JP2011074508A - Paper containing recycled pulp - Google Patents
Paper containing recycled pulp Download PDFInfo
- Publication number
- JP2011074508A JP2011074508A JP2009224636A JP2009224636A JP2011074508A JP 2011074508 A JP2011074508 A JP 2011074508A JP 2009224636 A JP2009224636 A JP 2009224636A JP 2009224636 A JP2009224636 A JP 2009224636A JP 2011074508 A JP2011074508 A JP 2011074508A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- pulp
- recycled pulp
- postcard
- fluorescence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、再生パルプを含有する紙に関し、特にはがき用紙に好適な紙に関する。 The present invention relates to paper containing recycled pulp, and more particularly to paper suitable for postcard paper.
一般に紙は、大きくは紙と板紙とに分類される。前者の紙の用途には様々なものがあるが、「官製はがき」(あるいは「郵政はがき」)、「私製はがき」と呼ばれる郵便はがきもその一つである。郵便はがきは、通常、原料パルプからはがき用紙を製造し所定のサイズに裁断したものであり、官製の場合、表面に切手と同じ効力を持つ額面が記載された料額印面が印刷され、お年玉付き年賀はがきや夏のお便りはがきなどでは、さらに下端に組番号や抽選番号が印刷される。このようなはがき用紙として、例えば特許文献1(特許第3755483号公報)には、化学パルプや脱墨パルプ等を混合し填料として炭酸カルシウムを使用することなどが記載されている。近年、紙の製造においては、リサイクルや省資源など環境意識の高まりに伴って、原料パルプとして古紙の利用が推進されている。はがき用紙や封書用紙においても、古紙の活用に対する要望は非常に高い。例えば、特許文献2(特開2005−35224号公報)には、原料パルプとして古紙から得られる再生パルプを含有するはがきの輸送システムが記載されている。 In general, paper is roughly classified into paper and paperboard. There are various uses of the former paper, and postcards called “public postcards” (or “postcards”) and “private postcards” are one of them. A postcard is usually a postcard paper made from raw pulp and cut into a specified size. In the case of a government-made postcard, a face stamp with a face value that has the same effect as a postage stamp is printed on it, with a new year In New Year's postcards and summer letter postcards, the group number and lottery number are printed at the bottom. As such a postcard paper, for example, Patent Document 1 (Japanese Patent No. 3755483) describes that chemical pulp, deinked pulp, or the like is mixed and calcium carbonate is used as a filler. In recent years, in the manufacture of paper, the use of waste paper as a raw material pulp has been promoted with an increase in environmental awareness such as recycling and resource saving. There is a very high demand for the use of used paper even for postcard paper and sealed paper. For example, Patent Document 2 (Japanese Patent Laid-Open No. 2005-35224) describes a transportation system for postcards containing recycled pulp obtained from waste paper as raw pulp.
一方、郵便局では、郵便物に差出人によって記載された郵便番号や住所氏名等をOCRで読み取り、これらの宛先情報をバーコードとして印字し、機械処理により搬送区分することが行われている。なお、このバーコードは、赤外線または紫外線励起の蛍光ステルスインクを用いて、目には見えない不可視情報として印字されている。例えば、特許文献3(特開平11−076950号公報)には、郵便物の仕分け用バーコード印字システムが記載されている。 On the other hand, in a post office, a postal code or address name written by a sender in a postal item is read by OCR, the destination information is printed as a bar code, and transported by machine processing. The bar code is printed as invisible information that cannot be seen with the eyes using infrared or ultraviolet excited fluorescent stealth ink. For example, Patent Document 3 (Japanese Patent Laid-Open No. 11-079650) describes a barcode printing system for sorting mail items.
上記のように、郵便物は、差出人が記載した宛先情報を光学的に読み取りステルスバーコード化することで、効率良く搬送されるシステムとなっている。しかし、紙の製造においてパルプ類には、塵、ピッチ、古紙由来の墨粕やトナー粕等の夾雑物が混入しやすく、これらの夾雑物により宛先情報の読み取り精度が低下して、正確にバーコード化されない問題がある。また、古紙に含まれる蛍光染料は、バーコードの印字部と地色部とのコントラストを低下させて、区分機でのバーコードの読み取りに支障を及ぼし、正確に搬送されない問題がある。そして、古紙を原料とする再生パルプを多量に配合する場合、差出人が記載した宛先情報やステルスバーコードの読み取り精度はさらに悪化してしまう。また、再生パルプの配合により、白色性など製品の外観も損なわれる問題がある。 As described above, the mail is a system that is efficiently transported by optically reading the destination information described by the sender and converting it into a stealth bar code. However, in the manufacture of paper, dusts, pitches, and other foreign substances such as ink and toner derived from waste paper are likely to be mixed into the pulp. There is a problem that is not coded. In addition, the fluorescent dye contained in the waste paper has a problem in that the contrast between the barcode printing portion and the ground color portion is lowered, which impedes the reading of the barcode by the sorting machine and is not accurately conveyed. When a large amount of recycled pulp made from waste paper is blended, the reading accuracy of the destination information and the stealth barcode described by the sender is further deteriorated. Further, there is a problem that the appearance of the product such as whiteness is also impaired by the blending of the recycled pulp.
このように、古紙利用の推進と郵便搬送システムとの効率化は反比例の関係にあり、宛先情報やバーコードの読み取り精度を悪化させることなく、再生パルプを増配することが望まれている。 In this way, the promotion of the use of used paper and the efficiency improvement of the postal transport system are in an inversely proportional relationship, and it is desired to increase the number of recycled pulp without deteriorating the reading accuracy of destination information and barcode.
これまでに、再生パルプ中の蛍光消去処理として種々の方法が提案されている。特許文献4(特許3118087号)では再生パルプ中にジクロルイソシアヌール酸塩を添加する方法が記載されている。また特許文献5には、脱墨または漂白した古紙パルプをクラフトパルプに混合して漂白し、蛍光除去処理する方法が記載されている。特許文献6には、N−ビニルホルムアミド系重合体及び/又はその誘導体を用いる方法が記載されている。 So far, various methods have been proposed as a fluorescence erasing treatment in recycled pulp. Patent Document 4 (Japanese Patent No. 3118087) describes a method of adding dichloroisocyanurate to recycled pulp. Further, Patent Document 5 describes a method in which deinked or bleached waste paper pulp is mixed with kraft pulp, bleached, and subjected to fluorescence removal treatment. Patent Document 6 describes a method using an N-vinylformamide polymer and / or a derivative thereof.
本発明は、再生パルプを高配合しながら、白色度が高く、蛍光強度が低く、チリやダートの少ないはがき用紙に適した紙を提供することを目的とする。 An object of the present invention is to provide a paper suitable for a postcard paper having a high whiteness, a low fluorescence intensity, and a small amount of dust and dirt while containing a high proportion of recycled pulp.
本発明者らは、再生パルプに蛍光失活剤を添加することで、上記課題を解決し、本発明に到達した。詳しくは、再生パルプを製造後、蛍光失活剤を対パルプ固形分あたり固形分質量で0.5〜2%添加して抄紙することで、課題が達成されることを見出した。 The inventors of the present invention have solved the above problems by adding a fluorescence deactivator to recycled pulp, and have reached the present invention. Specifically, it has been found that, after producing recycled pulp, the problem is achieved by adding 0.5 to 2% of a fluorescence deactivator in solid mass per pulp solid content and making paper.
本発明によれば、再生パルプを高配合することができ、環境に配慮した紙とすることができる。また、再生パルプを高配合しても、白色度が高く、蛍光強度が低く、チリやダートが少なく郵便搬送システムに適したはがき用紙を提供することが出来る。 According to the present invention, recycled pulp can be blended in a high amount, and an environmentally friendly paper can be obtained. Moreover, even if the recycled pulp is highly blended, postcard paper having high whiteness, low fluorescence intensity, little dust and dirt, and suitable for a mail transport system can be provided.
以下、はがき用紙の場合を例として本発明を詳細に説明する。 Hereinafter, the present invention will be described in detail by taking the case of postcard paper as an example.
(蛍光失活剤)
本発明においては、再生パルプに蛍光失活剤を添加する。蛍光失活剤としては、ジクロルイソシアヌール酸塩やN−ビニルホルムアミド系重合体、あるいは芳香族カルボン酸・アミン縮合物等が挙げられるが、これに限定されるものではない。
(Fluorescence quencher)
In the present invention, a fluorescence deactivator is added to the recycled pulp. Examples of the fluorescence quencher include dichloroisocyanurate, N-vinylformamide polymer, aromatic carboxylic acid / amine condensate, and the like, but are not limited thereto.
蛍光失活剤の配合量は、対パルプ固形分あたり固形分質量で0.5〜2%が好ましく、0.5〜1.5%であることが更に好ましい。蛍光失活剤の添加量が2%より多くても蛍光除去効果は頭打ちであり、またパルプの白色度が低下する傾向があるため好ましくなく、一方で蛍光失活剤の添加量が0.5%以下だと、効果が不十分である。 The blending amount of the fluorescence deactivator is preferably 0.5 to 2%, more preferably 0.5 to 1.5% in terms of solid mass per pulp solid content. Even if the addition amount of the fluorescence deactivator is more than 2%, the fluorescence removal effect is peaked and the whiteness of the pulp tends to decrease, which is not preferable, while the addition amount of the fluorescence deactivator is 0.5. If it is less than or equal to%, the effect is insufficient.
また、蛍光失活剤は、再生パルプの製造後が好ましい。本発明では蛍光失活剤のマスキング作用が発揮されることで、蛍光強度が低下すると推測される。再生パルプの製造前あるいは製造中に添加すると、その処理工程で水と一緒に流出したり、攪拌などによりパルプ繊維に十分に密着しないと考えられる。 Moreover, the fluorescence deactivator is preferably after production of recycled pulp. In the present invention, it is presumed that the fluorescence intensity decreases due to the masking action of the fluorescence quencher. If it is added before or during the production of regenerated pulp, it is considered that it does not flow out together with water in the treatment step or does not sufficiently adhere to the pulp fiber due to stirring or the like.
(パルプ原料)
再生パルプとしては、特に、白色度が60%以上に洗浄・漂白処理されたものが好ましく、全再生パルプの固形分に対して50質量%以上含有することで、ダートやチリなど再生パルプを高配合した場合の問題を解消できるとともに、優れた白色性を得ることができる。再生パルプの白色度は65%以上であることがより好ましく、70%以上であることがさらに好ましい。なお、本発明におけるパルプの白色度は、JIS P8148に準じて測定したものである。
(Pulp raw material)
The regenerated pulp is particularly preferably one that has been washed and bleached to a whiteness of 60% or more. By containing 50% by mass or more based on the solid content of the total regenerated pulp, regenerated pulp such as dirt and dust can be increased. In addition to resolving problems when blended, excellent whiteness can be obtained. The whiteness of the recycled pulp is more preferably 65% or more, and further preferably 70% or more. In addition, the whiteness of the pulp in the present invention is measured according to JIS P8148.
さらに必要に応じて、機械パルプ(MP)、広葉樹クラフトパルプ(LKP)、針葉樹クラフトパルプ(NKP)など、抄紙原料として一般的に使用されているものの1種類または2種類以上と再生パルプとを混合して使用することができる。機械パルプとしては、砕木パルプ(GP)、リファイナー砕木パルプ(RGP)、サーモメカニカルパルプ(TMP)、ケミサーモメカニカルパルプ(CTMP)、ケミグランドパルプ(CGP)、セミケミカルパルプ(SCP)などを併用することができる。環境の観点からは、再生パルプの使用量が多いことが望ましい。再生パルプと他のパルプを混合して使用する場合、両者の比率は任意に設定することができ特に限定されないが、再生パルプ:他のパルプ=50:50〜100:0が好適である。 If necessary, recycled pulp is mixed with one or more of the commonly used papermaking materials such as mechanical pulp (MP), hardwood kraft pulp (LKP), and softwood kraft pulp (NKP). Can be used. As mechanical pulp, groundwood pulp (GP), refiner groundwood pulp (RGP), thermomechanical pulp (TMP), chemithermomechanical pulp (CTMP), chemiground pulp (CGP), semi-chemical pulp (SCP) are used in combination. be able to. From the environmental viewpoint, it is desirable that the amount of recycled pulp used is large. When mixing and using recycled pulp and other pulp, the ratio of both can be set arbitrarily and is not particularly limited, but recycled pulp: other pulp = 50: 50 to 100: 0 is preferable.
再生パルプの原料となる古紙としては、上質紙、中質紙、下級紙、新聞紙、チラシ、雑誌などの選別古紙やこれらが混合している無選別古紙や、コピー紙や感熱紙、ノーカーボン紙などを含むオフィス古紙などを好適に使用することができる。 Used paper for recycled pulp includes high-quality paper, medium-quality paper, low-grade paper, newspaper, flyers, magazines, and other sorts of waste paper, unsorted waste paper mixed with these, copy paper, thermal paper, and carbonless paper. Office waste paper including the like can be suitably used.
(抄紙方法)
本発明のはがき用紙の製造方法は特に限定されるものでなく、従来公知の長網型湿式抄紙機、オントップ型抄紙機、ギャップフォーマー型抄紙機などによって本発明のはがき用紙を得ることができる。
(Paper making method)
The method for producing the postcard paper of the present invention is not particularly limited, and the postcard paper of the present invention can be obtained by a conventionally known long-net type wet paper machine, on-top type paper machine, gap former type paper machine and the like. it can.
(坪量)
はがき用紙の坪量としては180〜200g/m2であることが望ましい。
(Basis weight)
The basis weight of the postcard paper is desirably 180 to 200 g / m 2 .
(填料)
また、本発明のはがき用紙には、填料を含有しても良い。填料の種類は特に制限されないが、例えば、重質炭酸カルシウムや軽質炭酸カルシウムなどの炭酸カルシウム、炭酸カルシウム−シリカ複合物、酸化チタン、クレー、シリカ、タルク、カオリン、焼成カオリン、デラミカオリン、炭酸マグネシウム、炭酸バリウム、酸化亜鉛、酸化珪素、非晶質シリカ、水酸化アルミニウム、水酸化カルシウム、水酸化マグネシウム、水酸化亜鉛、酸化チタン、ベントナイトなどの無機填料;尿素−ホルマリン樹脂、ポリスチレン樹脂、メラミン樹脂、フェノール樹脂、微小中空粒子等の有機填料;を単独または適宜2種類以上を組み合わせて使用することができる。また、製紙スラッジや脱墨フロス等を原料とした再生填料も使用することができる。酸性抄紙の場合は、前記填料から、酸溶解性のものを除いた填料が使用され、その単独または適宜2種類以上を組み合わせて使用される。本発明では特に、リサイクル可能でかつ紙の不透明度や白色度を比較的低コストで向上させることができるため、炭酸カルシウムを使用して紙面pHが6.0〜9.5となるように中性抄紙することが好ましい。填料の含有量は、少なすぎると不透明度に劣り、多すぎるとオフセット印刷時や断裁時に紙粉が発生しやすいことなどから、対パルプ絶乾質量あたり1〜10質量%が好ましい。なお、ここでいう填料の含有量とは、再生パルプに由来するもの、および抄紙の際に添加されたものなどいずれも含む。
(Filler)
Further, the postcard paper of the present invention may contain a filler. The type of filler is not particularly limited. For example, calcium carbonate such as heavy calcium carbonate and light calcium carbonate, calcium carbonate-silica composite, titanium oxide, clay, silica, talc, kaolin, calcined kaolin, deramikaolin, magnesium carbonate , Inorganic fillers such as barium carbonate, zinc oxide, silicon oxide, amorphous silica, aluminum hydroxide, calcium hydroxide, magnesium hydroxide, zinc hydroxide, titanium oxide, bentonite; urea-formalin resin, polystyrene resin, melamine resin , Organic fillers such as phenol resin and fine hollow particles can be used alone or in appropriate combination of two or more. In addition, recycled fillers made from papermaking sludge, deinking floss, etc. can also be used. In the case of acidic papermaking, a filler obtained by removing acid-soluble ones from the filler is used, and the filler is used alone or in combination of two or more. In the present invention, in particular, since the paper can be recycled and the opacity and whiteness of the paper can be improved at a relatively low cost, the pH of the paper surface is adjusted to 6.0 to 9.5 using calcium carbonate. It is preferable to make a paper. If the content of the filler is too small, the opacity is inferior, and if it is too large, paper dust is likely to be generated during offset printing or cutting. The filler content mentioned here includes both those derived from recycled pulp and those added during papermaking.
(製紙用薬品)
また、本発明では必要に応じて各種の製紙用薬品を添加することができる。具体的には、ポリアクリルアミド系高分子、ポリビニルアルコール系高分子、カチオン性澱粉、各種変性澱粉、尿素・ホルマリン樹脂、メラミン・ホルマリン樹脂などの内添紙力増強剤;ロジン系サイズ剤、AKD系サイズ剤、ASA系サイズ剤、石油系サイズ剤、中性ロジンサイズ剤などの内添サイズ剤;などを挙げることができる。また、歩留剤、濾水性向上剤、凝結剤、硫酸バンド、ベントナイト、シリカ、染料、消泡剤、紫外線防止剤、退色防止剤、ピッチコントロール剤、スライムコントロール剤などを用いることができる。
(Paper chemicals)
In the present invention, various papermaking chemicals can be added as necessary. Specifically, polyacrylamide polymer, polyvinyl alcohol polymer, cationic starch, various modified starches, internal paper strength enhancers such as urea / formalin resin, melamine / formalin resin; rosin sizing agent, AKD type Sizing agents, ASA sizing agents, petroleum sizing agents, internal sizing agents such as neutral rosin sizing agents, and the like. In addition, a retention agent, a drainage improver, a coagulant, a sulfate band, bentonite, silica, a dye, an antifoaming agent, an ultraviolet ray inhibitor, a fading inhibitor, a pitch control agent, a slime control agent, and the like can be used.
(表面処理)
また、本発明のはがき用紙には、必要に応じて、片面または両面に表面処理剤を塗布することができる。表面処理剤の種類や組成は、特に限定はないが、表面強度の向上を目的とした水溶性高分子物質としては、生澱粉、酸化澱粉、エステル化澱粉、カチオン化澱粉、酵素変性澱粉、アルデヒド化澱粉、ヒドロキシエチル化澱粉、ヒドロキシプロピル化澱粉などの澱粉;カルボキシメチルセルロース、ヒドロキシエチルセルロース、メチルセルロースなどのセルロース誘導体;ポリビニルアルコール、カルボキシル変性ポリビニルアルコールなどの変性アルコール;スチレンブタジエン共重合体、ポリ酢酸ビニル、塩化ビニル−酢酸ビニル共重合体、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリアクリル酸エステル、ポリアクリルアミドなどを単独または併用する。また、本発明では筆記適性あるいはプリンターでの印字適性のため、ステキヒトサイズ度が250〜600秒であることが好ましく、の吸水抵抗性を高めるために、前記の水溶性高分子物質の他に、スチレンアクリル酸、スチレンマレイン酸、オレフィン系化合物など表面サイズ剤を併用塗布してもよい。表面処理剤の塗布量は特に制限されず、通常、両面当たり0.5〜5g/m2程度である。また、水溶性高分子物質と表面サイズ剤からなる表面処理剤を塗布する場合、水溶性高分子物質と表面サイズ剤との混合比率は公用の範囲で行えばよい。
(surface treatment)
The postcard paper of the present invention can be coated with a surface treatment agent on one side or both sides as necessary. There are no particular limitations on the type and composition of the surface treatment agent, but examples of water-soluble polymeric substances for the purpose of improving surface strength include raw starch, oxidized starch, esterified starch, cationized starch, enzyme-modified starch, and aldehyde. Starch such as modified starch, hydroxyethylated starch, hydroxypropylated starch; cellulose derivatives such as carboxymethylcellulose, hydroxyethylcellulose and methylcellulose; modified alcohols such as polyvinyl alcohol and carboxyl-modified polyvinyl alcohol; styrene-butadiene copolymer, polyvinyl acetate, A vinyl chloride-vinyl acetate copolymer, polyvinyl chloride, polyvinylidene chloride, polyacrylic acid ester, polyacrylamide or the like is used alone or in combination. Further, in the present invention, it is preferable that the Steecht sizing degree is 250 to 600 seconds for writing ability or printing ability with a printer. In order to increase the water absorption resistance, in addition to the water-soluble polymer substance, Surface sizing agents such as styrene acrylic acid, styrene maleic acid, and olefinic compounds may be used in combination. The coating amount of the surface treatment agent is not particularly limited, and is usually about 0.5 to 5 g / m 2 per both sides. Further, when a surface treatment agent comprising a water-soluble polymer substance and a surface sizing agent is applied, the mixing ratio of the water-soluble polymer substance and the surface sizing agent may be within a public range.
また、前述した表面処理剤を塗布する場合、塗工装置は一般に使用されるものを用いることができ、例えば、2ロールサイズプレス、ゲートロールコーター、ロッドメタリングサイズプレス、ブレードコーター、バーブレードコーター、エアナイフコーター、カーテンコーター、スプレーコーターなどをオンマシンまたはオフマシンで用いることができる。更に、本発明においては紙表面にカレンダー処理を施すこともできる。カレンダー装置の種類と処理条件は特に限定はなく、金属ロールから成る通常のカレンダーやソフトニップカレンダー、高温ソフトニップカレンダーなどの公用の装置を適宜選定し、品質目標値に応じて、これらの装置の制御可能な範囲内で条件を設定すればよい。 Moreover, when apply | coating the surface treating agent mentioned above, the coating apparatus can use what is generally used, for example, 2 roll size press, a gate roll coater, a rod metering size press, a blade coater, a bar blade coater Air knife coaters, curtain coaters, spray coaters, etc. can be used on-machine or off-machine. Furthermore, in the present invention, a calendar process can be applied to the paper surface. There are no particular limitations on the type and processing conditions of the calendar device, and public devices such as ordinary calenders made of metal rolls, soft nip calenders, and high-temperature soft nip calenders are appropriately selected, and according to the quality target values, What is necessary is just to set conditions within the controllable range.
(インクジェット印字適性)
本発明のはがき用紙には、インクジェットプリンターでの印字適性を付与することができる。インクジェット印字適性を付与する方法は特に制限されず、インクジェット記録紙の分野で公知の各種技術を適用すればよい。例えば、塗工タイプの技術としては、はがきの裏面(宛先情報を記載する面の反対面)に、顔料と結着剤とを含有するインク受容層を設けることなどが挙げられる。また、インク受容層をキャスト塗工方式で設けると、高光沢でより高画質な画像を得ることができる。普通紙タイプの技術としては、吸油性填料や内添サイズ剤の添加、染料定着剤としてカチオン性樹脂等を塗布することなどが挙げられる。
(Inkjet printing suitability)
The postcard paper of the present invention can be given printability with an inkjet printer. The method for imparting ink jet printability is not particularly limited, and various techniques known in the field of ink jet recording paper may be applied. For example, as a coating type technique, an ink receiving layer containing a pigment and a binder is provided on the back side of a postcard (the side opposite to the side on which destination information is written). Further, when the ink receiving layer is provided by a cast coating method, a high-gloss and higher-quality image can be obtained. Examples of the plain paper type technique include addition of an oil-absorbing filler and an internal sizing agent, and application of a cationic resin as a dye fixing agent.
(はがき用紙以外の用途)
本発明の紙は、はがき用紙以外にも、印刷用紙、情報用紙、新聞用紙、包装用紙等に使用することができる。坪量等の諸物性や製造方法などは、各用途に応じて適宜設定すればよい。
(Uses other than postcard paper)
In addition to postcard paper, the paper of the present invention can be used for printing paper, information paper, newsprint, packaging paper, and the like. What is necessary is just to set suitably various physical properties, such as basic weight, a manufacturing method, etc. according to each use.
以下、実施例に基づいて本発明を更に詳細に説明する。なお、本発明は実施例に制限されるものではない。実施例及び比較例において部及び%は固形分質量部及び固形分質量%を表す。 Hereinafter, the present invention will be described in more detail based on examples. In addition, this invention is not restrict | limited to an Example. In the examples and comparative examples, parts and% represent solid parts by mass and solids mass%.
[実施例1]
白色度70%の再生パルプ100部に対し、再生パルプの完成チェスト出口にて蛍光失活剤として芳香族カルボン酸・アミン縮合物(里田化工製FQ-50)を対パルプ0.75%添加して撹拌し、再生パルプ中の蛍光を失活させた。この再生パルプを20部とCSF400mlのLBKP80部とを混合し、填料として炭酸カルシウムを5部、内添サイズ剤を1.2部、硫酸バンドを2部添加して紙料スラリーを得た。この紙料スラリーを、オントップ型抄紙機で抄紙し、サイズプレスでポリビニルアルコールを1.8g/m2塗布し、ベック平滑度が40秒になるようにカレンダー処理を行って、坪量が190g/m2のはがき用紙を得た。
[Example 1]
Add 100% of recycled pulp with 70% whiteness and add 0.75% aromatic carboxylic acid / amine condensate (FQ-50 made by Satorita Chemical) as a fluorescence quencher at the exit of the finished chest of the recycled pulp. Then, the fluorescence in the recycled pulp was deactivated. 20 parts of this recycled pulp and 80 parts of LBKP 80 ml of CSF were mixed, 5 parts of calcium carbonate as a filler, 1.2 parts of an internal sizing agent, and 2 parts of a sulfuric acid band were added to obtain a paper slurry. This stock slurry is made with an on-top type paper machine, and 1.8 g / m 2 of polyvinyl alcohol is applied with a size press, calendering is performed so that the Beck smoothness becomes 40 seconds, and the basis weight is 190 g / m 2. m 2 postcard paper was obtained.
[実施例2]
再生パルプに対し蛍光失活剤として芳香族カルボン酸・アミン縮合物(里田化工製FQ-50)を対パルプ1.25%添加し、再生パルプ=40部、LBKP=60部とした以外は、実施例1と同様にしてはがき用紙を得た。
[Example 2]
Except for adding 1.25% of aromatic carboxylic acid / amine condensate (FQ-50 manufactured by Satorita Chemical Co., Ltd.) as a fluorescence quencher to recycled pulp, and setting recycled pulp = 40 parts, LBKP = 60 parts A postcard paper was obtained in the same manner as in 1.
[実施例3]
再生パルプに対し蛍光失活剤としてクロロイソシアヌル酸塩(日新化学DFL-11)を対パルプ1%添加し、再生パルプ=20部とCSF400mlのLBKP80部とした以外は実施例1と同様にしてはがき用紙を得た。
[Example 3]
Except for adding 1% chloroisocyanurate (Nisshin Chemical DFL-11) as a fluorescence quencher to the regenerated pulp to make 20 parts of regenerated pulp and 80 parts of LBKP 80 ml of CSF, the same as in Example 1. I got a postcard paper.
[比較例1]
再生パルプに蛍光失活剤を添加しない以外は、実施例1と同様にして比較例1のはがき用紙を得た。
[Comparative Example 1]
A postcard paper of Comparative Example 1 was obtained in the same manner as in Example 1 except that no fluorescence deactivator was added to the recycled pulp.
[比較例2]
再生パルプに蛍光失活剤を添加しない以外は、実施例2と同様にして比較例2のはがき用紙を得た。
[Comparative Example 2]
A postcard paper of Comparative Example 2 was obtained in the same manner as in Example 2 except that no fluorescent deactivator was added to the recycled pulp.
[比較例3]
再生パルプに対し蛍光失活剤として芳香族カルボン酸・アミン縮合物(里田化工製FQ-50)を対パルプ0.3%添加した以外は実施例1と同様にして比較例3のはがき用紙を得た。
[Comparative Example 3]
A postcard paper of Comparative Example 3 was obtained in the same manner as in Example 1 except that 0.3% of an aromatic carboxylic acid / amine condensate (FQ-50 manufactured by Satorita Chemical Co., Ltd.) was added to the recycled pulp as a fluorescence quencher. .
[比較例4]
再生パルプに対し蛍光失活剤として芳香族カルボン酸・アミン縮合物(里田化工製FQ-50)を対パルプ2.5%添加した以外は実施例2と同様にして比較例4のはがき用紙を得た。
[Comparative Example 4]
A postcard paper of Comparative Example 4 was obtained in the same manner as in Example 2 except that 2.5% of an aromatic carboxylic acid / amine condensate (FQ-50 manufactured by Satoda Kako) was added to the recycled pulp as a fluorescence quencher. .
[評価方法]
各実施例および比較例で得られたはがき用紙の評価を、以下に示す方法により行った。評価結果を表1にまとめて示す。
白色度:パルプおよびはがき用紙について、JIS P8148に従って測定した。
[Evaluation methods]
Evaluation of the postcard paper obtained in each example and comparative example was performed by the following method. The evaluation results are summarized in Table 1.
Whiteness: Measured according to JIS P8148 for pulp and postcard paper.
蛍光強度:JIS P8148に従って、紫外線領域を含む光を照射した時の白色度(X)と紫外線を含まない光を照射した時の白色度(Y)をそれぞれ測定し、両者の差(X-Y)により蛍光強度を求めた。値が小さいほど蛍光強度が小さいことを示す。 Fluorescence intensity: In accordance with JIS P8148, measure the whiteness (X) when irradiated with light including the ultraviolet region and the whiteness (Y) when irradiated with light that does not include ultraviolet light, and calculate the difference between the two (XY) The fluorescence intensity was determined. It shows that fluorescence intensity is so small that a value is small.
表1より、実施例1,2、3のはがき用紙は蛍光強度が低く、白色度も問題ないレベルである。一方、蛍光失活剤を添加しない比較例1、2や蛍光失活剤の添加量が少ない比較例3では蛍光強度の低下が不十分、はがきの区分機読取適性に問題が生じる可能性がある。蛍光失活剤を多量に添加した比較例4では、蛍光強度の変化も実施例に比べて大きな変化はなく、白色度低下など別の問題が生じることがわかる。 From Table 1, the postcard papers of Examples 1, 2, and 3 have low fluorescence intensity and are at a level where there is no problem with whiteness. On the other hand, in Comparative Examples 1 and 2 in which no fluorescence deactivator is added and in Comparative Example 3 in which the addition amount of the fluorescence deactivator is small, there is a possibility that the decrease in fluorescence intensity is insufficient and there is a problem in the readability of the postcard by the sorting machine . In Comparative Example 4 in which a large amount of the fluorescence deactivator was added, the change in fluorescence intensity was not significantly changed as compared with the Examples, and it was found that other problems such as a decrease in whiteness occurred.
本発明の紙は、古紙を活用した環境に優しい郵便はがきとして使用することができる。 The paper of the present invention can be used as an environmentally friendly postcard utilizing waste paper.
Claims (5)