atom, an alkyl group having 1 to 12 carbon atoms, a cycloalkyl group, An aryl group or an aralkyl group, R 19 represents a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, and R 20 represents a hydrogen atom or a methyl group.)

式（１４）中、好ましくはＲ１３およびＲ１４は炭素原子数１〜１２のアルキル基であり、より好ましくは炭素原子数１〜８のアルキル基である。式（１４）で表される化合物としては具体的に、トリス（ジメチルフェニル）ホスファイト、トリス（ジエチルフェニル）ホスファイト、トリス（ジ−ｉｓｏ−プロピルフェニル）ホスファイト、トリス（ジ−ｎ−ブチルフェニル）ホスファイト、トリス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）ホスファイト、トリス（２，６−ジ−ｔｅｒｔ−ブチルフェニル）ホスファイト、トリス（２，６−ジ−ｔｅｒｔ−ブチルフェニル）ホスファイトなどが挙げられ、特にトリス（２，６−ジ−ｔｅｒｔ−ブチルフェニル）ホスファイトが好ましい。 In the formula (14), R 13 and R 14 are preferably an alkyl group having 1 to 12 carbon atoms, and more preferably an alkyl group having 1 to 8 carbon atoms. Specific examples of the compound represented by the formula (14) include tris (dimethylphenyl) phosphite, tris (diethylphenyl) phosphite, tris (di-iso-propylphenyl) phosphite, and tris (di-n-butyl). Phenyl) phosphite, tris (2,4-di-tert-butylphenyl) phosphite, tris (2,6-di-tert-butylphenyl) phosphite, tris (2,6-di-tert-butylphenyl) Examples thereof include phosphite, and tris (2,6-di-tert-butylphenyl) phosphite is particularly preferable.

式（１５）で表される化合物としては具体的に、２，２’−メチレンビス（４，６−ジ−ｔｅｒｔ−ブチルフェノール）と２，６−ジ−ｔｅｒｔ−ブチルフェノールから誘導されるホスファイト、２，２’−メチレンビス（４，６−ジ−ｔｅｒｔ−ブチルフェノール）とフェノールから誘導されるホスファイト、が挙げられ、特に２，２’−メチレンビス（４，６−ジ−ｔｅｒｔ−ブチルフェノール）とフェノールから誘導されるホスファイトが好ましい。   Specific examples of the compound represented by the formula (15) include phosphites derived from 2,2′-methylenebis (4,6-di-tert-butylphenol) and 2,6-di-tert-butylphenol, 2 2,2'-methylenebis (4,6-di-tert-butylphenol) and phosphites derived from phenol, especially from 2,2'-methylenebis (4,6-di-tert-butylphenol) and phenol. Derived phosphites are preferred.

なお、式（１５）のリン化合物は公知の方法で製造できる。例えば下記一般式（１６）に示されるビスフェノール化合物と三塩化リンとを反応させて相当する塩化リン酸を得て、その後それと下記一般式（１７）で示されるフェノールとを反応させる方法などがある。   In addition, the phosphorus compound of Formula (15) can be manufactured by a well-known method. For example, there is a method in which a bisphenol compound represented by the following general formula (16) is reacted with phosphorus trichloride to obtain a corresponding phosphoric acid chloride, and then it is reacted with a phenol represented by the following general formula (17). .

Figure 2011099030
（式（１６）中、Ｒ２４、Ｒ２５、Ｒ２６、およびＲ２７はそれぞれ水素原子、炭素原子数１〜１２のアルキル基、シクロアルキル基、アリール基またはアラルキル基を示し、Ｒ２８は水素原子または炭素原子数１〜４のアルキル基を示し、およびＲ２９は水素原子またはメチル基を示す。）
Figure 2011099030
 (In the formula (16), R 24 , R 25 , R 26 and R 27 each represent a hydrogen atom, an alkyl group having 1 to 12 carbon atoms, a cycloalkyl group, an aryl group or an aralkyl group, and R 28 represents hydrogen. And represents an atom or an alkyl group having 1 to 4 carbon atoms, and R 29 represents a hydrogen atom or a methyl group.)

Figure 2011099030
（式（１７）中、Ｒ３０、Ｒ３１、およびＲ３２はそれぞれ水素原子、炭素原子数１〜１２のアルキル基、シクロアルキル基、アリール基またはアラルキル基を示す。）
Figure 2011099030
 (In the formula (17), R 30 , R 31 and R 32 each represent a hydrogen atom, an alkyl group having 1 to 12 carbon atoms, a cycloalkyl group, an aryl group or an aralkyl group.)

上記一般式（１６）の化合物の具体例としては、２，２’−メチレンビスフェノール、２，２’−メチレンビス（４−メチルフェノール）、２，２’−メチレンビス（６−メチルフェノール）、２，２’−メチレンビス（４，６−ジメチルフェノール）、２，２’−エチリデンビスフェノール、２，２’−エチリデンビス（４−メチルフェノール）、２，２’−イソプロピリデンビスフェノール、２，２’−メチレンビス（４−メチル−６−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４−エチル−６−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４，６−ジ−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４−メチル−６−シクロヘキシルフェノール）、２，２’−ジヒドロキシ−３，３’−ジ（α−メチルシクロヘキシル）−５，５’−ジメチルフェニルメタン、２，２’−メチレンビス（６−α−メチル−ベンジル−ｐ−クレゾール）、２，２’−エチリデン−ビス（４，６−ジ−ｔｅｒｔ−ブチルフェノール）、および２，２−ブチリデン−ビス（４−メチル−６−ｔｅｒｔ−ブチルフェノール）などが挙げられ、２，２’−メチレンビス（４−メチル−６−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４−エチル−６−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４，６−ジ−ｔｅｒｔ−ブチルフェノール）、２，２’−エチリデン−ビス（４，６−ジ−ｔｅｒｔ−ブチルフェノール）、および２，２’−ブチリデン−ビス（４−メチル−６−ｔｅｒｔ−ブチルフェノール）が好ましい。   Specific examples of the compound of the general formula (16) include 2,2′-methylenebisphenol, 2,2′-methylenebis (4-methylphenol), 2,2′-methylenebis (6-methylphenol), 2, 2'-methylenebis (4,6-dimethylphenol), 2,2'-ethylidenebisphenol, 2,2'-ethylidenebis (4-methylphenol), 2,2'-isopropylidenebisphenol, 2,2'-methylenebis (4-methyl-6-tert-butylphenol), 2,2′-methylenebis (4-ethyl-6-tert-butylphenol), 2,2′-methylenebis (4,6-di-tert-butylphenol), 2, 2'-methylenebis (4-methyl-6-cyclohexylphenol), 2,2'-dihydroxy-3,3'-di α-methylcyclohexyl) -5,5′-dimethylphenylmethane, 2,2′-methylenebis (6-α-methyl-benzyl-p-cresol), 2,2′-ethylidene-bis (4,6-di-) tert-butylphenol), 2,2-butylidene-bis (4-methyl-6-tert-butylphenol), and the like, and 2,2′-methylenebis (4-methyl-6-tert-butylphenol), 2,2 '-Methylenebis (4-ethyl-6-tert-butylphenol), 2,2'-methylenebis (4,6-di-tert-butylphenol), 2,2'-ethylidene-bis (4,6-di-tert- Butylphenol) and 2,2′-butylidene-bis (4-methyl-6-tert-butylphenol) are preferred.

一方、一般式（１７）の化合物の具体例としては、フェノール、２−メチルフェノール、３−メチルフェノール、４−メチルフェノール、２，４−ジメチルフェノール、２，６−ジメチルフェノール、２−ｔｅｒｔ−ブチル−４−メチルフェノール、２，４−ジ−ｔｅｒｔ−ブチルフェノール、２，６−ジ−ｔｅｒｔ−ブチルフェノール、２，６−ジ−ｔｅｒｔ−ブチル−４−メチルフェノール、２，４−ジメチル−６−ｔｅｒｔ−ブチルフェノール、２，６−ジ−ｔｅｒｔ−ブチル−４−エチルフェノール、２，４，６−トリ−ｔｅｒｔ−ブチルフェノール、および２，６−ジ−ｔｅｒｔ−ブチル−４−ｓ−ブチルフェノールなどが挙げられ、アルキル置換基を２つ以上有する化合物が好ましい。   On the other hand, specific examples of the compound of the general formula (17) include phenol, 2-methylphenol, 3-methylphenol, 4-methylphenol, 2,4-dimethylphenol, 2,6-dimethylphenol, 2-tert- Butyl-4-methylphenol, 2,4-di-tert-butylphenol, 2,6-di-tert-butylphenol, 2,6-di-tert-butyl-4-methylphenol, 2,4-dimethyl-6 Examples include tert-butylphenol, 2,6-di-tert-butyl-4-ethylphenol, 2,4,6-tri-tert-butylphenol, and 2,6-di-tert-butyl-4-s-butylphenol. And compounds having two or more alkyl substituents are preferred.

本発明の樹脂組成物に配合することができる酸化防止剤としてはフェノール系酸化防止剤を挙げることができる。フェノール系酸化防止剤により熱暴露時の変色を抑制できると共に、難燃性の向上に対してもある程度の効果を発揮する。かかるフェノール系酸化防止剤としては種々のものを使用することができる。   Examples of the antioxidant that can be added to the resin composition of the present invention include phenolic antioxidants. The phenolic antioxidant can suppress discoloration when exposed to heat and exhibits a certain degree of effect on improving flame retardancy. Various types of such phenolic antioxidants can be used.

かかるフェノール系酸化防止剤の具体例としては、例えばビタミンＥ、ｎ−オクタデシル−β−（４’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェル）プロピオネート、２−ｔｅｒｔ−ブチル−６−（３’−ｔｅｒｔ−ブチル−５’−メチル−２’−ヒドロキシベンジル）−４−メチルフェニルアクリレート、２，６−ジ−ｔｅｒｔ−ブチル−４−（Ｎ，Ｎ−ジメチルアミノメチル）フェノール、３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシベンジルホスホネートジエチルエステル、２，２’−メチレンビス（４−メチル−６−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４−エチル−６−ｔｅｒｔ−ブチルフェノール）、４，４’−メチレンビス（２，６−ジ−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４−メチル−６−シクロヘキシルフェノール）、２，２’−ジメチレン−ビス（６−α−メチル−ベンジル−ｐ−クレゾール）２，２’−エチリデン−ビス（４，６−ジ−ｔｅｒｔ−ブチルフェノール）、２，２’−ブチリデン−ビス（４−メチル−６−ｔｅｒｔ−ブチルフェノール）、４，４’−ブチリデンビス（３−メチル−６−ｔｅｒｔ−ブチルフェノール）、トリエチレングリコール−Ｎ−ビス−３−（３−ｔｅｒｔ−ブチル−４−ヒドロキシ−５−メチルフェニル）プロピオネート、１，６−へキサンジオールビス［３−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオネート、ビス［２−ｔｅｒｔ−ブチル−４−メチル６−（３−ｔｅｒｔ−ブチル−５−メチル−２−ヒドロキシベンジル）フェニル］テレフタレート、３，９−ビス｛２−［３−（３−ｔｅｒｔ−ブチル−４−ヒドロキシ−５−メチルフェニル）プロピオニルオキシ］−１，１，−ジメチルエチル｝−２，４，８，１０−テトラオキサスピロ［５，５］ウンデカン、４，４’−チオビス（６−ｔｅｒｔ−ブチル−ｍ−クレゾール）、４，４’−チオビス（３−メチル−６−ｔｅｒｔ−ブチルフェノール）、２，２’−チオビス（４−メチル−６−ｔｅｒｔ−ブチルフェノール）、ビス（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシベンジル）スルフィド、４，４’−ジ−チオビス（２，６−ジ−ｔｅｒｔ−ブチルフェノール）、４，４’−トリ−チオビス（２，６−ジ−ｔｅｒｔ−ブチルフェノール）、２，４−ビス（ｎ−オクチルチオ）−６−（４−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルアニリノ）−１，３，５−トリアジン、Ｎ，Ｎ’−ヘキサメチレンビス−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシヒドロシンナミド）、Ｎ，Ｎ’−ビス［３−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオニル］ヒドラジン、１，１，３−トリス（２−メチル−４−ヒドロキシ−５−ｔｅｒｔ−ブチルフェニル）ブタン、１，３，５−トリメチル−２，４，６−トリス（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシベンジル）ベンゼン、トリス（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）イソシアヌレート、トリス（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシベンジル）イソシアヌレート、１，３，５−トリス（４−ｔｅｒｔ−ブチル−３−ヒドロキシ−２，６−ジメチルベンジル）イソシアヌレート、１，３，５−トリス２［３（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオニルオキシ］エチルイソシアヌレート、テトラキス［メチレン−３−（３’，５’−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］メタンなどを挙げることができ、好ましく使用できる。   Specific examples of such phenolic antioxidants include, for example, vitamin E, n-octadecyl-β- (4′-hydroxy-3 ′, 5′-di-tert-butylfel) propionate, 2-tert-butyl-6- (3′-tert-butyl-5′-methyl-2′-hydroxybenzyl) -4-methylphenyl acrylate, 2,6-di-tert-butyl-4- (N, N-dimethylaminomethyl) phenol, 3 , 5-Di-tert-butyl-4-hydroxybenzylphosphonate diethyl ester, 2,2'-methylenebis (4-methyl-6-tert-butylphenol), 2,2'-methylenebis (4-ethyl-6-tert- Butylphenol), 4,4'-methylenebis (2,6-di-tert-butylphenol), 2,2'-me Renbis (4-methyl-6-cyclohexylphenol), 2,2′-dimethylene-bis (6-α-methyl-benzyl-p-cresol) 2,2′-ethylidene-bis (4,6-di-tert- Butylphenol), 2,2'-butylidene-bis (4-methyl-6-tert-butylphenol), 4,4'-butylidenebis (3-methyl-6-tert-butylphenol), triethylene glycol-N-bis-3 -(3-tert-butyl-4-hydroxy-5-methylphenyl) propionate, 1,6-hexanediol bis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate, bis [ 2-tert-butyl-4-methyl 6- (3-tert-butyl-5-methyl-2-hydroxybenzyl) fe Ru] terephthalate, 3,9-bis {2- [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionyloxy] -1,1, -dimethylethyl} -2,4,8, 10-tetraoxaspiro [5,5] undecane, 4,4′-thiobis (6-tert-butyl-m-cresol), 4,4′-thiobis (3-methyl-6-tert-butylphenol), 2, 2′-thiobis (4-methyl-6-tert-butylphenol), bis (3,5-di-tert-butyl-4-hydroxybenzyl) sulfide, 4,4′-di-thiobis (2,6-di-) tert-butylphenol), 4,4′-tri-thiobis (2,6-di-tert-butylphenol), 2,4-bis (n-octylthio) -6- (4-hydroxy 3 ', 5'-di-tert-butylanilino) -1,3,5-triazine, N, N'-hexamethylenebis- (3,5-di-tert-butyl-4-hydroxyhydrocinnamide), N , N′-bis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionyl] hydrazine, 1,1,3-tris (2-methyl-4-hydroxy-5-tert-butylphenyl) ) Butane, 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl) benzene, tris (3,5-di-tert-butyl-4-) Hydroxyphenyl) isocyanurate, tris (3,5-di-tert-butyl-4-hydroxybenzyl) isocyanurate, 1,3,5-tris (4-tert-butyl-3- Hydroxy-2,6-dimethylbenzyl) isocyanurate, 1,3,5-tris 2 [3 (3,5-di-tert-butyl-4-hydroxyphenyl) propionyloxy] ethyl isocyanurate, tetrakis [methylene-3 -(3 ', 5'-di-tert-butyl-4-hydroxyphenyl) propionate] methane can be mentioned and can be preferably used.

より好ましくは、ｎ−オクタデシル−β−（４’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェル）プロピオネート、２−ｔｅｒｔ−ブチル−６−（３’−ｔｅｒｔ−ブチル−５’−メチル−２’−ヒドロキシベンジル）−４−メチルフェニルアクリレート、３，９−ビス｛２−［３−（３−ｔｅｒｔ−ブチル−４−ヒドロキシ−５−メチルフェニル）プロピオニルオキシ］−１，１，−ジメチルエチル｝−２，４，８，１０−テトラオキサスピロ［５，５］ウンデカン、およびテトラキス［メチレン−３−（３’，５’−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］メタンであり、さらにｎ−オクタデシル−β−（４’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェル）プロピオネートが好ましい。   More preferably, n-octadecyl-β- (4′-hydroxy-3 ′, 5′-di-tert-butylfel) propionate, 2-tert-butyl-6- (3′-tert-butyl-5′-methyl) -2'-hydroxybenzyl) -4-methylphenyl acrylate, 3,9-bis {2- [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionyloxy] -1,1,- Dimethylethyl} -2,4,8,10-tetraoxaspiro [5,5] undecane and tetrakis [methylene-3- (3 ′, 5′-di-tert-butyl-4-hydroxyphenyl) propionate] methane Further, n-octadecyl-β- (4′-hydroxy-3 ′, 5′-di-tert-butylfel) propionate is preferable.

また、酸化防止剤としてイオウ含有酸化防止剤を使用することもできる。特に樹脂組成物が回転成形や圧縮成形に使用される場合には好適である。かかるイオウ含有酸化防止剤の具体例としては、ジラウリル−３，３’−チオジプロピオン酸エステル、ジトリデシル−３，３’−チオジプロピオン酸エステル、ジミリスチル−３，３’−チオジプロピオン酸エステル、ジステアリル−３，３’−チオジプロピオン酸エステル、ラウリルステアリル−３，３’−チオジプロピオン酸エステル、ペンタエリスリトールテトラ（β−ラウリルチオプロピオネート）エステル、ビス［２−メチル−４−（３−ラウリルチオプロピオニルオキシ）−５−ｔｅｒｔ−ブチルフェニル］スルフィド、オクタデシルジスルフィド、メルカプトベンズイミダゾール、２−メルカプト−６−メチルベンズイミダゾール、１，１’−チオビス（２−ナフトール）などを挙げることができる。より好ましくは、ペンタエリスリトールテトラ（β−ラウリルチオプロピオネート）エステルを挙げることができる。   Also, a sulfur-containing antioxidant can be used as the antioxidant. It is particularly suitable when the resin composition is used for rotational molding or compression molding. Specific examples of such sulfur-containing antioxidants include dilauryl-3,3'-thiodipropionate, ditridecyl-3,3'-thiodipropionate, dimyristyl-3,3'-thiodipropionate. , Distearyl-3,3′-thiodipropionate, laurylstearyl-3,3′-thiodipropionate, pentaerythritol tetra (β-laurylthiopropionate) ester, bis [2-methyl-4 -(3-laurylthiopropionyloxy) -5-tert-butylphenyl] sulfide, octadecyl disulfide, mercaptobenzimidazole, 2-mercapto-6-methylbenzimidazole, 1,1′-thiobis (2-naphthol) and the like. be able to. More preferably, a pentaerythritol tetra ((beta) -lauryl thiopropionate) ester can be mentioned.

上記に挙げたリン含有熱安定剤、フェノール系酸化防止剤、およびイオウ含有酸化防止剤はそれぞれ単独または２種以上併用することができる。より好ましくはリン含有安定剤であり、特にリン含有熱安定剤として上記一般式（１４）の化合物を含んでいることが好ましい。   The phosphorus-containing heat stabilizer, phenolic antioxidant, and sulfur-containing antioxidant listed above can be used alone or in combination of two or more. A phosphorus-containing stabilizer is more preferable, and it is particularly preferable that the phosphorus-containing heat stabilizer contains the compound of the general formula (14).

これらの安定剤の組成物中の割合としては、芳香族ポリカーボネート樹脂（Ａ成分）１００重量部当たり、リン含有安定剤、フェノール系酸化防止剤、またはイオウ含有酸化防止剤はそれぞれ０．０００１〜１重量部であることが好ましい。より好ましくは０．０００５〜０．５重量部であり、さらに好ましくは０．００１〜０．２重量部である。   The proportion of these stabilizers in the composition is 0.0001 to 1 for each of the phosphorus-containing stabilizer, phenol-based antioxidant, or sulfur-containing antioxidant per 100 parts by weight of the aromatic polycarbonate resin (component A). It is preferable that it is a weight part. More preferably, it is 0.0005-0.5 weight part, More preferably, it is 0.001-0.2 weight part.

本発明の樹脂組成物には、必要に応じて離型剤を配合することができる。本発明においてはＢ成分を含有することにより難燃性を有するため、通常難燃性に対して悪影響を及ぼしやすい離型剤を配合した場合であっても、良好な難燃性を達成することができる。かかる離型剤としてはそれ自体公知のものが使用できる。例えば、飽和脂肪酸エステル、不飽和脂肪酸エステル、ポリオレフィン系ワックス（ポリエチレンワックスまたは１−アルケン重合体が挙げられる。これらは酸変性などの官能基含有化合物で変性されているものも使用できる）、シリコーン化合物（本発明のＢ成分以外のもの。例えば直鎖状または環状のポリジメチルシロキサンオイルやポリメチルフェニルシリコーンオイルなどが挙げられる。これらは酸変性などの官能基含有化合物で変性されているものも使用できる）、フッ素化合物（ポリフルオロアルキルエーテルに代表されるフッ素オイルなど）、パラフィンワックス、蜜蝋などを挙げることができる。これらの中でも飽和脂肪酸エステル類、直鎖状または環状のポリジメチルシロキサンオイルやポリメチルフェニルシリコーンオイルなど、およびフッ素オイルを挙げることができる。好ましい離型剤としては飽和脂肪酸エステルが挙げられ、例えばステアリン酸モノグリセライドなどのモノグリセライド類、デカグリセリンデカステアレートおよびデカグリセリンテトラステアレート等のポリグリセリン脂肪酸エステル類、ステアリン酸ステアレートなどの低級脂肪酸エステル類、セバシン酸ベヘネートなどの高級脂肪酸エステル類、ペンタエリスリトールテトラステアレートなどのエリスリトールエステル類が使用される。かかる離型剤の含有量は芳香族ポリカーボネート樹脂（Ａ成分）１００重量部に対して０．０１〜０．３重量部が好ましい。   A release agent can be blended in the resin composition of the present invention as necessary. In the present invention, since it has flame retardancy by containing B component, it is possible to achieve good flame retardancy even when a release agent that usually has an adverse effect on flame retardancy is blended. Can do. As such a release agent, those known per se can be used. For example, saturated fatty acid ester, unsaturated fatty acid ester, polyolefin wax (polyethylene wax or 1-alkene polymer may be used. These may be modified with a functional group-containing compound such as acid modification), silicone compounds (Other than the component B of the present invention. For example, linear or cyclic polydimethylsiloxane oil, polymethylphenyl silicone oil, etc. are used. Those modified with a functional group-containing compound such as acid modification are also used. ), Fluorine compounds (fluorine oil typified by polyfluoroalkyl ether, etc.), paraffin wax, beeswax and the like. Among these, saturated fatty acid esters, linear or cyclic polydimethylsiloxane oil, polymethylphenyl silicone oil, and fluorine oil can be mentioned. Preferable mold release agents include saturated fatty acid esters. For example, monoglycerides such as stearic acid monoglyceride, polyglycerin fatty acid esters such as decaglycerin decastate and decaglycerin tetrastearate, and lower fatty acid esters such as stearic acid stearate. , Higher fatty acid esters such as sebacic acid behenate, and erythritol esters such as pentaerythritol tetrastearate are used. The content of the release agent is preferably 0.01 to 0.3 parts by weight with respect to 100 parts by weight of the aromatic polycarbonate resin (component A).

本発明の樹脂組成物は、ＯＡ機器の筐体などに使用されることが多いため、紫外線吸収剤を含んでいることが好ましい。紫外線吸収剤としては、例えば２，４−ジヒドロキシベンゾフェノン、２−ヒドロキシ−４−メトキシベンゾフェノン、２−ヒドロキシ−４−ｎ−オクトキシベンゾフェノン、２−ヒドロキシ−４−ｎ−ドデシルオキシベンゾフェノン、２−ヒドロキシ−４−ベンジロキシベンゾフェノン、２，２’−ジヒドロキシ−４−メトキシベンゾフェノン、２−ヒドロキシ−４−メトキシ−２’−カルボキシベンゾフェノン、２−ヒドロキシ−４−メトキシ−５−スルホキシベンゾフェノン、２，２’−ジヒドロキシ−４，４’−ジメトキシベンゾフェノン、２，２’，４，４’−テトラヒドロキシベンゾフェノン、２，２’−ジヒドロキシ−４，４’−ジメトキシ−５−ソジウムスルホキシベンゾフェノン、ビス（５−ベンゾイル−４−ヒドロキシ−２−メトキシフェニル）メタンなどに代表されるベンゾフェノン系紫外線吸収剤を挙げることができる。   Since the resin composition of the present invention is often used for a housing of OA equipment or the like, it is preferable that the resin composition contains an ultraviolet absorber. Examples of the ultraviolet absorber include 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-n-octoxybenzophenone, 2-hydroxy-4-n-dodecyloxybenzophenone, and 2-hydroxy. -4-benzyloxybenzophenone, 2,2'-dihydroxy-4-methoxybenzophenone, 2-hydroxy-4-methoxy-2'-carboxybenzophenone, 2-hydroxy-4-methoxy-5-sulfoxybenzophenone, 2,2 '-Dihydroxy-4,4'-dimethoxybenzophenone, 2,2', 4,4'-tetrahydroxybenzophenone, 2,2'-dihydroxy-4,4'-dimethoxy-5-sodiumsulfoxybenzophenone, bis ( 5-benzoyl-4-hydroxy 2-methoxyphenyl) benzophenone ultraviolet absorbers typified by methane and the like.

また紫外線吸収剤としては例えば２−（２’−ヒドロキシ−５’−メチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−５’−ｔｅｒｔ−ブチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−５’−ｔｅｒｔ−オクチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−アミルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−３’−ドデシル−５’−メチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５’−ビス（α，α’−ジメチルベンジル）フェニルベンゾトリアゾール、２−［２’−ヒドロキシ−３’−（３”，４”，５”，６”−テトラフタルイミドメチル）−５’−メチルフェニル］ベンゾトリアゾール、２−（２’−ヒドロキシ−３’−ｔｅｒｔ−ブチル−５’−メチルフェニル）−５−クロロベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェニル）−５−クロロベンゾトリアゾール、２，２’メチレンビス［４−（１，１，３，３−テトラメチルブチル）−６−（２Ｈ−ベンゾトリアゾール−２−イル）フェノール］、メチル−３−［３−ｔｅｒｔ−ブチル−５−（２Ｈ−ベンゾトリアゾール−２−イル）−４−ヒドロキシフェニルプロピオネート−ポリエチレングリコールとの縮合物に代表されるベンゾトリアゾール系紫外線吸収剤を挙げることができる。   Examples of the ultraviolet absorber include 2- (2′-hydroxy-5′-methylphenyl) benzotriazole, 2- (2′-hydroxy-5′-tert-butylphenyl) benzotriazole, and 2- (2′-hydroxy). -5'-tert-octylphenyl) benzotriazole, 2- (2'-hydroxy-3 ', 5'-di-tert-butylphenyl) benzotriazole, 2- (2'-hydroxy-3', 5'- Di-tert-amylphenyl) benzotriazole, 2- (2′-hydroxy-3′-dodecyl-5′-methylphenyl) benzotriazole, 2- (2′-hydroxy-3 ′, 5′-bis (α, α'-dimethylbenzyl) phenylbenzotriazole, 2- [2'-hydroxy-3 '-(3 ", 4", 5 ", 6" -tetraphthal Ruimidomethyl) -5'-methylphenyl] benzotriazole, 2- (2'-hydroxy-3'-tert-butyl-5'-methylphenyl) -5-chlorobenzotriazole, 2- (2'-hydroxy-3 ' , 5'-di-tert-butylphenyl) -5-chlorobenzotriazole, 2,2'methylenebis [4- (1,1,3,3-tetramethylbutyl) -6- (2H-benzotriazole-2- Yl) phenol], methyl-3- [3-tert-butyl-5- (2H-benzotriazol-2-yl) -4-hydroxyphenylpropionate-benzotriazole ultraviolet rays typified by condensation products with polyethylene glycol An absorbent can be mentioned.

さらに紫外線吸収剤としては例えば、２−（４，６−ジフェニル−１，３，５−トリアジン−２−イル）−５−ヘキシルオキシ−フェノール、２−（４，６−ビス−（２，４−ジメチルフェニル−１，３，５−トリアジン−２−イル）−５−ヘキシルオキシ−フェノールなどのヒドロキシフェニルトリアジン系化合物を挙げることができる。   Further, examples of the ultraviolet absorber include 2- (4,6-diphenyl-1,3,5-triazin-2-yl) -5-hexyloxy-phenol, 2- (4,6-bis- (2,4 There may be mentioned hydroxyphenyltriazine compounds such as -dimethylphenyl-1,3,5-triazin-2-yl) -5-hexyloxy-phenol.

本発明の樹脂組成物には、光安定剤を配合することもできる。かかる光安定剤としては、例えばビス（２，２，６，６−テトラメチル−４−ピペリジル）セバケート、ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）セバケート、ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）−２−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシベンジル）−２ｎ−ブチルマロネート、１，２，３，４−ブタンカルボン酸と２，２，６，６−テトラメチル−４−ピペリジノールとトリデシルアルコールとの縮合物、１，２，３，４−ブタンジカルボン酸と１，２，２，６，６−ペンタメチル−４−ピペリジノールとトリデシルアルコールとの縮合物、テトラキス（２，２，６，６−テトラメチル−４−ピペリジル）−１，２，３，４−ブタンテトラカルボキシレート、テトラキス（１，２，２，６，６−ペンタメチル−４−ピペリジル）−１，２，３，４−ブタンテトラカルボキシレート、ポリ｛［６−（１，１，３，３−テトラメチルブチル）アミノ−１，３，５−トリアジン−２，４−ジイル］［（２，２，６，６−テトラメチルピペリジル）イミノ］ヘキサメチレン［（２，２，６，６−テトラメチルピペリジル）イミノ］｝、ポリ｛［６−モルフォリノ−ｓ−トリアジン−２，４−ジイル］［（２，２，６，６−テトラメチルピペリジル）イミノ］ヘキサメチレン［（２，２，６，６−テトラメチルピペリジル）イミノ］｝、１，２，３，４−ブタンテトラカルボン酸と２，２，６，６−テトラメチル−４−ピペリジノールとβ，β，β’，β’−テトラメチル−３，９−（２，４，８，１０−テトラオキサスピロ［５，５］ウンデカン）ジエタノールとの縮合物、Ｎ，Ｎ’−ビス（３−アミノプロピル）エチレンジアミンと２，４−ビス［Ｎ−ブチル−Ｎ−（１，２，２，６，６−ペンタメチル−４−ピペリジル）アミノ］−クロロ−１，３，５−トリアジンとの縮合物、１，２，３，４−ブタンテトラカルボン酸と１，２，２，６，６−ペンタメチル−４−ピペリジノールとβ，β，β’，β’−テトラメチル−３，９−（２，４，８，１０−テトラオキサスピロ［５，５］ウンデカン）ジエタノールとの縮合物、ポリメチルプロピル３−オキシ−［４−（２，２，６，６−テトラメチル）ピペリジニル］シロキサンに代表されるヒンダードアミンが挙げられる。   A light stabilizer can also be mix | blended with the resin composition of this invention. Examples of such light stabilizers include bis (2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis (1,2,2,6,6-pentamethyl-4-piperidyl) sebacate, and bis (1 , 2,2,6,6-pentamethyl-4-piperidyl) -2- (3,5-di-tert-butyl-4-hydroxybenzyl) -2n-butyl malonate, 1,2,3,4-butane Condensation product of carboxylic acid, 2,2,6,6-tetramethyl-4-piperidinol and tridecyl alcohol, 1,2,3,4-butanedicarboxylic acid and 1,2,2,6,6-pentamethyl- A condensate of 4-piperidinol and tridecyl alcohol, tetrakis (2,2,6,6-tetramethyl-4-piperidyl) -1,2,3,4-butanetetracarboxylate, tetrakis (1, , 2,6,6-pentamethyl-4-piperidyl) -1,2,3,4-butanetetracarboxylate, poly {[6- (1,1,3,3-tetramethylbutyl) amino-1,3 , 5-triazine-2,4-diyl] [(2,2,6,6-tetramethylpiperidyl) imino] hexamethylene [(2,2,6,6-tetramethylpiperidyl) imino]}, poly {[ 6-morpholino-s-triazine-2,4-diyl] [(2,2,6,6-tetramethylpiperidyl) imino] hexamethylene [(2,2,6,6-tetramethylpiperidyl) imino]}, 1,2,3,4-butanetetracarboxylic acid, 2,2,6,6-tetramethyl-4-piperidinol and β, β, β ′, β′-tetramethyl-3,9- (2,4, 8,10-tetraoxaspiro [5 5] Condensate with undecane) diethanol, N, N′-bis (3-aminopropyl) ethylenediamine and 2,4-bis [N-butyl-N- (1,2,2,6,6-pentamethyl-4) -Piperidyl) amino] -chloro-1,3,5-triazine condensate, 1,2,3,4-butanetetracarboxylic acid, 1,2,2,6,6-pentamethyl-4-piperidinol and β , Β, β ′, β′-tetramethyl-3,9- (2,4,8,10-tetraoxaspiro [5,5] undecane) diethanol, polymethylpropyl 3-oxy- [4 Hindered amines represented by-(2,2,6,6-tetramethyl) piperidinyl] siloxane.

紫外線吸収剤および光安定剤の含有量は、それぞれ芳香族ポリカーボネート樹脂（Ａ成分）１００重量部当たり０．０１〜５重量部が好ましく、より好ましくは０．０２〜１重量部である。   The content of the ultraviolet absorber and the light stabilizer is preferably 0.01 to 5 parts by weight, more preferably 0.02 to 1 part by weight, per 100 parts by weight of the aromatic polycarbonate resin (component A).

また、本発明の樹脂組成物には紫外線吸収剤などに基づく黄色味を打ち消すためにブルーイング剤を配合することができる。ブルーイング剤としては通常ポリカーボネート樹脂に使用されるものであれば、特に支障なく使用することができる。一般的にはアンスラキノン系染料が入手容易であり好ましい。具体的なブルーイング剤としては、例えば一般名Ｓｏｌｖｅｎｔ Ｖｉｏｌｅｔ１３［ＣＡ．Ｎｏ（カラーインデックスＮｏ）６０７２５；商標名 バイエル社製「マクロレックスバイオレットＢ」、三菱化学（株）製「ダイアレジンブルーＧ」、住友化学工業（株）製「スミプラストバイオレットＢ」］、一般名Ｓｏｌｖｅｎｔ Ｖｉｏｌｅｔ３１［ＣＡ．Ｎｏ６８２１０；商標名 三菱化学（株）製「ダイアレジンバイオレットＤ」］、一般名Ｓｏｌｖｅｎｔ Ｖｉｏｌｅｔ３３［ＣＡ．Ｎｏ６０７２５；商標名 三菱化学（株）製「ダイアレジンブルーＪ」］、一般名Ｓｏｌｖｅｎｔ Ｂｌｕｅ９４［ＣＡ．Ｎｏ６１５００；商標名 三菱化学（株）製「ダイアレジンブルーＮ」］、一般名Ｓｏｌｖｅｎｔ Ｖｉｏｌｅｔ３６［ＣＡ．Ｎｏ６８２１０；商標名 バイエル社製「マクロレックスバイオレット３Ｒ」］、一般名Ｓｏｌｖｅｎｔ Ｂｌｕｅ９７［商標名 バイエル社製「マクロレックスブルーＲＲ」］および一般名Ｓｏｌｖｅｎｔ Ｂｌｕｅ４５［ＣＡ．Ｎｏ６１１１０；商標名 サンド社製「テラゾールブルーＲＬＳ」］等が挙げられ、特に、マクロレックスブルーＲＲ、マクロレックスバイオレットＢやテラゾールブルーＲＬＳが好ましい。ブルーイング剤の含有量は芳香族ポリカーボネート樹脂（Ａ成分）１００重量部当たり０．０００００５〜０．００１０重量部が好ましく、より好ましくは０．００００１〜０．０００１重量部である。   In addition, a blueing agent can be blended in the resin composition of the present invention in order to counteract the yellowishness based on the ultraviolet absorber and the like. Any bluing agent can be used without any problem as long as it is usually used for polycarbonate resin. In general, anthraquinone dyes are preferred because they are readily available. Specific examples of the bluing agent include the general name Solvent Violet 13 [CA. No. (Color Index No.) 60725; Trade names “Macrolex Violet B” manufactured by Bayer, “Diaresin Blue G” manufactured by Mitsubishi Chemical Corporation, “Sumiplast Violet B” manufactured by Sumitomo Chemical Co., Ltd.], general name Solvent Violet 31 [CA. No. 68210; Trade name “Diaresin Violet D” manufactured by Mitsubishi Chemical Corporation], generic name Solvent Violet 33 [CA. No. 60725; trade name “Diaresin Blue J” manufactured by Mitsubishi Chemical Corporation], generic name Solvent Blue 94 [CA. No. 61500; trade name “Diaresin Blue N” manufactured by Mitsubishi Chemical Corporation, generic name Solvent Violet 36 [CA. No. 68210; Trade name: “Macrolex Violet 3R” manufactured by Bayer, Inc., generic name: Solvent Blue 97 [trade name: “Macrolex Blue RR” manufactured by Bayer, Inc.], and generic name: Solvent Blue 45 [CA. No. 61110; trade name “Terrazol Blue RLS” manufactured by Sand Corp.] and the like, and Macrolex Blue RR, Macrolex Violet B and Terrazol Blue RLS are particularly preferable. The content of the bluing agent is preferably 0.000005 to 0.0010 parts by weight, more preferably 0.00001 to 0.0001 parts by weight per 100 parts by weight of the aromatic polycarbonate resin (component A).

本発明の樹脂組成物はドリップ防止性に優れるが、かかる性能をさらに補強するため通常のドリップ防止剤を併用することができる。しかしながら本発明の樹脂組成物において、かかる透明性を損なわないためその配合量はＡ成分１００重量部に対し０．２重量部以下が適切であり、０．１重量部以下が好ましく、０．０８重量部以下がより好ましく、０．０５重量部以下がさらに好ましい。かかるドリップ防止剤としてはフィブリル形成能を有する含フッ素ポリマーを挙げることができる。特にポリテトラフルオロエチレン（以下ＰＴＦＥと称することがある）が好ましい。ここでいう透明性を損なわないとは、例えば、２ｍｍ厚みのプレートのＨａｚｅが５％を超えない量のＰＴＦＥを使用するということである。フィブリル形成能を有するＰＴＦＥの分子量は極めて高い分子量を有し、せん断力などの外的作用によりＰＴＦＥ同士を結合して繊維状になる傾向を示すものである。その分子量は、標準比重から求められる数平均分子量において１００万〜１，０００万、より好ましくは２００万〜９００万である。かかるＰＴＦＥは、固体形状の他、水性分散液形態のものも使用可能である。またかかるフィブリル形成能を有するＰＴＦＥは樹脂中での分散性を向上させ、さらに良好な難燃性および透明性を得るために他の樹脂との混合形態のＰＴＦＥ混合物を使用することも可能である。混合形態のＰＴＦＥの市販品としては、三菱レイヨン（株）の「メタブレン Ａ３０００」（商品名）、「メタブレン Ａ３７００」（商品名）、「メタブレン Ａ３７５０」（商品名）、およびＧＥスペシャリティーケミカルズ社製「ＢＬＥＮＤＥＸ Ｂ４４９」（商品名）などを挙げることができる。   The resin composition of the present invention is excellent in anti-drip properties, but a normal anti-drip agent can be used in combination to further reinforce such performance. However, in the resin composition of the present invention, the blending amount is suitably 0.2 parts by weight or less, preferably 0.1 parts by weight or less, and preferably 0.08 parts by weight or less with respect to 100 parts by weight of component A in order not to impair such transparency. More preferred is less than or equal to parts by weight and even more preferred is less than or equal to 0.05 parts by weight. Examples of such an anti-drip agent include a fluorine-containing polymer having a fibril forming ability. Polytetrafluoroethylene (hereinafter sometimes referred to as PTFE) is particularly preferable. The term “transparency” does not impair transparency, for example, to use PTFE in an amount that does not exceed 5% of the Haze of a 2 mm thick plate. PTFE having a fibril forming ability has a very high molecular weight, and tends to be bonded to each other by an external action such as shearing force to form a fiber. The molecular weight is 1 million to 10 million, more preferably 2 million to 9 million in the number average molecular weight determined from the standard specific gravity. Such PTFE can be used in solid form or in the form of an aqueous dispersion. In addition, PTFE having such fibril-forming ability can improve the dispersibility in the resin, and it is also possible to use a PTFE mixture in a mixed form with other resins in order to obtain better flame retardancy and transparency. . Commercially available products of PTFE in a mixed form include “Metablene A3000” (trade name), “Metablene A3700” (trade name), “Metablene A3750” (trade name) manufactured by Mitsubishi Rayon Co., Ltd., and GE Specialty Chemicals “BLENDEX B449” (trade name) and the like.

＜樹脂組成物からなる押し出し成形品の製造について＞
本発明の樹脂組成物からなる押し出し成形品を製造するには、任意の方法が採用される。例えばＡ成分、Ｂ成分および任意に他の成分をそれぞれＶ型ブレンダー、ヘンシェルミキサー、メカノケミカル装置、押出混合機などの予備混合手段を用いて充分に混合した後、必要に応じて押出造粒器やブリケッティングマシーンなどにより造粒を行い、その後溶融押し出ししてシート（異型シートを含む）を製造することができる。別法として、Ａ成分、Ｂ成分および任意に他の成分をそれぞれ独立にベント式二軸ルーダーに代表される溶融混練機に供給する方法、Ａ成分および他の成分の一部を予備混合した後、残りの成分と独立に溶融混練機に供給する方法、Ｂ成分を水または有機溶剤で希釈混合した後、溶融混練機に供給、またはかかる希釈混合物を他の成分と予備混合した後、溶融混練機に供給する方法なども挙げられる。なお、配合する成分に液状のものがある場合には、溶融混練機への供給にいわゆる液注装置、または液添装置を使用することができる。 <About the manufacture of an extrusion molded product comprising a resin composition>
In order to produce an extrusion-molded article comprising the resin composition of the present invention, any method is adopted. For example, component A, component B and optionally other components are mixed thoroughly using premixing means such as a V-type blender, Henschel mixer, mechanochemical apparatus, extrusion mixer, etc., and then an extrusion granulator as necessary. Or a briquetting machine or the like, and then melt-extruded to produce a sheet (including an atypical sheet). Alternatively, the A component, the B component and optionally other components are each independently fed to a melt kneader represented by a vented twin-screw rudder, and after pre-mixing part of the A component and other components , A method of supplying to the melt kneader independently of the remaining components, the component B is diluted and mixed with water or an organic solvent, and then supplied to the melt kneader, or the diluted mixture is premixed with other components and then melt kneaded. The method of supplying to a machine is also mentioned. In addition, when there exists a liquid thing in the component to mix | blend, what is called a liquid injection apparatus or a liquid addition apparatus can be used for supply to a melt kneader.

また賦型シートは、例えば凸形状やＶ字形状を有する賦型ロールを用いて、溶融押し出ししたシートを製造する方法であり、賦型の形状については特に制限するものではない。
さらに樹脂組成物から形成された押し出し成形品には、各種の表面処理を行うことが可能である。表面処理としては、加飾塗装、ハードコート、撥水・撥油コート、親水コート、紫外線吸収コート、赤外線吸収コート、電磁波吸収コート、発熱コート、帯電防止コート、制電コート、導電コート、並びにメタライジング（メッキ、化学蒸着（ＣＶＤ）、物理蒸着（ＰＶＤ）、溶射など）などの各種の表面処理を行うことができる。殊にシートや賦型シートは必要に応じて、片面または／および両面に、例えばＵＶカット機能、帯電防止性能、ＩＲカット性能、電磁波カット性能を有する層（透明導電層）を積層させた積層体であってもよい。積層体を得る方法としては、共押出による方法あるいは溶融押出した後に、ラミネートフィルムや転写箔を熱圧着させる方法がある。 The shaping sheet is a method for producing a melt-extruded sheet using, for example, a shaping roll having a convex shape or a V-shape, and the shaping shape is not particularly limited.
Furthermore, various surface treatments can be performed on the extrusion-molded product formed from the resin composition. Surface treatment includes decorative coating, hard coat, water / oil repellent coat, hydrophilic coat, UV absorbing coat, infrared absorbing coat, electromagnetic wave absorbing coat, heat generating coat, antistatic coat, antistatic coating, conductive coating, and meta coating. Various surface treatments such as rising (plating, chemical vapor deposition (CVD), physical vapor deposition (PVD), thermal spraying, etc.) can be performed. In particular, a sheet or a molded sheet is a laminate in which a layer (transparent conductive layer) having, for example, a UV cut function, an antistatic performance, an IR cut performance, and an electromagnetic wave cut performance is laminated on one side and / or both sides as required. It may be. As a method for obtaining a laminate, there are a method by coextrusion or a method in which a laminate film or a transfer foil is thermocompression bonded after melt extrusion.

これらの押し出し成形品は、真空成形、圧空成形等の熱成形に利用することができる。
またこれらの押し出し成形品は、照明用カバーまたは透過型ティスプレイ用カバー用途等に好適に使用される。
本発明者らが現在最良と考える本発明の形態は、前記の各要件の好ましい範囲を集約したものとなるが、例えば、その代表例を下記の実施例中に記載する。もちろん本発明はこれらの形態に限定されるものではない。 These extruded products can be used for thermoforming such as vacuum forming and pressure forming.
Further, these extruded products are suitably used for illumination covers or transmission-type display covers.
The form of the present invention considered to be the best by the present inventors is a collection of the preferable ranges of the above requirements. For example, typical examples are described in the following examples. Of course, the present invention is not limited to these forms.

以下に実施例を挙げてさらに説明するが、本発明はそれに限定されるものではない。尚、評価としては以下の項目について実施した。   The present invention will be further described below with reference to examples, but the present invention is not limited thereto. The following items were evaluated.

（ｉ）透明性
実施例の各組成から得られたシートから縦１５０ｍｍ×横１５０ｍｍ、厚さ１．５ｍｍプレートを切り出し、ＪＩＳ Ｋ７１０５でＨａｚｅを測定した。ヘーズが２％以下のものを○、２％より大きく２０％未満のものを△、２０％以上のものを×とした。 (I) Transparency A plate having a length of 150 mm × width of 150 mm and a thickness of 1.5 mm was cut out from the sheet obtained from each composition of the Examples, and the haze was measured according to JIS K7105. A haze of 2% or less was evaluated as ◯, a haze greater than 2% and less than 20% was evaluated as Δ, and a test having 20% or more as x.

（ii）シート外観
実施例の各組成から得られた幅約１０００ｍｍのシートにおいて目視による評価を行った。外観が良好なものを○、押出成形時におけるガスにより外観が悪化したものを×とした。 (Ii) Sheet Appearance Visual evaluation was performed on a sheet having a width of about 1000 mm obtained from each composition of the examples. A sample having a good appearance was marked with ◯, and a sample with a deteriorated appearance due to gas during extrusion molding was marked with ×.

（iii）難燃性
実施例の各組成から得られたシートから難燃性評価用の試験片を作成した。ＵＬ規格９４の垂直燃焼試験を、厚み２．２ｍｍ、１．５ｍｍ、１．２ｍｍで行いその等級を評価した。なお、判定がＶ−０、Ｖ−１、Ｖ−２のいずれの基準も満たすことが出来なかった場合「ｎｏｔＶ」と示すこととする。 (Iii) Flame retardance A test piece for flame retardancy evaluation was prepared from a sheet obtained from each composition of the examples. The vertical combustion test of UL standard 94 was conducted at thicknesses of 2.2 mm, 1.5 mm, and 1.2 mm, and the grade was evaluated. When the determination fails to satisfy any of the criteria of V-0, V-1, and V-2, “notV” is indicated.

（iv）分岐状ポリカーボネート中の分岐剤含有率
１Ｈ−ＮＭＲ（ＪＥＯＬ製ＪＮＭ−ＡＬ４００）を用いて芳香族ポリカーボネート樹脂中の分岐剤含有率を測定した。 (Iv) Branching agent content in branched polycarbonate The branching agent content in the aromatic polycarbonate resin was measured using 1H-NMR (JNM-AL400 manufactured by JEOL).

［実施例１〜３０、および比較例１〜６］
表１〜表３記載の配合割合からなる樹脂組成物を以下の要領で作成した。尚、説明は以下の表中の記号にしたがって説明する。表１〜表３の割合の各成分を計量して、タンブラーを用いて均一に混合し、かかる混合物をベント付きＴダイ押出機により、押出機温度２７０〜３２０℃、ダイス温度２９０〜３２０℃で幅約１０００ｍｍ、厚み２．２ｍｍ、１．５ｍｍ、１．２ｍｍのシートをそれぞれ溶融押し出しした。得られたシートを上記の方法を用い、難燃性評価用および透明性評価用の試験片を作成した。なお、表１〜表３に記載の使用した原料等は以下の通りである。 [Examples 1 to 30 and Comparative Examples 1 to 6]
The resin composition which consists of a mixture ratio of Table 1-Table 3 was created in the following ways. The description will be made according to the symbols in the following table. Each component in the ratio of Table 1 to Table 3 is weighed and uniformly mixed using a tumbler, and this mixture is subjected to a T-die extruder with a vent at an extruder temperature of 270 to 320 ° C. and a die temperature of 290 to 320 ° C. Sheets having a width of about 1000 mm, a thickness of 2.2 mm, 1.5 mm, and 1.2 mm were respectively melt extruded. Using the obtained sheet, a test piece for flame retardancy evaluation and transparency evaluation was prepared. The raw materials used in Tables 1 to 3 are as follows.

（Ａ成分）
（Ａ−１成分）
ＰＣ−Ｂ９Ｈ：分岐構造を有する芳香族ポリカーボネート樹脂（分岐率０．９７ｍｏｌ％、分子量２５，１００）
（ＰＣ−Ｂ９Ｈの製造方法）
温度計、攪拌機、還流冷却器付き反応器にイオン交換水２３４０部、２５％水酸化ナトリウム水溶液９４７部、ハイドロサルファイト０．７部を仕込み、攪拌下にビスフェノールＡ７１０部を溶解した（ビスフェノールＡ溶液）後、塩化メチレン２２９９部と４８．５％水酸化ナトリウム水溶液１１２部、１４％濃度の水酸化ナトリウム水溶液に１，１，１−トリス（４−ヒドロキシフェニル）エタンを２５％濃度で溶解した水溶液３８．１部（１．００ｍｏｌ％）を加えて、１５〜２５℃でホスゲン３５４部を約９０分かけて吹き込みホスゲン化反応を行った。
ホスゲン化終了後、１１％濃度のｐ−ｔｅｒｔ−ブチルフェノールの塩化メチレン溶液２１９部と４８．５％水酸化ナトリウム水溶液８８部を加えて、攪拌を停止し、１０分間静置分離後、攪拌を行い乳化させ５分後、ホモミキサー（特殊機化工業（株））で回転数１２００ｒｐｍ、バス回数３５回で処理し高乳化ドープを得た。該高乳化ドープを重合槽（攪拌機付き）で、無攪拌条件下、温度３５℃で３時間反応し重合を終了した。
反応終了後、塩化メチレン５７２８部を加えて希釈した後、反応混合液から塩化メチレン相を分離し、分離した塩化メチレン相にイオン交換水５０００部を加え攪拌混合した後、攪拌を停止し、水相と有機相を分離した。次に水相の導電率がイオン交換水と殆ど同じになるまで水洗浄を繰返し精製ポリカーボネート樹脂溶液を得た。次に、該精製ポリカーボネート樹脂溶液をイオン交換水１００Ｌを投入した１０００Ｌニーダーで、液温７５℃にて塩化メチレンを蒸発させて粉粒体を得た。該粉粒体２５部と水７５部を攪拌機付熱水処理槽に投入し、水温９５℃で３０分間攪拌混合した。
次いで、該粉粒体と水の混合物を遠心分離機で分離して、塩化メチレン０．５重量％、水４５重量％を含む粉粒体を得た。次に、この粉粒体を１４０℃にコントロールされているＳＵＳ３１６Ｌ製伝導受熱式溝型２軸攪拌連続乾燥機に５０ｋｇ／ｈｒ（ポリカーボネート樹脂換算）で連続供給して、平均乾燥時間３時間の条件で乾燥して、分岐構造を有するポリカーボネート樹脂粉粒体を得た。このようにして得られた分岐構造を有するポリカーボネート樹脂は粘度平均分子量２５１００、分岐率０．９７ｍｏｌ％であった。 (A component)
(A-1 component)
PC-B9H: Aromatic polycarbonate resin having a branched structure (branching rate 0.97 mol%, molecular weight 25,100)
(Manufacturing method of PC-B9H)
A reactor equipped with a thermometer, a stirrer, and a reflux condenser was charged with 2340 parts of ion-exchanged water, 947 parts of a 25% aqueous sodium hydroxide solution, and 0.7 parts of hydrosulfite, and 710 parts of bisphenol A was dissolved with stirring (bisphenol A solution). ) After that, 2299 parts of methylene chloride, 112 parts of 48.5% sodium hydroxide aqueous solution, aqueous solution of 1,1,1-tris (4-hydroxyphenyl) ethane dissolved in 25% concentration in 14% sodium hydroxide aqueous solution 38.1 parts (1.00 mol%) was added, and phosgenation reaction was performed by blowing 354 parts of phosgene over 15 minutes at 15 to 25 ° C.
After completion of phosgenation, 219 parts of 11% strength p-tert-butylphenol in methylene chloride and 88 parts of 48.5% aqueous sodium hydroxide solution were added, stirring was stopped, and the mixture was allowed to stand for 10 minutes, followed by stirring. After 5 minutes of emulsification, the mixture was processed with a homomixer (Special Machine Industries Co., Ltd.) at a rotation speed of 1200 rpm and a bath frequency of 35 times to obtain a highly emulsified dope. The highly emulsified dope was reacted in a polymerization tank (with a stirrer) at a temperature of 35 ° C. for 3 hours under non-stirring conditions to complete the polymerization.
After completion of the reaction, 5728 parts of methylene chloride was added for dilution, the methylene chloride phase was separated from the reaction mixture, 5000 parts of ion-exchanged water was added to the separated methylene chloride phase and mixed with stirring, and the stirring was stopped. The phase and the organic phase were separated. Next, water washing was repeated until the conductivity of the aqueous phase was almost the same as that of ion-exchanged water to obtain a purified polycarbonate resin solution. Next, methylene chloride was evaporated at a liquid temperature of 75 ° C. with a 1000 L kneader in which 100 L of ion-exchanged water was added to the purified polycarbonate resin solution to obtain a granular material. 25 parts of the granular material and 75 parts of water were put into a hot water treatment tank equipped with a stirrer and stirred and mixed at a water temperature of 95 ° C. for 30 minutes.
Subsequently, the mixture of the granular material and water was separated by a centrifugal separator to obtain a granular material containing 0.5% by weight of methylene chloride and 45% by weight of water. Next, this granular material was continuously supplied at 50 kg / hr (in terms of polycarbonate resin) to a SUS316L conductive heat receiving groove type biaxial stirring continuous dryer controlled at 140 ° C., and the condition of an average drying time of 3 hours And dried to obtain a polycarbonate resin particle having a branched structure. The polycarbonate resin having a branched structure thus obtained had a viscosity average molecular weight of 25100 and a branching ratio of 0.97 mol%.

ＰＣ−Ｂ９Ｌ：分岐構造を有する芳香族ポリカーボネート樹脂（分岐率０．９５ｍｏｌ％、分子量２０，３００）
（ＰＣ−Ｂ９Ｌの製造方法）
１１％濃度のｐ−ｔｅｒｔ−ブチルフェノールの塩化メチレン溶液２６１部に変更した以外は、ＰＣ−Ｂ９Ｈの製造方法と同様に行い、分岐構造を有するポリカーボネート樹脂粉粒体を得た。このようにして得られた分岐構造を有するポリカーボネート樹脂は粘度平均分子量２０３００、分岐率０．９５ｍｏｌ％であった。 PC-B9L: Aromatic polycarbonate resin having a branched structure (branching rate 0.95 mol%, molecular weight 20,300)
(Manufacturing method of PC-B9L)
A polycarbonate resin particle having a branched structure was obtained in the same manner as in the method for producing PC-B9H, except that it was changed to 261 parts of a methylene chloride solution of 11% concentration of p-tert-butylphenol. The polycarbonate resin having a branched structure thus obtained had a viscosity average molecular weight of 20300 and a branching rate of 0.95 mol%.

ＰＣ−Ｂ７：分岐構造を有する芳香族ポリカーボネート樹脂（分岐率０．７１ｍｏｌ％、分子量２５，２００）
（ＰＣ−Ｂ７の製造方法）
ホスゲンを３５２部、１４％濃度の水酸化ナトリウム水溶液に１，１，１−トリス（４−ヒドロキシフェニル）エタンを２５％濃度で溶解した水溶液２８．６部（０．７５ｍｏｌ％）、１１％濃度のｐ−ｔｅｒｔ−ブチルフェノールの塩化メチレン溶液２０９部に変更した以外は、ＰＣ−Ｂ９Ｈの製造方法と同様に行い、分岐構造を有するポリカーボネート樹脂粉粒体を得た。このようにして得られた分岐構造を有するポリカーボネート樹脂は粘度平均分子量２５２００、分岐率０．７１ｍｏｌ％であった。 PC-B7: aromatic polycarbonate resin having a branched structure (branch rate 0.71 mol%, molecular weight 25,200)
(Manufacturing method of PC-B7)
352 parts of phosgene, 28.6 parts (0.75 mol%) of an aqueous solution prepared by dissolving 1,1,1-tris (4-hydroxyphenyl) ethane in a 14% strength aqueous sodium hydroxide solution at a 25% concentration, 11% strength A polycarbonate resin particle having a branched structure was obtained in the same manner as in the method for producing PC-B9H, except that 209 parts of p-tert-butylphenol in methylene chloride was used. The polycarbonate resin having a branched structure thus obtained had a viscosity average molecular weight of 25200 and a branching rate of 0.71 mol%.

ＰＣ−Ｂ１２：分岐構造を有する芳香族ポリカーボネート樹脂（分岐率１．６ｍｏｌ％、分子量２５，０００）
（ＰＣ−Ｂ１２の製造方法）
ホスゲンを３５７部、１４％濃度の水酸化ナトリウム水溶液に１，１，１−トリス（４−ヒドロキシフェニル）エタンを２５％濃度で溶解した水溶液６４．７部（１．７ｍｏｌ％）、１１％濃度のｐ−ｔｅｒｔ−ブチルフェノールの塩化メチレン溶液２４５部に変更した以外は、ＰＣ−Ｂ９Ｈの製造方法と同様に行い、分岐構造を有するポリカーボネート樹脂粉粒体を得た。このようにして得られた分岐構造を有するポリカーボネート樹脂は粘度平均分子量２５０００、分岐率１．６ｍｏｌ％であった。 PC-B12: Aromatic polycarbonate resin having a branched structure (branch rate 1.6 mol%, molecular weight 25,000)
(Manufacturing method of PC-B12)
357 parts of phosgene, 64.7 parts (1.7 mol%) of an aqueous solution prepared by dissolving 1,1,1-tris (4-hydroxyphenyl) ethane in a 14% strength aqueous sodium hydroxide solution at a 25% concentration, 11% strength A polycarbonate resin powder having a branched structure was obtained in the same manner as in the method for producing PC-B9H, except that 245 parts of p-tert-butylphenol in methylene chloride was used. The polycarbonate resin having a branched structure thus obtained had a viscosity average molecular weight of 25000 and a branching rate of 1.6 mol%.

ＰＣ−Ｂ６：分岐構造を有する芳香族ポリカーボネート樹脂（分岐率０．６６ｍｏｌ％、分子量約２５，２００）
（ＰＣ−Ｂ６の製造方法）
ホスゲンを３５２部、１４％濃度の水酸化ナトリウム水溶液に１，１，１−トリス（４−ヒドロキシフェニル）エタンを２５％濃度で溶解した水溶液２６．７部（０．７０ｍｏｌ％）、１１％濃度のｐ−ｔｅｒｔ−ブチルフェノールの塩化メチレン溶液２０６部に変更した以外は、ＰＣ−Ｂ９Ｈの製造方法と同様に行い、分岐構造を有するポリカーボネート樹脂粉粒体を得た。このようにして得られた分岐構造を有するポリカーボネート樹脂は粘度平均分子量２５２００、分岐率０．６６ｍｏｌ％であった。 PC-B6: Aromatic polycarbonate resin having a branched structure (branching rate 0.66 mol%, molecular weight about 25,200)
(Manufacturing method of PC-B6)
352 parts of phosgene, 26.7 parts (0.70 mol%) of an aqueous solution prepared by dissolving 1,1,1-tris (4-hydroxyphenyl) ethane in a 14% strength aqueous sodium hydroxide solution at a 25% concentration, 11% concentration A polycarbonate resin powder having a branched structure was obtained in the same manner as in the method for producing PC-B9H, except that it was changed to 206 parts of a methylene chloride solution of p-tert-butylphenol. The polycarbonate resin having a branched structure thus obtained had a viscosity average molecular weight of 25200 and a branching rate of 0.66 mol%.

ＰＣ−Ｂ２：分岐構造を有する芳香族ポリカーボネート樹脂（分岐率０．２８ｍｏｌ％、分子量約２５，０００）
（ＰＣ−Ｂ２製造方法）
ホスゲンを３４８部、１４％濃度の水酸化ナトリウム水溶液に１，１，１−トリス（４−ヒドロキシフェニル）エタンを２５％濃度で溶解した水溶液１０．７部（０．２８ｍｏｌ％）、１１％濃度のｐ−ｔｅｒｔ−ブチルフェノールの塩化メチレン溶液１６０部に変更した以外は、ＰＣ−Ｂ９Ｈの製造方法と同様に行い、分岐構造を有するポリカーボネート樹脂粉粒体を得た。このようにして得られた分岐構造を有するポリカーボネート樹脂は粘度平均分子量２５０００、分岐率０．２８ｍｏｌ％であった。 PC-B2: Aromatic polycarbonate resin having a branched structure (branching rate 0.28 mol%, molecular weight about 25,000)
(PC-B2 manufacturing method)
348 parts of phosgene, 10.7 parts (0.28 mol%) of an aqueous solution prepared by dissolving 1,1,1-tris (4-hydroxyphenyl) ethane in a 14% strength aqueous sodium hydroxide solution at a 25% concentration, 11% concentration A polycarbonate resin powder having a branched structure was obtained in the same manner as in the production method of PC-B9H, except that it was changed to 160 parts of a methylene chloride solution of p-tert-butylphenol. The polycarbonate resin having a branched structure thus obtained had a viscosity average molecular weight of 25000 and a branching rate of 0.28 mol%.

（Ａ−２成分）
ＰＣ−Ｌ１：直鎖状ポリカーボネート樹脂（ホスゲン法で作成されたビスフェノールＡおよび末端停止剤としてｐ−ｔｅｒｔ−ブチルフェノールからなるポリカーボネート樹脂。かかるポリカーボネート樹脂はアミン系触媒を使用せず製造され芳香族ポリカーボネート樹脂末端中、末端水酸基の割合は１０ｍｏｌ％であり、粘度平均分子量は２５，５００であった。）
ＰＣ−Ｌ２：直鎖状ポリカーボネート樹脂（ホスゲン法で作成されたビスフェノールＡおよび末端停止剤としてｐ−ｔｅｒｔ−ブチルフェノールからなるポリカーボネート樹脂。かかるポリカーボネート樹脂はアミン系触媒を使用せず製造され芳香族ポリカーボネート樹脂末端中、末端水酸基の割合は１０ｍｏｌ％であり、粘度平均分子量は１９，７００であった。）
ＰＣ−Ｌ３：直鎖状ポリカーボネート樹脂（ホスゲン法で作成されたビスフェノールＡおよび末端停止剤としてｐ−ｔｅｒｔ−ブチルフェノールからなるポリカーボネート樹脂。かかるポリカーボネート樹脂はアミン系触媒を使用せず製造され芳香族ポリカーボネート樹脂末端中、末端水酸基の割合は１０ｍｏｌ％であり、粘度平均分子量は１５，５００であった。） (A-2 component)
PC-L1: Linear polycarbonate resin (polycarbonate resin comprising bisphenol A prepared by the phosgene method and p-tert-butylphenol as a terminal terminator. Such a polycarbonate resin is produced without using an amine catalyst and is an aromatic polycarbonate resin. The ratio of the terminal hydroxyl group in the terminal was 10 mol%, and the viscosity average molecular weight was 25,500.)
PC-L2: Linear polycarbonate resin (a polycarbonate resin comprising bisphenol A prepared by the phosgene method and p-tert-butylphenol as a terminal terminator. Such a polycarbonate resin is produced without using an amine catalyst and is an aromatic polycarbonate resin. The ratio of the terminal hydroxyl group in the terminal was 10 mol%, and the viscosity average molecular weight was 19,700.)
PC-L3: a linear polycarbonate resin (a polycarbonate resin comprising bisphenol A prepared by the phosgene method and p-tert-butylphenol as a terminal terminator. This polycarbonate resin is produced without using an amine catalyst and is an aromatic polycarbonate resin. The ratio of the terminal hydroxyl group in the terminal was 10 mol%, and the viscosity average molecular weight was 15,500.)

（Ｂ−１成分）
Ｂ−１−１：パーフルオロブタンスルホン酸カリウム塩（大日本インキ（株）製メガファックＦ−１１４Ｐ）
Ｂ−１−２：パーフルオロブタンスルホン酸ナトリウム塩（大日本インキ（株）製メガファックＦ−１１４Ｓ）
Ｂ−１−３：ジフェニルスルホンスルホン酸カリウム（ユーシービージャパン製ＫＳＳ） (B-1 component)
B-1-1: Perfluorobutane sulfonic acid potassium salt (Megafac F-114P manufactured by Dainippon Ink Co., Ltd.)
B-1-2: Sodium perfluorobutanesulfonic acid salt (Megafac F-114S manufactured by Dainippon Ink Co., Ltd.)
B-1-3: Potassium diphenylsulfonesulfonate (KSS manufactured by UCB Japan)

（Ｂ−２成分）
Ｂ−２−１：Ｓｉ−Ｈ基および芳香族基を含有するシリコーン化合物
（Ｂ−２−１の製造）
攪拌機、冷却装置、温度計を取り付けた１Ｌフラスコに水３０１．９ｇとトルエン１５０ｇを仕込み、内温５℃まで冷却した。滴下ロートにトリメチルクロロシラン２１．７ｇ、メチルジクロロシラン２３．０ｇ、ジメチルジクロロシラン１２．９およびジフェニルジクロロシラン７６．０の混合物を仕込み、フラスコ内へ攪拌しながら２時間かけて滴下した。この間、内温を２０℃以下に維持するよう、冷却を続けた。滴下終了後、さらに内温２０℃で攪拌を４時間続けて熟成した後、静置して分離した塩酸水層を除去し、１０％炭酸ナトリウム水溶液を添加して５分間攪拌後、静置して分離した水層を除去した。その後、さらにイオン交換水で３回洗浄し、トルエン層が中性になったことを確認した。このトルエン溶液を減圧下内温１２０℃まで加熱してトルエンと低沸点物を除去した後、濾過により不溶物を取り除いてシリコーン化合物Ｂ−２−１を得た。このシリコーン化合物Ｂ−２−１はＳｉ−Ｈ基量が０．２１ｍｏｌ／１００ｇ、芳香族基量が４９重量％、平均重合度が８．０であった。 (B-2 component)
B-2-1: Silicone compound containing Si-H group and aromatic group (Production of B-2-1)
A 1 L flask equipped with a stirrer, a cooling device, and a thermometer was charged with 301.9 g of water and 150 g of toluene, and cooled to an internal temperature of 5 ° C. A mixture of trimethylchlorosilane (21.7 g), methyldichlorosilane (23.0 g), dimethyldichlorosilane (12.9) and diphenyldichlorosilane (76.0) was charged into the dropping funnel and dropped into the flask over 2 hours while stirring. During this time, cooling was continued to maintain the internal temperature at 20 ° C. or lower. After completion of the dropwise addition, the mixture was further aged for 4 hours with stirring at an internal temperature of 20 ° C., then left to stand to remove the separated hydrochloric acid aqueous layer, added with 10% aqueous sodium carbonate solution, stirred for 5 minutes and then left to stand. The separated aqueous layer was removed. Then, it wash | cleaned 3 times with ion-exchange water, and it confirmed that the toluene layer became neutral. The toluene solution was heated to an internal temperature of 120 ° C. under reduced pressure to remove toluene and low-boiling substances, and then insoluble materials were removed by filtration to obtain a silicone compound B-2-1. This silicone compound B-2-1 had an Si—H group content of 0.21 mol / 100 g, an aromatic group content of 49% by weight, and an average degree of polymerization of 8.0.

Ｂ−２−２：Ｓｉ−Ｈ基および芳香族基を含有するシリコーン化合物
（Ｂ−２−２の製造）
撹拌装置、冷却装置、温度計を取り付けた１Ｌフラスコに１，１，３，３−テトラメチルジシロキサン１００．７ｇ、１，３，５，７−テトラメチルシクロテトラシロキサン６０．１ｇ、オクタメチルシクロテトラシロキサン１２９．８ｇ、オクタフェニルシクロテトラシロキサン１４３．８ｇおよびフェニルトリメトキシシラン９９．１ｇを仕込み、さらに撹拌しながら濃硫酸２５．０ｇを添加した。内温１０℃まで冷却した後、水１３．８ｇをフラスコ内へ撹拌しながら３０分間かけて滴下した。この間、内温を２０℃以下に維持するよう、冷却を続けた。滴下終了後、さらに内温１０〜２０℃で撹拌を５時間続けて熟成した後、水８．５ｇとトルエン３００ｇを添加して３０分間撹拌後、静置して分離した水層を除去した。その後、さらに５％硫酸ナトリウム水溶液で４回洗浄し、トルエン層が中性になったことを確認した。このトルエン溶液を減圧下内温１２０℃まで加熱してトルエンと低沸分を除去した後、濾過により不溶物を取り除いてシリコーン化合物Ｂ−２−２を得た。このシリコーン化合物Ｂ−２−２はＳｉ−Ｈ基量が０．５０ｍｏｌ／１００ｇ、芳香族基量が３０重量％、平均重合度が１０．９５のシリコーン化合物であった。 B-2-2: Silicone compound containing Si-H group and aromatic group (Production of B-2-2)
In a 1 L flask equipped with a stirrer, a cooling device and a thermometer, 100.7 g of 1,1,3,3-tetramethyldisiloxane, 60.1 g of 1,3,5,7-tetramethylcyclotetrasiloxane, octamethylcyclo 129.8 g of tetrasiloxane, 143.8 g of octaphenylcyclotetrasiloxane, and 99.1 g of phenyltrimethoxysilane were charged, and 25.0 g of concentrated sulfuric acid was added with further stirring. After cooling to an internal temperature of 10 ° C., 13.8 g of water was dropped into the flask over 30 minutes while stirring. During this time, cooling was continued to maintain the internal temperature at 20 ° C. or lower. After completion of the dropwise addition, the mixture was further aged at an internal temperature of 10 to 20 ° C. for 5 hours. Then, 8.5 g of water and 300 g of toluene were added, stirred for 30 minutes, and allowed to stand to remove the separated aqueous layer. Thereafter, it was further washed four times with a 5% aqueous sodium sulfate solution, and it was confirmed that the toluene layer became neutral. This toluene solution was heated to an internal temperature of 120 ° C. under reduced pressure to remove toluene and low-boiling components, and then insoluble materials were removed by filtration to obtain a silicone compound B-2-2. This silicone compound B-2-2 was a silicone compound having an Si-H group amount of 0.50 mol / 100 g, an aromatic group amount of 30% by weight, and an average degree of polymerization of 10.95.

Ｂ−２−３：Ｓｉ−Ｈ基および芳香族基を含有するシリコーン化合物
（Ｂ−２−３の製造）
撹拌装置、冷却装置、温度計を取り付けた１Ｌフラスコにヘキサメチルジシロキサン１６．２ｇ、１，３，５，７−テトラメチルシクロテトラシロキサン６１．０ｇ、オクタメチルシクロテトラシロキサン１０３．８ｇ、およびジフェニルジメトキシシラン３９１．０ｇを仕込み、さらに撹拌しながら濃硫酸２５．０ｇを添加した。内温１０℃まで冷却した後、水２９．４ｇをフラスコ内へ撹拌しながら３０分間かけて滴下した。この間、内温を２０℃以下に維持するよう、冷却を続けた。滴下終了後、さらに内温１０〜２０℃で撹拌を５時間続けて熟成した後、水８．５ｇとトルエン３００ｇを添加して３０分間撹拌後、静置して分離した水層を除去した。その後、さらに５％硫酸ナトリウム水溶液で４回洗浄し、トルエン層が中性になったことを確認した。このトルエン溶液を減圧下内温１２０℃まで加熱してトルエンと低沸分を除去した後、濾過により不溶物を取り除いてシリコーン化合物Ｂ−２−３を得た。このシリコーン化合物Ｂ−２−３は、Ｓｉ−Ｈ基量が０．２０ｍｏｌ／１００ｇ、芳香族基量が５０重量％、平均重合度が４２．０のシリコーン化合物であった。 B-2-3: Silicone compound containing Si-H group and aromatic group (Production of B-2-3)
In a 1 L flask equipped with a stirrer, a cooling device, and a thermometer, 16.2 g of hexamethyldisiloxane, 61.0 g of 1,3,5,7-tetramethylcyclotetrasiloxane, 103.8 g of octamethylcyclotetrasiloxane, and diphenyl 391.0 g of dimethoxysilane was charged, and 25.0 g of concentrated sulfuric acid was added with further stirring. After cooling to an internal temperature of 10 ° C., 29.4 g of water was dropped into the flask over 30 minutes while stirring. During this time, cooling was continued to maintain the internal temperature at 20 ° C. or lower. After completion of the dropwise addition, the mixture was further aged at an internal temperature of 10 to 20 ° C. for 5 hours. Then, 8.5 g of water and 300 g of toluene were added, stirred for 30 minutes, and allowed to stand to remove the separated aqueous layer. Thereafter, it was further washed four times with a 5% aqueous sodium sulfate solution, and it was confirmed that the toluene layer became neutral. This toluene solution was heated to 120 ° C. under reduced pressure to remove toluene and low-boiling components, and then insoluble materials were removed by filtration to obtain silicone compound B-2-3. This silicone compound B-2-3 was a silicone compound having an Si—H group amount of 0.20 mol / 100 g, an aromatic group amount of 50 wt%, and an average degree of polymerization of 42.0.

Ｂ−２−４：Ｓｉ−Ｈ基および芳香族基を有するシリコーン化合物
（Ｂ−２−４の製造）
撹拌装置、冷却装置、温度計を取り付けた１Ｌフラスコにヘキサメチルジシロキサン１５．９ｇ、１，３，５，７−テトラメチルシクロテトラシロキサン１４７．３ｇ、オクタメチルシクロテトラシロキサン１４．５ｇおよびジフェニルジメトキシシラン３９５．１ｇを仕込み、さらに撹拌しながら濃硫酸２５．０ｇを添加した。内温１０℃まで冷却した後、水２９．７ｇをフラスコ内へ撹拌しながら３０分間かけて滴下した。この間、内温を２０℃以下に維持するよう、冷却を続けた。滴下終了後、さらに内温１０〜２０℃で撹拌を５時間続けて熟成した後、水８．５ｇとトルエン３００ｇを添加して３０分間撹拌後、静置して分離した水層を除去した。その後、さらに５％硫酸ナトリウム水溶液で４回洗浄し、トルエン層が中性になったことを確認した。このトルエン溶液を減圧下内温１２０℃まで加熱してトルエンと低沸分を除去した後、濾過により不溶物を取り除いてシリコーン化合物Ｂ−２−４を得た。このシリコーン化合物Ｂ−２−４はＳｉ−Ｈ基量が０．４９ｍｏｌ／１００ｇ、芳香族基量が５０重量％、平均重合度が４５．５であった。 B-2-4: Silicone compound having Si-H group and aromatic group (Production of B-2-4)
In a 1 L flask equipped with a stirrer, a cooling device and a thermometer, 15.9 g of hexamethyldisiloxane, 147.3 g of 1,3,5,7-tetramethylcyclotetrasiloxane, 14.5 g of octamethylcyclotetrasiloxane and diphenyldimethoxy 395.1 g of silane was charged, and 25.0 g of concentrated sulfuric acid was added with further stirring. After cooling to an internal temperature of 10 ° C., 29.7 g of water was dropped into the flask over 30 minutes while stirring. During this time, cooling was continued to maintain the internal temperature at 20 ° C. or lower. After completion of the dropwise addition, the mixture was further aged at an internal temperature of 10 to 20 ° C. for 5 hours. Then, 8.5 g of water and 300 g of toluene were added, stirred for 30 minutes, and allowed to stand to remove the separated aqueous layer. Thereafter, it was further washed four times with a 5% aqueous sodium sulfate solution, and it was confirmed that the toluene layer became neutral. This toluene solution was heated to 120 ° C. under reduced pressure to remove toluene and low-boiling components, and then insoluble materials were removed by filtration to obtain silicone compound B-2-4. This silicone compound B-2-4 had an Si—H group content of 0.49 mol / 100 g, an aromatic group content of 50 wt%, and an average degree of polymerization of 45.5.

＜各シリコーン化合物の示性式＞
Ｂ−２−１： Ｍ２ＤＨ ２Ｄ１Ｄφ２ ３
Ｂ−２−２： ＭＨ ３ＤＨ ２Ｄ３．５Ｄφ２ １．４５Ｔφ １
Ｂ−２−３： Ｍ２ＤＨ １０Ｄ１４Ｄφ２ １６
Ｂ−２−４： Ｍ２ＤＨ ２５Ｄ２Ｄφ２ １６．５
なお、上記示性式における各記号は以下のシロキサン単位を表し、各記号の係数（下付文字）は１分子中における各シロキサン単位の数（重合度）を示す。
Ｍ ：（ＣＨ３）３ＳｉＯ１／２
ＭＨ ： Ｈ（ＣＨ３）２ＳｉＯ１／２
Ｄ ：（ＣＨ３）２ＳｉＯ
ＤＨ ： Ｈ（ＣＨ３）ＳｉＯ
Ｄφ２ ：（Ｃ６Ｈ５）２ＳｉＯ
Ｔφ ：（Ｃ６Ｈ５）ＳｉＯ３／２
Ｂ−２−５：芳香族基を含有するシリコーン（信越化学工業（株）製ＫＦ５６）
Ｂ−２−６：芳香族基を含有するシリコーン（信越化学工業（株）製ＫＲ２１９） <Indication formula of each silicone compound>
B-2-1: M 2 DH 2 D 1 D φ2 3
B-2-2: MH 3 DH 2 D 3.5 D φ2 1.45 T φ 1
B-2-3: M 2 DH 10 D 14 D φ2 16
B-2-4: M 2 D H 25 D 2 D φ2 16.5
Each symbol in the above formula represents the following siloxane units, and the coefficient (subscript) of each symbol represents the number of siloxane units (degree of polymerization) in one molecule.
M: (CH 3 ) 3 SiO 1/2
M H : H (CH 3 ) 2 SiO 1/2
D: (CH 3 ) 2 SiO
D H: H (CH 3) SiO
D φ2 : (C 6 H 5 ) 2 SiO
Tφ : (C 6 H 5 ) SiO 3/2
B-2-5: Silicone containing an aromatic group (KF56 manufactured by Shin-Etsu Chemical Co., Ltd.)
B-2-6: Silicone containing an aromatic group (KR219 manufactured by Shin-Etsu Chemical Co., Ltd.)

（その他の成分）
ＩＲＳ：ホスファイト化合物（チバ・スペシャルティー・ケミカルズ社製Ｉｒｇａｆｏｓ１６８）
ＩＲＸ：ヒンダードフェノール系酸化防止剤（チバ・スペシャルティ・ケミカルズ社製Ｉｒｇａｎｏｘ１０７６）
ＰＥＰ：ペンタエリスリトールジホスファイト化合物（旭電化工業（株）製アデカスタブＰＥＰ−３６）
ＴＭ ：トリメチルホスフェート（大八化学工業（株）製ＴＭＰ）
ＵＶ ：紫外線吸収剤（ケミプロ化成工業（株）ケミソーブ７９）
ＶＢ ：ブルーイング剤（バイエル社製：マクロレックスバイオレットＢ） (Other ingredients)
IRS: Phosphite compound (Irgafos 168 manufactured by Ciba Specialty Chemicals)
IRX: hindered phenol antioxidant (Irganox 1076 manufactured by Ciba Specialty Chemicals)
PEP: Pentaerythritol diphosphite compound (Adeka Stub PEP-36 manufactured by Asahi Denka Kogyo Co., Ltd.)
TM: Trimethyl phosphate (TMP manufactured by Daihachi Chemical Industry Co., Ltd.)
UV: UV absorber (Kemipro Kasei Kogyo Co., Ltd. Chemisorb 79)
VB: Brewing agent (manufactured by Bayer: Macrolex Violet B)

Figure 2011099030
Figure 2011099030

Figure 2011099030
Figure 2011099030

Figure 2011099030
Figure 2011099030

以上より明らかなように、本発明の透明難燃性芳香族ポリカーボネート樹脂組成物から形成された押し出し成形品は、分岐率が狭い範囲に限定された分岐構造を有するポリカーボネート樹脂と難燃剤を主に含有し、かつ透明性、外観、機械物性に優れるものである。かかる特性は従来の難燃性芳香族ポリカーボネート樹脂から形成された押し出し成形品にはないものである。したがって、照明用カバー、透過型ディスプレイ用（保護）カバー、テレビ前面板用カバーのみならず、ＯＡ機器分野、電気電子機器分野、建材分野などの各種工業用途に極めて有用であり、その奏する工業的効果は極めて大である。   As is clear from the above, the extrusion molded product formed from the transparent flame-retardant aromatic polycarbonate resin composition of the present invention mainly comprises a polycarbonate resin having a branched structure limited to a narrow branching ratio and a flame retardant. It contains and is excellent in transparency, appearance, and mechanical properties. Such properties are not present in extruded products formed from conventional flame retardant aromatic polycarbonate resins. Therefore, it is extremely useful for various industrial uses such as lighting cover, transmissive display (protection) cover, TV front plate cover, OA equipment field, electrical and electronic equipment field, building material field, etc. The effect is extremely large.

Claims (8)

（Ａ）分岐率０．７０〜１．５０ｍｏｌ％の分岐構造を有する芳香族ポリカーボネート樹脂（Ａ成分）１００重量部に対して、（Ｂ）難燃剤（Ｂ成分）０．００５〜５重量部を含有する芳香族ポリカーボネート樹脂組成物からなる押し出し成形品。   (A) 0.005 to 5 parts by weight of (B) flame retardant (component B) with respect to 100 parts by weight of aromatic polycarbonate resin (component A) having a branched structure with a branching ratio of 0.70 to 1.50 mol% An extruded product comprising an aromatic polycarbonate resin composition. Ｂ成分が（Ｂ−１）アルカリ（土類）金属塩（Ｂ−１成分）および（Ｂ−２）芳香族基を有するシリコーン化合物（Ｂ−２成分）からなる群より選択される少なくとも１種の難燃剤である請求項１記載の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品。   B component is at least one selected from the group consisting of (B-1) alkali (earth) metal salt (B-1 component) and (B-2) silicone compound having aromatic group (B-2 component) An extruded product comprising the aromatic polycarbonate resin composition according to claim 1, which is a flame retardant. Ａ成分１００重量部に対して、Ｂ−１成分を０．００５〜１．０重量部含有することを特徴とする請求項２記載の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品。   The extrusion-molded article comprising the aromatic polycarbonate resin composition according to claim 2, comprising 0.005 to 1.0 part by weight of the B-1 component with respect to 100 parts by weight of the A component. Ａ成分１００重量部に対して、Ｂ−２成分を０．０５〜２．０重量部含有することを特徴とする請求項２または３記載の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品。   The extruded product comprising the aromatic polycarbonate resin composition according to claim 2 or 3, wherein 0.05 to 2.0 parts by weight of the B-2 component is contained with respect to 100 parts by weight of the A component. Ｂ−１成分がパーフルオロアルキルスルホン酸アルカリ（土類）金属塩、芳香族スルホン酸アルカリ（土類）金属塩、および芳香族系イミドのアルカリ（土類）金属塩からなる群より選択される１種以上の有機アルカリ（土類）金属塩であることを特徴とする請求項２〜４のいずれか１項記載の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品。   Component B-1 is selected from the group consisting of alkali (earth) metal salts of perfluoroalkyl sulfonates, alkali (earth) metal aromatic sulfonates, and alkali (earth) metal salts of aromatic imides. The extrusion molded article comprising the aromatic polycarbonate resin composition according to any one of claims 2 to 4, which is one or more organic alkali (earth) metal salts. Ｂ−２成分が分子中にＳｉ−Ｈ基を含有するシリコーン化合物であることを特徴とする請求項２〜５のいずれか１項記載の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品。   The extrusion molded article comprising the aromatic polycarbonate resin composition according to any one of claims 2 to 5, wherein the B-2 component is a silicone compound containing a Si-H group in the molecule. 押し出し成形品が、押し出しシート、押し出し賦型シート、または異型押し出し品である請求項１〜６のいずれか１項に記載の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品。   The extrusion-molded article comprising the aromatic polycarbonate resin composition according to any one of claims 1 to 6, wherein the extrusion-molded article is an extrusion sheet, an extrusion-molding sheet, or a modified extrusion-molded article. 押し出し成形品が、照明用カバーまたは透過型ティスプレイ用カバーである請求項１〜６のいずれか１項に記載の芳香族ポリカーボネート樹脂組成物からなる押し出し成形品。   The extrusion-molded article comprising the aromatic polycarbonate resin composition according to any one of claims 1 to 6, wherein the extrusion-molded article is an illumination cover or a transmission-type display cover.
JP2009254079A 2009-11-05 2009-11-05 Extrusion molded product made of aromatic polycarbonate resin composition Pending JP2011099030A (en)