JP2009507113A - 金属表面及びポリマー表面用のポリシラザン含有被覆材 - Google Patents
金属表面及びポリマー表面用のポリシラザン含有被覆材 Download PDFInfo
- Publication number
- JP2009507113A JP2009507113A JP2008529500A JP2008529500A JP2009507113A JP 2009507113 A JP2009507113 A JP 2009507113A JP 2008529500 A JP2008529500 A JP 2008529500A JP 2008529500 A JP2008529500 A JP 2008529500A JP 2009507113 A JP2009507113 A JP 2009507113A
- Authority
- JP
- Japan
- Prior art keywords
- polysilazane
- use according
- sir
- coating
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
-(SiR'R''-NR''')n- (1)
[式中、R'、R''、R'''は、同一かまたは異なり、そして互いに独立して水素または場合によっては置換されたアルキル基、アリール基、ビニル基もしくは(トリアルコキシシリル)アルキル基を表し、この際、nは整数であり、そしてnは、該ポリシラザンが、150〜150,000g/モルの数平均分子量を有するような数である]
で表されるポリシラザンを溶剤中に含む溶液または溶剤中の複数種のこのようなポリシラザンの混合物であることを特徴とする、前記使用。更に本発明は、上記被膜の形成方法にも関する。
Description
-(SiR'R''-NR''')n- (1)
[式中、R'、R''、R'''は、同一かまたは異なり、そして互いに独立して水素、または場合によっては置換されたアルキル基、アリール基、ビニル基もしくは(トリアルコキシシリル)アルキル基を表し、この際、nは整数であり、そしてnは、該ポリシラザンが150〜150,000g/モルの数平均分子量を有するような数である]
で表されるポリシラザンまたは複数種のポリシラザンの混合物を溶剤中に含む溶液を含む、金属表面及びポリマーの被覆のためにポリシラザンを使用することである。
-(SiR'R''-NR''')n-(SiR*R**-NR***)p- (2)
[式中、R'、R''、R'''、R*、R**及びR***は、互いに独立して、水素、または場合によっては置換されたアルキル基、アリール基、ビニル基または(トリアルコキシシリル)アルキル基を表し、この際、n及びpは、該ポリシラザンが150〜150,000g/モルの数平均分子量を有するような数である]
で表されるポリシラザンを含む。
− R'、R'''及びR***が水素を表し、そしてR''、R*及びR**がメチルを表す化合物;
− R'、R'''及びR***が水素を表し、R''、R*がメチルを表し、そしてR**がビニルを表す化合物;
− R'、R'''、R*及びR***が水素を表し、R''、R*がメチルを表す化合物、
である。
-(SiR'R''-NR''')n-(SiR*R**-NR***)p -(SiR1, R2-NR3)q- (3)
[式中、R'、R''、R'''、R*、R**、R***、R1、R2及びR3は、互いに独立して、水素、または場合によっては置換されたアルキル基、アリール基、ビニル基もしくは(トリアルコキシシリル)アルキル基を表し、この際、n、p及びqは、該ポリシラザンが150〜150,000g/モルの数平均分子量を有するような数である]
で表されるポリシラザンも同様に好ましく使用される。
R3が(トリエトキシシリル)プロピルを表し、そしてR1がアルキルまたは水素を表す化合物が特に好ましい。
調合物1
コポリマー1 35〜40 %
ポリアクリレート 0.5〜1 %
流動制御添加剤 < 2.0 %
上記の各成分を酢酸ブチル中に溶解し、そしてディスソルバーを用いて均一化する。酢酸ブチルの量は、合計で100%の被覆材調合物が得られるように計算される。
コポリマー1 35〜40 %
ポリアクリレート 0.5〜1 %
流動制御添加剤 < 2.0 %
AMEO < 2.0 %
上記の各成分を酢酸ブチル中に溶解し、そしてディスソルバーを用いて均一化する。酢酸ブチルの量は、合計で100%の被覆材調合物が得られるように計算される。
コポリマー2 35〜40 %
ポリアクリレート 0.5〜1 %
流動制御添加剤 < 2.0 %
AMEO < 2.0 %
上記の各成分を酢酸ブチル中に溶解し、そしてディスソルバーを用いて均一化する。酢酸ブチルの量は、合計で100%の被覆材調合物が得られるように計算される。
コポリマー2 35〜40 %
ポリアクリレート 0.5〜1 %
流動制御添加剤 < 2.0 %
上記の各成分を酢酸ブチル中に溶解し、そしてディスソルバーを用いて均一化する。酢酸ブチルの量は、合計で100%の被覆材調合物が得られるように計算される。
コポリマー2 20〜25 %
ポリアクリレート 0.5〜1 %
流動制御添加剤 < 2.0 %
AMEO < 2.0 %
増粘剤 < 5.0 %
上記の各成分を酢酸ブチル中に溶解し、そしてディスソルバーを用いて均一化する。酢酸ブチルの量は、合計で100%の被覆材調合物が得られるように計算される。
コポリマー3 35〜40 %
ポリアクリレート 0.5〜1 %
流動制御添加剤 < 2.0 %
上記の各成分を酢酸ブチル中に溶解し、そしてディスソルバーを用いて均一化する。酢酸ブチルの量は、合計で100%の被覆材調合物が得られるように計算される。
被覆材調合物の塗布
スプレーガンを用いた塗布の際には、塗布される被覆材の量、被膜の均一性及びスプレー強度が最適になるようにガンの設定を選択しなければならない。この設定は当業者に既知である。
参考ホイールリム、通例のホイールリムコート、ポリアクリレート粉体塗料クリアコートを含む多層コート系
参考例2:
参考ホイールリム、通例のホイールリムコート、溶剤系クリアコートを含む多層コート系
ブレーキダストを水で懸濁させ、そして上記の試験片上に塗る。次いで、これらの試験片を2時間160℃の条件下に置き、水ですすぎ、軽く拭きそして評価する(評点)。
Claims (17)
- 金属表面、ポリマー及び塗装の上の永久的な被膜としてのポリシラザンの使用であって、前記ポリシラザンが、以下の一般式1
-(SiR'R''-NR''')n- (1)
[式中、R'、R''、R'''は、同一かまたは異なり、そして互いに独立して水素、または場合によっては置換されたアルキル基、アリール基、ビニル基もしくは(トリアルコキシシリル)アルキル基を表し、この際、nは整数であり、そしてnは、該ポリシラザンが150〜150,000g/モルの数平均分子量を有するような数である]
で表されるポリシラザンまたは複数種のポリシラザンの混合物を溶剤中に含む溶液であることを特徴とする、前記使用。 - R'、R''、R'''が、互いに独立して、水素、メチル、エチル、プロピル、iso-プロピル、ブチル、iso-ブチル、tert.-ブチル、フェニル、ビニルまたは3-(トリエトキシシリル)プロピル、3-(トリメトキシシリルプロピル)からなる群から選択される基を表すことを特徴とする、請求項1の使用。
- 上記ポリシラザンが、次式(2)
-(SiR'R''-NR''')n-(SiR*R**-NR***)p - (2)
[式中、R’、R’’、R’’’、R*、R**及びR***は、互いに独立して、水素または場合によっては置換されたアルキル基、アリール基、ビニル基もしくは(トリアルコキシシリル)アルキル基を表し、この際、n及びpは整数であり、そしてnは、該ポリシラザンが、150〜150,000g/モルの数平均分子量を有するような数である]
で表されるポリシラザンであることを特徴とする、請求項1の使用。 - − R'、R'''及びR***が水素を表し、そしてR''、R*及びR**がメチルを表すか;
− R'、R'''及びR***が水素を表し、R''、R*がメチルを表し、そしてR**がビニルを表すか、または
− R'、R'''、R*及びR***が水素を表し、そしてR''及びR**がメチルを表す、
ことを特徴とする、請求項3の使用。 - 上記ポリシラザンが、次式(3)
-(SiR'R''-NR''')n-(SiR*R**-NR***)p -(SiR1, R2-NR3)q- (3)
[式中、R'、R''、R'''、R*、R**、R***、R1、R2及びR3は、互いに独立して、水素、または場合によっては置換されたアルキル基、アリール基、ビニル基もしくは(トリアルコキシシリル)アルキル基を表し、この際、n、p及びqは整数であり、そしてnは、該ポリシラザンが150〜150,000g/モルの数平均分子量を有するような数である]
で表されるポリシラザンであることを特徴とする、請求項1の使用。 - R’、R'''及びR***が水素を表し、R''、R*、R**及びR2がメチルを表し、R3が(トリエトキシシリル)プロピルを表し、そしてR1がアルキルまたは水素を表すことを特徴とする、請求項5の使用。
- 上記ポリシラザン溶液が、ポリシラザンを1〜80重量%、好ましくは5〜50重量%、特に好ましくは10〜40重量%の割合で含むことを特徴とする、請求項1〜6の少なくとも一つの使用。
- 上記ポリシラザン溶液が触媒を0.001〜10重量%の割合で含むことを特徴とする、請求項1〜7の少なくとも一つの使用。
- 有機アミン、酸、金属、金属塩、またはこれらの化合物の混合物を触媒として使用することを特徴とする、請求項8の使用。
- 反応性基を含まない水不含の有機溶剤が溶剤として使用されることを特徴とする、請求項1〜9の少なくとも一つの使用。
- 上記調合物が、調合物の粘度、下地の濡れ、成膜性、潤滑作用または曝気挙動に影響を及ぼす添加剤及びバインダーを含むことを特徴とする、請求項1〜10の少なくとも一つの使用。
- 上記調合物が無機ナノ粒子を含むことを特徴とする、請求項1〜11の少なくとも一つの使用。
- 金属表面またはポリマー表面上に永久的な被膜を形成する方法であって、次式(1)
-(SiR'R''-NR''')n- (1)
[式中、R'、R''、R'''は、同一かまたは異なり、水素または場合によっては置換されたアルキル基、アリール基もしくは(トリアルコキシシリル)アルキル基を表し、この際、nは整数であり、そしてnは、該ポリシラザンが150〜150,000g/モルの数平均分子量を有するような数である]
で表されるポリシラザンまたは複数種のポリシラザンの混合物を溶剤中に含む溶液を金属表面上に塗布しそしてその被膜を硬化することを特徴とする、前記方法。 - 請求項1〜13の少なくとも一つに記載の被覆材で塗装された金属表面を有する物品。
- 金属表面が、鉄、鋼、亜鉛メッキ鋼、アルミニウム、クロム、ニッケル、亜鉛、チタン、バナジウム、モリブデン、マグネシウムまたは銅の合金であることを特徴とする、請求項14の金属表面を有する物品。
- ポリマーが、ポリカーボネート、ポリメチルメタクリレート、ポリエーテルエーテルケトン、ポリエチレン、ポリプロピレン、ポリアミド、ポリエチレンテレフタレートであることを特徴とする、請求項14の金属表面を有する物品。
- 塗料がアクリレート、エポキシまたはウレタンに基づく塗料であることを特徴とする、請求項14の塗装表面を有する物品。