JP2009167298A - 難変色性の軟質ポリウレタン発泡体 - Google Patents
難変色性の軟質ポリウレタン発泡体 Download PDFInfo
- Publication number
- JP2009167298A JP2009167298A JP2008007125A JP2008007125A JP2009167298A JP 2009167298 A JP2009167298 A JP 2009167298A JP 2008007125 A JP2008007125 A JP 2008007125A JP 2008007125 A JP2008007125 A JP 2008007125A JP 2009167298 A JP2009167298 A JP 2009167298A
- Authority
- JP
- Japan
- Prior art keywords
- foam
- polyol
- polyether polyol
- polyurethane foam
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】難変色性の軟質ポリウレタン発泡体は、ポリオール類、ポリイソシアネート類、発泡剤及び触媒を含有する発泡体原料を反応及び発泡させてなるものである。この場合、ポリオール類は質量平均分子量が600〜1500のポリエーテルポリオールを含み、そのポリエーテルポリオールの含有量がポリオール類100質量部当たり50〜100質量部であると共に、ポリイソシアネート類はトリレンジイソシアネートであって、そのイソシアネート指数が90〜120である。前記ポリエーテルポリオールはアルキレンオキシド単位を有し、該アルキレンオキシド単位がプロピレンオキシド単位で構成されていることが好ましい。
【選択図】なし
Description
請求項1に係る難変色性の軟質ポリウレタン発泡体では、ポリオール類は質量平均分子量が600〜1500のポリエーテルポリオールを含み、そのポリエーテルポリオールの含有量がポリオール類100質量部当たり50〜100質量部である。このため、ポリオール類は比較的低分子量(中分子量)であって、発泡体の架橋密度が高くなり、紫外線照射により発泡体が分解しにくくなると同時に、発泡体が酸化窒素に曝露されたとき酸化窒素を吸収しにくくなる。上記ポリオール類の構成に加えて、ポリイソシアネート類はトリレンジイソシアネートであって、そのイソシアネート指数が90〜120に設定されていることから、樹脂化反応や泡化反応の反応性が良く、良好な発泡体が得られる。従って、紫外線及び大気中の酸化窒素に基づく変色を抑制することができると共に、機械的物性を向上させることができる。
本実施形態の難変色性(難着色性又は難黄変性)の軟質ポリウレタン発泡体(以下、単に軟質ポリウレタン発泡体、ポリウレタン発泡体又は発泡体とも称する)は、ポリオール類、ポリイソシアネート類、発泡剤及び触媒を含有する発泡体原料を反応及び発泡させてなるものである。この場合、ポリオール類は質量平均分子量が600〜1500のポリエーテルポリオールを含み、そのポリエーテルポリオールの含有量がポリオール類100質量部当たり50〜100質量部に設定される。また、ポリイソシアネート類はトリレンジイソシアネートであって、そのイソシアネート指数が90〜120に設定される。ここで、軟質ポリウレタン発泡体は軽量で、一般にセルが連通する連続気泡構造を有し、柔軟性があって、かつ復元性を有するものをいう。以下に、発泡体原料について順に説明する。
・ 本実施形態の難変色性の軟質ポリウレタン発泡体では、ポリオール類は質量平均分子量が600〜1500のポリエーテルポリオールを含み、そのポリエーテルポリオールの含有量がポリオール類100質量部当たり50〜100質量部である。このため、ポリオール類は比較的低分子量であって、発泡体の架橋密度が高くなり、紫外線照射により発泡体が分解しにくくなると同時に、発泡体が酸化窒素に曝露されたとき酸化窒素を吸収しにくくなる。上記ポリオール類の構成に加えて、ポリイソシアネート類はトリレンジイソシアネートであって、そのイソシアネート指数が90〜120に設定されていることから、樹脂化反応や泡化反応の反応性が良く、良好な発泡体が得られる。従って、紫外線及び大気中の酸化窒素に基づく変色を抑制することができると共に、硬さ、ひずみなどの機械的物性を向上させることができる。よって、この発泡体をドレス、ブラウス等の肩パッド、ブラジャー等のパッドなどに好適に使用することができる。
(実施例1〜20及び比較例1〜8)
ポリオール類、ポリイソシアネート類、発泡剤、整泡剤、触媒及び整泡剤を含有する軟質ポリウレタン発泡体の発泡体原料を、表1及び表2に示す組成にて調製した。表1及び表2における発泡体原料の数値は質量部を表す。そして、発泡体原料を常温で混合し、常法に従って反応及び発泡(スラブ発泡)させることにより、縦400mm、横400mm及び厚さ300mm程度の軟質ポリウレタン発泡体(ブロック体)を製造した。各物性の測定は、前記ブロック体を裁断加工することにより得られるサンプルについて行った。
ポリオールGP400:ポリエーテルポリオール、質量平均分子量400、水酸基価421mgKOH/g、1分子中の水酸基数3、アルキレンオキシド単位はプロピレンオキシドのみで構成されたもの、三洋化成工業(株)製、GP400
ポリオールGP600:ポリエーテルポリオール、質量平均分子量600、水酸基価280mgKOH/g、1分子中の水酸基数3、アルキレンオキシド単位はプロピレンオキシドのみで構成されたもの、三洋化成工業(株)製、GP600
ポリオールG700:ポリエーテルポリオール、質量平均分子量700、水酸基価225mgKOH/g、1分子中の水酸基数3、アルキレンオキシド単位はプロピレンオキシドのみで構成されたもの、旭電化工業(株)製、G700
ポリオールGP1000:ポリエーテルポリオール、質量平均分子量1000、水酸基価168mgKOH/g、1分子中の水酸基数3、アルキレンオキシド単位はプロピレンオキシドのみで構成されたもの、三洋化成工業(株)製、GP1000
ポリオールG1500:ポリエーテルポリオール、質量平均分子量1500、水酸基価112mgKOH/g、1分子中の水酸基数3、アルキレンオキシド単位はプロピレンオキシドのみで構成されたもの、旭電化工業(株)製、G1500
ポリオールGP3000:ポリエーテルポリオール、質量平均分子量3000、水酸基価56mgKOH/g、1分子中の水酸基数3、アルキレンオキシド単位はプロピレンオキシドのみで構成されたもの、三洋化成工業(株)製、GP3000
ポリオールGEP2800:ポリエーテルポリオール、質量平均分子量3000、水酸基価65mgKOH/g、1分子中の水酸基数3、アルキレンオキシド単位はプロピレンオキシド50質量%及びエチレンオキシド50質量%で構成されたもの、三洋化成工業(株)製、GEP2800
アミン触媒33LV:トリエチレンジアミン、日本乳化剤(株)製、33LV
整泡剤L626:シリコーン整泡剤、モメンティブ・パフォーマンス・マテリアルズ社製、L626
ポリイソシアネートT65:2,4−トリレンジイソシアネート65質量%と2,6−トリレンジイソシアネート35質量%との混合物、日本ポリウレタン工業(株)製、コロネートT65
得られた軟質ポリウレタン発泡体のサンプルについて、見掛け密度、硬さ及び変色性を下記に示す方法で測定した。変色性については、初期及び紫外線(UV)照射後、酸化窒素(NOx)暴露後の黄色度(YI)を測定し、初期値との差を色差(ΔYI)として算出した。
硬さ(N):JIS K 6400−2(2004)に準拠して測定した値である。
・ ポリオール類として、質量平均分子量が600〜1500のポリエーテルポリオールを複数組合せ、ポリオール類全体の質量平均分子量、水酸基価、水酸基数などを調整して使用することもできる。
・ 本発明の軟質ポリウレタン発泡体では、酸化硫黄(SOx)などの大気中の汚染ガスを吸収することができ、それによる変色を抑制することができる。
・ 色差計により測定された、紫外線照射前後及び酸化窒素曝露前後における変色性を示す色差ΔYIが70以下であることを特徴とする請求項1から請求項4のいずれか1項に記載の難変色性の軟質ポリウレタン発泡体。このように構成した場合、請求項1から請求項4のいずれかに係る発明の効果に加えて、紫外線及び大気中の酸化窒素による変色を十分に抑制することができる。
Claims (4)
- ポリオール類、ポリイソシアネート類、発泡剤及び触媒を含有する発泡体原料を反応及び発泡させてなる軟質ポリウレタン発泡体であって、
前記ポリオール類は質量平均分子量が600〜1500のポリエーテルポリオールを含み、そのポリエーテルポリオールの含有量がポリオール類100質量部当たり50〜100質量部であると共に、ポリイソシアネート類はトリレンジイソシアネートであって、そのイソシアネート指数が90〜120であることを特徴とする難変色性の軟質ポリウレタン発泡体。 - 前記ポリエーテルポリオールはアルキレンオキシド単位を有し、該アルキレンオキシド単位がプロピレンオキシド単位で構成されていることを特徴とする請求項1に記載の難変色性の軟質ポリウレタン発泡体。
- 前記ポリエーテルポリオールの水酸基価は100〜300mgKOH/gであることを特徴とする請求項1又は請求項2に記載の難変色性の軟質ポリウレタン発泡体。
- 前記ポリエーテルポリオールの1分子中における水酸基数は2〜4であることを特徴とする請求項1から請求項3のいずれか1項に記載の難変色性の軟質ポリウレタン発泡体。