JP2010280073A - Moisture-permeable waterproof fabric and fiber product - Google Patents
Moisture-permeable waterproof fabric and fiber product Download PDFInfo
- Publication number
- JP2010280073A JP2010280073A JP2009132993A JP2009132993A JP2010280073A JP 2010280073 A JP2010280073 A JP 2010280073A JP 2009132993 A JP2009132993 A JP 2009132993A JP 2009132993 A JP2009132993 A JP 2009132993A JP 2010280073 A JP2010280073 A JP 2010280073A
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- moisture
- permeable
- waterproof
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、蓄熱性に優れた透湿防水性布帛および該透湿防水性布帛を用いてなる繊維製品に関する。 The present invention relates to a moisture-permeable and waterproof fabric excellent in heat storage and a fiber product using the moisture-permeable and waterproof fabric.
従来、スポーツ衣料やユニフォーム衣料などに使用されている透湿防水性布帛において、透湿性および防水性を備えた樹脂製の薄膜が広く使用されている。例えば、織編物などの基布に、多孔質または無孔質ポリウレタンをコーティングしたものや、ポリウレタンなどの多孔質または無孔質樹脂製フィルムを接着剤により基布にラミネーションしたものなどがある。多孔質樹脂製薄膜はその孔の大きさにより、また、無孔質樹脂製薄膜の場合は孔が無いものの吸湿性物質を含有することで親水性となり、雨やその他の水を通さず、湿気（水蒸気）を通すことにより透湿防水性を呈している。 Conventionally, in a moisture-permeable and waterproof fabric used for sports clothing, uniform clothing, and the like, a resin thin film having moisture permeability and waterproof properties has been widely used. For example, a base fabric such as woven or knitted fabric is coated with porous or nonporous polyurethane, or a porous or nonporous resin film such as polyurethane is laminated on the base fabric with an adhesive. Porous resin thin films are hydrophilic due to the size of their pores, and nonporous resin thin films do not have pores but contain moisture-absorbing substances. Moisture permeable and waterproof properties are exhibited by passing (water vapor).
他方、透湿防水性布帛を用いた衣料は、雨天時など比較的寒い環境下で使用されることが多いため、蓄熱性を向上させたり、布帛に付着した水滴を速やかに蒸発させることが望まれていた。 On the other hand, clothing using a moisture-permeable and waterproof fabric is often used in a relatively cold environment such as rainy weather, so it is desirable to improve heat storage and to quickly evaporate water droplets adhering to the fabric. It was rare.
本発明は上記の背景に鑑みなされたものであり、その目的は蓄熱性に優れた透湿防水性布帛および該透湿防水性布帛を用いてなる繊維製品を提供することにある。 The present invention has been made in view of the above background, and an object thereof is to provide a moisture-permeable waterproof fabric excellent in heat storage and a fiber product using the moisture-permeable waterproof fabric.
本発明者は、基布の片面に透湿防水層が積層された透湿防水性布帛において、赤外線吸収剤を含む布帛を透湿防水層の上に積層することにより、蓄熱性に優れた透湿防水性布帛が得られることを見出し、さらに鋭意検討を重ねることにより本発明を完成するに至った。 The present inventor, in a moisture permeable waterproof fabric in which a moisture permeable waterproof layer is laminated on one side of a base fabric, laminates a fabric containing an infrared absorbent on the moisture permeable waterproof layer, thereby achieving excellent permeability in heat storage. The inventors have found that a wet waterproof fabric can be obtained, and have made further studies, and have completed the present invention.
かくして、本発明によれば「基布の片面に透湿防水層が積層され、該透湿防水層の基布とは反対側面上に、赤外線吸収剤を含む布帛Ａが積層されてなることを特徴とする透湿防水性布帛。」が提供される。 Thus, according to the present invention, “a moisture permeable waterproof layer is laminated on one side of the base fabric, and a fabric A containing an infrared absorber is laminated on the side opposite to the base fabric of the moisture permeable waterproof layer. A moisture permeable waterproof fabric is provided. "
その際、前記赤外線吸収剤がカーボンブラックであることが好ましい。また、前記赤外線吸収剤がポリエステル繊維に練り込まれており、布帛Ａが該ポリエステル繊維を含むことが好ましい。また、前記布帛Ａが、編密度が３０〜１５０コース／２．５４ｃｍかつ２０〜１３０ウエール／２．５４ｃｍの編物であることが好ましい。また、前記布帛Ａが、下記式により定義されるカバーファクターＣＦが３００〜３５００の織物であることが好ましい。
ＣＦ＝（ＤＷｐ／１．１）１／２×ＭＷｐ＋（ＤＷｆ／１．１）１／２×ＭＷｆ
［ＤＷｐは経糸総繊度（ｄｔｅｘ）、ＭＷｐは経糸織密度（本／２．５４ｃｍ）、ＤＷｆは緯糸総繊度（ｄｔｅｘ）、ＭＷｆは緯糸織密度（本／２．５４ｃｍ）である。］
In that case, it is preferable that the said infrared absorber is carbon black. Moreover, it is preferable that the said infrared absorber is kneaded in the polyester fiber and the fabric A contains this polyester fiber. The fabric A is preferably a knitted fabric having a knitting density of 30 to 150 courses / 2.54 cm and 20 to 130 wales / 2.54 cm. Further, the fabric A is preferably a woven fabric having a cover factor CF defined by the following formula of 300 to 3500.
CF = (DWp / 1.1) 1/2 × MWp + (DWf / 1.1) 1/2 × MWf
[DWp is the total warp fineness (dtex), MWp is the warp weave density (main / 2.54 cm), DWf is the total weft fineness (dtex), and MWf is the weft weave density (main / 2.54 cm). ]
本発明の透湿防水性布帛において、前記基布が織物組織または編物組織を有することが好ましい。また、前記基布がポリエステル繊維で構成されることが好ましい。また、前記基布に撥水加工が施されていることが好ましい。また、前記透湿防水層が、厚さ２〜３０μｍの透湿防水性ポリエステル膜であることが好ましい。 In the moisture-permeable and waterproof fabric of the present invention, it is preferable that the base fabric has a woven fabric or a knitted fabric. Moreover, it is preferable that the said base fabric is comprised with a polyester fiber. Moreover, it is preferable that the said base fabric is water-repellent. The moisture-permeable and waterproof layer is preferably a moisture-permeable and waterproof polyester film having a thickness of 2 to 30 μm.
また、本発明によれば、前記の透湿防水性布帛を用いてなる、スポーツウェア、アウトドアウェア、レインコート、紳士衣服、婦人衣服、作業衣、防護服、人工皮革、履物、鞄、カーテン、テント、寝袋、防水シート、およびカーシートの群より選ばれるいずれかの繊維製品が提供される。 Further, according to the present invention, sportswear, outdoor wear, raincoat, men's clothing, women's clothing, work clothing, protective clothing, artificial leather, footwear, heels, curtains, comprising the moisture permeable and waterproof fabric described above, Any textile product selected from the group of tents, sleeping bags, tarpaulins, and car seats is provided.
本発明によれば、蓄熱性に優れた透湿防水性布帛および該透湿防水性布帛を用いてなる繊維製品が得られる。かかる透湿防水性布帛および該透湿防水性布帛を用いてなる繊維製品によれば、透湿防水性が得られるだけでなく、布帛の蓄熱性を向上させたり、布帛に付着した水滴を速やかに蒸発させることが可能となる。 ADVANTAGE OF THE INVENTION According to this invention, the moisture-permeable waterproof fabric excellent in heat storage property and the textiles using this moisture-permeable waterproof fabric are obtained. According to such a moisture permeable waterproof fabric and a fiber product using the moisture permeable waterproof fabric, not only moisture permeable and waterproof properties can be obtained, but also the heat storage property of the fabric can be improved, or water droplets attached to the fabric can be quickly removed. Can be evaporated.
本発明の透湿防水性布帛において、基布の片面に透湿防水層が積層され、さらにその上に、赤外線吸収剤を含む布帛Ａが積層されている。すなわち、基布の片面に、透湿防水層および布帛Ａがこの順で積層されている。 In the moisture-permeable and waterproof fabric of the present invention, a moisture-permeable and waterproof layer is laminated on one side of the base fabric, and a fabric A containing an infrared absorber is further laminated thereon. That is, the moisture permeable waterproof layer and the fabric A are laminated in this order on one surface of the base fabric.
ここで、前記赤外線吸収剤としては、波長７００〜２０００ｎｍの赤外線領域で１０％以上の吸収率を有する物質であれば特に限定されず、金属酸化物系微粒子、カーボンブラック、有機化合物の赤外線吸収色素などが例示される。特に、優れた赤外線吸収性能を得る上でカーボンブラックが好ましい。 Here, the infrared absorber is not particularly limited as long as it is a substance having an absorptance of 10% or more in an infrared region having a wavelength of 700 to 2000 nm. Etc. are exemplified. In particular, carbon black is preferable for obtaining excellent infrared absorption performance.
前記布帛Ａにおいて、赤外線吸収剤は後加工により付与されていてもよいが、洗濯耐久性の点で、布帛を構成する繊維に練り込まれていることが好ましい。その際、赤外線吸収剤の含有量としては繊維重量に対して０．３重量％以上（より好ましくは０．３〜３．０重量％）であることが好ましい。 In the fabric A, the infrared absorber may be applied by post-processing, but is preferably kneaded into the fibers constituting the fabric from the viewpoint of washing durability. At that time, the content of the infrared absorber is preferably 0.3% by weight or more (more preferably 0.3 to 3.0% by weight) with respect to the fiber weight.
その際、該繊維を構成するポリマーとしては、赤外線吸収剤を練り込むことが可能なポリマーであれば特に限定されず、ポリエステル、ポリアミド、ポリオレフィン、ポリ乳酸、ステレオコンプレックスポリ乳酸などの通常の繊維形成性ポリマーなどでよい。なかでも、ポリエチレンテレフタレートやポリトリメチレンテレフタレート、ポリブチレンテレフタレート、ポリ乳酸、ステレオコンプレックスポリ乳酸、第３成分を共重合させたポリエステルなどが好ましく例示される。かかるポリエステルとしては、マテリアルリサイクルまたはケミカルリサイクルされたポリエステルであってもよい。さらには、特開２００４−２７００９７号公報や特開２００４−２１１２６８号公報に記載されているような、特定のリン化合物およびチタン化合物を含む触媒を用いて得られたポリエステルでもよい。該ポリマー中には、本発明の目的を損なわない範囲内で必要に応じて、微細孔形成剤、カチオン染料可染剤、着色防止剤、熱安定剤、蛍光増白剤、艶消し剤、着色剤、吸湿剤、無機微粒子が１種または２種以上含まれていてもよい。 At that time, the polymer constituting the fiber is not particularly limited as long as it is a polymer capable of kneading an infrared absorber, and normal fiber formation such as polyester, polyamide, polyolefin, polylactic acid, and stereocomplex polylactic acid is used. May be a functional polymer. Of these, polyethylene terephthalate, polytrimethylene terephthalate, polybutylene terephthalate, polylactic acid, stereocomplex polylactic acid, polyester obtained by copolymerizing the third component, and the like are preferably exemplified. Such polyester may be material recycled or chemically recycled polyester. Furthermore, the polyester obtained using the catalyst containing the specific phosphorus compound and titanium compound which are described in Unexamined-Japanese-Patent No. 2004-270097 and 2004-2111268 may be sufficient. In the polymer, a fine pore forming agent, a cationic dye dyeing agent, an anti-coloring agent, a heat stabilizer, a fluorescent whitening agent, a matting agent, a coloring agent may be added as necessary within the range not impairing the object of the present invention. 1 type (s) or 2 or more types of an agent, a hygroscopic agent, and inorganic fine particles may be contained.
布帛Ａは、赤外線吸収剤を繊維中に練り込んだ赤外線吸収性繊維のみで構成されることが好ましいが、布帛Ａの重量に対して８０重量％以下であれば他の繊維が含まれていてもよい。 The fabric A is preferably composed only of infrared absorbing fibers in which an infrared absorbent is kneaded into the fibers, but other fibers are included as long as it is 80% by weight or less based on the weight of the fabric A. Also good.
布帛Ａの布帛組織は特に限定されず織物、編物、不織布などいずれでもよい。なかでも、摩耗耐久性の点で織物または編物が好ましい。特に蓄熱性を高める上で、前記布帛Ａが、編密度が３０〜１５０コース／２．５４ｃｍかつ２０〜１３０ウエール／２．５４ｃｍの編物であるか、下記式により定義されるカバーファクターＣＦが３００〜３５００（より好ましくは３００〜１０００）の織物であることが好ましい。
ＣＦ＝（ＤＷｐ／１．１）１／２×ＭＷｐ＋（ＤＷｆ／１．１）１／２×ＭＷｆ
［ＤＷｐは経糸総繊度（ｄｔｅｘ）、ＭＷｐは経糸織密度（本／２．５４ｃｍ）、ＤＷｆは緯糸総繊度（ｄｔｅｘ）、ＭＷｆは緯糸織密度（本／２．５４ｃｍ）である。］
The fabric structure of the fabric A is not particularly limited, and may be any one of woven fabric, knitted fabric, non-woven fabric and the like. Of these, a woven fabric or a knitted fabric is preferable in terms of wear durability. In particular, in order to enhance the heat storage property, the fabric A is a knitted fabric having a knitting density of 30 to 150 courses / 2.54 cm and 20 to 130 wales / 2.54 cm, or a cover factor CF defined by the following formula is 300. A woven fabric of ˜3500 (more preferably 300 to 1000) is preferable.
CF = (DWp / 1.1) 1/2 × MWp + (DWf / 1.1) 1/2 × MWf
[DWp is the total warp fineness (dtex), MWp is the warp weave density (main / 2.54 cm), DWf is the total weft fineness (dtex), and MWf is the weft weave density (main / 2.54 cm). ]
ここで、織物組織および編物組織としては特に限定されないが、よこ編組織としては、平編、ゴム編、両面編、パール編、タック編、浮き編、片畔編、レース編、添え毛編等が例示され、たて編組織としては、シングルデンビー編、シングルアトラス編、ダブルコード編、ハーフ編、ハーフベース編、サテン編、ハーフトリコット編、裏毛編、ジャガード編等などが例示され、織物組織としては、平織、綾織、朱子織等の三原組織、変化組織、たて二重織、よこ二重織等の片二重組織、たてビロードなどが例示されるがこれらに限定されない。層数も単層でもよいし、２層以上の多層でもよい。
また、布帛Ａの目付としては、軽量性の点で３０ｇｒ／ｍ２以下（より好ましくは２〜３０ｇｒ／ｍ２）であることが好ましい。
Here, the woven structure and the knitted structure are not particularly limited, but the weft knitted structure includes a flat knitted fabric, a rubber knitted fabric, a double-sided knitted fabric, a pearl knitted fabric, a tucked knitted fabric, a floating knitted fabric, a single knitted knitted fabric, a lace knitted fabric, a spliced knitted fabric, etc. Examples of the warp knitting structure include single denby knitting, single atlas knitting, double cord knitting, half knitting, half base knitting, satin knitting, half tricot knitting, fleece knitting, jacquard knitting, etc. Examples of the structure include, but are not limited to, a three-layer structure such as plain weave, twill weave, and satin weave, a change structure, a single double structure such as a vertical double weave and a horizontal double weave, and a vertical velvet. The number of layers may be a single layer or a multilayer of two or more layers.
Further, the basis weight of the fabric A is preferably 30 gr / m 2 or less (more preferably 2 to 30 gr / m 2 ) in terms of lightness.
本発明の透湿防水性布帛において、基布を構成する繊維は特に限定されず、ポリエステル繊維、アセテート繊維、ポリアミド繊維、アラミド繊維、炭素繊維、綿や羊毛などの天然繊維などいずれでもよい。なかでも、ポリエチレンテレフタレートやポリトリメチレンテレフタレート、ポリブチレンテレフタレート、ポリ乳酸、ステレオコンプレックスポリ乳酸、第３成分を共重合させたポリエステルなどからなるポリエステル繊維が５０重量％以上（特に好ましくは１００重量％）基布に含まれることがリサイクル性の点で好ましい。なお、かかるポリエステルとしては、マテリアルリサイクルまたはケミカルリサイクルされたポリエステルであってもよい。さらには、特開２００４−２７００９７号公報や特開２００４−２１１２６８号公報に記載されているような、特定のリン化合物およびチタン化合物を含む触媒を用いて得られたポリエステルでもよい。該ポリマー中には、本発明の目的を損なわない範囲内で必要に応じて、微細孔形成剤、カチオン染料可染剤、着色防止剤、熱安定剤、蛍光増白剤、艶消し剤、着色剤、吸湿剤、無機微粒子が１種または２種以上含まれていてもよい。 In the moisture permeable waterproof fabric of the present invention, the fibers constituting the base fabric are not particularly limited, and may be any of polyester fibers, acetate fibers, polyamide fibers, aramid fibers, carbon fibers, natural fibers such as cotton and wool. Among these, 50% or more (particularly preferably 100% by weight) of polyester fiber made of polyethylene terephthalate, polytrimethylene terephthalate, polybutylene terephthalate, polylactic acid, stereocomplex polylactic acid, polyester copolymerized with the third component, or the like. It is preferable that it is contained in the base fabric from the viewpoint of recyclability. The polyester may be material recycled or chemically recycled polyester. Furthermore, the polyester obtained using the catalyst containing the specific phosphorus compound and titanium compound which are described in Unexamined-Japanese-Patent No. 2004-270097 and 2004-2111268 may be sufficient. In the polymer, a fine pore forming agent, a cationic dye dyeing agent, an anti-coloring agent, a heat stabilizer, a fluorescent whitening agent, a matting agent, a coloring agent may be added as necessary within the range not impairing the object of the present invention. 1 type (s) or 2 or more types of an agent, a hygroscopic agent, and inorganic fine particles may be contained.
前記基布を構成する繊維形態は特に限定されないが、透湿防水層との接着性の点で長繊維（マルチフィラメント糸）であることが好ましい。単繊維の断面形状も特に限定されず、丸、三角、扁平、中空など公知の断面形状でよい。また、通常の空気加工、仮撚捲縮加工が施されていてもさしつかえない。単糸繊維繊度、総繊度、フィラメント数は特に限定されないが、ソフトな風合いを得る上で、それぞれ単糸繊維繊度０．１〜２．０ｄｔｅｘ、総繊度３０〜２００ｄｔｅｘ、フィラメント数３０〜２００本の範囲内であることが好ましい。 Although the fiber form which comprises the said base fabric is not specifically limited, It is preferable that it is a long fiber (multifilament yarn) at the point of adhesiveness with a moisture-permeable waterproof layer. The cross-sectional shape of the single fiber is not particularly limited, and may be a known cross-sectional shape such as a circle, a triangle, a flat shape, or a hollow shape. In addition, normal air processing and false twist crimping may be applied. The single yarn fiber fineness, the total fineness, and the number of filaments are not particularly limited, but for obtaining a soft texture, the single yarn fiber fineness is 0.1 to 2.0 dtex, the total fineness is 30 to 200 dtex, and the number of filaments is 30 to 200. It is preferable to be within the range.
前記基布の布帛組織は特に限定されず織物、編物、不織布などいずれでもよい。なかでも、引裂き強力の強さの点で織物または編物が好ましい。特に織物が好ましい。織物組織としては、平織、綾織、朱子織等の三原組織、変化組織、たて二重織、よこ二重織等の片二重組織、たてビロードなどが例示されるがこれらに限定されない。層数は単層でもよいし、２層以上の多層でもよい。前記基布の目付けとしては、３０〜９００ｇ／ｍ２（より好ましくは４０〜７００ｇ／ｍ２）の範囲内であることが好ましい。 The fabric structure of the base fabric is not particularly limited, and may be any of woven fabric, knitted fabric, non-woven fabric and the like. Of these, a woven fabric or a knitted fabric is preferable in terms of tear strength. A woven fabric is particularly preferable. Examples of the fabric structure include, but are not limited to, a three-layer structure such as plain weave, twill weave, and satin weave, a change structure, a single double structure such as a vertical double weave and a horizontal double weave, and a vertical velvet. The number of layers may be a single layer or a multilayer of two or more layers. The basis weight of the base fabric is preferably in the range of 30 to 900 g / m 2 (more preferably 40 to 700 g / m 2 ).
また、前記基布には、通常の染色加工、減量加工、起毛加工、撥水加工、蓄熱加工、吸汗加工などの後加工を適宜施しても良い。その際、染色に用いる染料は分散染料、カチオン性染料など特に限定はされないが、カチオン性染料はカチオン性染料で染色可能な繊維を選択する必要があるため、より汎用性が高い分散染料を染色に用いるほうが好適である。また、撥水加工に用いられる撥水剤としては、パラフィン系撥水剤やポリシロキサン系撥水処理剤、フッ素系撥水処理剤などの公知のものが使用でき、その処理も一般に行われているパディング法、スプレー法などの公知の方法で行えばよい。 In addition, the base fabric may be appropriately subjected to post-processing such as normal dyeing processing, weight reduction processing, raising processing, water repellent processing, heat storage processing, and sweat absorption processing. At that time, the dye used for dyeing is not particularly limited, such as a disperse dye or a cationic dye. However, it is necessary to select a fiber that can be dyed with a cationic dye. It is more suitable to use for. In addition, as the water repellent used in the water repellent processing, known ones such as a paraffin water repellent, a polysiloxane water repellent, a fluorine water repellent can be used, and the treatment is generally performed. A known method such as a padding method or a spray method may be used.
本発明の透湿防水性布帛において、基布の片面に積層される透湿防水層としては、透湿性を有するウレタン樹脂からなるフィルム、ウレタン樹脂コーティング、アクリル樹脂コーティング、ポリテトラフロロエチレン樹脂フィルム、ポリエステルフィルムなどがあげられが限定されるものではない。特に、ケミカルリサイクル処理により再度ポリエステルの原料として再生可能であり何度でもリサイクル使用できる点で省資源かつ環境保全できる点より、より好ましくは無色透明のポリエステルフィルムであるほうがよい。 In the moisture permeable waterproof fabric of the present invention, as the moisture permeable waterproof layer laminated on one side of the base fabric, a film made of urethane resin having moisture permeability, urethane resin coating, acrylic resin coating, polytetrafluoroethylene resin film, Examples include, but are not limited to, polyester films. In particular, a colorless and transparent polyester film is more preferable from the viewpoint that it can be recycled as a raw material of polyester again by chemical recycling treatment and can be reused any number of times, thus saving resources and protecting the environment.
かかるポリエステルフィルムとしては、ポリエーテル−エステル系エラストマーやＰＢＴ（ポリブチレンテレフタレート）からなるポリエステルフィルムが好適に用いられる。また、上記フィルムは透湿性を有するが、該フィルムは多孔質でもよいが、透湿性を有するポリエステルを主成分とする無孔質フィルムであることが好ましい。多孔質フィルムである場合、無色透明にはなり得ないからである。ポリエステルに透湿性を付与するには、特に限定されるものではないが、ポリエチレングリコールなどの吸湿性材料をポリエステルに共重合する方法が好適に用いられる。 As such a polyester film, a polyester film made of a polyether-ester elastomer or PBT (polybutylene terephthalate) is preferably used. Moreover, although the said film has moisture permeability, this film may be porous, but it is preferable that it is a nonporous film which has polyester which has moisture permeability as a main component. This is because a porous film cannot be colorless and transparent. To impart moisture permeability to the polyester, although not particularly limited, a method of copolymerizing a hygroscopic material such as polyethylene glycol with the polyester is preferably used.
上記ポリエーテル−エステル系エラストマーは、長鎖エステル単位および短鎖エステル単位からなり、該短鎖エステル単位は、全ポリエーテル−エステル系エラストマーの３０〜７０重量％の範囲にあることが好ましい。上記短鎖エステル単位の割合が、３０重量％未満であるポリエーテル−エステル系エラストマーは比較的低融点であって、加工性が不良であり、また、該短鎖エステル単位が、７０重量％を超えるポリエーテル−エステル系エラストマーの場合には、比較的高融点であり、加工性が不良である。 The polyether-ester elastomer is composed of a long-chain ester unit and a short-chain ester unit, and the short-chain ester unit is preferably in the range of 30 to 70% by weight of the total polyether-ester elastomer. The polyether-ester elastomer having a proportion of the short chain ester unit of less than 30% by weight has a relatively low melting point and poor processability, and the short chain ester unit accounts for 70% by weight. In the case of exceeding polyether-ester elastomer, the melting point is relatively high and the processability is poor.
前記ポリエーテル-エステル系エラストマーの酸成分は、テレフタル酸、イソフタル酸、フタル酸、ナフタレン−２，６−ジカルボン酸、ナフタレン−２，７−ジカルボン酸、ジフェニル−４，４’−ジカルボン酸、ジフェノキシエタンジカルボン酸、３−スルホイソフタル酸ナトリウムなどの芳香族ジカルボン酸、１，４−シクロヘキサンジカルボン酸などの脂環式ジカルボン酸、コハク酸、シュウ酸、アジピン酸、セバシン酸、ドデカンジ酸、ダイマー酸などの脂肪族ジカルボン酸、または、これらのエステル形成性誘導体から選ばれた少なくとも１種が挙げられるが、好ましくは、テレフタル酸、イソフタル酸、ナフタレン−２，６−ジカルボン酸、またはこれらのエステル形成性誘導体が例示される。 The acid component of the polyether-ester elastomer is terephthalic acid, isophthalic acid, phthalic acid, naphthalene-2,6-dicarboxylic acid, naphthalene-2,7-dicarboxylic acid, diphenyl-4,4′-dicarboxylic acid, diester Aromatic dicarboxylic acids such as phenoxyethanedicarboxylic acid and sodium 3-sulfoisophthalate, alicyclic dicarboxylic acids such as 1,4-cyclohexanedicarboxylic acid, succinic acid, oxalic acid, adipic acid, sebacic acid, dodecanediic acid, dimer acid And at least one selected from aliphatic dicarboxylic acids such as these or ester-forming derivatives thereof, preferably terephthalic acid, isophthalic acid, naphthalene-2,6-dicarboxylic acid, or ester formation thereof Sex derivatives are exemplified.
もちろん、このような酸成分の一部（通常は、全酸成分を基準として３０モル％以下）は、他のジカルボン酸成分やオキシカルボン酸成分で置換されていてもよい。
なお、上記ポリマー中には、各種安定剤、紫外線吸収剤などが必要に応じて配合されていてもよい。
Of course, a part of these acid components (usually 30 mol% or less based on the total acid components) may be substituted with other dicarboxylic acid components or oxycarboxylic acid components.
In addition, various stabilizers, ultraviolet absorbers, and the like may be blended in the polymer as necessary.
次に、前記ポリエーテル−エステル系エラストマーの長鎖エステル単位のグリコール成分としては、ポリエチレングリコール、ポリ１，２−プロピレングリコール、ポリ１，３−プロピレングリコール、エチレンオキシドとプロピレンオキシドとの共重合体、エチレンオキシドとテトラヒドロフランとの共重合体などのポリアルキレングリコールのうち少なくとも１種が挙げられるが、満足できる透湿性を得るためにはポリエチレングリコールが最も好ましく例示され、その平均分子量が６００〜８,０００の範囲にあるものが好ましい。上記平均分子量が６００未満であると、満足できる機械的物性が得られず、一方、該平均分子量が８,０００を超えた場合には、相分離のためにポリエーテル-エステルの調製において問題を引き起こす場合がある。 Next, as a glycol component of the long-chain ester unit of the polyether-ester elastomer, polyethylene glycol, poly 1,2-propylene glycol, poly 1,3-propylene glycol, a copolymer of ethylene oxide and propylene oxide, Although at least 1 type is mentioned among polyalkylene glycols, such as a copolymer of ethylene oxide and tetrahydrofuran, in order to obtain satisfactory moisture permeability, polyethylene glycol is most preferably exemplified, and its average molecular weight is 600 to 8,000. Those in the range are preferred. If the average molecular weight is less than 600, satisfactory mechanical properties cannot be obtained. On the other hand, if the average molecular weight exceeds 8,000, there is a problem in the preparation of the polyether-ester for phase separation. May cause.
また、ポリエーテル−エステル系エラストマーの短鎖エステル単位のグリコール成分は、エチレングリコールおよびテトラメチレングリコールからなり、該エチレングリコールおよびテトラメチレングリコール中に占めるテトラメチレングリコールのモル分率が７０モル％未満のものが好ましく使用される。上記テトラメチレングリコールが７０モル％を超えると、コート層又はフィルム層自体は柔軟となるが、布帛とのモジュラス差が大きすぎるため、耐揉み性が悪く、コート層またはフィルム層と布帛の界面に剥離が生じやすい。 The glycol component of the short-chain ester unit of the polyether-ester elastomer is composed of ethylene glycol and tetramethylene glycol, and the molar fraction of tetramethylene glycol in the ethylene glycol and tetramethylene glycol is less than 70 mol%. Those are preferably used. When the tetramethylene glycol exceeds 70 mol%, the coat layer or the film layer itself becomes flexible, but the modulus difference from the fabric is too large, so that the sag resistance is poor and the interface between the coat layer or film layer and the fabric is poor. Peeling easily occurs.
上記テトラメチレングリコールのモル分率のさらに好ましい範囲は、７０モル％未満〜５０モル％以上の範囲である。
このようなポリエーテル−エステル系エラストマーが少なくとも布帛の片側面の一部にコーティングされるか、若しくは、ポリエーテル−エステル系エラストマーからなるフィルムが少なくとも基布の片側面にラミネートされていることが好ましい。
A more preferable range of the molar fraction of the tetramethylene glycol is a range of less than 70 mol% to 50 mol% or more.
It is preferable that such a polyether-ester elastomer is coated on at least a part of one side of the fabric, or a film made of a polyether-ester elastomer is laminated on at least one side of the base fabric. .
ポリエーテル−エステル系エラストマーを布帛の片側面の一部にコーティングする方法としては、ポリエーテル−エステル系エラストマーを該エラストマーが溶解可能な溶剤で溶解した後に、該布帛表面上にコーティングし、乾式法、若しくは、湿式法により溶剤を除去することにより得られる。 As a method of coating the polyether-ester elastomer on a part of one side of the fabric, the polyether-ester elastomer is dissolved in a solvent capable of dissolving the elastomer, and then coated on the surface of the fabric, followed by a dry method. Alternatively, it can be obtained by removing the solvent by a wet method.
該ポリエーテル−エステル系エラストマーが溶解可能な溶剤としては、ジメチルホルムアミド、ジオキサン、エチレンホルマール、トルエン、クロロホルム、塩化メチレンの１種、又は、２種以上の有機溶剤が挙げらが、低沸点および毒性を考慮した場合、エチレンホルマールを使用するものが最も好ましい。 Solvents in which the polyether-ester elastomer can be dissolved include one kind of dimethylformamide, dioxane, ethylene formal, toluene, chloroform, methylene chloride, or two or more kinds of organic solvents. In view of the above, it is most preferable to use ethylene formal.
エチレンホルマールを用いる場合は、該ポリエーテル−エステル系エラストマーを２〜３０重量％、好ましくは、５〜２０重量％の範囲で使用して、５０〜６０℃の温度でエチレンホルマールに溶解させ溶液を調合する。 In the case of using ethylene formal, the polyether-ester elastomer is used in the range of 2 to 30% by weight, preferably 5 to 20% by weight, and the solution is dissolved in ethylene formal at a temperature of 50 to 60 ° C. Mix.
また、布帛上にコーティングする方法としては、通常のコーティング法、例えば、ナイフコーター等を用いて行えばよいが、コーティングの量としては、コーティング層が２〜５０μｍ、好ましくは、１０〜２０μｍの範囲となるように行えばよい。該コーティング層が２μｍ未満の場合には、均一な皮膜を形成することが困難であり、また、５０μｍを超える場合には風合として弾性が強くなり、また、透湿性も低下するので好ましくない。 Moreover, as a method of coating on the fabric, a normal coating method, for example, a knife coater or the like may be used. The amount of coating is such that the coating layer is 2 to 50 μm, preferably 10 to 20 μm. It can be done so that When the coating layer is less than 2 μm, it is difficult to form a uniform film, and when it exceeds 50 μm, elasticity is increased as a texture and moisture permeability is also deteriorated.
該エチレンホルマールを除去する方法としては、乾式法と湿式法とがあるが、乾式法においては、温度：７０〜１７０℃の乾熱条件下、好ましくは、温度：７０〜１５０℃の範囲で行われる。湿式法においては、ポリエステル 系エラストマーが不溶で、エチレンホルマールが可溶な溶液、例えば、温水中にてエチレンホルマールを抽出した後、乾燥を行う。 As a method for removing the ethylene formal, there are a dry method and a wet method. In the dry method, the temperature is 70 to 170 ° C., preferably, the temperature is 70 to 150 ° C. Is called. In the wet method, the polyester-based elastomer is insoluble and the ethylene formal is soluble, for example, the ethylene formal is extracted in warm water and then dried.
また、ポリエーテル−エステル系エラストマーからなるフィルムを作成する方法としては、公知の方法、例えば、インフレーション法やダイ押出し法により得た、厚さが好ましくは２〜５０μｍ、さらに好ましくは５〜２０μｍの均一なフィルムを使用するものがよい。上記フィルムの厚さが２μｍ未満の場合には、ラミネートの作業が困難となり均一な耐水圧が得られないおそれがあり、また透湿防水層の強度が著しく低下してしまい、一方、フィルムの厚さが５０μｍを超える場合には、透湿性が低下するおそれがあり、また防水透湿層の曲げ硬さが硬くなってしまうことで布帛全体が硬くなってしまう。 Moreover, as a method of producing a film comprising a polyether-ester elastomer, a thickness obtained by a known method, for example, an inflation method or a die extrusion method, is preferably 2 to 50 μm, more preferably 5 to 20 μm. It is preferable to use a uniform film. When the thickness of the film is less than 2 μm, the laminating operation becomes difficult and there is a possibility that uniform water pressure resistance may not be obtained, and the strength of the moisture permeable waterproof layer is significantly reduced. If the thickness exceeds 50 μm, the moisture permeability may be lowered, and the bending hardness of the waterproof and moisture-permeable layer becomes hard, so that the entire fabric becomes hard.
なお、ポリエステルフィルムに用いられるポリエステルとしては、上記以外に、例えば「主として結晶性芳香族ポリエステル単位からなるハードセグメントと、主として脂肪族ポリエーテル単位および／または脂肪族ポリエステル単位からなるソフトセグメントとを主たる構成成分とするポリエステルブロック共重合体」であってもよい。このポリエステルブロック共重合体の詳細は、例えば特開平１１−１７０４６１号公報の段落「０００９」〜「００１５」に詳述されている。 In addition to the above, the polyester used for the polyester film mainly includes, for example, “a hard segment mainly composed of a crystalline aromatic polyester unit and a soft segment mainly composed of an aliphatic polyether unit and / or an aliphatic polyester unit. It may be a “polyester block copolymer as a constituent”. Details of this polyester block copolymer are described in detail in paragraphs “0009” to “0015” of JP-A-11-170461, for example.
得られたフィルムは、種々の方法、例えば、熱処理、ミシン掛け、あるいは、接着剤の使用により、基布となる布帛とラミネートすることができる。好ましくは、接着剤である。 The obtained film can be laminated with a fabric to be a base fabric by various methods, for example, heat treatment, sewing, or use of an adhesive. Preferably, it is an adhesive.
上記基布となる布帛と透湿防水性フィルムとの接着剤としては、ポリエーテルエステル系エラストマーなどのポリエステル樹脂からなる接着剤がリサイクル効率の上で好適ではあるが、重量比率が少ないので、ポリウレタン系接着剤であってもよい。 As an adhesive between the fabric to be the base fabric and the moisture permeable waterproof film, an adhesive made of a polyester resin such as a polyetherester elastomer is suitable in terms of recycling efficiency, but the polyurethane has a low weight ratio. It may be a system adhesive.
また、前記透湿防水層の上に、例えば無機微粒子を含む透湿性高分子樹脂が全面にまたは部分的に積層されていてもよい。また、透湿防水層には目止めテープが貼られていてもよい。 Further, on the moisture permeable waterproof layer, for example, a moisture permeable polymer resin containing inorganic fine particles may be laminated on the entire surface or partially. Moreover, the sealing tape may be affixed on the moisture-permeable waterproof layer.
本発明の透湿防水性布帛において、前記透湿防水層上に前記布帛Ａが積層されている。すなわち、本発明の透湿防水性布帛において、基布、透湿防水層、布帛Ａがこの順に配されている。
その際、布帛Ａを積層する方法としては縫製でもよいが、ウレタン系接着剤などの接着剤で接着させることが好ましい。
In the moisture-permeable and waterproof fabric of the present invention, the fabric A is laminated on the moisture-permeable and waterproof layer. That is, in the moisture-permeable and waterproof fabric of the present invention, the base fabric, the moisture-permeable and waterproof layer, and the fabric A are arranged in this order.
At this time, as a method of laminating the fabric A, sewing may be performed, but it is preferable to bond the fabric A with an adhesive such as a urethane-based adhesive.
本発明の透湿防水性布帛において、前記布帛Ａの上（透湿防水層とは反対側表面）に、さらにウレタン系樹脂などの透湿性樹脂をコーテイング等により積層すると、前記布帛Ａの保護となり好ましい。布帛Ａの上に透湿性樹脂を積層しない場合、洗濯や着用の際の摩擦により前記布帛Ａが剥離し耐久性が損われるおそれがある。 In the moisture-permeable and waterproof fabric of the present invention, when a moisture-permeable resin such as urethane resin is further laminated on the fabric A (surface opposite to the moisture-permeable and waterproof layer) by coating or the like, the fabric A is protected. preferable. When a moisture-permeable resin is not laminated on the fabric A, the fabric A may be peeled off due to friction during washing or wearing, and durability may be impaired.
本発明の透湿防水性布帛において、透湿防水性布帛をケミカルリサイクルし、再度、ポリエステル原料として再生する上で、布帛全体のポリエステルが重量比５０％以上（さらに好ましくは７０％以上）でることが好ましい。ポリエステルの重量比率が５０％より小さいとリサイクル効率が低下してしまいコストアップやエネルギー消費量アップしてしまう。リサイクル効率を上げるためにはできる限りポリエステル比率を高めるほうがよい。そのため、透湿防水性布帛の構成は特に限定されるものではないが、ポリエステル繊維のみからなる基布およびポリエステルフィルムおよびポリエステル繊維からなる布帛Ａで構成することが好ましい。また、基布とフィルムをラミネーションする接着剤もポリエステル系樹脂であることが好ましい。さらに、透湿防水層の上にさらに樹脂を積層する場合も該樹脂がポリエステル系樹脂であることが好ましい。
本発明の透湿防水性布帛において、基布の片面に透湿防水層が積層され、さらにその上に、赤外線吸収剤を含む布帛Ａが積層されているので、蓄熱性に優れる。
In the moisture-permeable and waterproof fabric of the present invention, when the moisture-permeable and waterproof fabric is chemically recycled and recycled again as a polyester raw material, the polyester of the entire fabric is 50% or more by weight (more preferably 70% or more). Is preferred. If the weight ratio of the polyester is less than 50%, the recycling efficiency is lowered, resulting in an increase in cost and energy consumption. In order to increase the recycling efficiency, it is better to increase the polyester ratio as much as possible. Therefore, the configuration of the moisture-permeable and waterproof fabric is not particularly limited, but it is preferable that the moisture-permeable and waterproof fabric is configured with a base fabric made of only polyester fibers and a fabric A made of polyester film and polyester fibers. The adhesive for laminating the base fabric and the film is also preferably a polyester resin. Furthermore, when a resin is further laminated on the moisture permeable waterproof layer, the resin is preferably a polyester resin.
In the moisture-permeable and waterproof fabric of the present invention, the moisture-permeable and waterproof layer is laminated on one side of the base fabric, and the fabric A containing an infrared absorber is further laminated thereon, so that the heat storage property is excellent.
次に、本発明によれば、前記の透湿防水性布帛を用いてなる、スポーツウェア、アウトドアウェア、レインコート、紳士衣服、婦人衣服、作業衣、防護服、人工皮革、履物、鞄、カーテン、テント、寝袋、防水シート、およびカーシートの群より選ばれるいずれかの繊維製品が提供される。
ここで、繊維製品がスポーツウェア、アウトドアウェア、レインコート、紳士衣服、婦人衣服、作業衣、防護服の場合、通常、布帛Ａが人体側となるよう使用される。
かかる繊維製品は前記の透湿防水性布帛を用いているので、蓄熱性に優れる。
Next, according to the present invention, sportswear, outdoor wear, raincoat, men's clothing, women's clothing, work clothing, protective clothing, artificial leather, footwear, heels, curtains using the moisture-permeable and waterproof fabric described above Any fiber product selected from the group consisting of a tent, a sleeping bag, a tarpaulin, and a car seat is provided.
Here, when the textile product is sportswear, outdoor clothing, raincoat, men's clothing, women's clothing, work clothing, or protective clothing, the fabric A is usually used on the human body side.
Since such a fiber product uses the moisture-permeable and waterproof fabric, it has excellent heat storage properties.
次に、本発明の実施例および比較例を詳述するが、本発明はこれらによって限定されるものではない。
＜目付＞
ＪＩＳＬ１０９６ ６．４により測定した。
＜蓄熱性＞
２３℃、４５％ＲＨの環境下で、発泡スチロール製試料台の上に試料を設置し、該試料と試料台との間に熱電対温度センサーを挿入した。
次いで、試料表面（基布表面）の上方３０ｃｍの距離から試料表面を、Ｐａｎａｓｏｎｉｃ社製写真用ランプ「ＰＲＦ−５００ＷＢ」で１０分間照射し、前記熱電対温度センサーで温度を測定した。
Next, although the Example and comparative example of this invention are explained in full detail, this invention is not limited by these.
<Unit weight>
It was measured according to JISL1096 6.4.
<Heat storage>
In an environment of 23 ° C. and 45% RH, a sample was placed on a polystyrene foam sample table, and a thermocouple temperature sensor was inserted between the sample and the sample table.
Next, the sample surface was irradiated for 10 minutes with a photographic lamp “PRF-500WB” manufactured by Panasonic, from a distance of 30 cm above the sample surface (base fabric surface), and the temperature was measured with the thermocouple temperature sensor.
［実施例１］
基布としてポリエチレンテレフタレートマルチフィラメント仮撚捲縮加工糸８４ｄｔｅｘ／７２ｆｉｌを経糸および緯糸に用いて公知の平組織の生機を織成した後、撥水加工を含む通常の染色工程にて分散染料により黒色に染色することにより、基布としてポリエステル織物（目付９３ｇｒ／ｍ２）を得た。その後、デュポン(株)製無孔質透湿性透明ポリエステルフィルム（商品名：アクティブレイヤー、厚み１０μｍ）を、ウレタン系接着剤を用いて前記基布の片面にラミネーションすることにより透湿防水層を形成した。
一方、赤外線吸収剤としてカーボンブラックをポリエチレンテレフタレート重量に対して１．２重量％含有するポリエチレンテレフタレートを常法により、紡糸、延伸して３３ｄｔｅｘ／１２ｆｉｌの延伸糸を得た後、該延伸糸だけを用いて、公知のトリコット編地を得て、通常の染色加工を施すことにより、布帛Ａ（５７コース／２．５４ｃｍかつ４０ウエール／２．５４ｃｍ、目付４０ｇｒ／ｍ２）とした。
[Example 1]
After weaving a known plain texture using a polyethylene terephthalate multifilament false-twist crimped yarn 84dtex / 72fil as a base fabric for warp and weft, it is blackened with a disperse dye in a normal dyeing process including water-repellent processing By dyeing, a polyester woven fabric (weighing 93 gr / m 2 ) was obtained as a base fabric. Thereafter, a non-porous moisture-permeable transparent polyester film (product name: active layer, thickness 10 μm) manufactured by DuPont Co., Ltd. is laminated on one side of the base fabric with a urethane adhesive to form a moisture-permeable waterproof layer. did.
On the other hand, polyethylene terephthalate containing 1.2% by weight of carbon black as an infrared absorber with respect to the weight of polyethylene terephthalate was spun and stretched by a conventional method to obtain a stretched yarn of 33 dtex / 12 fil. Using this, a known tricot knitted fabric was obtained and subjected to ordinary dyeing to obtain a fabric A (57 course / 2.54 cm and 40 wale / 2.54 cm, basis weight 40 gr / m 2 ).
次いで、前記の透湿防水層の、基布とは反対側の面に、前記布帛Ａをウレタン系接着剤で接着した。そして、さらに布帛Ａの表面（透湿防水層とは反対側の面）に透湿性ウレタン系樹脂を全面にコーティングを行い、透湿防水布帛を得た（目付１７０ｇｒ／ｍ２）。
得られた布帛は、蓄熱性評価で温度が下記の比較例１対比５．３℃高く、蓄熱性に優れたものであった。
次いで、前記透湿防水性布帛を用いて、布帛Ａを基布よりも人体側に位置するようスポーツウェアを縫製して着用したところ、透湿防湿性に優れ、また、蓄熱性にも優れるものであった。
Next, the fabric A was adhered to the surface of the moisture-permeable waterproof layer on the side opposite to the base fabric with a urethane-based adhesive. Then, further breathable urethane resin (surface opposite to the moisture-permeable waterproof layer) performs a coating on the entire surface of the fabric A, to obtain a moisture-permeable waterproof fabric (basis weight 170gr / m 2).
The obtained fabric had a heat storage evaluation of 5.3 ° C. higher than that of Comparative Example 1 below, and was excellent in heat storage.
Next, when the sportswear is sewn and worn so that the fabric A is located on the human body side with respect to the base fabric using the moisture permeable and waterproof fabric, the moisture permeable and moisture proof property is also excellent. Met.
［比較例１］
実施例１において、カーボンブラックを含有しないポリエチレンテレフタレートを用いて３３ｄｔｅｘ／１２ｆｉｌの延伸糸を得たこと以外は実施例１と同様にした。
[Comparative Example 1]
Example 1 was carried out in the same manner as in Example 1 except that 33 dtex / 12 fil drawn yarn was obtained using polyethylene terephthalate containing no carbon black.
本発明によれば、蓄熱性に優れた透湿防水性布帛および該透湿防水性布帛を用いてなる繊維製品が提供され、その工業的価値は極めて大である。 ADVANTAGE OF THE INVENTION According to this invention, the moisture-permeable waterproof fabric excellent in heat storage and the textiles using this moisture-permeable waterproof fabric are provided, The industrial value is very large.
Claims (10)
ＣＦ＝（ＤＷｐ／１．１）１／２×ＭＷｐ＋（ＤＷｆ／１．１）１／２×ＭＷｆ
［ＤＷｐは経糸総繊度（ｄｔｅｘ）、ＭＷｐは経糸織密度（本／２．５４ｃｍ）、ＤＷｆは緯糸総繊度（ｄｔｅｘ）、ＭＷｆは緯糸織密度（本／２．５４ｃｍ）である。］ The moisture-permeable waterproof fabric according to any one of claims 1 to 3, wherein the fabric A is a woven fabric having a cover factor CF defined by the following formula of 300 to 3500.
CF = (DWp / 1.1) 1/2 × MWp + (DWf / 1.1) 1/2 × MWf
[DWp is the total warp fineness (dtex), MWp is the warp weave density (main / 2.54 cm), DWf is the total weft fineness (dtex), and MWf is the weft weave density (main / 2.54 cm). ]