JP2010275155A - Concrete composition, concrete structure and block for fish reef or spawning reef - Google Patents
Concrete composition, concrete structure and block for fish reef or spawning reef Download PDFInfo
- Publication number
- JP2010275155A JP2010275155A JP2009130443A JP2009130443A JP2010275155A JP 2010275155 A JP2010275155 A JP 2010275155A JP 2009130443 A JP2009130443 A JP 2009130443A JP 2009130443 A JP2009130443 A JP 2009130443A JP 2010275155 A JP2010275155 A JP 2010275155A
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- waste
- concrete composition
- block
- fish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、産業廃棄物を骨材として使用したコンクリート組成物、コンクリート構造物、および魚礁用または産卵礁用ブロックに関する。 The present invention relates to a concrete composition, a concrete structure, and a block for fish reef or laying reef using industrial waste as an aggregate.
従来、固形の廃棄物を粉砕して、コンクリート組成物中に骨材として配合する技術が提案されている(例えば、特許文献1参照。)。また、そのようなコンクリート組成物で魚礁用ブロックを製造することも提案されている。このような技術を利用すれば、廃棄物の再利用を図ることができた。 Conventionally, a technique has been proposed in which solid waste is pulverized and blended as an aggregate in a concrete composition (see, for example, Patent Document 1). It has also been proposed to produce reef blocks with such a concrete composition. By using such technology, it was possible to reuse the waste.
しかし、特許文献1に記載のコンクリート組成物のように、廃棄物を骨材として利用すると、最終的に得られるコンクリート構造物の強度を日本工業規格(JIS規格)に定められた基準を満たす程度で、かつ十分に高くすることができないことがある。具体的には、例えば、骨材中に含まれる耐用年数を超えて解体廃棄される劣化の激しいコンクリートくず類の量が比較的多い場合には、最終的に得られるコンクリート構造物の強度が低下する傾向にある。 However, as in the concrete composition described in Patent Document 1, when waste is used as an aggregate, the strength of the concrete structure finally obtained satisfies the standard defined in the Japanese Industrial Standard (JIS standard). And sometimes it cannot be high enough. Specifically, for example, when there is a relatively large amount of rapidly deteriorating concrete waste that is dismantled beyond the useful life contained in the aggregate, the strength of the concrete structure that is finally obtained decreases. Tend to.
そのため、十分に高い強度が要求されるコンクリート構造物を製造する際には、廃棄物由来の骨材を含むコンクリート組成物を利用することが難しい、という問題があった。
本発明は、上記問題を解決するためになされたものであり、その目的は、固形の廃棄物を骨材として使用しているにもかかわらず、従来品よりも強度に優れたコンクリート硬化体を形成可能なコンクリート組成物を提供することにある。
Therefore, when manufacturing a concrete structure requiring sufficiently high strength, there is a problem that it is difficult to use a concrete composition containing aggregate derived from waste.
The present invention has been made in order to solve the above problems, and its purpose is to provide a hardened concrete body that is superior in strength to conventional products, despite using solid waste as an aggregate. It is to provide a formable concrete composition.
以下、本発明において、上記目的を達成するために採用した構成について説明する。
本発明のコンクリート組成物は、セメントと、貝殻類、廃プラスチック類、ゴムくず、金属くず、ガラスくず、コンクリートくず、陶磁器くず、および瓦礫類の中から選ばれる少なくとも1種を破砕することによって得られた破砕物からなる粗骨材と、石炭灰、副産石膏、焼却灰、燃えがら、粉塵、ばい塵、汚泥類、廃残土、および廃砂の中から選ばれる少なくとも1種の細骨材と、高炉スラグ微粉末、フライアッシュ、クリンカーアッシュ、およびシリカフュームの中から選ばれる少なくとも1種の混和材と、ガラス繊維および炭素繊維の中から選ばれる少なくとも1種の強化繊維とを含むことを特徴とする。
Hereinafter, the configuration adopted to achieve the above object in the present invention will be described.
The concrete composition of the present invention is obtained by crushing cement and at least one selected from shells, waste plastics, rubber scraps, metal scraps, glass scraps, concrete scraps, ceramic scraps, and rubbles. Coarse aggregate made of crushed material and at least one fine aggregate selected from coal ash, by-product gypsum, incinerated ash, cinder, dust, dust, sludge, waste soil, and waste sand And at least one admixture selected from among blast furnace slag fine powder, fly ash, clinker ash, and silica fume, and at least one reinforcing fiber selected from glass fiber and carbon fiber, To do.
このようなコンクリート組成物を硬化させてコンクリート硬化体を製造すれば、コンクリート組成物中に含まれる強化繊維によって、コンクリート硬化体の強度がJIS規格に定められた基準を満たすことが可能となる。したがって、仮にコンクリート硬化体の強度を低下させる原因となる骨材(例えば、耐用年数を超えて解体廃棄される劣化の激しいコンクリートくず、あるいは塩害または寒冷等により劣化したコンクリートくず由来の骨材)が比較的多く含まれていたとしても、最終的に得られるコンクリート硬化体の強度が、強化繊維を含まない従来のコンクリート製品よりも高くなり、JIS規格を満たすだけでなく、JIS規格に定められた最低基準値に比べ、はるかに優れた強度を備えたコンクリート製品を提供することができる。 If such a concrete composition is cured to produce a hardened concrete body, the strength of the hardened concrete body can satisfy the standard defined in the JIS standard by the reinforcing fibers contained in the concrete composition. Therefore, aggregates that cause a decrease in the strength of the hardened concrete (for example, severely deteriorated concrete scraps that are dismantled and discarded beyond their useful lives, or aggregates derived from concrete scraps that have deteriorated due to salt damage or cold) Even if it is contained in a relatively large amount, the strength of the concrete hardened body finally obtained is higher than that of conventional concrete products that do not contain reinforcing fibers, not only meeting the JIS standard but also stipulated in the JIS standard. It is possible to provide a concrete product with much superior strength compared to the minimum standard value.
また、本発明のコンクリート組成物は、様々なコンクリート製品を製造する際に利用できるが、具体例を挙げれば、魚礁用ブロック、産卵礁用ブロック、波消しブロック、人工海底山脈構成用ブロック、橋脚、その他の様々な建設用資材、港湾土木資材等として使用することができる。 In addition, the concrete composition of the present invention can be used for producing various concrete products. Specific examples include fish reef blocks, laying reef blocks, wave-dissipating blocks, artificial submarine mountain range building blocks, piers. It can be used as various other construction materials and harbor civil engineering materials.
これらのコンクリート製品を製造するには、工場などで本発明のコンクリート組成物を利用してコンクリート製品を製造してもよいし、現場打ちの施工によってコンクリート製品を製造してもよい。 In order to manufacture these concrete products, a concrete product may be manufactured using the concrete composition of the present invention in a factory or the like, or a concrete product may be manufactured by on-site construction.
現場打ちの施工を行う例としては、例えば、このコンクリート組成物を山肌の法面に吹き付けて、崩落防止用のコンクリートコーティングを行う、あるいは、老朽化した陸屋根の表面に吹き付けて、防水対策用のコンクリートコーティングを行う、といった施工例を挙げることができる。 As an example of on-site construction, for example, this concrete composition is sprayed on the slope of the mountain surface, and concrete coating for preventing collapse is applied, or it is sprayed on the surface of an aged flat roof for waterproofing measures. Examples of construction such as concrete coating can be given.
ところで、粗骨材として使用するために破砕された破砕物の中には、ガラス類や陶磁器類等、尖った形状となるものもある。そのため、このような粗骨材をそのまま使用する場合に、尖った部分がコンクリート硬化体の外面に露出したり、設置後の破損等により尖った骨材が露出したりするのを防ぐには、コンクリート硬化体の外面にコーティング層を追加する等の対策が必要となる。 By the way, some crushed materials crushed for use as coarse aggregates have a sharp shape, such as glass and ceramics. Therefore, when using such coarse aggregate as it is, in order to prevent the pointed part from being exposed to the outer surface of the hardened concrete body, or the pointed aggregate due to damage after installation, etc. It is necessary to take measures such as adding a coating layer to the outer surface of the hardened concrete.
その点、本発明のコンクリート組成物において、前記破砕物を研磨材とともに攪拌することにより、前記破砕物の角を面取りしたものを、前記粗骨材として利用すると、尖った形状の骨材を含むコンクリート構造物のように、骨材の尖った部分が外面に露出してしまうことがない。 In that regard, in the concrete composition of the present invention, when the crushed material is agitated with an abrasive and the chamfered corners of the crushed material are used as the coarse aggregate, a sharp aggregate is included. Like a concrete structure, the sharp part of aggregate is not exposed to the outer surface.
したがって、このようなコンクリート組成物であれば、従来のように骨材の尖った部分が露出しないような対策を実施しなくてもよい。
次に、本発明のコンクリート構造物は、本発明のコンクリート組成物を硬化させてなる基部と、炭素繊維が添加されたセメントを硬化させてなり、前記基部を被覆する第1被覆層とを備えることを特徴とする。
Therefore, if it is such a concrete composition, it is not necessary to implement the measure which does not expose the pointed part of aggregate like the past.
Next, the concrete structure of the present invention includes a base formed by curing the concrete composition of the present invention, and a first coating layer formed by curing cement to which carbon fiber is added and covering the base. It is characterized by that.
このようなコンクリート構造物であれば、被覆層の表面に炭素繊維が露出した状態となるので、魚礁用または産卵礁用ブロックとして利用した際、炭素繊維を含むセメントで被覆されていない従来のコンクリート製品に比べ、表面に露出した炭素繊維に藻類が早期に付着して、そのまま定着する。そのため、従来のコンクリート製品に比べ、短期間で藻類の繁殖を促すことができる。また、ブロック表面の炭素繊維には、海草の胞子、魚介類の卵、サンゴのポリプなども付着するので、海草、魚介類およびサンゴの成長促進を期待できる。 With such a concrete structure, the carbon fiber is exposed on the surface of the coating layer, so when used as a block for fish reefs or laying reefs, conventional concrete not coated with cement containing carbon fibers Compared to the product, algae adheres to the carbon fiber exposed on the surface at an early stage and settles as it is. Therefore, algae can be promoted in a short period of time compared to conventional concrete products. In addition, since seaweed spores, seafood eggs, coral polyps, and the like adhere to the carbon fibers on the block surface, growth of seagrass, seafood, and corals can be expected to be promoted.
また、このようなコンクリート構造物をヘドロで汚れた海や河川に設置すると、表面の炭素繊維にヘドロが絡まる。したがって、このようにヘドロが絡まった状態のコンクリート硬化体を、水中から引き上げてヘドロを除去することで、海や河川の水質浄化を図ることもできる。 Moreover, when such a concrete structure is installed in the sea and river which became dirty with sludge, sludge gets entangled in the carbon fiber on the surface. Therefore, it is possible to purify the water quality of the sea and rivers by removing the sludge by pulling up the hardened concrete in a state where the sludge is tangled in this way from the water.
また、本発明のコンクリート構造物は、本発明のコンクリート組成物を硬化させてなる基部と、魚粉、炭酸カルシウム、窒素質肥料、リン酸質肥料、ケイ酸質肥料、ビタミン類、およびミネラル成分のうち、少なくとも1つが添加されたセメントを硬化させてなり、前記基部を被覆する第2被覆層とを備えることを特徴とする。 Further, the concrete structure of the present invention comprises a base formed by curing the concrete composition of the present invention, and fish meal, calcium carbonate, nitrogenous fertilizer, phosphate fertilizer, siliceous fertilizer, vitamins, and mineral components. Of these, a cement to which at least one is added is hardened and includes a second coating layer that covers the base.
このようなコンクリート構造物であれば、魚礁用または産卵礁用ブロックとして利用した際、第2被覆層に含まれている魚粉、炭酸カルシウム、窒素質肥料、リン酸質肥料、ケイ酸質肥料、ビタミン類、およびミネラル成分が河川または海中へ溶出される。このように、水中へ溶け出た魚粉等は、魚類やプランクトンの餌、および海草の養分等となる。そのため、魚粉等を含まない従来品に比べ、海草やプランクトンの繁殖を促すことができ、これらを捕食する海洋生物も集まってくるので、魚介類の棲息の場あるいは産卵の場として有効に機能させることができる。 If it is such a concrete structure, when used as a block for fish reef or spawning reef, fish meal, calcium carbonate, nitrogenous fertilizer, phosphate fertilizer, siliceous fertilizer contained in the second coating layer, Vitamins and minerals are eluted into the river or sea. In this way, fish meal and the like dissolved into water become fish and plankton feed, seaweed nutrients, and the like. Therefore, compared to conventional products that do not contain fish meal etc., it can promote the propagation of seagrass and plankton, and marine organisms that prey on these also gather, so it functions effectively as a place of habitat or spawning for seafood be able to.
次に、本発明の実施形態について、いくつかの具体的な例を挙げて説明する。
[第1実施形態]
第1実施形態では、本発明のコンクリート組成物を利用して魚礁用ブロックを製造する事例について説明する。
Next, embodiments of the present invention will be described with some specific examples.
[First Embodiment]
1st Embodiment demonstrates the example which manufactures the block for fish reef using the concrete composition of this invention.
第1実施形態で利用するコンクリート組成物は、セメントと、粗骨材と、細骨材と、コンクリート混和材と、強化繊維を混合したものである。
これらのうち、セメントとしては、魚礁という用途に配慮し、生体に対する安全性が高いもの(具体的には、歯科治療で用いられるセメント成分と同等の組成成分で構成されたもの)を利用している。
The concrete composition used in the first embodiment is a mixture of cement, coarse aggregate, fine aggregate, concrete admixture, and reinforcing fibers.
Among these, as cement, taking into account the use of fish reef, the one with high safety to living body (specifically, composed of the same composition component as the cement component used in dental treatment) is used. Yes.
粗骨材としては、貝殻類、廃プラスチック類、ゴムくず、金属くず、ガラスくず、コンクリートくず、陶磁器くず、および瓦礫類のうち、いずれか1種または複数種を原料とし、これらの原料を破砕して、その破砕物に対して面取り加工を施したものを利用している。 Coarse aggregates are shells, waste plastics, rubber scraps, metal scraps, glass scraps, concrete scraps, ceramic scraps, and rubbles. And what chamfered the crushed material is used.
なお、JIS規格において、粗骨材は「5mm網ふるいに質量で85%以上とどまる骨材(JIS A 0203)」と規定されているので、本実施形態においても、上記各原料をJIS規格に準拠するサイズに破砕し、ふるい分けにより分級している。 In the JIS standard, the coarse aggregate is defined as “aggregate with a mass of 85% or more on a 5 mm screen (JIS A 0203)”. In this embodiment, the raw materials are also compliant with the JIS standard. The size is crushed and classified by sieving.
細骨材としては、石炭灰、副産石膏、焼却灰、燃えがら、粉塵、ばい塵、汚泥類(例えば、下水・湖沼・河川・港湾汚泥等自然発生する汚泥類、製紙スラッジ・研磨スラッジ等産業発生型汚泥類、建設汚泥等がある。)、廃残土、および廃砂のうち、いずれか1種または複数種を原料とし、これらの原料に対して無害化処理(原料を1000℃〜1400℃で焼成することにより特定有害物質やダイオキシン類等を除去して無害化する焼成処理、または原料と水の混合物に凝集剤等を添加することにより凝集する有害物質を濾過することで除去して無害化する処理等)を施したものを利用している。 Fine aggregates include coal ash, by-product gypsum, incinerated ash, cinder, dust, dust, sludge (eg, sludge generated naturally such as sewage, lakes, rivers, harbor sludge, paper sludge, abrasive sludge, etc.) There are generation type sludges, construction sludges, etc.), waste residual soil, and waste sand. It is harmless by removing the harmful substances that are aggregated by adding a flocculant etc. to the mixture of raw materials and water by baking treatment that removes specific harmful substances and dioxins etc. by detoxifying them by baking That have been processed).
なお、JIS規格において、細骨材は「10mm網ふるいを全部通り、5mm網ふるいを質量で85%以上通過する骨材(JIS A 0203)」と規定されているので、本実施形態においても、上記副産石膏をJIS規格に準拠するサイズに加工し分級している。 In addition, in the JIS standard, the fine aggregate is defined as “aggregate that passes through the entire 10 mm mesh screen and passes through the 5 mm mesh screen by 85% or more (JIS A 0203)”. The by-product gypsum is processed into a size that conforms to JIS standards and classified.
コンクリート混和材としては、高炉スラグ微粉末(微粉炭燃焼ボイラより発生する石炭灰)、フライアッシュ、クリンカーアッシュ、シリカフュームのうち、いずれか1種または複数種を利用している。 As the concrete admixture, one or more of blast furnace slag fine powder (coal ash generated from a pulverized coal combustion boiler), fly ash, clinker ash, and silica fume are used.
強化繊維としては、ガラス繊維または炭素繊維であって、直径が10〜50μm、長さが5〜50mmのものを利用している。
次に、上述した本発明のコンクリート組成物の製造方法について説明する。
As the reinforcing fiber, glass fiber or carbon fiber having a diameter of 10 to 50 μm and a length of 5 to 50 mm is used.
Next, the manufacturing method of the concrete composition of this invention mentioned above is demonstrated.
まず、粗骨材については、次のような手順で製造した。なお、粗骨材の原料になる貝殻類としては、貝類の加工工場において廃棄される貝殻を利用した。また、廃プラスチック類、ゴムくず、金属くず、ガラスくず、コンクリートくず、陶磁器くず、および瓦礫類としては、建設物の解体によって発生する産業廃棄物(安定型5品目に分類されるもの)を利用した。 First, the coarse aggregate was manufactured by the following procedure. The shells used as raw materials for coarse aggregates were shells discarded at shellfish processing plants. In addition, waste plastics, rubber scraps, metal scraps, glass scraps, concrete scraps, ceramic scraps, and rubbles are made from industrial waste generated by the demolition of construction (those classified into five stable types). did.
粗骨材として利用する産業廃棄物については、複数種の原料が混ざった状態なので、まず、原料の種類毎に仕分けする処理が施される。そして、原料の種類毎に図示しない破砕機で適度な大きさに破砕されて破砕物とされ、その後、図1(a)に示す面取り加工装置1を利用して、これらの破砕物に対して面取り加工が施される。 Since the industrial waste used as the coarse aggregate is in a state where a plurality of types of raw materials are mixed, first, a process for sorting the types of raw materials is performed. And it crushes to an appropriate magnitude | size with the crusher which is not illustrated for every kind of raw material, and is made into a crushing thing, Then, it uses with the chamfering processing apparatus 1 shown to Fig.1 (a) with respect to these crushing goods. Chamfering is performed.
面取り加工装置1は、面取り加工機3、ベルトコンベア5、磁気選別機7、および回収容器9などを備えている。
面取り加工機3は、図1(b)に示すように、ドラム支持部3a、回動ドラム3b、回転軸3c、および攪拌羽根3dを備えている。回動ドラム3bは、ドラム支持部3aのモータによって回転軸3cを中心として回動可能に構成されている。また、回動ドラム3bの内部には、攪拌羽根3dが設けられている。
The chamfering apparatus 1 includes a chamfering machine 3, a belt conveyor 5, a magnetic sorter 7, a collection container 9, and the like.
As shown in FIG. 1B, the chamfering machine 3 includes a drum support portion 3a, a rotating drum 3b, a rotating shaft 3c, and a stirring blade 3d. The rotating drum 3b is configured to be rotatable about a rotating shaft 3c by a motor of the drum support portion 3a. A stirring blade 3d is provided inside the rotating drum 3b.
破砕物の面取り加工を行う際には、破砕物が複数の研磨材4とともに、面取り加工機3の回動ドラム3b内へ投入される。研磨材4は、直径5〜30mm程度の鋼球である。また、このとき、破砕物の表面を均一に研磨するため、回動ドラム3b内へは水も投入される。回動ドラム3b内へ投入される破砕物:研磨材:水の重量比は、5:1:6〜9程度が好ましい。 When chamfering the crushed material, the crushed material is put into the rotating drum 3 b of the chamfering machine 3 together with the plurality of abrasives 4. The abrasive 4 is a steel ball having a diameter of about 5 to 30 mm. At this time, water is also poured into the rotating drum 3b in order to uniformly grind the surface of the crushed material. The weight ratio of the crushed material: abrasive material: water charged into the rotating drum 3b is preferably about 5: 1: 6-9.
次に、回動ドラム3bを回転駆動して破砕物および研磨材4を攪拌すると、破砕物と研磨材、あるいは破砕物同士が衝突して破砕物の尖った部分が削り取られ、破砕物は徐々に丸みを帯びた面取加工物となってゆく。そして、所望の程度の面取りがなされたら、その後は、回動ドラム3bの回動を停止させ、回動ドラム3bから面取加工物および研磨材4が取り出される。 Next, when the crushed material and the abrasive 4 are agitated by rotationally driving the rotating drum 3b, the crushed material and the abrasive or the crushed material collide with each other, and the pointed portion of the crushed material is scraped off. It becomes a rounded chamfered workpiece. Then, when the desired degree of chamfering is performed, thereafter, the rotation of the rotating drum 3b is stopped, and the chamfered workpiece and the abrasive 4 are taken out from the rotating drum 3b.
そして、回動ドラム3bから取り出された面取加工物および研磨材4は、図2(a)に示すように、ベルトコンベア5で搬送される。このベルトコンベア5の搬送路上には、電磁石によって強力な磁力が発生する磁気選別機7が設置されている。 Then, the chamfered workpiece and the abrasive 4 taken out from the rotating drum 3b are conveyed by the belt conveyor 5 as shown in FIG. On the conveying path of the belt conveyor 5, a magnetic sorter 7 that generates a strong magnetic force by an electromagnet is installed.
ベルトコンベア5によって搬送される面取加工物および研磨材4が、磁気選別機7の設置箇所を通過する際には、鋼球である研磨材4のみがこの磁気選別機7に吸引される。そして、面取加工物のみがベルトコンベア5によって、回収容器9へ搬送される。 When the chamfered workpiece and the abrasive 4 conveyed by the belt conveyor 5 pass through the installation location of the magnetic sorter 7, only the abrasive 4 that is a steel ball is attracted to the magnetic sorter 7. Then, only the chamfered workpiece is conveyed to the collection container 9 by the belt conveyor 5.
そして、回収容器9に回収された面取加工物は2mm網ふるいを用いて分級し、2mm網ふるいを通過しなかったものを粗骨材として利用する。また、2mm網ふるいを通過したものについては、必要があれば細骨材として利用することもできる。 Then, the chamfered workpieces collected in the collection container 9 are classified using a 2 mm mesh sieve, and those that have not passed through the 2 mm mesh sieve are used as coarse aggregate. Moreover, about what passed 2 mm net sieve, if necessary, it can also be utilized as a fine aggregate.
なお、細骨材、コンクリート混和剤については、粗骨材のように面取り加工を施さずに利用する。
以上説明したセメント、粗骨材、細骨材、コンクリート混和剤、および強化繊維を、下記の表1に示すように各原材料の比重で分類し、各分類に対応する配合比の範囲内で配合することによって、コンクリート組成物を製造する。
Note that fine aggregates and concrete admixtures are used without chamfering like coarse aggregates.
Cement, coarse aggregate, fine aggregate, concrete admixture, and reinforcing fibers described above are classified according to the specific gravity of each raw material as shown in Table 1 below, and are mixed within the range of the mixing ratio corresponding to each classification. To produce a concrete composition.
本実施形態の魚礁用ブロック10は、図2(a)に示すように、自然石に似せて成形されたものである。この魚礁用ブロック10は、次のような手順で製造したものである。
まず、この魚礁用ブロック10専用のコンクリート組成物を生成する。本実施形態においては、セメント50%、コンクリートくず(粗骨材B)10%、陶磁器くず(粗骨材C)15%、ガラスくず(粗骨材D)5%、貝殻類(粗骨材D)5%、副産石膏(細骨材F)8%、高炉スラグ微粉末(コンクリート混和剤)5%、およびガラス繊維(強化繊維)2%の配合比で、各原材料を配合した。
As shown in FIG. 2A, the fish reef block 10 of the present embodiment is shaped to resemble natural stone. This fish reef block 10 is manufactured by the following procedure.
First, a concrete composition dedicated to the fish reef block 10 is generated. In this embodiment, cement 50%, concrete scrap (coarse aggregate B) 10%, ceramic scrap (coarse aggregate C) 15%, glass scrap (coarse aggregate D) 5%, shells (coarse aggregate D) ) 5%, by-product gypsum (fine aggregate F) 8%, blast furnace slag fine powder (concrete admixture) 5%, and glass fiber (reinforced fiber) 2%.
そして、このコンクリート組成物と水(JIS規格に規定された量の水)を混練したものを自然石の形状の型枠に流し込んで、硬化させることにより、魚礁用ブロック10を製造する。 Then, the reef block 10 is manufactured by pouring and kneading the concrete composition and water (the amount of water specified in JIS standard) into a natural stone mold.
こうして製造された魚礁用ブロック10は、水中に設置する際に単に積み上げるだけでも構わないが、例えば、台風などの災害時に備えて複数の魚礁用ブロック10を根固め連結してもよい。連結する場合は、専用の連結金具を利用して複数の魚礁用ブロック10を連結すればよく、具体的には、図2(b)、(c)、および(d)に示すような魚礁用ブロックユニット15を構成すればよい。 The fish reef blocks 10 manufactured in this way may be simply stacked when installed in the water, but for example, a plurality of fish reef blocks 10 may be consolidated in preparation for a disaster such as a typhoon. In the case of connection, a plurality of fish reef blocks 10 may be connected using a dedicated connection fitting. Specifically, for fish reef as shown in FIGS. 2 (b), (c), and (d). The block unit 15 may be configured.
魚礁用ブロックユニット15は、図2(b)、(c)、および(d)に示すように、4つの魚礁用ブロック10、連結金具17、および固定金具18から構成される。
連結金具17は、4つの魚礁用ブロック10の間を連結するための金具であり、固定金具18は、水中に設置される際に、海底等に固定するための金具である。なお、連結金具17および固定金具18としては、海洋環境中でも50年以上の耐久性が見込める亜鉛メッキ仕様またはアルミ合金メッキ仕様のものを利用した。
As shown in FIGS. 2B, 2C, and 2D, the fish reef block unit 15 includes four fish reef blocks 10, a connection fitting 17, and a fixing fitting 18.
The connecting metal fitting 17 is a metal fitting for connecting the four fish reef blocks 10, and the fixing metal fitting 18 is a metal fitting for fixing to the seabed or the like when installed in water. In addition, as the connection metal fitting 17 and the fixed metal fitting 18, the thing of the galvanization specification or aluminum alloy plating specification which can anticipate the durability of 50 years or more also in the marine environment was utilized.
以上説明したような魚礁用ブロック10であれば、ガラス繊維が含まれていない従来の魚礁用ブロックに比べ、コンクリート組成物中に含まれるガラス繊維によって、コンクリート硬化体の強度がJIS規格に定められた基準を満たすことが可能となる。 In the case of the fish reef block 10 as described above, the strength of the hardened concrete body is determined by the JIS standard by the glass fiber contained in the concrete composition as compared with the conventional fish reef block not containing the glass fiber. Meeting the standards.
したがって、本実施形態のコンクリート組成物のように、魚礁用ブロック10の強度を低下させる原因となるコンクリートくず由来の骨材が比較的多く含まれていたとしても、最終的に得られる魚礁用ブロック10の強度が、強化繊維を含まない従来のものよりも高くなり、JIS規格を満たすだけでなく、JIS規格に定められた最低基準値に比べ、はるかに優れた強度を備えた魚礁用ブロック10を提供することができる。 Therefore, even if a relatively large amount of aggregate derived from concrete scraps that causes the strength of the fish reef block 10 to be reduced is included as in the concrete composition of the present embodiment, the finally obtained fish reef block The strength of 10 is higher than that of the conventional one not containing reinforcing fibers, and not only satisfies the JIS standard, but also has a much superior strength compared to the minimum standard value defined in the JIS standard. Can be provided.
また、上述した魚礁用ブロック10であれば、河川や海に設置した後、セメント部分等が水や海水に浸食されて粗骨材が魚礁用ブロック10の外面に露出したとしても、面取り加工が施された粗骨材が露出するだけで、鋭利な角を持つ粗骨材が露出することはない。したがって、このような魚礁用ブロック10であれば、鋭利な角を持つ粗骨材が含まれるコンクリート製品とは異なり、骨材の尖った部分が露出するのを防止するための対策を実施しなくても済む。 Further, in the case of the above-described fish reef block 10, the chamfering process is performed even when the cement portion or the like is eroded by water or sea water and the coarse aggregate is exposed on the outer surface of the fish reef block 10 after being installed in the river or the sea. Only the applied coarse aggregate is exposed, and the coarse aggregate with sharp corners is not exposed. Therefore, in the case of such a reef block 10, unlike a concrete product including a coarse aggregate having a sharp angle, no measures are taken to prevent the sharp portion of the aggregate from being exposed. You can do it.
[第2実施形態]
本実施形態において例示する魚礁用ブロック20は、図3(a)に示すように、基部21aと、基部21aを被覆する被覆層21bとから構成される。基部21aは、第1実施形態のコンクリート組成物を硬化させたものである。
[Second Embodiment]
As shown in FIG. 3A, the fish reef block 20 exemplified in the present embodiment includes a base portion 21a and a covering layer 21b that covers the base portion 21a. The base 21a is obtained by curing the concrete composition of the first embodiment.
被覆層21bは、炭素繊維が添加されたセメントで、約5mmの厚さに形成されている。このセメントとしては、第1実施形態同様、生体に対する安全性が高いものを利用している。また、炭素繊維としては、直径が10〜50μm、長さが5〜50mmのものを利用している。 The covering layer 21b is a cement to which carbon fibers are added, and has a thickness of about 5 mm. As this cement, the thing with high safety | security with respect to a biological body is utilized like 1st Embodiment. Carbon fibers having a diameter of 10 to 50 μm and a length of 5 to 50 mm are used.
この被覆層21bは、基部21aを成形した後、炭素繊維が添加されたセメントと適量の水を混練したものを基部21aの表面に吹き付けることによって製造される。
吹き付け装置については一般的なものを使用すればよく、例えば、コンクリート組成物ポンプ、急結剤ポンプ、エアーコンプレッサー、吹き付けノズル、および各部を結ぶ供給ホースなどを備えた周知の装置を利用できる。
The covering layer 21b is manufactured by forming a base portion 21a and then spraying a mixture of cement containing carbon fibers and an appropriate amount of water onto the surface of the base portion 21a.
As the spraying device, a general device may be used. For example, a well-known device including a concrete composition pump, a quick-setting agent pump, an air compressor, a spraying nozzle, a supply hose connecting each part, and the like can be used.
以上説明したような魚礁用ブロック20であれば、被覆層21bの表面に炭素繊維が露出した状態となるので、河川または海中に設置すると、炭素繊維を含むセメントで被覆されていない従来のコンクリート製品に比べ、表面に露出した炭素繊維に藻類が早期に付着して、そのまま定着する。そのため、従来のコンクリート製品に比べ、短い期間で藻類の繁殖を図ることができる。 In the fish reef block 20 as described above, the carbon fiber is exposed on the surface of the coating layer 21b. Therefore, when installed in a river or in the sea, a conventional concrete product not covered with cement containing carbon fiber. Compared to, the algae adheres to the carbon fibers exposed on the surface at an early stage and settles as it is. Therefore, algae can be propagated in a shorter period of time than conventional concrete products.
また、ブロック表面の炭素繊維に海草の胞子、魚介類の卵、サンゴのポリプが付着して、そのまま成長したりもする。そのため、炭素繊維を含むセメントで被覆されていない従来のコンクリート製品に比べ、海草、魚介類およびサンゴが多い豊かな魚礁を形成することができる。 In addition, seaweed spores, seafood eggs, and coral polyps are attached to the carbon fibers on the surface of the block and grow as they are. Therefore, it is possible to form a rich fish reef rich in seaweed, seafood, and coral as compared with conventional concrete products not covered with cement containing carbon fiber.
[第3実施形態]
本実施形態において例示する魚礁用ブロック30は、図3(b)に示すように、基部31aと、基部31aを被覆する被覆層31bとから構成される。基部31aは、第1実施形態のコンクリート組成物を硬化させたものである。
[Third Embodiment]
As shown in FIG. 3B, the fish reef block 30 exemplified in the present embodiment includes a base portion 31a and a covering layer 31b that covers the base portion 31a. The base 31a is obtained by curing the concrete composition of the first embodiment.
被覆層31bは、魚粉が添加されたセメントで、約5mmの厚さに形成されている。このセメントとしては、第1実施形態同様、生体に対する安全性が高いものを利用している。また、魚粉としては、魚介類の食品加工工場において廃棄される魚のアラ等を乾燥、粉砕してミール状にしたものを利用している。 The coating layer 31b is a cement to which fish meal is added and is formed to a thickness of about 5 mm. As this cement, the thing with high safety | security with respect to a biological body is utilized like 1st Embodiment. In addition, fish meal is used that is obtained by drying and pulverizing fish arabe, etc., which are discarded at a food processing plant for seafood.
この被覆層31bは、基部31aを成形した後、魚粉が添加されたセメントと適量の水を混練したものを基部21aの表面に吹き付けることによって製造される。なお、吹き付け装置については、第2実施形態で説明したものと同じ構成の周知の装置を利用できる。 The covering layer 31b is manufactured by molding the base portion 31a and then spraying the surface of the base portion 21a with a kneaded mixture of cement added with fish meal and an appropriate amount of water. In addition, about a spraying apparatus, the well-known apparatus of the same structure as what was demonstrated in 2nd Embodiment can be utilized.
以上説明したような魚礁用ブロック30であれば、河川または海中に設置すると、被覆層31bに含まれている魚粉が河川または海中へ溶出される。このように、水中へ溶け出た魚粉は、魚類やプランクトンの餌となる。そのため、魚粉を含まない従来品に比べ、魚介類が多く集まり、豊かな魚礁にすることができる。 If it is the block 30 for fish reefs demonstrated above, if it installs in a river or the sea, the fish meal contained in the coating layer 31b will be eluted to the river or the sea. In this way, the fish meal that has melted into the water serves as food for fish and plankton. Therefore, compared with the conventional product which does not contain fish meal, a lot of seafood gathers and it can be made a rich fish reef.
なお、本実施形態では、魚類やプランクトンの餌となる成分として魚粉をセメントに添加する例を示したが、上記餌となる成分は魚粉に限定されるものではなく、また、海草の養分となる成分を添加してもよい。そのような、魚類やプランクトンの餌となる成分、あるいは海草の養分となる成分としては、例えば、炭酸カルシウム、窒素質肥料、リン酸質肥料、ケイ酸質肥料、ビタミン類、およびミネラル成分などを挙げることができる。これらの各成分は、単独で添加してもよいし、2種以上を添加してもよい。 In addition, in this embodiment, although the example which adds fish meal to a cement as an ingredient used as the feed of fish and plankton was shown, the ingredient used as the feed is not limited to fish meal, and is a seaweed nutrient. Ingredients may be added. Examples of ingredients that feed fish and plankton or nutrients for seaweed include calcium carbonate, nitrogenous fertilizer, phosphate fertilizer, siliceous fertilizer, vitamins, and mineral ingredients. Can be mentioned. Each of these components may be added alone or in combination of two or more.
[その他の実施形態]
以上、本発明の実施形態について説明したが、本発明は上記の具体的な一実施形態に限定されず、この他にも種々の形態で実施することができる。
[Other Embodiments]
As mentioned above, although embodiment of this invention was described, this invention is not limited to said specific one Embodiment, In addition, it can implement with a various form.
上記の第1実施形態では、粗骨材の原料として、貝殻類、廃プラスチック類、ゴムくず、金属くず、ガラスくず、コンクリートくず、陶磁器くず、および瓦礫類のうち、いずれか1種または複数種を利用していたが、粗骨材として利用する原料は、これに限定されるものではなく、例えば、高炉スラグ等金属工業廃棄物類なども粗骨材の原料として利用してもよい。 In the first embodiment, the raw material of the coarse aggregate is any one or more of shells, waste plastics, rubber scraps, metal scraps, glass scraps, concrete scraps, ceramic scraps, and rubbles. However, the raw material used as the coarse aggregate is not limited to this. For example, metal industrial wastes such as blast furnace slag may be used as the raw material for the coarse aggregate.
また、細骨材についても、石炭灰、副産石膏、焼却灰、燃えがら、粉塵、ばい塵、汚泥類、廃残土、および廃砂のうち、いずれか1種または複数種に限定されない。
なお、細骨材として利用する原料は、自治体や企業などの排出元の責任で無害化処理が施されたものであってもよく、このような原料を利用する場合には、入手した後に無害化処理を施さずに利用してもよい。
Further, the fine aggregate is not limited to any one or plural kinds of coal ash, by-product gypsum, incinerated ash, cinder, dust, dust, sludge, waste soil, and waste sand.
In addition, the raw materials used as fine aggregates may be those that have been detoxified at the responsibility of the emission source of local governments or companies. It may be used without performing the conversion process.
また、第1実施形態では、魚礁用ブロックの形状として、自然石に似せて成形されたものを説明したが、魚礁用ブロックの形状はこれに限定されるものではない。
例えば、図4(a)、(b)、および(c)に示す魚礁用ブロック40のように、放射状に4つの脚部45が延びた形状のものであってもよい。
In the first embodiment, the shape of the fish reef block has been described to resemble a natural stone, but the shape of the fish reef block is not limited to this.
For example, it may have a shape in which four legs 45 extend radially like a fish reef block 40 shown in FIGS. 4 (a), 4 (b), and 4 (c).
また、例えば、図5(a)、(b)、および(c)に示す魚礁用ブロック50のような形状のものであってもよい。魚礁用ブロック50は、基部51、鉄筋部53、および貝殻魚礁ロール55から構成される。基部51は、第1実施形態のコンクリート組成物からなる六面体のコンクリート構造物であり、内部に空洞部が形成され、空洞に通じる開口が各々の面に形成されたものである。貝殻魚礁ロール55は、セメントと貝殻を混ぜ合わせて、鉄筋部53に絡めて硬化させたものであり、基部51の空洞部内に固定されている。 Further, for example, it may be shaped like a fish reef block 50 shown in FIGS. 5 (a), 5 (b), and 5 (c). The reef block 50 includes a base 51, a reinforcing bar 53, and a shellfish reef roll 55. The base 51 is a hexahedral concrete structure made of the concrete composition according to the first embodiment, in which a cavity is formed inside and an opening leading to the cavity is formed on each surface. The shellfish reef roll 55 is a mixture of cement and shells, entangled with the reinforcing bar 53 and hardened, and is fixed in the cavity of the base 51.
このような貝殻魚礁ロール55を備えていると、貝殻魚礁ロール55に形成されている隙間が魚介類の産卵場所として利用される。
また、例えば、図6(a)に示す魚礁用ブロック60のように、碁盤目状の溝が形成されていてもよい。この魚礁用ブロック60の表面には、図6(b)および(c)に示すように、縦横とも10cm間隔で、深さが5mm〜15mmの溝65が形成されている。このような溝65は、上記実施形態で例示した魚礁用ブロック10,20,30,40,50の表面に形成されていてもよい。
When such a shellfish reef roll 55 is provided, the gap formed in the shellfish reef roll 55 is used as a spawning place for seafood.
Further, for example, a grid-like groove may be formed like a fish reef block 60 shown in FIG. As shown in FIGS. 6B and 6C, grooves 65 having a depth of 5 mm to 15 mm are formed on the surface of the fish reef block 60 at intervals of 10 cm both vertically and horizontally. Such a groove | channel 65 may be formed in the surface of the block 10, 20, 30, 40, 50 for fish reef illustrated by the said embodiment.
あるいは、このような直線状の溝に限らず、曲線状の溝が形成されていてもよいし、魚礁用ブロックの表面に多数の穴(窪み)が形成されていてもよい。このような穴を形成する場合でも、個々の穴については、深さを5mm〜15mm程度にしておくとよい。 Or not only such a linear groove | channel but a curved groove | channel may be formed, and many holes (dent) may be formed in the surface of the block for fish reefs. Even when such a hole is formed, the depth of each hole is preferably about 5 mm to 15 mm.
このような溝や穴が形成された魚礁用ブロック60であれば、溝や穴にサンゴを接着剤で固定した状態で海中に設置すると、従来品に比べ、サンゴを魚礁ブロックに早く定着させることができる。 With the reef block 60 having such grooves and holes formed, the coral can be fastened to the reef block faster than conventional products when installed in the sea with the corals fixed in the grooves and holes with an adhesive. Can do.
また、藻類、サンゴのポリプ、海草の胞子、および魚介類の卵がその溝や穴に入り込んで、そのまま定着するため、溝や穴が形成されていないものに比べ、海草、魚介類およびサンゴの繁殖を促すことができる。 In addition, algae, coral polyps, seaweed spores, and seafood eggs enter the grooves and holes and settle as they are, so that seaweeds, seafood and corals are more stable than those without grooves or holes. It can encourage breeding.
また、上記各実施形態で例示した魚礁用ブロック10,20,30,40,50,60、および魚礁用ブロックユニット15は、魚礁として利用する態様を説明したが、これに限定されるものではない。例えば、産卵礁として利用してもよい。 Moreover, although the fish reef blocks 10, 20, 30, 40, 50, 60 and the fish reef block unit 15 exemplified in the above embodiments have been described as being used as fish reefs, the present invention is not limited thereto. . For example, it may be used as a spawning reef.
また、上記の第1実施形態では、破砕物を面取り加工する際に、研磨材として鋼球を利用していたが、研磨材として利用するものの形態は、これに限定されるものではない。例えば、図7(a)〜(h)に示すような形態の研磨材を利用してもよい。 Moreover, in said 1st Embodiment, when crushing a crushing thing, the steel ball was utilized as an abrasive | polishing material, However, The form of what is utilized as an abrasive | polishing material is not limited to this. For example, you may utilize the abrasive | polishing material of a form as shown to Fig.7 (a)-(h).
図7(a)に示す研磨材70aは、鋼球の表面に一定間隔の幅狭の溝が刻設されている。図7(b)に示す研磨材70bは、鋼球の表面に鱗状の凹凸が刻設されている。図7(c)に示す研磨材70cは、鋼球の表面に複数のディンプルが形成されている。図7(d)に示す研磨材70dは、鋼球の表面に長さ1〜3mm程度の先端が丸い略釣鐘状の突起が多数放射状に設けられている。図7(e)に示す研磨材70eは、鋼球の表面に長さ1〜3mm程度の略円錐または略多角錐状の突起が多数放射状に設けられている。 In the abrasive 70a shown in FIG. 7A, narrow grooves having a constant interval are formed on the surface of a steel ball. As for the abrasive 70b shown in FIG.7 (b), the scale-like unevenness | corrugation is engraved on the surface of the steel ball. In the abrasive 70c shown in FIG. 7C, a plurality of dimples are formed on the surface of a steel ball. A polishing material 70d shown in FIG. 7 (d) is provided with a large number of substantially bell-shaped projections having a rounded tip having a length of about 1 to 3 mm radially on the surface of a steel ball. The abrasive 70e shown in FIG. 7 (e) is provided with a large number of substantially conical or substantially polygonal conical projections having a length of about 1 to 3 mm on the surface of a steel ball.
図7(f)に示す研磨材70fは、ドリル形状であり、略円柱形状の鋼片の側面上に螺旋状の溝が設けられている。図7(g)に示す研磨材70gは、タップ形状であり、円筒の鋼片の側面一端をその円筒の底面に略垂直な平面で切断した形状をしている。図7(h)に示す研磨材70hは、略円柱形状の鋼片の側面上に、研磨材70gに比べ狭い間隔で螺旋状の溝が設けられている。 The abrasive 70f shown in FIG. 7 (f) has a drill shape, and a spiral groove is provided on the side surface of a substantially cylindrical steel piece. The abrasive 70g shown in FIG. 7 (g) has a tap shape and is formed by cutting one end of a side surface of a cylindrical steel piece along a plane substantially perpendicular to the bottom surface of the cylinder. In the abrasive 70h shown in FIG. 7 (h), spiral grooves are provided on the side surface of the substantially cylindrical steel piece at a narrower interval than the abrasive 70g.
以上のような研磨材70a〜70hを利用しても、第1実施形態において説明した研磨材4を利用した場合と同様か、それ以上の効率で面取り加工をすることができる。
また、上述の第1実施形態では、コンクリート組成物からなる魚礁用ブロックについて説明したが、現場打ちの施工によって、このコンクリート組成物から様々なコンクリート構造物を成形してもよい。
Even if the abrasives 70a to 70h as described above are used, the chamfering can be performed with the same or higher efficiency as when the abrasive 4 described in the first embodiment is used.
Moreover, although the above-mentioned 1st Embodiment demonstrated the block for fish reef which consists of a concrete composition, you may shape | mold various concrete structures from this concrete composition by construction on the spot.
現場打ちの施工の具体的な方法としては、例えば、コンクリート組成物を離型剤が塗布された型枠に打ち込み、養生させることによってコンクリート構造物を成形する、という方法がある。このような方法で成形できるコンクリート構造物としては、橋脚、家屋の基礎等がある。このようなコンクリート構造物であれば、従来品に比べ強度が高いものとすることができる。 As a concrete method of on-site construction, there is, for example, a method in which a concrete structure is formed by driving a concrete composition into a formwork coated with a release agent and curing it. Concrete structures that can be formed by such methods include piers, house foundations, and the like. Such a concrete structure can have higher strength than conventional products.
また、山肌における落石や地すべり等を防止するために、コンクリート組成物を山肌の法面に吹き付けてコンクリートコーティングを施してもよい。山肌の法面にコンクリート組成物を吹き付ける際には、例えば、第2実施形態および第3実施形態で説明した吹き付け装置を利用すればよい。このように本発明のコンクリート組成物を利用すれば、強化繊維が含まれていないコンクリート組成物に比べ、強度に優れた落石防止構造を山肌の法面に構築することができる。 Moreover, in order to prevent falling rocks and landslides on the mountain surface, the concrete composition may be sprayed onto the slope of the mountain surface to provide a concrete coating. When spraying the concrete composition on the slope of the mountain surface, for example, the spraying device described in the second embodiment and the third embodiment may be used. Thus, if the concrete composition of this invention is utilized, compared with the concrete composition which does not contain a reinforced fiber, the fall prevention structure excellent in intensity | strength can be constructed on the slope of a mountain surface.
また、陸屋根において溜まった雨水が家屋内に浸水することを防止するために、コンクリート組成物を陸屋根の表面に吹き付けてもよい。このように本発明のコンクリート組成物を陸屋根の表面に吹き付ければ、強化繊維が含まれていないコンクリート組成物に比べ、経年変化によるひび割れなどが発生しにくくなり、耐久性に優れた防水構造を構成することができる。 Moreover, in order to prevent rainwater collected on the land roof from entering the house, a concrete composition may be sprayed on the surface of the land roof. In this way, if the concrete composition of the present invention is sprayed on the surface of a flat roof, cracks due to secular change are less likely to occur compared to a concrete composition that does not contain reinforcing fibers, and a waterproof structure with excellent durability is achieved. Can be configured.
また、左官工事における塗り工事、土木工事における土間コンクリート均し工事等の施工では、セメントと細骨材を混練したものを利用しているが、この場合に本発明のコンクリート組成物に配合されていた細骨材を利用してもよい。 In addition, in the construction work such as plastering work in plastering work and soil concrete leveling work in civil engineering work, a mixture of cement and fine aggregate is used. In this case, it is blended in the concrete composition of the present invention. Fine aggregate may be used.
1・・・面取り加工装置、3・・・面取り加工機、4,70a,70b,70c,70d,70e,70f,70g,70h・・・研磨材、3a・・・ドラム支持部、3b・・・回動ドラム、3c・・・回転軸、3d・・・攪拌羽根、5・・・ベルトコンベア、7・・・磁気選別機、9・・・回収容器、10,20,30,40,50,60・・・魚礁用ブロック、15・・・魚礁用ブロックユニット、17・・・連結金具、18・・・固定金具、21a,31a,51・・・基部、21b,31b・・・被覆層、45・・・脚部、53・・・鉄筋部、55・・・貝殻魚礁ロール、65・・・溝。 DESCRIPTION OF SYMBOLS 1 ... Chamfering processing apparatus, 3 ... Chamfering processing machine, 4,70a, 70b, 70c, 70d, 70e, 70f, 70g, 70h ... Abrasive material, 3a ... Drum support part, 3b ... Rotating drum, 3c ... rotating shaft, 3d ... stirring blade, 5 ... belt conveyor, 7 ... magnetic sorter, 9 ... collection container, 10, 20, 30, 40, 50 , 60 ... Fish reef block, 15 ... Fish reef block unit, 17 ... Connection fitting, 18 ... Fixing fitting, 21a, 31a, 51 ... Base, 21b, 31b ... Covering layer 45 ... Legs, 53 ... Reinforcing bars, 55 ... Shellfish reef rolls, 65 ... Grooves.
Claims (8)
貝殻類、廃プラスチック類、ゴムくず、金属くず、ガラスくず、コンクリートくず、陶磁器くず、および瓦礫類の中から選ばれる少なくとも1種を破砕することによって得られた破砕物からなる粗骨材と、
石炭灰、副産石膏、焼却灰、燃えがら、粉塵、ばい塵、汚泥類、廃残土、および廃砂の中から選ばれる少なくとも1種の細骨材と、
高炉スラグ微粉末、フライアッシュ、およびシリカフュームの中から選ばれる少なくとも1種の混和材と、
ガラス繊維および炭素繊維の中から選ばれる少なくとも1種の強化繊維と
を含むことを特徴とするコンクリート組成物。 Cement,
Coarse aggregate made of crushed material obtained by crushing at least one selected from shells, waste plastics, rubber scraps, metal scraps, glass scraps, concrete scraps, ceramic scraps, and rubbles;
At least one fine aggregate selected from coal ash, by-product gypsum, incinerated ash, cinder, dust, dust, sludge, waste soil, and waste sand;
At least one admixture selected from blast furnace slag fine powder, fly ash, and silica fume;
A concrete composition comprising: at least one reinforcing fiber selected from glass fiber and carbon fiber.
ことを特徴とする請求項1に記載のコンクリート組成物。 The concrete composition according to claim 1, wherein the coarse aggregate is obtained by chamfering the corners of the crushed material by stirring the crushed material together with an abrasive.
炭素繊維が添加されたセメントを硬化させてなり、前記基部を被覆する第1被覆層と
を備えることを特徴とするコンクリート構造物。 A base formed by curing the concrete composition according to claim 1 or 2,
A concrete structure comprising: a first coating layer formed by curing cement to which carbon fiber is added and covering the base.
魚粉、炭酸カルシウム、窒素質肥料、リン酸質肥料、ケイ酸質肥料、ビタミン類、およびミネラル成分のうち、少なくとも1つが添加されたセメントを硬化させてなり、前記基部を被覆する第2被覆層と
を備えることを特徴とするコンクリート構造物。 A base formed by curing the concrete composition according to claim 1 or 2,
A second coating layer that hardens cement added with at least one of fish meal, calcium carbonate, nitrogenous fertilizer, phosphate fertilizer, siliceous fertilizer, vitamins, and mineral components, and covers the base. A concrete structure comprising:
ことを特徴とする魚礁用ブロック。 It consists of the concrete structure of Claim 3 or Claim 4. The block for fish reefs characterized by the above-mentioned.
ことを特徴とするコンクリート施工方法。 A concrete construction method characterized by forming a concrete structure from a concrete composition according to claim 1 or 2 by on-site construction.
ことを特徴とするコンクリート施工方法。 The concrete composition of Claim 1 or Claim 2 is sprayed on the slope of a mountain surface. The concrete construction method characterized by the above-mentioned.
ことを特徴とするコンクリート施工方法。 A concrete construction method comprising spraying the concrete composition according to claim 1 or 2 onto a surface of a flat roof.