JP2010084433A - Method of reinforcing corrugated asbestos slate, and reinforcing structure for reinforcing existing corrugated asbestos slate - Google Patents
Method of reinforcing corrugated asbestos slate, and reinforcing structure for reinforcing existing corrugated asbestos slate Download PDFInfo
- Publication number
- JP2010084433A JP2010084433A JP2008255036A JP2008255036A JP2010084433A JP 2010084433 A JP2010084433 A JP 2010084433A JP 2008255036 A JP2008255036 A JP 2008255036A JP 2008255036 A JP2008255036 A JP 2008255036A JP 2010084433 A JP2010084433 A JP 2010084433A
- Authority
- JP
- Japan
- Prior art keywords
- slate
- reinforcing
- layer
- coating
- corrugated asbestos
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、既設の波形石綿スレート（以下「波形スレート」と称する。）の補強方法及び既設の波形スレートを補強した補強構造体に関する。
更に詳しくは、既設の波形スレートに対し衝撃や荷重が加わったとしても完全な破断を防止する、または、完全な破断を防止し且つ曲げ強度を向上させる、波形スレートの補強方法及び既設の波形スレートを補強した補強構造体に関する。
The present invention relates to a method for reinforcing an existing corrugated asbestos slate (hereinafter referred to as “corrugated slate”) and a reinforcing structure in which the existing corrugated slate is reinforced.
In more detail, even if an impact or load is applied to an existing corrugated slate, the corrugated slate reinforcement method and the existing corrugated slate that prevent complete fracture or prevent complete fracture and improve bending strength. The present invention relates to a reinforced structure that reinforces.
波形スレートは、安価で施工が容易なため、工場や倉庫等の屋根材として広く使用されており、このような既設の波形スレートは設置環境や経年劣化等の理由から補修が必要となる場合がある。 Since corrugated slate is inexpensive and easy to construct, it is widely used as a roofing material in factories and warehouses. Such existing corrugated slate may need to be repaired for reasons such as installation environment or aging deterioration. is there.
このような劣化した既設の波形スレートを補修する方法として、例えば、下記特許文献１に記載されたようなスレート補強工法が提案されている。
下記特許文献１記載の工法によれば、設置されたスレートの腐食部分を剥落させた後、当該スレートに硬質ウレタンフォーム層を形成することでスレートの寿命を延長することができる。
As a method of repairing such a deteriorated existing waveform slate, for example, a slate reinforcement method as described in Patent Document 1 has been proposed.
According to the construction method described in the following Patent Document 1, after the corrosion portion of the installed slate is peeled off, the life of the slate can be extended by forming a hard urethane foam layer on the slate.
特許文献１記載のような方法を用いて屋根の波形スレートを補修する場合、一般的に波形スレートの上に足場を組んで作業を行うが、該足場から作業者や作業に使用する物等が波形スレート上に落下する事故が起きることがある。
このような事故が発生すると、波形スレートが破断し、破断箇所から作業者等が波形スレート下へ落下する危険性がある。また、落下した作業者や物、スレートの破片等によって波形スレート下にいる者や物にも被害が及ぶ危険性もある。更に、既設の波形スレートが経年劣化等により曲げ強度が低下していた場合は、破断の可能性がより高くなる。
When repairing a corrugated slate on a roof using a method as described in Patent Document 1, generally, a scaffold is assembled on the corrugated slate, and an operator, an object used for the work, or the like is used from the scaffold. Accidents that fall on corrugated slate may occur.
When such an accident occurs, the corrugated slate breaks, and there is a risk that an operator or the like falls from the broken portion to the corrugated slate. In addition, there is a risk that a worker or an object that falls under a corrugated slate may be damaged by a fallen worker or object or a piece of slate. Furthermore, when the existing corrugated slate has a reduced bending strength due to aging or the like, the possibility of breakage becomes higher.
なお、落下防止のみを目的とするのであれば足場間にネットを張れば事足りるが、該ネットが波形スレート補強作業の邪魔となる。
このため、波形スレートを補修する作業にあたり、作業を妨げず且つ前記のような施工中の事故を防止する方法が求められていた。
For the purpose of preventing the fall only, it is sufficient to put a net between the scaffolds, but this net interferes with the waveform slate reinforcement work.
For this reason, in the work which repairs a waveform slate, the method of preventing the accident under construction as mentioned above was calculated | required, without disturbing work.
（発明の目的）
そこで、本発明の目的は、既設の波形スレートに対し衝撃や荷重が加わったとしても完全な破断を防止する、または、完全な破断を防止し且つ曲げ強度を向上させる、波形スレートの補強方法及び既設の波形スレートを補強した補強構造体を提供することにある。
また、本発明の他の目的としては、耐候性または熱反射性、耐候性および熱反射性を備える前記波形スレートの補強方法及び既設の波形スレートを補強した補強構造体を提供することにある。
(Object of invention)
Therefore, an object of the present invention is to provide a method for reinforcing a corrugated slate that prevents complete fracture even when an impact or load is applied to an existing corrugated slate, or prevents complete fracture and improves bending strength, and An object of the present invention is to provide a reinforcing structure in which an existing corrugated slate is reinforced.
Another object of the present invention is to provide a method for reinforcing the corrugated slate having weather resistance or heat reflectivity, weather resistance and heat reflectivity, and a reinforcing structure reinforced with an existing corrugated slate.
上記目的を達成するために講じた本発明の手段は次のとおりである。
本発明は、波形スレート表面に塗剤を塗布し、該塗剤によって少なくとも表面の劣化部分を固めて下地層又は下地膜を形成する工程と、下地層又は下地膜が形成された前記スレートの山部にアラミド繊維又はカーボン繊維の帯状物を貼り付ける工程と、を含む、既設の波形スレートの補強方法である。
The means of the present invention taken to achieve the above object are as follows.
The present invention includes a step of applying a coating agent to a corrugated slate surface, solidifying at least a deteriorated portion of the surface with the coating agent to form a base layer or a base film, and a slate pile on which the base layer or base film is formed. A method of reinforcing an existing corrugated slate, including a step of affixing a strip of aramid fiber or carbon fiber to a portion.
なお、前記波形スレート表面に塗布する塗剤は、前記スレート内部に浸透して硬化する液状塗剤であり、該塗剤は前記スレート表面或いは前記スレートの劣化部分、または前記スレート表面と劣化部分に加えて健全部分の一部にまで浸透した後、浸透箇所が硬化して補強部を形成するものであってもよい。 The coating applied to the corrugated slate surface is a liquid coating that penetrates and cures inside the slate, and the coating is applied to the slate surface, the deteriorated portion of the slate, or the slate surface and the deteriorated portion. In addition, after the penetration to a part of the healthy portion, the penetration portion may be cured to form a reinforcing portion.
更に、前記既設の波形スレートの補強方法は、波形スレートの山部にアラミド繊維又はカーボン繊維の帯状物を貼り付ける工程後に、下地層又は下地膜が形成された前記スレート表面及び貼り付けた帯状物の上から耐候性または／および熱反射性を備える塗剤を塗布して表層を形成する工程を含むものであってもよい。 Furthermore, the existing corrugated slate reinforcing method includes the step of pasting a strip of aramid fiber or carbon fiber on the peak portion of the corrugated slate, and the pasted strip and the slate surface on which the base layer or base film is formed. It may include a step of forming a surface layer by applying a coating having weather resistance and / or heat reflectivity from above.
本発明は、既設の波形スレートを補強した補強構造体であって、補強構造体は、波形スレート表面へ前記スレート内部に浸透して硬化する液状塗剤を塗布して形成された下地層又は下地膜と、前記下地層又は下地膜のうち、前記スレートの山部の長さ方向にわたって貼り付けられたアラミド繊維又はカーボン繊維の帯状物と、を備えており、前記下地層又は下地膜は、塗布した塗剤が、前記スレート表面、前記スレート表面と前記スレートの劣化部分、または、前記スレート表面と劣化部分に加えて健全部分の一部、のいずれかの箇所に浸透した後、浸透箇所が硬化して補強部となり、少なくとも表面の劣化部分が固めてある、既設の波形スレートを補強した補強構造体である。 The present invention is a reinforcing structure in which an existing corrugated slate is reinforced, and the reinforcing structure is formed by applying a liquid coating that penetrates and cures into the corrugated slate surface into the inside of the slate. A base film and a strip of aramid fiber or carbon fiber pasted over the length direction of the slate peak portion of the base layer or base film, and the base layer or base film is coated After the applied coating material penetrates into any part of the slate surface, the slate surface and a deteriorated part of the slate, or a part of a healthy part in addition to the slate surface and the deteriorated part, the penetration part is cured. Thus, the reinforcing structure is formed by reinforcing an existing corrugated slate in which at least a deteriorated portion of the surface is hardened.
また、本発明は、既設の波形スレートを補強した補強構造体であって、補強構造体は、波形スレート表面へ前記スレート内部に浸透して硬化する液状塗剤を塗布して形成された下地層又は下地膜と、前記下地層又は下地膜のうち、前記スレートの山部の長さ方向にわたって貼り付けられたアラミド繊維又はカーボン繊維の帯状物と、前記下地層又は下地膜及び帯状物による表面の凹凸を整える塗剤を、下地層又は下地膜及び帯状物の表面を覆うよう塗布して形成された中間層と、耐候性または／および熱反射性を備える塗剤を、中間層を覆うように塗布して形成された表層と、を備えており、前記下地層又は下地膜は、塗布した塗剤が、前記スレート表面、前記スレート表面と前記スレートの劣化部分、または、前記スレート表面と劣化部分に加えて健全部分の一部、のいずれかの箇所に浸透した後、浸透箇所が硬化して補強部となり、少なくとも表面の劣化部分が固めてある、既設の波形スレートを補強した補強構造体である。 Further, the present invention is a reinforcing structure in which an existing corrugated slate is reinforced, and the reinforcing structure is formed by applying a liquid coating material that penetrates and hardens into the corrugated slate surface. Alternatively, a base film, a band of aramid fibers or carbon fibers attached over the length direction of the slate peak portion of the base layer or base film, and a surface of the base layer or base film and the strip An intermediate layer formed by applying a coating agent for adjusting irregularities so as to cover the surface of the base layer or the base film and the belt-like material, and a coating agent having weather resistance or / and heat reflectivity so as to cover the intermediate layer A surface layer formed by coating, and the base layer or base film is formed by applying the coating agent to the slate surface, the slate surface and the deteriorated portion of the slate, or the slate surface and the deteriorated portion. In addition, after infiltrating any part of the healthy part, the infiltrated part is cured and becomes a reinforcing part, and at least the deteriorated part of the surface is solidified, and this is a reinforcing structure reinforced with an existing corrugated slate. .
本明細書及び本特許請求の範囲における波形スレートとは、例えば、その基材が石綿を含むセメント、けい酸カルシウム、石膏等であり、横断方向において山と谷が連続する波状の板体であって、波の形状が側面視で円弧状、または、一山又は一谷ごとに１又は２以上の角部を有するものを含む意味で使用している。また、「山部」は、前記スレートの山側（例えば上方に膨らんだ部分）を指す意味で使用している。
更に、補強の対象となる波形スレートは、屋根材として使用しているもののみならず、壁材として使用しているものをも含む。
The corrugated slate in the present specification and claims is, for example, a corrugated plate whose base material is cement containing asbestos, calcium silicate, gypsum, etc., and peaks and valleys are continuous in the transverse direction. Thus, the shape of the wave is used in the meaning of including an arc shape in a side view or one having one or two or more corners per mountain or valley. The “mountain portion” is used to indicate the mountain side of the slate (for example, a portion that swells upward).
Furthermore, the corrugated slate to be reinforced includes not only those used as roofing materials but also those used as wall materials.
基材内部に浸透して硬化する液状塗剤は、例えば、ウレタン系又はエポキシ系の樹脂塗剤が挙げられ、ＳＲプライマー（ロックペイント株式会社製品）、ダイヤプライマー（恒和化学株式会社製品）、ＳＫスーパーシーラー（エスケー化研製品）等が好適に使用されるが、これに限定するものではなく、同様の効果を有する他の塗剤を使用してもよい。 Examples of the liquid coating that penetrates into the substrate and cures include a urethane-based or epoxy-based resin coating, SR primer (Rock Paint Co., Ltd. product), diamond primer (Kohwa Chemical Co., Ltd. product), SK super sealer (SK Kaken product) or the like is preferably used, but is not limited thereto, and other coating agents having the same effect may be used.
劣化部分とは、波形スレートのうち、雨や日光等の影響により表面が劣化して繊維等が露出したり、凹凸が生じたり、あるいは経時的硬化によりセメントが収縮して表面がひび割れたり、波形スレートの内部側がポーラス状態になったり、また、黒ずんだり、苔や藻が発生した部分等をいう。一方、健全部分とは、前記劣化部分を除く部分を示す意味で使用している。 The deteriorated part is a corrugated slate whose surface deteriorates due to the influence of rain, sunlight, etc., and fibers are exposed, unevenness occurs, or the cement shrinks due to hardening over time and the surface cracks. This refers to the part where the inside of the slate is in a porous state, darkened, or where moss or algae are generated. On the other hand, the healthy part is used to indicate a part excluding the deteriorated part.
耐候性または／および熱反射性を備えるとは、耐候性または熱反射性のいずれか一方を備えることもあるし、あるいは、耐候性および熱反射性の両方を備えるということもある、という意味で使用している。 Having weather resistance and / or heat reflectivity means having either weather resistance or heat reflectivity, or having both weather resistance and heat reflectivity. I use it.
なお、塗布とは、吹き付け又は刷毛等の公知の手段によるものを含む意味で使用している。 In addition, it has used by the meaning including what is by application | coating by well-known means, such as spraying or a brush.
本発明に係る波形スレートの補強方法の手順を説明する。
（１）既設の（施工前の）波形スレート表面に塗剤を塗布し、少なくとも表面の劣化部分を固めた下地層又は下地膜を形成する。
（２）前記下地層又は下地膜を形成した施工後のスレートのうち、少なくとも山部に帯状物を貼り付ける。
（３）なお、前記塗剤が施工前のストレート内部に浸透して硬化する液状塗剤であれば、該塗剤が施工前のスレート表面、施工前のスレート内の劣化部分、または前記表面及び劣化部分に加えて健全部分に達するまで浸透し、浸透した塗剤が硬化した後に、帯状物を貼り付ける。
（４）更に、施工後のスレートの山部へ帯状物を貼り付けた後に、貼り付けた帯状物の上から耐候性または／および熱反射性を備える塗剤を塗布し、表層を形成する場合もある。
The procedure of the waveform slate reinforcement method according to the present invention will be described.
(1) A coating agent is applied to an existing (before construction) corrugated slate surface to form a base layer or base film in which at least a deteriorated portion of the surface is hardened.
(2) A belt-like material is attached to at least the mountain portion of the slate after the construction on which the base layer or the base film is formed.
(3) If the coating material is a liquid coating material that penetrates and cures inside the straight before construction, the coating material is a slate surface before construction, a deteriorated portion in the slate before construction, or the surface and It penetrates until it reaches the healthy part in addition to the deteriorated part, and after the penetrating coating has hardened, the band is pasted.
(4) Furthermore, after a strip is pasted on the slate peak after construction, a coating having weather resistance or / and heat reflectivity is applied from above the pasted strip to form a surface layer. There is also.
（作 用）
前記補強方法を行った波形スレートは、その表面に塗剤を塗布して下地層又は下地膜を形成してあるので、少なくとも表面の劣化部分が固まる。
劣化した波形スレートに直接帯状物を貼り付けた場合、波形スレート表面に衝撃又は荷重が加わると波形スレート表面の劣化部分と帯状物が剥離しやすいが、本願方法では前記の通り少なくとも表面の劣化部分が固めてあるので、波形スレート表面と帯状物が剥離しにくくなる。
(Work)
Since the corrugated slate subjected to the reinforcing method has a base layer or base film formed by applying a coating on the surface, at least the deteriorated portion of the surface is hardened.
When a strip is pasted directly on a deteriorated corrugated slate, when an impact or load is applied to the corrugated slate surface, the corrugated slate surface deteriorates easily from the strip. Is hardened, it becomes difficult for the corrugated slate surface and the strip to peel off.
また、工事の際に、前記補強を行った波形スレート上に作業者等が落下し、衝撃や重量により該波形スレートが割れたとしても、貼り付けられた帯状物が該波形スレートの完全破断を防止し、且つ当該落下物を受け止める。 In addition, even when an operator falls on the corrugated slate to which the reinforcement is performed and the corrugated slate is cracked due to an impact or weight, the attached band-like object completely breaks the corrugated slate. Prevent and catch the fallen object.
なお、貼り付けた帯状物は、波形スレートを補強する作業の邪魔とならず、作業終了後も貼り付けたままにしておけば既設の波形スレートの耐久性が向上する。 Note that the pasted strip does not interfere with the work of reinforcing the corrugated slate, and the durability of the existing corrugated slate is improved if it is kept pasted after the work is completed.
更に、波形スレート表面に塗布する塗剤が、波形ストレート内部に浸透して硬化する液状塗剤である場合は、該塗剤が波形スレート表面或いは波形スレート内部の劣化部分、または波形スレート表面と劣化部分に加えて健全部分の一部にまで浸透し、その後浸透部分が硬化して補強層となる。 Furthermore, when the coating material applied to the corrugated slate surface is a liquid coating material that penetrates and cures inside the corrugated straight, the coating material deteriorates with the corrugated slate surface, the deteriorated portion inside the corrugated slate, or the corrugated slate surface. In addition to the part, it penetrates to a part of the healthy part, and then the penetrated part is cured to become a reinforcing layer.
下地層又は下地膜及び貼り付けた帯状物へ耐候性または／および熱反射性を備える塗剤を塗布して表層を形成した場合、既設の波形スレートの耐久性向上に加えて、耐候性または／および熱反射性が向上する。 When a surface layer is formed by applying a coating having weather resistance or / and heat reflectivity to the base layer or base film and the attached band-like material, in addition to improving the durability of the existing corrugated slate, And heat reflectivity is improved.
本発明によれば、次の効果を奏する。
（１）本発明に係る波形スレートの補強方法によれば、簡易な工事でありながら、既設の劣化した波形スレートの耐久性及び耐破断性を向上させることができる。この結果、特に屋根の工事中に、工事作業者や物が屋根材である波形スレート上へ落下等して該波形スレートが割れたとしても完全に破断しないか又は破断しにくいので、工事作業者等の屋内への落下を防止できる。ひいては、該波形スレートが割れた箇所の下の屋内にいる者又は物に対する落下物衝突の被害も防止できる。
The present invention has the following effects.
(1) According to the method for reinforcing a corrugated slate according to the present invention, it is possible to improve the durability and rupture resistance of an existing deteriorated corrugated slate while being a simple construction. As a result, especially during the construction of the roof, even if the corrugated slate breaks due to the construction worker or objects falling onto the corrugated slate, which is the roofing material, it will not break completely or is difficult to break. Can be prevented from falling indoors. As a result, it is possible to prevent damage caused by a falling object colliding with a person or an object indoors under the broken portion of the corrugated slate.
（２）下地層又は下地膜の作成の際に、波形スレート表面に塗布する塗剤が、波形ストレート内部に浸透して硬化する液状塗剤であれば、該塗剤が波形スレート表面に下地層又は下地膜を作成すると共に、波形スレート内の劣化部分、または劣化部分及び健全部分に達するまで浸透し、浸透した塗剤が硬化して該劣化部分等を補強するので、貼り付けられた帯状物による耐破断性の向上と相俟って、既設の波形スレートの強度及び耐久性が向上する。つまり、既設の波形スレートを引き続き使用することができる。
この結果、全面張替工事を行った場合に廃棄処分となる既設の波形スレートをそのまま有効利用できるので、廃棄物の発生を抑制し、ひいては、新たな産業廃棄物処分場等の開発の必要性を低減させ、環境負荷の低減に寄与する効果が期待できる。
(2) If the coating applied to the corrugated slate surface is a liquid coating that penetrates into the corrugated straight and cures when the base layer or the base film is created, the coating is applied to the corrugated slate surface. Or while creating a base film, it penetrates until it reaches the deteriorated part in the corrugated slate, or the deteriorated part and the healthy part, and the infiltrated coating hardens and reinforces the deteriorated part. The strength and durability of the existing corrugated slate are improved in combination with the improvement of the fracture resistance due to. That is, the existing waveform slate can be used continuously.
As a result, the existing corrugated slate that will be disposed of in the event of full-scale replacement work can be effectively used as it is, so it is possible to control the generation of waste and eventually develop a new industrial waste disposal site, etc. The effect which contributes to reduction of environmental load and reduction of environmental impact can be expected.
（３）下地層又は下地膜及び貼り付けた帯状物へ耐候性または／および熱反射性を備える塗剤を塗布して表層を形成した既設の波形スレートは、耐破断性の向上に加え、耐候性または／および熱反射性が向上する。該波形スレートによって、前記の効果に加え、建物内部の温度上昇または放熱、波形スレート表面の劣化が抑制される。 (3) The existing corrugated slate in which the surface layer is formed by applying a coating having weather resistance or / and heat reflectivity to the base layer or base film and the attached band-like material is not only improved in fracture resistance but also in weather resistance Or / and heat reflectivity are improved. In addition to the above effects, the waveform slate suppresses temperature rise or heat dissipation inside the building and deterioration of the surface of the waveform slate.
［第１実施形態］
本発明の第１実施形態を図面に基づき更に詳細に説明する。
図１は波形スレート構造１を示した斜視図、図２は図１に示す波形スレート構造１の山部を拡大した断面図である。
図１及び図２に示す波形スレート構造１について説明する。
なお、補強前の波形スレート１２は、数年間屋外に設置された石綿を含むセメントにより形成された波形の石綿スレートであって、その表面に劣化部分１２２が生じている。なお、劣化部分１２２よりも更に内奥部は、劣化状態にない健全部分１２４である。
[First Embodiment]
A first embodiment of the present invention will be described in more detail with reference to the drawings.
FIG. 1 is a perspective view showing a corrugated slate structure 1, and FIG. 2 is an enlarged cross-sectional view of a peak portion of the corrugated slate structure 1 shown in FIG.
The waveform slate structure 1 shown in FIGS. 1 and 2 will be described.
The corrugated slate 12 before reinforcement is a corrugated asbestos slate formed of cement containing asbestos that has been installed outdoors for several years, and has a deteriorated portion 122 on its surface. In addition, the inner back part is a healthy part 124 that is not in a deteriorated state than the deteriorated part 122.
波形スレート構造１における波形スレート１２は、山部１０と谷部１１が幅方向に連続する形状である。
波形スレート１２は、その表面（山部１０と谷部１１のいずれも含む）における劣化部分１２２と内部（及び非劣化の表面）の健全部分１２４の一部にわたって下地層１４が形成されている。
また、山部１０については、前記下地層１４表面に帯状物である補強帯１６が貼り付けてある。
The corrugated slate 12 in the corrugated slate structure 1 has a shape in which a crest 10 and a trough 11 are continuous in the width direction.
The corrugated slate 12 has an underlying layer 14 formed over a part of a deteriorated portion 122 on the surface (including both the peak portion 10 and the valley portion 11) and a healthy portion 124 inside (and a non-deteriorated surface).
In addition, for the peak portion 10, a reinforcing band 16, which is a band-like material, is attached to the surface of the base layer 14.
なお、本実施形態においては、前記補強帯はアラミド繊維で形成されているが、カーボン繊維で形成されたものであってもよい。 In addition, in this embodiment, although the said reinforcement belt | band | zone is formed with the aramid fiber, it may be formed with the carbon fiber.
下地層１４は、既設（施工前）の波形スレート１２表面に付着した苔や塵等の付着物除去や清掃あるいは洗浄作業を行わずに、波形スレート１２内部に浸透して硬化する液状塗剤（以下「浸透プライマー」という。）を直接を塗布して形成されている。該浸透プライマーは、波形スレート１２の劣化部分１２２及び健全部分１２４の一部まで浸透して硬化している（図２参照）。 The undercoat layer 14 is a liquid coating material that penetrates and cures inside the corrugated slate 12 without removing adhering substances such as moss and dust adhering to the surface of the existing corrugated slate 12 (before construction), cleaning, or washing. (Hereinafter referred to as “penetration primer”) is applied directly. The penetration primer penetrates to a part of the deteriorated portion 122 and the healthy portion 124 of the corrugated slate 12 and is cured (see FIG. 2).
なお、浸透プライマーとしては、浸透性がよい一液型の湿気硬化型ウレタン樹脂塗料が好適であり、その濃度は溶媒に対し１５％〜３０％の範囲内が好ましい。濃度が１５％未満の場合は、表面は塗装面が硬化せず、表面を塗ることはできても乾燥後に塗膜が無くなり、一方３０％を超えると健全部分まで浸透しにくくなる。より好ましくは、上記浸透プライマーの濃度が１５％〜２０％の範囲内である。
更には、浸透プライマーは二度塗りを行うことが好ましく、二度塗りを行う場合は、最初に波形スレートの健全部分まで浸透しやすい濃度に調整した浸透プライマーを塗布し、次に波形スレート表面の塗装面が硬化し乾燥後も塗膜が保たれる濃度に調整した浸透プライマーを塗布することがより好ましい。
The penetrating primer is preferably a one-component moisture-curing urethane resin paint having good penetrability, and its concentration is preferably in the range of 15% to 30% with respect to the solvent. When the concentration is less than 15%, the coated surface does not harden, and even if the surface can be coated, the coating film disappears after drying. On the other hand, when the concentration exceeds 30%, it does not easily penetrate into a healthy part. More preferably, the concentration of the penetrating primer is in the range of 15% to 20%.
Furthermore, it is preferable to apply the penetrating primer twice. In the case of applying the penetrating primer twice, first apply the penetrating primer adjusted to a concentration that allows easy penetration of the corrugated slate to the healthy part, and then apply the surface of the corrugated slate surface. It is more preferable to apply a penetrating primer adjusted to such a concentration that the coated surface is cured and the coating film is maintained even after drying.
補強帯１６は、所要の間隔を空けて配置されており、山部１０に形成された下地層１４上面に接着されている。
なお、本実施形態においては、所要の間隔として、山部１つ分の間隔をとって補強帯を配置している（図１参照）が、例えば、各山部毎に補強帯を配置することもできるし、山部２つ分以上の間隔とって補強帯を配置してもよい。更に、不規則な間隔で補強帯を配置することもできる。
また、補強帯は、波形スレートの破断防止及び設置コストの観点から、山部１つ分〜５つ分の間隔をとって配置することが好ましい。
The reinforcing bands 16 are arranged at a required interval and are bonded to the upper surface of the base layer 14 formed in the peak portion 10.
In the present embodiment, the reinforcing band is arranged as a required interval with an interval corresponding to one peak (see FIG. 1). For example, the reinforcing band is arranged for each peak. Alternatively, reinforcing bands may be arranged at intervals of two or more peaks. Furthermore, it is possible to arrange reinforcing bands at irregular intervals.
Moreover, it is preferable to arrange | position a reinforcement band at intervals for one to five peak parts from a viewpoint of the fracture | rupture prevention of a waveform slate and installation cost.
既設の波形スレート構造１の補強方法は、以下の手順にて行う。
（１）既設（施工前）の波形スレート構造１の波形スレート１２表面に浸透プライマーを塗布する。
このとき、前記浸透プライマーが、施工前の波形スレート１２の劣化部分１２２及び健全部分１２４の一部に達するまで浸透し、浸透した浸透プライマーにより該浸透箇所が硬化する。この結果、浸透プライマーの浸透箇所には、従前の波形スレート１２よりも補強されて曲げ強度が向上し、かつ、表面の劣化部分が固められた下地層１４が形成される。
The existing corrugated slate structure 1 is reinforced by the following procedure.
(1) A permeation primer is applied to the surface of the corrugated slate 12 of the existing corrugated slate structure 1 (before construction).
At this time, the penetration primer penetrates until it reaches a part of the deteriorated portion 122 and the healthy portion 124 of the waveform slate 12 before construction, and the penetration portion is cured by the penetrated penetration primer. As a result, the base layer 14 is formed at the permeation location of the permeation primer so as to be reinforced more than the conventional corrugated slate 12 to improve the bending strength and to harden the deteriorated portion of the surface.
（２）前記下地層１４が形成された後の波形スレート構造１のうち、所定の山部１０の長さ方向にわたり、補強帯１６を貼り付ける。 (2) In the corrugated slate structure 1 after the foundation layer 14 is formed, the reinforcing band 16 is pasted over the length direction of a predetermined peak portion 10.
（作 用）
前記補強方法を行った波形スレート１２は、その表面に塗剤を塗布して下地層１４が形成されたことにより、表面の劣化部分が固まる。
劣化した（施工前の）波形スレート１２に直接補強帯１６を貼り付けた場合、波形スレート１２表面に衝撃又は荷重が加わると波形スレート１２表面（特に劣化部分１２２）と補強帯１６が剥離しやすいという問題があった。
しかし、前記補強方法によれば、波形スレート１２表面の劣化部分１２２が固めてある（劣化部分１２２へ浸透した浸透プライマーが該箇所を硬化させている）ので、施工後の波形スレート表面と補強帯１６が剥離しにくくなる。
(Work)
The corrugated slate 12 subjected to the reinforcing method is coated with a coating material on the surface thereof to form the base layer 14, so that the deteriorated portion of the surface is hardened.
When the reinforcing band 16 is directly attached to the deteriorated (before construction) corrugated slate 12, the surface of the corrugated slate 12 (particularly the deteriorated portion 122) and the reinforcing band 16 easily peel off when an impact or load is applied to the corrugated slate 12 surface. There was a problem.
However, according to the reinforcing method, since the deteriorated portion 122 of the surface of the corrugated slate 12 is hardened (the permeation primer that has penetrated into the deteriorated portion 122 hardens the portion), the corrugated slate surface after the construction and the reinforcing band 16 becomes difficult to peel.
前記のとおり浸透プライマーが浸透した箇所が硬化するので、下地層１４は波形スレート１２の補強層となり、曲げ強度が向上した波形スレート１２と高強度（引張力の強さ）を備えるアラミド繊維で形成された補強帯１６との相乗効果によって、波形スレート１２の耐破断性が向上する。仮に、補強済みの波形スレート１２上へ作業者等が落下等し、その衝撃や重量により波形スレート１２が割れたとしても、貼り付けられた補強帯１６が波形スレート１２の破断を防止するか又は破断しにくくし、且つ当該落下物を受け止めることができる。 As described above, the portion penetrated by the penetrating primer is cured, so that the base layer 14 becomes a reinforcing layer of the corrugated slate 12, and is formed of the corrugated slate 12 with improved bending strength and aramid fibers having high strength (tensile strength). The rupture resistance of the corrugated slate 12 is improved by a synergistic effect with the reinforcing band 16 thus made. Even if an operator or the like falls onto the reinforced corrugated slate 12 and the corrugated slate 12 is broken due to the impact or weight, the attached reinforcing band 16 prevents the corrugated slate 12 from breaking or It is difficult to break and can catch the fallen object.
なお、貼り付けた補強帯１６は、補強作業の邪魔とならず、作業終了後も貼り付けたままにしておけば、既設の波形スレート１２の耐久性が向上する。 The pasted reinforcing band 16 does not interfere with the reinforcing work, and the durability of the existing corrugated slate 12 can be improved if the pasted band 16 is left stuck after the work is finished.
また、補強後は既設の波形スレート１２を引き続き使用することができるので、全面張替工事を行えば本来廃棄処分となるはずの既存の波形スレート１２をそのまま利用することになり、結果として、このような廃棄物の発生を抑制し、ひいては、新たな産業廃棄物処分場等の開発の必要性を低減させ、環境負荷の低減に寄与する効果が期待できる。 In addition, since the existing corrugated slate 12 can be continuously used after reinforcement, the existing corrugated slate 12 that should originally be disposed of when the entire surface is replaced is used as a result. The generation of such waste can be suppressed, and as a result, the need to develop a new industrial waste disposal site and the like can be reduced, and the effect of contributing to the reduction of environmental burden can be expected.
前記方法によれば、下地層１４を形成する際に、施工前の波形スレート１２表面に付着した苔や塵等の除去、洗浄等の作業工程が省略できるので、工期が短縮され、工費抑制に寄与するすることも期待できる。 According to the above method, when forming the base layer 14, work steps such as removal of moss and dust attached to the surface of the corrugated slate 12 before construction, cleaning, etc. can be omitted. We can also expect to contribute.
なお、波形スレートの谷部に補強帯を配置しても破断防止を達成することはできるが、一般的に谷部は山部よりも多くの塵等が溜まる又は付着して劣化部分が奥まで達しているか又は劣化部分の層が厚い場合が多く、このような谷部の付着物の上から浸透プライマーを塗布し劣化部分を補強するためには、山部に施工するよりもより多くの量の浸透プライマーを必要とする場合が多い。このため、波形スレートのうち山部にのみ補強帯を配置することが好ましい。 Although it is possible to prevent breakage even if a reinforcing band is disposed in the valley of the corrugated slate, generally, the valley has more dust or the like accumulated or adhered to the valley than the peak. It is often the case that the layer of the deteriorated part is reached or thicker, and in order to reinforce the deteriorated part by applying the penetrating primer on the deposits of such valleys, a larger amount than that applied to the peak part. Often requires a penetrating primer. For this reason, it is preferable to arrange the reinforcing band only in the peak portion of the waveform slate.
また、下地層１４を形成する際に、波形スレート１２表面の凹凸が無くなるか又は少なくなる程度の厚みとなるように浸透プライマーを塗布すれば、波形スレート１２表面の凹凸が無くなるか又は少なくなるので、貼り付けた補強帯１６の貼付面側と下地層１４表面の間に隙間が生じないか又は生じにくく密接して貼り付けられるので、両部材が剥離しにくくなる。 Further, when the base layer 14 is formed, if the penetration primer is applied so that the thickness of the corrugated slate 12 surface is eliminated or reduced, the corrugated slate 12 surface unevenness is eliminated or reduced. Since the gap is not formed or hardly adhered between the sticking surface side of the attached reinforcing band 16 and the surface of the base layer 14, the two members are hardly peeled off.
［第２実施形態］
本発明の第２実施形態を図面に基づき更に詳細に説明する。
図３は波形スレート構造２を示した斜視図、図４は図３に示す波形スレート構造２の山部を拡大した断面図である。
なお、図３及び図４に示す波形スレート構造２は、図１及び図２に示す波形スレート構造１と構造及び作用が一部共通するため当該部分の説明は省略し、相違する構造及び作用について以下説明する。
[Second Embodiment]
A second embodiment of the present invention will be described in more detail based on the drawings.
FIG. 3 is a perspective view showing the corrugated slate structure 2, and FIG. 4 is an enlarged cross-sectional view of the peak portion of the corrugated slate structure 2 shown in FIG.
The waveform slate structure 2 shown in FIGS. 3 and 4 is partially the same in structure and operation as the waveform slate structure 1 shown in FIGS. This will be described below.
波形スレート構造２における波形スレート２２は、山部２０と谷部２１が幅方向に連続する形状である。
波形スレート２２は、その表面（山部２０と谷部２１のいずれも含む）における劣化部分２２２と内部（及び非劣化の表面）の健全部分２２４の一部にわたって下地層２４が形成されている。
山部２０については、前記下地層２４表面に帯状物である補強帯２６が貼り付けてある。
下地層２４及び補強帯２６を覆うように中間層２７が形成され、中間層２７を覆うように表層２８が形成されている（図４参照）。
The corrugated slate 22 in the corrugated slate structure 2 has a shape in which a crest 20 and a trough 21 are continuous in the width direction.
The corrugated slate 22 has a base layer 24 formed over a part of a deteriorated portion 222 on the surface (including both the peak portion 20 and the valley portion 21) and a healthy portion 224 inside (and a non-deteriorated surface).
As for the mountain portion 20, a reinforcing band 26, which is a band-like material, is attached to the surface of the base layer 24.
An intermediate layer 27 is formed so as to cover the base layer 24 and the reinforcing band 26, and a surface layer 28 is formed so as to cover the intermediate layer 27 (see FIG. 4).
中間層２７は、ケミカルカチオン（ムライケミカルパック株式会社製品）を塗布して形成されており、下地層２４及び補強帯２６を覆うように塗布してある。ケミカルカチオンは、塗布後の塗装部が断熱効果を備える塗剤である。
なお、本実施の形態では、中間層の形成にケミカルカチオンを使用しているが、これに限定するものではなく、少なくともケミカルカチオンと同様、塗布によって基材表面の凹凸を整えて表層を形成しやすくする塗剤であればよい。
The intermediate layer 27 is formed by applying a chemical cation (product of Murai Chemical Pack Co., Ltd.), and is applied so as to cover the base layer 24 and the reinforcing band 26. A chemical cation is a coating agent in which the coated part after application has a heat insulating effect.
In this embodiment, the chemical cation is used for forming the intermediate layer. However, the present invention is not limited to this, and at least as in the case of the chemical cation, the surface layer is formed by adjusting the unevenness of the substrate surface by coating. Any coating agent that facilitates the coating may be used.
表層２８は、ケミカルパックＭＳ６０（ムライケミカルパック株式会社製品）を塗布して形成されている。ケミカルパックＭＳ６０は、塗布後の塗装部が耐候性と熱反射性を備える塗剤である。
なお、本実施の形態では、表層の形成にケミカルパックＭＳ６０を使用しているが、これに限定するものではなく、塗剤の塗布により耐候性又は熱反射性、耐候性及び熱反射性を備える表層を形成できる塗剤であればよい。
The surface layer 28 is formed by applying chemical pack MS60 (product of Murai Chemical Pack Co., Ltd.). The chemical pack MS60 is a coating agent in which the coated part after application has weather resistance and heat reflectivity.
In the present embodiment, the chemical pack MS60 is used to form the surface layer, but the present invention is not limited to this, and it has weather resistance or heat reflectivity, weather resistance, and heat reflectivity by application of a coating agent. Any coating agent that can form a surface layer may be used.
既設の波形スレート２２の補強方法は、以下の手順にて行う。なお、既設の波形スレート２２表面に浸透プライマーを塗布する手順から、山部２０に補強帯２６を貼り付ける手順までは、前記第１実施形態における段落００３３〜００３４で説明した手順（１）及び（２）と同様であるため説明を省略し、その後の相違する手順について以下（３）及び（４）として説明する。 A method of reinforcing the existing waveform slate 22 is performed according to the following procedure. Note that from the procedure of applying the permeation primer to the surface of the existing corrugated slate 22 to the procedure of attaching the reinforcing band 26 to the peak portion 20, the procedures (1) and (1) described in paragraphs 0033 to 0034 in the first embodiment are performed. Since it is the same as 2), the description thereof is omitted, and the different procedures thereafter will be described as (3) and (4) below.
（３）波形スレート２２表面に設けられた下地層２４及び補強帯２６の表面を覆うようにケミカルカチオンを塗布して、中間層２７を形成する。 (3) The intermediate layer 27 is formed by applying chemical cations so as to cover the surface of the foundation layer 24 and the reinforcing band 26 provided on the surface of the corrugated slate 22.
（４）その後、中間層２７表面に、ケミカルパックＭＳ６０を塗布して表層２８を形成する。 (4) Then, the chemical layer MS60 is applied to the surface of the intermediate layer 27 to form the surface layer 28.
（作 用）
中間層２７及び表層２８が形成された既設の波形スレート２２は、前記実施形態１記載の作用及び効果に加え、耐候性及び熱反射性が向上する。この結果、補強工事がなされた波形スレート２２を備える建物内部は、夏期は室温上昇、冬季は放熱が抑制できる。これにより、施設の省エネルギーを達成することができ、ひいては、発電所等が排出するＣＯ２削減につながって環境保全に貢献する効果が期待できる。また、耐候性の向上により既設のスレート２表面の劣化が修復及び抑制されるので、耐用年数が長くなる。
(Work)
The existing corrugated slate 22 on which the intermediate layer 27 and the surface layer 28 are formed has improved weather resistance and heat reflectivity in addition to the functions and effects described in the first embodiment. As a result, the interior of the building including the corrugated slate 22 subjected to the reinforcement work can increase the room temperature in the summer and suppress heat dissipation in the winter. Thereby, the energy saving of the facility can be achieved, and as a result, the effect of contributing to environmental conservation by reducing the CO 2 emitted from the power plant can be expected. Moreover, since the deterioration of the surface of the existing slate 2 is repaired and suppressed by improving the weather resistance, the service life becomes longer.
また、同じ期間、同じ場所に屋根として設置されていた劣化した波形スレート３枚を使用して、
（１）劣化した波形スレート、
（２）劣化した波形スレートへ第１実施形態に係る補強を施したもの、
（３）劣化した波形スレートへ第２実施形態に係る補強を施したもの、
を作成し、各波形スレートを地上１メートルの高さの枠体へ設置し、枠の無い箇所の各波形スレートへ高さ１メートルから重さ２５ｋｇの土砂を詰めた袋を落下させて耐衝撃性の比較試験を行った。
In addition, using three deteriorated waveform slate that was installed as a roof in the same place for the same period,
(1) degraded waveform slate,
(2) Reinforcing waveform slate with reinforcement according to the first embodiment,
(3) What provided the reinforcement which concerns on 2nd Embodiment to the waveform slate which deteriorated,
, Each corrugated slate is placed on a frame 1 meter above the ground, and a bag filled with earth and sand weighing 25 kg is dropped onto each corrugated slate where there is no frame. A sex comparison test was conducted.
試験の結果、（１）の波形スレートは完全に破断し、土砂を詰めた袋は枠下へ落下した。
一方、（２）及び（３）の波形スレートについては、スレート基材は割れたものの補強帯１６，２６によって完全破断するには至らずに折れ曲がった状態となり、該部分に支えられて土砂を詰めた袋は枠下へ落下しなかった。
As a result of the test, the corrugated slate of (1) was completely broken, and the bag filled with earth and sand fell below the frame.
On the other hand, for the corrugated slate of (2) and (3), although the slate base material is broken, it is bent without being completely broken by the reinforcing bands 16 and 26, and is supported by the portion and filled with earth and sand. The bag did not fall below the frame.
このことから、
（ａ）既設の波形スレート上における作業の際に、作業者が該スレートを踏み抜く危険性が減少する、
（ｂ）飛来物及び落下物により既設の波形スレートが衝撃を受けた場合でも、該スレートが完全破壊される（完全に破断する）危険性が減少する、
という効果が期待される。
From this,
(A) When working on an existing waveform slate, the risk of the operator stepping over the slate decreases.
(B) Even when an existing corrugated slate is impacted by flying objects and falling objects, the risk of the slate being completely destroyed (completely broken) is reduced.
The effect is expected.
本明細書及び特許請求の範囲で使用している用語と表現は、あくまでも説明上のものであって、なんら限定的なものではなく、本明細書及び特許請求の範囲に記述された特徴およびその一部と等価の用語や表現を除外する意図はない。また、本発明の技術思想の範囲内で、種々の変形態様が可能であるということは言うまでもない。 The terms and expressions used in the present specification and claims are for illustrative purposes only, and are not intended to be limiting in any way. The features described in the present specification and claims and their terms There is no intention of excluding some equivalent terms and expressions. It goes without saying that various modifications are possible within the scope of the technical idea of the present invention.
１ 波形スレート構造
１０ 山部
１１ 谷部
１２ 波形スレート
１２２ 劣化部分
１２４ 健全部分
１４ 下地層
１６ 補強帯
２ 波形スレート構造
２０ 山部
２１ 谷部
２２ 波形スレート
２２２ 劣化部分
２２４ 健全部分
２４ 下地層
２６ 補強帯
２７ 中間層
２８ 表層
DESCRIPTION OF SYMBOLS 1 Wave slate structure 10 Mountain part 11 Valley part 12 Wave slate 122 Degraded part 124 Sound part 14 Underlayer 16 Reinforcement belt 2 Wave slate structure 20 Mountain part 21 Valley part 22 Wave slate 222 Degraded part 224 Healthy part 24 Underlayer 26 Reinforcement belt 27 Intermediate layer 28 Surface layer
Claims (5)
波形石綿スレート表面に塗剤を塗布し、該塗剤によって少なくとも表面の劣化部分を固めて下地層又は下地膜(14,24)を形成する工程と、
下地層又は下地膜(14,24)が形成された前記スレートの山部(10,20)にアラミド繊維又はカーボン繊維の帯状物(16,26)を貼り付ける工程と、
を含む、
既設の波形石綿スレートの補強方法。 A method for reinforcing an existing corrugated asbestos slate,
Applying a coating agent to the corrugated asbestos slate surface, solidifying at least the surface degradation portion with the coating agent to form a base layer or a base film (14, 24);
Affixing a strip of aramid fiber or carbon fiber (16, 26) to the peak (10, 20) of the slate on which the base layer or base film (14, 24) is formed;
including,
A method of reinforcing existing corrugated asbestos slate.
請求項１記載の既設の波形石綿スレートの補強方法。 The coating applied to the corrugated asbestos slate surface is a liquid coating that penetrates and cures inside the slate, and the coating is the slate surface or the deteriorated portion of the slate (122, 222), or the slate surface and the deteriorated portion. After penetrating to a part of the healthy part (124, 224) in addition to (122, 222), the penetrating part hardens and becomes a reinforcing part.
The reinforcing method of the existing corrugated asbestos slate according to claim 1.
請求項１又は２記載のいずれかの既設の波形石綿スレートの補強方法。 After the step of affixing the band (26) of aramid fiber or carbon fiber to the peak (20) of the corrugated asbestos slate, the slate surface on which the underlayer or the underlayer film (24) is formed and the attached band (26 A step of forming a surface layer (28) by applying a coating having weather resistance and / or heat reflectivity from above.
The reinforcement method of the existing corrugated asbestos slate in any one of Claim 1 or 2.
補強構造体(1,2)は、
波形石綿スレート(12,22)表面へ前記スレート内部に浸透して硬化する液状塗剤を塗布して形成された下地層又は下地膜(14,24)と、
前記下地層又は下地膜(14,24)のうち、前記スレートの山部(10,20)の長さ方向にわたって貼り付けられたアラミド繊維又はカーボン繊維の帯状物(16,26)と、
を備えており、
前記下地層又は下地膜(14,24)は、塗布した塗剤が、前記スレート(12,22)表面、前記スレート(12,22)表面と前記スレートの劣化部分(122,222)、または、前記スレート表面と劣化部分(122,222)に加えて健全部分(124,224)の一部、のいずれかの箇所に浸透した後、浸透箇所が硬化して補強部となり、少なくとも表面の劣化部分が固めてある、
既設の波形石綿スレートを補強した補強構造体。 Reinforced structure (1,2) reinforced existing corrugated asbestos slate,
Reinforced structure (1,2)
Undercoat layer or base film (14, 24) formed by applying a liquid coating that penetrates and hardens into the corrugated asbestos slate (12, 22) surface;
Of the base layer or base film (14, 24), a band of aramid fibers or carbon fibers (16, 26) affixed over the length direction of the slate peak (10, 20), and
With
The undercoat layer or the undercoat film (14, 24) is applied to the slate (12, 22) surface, the slate (12, 22) surface and the deteriorated portion of the slate (122, 222), or the slate. After penetrating any part of the healthy part (124,224) in addition to the surface and the deteriorated part (122,222), the infiltrated part is cured and becomes a reinforcing part, and at least the deteriorated part of the surface is solidified,
Reinforcement structure reinforced existing corrugated asbestos slate.
補強構造体(2)は、
波形石綿スレート(22)表面へ前記スレート内部に浸透して硬化する液状塗剤を塗布して形成された下地層又は下地膜(24)と、
前記下地層又は下地膜(24)のうち、前記スレートの山部(20)の長さ方向にわたって貼り付けられたアラミド繊維又はカーボン繊維の帯状物(26)と、
前記下地層又は下地膜(24)及び帯状物(26)による表面の凹凸を整える塗剤を、下地層又は下地膜(24)及び帯状物(26)の表面を覆うよう塗布して形成された中間層(27)と、
耐候性または／および熱反射性を備える塗剤を、中間層(27)を覆うように塗布して形成された表層(28)と、
を備えており、
前記下地層又は下地膜(24)は、塗布した塗剤が、前記スレート(22)表面、前記スレート(22)表面と前記スレートの劣化部分(222)、または、前記スレート表面と劣化部分(222)に加えて健全部分(224)の一部、のいずれかの箇所に浸透した後、浸透箇所が硬化して補強部となり、少なくとも表面の劣化部分が固めてある、
既設の波形石綿スレートを補強した補強構造体。 Reinforced structure (2) reinforced existing corrugated asbestos slate,
Reinforcing structure (2)
A ground layer or base film (24) formed by applying a liquid coating that penetrates and hardens into the corrugated asbestos slate (22) surface,
Of the base layer or base film (24), a band of aramid fibers or carbon fibers (26) attached over the length direction of the slate peak (20), and
A coating agent for adjusting the surface irregularities of the base layer or base film (24) and the strip (26) was formed by coating so as to cover the surface of the base layer or base film (24) and the strip (26). The middle layer (27),
A surface layer (28) formed by applying a coating having weather resistance or / and heat reflectivity so as to cover the intermediate layer (27);
With
The base layer or the base film (24) is applied to the slate (22) surface, the slate (22) surface and the deteriorated portion of the slate (222), or the slate surface and the deteriorated portion (222). ) In addition to a part of the healthy part (224), the penetration part is cured and becomes a reinforcing part, at least the deteriorated part of the surface is solidified,
Reinforcement structure reinforced existing corrugated asbestos slate.