JP2010040640A

JP2010040640A - Electromagnetic wave shielding body

Info

Publication number: JP2010040640A
Application number: JP2008199593A
Authority: JP
Inventors: Hajime Murazaki; 肇村崎; Takeshi Murazaki; 毅村崎
Original assignee: Individual
Current assignee: Individual
Priority date: 2008-08-01
Filing date: 2008-08-01
Publication date: 2010-02-18

Abstract

<P>PROBLEM TO BE SOLVED: To provide an electromagnetic wave shielding body which stably has high shielding performance of about 100 dB in a band almost up to 10 GHz covering a frequency band to be used of a wireless LAN. <P>SOLUTION: The electromagnetic wave shielding body comprises a first base layer, a carbon felt stacked on the first base layer, a second base layer stacked on the carbon felt, and a shield cloth stacked on a surface of the second base layer. Here, the carbon felt has attenuation characteristics of 80 to 90 dB and the shield cloth has attenuation characteristics of 40 to 50 dB. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明は、電磁遮蔽機能を必要とするオフィスビルや工場などの建築物の電磁遮蔽建材に用いられる電磁遮蔽体に関する。 The present invention relates to an electromagnetic shielding body used for electromagnetic shielding building materials for buildings such as office buildings and factories that require an electromagnetic shielding function.

最近のＩＴ技術やブロードバンド化による情報通信の広帯域化、ワイヤレス化が発展するなか、携帯電話機や無線ＬＡＮなどのように室内で無線による情報の伝達が多く行われるようになっているが、情報を傍受され易いために情報漏洩の問題が多く発生している。このため、オフィスなどにおいては、部屋の内面全体に電磁波を遮蔽する電磁波遮蔽材を配置して、室内から室外への電磁波の漏洩と、室外から室内への電磁波の侵入を防止することが求められている。 With the development of broadband and wireless information communication due to recent IT technology and broadbandization, wireless information transmission is becoming more common indoors, such as mobile phones and wireless LANs. There are many problems of information leakage because it is easily intercepted. For this reason, in an office or the like, it is required to arrange an electromagnetic shielding material that shields electromagnetic waves on the entire inner surface of a room to prevent leakage of electromagnetic waves from the room to the outside and intrusion of electromagnetic waves from the room to the room. ing.

特に、無線ＬＡＮの使用周波数帯である２．４５ＧＨｚ帯と５．２ＧＨｚ帯では、建物内で使用する場合には、高度な機密情報を扱うパソコンと中継アンテナが設置される室内や、サーバ室などでは、最近１００ｄＢ（１／１０００００まで減衰）程度の高い遮蔽性能が求められている。 In particular, in the 2.45 GHz band and the 5.2 GHz band, which are the frequency bands used for wireless LAN, when used in a building, a room in which a personal computer and a relay antenna for handling highly confidential information are installed, a server room, etc. In recent years, a high shielding performance of about 100 dB (attenuation to 1/100000) has been demanded.

従来、この種の電磁遮蔽材としては、電磁波を反射する素材を用いたものとして例えば、箔状、薄板状の金属を単体で下地に貼り付けて使用するものがある。しかしながら、この金属単体は施工時に裂け易く取扱いに熟練を要し、また、施工後の下地の熱変形などにより裂けが生じ易く、電磁波漏洩の原因となる。更に、電磁遮蔽材の上には内装クロス材を別途取付けることになり、施工に手間がかかり施工コストも上昇する。 Conventionally, as this type of electromagnetic shielding material, there is a material that uses a material that reflects electromagnetic waves, for example, a foil-like or thin-plate-like metal that is affixed to a base alone. However, this single metal is easy to tear at the time of construction and requires skill in handling, and it is easy to tear due to thermal deformation of the base after construction, which causes electromagnetic leakage. Furthermore, an interior cloth material is separately attached on the electromagnetic shielding material, which takes time for construction and increases the construction cost.

また、電磁波遮蔽材として電磁波を吸収する素材を用いたものとして、例えば特許文献１に記載された電磁波遮蔽材がある。具体的には電磁波吸収層がフェライトや使用済みの磁気切符などの電波を吸収する素材を含み、適宜の手段によりシート状に形成されている。 Moreover, there exists an electromagnetic wave shielding material described in patent document 1, for example as a thing using the raw material which absorbs an electromagnetic wave as an electromagnetic wave shielding material. Specifically, the electromagnetic wave absorbing layer includes a material that absorbs radio waves such as ferrite and used magnetic tickets, and is formed into a sheet shape by appropriate means.

特開２００６−３３２２６０号公報JP 2006-332260 A

しかしながら、フェライトや磁気切符等の電磁波の吸収素材は整合周波数が０．３ＧＨｚ〜１．５ＧＨｚであり、無線ＬＡＮの使用周波数帯が十分にカバーされてないため、この使用周波数帯で高い遮蔽性能が得にくいものである。 However, electromagnetic wave absorbing materials such as ferrite and magnetic tickets have a matching frequency of 0.3 GHz to 1.5 GHz, and the use frequency band of the wireless LAN is not sufficiently covered. It is hard to get.

本発明は、上記従来例の問題点に鑑み、無線ＬＡＮの使用周波数帯をカバーする１０ＧＨｚ付近までの帯域で、安定して１００ｄＢ程度の高い遮蔽性能をもつ電磁波遮蔽材を提供するものである。 The present invention provides an electromagnetic wave shielding material that stably has a high shielding performance of about 100 dB in a band up to about 10 GHz that covers the use frequency band of a wireless LAN in view of the problems of the conventional example.

上記課題を解決するために、本発明は、第１下地層と、この第1下地層の上方に積層されるカーボンフェルトと、このカーボンフェルトに積層される第２下地層と、この第２下地層の表面に積層されるシールドクロスからなることを特徴とする。 In order to solve the above-described problems, the present invention provides a first underlayer, a carbon felt laminated above the first underlayer, a second underlayer laminated on the carbon felt, and the second lower layer. It consists of a shield cloth laminated on the surface of the formation.

また、上記第１下地層は、壁またはボードであることを特徴とする。また、上記第１下地層は、壁とその上に積層された断熱層から構成されることを特徴とする。また、上記第１下地層は、断熱材とその上に積層されたボードから構成されることを特徴とする。また、上記第２下地層は、ボードであることを特徴とする。上記ボードは石膏ボードであることを特徴とする。 The first underlayer is a wall or a board. In addition, the first base layer includes a wall and a heat insulating layer laminated thereon. In addition, the first underlayer is composed of a heat insulating material and a board laminated thereon. Further, the second underlayer is a board. The board is a gypsum board.

また、前記カーボンフェルトは７００ＭＨｚ〜１ＧＨｚの周波数範囲で８０〜９０ｄＢの電磁波減衰特性を有し、前記シールドクロスは３００ＭＨｚ〜１ＧＨｚの周波数範囲で４０〜５０ｄＢの電磁波減衰特性を有することを特徴とする。 The carbon felt has an electromagnetic wave attenuation characteristic of 80 to 90 dB in a frequency range of 700 MHz to 1 GHz, and the shield cloth has an electromagnetic wave attenuation characteristic of 40 to 50 dB in a frequency range of 300 MHz to 1 GHz.

本発明によれば、上記構成により１０ＧＨｚ付近までの帯域で安定的に１００ｄＢ程度の高い電磁波減衰特性を得ることができる。しかも、カーボンフェルトと壁紙兼用のシールドクロスによる簡単な構成により達成できる。 According to the present invention, a high electromagnetic wave attenuation characteristic of about 100 dB can be stably obtained in the band up to about 10 GHz by the above configuration. In addition, this can be achieved by a simple configuration using a carbon cloth and a shield cloth used as wallpaper.

以下図面を用いて本発明実施例を説明する。図１は、壁のない建物の柱の室内側に電磁波遮蔽体を施工した場合の実施例１の断面図である。１は複数本建てられた支柱、２は複数本の支柱１に跨って室内側に挟み込んで取付けられた断熱材で、アルミで被覆されたグラスウールで構成される。なお、断熱材２は柱１の間に挟み込まれて設置されても良い。 Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a cross-sectional view of Example 1 when an electromagnetic wave shielding body is constructed on the indoor side of a pillar of a building without a wall. Reference numeral 1 denotes a plurality of pillars that are built, and reference numeral 2 denotes a heat insulating material that is sandwiched and attached to the indoor side across the plurality of pillars 1 and is made of glass wool coated with aluminum. The heat insulating material 2 may be interposed between the pillars 1 and installed.

３は断熱材の上に積層配置され、断熱材２を前記支柱１との間で挟み込むように、前記支柱１に固定された石膏ボード、４は前記石膏ボード３の上に接着剤（ボンドや糊）で貼り付けられたカーボンフェルト、５は前記カーボンフェルト４の上に積層配置され、前記石膏ボード３との間でカーボンフェルト４を潰し過ぎないような所定間隔をおいて前記石膏ボード３に固定された石膏ボード、６は石膏ボード５の表面に接着剤（でんぷん糊等）で貼り付けられたシールドクロスである。 3 is laminated on the heat insulating material, and gypsum board fixed to the support 1 so that the heat insulating material 2 is sandwiched between the support 1 and 4 is an adhesive (bond or bond) on the gypsum board 3. The carbon felt 5 attached with glue is laminated on the carbon felt 4 and is placed on the gypsum board 3 at a predetermined interval so as not to crush the carbon felt 4 with the gypsum board 3. A fixed gypsum board 6 is a shield cloth affixed to the surface of the gypsum board 5 with an adhesive (such as starch paste).

本実施例では石膏ボード３が第1下地層で、石膏ボード５が第２下地層となり、各下地層の上にそれぞれカーボンフェルト４とシールドクロス６が接着剤で貼り付けられている。ここで、石膏ボード３、４は石膏を心材としてボード用原紙でくるみ板状に成形したもので１２ｍｍのものが用いられる。 In this embodiment, the gypsum board 3 is a first foundation layer, the gypsum board 5 is a second foundation layer, and the carbon felt 4 and the shield cloth 6 are bonded to each foundation layer with an adhesive. Here, the gypsum boards 3 and 4 are made of gypsum as a core material and formed into a wrapping plate shape with a base paper for board, and those with 12 mm are used.

カーボンフェルト４は、例えば日本グラスファイバー工業株式会社製の電磁シールドフェルトで、ＰＡＮ（ポリアクリロニトリル）系炭素繊維とＰＰ（ポリプロピレン）繊維を混合し、ニードルパンチ方式で成形し、目止め処理を施したもので厚さが５ｍｍのものを用いる。このカーボンフェルト４の単体の３００ＭＨｚ〜１ＧＨｚの周波数範囲での電磁波遮蔽特性（電磁波減衰特性）を図４に示す。図に示すように、１０００ＭＨｚ（１ＧＨｚ）付近で約８０ｄＢの減衰（１／１００００まで減衰）が得られ、無線ＬＡＮの使用周波数帯の２．４５ＧＨｚ帯と５．２ＧＨｚ帯では、約９０ｄＢ（１／３００００まで減衰）付近の減衰特性が得られ、７００ＭＨｚ〜１ＧＨｚの範囲で８０〜９０ｄＢの減衰特性を有している。 The carbon felt 4 is, for example, an electromagnetic shield felt manufactured by Nippon Glass Fiber Industries, Ltd. A PAN (polyacrylonitrile) -based carbon fiber and PP (polypropylene) fiber are mixed, molded by a needle punch method, and subjected to a sealing treatment. A thing with a thickness of 5 mm is used. FIG. 4 shows electromagnetic wave shielding characteristics (electromagnetic wave attenuation characteristics) in the frequency range of 300 MHz to 1 GHz of the carbon felt 4 alone. As shown in the figure, an attenuation of about 80 dB (attenuation to 1/10000) is obtained in the vicinity of 1000 MHz (1 GHz), and about 90 dB (1/1) in the 2.45 GHz band and the 5.2 GHz band of the wireless LAN use frequency band. (Attenuation up to 30000) is obtained, and it has an attenuation characteristic of 80 to 90 dB in the range of 700 MHz to 1 GHz.

シールドクロス６は、アルミ箔またはアルミ蒸着したものを裏打紙と表面化粧層の間に挟んで構成されたもの（株式会社村崎製の商品名シールドプロテクター）で、電磁波シールド層であると共に室内の壁面の表面を化粧する壁紙となる。このシールドクロス６の単体の３００ＭＨｚ〜１ＧＨｚの周波数範囲での電磁波遮蔽特性を図５に示す。図に示すように、１０００ＭＨｚ（１ＧＨｚ）付近で約４０ｄＢ（１／１００まで減衰）の減衰特性が得られ、無線ＬＡＮの使用周波数帯の２．４５ＧＨｚ帯と５．２ＧＨｚ帯では、約３５〜４０ｄＢ（１／１００まで減衰）の減衰特性が得られ、３００ＭＨｚ〜１ＧＨｚの範囲で全体として４０〜５０ｄＢの減衰特性を有している。このように、本実施例ではシールドクロス６も電磁波遮蔽材として用いる。 The shield cloth 6 is made of aluminum foil or aluminum vapor-deposited between the backing paper and the surface decorative layer (trade name shield protector, manufactured by Murasaki Co., Ltd.). It becomes a wallpaper to make up the surface of. FIG. 5 shows the electromagnetic shielding characteristics in the frequency range of 300 MHz to 1 GHz of the shield cloth 6 alone. As shown in the figure, an attenuation characteristic of about 40 dB (attenuated to 1/100) is obtained in the vicinity of 1000 MHz (1 GHz), and about 35 to 40 dB in the 2.45 GHz band and the 5.2 GHz band of the wireless LAN use frequency band. Attenuation characteristics of (attenuate to 1/100) are obtained, and as a whole, it has an attenuation characteristic of 40 to 50 dB in the range of 300 MHz to 1 GHz. Thus, in this embodiment, the shield cloth 6 is also used as an electromagnetic wave shielding material.

本実施例１の遮蔽体の構成の中の一部の構成の減衰特性を図６に示す。これは、間に石膏ボードを介在させた、カーボンフェルト４とシールドクロス６のみの構成体の減衰特性である。図６では、１０００ＭＨｚ（１ＧＨｚ）付近で９０〜１００ｄＢ（１／３００００〜１／１０００００まで減衰）の減衰特性が得られ、無線ＬＡＮの使用周波数帯の２．４５ＧＨｚ帯では１００ｄＢ以上の減衰特性が得られ、さらに５．２ＧＨｚ帯では１００ｄＢ弱の減衰特性が得られる。このようにカーボンフェルト４とシールドクロス６を組合せることにより、各単体では得られない１００ｄＢレベルの極めて高い減衰特性が得られる。なお、本実施例１の遮蔽体では、電磁波遮蔽材としてカーボンフェルト４とシールドクロス６の他に、アルミで被覆された断熱材２を設けているので、さらに遮蔽性能は高まると考えられる。 FIG. 6 shows the attenuation characteristics of a part of the configuration of the shield according to the first embodiment. This is a damping characteristic of a structure including only the carbon felt 4 and the shield cloth 6 with a gypsum board interposed therebetween. In FIG. 6, an attenuation characteristic of 90 to 100 dB (attenuated to 1 / 30,000 to 1/100000) is obtained near 1000 MHz (1 GHz), and an attenuation characteristic of 100 dB or more is obtained in the 2.45 GHz band of the wireless LAN use frequency band. Furthermore, in the 5.2 GHz band, an attenuation characteristic of a little less than 100 dB is obtained. By combining the carbon felt 4 and the shield cloth 6 in this way, an extremely high attenuation characteristic of 100 dB level that cannot be obtained by each single unit can be obtained. In addition, in the shielding body of the first embodiment, since the heat insulating material 2 covered with aluminum is provided in addition to the carbon felt 4 and the shield cloth 6 as an electromagnetic wave shielding material, it is considered that the shielding performance is further improved.

図７は、カーボンフェルト４とシールドクロス６の間に石膏ボードを設けない（空間を設けた）状態で測定した遮蔽性能を示す特性図である。図６と比べて全体的に性能が低下しているが、無線ＬＡＮの使用周波数帯の２．４５ＧＨｚ帯と５．２ＧＨｚ帯では、１００ｄＢに近い遮蔽性能が得られている。これは、石膏ボードにも遮蔽性能があることを示している。 FIG. 7 is a characteristic diagram showing the shielding performance measured in a state where a gypsum board is not provided (a space is provided) between the carbon felt 4 and the shield cloth 6. Although the overall performance is lower than that in FIG. 6, shielding performance close to 100 dB is obtained in the 2.45 GHz band and the 5.2 GHz band of the wireless LAN used frequency band. This indicates that the gypsum board also has a shielding performance.

また、本実施例では前記下地層として固いボードを用いているが、これはカーボンフェルト４やシールドクロス６を施工時の貼付作業性を良くし、裂け等が起らないようにしたものである。また、ボードとして石膏ボードを用いているが、他の木質ボードやセメントボードと比べて、温度や湿度の変化に影響されず伸び縮みや歪みがほとんどないため、施工後に冷熱サイクルが加わっても、カーボンフェルト４やシールドクロス６に裂けが起ることがない。従って、施工後にカーボンフェルト４やシールドクロス６の裂け等による遮蔽性能の劣化がないため、高い遮蔽性能を長年維持できる。 Further, in this embodiment, a hard board is used as the base layer, but this improves the workability of attaching the carbon felt 4 and the shield cloth 6 at the time of construction so that tearing and the like do not occur. . In addition, gypsum board is used as the board, but compared to other wooden boards and cement boards, it is not affected by changes in temperature and humidity and there is almost no expansion or contraction or distortion, so even if a thermal cycle is added after construction, The carbon felt 4 and the shield cloth 6 do not tear. Therefore, since there is no deterioration of the shielding performance due to tearing of the carbon felt 4 or the shield cloth 6 after construction, high shielding performance can be maintained for many years.

図２は建物に壁がある場合を示し、壁の室内側に電磁波遮蔽体を施工した実施例２の断面図である。７は建物を構成するコンクリートなどの壁、２は前記壁７の上に積層された断熱材で、アルミで被覆されたグラスウールで構成される。４は断熱材２の上に接着剤で接着されたカーボンフェルト、５は前記カーボンフェルト４の上に積層された石膏ボード、６は石膏ボード５の表面に接着剤で貼り付けられたシールドクロスである。石膏ボード５は、断熱材２とカーボンフェルト４を潰し過ぎないように壁７に押圧積層した形で、壁７に取付けられる。 FIG. 2 shows a case where there is a wall in a building, and is a cross-sectional view of Example 2 in which an electromagnetic wave shielding body is constructed on the indoor side of the wall. 7 is a wall made of concrete or the like constituting the building, and 2 is a heat insulating material laminated on the wall 7 and is made of glass wool coated with aluminum. 4 is a carbon felt bonded to the heat insulating material 2 with an adhesive, 5 is a gypsum board laminated on the carbon felt 4, and 6 is a shield cloth adhered to the surface of the gypsum board 5 with an adhesive. is there. The gypsum board 5 is attached to the wall 7 in a form in which the heat insulating material 2 and the carbon felt 4 are pressed and laminated on the wall 7 so as not to crush too much.

本実施例２では、壁７と断熱材２で第1下地層が形成され、その上にカーボンフェルト４が積層されており、石膏ボード５が第２下地層となり、その上にシールドクロス６が貼り付けられている。 In the second embodiment, a first ground layer is formed by the wall 7 and the heat insulating material 2, a carbon felt 4 is laminated thereon, a gypsum board 5 becomes a second ground layer, and a shield cloth 6 is formed thereon. It is pasted.

図３は建物に壁がある場合を示し、壁の室内側に電磁波遮蔽体を施工した場合の実施例３の断面図である。７は建物を構成するコンクリートなどの壁、４は壁７の上に接着剤で接着されたカーボンフェルト、２は前記カーボンフェルト４の上に積層された断熱材で、アルミで被覆されたグラスウールで構成される。５は断熱材２の上に積層された石膏ボード、６は石膏ボード５の表面に接着剤で貼り付けられたシールドクロスである。石膏ボード５は、断熱材２とカーボンフェルト４を潰し過ぎないように壁７に押圧積層した形で、壁７に取付けられる。実施例２と異なるのは、カーボンフェルト４と断熱材２の配置が逆となっている点である。 FIG. 3 shows a case where there is a wall in the building, and is a cross-sectional view of Example 3 when an electromagnetic wave shielding body is constructed on the indoor side of the wall. 7 is a wall made of concrete or the like constituting the building, 4 is a carbon felt bonded to the wall 7 with an adhesive, and 2 is a heat insulating material laminated on the carbon felt 4 and is made of glass wool coated with aluminum. Composed. 5 is a gypsum board laminated on the heat insulating material 2, and 6 is a shield cloth adhered to the surface of the gypsum board 5 with an adhesive. The gypsum board 5 is attached to the wall 7 in a form in which the heat insulating material 2 and the carbon felt 4 are pressed and laminated on the wall 7 so as not to crush too much. The difference from the second embodiment is that the arrangement of the carbon felt 4 and the heat insulating material 2 is reversed.

本実施例では、壁７が第1下地層となり、その上にカーボンフェルト４が積層されており、石膏ボード５が第２下地層となり、その上にシールドクロス６が貼り付けられている。 In this embodiment, the wall 7 serves as the first foundation layer, the carbon felt 4 is laminated thereon, the gypsum board 5 serves as the second foundation layer, and the shield cloth 6 is pasted thereon.

上記各実施例の電磁波遮蔽体は、電磁波遮蔽材としてカーボンフェルト４を接着剤で接着して積層しており、他の材料として建物の内壁材として本来用いられる、断熱材、下地（ボード）、壁紙（シールドクロス）を用いている。従って、施工は一般のクロス用の接着剤を用いてカーボンフェルト４とシールドクロス６を接着により積層しているので、工数が特別増加することがなく、また、カーボンフェルトも低価格であることから、コスト圧縮が図れる。また、下地として石膏ボードを用いているので、冷熱サイクルによりカーボンフェルト４とシールドクロス６に裂けが生じることがなく、電磁波遮蔽機能を長期間維持することができ、また、石膏ボード自身を電磁波遮蔽材料に利用できる。 The electromagnetic wave shielding body of each of the above embodiments is laminated by adhering carbon felt 4 as an electromagnetic wave shielding material with an adhesive, and is originally used as an inner wall material of a building as another material, a base (board), Uses wallpaper (shield cloth). Therefore, since the carbon felt 4 and the shield cloth 6 are laminated by bonding using a general cloth adhesive, there is no special increase in man-hours, and the carbon felt is also inexpensive. Cost reduction can be achieved. In addition, since the gypsum board is used as the base, the carbon felt 4 and the shield cloth 6 are not torn due to the thermal cycle, the electromagnetic wave shielding function can be maintained for a long time, and the gypsum board itself is shielded from electromagnetic waves. Available for material.

上記カーボンフェルト４とシールドクロス６は定尺のものが用いられるので、この定尺の寸法（面積）より広い面積の壁、床、天井では、複数枚をつないで貼り付けられることになる。また、前記各部の境目（例えば壁と天井の境目、壁と床の境目、等）でも、別個のシールドクロスのつなぎ目となることがある。このようなつなぎ部分では、電磁波の漏れが生じ易いので、その遮蔽対策が必要である。更に、壁と支柱の境界の取り合いや、ドアとこれを支える支柱の境界の取り合いでも電磁波の漏れが起りやすいので、上記と同様な遮蔽対策が必要である。 Since the carbon felt 4 and the shield cloth 6 are of a fixed size, a plurality of walls, floors, and ceilings having a larger area (area) than the fixed size are bonded and bonded together. In addition, the boundary between the parts (for example, the boundary between a wall and a ceiling, the boundary between a wall and a floor, etc.) may be a joint between separate shield cloths. In such a connection part, leakage of electromagnetic waves is likely to occur, so a countermeasure for shielding is necessary. Further, since the leakage of electromagnetic waves is likely to occur even when the boundary between the wall and the column or the boundary between the door and the column supporting the door is used, the same shielding measures as described above are required.

以下、上記のようなつなぎ部分や境界部分での遮蔽構造について説明する。図８は、本発明実施例４の定尺の電磁波遮蔽体をつなぐ場合の境界断面図であり、（ａ）に電磁波遮蔽体の端部を重ね合わせることによる遮蔽構造を示し、（ｂ）に電磁波遮蔽体の端部を突き合せることによる遮蔽構造を示す。図８では、遮蔽体としてカーボンフェルト４とシールドクロス６のみを示し、下地のボードを省略して示してある。 Hereinafter, the shielding structure at the connecting part and the boundary part will be described. FIG. 8 is a cross-sectional view of the boundary when connecting the standard-sized electromagnetic wave shields of Example 4 of the present invention. FIG. 8A shows a shielding structure by overlapping the end portions of the electromagnetic wave shields, and FIG. The shielding structure by abutting the edge part of an electromagnetic shielding body is shown. In FIG. 8, only the carbon felt 4 and the shield cloth 6 are shown as a shield, and the base board is omitted.

図８（ａ）では、電磁波遮蔽体の端部を約３０〜５０ｍｍの長さ重ね合わせることにより、重なり部分を遮蔽体の二重構造として、境界での電磁波の遮蔽能力が増加させている。図８（ｂ）では、電磁波遮蔽体の端部の突合せ部分６ａの下に約１００ｍｍの長さの導電テープ８を積層して貼り合わせている。導電テープ８としては、単なるアルミ箔からなるテープ、紙（裏打層）にアルミ箔を貼り付けたアルミ箔紙、または裏打紙（裏打層）にアルミを蒸着したアルミ蒸着紙がある。 In Fig.8 (a), the shielding part of the electromagnetic wave in a boundary is made to increase by making the overlap part into the double structure of a shielding body by overlapping the edge part of an electromagnetic shielding body about 30-50 mm in length. In FIG. 8B, a conductive tape 8 having a length of about 100 mm is laminated and bonded under the butted portion 6a at the end of the electromagnetic wave shield. Examples of the conductive tape 8 include a tape made of a simple aluminum foil, an aluminum foil paper in which an aluminum foil is attached to a paper (backing layer), or an aluminum vapor-deposited paper in which aluminum is vapor-deposited on a backing paper (backing layer).

図８（ｂ）では、シールドクロス６に接着剤が付着しており、導電テープ８のアルミ部分がこの接着剤に触れると、機械的強度の小さなアルミが破れて突合せ部分６ａ（クロスジョイント）が口を開く恐れがある。突合せ部分６ａが開くと裏に貼り付けられた導電テープ８が見えて仕上がりが悪くなると共に、電磁波の遮蔽機能が損なわれる恐れがある。本実施例では突合せ部分６ａの下に導電テープ８の裏打層１０側を接着するようにし、裏打層１０の下にアルミ部分１１が位置するように構成している。従って、導電テープ８の機械的強度の強い裏打層１０側に突合せ部分６ａが接着されるので、開くことがなく、アルミ部分１１が破れることがない。従って、突合せ部分６ａが閉じているため仕上がりが良く、電磁波の遮蔽機能が損なわれることもない。 In FIG. 8B, the adhesive is adhered to the shield cloth 6, and when the aluminum portion of the conductive tape 8 touches the adhesive, the aluminum having a low mechanical strength is broken and the butt portion 6a (cross joint) is formed. There is a risk of opening his mouth. When the butted portion 6a is opened, the conductive tape 8 attached to the back is visible, the finish is deteriorated, and the electromagnetic wave shielding function may be impaired. In the present embodiment, the side of the backing layer 10 of the conductive tape 8 is adhered under the butted portion 6 a, and the aluminum portion 11 is positioned under the backing layer 10. Therefore, the butt portion 6a is bonded to the backing layer 10 side of the conductive tape 8 having a high mechanical strength, so that it does not open and the aluminum portion 11 is not torn. Therefore, since the butted portion 6a is closed, the finish is good and the electromagnetic wave shielding function is not impaired.

次に、本発明実施例５の電磁波遮蔽体の支柱との境界の取り合い部分や、ドアとこれを支える支柱との境界の取り合い部分の処理構造について説明する。 Next, a description will be given of the processing structure of the interface portion of the electromagnetic shielding member according to Embodiment 5 of the present invention and the interface portion of the boundary between the door and the support column supporting the door.

図９において、柱１に取付けられた厚さ１２ｍｍの石膏の下地ボード３にカーボンフェルト４が張り付けられ、その上に厚さ１２ｍｍの石膏の下地ボードを積層し、更にその上にシールドクロス６を貼り付けている。１２は接地されたスチール製のドア枠、１３は矢印方向に開閉するスチール製のドアで、閉じたときその端部がドア枠１２に接触して停止する。１４は、ドア１３が閉じている状態で、ドアの端部とドア枠１２の間に設置された導電性のシール材からなる導電ガスケットで、ドア枠１２とドア１３の間を電気的に接続して電磁波の遮蔽機能を果たす。 In FIG. 9, a carbon felt 4 is attached to a 12 mm thick gypsum base board 3 attached to a pillar 1, a 12 mm thick gypsum base board is laminated thereon, and a shield cloth 6 is further formed thereon. Paste. Reference numeral 12 denotes a grounded steel door frame, and reference numeral 13 denotes a steel door that opens and closes in the direction of the arrow. When the door is closed, its end contacts the door frame 12 and stops. 14 is a conductive gasket made of a conductive sealing material installed between the end of the door and the door frame 12 with the door 13 closed, and electrically connects the door frame 12 and the door 13. And serve to shield electromagnetic waves.

１５は、３〜６で構成される電磁波遮蔽体と前記ドア枠１２との間に設置された略Ｌ字型の導通テープあり、電磁波遮蔽体とドア枠１２を電気的に接続して電磁波の遮蔽機能を果たす。すなわち、導通テープ１５は、カーボンフェルト４とシールドクロス６とドア枠１２を電気的に接続している。従って、ドア１３を閉じた状態では、電磁波遮蔽体、ドア枠１２、およびドア１３が電気的に接続されることにより電気的にシールされ、電磁波の遮蔽機能を果たす。 15 is a substantially L-shaped conductive tape installed between the electromagnetic wave shielding body composed of 3 to 6 and the door frame 12, and electrically connects the electromagnetic wave shielding body and the door frame 12 to prevent electromagnetic waves. Performs a shielding function. That is, the conductive tape 15 electrically connects the carbon felt 4, the shield cloth 6, and the door frame 12. Therefore, when the door 13 is closed, the electromagnetic wave shielding body, the door frame 12, and the door 13 are electrically connected to each other to be electrically sealed, thereby fulfilling an electromagnetic wave shielding function.

上記構成によれば、電磁波遮蔽体とドア枠１２の取り合い部分は、導電テープ１５により電磁波の漏れがなく、また、ドア枠１２とドア１３の取り合い部分では、導電ガスケットにより電磁波の漏れがなく、十分な電磁波遮蔽機能を果たすことができる。 According to the above configuration, the electromagnetic wave shield and the door frame 12 have no electromagnetic wave leakage due to the conductive tape 15, and the door frame 12 and the door 13 have no electromagnetic wave leakage due to the conductive gasket. A sufficient electromagnetic wave shielding function can be achieved.

本発明の実施例１の断面図である。It is sectional drawing of Example 1 of this invention. 本発明の実施例２の断面図である。It is sectional drawing of Example 2 of this invention. 本発明の実施例３の断面図である。It is sectional drawing of Example 3 of this invention. 本発明の実施例のカーボンフェルト単体の電磁波遮蔽特性図である。It is an electromagnetic wave shielding characteristic figure of the carbon felt simple substance of the example of the present invention. 本発明の実施例のシールドクロスの電磁波遮蔽特性図である。It is an electromagnetic wave shielding characteristic figure of the shield cloth of the example of the present invention. カーボンフェルトとシールドクロスの間に石膏ボードを設けた場合の電磁波遮蔽特性図である。It is an electromagnetic wave shielding characteristic figure at the time of providing a gypsum board between carbon felt and a shield cloth. カーボンフェルトとシールドクロスの間に石膏ボードを設けない場合の電磁波遮蔽特性図である。It is an electromagnetic wave shielding characteristic figure in case a gypsum board is not provided between carbon felt and a shield cloth. 本発明の実施例４の電磁波遮蔽体をつなぐ場合の境界断面図である。It is boundary sectional drawing in the case of connecting the electromagnetic wave shielding body of Example 4 of this invention. 本発明の実施例５の電磁波遮蔽体と支柱との取合い部分の断面図である。It is sectional drawing of the connection part of the electromagnetic wave shielding body of Example 5 of this invention, and a support | pillar.

符号の説明Explanation of symbols

１…柱、２…断熱材、３、５…下地ボード、４…カーボンフェルト、６…シールドクロス、７…壁。 DESCRIPTION OF SYMBOLS 1 ... Column, 2 ... Thermal insulation material, 3, 5 ... Base board, 4 ... Carbon felt, 6 ... Shield cloth, 7 ... Wall.

Claims

第１下地層と、この第1下地層の上方に積層されるカーボンフェルトと、このカーボンフェルトに積層される第２下地層と、この第２下地層の表面に積層されるシールドクロスからなることを特徴とする電磁波遮蔽体。 It consists of a first underlayer, a carbon felt laminated above the first underlayer, a second underlayer laminated on the carbon felt, and a shield cloth laminated on the surface of the second underlayer. An electromagnetic wave shield characterized by.

上記第１下地層は、壁またはボードであることを特徴とする請求項１記載の電磁波遮蔽体。 The electromagnetic wave shielding body according to claim 1, wherein the first base layer is a wall or a board.

上記第１下地層は、壁とその上に積層された断熱層から構成されることを特徴とする請求項１記載の電磁波遮蔽体。 The electromagnetic shielding body according to claim 1, wherein the first base layer is composed of a wall and a heat insulating layer laminated thereon.

上記第１下地層は、断熱材とその上に積層されたボードから構成されることを特徴とする請求項１記載の電磁波遮蔽体。 The electromagnetic shielding body according to claim 1, wherein the first base layer is composed of a heat insulating material and a board laminated thereon.

上記第２下地層は、ボードであることを特徴とする請求項１〜４のいずれかに記載の電磁波遮蔽体。 The electromagnetic wave shielding body according to claim 1, wherein the second base layer is a board.

上記ボードは石膏ボードであることを特徴とする請求項１〜５の何れかに記載の電磁波遮蔽体。 The electromagnetic wave shielding body according to claim 1, wherein the board is a gypsum board.

前記カーボンフェルトは８０〜９０ｄＢの電磁波減衰特性を有し、前記シールドクロスは４０〜５０ｄＢの電磁波減衰特性を有することを特徴とする請求項１〜６の何れかに記載の電磁波遮蔽体。 The electromagnetic shield according to claim 1, wherein the carbon felt has an electromagnetic wave attenuation characteristic of 80 to 90 dB, and the shield cloth has an electromagnetic wave attenuation characteristic of 40 to 50 dB.