JP2010280758A - Molded body with water absorptive and water retentive ability and biodegradability and base for flower arrangement comprising the molded body - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a molded body that can be suitably used for a base for flower arrangement and has biodegradability and also both water absorptive and water retentive abilities. <P>SOLUTION: The molded body comprises solidifying a poorly water-soluble and biodegradable material having any one or more forms selected from the group consisting of an amorphous powder, a scale-like powder, a chopped strand with a length of 10 mm or less, and a cotton-like fiber with a length of 10 mm or less using a biodegradable material capable of composing an aqueous gel, as a binder. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

本発明は、生分解性と吸水・保水性能を併せ持った成形体および該成形体からなるフラワーアレンジメント用台座に関する。   The present invention relates to a molded article having both biodegradability and water absorption / water retention performance and a flower arrangement pedestal comprising the molded article.

日本では、伝統的に切り花植物等を用いた生け花が盛んに行われており、これらは家庭の中は勿論、例えば、冠婚葬祭等の会場内を飾ったり、飲食店等の商業用店舗の店頭、近代建築ビルの玄関等を飾るために用いられている。最近では、このような伝統的な生け花のほかに、西洋フラワーアレンジメント、近代フラワーアート等も盛んに行われるようになっている。   In Japan, traditionally ikebana using cut plants is actively performed, and these can be used not only in the home, but also in the venues such as ceremonial occasions and in commercial stores such as restaurants. It is used to decorate storefronts and modern building entrances. Recently, in addition to such traditional ikebana, Western flower arrangements, modern flower art, etc. have been actively performed.

上述した切り花や他の植物等を美的に配置する種々の行為を、本明細書ではフラワーアレンジメントと呼ぶことにするが、このフラワーアレンジメントにおいて切り花や他の植物等を支持、固定する台座として、日本古来の華道では伝統的に金属製の剣山が使用されており、現在でも剣山が主流である。   Various actions for aesthetically arranging cut flowers and other plants mentioned above will be referred to as flower arrangements in this specification, but as a pedestal for supporting and fixing cut flowers and other plants in this flower arrangement, Japan Traditional Chinese swordsmen have traditionally been used for metal swords, and swords are still mainstream.

しかしながら、剣山は花の支持・固定できる角度や高さが限定されており、表現の自由が制限され、利便性に優れるものではなかった。そこで、より手軽に、アーティフィシャルに、かつ広範囲の用途に使用できる台座として、例えば、特許文献１などにはフェノール樹脂の発泡体、いわゆるフェノールフォーム製の台座が開示されており、欧米だけでなく日本でも広く使用されている。   However, Kenyama was limited in the angle and height at which flowers can be supported and fixed, and the freedom of expression was limited, so it was not very convenient. Therefore, as a pedestal that can be used more easily, artificially, and in a wide range of applications, for example, Patent Document 1 discloses a foamed phenol resin, a so-called pedestal made of phenol foam, not only in the West Widely used in Japan.

このようなフェノールフォーム製の台座は、軽量で加工や表現の自由度が高く、手軽に使用できるものであったが、フェノールフォームは熱硬化性樹脂であるため再生（リサイクル）使用ができず、また、廃棄された際、環境ホルモンの疑いがあるビスフェノールを発生するおそれがある。   Such a phenol foam pedestal is lightweight, has a high degree of freedom of processing and expression, and can be used easily, but since phenol foam is a thermosetting resin, it cannot be recycled (recycled). In addition, when discarded, bisphenol, which is suspected of being an environmental hormone, may be generated.

また、特許文献２には、フェノールフォーム成分に生分解性成分を副成分として添加し、生物学的に分解可能としたフォームが開示されている。しかしながら、このような生物学的に分解可能なフォームであっても、フェノール成分を含有するかぎり、環境ホルモンの問題は解決されず、逆に、分解することにより、フェノール成分は土中への拡散が促進される。   Patent Document 2 discloses a foam that is biodegradable by adding a biodegradable component as a subcomponent to a phenol foam component. However, even such biologically degradable foams do not solve the problem of environmental hormones as long as they contain a phenol component, and conversely, decomposition causes the phenol component to diffuse into the soil. Is promoted.

以上のような理由から、フラワーアレンジメント用台座についても、環境に優しい生分解性プラスチック製のものが望まれている。特許文献３は、吸水率、吸水速度および保水性に優れたポリウレタンフォーム複合体に関するものであるが、給水・保水性不足の改善を目的として、ポリオールとイソシアネートを混合して発泡固化させるに際し、植物質物質の粉体およびゲル形成型吸水性ポリマー（いわゆる高級水性高分子）を共存させることによって、ポリウレタン製フラワーアレンジメント台座に吸水保水性を付与できることを開示している。しかしながら、特許文献３の技術は、植物質物質やゲル形成型吸水性ポリマーを、ポリウレタンをマトリックスとして形状保持したものである。また、添加する植物質物質やゲル形成型吸水性ポリマーのサイズを１００μｍ以下の微粉を使用していることから、ポリウレタンマトリックス中に埋没してしまい、本来の親水性や吸水性が発揮されず十分な給水量を確保できない恐れがある。   For the reasons described above, an environmentally friendly biodegradable plastic is also desired for the flower arrangement pedestal. Patent Document 3 relates to a polyurethane foam composite excellent in water absorption rate, water absorption rate, and water retention. For the purpose of improving water supply / water retention deficiency, a polyol and isocyanate are mixed and foamed and solidified. It is disclosed that water-absorbing water retention property can be imparted to a polyurethane flower arrangement pedestal by coexisting a powdery substance and a gel-forming water-absorbing polymer (so-called high-grade water-based polymer). However, the technique of Patent Document 3 is a technique in which a plant material or a gel-forming water-absorbing polymer is held in a polyurethane matrix. In addition, since the plant material to be added and the size of the gel-forming water-absorbing polymer used are fine powders of 100 μm or less, they are buried in the polyurethane matrix, and the original hydrophilicity and water absorption are not sufficiently exhibited. There is a risk that a sufficient amount of water supply cannot be secured.

特開平９−７５１９３号公報Japanese Patent Laid-Open No. 9-75193 特開平８−５３５６４号公報JP-A-8-53564 特開２００７−１８６６５７号公報JP 2007-186657 A

本発明の目的は、生分解性を有し、かつ、吸水・保水性能を併せ持った成形体を提供することにある。   An object of the present invention is to provide a molded article having biodegradability and having both water absorption and water retention performance.

本研究者らは上述のごとき事情に鑑み鋭意検討を行った結果、従来の発泡技術を基礎とする吸水・保水性材料とは全く異なる技術によって所望の性能を有した成形体を獲得することに成功した。すなわち、特定の形状を有した難水溶性の生分解性材料を、水性ゲルを構成しうる生分解性材料をバインダーとして固化することによって、生分解性を維持しつつフラワーアレンジメント用台座に必要な高い吸水・保水性を有する成形体となることを見出した。   As a result of intensive studies in view of the circumstances as described above, the present researchers have obtained a molded product having a desired performance by a technology completely different from a water-absorbing / water-holding material based on the conventional foaming technology. Successful. In other words, a hardly water-soluble biodegradable material having a specific shape is solidified using a biodegradable material that can form an aqueous gel as a binder, so that it is necessary for a pedestal for flower arrangement while maintaining biodegradability. It has been found that the molded article has high water absorption and water retention.

即ち、本発明は以下の構成よりなる。
〔１〕 不定形の粉末、鱗片状の粉末、長さ１０ｍｍ以下のチョップドストランド、長さ１０ｍｍ以下の綿状の繊維からなる群から選ばれる何れか１以上の形状である難水溶性生分解性材料を、水性ゲルを構成しうる生分解性材料をバインダーとして固化してなる成形体。
〔２〕 難水溶性生分解性材料が、脂肪族ポリエステル系樹脂、セルロース、セルロース誘導体、タンパク質、タンパク質誘導体からなる群から選ばれる１以上を含んでなる〔１〕記載の成形体。
〔３〕 難水溶性生分解性材料が、脂肪族ポリエステル系樹脂である〔２〕記載の成形体。
〔４〕 脂肪族ポリエステル系樹脂が、ポリ乳酸系樹脂である〔３〕に記載の成形体。
〔５〕 水性ゲルを構成しうる生分解性材料が、水溶性多糖類、ゼラチン、ゼラチン誘導体から選ばれる１以上を主たる成分とする〔１〕〜〔４〕何れかに記載の成形体。
〔６〕 〔１〕〜〔５〕何れかに記載の成形体からなるフラワーアレンジメント用台座。 That is, the present invention has the following configuration.
[1] Slightly water-soluble biodegradable material having any one or more shapes selected from the group consisting of amorphous powder, scaly powder, chopped strands having a length of 10 mm or less, and cotton-like fibers having a length of 10 mm or less A molded body obtained by solidifying a material using a biodegradable material that can form an aqueous gel as a binder.
[2] The molded article according to [1], wherein the hardly water-soluble biodegradable material includes one or more selected from the group consisting of aliphatic polyester resins, cellulose, cellulose derivatives, proteins, and protein derivatives.
[3] The molded article according to [2], wherein the hardly water-soluble biodegradable material is an aliphatic polyester resin.
[4] The molded article according to [3], wherein the aliphatic polyester resin is a polylactic acid resin.
[5] The molded article according to any one of [1] to [4], wherein the biodegradable material that can form the aqueous gel contains one or more selected from water-soluble polysaccharides, gelatin, and gelatin derivatives as main components.
[6] A pedestal for flower arrangement comprising the molded article according to any one of [1] to [5].

本発明の成形体は、生分解性であり、かつ吸水・保水性能を有している。そのため、フラワーアレンジメント用台座として好適に使用することが出来る。   The molded body of the present invention is biodegradable and has water absorption and water retention performance. Therefore, it can be suitably used as a pedestal for flower arrangement.

本発明のフラワーアレンジメント用台座は、花の挿し性、花の保持性がよく、また、吸水・保水性に優れているため、花持ちがよい。   The pedestal for flower arrangement of the present invention has good flower insertion and flower retention, and also has excellent water absorption and water retention, and therefore has a long flower life.

本発明の成形体は、形状が、不定形の粉末、鱗片状の粉末、長さ１０ｍｍ以下のチョップドストランド、長さ１０ｍｍ以下の綿状の繊維からなる群から選ばれる何れか１以上である、難水溶性生分解性材料を、水性ゲルを構成しうる生分解性材料をバインダーとして固化することによって得られる。   The molded body of the present invention is any one or more selected from the group consisting of an amorphous powder, a scaly powder, a chopped strand having a length of 10 mm or less, and a cotton-like fiber having a length of 10 mm or less. The hardly water-soluble biodegradable material is obtained by solidifying a biodegradable material that can constitute an aqueous gel as a binder.

本発明の難水溶性生分解性材料の形状は、不定形の粉末、鱗片状の粉末、長さ１０ｍｍ以下のチョップドストランド、長さ１０ｍｍ以下の綿状の繊維からなる群から選ばれる何れか１以上である。これらは、後述する単一の材料種で、異なる形状を有した複数の難水溶性生分解性材料を使用してもよいし、異なる材料種でそれぞれが異なる形状を有していてもよい。   The shape of the hardly water-soluble biodegradable material of the present invention is any one selected from the group consisting of amorphous powder, scaly powder, chopped strands having a length of 10 mm or less, and cotton-like fibers having a length of 10 mm or less. That's it. These may be a single material type to be described later, and a plurality of poorly water-soluble biodegradable materials having different shapes may be used, or different material types may have different shapes.

不定形の粉末とは、目開き４ｍｍ（５メッシュ；ＵＳＡ）を通過するものをいう。具体的には、生分解性プラスチック成形体の破砕物、籾殻、小麦ふすま、落花生の殻などの破砕物や、おからやコーヒーの絞り粕の乾燥物、などが例示できる。   The amorphous powder means a powder that passes through an opening of 4 mm (5 mesh; USA). Specific examples include crushed materials of biodegradable plastic moldings, crushed materials such as rice husks, wheat bran, and peanut shells, and dried products such as okara and coffee squeezed rice cakes.

燐片状の粉末とは前記不定形の粉末以外のものであってアスペクト比が３以上であり、最大長が１０ｍｍ以下であるものをいう。具体的には、紙を千切ったもの、生分解性ポリマーのフィルムをスリット後所定の長さにカットしたもの、あるいは上記不定形の粉末の原料となる物質を祖粉砕したもの等が例示できる。   The flake-like powder means a powder other than the irregular powder having an aspect ratio of 3 or more and a maximum length of 10 mm or less. Specific examples include a piece of paper, a biodegradable polymer film cut to a predetermined length after slitting, or a material obtained by pulverizing a material that is a raw material for the above-mentioned amorphous powder. .

チョップドストランドとは、ストランドをカットしたものであり、ストランド径が、好ましくは、０．００１ｍｍ〜１ｍｍのストランドを、１０ｍｍ以下の長さにカットしたものを本発明においては使用しうる。具体的には、市販されているポリ乳酸系マルチフィラメント、ステープル、モノフィラメントを所定の長さにカットしたものなどが例示できる。   The chopped strand is obtained by cutting a strand, and a strand having a strand diameter of preferably 0.001 mm to 1 mm cut into a length of 10 mm or less can be used in the present invention. Specific examples include commercially available polylactic acid-based multifilaments, staples, monofilaments cut to a predetermined length, and the like.

長さ１０ｍｍ以下の綿状の繊維とは、太さが０．０１ｍｍ〜０．１ｍｍ程度のものを言い、具体的には、絹、コットン、羊毛やカシミヤ、アルパカなどに代表される獣毛繊維、再生古紙繊維等が例示できる。   Cotton-like fibers having a length of 10 mm or less are those having a thickness of about 0.01 mm to 0.1 mm. Specifically, animal fibers represented by silk, cotton, wool, cashmere, alpaca, etc. Recycled recycled paper fibers can be exemplified.

本発明で用いる難水溶性生分解性材料とは、２３℃、ｐＨ７．０の水１００ｇに対し、０．１ｇ以下の溶解度のものをいい、一般的に「不溶性」といわれる、全く水に溶けない概念をも含んでいる。難水溶性生分解性材料としては、脂肪族ポリエステル系樹脂、セルロース、セルロース誘導体、タンパク質、タンパク質誘導体、天然有機物系廃材、非水溶性無機塩、鉱物、セラミックスなどが挙げられる。中でも、脂肪族ポリエステル系樹脂、セルロース、セルロース誘導体、タンパク質、タンパク質誘導体、天然有機物系廃材からなる群から選ばれる１以上であることが、フラワーアレンジメント用台座全体として生分解性を確保できるため好ましい。   The poorly water-soluble biodegradable material used in the present invention has a solubility of 0.1 g or less with respect to 100 g of water at 23 ° C. and pH 7.0, and is generally insoluble in water, generally referred to as “insoluble”. It also contains no concept. Examples of the hardly water-soluble biodegradable materials include aliphatic polyester resins, cellulose, cellulose derivatives, proteins, protein derivatives, natural organic waste materials, water-insoluble inorganic salts, minerals, ceramics, and the like. Among these, one or more selected from the group consisting of aliphatic polyester resins, cellulose, cellulose derivatives, proteins, protein derivatives, and natural organic waste materials is preferable because biodegradability can be ensured for the entire flower arrangement pedestal.

脂肪族ポリエステル系樹脂は、脂肪族ポリエステルを少なくとも３５モル％以上含んでなるものであり、生分解性であれば特に限定はないが、例えば、ポリ乳酸を主たる成分とするポリ乳酸系樹脂、ヒドロキシ酸重縮合物、ポリカプロラクトン等のラクトンの開環重合物、ポリブチレンサクシネート、ポリブチレンアジペート、ポリブチレンサクシネートアジペート、ポリ（ブチレンアジペート／テレフタレート）等の脂肪族多価アルコールと脂肪族多価カルボン酸との重縮合物などが例示でき、これらの群より選ばれる少なくとも１種を用いることができる。   The aliphatic polyester-based resin contains at least 35 mol% of aliphatic polyester and is not particularly limited as long as it is biodegradable. For example, a polylactic acid-based resin mainly composed of polylactic acid, hydroxy Acid polycondensates, ring-opening polymerization products of lactones such as polycaprolactone, polybutylene succinate, polybutylene adipate, polybutylene succinate adipate, poly (butylene adipate / terephthalate) and other polyhydric alcohols and aliphatic polyhydric acids Examples thereof include polycondensates with carboxylic acids, and at least one selected from these groups can be used.

脂肪族多価アルコールとしては、グリコール酸、ヒドロキシ酪酸、ヒドロキシ吉酸、ヒドロキシカプロン酸、ヒドロキシヘプタン酸等が挙げられる。脂肪族多価カルボン酸としては、コハク酸、アジピン酸、スベリン酸、セバシン酸、ドデカンジカルボン酸、無水コハク酸、無水アジピン酸、トリメシン酸、プロパントリカルボン酸、ピロメリット酸、無水ピロメリット酸等が挙げられる。脂肪族多価アルコールとしては、エチレングリコール、１，４−ブタンジオール、１，６−ヘキサンジオール、１，４−シクロヘキサンジメタノール、ネオペンチルグリコール、デカメチレングリコール、グリセリン、トリメチロールプロパン、ペンタエリトリット等が挙げられる。   Examples of the aliphatic polyhydric alcohol include glycolic acid, hydroxybutyric acid, hydroxyvaleric acid, hydroxycaproic acid, and hydroxyheptanoic acid. Examples of aliphatic polycarboxylic acids include succinic acid, adipic acid, suberic acid, sebacic acid, dodecanedicarboxylic acid, succinic anhydride, adipic anhydride, trimesic acid, propanetricarboxylic acid, pyromellitic acid, and pyromellitic anhydride. Can be mentioned. Aliphatic polyhydric alcohols include ethylene glycol, 1,4-butanediol, 1,6-hexanediol, 1,4-cyclohexanedimethanol, neopentyl glycol, decamethylene glycol, glycerin, trimethylolpropane, pentaerythritol Etc.

ポリ乳酸系樹脂は、生分解性を大きく阻害しない限りは、一部モノマーが乳酸と交換可能な脂肪族ヒドロキシカルボン酸、脂肪族多価カルボン酸、脂肪族多価アルコール等で置き換わってもよく、エポキシ化大豆油やエポキシ化亜麻仁油などで一部架橋されていてもよい。   The polylactic acid-based resin may be replaced with an aliphatic hydroxycarboxylic acid, an aliphatic polyvalent carboxylic acid, an aliphatic polyhydric alcohol, etc., in which some monomers can be exchanged with lactic acid, as long as the biodegradability is not greatly inhibited. It may be partially crosslinked with epoxidized soybean oil or epoxidized linseed oil.

本発明の効果を阻害しない範囲においては、脂肪族ポリエステル系樹脂に他の樹脂を添加して使用してもよい。その場合脂肪族ポリエステル系樹脂が５０重量％以上含まれることが好ましく、より好ましくは７０重量％以上、更に好ましくは９０重量％以上である。前記他の樹脂としては、ポリエチレン系樹脂、ポリプロピレン系樹脂、ポリスチレン系樹脂、ポリエステル系樹脂、アクリル系樹脂、ビニル系樹脂、ポリ乳酸系樹脂以外の脂肪族ポリエステル系樹脂が挙げられるが、フラワーアレンジメント用台座として用いる場合は花卉とともに廃棄する場合のことを考慮し、生分解性素材との組み合わせが好ましい。   As long as the effects of the present invention are not impaired, other resins may be added to the aliphatic polyester resin. In that case, it is preferable that 50 weight% or more of aliphatic polyester-type resin is contained, More preferably, it is 70 weight% or more, More preferably, it is 90 weight% or more. Examples of the other resins include polyethylene resins, polypropylene resins, polystyrene resins, polyester resins, acrylic resins, vinyl resins, and aliphatic polyester resins other than polylactic acid resins. When used as a pedestal, a combination with a biodegradable material is preferable in consideration of the case of discarding together with the groom.

セルロース、およびセルロース誘導体は、生分解性や親水性を大きく損なわない限り特に限定されないが、具体的には、セルロース、アセチルセルロース、キチン、キトサン等やそれらの誘導体が挙げられ、これらを１種または２種以上混合して用いることができる。それらは単離・精製されたものである必要はなく、例えば、古紙裁断・解繊品や蝦・蟹殻の破砕品、コットンリンター、ケナフ、麦わら・ふすま、籾殻などのバイオマスであっても良い。   Cellulose and cellulose derivatives are not particularly limited as long as they do not significantly impair biodegradability and hydrophilicity, and specific examples include cellulose, acetylcellulose, chitin, chitosan and the like, and derivatives thereof. Two or more kinds can be mixed and used. They do not need to be isolated and purified, and may be biomass such as waste paper cutting / defibration products, crushed rice husks, rice husks, cotton linters, kenaf, straw, bran and rice husks.

タンパク質、および、タンパク質誘導体は、特に限定されないが、絹や羊毛、カシミヤ、アルパカなどに代表される獣毛繊維やそれらの再生品が例示でき、これらを１種または２種以上混合して用いることができる。   Proteins and protein derivatives are not particularly limited, and examples thereof include animal fibers such as silk, wool, cashmere, and alpaca, and regenerated products thereof, and these may be used alone or in combination of two or more. Can do.

これら難水溶性生分解性材料は、成形体１００重量部中、４０重量部以上９０重量部以下であることが好ましく、５０重量部以上８０重量部以下であることがより好ましい。ただし、前記成形体重量は、水分を含まない乾燥重量である。   These hardly water-soluble biodegradable materials are preferably 40 to 90 parts by weight, more preferably 50 to 80 parts by weight, in 100 parts by weight of the molded body. However, the weight of the compact is a dry weight not including moisture.

本発明の水性ゲルを構成しうる生分解性材料は水溶液が冷却、イオン架橋、ｐＨ変化、化学反応などによってゲル状になる生分解性材料をいい、具体的には、水溶性多糖類、ゼラチン、ゼラチン誘導体などが挙げられる。これらの１以上を好適に使用することが出来る。中でも、水溶性多糖類から選ばれる１以上を主たる成分とするものが比較的安価に入手でき、ゲル化も容易であるため好ましい。ここでいう、主たる成分とは５０重量％を占めることをいう。   The biodegradable material that can constitute the aqueous gel of the present invention refers to a biodegradable material in which an aqueous solution becomes a gel by cooling, ionic crosslinking, pH change, chemical reaction, and the like. Specifically, a water-soluble polysaccharide, gelatin And gelatin derivatives. One or more of these can be preferably used. Among these, those containing at least one selected from water-soluble polysaccharides as main components are preferable because they are available at relatively low cost and gelation is easy. As used herein, the main component means 50% by weight.

水溶性多糖類は何らかの要因によってゲル化させることが可能なものであれば特に限定されないが、単独または他の水溶性多糖類との混合水溶液を冷却したり、特定のカチオンと接触させるたり、ｐＨ変化を変化させたりした場合にゲル化するものが好ましく用いられる。具体的には、アガロース（寒天）、κ−カラギーナン、アルギン酸とその塩、ジェランガム、グルコマンナン（こんにゃくマンナン）、カードランやこれらの誘導体が挙げられ、これらを単独または混合して用いることができる。   The water-soluble polysaccharide is not particularly limited as long as it can be gelled for some reason, but it can cool an aqueous solution alone or mixed with another water-soluble polysaccharide, contact with a specific cation, pH Those that gel when the change is changed are preferably used. Specific examples include agarose (agar), κ-carrageenan, alginic acid and salts thereof, gellan gum, glucomannan (konjac mannan), curdlan and derivatives thereof, and these can be used alone or in combination.

ゼラチン、およびゼラチン誘導体とは、コラーゲン等を出発物質として得られるゼラチンあるいは化学的に変性したゼラチン誘導体のうち、加温溶解した水溶液を冷却あるいは冷却と同時にｐＨを調整することなどによってゲル化するものをいうが、入手のしやすさ、取扱の容易さなどからゼラチンが好ましく用いられる。   Gelatin and gelatin derivatives are gelatin or chemically modified gelatin derivatives obtained by using collagen or the like as a starting material, and gelled by adjusting the pH at the same time as cooling or cooling an aqueous solution dissolved by heating. However, gelatin is preferably used because of its availability and ease of handling.

これらの水性ゲルを構成しうる生分解性材料には、ゲル化性能を損なわない範囲で他の水溶性成分を混合してゲルの特性や強度を改善することができる。他の水溶性成分としては特に限定されないが、ローカストビーンガム、グアーガム、キサンタンガム、アラビアガム、ウェランガム、イヌリン、デキストラン、プルラン、デンプン、およびそれらの誘導体等、を用いることができる。   The biodegradable material that can constitute these aqueous gels can be mixed with other water-soluble components within a range that does not impair the gelling performance, thereby improving the properties and strength of the gel. Although it does not specifically limit as another water-soluble component, Locust bean gum, guar gum, xanthan gum, gum arabic, welan gum, inulin, dextran, pullulan, starch, derivatives thereof, etc. can be used.

これら水性ゲルを構成しうる生分解性材料は、成形体１００重量部中、１０重量部以上６０重量部以下であることが好ましく、２０重量部以上５０重量部以下であることがより好ましい。ただし、前記成形体、および、水性ゲルを構成しうる生分解性材料の重量は、水分を含まない乾燥重量である。   The biodegradable material that can constitute these aqueous gels is preferably 10 to 60 parts by weight, more preferably 20 to 50 parts by weight, in 100 parts by weight of the molded body. However, the weight of the molded body and the biodegradable material that can constitute the aqueous gel is a dry weight that does not contain moisture.

本発明の成形体は、難水溶性生分解材料を、水性ゲルを構成しうる生分解性材料をバインダーとして固化してなる。具体的には、水性ゲルを構成しうる生分解性材料を水に溶かした後、難水溶性生分解性材料を分散させ、系全体をゲル化条件（温度調整、ｐＨ調整あるいは金属塩の添加攪拌など）に調整し、系全体をゲル化させた後、ゲルが採用介しない条件で乾燥させる。   The molded article of the present invention is obtained by solidifying a hardly water-soluble biodegradable material with a biodegradable material that can constitute an aqueous gel as a binder. Specifically, after dissolving the biodegradable material that can constitute the aqueous gel in water, the slightly water-soluble biodegradable material is dispersed, and the entire system is gelled (temperature adjustment, pH adjustment, or addition of metal salt) Stirring) and the like, and the entire system is gelled, and then dried under conditions where no gel is employed.

このようにして得られた本発明の成形体は、吸水・保水性能に優れているため、例えばフラワーアレンジメント用台座として好適に使用することが出来る。   The molded article of the present invention thus obtained is excellent in water absorption and water retention performance, and can be suitably used, for example, as a pedestal for flower arrangement.

以下に実施例を示し、本発明をより具体的に説明するが、本発明はこれらの実施例に何ら限定されるものではない。   EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not limited to these examples.

（吸水性の評価）
吸水性の評価は成形体から１辺３ｃｍの立方体を切り出し、大過剰のエタノール中で液中乾燥した後、２５℃、０．１Ｔｏｒｒ以下の条件にて２４時間減圧乾燥させたものを試料とし、２５℃水中に浸漬して３分後に取り出して余分な水分を濾紙でふき取った後、秤量して浸漬前後の重量差を吸水量とし、浸漬前の成形体の重量に対する割合を求めた。 (Evaluation of water absorption)
Evaluation of water absorption was made by cutting a cube with a side of 3 cm from the molded body, drying in liquid in a large excess of ethanol, and then drying under reduced pressure for 24 hours under conditions of 25 ° C. and 0.1 Torr or less. After 3 minutes of immersion in water at 25 ° C., the excess water was wiped off with filter paper and weighed, and the weight difference before and after immersion was taken as the amount of water absorption to determine the ratio to the weight of the molded body before immersion.

（フラワーアレンジメント用台座としての評価）
フラワーアレンジメントの講師５名をパネラーとし、茎の直径３〜４ｍｍのガーベラを用いて評価した。評価項目としては、花挿し性、花の保持性、花もち（枯れない；保水性）を挙げ、以下に記載する評価基準で評価し、最大評価最小評価各々一人を除いた３名の平均を求めた。花もちについては通常のフラワーアレンジメント用台座は３日後に加水するため、３日後加水前の花の状態で評価した。
評価基準：市販品（スミザーズ・オアシス社製）を３として、１：かなり劣る、２、やや劣る、４：やや優れる、５：かなり優れる (Evaluation as a pedestal for flower arrangement)
Evaluation was made using five garbera stalks with a diameter of 3 to 4 mm, using five flower arrangement teachers as panelists. Evaluation items include flower insertion, flower retention, flower motility (does not wither; water retention), evaluated according to the evaluation criteria described below, and the average of three persons excluding one person each for maximum evaluation and minimum evaluation. Asked. As for the flower mochi, since a normal flower arrangement pedestal hydrates after 3 days, it was evaluated after 3 days in the state of flowers before hydration.
Evaluation criteria: Commercially available product (manufactured by Smithers Oasis Co., Ltd.) is set to 3, 1: considerably inferior, 2, slightly inferior, 4: slightly superior, 5: considerably excellent

（実施例１）
ポリ乳酸発泡成形体（株式会社カネカ製 カネパールＰＬＡフォーム（登録商標）・３７倍発泡）を破砕し、目開き２ｍｍのふるいを通した粉末５ｇを１００ｍｌビーカーに入れ、６０℃に調整した５％アガロース水溶液を５０ｍｌ添加・攪拌混合した後、静置・冷却して成形体１を得た。 Example 1
5% agarose adjusted to 60 ° C by pulverizing polylactic acid foamed molded product (Kanepal PLA foam (registered trademark), 37 times foamed by Kaneka Corp.) After adding 50 ml of the aqueous solution and mixing with stirring, the molded product 1 was obtained by standing and cooling.

吸水性評価には、この成形体から所定サイズの試料を切出して大過剰のエタノール中で液中乾燥した後、２５℃、０．１Ｔｏｒｒ以下で２４時間乾燥したものを用いた。   For water absorption evaluation, a sample of a predetermined size was cut out from this molded body, dried in liquid in a large excess of ethanol, and then dried for 24 hours at 25 ° C. and 0.1 Torr or less.

（実施例２）
綿状の再生古紙粉末（ネオファイバー、王子製袋株式会社製）５ｇを１００ｍｌビーカーに入れ、６０℃に調整した５％κ−カラギーナン水溶液を５０ｍｌ添加・攪拌・混合した後、５％塩化カリウム溶液を数滴加えて攪拌後冷却して成形体２を得た。吸水性評価は実施例１と同様にして調整したサンプルを用いた。 (Example 2)
Put 5g of cotton-like recycled waste paper powder (Neofiber, Oji Bags Co., Ltd.) in a 100ml beaker, add 50ml of 5% κ-carrageenan aqueous solution adjusted to 60 ° C, stir and mix, then 5% potassium chloride solution A few drops of were added, and the mixture was stirred and cooled to obtain a molded body 2. For water absorption evaluation, a sample prepared in the same manner as in Example 1 was used.

（実施例３）
ポリ乳酸発泡成形体（株式会社カネカ製 カネパールＰＬＡフォーム（登録商標）・３７倍発泡）を８５℃、９５％ＲＨの環境下で４８時間処理したものを破砕し、目開き０．５ｍｍのふるいを通した鱗片状の粉末５ｇを用いた以外は実施例１と同様にして成形体３を得た。 (Example 3)
Polylactic acid foamed molding (Kaneka Corp. Kanepal PLA Foam (registered trademark), 37 times foaming) treated for 48 hours in an environment of 85 ° C and 95% RH is crushed and sieved with a 0.5mm mesh A molded body 3 was obtained in the same manner as in Example 1 except that 5 g of the passed scaly powder was used.

（実施例４）
ポリ乳酸繊維（５０フィラメント／４０ｄＴｅｘ；太さ１．３μｍの単繊維を４０本束ねたもの）の撚糸を６ｍｍ長にカットしたもの５ｇを用いた以外は実施例１と同様にして成形体４を得た。 Example 4
A molded body 4 was prepared in the same manner as in Example 1 except that 5 g of a twisted yarn of polylactic acid fibers (50 filaments / 40 dTex; 40 bundles of 1.3 μm thick single fibers) was cut into a length of 6 mm was used. Obtained.

（実施例５）
精錬した家蚕絹繊維（平均太さ１５μｍ）を８ｍｍ長のカットファイバーにしたものを５ｇ用いた以外は実施例１と同様にして成形体５を得た。 (Example 5)
A molded body 5 was obtained in the same manner as in Example 1 except that 5 g of refined rabbit silk fiber (average thickness: 15 μm) was cut into an 8 mm long cut fiber.

（実施例６）
羊毛（メリノ種、平均太さ２０μｍ、平均繊維長７２ｍｍ）を３ｍｍ長のカットファイバーにしたものを５ｇ用いた以外は実施例１と同様にして成形体６を得た。 (Example 6)
A molded body 6 was obtained in the same manner as in Example 1, except that 5 g of wool (merino species, average thickness 20 μm, average fiber length 72 mm) cut into a 3 mm long cut fiber was used.

（実施例７）
綿状の再生古紙粉末（ネオファイバー、王子製袋株式会社製）５ｇ、κ−カラギーナン４．５ｇ、ローカストビーンガム０．５ｇに水５０ｍｌを加えて加熱溶解した後、５％塩化カリウム溶液を数滴加えて静置し、冷却・固化させて成形体７を得た。吸水性評価にはこの成形体から所定サイズの試料を切出してエタノール中で液中乾燥した後、常温、０．１Ｔｏｒｒ以下で２４時間乾燥したものを用いた。 (Example 7)
After adding 50 ml of water to 5 g of cotton-like recycled paper powder (Neofiber, Oji Bags Co., Ltd.), 4.5 g of κ-carrageenan and 0.5 g of locust bean gum, heat-dissolve and add 5% potassium chloride solution. Drops were added and allowed to stand, cooled and solidified to obtain a molded body 7. For water absorption evaluation, a sample of a predetermined size was cut out from the molded body, dried in liquid in ethanol, and then dried at room temperature and 0.1 Torr or lower for 24 hours.

（比較例１）
ポリ乳酸発泡成形体（株式会社カネカ製 カネパールＰＬＡフォーム（登録商標）・３７倍発泡）をそのまま成形体８とした。 (Comparative Example 1)
A polylactic acid foam molded product (Kanepal PLA Foam (registered trademark), 37 times foamed product manufactured by Kaneka Corporation) was used as the molded product 8 as it was.

（比較例２）
ポリ乳酸発泡成形体（株式会社カネカ製 カネパールＰＬＡフォーム（登録商標）・３７倍発泡）を破砕し、目開き８ｍｍ（対角１１ｍｍ強）のふるいを通した粉末５ｇを用いた以外は実施例１と同様にして成形体９を得た。 (Comparative Example 2)
Example 1 except that a polylactic acid foamed molded product (Kaneka PLANE (registered trademark), 37 times foamed by Kaneka Corporation) was crushed and 5 g of powder passed through a sieve having an opening of 8 mm (diagonal 11 mm or more) was used. In the same manner as above, a molded body 9 was obtained.

（比較例３）
実施例４で用いたポリ乳酸繊維を５１ｍｍにカットしたものを用いた以外は実施例４と同様にして、成形体１０を得た。 (Comparative Example 3)
A molded body 10 was obtained in the same manner as in Example 4 except that the polylactic acid fiber used in Example 4 was cut to 51 mm.

（比較例４）
実施例５で用いた精錬した家蚕絹繊維のカット長を１５ｍｍにしたものを用いた以外は実施例５と同様にして成形体１１を得た。 (Comparative Example 4)
A molded body 11 was obtained in the same manner as in Example 5 except that the refined rabbit silk fiber used in Example 5 had a cut length of 15 mm.

（比較例５）
実施例６で用いた羊毛をそのまま５ｇ用いた以外は実施例６と同様にして成形体１２を得た。 (Comparative Example 5)
A molded body 12 was obtained in the same manner as in Example 6 except that 5 g of the wool used in Example 6 was used as it was.

得られた成形物の評価結果を表１に示す。   Table 1 shows the evaluation results of the obtained molded product.

Claims (6)

不定形の粉末、鱗片状の粉末、長さ１０ｍｍ以下のチョップドストランド、長さ１０ｍｍ以下の綿状の繊維からなる群から選ばれる何れか１以上の形状である難水溶性生分解性材料を、水性ゲルを構成しうる生分解性材料をバインダーとして固化してなる成形体。   A hardly water-soluble biodegradable material having one or more shapes selected from the group consisting of amorphous powder, scaly powder, chopped strands having a length of 10 mm or less, and cotton-like fibers having a length of 10 mm or less, A molded product obtained by solidifying a biodegradable material that can constitute an aqueous gel as a binder. 難水溶性生分解性材料が、脂肪族ポリエステル系樹脂、セルロース、セルロース誘導体、タンパク質、タンパク質誘導体からなる群から選ばれる１以上を含んでなる請求項１記載の成形体。   The molded article according to claim 1, wherein the hardly water-soluble biodegradable material comprises one or more selected from the group consisting of aliphatic polyester resins, cellulose, cellulose derivatives, proteins, and protein derivatives. 難水溶性生分解性材料が、脂肪族ポリエステル系樹脂である請求項２記載の成形体。   The molded article according to claim 2, wherein the hardly water-soluble biodegradable material is an aliphatic polyester resin. 脂肪族ポリエステル系樹脂が、ポリ乳酸系樹脂である請求項３に記載の成形体。   The molded article according to claim 3, wherein the aliphatic polyester resin is a polylactic acid resin. 水性ゲルを構成しうる生分解性材料が、水溶性多糖類、ゼラチン、ゼラチン誘導体から選ばれる１以上を主たる成分とする請求項１〜４何れか一項に記載の成形体。   The molded article according to any one of claims 1 to 4, wherein the biodegradable material that can constitute the aqueous gel contains, as a main component, one or more selected from water-soluble polysaccharides, gelatin, and gelatin derivatives. 請求項１〜５何れか一項に記載の成形体からなるフラワーアレンジメント用台座。   A pedestal for flower arrangement comprising the molded article according to any one of claims 1 to 5.