JP2009160659A - ろう付け材及びそれで得られる製品 - Google Patents
ろう付け材及びそれで得られる製品 Download PDFInfo
- Publication number
- JP2009160659A JP2009160659A JP2009099110A JP2009099110A JP2009160659A JP 2009160659 A JP2009160659 A JP 2009160659A JP 2009099110 A JP2009099110 A JP 2009099110A JP 2009099110 A JP2009099110 A JP 2009099110A JP 2009160659 A JP2009160659 A JP 2009160659A
- Authority
- JP
- Japan
- Prior art keywords
- brazing
- iron
- brazing material
- product
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ろう付けによって物品を接合するための鉄を母材とするろう付け材は、鉄を別として、質量%で、0〜40%、好ましくは9〜30%のCr、0〜16%、好ましくは0〜8%、より好ましくは0〜5%のMn、0〜25%のNi、0〜1%のN、及び最大7%のMo6%未満のSi及び/または0〜2%、好ましくは0〜1.5%のB、及び/または0〜15%のPを含む合金であって、B、P、Siの組み合わせまたは個別の添加により、ろう付け材が完全に溶融される温度である液相線温度が低下される合金に相当する。ろう付け製品は、B及び/またはP及び/またはSiを液相線温度を低下させる成分として合金化した、鉄を母材とするろう付け材によって、鉄を母材とする物品をろう付けすることによって製造される。
【選択図】なし
Description
本発明はまた、本発明による鉄を母材とするろう付け材によって鉄を母材とする物品をろ
う付けして製造されるろう付け製品を含む。
でろう付けされる。
固定または接合するプロセスである。
のための材料を含む。
n、5−8%のSi,4−6%のCu、0.6−1.8%のBと他より少ない元素を別と
して残りNiを含む。US4314661は他の種類のNiを母材とした合金が記載され
、これは原子%で0−4%のFe、0−21%のCr,0−19%のB、0−12%のS
i、0−22%のPと残りのNiを含む。
け材はくっきりと明確な融点を持つが、一方、ニッケルを母材とするろう付け材は合金で
あることによってしばしば溶融間隔を持つ。
しば用いられる。しかしながら、銅は全ての用途には適していない。銅のろう付け材の食
品用途での使用は許されていないが、地域暖房用や水道設備用の板状熱交換器に用いられ
る。
食品用途に許されている。
に用いられると、ろう付け接合部の組成が、接合された物品の組成とは大きな相違がある
。これは化学的特性または機械的特性に好ましくない相違となり得る。
度を低下させる添加成分を含むろう付け材を用いて、ろう付けすることによって物品を接
合する可能性を提供する。
板状熱交換器としての装置を製造する可能性を提供する。本発明は、主として、ろう付け
材が、鉄を別として、質量%として、0〜40%、好ましくは9〜30%のCr、0〜1
6%、好ましくは0〜8%、より好ましくは0〜5%のMn、0〜25%のNi、0〜1
%のN、最大7%のMo及び6%未満のSi及び/または0〜2%、好ましくは0〜1.
5%のB、及び/または0〜15%のPを含む合金からなり、ボロン、リン及びシリコン
の組み合わせまたは個別の添加により、ろう付け材が完全に溶融される温度である液相線
温度が低下されることを特徴とする。
付け材は、常にFeとCrを含まなければならない。
実用的な量は、上記の範囲にしなければならない。例えばSiは、炭化ケイ素または窒化
ケイ素の状態や、酸素と結合されて、または他の方法で焼結されるため、Siの分析値は
かなり高くなるかもしれない。同様な理由によってBまたはPの分析値も高くなるかもし
れない。
の他を含んでも良い。組成の変化は少量で不可避の量のC、O及びSの混在物の影響であ
ろう。
インデックス=P%+1.1×Si%+3×B%
ここで該インデックスの値は4.5〜18にすべきである。
このようなインゴットの粉砕で好ましくは製造される。他の製造方法は溶融スピニングで
ある。
物品をB及び/またはP及び/またはSiのような液相線を低下させる成分を含む合金の
鉄を母材とするろう付け材でろう付けしたものであることを特徴とするものである。鉄を
母材とするろう付け材は主請求項に記載の組成が好ましい。
9〜30%のCrを含む。
の熱交換流体のためのもので、それは鉄を母材とする薄い壁を有する熱交換板の幾つかを
、鉄を母材とするろう付け材によってろう付けして製造された少なくとも一つの板状パッ
ケージを含む。熱交換板は相対で熱交換流体のための内部スペースの輪郭を定める。鉄を
母材とする板材と比べて、内部または周囲において局部的に高いB、P、Si量を有するろう
付け接合部は、鉄を母材とするろう付け材の組成に近い冶金組成を持つ。
いられていた。驚くべきことに、今や、接合したい物品の材料と同じ組成の母材から開始
できることが見つけられた。このような材料をシリコン及び/またはホウ素及び/または
リンと合金化することによってうまく機能するろう付け材が得られる。鉄とSi、B及びPの
二相ダイアグラムの検討によって、Fe-Si合金が約19%のSiで1212℃の最低融点を持つ
ことを見出すであろう。Fe−B合金については、約4%のBで1174℃の融点の最低
がある。Fe−P系では約10%のPで1048℃の融点の最低がある。
を含む合金が用いられる。また多くの合金にMoとMnが含まれる。このような合金に異
なった量のホウ素及び/またはリン及び/またはシリコンを添加する効果を、相ダイアグ
ラムを用いて理論的に確立する試みは、次元数が合金の成分の数と同じとなるので、ほと
んど不可能である。
は1200℃以下であるべきである。
添加すると、液相線温度が低下し、好ましいろう付け材が得られることが見出された。
は全ての試料は溶融し、ろう付け接合物が得られ、またすべての接合物で機械強度が得ら
れた。
しこれを破砕した後に、粉砕して調製されても良い。材料の壊れやすい性質はこの製造方
法で利用される。インゴットキャスティングの欠点は、融解間隔がはっきりしないか広い
という不均一性物質となる偏析の危険がありことである。より小さなインゴット及び/ま
たは急冷は偏析の危険を減らす。インゴットキャスティングにおいては、真空キャスティ
ングまたはガスシールキャスティングによって、空気との接触を最小にすることが重要で
ある。機械的処理によって、ろう付け材のエネルギー含有量が増加しそれに伴ってその反
応性も増加する。
製造方法によって変化する。破砕され粉砕された粒子は角があり先がとがっている。水で
微粉化されたものは団塊状(nodular)であり、ガスで微粉化されたものはほとん
ど球状である。この粒子形状の相違はろう付けに使用する際にろう付け材に多少の性質の
変化を与える。異なった微粉化法の選択、破砕/粉砕の程度及びふるい分けとの組み合わ
せによって粒子サイズ分布が調整できるであろう。水微粉化においては、ガス微粉化より
も酸素ポテンシャルが高くなるので、一般に酸素含有率が高くなるであろう。高い酸素含
有率は、材料の酸化物の形成をもたらし、ろう付け接合の機械的性質に悪い影響を与える
であろう。ろう付け材中の有効なSi及び/またはB及び/またはPの割合は低くなるで
あろう。これはこのために融解範囲が移動することを意味する。
却され、例えば箔が形成されるような方法で行われる。通常の連続箔製造においては、冷
却表面は銅または銅合金で作られた冷却ロールよりなる。非晶性の箔を得ることができる
が、この場合、通常はホウ素が加えられる。
れたいかなる方法によって得られた粉末ろう付け材も、適当な方法で適用するためにバイ
ンダー中に懸濁させても良い。
Claims (7)
- ろう付けによって物品を接合するための鉄を母材とするろう付け材であって、該ろう付
け材が、鉄を別として、質量%で、0〜40%、好ましくは9〜30%のCr、0〜16
%、好ましくは0〜8%、より好ましくは0〜5%のMn、0〜25%のNi、0〜1%
のN、最大7%のMo及び6%未満のSi及び/または0〜2%、好ましくは0〜1.5
%のB、及び/または0〜15%のPを含む合金からなり、該B、P、Siの組み合わせ
または個別の添加により、ろう付け材が完全に溶融される温度である液相線温度が低下さ
れることを特徴とするろう付け材。 - 融点低下成分がろう付け材に次式
インデックス=P%+1.1×Si%+3×B%
ここで該インデックスの値は4.5〜18である
による量で添加されることを特徴とする請求項1記載の鉄を母材とするろう付け材。 - ガス微粉化もしくは水微粉化もしくは上記組成のインゴットの破砕または溶融物のスピ
ニングによって製造されることを特徴とする請求項1または2記載の鉄を母材とするろう
付け材。 - 0〜20%のHf及び/または0−2%のCを含むことを特徴とする先の請求項のいず
れか記載の鉄を母材とするろう付け材。 - 鉄を母材とする物品をろう付けすることによって製造されるろう付け製品であって、B
及び/またはP及び/またはSiを液相線温度を低下させる成分として合金化した鉄を母
材とするろう付け材によって接合されることを特徴とするろう付け製品。 - 鉄を母材とする物品と鉄を母材とするろう付け材が9−30%のCrを含むことを特徴
とする請求項5記載のろう付け製品。 - 請求項6記載のろう付け製品であって、該製品は少なくとも二つの熱交換流体のための
板状熱交換器であって、鉄を母材とする薄い壁を有する熱交換板の幾つかを、鉄を母材と
するろう付け材によってろう付けして製造された少なくとも一つの板状パッケージを含み
、該熱交換板は相対で熱交換流体のための内部スペースの輪郭を定め、得られたろう付け
接合部が、鉄を母材とする板材と比べて、内部または周囲において局部的に高いB、P、Si
量を有し、鉄を母材とするろう付け材の組成に近い冶金組成を持つことを特徴とするろう
付け製品。