JP2010007181A - 還元鉄製造方法 - Google Patents
還元鉄製造方法 Download PDFInfo
- Publication number
- JP2010007181A JP2010007181A JP2009129831A JP2009129831A JP2010007181A JP 2010007181 A JP2010007181 A JP 2010007181A JP 2009129831 A JP2009129831 A JP 2009129831A JP 2009129831 A JP2009129831 A JP 2009129831A JP 2010007181 A JP2010007181 A JP 2010007181A
- Authority
- JP
- Japan
- Prior art keywords
- dust
- zinc
- raw material
- generated
- amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】鉄鉱石11と炭素系固体還元材12と造滓材13とを混合した混合原料を移動型炉床炉15の炉床上に積載し、該炉床上部から熱供給して混合原料を還元し、更に溶融させて、還元鉄を製造する際に、前記移動型炉床炉15で発生するダストの一部を21aで混合原料に混合して循環使用し、ダストの残部を高亜鉛含有ダストとして21bで分離することを特徴とする還元鉄製造方法を用いる。混合原料中の亜鉛濃度に基づいて、高亜鉛含有ダストとして分離するダストの量を決定すること、または移動型炉床炉で発生するダストの亜鉛濃度を分析し、該分析濃度に基づいて高亜鉛含有ダストとして分離するダストの量を決定することが好ましい。
【選択図】図2
Description
(1)鉄鉱石と炭素系固体還元材と造滓材とを混合した混合原料を移動型炉床炉の炉床上に積載し、該炉床上部から熱供給して前記混合原料を還元し、更に溶融させて、還元鉄を製造する際に、前記移動型炉床炉で発生するダストの一部を前記混合原料に混合して循環使用し、前記ダストの残部を高亜鉛含有ダストとして分離することを特徴とする還元鉄製造方法。
(2)混合原料中の亜鉛濃度に基づいて、高亜鉛含有ダストとして分離するダストの量を決定することを特徴とする(1)に記載の還元鉄製造方法。
(3)高亜鉛含有ダストとして分離するダストの量(kg/t−Fe)を下記(Y)式により決定することを特徴とする(2)に記載の還元鉄製造方法。
(高亜鉛含有ダストとして分離するダストの量(kg/t−Fe))≦10×Σ{(原料i中亜鉛濃度)×(原料i原単位)}・・・(Y)
ただし、原料iは混合原料中の各成分を示す。
(4)高亜鉛含有ダストとして分離するダストの量(kg/t−Fe)を下記(Z)式により決定することを特徴とする(2)に記載の還元鉄製造方法。
(高亜鉛含有ダストとして分離するダストの量(kg/t−Fe))≦2×Σ{(原料i中亜鉛濃度)×(原料i原単位)}・・・(Z)
ただし、原料iは混合原料中の各成分を示す。
(5)移動型炉床炉で発生するダストの亜鉛濃度を分析し、該分析濃度に基づいて高亜鉛含有ダストとして分離するダストの量を決定することを特徴とする(1)に記載の還元鉄製造方法。
(6)移動型炉床炉で発生するダストの亜鉛濃度が10mass%以上になるように、高亜鉛含有ダストとして分離するダストの量を決定することを特徴とする(5)に記載の還元鉄製造方法。
(7)移動型炉床炉で発生するダストの亜鉛濃度が50mass%以上になるように、高亜鉛含有ダストとして分離するダストの量を決定することを特徴とする(5)に記載の還元鉄製造方法。
ここで、原料iは、混合原料中の成分を示す。例えば、鉄鉱石、フラックス、石炭、他所で発生したダスト等である。なお、原料i原単位とは還元鉄1トンを製造するために必要な原料i量であり、自家発生ダストの抜き出し量は還元鉄1トンを製造するときに、自家発生ダストのうち循環使用せず、高亜鉛含有ダストとして抜き出すダスト量である。Σは各原料iについての亜鉛濃度と原単位の積を合算することを示すものである。
なお、鉄鉱石原単位とは還元鉄1トンを製造するために必要な鉄鉱石量であり、自家発生ダスト抜き出し量は還元鉄1トンを製造するときに、自家発生ダストのうち循環使用せず、高亜鉛含有ダストとして抜き出すダスト量である。
鉄鉱石以外の原料に亜鉛分が含まれない場合等、他の成分の影響が無視できる場合については上記(Y)式は、下記の(Y2)式で示される。
(自家発生ダストの抜き出し量(kg/t−Fe))≦10×(鉱石中亜鉛濃度)×(鉱石原単位)・・・(Y2)
また、自家発生ダストの亜鉛濃度が50mass%以上であれば、このダストを高亜鉛含有ダストとして抜き出し、直接処理して、粗酸化亜鉛を得ることができる。上記(W)式を用いれば10mass%以上の亜鉛濃度を得るためには自家発生ダスト抜き出し量は以下の(Z)式を満たす必要がある。原料iは、上記と同様混合原料中の成分を示す。
鉄鉱石以外の原料に亜鉛分が含まれない場合等、他の成分の影響が無視できる場合については上記(Z)式は、下記の(Z2)式で示される。
なお、上記において「自家発生ダストの抜き出し量」は、「高亜鉛含有ダストとして分離するダストの量」と同意である。
2 炉体
2a 予熱帯
2b 還元帯
2c 溶融帯
2d 冷却帯
3 回転炉床
4 混合原料
5 バーナー
6 装入装置
7 排出装置
8 冷却装置
11 鉱石ホッパー
12 石炭ホッパー
13 造滓材ホッパー
14 混合機
15 回転炉床炉
16 還元鉄排出口
17 排ガスダクト用バグフィルター
18 粉体搬送用ローリー
19 吸引ファン
20 煙突
21(21a、21b) 自家発生ダスト搬送コンベアー
22 自家発生ダスト貯蔵ホッパー
Claims (7)
- 鉄鉱石と炭素系固体還元材と造滓材とを混合した混合原料を移動型炉床炉の炉床上に積載し、該炉床上部から熱供給して前記混合原料を還元し、更に溶融させて、還元鉄を製造する際に、前記移動型炉床炉で発生するダストの一部を前記混合原料に混合して循環使用し、前記ダストの残部を高亜鉛含有ダストとして分離することを特徴とする還元鉄製造方法。
- 混合原料中の亜鉛濃度に基づいて、高亜鉛含有ダストとして分離するダストの量を決定することを特徴とする請求項1に記載の還元鉄製造方法。
- 高亜鉛含有ダストとして分離するダストの量(kg/t−Fe)を下記(Y)式により決定することを特徴とする請求項2に記載の還元鉄製造方法。
(高亜鉛含有ダストとして分離するダストの量(kg/t−Fe))≦10×Σ{(原料i中亜鉛濃度)×(原料i原単位)}・・・(Y)
ただし、原料iは混合原料中の各成分を示す。 - 高亜鉛含有ダストとして分離するダストの量(kg/t−Fe)を下記(Z)式により決定することを特徴とする請求項2に記載の還元鉄製造方法。
(高亜鉛含有ダストとして分離するダストの量(kg/t−Fe))≦2×Σ{(原料i中亜鉛濃度)×(原料i原単位)}・・・(Z)
ただし、原料iは混合原料中の各成分を示す。 - 移動型炉床炉で発生するダストの亜鉛濃度を分析し、該分析濃度に基づいて高亜鉛含有ダストとして分離するダストの量を決定することを特徴とする請求項1に記載の還元鉄製造方法。
- 移動型炉床炉で発生するダストの亜鉛濃度が10mass%以上になるように、高亜鉛含有ダストとして分離するダストの量を決定することを特徴とする請求項5に記載の還元鉄製造方法。
- 移動型炉床炉で発生するダストの亜鉛濃度が50mass%以上になるように、高亜鉛含有ダストとして分離するダストの量を決定することを特徴とする請求項5に記載の還元鉄製造方法。