JP2008105348A - Heat-sensitive recording medium - Google Patents
Heat-sensitive recording medium Download PDFInfo
- Publication number
- JP2008105348A JP2008105348A JP2006292706A JP2006292706A JP2008105348A JP 2008105348 A JP2008105348 A JP 2008105348A JP 2006292706 A JP2006292706 A JP 2006292706A JP 2006292706 A JP2006292706 A JP 2006292706A JP 2008105348 A JP2008105348 A JP 2008105348A
- Authority
- JP
- Japan
- Prior art keywords
- undercoat layer
- heat
- layer
- sensitive recording
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、ロイコ染料と呈色剤との発色反応を利用した感熱記録体に関する。 The present invention relates to a heat-sensitive recording material utilizing a color development reaction between a leuco dye and a colorant.
ロイコ染料と呈色剤との発色反応を利用し、熱により記録像を得るようにした感熱記録体はよく知られている。このような感熱記録体は比較的安価であり、また記録機器がコンパクトで且つその保守も容易なため、ファクシミリや各種計算機等のアウトプット、科学計測機器のプリンター等の記録媒体としてだけでなくＰＯＳラベル、ＡＴＭ、ＣＡＤ、ハンディーターミナル、各種チケット用紙等の各種プリンターの記録媒体として広範囲に使用されている。 A heat-sensitive recording material that utilizes a color reaction between a leuco dye and a color former to obtain a recorded image by heat is well known. Such a thermal recording medium is relatively inexpensive, and the recording device is compact and easy to maintain. Therefore, it is not only used as a recording medium for output of facsimiles and various computers, printers of scientific measuring devices, etc. It is widely used as a recording medium for various printers such as labels, ATMs, CAD, handy terminals, and various ticket sheets.
感熱記録体の記録感度や画質を向上させるために、支持体と感熱記録層との間に顔料とバインダーを含有する下塗層を設け、空隙を形成して多孔性、或いは嵩高にし、断熱性を付与することが知られている。例えば、均一で安定な下塗層構造を得るために、特定粘度の下塗層用塗液をブレード塗工することが記載されている（特許文献１を参照）。また、感熱紙を高画質化するために下塗層の厚さの変動を一定範囲内にすることが記載されている（特許文献２を参照）。更に、表面の静摩擦係数を低くするために、ブレード塗工によって２層以上の下塗層を形成することが記載されている（特許文献３を参照）。
しかし、近年、印字の高速化はますます進み、感熱記録体の高感度高画質化の要求もますます高まってきており、高平滑化した原紙を使用したり、単に下塗層を設けるだけでは十分な品質は得られなくなってきている。
下塗層を設ける方法としては、下塗層は通常塗布量が多いほど断熱効果を発揮し記録感度を向上させるが、高塗布量になるほど均一な塗工層が得られ難くなり、その後に形成する感熱記録層、保護層が均一な層とすることが難しくなるために、その結果として、記録感度や画質の低下を引き起こしたり、保護層バリア性能の低下を招くことになる。
また、成熟市場に移行しつつある感熱記録体市場においては、製造コストは重要な問題となってきており、生産性の低い塗工方式や塗工欠陥の発生し易い塗工方式は、例え高品質な製品が得られる場合でも、実際に製造することは困難な状況になる。
In order to improve the recording sensitivity and image quality of the thermosensitive recording medium, an undercoat layer containing a pigment and a binder is provided between the support and the thermosensitive recording layer, and a void is formed to make it porous or bulky. It is known to give For example, in order to obtain a uniform and stable undercoat layer structure, it is described that an undercoat layer coating solution having a specific viscosity is applied by blades (see Patent Document 1). Further, it is described that the variation of the thickness of the undercoat layer is within a certain range in order to improve the image quality of the thermal paper (see Patent Document 2). Furthermore, in order to lower the static friction coefficient of the surface, it is described that two or more undercoat layers are formed by blade coating (see Patent Document 3).
However, in recent years, the printing speed has been further increased, and the demand for high sensitivity and high image quality of thermal recording media has been increasing. By simply using a highly smoothed base paper or simply providing an undercoat layer, Sufficient quality cannot be obtained.
As a method of providing an undercoat layer, the undercoat layer usually exhibits a heat insulation effect and improves the recording sensitivity as the coating amount increases. However, it becomes difficult to obtain a uniform coating layer as the coating amount increases. As a result, it is difficult to make the heat-sensitive recording layer and the protective layer uniform. As a result, the recording sensitivity and the image quality are lowered, and the protective layer barrier performance is lowered.
In addition, in the thermal recording material market, which is shifting to a mature market, manufacturing costs have become an important issue, and low-productivity coating methods and coating methods that tend to cause coating defects are high. Even when a quality product is obtained, it is difficult to actually manufacture the product.
また、感熱記録体の支持体に関しては、一般的な上質紙以外にも合成紙、フィルム、プラスチック等が知られているが、近年資源保護の観点から紙類においても古紙を回収し、これを原料として使用することが求められているが、感熱記録体に古紙パルプを含有する支持体を用いると、発色能が低下したり、発色画像の保存安定性に問題を生じたり、地肌カブリの問題が生じたりする。上記の問題点を改良するために、感熱記録層中に特定の染料や呈色剤を含有する感熱記録体（特許文献４、５、６参照）が開示されている。また、古紙パルプを含有する支持体と感熱記録層との間に、特定の粘度を有した塗布液を特定の塗布方式を使用して形成したアンダーコート層を設けることにより、白抜けのない、ベタ黒発色均一性に優れた感熱記録体（特許文献７参照）が開示されている。しかし、更なる改良が要望されているのが現状である。 In addition to general high-quality paper, synthetic paper, film, plastic, and the like are known as the support for the thermal recording medium. However, in recent years, waste paper has been recovered from paper to protect resources. Although it is required to be used as a raw material, if a support containing waste paper pulp is used for the thermal recording material, the color developing ability is lowered, the storage stability of the color image is caused, or the background fogging is a problem. May occur. In order to improve the above problems, thermal recording materials (see Patent Documents 4, 5, and 6) containing specific dyes and colorants in the thermal recording layer are disclosed. In addition, by providing an undercoat layer formed by using a specific coating method, a coating liquid having a specific viscosity between the support containing the used paper pulp and the heat-sensitive recording layer, there is no white spot, A thermal recording material excellent in solid black color uniformity (see Patent Document 7) is disclosed. However, the current situation is that further improvements are desired.
このような事情に鑑み本発明は、古紙パルプを含有する紙支持体を用いても、地肌部の耐地肌カブリ性や記録部の保存性に優れ、記録感度が高く、低エネルギーで印字されても良好な画質が得られ、更に塗工欠陥の少ない感熱記録体を提供することにある。 In view of such circumstances, the present invention is excellent in the background fog resistance of the background portion and the storage stability of the recording portion, and has high recording sensitivity and is printed with low energy even when using a paper support containing waste paper pulp. Is to provide a heat-sensitive recording material having good image quality and less coating defects.
本発明者は上記課題を解決するために鋭意検討の結果、古紙パルプを含有する紙支持体を用いて、下塗層を２層以上の多層構造とし、なおかつ特定の塗工方式を用いて下塗層を形成することにより、課題を解決できることを見出し、更に鋭意検討を重ねて本発明を完成するに至った。 As a result of intensive studies to solve the above-mentioned problems, the present inventor made a paper support containing waste paper pulp, made the undercoat layer into a multilayer structure of two or more layers, and applied a specific coating method. It has been found that the problem can be solved by forming a coating layer, and the present invention has been completed through further intensive studies.
即ち、本発明は、以下の感熱記録体を提供するものである。 That is, the present invention provides the following thermal recording material.
項１：（Ｉ）紙支持体、
（ＩＩ）該紙支持体上に形成された下塗り層、及び
（ＩＩＩ）該下塗り層上に形成された感熱記録層
を備えた感熱記録体であって、
ａ）紙支持体が、古紙パルプを含有しており、
ｂ）前記下塗り層が、少なくとも第一下塗り層及び該第一下塗り層上に形成された第二下塗り層からなる多層構造を有しており、
ｃ）第一下塗り層をブレード塗工方式で形成し、さらに二層目以降の下塗り層をロッド塗工方式で形成したことを特徴とする
感熱記録体。
項２：前記感熱記録層の厚さの標準偏差が０．３０以下である、請求項１記載の感熱記録体。
項３：前記第一下塗り層と第二下塗り層とが同一の下塗り層用塗液を塗布、乾燥したものである、請求項１または２に記載の感熱記録体。
項４：前記第一下塗り層と第二下塗り層との乾燥後の塗工量の割合が２：８〜８：２である、請求項１から３のいずれか一項に記載の感熱記録体。
項５：前記第一下塗り層及び第二下塗り層の乾燥後の合計塗工量が５〜３５ｇ／ｍ２である、請求項１から４のいずれか一項に記載の感熱記録体。
項６：下塗層用塗液の、ハーキュレス粘度計の８８００ｒｐｍにおける粘度が２５〜４０ｍＰａ・ｓであり、ＢＬ粘度計の６０ｒｐｍにおける粘度が７００〜２０００ｍＰａ・ｓである、請求項３に記載の感熱記録体。
項７：前記第一下塗り層を形成させた後、第一下塗り層形成紙支持体を巻き取らずに、第二下塗り層を形成させることにより得られる、請求項１から６のいずれか一項に記載の感熱記録体。
項８：前記感熱記録層上に更に保護層が形成されている、請求項１から７のいずれか一項に記載の感熱記録体。
項９：前記保護層の厚さが０．４〜２．５μｍである、請求項８に記載の感熱記録体。
項１０：紙支持体上に下塗り層、感熱記録層を順次形成してなる感熱記録体の製造方法であって、
前記紙支持体が古紙パルプを含有しており、
前記紙支持体上にブレード塗工方式で塗布及び乾燥することにより、第一下塗り層を形成する第１工程、及び、
前記第一下塗り層上にロッド塗工方式で塗布及び乾燥することにより、第二下塗り層を形成する第２工程、
を備えた、製造方法。
項１１：前記第１工程の後、第一下塗り層形成紙支持体を巻き取らずに、第２工程を行う、請求項１０に記載の製造方法。
Item 1: (I) a paper support,
(II) a thermal recording medium comprising an undercoat layer formed on the paper support, and (III) a thermal recording layer formed on the undercoat layer,
a) the paper support contains waste paper pulp;
b) The undercoat layer has a multilayer structure comprising at least a first undercoat layer and a second undercoat layer formed on the first undercoat layer,
c) A heat-sensitive recording material, wherein the first undercoat layer is formed by a blade coating method, and the second and subsequent undercoat layers are formed by a rod coating method.
Item 2: The heat-sensitive recording material according to claim 1, wherein the standard deviation of the thickness of the heat-sensitive recording layer is 0.30 or less.
Item 3: The heat-sensitive recording material according to claim 1 or 2, wherein the first undercoat layer and the second undercoat layer are obtained by applying and drying the same undercoat layer coating solution.
Item 4: The thermal recording according to any one of claims 1 to 3, wherein a ratio of a coating amount after drying of the first undercoat layer and the second undercoat layer is 2: 8 to 8: 2. body.
Claim 5: The total coating amount after drying of the first subbing layer and second subbing layer is 5~35g / m 2, heat-sensitive recording material according to any one of claims 1 to 4.
Item 6: The thermosensitive composition according to claim 3, wherein the coating liquid for the undercoat layer has a viscosity of 25 to 40 mPa · s at 8800 rpm in a Hercules viscometer and a viscosity of 700 to 2000 mPa · s in 60 rpm of a BL viscometer. Recorded body.
Item 7: The method according to any one of claims 1 to 6, which is obtained by forming the first undercoat layer and then forming the second undercoat layer without winding up the first undercoat layer-forming paper support. The thermosensitive recording material according to one item.
Item 8: The heat-sensitive recording material according to any one of claims 1 to 7, wherein a protective layer is further formed on the heat-sensitive recording layer.
Item 9: The heat-sensitive recording material according to item 8, wherein the protective layer has a thickness of 0.4 to 2.5 µm.
Item 10: A method for producing a thermal recording body, wherein an undercoat layer and a thermal recording layer are sequentially formed on a paper support,
The paper support contains waste paper pulp;
A first step of forming a first undercoat layer by applying and drying on the paper support by a blade coating method; and
A second step of forming a second undercoat layer by applying and drying on the first undercoat layer by a rod coating method;
A manufacturing method comprising:
Item 11: The method according to claim 10, wherein after the first step, the second step is performed without winding up the first undercoat layer-formed paper support.
本発明の感熱記録体は、古紙パルプを含有する紙支持体を用いても、地肌部の耐熱地肌カブリ性や記録部の保存性に優れ、記録感度が高く、低エネルギーで印字されても良好な画質が得られ、更に塗工欠陥の少ない感熱記録体を提供するものである。 The heat-sensitive recording material of the present invention is excellent in heat-resistant background fogging of the background portion and storage stability of the recording portion even when a paper support containing waste paper pulp is used, and has high recording sensitivity and may be printed with low energy. It is intended to provide a heat-sensitive recording material which can obtain a high image quality and has few coating defects.
以下、本発明について、更に詳細に説明する。 Hereinafter, the present invention will be described in more detail.
本発明の感熱記録体には、
紙支持体上に、下塗り層、ロイコ染料と呈色剤を含有する感熱記録層を順次積層してなる感熱記録体において、該紙支持体が古紙パルプを含有し、且つ下塗り層を２層以上形成し、その第一下塗り層をブレード塗工方式で形成し、更にニ層目以降の下塗り層をロッド塗工方式で形成した感熱記録体が含まれる。
In the thermal recording material of the present invention,
In a heat-sensitive recording material comprising a paper support and an undercoat layer, and a heat-sensitive recording layer containing a leuco dye and a colorant, which are sequentially laminated, the paper support contains waste paper pulp, and two or more undercoat layers are provided. And a thermal recording medium in which the first undercoat layer is formed by a blade coating method and the second and subsequent undercoat layers are formed by a rod coating method.
紙支持体
紙支持体中の古紙パルプの含有比率としては、紙支持体に対して２０〜９５質量％程度が好ましい。古紙の含有比率が２０〜９５質量％の範囲であれば、記録後の耐巻癖カール性（巻癖カール性が少ない)や引裂強さの低下（感熱記録体を紙幅４０〜７０ｍｍ程度の小巻取状に加工し難い）が実用上、問題なく、より好ましくは４０〜８０質量％程度である。
Paper Support The content ratio of waste paper pulp in the paper support is preferably about 20 to 95% by mass with respect to the paper support. When the content ratio of the used paper is in the range of 20 to 95% by mass, the curling resistance against curling (less curling curling) after recording and the reduction in tearing strength (the thermal recording medium has a small paper width of about 40 to 70 mm). However, it is practically no problem and more preferably about 40 to 80% by mass.
古紙パルプの原料としては、例えば雑誌、チラシ、新聞紙、ノーカーボン紙、複写紙等の印刷された古紙を主体とし、更に紙製造中に発生する上質紙、コート紙等の損紙が含まれていてもよい。 The raw material for waste paper pulp is mainly printed waste paper such as magazines, flyers, newspapers, carbonless paper, and copy paper, and also includes damaged paper such as high-quality paper and coated paper generated during paper manufacture. May be.
古紙パルプは、一般には古紙、及び損紙を低濃度パルパーまたは高濃度パルパーによる離解工程、スクリーンまたはクリーナーによる粗選工程と精選工程、浮選法または水洗法による脱墨工程、塩素漂白、二酸化塩素漂白、次亜塩素酸ソーダ漂白、酸素漂白等による漂白工程等を適宜、組み合わせることにより得られる。 Waste paper pulp generally consists of waste paper and waste paper, a disaggregation process using a low-concentration pulper or a high-concentration pulper, a rough and selective process using a screen or a cleaner, a deinking process using a flotation method or a water washing method, chlorine bleaching, chlorine dioxide It can be obtained by appropriately combining bleaching steps such as bleaching, sodium hypochlorite bleaching and oxygen bleaching.
紙支持体は、古紙パルプ、及び必要により木材パルプを主体として非木材パルプ、合成パルプ、無機繊維等の抄紙用パルプ繊維が用いられ、例えば叩解度がカナディアン・スタンダード・フリーネス（以下ＣＦＳとする）で１５０〜５００ｍｌ程度のパルプスラリーを抄紙することにより得られる。 The paper support is made of waste paper pulp and, if necessary, wood pulp, mainly non-wood pulp, synthetic pulp, inorganic fiber, etc., and for example, the beating degree is Canadian Standard Freeness (hereinafter referred to as CFS). Is obtained by papermaking about 150 to 500 ml of pulp slurry.
更に、紙支持体中には、タルク、カオリン、クレー、焼成カオリン、軽質（重質）炭酸カルシウム、水酸化アルミニウム、酸化チタン、珪酸マグネシウム、硫酸マグネシウム、アルミノ珪酸塩、シリカ、ベントナイト等の無機系填料やポリスチレン樹脂微粒子、尿素ホルマリン樹脂微粒子、及び熱膨張性微小中空粒子やその他有機填料が適宜含有される。 Furthermore, in the paper support, inorganic materials such as talc, kaolin, clay, calcined kaolin, light (heavy) calcium carbonate, aluminum hydroxide, titanium oxide, magnesium silicate, magnesium sulfate, aluminosilicate, silica, bentonite, etc. Fillers, polystyrene resin fine particles, urea formalin resin fine particles, thermally expandable fine hollow particles, and other organic fillers are appropriately contained.
パルプスラリー中には、ロジン系、石油樹脂系、アルキルケテンダイマー系、アルケニル無水コハク酸系及び無水ステアリン酸系等のサイズ剤、アニオン系、カチオン系、ノニオン系、または両性のポリアクリルアミド重合体、ポリエチレンイミン及びその誘導体、ポリアミン、ポリアミド・ポリアミン及びその誘導体、ポリエチレンオキサイド、植物ガム、ポリビニルアルコール、カチオン系ラテックス、カチオン系尿素ホルマリン樹脂、メラミンホルマリン樹脂、ポリアミド樹脂等の有機系化合物、更に染料、ｐＨ調整剤、ピッチコントロール剤、消泡剤等を必要に応じて適宜添加することができる。 In the pulp slurry, sizing agents such as rosin, petroleum resin, alkyl ketene dimer, alkenyl succinic anhydride and stearic anhydride, anionic, cationic, nonionic or amphoteric polyacrylamide polymer, Polyethyleneimine and derivatives thereof, polyamine, polyamide / polyamine and derivatives thereof, polyethylene oxide, plant gum, polyvinyl alcohol, cationic latex, cationic urea formalin resin, melamine formalin resin, polyamide resin and other organic compounds, further dyes, pH A regulator, a pitch control agent, an antifoaming agent, etc. can be added suitably as needed.
抄紙方法は、酸性抄紙または中性抄紙により、長網、円網、各種のツインワイヤー等通常の抄紙機で抄紙される。乾燥工程にはシリンダードライヤー、ヤンキードライヤー、エアドライヤー等の方法が使用できる。また、その表面上にサイズプレス等の方法で、表面サイズ剤、表面紙力剤、帯電防止剤、染料等を適宜塗布したものであってもよく、またキャレンダー掛けにより表面の平滑度を上げてから支持体として使用してもよい。 Paper making is carried out by an ordinary paper machine such as a long net, a circular net, and various twin wires by an acid paper or a neutral paper. For the drying process, methods such as a cylinder dryer, a Yankee dryer, and an air dryer can be used. In addition, a surface sizing agent, surface paper strength agent, antistatic agent, dye or the like may be appropriately applied on the surface by a method such as a size press, and the surface smoothness is increased by calendaring. After that, it may be used as a support.
下塗層
下塗り層は、少なくとも２層からなる。下塗り層の層数は、２層以上であれば特に限定されないが、上限は４層程度とすればよい。特に好ましい層数は２層である。
Undercoat layer The undercoat layer comprises at least two layers. The number of undercoat layers is not particularly limited as long as it is 2 or more, but the upper limit may be about 4 layers. A particularly preferred number of layers is two.
下塗り層を２層以上の多層構造とし、第一下塗り層をブレード塗工方式で形成し、さらに二層目以降の下塗り層をロッド塗工方式で形成することで、古紙パルプを含有した紙支持体であっても、発色能が低下したり、発色画像の保存安定性に問題を生じたり、地肌カブリの問題が生じたりすることが少なく、実用上、問題ないレベルである。また、感熱記録層及び保護層の浸透ムラが大幅に軽減できる。これにより、感熱記録層に含有される発色成分が、印字の際に表層から受ける印字エネルギーを有効に活用できるようになるため、高感度とすることができる。一方、保護層についても浸透ムラが少なくなり、感熱記録層表層を保護する有効成分が増加するため、バリア性を向上できる。 Paper containing waste paper pulp by forming the undercoat layer into a multilayer structure of two or more layers, forming the first undercoat layer by a blade coating method, and further forming the second and subsequent undercoat layers by a rod coating method Even if it is a support body, it is a level which is practically satisfactory, since it is less likely to cause a decrease in coloring ability, a problem in storage stability of a color image, and a problem of background fogging. Further, the uneven penetration of the heat-sensitive recording layer and the protective layer can be greatly reduced. As a result, the coloring component contained in the heat-sensitive recording layer can effectively utilize the printing energy received from the surface layer during printing, so that high sensitivity can be achieved. On the other hand, the permeation unevenness of the protective layer is reduced and the effective component for protecting the surface layer of the heat-sensitive recording layer is increased, so that the barrier property can be improved.
一般的に、下塗り層の塗工方法は、メイヤーバー塗工方式、エアナイフ塗工方式、ブレード塗工方式、ロッド塗工方式などがある。本発明において、メイヤーバー塗工方式とは、塗料を一般的にはロール方式で紙にアプリケートした後、細いワイヤーを金属の円柱に巻き付けた棒（バー）を押し付けて塗料を掻き落とすことにより、塗工量を制御するという方式である。エアナイフ塗工方式とは、塗料を一般的にはロール方式で紙に紙にアプリケートした塗料を、薄いスリットから塗出される高圧の空気を用いて、空気圧で掻き落とすことにより塗工量を制御するという方式である。これらは、高速塗工に適していないことから、生産性が低下するという欠点がある。 In general, the coating method of the undercoat layer includes a Mayer bar coating method, an air knife coating method, a blade coating method, a rod coating method, and the like. In the present invention, the Mayer bar coating method is a method in which a paint is applied to paper by a roll method, and then a stick (bar) in which a thin wire is wound around a metal cylinder is pressed to scrape the paint. In this method, the coating amount is controlled. The air knife coating method is a method of controlling the coating amount by scraping the coating material applied to paper on paper by a roll method with air pressure using high-pressure air that is applied from a thin slit. It is a method to do. Since these are not suitable for high-speed coating, there is a drawback that productivity is lowered.
ブレード塗工とは、塗料をロールやファウンテン方式で紙にアプリケートした後、ベベルタイプやベントタイプに代表される厚さ数ミリの薄い鋼板を押し付けて塗料を掻き落とすことにより、塗工量を制御する方式である。ブレード塗工方式は表面平滑の高い均一な塗工面を形成できる反面、ストリークやスクラッチ等の塗工欠陥が発生しやすいという欠点がある。 With blade coating, paint is applied to paper by the roll or fountain method, and then a thin steel plate with a thickness of several millimeters typified by the bevel type and vent type is pressed to scrape the paint. This is a control method. The blade coating method can form a uniform coated surface with high surface smoothness, but has a drawback that coating defects such as streaks and scratches are likely to occur.
一方、ロッド塗工方式は薄い鋼板の代わりに、金属の円柱を回転させながら押し付けることにより、塗布した塗料を掻き落として塗工量を制御する方式である。塗工欠陥は比較的少ないが、特に原紙等の平滑性が低い塗工面に塗工すると均一な塗工面は得難いという欠点がある。なお、本発明においては、ロッド塗工方式とメイヤーバー塗工方式とは明確に区別されるものであり、本発明のロッド塗工方式にメイヤーバー塗工方式は含まれない。 On the other hand, the rod coating method is a method of controlling the coating amount by scraping off the applied paint by pressing while rotating a metal cylinder instead of a thin steel plate. Although there are relatively few coating defects, there is a drawback that it is difficult to obtain a uniform coated surface especially when coated on a coated surface with low smoothness such as a base paper. In the present invention, the rod coating method and the Mayer bar coating method are clearly distinguished, and the Mayer bar coating method is not included in the rod coating method of the present invention.
これらに対し、本発明の感熱記録体は第一下塗り層をブレード塗工方式で形成することにより、均一で平滑性の高い塗工面が形成され、その上にロッド塗工方式でさらに下塗り層を形成することにより、塗工欠陥の少ない均一で平滑性の高い下塗り層を形成することが可能となり、これらの塗工方式の相互作用により、上記欠点を克服し、高感度及び高画質を達成できる。 On the other hand, in the heat-sensitive recording material of the present invention, a uniform and highly smooth coated surface is formed by forming the first undercoat layer by a blade coating method, and further an undercoat layer is formed thereon by a rod coating method. This makes it possible to form a uniform and highly smooth undercoat layer with few coating defects. Overcoming the above-mentioned drawbacks and achieving high sensitivity and high image quality through the interaction of these coating methods. it can.
本発明では、下塗り層を構成する複数の層のうち第一下塗り層及び第二下塗り層の少なくとも２層は、同一下塗り層用塗液を塗布、乾燥したものであってもよく、また、異なる下塗り層用塗液を塗布、乾燥したものでもよいが、本発明では、同一下塗り層用塗液を塗布、乾燥したもののほうが好ましい。同一の下塗り層用塗液とすることにより、塗料調製を一括化することが可能となり、塗料歩留まりを向上させ、製造コストを抑制することができる。 In the present invention, among the plurality of layers constituting the undercoat layer, at least two layers of the first undercoat layer and the second undercoat layer may be coated with the same undercoat layer coating solution and dried, Different undercoat layer coating solutions may be applied and dried, but in the present invention, the same undercoat layer coating solution is preferably applied and dried. By using the same coating solution for the undercoat layer, it is possible to integrate the preparation of paints, improve the paint yield, and suppress the manufacturing cost.
下塗り層は、通常、i)吸油量が７０ｍｌ／１００ｇ以上、特に８０〜１５０ｍｌ／１００ｇ程度の吸油性顔料、ii)有機中空粒子、及びiii)熱膨張性粒子からなる群から選ばれる少なくとも１種、並びに接着剤を主成分とする下塗り層用塗液を支持体上に塗布乾燥して形成することができる。
前記吸油性顔料、有機中空粒子及び熱膨張性粒子からなる群から選ばれる少なくとも１種の顔料を用いることにより、下塗り層の空隙が増し、その上に感熱記録層等を設けた際に熱エネルギーの原紙方向への拡散を防ぎ、印字エネルギーの有効利用が可能となるため、高い発色濃度を得ることができるようになる。
ここで、上記吸油量はＪＩＳ Ｋ５１０１−１９９１の方法に従い求められる値である。
吸油性顔料としては、各種のものが使用できるが、具体例としては、焼成カオリン、シリカ、軽質炭酸カルシウム等の無機顔料が挙げられる。
吸油性顔料の平均粒子径は０．０１〜５μｍ程度、特に０．０２〜３μｍ程度であることが好ましい。ここで平均粒子径は、レーザー回折式粒度分布測定装置（商品名：ＳＡＬＤ２０００、島津製作所製）による５０％値である。
吸油性顔料の使用量は、広い範囲から選択できるが、一般に下塗り層中の顔料成分中、５０〜９５質量％程度、特に６０〜９０質量％程度であることが好ましい。
また、有機中空粒子としては、従来公知のもの、例えば、膜材がアクリル系樹脂、スチレン系樹脂、塩化ビニリデン系樹脂等からなる中空率が５０〜９９％程度の粒子が例示できる。ここで中空率は（ｄ／Ｄ）×１００で求められる値である。該式中、ｄは有機中空粒子の内径を示し、Ｄは有機中空粒子の外径を示す。
有機中空粒子の平均粒子径は０．５〜１０μｍ程度、特に０．７〜２μｍ程度であるのが好ましい。なお、この平均粒子径は上記吸油性顔料の平均粒子径と同様の測定方法で測られるものである。
有機中空粒子の使用量は、広い範囲から選択できるが、一般に下塗り層中の顔料成分中、２０〜９０質量％、特に２５〜７０質量％程度であるのが好ましい。
熱膨張性粒子としては、各種のものが使用できるが、具体例としては、低沸点炭化水素をインサイト重合法により、塩化ビニリデン、アクリロニトリルなどの共重合物でマイクロカプセル化した熱膨張性微粒子等があげられる。低沸点炭化水素としては、例えば、エタン、プロパン等が挙げられる。
熱膨張性粒子の使用量は、広い範囲から選択できるが、一般に下塗り層の顔料成分中、１〜８０質量％程度、特に１０〜７０質量％程度であることが好ましい。
吸油性無機顔料、有機中空粒子及び熱膨張性粒子から選ばれる２種以上を併用して用いる場合、合計量が下塗り層全固形分に対して、４０〜９０質量％、特に５０〜８０質量％程度であるのが好ましい。
The undercoat layer is usually at least one selected from the group consisting of i) an oil-absorbing pigment having an oil absorption of 70 ml / 100 g or more, particularly about 80 to 150 ml / 100 g, ii) organic hollow particles, and iii) thermally expandable particles. In addition, an undercoat layer coating solution containing an adhesive as a main component can be formed by coating and drying on a support.
By using at least one pigment selected from the group consisting of the oil-absorbing pigment, organic hollow particles, and thermally expandable particles, the gap in the undercoat layer is increased, and heat energy is provided when a thermal recording layer or the like is provided thereon. Therefore, it is possible to obtain a high color density because it is possible to prevent the diffusion of the ink in the direction of the base paper and to effectively use the printing energy.
Here, the oil absorption is a value determined according to the method of JIS K5101-1991.
Various oil-absorbing pigments can be used, and specific examples include inorganic pigments such as calcined kaolin, silica, and light calcium carbonate.
The average particle diameter of the oil-absorbing pigment is preferably about 0.01 to 5 μm, particularly preferably about 0.02 to 3 μm. Here, the average particle diameter is a 50% value measured by a laser diffraction particle size distribution measuring device (trade name: SALD2000, manufactured by Shimadzu Corporation).
The amount of the oil-absorbing pigment used can be selected from a wide range, but generally it is preferably about 50 to 95% by mass, particularly preferably about 60 to 90% by mass in the pigment component in the undercoat layer.
Moreover, as an organic hollow particle, a conventionally well-known thing, for example, the particle | grains whose hollow rate which a film | membrane material consists of acrylic resin, a styrene resin, vinylidene chloride resin etc. are about 50 to 99% can be illustrated. Here, the hollow ratio is a value obtained by (d / D) × 100. In the formula, d represents the inner diameter of the organic hollow particles, and D represents the outer diameter of the organic hollow particles.
The average particle diameter of the organic hollow particles is preferably about 0.5 to 10 μm, particularly preferably about 0.7 to 2 μm. In addition, this average particle diameter is measured by the same measuring method as the average particle diameter of the oil-absorbing pigment.
The amount of the organic hollow particles to be used can be selected from a wide range, but generally it is preferably about 20 to 90% by mass, particularly about 25 to 70% by mass in the pigment component in the undercoat layer.
Various types of thermally expandable particles can be used. Specific examples include thermally expandable fine particles obtained by microencapsulating low-boiling hydrocarbons with a copolymer such as vinylidene chloride and acrylonitrile by an in situ polymerization method. Can be given. Examples of the low boiling point hydrocarbon include ethane and propane.
The use amount of the heat-expandable particles can be selected from a wide range, but is generally about 1 to 80% by mass, and particularly preferably about 10 to 70% by mass in the pigment component of the undercoat layer.
When two or more kinds selected from oil-absorbing inorganic pigments, organic hollow particles and thermally expandable particles are used in combination, the total amount is 40 to 90% by mass, particularly 50 to 80% by mass, based on the total solid content of the undercoat layer. It is preferable that it is about.
下塗り層中に使用される顔料としては、上記の吸油性無機顔料、有機中空粒子及び熱膨張性粒子の他に、本発明の効果を阻害しない範囲で各種公知の塗工用顔料を使用することができ、例えば、カオリン、重質炭酸カルシウム、酸化チタン、炭酸マグネシウム、水酸化アルミニウム、合成マイカ等が挙げられる。これらは単独で使用しても、２種以上の顔料を併用することもできる。 As the pigment used in the undercoat layer, in addition to the oil-absorbing inorganic pigment, the organic hollow particles, and the heat-expandable particles, various known coating pigments may be used as long as the effects of the present invention are not impaired. Examples thereof include kaolin, heavy calcium carbonate, titanium oxide, magnesium carbonate, aluminum hydroxide, and synthetic mica. These may be used alone or in combination of two or more pigments.
下塗り層用塗液に使用される接着剤としては、例えば種々の分子量のポリビニルアルコール、変性ポリビニルアルコール、デンプン及びその誘導体、メトキシセルロース、カルボキシメチルセルロース、メチルセルロース、及びエチルセルロース等のセルロース誘導体、ポリアクリル酸ソーダ、ポリビニルピロリドン、アクリル酸アミド−アクリル酸エステル共重合体、アクリル酸アミド−アクリル酸エステル−メタクリル酸３元共重合体、スチレン−無水マレイン酸共重合体アルカリ塩、ポリアクリルアミド、アルギン酸ソーダ、ゼラチン、及びカゼインなどの水溶性高分子材料、並びにポリ酢酸ビニル、ポリウレタン、スチレン−ブタジエン共重合体、ポリアクリル酸、ポリアクリル酸エステル、塩化ビニル−酢酸ビニル共重合体、ポリブチルメタクリレート、エチレン−酢酸ビニル共重合体、及びスチレン−ブタジエン−アクリル系共重合体、シリル化ウレタン、アクリルーシリコン複合体、アクリル−シリコン−ウレタン複合体エマルジョンなどの疎水性重合体のラテックスなどが挙げられ、一種類または二種類以上を併用することも可能である。 Examples of the adhesive used in the coating solution for the undercoat layer include polyvinyl alcohols having various molecular weights, modified polyvinyl alcohols, starches and derivatives thereof, cellulose derivatives such as methoxycellulose, carboxymethylcellulose, methylcellulose, and ethylcellulose, sodium polyacrylate , Polyvinylpyrrolidone, acrylic acid amide-acrylic acid ester copolymer, acrylic acid amide-acrylic acid ester-methacrylic acid terpolymer, styrene-maleic anhydride copolymer alkali salt, polyacrylamide, sodium alginate, gelatin, And water-soluble polymer materials such as casein, polyvinyl acetate, polyurethane, styrene-butadiene copolymer, polyacrylic acid, polyacrylate ester, vinyl chloride-vinyl acetate copolymer, poly Latex of hydrophobic polymer such as til methacrylate, ethylene-vinyl acetate copolymer, styrene-butadiene-acrylic copolymer, silylated urethane, acrylic-silicon composite, acrylic-silicon-urethane composite emulsion, etc. It is also possible to use one kind or two or more kinds in combination.
下塗り層中の接着剤の含有量は、下塗り層の全固形分に対して３〜３５質量％含有することが好ましく、より好ましくは５〜３０質量％である。３質量％以上とすることにより、塗工層の強度を向上させることができる。一方、３５質量％以下とすることにより、下塗り層の目的とする空隙を多くして、記録感度を向上させることができる。 The content of the adhesive in the undercoat layer is preferably 3 to 35% by mass, more preferably 5 to 30% by mass with respect to the total solid content of the undercoat layer. By setting it as 3 mass% or more, the intensity | strength of a coating layer can be improved. On the other hand, when the content is 35% by mass or less, the target void of the undercoat layer can be increased, and the recording sensitivity can be improved.
助剤としては、例えばアルキルベンゼンスルホン酸ナトリウム、ジオクチルスルホコハク酸ナトリウム、スルホン変性ポリビニルアルコール、ポリアクリル酸ナトリウムなどの界面活性剤、グリオキザール、ホウ酸、ジアルデヒドデンプン、メチロール尿素、エポキシ系化合物、ヒドラジン系化合物などの耐水化剤（架橋剤）、ステアリン酸亜鉛、ステアリン酸カルシウム、ポリエチレンワックス、カルナバロウ、パラフィンワックス、エステルワックスなどの滑剤、紫外線吸収剤、蛍光染料、着色染料、離型剤、酸化防止剤などが挙げられる。助剤の使用量は、広い範囲から適宜設定することができる。 Examples of the auxiliary agent include surfactants such as sodium alkylbenzenesulfonate, sodium dioctylsulfosuccinate, sulfone-modified polyvinyl alcohol, sodium polyacrylate, glyoxal, boric acid, dialdehyde starch, methylolurea, epoxy compound, hydrazine compound. Water-resistant agents (crosslinking agents), zinc stearate, calcium stearate, polyethylene wax, carnauba wax, paraffin wax, ester wax and other lubricants, UV absorbers, fluorescent dyes, coloring dyes, mold release agents, antioxidants, etc. Can be mentioned. The usage-amount of auxiliary agent can be suitably set from a wide range.
下塗り層用塗液の調製方法については、特に制限されず、また塗液の濃度についても特に制限されないが、通常２０〜５０質量％、好ましくは３５〜４５質量％で塗工すればよい。２０質量％以上とすることにより、塗液の粘度が高くでき、浸透ムラ、ひいては下塗り層のムラの発生を抑制でき、画質を向上させることができる。それと同時に、塗工速度を上げ、生産性を向上できる。また、５０質量％以下とすることにより、塗料の粘度を適度なものとして、加工を容易にできる。 The method for preparing the coating solution for the undercoat layer is not particularly limited, and the concentration of the coating solution is not particularly limited, but is usually 20 to 50% by mass, preferably 35 to 45% by mass. By setting the content to 20% by mass or more, the viscosity of the coating liquid can be increased, the occurrence of uneven penetration and hence unevenness of the undercoat layer can be suppressed, and the image quality can be improved. At the same time, the coating speed can be increased to improve productivity. Moreover, by setting it as 50 mass% or less, the viscosity of a coating material can be made moderate and a process can be made easy.
本発明における下塗り層用塗液については、液温２５℃におけるハーキュレス粘度計の８８００ｒｐｍにおける粘度が２５〜４０ｍＰａ・ｓであることが好ましい。また、液温２５℃におけるＢＬ粘度計の６０ｒｐｍにおける粘度が７００〜２０００ｍＰａ・ｓ程度であることが好ましい。前記粘度をそれぞれ２５ｍＰａ・ｓ以上又は７００ｍＰａ・ｓ以上とすることにより、浸透ムラの発生を抑制し、結果として高感度高画質の感熱記録体が得やすくでき、同時に生産性も高くできる。また前記粘度をそれぞれ４０ｍＰａ・ｓ又は２０００ｍＰａ・ｓを以下とすることにより、塗工を容易とできる結果、所望の感熱記録体を得やすくできる。 About the coating liquid for undercoat in this invention, it is preferable that the viscosity in 8800 rpm of the Hercules viscometer in liquid temperature 25 degreeC is 25-40 mPa * s. Moreover, it is preferable that the viscosity at 60 rpm of the BL viscometer at a liquid temperature of 25 ° C. is about 700 to 2000 mPa · s. By setting the viscosity to 25 mPa · s or more or 700 mPa · s or more, it is possible to suppress occurrence of uneven penetration, and as a result, it is easy to obtain a high-sensitivity high-quality heat-sensitive recording material, and at the same time, productivity can be increased. Further, by setting the viscosity to 40 mPa · s or 2000 mPa · s, respectively, the coating can be facilitated, and a desired heat-sensitive recording material can be easily obtained.
下塗り層用塗液の粘度の調整については、下塗り層用塗液の調製で使用される顔料、接着剤、助剤等の種類および配合量を選択することによって、適宜おこなえばよい。 The viscosity of the undercoat layer coating solution may be adjusted as appropriate by selecting the type and blending amount of pigments, adhesives, auxiliaries, etc. used in the preparation of the undercoat layer coating solution.
下塗り層の塗工量については、特に制限はなく、下塗り層一層の厚さが３〜１２μｍ（好ましくは、５〜１０μｍ）、下塗り層の総厚さが６〜３０μｍ（好ましくは、１０〜２５μｍ）になるように適宜調節すればよい。一層あたりの乾燥後の塗工量は１〜１５ｇ／ｍ２程度（好ましくは、２．５〜１０ｇ／ｍ２が好ましく、下塗り層の総塗工量としては、５〜３５ｇ／ｍ２程度であり、より好ましくは７〜２０ｇ／ｍ２である。 The coating amount of the undercoat layer is not particularly limited, and the thickness of the undercoat layer is 3 to 12 μm (preferably 5 to 10 μm), and the total thickness of the undercoat layer is 6 to 30 μm (preferably 10 to 25 μm). ) May be adjusted as appropriate. The coating amount after drying per layer is about 1 to 15 g / m 2 (preferably 2.5 to 10 g / m 2 is preferable, and the total coating amount of the undercoat layer is about 5 to 35 g / m 2 . Yes, more preferably 7 to 20 g / m 2 .
特に、第一下塗り層と第二下塗り層との乾燥後の塗工量の割合が、２：８〜８：２であることが好ましく、より好ましくは４：６〜６：４である。
この範囲とすることにより、下塗り層が十分な断熱層としての機能を発揮すると共に感熱記録層塗工時の余計な浸透を抑制する効果を高めることができ、厚さムラの少ない感熱記録層を形成することができる。
In particular, the ratio of the coating amount after drying of the first undercoat layer and the second undercoat layer is preferably 2: 8 to 8: 2, more preferably 4: 6 to 6: 4.
By setting it within this range, the undercoat layer can exhibit a function as a sufficient heat insulating layer and can enhance the effect of suppressing excessive penetration during coating of the thermal recording layer. Can be formed.
また、下塗り層塗工後の下塗り層の平滑度は２００〜１２００秒であることが好ましく、より好ましくは３００〜１０００秒である。平滑度は、王研式平滑度計（Ｊ．ＴＡＰＰＩ Ｎｏ．５）で測定したものである。 Further, the smoothness of the undercoat layer after the undercoat layer coating is preferably 200 to 1200 seconds, more preferably 300 to 1000 seconds. The smoothness is measured with a Oken type smoothness meter (J.TAPPI No. 5).
また、下塗り層の形成に際しては、例えば２層の下塗り層形成の場合は、アンワインダーから繰り出した原紙に一層目を塗布、乾燥した後、巻き取り工程を経ずにそのまま、二層目を塗布、乾燥してから巻き取る方式が好ましい。すなわち、第一下塗り層を形成して得られる第一下塗り層形成紙支持体を巻き取らずに連続して第二下塗り層を形成した後に、巻き取ることが好ましい。一層目を塗工した後、第二下塗り層を塗工する前に、一旦巻き取る工程を経ると、原紙裏面が接触することから、ブレード塗工方式で形成された高平滑な塗工面（第一下塗り層表面）に悪影響を及ぼすおそれがある。これに対し、上記巻き取り工程を下塗り層形成途中に行わなくすることにより、ブレード塗工で形成された塗工面が高平滑な状態で第二下塗り層を形成できることから、第二下塗り層以降の塗工層は高平滑な塗工面が形成されることになる。
さらに本発明においては、例えばロッド塗工方式等で２層目以降の下塗り層を形成した後、要求される品質に応じてスーパーカレンダー等の平滑化処理を施しても良い。
When forming the undercoat layer, for example, in the case of forming two undercoat layers, the first layer is applied to the base paper fed from the unwinder, dried, and then the second layer is applied without going through the winding process. A method of winding after drying is preferable. That is, it is preferable to wind up after forming the second undercoat layer continuously without winding up the first undercoat layer-formed paper support obtained by forming the first undercoat layer. After coating the first layer, before coating the second undercoat layer, once the winding process is performed, the back surface of the base paper comes into contact with each other. Therefore, a highly smooth coated surface formed by the blade coating method (first coating) There is a risk of adversely affecting the surface of the undercoat layer. On the other hand, since the second undercoat layer can be formed in a state in which the coating surface formed by blade coating is highly smooth by not performing the winding step during the formation of the undercoat layer, A highly smooth coated surface is formed in the coating layer.
Furthermore, in the present invention, for example, after the second and subsequent undercoat layers are formed by a rod coating method or the like, a smoothing process such as a super calendar may be performed according to the required quality.
感熱記録層
本発明の感熱記録層は、各種公知のロイコ染料、呈色剤及び接着剤を含有する。その他、必要に応じて、増感剤、顔料、各種助剤などを含有してもよい。
ロイコ染料の具体例としては、例えば、３−（４−ジエチルアミノ−２−エトキシフェニル）−３−（１−エチル−２−メチルインドール−３−イル）−４−アザフタリド、クリスタルバイオレットラクトン、３−（Ｎ−エチル−Ｎ−イソペンチルアミノ）−６−メチル−７−アニリノフルオラン、３−ジエチルアミノ−６−メチル−７−アニリノフルオラン、３−ジエチルアミノ−６−メチル−７−（ｏ，ｐ−ジメチルアニリノ）フルオラン、３−（Ｎ−エチル−Ｎ−ｐ−トルイジノ）−６−メチル−７−アニリノフルオラン、３−ピロリジノ−６−メチル−７−アニリノフルオラン、３−ジ（Ｎ−ブチル）アミノ−６−メチル−７−アニリノフルオラン、３−（Ｎ−シクロヘキシル−Ｎ−メチルアミノ）−６−メチル−７−アニリノフルオラン、３−ジエチルアミノ−７−（ｏ−クロロアニリノ）フルオラン、３−ジエチルアミノ−７−（ｍ−トリフルオロメチルアニリノ）フルオラン、３−ジエチルアミノ−６−メチル−７−クロロフルオラン、３−ジエチルアミノ−６−メチルフルオラン、３−シクロヘキシルアミノ−６−クロロフルオラン、３−（Ｎ−エチル−Ｎ−ヘキシルアミノ）−６−メチル−７−（ｐ−クロロアニリノ）フルオラン、３−ジ（ｎ−ペンチル）アミノ−６−メチル−７−アニリノフルオラン、３−（Ｎ−イソアミル−Ｎ−エチルアミノ）−７−（ｏ−クロロアニリノ）フルオラン、３−（Ｎ−エチル−Ｎ−２−テトラヒドロフルフリルアミノ）−６−メチル−７−アニリノフルオラン、３−ジエチルアミノ−６−クロロ−７−アニリノフルオラン、３−（Ｎ−ｎ−ヘキシル−Ｎ−エチルアミノ）−６−メチル−７−アニリノフルオラン、３−〔Ｎ−（３−エトキシプロピル）−Ｎ−エチルアミノ〕−６−メチル−７−アニリノフルオラン、３−〔Ｎ−（３−エトキシプロピル）−Ｎ−メチルアミノ〕−６−メチル−７−アニリノフルオラン、３−ジエチルアミノ−７−（２−クロロアニリノ）フルオラン、３−（Ｎ−エチル−ｐ−トルイジノ）−６−メチル−７−（ｐ−トルイジノ）フルオラン、３−ピペリジノ−６−メチル−７−アニリノフルオラン、３−ジエチルアミノ−７−（ｏ−フルオロアニリノ）フルオラン、３−（４−ジメチルアミノ）アリニノ−５，７−ジメチルフルオランなどが挙げられる。これらのうち、１種を単独で使用することもでき、２種以上を併用することも可能である。
Heat-sensitive recording layer The heat-sensitive recording layer of the present invention contains various known leuco dyes, colorants and adhesives. In addition, you may contain a sensitizer, a pigment, various adjuvants, etc. as needed.
Specific examples of the leuco dye include 3- (4-diethylamino-2-ethoxyphenyl) -3- (1-ethyl-2-methylindol-3-yl) -4-azaphthalide, crystal violet lactone, 3- (N-ethyl-N-isopentylamino) -6-methyl-7-anilinofluorane, 3-diethylamino-6-methyl-7-anilinofluorane, 3-diethylamino-6-methyl-7- (o , P-dimethylanilino) fluorane, 3- (N-ethyl-Np-toluidino) -6-methyl-7-anilinofluorane, 3-pyrrolidino-6-methyl-7-anilinofluorane, 3 -Di (N-butyl) amino-6-methyl-7-anilinofluorane, 3- (N-cyclohexyl-N-methylamino) -6-methyl-7-anilinofur Lan, 3-diethylamino-7- (o-chloroanilino) fluorane, 3-diethylamino-7- (m-trifluoromethylanilino) fluorane, 3-diethylamino-6-methyl-7-chlorofluorane, 3-diethylamino- 6-methylfluorane, 3-cyclohexylamino-6-chlorofluorane, 3- (N-ethyl-N-hexylamino) -6-methyl-7- (p-chloroanilino) fluorane, 3-di (n-pentyl) ) Amino-6-methyl-7-anilinofluorane, 3- (N-isoamyl-N-ethylamino) -7- (o-chloroanilino) fluorane, 3- (N-ethyl-N-2-tetrahydrofurfuryl) Amino) -6-methyl-7-anilinofluorane, 3-diethylamino-6-chloro-7-anilinofluorane, -(Nn-hexyl-N-ethylamino) -6-methyl-7-anilinofluorane, 3- [N- (3-ethoxypropyl) -N-ethylamino] -6-methyl-7-ani Linofluorane, 3- [N- (3-ethoxypropyl) -N-methylamino] -6-methyl-7-anilinofluorane, 3-diethylamino-7- (2-chloroanilino) fluorane, 3- (N -Ethyl-p-toluidino) -6-methyl-7- (p-toluidino) fluorane, 3-piperidino-6-methyl-7-anilinofluorane, 3-diethylamino-7- (o-fluoroanilino) fluorane , 3- (4-dimethylamino) alinino-5,7-dimethylfluorane and the like. Of these, one can be used alone, or two or more can be used in combination.
呈色剤としては、単独または２種以上混合することができる。呈色剤の具体例として例えば、４−ヒドロキシ−４'−イソプロポキシジフェニルスルホン、４−ヒドロキシ−４'−アリルオキシジフェニルスルホン、４，４'−イソプロピリデンジフェノール、４，４'−シクロヘキシリデンジフェノール、２，２−ビス（４−ヒドロキシフェニル）−４−メチルペンタン、２，４'−ジヒドロキシジフェニルスルホン、４，４'−ジヒドロキシジフェニルスルホン、３，３'−ジアリル−４，４'−ジヒドロキシジフェニルスルホン、４−ヒドロキシ−４'−メチルジフェニルスルホン、１，１−ビス（４−ヒドロキシフェニル）−１−フェニルエタン、１，４−ビス〔α−メチル−α−（４'−ヒドロキシフェニル）エチル〕ベンゼンなどのフェノール性化合物、Ｎ−ｐ−トリルスルホニル−Ｎ'−フェニルウレア、４，４'−ビス〔（４−メチル−３−フェノキシカルボニルアミノフェニル）ウレイド〕ジフェニルメタン、Ｎ−ｐ−トリルスルホニル−Ｎ'−ｐ−ブトキシフエニルウレアなどの分子内にスルホニル基とウレイド基を有する化合物、４−〔２−（ｐ−メトキシフェノキシ）エチルオキシ〕サリチル酸亜鉛、４−〔３−（ｐ−トリルスルホニル）プロピルオキシ〕サリチル酸亜鉛、５−〔ｐ−（２−ｐ−メトキシフェノキシエトキシ）クミル〕サリチル酸亜鉛などの芳香族カルボン酸の亜鉛塩化合物などが挙げられる。 As the color former, one kind or a mixture of two or more kinds can be used. Specific examples of the colorant include, for example, 4-hydroxy-4′-isopropoxydiphenylsulfone, 4-hydroxy-4′-allyloxydiphenylsulfone, 4,4′-isopropylidenediphenol, 4,4′-cyclohexylene. Dendiphenol, 2,2-bis (4-hydroxyphenyl) -4-methylpentane, 2,4'-dihydroxydiphenylsulfone, 4,4'-dihydroxydiphenylsulfone, 3,3'-diallyl-4,4'- Dihydroxydiphenylsulfone, 4-hydroxy-4′-methyldiphenylsulfone, 1,1-bis (4-hydroxyphenyl) -1-phenylethane, 1,4-bis [α-methyl-α- (4′-hydroxyphenyl) ) Ethyl] phenolic compounds such as benzene, Np-tolylsulfonyl-N′-phenylurea, , 4′-bis [(4-methyl-3-phenoxycarbonylaminophenyl) ureido] diphenylmethane, Np-tolylsulfonyl-N′-p-butoxyphenylurea and the like have a sulfonyl group and a ureido group in the molecule. Compound, zinc 4- [2- (p-methoxyphenoxy) ethyloxy] salicylate, zinc 4- [3- (p-tolylsulfonyl) propyloxy] salicylate, 5- [p- (2-p-methoxyphenoxyethoxy) cumyl ] Zinc salt compounds of aromatic carboxylic acids such as zinc salicylate.
接着剤としては、種々の分子量のポリビニルアルコール、変性ポリビニルアルコール、デンプン及びその誘導体、メトキシセルロース、カルボキシメチルセルロース、メチルセルロース、及びエチルセルロース等のセルロース誘導体、ポリアクリル酸ソーダ、ポリビニルピロリドン、アクリル酸アミド−アクリル酸エステル共重合体、アクリル酸アミド−アクリル酸エステル−メタクリル酸３元共重合体、スチレン−無水マレイン酸共重合体アルカリ塩、ポリアクリルアミド、アルギン酸ソーダ、ゼラチン、及びカゼインなどの水溶性高分子材料、並びに、ポリ酢酸ビニル、ポリウレタン、スチレン−ブタジエン共重合体、ポリアクリル酸、ポリアクリル酸エステル、塩化ビニル−酢酸ビニル共重合体、ポリブチルメタクリレート、エチレン−酢酸ビニル共重合体、及びスチレン−ブタジエン−アクリル系共重合体などの疎水性重合体のラテックスなどが挙げられる。 Adhesives include polyvinyl alcohols of various molecular weights, modified polyvinyl alcohols, starches and derivatives thereof, cellulose derivatives such as methoxycellulose, carboxymethylcellulose, methylcellulose, and ethylcellulose, sodium polyacrylate, polyvinylpyrrolidone, acrylamide-acrylic acid Water-soluble polymer materials such as ester copolymers, acrylic acid amide-acrylic acid ester-methacrylic acid terpolymers, styrene-maleic anhydride copolymer alkali salts, polyacrylamide, sodium alginate, gelatin, and casein, Polyvinyl acetate, polyurethane, styrene-butadiene copolymer, polyacrylic acid, polyacrylate ester, vinyl chloride-vinyl acetate copolymer, polybutyl methacrylate, ethylene Vinyl acetate copolymers, and styrene - butadiene - such as latex of a hydrophobic polymer such as an acrylic copolymer.
増感剤としては、単独または２種以上を併用することができる。増感剤の具体例として例えば、ステアリン酸アミド、ステアリン酸メチレンビスアミド、ステアリン酸エチレンビスアミド、４−ベンジルビフェニル、ｐ−トリルビフェニルエーテル、ジ（ｐ−メトキシフェノキシエチル）エーテル、１，２−ジ（３−メチルフェノキシ）エタン、１，２−ジ（４−メチルフェノキシ）エタン、１，２−ジ（４−メトキシフェノキシ）エタン、１，２−ジ（４−クロロフェノキシ）エタン、１，２−ジフェノキシエタン、１−（４−メトキシフェノキシ）−２−（３−メチルフェノキシ）エタン、２−ナフチルベンジルエーテル、１−（２−ナフチルオキシ）−２−フェノキシエタン、１，３−ジ（ナフチルオキシ）プロパン、シュウ酸ジベンジル、シュウ酸ジ−ｐ−メチル−ベンジル、シュウ酸ジ−ｐ−クロルベンジル、テレフタル酸ジブチル、テレフタル酸ジベンジル、２−（２'−ヒドロキシ−５'−メチルフェニル）ベンゾトリアゾールなどが挙げられる。 As a sensitizer, it can use individually or in combination of 2 or more types. Specific examples of the sensitizer include, for example, stearamide, stearic acid methylenebisamide, stearic acid ethylenebisamide, 4-benzylbiphenyl, p-tolylbiphenyl ether, di (p-methoxyphenoxyethyl) ether, 1,2-di ( 3-methylphenoxy) ethane, 1,2-di (4-methylphenoxy) ethane, 1,2-di (4-methoxyphenoxy) ethane, 1,2-di (4-chlorophenoxy) ethane, 1,2- Diphenoxyethane, 1- (4-methoxyphenoxy) -2- (3-methylphenoxy) ethane, 2-naphthylbenzyl ether, 1- (2-naphthyloxy) -2-phenoxyethane, 1,3-di (naphthyl) Oxy) propane, dibenzyl oxalate, di-p-methyl-benzyl oxalate, di-p-oxalate Rubenjiru, dibutyl terephthalate, dibenzyl terephthalate, 2- (2'-hydroxy-5'-methylphenyl) benzotriazole.
顔料としては、例えば炭酸カルシウム、シリカ、酸化亜鉛、酸化チタン、水酸化アルミニウム、水酸化亜鉛、硫酸バリウム、クレー、焼成クレー、タルク、及び表面処理された炭酸カルシウムやシリカ等の無機系微粉末、並びに尿素−ホルマリン樹脂、スチレン−メタクリル酸共重合体、ポリスチレン樹脂等の有機系の微粉末などが挙げられる。 Examples of the pigment include calcium carbonate, silica, zinc oxide, titanium oxide, aluminum hydroxide, zinc hydroxide, barium sulfate, clay, calcined clay, talc, and surface-treated inorganic fine powder such as calcium carbonate and silica, In addition, organic fine powders such as urea-formalin resin, styrene-methacrylic acid copolymer and polystyrene resin can be used.
これらの顔料のうち、シリカ、特に、粒子径３以上３０ｎｍ未満の無定形シリカ一次粒子が凝集してなる平均粒子直径３０〜９００ｎｍの二次粒子である無定形シリカを用いることが好ましい。これにより、サーマルヘッドでの印字の際に溶融した感熱記録体の溶融成分が、すばやく、且つ多量に吸収されることで、スティッキングが抑制される。しかも、粒子径を制御することにより、スクラッチが起きにくく、また透明性が高いため記録感度が向上する。 Among these pigments, it is preferable to use silica, in particular, amorphous silica that is secondary particles having an average particle diameter of 30 to 900 nm formed by agglomerating amorphous silica primary particles having a particle diameter of 3 or more and less than 30 nm. As a result, the molten component of the heat-sensitive recording material melted at the time of printing with the thermal head is absorbed quickly and in a large amount, thereby suppressing sticking. In addition, by controlling the particle size, scratches are less likely to occur, and the recording sensitivity is improved due to high transparency.
感熱記録層で使用する無定形シリカ一次粒子の粒子径は、通常、３以上３０ｎｍ未満、特に３〜２９ｎｍ、好ましくは５〜２７ｎｍ、より好ましくは７〜２５ｎｍである。
また、二次粒子の平均粒子径は、通常、３０〜９００ｎｍ、好ましくは４０〜７００ｎｍ、より好ましくは５０〜５００ｎｍ、特に５０〜４５０ｎｍである。
なお、これら一次粒子の粒子径及び二次粒子の平均粒子直径の算出は実施例にて後述する。
The particle size of the amorphous silica primary particles used in the thermosensitive recording layer is usually 3 or more and less than 30 nm, particularly 3 to 29 nm, preferably 5 to 27 nm, more preferably 7 to 25 nm.
The average particle size of the secondary particles is usually 30 to 900 nm, preferably 40 to 700 nm, more preferably 50 to 500 nm, and particularly 50 to 450 nm.
In addition, calculation of the particle diameter of these primary particles and the average particle diameter of secondary particles will be described later in Examples.
その他、各種助剤としては、滑剤、消泡剤、濡れ剤、防腐剤、蛍光増白剤、分散剤、増粘剤、着色剤、帯電防止剤など公知のものを用いることができる。
本発明の感熱記録層において、上記ロイコ染料の感熱記録層中の含有率は、一般に３〜５０質量％程度（好ましくは５〜２０質量％程度）であり、呈色剤の含有率は一般に３〜６０質量％程度（好ましくは５〜４０質量％）程度である。接着剤の含有率は一般に３〜５０質量％程度（好ましくは５〜２０質量％程度）である。
In addition, as the various auxiliary agents, known agents such as a lubricant, an antifoaming agent, a wetting agent, an antiseptic, a fluorescent brightening agent, a dispersing agent, a thickening agent, a coloring agent, and an antistatic agent can be used.
In the heat-sensitive recording layer of the present invention, the content of the leuco dye in the heat-sensitive recording layer is generally about 3 to 50% by mass (preferably about 5 to 20% by mass), and the content of the colorant is generally 3%. It is about -60 mass% (preferably 5-40 mass%). The content of the adhesive is generally about 3 to 50% by mass (preferably about 5 to 20% by mass).
増感剤が含まれる場合は、増感剤の含有率は１０〜４０質量％程度であることが好ましい。また、滑剤類は、５〜２０質量％程度の含有率で含まれることが好ましく、顔料は、１０〜５０質量％程度の含有率で含まれることが好ましい。 When a sensitizer is included, the content of the sensitizer is preferably about 10 to 40% by mass. Further, the lubricants are preferably contained at a content of about 5 to 20% by mass, and the pigment is preferably contained at a content of about 10 to 50% by mass.
本発明の感熱記録層用塗液の調製方法および塗工方法は、一般的に知られている方法により作成することができる。例えば、感熱記録層用塗液はロイコ染料、呈色剤を別々に接着剤水溶液と共に、ボールミルなどの分散機により粉砕分散した後、必要に応じて増感剤、顔料、各種助剤と混合攪拌して調製する。次いで、前記下塗り層上に感熱記録層用塗液を公知の方法で塗布、乾燥すればよい。 The preparation method and coating method of the heat-sensitive recording layer coating liquid of the present invention can be prepared by generally known methods. For example, the heat-sensitive recording layer coating solution is a leuco dye and a colorant separately pulverized and dispersed together with an aqueous adhesive solution by a dispersing machine such as a ball mill, and then mixed with a sensitizer, pigment, and various auxiliary agents as necessary. To prepare. Next, a thermal recording layer coating solution may be applied and dried on the undercoat layer by a known method.
感熱記録層用塗液の塗布方法は、特に限定されず、例えば、エアナイフコーティング、ブレードコーティング、グラビアコーティング、ロッドコーティング、ショートドウェルコーティング、カーテンコーティング、ダイコーティング等の従来公知の塗布方法がいずれも採用できる。 The coating method for the thermal recording layer coating liquid is not particularly limited. For example, any conventionally known coating methods such as air knife coating, blade coating, gravure coating, rod coating, short dwell coating, curtain coating, and die coating are adopted. it can.
感熱記録層用塗液の塗布量は特に制限はなく、乾燥重量で１〜１５ｇ／ｍ２程度、特に２〜１０ｇ／ｍ２程度であれば所望の品質を達成できる。 The coating amount of the thermal recording layer coating liquid is not particularly limited, and a desired quality can be achieved if the dry weight is about 1 to 15 g / m 2 , particularly about 2 to 10 g / m 2 .
本発明の感熱記録層の厚さの標準偏差が０．３０以下である。好ましくは０．２５以下、より好ましくは０．２０以下である。このような厚さムラの少ない均一な記録層により、高感度及び高画質な感熱記録体とすることができる。なお、前記標準偏差は、感熱記録層用塗液の物性、例えば粘度等を調節することにより、調整することができる。 The standard deviation of the thickness of the thermosensitive recording layer of the present invention is 0.30 or less. Preferably it is 0.25 or less, More preferably, it is 0.20 or less. Such a uniform recording layer with little thickness unevenness can provide a high-sensitivity and high-quality heat-sensitive recording material. The standard deviation can be adjusted by adjusting the physical properties of the thermal recording layer coating solution, such as viscosity.
特に、本発明では、第一下塗り層をブレード塗工方式で形成し、さらに二層目以降の下塗り層をロッド塗工方式で形成された下塗り層上に感熱記録層を形成することにより、好適に上記標準偏差の厚さにすることができる。下塗り層の平滑度が２００〜１２００秒（好ましくは３００〜１０００秒）である場合は、より好適に上記標準偏差の厚さにすることができる。 In particular, in the present invention, the first undercoat layer is formed by a blade coating method, and the second and subsequent undercoat layers are formed on the undercoat layer formed by the rod coating method, The thickness of the standard deviation can be preferably used. When the smoothness of the undercoat layer is 200 to 1200 seconds (preferably 300 to 1000 seconds), the thickness of the standard deviation can be more suitably achieved.
本発明において、各塗工層の厚さについては、感熱記録体の断面を電子顕微鏡を使用して１０００倍から３０００倍の倍率で撮影した反射電子組成像の任意の５箇所から厚さを測定し、その最大値及び最小値を除いた３箇所の平均値を求めたものであり、感熱記録層の厚さの標準偏差は、電子顕微鏡観察より得られた厚さデータより（数１）に基づき算出したものである。 In the present invention, as for the thickness of each coating layer, the thickness is measured from any five locations of the reflected electron composition image obtained by photographing the cross section of the thermal recording medium at a magnification of 1000 to 3000 using an electron microscope. The average value of three locations excluding the maximum value and the minimum value was obtained, and the standard deviation of the thickness of the thermosensitive recording layer was calculated from the thickness data obtained by electron microscope observation (Equation 1). It is calculated based on.
保護層
本発明の感熱記録体においては、感熱記録層上に保護層を設けることが好ましい。これにより、保存性及び記録時の走行性を向上させることができる。
保護層は、水溶性高分子及び／又は合成樹脂エマルジョンを主成分とすることが好ましい。
Protective layer In the heat-sensitive recording material of the present invention, a protective layer is preferably provided on the heat-sensitive recording layer. As a result, it is possible to improve storage stability and running performance during recording.
The protective layer preferably contains a water-soluble polymer and / or a synthetic resin emulsion as a main component.
水溶性高分子としては、例えば、完全ケン化または部分ケン化ポリビニルアルコール、アセトアセチル変性ポリビニルアルコール、ジアセトン変性ポリビニルアルコール、カルボキシ変性ポリビニルアルコール、ケイ素変性ポリビニルアルコール等のポリビニルアルコール、ヒドロキシエチルセルロース、メチルセルロース、カルボキシメチルセルロース等のセルロース系樹脂、ゼラチン、カゼイン、スチレン・無水マレイン酸共重合体のアルカリ塩、エチレン・アクリル酸共重合体のアルカリ塩、スチレン・アクリル酸共重合体のアルカリ塩等が挙げられる。 Examples of the water-soluble polymer include fully saponified or partially saponified polyvinyl alcohol, acetoacetyl-modified polyvinyl alcohol, diacetone-modified polyvinyl alcohol, carboxy-modified polyvinyl alcohol, silicon-modified polyvinyl alcohol, and the like, hydroxyethyl cellulose, methyl cellulose, carboxy Cellulose resins such as methylcellulose, gelatin, casein, alkali salts of styrene / maleic anhydride copolymers, alkali salts of ethylene / acrylic acid copolymers, alkali salts of styrene / acrylic acid copolymers, and the like.
合成樹脂エマルジョンとしては、例えば、スチレン−ブタジエン系ラテックス、アクリル系ラテックス、ウレタン系ラテックス等のラテックスが挙げられる。 Examples of the synthetic resin emulsion include latexes such as styrene-butadiene latex, acrylic latex, and urethane latex.
なかでも、重合度が１０００以上の変性ポリビニルアルコールは表面のバリア性を向上させ、耐薬品性などの保存性を向上させることができるという理由で好ましく使用される。重合度の上限は限定的でないが、通常は５０００程度、好ましくは４５００程度である。 Among them, modified polyvinyl alcohol having a degree of polymerization of 1000 or more is preferably used because it can improve surface barrier properties and improve storage stability such as chemical resistance. The upper limit of the degree of polymerization is not limited, but is usually about 5000, preferably about 4500.
水溶性高分子及び／又は合成樹脂エマルジョン（固形分）の含有量は、総計で、保護層の全固形分に対して３０〜８０質量％程度が好ましく、特に４０〜７５質量％程度がより好ましい。３０質量％以上とすることによりバリア性を十分に発揮させることができ、さらに表面強度が向上させ、紙粉の悪化等を防止できる。一方、８０質量％以下とすることにより、スティッキングの悪化を防止できる。 The total content of the water-soluble polymer and / or synthetic resin emulsion (solid content) is preferably about 30 to 80% by mass, and more preferably about 40 to 75% by mass, based on the total solid content of the protective layer. . By setting it to 30% by mass or more, the barrier property can be sufficiently exhibited, the surface strength can be further improved, and the deterioration of the paper powder can be prevented. On the other hand, by setting it to 80% by mass or less, deterioration of sticking can be prevented.
水溶性高分子及び合成樹脂エマルジョンを併用する場合、その使用比率は、水溶性高分子１００質量部に対して合成樹脂エマルジョン（固形分）が５〜１００質量部程度である。 When the water-soluble polymer and the synthetic resin emulsion are used in combination, the use ratio thereof is about 5 to 100 parts by mass of the synthetic resin emulsion (solid content) with respect to 100 parts by mass of the water-soluble polymer.
保護層は、水を媒体とし、上記水溶性高分子及び／又は合成樹脂エマルジョン、及び必要により添加される顔料や各種助剤を、混合攪拌して得られる保護層用塗液を、感熱記録層上に塗布、乾燥することにより、得ることができる。 The protective layer is a thermosensitive recording layer obtained by mixing and stirring the water-soluble polymer and / or synthetic resin emulsion, and optionally added pigments and various auxiliary agents using water as a medium. It can be obtained by coating and drying on top.
顔料としては、例えば、炭酸カルシウム、酸化亜鉛、酸化アルミニウム、二酸化チタン、無定形シリカ、合成マイカ、水酸化アルミニウム、硫酸バリウム、タルク、カオリン、クレー、焼成カオリンなどの無機顔料、ナイロン樹脂フィラー、尿素・ホルマリン樹脂フィラー、生デンプン粒子などの有機顔料が挙げられる。なかでも、カオリン、合成マイカおよび水酸化アルミニウムは、可塑剤、油などの薬品に対するバリア性が低下しづらく、かつ記録濃度も低下しにくいため、好ましい。 Examples of the pigment include inorganic pigments such as calcium carbonate, zinc oxide, aluminum oxide, titanium dioxide, amorphous silica, synthetic mica, aluminum hydroxide, barium sulfate, talc, kaolin, clay, and calcined kaolin, nylon resin filler, urea -Organic pigments such as formalin resin filler and raw starch particles. Of these, kaolin, synthetic mica, and aluminum hydroxide are preferable because barrier properties against chemicals such as plasticizers and oils are difficult to decrease and the recording density is difficult to decrease.
また、顔料として、無定形シリカを用いることも好ましい。特に、粒子径３〜７０ｎｍの無定形シリカ一次粒子が凝集してなる平均粒子直径３０〜９００ｎｍの二次粒子である無定形シリカを用いることが好ましい。これにより、スティッキングが実質上完全に又は実用上問題ないレベルに抑制され、サーマルヘッドへの粕付着が少なく、記録感度が高く、しかも耐可塑剤性（バリアー性）に優れた感熱記録体が得られる。 It is also preferable to use amorphous silica as the pigment. In particular, it is preferable to use amorphous silica which is secondary particles having an average particle diameter of 30 to 900 nm formed by agglomerating amorphous silica primary particles having a particle diameter of 3 to 70 nm. As a result, sticking is suppressed to a level that is substantially completely or practically not problematic, there is little flaw adhesion to the thermal head, recording sensitivity is high, and a thermal recording material excellent in plasticizer resistance (barrier properties) is obtained. It is done.
保護層で使用する無定形シリカ一次粒子の粒子径は、好ましくは３〜７０ｎｍ、より好ましくは５〜５０ｎｍ、さらに好ましくは７〜４０ｎｍである。
また、二次粒子の平均粒子径は、好ましくは３０〜９００ｎｍ、より好ましくは４０〜７００ｎｍ、さらに好ましくは５０〜５００ｎｍである。
なお、これら一次粒子の粒子径及び二次粒子の平均粒子直径の算出は実施例にて後述する。
The particle diameter of the amorphous silica primary particles used in the protective layer is preferably 3 to 70 nm, more preferably 5 to 50 nm, and still more preferably 7 to 40 nm.
Moreover, the average particle diameter of secondary particles becomes like this. Preferably it is 30-900 nm, More preferably, it is 40-700 nm, More preferably, it is 50-500 nm.
In addition, calculation of the particle diameter of these primary particles and the average particle diameter of secondary particles will be described later in Examples.
顔料の使用量は、保護層の全固形量に対して５〜８０質量％程度であり、特に１０〜６０質量％程度の範囲が好ましい。５質量％以上とすることにより、感熱ヘッドとの滑りを向上させ、スティッキングやヘッド粕の悪化を防止できる。一方、８０質量％以下とすることにより、バリア性が向上し、保護層としての機能を大幅に向上できる。 The usage-amount of a pigment is about 5-80 mass% with respect to the total solid of a protective layer, and the range of about 10-60 mass% is especially preferable. By setting the content to 5% by mass or more, it is possible to improve slippage with the thermal head and to prevent sticking and head wrinkles from deteriorating. On the other hand, by setting it as 80 mass% or less, barrier property improves and the function as a protective layer can be improved significantly.
助剤としては、例えばステアリン酸亜鉛、ステアリン酸カルシウム、ポリエチレンワックス、カルナバロウ、パラフィンワックス、エステルワックスなどの滑剤、アルキルベンゼンスルホン酸ナトリウム、ジオクチルスルホコハク酸ナトリウム、スルホン変性ポリビニルアルコール、ポリアクリル酸ナトリウムなどの界面活性剤、グリオキザール、ホウ酸、ジアルデヒドデンプン、メチロール尿素、エポキシ系化合物、ヒドラジン系化合物などの耐水化剤（架橋剤）、紫外線吸収剤、蛍光染料、着色染料、離型剤、酸化防止剤などが挙げられる。助剤の使用量は、広い範囲から適宜設定することができる。 As an auxiliary agent, for example, zinc stearate, calcium stearate, polyethylene wax, carnauba wax, paraffin wax, ester wax and other lubricants, alkylbenzene sulfonate sodium, dioctyl sulfosuccinate sodium, sulfone-modified polyvinyl alcohol, polyacrylic acid sodium and other surface activity Agents, glyoxal, boric acid, dialdehyde starch, methylol urea, epoxy compounds, hydrazine compounds and other water resistance agents (crosslinking agents), UV absorbers, fluorescent dyes, coloring dyes, mold release agents, antioxidants, etc. Can be mentioned. The usage-amount of auxiliary agent can be suitably set from a wide range.
保護層用塗液の塗布方法は特に限定されず、例えばエヤーナイフコーティング、ブレードコーティング、ロッドコーティング、ショートドウェルコーティング、カーテンコーティング、ダイコーティング等の公知の手段を用いることができる。 The method for applying the protective layer coating solution is not particularly limited, and known means such as air knife coating, blade coating, rod coating, short dwell coating, curtain coating, and die coating can be used.
保護層用塗液の塗布量は、乾燥重量で０．５〜３．０ｇ／ｍ２程度、好ましくは０．８〜２．５ｇ／ｍ２程度であり、保護層の厚さは０．４〜２．５μｍ程度であり、より好ましくは０．６〜２．０μｍ程度である。０．５ｇ／ｍ２以上とすることにより厚さを０．４μｍとすることができるため、感熱記録層を効果的に保護できる。一方、３．０ｇ／ｍ２以下とすることにより、厚さを２．５μｍ以下とできるため、記録感度を向上させ、低エネルギーで印字された場合においても判読しやすくできる。 The coating amount of the protective layer coating solution, dry weight 0.5 to 3.0 g / m 2 approximately, preferably 0.8~2.5g / m 2 approximately, the thickness of the protective layer 0.4 It is about -2.5 micrometers, More preferably, it is about 0.6-2.0 micrometers. By setting the thickness to 0.5 g / m 2 or more, the thickness can be set to 0.4 μm, so that the thermosensitive recording layer can be effectively protected. On the other hand, when the thickness is 3.0 g / m 2 or less, the thickness can be 2.5 μm or less. Therefore, the recording sensitivity can be improved, and even when printed with low energy, it can be easily read.
なお、本発明には、各種層を形成した後或いは全ての層を形成した後に、スーパーカレンダー掛け等の平滑化処理を施したり、必要に応じて感熱記録体の支持体の裏面側に保護層、印刷用塗被層、磁気記録層、帯電防止層、熱転写記録層、インクジェット記録層等を設けたり、支持体裏面に粘着剤処理を施して粘着ラベルに加工したり、感熱記録体にミシン目を入れたりするなど、感熱記録体製造分野における各種の公知技術が必要に応じて付加し得るものである。更に、感熱記録体における感熱記録層を多色記録が可能な構成とすることもできる。 In the present invention, after various layers are formed or after all layers are formed, a smoothing process such as supercalendering is performed, or a protective layer is formed on the back side of the support of the thermal recording medium as necessary. A coating layer for printing, a magnetic recording layer, an antistatic layer, a thermal transfer recording layer, an ink jet recording layer, etc. are provided, an adhesive treatment is applied to the back surface of the support to process it into an adhesive label, or a perforation is formed on the thermal recording medium. Various known techniques in the heat-sensitive recording material manufacturing field, such as putting in, can be added as necessary. Furthermore, the heat-sensitive recording layer in the heat-sensitive recording material can be configured to be capable of multicolor recording.
以下に実施例を挙げて、本発明をより具体的に説明するが、勿論これらに限定されるものではない。また、例中の「部」及び「％」は、特に断らない限り、それぞれ「質量部」及び「質量％」を示す。
なお、感熱記録層の厚さの標準偏差、下塗り層の厚さ、保護層の厚さについては、以下の方法で算出した。
・感熱記録層の厚さの標準偏差
感熱記録層の厚さの標準偏差は、感熱記録体の断面を電子顕微鏡を使用して１０００倍から３０００倍の倍率で撮影した反射電子組成像の任意の５箇所から厚さを測定し、その最大値及び最小値を除いた３箇所の平均値を求めたものであり、電子顕微鏡観察より得られた厚さデータより（数２）に基づき算出した。
Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not limited to these examples. Further, “parts” and “%” in the examples indicate “parts by mass” and “% by mass”, respectively, unless otherwise specified.
The standard deviation of the thickness of the thermosensitive recording layer, the thickness of the undercoat layer, and the thickness of the protective layer were calculated by the following method.
Standard deviation of the thickness of the heat - sensitive recording layer The standard deviation of the thickness of the heat - sensitive recording layer is an arbitrary reflection electron composition image obtained by photographing the cross section of the heat-sensitive recording body at a magnification of 1000 to 3000 using an electron microscope. Thickness was measured from five places, the average value of three places except the maximum value and the minimum value was calculated | required, and it computed based on (Equation 2) from the thickness data obtained by electron microscope observation.
・下塗り層の厚さ、保護層の厚さ
感熱記録体の断面を電子顕微鏡を使用して１０００倍から３０００倍の倍率で撮影した反射電子組成像の任意の５箇所から厚さを測定し、その最大値及び最小値を除いた３箇所の平均値から求めた。
-The thickness of the undercoat layer, the thickness of the protective layer Measure the thickness from any five locations of the reflected electron composition image obtained by photographing the cross section of the thermosensitive recording medium at a magnification of 1000 to 3000 times using an electron microscope, It calculated | required from the average value of three places except the maximum value and the minimum value.
感熱記録層用塗液およびシリカ分散液に使用した市販のシリカの「平均二次粒子径」は、特に断らない限り、メーカーのカタログ記載値を記載している。 Unless otherwise specified, the “average secondary particle size” of commercially available silica used in the thermal recording layer coating liquid and silica dispersion is the value described in the manufacturer's catalog.
また、シリカ分散液に使用した市販シリカおよび粉砕分散後のシリカ分散液に関して、「一次粒子の粒子径」は、比表面積の値を用いて後記式（２）に従って算出した値である。また、粉砕分散後のシリカ分散液に関して、「二次粒子の平均粒子直径」は、後記の＜二次粒子の平均粒子直径＞の項に記載の方法に従って測定した値である。
ここで、一次粒子の粒子径Ｄｐは、下記計算式から算出できる。
Ａｓｐ（ｍ２／ｇ）＝ＳＡ×ｎ （１）
上記式（１）において、Ａｓｐは比表面積を示し、ＳＡは一次粒子１つの表面積を示し、ｎは１ｇ当りの一次粒子の個数を示す。
Ｄｐ（ｎｍ）＝３０００／Ａｓｐ （２）
上記式（２）において、Ｄｐは一次粒子の粒子径を示し、Ａｓｐは比表面積を示す。
上記式（２）は、シリカの形状を真球と仮定し、且つ、シリカの密度ｄ＝２（ｇ／ｃｍ３）と仮定して導出されたものである。
ここで、無定形シリカの比表面積は、微細顔料（即ち、本発明で使用する無定型シリカ）を１０５℃にて乾燥し、得られた粉体試料の窒素吸脱着等温線を、比表面積測定装置（Ｃｏｕｌｔｅｒ社製のＳＡ３１００型）を用いて、２００℃で２時間真空脱気した後測定し、Ｂ．Ｅ．Ｔ比表面積を算出したものである。
以上より、本発明で使用する無定型シリカの一次粒子の粒径は、比表面積を上記比表面積測定装置（Ｃｏｕｌｔｅｒ社製のＳＡ３１００型）を用いて実測し、上記式（２）により、算出されたものである。
＜二次粒子の平均粒子直径＞
調製して得られたシリカ分散液を水で希釈して５質量％濃度に調整し、得られた希釈シリカ分散液をホモミキサーにて５０００ｒｐｍで３０分間撹拌分散した。その直後に当該分散液を、親水性処理したポリエステルフィルム上に、乾燥後の重量が３ｇ／ｍ２程度になるように塗布、乾燥してサンプルとし、電子顕微鏡（ＳＥＭとＴＥＭ）で観察し、１万〜４０万倍の電子顕微鏡写真を撮り、５ｃｍ四方中の二次粒子のマーチン径を測定して平均したものである（「微粒子ハンドブック」、朝倉書店、ｐ５２、１９９１年参照）。
Moreover, regarding the commercially available silica used for the silica dispersion and the silica dispersion after pulverization and dispersion, the “particle diameter of the primary particles” is a value calculated according to the following formula (2) using the value of the specific surface area. In addition, regarding the silica dispersion after pulverization and dispersion, the “average particle diameter of secondary particles” is a value measured according to the method described in the section “Average particle diameter of secondary particles” below.
Here, the particle diameter Dp of the primary particles can be calculated from the following formula.
Asp (m 2 / g) = SA × n (1)
In the above formula (1), Asp represents the specific surface area, SA represents the surface area of one primary particle, and n represents the number of primary particles per gram.
Dp (nm) = 3000 / Asp (2)
In the above formula (2), Dp represents the particle size of the primary particles, and Asp represents the specific surface area.
The above formula (2) is derived on the assumption that the shape of silica is a true sphere and the density of silica is d = 2 (g / cm 3 ).
Here, the specific surface area of the amorphous silica was measured by measuring the nitrogen adsorption and desorption isotherm of the powder sample obtained by drying the fine pigment (that is, the amorphous silica used in the present invention) at 105 ° C. Measured after vacuum degassing at 200 ° C. for 2 hours using an apparatus (SA3100 type manufactured by Coulter). E. The T specific surface area is calculated.
From the above, the particle size of the primary particles of the amorphous silica used in the present invention is calculated from the above formula (2) by measuring the specific surface area using the above specific surface area measuring device (SA3100 type manufactured by Coulter). It is a thing.
<Average particle diameter of secondary particles>
The prepared silica dispersion was diluted with water to adjust the concentration to 5% by mass, and the obtained diluted silica dispersion was stirred and dispersed at 5000 rpm for 30 minutes with a homomixer. Immediately thereafter, the dispersion was applied onto a hydrophilically treated polyester film so that the weight after drying was about 3 g / m 2 , dried to obtain a sample, and observed with an electron microscope (SEM and TEM). This is an average of the results of taking an electron micrograph at a magnification of 10,000 to 400,000 and measuring and averaging the diameter of the secondary particles in a 5 cm square (see “Fine Particle Handbook”, Asakura Shoten, p52, 1991).
実施例１
（１ａ）古紙パルプの作製
新聞古紙２部、印刷された上質紙古紙３部、苛性ソーダの１％水溶液１部及び水９５部からなる組成物をパルパーにて離解した後、スクリーンとクリーナーにより除塵処理、脱水処理（パルプ濃度２５％）、過酸化水素とノニオン系界面活性剤（ポリオキシエチレンノニルフェニルエーテル）による漂白、脱墨処理する。処理後の古紙パルプ濃度が１％となるように希釈した後、フローテーション及び水性処理してハンター白色度７５％の古紙パルプを得た。
Example 1
(1a) Preparation of Waste Paper Pulp A composition consisting of 2 parts of used newspaper waste paper, 3 parts of printed high quality paper waste paper, 1 part of 1% aqueous solution of caustic soda and 95 parts of water was removed with a pulper, followed by dust removal with a screen and a cleaner. , Dehydration treatment (pulp concentration 25%), bleaching with hydrogen peroxide and nonionic surfactant (polyoxyethylene nonylphenyl ether), deinking treatment. After being diluted so that the used paper pulp concentration after treatment was 1%, the waste paper pulp having a Hunter whiteness of 75% was obtained by flotation and aqueous treatment.
（１ｂ）紙支持体の作製
上記の古紙パルプ濃度１％のスラリー（ＣＳＦ２１０ｍｌ）８０部とパルプ濃度１％のＬＢＫＰスラリー（ＣＳＦ４８０ｍｌ）２０部の比率で混合した後、紙支持体に対してアルキルケテンダイマーが０．３％、カチオン変性澱粉（商品名：ケートＦ、王子ナショナル社製）が０．５％、硫酸バンドが０．２％、軽質炭酸カルシウムが７％となるように内添されたパルプスラリーを長網抄紙機にて抄紙し、サイズプレス液を乾燥後の塗布量が１．０ｇ／ｍ２となるようにプレスし、マシンキャレンダー処理して坪量５０ｇ／ｍ２、両面共にベック平滑度６０秒の紙支持体を得た。
(1b) Preparation of paper support After mixing the above-mentioned waste paper pulp concentration 1% slurry (CSF 210 ml) and pulp concentration 1% LBKP slurry (CSF 480 ml) 20 parts, alkyl ketene to the paper support It was internally added so that the dimer was 0.3%, the cation-modified starch (trade name: Kate F, manufactured by Oji National) was 0.5%, the sulfate band was 0.2%, and the light calcium carbonate was 7%. The pulp slurry is made with a long paper machine, the size press solution is pressed so that the coating amount after drying is 1.0 g / m 2 , machine calendering is performed, and the basis weight is 50 g / m 2 . A paper support having a Beck smoothness of 60 seconds was obtained.
（１ｃ）下塗り層用塗液の調製
焼成カオリン（商品名：アンシレックス、エンゲルハード社製、吸油量９０ｍｌ／１００ｇ）８５部を水１００部に分散して得られた分散物（平均粒子径：０．６μｍ）に、スチレン−ブタジエン共重合物エマルジョン（固形分５０％）４０部と、酸化澱粉の１０％水溶液５０部、カルボキシメチルセルロース（商品名：セロゲンＡＧガム、第一工業製薬社製）１部を混合攪拌し、下塗層用塗液を得た。なお、下塗層用塗液の粘度は、３４ｍＰａ・ｓ（ハーキュレス粘度計の８８００ｒｐｍ）、１３８０ｍＰａ・ｓ（ＢＬ粘度計の６０ｒｐｍ）であった。
(1c) Preparation of coating liquid for undercoat layer Dispersion obtained by dispersing 85 parts of calcined kaolin (trade name: Ansilex, Engelhard, Inc., oil absorption 90 ml / 100 g) in 100 parts of water (average particle diameter: 0.6 μm), 40 parts of a styrene-butadiene copolymer emulsion (solid content 50%), 50 parts of a 10% aqueous solution of oxidized starch, carboxymethyl cellulose (trade name: Cellogen AG gum, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) 1 The parts were mixed and stirred to obtain a coating solution for an undercoat layer. In addition, the viscosity of the coating liquid for undercoat layers was 34 mPa * s (8800 rpm of a Hercules viscometer) and 1380 mPa * s (60 rpm of a BL viscometer).
（１ｄ）各成分の調製
・Ａ液調製（ロイコ染料分散液の調製）
３−（Ｎ−エチル−ｐ−トルイジノ）−６−メチル−７−アニリノフルオラン１０部、メチルセルロースの５％水溶液５部、及び水１５部からなる組成物をサンドミルで平均粒子径が０．３μｍとなるまで粉砕してＡ液を得た。
(1d) Preparation of each component / A solution preparation (preparation of leuco dye dispersion)
A composition consisting of 10 parts of 3- (N-ethyl-p-toluidino) -6-methyl-7-anilinofluorane, 5 parts of a 5% aqueous solution of methylcellulose, and 15 parts of water in a sand mill has an average particle size of 0. A liquid A was obtained by pulverizing to 3 μm.
・Ｂ液調製（呈色剤分散液の調製）
２，４’−ジヒドロキシジフェニルスルホン１０部、メチルセルロースの５％水溶液５部、及び水１５部からなる組成物をサンドミルで平均粒子径が０．３μｍとなるまで粉砕してＢ液を得た。
・ B liquid preparation (preparation of colorant dispersion)
A composition consisting of 10 parts of 2,4′-dihydroxydiphenylsulfone, 5 parts of a 5% aqueous solution of methylcellulose, and 15 parts of water was pulverized with a sand mill until the average particle size became 0.3 μm to obtain a liquid B.
・Ｃ液調製（増感剤分散液の調製）
シュウ酸ジ−ｐ−メチルベンジルエステル２０部、メチルセルロースの５％水溶液５部、及び水５５部からなる組成物をサンドミルで平均粒子径が０．３μｍとなるまで粉砕してＣ液を得た。
・ C liquid preparation (preparation of sensitizer dispersion)
A composition consisting of 20 parts of di-p-methylbenzyl oxalate ester, 5 parts of a 5% aqueous solution of methylcellulose, and 55 parts of water was pulverized with a sand mill until the average particle size became 0.3 μm to obtain a liquid C.
（１ｅ）感熱記録層用塗液の調製
Ａ液２５部、Ｂ液５０部、Ｃ液５０部、微粒子無定形シリカ分散液（商品名：サイロジェット７０３Ａ、平均二次粒子径：３００ｎｍ、一次粒子の粒子径：１１ｎｍ、比表面積２８０ｍ２／ｇ、二次粒子の平均粒子直径：３００ｎｍ、固形分２０％、グレースデビソン社製）２０部、酸化デンプンの２０％水溶液３０部、及びアセトアセチル変性ポリビニルアルコール（商品名：ゴーセファイマーＺ−２００、日本合成化学工業社製）の１０％水溶液５０部からなる組成物を混合撹拌して感熱記録層用塗液を得た。
(1e) Preparation of coating solution for heat-sensitive recording layer A part 25 parts, B part 50 parts, C part 50 parts, fine particle amorphous silica dispersion (trade name: Silojet 703A, average secondary particle size: 300 nm, primary particles Particle diameter: 11 nm, specific surface area 280 m 2 / g, average particle diameter of secondary particles: 300 nm, solid content 20%, manufactured by Grace Devison) 20 parts, oxidized starch 30% aqueous solution 30 parts, and acetoacetyl-modified polyvinyl A composition consisting of 50 parts of a 10% aqueous solution of alcohol (trade name: Goosefimmer Z-200, manufactured by Nippon Synthetic Chemical Industry Co., Ltd.) was mixed and stirred to obtain a thermal recording layer coating solution.
（１ｆ）感熱記録体の作製
（１ｂ）で作製した紙支持体の１面上に、乾燥後の塗布量が７．０ｇ／ｍ２になるようにブレード塗工方式にて下塗層用塗液を塗布乾燥して第１下塗層を形成し、更に巻き取らずに乾燥後の塗布量が８．０ｇ／ｍ２になるようにロッド塗工方式にて第１下塗層上に、下塗層用塗液を塗布乾燥して、第２下塗層を形成した。得られた２層からなる下塗層上に乾燥後の塗布量が５．０ｇ／ｍ２となるように感熱記録層用塗液を塗布乾燥した。その後、線圧７８Ｎ／ｍの加圧条件でスーパーキャレンダーによって平滑化処理し感熱記録体を得た。
(1f) Production of thermosensitive recording material On the one side of the paper support produced in (1b), the coating for the undercoat layer was applied by a blade coating method so that the coating amount after drying was 7.0 g / m 2. The liquid is applied and dried to form a first undercoat layer, and further on the first undercoat layer by a rod coating method so that the coating amount after drying is 8.0 g / m 2 without winding. The undercoat layer coating solution was applied and dried to form a second undercoat layer. The thermosensitive recording layer coating solution was applied and dried on the resulting two-layered undercoat layer so that the coating amount after drying was 5.0 g / m 2 . Thereafter, the recording material was smoothed by a super calender under a pressurizing condition of a linear pressure of 78 N / m to obtain a heat-sensitive recording material.
実施例２
（２ａ）保護層用塗液の調製
カオリン（商品名：ＵＷ−９０、エンゲルハード社製）５０部を水１００部に分散して得られた分散物に、アセトアセチル変性ポリビニルアルコール（商品名：ゴーセファイマーＺ−２００、前出）の１０％水溶液６００部、及びステアリン酸亜鉛（商品名：ハイドリンＺ−８−３６、固形分３６％、中京油脂社製）２５部を混合攪拌して保護層用塗液を得た。
Example 2
(2a) Preparation of coating solution for protective layer To a dispersion obtained by dispersing 50 parts of kaolin (trade name: UW-90, manufactured by Engelhard) in 100 parts of water, acetoacetyl-modified polyvinyl alcohol (trade name: Protected by mixing and stirring 600 parts of 10% aqueous solution of Goosefimmer Z-200, supra) and 25 parts of zinc stearate (trade name: Hydrin Z-8-36, solid content 36%, manufactured by Chukyo Yushi Co., Ltd.) A layer coating solution was obtained.
（２ｂ）感熱記録体の作製
実施例１の感熱記録体の作製において、感熱記録層を形成後、前記保護層用塗液を乾燥後の塗布量が１．３ｇ／ｍ２となるように前記保護層用塗液を塗布乾燥した以外は、実施例１と同様にして感熱記録体を得た。
(2b) Production of thermal recording material In the production of the thermal recording material of Example 1, after forming the thermal recording layer, the coating amount for the protective layer was dried so that the coating amount after drying was 1.3 g / m 2. A heat-sensitive recording material was obtained in the same manner as in Example 1 except that the protective layer coating solution was applied and dried.
実施例３
実施例１の感熱記録体の作製において、第１下塗り層及び第２下塗り層の塗工量をそれぞれ５．０ｇ／ｍ２、１０．０ｇ／ｍ２とした以外は、実施例１と同様にして感熱記録体を得た。
Example 3
In the preparation of heat-sensitive recording material of Example 1, 5.0 g / m 2 coating amount of the first undercoat layer and the second undercoat layer, respectively, except that the 10.0 g / m 2 are in the same manner as in Example 1 A heat-sensitive recording material was obtained.
実施例４
実施例１の感熱記録体の作製において、第１下塗り層及び第２下塗り層の塗工量をそれぞれ５．０ｇ／ｍ２、５．０ｇ／ｍ２とした以外は、実施例１と同様にして感熱記録体を得た。
Example 4
In the preparation of heat-sensitive recording material of Example 1, 5.0 g / m 2 coating amount of the first undercoat layer and the second undercoat layer, respectively, except that the 5.0 g / m 2 are in the same manner as in Example 1 A heat-sensitive recording material was obtained.
実施例５
実施例１の感熱記録体の作製において、下塗り層用塗液として下記の塗液を用いた以外は、実施例１と同様にして感熱記録体を得た。
（５ａ）下塗り層用塗液の調製
焼成カオリン（商品名：アンシレックス、エンゲルハード社製、吸油量９０ｍｌ／１００ｇ）５５部を水７５部に分散して得られた分散物（平均粒子径：０．６μｍ）に、微小中空粒子（商品名：ＡＥ−８５１、ＪＳＲ社製、固形分５５％、平均粒子径０．９μｍ）５５部、スチレン−ブタジエン共重合物エマルジョン（固形分５０％）４０部と、酸化澱粉の１０％水溶液５０部、カルボキシメチルセルロース（商品名：セロゲンＡＧガム、第一工業製薬社製）1部を混合攪拌して下塗層用塗液を得た。なお、下塗層用塗液の粘度は、３７ｍＰａ・ｓ（ハーキュレス粘度計の８８００ｒｐｍ）、１５８０ｍＰａ・ｓ（ＢＬ粘度計の６０ｒｐｍ）であった。
Example 5
In the production of the thermal recording material of Example 1, a thermal recording material was obtained in the same manner as in Example 1 except that the following coating solution was used as the coating solution for the undercoat layer.
(5a) Preparation of coating solution for undercoat layer Dispersion obtained by dispersing 55 parts of calcined kaolin (trade name: Ancilex, Engelhard, Inc., oil absorption 90 ml / 100 g) in 75 parts of water (average particle size: 0.6 μm), 55 parts of fine hollow particles (trade name: AE-851, manufactured by JSR, solid content 55%, average particle size 0.9 μm), styrene-butadiene copolymer emulsion (solid content 50%) 40 Part and 50 parts of a 10% aqueous solution of oxidized starch and 1 part of carboxymethylcellulose (trade name: Cellogen AG gum, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) were mixed and stirred to obtain a coating solution for an undercoat layer. In addition, the viscosity of the coating liquid for undercoat layers was 37 mPa · s (8800 rpm of Hercules viscometer) and 1580 mPa · s (60 rpm of BL viscometer).
実施例６
実施例１の感熱記録体の作製において、第１下塗り層を塗工、乾燥した後に一旦巻き取り、その後第２下塗り層を塗布乾燥した以外は、実施例１と同様にして感熱記録体を得た。
Example 6
In the production of the heat-sensitive recording material of Example 1, a heat-sensitive recording material was obtained in the same manner as in Example 1 except that the first undercoat layer was coated and dried and then wound up and then the second undercoat layer was applied and dried. It was.
比較例１
実施例１の感熱記録体の作製において、第２下塗り層を形成しなかった以外は、実施例１と同様にして感熱記録体を得た。
Comparative Example 1
A heat-sensitive recording material was obtained in the same manner as in Example 1 except that the second undercoat layer was not formed in the production of the heat-sensitive recording material of Example 1.
比較例２
実施例１の感熱記録体の作製において、第１下塗層の塗工量を１５．０ｇ／ｍ２とし、且つ第２下塗り層を形成しなかった以外は、実施例１と同様にして感熱記録体を得た。
Comparative Example 2
In the production of the thermal recording material of Example 1, the thermal sensitivity was the same as in Example 1 except that the coating amount of the first undercoat layer was 15.0 g / m 2 and the second undercoat layer was not formed. A record was obtained.
比較例３
実施例１の感熱記録体の作製において、第２下塗り層の塗工をブレード塗工方式に変更した以外は、実施例１と同様にして感熱記録体を得た。得られた感熱記録体は第２下塗層塗工時に多発した塗工欠陥（ストリーク）が散在していた。
Comparative Example 3
A heat-sensitive recording material was obtained in the same manner as in Example 1 except that in the production of the heat-sensitive recording material of Example 1, the coating of the second undercoat layer was changed to the blade coating method. The obtained heat-sensitive recording material was scattered with coating defects (streaks) frequently generated during the application of the second undercoat layer.
比較例４
実施例１の感熱記録体の作製において、第１下塗層、及び第２下塗層の塗工をバー塗工方式に変更した以外は、実施例１と同様にして感熱記録体を得た。
Comparative Example 4
In the production of the thermal recording material of Example 1, a thermal recording material was obtained in the same manner as in Example 1 except that the coating of the first undercoat layer and the second undercoat layer was changed to the bar coating method. .
比較例５
実施例２の感熱記録体の作製において、下塗り層として、比較例２を使用した以外は、実施例２と同様にして感熱記録体を得た。
Comparative Example 5
In the production of the heat-sensitive recording material of Example 2, a heat-sensitive recording material was obtained in the same manner as in Example 2 except that Comparative Example 2 was used as the undercoat layer.
比較例６
実施例２の感熱記録体の作製において、下塗り層として、比較例３を使用した以外は、実施例２と同様にして感熱記録体を得た。
Comparative Example 6
In the production of the heat-sensitive recording material of Example 2, a heat-sensitive recording material was obtained in the same manner as in Example 2 except that Comparative Example 3 was used as the undercoat layer.
かくして得られた１２種類の感熱記録体について以下の評価を行い、その結果を表１に示した。 The following evaluations were carried out on the 12 types of heat-sensitive recording materials thus obtained, and the results are shown in Table 1.
・平滑度（王研式平滑度；Ｊ.ＴＡＰＰＩ Ｎｏ.５）
感熱記録体において、下塗り層最上層表面を王研式平滑度計で測定した。
・ Smoothness (Oken type smoothness; J.TAPPI No.5)
In the thermosensitive recording material, the surface of the uppermost layer of the undercoat layer was measured with a Oken type smoothness meter.
・記録感度
感熱評価機（商品名：ＴＨ−ＰＭＤ、大倉電気社製）を用い、０．１６ｍＪ／ｄｏｔで各感熱記録体を発色させ、記録部の濃度をマクベス濃度計（商品名：ＲＤ−９１４、マクベス社製）のビジュアルモードで測定した。
Recording sensitivity Using a thermal evaluation machine (trade name: TH-PMD, manufactured by Okura Electric Co., Ltd.), each thermal recording medium was colored at 0.16 mJ / dot, and the density of the recording area was measured using a Macbeth densitometer (trade name: RD- 914, manufactured by Macbeth Co.).
・画質
上記０．１６ｍｊ／ｄｏｔで発色させた部分の発色状況をマイクロスコープで拡大観察し、以下のように評価した。
◎：ドットが均一に発色しており、濃淡ムラがない。
○：僅かにドットの未発色部分が見られるが、問題のないレベル。
△：明らかなドット未発色部分が見られ、目視評価でも濃淡ムラが大きく、実用上問題あり。
×：ドット未発色部分が多く、濃淡ムラが激しい。
Image quality The color development state of the portion developed with 0.16 mj / dot was observed with a microscope and evaluated as follows.
A: The dots are uniformly colored and there is no shading unevenness.
○: Slightly uncolored part of the dot is seen, but there is no problem.
Δ: A clear dot non-colored portion is observed, and the unevenness in density is large even by visual evaluation, which is problematic in practical use.
X: There are many dot non-colored portions, and shading unevenness is intense.
・バリア性
感熱記録体の地肌部上に、５０％濃度のエタノール溶液を塗布放置し、乾燥後の感熱記録体の発色状況を目視観察し、以下のように評価した。
◎：発色が全くなく、バリア性に優れていた。
○：極僅かに発色している部分が見られたが、実用上問題なし。
△：○よりは、発色している部分の面積や発色程度は大きく、実用上問題あり。
×：大部分で発色が見られ、発色程度もひどく、実用上問題あり。
Barrier property A 50% concentration ethanol solution was applied and left on the background of the heat-sensitive recording medium, and the color development of the heat-sensitive recording body after drying was visually observed and evaluated as follows.
A: There was no color development and the barrier property was excellent.
○: A very slightly colored portion was observed, but there was no practical problem.
Δ: The area of the colored portion and the degree of color development are larger than those of ○, and there are practical problems.
×: Color development was observed in the majority, the color development level was severe, and there was a problem in practical use.
・耐熱地肌カブリ性
各感熱記録体を１００℃で２４時間放置し、地肌部をマクベス濃度計［ＲＤ−９１４、マクベス社製］のビジュアルモードで測定した。
Heat-resistant background fogging Each heat-sensitive recording material was allowed to stand at 100 ° C. for 24 hours, and the background portion was measured with a Macbeth densitometer [RD-914, manufactured by Macbeth Co., Ltd.] in visual mode.
Claims (11)
（ＩＩ）該紙支持体上に形成された下塗り層、及び
（ＩＩＩ）該下塗り層上に形成された感熱記録層
を備えた感熱記録体であって、
ａ）紙支持体が、古紙パルプを含有しており、
ｂ）前記下塗り層が、少なくとも第一下塗り層及び該第一下塗り層上に形成された第二下塗り層からなる多層構造を有しており、
ｃ）第一下塗り層をブレード塗工方式で形成し、さらに二層目以降の下塗り層をロッド塗工方式で形成したことを特徴とする
感熱記録体。 (I) a paper support,
(II) a thermal recording medium comprising an undercoat layer formed on the paper support, and (III) a thermal recording layer formed on the undercoat layer,
a) the paper support contains waste paper pulp;
b) The undercoat layer has a multilayer structure comprising at least a first undercoat layer and a second undercoat layer formed on the first undercoat layer,
c) A heat-sensitive recording material, wherein the first undercoat layer is formed by a blade coating method, and the second and subsequent undercoat layers are formed by a rod coating method.
前記紙支持体が古紙パルプを含有しており、
前記紙支持体上にブレード塗工方式で塗布及び乾燥することにより、第一下塗り層を形成する第１工程、及び、
前記第一下塗り層上にロッド塗工方式で塗布及び乾燥することにより、第二下塗り層を形成する第２工程、
を備えた、製造方法。 A method for producing a heat-sensitive recording body comprising an undercoat layer and a heat-sensitive recording layer sequentially formed on a paper support,
The paper support contains waste paper pulp;
A first step of forming a first undercoat layer by applying and drying on the paper support by a blade coating method; and
A second step of forming a second undercoat layer by applying and drying on the first undercoat layer by a rod coating method;
A manufacturing method comprising: