JP2010534275A - 水性ポリウレタン尿素組成物含有分散体およびフィルム - Google Patents
水性ポリウレタン尿素組成物含有分散体およびフィルム Download PDFInfo
- Publication number
- JP2010534275A JP2010534275A JP2010518298A JP2010518298A JP2010534275A JP 2010534275 A JP2010534275 A JP 2010534275A JP 2010518298 A JP2010518298 A JP 2010518298A JP 2010518298 A JP2010518298 A JP 2010518298A JP 2010534275 A JP2010534275 A JP 2010534275A
- Authority
- JP
- Japan
- Prior art keywords
- composition
- dispersion
- prepolymer
- molecular weight
- polyisocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【選択図】 なし
Description
(a)ポリエーテル、ポリエステル、ポリカーボネートおよびこれらの組み合わせから選択される数平均分子量が600から4000の少なくとも1種のポリオール、
(b)芳香族ジイソシアネート、脂肪族ジイソシアネート、脂環式ジイソシアネートおよびこれらの組み合わせから成る群より選択される一員を含有して成るポリイソシアネート、
(c)(i)ポリイソシアネートと反応し得るヒドロキシ基および(ii)中和時に塩を形成する能力を有しかつ前記ポリイソシアネートと反応する能力を持たない少なくとも1種のカルボン酸基を含有して成る少なくとも1種のジオール化合物、
(d)中和剤、
(e)鎖延長剤、
(f)少なくとも1種の単官能アルコールを含有して成るイソシアネート基用ブロッキング剤、
の反応生成物である重合体、および
少なくとも1種の表面活性剤、
を含有する。
(a)(i)ポリエーテル、ポリエステル、ポリカーボネートおよびこれらの組み合わせから選択した数平均分子量が600から4000の少なくとも1種のポリオール、
(ii)芳香族ジイソシアネート、脂肪族ジイソシアネート、脂環式ジイソシアネートおよびこれらの組み合わせから成る群より選択した一員を含有して成るポリイソシアネート、
(iii)(i)ポリイソシアネートと反応し得るヒドロキシ基および(ii)中和時に塩を形成する能力を有しかつ前記ポリイソシアネートと反応する能力を持たない少なくとも1種のカルボン酸基を含有する少なくとも1種のジオール化合物、
の反応生成物を含有するプレポリマー組成物を調製し、
(b)前記プレポリマーを中和剤と表面活性剤を含有する水性組成物に入れて分散させ、(c)前記プレポリマーの鎖延長を起こさせることで重量平均分子量が約40,000から約250,000のポリウレタン尿素重合体が入っているポリウレタン尿素分散体を生じさせ、そして
(d)イソシアネート基用ブロッキング剤を用いて前記重合体の分子量を調節する、
ことを包含する。
本発明の範囲内に入る水性ポリウレタン分散体を特定のウレタンプレポリマーから生じさせるが、それもまたいくつかの態様の一面を構成する。
、600から3500など)の、これらに限定するものでないが、ポリエーテルグリコール、ポリエステルグリコール、ポリカーボネートグリコール、ポリブタジエングリコールまたはこれらの水素添加重合体およびヒドロキシ末端ポリジメチルシロキサンを包含するポリオールもしくはポリオール共重合体もしくはポリオール混合物、b)ジイソシアネート、例えば脂肪族ジイソシアネート、芳香族ジイソシアネートおよび脂環式ジイソシアネートを包含するポリイソシアネート、およびc)(i)ポリイソシアネートと反応し得るヒドロキシ基および(ii)中和時に塩を形成する能力を有しかつ前記ポリイソシアネートと反応する能力を持たない少なくとも1種のカルボン酸基を含有するジオール化合物、d)鎖延長剤、例えば水または脂肪族ジアミン系鎖延長剤または脂肪族ジアミン系鎖延長剤と炭素原子数が2から13の脂肪族ジアミンおよび脂環式ジアミンから選択される1種以上のジアミンの組み合わせまたはアミノ末端重合体を包含するジアミン系鎖延長剤、およびe)場合によりブロッキング剤または連鎖停止剤としての第一級もしくは第二級モノアルコールもしくはモノアミン、および場合により第一級もしくは第二級アミン基を少なくとも3個有する有機化合物もしくは重合体を含有する。
つであってもよい。
ウレタン尿素組成物を含有させることで内側衣服(例えばスリップ)の相対的位置を維持することも可能である。
装飾の目的で特定の領域に入れるフィルムの一部として用いるに有用であり得る。
いずれであってもよい。加うるに、本ポリウレタン尿素組成物は構造的特性、柔軟性、接着性またはそれらの任意組み合わせを示し得る。層配置の順は(1)布層、発泡層、ポリウレタン尿素組成物層、(2)布層、発泡層、ポリウレタン尿素組成物層、発泡層、布層、(3)布層、ポリウレタン尿素組成物層、布層、(4)発泡層、ポリウレタン尿素層、発泡層、(5)発泡層、ポリウレタン尿素層、(6)布層、ポリウレタン尿素層であってもよいか、或は布構造物の中により多くの層を達成する目的で組み合わせてもよいそれらの任意組み合わせであってもよい。それらの層のいずれかを接着させる目的で接着剤を含めることも可能であり、それには、本ポリウレタン尿素組成物が接着剤である場合が含まれる。
本発明に従うウレタンプレポリマーを生じさせる時に出発材料として用いるに適したポリオール成分は、数平均分子量が約600から約3,500もしくは約4,000のポリエーテルグリコール、ポリカーボネートグリコールおよびポリエステルグリコールである。
適切なポリイソシアネート成分の例には、ジイソシアネート、例えば1,6−ジイソシアナトヘキサン、1,12−ジイソシアナトドデカン、イソホロンジイソシアネート、トリメチルヘキサメチレンジイソシアネート、1,5−ジイソシアナト−2−メチルペンタン、ジイソシアナト−シクロヘキサン、メチレン−ビス(4−シクロヘキシルイソシアネート)、テトラメチル−キシレンジイソシアネート、ビス(イソシアナトメチル)シクロヘキサン、トルエンジイソシアネート、メチレンビス(4−フェニルイソシアネート)、フェニレンジイソシアネート、キシレンジイソシアネートおよび前記ジイソシアネートの混合物などが含まれる。例えば、そのようなジイソシアネートは芳香族ジイソシアネート、例えばフェニレンジイソシアネート、トリレンジイソシアネート(TDI)、キシリレンジイソシアネート、ビフェニレンジイソシアネート、ナフチレンジイソシアネート、ジフェニルメタンジイソシアネート(MDI)およびこれらの組み合わせであってもよい。
本発明に従うウレタンプレポリマーを生じさせる時にさらなる出発材料として用いるに適したジオール化合物には、(i)ポリイソシアネートと反応し得るヒドロキシ基を2個および(ii)中和時に塩を形成する能力を有しかつ前記ポリイソシアネート(b)と反応する能力を持たない少なくとも1種のカルボン酸基を有する少なくとも1種のジオール化合物が含まれる。カルボン酸基を有するジオール化合物の典型的な例には、2,2−ジメチロプロピオン酸(DMPA)、2,2−ジメチロブタン酸、2,2−ジメチロ吉草酸およびDMPA開始カプロラクトン、例えばCAPA(商標)HC 1060(Solvay)などが含まれる。本発明ではDMPAが好適である。
酸基を塩基に変化させるに適した中和剤の例には、第三級アミン(例えばトリエチルアミン、N,N−ジエチルメチルアミン、N−メチルモルホリン、N,N−ジイソプロピルエチルアミンおよびトリエタノールアミン)およびアルカリ金属の水酸化物(例えばリチウム、ナトリウムおよびカリウムの水酸化物)が含まれる。また、第一級および/または第二級アミンを酸基中和用の中和剤として用いることも可能である。その中和の度合は一般に酸基の約60%から約140%、例えば約80%から約120%の範囲である。
本発明で用いるに有用な鎖延長剤には、ジアミン系鎖延長剤および水が含まれる。有用な鎖延長剤の数多くの例が通常の当業者に公知である。適切なジアミン系鎖延長剤の例には、1,2−エチレンジアミン、1,4−ブタンジアミン、1,6−ヘキサメチレンジアミン、1,12−ドデカンジアミン、1,2−プロパンジアミン、2−メチル−1,5−ペンタンジアミン、1,2−シクロヘキサンジアミン、1,4−シクロヘキサンジアミン、4,4’−メチレン−ビス(シクロヘキシルアミン)、イソホロンジアミン、2,2−ジメチル−1,3−プロパンジアミン、メタ−テトラメチルキシレンジアミンおよび分子量が500未満のJeffamine(商標)(Texaco)が含まれる。
適切な表面活性剤(界面活性剤)の例には、アニオン性、カチオン性または非イオン性分散剤または界面活性剤、例えばドデシル硫酸ナトリウム、ナトリウムジオクチルスルホスクシネート、ドデシルベンゼンスルホン酸ナトリウム、エトキシル化アルキルフェノール、例えばエトキシル化ノニルフェノールなど、およびエトキシル化脂肪アルコール、臭化ラウリルピリジニウム、ポリエーテルホスフェートおよび燐酸エステル、修飾アルコール−エトキシレートおよびこれらの組み合わせが含まれる。
イソシアネート基用ブロッキング剤は、単官能アルコールまたは単官能アミンのいずれであってもよい。このブロッキング剤を添加する時期はプレポリマー生成前、プレポリマー生成中またはプレポリマー生成後のいずれであってもよく、それには、プレポリマーを水性媒体、例えば脱イオン水などに入れて分散させる前および後が含まれる。いくつかの態様では、そのブロッキング剤は任意であるか或はそれを排除してもよい。他の態様では、そのようなブロッキング剤を当該プレポリマーの重量を基準にして約0.05%から約10.0%(約0.1%から約6.0%および約1.0%から約4.0%を包含)の量で含有させてもよい。そのようなブロッキング剤を最終的分散体の重量を基準にして約0.01%から約6.0%(約0.05%から約3%および約0.1%から約1.0%を包含)の量で存在させてもよい。
(2−ヒドロキシエチル)スクシニミド、4−(2−ヒドロキシエチル)モルホリン、メタノール、エタノール、ブタノール、ネオペンチルアルコール、ヘキサノール、シクロヘキサノール、シクロヘキサンメタノール、ベンジルアルコール、オクタノール、オクタデカノール、N,N−ジエチルヒドロキシルアミン、2−(ジエチルアミノ)エタノール、2−ジメチルアミノエタノールおよび4−ピペリジンエタノールおよびこれらの組み合わせが含まれる。
適切な消泡もしくは脱泡または泡制御剤の例には、Additive 65およびAdditive 62(Dow Corningのシリコーンが基になった添加剤)、FoamStar(商標)I 300[Cognisの鉱油が基になった脱泡剤(シリコーンを含有しない)]およびSurfynol(商標)DF 110L(Air Products & Chemicalsの非イオン性界面活性剤である高分子量のアセチレン系グリコール)が含まれる。
電防止剤、抗クレーター形成剤、抗クローリング剤、光学的光沢剤、合体剤、導電性添加剤、発光添加剤、流動および平滑化剤、凍結解凍安定剤、滑剤、有機および無機充填剤、防腐剤、テクスチャリング剤、サーモクロミック添加剤、昆虫忌避剤および湿潤剤が含まれる。
ポリオールを約34%から約89%(約61%から約80%を包含)、
ポリイソシアネートを約10%から約59%(約18%から約35%を包含)、および
ジオール化合物を約1.0%から約7.0%(約2.0%から約4.0%を包含)。
均一性を向上させる目的、例えば被覆/フィルム形成工程における筋および亀裂を減少させる目的などでも使用可能である。
1)重合が完了した後であるがプレポリマーを移送して分散させる前のプレポリマーに溶媒を添加して混合してもよく、その希釈されたプレポリマーはバックボーン中にカルボン酸基(ジオール化合物に由来)および鎖末端にイソシアネート基を含有し、それを中和した後、それを水に分散させながら鎖延長を起こさせる。
2)溶媒を他の材料、例えばポリオール、ポリイソシアネートおよびジオール化合物などと一緒に添加して混合することでプレポリマーを溶液中で生じさせた後、そのようにバックボーン中にカルボン酸基を含有しかつ鎖末端にイソシアネート基を含有するプレポリマーを溶液の状態で水に分散させると同時にそれの中和および鎖延長を起こさせる。
3)溶媒をジオール化合物と中和剤の中和された塩と一緒に添加した後にポリオールおよびポリイソシアネートと混合することでプレポリマーを生じさせた後、分散を起こさせてもよい。
4)溶媒をTEAと混合しそして次に生成プレポリマーに添加した後、分散を起こさせてもよい。
5)溶媒をポリオールと一緒に添加して混合した後、ジオール化合物および中和剤を添加しそして次に続いてポリイソシアネートを溶液の状態の中和されたプレポリマーに添加した後、分散を起こさせてもよい。
6)また、溶媒を分散体から除去することも可能であり、特にアセトン工程の場合に可能である。
な方法で約100℃未満の温度で行って水を除去することで前記剥離紙の上にフィルムを生じさせることで実施可能である。そのフィルムは単層または多層であってもよい。多層フィルムを生じさせる場合、同じ分散体もしくは異なる分散体を一緒に積層方法または逐次的被覆方法もしくは直接被覆方法で接着させることで多層フィルムを生じさせることができる。その生じさせたフィルムシートを細長く切ることで所望幅の片を生じさせそして後で伸縮製品、例えば織布などを成形する用途で使用する目的でスプールに巻き上げてもよい。そのような用途の例には、縫い目無しもしくは継ぎ目無し衣類構造物、継ぎ目の密封および補強、衣類に接着させるラベルおよびパッチ、および局所的引き伸ばし/回復補強が含まれる。接着による結合を約100℃から約200℃、例えば約130℃から約200℃、例えば約140℃から約180℃の範囲の温度で0.1秒から数分、例えば約1分以内の時間で生じさせることができる。典型的な結合用機械はSew Free[SewSystems(Leicester、英国)から商業的に入手可能]、Macpi裾縫い機[Macpi Group(Brescia、イタリア)から商業的に入手可能]、Framis熱風溶着機[Framis Italy,sp.a.(ミラノ、イタリア)から商業的に入手可能]である。そのような結合は織布衣類が繰り返し着用、洗濯および引き伸ばされた時に強くかつ耐久性があると期待する。
的/より重質な層が要求される場合にはそれを繰り返してもよい。本分散体を被覆、結合、積層および接着の目的で合成、天然または合成/天然混合材料で出来ている編み、織りもしくは不織布のいずれかに付着させることができる。本分散体を加工中に乾燥(例えば空気乾燥またはオーブンの使用による)させることでそれに入っている水を除去して、沈澱して合体したポリウレタン層を布上に残存させることで接着結合を形成させることができる。
限定するものでないが、衣服(如何なる種類の衣類も衣服製品も包含)、編み手袋、室内装飾品、髪アクセサリー、ベッドシーツ、カーペットおよびカーペット裏地、コンベアベルト、医学用途、例えば伸縮性包帯など、パーソナルケア品目(失禁および女性衛生品を包含)および履物が含まれる。分散体で被覆された製品またはフィルムもしくはテープで覆われた製品は騒音防止製品として使用可能である。
− 引き伸ばした後の永久歪みが約0から10%、例えば約0から5%、典型的には約0から約3%、
− 伸びが約400から約800%、および
− じん性が約0.5から約3Mpa。
− 50回洗濯した後の剥離強度に関して、洗濯前にそれが示した強度の少なくとも50%を維持、
− 空気透過率が少なくとも約0から約0.5cfm、および
− 24時間の水蒸気透過率が少なくとも約0から約300g/m2。
Pluracol(商標)HP 4000Dは、数平均分子量が4000の第一ヒドロキシ末端線状ポリプロピレンエーテルグリコール[BASF(Bruxelles、ベルギー)から商業的に入手可能]であり、
Mondur(商標)MLは、2,4’−MDI異性体含有量が50−60%で4,4’−MDI異性体含有量が50−40%のジフェニルメタンジイソシアネート(MDI)異性体混合物[Bayer(Baytown、TX)から商業的に入手可能]であり、
Lupranate(商標)MIは、2,4’−MDI異性体含有量が45−55%で4,4’−MDI異性体含有量が55−45%のジフェニルメタンジイソシアネート(MDI)異性体混合物[BASF(Wyandotte、ミシガン)から商業的に入手可能]であり、
Isonate(商標)125MDRは、4,4’−MDI異性体含有量が98%で2,4’−MDI異性体含有量が2%の高純度ジフェニルメタンジイソシアネート(MDI)混合物[Dow Company(Midland、ミシガン)から商業的に入手可能]であり、そして
DMPAは2,2−ジメチロプロピオン酸である。
D1343−69の一般的方法に従ってModel DV−8の落球粘度計[Duratech Corp.(Waynesboro、VA)が販売]を用いてそれを約40℃で操作することで実施した。そのキャップドグリコールプレポリマーが有するNCO基の重量パーセントに換算した総イソシアネート部分含有量の測定をS.Siggia、「Quantitative Organic Analysis via Functio
nal Group」、第3版、Wiley & Sons、New York、559−561頁(1963)(これの開示は全体が引用することによって本明細書に組み入れられる)の方法を用いて実施した。
で室温で貯蔵した。その分散体の固体量は40%で粘度は約28センチポイズであった。この分散体から流延したフィルムは柔らかで粘着性がありかつゴム弾性を示した。
Claims (27)
- ポリウレタン尿素の水性分散体を含有して成る組成物であって、前記分散体が、
(a)ポリエーテル、ポリエステル、ポリカーボネートおよびこれらの組み合わせから選択される数平均分子量が600から4000の少なくとも1種のポリオール、
(b)芳香族ジイソシアネート、脂肪族ジイソシアネート、脂環式ジイソシアネートおよびこれらの組み合わせから成る群より選択される一員を含有して成るポリイソシアネート、
(c)(i)ポリイソシアネートと反応し得るヒドロキシ基および(ii)中和時に塩を形成する能力を有しかつ前記ポリイソシアネートと反応する能力を持たない少なくとも1種のカルボン酸基を含有して成る少なくとも1種のジオール化合物、
(d)中和剤、
(e)鎖延長剤、
(f)少なくとも1種の単官能アルコールを含有して成るイソシアネート基用ブロッキング剤、
の反応生成物である重合体、および
少なくとも1種の表面活性剤、
を含有して成る組成物。 - 前記分散体に溶媒が実質的に添加されていない請求項1記載の組成物。
- 前記ポリオールが示す数平均分子量が600から3500である請求項1記載の組成物。
- 前記単官能アルコールが炭素数が1から18の脂肪族および脂環式第一級および第二級アルコール、フェノール、置換フェノール、分子量が750未満のエトキシル化アルキルフェノールおよびエトキシル化脂肪アルコール、ヒドロキシアミン、ヒドロキシメチルおよびヒドロキシエチルで置換されている第三級アミン、ヒドロキシメチルおよびヒドロキシエチルで置換されている複素環式化合物およびこれらの組み合わせから成る群より選択される少なくとも一員を含有して成る請求項1記載の組成物。
- 前記単官能アルコールがフルフリルアルコール、テトラヒドロフルフリルアルコール、N−(2−ヒドロキシエチル)スクシニミド、4−(2−ヒドロキシエチル)モルホリン、メタノール、エタノール、ブタノール、ネオペンチルアルコール、ヘキサノール、シクロヘキサノール、シクロヘキサンメタノール、ベンジルアルコール、オクタノール、オクタデカノール、N,N−ジエチルヒドロキシルアミン、2−(ジエチルアミノ)エタノール、2−ジメチルアミノエタノールおよび4−ピペリジンエタノールおよびこれらの組み合わせから成る群より選択される少なくとも一員を含有して成る請求項1記載の組成物。
- 前記ポリオールが数平均分子量が1400から2400のポリ(テトラメチレンエーテル)グリコールを含有して成る請求項1記載の組成物。
- 前記鎖延長剤が水、ジアミン系鎖延長剤およびこれらの組み合わせから選択される請求項1記載の組成物。
- 前記ポリイソシアネートが4,4’−と2,4’−メチレンビス(フェニルイソシアネート)(MDI)異性体の混合物を4,4’−MDIと2,4’−MDI異性体の比率が65:35から35:65の範囲であるように含有して成る請求項1記載の組成物。
- 前記ジオールが2,2−ジメチロプロピオン酸(DMPA)、2,2−ジメチロブタン
酸、2,2−ジメチロ吉草酸およびこれらの組み合わせから成る群より選択される請求項1記載の組成物。 - 前記分散体が重量平均分子量が約40,000から約250,000のポリウレタン尿素重合体を含有して成る請求項1記載の組成物。
- 前記分散体が重量平均分子量が約40,000から約150,000のポリウレタン尿素重合体を含有して成る請求項1記載の組成物。
- 前記中和剤が第三級アミンおよびアルカリ金属の水酸化物から成る群より選択される少なくとも一員を含有して成りかつ前記少なくとも1種のブロッキング剤がN,N−ジエチルアミン、N−エチル−N−プロピルアミン、N,N−ジイソプロピルアミン、N−t−ブチル−N−メチルアミン、N−t−ブチル−N−ベンジルアミン、N,N−ジシクロヘキシルアミン、N−エチル−N−イソプロピルアミン、N−t−ブチル−N−イソプロピルアミン、N−イソプロピル−N−シクロヘキシルアミン、N−エチル−N−シクロヘキシルアミン、N,N−ジエタノールアミンおよび2,2,6,6−テトラメチルピペリジンから成る群より選択される請求項1記載の組成物。
- 前記表面活性剤がドデシル硫酸ナトリウム、ナトリウムジオクチルスルホスクシネート、ドデシルベンゼンスルホン酸ナトリウム、エトキシル化アルキルフェノール、臭化ラウリルピリジニウム、エトキシル化脂肪アルコール、ポリエーテルホスフェート、燐酸エステル、修飾アルコール−エトキシレートおよびこれらの組み合わせから成る群より選択される少なくとも一員を含有して成る請求項1記載の組成物。
- ポリウレタン尿素の水性分散体を含有して成る組成物であって、前記分散体がプレポリマー組成物、中和剤および鎖延長剤を含有して成る組成物の反応生成物である重合体を含有して成り、かつ前記プレポリマー組成物がポリオール、ポリイソシアネート、ジオールおよびブロッキング剤を含有して成る組成物の反応生成物である組成物。
- 前記ポリオールがポリエーテル、ポリエステル、ポリカーボネートおよびこれらの組み合わせから選択されかつ前記ポリオールが示す数平均分子量が600から4000である請求項14記載の組成物。
- 前記ポリオールがポリエーテル、ポリエステル、ポリカーボネートおよびこれらの組み合わせから選択されかつ前記ポリオールが示す数平均分子量が600から3500である請求項14記載の組成物。
- 前記ポリイソシアネートが芳香族ジイソシアネート、脂肪族ジイソシアネート、脂環式ジイソシアネートおよびこれらの組み合わせから成る群より選択される一員を含有して成る請求項14記載の組成物。
- 前記ジオール化合物が(i)ポリイソシアネートと反応し得るヒドロキシ基および(ii)中和時に塩を形成する能力を有しかつ前記ポリイソシアネートと反応する能力を持たない少なくとも1種のカルボン酸基を含有して成る請求項14記載の組成物。
- 前記イソシアネート基用ブロッキング剤が少なくとも1種の単官能アルコールを含有して成る請求項14記載の組成物。
- 落球方法を用いて40℃で測定した時に前記プレポリマー組成物が500から6,000ポイズの体積粘度を示す請求項14記載の組成物。
- 前記プレポリマー組成物が溶媒の添加無しに調製された組成物である請求項14記載の組成物。
- ポリウレタン尿素の水性分散体を製造する方法であって、
(a)(i)ポリエーテル、ポリエステル、ポリカーボネートおよびこれらの組み合わせから選択した数平均分子量が600から4000の少なくとも1種のポリオール、
(ii)芳香族ジイソシアネート、脂肪族ジイソシアネート、脂環式ジイソシアネートおよびこれらの組み合わせから成る群より選択した一員を含有して成るポリイソシアネート、
(iii)(i)ポリイソシアネートと反応し得るヒドロキシ基および(ii)中和時に塩を形成する能力を有しかつ前記ポリイソシアネートと反応する能力を持たない少なくとも1種のカルボン酸基を含有して成る少なくとも1種のジオール化合物、
の反応生成物を含有して成るプレポリマー組成物を調製し、
(b)前記プレポリマーを中和剤と界面活性剤を含有して成る水性組成物に入れて分散させ、
(c)前記プレポリマーの鎖延長を起こさせることで重量平均分子量が約40,000から約250,000のポリウレタン尿素重合体が入っているポリウレタン尿素分散体を生じさせ、そして
(d)イソシアネート基用ブロッキング剤を用いて前記重合体の分子量を調節する、
ことを含んで成る方法。 - 前記分子量の調節が前記重量平均分子量の調節および前記重合体の分子量分布の調節を包含する請求項22記載の方法。
- 前記ブロッキング剤を単官能アルコール、単官能アミンおよびこれらの組み合わせから選択する請求項22記載の方法。
- 前記ブロッキング剤を前記プレポリマー組成物、前記水性組成物または両方に添加する請求項22記載の方法。
- 前記ブロッキング剤が少なくとも1種の単官能アルコールでありそして前記ブロッキング剤を前記プレポリマー組成物に(a)前記プレポリマー生成前、(b)前記プレポリマー生成後、(c)前記プレポリマー生成中およびこれらの組み合わせから選択した時間点で添加する請求項22記載の方法。
- ポリウレタン尿素の水性分散体および基質を含有して成る組成物であって、前記分散体が、
(a)ポリエーテル、ポリエステル、ポリカーボネートおよびこれらの組み合わせから選択される数平均分子量が600から4000の少なくとも1種のポリオール、
(b)芳香族ジイソシアネート、脂肪族ジイソシアネート、脂環式ジイソシアネートおよびこれらの組み合わせから成る群より選択される一員を含有して成るポリイソシアネート、
(c)(i)ポリイソシアネートと反応し得るヒドロキシ基および(ii)中和時に塩を形成する能力を有しかつ前記ポリイソシアネートと反応する能力を持たない少なくとも1種のカルボン酸基を含有して成る少なくとも1種のジオール化合物、
(d)中和剤、
(e)鎖延長剤、
(f)少なくとも1種の単官能アルコールを含有して成るイソシアネート基用ブロッキング剤、
の反応生成物である重合体、および
少なくとも1種の表面活性剤、
を含有して成る組成物。