JP2008138142A - Polymerizable liquid crystal composition and optically anisotropic thin film - Google Patents
Polymerizable liquid crystal composition and optically anisotropic thin film Download PDFInfo
- Publication number
- JP2008138142A JP2008138142A JP2006328530A JP2006328530A JP2008138142A JP 2008138142 A JP2008138142 A JP 2008138142A JP 2006328530 A JP2006328530 A JP 2006328530A JP 2006328530 A JP2006328530 A JP 2006328530A JP 2008138142 A JP2008138142 A JP 2008138142A
- Authority
- JP
- Japan
- Prior art keywords
- formula
- independently
- liquid crystal
- component
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、重合性官能基を有する液晶化合物を含む重合性液晶組成物、該組成物からなる重合体およびこれらの用途に関する。 The present invention relates to a polymerizable liquid crystal composition containing a liquid crystal compound having a polymerizable functional group, a polymer comprising the composition, and uses thereof.
液晶相を有する重合性化合物は重合によって光学補償(optical compensation)などの機能を有する重合体を与える。これは、液晶分子の配向が重合によって固定されるからである。このような重合体の機能を活用するために、種々の重合性化合物が開発されているが、1つの重合性化合物では充分な機能を満たさないことがある。そのため、幾つかの重合性化合物を用いて組成物を調製し、該組成物を重合させるという試みがなされている。 The polymerizable compound having a liquid crystal phase gives a polymer having a function such as optical compensation by polymerization. This is because the alignment of liquid crystal molecules is fixed by polymerization. In order to utilize the function of such a polymer, various polymerizable compounds have been developed, but one polymerizable compound may not satisfy a sufficient function. Therefore, an attempt has been made to prepare a composition using several polymerizable compounds and polymerize the composition.
ネマチック状態で配向させた重合性液晶化合物を重合させると、配向状態が固定化されて光学異方性を有するフィルムが得られる。このような光学異方性を有するフィルムは、液晶表示素子の光学補償膜として活用される。中でもハイブリッドネマチック配向が固定化されたフィルムは、ツイステッドネマチック型液晶表示素子の視野角補償素子として使用することができる。また、偏光板と組み合せることにより楕円偏光板として使用することができる。 When the polymerizable liquid crystal compound aligned in the nematic state is polymerized, the alignment state is fixed and a film having optical anisotropy is obtained. Such a film having optical anisotropy is utilized as an optical compensation film of a liquid crystal display element. Among them, a film in which hybrid nematic alignment is fixed can be used as a viewing angle compensation element of a twisted nematic liquid crystal display element. Moreover, it can be used as an elliptically polarizing plate by combining with a polarizing plate.
重合性液晶材料を重合して得られる光学異方性を有する液晶薄膜の製造には、次のような特性が求められている。重合前の特性としては、室温で十分安定したネマチック相を有し、さらに、重合前後で均一な配向性を示し、重合後には所望の配向形態を容易に達成し、薄膜の表面にベタつきがない等である。 The following characteristics are required for the production of a liquid crystal thin film having optical anisotropy obtained by polymerizing a polymerizable liquid crystal material. As characteristics before polymerization, it has a nematic phase that is sufficiently stable at room temperature, shows uniform orientation before and after polymerization, easily achieves a desired orientation form after polymerization, and has no stickiness on the surface of the thin film Etc.
これまでのハイブリッド配向を有する組成物(たとえば、特許文献1および2参照)は、配向に関しては均一で良好であった。しかしながら、重合体の製造工程において、組成物を基板に塗布し、予備焼成した後に、紫外線照射によって重合体を得るまでの間、直ちに結晶が析出することはなかったものの、組成物の室温液晶相安定性がまだ十分とはいえなかった。
本発明の課題は、室温で十分安定したネマチック相を有し、かつ、均一なハイブリッド配向性を示す重合体を得ることを可能にする組成物を提供することである。 An object of the present invention is to provide a composition that makes it possible to obtain a polymer having a nematic phase sufficiently stable at room temperature and showing uniform hybrid orientation.
本発明は、以下に示す重合性液晶組成物、該組成物を重合させることによって得られる重合体、およびこれらの用途を含む。
[1] 第1成分として下記式(1−1)および式(1−2)で表される化合物の群から選択される少なくとも1つの化合物と、第2成分として下記式(2−1)で表される化合物の群から選択される少なくとも1つの化合物と、第3成分として下記式(3−1)、式(3−2)および式(3−3)で表される化合物の群から選択される少なくとも1つの化合物とを含有することを特徴とする重合性液晶組成物。
The present invention includes the following polymerizable liquid crystal composition, a polymer obtained by polymerizing the composition, and uses thereof.
[1] At least one compound selected from the group of compounds represented by the following formula (1-1) and formula (1-2) as the first component, and the following formula (2-1) as the second component At least one compound selected from the group of compounds represented, and a third component selected from the group of compounds represented by formula (3-1), formula (3-2) and formula (3-3) And a polymerizable liquid crystal composition comprising at least one compound.
式(1−1)および式(1−2)において、Y1は独立に−O−または−O−CO−O
−であり;W1は独立に水素またはフッ素であり、W2は水素またはメチルであり;R1お
よびR2は独立に水素またはメチルであり;P1、P2、P3およびP4は独立に下記式(A
1)〜(A8)のいずれかで表される重合性基であり;k1、k2、q1およびq2は独立に0〜1の整数であり;m1、m2、j1およびj2は独立に1〜10の整数であり;
式(2−1)において、R3およびR4は独立に水素または炭素数1〜10のアルキルであり;P5は下記式(A1)〜(A8)のいずれかで表される重合性基であり;q3は0〜1の整数であり;j3は1〜10の整数であり;
式(3−1)、式(3−2)および式(3−3)において、X1、X2およびX3は、そ
れぞれ独立に単結合、−(CH2)2−または−HC=CH−であり;W3、W4およびW5
は、それぞれ独立に水素またはフッ素であり;P6、P7、P8、P9、P10およびP11は独立に下記(A1)〜(A8)のいずれかで表される重合性基であり;k3、k4、k5、q4、q5およびq6は独立に0〜1の整数であり;m3、m4、m5、j4、j5およびj6は独立に1〜10の整数である。
In Formula (1-1) and Formula (1-2), Y 1 is independently —O— or —O—CO—O.
W 1 is independently hydrogen or fluorine, W 2 is hydrogen or methyl; R 1 and R 2 are independently hydrogen or methyl; P 1 , P 2 , P 3 and P 4 are Independently the following formula (A
A polymerizable group represented by any one of 1) to (A8); k 1 , k 2 , q 1 and q 2 are each independently an integer of 0 to 1 ; m 1 , m 2 , j 1 and j 2 is independently an integer from 1 to 10;
In the formula (2-1), R 3 and R 4 are independently hydrogen or alkyl having 1 to 10 carbon atoms; P 5 is a polymerizable group represented by any of the following formulas (A1) to (A8) Q 3 is an integer from 0 to 1; j 3 is an integer from 1 to 10;
In formula (3-1), formula (3-2) and formula (3-3), X 1 , X 2 and X 3 are each independently a single bond, — (CH 2 ) 2 — or —HC═CH -; W 3 , W 4 and W 5
Are each independently hydrogen or fluorine; P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are each independently a polymerizable group represented by any one of the following (A1) to (A8): Yes; k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are independently integers from 0 to 1; m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are independently It is an integer of 1-10.
[2] 第1成分の含有割合が20〜40重量%の範囲であり、第2成分の含有割合が30〜50重量%の範囲であり、第3成分の含有割合が20〜40重量%の範囲であり(ただし、重合性液晶組成物において、第1成分、第2成分および第3成分の合計量を100重量%とした場合。);
式(1−1)および式(1−2)において、Y1が独立に−O−または−O−CO−O
−であり;W1が独立に水素であり;W2が水素またはメチルであり;R1およびR2が独立に水素またはメチルであり;P1、P2、P3およびP4が式(A1)で表される重合性基であり;k1、k2、q1およびq2が1であり;m1、m2、j1およびj2が独立に2〜8の整数であり;
式(2−1)において、R3およびR4が独立に水素または炭素数1〜8のアルキルであり;P5が式(A1)で表される重合性基であり;q3が1であり;j3が2〜8の整数で
あり;
式(3−1)、式(3−2)および式(3−3)において、X1、X2およびX3が、そ
れぞれ独立に単結合、−(CH2)2−または−HC=CH−であり;W3、W4およびW5
が、それぞれ独立に水素またはフッ素であり;P6、P7、P8、P9、P10およびP11が式(A1)で表される重合性基であり;k3、k4、k5、q4、q5およびq6が1であり;m3、m4、m5、j4、j5およびj6が独立に2〜8の整数であること
を特徴とする項[1]に記載の重合性液晶組成物。
[2] The content ratio of the first component is in the range of 20 to 40% by weight, the content ratio of the second component is in the range of 30 to 50% by weight, and the content ratio of the third component is 20 to 40% by weight. (However, in the polymerizable liquid crystal composition, when the total amount of the first component, the second component and the third component is 100% by weight);
In Formula (1-1) and Formula (1-2), Y 1 is independently —O— or —O—CO—O.
W 1 is independently hydrogen; W 2 is hydrogen or methyl; R 1 and R 2 are independently hydrogen or methyl; and P 1 , P 2 , P 3 and P 4 are of the formula ( A polymerizable group represented by A1); k 1 , k 2 , q 1 and q 2 are 1; m 1 , m 2 , j 1 and j 2 are each independently an integer of 2 to 8;
In the formula (2-1), R 3 and R 4 is hydrogen or alkyl of 1 to 8 carbon atoms independently; with q 3 is 1; P 5 is located at the polymerizable group represented by the formula (A1) Yes; j 3 is an integer from 2 to 8;
In Formula (3-1), Formula (3-2), and Formula (3-3), X 1 , X 2, and X 3 are each independently a single bond, — (CH 2 ) 2 — or —HC═CH -; W 3 , W 4 and W 5
Are each independently hydrogen or fluorine; P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are polymerizable groups represented by formula (A1); k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are 1; and m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are independently integers of 2 to 8, ] The polymerizable liquid crystal composition described in the above.
[3] 第1成分が式(1−1)で表される化合物の群から選択される少なくとも1つの化合物であり;
第1成分の含有割合が25〜35重量%の範囲であり、第2成分の含有割合が35〜45重量%の範囲であり、第3成分の含有割合が25〜35重量%の範囲であり(ただし、重合性液晶組成物において、第1成分、第2成分および第3成分の合計量を100重量%とした場合。);
式(1−1)において、W1が水素であり;R1およびR2が独立に水素またはメチルで
あり;P1およびP2が式(A1)で表される重合性基であり;k1およびq1が1であり;m1およびj1が独立に2〜6の整数であり;
式(2−1)において、R3およびR4が独立に水素または炭素数2〜6のアルキルであり;P5が式(A1)で表される重合性基であり;q3が1であり;j3が2〜6の整数で
あり;
式(3−1)、式(3−2)および式(3−3)において、X1が独立に単結合、−(
CH2)2−または−HC=CH−であり;X2およびX3が、それぞれ独立に単結合または−(CH2)2−であり;W3、W4およびW5が、それぞれ独立に水素であり;P6、P7、
P8、P9、P10およびP11が式(A1)で表される重合性基であり;k3、k4、k5、q4、q5およびq6が1であり;m3、m4、m5、j4、j5およびj6が独立に4〜6の整数であること
を特徴とする項[1]に記載の重合性液晶組成物。
[3] The first component is at least one compound selected from the group of compounds represented by formula (1-1);
The content ratio of the first component is in the range of 25 to 35% by weight, the content ratio of the second component is in the range of 35 to 45% by weight, and the content ratio of the third component is in the range of 25 to 35% by weight. (However, in the polymerizable liquid crystal composition, the total amount of the first component, the second component, and the third component is 100% by weight.);
In formula (1-1), W 1 is hydrogen; R 1 and R 2 are independently hydrogen or methyl; P 1 and P 2 are a polymerizable group represented by formula (A1); k 1 and q 1 are 1; m 1 and j 1 are independently integers of 2 to 6;
In the formula (2-1), R 3 and R 4 is hydrogen or alkyl of 2 to 6 carbon atoms independently; with q 3 is 1; P 5 is located at the polymerizable group represented by the formula (A1) Yes; j 3 is an integer from 2 to 6;
In Formula (3-1), Formula (3-2), and Formula (3-3), X 1 is independently a single bond,-(
CH 2 ) 2 — or —HC═CH—; X 2 and X 3 are each independently a single bond or — (CH 2 ) 2 —; W 3 , W 4 and W 5 are each independently Hydrogen; P 6 , P 7 ,
P 8 , P 9 , P 10 and P 11 are polymerizable groups represented by the formula (A1); k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are 1; m 3 , M 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 4 to 6, The polymerizable liquid crystal composition according to item [1].
[4] 第1成分が式(1−2)で表される化合物の群から選択される少なくとも1つの化合物であり;
第1成分の含有割合が20〜40重量%の範囲であり、第2成分の含有割合が30〜50重量%の範囲であり、第3成分の含有割合が20〜40重量%の範囲であり(ただし、重合性液晶組成物において、第1成分、第2成分および第3成分の合計量を100重量%とした場合。);
式(1−2)において、Y1が独立に−O−または−O−CO−O−であり;W2が水素またはメチルであり;P3およびP4が式(A1)で表される重合性基であり;k2および
q2が1であり;m2およびj2が独立に2〜8の整数であり;
式(2−1)において、R3およびR4が独立に水素または炭素数1〜8のアルキルであり;P5が式(A1)で表される重合性基であり;q3が1であり;j3が2〜8の整数で
あり;
式(3−1)、式(3−2)および式(3−3)において、X1が独立に単結合、−(
CH2)2−または−HC=CH−であり;X2およびX3が、それぞれ独立に単結合または−(CH2)2−であり;W3、W4およびW5が水素であり;P6、P7、P8、P9、P10お
よびP11が式(A1)で表される重合性基であり;k3、k4、k5、q4、q5およびq6が1であり;m3、m4、m5、j4、j5およびj6が独立に2〜8の整数であること
を特徴とする項[1]に記載の重合性液晶組成物。
[4] The first component is at least one compound selected from the group of compounds represented by formula (1-2);
The content ratio of the first component is in the range of 20 to 40% by weight, the content ratio of the second component is in the range of 30 to 50% by weight, and the content ratio of the third component is in the range of 20 to 40% by weight. (However, in the polymerizable liquid crystal composition, the total amount of the first component, the second component, and the third component is 100% by weight.);
In formula (1-2), Y 1 is independently —O— or —O—CO—O—; W 2 is hydrogen or methyl; P 3 and P 4 are represented by formula (A1) A polymerizable group; k 2 and q 2 are 1; m 2 and j 2 are independently integers of 2 to 8;
In the formula (2-1), R 3 and R 4 is hydrogen or alkyl of 1 to 8 carbon atoms independently; with q 3 is 1; P 5 is located at the polymerizable group represented by the formula (A1) Yes; j 3 is an integer from 2 to 8;
In Formula (3-1), Formula (3-2), and Formula (3-3), X 1 is independently a single bond,-(
CH 2 ) 2 — or —HC═CH—; X 2 and X 3 are each independently a single bond or — (CH 2 ) 2 —; W 3 , W 4 and W 5 are hydrogen; P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are a polymerizable group represented by the formula (A1); k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are The polymerizable liquid crystal composition according to item [1], wherein m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 2 to 8.
[5] 第1成分が式(1−2)で表される化合物の群から選択される少なくとも1つの化合物であり;
第1成分の含有割合が25〜35重量%の範囲であり、第2成分の含有割合が35〜45重量%の範囲であり、第3成分の含有割合が25〜35重量%の範囲であり(ただし、重合性液晶組成物において、第1成分、第2成分および第3成分の合計量を100重量%とした場合。);
式(1−2)において、Y1が独立に−O−または−O−CO−O−であり;W2がメチルであり;P1、P2、P3およびP4が式(A1)で表される重合性基であり;k2および
q2が1であり;m2およびj2が独立に2〜6の整数であり;
式(2−1)において、R3およびR4が独立に水素または炭素数2〜6のアルキルであり;P5が式(A1)で表される重合性の基であり;q3が1であり;j3が2〜6の整数
であり;
式(3−1)、式(3−2)および式(3−3)において、X1が独立に単結合、−(
CH2)2−または−HC=CH−であり;X2およびX3が、それぞれ独立に単結合または−(CH2)2−であり;W3、W4およびW5が水素であり;P6、P7、P8、P9、P10お
よびP11が式(A1)で表される重合性基であり;k3、k4、k5、q4、q5およびq6が1であり;m3、m4、m5、j4、j5およびj6が独立に4〜6の整数であること
を特徴とする項[1]に記載の重合性液晶組成物。
[5] The first component is at least one compound selected from the group of compounds represented by formula (1-2);
The content ratio of the first component is in the range of 25 to 35% by weight, the content ratio of the second component is in the range of 35 to 45% by weight, and the content ratio of the third component is in the range of 25 to 35% by weight. (However, in the polymerizable liquid crystal composition, the total amount of the first component, the second component, and the third component is 100% by weight.);
In formula (1-2), Y 1 is independently —O— or —O—CO—O—; W 2 is methyl; P 1 , P 2 , P 3 and P 4 are represented by formula (A1) And k 2 and q 2 are 1; m 2 and j 2 are each independently an integer of 2 to 6;
In Formula (2-1), R 3 and R 4 are independently hydrogen or alkyl having 2 to 6 carbon atoms; P 5 is a polymerizable group represented by Formula (A1); q 3 is 1 J 3 is an integer from 2 to 6;
In Formula (3-1), Formula (3-2), and Formula (3-3), X 1 is independently a single bond,-(
CH 2 ) 2 — or —HC═CH—; X 2 and X 3 are each independently a single bond or — (CH 2 ) 2 —; W 3 , W 4 and W 5 are hydrogen; P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are a polymerizable group represented by the formula (A1); k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are The polymerizable liquid crystal composition according to item [1], wherein m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 4 to 6.
[6] さらに、重合開始剤を含有することを特徴とする項[1]〜[5]のいずれかに記載の重合性液晶組成物。
[7] さらに、溶媒を含有することを特徴とする項[1]〜[6]のいずれかに記載の重合性液晶組成物。
[6] The polymerizable liquid crystal composition according to any one of items [1] to [5], further comprising a polymerization initiator.
[7] The polymerizable liquid crystal composition according to any one of items [1] to [6], further comprising a solvent.
[8] 項[1]〜[7]のいずれかに記載の重合性液晶組成物からなり、ハイブリッド配向していることを特徴とする重合性液晶層。
[9] 項[1]〜[7]のいずれかに記載の重合性液晶組成物を重合して得られ、かつ配向が固定化されていることを特徴とする重合体。
[8] A polymerizable liquid crystal layer comprising the polymerizable liquid crystal composition according to any one of items [1] to [7] and being hybrid-aligned.
[9] A polymer obtained by polymerizing the polymerizable liquid crystal composition according to any one of items [1] to [7], and having a fixed orientation.
[10] 項[8]に記載の重合性液晶層を構成する重合性液晶組成物を重合し、配向を固定化することによって得られることを特徴とする光学異方性フィルム。
[11] 基板上に、項[1]〜[7]のいずれかに記載の重合性液晶組成物を塗布し、ハイブリッド配向させて重合性液晶層を形成し、該液晶層を構成する重合性液晶組成物を重合して配向を固定化することを特徴とする光学異方性フィルムの製造方法。
[10] An optically anisotropic film obtained by polymerizing the polymerizable liquid crystal composition constituting the polymerizable liquid crystal layer according to item [8] and fixing the alignment.
[11] A polymerizable liquid crystal composition according to any one of items [1] to [7] is applied on a substrate, and is hybrid-aligned to form a polymerizable liquid crystal layer, thereby forming the liquid crystal layer. A method for producing an optically anisotropic film, comprising: polymerizing a liquid crystal composition to fix alignment.
[12] 基板が、トリアセチルセルロースフィルムまたはノルボルネン系樹脂フィルムであることを特徴とする項[11]に記載の光学異方性フィルムの製造方法。
[13] 基板が、ラビング処理されたポリイミド配向膜を表面に有するガラス基板、鹸化処理したトリアセチルセルロースフィルムまたは親水化処理したノルボルネン系樹脂フィルムであることを特徴とする項[11]に記載の光学異方性フィルムの製造方法。
[12] The method for producing an optically anisotropic film according to item [11], wherein the substrate is a triacetylcellulose film or a norbornene-based resin film.
[13] Item [11] is characterized in that the substrate is a glass substrate having a rubbed polyimide alignment film on its surface, a saponified triacetyl cellulose film or a hydrophilized norbornene resin film. A method for producing an optically anisotropic film.
[14] ノルボルネン系樹脂フィルムの親水化処理が、プラズマ処理またはコロナ処理であることを特徴とする項[13]に記載の光学異方性フィルムの製造方法。
[15] 項[10]に記載の光学異方性フィルムを有することを特徴とする光学補償素子。
[14] The method for producing an optically anisotropic film according to item [13], wherein the hydrophilization treatment of the norbornene-based resin film is a plasma treatment or a corona treatment.
[15] An optical compensation element comprising the optically anisotropic film according to item [10].
[16] 項[10]に記載の光学異方性フィルムと偏光板とを有することを特徴とする光学素子。
[17] 項[15]に記載の光学補償素子を、液晶セルの内面または外面に有することを特徴とする液晶表示装置。
[16] An optical element comprising the optically anisotropic film according to item [10] and a polarizing plate.
[17] A liquid crystal display device comprising the optical compensation element according to item [15] on an inner surface or an outer surface of a liquid crystal cell.
[18] 項[16]に記載の光学素子を、液晶セルの内面または外面に有することを特徴とする液晶表示装置。 [18] A liquid crystal display device comprising the optical element according to item [16] on an inner surface or an outer surface of a liquid crystal cell.
本発明の重合性液晶組成物を用いれば、室温で十分安定したネマチック相を有し、かつ、均一な配向性を示す、光学異方性を有する液晶相もしくは液晶薄膜を得ることが可能である。また、液晶骨格の配向状態がハイブリッド配向である光学異方性フィルムを得ることができる。さらに、本発明の光学異方性フィルムは、各種の光学素子に適用可能であり、さらに、この光学異方性フィルムを用いた光学素子は表示装置、特に液晶表示装置に適用可能である。 By using the polymerizable liquid crystal composition of the present invention, it is possible to obtain a liquid crystal phase or a liquid crystal thin film having an optical anisotropy having a nematic phase sufficiently stable at room temperature and showing uniform alignment. . In addition, an optically anisotropic film in which the alignment state of the liquid crystal skeleton is hybrid alignment can be obtained. Furthermore, the optically anisotropic film of the present invention can be applied to various optical elements, and the optical element using the optically anisotropic film can be applied to a display device, particularly a liquid crystal display device.
以下、本発明に係る重合性液晶組成物、該組成物からなる重合体およびこれらの用途について、詳細に説明する。
[用語の説明]
この明細書における用語の使い方は次のとおりである。液晶化合物は、液晶相を有する化合物、および液晶相を有しないが液晶組成物の成分として有用な化合物の総称である。液晶相はネマチック相、スメクチック相、コレステリック相などであり、多くの場合ネマチック相を意味する。重合性は、光、熱、触媒などの手段により単量体が重合し、重合体を与える能力を意味する。「化合物(1−1)」は式(1−1)で表される化合物を意味し、他の式で表される化合物や基などについても同様に表記する。また、「化合物(1)」は、化合物(1−1)および化合物(1−2)の群から選択される少なくとも1つの化合物を意味し、化合物(2)および化合物(3)についても同様である。組成物の成分である化合物(1)、化合物(2)および化合物(3)の割合(%)は、これら3種類の重合性化合物の全重量に基づいて算出した重量%(wt%)である。また、組成物における、その他の成分の添加量(%)は、化合物(1)、(2)および(3)の全重量に基づいた重量%である。
Hereinafter, the polymerizable liquid crystal composition according to the present invention, the polymer comprising the composition, and their uses will be described in detail.
[Explanation of terms]
Terms used in this specification are as follows. A liquid crystal compound is a generic term for a compound having a liquid crystal phase and a compound having no liquid crystal phase but useful as a component of a liquid crystal composition. The liquid crystal phase is a nematic phase, a smectic phase, a cholesteric phase or the like, and often means a nematic phase. Polymerizability means the ability of a monomer to polymerize and give a polymer by means such as light, heat, or catalyst. “Compound (1-1)” means a compound represented by Formula (1-1), and the same applies to compounds and groups represented by other formulas. The “compound (1)” means at least one compound selected from the group of the compound (1-1) and the compound (1-2), and the same applies to the compound (2) and the compound (3). is there. The ratio (%) of the compound (1), the compound (2) and the compound (3) which are the components of the composition is weight% (wt%) calculated based on the total weight of these three kinds of polymerizable compounds. . Moreover, the addition amount (%) of the other components in the composition is% by weight based on the total weight of the compounds (1), (2) and (3).
液晶分子における配向は、チルト角の大きさなどに基づいて分類され、ハイブリッド、ツイスト(twisted;チルト角は、液晶分子の配向ベクトルおよび支持基板のあいだの角
度であるねじれ)などに分類される。ホモジニアス(homogenerous;平行)は、配向ベクトルが基板に平行で、かつ一方向に並んでいる状態をいう。ホモジニアス配向におけるチルト角の例は0度から5度である。ホメオトロピック(homeotropic;垂直)は、配向ベ
クトルが基板に垂直である状態をいう。ホメオトロピック配向におけるチルト角の例は、85度から90度である。ハイブリッド(hybrid)は、配向ベクトルが基板から離れるにしたがって、平行から垂直に立ちあがっている状態をいう。チルト配向におけるチルト角(傾き角)の例は5度から85度である。ツイストは、配向ベクトルが基板に平行ではあるが、らせん軸を中心に階段状にねじれている状態をいう。ツイスト配向におけるチルト角の例は0度から5度である。
The alignment in the liquid crystal molecules is classified based on the magnitude of the tilt angle and the like, and is classified into hybrid, twisted (the tilt angle is a twist that is an angle between the alignment vector of the liquid crystal molecule and the support substrate), and the like. Homogeneous (parallel) means a state in which the orientation vectors are parallel to the substrate and aligned in one direction. An example of the tilt angle in the homogeneous alignment is 0 degree to 5 degrees. Homeotropic (vertical) refers to the state where the orientation vector is perpendicular to the substrate. An example of the tilt angle in homeotropic alignment is 85 degrees to 90 degrees. Hybrid refers to a state in which the orientation vector rises vertically from parallel as it moves away from the substrate. An example of a tilt angle (tilt angle) in the tilt alignment is 5 degrees to 85 degrees. The twist refers to a state in which the orientation vector is parallel to the substrate but twisted stepwise about the helical axis. An example of the tilt angle in the twist orientation is 0 degree to 5 degrees.
[重合性液晶組成物]
<主成分>
本発明の重合性液晶組成物は、第1成分、第2成分および第3成分を含有し、第1成分は上記式(1−1)および式(1−2)で表される化合物の群から選択される少なくとも1つの化合物(1)であり、第2成分は上記式(2−1)で表される群から選択される少なくとも1つの化合物(2)であり、第3成分は上記式(3−1)、式(3−2)および式(3−3)で表される化合物の群から選択される少なくとも1つの化合物(3)である。
[Polymerizable liquid crystal composition]
<Main component>
The polymerizable liquid crystal composition of the present invention contains a first component, a second component, and a third component, and the first component is a group of compounds represented by the above formulas (1-1) and (1-2). And the second component is at least one compound (2) selected from the group represented by the above formula (2-1), and the third component is the above formula. (3-1) At least one compound (3) selected from the group of compounds represented by formula (3-2) and formula (3-3).
上記式(1−1)および式(1−2)において、Y1は独立に−O−または−O−CO
−O−である。W1は独立に水素またはフッ素であり、好ましくは水素である。W2は水素またはメチルであり、好ましくはメチルである。R1およびR2は独立に水素またはメチルである。P1、P2、P3およびP4は、独立に上記式(A1)〜(A8)で表される重合性基のいずれかであり、好ましくは重合性基(A1)である。k1、k2、q1およびq2は独立に0〜1の整数であり、好ましくは1である。m1、m2、j1およびj2は独立に1〜10の整数であり、好ましくは2〜8の整数であり、さらに好ましくは2〜6の整数である。
In the above formula (1-1) and formula (1-2), Y 1 is independently —O— or —O—CO.
-O-. W 1 is independently hydrogen or fluorine, preferably hydrogen. W 2 is hydrogen or methyl, preferably methyl. R 1 and R 2 are independently hydrogen or methyl. P 1 , P 2 , P 3 and P 4 are each independently any of the polymerizable groups represented by the above formulas (A1) to (A8), preferably the polymerizable group (A1). k 1 , k 2 , q 1 and q 2 are each independently an integer of 0 to 1, preferably 1. m 1 , m 2 , j 1 and j 2 are each independently an integer of 1 to 10, preferably an integer of 2 to 8, more preferably an integer of 2 to 6.
式(2−1)において、R3およびR4は独立に水素または炭素数1〜10のアルキルであり、好ましくは水素または炭素数1〜8のアルキルであり、さらに好ましくは水素または炭素数2〜6のアルキルである。P5は重合性基(A1)〜(A8)のいずれかであり
、好ましくは重合性基(A1)である。q3は0〜1の整数であり、好ましくは1である
。j3は1〜10の整数であり、好ましくは2〜8の整数であり、さらに好ましくは2〜
6の整数である。
In the formula (2-1), R 3 and R 4 are independently hydrogen or alkyl having 1 to 10 carbons, preferably hydrogen or alkyl having 1 to 8 carbons, more preferably hydrogen or carbon 2 ~ 6 alkyl. P 5 is either a polymerizable group (A1) ~ (A8), preferably a polymerizable group (A1). q 3 is an integer of 0 to 1, preferably 1. j 3 is an integer of 1 to 10, preferably an integer of 2 to 8, and more preferably 2 to 2.
It is an integer of 6.
式(3−1)、式(3−2)および式(3−3)において、X1、X2およびX3は、そ
れぞれ独立に単結合、−(CH2)2−または−HC=CH−であり、X2およびX3は独立に単結合または−(CH2)2−であることが好ましい。W3、W4およびW5は、それぞれ
独立に水素またはフッ素であり、好ましくは水素である。P6、P7、P8、P9、P10およびP11は、重合性基(A1)〜(A8)のいずれかであり、好ましくは重合性基(A1)である。k3、k4、k5、q4、q5およびq6は、それぞれ独立に0〜1の整数であり、好ましくは1である。m3、m4、m5、j4、j5およびj6は、それぞれ独立に1〜10の整数であり、好ましくは2〜8の整数であり、さらに好ましくは4〜6の整数である。
In formula (3-1), formula (3-2) and formula (3-3), X 1 , X 2 and X 3 are each independently a single bond, — (CH 2 ) 2 — or —HC═CH It is preferable that X 2 and X 3 are independently a single bond or — (CH 2 ) 2 —. W 3 , W 4 and W 5 are each independently hydrogen or fluorine, preferably hydrogen. P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are any of the polymerizable groups (A1) to (A8), preferably the polymerizable group (A1). k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are each independently an integer of 0 to 1, preferably 1. m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 1 to 10, preferably an integer of 2 to 8, more preferably an integer of 4 to 6. .
重合性液晶を構成する第1成分の化合物(1)は、液晶相の温度範囲が広いので、組成物の液晶温度範囲を調整する目的に使用する。また、化合物(1)は、他の重合性液晶との相溶性に優れているので、これを用いて好適に重合性液晶組成物を調製することができる。化合物(1)の好ましい例を以下に示す。 Since the temperature range of the liquid crystal phase is wide, the first component compound (1) constituting the polymerizable liquid crystal is used for the purpose of adjusting the liquid crystal temperature range of the composition. Moreover, since the compound (1) is excellent in compatibility with other polymerizable liquid crystals, a polymerizable liquid crystal composition can be suitably prepared using this. Preferred examples of compound (1) are shown below.
重合性液晶組成物を構成する第2成分の化合物(2)は、ハイブリッド配向性を発現させる目的で使用する。化合物(2)の好ましい例を以下に示す。 The second component compound (2) constituting the polymerizable liquid crystal composition is used for the purpose of developing the hybrid alignment. Preferred examples of compound (2) are shown below.
重合性液晶組成物を構成する第3成分の化合物(3)は、重合性液晶組成物の配向を安定化させる目的で使用する。重合性液晶組成物が化合物(3)を含むことにより、配向欠陥を少なくすることができる。化合物(3)は液晶相を有する化合物でなくてもよい。化合物(3)の好ましい例を以下に示す。 The third component compound (3) constituting the polymerizable liquid crystal composition is used for the purpose of stabilizing the alignment of the polymerizable liquid crystal composition. When the polymerizable liquid crystal composition contains the compound (3), alignment defects can be reduced. Compound (3) may not be a compound having a liquid crystal phase. Preferred examples of compound (3) are shown below.
本発明の重合性液晶組成物において、第1成分、第2成分および第3成分の合計量を100重量%とした場合、第1成分の割合は20〜40重量%、好ましくは25〜35重量%であり、第2成分の割合は30〜50重量%、好ましくは35〜45重量%であり、第3成分の割合は20〜40重量%、好ましくは25〜35重量%である。 In the polymerizable liquid crystal composition of the present invention, when the total amount of the first component, the second component and the third component is 100% by weight, the proportion of the first component is 20 to 40% by weight, preferably 25 to 35% by weight. %, The proportion of the second component is 30 to 50% by weight, preferably 35 to 45% by weight, and the proportion of the third component is 20 to 40% by weight, preferably 25 to 35% by weight.
第1成分、第2成分および第3成分の含有割合が上記範囲内にあることにより、均一なハイブリッド配向を示すとともに、室温で十分安定したネマチック相を有する組成物を得ることができる。なお、第1成分、第2成分および第3成分のいずれも、1つの化合物を用いてもよいし、複数の化合物を組み合わせてもよい。 When the content ratios of the first component, the second component, and the third component are within the above ranges, a composition that exhibits a uniform hybrid orientation and has a nematic phase that is sufficiently stable at room temperature can be obtained. One of the first component, the second component, and the third component may be used, or a plurality of compounds may be combined.
化合物(1)〜(3)は、フーベン・ヴァイル(Houben Wyle, Methoden der Organischen Chemie, Georg Thieme Verlag, Stuttgart)、オーガニック・リアクションズ(Organic Reactions, John Wily & Sons Inc.)、オーガニック・シンセセーズ(Organic Syntheses, John Wily & Sons, Inc.)、コンプリヘンシブ・オーガニック・シンセシス(Comprehensive Organic Synthesis, Pergamon Press)、新実験化学講座(丸善)などに記載された、有機化学における合成方法を適切に組み合わせることにより合成できる。 Compounds (1)-(3) were prepared by Houben Wyle (Methoden der Organischen Chemie, Georg Thieme Verlag, Stuttgart), Organic Reactions (Organic Reactions, John Wily & Sons Inc.), Organic Syntheses (Organic Syntheses). , John Wily & Sons, Inc.), Comprehensive Organic Synthesis, Pergamon Press, New Experimental Chemistry Course (Maruzen), etc. Can be synthesized.
化合物(1−1)は、特開2003−238491号公報、特開2006−307150号公報、特開2005−60373号公報に記載の方法に従って合成することができる。化合物(1−2)は、Macromol.Chem.,190,3201-3215(1998)、WO97/00600に記載の方法に従って合成することができる。化合物(2−1)は、WO00/59966、WO02/090447、特願2005−355180号、特願2005−355181号に記載の方法に従って合成することができる。化合物(3−1)は特開2004−231638号公報に記載の方法に従って合成することができる。化合物(3−2)および化合物(3−3)は、特願2005−169337号に記載の方法に従って合成することができる。 Compound (1-1) can be synthesized according to the methods described in JP2003-238491A, JP2006-307150A, and JP2005-60373A. Compound (1-2) can be synthesized according to the method described in Macromol. Chem., 190, 3201-3215 (1998), WO 97/00600. Compound (2-1) can be synthesized according to the method described in WO00 / 59966, WO02 / 090447, Japanese Patent Application No. 2005-355180, and Japanese Patent Application No. 2005-355181. Compound (3-1) can be synthesized according to the method described in JP-A No. 2004-231638. Compound (3-2) and compound (3-3) can be synthesized according to the method described in Japanese Patent Application No. 2005-169337.
<組成物の特性>
本発明の重合性液晶組成物を基板上で重合させて得られる光学異方性フィルムは、均一で良好なハイブリッド配向性を示し、フィルム表面にベタつきがない。また、重合前には室温で十分安定したネマチック相を有している。したがって、重合体の製造工程において、組成物を基板に塗布し、予備焼成した後に、紫外線照射によって重合体を得るまでの間、すぐに結晶が析出することはないことから、本発明の重合性液晶組成物は、室温で十分安定したネマチック相を有し、非常に取扱いが容易であるといえる。
<Characteristics of composition>
The optically anisotropic film obtained by polymerizing the polymerizable liquid crystal composition of the present invention on a substrate exhibits uniform and good hybrid orientation, and has no stickiness on the film surface. Moreover, it has a nematic phase sufficiently stable at room temperature before polymerization. Therefore, in the polymer production process, after the composition is applied to a substrate and pre-baked, crystals are not immediately precipitated until the polymer is obtained by ultraviolet irradiation. The liquid crystal composition has a nematic phase sufficiently stable at room temperature and can be said to be very easy to handle.
本発明の重合性液晶組成物は、配向処理した表面を有するガラス基板や、ラビングなどの配向処理がされた透明な高分子支持基板などの上で容易に配向する。得られる重合性液晶層は、配向の欠陥がないか、または少なく、塗工性に優れている。 The polymerizable liquid crystal composition of the present invention is easily aligned on a glass substrate having an alignment-treated surface, a transparent polymer support substrate subjected to alignment treatment such as rubbing, and the like. The resulting polymerizable liquid crystal layer has no or few alignment defects and is excellent in coatability.
本発明の重合性液晶組成物は、室温で十分安定したネマチック相を有し、ラジカル重合触媒や光カチオン重合触媒の存在下、紫外線などの照射によって室温で重合する。支持基板上に得られた重合体である液晶フィルムは、光学異方性を有する液晶フィルムであり、配向ベクトルが基板から離れるにしたがって平行から垂直に立ちあがるハイブリッド配向を示す。 The polymerizable liquid crystal composition of the present invention has a nematic phase sufficiently stable at room temperature, and is polymerized at room temperature by irradiation with ultraviolet rays or the like in the presence of a radical polymerization catalyst or a photocationic polymerization catalyst. The liquid crystal film, which is a polymer obtained on the support substrate, is a liquid crystal film having optical anisotropy, and exhibits a hybrid alignment in which the alignment vector rises from parallel to vertical as the distance from the substrate increases.
<添加剤>
本発明の重合性液晶組成物は、必要に応じて、上記化合物(1)〜(3)以外の重合性化合物(以下「その他の重合性化合物」ともいう。)や添加物などをさらに含有してもよい。その他の重合性化合物は、組成物や重合体の特性をさらに調節するのに適している。添加剤としては、たとえば、シランカップリング剤、界面活性剤、酸化防止剤、紫外線吸収剤、微粒子、溶媒などが挙げられる。これらの添加物は、重合体の物性を調整するために用いたり、単量体を重合させるために用いることができる。組成物を希釈するためには有機溶媒が好ましい。これらの添加物の量は、その目的を達する程度の少ない量が好ましい。その他の重合性化合物および添加物の例を以下に示す。
<Additives>
The polymerizable liquid crystal composition of the present invention further contains a polymerizable compound other than the above compounds (1) to (3) (hereinafter also referred to as “other polymerizable compounds”), additives, and the like, as necessary. May be. Other polymerizable compounds are suitable for further adjusting the properties of the composition or polymer. Examples of the additive include a silane coupling agent, a surfactant, an antioxidant, an ultraviolet absorber, fine particles, and a solvent. These additives can be used for adjusting the physical properties of the polymer or for polymerizing the monomer. Organic solvents are preferred for diluting the composition. The amount of these additives is preferably small enough to achieve the purpose. Examples of other polymerizable compounds and additives are shown below.
次の三例は、任意の成分として用いられる重合性の非液晶化合物である。
第一の例は、ラジカル重合に適した化合物である。このような化合物としては、たとえば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、ブチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、フェニル(メタ)アクリレート、2−ヒドロキシエチルアクリレート、塩化ビニル、フッ化ビニル、酢酸ビニル、ピバリン酸
ビニル、2,2−ジメチルブタン酸ビニル、2,2−ジメチルペンタン酸ビニル、2−メチル−2−ブタン酸ビニル、プロピオン酸ビニル、ステアリン酸ビニル、2−エチル−2−メチルブタン酸ビニル、N−ビニルアセトアミド、p−t−ブチル安息香酸ビニル、N,N−ジメチルアミノ安息香酸ビニル、安息香酸ビニル、スチレン、o−、m−またはp−クロロメチルスチレン、α−メチルスチレン、テトラフルオロエチレン、ヘキサフルオロプロペンなどが挙げられる。これらの化合物は、組成物の粘度を調整するのに適している。これらの化合物は、−OCOCH=CH2を有する化合物を主成分とする組成物に添
加するのに適している。
The next three examples are polymerizable non-liquid crystal compounds used as optional components.
The first example is a compound suitable for radical polymerization. Examples of such compounds include methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, phenyl (meth) acrylate, 2-hydroxyethyl acrylate, vinyl chloride, Vinyl fluoride, vinyl acetate, vinyl pivalate, vinyl 2,2-dimethylbutanoate, vinyl 2,2-dimethylpentanoate, vinyl 2-methyl-2-butanoate, vinyl propionate, vinyl stearate, 2-ethyl 2-methylbutanoic acid vinyl, N-vinylacetamide, pt-butylvinylbenzoate, N, N-dimethylaminovinylbenzoate, vinylbenzoate, styrene, o-, m- or p-chloromethylstyrene, α -Methylstyrene, tetrafluoroethylene, hexa Ruoropuropen and the like. These compounds are suitable for adjusting the viscosity of the composition. These compounds are suitable for addition to compositions based on compounds having —OCOCH═CH 2 .
第二の例は、ラジカル重合に適した多官能アクリレートである。好ましい多官能アクリレートとしては、たとえば、1,4−ブタンジオールジアクリレート、1,6−ヘキサンジオールジアクリレート、1,9−ノナンジオールジアクリレート、ネオペンチルグリコールジアクリレート、トリエチレングリコールジアクリレート、ジプロピレングリコールジアクリレート、トリプロピレングリコールジアクリレート、テトラエチレングリコールジアクリレート、トリメチロールプロパントリアクリレート、トリメチロールEO付加トリアクリレート、ペンタエリストールトリアクリレート、トリスアクリロキシエチルフォスフェート、ビスフェノールA EO付加ジアクリレート、ビスフェノールAグリシジルジアクリレート(大阪有機化学株式会社製、商品名:ビスコート700)、ポリエチレングリコールジアクリレートでなどが挙げられる。これらの化合物は、重合体の被膜形成能をさらに高めるのに適している。 The second example is a polyfunctional acrylate suitable for radical polymerization. Preferred polyfunctional acrylates include, for example, 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, 1,9-nonanediol diacrylate, neopentyl glycol diacrylate, triethylene glycol diacrylate, dipropylene Glycol diacrylate, tripropylene glycol diacrylate, tetraethylene glycol diacrylate, trimethylolpropane triacrylate, trimethylol EO addition triacrylate, pentaerythritol triacrylate, trisacryloxyethyl phosphate, bisphenol A EO addition diacrylate, bisphenol A glycidyl diacrylate (trade name: Biscoat 700, manufactured by Osaka Organic Chemical Co., Ltd.), polyethylene glycol And the like in diacrylate. These compounds are suitable for further enhancing the film-forming ability of the polymer.
第三の例は、カチオン重合に適した重合性化合物である。このような化合物としては、たとえば、エチルビニルエーテル、ヒドロキシブチルモノビニルエーテル、t−アミルビニルエーテル、シクロヘキサンジメタノールメチルビニルエーテル、3−エチル−3−ヒドロキシメチルオキセタン、3−メチル−3−ヒドロキシメチルオキセタン、ジ(3−エチル−オキセタ−3−イルメチル)、3−エチル−3−(2−エチルヘキシロキシメチル)オキセタンなどが挙げられる。これらの化合物は、組成物の粘度を調整するのに適している。また、オキセタン環またはオキシラン環を有する化合物を主成分とする組成物に添加するのに適している。 The third example is a polymerizable compound suitable for cationic polymerization. Examples of such compounds include ethyl vinyl ether, hydroxybutyl monovinyl ether, t-amyl vinyl ether, cyclohexanedimethanol methyl vinyl ether, 3-ethyl-3-hydroxymethyl oxetane, 3-methyl-3-hydroxymethyl oxetane, di ( 3-ethyl-oxeta-3-ylmethyl), 3-ethyl-3- (2-ethylhexyloxymethyl) oxetane and the like. These compounds are suitable for adjusting the viscosity of the composition. Moreover, it is suitable for adding to the composition which has as a main component the compound which has an oxetane ring or an oxirane ring.
シランカップリング剤としては、たとえば、ビニルトリアルコキシシラン、3−アミノプロピルトリアルコキシシラン、N−(2−アミノエチル)3−アミノプロピルトリアルコキシシラン、3−グリシドキシプロピルトリアルコキシシラン、3−クロロトリアルコキシシラン、3−メタクリロキシプロピルトリアルコキシシランなどが挙げられる。別の例としては、これらの化合物において、3つのアルコキシ基のうちの1つをメチルに置き換えたジアルコキシメチルシランなどが挙げられる。好ましいシランカップリング剤は、3−アミノプロピルトリエトキシシランである。 Examples of the silane coupling agent include vinyl trialkoxysilane, 3-aminopropyltrialkoxysilane, N- (2-aminoethyl) 3-aminopropyltrialkoxysilane, 3-glycidoxypropyltrialkoxysilane, 3- Examples include chlorotrialkoxysilane and 3-methacryloxypropyltrialkoxysilane. Another example includes dialkoxymethylsilane in which one of three alkoxy groups is replaced with methyl in these compounds. A preferred silane coupling agent is 3-aminopropyltriethoxysilane.
界面活性剤としては、たとえば、4級アンモニウム塩、アルキルアミンオキサイド、ポリアミン誘導体、ポリオキシエチレン−ポリオキシプロピレン縮合物、ポリエチレングリコールおよびそのエステル、ラウリル硫酸ナトリウム、ラウリル硫酸アンモニウム、ラウリル硫酸アミン類、アルキル置換芳香族スルホン酸塩、アルキルリン酸塩、ペルフルオロアルキルスルホン酸塩、ペルフルオロアルキルカルボン酸塩、ペルフルオロアルキルエチレンオキシド付加物、ペルフルオロアルキルトリメチルアンモニウム塩などが挙げられる。界面活性剤は、組成物を支持基板などに塗布するのを容易にするなどの効果を有する。界面活性剤の含有量は、界面活性剤の種類、組成物の組成比などにより異なるが、重合性化合物の全重量に基づいて、好ましくは100ppm〜5重量%、さらに好ましくは0.1〜1重量%の範囲である。 Examples of surfactants include quaternary ammonium salts, alkylamine oxides, polyamine derivatives, polyoxyethylene-polyoxypropylene condensates, polyethylene glycol and esters thereof, sodium lauryl sulfate, ammonium lauryl sulfate, lauryl sulfate amines, alkyl substitution Aromatic sulfonates, alkyl phosphates, perfluoroalkyl sulfonates, perfluoroalkyl carboxylates, perfluoroalkyl ethylene oxide adducts, perfluoroalkyl trimethyl ammonium salts and the like can be mentioned. The surfactant has effects such as facilitating application of the composition to a support substrate or the like. The content of the surfactant varies depending on the type of the surfactant, the composition ratio of the composition, etc., but is preferably 100 ppm to 5% by weight, more preferably 0.1 to 1%, based on the total weight of the polymerizable compound. It is in the range of wt%.
酸化防止剤としては、たとえば、ヒドロキノン、2,6−ジ−t−ブチル−p−クレゾ
ール、2,6−ジ−t−ブチルフェノール、トリフェニルフォスファイト、トリアルキルフォスファイトなどが挙げられる。好ましい市販品としては、チバ・スペシャリティーズ製の「イルガノックス245」、「イルガノックス1035」などが挙げられる。
Examples of the antioxidant include hydroquinone, 2,6-di-t-butyl-p-cresol, 2,6-di-t-butylphenol, triphenyl phosphite, and trialkyl phosphite. Preferred commercially available products include “Irganox 245” and “Irganox 1035” manufactured by Ciba Specialties.
紫外線吸収剤としては、たとえば、チバ・スペシャリティ・ケミカルズ製の「TINUVIN PS」、「TINUVIN 292」、「TINUVIN 109」、「TINUVIN 328」、「TINUVIN 384−2」、「TINUVIN 123」、「TINUVIN 400」、「TINUVIN 400L」などが挙げられる。 Examples of the ultraviolet absorber include “TINUVIN PS”, “TINUVIN 292”, “TINUVIN 109”, “TINUVIN 328”, “TINUVIN 384-2”, “TINUVIN 123”, and “TINUVIN 400” manufactured by Ciba Specialty Chemicals. And “TINUVIN 400L”.
微粒子の材質としては、たとえば、無機物、有機物、金属などが挙げられる。微粒子の粒径は、好ましくは0.001〜0.1μm、さらに好ましくは0.001〜0.05μmである。材質にもよるが、凝集現象を防止するために小さい粒径が好ましく、粒径の分布はシャープな方が好ましい。このような微粒子は、光学異方性の調整や重合体の強度向上などに有用である。微粒子の含有量は、重合性化合物の全重量に基づいて、好ましくは0.1〜30重量%である。添加の目的を達する限り、少ない割合が好ましい。 Examples of the material of the fine particles include inorganic substances, organic substances, metals, and the like. The particle diameter of the fine particles is preferably 0.001 to 0.1 μm, more preferably 0.001 to 0.05 μm. Although it depends on the material, a small particle size is preferable to prevent the aggregation phenomenon, and a sharp particle size distribution is preferable. Such fine particles are useful for adjusting the optical anisotropy and improving the strength of the polymer. The content of the fine particles is preferably 0.1 to 30% by weight based on the total weight of the polymerizable compound. A small proportion is preferable as long as the purpose of addition is achieved.
微粒子の材質である無機物としては、たとえば、セラミックス、フッ素金雲母、フッ素四ケイ素雲母、テニオライト、フッ素バーミキュライト、フッ素ヘクトライト、ヘクトライト、サポナイト、スチブンサイト、モンモリロナイト、バイデライト、カオリナイト、フライポンタイト、ZnO、TiO2、CeO2、Al2O3、Fe2O3、ZrO2、MgF2、SiO2、SrCO3、Ba(OH)2、Ca(OH)2、Ga(OH)3、Al(OH)3、Mg(OH)2、Zr(OH)4などが挙げられる。炭酸カルシウムの針状結晶などの微粒子は光学異方性を有する。このような微粒子によって、重合体の光学異方性を調節できる。また、微粒子の材質である有機物としては、たとえば、カーボンナノチューブ、フラーレン、デンドリマー、ポリビニルアルコール、ポリメタクリレート、ポリイミドなどが挙げられる。 Examples of inorganic substances that are fine particles include ceramics, fluorine phlogopite, fluorine tetrasilicon mica, teniolite, fluorine vermiculite, fluorine hectorite, hectorite, saponite, stevensite, montmorillonite, beidellite, kaolinite, frypontite, ZnO. , TiO 2 , CeO 2 , Al 2 O 3 , Fe 2 O 3 , ZrO 2 , MgF 2 , SiO 2 , SrCO 3 , Ba (OH) 2 , Ca (OH) 2 , Ga (OH) 3 , Al (OH) ) 3 , Mg (OH) 2 , Zr (OH) 4 and the like. Fine particles such as calcium carbonate needle crystals have optical anisotropy. Such fine particles can adjust the optical anisotropy of the polymer. Examples of the organic substance that is the material of the fine particles include carbon nanotubes, fullerenes, dendrimers, polyvinyl alcohol, polymethacrylate, and polyimide.
光ラジカル重合開始剤は汎用品を用いることができる。たとえば、チバ・スペシャリティー・ケミカルズ(株)製品の「DAROCUR1173」(2−ヒドロキシ−2−メチル−1−フェニルプロパン−1−オン)、「IRGACURE184」(1−ヒドロキシシクロヘキシルフェニルケトン)、「IRGACURE651」(2,2−ジメトキシ−1,2−ジフェニルエタン−1−オン)、「IRGACURE500」、「IRGACURE2959」、「IRGACURE907」、「IRGACURE369」、「IRGACURE1300」、「IRGACURE819」、「IRGACURE1700」、「IRGACURE1800」、「IRGACURE1850」、「DAROCUR4265」、「IRGACURE784」などである。このような開始剤は、組成物の主成分に−OCOCH=CH2を有する化合物がある場合に適している。 A general-purpose product can be used as the radical photopolymerization initiator. For example, “DAROCUR1173” (2-hydroxy-2-methyl-1-phenylpropan-1-one), “IRGACURE184” (1-hydroxycyclohexylphenylketone), “IRGACURE651” manufactured by Ciba Specialty Chemicals Co., Ltd. (2,2-dimethoxy-1,2-diphenylethane-1-one), “IRGACURE500”, “IRGACURE2959”, “IRGACURE907”, “IRGACURE369”, “IRGACURE1300”, “IRGACURE819”, “IRGACURE1700”, “IRGACURE1800” , “IRGACURE1850”, “DAROCUR4265”, “IRGACURE784”, and the like. Such an initiator is suitable when there is a compound having —OCOCH═CH 2 as a main component of the composition.
光ラジカル重合開始剤のその他の例としては、p−メトキシフェニル−2,4−ビス(トリクロロメチル)トリアジン、2−(p−ブトキシスチリル)−5−トリクロロメチル−1,3,4−オキサジアゾール、9−フェニルアクリジン、9,10−ベンズフェナジン、ベンゾフェノン/ミヒラーズケトン混合物、ヘキサアリールビイミダゾール/メルカプトベンズイミダゾール混合物、1−(4−イソプロピルフェニル)−2−ヒドロキシ−2−メチルプロパン−1−オン、ベンジルジメチルケタール、2−メチル−1−[4−(メチルチオ)フェニル]−2−モルホリノプロパン−1−オン、2,4−ジエチルキサントン/p−ジメチルアミノ安息香酸メチル混合物、ベンゾフェノン/メチルトリエタノールアミン混合物などが挙げられる。 Other examples of the photo radical polymerization initiator include p-methoxyphenyl-2,4-bis (trichloromethyl) triazine, 2- (p-butoxystyryl) -5-trichloromethyl-1,3,4-oxadi Azole, 9-phenylacridine, 9,10-benzphenazine, benzophenone / Michler's ketone mixture, hexaarylbiimidazole / mercaptobenzimidazole mixture, 1- (4-isopropylphenyl) -2-hydroxy-2-methylpropan-1-one , Benzyldimethyl ketal, 2-methyl-1- [4- (methylthio) phenyl] -2-morpholinopropan-1-one, 2,4-diethylxanthone / methyl p-dimethylaminobenzoate, benzophenone / methyltriethanol Such as amine mixtures. .
光カチオン重合開始剤としては、たとえば、ジアリールヨードニウム塩、トリアリールスルホニウム塩などが挙げられる。このような開始剤は、組成物の主成分にオキセタン環
またはオキシラン環を有する化合物がある場合に適している。
Examples of the photocationic polymerization initiator include diaryliodonium salts and triarylsulfonium salts. Such an initiator is suitable when there is a compound having an oxetane ring or an oxirane ring as a main component of the composition.
光カチオン重合開始剤の市販品としては、たとえば、みどり化学(株)製のDTS−102、サンアプロ社製のCPI−100P、CPI−100A、UCC社製のサイラキューアーUVI−6990、サイラキュアーUVI−6974、サイラキュアーUVI−6992」、旭電化(株)製のアデカオプトマーSP−150、SP−152、SP−170、SP−172、ローディア社製のPHOTOINITIATOR2074、チバスペシャリティー社製のIRGACURE250、GEシリコンズ社製のUV−9380Cなどが挙げられる。 Commercially available photocationic polymerization initiators include, for example, DTS-102 manufactured by Midori Chemical Co., Ltd., CPI-100P and CPI-100A manufactured by Sun Apro, Syracure UVI-6990, and Cycure UVI manufactured by UCC. -6974, Cyracure UVI-6992 ", Adeka optomer SP-150, SP-152, SP-170, SP-172 manufactured by Asahi Denka Co., Ltd., PHOTOINITIATOR 2074 manufactured by Rhodia, IRGACURE250 manufactured by Ciba Specialty, Examples thereof include UV-9380C manufactured by GE Silicones.
溶媒としては、たとえば、ベンゼン、トルエン、キシレン、メシチレン、ブチルベンゼン、ジエチルベンゼン、テトラリン、メトキシベンゼン、1,2−ジメトキシベンゼン、エチレングリコールジメチルエーテル、ジエチレングリコールジメチルエーテル、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロペンタノン、シクロヘキサノン、酢酸エチル、乳酸エチル、エチレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、γ−ブチロラクトン、2−ピロリドン、N−メチル−2−ピロリドン、ジメチルホルムアミド、クロロホルム、ジクロロメタン、四塩化炭素、ジクロロエタン、テトラクロロエチレン、トリクロロエチレン、クロロベンゼン、t−ブチルアルコール、ジアセトンアルコール、グリセリン、モノアセチン、エチレングリコール、トリエチレングリコール、ヘキシレングリコール、エチレングリコールモノメチルエーテル、エチルセルソルブ、ブチルセルソルブなどが挙げられる。溶媒は、1種単独で用いてもよく、2種以上を混合して用いてもよい。溶媒は、例えば、組成物を支持基板に塗布するときに用いられる。 Examples of the solvent include benzene, toluene, xylene, mesitylene, butylbenzene, diethylbenzene, tetralin, methoxybenzene, 1,2-dimethoxybenzene, ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclopentanone, Cyclohexanone, ethyl acetate, ethyl lactate, ethylene glycol monomethyl ether acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, γ-butyrolactone, 2-pyrrolidone, N-methyl-2-pyrrolidone, dimethylformamide, chloroform, dichloromethane, Carbon tetrachloride, dichloroethane, tetrachloroethylene, trimethyl Roechiren, chlorobenzene, t- butyl alcohol, diacetone alcohol, glycerin, monoacetin, ethylene glycol, triethylene glycol, hexylene glycol, ethylene glycol monomethyl ether, ethyl cellosolve, butyl cellosolve and the like. A solvent may be used individually by 1 type and may be used in mixture of 2 or more types. A solvent is used when apply | coating a composition to a support substrate, for example.
[重合体]
本発明の重合性液晶組成物を重合させることによって重合体が得られる。この重合体は、室温で十分安定したネマチック相を有し、さらに、重合前後で均一なハイブリッド配向性を示し、重合後には所望の配向形態を容易に達成し、薄膜の表面にベタつきがない。なお、重合体フィルムを調製するに際し、組成物の室温液晶安定性に優れるという特性が特に重要である。
[Polymer]
A polymer is obtained by polymerizing the polymerizable liquid crystal composition of the present invention. This polymer has a nematic phase that is sufficiently stable at room temperature, and further exhibits a uniform hybrid orientation before and after the polymerization, and easily achieves a desired orientation form after the polymerization and has no stickiness on the surface of the thin film. In preparing the polymer film, the property that the composition has excellent room temperature liquid crystal stability is particularly important.
重合反応の種類は、ラジカル重合、アニオン重合、カチオン重合、配位重合、リビング重合などである。組成物中の重合性化合物が有する重合性基の種類によって、適当な反応を選択する。化合物(1)、(2)、(3)の重合性基によって例示すると、重合性基(A1)、(A2)、(A3)または(A4)の場合、好ましい反応はラジカル重合であり、重合性基(A5)、(A6)、(A7)または(A8)の場合、好ましい反応はカチオン重合である。優れた配向の重合体を得るときは、熱重合よりも光重合開始剤を用いた重合が好ましい。組成物が液晶である条件下で、重合を行なわせるのが容易だからである。 Types of the polymerization reaction include radical polymerization, anionic polymerization, cationic polymerization, coordination polymerization, living polymerization and the like. An appropriate reaction is selected depending on the type of polymerizable group possessed by the polymerizable compound in the composition. When exemplified by the polymerizable group of the compound (1), (2), (3), in the case of the polymerizable group (A1), (A2), (A3) or (A4), the preferred reaction is radical polymerization, In the case of the sex group (A5), (A6), (A7) or (A8), the preferred reaction is cationic polymerization. When a polymer having an excellent orientation is obtained, polymerization using a photopolymerization initiator is preferable to thermal polymerization. This is because it is easy to perform polymerization under the condition that the composition is liquid crystal.
光重合に用いられる光の種類は、通常、紫外線、可視光線、赤外線などであるが、電子線、X線などの電磁波を用いてもよい。これらの中では、紫外線および可視光線が好ましい。波長の範囲は、好ましくは150〜500nm、さらに好ましくは250〜450nm、特に好ましくは300〜400nmである。 The type of light used for photopolymerization is usually ultraviolet rays, visible rays, infrared rays, or the like, but electromagnetic waves such as electron beams and X-rays may be used. Among these, ultraviolet rays and visible rays are preferable. The wavelength range is preferably 150 to 500 nm, more preferably 250 to 450 nm, and particularly preferably 300 to 400 nm.
光源は、低圧水銀ランプ(殺菌ランプ、蛍光ケミカルランプ、ブラックライト)、高圧放電ランプ(高圧水銀ランプ、メタルハライドランプ)、ショートアーク放電ランプ(超高圧水銀ランプ、キセノンランプ、水銀キセノンランプ)などである。好ましい光源は超高圧水銀ランプである。光源からの光はそのまま組成物に照射してもよい。フィルターによって選択した特定の波長(または特定の波長領域)を組成物に照射してもよい。 The light source is a low-pressure mercury lamp (sterilization lamp, fluorescent chemical lamp, black light), high-pressure discharge lamp (high-pressure mercury lamp, metal halide lamp), short arc discharge lamp (ultra-high pressure mercury lamp, xenon lamp, mercury xenon lamp), etc. . A preferred light source is an ultra high pressure mercury lamp. You may irradiate the composition with the light from a light source as it is. The composition may be irradiated with a specific wavelength (or a specific wavelength region) selected by a filter.
照射エネルギー密度は、好ましくは2〜5000mJ/cm2、さらに好ましくは10
〜3000mJ/cm2、特に好ましくは100〜2000mJ/cm2である。照度は、好ましくは0.1〜5000mW/cm2、さらに好ましくは1〜2000mW/cm2である。組成物が液晶相を有するように、光を照射するときの温度を設定する。好ましい照射温度は100℃以下である。100℃以下の温度であれば熱による重合が起こりにくいので、良好な配向が得られる。
The irradiation energy density is preferably 2 to 5000 mJ / cm 2 , more preferably 10
~3000mJ / cm 2, particularly preferably from 100 to 2000 mJ / cm 2. The illuminance is preferably 0.1 to 5000 mW / cm 2 , more preferably 1 to 2000 mW / cm 2 . The temperature at which light is irradiated is set so that the composition has a liquid crystal phase. A preferable irradiation temperature is 100 ° C. or less. Since the polymerization due to heat hardly occurs at a temperature of 100 ° C. or less, good orientation can be obtained.
重合体の形状は、フィルム、板、粒、粉末などである。重合体は成形されてもよい。フィルムの重合体を得るには、支持基板が一般的に用いられる。支持基板の上に組成物を塗布し、液晶相を有している塗膜(paint film)を重合させるとフィルムが得られる。好ましい重合体の厚さは、重合体の光学異方性の値および用途に依存する。したがって、その範囲を厳密に決定することはできないが、好ましい厚さは0.05〜50μm、さらに好ましくは0.1〜20μm、特に好ましくは0.5〜10μmの範囲である。これらの重合体のヘイズ値(haze value;曇り度)は、概して1.5%以下である。これらの重合体の透過率は、可視光領域において一般的に80%以上である。このような重合体は液晶表示素子に用いる光学異方性の薄膜として適している。 The shape of the polymer is a film, plate, grain, powder or the like. The polymer may be molded. To obtain a film polymer, a support substrate is generally used. A film is obtained by applying the composition on a support substrate and polymerizing a paint film having a liquid crystal phase. The preferred polymer thickness depends on the value of the optical anisotropy of the polymer and the application. Therefore, although the range cannot be determined strictly, the preferred thickness is 0.05 to 50 μm, more preferably 0.1 to 20 μm, and particularly preferably 0.5 to 10 μm. The haze value (haze value) of these polymers is generally 1.5% or less. The transmittance of these polymers is generally 80% or more in the visible light region. Such a polymer is suitable as an optically anisotropic thin film used for a liquid crystal display element.
支持基板としては、たとえば、ガラス基板や、トリアセチルセルロース(以下「TAC」と略記することがある。)、ポリビニルアルコール、ポリイミド、ポリエステル、ポリアリレート、ポリエーテルイミド、ポリエチレンテレフタレート、ポリエチレンナフタレートなどの樹脂フィルムが挙げられる。市販の樹脂フィルムとしては、たとえば、JSR(株)の「アートン」、日本ゼオン(株)の「ゼオネックス」および「ゼオノア」、三井化学(株)の「アペル」などが挙げられる。樹脂フィルムは、一軸延伸フィルム、二軸延伸フィルムなどである。好ましい支持基板は、配向処理されたガラス基板、TACフィルムまたはノルボルネン樹脂フィルムであり、特に好ましい支持基板は、ラビング処理されたポリイミド配向膜を表面に有するガラス基板、ケン化処理したTACフィルムまたは親水化処理したノルボルネン樹脂フィルムである。なお、前記親水化処理とは、プラズマ処理またはコロナ処理である。 Examples of the support substrate include a glass substrate, triacetyl cellulose (hereinafter sometimes abbreviated as “TAC”), polyvinyl alcohol, polyimide, polyester, polyarylate, polyetherimide, polyethylene terephthalate, polyethylene naphthalate, and the like. A resin film is mentioned. Examples of commercially available resin films include “Arton” from JSR Corporation, “Zeonex” and “Zeonoa” from Nippon Zeon Corporation, “Apel” from Mitsui Chemicals, Inc., and the like. The resin film is a uniaxially stretched film, a biaxially stretched film, or the like. A preferred support substrate is an alignment-treated glass substrate, a TAC film or a norbornene resin film, and a particularly preferred support substrate is a glass substrate having a rubbing-treated polyimide alignment film on its surface, a saponified TAC film or a hydrophilization. It is the processed norbornene resin film. The hydrophilic treatment is plasma treatment or corona treatment.
支持基板上の塗膜は、組成物をそのまま塗布することによって調製される。塗膜は、組成物を適切な溶媒に溶解させて塗布した後、溶媒を除去することによっても調製される。塗布の方法は、スピンコート、ロールコート、カーテンコート、フローコート、プリント、マイクログラビアコート、グラビアコート、ワイヤーバーコート、デップコート、スプレーコート、メニスカスコート、流延成膜法などである。 The coating film on the support substrate is prepared by applying the composition as it is. The coating film can also be prepared by dissolving the composition in a suitable solvent and applying it, and then removing the solvent. Examples of the coating method include spin coating, roll coating, curtain coating, flow coating, printing, micro gravure coating, gravure coating, wire bar coating, dip coating, spray coating, meniscus coating, and cast film formation.
組成物において、液晶分子の配向を決定する因子は、1)組成物に含有される化合物の種類、2)支持基板の種類、3)配向処理の方法などである。因子1)としては、化合物(1)〜(3)などの種類や組成比などが挙げられる。因子2)としては、支持基板を構成する重合体などの種類などが挙げられる。因子3)としては、レーヨン布などで一方向にこする(ラビング)方法、酸化ケイ素を斜方蒸着させる方法、スリット状にエッチング加工する方法などの配向処理方法が挙げられる。ラビング処理においては、支持基板を直接的にラビングしてもよく、あるいは、支持基板をポリイミドやポリビニルアルコールなどの薄膜でコーティングし、この薄膜をラビングしてもよい。 In the composition, factors that determine the alignment of liquid crystal molecules are 1) the type of compound contained in the composition, 2) the type of support substrate, and 3) the method of alignment treatment. Examples of factor 1) include the types and composition ratios of compounds (1) to (3). Examples of the factor 2) include the types of polymers constituting the support substrate. Factor 3) includes orientation treatment methods such as rubbing in one direction with a rayon cloth or the like, a method of obliquely depositing silicon oxide, and a method of etching into a slit. In the rubbing treatment, the support substrate may be directly rubbed, or the support substrate may be coated with a thin film such as polyimide or polyvinyl alcohol, and the thin film may be rubbed.
本発明の重合体の用途は次のとおりである。本発明の重合体は、光学異方性を有する成形体として使用できる。この重合体の用途の例は、位相差板(1/2波長板、1/4波長板など)、反射防止膜、選択反射膜、視野角補償膜などの光学フィルムである。ホモジニアス、ハイブリッド、ホメオトロピックなどの配向を有する重合体は、位相差板、偏光素子、液晶配向膜、反射防止膜、選択反射膜、視野角補償膜などに利用できる。このような
重合体は、液晶表示素子の位相差板や視野角補償膜などに、光学補償を目的として用いられる。産業上の重要な用途の例は、VAモード、IPSモード、TNモード、MVAモードなどの液晶表示素子における視野角補償である。この重合体は、高熱伝導性エポキシ樹脂、接着剤、機械的異方性を持つ合成高分子、化粧品、装飾品、非線型光学材料、情報記憶材料などにも利用できる。
Applications of the polymer of the present invention are as follows. The polymer of the present invention can be used as a molded product having optical anisotropy. Examples of the use of this polymer are optical films such as retardation plates (1/2 wavelength plates, 1/4 wavelength plates, etc.), antireflection films, selective reflection films, and viewing angle compensation films. Polymers having an orientation such as homogeneous, hybrid, and homeotropic can be used for retardation plates, polarizing elements, liquid crystal alignment films, antireflection films, selective reflection films, viewing angle compensation films, and the like. Such a polymer is used for the purpose of optical compensation in a phase difference plate of a liquid crystal display element, a viewing angle compensation film, and the like. An example of an important industrial application is viewing angle compensation in liquid crystal display elements such as VA mode, IPS mode, TN mode, and MVA mode. This polymer can also be used for highly heat-conductive epoxy resins, adhesives, synthetic polymers having mechanical anisotropy, cosmetics, decorations, non-linear optical materials, information storage materials, and the like.
重合体の用途の一例である位相差板は、偏光の状態を変換する機能を有する。たとえば、1/2波長機能板は、直線偏光の振動方向を90度回転させる機能を有する。この1/2波長機能板は、d=λ/2×Δnの式(dは組成物の厚さ、λは波長、Δnは光学異方性)を満たすように組成物を支持基板上に塗布して配向させた後、光重合させることによって得られる。一方、1/4波長機能板は、直線偏光を円偏光に、または円偏光を直線偏光に変換する機能を有する。この場合、d=λ/4×Δnの条件を満たすように組成物の塗膜を調製すればよい。 A retardation plate, which is an example of a polymer application, has a function of converting the state of polarization. For example, the half-wave function plate has a function of rotating the vibration direction of linearly polarized light by 90 degrees. This half-wavelength functional plate is coated on a supporting substrate so as to satisfy the formula d = λ / 2 × Δn (d is the thickness of the composition, λ is the wavelength, and Δn is the optical anisotropy). Then, it is obtained by photopolymerization after orientation. On the other hand, the quarter wavelength functional plate has a function of converting linearly polarized light into circularly polarized light or converting circularly polarized light into linearly polarized light. In this case, a coating film of the composition may be prepared so as to satisfy the condition of d = λ / 4 × Δn.
重合体の厚さ(d)は次のように調整される。組成物を溶媒で希釈した後、支持基板上に塗布する方法では、組成物の濃度、塗布する方法、塗布する条件などを適切に選択することによって、目的とする厚さの塗膜を得ることができる。液晶セルを利用する方法も好ましい。液晶セルはポリイミドなどの配向膜を有しているので都合がよい。この液晶セルに組成物を注入する場合には、液晶セルの間隔によって塗膜の厚さを調整することができる。 The thickness (d) of the polymer is adjusted as follows. In the method of applying the composition on a support substrate after diluting the composition with a solvent, a coating film having a desired thickness can be obtained by appropriately selecting the concentration of the composition, the application method, the application conditions, and the like. Can do. A method using a liquid crystal cell is also preferable. The liquid crystal cell is convenient because it has an alignment film such as polyimide. When injecting the composition into the liquid crystal cell, the thickness of the coating film can be adjusted by the interval of the liquid crystal cell.
[実施例]
以下、実施例に基づいて本発明をより具体的に説明するが、本発明はこれら実施例に何ら限定されるものではない。
[Example]
EXAMPLES Hereinafter, although this invention is demonstrated more concretely based on an Example, this invention is not limited to these Examples at all.
なお、以下の実施例等で用いた化合物は、フーベン・ヴァイル(Houben Wyle, Methoden der Organischen Chemie, Georg Thieme Verlag, Stuttgart)、オーガニック・リアクションズ(Organic Reactions, John Wily & Sons Inc.)、オーガニック・シンセセーズ(Organic Syntheses, John Wily & Sons, Inc.)、コンプリヘンシブ・オーガニック・
シンセシス(Comprehensive Organic Synthesis, Pergamon Press)、新実験化学講座(
丸善)などに記載された、有機化学における合成方法を適切に組み合わせることにより合成できる。
The compounds used in the following examples and the like are Houben Wyle (Methoden der Organischen Chemie, Georg Thieme Verlag, Stuttgart), Organic Reactions (Organic Reactions, John Wily & Sons Inc.), Organic Synthises. (Organic Syntheses, John Wily & Sons, Inc.), Comprehensive Organic
Synthesis (Comprehensive Organic Synthesis, Pergamon Press), New Experimental Chemistry Course (
Can be synthesized by appropriately combining synthetic methods in organic chemistry, such as described in Maruzen).
化合物(1−1−27)は特開2003−238491号公報、化合物(1−1−31)は特開2005−60373号公報に記載の方法に従って合成した。化合物(1−2−2)は、Macromol.Chem.,190,3201-3215(1998)、WO97/00600に記載の方法に従って合成した。化合物(2−1−11)および化合物(2−1−20)は、WO00/59966、WO02/090447、特願2005−355180号に記載の方法に従って合成した。化合物(2−1−37)は特願2005−355181号に記載の方法に従って合成した。化合物(3−1−7)および化合物(3−1−12)は特開2004−231638号公報に記載の方法に従って合成した。化合物(3−2−3)および化合物(3−3−3)は、特願2005−169337号に記載の方法に従って合成した。化合物(CP1)は、特開2005−320317号公報に記載の方法に従って合成した。 The compound (1-1-27) was synthesized according to the method described in JP-A-2003-238491, and the compound (1-1-31) was synthesized according to the method described in JP-A-2005-60373. Compound (1-2-2) was synthesized according to the method described in Macromol. Chem., 190, 3201-3215 (1998), WO 97/00600. Compound (2-1-11) and compound (2-1-20) were synthesized according to the method described in WO00 / 59966, WO02 / 090447, and Japanese Patent Application No. 2005-355180. Compound (2-1-37) was synthesized according to the method described in Japanese Patent Application No. 2005-355181. Compound (3-1-7) and compound (3-1-12) were synthesized according to the method described in JP-A-2004-231638. Compound (3-2-3) and compound (3-3-3) were synthesized according to the method described in Japanese Patent Application No. 2005-169337. Compound (CP1) was synthesized according to the method described in JP-A-2005-320317.
また、フィルムの配向については、以下に示す目視による観察と、偏光解析装置を用いた測定とで判定した。
1)目視による観察
クロスニコルに配置した2枚の偏光板の間に重合体フィルムを狭持して、フィルム面に垂直方向(傾斜角は0度)から光を照射した。照射の傾斜角を0度から例えば50度に増大させながら透過光の変化を観察した。照射を傾ける方向は、ラビングの方向(液晶の長
軸方向)に一致させた。垂直方向からの透過光が最大であり、垂直方向を中心にラビング方向の左右で透過光強度が対称であることが確認された場合には、ホモジニアス配向(図2参照)であると判断した。ホモジニアス配向では、液晶の配向ベクトルが支持基板(TACフィルム)と平行であるからである。一方、垂直方向を中心にラビング方向の左右で非対称の変化であることが確認された場合には、この液晶分子の配向ベクトルが支持基板(TACフィルム)に対して傾いていることを示すため、ハイブリッド配向(図1参照)であると判断した。
Moreover, about the orientation of the film, it determined by the observation by visual observation shown below, and the measurement using an ellipsometer.
1) Observation by visual observation A polymer film was sandwiched between two polarizing plates arranged in crossed Nicols, and light was irradiated from the direction perpendicular to the film surface (the inclination angle was 0 degree). The change in transmitted light was observed while increasing the tilt angle of irradiation from 0 degree to, for example, 50 degrees. The direction of tilting the irradiation was matched with the rubbing direction (long axis direction of the liquid crystal). When it was confirmed that the transmitted light from the vertical direction was the maximum and the transmitted light intensity was symmetrical on the left and right in the rubbing direction with the vertical direction as the center, it was determined that the orientation was homogeneous (see FIG. 2). This is because in homogeneous alignment, the alignment vector of the liquid crystal is parallel to the support substrate (TAC film). On the other hand, when it is confirmed that the change is asymmetrical in the rubbing direction on the left and right with respect to the vertical direction, this indicates that the alignment vector of the liquid crystal molecules is inclined with respect to the support substrate (TAC film). The hybrid orientation was determined (see FIG. 1).
2)偏光解析装置を用いた測定
シンテック(株)製偏光解析装置(商品名;OPTIPRO)を用いて、重合体フィルムに550nmの波長の光を照射し、この光の入射角度をフィルム面に対して垂直方向からラビング方向に傾斜させながらレタデーションを測定した。レタデーションはΔn×dで表される。Δnは光学異方性であり、dは重合体フィルムの厚さである。
2) Measurement using an ellipsometer Using a ellipsometer (trade name; OPTIPRO) manufactured by Shintec Co., Ltd., the polymer film was irradiated with light having a wavelength of 550 nm, and the incident angle of this light was measured with respect to the film surface. The retardation was measured while tilting from the vertical direction to the rubbing direction. The retardation is expressed by Δn × d. Δn is the optical anisotropy and d is the thickness of the polymer film.
〔実施例1〕
<組成物(PLC−1)の調製>
以下に示す化合物(1−1−27)30重量%、化合物(2−1−11)40重量%および化合物(3−1−7)30重量%から成る組成物(MIX1)を調製した。
[Example 1]
<Preparation of composition (PLC-1)>
A composition (MIX1) comprising 30% by weight of the compound (1-1-27) shown below, 40% by weight of the compound (2-1-11) and 30% by weight of the compound (3-1-7) was prepared.
次に、得られた組成物(MIX1)に重合開始剤(チバ・スペシャリティ・ケミカルズ製、商品名:IRGACURE 907)を3重量%加えた後、混合溶媒(重量比;トルエン/シクロペンタノン=2:1)を加えて20重量%の溶液を調製して組成物(PLC−1)を得た。 Next, 3% by weight of a polymerization initiator (manufactured by Ciba Specialty Chemicals, trade name: IRGACURE 907) was added to the resulting composition (MIX1), and then a mixed solvent (weight ratio; toluene / cyclopentanone = 2). 1) was added to prepare a 20 wt% solution to obtain a composition (PLC-1).
<組成物(PLC−1)の安定性評価>
支持基板として、ケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−1)を、バーコーターを用いてTACフィルムに塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去した。生成した塗膜を室温で静置し、表面から結晶の析出が発生するか否かについて観察し、組成物の安定性を評価した。その結果、3日経過しても結晶の析出も無く、組成物(PLC−1)は十分に安定な組成物であることを確認した。
<Stability evaluation of composition (PLC-1)>
As the support substrate, a saponified TAC film was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-1) was applied to a TAC film using a bar coater and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent. The produced coating film was allowed to stand at room temperature, and it was observed whether or not crystal precipitation occurred from the surface, and the stability of the composition was evaluated. As a result, it was confirmed that the composition (PLC-1) was a sufficiently stable composition without crystal precipitation even after 3 days.
<重合体フィルム(F1)の評価>
組成物(PLC−1)の安定性評価と同様に、支持基板としてケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−1)を、バーコーターを用いてTACフィルム上に塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去して液晶層を配向させた。生成した塗膜に、超高圧水銀灯(250W)を用いて紫外線(30mW/cm2;365nm)
を窒素雰囲気下、25℃で30秒間照射した。これにより重合体フィルム(F1)が得られた。目視による観察では、重合体フィルム(F1)の配向はハイブリッド配向であった。また、偏光解析装置による測定結果(図1に示す)によってもハイブリッド配向であることを確認した。
<Evaluation of polymer film (F1)>
Similarly to the stability evaluation of the composition (PLC-1), a TAC film subjected to saponification treatment as a support substrate was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-1) was applied onto a TAC film using a bar coater and then heat treated in an oven set at 70 ° C. for 5 minutes to remove the solvent and align the liquid crystal layer. Ultraviolet light (30 mW / cm 2 ; 365 nm) is applied to the formed coating film using an ultrahigh pressure mercury lamp (250 W).
Was irradiated at 25 ° C. for 30 seconds in a nitrogen atmosphere. Thereby, a polymer film (F1) was obtained. In visual observation, the orientation of the polymer film (F1) was a hybrid orientation. Moreover, it confirmed that it was a hybrid orientation also by the measurement result (shown in FIG. 1) by an ellipsometer.
〔実施例2〕
<組成物(PLC−2)の調製>
以下に示す化合物(1−2−2)30重量%、化合物(2−1−20)45重量%および化合物(3−2−3)25重量%から成る組成物(MIX2)を調製した。
[Example 2]
<Preparation of composition (PLC-2)>
A composition (MIX2) comprising 30% by weight of the compound (1-2-2) shown below, 45% by weight of the compound (2-1-20) and 25% by weight of the compound (3-2-3) was prepared.
次に、得られた組成物(MIX2)に重合開始剤(チバ・スペシャリティ・ケミカルズ製、商品名:IRGACURE 651)を3重量%加えた後、混合溶媒(重量比;トルエン/シクロペンタノン=2:1)を加えて20重量%の溶液を調製して組成物(PLC−2)を得た。 Next, 3% by weight of a polymerization initiator (manufactured by Ciba Specialty Chemicals, trade name: IRGACURE 651) was added to the resulting composition (MIX2), and then a mixed solvent (weight ratio; toluene / cyclopentanone = 2). 1) was added to prepare a 20 wt% solution to obtain a composition (PLC-2).
<組成物(PLC−2)の安定性評価>
支持基板として、ケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−2)を、バーコーターを用いてTACフィルムに塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去した。生成した塗膜を室温で静置し、表面から結晶の析出が発生するか否かについて観察し、組成物の安定性を評価した。その結果、3日経過しても結晶の析出も無く、組成物(PLC−2)は十分に安定な組成物であることを確認した。
<Stability evaluation of composition (PLC-2)>
As the support substrate, a saponified TAC film was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-2) was applied to a TAC film using a bar coater, and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent. The produced coating film was allowed to stand at room temperature, and it was observed whether or not crystal precipitation occurred from the surface, and the stability of the composition was evaluated. As a result, it was confirmed that the composition (PLC-2) was a sufficiently stable composition without crystal precipitation even after 3 days.
<重合体フィルム(F2)の評価>
組成物(PLC−2)の安定性評価と同様に、支持基板としてケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−2)を、バーコーターを用いてTACフィルム上に塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去して液晶層を配向させた。生成し
た塗膜に、超高圧水銀灯(250W)を用いての紫外線(30mW/cm2;365nm
)を窒素雰囲気下、25℃で30秒間照射した。これにより重合体フィルム(F2)が得られた。目視による観察では、重合体フィルム(F2)の配向はハイブリッド配向であった。また、偏光解析装置による測定結果からもハイブリッド配向であることを確認した。
<Evaluation of polymer film (F2)>
Similar to the stability evaluation of the composition (PLC-2), a TAC film subjected to saponification treatment as a support substrate was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-2) was applied onto a TAC film using a bar coater and then heat treated in an oven set at 70 ° C. for 5 minutes to remove the solvent and align the liquid crystal layer. Ultraviolet light (30 mW / cm 2 ; 365 nm) using an ultrahigh pressure mercury lamp (250 W) is applied to the formed coating film.
) In a nitrogen atmosphere at 25 ° C. for 30 seconds. As a result, a polymer film (F2) was obtained. By visual observation, the orientation of the polymer film (F2) was a hybrid orientation. Moreover, it was confirmed from the measurement result by the ellipsometer that it was a hybrid orientation.
〔実施例3〕
<組成物(PLC−3)の調製>
以下に示す化合物(1−1−27)30重量%、化合物(2−1−11)40重量%および化合物(3−3−3)30重量%から成る組成物(MIX3)を調製した。
Example 3
<Preparation of composition (PLC-3)>
A composition (MIX3) comprising 30% by weight of the compound (1-1-27) shown below, 40% by weight of the compound (2-1-11) and 30% by weight of the compound (3-3-3) was prepared.
次に、得られた組成物(MIX3)に重合開始剤(チバ・スペシャリティ・ケミカルズ製、商品名:IRGACURE 907)を3重量%加えた後、混合溶媒(重量比;トルエン/シクロペンタノン=2:1)を加えて20重量%の溶液を調製して組成物(PLC−3)を得た。 Next, 3% by weight of a polymerization initiator (manufactured by Ciba Specialty Chemicals, trade name: IRGACURE 907) was added to the resulting composition (MIX3), and then a mixed solvent (weight ratio; toluene / cyclopentanone = 2). 1) was added to prepare a 20 wt% solution to obtain a composition (PLC-3).
<組成物(PLC−3)の安定性評価>
支持基板として、ケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−3)を、バーコーターを用いてTACフィルムに塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去した。生成した塗膜を室温で静置し、表面から結晶の析出が発生するか否かについて観察し、組成物の安定性を評価した。その結果、3日経過しても結晶の析出も無く、組成物(PLC−3)は十分に安定な組成物であることを確認した。
<Stability evaluation of composition (PLC-3)>
As the support substrate, a saponified TAC film was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-3) was applied to a TAC film using a bar coater, and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent. The produced coating film was allowed to stand at room temperature, and it was observed whether or not crystal precipitation occurred from the surface, and the stability of the composition was evaluated. As a result, it was confirmed that the composition (PLC-3) was a sufficiently stable composition without crystal precipitation even after 3 days.
<重合体フィルム(F3)の評価>
組成物(PLC−3)の安定性評価と同様に、支持基板としてケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−3)を、バーコーターを用いてTACフィルム上に塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去して液晶層を配向させた。生成した塗膜に、超高圧水銀灯(250W)を用いての紫外線(30mW/cm2;365nm
)を窒素雰囲気下、25℃で30秒間照射した。これにより重合体フィルム(F3)が得られた。目視による観察では、重合体フィルム(F3)の配向はハイブリッド配向であった。また、偏光解析装置による測定結果からもハイブリッド配向であることを確認した。
<Evaluation of polymer film (F3)>
Similarly to the stability evaluation of the composition (PLC-3), a TAC film subjected to saponification treatment as a support substrate was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-3) was applied onto a TAC film using a bar coater and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent and align the liquid crystal layer. Ultraviolet light (30 mW / cm 2 ; 365 nm) using an ultrahigh pressure mercury lamp (250 W) is applied to the formed coating film.
) In a nitrogen atmosphere at 25 ° C. for 30 seconds. As a result, a polymer film (F3) was obtained. By visual observation, the orientation of the polymer film (F3) was a hybrid orientation. Moreover, it was confirmed from the measurement result by the ellipsometer that it was a hybrid orientation.
〔実施例4〕
<組成物(PLC−4)の調製>
以下に示す化合物(1−1−31)35重量%、化合物(2−1−37)40重量%および化合物(3−1−12)25重量%から成る組成物(MIX4)を調製した。
Example 4
<Preparation of composition (PLC-4)>
A composition (MIX4) comprising 35% by weight of the following compound (1-1-31), 40% by weight of the compound (2-1-37) and 25% by weight of the compound (3-1-12) was prepared.
次に、得られた組成物(MIX4)に重合開始剤(サンアプロ製、商品名:CPI−100P)を3重量%加えた後、混合溶媒(重量比;トルエン/シクロペンタノン=2:1)を加えて20重量%の溶液を調製して組成物(PLC−4)を得た。 Next, 3% by weight of a polymerization initiator (trade name: CPI-100P, manufactured by San Apro) was added to the resulting composition (MIX4), and then a mixed solvent (weight ratio; toluene / cyclopentanone = 2: 1). Was added to prepare a 20 wt% solution to obtain a composition (PLC-4).
<組成物(PLC−4)の安定性評価>
支持基板として、ケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−4)を、バーコーターを用いてTACフィルムに塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去した。生成した塗膜を室温で静置し、表面から結晶の析出が発生するか否かについて観察し、組成物の安定性を評価した。その結果、3日経過しても結晶の析出も無く、組成物(PLC−4)は十分に安定な組成物であることを確認した。
<Stability evaluation of composition (PLC-4)>
As the support substrate, a saponified TAC film was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-4) was applied to a TAC film using a bar coater and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent. The produced coating film was allowed to stand at room temperature, and it was observed whether or not crystal precipitation occurred from the surface, and the stability of the composition was evaluated. As a result, it was confirmed that the composition (PLC-4) was a sufficiently stable composition without crystal precipitation even after 3 days.
<重合体フィルム(F4)の評価>
組成物(PLC−4)の安定性評価と同様に、支持基板としてケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−4)を、バーコーターを用いてTACフィルム上に塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去して液晶層を配向させた。生成した塗膜に、超高圧水銀灯(250W)を用いての紫外線(30mW/cm2;365nm
)を窒素雰囲気下、25℃で30秒間照射した。これにより重合体フィルム(F4)が得られた。目視による観察では、重合体フィルム(F4)の配向はハイブリッド配向であった。また、偏光解析装置による測定結果からもハイブリッド配向であることを確認した。
<Evaluation of polymer film (F4)>
Similar to the stability evaluation of the composition (PLC-4), a TAC film subjected to saponification treatment as a supporting substrate was used after the surface of the film was previously rubbed with a rayon cloth. The composition (PLC-4) was applied onto a TAC film using a bar coater and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent and align the liquid crystal layer. Ultraviolet light (30 mW / cm 2 ; 365 nm) using an ultrahigh pressure mercury lamp (250 W) is applied to the formed coating film.
) In a nitrogen atmosphere at 25 ° C. for 30 seconds. Thereby, a polymer film (F4) was obtained. By visual observation, the orientation of the polymer film (F4) was a hybrid orientation. Moreover, it was confirmed from the measurement result by the ellipsometer that it was a hybrid orientation.
〔比較例1〕
<組成物(PLC−5)の調製>
以下に示す化合物(CP1)35重量%および化合物(1−1−31)65重量%から成る組成物(MIX5)を調製した。
[Comparative Example 1]
<Preparation of composition (PLC-5)>
A composition (MIX5) comprising 35% by weight of the following compound (CP1) and 65% by weight of the compound (1-1-31) was prepared.
次に、組成物(MIX5)に重合開始剤(みどり化学(株)製、商品名:DTS−102)を3重量%加えた後、混合溶媒(重量比;トルエン/シクロペンタノン=2:1)を加えて20重量%の溶液を調製して組成物(PLC−5)を得た。 Next, 3% by weight of a polymerization initiator (manufactured by Midori Chemical Co., Ltd., trade name: DTS-102) was added to the composition (MIX5), and then a mixed solvent (weight ratio; toluene / cyclopentanone = 2: 1). ) Was added to prepare a 20 wt% solution to obtain a composition (PLC-5).
<組成物(PLC−5)の安定性評価>
支持基板としてケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−5)を、バーコーターを用いてTACフィルムに塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去した。生成した塗膜を室温で静置し、表面から結晶の析出が発生するか否かについて観察し、組成物の安定性を評価した。その結果、組成物(PLC−5)はわずか8分で結晶が析出し始め、液晶相が十分に安定な組成物ではないことを確認した。
<Stability evaluation of composition (PLC-5)>
A TAC film subjected to saponification treatment as a supporting substrate was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-5) was applied to a TAC film using a bar coater and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent. The produced coating film was allowed to stand at room temperature, and it was observed whether or not crystal precipitation occurred from the surface, and the stability of the composition was evaluated. As a result, it was confirmed that the composition (PLC-5) started to crystallize in only 8 minutes and the liquid crystal phase was not a sufficiently stable composition.
<重合体フィルム(F5)の評価>
組成物(PLC−5)の安定性評価と同様に、支持基板としてケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−5)を、バーコーターを用いてTACフィルムに塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去して液晶層を配向させた。生成した塗膜に、超高圧水銀灯(250W)を用いての紫外線(30mW/cm2;365nm)
を窒素雰囲気下、25℃で30秒間照射した。これにより重合体フィルム(F5)が得られた。目視による観察では、重合体フィルム(F5)の配向はハイブリッド配向であった。また、偏光解析装置による測定結果からもハイブリッド配向であることを確認した。
<Evaluation of polymer film (F5)>
Similar to the stability evaluation of the composition (PLC-5), a TAC film subjected to saponification treatment as a supporting substrate was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-5) was applied to a TAC film using a bar coater and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent and align the liquid crystal layer. Ultraviolet light (30 mW / cm 2 ; 365 nm) using an ultrahigh pressure mercury lamp (250 W) on the formed coating film
Was irradiated at 25 ° C. for 30 seconds in a nitrogen atmosphere. As a result, a polymer film (F5) was obtained. By visual observation, the orientation of the polymer film (F5) was a hybrid orientation. Moreover, it was confirmed from the measurement result by the ellipsometer that it was a hybrid orientation.
〔比較例2〕
<組成物(PLC−6)の調製>
以下に示す化合物(1−1−27)60重量%および化合物(3−1−7)40重量%から成る組成物(MIX6)を調製した。
[Comparative Example 2]
<Preparation of composition (PLC-6)>
A composition (MIX6) comprising 60% by weight of the following compound (1-1-27) and 40% by weight of the compound (3-1-7) was prepared.
次に、得られた組成物(MIX6)に重合開始剤(チバ・スペシャリティ・ケミカルズ製、商品名:IRGACURE 907)を3重量%加えた後、混合溶媒(重量比;トルエン/シクロペンタノン=2:1)を加えて20重量%の溶液を調製して組成物(PLC−6)を得た。 Next, 3% by weight of a polymerization initiator (manufactured by Ciba Specialty Chemicals, trade name: IRGACURE 907) was added to the resulting composition (MIX6), and then a mixed solvent (weight ratio; toluene / cyclopentanone = 2). 1) was added to prepare a 20 wt% solution to obtain a composition (PLC-6).
<組成物(PLC−6)の安定性評価>
支持基板として、ケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−6)を、バーコーターを用いてTACフィルムに塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去した。生成した塗膜を室温で静置し、表面から結晶の析出が発生するか否かについて観察し、組成物の安定性を評価した。その結果、組成物(PLC−6)はわずか7分で結晶が析出し始め、液晶相が十分に安定な組成物ではないことを確認した。
<Stability evaluation of composition (PLC-6)>
As the support substrate, a saponified TAC film was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-6) was applied to a TAC film using a bar coater, and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent. The produced coating film was allowed to stand at room temperature, and it was observed whether or not crystal precipitation occurred from the surface, and the stability of the composition was evaluated. As a result, it was confirmed that the composition (PLC-6) started to crystallize in only 7 minutes and the liquid crystal phase was not a sufficiently stable composition.
<重合体フィルム(F6)の評価>
組成物(PLC−6)の安定性評価と同様に、支持基板としてケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−6)を、バーコーターを用いてTACフィルム上に塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去して液晶層を配向させた。生成した塗膜に、超高圧水銀灯(250W)を用いての紫外線(30mW/cm2;365nm
)を窒素雰囲気下、25℃で30秒間照射した。これにより重合体フィルム(F6)が得られた。目視による観察では、重合体フィルム(F6)の配向はホモジニアス配向であった。また、偏光解析装置による測定結果(図2に示す)によってもホモジニアス配向であることを確認した。
<Evaluation of polymer film (F6)>
Similar to the stability evaluation of the composition (PLC-6), a TAC film subjected to saponification treatment as a support substrate was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-6) was applied onto a TAC film using a bar coater and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent and align the liquid crystal layer. Ultraviolet light (30 mW / cm 2 ; 365 nm) using an ultrahigh pressure mercury lamp (250 W) is applied to the formed coating film.
) In a nitrogen atmosphere at 25 ° C. for 30 seconds. As a result, a polymer film (F6) was obtained. By visual observation, the orientation of the polymer film (F6) was homogeneous orientation. Moreover, it confirmed that it was homogeneous orientation also by the measurement result (shown in FIG. 2) by an ellipsometer.
〔比較例3〕
<組成物(PLC−7)の調製>
以下に示す化合物(1−1−27)70重量%および化合物(2−1−11)30重量%から成る組成物(MIX7)を調製した。
[Comparative Example 3]
<Preparation of composition (PLC-7)>
A composition (MIX7) comprising 70% by weight of the following compound (1-1-27) and 30% by weight of the compound (2-1-11) was prepared.
次に、得られた組成物(MIX7)に重合開始剤(チバ・スペシャリティ・ケミカルズ製、商品名:IRGACURE 907)を3重量%加えた後、混合溶媒(重量比;トルエン/シクロペンタノン=2:1)を加えて20重量%の溶液を調製して組成物(PLC−7)を得た。 Next, 3% by weight of a polymerization initiator (manufactured by Ciba Specialty Chemicals, trade name: IRGACURE 907) was added to the resulting composition (MIX7), and then a mixed solvent (weight ratio; toluene / cyclopentanone = 2). 1) was added to prepare a 20 wt% solution to obtain a composition (PLC-7).
<組成物(PLC−7)の安定性評価>
支持基板として、ケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−7)を、バーコーターを用いてTAC
フィルムに塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去した。生成した塗膜を室温で静置し、表面から結晶の析出が発生するか否かについて観察し、組成物の安定性を評価した。その結果、組成物(PLC−7)はわずか5分で結晶が析出し始め、液晶相が十分に安定な組成物ではないことを確認した。
<Stability evaluation of composition (PLC-7)>
As the support substrate, a saponified TAC film was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-7) was converted to TAC using a bar coater.
After application to the film, the solvent was removed by heat treatment in an oven set at 70 ° C. for 5 minutes. The produced coating film was allowed to stand at room temperature, and it was observed whether or not crystal precipitation occurred from the surface, and the stability of the composition was evaluated. As a result, it was confirmed that the composition (PLC-7) started to crystallize in only 5 minutes and the liquid crystal phase was not a sufficiently stable composition.
<重合体フィルム(F7)の評価>
組成物(PLC−7)の安定性評価と同様に、支持基板としてケン化処理したTACフィルムを、予めフィルムの表面をレーヨン布によりラビング処理して用いた。組成物(PLC−7)を、バーコーターを用いてTACフィルム上に塗布した後、70℃に設定したオーブン中で5分間熱処理することにより、溶媒を除去して液晶層を配向させた。生成した塗膜に、超高圧水銀灯(250W)を用いての紫外線(30mW/cm2;365nm
)を窒素雰囲気下、25℃で30秒間照射した。これにより重合体フィルム(F7)が得られた。目視による観察では、重合体フィルム(F7)の配向はハイブリッド配向であった。また、偏光解析装置による測定結果からもハイブリッド配向であることを確認した。
<Evaluation of polymer film (F7)>
Similar to the stability evaluation of the composition (PLC-7), a TAC film subjected to saponification treatment as a supporting substrate was used by rubbing the surface of the film with a rayon cloth in advance. The composition (PLC-7) was applied onto a TAC film using a bar coater and then heat-treated in an oven set at 70 ° C. for 5 minutes to remove the solvent and align the liquid crystal layer. Ultraviolet light (30 mW / cm 2 ; 365 nm) using an ultrahigh pressure mercury lamp (250 W) is applied to the formed coating film.
) In a nitrogen atmosphere at 25 ° C. for 30 seconds. As a result, a polymer film (F7) was obtained. By visual observation, the orientation of the polymer film (F7) was a hybrid orientation. Moreover, it was confirmed from the measurement result by the ellipsometer that it was a hybrid orientation.
Claims (18)
Y1は独立に−O−または−O−CO−O−であり;
W1は独立に水素またはフッ素であり、W2は水素またはメチルであり;
R1およびR2は独立に水素またはメチルであり;
P1、P2、P3およびP4は独立に下記式(A1)〜(A8)のいずれかで表される重合性基であり;
k1、k2、q1およびq2は独立に0〜1の整数であり;
m1、m2、j1およびj2は独立に1〜10の整数であり;
式(2−1)において、
R3およびR4は独立に水素または炭素数1〜10のアルキルであり;
P5は下記式(A1)〜(A8)のいずれかで表される重合性基であり;
q3は0〜1の整数であり;j3は1〜10の整数であり;
式(3−1)、式(3−2)および式(3−3)において、
X1、X2およびX3は、それぞれ独立に単結合、−(CH2)2−または−HC=CH−で
あり;
W3、W4およびW5は、それぞれ独立に水素またはフッ素であり;
P6、P7、P8、P9、P10およびP11は独立に下記(A1)〜(A8)のいずれかで表される重合性基であり;
k3、k4、k5、q4、q5およびq6は独立に0〜1の整数であり;
m3、m4、m5、j4、j5およびj6は独立に1〜10の整数である。]
Y 1 is independently —O— or —O—CO—O—;
W 1 is independently hydrogen or fluorine, W 2 is hydrogen or methyl;
R 1 and R 2 are independently hydrogen or methyl;
P 1 , P 2 , P 3 and P 4 are each independently a polymerizable group represented by any of the following formulas (A1) to (A8);
k 1 , k 2 , q 1 and q 2 are independently integers from 0 to 1 ;
m 1 , m 2 , j 1 and j 2 are each independently an integer from 1 to 10;
In formula (2-1),
R 3 and R 4 are independently hydrogen or alkyl having 1 to 10 carbons;
P 5 is a polymerizable group represented by any of the following formulas (A1) to (A8);
q 3 is an integer from 0 to 1; j 3 is an integer from 1 to 10;
In formula (3-1), formula (3-2) and formula (3-3),
X 1 , X 2 and X 3 are each independently a single bond, — (CH 2 ) 2 — or —HC═CH—;
W 3 , W 4 and W 5 are each independently hydrogen or fluorine;
P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are each independently a polymerizable group represented by any one of (A1) to (A8) below;
k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are each independently an integer from 0 to 1;
m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 1 to 10. ]
式(1−1)および式(1−2)において、Y1が独立に−O−または−O−CO−O
−であり;W1が独立に水素であり;W2が水素またはメチルであり;R1およびR2が独立に水素またはメチルであり;P1、P2、P3およびP4が式(A1)で表される重合性基であり;k1、k2、q1およびq2が1であり;m1、m2、j1およびj2が独立に2〜8の整数であり;
式(2−1)において、R3およびR4が独立に水素または炭素数1〜8のアルキルであり;P5が式(A1)で表される重合性基であり;q3が1であり;j3が2〜8の整数で
あり;
式(3−1)、式(3−2)および式(3−3)において、X1、X2およびX3が、そ
れぞれ独立に単結合、−(CH2)2−または−HC=CH−であり;W3、W4およびW5
が、それぞれ独立に水素またはフッ素であり;P6、P7、P8、P9、P10およびP11が式(A1)で表される重合性基であり;k3、k4、k5、q4、q5およびq6が1であり;m3、m4、m5、j4、j5およびj6が独立に2〜8の整数であること
を特徴とする請求項1に記載の重合性液晶組成物。 The content ratio of the first component is in the range of 20 to 40% by weight, the content ratio of the second component is in the range of 30 to 50% by weight, and the content ratio of the third component is in the range of 20 to 40% by weight. (However, in the polymerizable liquid crystal composition, the total amount of the first component, the second component, and the third component is 100% by weight.);
In Formula (1-1) and Formula (1-2), Y 1 is independently —O— or —O—CO—O.
W 1 is independently hydrogen; W 2 is hydrogen or methyl; R 1 and R 2 are independently hydrogen or methyl; and P 1 , P 2 , P 3 and P 4 are of the formula ( A polymerizable group represented by A1); k 1 , k 2 , q 1 and q 2 are 1; m 1 , m 2 , j 1 and j 2 are each independently an integer of 2 to 8;
In the formula (2-1), R 3 and R 4 is hydrogen or alkyl of 1 to 8 carbon atoms independently; with q 3 is 1; P 5 is located at the polymerizable group represented by the formula (A1) Yes; j 3 is an integer from 2 to 8;
In Formula (3-1), Formula (3-2), and Formula (3-3), X 1 , X 2, and X 3 are each independently a single bond, — (CH 2 ) 2 — or —HC═CH -; W 3 , W 4 and W 5
Are each independently hydrogen or fluorine; P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are polymerizable groups represented by formula (A1); k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are 1; and m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 2-8. The polymerizable liquid crystal composition described in 1.
第1成分の含有割合が25〜35重量%の範囲であり、第2成分の含有割合が35〜45重量%の範囲であり、第3成分の含有割合が25〜35重量%の範囲であり(ただし、重合性液晶組成物において、第1成分、第2成分および第3成分の合計量を100重量%とした場合。);
式(1−1)において、W1が水素であり;R1およびR2が独立に水素またはメチルで
あり;P1およびP2が式(A1)で表される重合性基であり;k1およびq1が1であり;m1およびj1が独立に2〜6の整数であり;
式(2−1)において、R3およびR4が独立に水素または炭素数2〜6のアルキルであり;P5が式(A1)で表される重合性基であり;q3が1であり;j3が2〜6の整数で
あり;
式(3−1)、式(3−2)および式(3−3)において、X1が独立に単結合、−(
CH2)2−または−HC=CH−であり;X2およびX3が、それぞれ独立に単結合または
−(CH2)2−であり;W3、W4およびW5が、それぞれ独立に水素であり;P6、P7、
P8、P9、P10およびP11が式(A1)で表される重合性基であり;k3、k4、k5、q4、q5およびq6が1であり;m3、m4、m5、j4、j5およびj6が独立に4〜6の整数であること
を特徴とする請求項1に記載の重合性液晶組成物。 The first component is at least one compound selected from the group of compounds represented by formula (1-1);
The content ratio of the first component is in the range of 25 to 35% by weight, the content ratio of the second component is in the range of 35 to 45% by weight, and the content ratio of the third component is in the range of 25 to 35% by weight. (However, in the polymerizable liquid crystal composition, the total amount of the first component, the second component, and the third component is 100% by weight.);
In formula (1-1), W 1 is hydrogen; R 1 and R 2 are independently hydrogen or methyl; P 1 and P 2 are a polymerizable group represented by formula (A1); k 1 and q 1 are 1; m 1 and j 1 are independently integers of 2 to 6;
In the formula (2-1), R 3 and R 4 is hydrogen or alkyl of 2 to 6 carbon atoms independently; with q 3 is 1; P 5 is located at the polymerizable group represented by the formula (A1) Yes; j 3 is an integer from 2 to 6;
In Formula (3-1), Formula (3-2), and Formula (3-3), X 1 is independently a single bond,-(
CH 2 ) 2 — or —HC═CH—; X 2 and X 3 are each independently a single bond or — (CH 2 ) 2 —; W 3 , W 4 and W 5 are each independently Hydrogen; P 6 , P 7 ,
P 8 , P 9 , P 10 and P 11 are polymerizable groups represented by the formula (A1); k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are 1; m 3 M 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 4 to 6, wherein the polymerizable liquid crystal composition according to claim 1 is characterized.
第1成分の含有割合が20〜40重量%の範囲であり、第2成分の含有割合が30〜50重量%の範囲であり、第3成分の含有割合が20〜40重量%の範囲であり(ただし、重合性液晶組成物において、第1成分、第2成分および第3成分の合計量を100重量%とした場合。);
式(1−2)において、Y1が独立に−O−または−O−CO−O−であり;W2が水素またはメチルであり;P3およびP4が式(A1)で表される重合性基であり;k2および
q2が1であり;m2およびj2が独立に2〜8の整数であり;
式(2−1)において、R3およびR4が独立に水素または炭素数1〜8のアルキルであり;P5が式(A1)で表される重合性基であり;q3が1であり;j3が2〜8の整数で
あり;
式(3−1)、式(3−2)および式(3−3)において、X1が独立に単結合、−(
CH2)2−または−HC=CH−であり;X2およびX3が、それぞれ独立に単結合または−(CH2)2−であり;W3、W4およびW5が水素であり;P6、P7、P8、P9、P10お
よびP11が式(A1)で表される重合性基であり;k3、k4、k5、q4、q5およびq6が1であり;m3、m4、m5、j4、j5およびj6が独立に2〜8の整数であること
を特徴とする請求項1に記載の重合性液晶組成物。 The first component is at least one compound selected from the group of compounds represented by formula (1-2);
The content ratio of the first component is in the range of 20 to 40% by weight, the content ratio of the second component is in the range of 30 to 50% by weight, and the content ratio of the third component is in the range of 20 to 40% by weight. (However, in the polymerizable liquid crystal composition, the total amount of the first component, the second component, and the third component is 100% by weight.);
In formula (1-2), Y 1 is independently —O— or —O—CO—O—; W 2 is hydrogen or methyl; P 3 and P 4 are represented by formula (A1) A polymerizable group; k 2 and q 2 are 1; m 2 and j 2 are independently integers of 2 to 8;
In the formula (2-1), R 3 and R 4 is hydrogen or alkyl of 1 to 8 carbon atoms independently; with q 3 is 1; P 5 is located at the polymerizable group represented by the formula (A1) Yes; j 3 is an integer from 2 to 8;
In Formula (3-1), Formula (3-2), and Formula (3-3), X 1 is independently a single bond,-(
CH 2 ) 2 — or —HC═CH—; X 2 and X 3 are each independently a single bond or — (CH 2 ) 2 —; W 3 , W 4 and W 5 are hydrogen; P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are a polymerizable group represented by the formula (A1); k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are The polymerizable liquid crystal composition according to claim 1, wherein m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 2 to 8.
第1成分の含有割合が25〜35重量%の範囲であり、第2成分の含有割合が35〜45重量%の範囲であり、第3成分の含有割合が25〜35重量%の範囲であり(ただし、重合性液晶組成物において、第1成分、第2成分および第3成分の合計量を100重量%とした場合。);
式(1−2)において、Y1が独立に−O−または−O−CO−O−であり;W2がメチルであり;P1、P2、P3およびP4が式(A1)で表される重合性基であり;k2および
q2が1であり;m2およびj2が独立に2〜6の整数であり;
式(2−1)において、R3およびR4が独立に水素または炭素数2〜6のアルキルであり;P5が式(A1)で表される重合性の基であり;q3が1であり;j3が2〜6の整数
であり;
式(3−1)、式(3−2)および式(3−3)において、X1が独立に単結合、−(
CH2)2−または−HC=CH−であり;X2およびX3が、それぞれ独立に単結合または−(CH2)2−であり;W3、W4およびW5が水素であり;P6、P7、P8、P9、P10お
よびP11が式(A1)で表される重合性基であり;k3、k4、k5、q4、q5およびq6が1であり;m3、m4、m5、j4、j5およびj6が独立に4〜6の整数であること
を特徴とする請求項1に記載の重合性液晶組成物。 The first component is at least one compound selected from the group of compounds represented by formula (1-2);
The content ratio of the first component is in the range of 25 to 35% by weight, the content ratio of the second component is in the range of 35 to 45% by weight, and the content ratio of the third component is in the range of 25 to 35% by weight. (However, in the polymerizable liquid crystal composition, the total amount of the first component, the second component, and the third component is 100% by weight.);
In formula (1-2), Y 1 is independently —O— or —O—CO—O—; W 2 is methyl; P 1 , P 2 , P 3 and P 4 are represented by formula (A1) And k 2 and q 2 are 1; m 2 and j 2 are each independently an integer of 2 to 6;
In Formula (2-1), R 3 and R 4 are independently hydrogen or alkyl having 2 to 6 carbon atoms; P 5 is a polymerizable group represented by Formula (A1); q 3 is 1 J 3 is an integer from 2 to 6;
In Formula (3-1), Formula (3-2), and Formula (3-3), X 1 is independently a single bond,-(
CH 2 ) 2 — or —HC═CH—; X 2 and X 3 are each independently a single bond or — (CH 2 ) 2 —; W 3 , W 4 and W 5 are hydrogen; P 6 , P 7 , P 8 , P 9 , P 10 and P 11 are a polymerizable group represented by the formula (A1); k 3 , k 4 , k 5 , q 4 , q 5 and q 6 are 2. The polymerizable liquid crystal composition according to claim 1, wherein m 3 , m 4 , m 5 , j 4 , j 5 and j 6 are each independently an integer of 4-6.