JP2008087278A - Thermosensitive transfer image receiving sheet and manufacturing method thereof - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a thermosensitive transfer image receiving sheet provided with high-speed printer aptitude and a manufacturing method thereof. <P>SOLUTION: The thermosensitive transfer image receiving sheet has at least one kind of accepting layers containing a matting agent on a support body, wherein the matting agent comprises fine particles with particle sizes of 1 to 10 μm and containing an organic compound. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、感熱転写受像シートおよびその製造方法に関する。   The present invention relates to a thermal transfer image receiving sheet and a method for producing the same.

従来、種々の熱転写記録方法が知られているが、中でも染料拡散転写記録方式は、銀塩写真の画質に最も近いカラーハードコピーが作製できるプロセスとして注目されている（例えば、非特許文献１及び２参照）。しかも、銀塩写真に比べて、ドライであること、デジタルデータから直接可視像化できる、複製作りが簡単であるなどの利点を持っている。   Conventionally, various thermal transfer recording methods are known, and among them, the dye diffusion transfer recording method is attracting attention as a process capable of producing a color hard copy closest to the image quality of a silver salt photograph (for example, Non-Patent Document 1 and 2). In addition, it has the advantages of being dry, being able to visualize directly from digital data, and being easy to duplicate, compared to silver salt photography.

この染料拡散転写記録方式では、色素を含有する感熱転写シート（以下、インクシートともいう。）と感熱転写受像シート（以下、受像シートともいう。）とを重ね合わせ、次いで、電気信号によって発熱が制御されるサーマルヘッドによってインクシートを加熱することでインクシート中の色素を受像シートに転写して画像情報の記録を行うものであり、シアン、マゼンタ、イエローの３色を重ねて記録することで色の濃淡に連続的な変化を有するカラー画像を転写記録することができる。染料拡散転写記録方式では、上記のように、感熱転写受像シートとインクシートとが直に接触するために、感熱転写受像シートの表面性（離型性、凹凸等を意味する）は重要である。   In this dye diffusion transfer recording system, a thermal transfer sheet containing a pigment (hereinafter also referred to as an ink sheet) and a thermal transfer image receiving sheet (hereinafter also referred to as an image receiving sheet) are superposed, and then heat is generated by an electrical signal. By heating the ink sheet with a controlled thermal head, the dye in the ink sheet is transferred to the image receiving sheet to record image information. By recording three colors of cyan, magenta, and yellow in an overlapping manner, A color image having a continuous change in color shading can be transferred and recorded. In the dye diffusion transfer recording system, as described above, since the thermal transfer image receiving sheet and the ink sheet are in direct contact with each other, the surface properties of the thermal transfer image receiving sheet (meaning releasability, unevenness, etc.) are important. .

近年では、染料拡散転写記録方式が普及するに従い、印画速度の高速化が進んでおり、従来の感熱転写受像シートを従来の熱エネルギーで印画しても十分な転写濃度が得られないとの問題が生じてきた。さらに熱転写による画像の印画物に対し、より高濃度で鮮明なものが要求されており、転写感度を向上する試みがなされている。その中の一つが、印画時の熱エネルギーを増加させて、より鮮明な転写濃度を得る、という改良手段である。しかし、この方法では、感熱転写受像シートにかかる熱ダメージが大きく、インクリボン染料層と被転写材料の感熱転写受像シートの染料受容層とが熱融着したり、さらには、インクリボン染料層の染料だけでなく、染料層ごと被転写材料の感熱転写受像シートに転写する、いわゆる異常転写が生じる等の問題が顕著化してきている。これらの高速プリンターに用いる感熱転写受像シートの設計には、従来の印画速度が遅いときの感熱転写受像シートとは異なる表面性、特に離型性の配慮が必要である。   In recent years, as the dye diffusion transfer recording system has become widespread, the printing speed has been increasing, and even if the conventional thermal transfer image-receiving sheet is printed with conventional thermal energy, a sufficient transfer density cannot be obtained. Has arisen. Furthermore, there is a demand for a higher density and clearer image printed by thermal transfer, and attempts have been made to improve transfer sensitivity. One of them is an improvement means for increasing the thermal energy during printing to obtain a clearer transfer density. However, in this method, thermal damage to the thermal transfer image-receiving sheet is large, and the ink ribbon dye layer and the dye-receiving layer of the thermal transfer image-receiving sheet of the material to be transferred are thermally fused, and further, the ink ribbon dye layer Problems such as the occurrence of so-called abnormal transfer, in which not only the dye but also the dye layer are transferred to the heat-sensitive transfer image-receiving sheet of the material to be transferred, have become prominent. In designing a thermal transfer image-receiving sheet used in these high-speed printers, consideration must be given to surface properties, particularly releasability, different from those of conventional thermal transfer image-receiving sheets when the printing speed is low.

従来より、感熱転写受像シートの表面性（離型性、凹凸等）を工夫して改良する試みは行われている（例えば、特許文献１〜７）。
特許文献１、２、３では、感熱転写受像シートの受容層に、離型剤としてポリエチレンワックス、アミドワックス、テフロン（登録商標）、ウレタン変性ワックス等のワックス類を添加することが記載されている。しかし、離型剤として、凹凸を制御する微粒子を感熱転写受像シートに添加することは記載されていない。
特許文献４、５では、感熱転写受像シートの受容層に有機系フィラーとしてスチレン樹脂や尿素−ホルマリン縮重合物樹脂等を含有させることが記載されている。しかし、ここでは熱転写画像の濃度を高めることが目的である。この当時、上述したプリンターの高速化による問題は顕著化しておらず、その結果、特許文献４、５では有機系フィラーの離型性の機能については明記されていない。
特許文献６では、無機フィラーを表面性の改質手段として用いているが、これは筆記性付与の観点であり、特定の無機フィラーを加えることによる離型性付与の機能について明記されていない。
一方で、銀塩写真業界では光沢度制御の観点から、微粒子を添加して表面に凹凸をつける検討が以前よりなされており、このような表面に凹凸をつける機能を有する微粒子を広くマット剤と称している。光沢制御の観点以外にも、表面の接着、摩擦制御などの観点で表面凹凸の制御の検討がマット剤を用いてなされており、具体的には、フィルム同士の張り付き、擦り傷、熱現像時のマット剤の変形、剥がれ落ち等が問題となっておりマット剤のさまざまな検討が行われている（例えば特許文献７）。しかしながら、このようなハロゲン化銀写真感光材料では、色素の転写で画像を形成するものでなく、転写シートと受像シートとの離型性を考慮する必要はない。しかも転写シートから受像シートへの転写時の転写阻害、転写ムラを全く考慮する必要がない。
なお、カラーフィルターなどの転写材料でもマット剤の使用が提案（特許文献８）されているが、転写層ではなく、バック層に使用するものである。 Conventionally, attempts have been made to devise and improve the surface properties (releasing properties, unevenness, etc.) of the thermal transfer image-receiving sheet (for example, Patent Documents 1 to 7).
Patent Documents 1, 2, and 3 describe that waxes such as polyethylene wax, amide wax, Teflon (registered trademark), and urethane-modified wax are added as a release agent to the receiving layer of the thermal transfer image-receiving sheet. . However, it is not described that fine particles for controlling unevenness are added to the heat-sensitive transfer image-receiving sheet as a release agent.
Patent Documents 4 and 5 describe that the receiving layer of the thermal transfer image-receiving sheet contains a styrene resin, a urea-formalin condensation polymer resin, or the like as an organic filler. However, the purpose here is to increase the density of the thermal transfer image. At this time, the problem due to the speeding up of the printer described above has not become significant, and as a result, Patent Documents 4 and 5 do not specify the release function of the organic filler.
In Patent Document 6, an inorganic filler is used as a surface property modifying means. However, this is from the viewpoint of imparting writability, and the function of imparting releasability by adding a specific inorganic filler is not specified.
On the other hand, in the silver salt photography industry, from the viewpoint of glossiness control, studies have been made to add irregularities to the surface by adding fine particles. It is called. In addition to gloss control, surface unevenness control has been studied from the viewpoint of surface adhesion, friction control, etc. using a matting agent. Specifically, adhesion between films, scratches, and heat development There are problems with deformation and peeling off of the matting agent, and various studies of the matting agent have been conducted (for example, Patent Document 7). However, such a silver halide photographic light-sensitive material does not form an image by transfer of a dye, and it is not necessary to consider releasability between the transfer sheet and the image receiving sheet. In addition, there is no need to consider transfer inhibition or transfer unevenness during transfer from the transfer sheet to the image receiving sheet.
Note that the use of a matting agent has also been proposed for a transfer material such as a color filter (Patent Document 8), but it is used for a back layer, not a transfer layer.

特許第２５７２７６９号公報Japanese Patent No. 2572769 特許第２８５４３１９号公報Japanese Patent No. 2854319 特開２００５−２３８７４８号公報JP 2005-238748 A 特開昭５９−２１４６９６号公報JP 59-214696 A 特開昭６２−１０５６８９号公報JP 62-105689 A 特許第２８７２７８１号公報Japanese Patent No. 2872781 特開２００５−７０２５１号公報Japanese Patent Laid-Open No. 2005-70251 特開２００６−４８０２４号公報JP 2006-48024 A 「情報記録（ハードコピー）とその材料の新展開」，(株)東レリサーチセンター発行，１９９３年，ｐ．２４１−２８５“New development of information recording (hard copy) and its materials”, published by Toray Research Center, Inc., 1993, p. 241-285 「プリンター材料の開発」，(株)シーエムシー発行，１９９５年，ｐ．１８０“Development of Printer Materials”, issued by CMC Co., Ltd., 1995, p. 180

本発明は、高速プリンター適性を付与した感熱転写受像シートおよびその製造方法を提供することである。特に、離型性に優れ、画像の粒状性が高く、転写ムラがない等の画質の高い感熱転写受像シートおよびその製造方法を提供することにある。   An object of the present invention is to provide a thermal transfer image-receiving sheet imparted with high-speed printer suitability and a method for producing the same. In particular, it is to provide a heat-sensitive transfer image-receiving sheet having high image quality such as excellent releasability, high image graininess, and no transfer unevenness, and a method for producing the same.

本発明者らは鋭意検討を重ねた結果、上記課題は下記の手段により達成された。
（１）支持体上に、マット剤を含む少なくとも１層の受容層を有し、該マット剤が、粒径１〜１０μｍであって、かつ有機化合物を含有する微粒子であることを特徴とする感熱転写受像シート。
（２）前記マット剤のガラス転移温度が９０℃以上であることを特徴とする（１）に記載の感熱転写受像シート。
（３）前記マット剤のガラス転移温度が１３０℃以上であることを特徴とする（１）に記載の感熱転写受像シート。
（４）前記マット剤の分解温度が２００℃以上であることを特徴とする（１）に記載の感熱転写受像シート。
（５）前記マット剤がメラミン樹脂を含有することを特徴とする（１）〜（４）のいずれか１項に記載の感熱転写受像シート。
（６）前記受容層と支持体の間に少なくとも１層の中空ポリマーラテックス及び水溶性ポリマーを含有する断熱層を有することを特徴とする（１）〜（５）のいずれか１項に記載の感熱転写受像シート。
（７）前記受容層が、少なくとも１種のポリマーラテックスを含有することを特徴とする（１）〜（６）のいずれか１項に記載の感熱転写受像シート。
（８）前記（１）〜（７）のいずれか１項に記載の感熱転写受像シートの製造工程において、前記受容層とこれに隣接する層とを同時に塗布して製造することを特徴とする感熱転写受像シートの製造方法。
（９）前記隣接層が断熱層であることを特徴とする（８）に記載の感熱転写受像シートの製造方法。 As a result of intensive studies, the present inventors have achieved the above-described problem by the following means.
(1) The support has at least one receiving layer containing a matting agent, and the matting agent is a fine particle having a particle diameter of 1 to 10 μm and containing an organic compound. Thermal transfer image-receiving sheet.
(2) The heat-sensitive transfer image-receiving sheet as described in (1), wherein the matting agent has a glass transition temperature of 90 ° C. or higher.
(3) The heat-sensitive transfer image-receiving sheet as described in (1), wherein the matting agent has a glass transition temperature of 130 ° C. or higher.
(4) The thermal transfer image-receiving sheet as described in (1), wherein the decomposition temperature of the matting agent is 200 ° C. or higher.
(5) The thermal transfer image-receiving sheet according to any one of (1) to (4), wherein the matting agent contains a melamine resin.
(6) It has a heat insulation layer containing at least 1 layer of hollow polymer latex and water-soluble polymer between the said receiving layer and a support body, It is any one of (1)-(5) characterized by the above-mentioned. Thermal transfer image-receiving sheet.
(7) The heat-sensitive transfer image-receiving sheet according to any one of (1) to (6), wherein the receptor layer contains at least one polymer latex.
(8) In the manufacturing process of the heat-sensitive transfer image-receiving sheet according to any one of (1) to (7), the receiving layer and a layer adjacent to the receiving layer are simultaneously coated and manufactured. A method for producing a thermal transfer image-receiving sheet.
(9) The method for producing a thermal transfer image-receiving sheet as described in (8), wherein the adjacent layer is a heat insulating layer.

本発明により、離型性が優れた高品位な画質（画像の粒状性が高く、転写ムラが少ない）が得られる感熱転写受像シートを提供できる。特に、高速プリンターに対する適性が向上した感熱転写受像シートを提供することが可能となる。   According to the present invention, it is possible to provide a heat-sensitive transfer image-receiving sheet capable of obtaining high-quality image quality (high image graininess and little transfer unevenness) with excellent releasability. In particular, it is possible to provide a thermal transfer image-receiving sheet with improved suitability for a high-speed printer.

まず、本発明の感熱転写受像シートについて説明する。
本発明の感熱転写受像シート（以後、受像シートとも称す）は、少なくとも支持体上に染料受容層（受容層）を有する。本発明においては、該受容層と支持体との間に少なくとも１層の断熱層を形成することが特に好ましい。受容層と支持体との間には下地層が形成されていることが好ましく、例えば白地調整層、帯電調節層、接着層、プライマー層が形成される。また、下地層と支持体との間には断熱層が形成されていることが好ましい。さらに、支持体の裏面側にはカール調整層、筆記層、帯電調整層が形成されていることが好ましい。各層の塗布は、ロールコート、バーコート、グラビアコート、グラビアリバースコート、ダイコート、スライドコート、カーテンコート等の一般的な方法で行われるが、スライドコート、カーテンコート等の複数の層を同時重層塗布できる方法が好ましい。 First, the thermal transfer image receiving sheet of the present invention will be described.
The heat-sensitive transfer image-receiving sheet of the present invention (hereinafter also referred to as image-receiving sheet) has a dye-receiving layer (receiving layer) on at least a support. In the present invention, it is particularly preferable to form at least one heat insulating layer between the receptor layer and the support. A base layer is preferably formed between the receptor layer and the support. For example, a white background adjustment layer, a charge adjustment layer, an adhesive layer, and a primer layer are formed. Moreover, it is preferable that the heat insulation layer is formed between the base layer and the support body. Furthermore, a curl adjusting layer, a writing layer, and a charge adjusting layer are preferably formed on the back side of the support. Each layer is applied by a general method such as roll coating, bar coating, gravure coating, gravure reverse coating, die coating, slide coating, curtain coating, etc., but multiple layers such as slide coating, curtain coating, etc. are applied simultaneously in multiple layers. Preferred is a method that can

（受容層）
受容層は、インクシートから移行してくる染料を受容し、形成された画像を維持する役割を果たす。本発明に用いられる受像シートは、少なくとも染料を受容し得る熱可塑性の受容ポリマーを有する少なくとも１層の受容層を有する。
受容ポリマーはポリマーラテックスとして水溶性の分散媒中に分散して使用することが好ましい。更に、受容層は該ポリマーラテックス以外に水溶性ポリマーを含有することが好ましい。ポリマーラテックスと水溶性ポリマーとを含有させることで、染料に染着し難い水溶性ポリマーをポリマーラテックス間に存在させ、ポリマーラテックスに染着した染料が拡散するのを防止することができ、この結果、受容層の経時による鮮鋭性の変化を少なくし、転写画像の経時変化が小さい記録画像を形成することができる。
受容層は、受容ポリマーのポリマーラテックス以外にも、例えば、膜の弾性率を調整するなどの目的で、他の機能を有するポリマーラテックスも併用して用いることができる。 (Receptive layer)
The receiving layer serves to receive the dye transferred from the ink sheet and maintain the formed image. The image-receiving sheet used in the present invention has at least one receiving layer having a thermoplastic receiving polymer capable of receiving at least a dye.
The accepting polymer is preferably used as a polymer latex dispersed in a water-soluble dispersion medium. Furthermore, the receiving layer preferably contains a water-soluble polymer in addition to the polymer latex. By containing a polymer latex and a water-soluble polymer, a water-soluble polymer that is difficult to be dyed on the dye can be present between the polymer latexes, and the dye dyed on the polymer latex can be prevented from diffusing. Thus, it is possible to reduce a change in sharpness of the receiving layer with time and to form a recorded image with a small change in transfer image with time.
For the receiving layer, in addition to the polymer latex of the receiving polymer, for example, a polymer latex having other functions can be used in combination for the purpose of adjusting the elastic modulus of the film.

＜ポリマーラテックス＞
本発明に用いられるポリマーラテックスについて説明する。
一般的なポリマーラテックスは次に示すような文献に記載されている。奥田平，稲垣寛編集，「合成樹脂エマルジョン」，高分子刊行会発行（1978年）、杉村孝明，片岡靖男，鈴木聡一，笠原啓司編集，「合成ラテックスの応用」，高分子刊行会発行（1993年）、室井宗一著，「合成ラテックスの化学」，高分子刊行会発行（1970年）、三代澤良明監修，「水性コーティング材料の開発と応用」，シーエムシー出版（2004年）および特開昭64-538号公報。
本発明の感熱転写受像シートにおいて受容層に用いうるポリマーラテックスは、水不溶な疎水性ポリマーが微細な粒子として水溶性の分散媒中に分散したものである。ポリマーラテックスとしては、異なる数種類のポリマーラテックスを併用してもよいが、本発明で使用するポリマーラッテックスは、特に制限はないが、塩化ビニル類、アクリレート類、ポリエステル類、ゴム類（例えばＳＢＲ樹脂）、ポリウレタン類、ポリ塩化ビニル類、ポリ酢酸ビニル類、ポリ塩化ビニリデン類、ポリオレフィン類等の疎水性ポリマーを好ましく用いることができる。より好ましくは塩化ビニル類、アクリルレート類、ゴム類（例えばＳＢＲ類）、ポリ酢酸ビニル類であり、さらに好ましくは塩化ビニル類である。 <Polymer latex>
The polymer latex used in the present invention will be described.
Common polymer latices are described in the following literature. Tadashi Okuda, Hiroshi Inagaki, "Synthetic Resin Emulsion", published by Polymer Publishing Association (1978), Takaaki Sugimura, Akio Kataoka, Junichi Suzuki, Keiji Kasahara, "Application of Synthetic Latex", Published by Polymer Publishing Society (1993) 1), Soichi Muroi, “Chemistry of Synthetic Latex”, published by Kobunshi Publishing Co., Ltd. (1970), supervised by Yoshiaki Mitsuzawa, “Development and Application of Water-Based Coating Materials”, CM Publishing (2004) and JP Sho 64-538.
The polymer latex that can be used in the receiving layer in the heat-sensitive transfer image-receiving sheet of the present invention is obtained by dispersing a water-insoluble hydrophobic polymer as fine particles in a water-soluble dispersion medium. As the polymer latex, several different types of polymer latex may be used in combination, but the polymer latex used in the present invention is not particularly limited, but vinyl chlorides, acrylates, polyesters, rubbers (for example, SBR resin) ), Hydrophobic polymers such as polyurethanes, polyvinyl chlorides, polyvinyl acetates, polyvinylidene chlorides and polyolefins can be preferably used. More preferred are vinyl chlorides, acrylates, rubbers (for example, SBRs) and polyvinyl acetates, and even more preferred are vinyl chlorides.

塩化ビニルをモノマー単位として含むラテックスの合成において、塩化ビニルモノマーと併用して用いる他のモノマーとしては、特に制限はなく、通常のラジカル重合又はイオン重合法で重合可能なものでは、下記に示すモノマー群（ａ）〜（ｊ）を好適に用いることができる。これらモノマーを独立かつ自由に組み合わせて選択し、ポリマーラテックスを合成することができる。   In the synthesis of latex containing vinyl chloride as a monomer unit, other monomers used in combination with the vinyl chloride monomer are not particularly limited, and monomers that can be polymerized by a normal radical polymerization or ionic polymerization method are shown below. Groups (a) to (j) can be preferably used. Polymer monomers can be synthesized by selecting these monomers independently and freely in combination.

−モノマー群（ａ）〜（ｊ）−
（ａ） 共役ジエン類：１，３−ペンタジエン、イソプレン、１−フェニル−１，３−ブタジエン、１−α−ナフチル−１，３−ブタジエン、１−β−ナフチル−１，３−ブタジエン、シクロペンタジエン等。
（ｂ） オレフィン類：エチレン、プロピレン、塩化ビニル、塩化ビニリデン、６−ヒドロキシ−１−ヘキセン、４−ペンテン酸、８−ノネン酸メチル、ビニルスルホン酸、トリメチルビニルシラン、トリメトキシビニルシラン、１，４−ジビニルシクロヘキサン、１，２，５−トリビニルシクロヘキサン等。 -Monomer group (a)-(j)-
(A) Conjugated dienes: 1,3-pentadiene, isoprene, 1-phenyl-1,3-butadiene, 1-α-naphthyl-1,3-butadiene, 1-β-naphthyl-1,3-butadiene, cyclo Pentadiene and the like.
(B) Olefins: ethylene, propylene, vinyl chloride, vinylidene chloride, 6-hydroxy-1-hexene, 4-pentenoic acid, methyl 8-nonenoate, vinylsulfonic acid, trimethylvinylsilane, trimethoxyvinylsilane, 1,4- Divinylcyclohexane, 1,2,5-trivinylcyclohexane, etc.

（ｃ） α，β−不飽和カルボン酸エステル類：アルキルアクリレート（例えば、メチルアクリレート、エチルアクリレート、ブチルアクリレート、シクロヘキシルアクリレート、２−エチルヘキシルアクリレート、ドデシルアクリレート等）、置換アルキルアクリレート（例えば、２−クロロエチルアクリレート、ベンジルアクリレート、２−シアノエチルアクリレート等）、アルキルメタクリレート（例えば、メチルメタクリレート、ブチルメタクリ−レート、２−エチルヘキシルメタクリレート、ドデシルメタクリレート等）、置換アルキルメタクリレート（例えば、２−ヒドロキシエチルメタクリレート、グリシジルメタクリレート、グリセリンモノメタクリレート、２−アセトキシエチルメタクリレート、テトラヒドロフルフリルメタクリレート、２−メトキシエチルメタクリレート、ポリプロピレングリコールモノメタクリレート（ポリオキシプロピレンの付加モル数＝２ないし１００のもの）、３−Ｎ，Ｎ−ジメチルアミノプロピルメタクリレート、クロロ−３−Ｎ，Ｎ，Ｎ−トリメチルアンモニオプロピルメタクリレート、（２−カルボキシエチルメタクリレート、３−スルホプロピルメタクリレート、４−オキシスルホブチルメタクリレート、３−トリメトキシシリルプロピルメタクリレート、アリルメタクリレート、２−イソシアナトエチルメタクリレート等）、不飽和ジカルボン酸の誘導体（例えば、マレイン酸モノブチル、マレイン酸ジメチル、イタコン酸モノメチル、イタコン酸ジブチル等）、多官能エステル類（例えばエチレングリコールジアクリレート、エチレングリコールジメタクリレート、１，４−シクロヘキサンジアクリレート、ペンタエリスリトールテトラメタクリレート、ペンタエリスリトールトリアクリレート、トリメチロールプロパントリアクリレート、トリメチロールエタントリアクリレート、ジペンタエリスリトールペンタメタクリレート、ペンタエリスリトールヘキサアクリレート、１，２，４−シクロヘキサンテトラメタクリレート等）。   (C) α, β-unsaturated carboxylic acid esters: alkyl acrylate (eg, methyl acrylate, ethyl acrylate, butyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, dodecyl acrylate, etc.), substituted alkyl acrylate (eg, 2-chloro Ethyl acrylate, benzyl acrylate, 2-cyanoethyl acrylate, etc.), alkyl methacrylate (eg, methyl methacrylate, butyl methacrylate, 2-ethylhexyl methacrylate, dodecyl methacrylate, etc.), substituted alkyl methacrylate (eg, 2-hydroxyethyl methacrylate, glycidyl methacrylate) Glycerin monomethacrylate, 2-acetoxyethyl methacrylate, tetrahydrofurfurylme Chryrate, 2-methoxyethyl methacrylate, polypropylene glycol monomethacrylate (polyoxypropylene added mole number = 2 to 100), 3-N, N-dimethylaminopropyl methacrylate, chloro-3-N, N, N-trimethyl Ammoniopropyl methacrylate (2-carboxyethyl methacrylate, 3-sulfopropyl methacrylate, 4-oxysulfobutyl methacrylate, 3-trimethoxysilylpropyl methacrylate, allyl methacrylate, 2-isocyanatoethyl methacrylate, etc.), unsaturated dicarboxylic acid Derivatives (eg, monobutyl maleate, dimethyl maleate, monomethyl itaconate, dibutyl itaconate, etc.), polyfunctional esters (eg, ethylene glycol diacrylate) , Ethylene glycol dimethacrylate, 1,4-cyclohexanediacrylate, pentaerythritol tetramethacrylate, pentaerythritol triacrylate, trimethylolpropane triacrylate, trimethylolethane triacrylate, dipentaerythritol pentamethacrylate, pentaerythritol hexaacrylate, 1,2 , 4-cyclohexanetetramethacrylate, etc.).

（ｄ） α，β−不飽和カルボン酸のアミド類：例えばアクリルアミド、メタクリルアミド、Ｎ−メチルアクリルアミド、Ｎ，Ｎ−ジメチルアクリルアミド、Ｎ−メチル−Ｎ−ヒドロキシエチルメタクリルアミド、Ｎ−ｔｅｒｔ−ブチルアクリルアミド、Ｎ−ｔｅｒｔ−オクチルメタクリルアミド、Ｎ−シクロヘキシルアクリルアミド、Ｎ−フェニルアクリルアミド、Ｎ−（２−アセトアセトキシエチル）アクリルアミド、Ｎ−アクリロイルモルフォリン、ジアセトンアクリルアミド、イタコン酸ジアミド、Ｎ−メチルマレイミド、２−アクリルアミド−メチルプロパンスルホン酸、メチレンビスアクリルアミド、ジメタクリロイルピペラジン等。
（ｅ） 不飽和ニトリル類：アクリロニトリル、メタクリロニトリル等。
（ｆ） スチレン及びその誘導体：スチレン、ビニルトルエン、ｐ−ｔｅｒｔ−ブチルスチレン、ビニル安息香酸、ビニル安息香酸メチル、α−メチルスチレン、ｐ−クロロメチルスチレン、ビニルナフタレン、ｐ−ヒドロキシメチルスチレン、ｐ−スチレンスルホン酸ナトリウム塩、ｐ−スチレンスルフィン酸カリウム塩、ｐ−アミノメチルスチレン、１，４−ジビニルベンゼン等。
（ｇ） ビニルエーテル類：メチルビニルエーテル、ブチルビニルエーテル、メトキシエチルビニルエーテル等。
（ｈ） ビニルエステル類：酢酸ビニル、プロピオン酸ビニル、安息香酸ビニル、サリチル酸ビニルクロロ酢酸ビニル等。
（ｉ） α，β−不飽和カルボン酸及びその塩類：アクリル酸、メタクリル酸、イタコン酸、マレイン酸、アクリル酸ナトリウム、メタクリル酸アンモニウム、イタコン酸カリウム等。
（ｊ） その他の重合性単量体：Ｎ−ビニルイミダゾール、４−ビニルピリジン、Ｎ−ビニルピロリドン、２−ビニルオキサゾリン、２−イソプロペニルオキサゾリン、ジビニルスルホン等。 (D) Amides of α, β-unsaturated carboxylic acid: for example, acrylamide, methacrylamide, N-methylacrylamide, N, N-dimethylacrylamide, N-methyl-N-hydroxyethylmethacrylamide, N-tert-butylacrylamide N-tert-octylmethacrylamide, N-cyclohexylacrylamide, N-phenylacrylamide, N- (2-acetoacetoxyethyl) acrylamide, N-acryloylmorpholine, diacetone acrylamide, itaconic acid diamide, N-methylmaleimide, 2 -Acrylamide-methylpropane sulfonic acid, methylene bisacrylamide, dimethacryloyl piperazine and the like.
(E) Unsaturated nitriles: acrylonitrile, methacrylonitrile and the like.
(F) Styrene and its derivatives: styrene, vinyl toluene, p-tert-butyl styrene, vinyl benzoic acid, methyl vinyl benzoate, α-methyl styrene, p-chloromethyl styrene, vinyl naphthalene, p-hydroxymethyl styrene, p -Styrene sulfonic acid sodium salt, p-styrene sulfinic acid potassium salt, p-aminomethylstyrene, 1,4-divinylbenzene and the like.
(G) Vinyl ethers: methyl vinyl ether, butyl vinyl ether, methoxyethyl vinyl ether, and the like.
(H) Vinyl esters: vinyl acetate, vinyl propionate, vinyl benzoate, vinyl salicylate, vinyl chloroacetate, and the like.
(I) α, β-unsaturated carboxylic acid and salts thereof: acrylic acid, methacrylic acid, itaconic acid, maleic acid, sodium acrylate, ammonium methacrylate, potassium itaconate and the like.
(J) Other polymerizable monomers: N-vinylimidazole, 4-vinylpyridine, N-vinylpyrrolidone, 2-vinyloxazoline, 2-isopropenyloxazoline, divinylsulfone, and the like.

これらのポリマーは直鎖のポリマーでも枝分かれしたポリマーでもまた架橋されたポリマーでもよい。また、コポリマーの場合はランダムコポリマーでも、ブロックコポリマーでもよい。これらポリマーの分子量は数平均分子量で5000〜1000000、好ましくは10000〜500000がよい。分子量が小さすぎるものはラテックスを含有する層の力学強度が不十分であり、大きすぎるものは成膜性が悪く好ましくない。また、架橋性のポリマーラテックスも好ましく使用される。   These polymers may be linear polymers, branched polymers, or crosslinked polymers. In the case of a copolymer, it may be a random copolymer or a block copolymer. These polymers have a number average molecular weight of 5,000 to 100,000, preferably 10,000 to 500,000. If the molecular weight is too small, the mechanical strength of the layer containing the latex is insufficient, and if it is too large, the film formability is poor and this is not preferred. A crosslinkable polymer latex is also preferably used.

塩化ビニルから得られる繰り返し単位を含むポリマーラテックス（塩化ビニル類ラテックス）と併用して使用される、他の構造を有したポリマーラテックスは特に制限はないが、アクリル系ポリマー、ポリエステル類、ゴム類（例えばＳＢＲ樹脂）、ポリウレタン類、ポリ塩化ビニル類、ポリ酢酸ビニル類、ポリ塩化ビニリデン類、ポリオレフィン類等の疎水性ポリマーを好ましく用いることができる。これらポリマーとしては直鎖のポリマーでも枝分かれしたポリマーでもまた架橋されたポリマーでもよいし、単一のモノマーが重合したいわゆるホモポリマーでもよいし、２種類以上のモノマーが重合したコポリマーでもよい。コポリマーの場合はランダムコポリマーでも、ブロックコポリマーでもよい。これらポリマーの分子量は数平均分子量で５０００〜１００００００、好ましくは１００００〜５０００００がよい。分子量が小さすぎるものはラテックスを含有する層の力学強度が不十分であり、大きすぎるものは成膜性が悪く好ましくない。また、架橋性のポリマーラテックスも好ましく使用される。   There are no particular restrictions on polymer latexes having other structures that are used in combination with polymer latexes containing vinyl chloride-containing repeating units (vinyl chloride latexes), but acrylic polymers, polyesters, rubbers ( For example, hydrophobic polymers such as SBR resin), polyurethanes, polyvinyl chlorides, polyvinyl acetates, polyvinylidene chlorides and polyolefins can be preferably used. These polymers may be linear polymers, branched polymers, crosslinked polymers, so-called homopolymers obtained by polymerizing a single monomer, or copolymers obtained by polymerizing two or more types of monomers. In the case of a copolymer, it may be a random copolymer or a block copolymer. These polymers have a number average molecular weight of 5,000 to 1,000,000, preferably 10,000 to 500,000. If the molecular weight is too small, the mechanical strength of the layer containing the latex is insufficient, and if it is too large, the film formability is poor and this is not preferred. A crosslinkable polymer latex is also preferably used.

ポリマーラテックスとしては通常の均一構造のポリマーラテックス以外、いわゆるコア／シェル型のラテックスでもよい。この場合コアとシェルはガラス転移温度を変えると好ましい場合がある。本発明に用いられるポリマーラテックスのガラス転移温度は、−３０℃〜１００℃が好ましく、０℃〜８０℃がより好ましく、１０℃〜７０℃がさらに好ましく、１５℃〜６０℃が特に好ましい。   The polymer latex may be a so-called core / shell type latex in addition to a normal uniform polymer latex. In this case, it may be preferable to change the glass transition temperature between the core and the shell. The glass transition temperature of the polymer latex used in the present invention is preferably −30 ° C. to 100 ° C., more preferably 0 ° C. to 80 ° C., further preferably 10 ° C. to 70 ° C., and particularly preferably 15 ° C. to 60 ° C.

このガラス転移温度（Ｔｇ）は下記式で計算することができる。
1／Tg＝Σ(Xi／Tgi)
ここでは、ポリマーはｉ＝１からｎまでのｎ個のモノマー成分が共重合しているとする。Xiはi番目のモノマーの質量分率（ΣXi=1）、Tgiはi番目のモノマーの単独重合体のガ
ラス転移温度（絶対温度）である。ただしΣはｉ＝１からｎまでの和をとる。尚、各モノマーの単独重合体ガラス転移温度の値（Tgi）は「Polymer Handbook(3rd Edition)」(J.Brandrup，E.H.Immergut著(Wiley-Interscience、1989))の値を採用できる。 This glass transition temperature (Tg) can be calculated by the following formula.
1 / Tg = Σ (Xi / Tgi)
Here, it is assumed that n monomer components from i = 1 to n are copolymerized in the polymer. Xi is the mass fraction of the i-th monomer (ΣXi = 1), and Tgi is the glass transition temperature (absolute temperature) of the homopolymer of the i-th monomer. However, Σ is the sum from i = 1 to n. In addition, the value of the homopolymer glass transition temperature (Tgi) of each monomer can adopt the value of “Polymer Handbook (3rd Edition)” (J. Brandrup, EHImmergut (Wiley-Interscience, 1989)).

本発明に用いられる塩化ビニルをモノマー単位含むラテックスと併用して使用される他の構造を有したポリマーラテックスは、加工脆性と画像保存性の点でガラス転移温度（Ｔｇ）が−３０℃〜１００℃の範囲のものが好ましく、より好ましくは０℃〜８０℃の範囲、さらに好ましくは２０℃〜７０℃の範囲である。バインダーとして２種以上のポリマーをブレンドして用いることも可能で、この場合、組成分を考慮し加重平均したＴｇが上記の範囲に入ることが好ましい。また、相分離した場合やコア−シェル構造を有する場合には加重平均したＴｇが上記の範囲に入ることが好ましい。   The polymer latex having another structure used in combination with the latex containing the monomer unit of vinyl chloride used in the present invention has a glass transition temperature (Tg) of −30 ° C. to 100 in terms of processing brittleness and image storage stability. The thing of the range of ° C is preferable, More preferably, it is the range of 0 degreeC-80 degreeC, More preferably, it is the range of 20 degreeC-70 degreeC. It is also possible to use a blend of two or more polymers as the binder, and in this case, it is preferable that the weighted average Tg in consideration of the composition falls within the above range. Moreover, when phase-separating or having a core-shell structure, the weighted average Tg is preferably within the above range.

ポリマーラテックスの最低造膜温度（ＭＦＴ）は−３０℃〜９０℃、より好ましくは０℃〜７０℃程度が好ましい。最低造膜温度をコントロールするために造膜助剤を添加してもよい。造膜助剤は一時可塑剤ともよばれポリマーラテックスの最低造膜温度を低下させる有機化合物(通常有機溶剤)で、例えば室井宗一著，「合成ラテックスの化学」，高分子刊行会発行（１９７０年）に記載されている。好ましい造膜助剤は以下の化合物であるが、本発明で用い得る化合物は以下の具体例に限定されるものではない。
Ｚ−１：ベンジルアルコール
Ｚ−２：２，２，４−トリメチルペンタンジオール−１，３−モノイソブチレート
Ｚ−３：２−ジメチルアミノエタノール
Ｚ−４：ジエチレングルコール The minimum film-forming temperature (MFT) of the polymer latex is preferably −30 ° C. to 90 ° C., more preferably about 0 ° C. to 70 ° C. A film-forming auxiliary may be added to control the minimum film-forming temperature. A film-forming aid, also called a temporary plasticizer, is an organic compound (usually an organic solvent) that lowers the minimum film-forming temperature of polymer latex. For example, Soichi Muroi, “Synthetic Latex Chemistry”, published by Kobunshi Shuppankai (1970) )It is described in. Preferred film-forming aids are the following compounds, but the compounds that can be used in the present invention are not limited to the following specific examples.
Z-1: benzyl alcohol Z-2: 2,2,4-trimethylpentanediol-1,3-monoisobutyrate Z-3: 2-dimethylaminoethanol Z-4: diethylene glycol

本発明で使用できる塩化ビニルから得られる繰り返し単位を含むポリマーラテックス（塩化ビニル類ラテックス）は市販もされており、以下のようなポリマーが利用できる。例としては、日本ゼオン(株)製G351、G576、日信化学工業(株)製ビニブラン240、270、277、375、386、609、550、601、602、630、660、671、683、680、680S、681N、685R、277、380、381、410、430、432、860、863、865、867、900、900GT、938、950などが挙げられる（いずれも商品名）。   Polymer latex (vinyl chloride latex) containing a repeating unit obtained from vinyl chloride that can be used in the present invention is commercially available, and the following polymers can be used. Examples include G351 and G576 manufactured by Nippon Zeon Co., Ltd., Vinibrand 240, 270, 277, 375, 386, 609, 550, 601, 602, 630, 660, 671, 683, 680 manufactured by Nissin Chemical Industry Co., Ltd. 680S, 681N, 685R, 277, 380, 381, 410, 430, 432, 860, 863, 865, 867, 900, 900GT, 938, 950, etc. (all are trade names).

塩化ビニルから得られる繰り返し単位を含むポリマーラテックス（塩化ビニル類ラテックス）と併用可能な、他の構造を有するポリマーラテックスも市販されており、併用して利用できる。アクリル系ポリマーの例としては、ダイセル化学工業（株）製セビアンＡ−４６３５，４７１８，４６０１、日本ゼオン（株）製Ｎｉｐｏｌ Ｌｘ８１１、８１４、８２１、８２０、８５５（Ｐ−１７：Ｔｇ３６℃）、８５７ｘ２（Ｐ−１８：Ｔｇ４３℃）、大日本インキ化学（株）製Ｖｏｎｃｏａｔ Ｒ３３７０（Ｐ−１９：Ｔｇ２５℃）、４２８０（Ｐ−２０：Ｔｇ１５℃）、日本純薬（株）製ジュリマーＥＴ−４１０（Ｐ−２１：Ｔｇ４４℃）、ＪＳＲ（株）製ＡＥ１１６（Ｐ−２２：Ｔｇ５０℃）、ＡＥ１１９（Ｐ−２３：Ｔｇ５５℃）、ＡＥ１２１（Ｐ−２４：Ｔｇ５８℃）、ＡＥ１２５（Ｐ−２５：Ｔｇ６０℃）、ＡＥ１３４（Ｐ−２６：Ｔｇ４８℃）、ＡＥ１３７（Ｐ−２７：Ｔｇ４８℃）、ＡＥ１４０（Ｐ−２８：Ｔｇ５３℃）、ＡＥ１７３（Ｐ−２９：Ｔｇ６０℃）、東亞合成（株）製アロンＡ−１０４（Ｐ−３０：Ｔｇ４５℃）、高松油脂（株）製ＮＳ−６００Ｘ、ＮＳ−６２０Ｘ、日信化学工業（株）製ビニブラン２５８０、２５８３、２６４１、２７７０、２７７０Ｈ、２６３５、２８８６、５２０２Ｃ、２７０６などが挙げられる（いずれも商品名）。   Polymer latexes having other structures that can be used in combination with a polymer latex containing a repeating unit obtained from vinyl chloride (vinyl chloride latex) are also commercially available and can be used in combination. Examples of the acrylic polymer include Sebian A-4635, 4718, 4601 manufactured by Daicel Chemical Industries, Ltd., Nipol Lx811, 814, 821, 820, 855 manufactured by Nippon Zeon Co., Ltd. (P-17: Tg 36 ° C.), 857 × 2 (P-18: Tg 43 ° C.), Voncoat R3370 (P-19: Tg 25 ° C.), 4280 (P-20: Tg 15 ° C.) manufactured by Dainippon Ink & Chemicals, Jurimer ET-410 (manufactured by Nippon Pure Chemical Co., Ltd.) P-21: Tg44 ° C), AE116 (P-22: Tg50 ° C) manufactured by JSR Corporation, AE119 (P-23: Tg55 ° C), AE121 (P-24: Tg58 ° C), AE125 (P-25: Tg60) ° C), AE134 (P-26: Tg48 ° C), AE137 (P-27: Tg48 ° C), AE140 (P-28: Tg53 ° C) ), AE173 (P-29: Tg 60 ° C.), Toagosei Co., Ltd. Aron A-104 (P-30: Tg 45 ° C.), Takamatsu Yushi Co., Ltd. NS-600X, NS-620X, Nissin Chemical Industry ( Vinibrand 2580, 2583, 2641, 2770, 2770H, 2635, 2886, 5202C, 2706, etc. manufactured by Co., Ltd. (all are trade names).

ポリエステル類の例としては、大日本インキ化学（株）製ＦＩＮＥＴＥＸ ＥＳ６５０、６１１、６７５、８５０、イーストマンケミカル製ＷＤ−ｓｉｚｅ、ＷＭＳ、高松油脂（株）製Ａ−１１０、Ａ−１１５ＧＥ、Ａ−１２０、Ａ−１２１、Ａ−１２４ＧＰ、Ａ−１２４Ｓ、Ａ−１６０Ｐ、Ａ−２１０、Ａ−２１５ＧＥ、Ａ−５１０、Ａ−５１３Ｅ、Ａ−５１５ＧＥ、Ａ−５２０、Ａ−６１０、Ａ−６１３、Ａ−６１５ＧＥ、Ａ−６２０、ＷＡＣ−１０、ＷＡＣ−１５、ＷＡＣ−１７ＸＣ、ＷＡＣ−２０、Ｓ−１１０、Ｓ−１１０ＥＡ、Ｓ−１１１ＳＬ、Ｓ−１２０、Ｓ−１４０、Ｓ−１４０Ａ、Ｓ−２５０、Ｓ−２５２Ｇ、Ｓ−２５０Ｓ、Ｓ−３２０、Ｓ−６８０、ＤＮＳ−６３Ｐ、ＮＳ−１２２Ｌ、ＮＳ−１２２ＬＸ、ＮＳ−２４４ＬＸ、ＮＳ−１４０Ｌ、ＮＳ−１４１ＬＸ、ＮＳ−２８２ＬＸ、東亞合成（株）製アロンメルトＰＥＳ−１０００シリーズ、ＰＥＳ−２０００シリーズ、東洋紡（株）製バイロナールＭＤ−１１００、ＭＤ−１２００、ＭＤ−１２２０、ＭＤ−１２４５、ＭＤ−１２５０、ＭＤ−１３３５、ＭＤ−１４００、ＭＤ−１４８０、ＭＤ−１５００、ＭＤ−１９３０、ＭＤ−１９８５、住友精化（株）製セポルジョンＥＳなどが挙げられる（いずれも商品名）。   Examples of polyesters include: FINETENX ES650, 611, 675, 850 manufactured by Dainippon Ink Chemical Co., Ltd., WD-size, WMS manufactured by Eastman Chemical, A-110, A-115GE manufactured by Takamatsu Yushi Co., Ltd., A- 120, A-121, A-124GP, A-124S, A-160P, A-210, A-215GE, A-510, A-513E, A-515GE, A-520, A-610, A-613, A-615GE, A-620, WAC-10, WAC-15, WAC-17XC, WAC-20, S-110, S-110EA, S-111SL, S-120, S-140, S-140A, S- 250, S-252G, S-250S, S-320, S-680, DNS-63P, NS-122L, NS-122LX, NS-244L NS-140L, NS-141LX, NS-282LX, Aronmelt PES-1000 series, PES-2000 series, Toyobo Co., Ltd. Bironal MD-1100, MD-1200, MD-1220, MD- 1245, MD-1250, MD-1335, MD-1400, MD-1480, MD-1500, MD-1930, MD-1985, Sephorjon ES manufactured by Sumitomo Seika Co., Ltd. (all are trade names).

ポリウレタン類の例としては、大日本インキ化学（株）製ＨＹＤＲＡＮ ＡＰ１０、ＡＰ２０、ＡＰ３０、ＡＰ４０、１０１Ｈ、Ｖｏｎｄｉｃ １３２０ＮＳ、１６１０ＮＳ、大日精化（株）製Ｄ−１０００、Ｄ−２０００、Ｄ−６０００、Ｄ−４０００、Ｄ−９０００、高松油脂（株）製ＮＳ−１５５Ｘ、ＮＳ−３１０Ａ、ＮＳ−３１０Ｘ、ＮＳ−３１１Ｘ、第一工業製薬（株）製エラストロンなどが挙げられる（いずれも商品名）。   Examples of polyurethanes include HYDRAN AP10, AP20, AP30, AP40, 101H, Vonic 1320NS, 1610NS, manufactured by Dainippon Ink and Chemicals, Inc., D-1000, D-2000, D-6000, manufactured by Dainichi Seika Co., Ltd. Examples include D-4000, D-9000, NS-155X, NS-310A, NS-310X, NS-311X manufactured by Takamatsu Yushi Co., Ltd., and Elastron manufactured by Daiichi Kogyo Seiyaku Co., Ltd. (all trade names).

ゴム類の例としては、ＬＡＣＳＴＡＲ ７３１０Ｋ、３３０７Ｂ、４７００Ｈ、７１３２Ｃ（以上、大日本インキ化学（株）製）、Ｎｉｐｏｌ Ｌｘ４１６、ＬＸ４１０、ＬＸ４３０、ＬＸ４３５、ＬＸ１１０、ＬＸ４１５Ａ、ＬＸ４３８Ｃ、２５０７Ｈ、ＬＸ３０３Ａ、ＬＸ４０７ＢＰシリーズ、Ｖ１００４、ＭＨ５０５５（以上日本ゼオン（株）製）などが挙げられる（いずれも商品名）。   Examples of rubbers include LACSTAR 7310K, 3307B, 4700H, 7132C (manufactured by Dainippon Ink and Chemicals), Nipol Lx416, LX410, LX430, LX435, LX110, LX415A, LX438C, 2507H, LX303A, LX407BP series, V1004, MH5055 (manufactured by Nippon Zeon Co., Ltd.) and the like (all are trade names).

ポリオレフィン類の例としては、三井石油化学（株）製ケミパールＳ１２０、ＳＡ１００、Ｖ３００（Ｐ−４０：Ｔｇ８０℃）、大日本インキ化学（株）製Ｖｏｎｃｏａｔ ２８３０、２２１０、２９６０、住友精化（株）製ザイクセン、セポルジョンＧ、共重合ナイロン類の例としては、住友精化（株）製セポルジョンＰＡ、などが挙げられる（いずれも商品名）。   Examples of polyolefins include Chemipearl S120, SA100, V300 (P-40: Tg 80 ° C.) manufactured by Mitsui Petrochemical Co., Ltd., Voncoat 2830, 2210, 2960 manufactured by Dainippon Ink Chemical Co., Ltd., Sumitomo Seika Co., Ltd. Examples of Zyxen, Sepoljon G, and copolymerized nylons include Sepoljon PA manufactured by Sumitomo Seika Co., Ltd. (all are trade names).

ポリ酢酸ビニル類の例としては、日信化学工業（株）製ビニブラン１０８０、１０８２、１０８５Ｗ、１１０８Ｗ、１１０８Ｓ、１５６３Ｍ、１５６６、１５７０、１５８８Ｃ、Ａ２２Ｊ７−Ｆ２、１１２８Ｃ、１１３７、１１３８、Ａ２０Ｊ２、Ａ２３Ｊ１、Ａ２３Ｊ１、Ａ２３Ｋ１、Ａ２３Ｐ２Ｅ、Ａ６８Ｊ１Ｎ、１０８６Ａ、１０８６、１０８６Ｄ、１１０８Ｓ、１１８７、１２４１ＬＴ、１５８０Ｎ、１０８３、１５７１、１５７２、１５８１、４４６５、４４６６、４４６８Ｗ、４４６８Ｓ、４４７０、４４８５ＬＬ、４４９５ＬＬ、１０２３、１０４２、１０６０、１０６０Ｓ、１０８０Ｍ、１０８４Ｗ、１０８４Ｓ、１０９６、１５７０Ｋ、１０５０、１０５０Ｓ、３２９０、１０１７ＡＤ、１００２、１００６、１００８、１１０７Ｌ、１２２５、１２４５Ｌ、ＧＶ−６１７０、ＧＶ−６１８１、４４６８Ｗ、４４６８Ｓなどが挙げられる（いずれも商品名）。   Examples of the polyvinyl acetates include Nibsin Chemical Industry Co., Ltd. Vinibrand 1080, 1082, 1085W, 1108W, 1108S, 1563M, 1566, 1570, 1588C, A22J7-F2, 1128C, 1137, 1138, A20J2, A23J1, A23J1, A23K1, A23P2E, A68J1N, 1086A, 1086A, 1086D, 1108S, 1187, 1241LT, 1580N, 1083, 1571, 1572, 1581, 4465, 4466, 4468W, 4468S, 4470, 4485LL, 4495LL, 1023, 1042, 1060, 1060S, 1080M, 1084W, 1084S, 1096, 1570K, 1050, 1050S, 3290, 1017AD, 1002, 1006, 1008, 107L, 1225,1245L, GV-6170, GV-6181,4468W, such as 4468S, and the like (all trade names).

これらのポリマーラテックスは単独で用いてもよいし、必要に応じて２種以上ブレンドしてもよい。本発明の受容層において、塩化ビニルをモノマー単位として含むポリマーラテックス量は、受容層中の全固形分に対して５０％以上占めることが好ましく、７０％以上であることがさらに好ましい。   These polymer latexes may be used alone or in combination of two or more as required. In the receiving layer of the present invention, the amount of the polymer latex containing vinyl chloride as a monomer unit is preferably 50% or more, more preferably 70% or more, based on the total solid content in the receiving layer.

分散状態としてはポリマーが分散媒中に乳化されているもの、乳化重合されたもの、ミセル分散されたもの、あるいはポリマー分子中に部分的に親水的な構造を持ち分子鎖自身が分子状分散したものなどいずれでもよい。   As the dispersion state, the polymer is emulsified in a dispersion medium, the emulsion is polymerized, the micelle is dispersed, or the polymer molecule has a partially hydrophilic structure and the molecular chain itself is molecularly dispersed. Anything may be used.

本発明に用いられるポリマーラテックスは、溶液重合法、懸濁重合法、乳化重合法、分散重合法、アニオン重合法、カチオン重合等により容易に得ることができるが、ラテックスとして得られる乳化重合法が最も好ましい。また、ポリマーを溶液中で調製し、中和するか乳化剤を添加後に水を加え、強制的に撹拌により水分散体を調製する方法も好ましい。乳化重合法は、例えば、水、或いは、水と水に混和し得る有機溶媒（例えばメタノール、エタノール、アセトン等）との混合溶媒を分散媒とし、分散媒に対して５〜１５０質量％のモノマー混合物と、モノマー総量に対して乳化剤と重合開始剤を用い、３０〜１００℃程度、好ましくは６０〜９０℃で３〜２４時間、攪拌下重合させることにより行われる。分散媒、モノマー濃度、開始剤量、乳化剤量、分散剤量、反応温度、モノマー添加方法等の諸条件は、使用するモノマーの種類を考慮し、適宜設定される。また、必要に応じて分散剤を用いることが好ましい。   The polymer latex used in the present invention can be easily obtained by a solution polymerization method, a suspension polymerization method, an emulsion polymerization method, a dispersion polymerization method, an anionic polymerization method, a cationic polymerization or the like. Most preferred. Also preferred is a method of preparing a polymer in a solution and neutralizing or adding an emulsifier and then adding water and forcibly stirring to prepare an aqueous dispersion. In the emulsion polymerization method, for example, water or a mixed solvent of water and an organic solvent miscible with water (for example, methanol, ethanol, acetone, etc.) is used as a dispersion medium, and the monomer is 5 to 150% by mass with respect to the dispersion medium. Using the mixture and the total amount of monomers, an emulsifier and a polymerization initiator are used, and polymerization is carried out with stirring at about 30 to 100 ° C., preferably 60 to 90 ° C. for 3 to 24 hours. Various conditions such as the dispersion medium, the monomer concentration, the initiator amount, the emulsifier amount, the dispersant amount, the reaction temperature, and the monomer addition method are appropriately set in consideration of the type of monomer used. Moreover, it is preferable to use a dispersing agent as needed.

乳化重合法は、一般的には次に示す文献に従って行うことができる。奥田平，稲垣寛編集，「合成樹脂エマルジョン」，高分子刊行会発行（1978年）、杉村孝明，片岡靖男，鈴木聡一，笠原啓司編集，「合成ラテックスの応用」，高分子刊行会発行（1993年）、室井宗一著，「合成ラテックスの化学」，高分子刊行会発行（1970年）。本発明に用いられるポリマーラテックスを合成する乳化重合法において、一括重合法、モノマー（連続・分割）添加法、エマルジョン添加法、シード重合法などを選択することができ、ラテックスの生産性の観点から一括重合法、モノマー（連続・分割）添加法、エマルジョン添加法が好ましい。   The emulsion polymerization method can be generally performed according to the following literature. Tadashi Okuda, Hiroshi Inagaki, "Synthetic Resin Emulsion", published by Polymer Publishing Association (1978), Takaaki Sugimura, Akio Kataoka, Junichi Suzuki, Keiji Kasahara, "Application of Synthetic Latex", Published by Polymer Publishing Society (1993) 1), Soichi Muroi, “Chemistry of Synthetic Latex”, published by Kobunshi Shuppankai (1970). In the emulsion polymerization method for synthesizing the polymer latex used in the present invention, a batch polymerization method, a monomer (continuous / divided) addition method, an emulsion addition method, a seed polymerization method, etc. can be selected from the viewpoint of latex productivity. A batch polymerization method, a monomer (continuous / divided) addition method, and an emulsion addition method are preferred.

前記重合開始剤としてはラジカル発生能があればよく、過硫酸塩や過酸化水素などの無機過酸化物、日本油脂(株)有機過酸化物カタログなどに記載の過酸化物および和光純薬工業(株)アゾ重合開始剤カタログなどに記載のアゾ化合物を用いることができる。その中でも、過硫酸塩などの水溶性過酸化物および和光純薬工業(株)アゾ重合開始剤カタログなどに記載の水溶性アゾ化合物が好ましく、過硫酸アンモニウム、過硫酸ナトリウム、過硫酸カリウム、アゾビス（２−メチルプロピオンアミジン）塩酸塩、アゾビス（２−メチル−N−（２−ヒドロキシエチル）プロピオンアミド）、アゾビスシアノ吉草酸がより好まし
く、特に、過硫酸アンモニウム、過硫酸ナトリウム、過硫酸カリウムなどの過酸化物が画像保存性、溶解性、コストの観点から好ましい。 The polymerization initiator only needs to have radical generating ability, such as inorganic peroxides such as persulfate and hydrogen peroxide, peroxides described in Nippon Oil & Fats Co., Ltd. organic peroxide catalog, and Wako Pure Chemical Industries, Ltd. The azo compounds described in the azo polymerization initiator catalog can be used. Among them, water-soluble peroxides such as persulfate and water-soluble azo compounds described in the Wako Pure Chemical Industries, Ltd. Azo Polymerization Initiator Catalog are preferable. Ammonium persulfate, sodium persulfate, potassium persulfate, azobis ( 2-methylpropionamidine) hydrochloride, azobis (2-methyl-N- (2-hydroxyethyl) propionamide), and azobiscyanovaleric acid are more preferable, and in particular, peroxidation such as ammonium persulfate, sodium persulfate, potassium persulfate and the like. The product is preferable from the viewpoint of image preservability, solubility, and cost.

前記重合開始剤の添加量としては、重合開始剤がモノマー総量に対して０．３質量％〜２．０質量％であることが好ましく、０．４質量％〜１．７５質量％であることがより好ましく、０．５質量％〜１．５質量％であることが特に好ましい。   As the addition amount of the polymerization initiator, the polymerization initiator is preferably 0.3% by mass to 2.0% by mass, and 0.4% by mass to 1.75% by mass with respect to the total amount of monomers. Is more preferable, and 0.5% by mass to 1.5% by mass is particularly preferable.

前記重合乳化剤としては、アニオン性界面活性剤、ノニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤のいずれも用いることができるが、アニオン性界面活性剤が分散性と画像保存性の観点から好ましく、少量で重合安定性が確保でき、加水分解耐性もあることからスルホン酸型アニオン界面活性剤がより好ましく、ペレックスＳＳ−Ｈ（商品名、花王(株)）に代表される長鎖アルキルジフェニルエーテルジスルホン酸塩がさらに好ましく、パイオニンＡ−４３−Ｓ（商品名、竹本油脂(株)）のような低電解質タイプが特に好ましい。   As the polymerization emulsifier, any of an anionic surfactant, a nonionic surfactant, a cationic surfactant, and an amphoteric surfactant can be used, but the anionic surfactant has dispersibility and image storability. From the viewpoint, it is preferable to use a sulfonic acid type anionic surfactant because polymerization stability can be secured in a small amount and resistance to hydrolysis, and a long chain represented by Perex SS-H (trade name, Kao Corp.). Alkyl diphenyl ether disulfonate is more preferable, and a low electrolyte type such as Pionine A-43-S (trade name, Takemoto Yushi Co., Ltd.) is particularly preferable.

前記重合乳化剤として、スルホン酸型アニオン界面活性剤がモノマー総量に対して０．１質量％〜１０．０質量％使用されていることが好ましく、０．２質量％〜７．５質量％使用されていることがより好ましく、０．３質量％〜５．０質量％使用されていることが特に好ましい。   As the polymerization emulsifier, a sulfonic acid type anionic surfactant is preferably used in an amount of 0.1% by mass to 10.0% by mass with respect to the total amount of monomers, and 0.2% by mass to 7.5% by mass is used. It is more preferable that 0.3% by mass to 5.0% by mass is used.

本発明に用いられるポリマーラテックスの合成には、キレート剤を使用するのが好ましい。キレート剤は、鉄イオンなど金属イオンやカルシウムイオンなどのアルカリ土類金属イオンなどの多価イオンを配位（キレート）できる化合物であり、特公平6-8956号、米国特許5053322号、特開平4-73645号、特開平4-127145号、特開平4-247073号、特開平4-305572号、特開平6−11805号、特開平5−173312号、特開平5−66527号、特開平5−158195号、特開平6−118580号、特開平6−110168号、特開平6−161054号、特開平6−175299号、特開平6−214352号、特開平7−114161号、特開平7−114154号、特開平7−120894号、特開平7−199433号、特開平7−306504号、特開平9−43792号、特開平8−314090号、特開平10−182571号、特開平10−182570号、特開平11−190892号の公報または明細書に記載の化合物を用いることができる。   In the synthesis of the polymer latex used in the present invention, it is preferable to use a chelating agent. A chelating agent is a compound capable of coordinating (chelating) a multivalent ion such as a metal ion such as iron ion or an alkaline earth metal ion such as calcium ion. Japanese Patent Publication No. 6-8956, US Pat. JP-A-73645, JP-A-4-127145, JP-A-4-47073, JP-A-4-305572, JP-A-6-11805, JP-A-5-1773312, JP-A-5-66527, JP-A-5- 158195, JP-A-6-118580, JP-A-6-110168, JP-A-6-161054, JP-A-6-175299, JP-A-6-214352, JP-A-7-114161, JP-A-7-114154 JP, 7-120894, JP 7-199433, JP 7-306504, JP 9-43792, JP 8-314090, JP 10-182571, JP 10-182570. The compounds described in JP-A-11-190892 or the specification can be used.

前記キレート剤としては、無機キレート化合物（トリポリリン酸ナトリウム、ヘキサメタリン酸ナトリウム、テトラポリリン酸ナトリウム等）、アミノポリカルボン酸系キレート化合物（ニトリロトリ三酢酸、エチレンジアミン四酢酸等）、有機ホスホン酸系キレート化合物（Research Disclosure１８１７０号、特開昭５２−１０２７２６号、同５３−４２７３０号、同５６−９７３４７号、同５４−１２１１２７号、同５５−４０２４号、同５５−４０２５号、同５５−２９８８３号、同５５−１２６２４１号、同５５−６５９５５号、同５５−６５９５６号、同５７−１７９８４３号、同５４−６１１２５号、及び***特許１０４５３７３号の公報または明細書などに記載の化合物）、ポリフェノール系キレート剤、ポリアミン系キレート化合物など好ましく、アミノポリカルボン酸誘導体が特に好ましい。   Examples of the chelating agent include inorganic chelate compounds (sodium tripolyphosphate, sodium hexametaphosphate, sodium tetrapolyphosphate, etc.), aminopolycarboxylic acid chelate compounds (nitrilotritriacetic acid, ethylenediaminetetraacetic acid, etc.), organic phosphonic acid chelate compounds ( Research Disclosure 18170, JP-A-52-102726, 53-42730, 56-97347, 54-121127, 55-4024, 55-4025, 55-29883, 55 -126241, 55-65955, 55-65956, 57-17943, 54-61125, and West German Patent No. 1045373, and the like, polyphenol-based chelating agents, Polyamine chelation Preferably such things, aminopolycarboxylic acid derivatives being particularly preferred.

前記アミノポリカルボン酸誘導体の好ましい例としては、「ＥＤＴＡ（−コンプレキサンの化学−）」（南江堂、1977年）の付表の化合物があげられ、またこれら化合物のカルボキシル基の一部がナトリウムやカリウムなどのアルカリ金属塩やアンモニウム塩など置換されてもよい。特に好ましいアミノカルボン酸誘導体としては、イミノ二酢酸、N−メチルイミノ二酢酸、N−(２−アミノエチル)イミノ二酢酸、N−(カルバモイルメチル)イミノ二酢酸、ニトリロ三酢酸、エチレンジアミン−N,N'−二酢酸、エチレンジアミン−N,N'−ジ−α−プロピオン酸、エチレンジアミン−N,N'−ジ−β−プロピオン酸、N,N'−エチレン−ビス(α−o−ヒドロキシフェニル)グリシン、N,N'−ジ(２−ヒドロキシベンジル)エチレンジアミン−N,N'−二酢酸、エチレンジアミン−N,N'−二酢酸−N,N'−ジアセトヒドロキサム酸、N−ヒドロキシエチルエチレンジアミン−N,N',N'−三酢酸、エチレンジアミン−N,N,N',N'−四酢酸、１,２−プロピレンジアミン−N,N,N',N'−四酢酸、ｄ,ｌ−２,３−ジアミノブタン−N,N,N',N'−四酢酸、meso−２,３−ジアミノブタン−N,N,N',N'−四酢酸、１−フェニルエチレンジアミン−N,N,N',N'−四酢酸、ｄ,ｌ−１,２−ジフェニルエチレンジアミン−N,N,N',N'−四酢酸、１,４−ジアミノブタン−N,N,N',N'−四酢酸、trans−シクロブタン−１,２−ジアミン−N,N,N',N'−四酢酸、trans−シクロペンタン−１,２−ジアミン−N,N,N',N'−四酢酸、trans−シクロヘキサン−１,２−ジアミン−N,N,N',N'−四酢酸、cis−シクロヘキサン−１,２−ジアミン−N,N,N',N'−四酢酸、シクロヘキサン−１,３−ジアミン−N,N,N',N'−四酢酸、シクロヘキサン−１,４−ジアミン−N,N,N',N'−四酢酸、o−フェニレンジアミン−N,N,N',N'−四酢酸、cis−１,４−ジアミノブテン−N,N,N',N'−四酢酸、trans−１,４−ジアミノブテン−N,N,N',N'−四酢酸、α,α'−ジアミノ−o−キシレン−N,N,N',N'−四酢酸、２−ヒドロキシ−１,３−プロパンジアミン−N,N,N',N'−四酢酸、２,２'−オキシ−ビス(エチルイミノ二酢酸)、２,２'−エチレンジオキシ−ビス(エチルイミノ二酢酸)、エチレンジアミン−N,N'−二酢酸−N,N'−ジ−α−プロピオン酸、エチレンジアミン−N,N'−二酢酸−N,N'−ジ−β−プロピオン酸、エチレンジアミン−N,N,N',N'−テトラプロピオン酸、ジエチレントリアミン−N,N,N',N'',N''−五酢酸、トリエチレンテトラミン−N,N,N',N'',N''',N'''−六酢酸、１,２,３−トリアミノプロパン−N,N,N',N'',N''',N'''−六酢酸が挙げられ、またこれら化合物のカルボキシル基の一部がナトリウムやカリウムなどのアルカリ金属塩やアンモニウム塩など置換されたものも挙げることができる。   Preferable examples of the aminopolycarboxylic acid derivatives include the compounds listed in the appendix of “EDTA (-Complexane Chemistry)” (Nanedo, 1977), and some of the carboxyl groups of these compounds are sodium or potassium. Alkali metal salts and ammonium salts such as may be substituted. Particularly preferred aminocarboxylic acid derivatives include iminodiacetic acid, N-methyliminodiacetic acid, N- (2-aminoethyl) iminodiacetic acid, N- (carbamoylmethyl) iminodiacetic acid, nitrilotriacetic acid, ethylenediamine-N, N '-Diacetic acid, ethylenediamine-N, N'-di-α-propionic acid, ethylenediamine-N, N'-di-β-propionic acid, N, N'-ethylene-bis (α-o-hydroxyphenyl) glycine N, N′-di (2-hydroxybenzyl) ethylenediamine-N, N′-diacetic acid, ethylenediamine-N, N′-diacetic acid-N, N′-diacethydroxamic acid, N-hydroxyethylethylenediamine-N , N ′, N′-triacetic acid, ethylenediamine-N, N, N ′, N′-tetraacetic acid, 1,2-propylenediamine-N, N, N ′, N′-tetraacetic acid, d, l-2 , 3-Diaminobutane-N, N, N ′, N′-tetraacetic acid, meso-2,3-diaminobutane-N, N, N ′, N ′ Tetraacetic acid, 1-phenylethylenediamine-N, N, N ′, N′-tetraacetic acid, d, l-1,2-diphenylethylenediamine-N, N, N ′, N′-tetraacetic acid, 1,4-diamino Butane-N, N, N ′, N′-tetraacetic acid, trans-cyclobutane-1,2-diamine-N, N, N ′, N′-tetraacetic acid, trans-cyclopentane-1,2-diamine-N , N, N ′, N′-tetraacetic acid, trans-cyclohexane-1,2-diamine-N, N, N ′, N′-tetraacetic acid, cis-cyclohexane-1,2-diamine-N, N, N ', N'-tetraacetic acid, cyclohexane-1,3-diamine-N, N, N', N'-tetraacetic acid, cyclohexane-1,4-diamine-N, N, N ', N'-tetraacetic acid, o-phenylenediamine-N, N, N ′, N′-tetraacetic acid, cis-1,4-diaminobutene-N, N, N ′, N′-tetraacetic acid, trans-1,4-diaminobutene-N , N, N ′, N′-tetraacetic acid, α, α′-diamino-o-xylene-N, N, N ′, N′-tetraacetic acid, 2-hydroxy-1,3-propanedia -N, N, N ', N'-tetraacetic acid, 2,2'-oxy-bis (ethyliminodiacetic acid), 2,2'-ethylenedioxy-bis (ethyliminodiacetic acid), ethylenediamine-N, N '-Diacetic acid-N, N'-di-α-propionic acid, ethylenediamine-N, N'-diacetic acid-N, N'-di-β-propionic acid, ethylenediamine-N, N, N', N ' -Tetrapropionic acid, diethylenetriamine-N, N, N ', N' ', N' '-pentaacetic acid, triethylenetetramine-N, N, N', N '', N '' ', N' ''- Hexaacetic acid, 1,2,3-triaminopropane-N, N, N ′, N ″, N ′ ″, N ′ ″-hexaacetic acid, and some of the carboxyl groups of these compounds are Examples include substituted alkali metal salts such as sodium and potassium, and ammonium salts.

前記キレート剤の添加量は、モノマー総量に対して０．０１質量％〜０．４質量％であることが好ましく、０．０２質量％〜０．３質量％であることがより好ましく、０．０３質量％〜０．１５質量％であることが特に好ましい。キレート剤量が０．０１質量％未満であると、ポリマーラテックスの製造工程で混入する金属イオンの捕捉が不十分となり、ラテックスの凝集に対する安定性が低下し、塗布性を悪化させる。また、０．４％を超えると、ラテックスの粘度が上昇し塗布性を低下させる。   The addition amount of the chelating agent is preferably 0.01% by mass to 0.4% by mass, more preferably 0.02% by mass to 0.3% by mass with respect to the total amount of monomers. It is especially preferable that it is 03 mass%-0.15 mass%. When the amount of the chelating agent is less than 0.01% by mass, capture of metal ions mixed in the production process of the polymer latex becomes insufficient, stability against aggregation of the latex is lowered, and applicability is deteriorated. On the other hand, if it exceeds 0.4%, the viscosity of the latex increases and the coatability is lowered.

本発明に用いられるポリマーラテックスの合成には、連鎖移動剤を使用することが好ましい。連鎖移動剤としては、「Polymer Handbook，第３版」（Wiley-Interscience，1989）に記載されているものが好ましい。硫黄化合物は連鎖移動能が高く、少量で用いることで済むことからより好ましい。ｔｅｒｔ−ドデシルメルカプタンやｎ−ドデシルメルカプタン等疎水的なメルカプタン系の連鎖移動剤が特に好ましい。   A chain transfer agent is preferably used for the synthesis of the polymer latex used in the present invention. As the chain transfer agent, those described in “Polymer Handbook, 3rd edition” (Wiley-Interscience, 1989) are preferable. Sulfur compounds are more preferred because they have high chain transfer ability and can be used in small amounts. Hydrophobic mercaptan-based chain transfer agents such as tert-dodecyl mercaptan and n-dodecyl mercaptan are particularly preferred.

前記連鎖移動剤量は、モノマー総量に対して０．２質量％〜２．０質量％が好ましく、０．３質量％〜１．８質量％がより好ましく、０．４質量％〜１．６質量％が特に好ましい。   The amount of the chain transfer agent is preferably 0.2% by mass to 2.0% by mass, more preferably 0.3% by mass to 1.8% by mass, and 0.4% by mass to 1.6% by mass with respect to the total amount of monomers. Mass% is particularly preferred.

乳化重合では、上記化合物以外に、電解質、安定化剤、増粘剤、消泡剤、酸化防止剤、加硫剤、凍結防止剤、ゲル化剤、加硫促進剤など合成ゴムハンドブック等に記載の添加剤を使用してもよい。   In emulsion polymerization, in addition to the above compounds, electrolytes, stabilizers, thickeners, antifoaming agents, antioxidants, vulcanizing agents, antifreezing agents, gelling agents, vulcanization accelerators, etc. are described in synthetic rubber handbooks, etc. These additives may be used.

本発明に用いられるポリマーラテックスは、水系の塗布液を塗布後乾燥して調製することが好ましい。ただし、ここで言う「水系」とは塗布液の溶媒(分散媒)の６０質量％以上が水であることをいう。塗布液の水以外の成分としてはメチルアルコール、エチルアルコール、イソプロピルアルコール、メチルセロソルブ、エチルセロソルブ、ジメチルホルムアミド、酢酸エチル、ジアセトンアルコール、フルフリルアルコール、ベンジルアルコール、ジエチレングリコールモノエチルエーテル、オキシエチルフェニルエーテルなどの水混和性の有機溶媒を用いることができる。
なお、本発明に用いられる受像シートにおけるポリマーラテックスは、塗布後に溶媒の一部を乾燥させることにより形成されるゲルまたは乾燥皮膜の状態を含む。 The polymer latex used in the present invention is preferably prepared by applying an aqueous coating solution and then drying it. However, “aqueous” as used herein means that 60% by mass or more of the solvent (dispersion medium) of the coating solution is water. Components other than water in the coating solution include methyl alcohol, ethyl alcohol, isopropyl alcohol, methyl cellosolve, ethyl cellosolve, dimethylformamide, ethyl acetate, diacetone alcohol, furfuryl alcohol, benzyl alcohol, diethylene glycol monoethyl ether, oxyethyl phenyl ether A water miscible organic solvent such as can be used.
In addition, the polymer latex in the image-receiving sheet used in the present invention includes a gel or a dried film formed by drying a part of the solvent after coating.

＜マット剤＞
本発明において、離型性付与のためにマット剤を受容層に含有する。マット剤は感熱転写受像シートの最外表面層若しくは最外表面層として機能する層、または外表面に近い層に含有されるのが好ましい。最外表面層は必要に応じて２層にすることもできる。最も好ましいのは、最外層である受容層に含有する場合である。マット剤は、画像形成層面の最外層及びバック面の最外層いずれにも含有することが可能であり、両層に添加することもできる。特に、支持体に対し、すべり剤を含有する面側にマット剤を含有させることが好ましい。 <Matting agent>
In the present invention, a matting agent is contained in the receiving layer for imparting releasability. The matting agent is preferably contained in the outermost surface layer, the layer functioning as the outermost surface layer of the heat-sensitive transfer image-receiving sheet, or a layer close to the outer surface. The outermost surface layer can be made into two layers as required. Most preferably, it is contained in the outermost receiving layer. The matting agent can be contained in both the outermost layer on the image forming layer surface and the outermost layer on the back surface, and can also be added to both layers. In particular, it is preferable to include a matting agent on the side of the support containing the slip agent.

マット剤は、予めバインダーによって分散し、マット剤粒子分散物として使用することが好ましい。   The matting agent is preferably dispersed in advance with a binder and used as a matting agent particle dispersion.

マット剤は、一般に水に不溶性の有機化合物の微粒子、無機化合物の微粒子を挙げることができるが、本発明では、分散性の観点ならびに本発明の効果の点で、粒径１〜１０μｍの有機化合物を含有する微粒子を使用する。有機化合物を含有していれば、有機化合物単独からなる有機化合物微粒子であっても良いし、有機化合物だけでなく無機化合物をも含有した有機／無機複合微粒子であっても良い。マット剤の例としては、例えば米国特許第１，９３９，２１３号、同２，７０１，２４５号、同２，３２２，０３７号、同３，２６２，７８２号、同３，５３９，３４４号、同３，７６７，４４８号等の各明細書に記載の有機マット剤など、銀塩感材業界で良く知られたものを用いることができる。   Examples of the matting agent generally include fine particles of an organic compound insoluble in water and fine particles of an inorganic compound. In the present invention, an organic compound having a particle size of 1 to 10 μm is used from the viewpoint of dispersibility and the effects of the present invention. Fine particles containing are used. As long as it contains an organic compound, it may be an organic compound fine particle composed of an organic compound alone, or an organic / inorganic composite fine particle containing not only an organic compound but also an inorganic compound. Examples of the matting agent include, for example, U.S. Pat. Nos. 1,939,213, 2,701,245, 2,322,037, 3,262,782, 3,539,344, Those well known in the silver salt sensitive material industry such as the organic matting agent described in each specification such as US Pat. No. 3,767,448 can be used.

マット剤として含有することができる有機化合物としては、ポリメチルメタクリレート、ポリスチレン、ポリカーボネート、エポキシ、メラミン、シリコーン、フッ素、ベンゾグアナミン、ポリアクリレートの樹脂、及びこれらの共重合体樹脂、例えばスチレン−アクリル共重合体等の樹脂を挙げることができる。この中では、ポリメチルメタクリレート樹脂、メラミン樹脂、シリコーン樹脂、フッ素樹脂を含むマット剤が好ましく、ポリメチルメタクリレート樹脂、メラミン樹脂を含むマット剤が更に好ましく、メラミン樹脂を含むマット剤が最も好ましい。   Organic compounds that can be contained as a matting agent include polymethyl methacrylate, polystyrene, polycarbonate, epoxy, melamine, silicone, fluorine, benzoguanamine, polyacrylate resins, and copolymer resins thereof such as styrene-acrylic copolymer. Resins such as coalescence can be mentioned. Among these, a matting agent containing polymethyl methacrylate resin, melamine resin, silicone resin and fluorine resin is preferable, a matting agent containing polymethyl methacrylate resin and melamine resin is more preferable, and a matting agent containing melamine resin is most preferable.

本発明においては、ポリマーマット剤がより好ましい。   In the present invention, a polymer matting agent is more preferable.

本発明において、マット剤の形状に特に限定はなく、任意の形状のものを用いることができる。マット剤の粒径（平均粒子サイズ）は、本発明の実施に際しては表面に凹凸を付与する観点ならびに本発明の効果の点で、１μｍ〜１０μｍの粒径のものを用いる。マット剤の粒径は、より好ましくは1μｍ〜８μｍ、更に好ましくは２μｍ〜７μｍである。また、マット剤の粒径分布は狭くても広くても良い。サイズ分布の変動係数は５０％以下であることが好ましく、より好ましくは４０％以下、さらに好ましくは、３０％以下である。ここで変動係数とは（粒径の標準偏差）／（粒径の平均値）×１００で表される値である。また、変動係数が小さいマット剤で平均粒径の比が異なるものを２種併用することも好ましい。
一方、マット剤は塗膜のヘイズ、表面光沢に大きく影響することから、マット剤作製時の条件調整または複数のマット剤の混合により、粒径、形状及び粒径分布を必要に応じた状態にすることが好ましい。
また、本発明で使用するマット剤に加え、必要に応じて平均粒子サイズやサイズ分布、および形状の異なる種類のものを混合して用いることができる。 In the present invention, the shape of the matting agent is not particularly limited, and an arbitrary shape can be used. As the particle size (average particle size) of the matting agent, a particle size of 1 μm to 10 μm is used from the viewpoint of imparting unevenness to the surface and the effect of the present invention. The particle size of the matting agent is more preferably 1 μm to 8 μm, still more preferably 2 μm to 7 μm. Further, the particle size distribution of the matting agent may be narrow or wide. The variation coefficient of the size distribution is preferably 50% or less, more preferably 40% or less, and still more preferably 30% or less. Here, the coefficient of variation is a value represented by (standard deviation of particle size) / (average value of particle size) × 100. It is also preferable to use two types of matting agents having a small variation coefficient and different average particle diameter ratios.
On the other hand, since the matting agent greatly affects the haze and surface gloss of the coating film, the particle size, shape, and particle size distribution can be brought into a state as required by adjusting the conditions during the preparation of the matting agent or mixing a plurality of matting agents. It is preferable to do.
In addition to the matting agent used in the present invention, those having different average particle size, size distribution, and shape can be mixed and used as necessary.

画像プリント時、受容層表面の温度は高温になるため、マット剤は耐熱性を有することが好ましい。
本発明において、好ましいマット剤は、上記に挙げた有機化合物のようなポリマーを含有するものであって、ガラス転位温度が９０℃以上のポリマーであることが好ましい。より好ましくは、ガラス転位温度が１３０℃以上のポリマーである。
本発明において、好ましいマット剤は、上記に挙げた有機化合物のようなポリマーからなるものであって、さらに、熱分解温度が２００℃以上のポリマーであることが好ましい。最も好ましくは、熱分解温度が２４０℃以上のポリマーである。
また、画像プリント時、熱だけでなく圧力も受容層表面にかかるため、マット剤は硬いものが好ましい。 Since the temperature of the receiving layer surface becomes high during image printing, the matting agent preferably has heat resistance.
In the present invention, a preferred matting agent contains a polymer such as the organic compounds listed above, and is preferably a polymer having a glass transition temperature of 90 ° C. or higher. More preferably, the polymer has a glass transition temperature of 130 ° C. or higher.
In the present invention, a preferable matting agent is made of a polymer such as the organic compounds listed above, and is preferably a polymer having a thermal decomposition temperature of 200 ° C. or higher. Most preferably, the polymer has a thermal decomposition temperature of 240 ° C. or higher.
In addition, when the image is printed, not only heat but also pressure is applied to the surface of the receiving layer.

以下に本発明において好ましく使用されるマット剤の例を示すが、本発明は以下の化合物に限定されるものではない。
Ｍ−１：シリコーン粒子 比重０．９７
Ｍ−２：シリコーン粒子 比重１．００（Ｅ７０１ 東レダウシリコーン（株）製）
Ｍ−３：シリコーン粒子 比重１．０３
Ｍ−４：ポリスチレン粒子 比重１．０５（ＳＢ−６ 積水化成品工業（株）製）
Ｍ−５：ポリ（Ｓｔ／ＭＡＡ＝９７／３）共重合体粒子 比重１．０５
Ｍ−６：ポリ（Ｓｔ／ＭＡＡ＝９０／１０）共重合体粒子 比重１．０６
Ｍ−７：ポリ（Ｓｔ／ＭＭＡ／ＭＡＡ＝５０／４０／１０）共重合体粒子 比重１．０９
Ｍ−８：架橋シリコーン粒子 比重０．９９
Ｍ−９：架橋シリコーン粒子 比重１．０２
Ｍ−１０：架橋シリコーン粒子 比重１．０４
Ｍ−１１：ポリ（Ｓｔ／ＤＶＢ＝９０／１０）粒子 比重１．０６（ＳＸ−７１３ 綜研化学（株）製）
Ｍ−１２：ポリ（Ｓｔ／ＤＶＢ＝８０／２０）粒子 比重１．０６（ＳＸ−７１３ 綜研化学（株）製）
Ｍ−１３：ポリ（Ｓｔ／ＤＶＢ＝７０／３０）粒子 比重１．０７（ＳＸ−７１３ 綜研化学（株）製）
Ｍ−１４：ポリ（Ｓｔ／ＭＡＡ／ＤＶＢ＝８７／３／１０）共重合体粒子 比重１．０６（ＳＸ−７１３Ａ 綜研化学（株）製）
Ｍ−１５：ポリ（Ｓｔ／ＭＡＡ／ＤＶＢ＝８０／１０／１０）共重合体粒子、比重１．０７（ＳＸ−７１３Ｂ 綜研化学（株）製）
Ｍ−１６：ポリ（Ｓｔ／ＭＭＡ／ＭＡＡ／ＤＶＢ＝４０／４０／１０／１０）共重合体粒子 比重１．１０
Ｍ−１７：メラミン-シリカ樹脂 比重１．６５（オプトビーズ５００ｓ 日産化学工業（株）製）
Ｍ−１８：メラミン-シリカ樹脂 比重１．６５（オプトビーズ２０００Ｍ 日産化学工業（株）製）
Ｍ−１９：メラミン-シリカ樹脂 比重１．６５（オプトビーズ３５００Ｍ 日産化学工業（株）製）
Ｍ−２０：メラミン-シリカ樹脂 比重１．６５（オプトビーズ６５００ｓ 日産化学工業（株）製）
Ｍ−２１：メラミン-シリカ樹脂 比重１．６５（オプトビーズ１０５００ｓ 日産化学工業（株）製）
Ｍ−２２：架橋ＰＭＭＡ粒子 （ＭＸシリーズ 綜研化学（株）製）
Ｍ−２３：架橋ＰＭＭＡ粒子 （ＭＲシリーズ 綜研化学（株）製）
ここで、Ｓｔはスチレンを、ＭＡＡはメタクリル酸を、ＭＭＡはメタクリル酸メチルを、ＤＶＢはジビニルベンゼンを、ＰＭＭＡはポリ（メタクリル酸メチル）を、それぞれ表す。 Examples of matting agents preferably used in the present invention are shown below, but the present invention is not limited to the following compounds.
M-1: Silicone particles, specific gravity 0.97
M-2: Silicone particles Specific gravity 1.00 (E701, Toray Dow Silicone Co., Ltd.)
M-3: Silicone particle specific gravity 1.03
M-4: Polystyrene particles, specific gravity 1.05 (SB-6 Sekisui Plastics Co., Ltd.)
M-5: Poly (St / MAA = 97/3) copolymer particles Specific gravity 1.05
M-6: Poly (St / MAA = 90/10) copolymer particles Specific gravity 1.06
M-7: Poly (St / MMA / MAA = 50/40/10) copolymer particles Specific gravity 1.09
M-8: Cross-linked silicone particles, specific gravity 0.99
M-9: Cross-linked silicone particles, specific gravity 1.02
M-10: Cross-linked silicone particles, specific gravity 1.04
M-11: Poly (St / DVB = 90/10) particles Specific gravity 1.06 (SX-713, manufactured by Soken Chemical Co., Ltd.)
M-12: Poly (St / DVB = 80/20) particles Specific gravity 1.06 (SX-713, manufactured by Soken Chemical Co., Ltd.)
M-13: Poly (St / DVB = 70/30) particles Specific gravity 1.07 (SX-713, manufactured by Soken Chemical Co., Ltd.)
M-14: Poly (St / MAA / DVB = 87/3/10) copolymer particles Specific gravity 1.06 (SX-713A, manufactured by Soken Chemical Co., Ltd.)
M-15: Poly (St / MAA / DVB = 80/10/10) copolymer particles, specific gravity 1.07 (SX-713B manufactured by Soken Chemical Co., Ltd.)
M-16: Poly (St / MMA / MAA / DVB = 40/40/10/10) copolymer particles Specific gravity 1.10
M-17: Melamine-silica resin, specific gravity 1.65 (Opto beads 500s, manufactured by Nissan Chemical Industries, Ltd.)
M-18: Melamine-silica resin, specific gravity 1.65 (Opto Beads 2000M manufactured by Nissan Chemical Industries, Ltd.)
M-19: Melamine-silica resin, specific gravity 1.65 (Opto beads 3500M, manufactured by Nissan Chemical Industries, Ltd.)
M-20: Melamine-silica resin, specific gravity 1.65 (Opto beads 6500s, manufactured by Nissan Chemical Industries, Ltd.)
M-21: Melamine-silica resin, specific gravity 1.65 (Opto beads 10500s, manufactured by Nissan Chemical Industries, Ltd.)
M-22: Cross-linked PMMA particles (MX series, manufactured by Soken Chemical Co., Ltd.)
M-23: Cross-linked PMMA particles (MR series, manufactured by Soken Chemical Co., Ltd.)
Here, St represents styrene, MAA represents methacrylic acid, MMA represents methyl methacrylate, DVB represents divinylbenzene, and PMMA represents poly (methyl methacrylate).

画像形成層面側の最外層及び最外層隣接層に含有されるマット剤は、予めバインダーによって分散して、マット剤粒子分散物として使用されるが、その分散方法は、（ａ）マット剤となるべきポリマーを溶液（例えば低沸点の有機溶媒に溶解）として、水性媒体中で乳化分散させてポリマーの液滴を得て、乳化物から低沸点有機溶媒を除去することにより、マット剤の分散物を調製する方法、（ｂ）予めマット剤となるべきポリマーなどの微粒子を用意しておき、水性媒体中でダマの発生がないように分散物を調製する方法の２通りの方法がある。本発明においては、環境に配慮し低沸点の有機溶媒を環境に排出しない（ｂ）の方法が好ましい。   The matting agent contained in the outermost layer on the image forming layer side and the outermost layer adjacent layer is dispersed in advance with a binder and used as a matting agent particle dispersion. The dispersion method is (a) a matting agent. The dispersion of the matting agent by removing the low boiling point organic solvent from the emulsion by emulsifying and dispersing the polymer to be dissolved in an aqueous medium as a solution (for example, dissolved in a low boiling point organic solvent) to obtain polymer droplets There are two methods: (b) a method in which fine particles such as a polymer to be a matting agent are prepared in advance, and a dispersion is prepared so as not to cause lumps in an aqueous medium. In the present invention, in consideration of the environment, the method (b) in which a low-boiling organic solvent is not discharged to the environment is preferable.

上述のマット剤を分散する方法は、水性溶媒中に予め分散助剤として、バインダーを含有する水性媒体を存在させ、公知の高速撹拌手段（例えば、ディスバー乳化機、ホモミキサー、タービンミキサー、ホモジナイザー）や超音波乳化機等を用い、機械的に分散することができる。分散に際しては、起泡を抑制するために、大気圧よりも減圧状態にて分散する手段を併用することもできる。使用する分散助剤は、予め水性媒体中に溶解してから、マット剤を添加するのが一般的な方法であるが、予めマット剤が重合によって得られた水分散物のままで（乾燥工程を経ることなしに）添加されても良い。分散助剤は、分散中に分散液に添加することもできる。また、分散後の物性の安定化のために、分散液に添加することもできる。いずれの場合も、溶媒（例えば、水・アルコールなど）を共存させるのが一般的である。分散前後または分散中に、適当なｐＨ調整剤によりｐＨコントロールしても良い。
機械的に分散する手段以外にも、ｐＨをコントロールすることで、分散後のマット剤分散物の安定性を増しても良い。また、分散には補助的に極少量の低沸点有機溶媒を使用しても良く、通常有機溶媒は、微粒子化終了後除去される。
調製された分散物は、保存時のマット剤の沈降を抑える目的で、撹拌しながら保存したり、親水性コロイドにより粘性の高い状態（例えば、ゼラチンを使用しゼリー状態にする）で保存したりすることもできる。また、保存時の雑菌などの繁殖を防止する目的で、防腐剤を添加することが好ましい。
バインダーは、マット剤に対して５質量％以上３００質量％以下となるように添加し分散させることが好ましい。より好ましくは、１０質量％以上２００質量％以下となるように添加する。 In the method of dispersing the matting agent, an aqueous medium containing a binder is previously present as a dispersion aid in an aqueous solvent, and known high-speed stirring means (for example, a disperser emulsifier, a homomixer, a turbine mixer, a homogenizer) Or using an ultrasonic emulsifier or the like. In dispersing, in order to suppress foaming, means for dispersing in a reduced pressure state rather than atmospheric pressure can be used in combination. The dispersion aid to be used is generally dissolved in an aqueous medium in advance, and then the matting agent is generally added, but the matting agent remains in an aqueous dispersion obtained by polymerization (drying step). (Without going through). The dispersion aid can also be added to the dispersion during dispersion. Moreover, it can also add to a dispersion liquid for stabilization of the physical property after dispersion | distribution. In either case, it is common that a solvent (for example, water / alcohol) coexists. You may control pH by a suitable pH adjuster before and after dispersion | distribution or during dispersion | distribution.
In addition to the mechanical dispersion means, the stability of the dispersed matting agent may be increased by controlling the pH. In addition, a very small amount of a low-boiling organic solvent may be used for dispersion, and the organic solvent is usually removed after the formation of fine particles.
The prepared dispersion is stored with stirring for the purpose of suppressing the settling of the matting agent during storage, or stored in a highly viscous state (for example, using gelatin to make a jelly state) with a hydrophilic colloid. You can also Moreover, it is preferable to add a preservative for the purpose of preventing the propagation of various germs during storage.
The binder is preferably added and dispersed so as to be 5% by mass to 300% by mass with respect to the matting agent. More preferably, it adds so that it may become 10 mass% or more and 200 mass% or less.

本発明におけるマット粒子分散物は、界面活性剤を含有すると分散状態が安定するため、界面活性剤を添加することが好ましい。   Since the dispersion state of the mat particle dispersion in the present invention is stabilized when it contains a surfactant, it is preferable to add a surfactant.

＜水溶性ポリマー＞
受容層は水溶性ポリマーを含有することが好ましい。
ここで、水溶性ポリマーとは、２０℃における水１００ｇに対し０．０５ｇ以上溶解すればよく、より好ましくは０．１ｇ以上、さらに好ましくは０．５ｇ以上、特に好ましくは１ｇ以上である。
本発明に用いることのできる水溶性ポリマーは、天然高分子（多糖類系、微生物系、動物系）、半合成高分子（セルロース系、デンプン系、アルギン酸系）および合成高分子系（ビニル系、その他）であり、以下に述べるポリビニルアルコールを始めとする合成ポリマーや、植物由来のセルロース等を原料とする天然あるいは半合成ポリマーが本発明で使用できる水溶性ポリマーに該当する。なお、本発明における水溶性ポリマーには、前記ポリマーラテックスは含まれない。
本発明において、水溶性ポリマーを前記ポリマーラテックスと区別するためにバインダーと標記することもある。 <Water-soluble polymer>
The receiving layer preferably contains a water-soluble polymer.
Here, the water-soluble polymer may be dissolved in an amount of 0.05 g or more with respect to 100 g of water at 20 ° C., more preferably 0.1 g or more, still more preferably 0.5 g or more, and particularly preferably 1 g or more.
Water-soluble polymers that can be used in the present invention include natural polymers (polysaccharides, microorganisms, animals), semi-synthetic polymers (cellulose, starch, alginic acid), and synthetic polymers (vinyl, Others), synthetic polymers such as polyvinyl alcohol described below, and natural or semi-synthetic polymers made from plant-derived cellulose or the like correspond to water-soluble polymers that can be used in the present invention. The water-soluble polymer in the present invention does not include the polymer latex.
In the present invention, a water-soluble polymer may be labeled as a binder to distinguish it from the polymer latex.

本発明に用いることのできる水溶性ポリマーのうち、天然高分子および半合成高分子について詳しく説明する。植物系多糖類としては、アラビアガム、κ−カラギーナン、ι−カラギーナン、λ−カラギーナン、グアガム（Squalon製Supercolなど）、ローカストビーンガム、ペクチン、トラガント、トウモロコシデンプン（National Starch ＆ Chemical Co.製Purity-21など）、リン酸化デンプン（National Starch ＆ Chemical Co.製National 78-1898など）など、微生物系多糖類としては、キサンタンガム（Kelco製Keltrol Tなど）、デキストリン（National Starch ＆ Chemical Co.製Nadex360など）など、動物系天然高分子としては、ゼラチン（Croda製Crodyne B419など）、カゼイン、コンドロイチン硫酸ナトリウム（Croda製Cromoist CSなど）などが挙げられる（いずれも商品名）。セルロース系としては、エチルセルロース（I.C.I.製Cellofas WLDなど）、カルボキシメチルセルロース(ダイセル製CMCなど)、ヒドロキシエチルセルロース(ダイセル製HECなど)、ヒドロキシプロピルセルロース（Aqualon製Klucelなど）、メチルセルロース（Henkel製Viscontranなど）、ニトロセルロース（Hercules製Isopropyl Wetなど）、カチオン化セルロース（Croda製Crodacel QMなど）などが挙げられる（いずれも商品名）。デンプン系としては、リン酸化デンプン（National Starch ＆ Chemical製National 78-1898など）、アルギン酸系としては、アルギン酸ナトリウム（Kelco製Keltoneなど）、アルギン酸プロピレングリコールなど、その他の分類として、カチオン化グアガム（Alcolac製Hi-care1000など）、ヒアルロン酸ナトリウム（Lifecare Biomedial製Hyalureなど）が挙げられる（いずれも商品名）。
本発明においてはゼラチンが好ましい態様の一つである。本発明に用いるゼラチンは分子量10,000から1,000,000までのものを用いることができる。本発明に用いられるゼラチンはＣｌ^-、ＳＯ₄ ^2-等の陰イオンを含んでいてもよいし、Ｆｅ²⁺、Ｃａ²⁺、Ｍｇ²⁺、Ｓｎ²⁺、Ｚｎ²⁺などの陽イオンを含んでいても良い。ゼラチンは水に溶かして添加することが好ましい。 Of the water-soluble polymers that can be used in the present invention, natural polymers and semi-synthetic polymers will be described in detail. Plant polysaccharides include gum arabic, κ-carrageenan, ι-carrageenan, λ-carrageenan, guar gum (such as Supercol from Squall), locust bean gum, pectin, tragacanth, corn starch (Purity- from National Starch & Chemical Co.) 21), phosphorylated starch (National 78-1898 made by National Starch & Chemical Co.), and other microbial polysaccharides such as xanthan gum (Kelco Keltrol T, etc.) and dextrin (Nadex360 made by National Starch & Chemical Co., etc.) Examples of animal natural polymers include gelatin (such as Crodyne B419 from Croda), casein, sodium chondroitin sulfate (such as Cromoist CS from Croda), and the like (all are trade names). Cellulose systems include ethyl cellulose (ICI Cellofas WLD, etc.), carboxymethyl cellulose (Daicel CMC, etc.), hydroxyethyl cellulose (Daicel HEC, etc.), hydroxypropyl cellulose (Aqualon Klucel, etc.), methyl cellulose (Henkel Viscontran, etc.), Examples include nitrocellulose (such as Isopropyl Wet from Hercules) and cationized cellulose (such as Crodacel QM from Croda). Other starches such as phosphorylated starch (National Starch &Chemical's National 78-1898) and alginic acid are sodium alginate (such as Kelco's Keltone) and propylene glycol alginate. Hi-care1000, etc.) and sodium hyaluronate (Hyalure, etc. from Lifecare Biomedial) are included (all are trade names).
In the present invention, gelatin is one of the preferred embodiments. The gelatin used in the present invention may have a molecular weight of 10,000 to 1,000,000. Gelatin used in the present invention may contain anions such as Cl ⁻ , SO ₄ ²⁻ , and cations such as Fe ²⁺ , Ca ²⁺ , Mg ²⁺ , Sn ²⁺ and Zn ^2+. It may be included. It is preferable to add gelatin dissolved in water.

本発明に用いることのできる水溶性ポリマーのうち、合成高分子について詳しく説明する。アクリル系としてはポリアクリル酸ナトリウム、ポリアクリル酸共重合体、ポリアクリルアミド、ポリアクリルアミド共重合体、ポリジエチルアミノエチル（メタ）アクリレート四級塩またはその共重合体など、ビニル系としては、ポリビニルピロリドン、ポリビニルピロリドン共重合体、ポリビニルアルコールなど、その他としては、ポリエチレングリコール、ポリプロピレングリコール、ポリイソプロピルアクリルアミド、ポリメチルビニルエーテル、ポリエチレンイミン、ポリスチレンスルホン酸又はその共重合体、ナフタレンスルホン酸縮合物塩、ポリビニルスルホン酸又はその共重合体、ポリアクリル酸又はその共重合体、アクリル酸又はその共重合体等、マレイン酸共重合体、マレイン酸モノエステル共重合体、アクリロイルメチルプロパンスルホン酸又はその共重合体、など）、ポリジメチルジアリルアンモニウムクロライドまたはその共重合体、ポリアミジンまたはその共重合体、ポリイミダゾリン、ジシアンシアミド系縮合物、エピクロルヒドリン・ジメチルアミン縮合物、ポリアクリルアミドのホフマン分解物、水溶性ポリエステル（互応化学(株)製プラスコートZ-221、Z-446、Z-561、Z-450、Z-565、Z-850、Z-3308、RZ-105、RZ-570、Z-730、RZ-142（いずれも商品名））などである。   Of the water-soluble polymers that can be used in the present invention, synthetic polymers will be described in detail. Examples of the acrylic system include sodium polyacrylate, polyacrylic acid copolymer, polyacrylamide, polyacrylamide copolymer, polydiethylaminoethyl (meth) acrylate quaternary salt or a copolymer thereof, and the vinyl system includes polyvinylpyrrolidone, Polyvinyl pyrrolidone copolymer, polyvinyl alcohol, etc. include polyethylene glycol, polypropylene glycol, polyisopropyl acrylamide, polymethyl vinyl ether, polyethylene imine, polystyrene sulfonic acid or copolymer thereof, naphthalene sulfonic acid condensate salt, polyvinyl sulfonic acid Or a copolymer thereof, polyacrylic acid or a copolymer thereof, acrylic acid or a copolymer thereof, a maleic acid copolymer, a maleic acid monoester copolymer, an acryloylme Propane sulfonic acid or its copolymer, etc.), polydimethyldiallylammonium chloride or its copolymer, polyamidine or its copolymer, polyimidazoline, dicyanciamide condensate, epichlorohydrin-dimethylamine condensate, polyacrylamide Hoffman Decomposed product, water-soluble polyester (Plus coat Z-221, Z-446, Z-561, Z-450, Z-565, Z-850, Z-3308, RZ-105, RZ-570, manufactured by Kyodo Chemical Co., Ltd.) , Z-730, RZ-142 (both are trade names)).

また、米国特許第４，９６０，６８１号明細書、特開昭６２−２４５２６０号公報等に記載の高吸水性ポリマー、すなわち−ＣＯＯＭまたは−ＳＯ₃Ｍ（Ｍは水素原子またはア
ルカリ金属）を有するビニルモノマーの単独重合体またはこのビニルモノマー同士もしくは他のビニルモノマーの共重合体（例えばメタクリル酸ナトリウム、メタクリル酸アンモニウム、住友化学(株)製のスミカゲルＬ−５Ｈ（商品名））も使用することができる。 Further, it has a superabsorbent polymer described in US Pat. No. 4,960,681, JP-A-62-245260, etc., that is, —COOM or —SO ₃ M (M is a hydrogen atom or an alkali metal). A homopolymer of vinyl monomers or a copolymer of these vinyl monomers or other vinyl monomers (for example, sodium methacrylate, ammonium methacrylate, Sumikagel L-5H (trade name) manufactured by Sumitomo Chemical Co., Ltd.) should also be used. Can do.

本発明に用いることのできる水溶性合成高分子のうちポリビニルアルコール類が好ましい。
以下に、ポリビニルアルコールについてさらに詳しく説明する。
完全けん化物としては、ＰＶＡ−１０５［ポリビニルアルコール（ＰＶＡ）含有率９４．０質量％以上、鹸化度９８．５±０．５モル％、酢酸ナトリウム含有率１．５質量％以下、揮発分５．０質量％以下、粘度（４質量％、２０℃）５．６±０．４ＣＰＳ］、ＰＶＡ−１１０［ＰＶＡ含有率９４．０質量％、鹸化度９８．５±０．５モル％、酢酸ナトリウム含有率１．５質量％、揮発分５．０質量％、粘度（４質量％、２０℃）１１．０±０．８ＣＰＳ］、ＰＶＡ−１１７［ＰＶＡ含有率９４．０質量％、鹸化度９８．５±０．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）２８．０±３．０ＣＰＳ］、 Of the water-soluble synthetic polymers that can be used in the present invention, polyvinyl alcohols are preferred.
Hereinafter, polyvinyl alcohol will be described in more detail.
As a complete saponified product, PVA-105 [polyvinyl alcohol (PVA) content 94.0% by mass or more, saponification degree 98.5 ± 0.5 mol%, sodium acetate content 1.5% by mass or less, volatile content 5 0.0 mass% or less, viscosity (4 mass%, 20 ° C.) 5.6 ± 0.4 CPS], PVA-110 [PVA content 94.0 mass%, saponification degree 98.5 ± 0.5 mol%, acetic acid Sodium content 1.5% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20 ° C.) 11.0 ± 0.8 CPS], PVA-117 [PVA content 94.0% by mass, saponification degree 98.5 ± 0.5 mol%, sodium acetate content 1.0 mass%, volatile content 5.0 mass%, viscosity (4 mass%, 20 ° C.) 28.0 ± 3.0 CPS],

ＰＶＡ−１１７Ｈ［ＰＶＡ含有率９３．５質量％、鹸化度９９．６±０．３モル％、酢酸ナトリウム含有率１．８５質量％、揮発分５．０質量％、粘度（４質量％、２０℃）２９．０±３．０ＣＰＳ］、ＰＶＡ−１２０［ＰＶＡ含有率９４．０質量％、鹸化度９８．５±０．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）３９．５±４．５ＣＰＳ］、ＰＶＡ−１２４［ＰＶＡ含有率９４．０質量％、鹸化度９８．５±０．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）６０．０±６．０ＣＰＳ］、 PVA-117H [PVA content 93.5% by mass, saponification degree 99.6 ± 0.3 mol%, sodium acetate content 1.85% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20% ° C) 29.0 ± 3.0 CPS], PVA-120 [PVA content 94.0 mass%, saponification degree 98.5 ± 0.5 mol%, sodium acetate content 1.0 mass%, volatile content 5. 0 mass%, viscosity (4 mass%, 20 ° C.) 39.5 ± 4.5 CPS], PVA-124 [PVA content 94.0 mass%, saponification degree 98.5 ± 0.5 mol%, sodium acetate contained 1.0 mass%, volatile matter 5.0 mass%, viscosity (4 mass%, 20 ° C.) 60.0 ± 6.0 CPS],

ＰＶＡ−１２４Ｈ［ＰＶＡ含有率９３．５質量％、鹸化度９９．６±０．３モル％、酢酸ナトリウム含有率１．８５質量％、揮発分５．０質量％、粘度（４質量％、２０℃）６１．０±６．０ＣＰＳ］、ＰＶＡ−ＣＳ［ＰＶＡ含有率９４．０質量％、鹸化度９７．５±０．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）２７．５±３．０ＣＰＳ］、ＰＶＡ−ＣＳＴ［ＰＶＡ含有率９４．０質量％、鹸化度９６．０±０．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）２７．０±３．０ＣＰＳ］、ＰＶＡ−ＨＣ［ＰＶＡ含有率９０．０質量％、鹸化度９９．８５モル％以上、酢酸ナトリウム含有率２．５質量％、揮発分８．５質量％、粘度（４質量％、２０℃）２５．０±３．５ＣＰＳ］（以上、いずれもクラレ(株)製の商品名）など、 PVA-124H [PVA content 93.5% by mass, saponification degree 99.6 ± 0.3 mol%, sodium acetate content 1.85% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20% ° C) 61.0 ± 6.0 CPS], PVA-CS [PVA content 94.0% by mass, saponification degree 97.5 ± 0.5 mol%, sodium acetate content 1.0% by mass, volatile content 5. 0 mass%, viscosity (4 mass%, 20 ° C.) 27.5 ± 3.0 CPS], PVA-CST [PVA content 94.0 mass%, saponification degree 96.0 ± 0.5 mol%, sodium acetate contained 1.0 mass%, volatile matter 5.0 mass%, viscosity (4 mass%, 20 ° C.) 27.0 ± 3.0 CPS], PVA-HC [PVA content 90.0 mass%, saponification degree 99. 85 mol% or more, sodium acetate content 2.5 mass%, volatile content 8.5 mass%, viscosity (4 quality %, 20 ℃) 25.0 ± 3.5CPS] (or more, both of Kuraray Co., Ltd., trade name of) such as,

部分鹸化物としては、ＰＶＡ−２０３［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）３．４±０．２ＣＰＳ］、ＰＶＡ−２０４［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）３．９±０．３ＣＰＳ］、ＰＶＡ−２０５［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）５．０±０．４ＣＰＳ］、 As a partially saponified product, PVA-203 [PVA content 94.0% by mass, saponification degree 88.0 ± 1.5 mol%, sodium acetate content 1.0% by mass, volatile matter 5.0% by mass, viscosity (4 mass%, 20 ° C.) 3.4 ± 0.2 CPS], PVA-204 [PVA content 94.0 mass%, saponification degree 88.0 ± 1.5 mol%, sodium acetate content 1.0 mass %, Volatile matter 5.0 mass%, viscosity (4 mass%, 20 ° C.) 3.9 ± 0.3 CPS], PVA-205 [PVA content 94.0 mass%, saponification degree 88.0 ± 1.5 Mol%, sodium acetate content 1.0% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20 ° C.) 5.0 ± 0.4 CPS],

ＰＶＡ−２１０［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．０モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）９．０±１．０ＣＰＳ］、ＰＶＡ−２１７［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．０モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）２２．５±２．０ＣＰＳ］、ＰＶＡ−２２０［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．０モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）３０．０±３．０ＣＰＳ］、 PVA-210 [PVA content 94.0% by mass, saponification degree 88.0 ± 1.0 mol%, sodium acetate content 1.0% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20% ° C) 9.0 ± 1.0 CPS], PVA-217 [PVA content 94.0 mass%, saponification degree 88.0 ± 1.0 mol%, sodium acetate content 1.0 mass%, volatile content 5. 0 mass%, viscosity (4 mass%, 20 ° C.) 22.5 ± 2.0 CPS], PVA-220 [PVA content 94.0 mass%, saponification degree 88.0 ± 1.0 mol%, sodium acetate contained 1.0 mass%, volatile matter 5.0 mass%, viscosity (4 mass%, 20 ° C.) 30.0 ± 3.0 CPS],

ＰＶＡ−２２４［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）４４．０±４．０ＣＰＳ］、ＰＶＡ−２２８［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）６５．０±５．０ＣＰＳ］、ＰＶＡ−２３５［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）９５．０±１５．０ＣＰＳ］、 PVA-224 [PVA content 94.0% by mass, saponification degree 88.0 ± 1.5 mol%, sodium acetate content 1.0% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20% ° C) 44.0 ± 4.0 CPS], PVA-228 [PVA content 94.0 mass%, saponification degree 88.0 ± 1.5 mol%, sodium acetate content 1.0 mass%, volatile content 5. 0 mass%, viscosity (4 mass%, 20 ° C.) 65.0 ± 5.0 CPS], PVA-235 [PVA content 94.0 mass%, saponification degree 88.0 ± 1.5 mol%, sodium acetate contained 1.0 mass%, volatile matter 5.0 mass%, viscosity (4 mass%, 20 ° C.) 95.0 ± 15.0 CPS],

ＰＶＡ−２１７ＥＥ［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．０モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）２３．０±３．０ＣＰＳ］、ＰＶＡ−２１７Ｅ［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．０モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）２３．０±３．０ＣＰＳ］、ＰＶＡ−２２０Ｅ［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．０モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）３１．０±４．０ＣＰＳ］、 PVA-217EE [PVA content 94.0% by mass, saponification degree 88.0 ± 1.0 mol%, sodium acetate content 1.0% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20% ° C) 23.0 ± 3.0 CPS], PVA-217E [PVA content 94.0% by mass, saponification degree 88.0 ± 1.0 mol%, sodium acetate content 1.0% by mass, volatile content 5. 0 mass%, viscosity (4 mass%, 20 ° C.) 23.0 ± 3.0 CPS], PVA-220E [PVA content 94.0 mass%, saponification degree 88.0 ± 1.0 mol%, sodium acetate contained 1.0 mass%, volatile matter 5.0 mass%, viscosity (4 mass%, 20 ° C.) 31.0 ± 4.0 CPS],

ＰＶＡ−２２４Ｅ［ＰＶＡ含有率９４．０質量％、鹸化度８８．０±１．０モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）４５．０±５．０ＣＰＳ］、ＰＶＡ−４０３［ＰＶＡ含有率９４．０質量％、鹸化度８０．０±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）３．１±０．３ＣＰＳ］、ＰＶＡ−４０５［ＰＶＡ含有率９４．０質量％、鹸化度８１．５±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）４．８±０．４ＣＰＳ］、 PVA-224E [PVA content 94.0% by mass, saponification degree 88.0 ± 1.0 mol%, sodium acetate content 1.0% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20% ° C) 45.0 ± 5.0 CPS], PVA-403 [PVA content 94.0 mass%, saponification degree 80.0 ± 1.5 mol%, sodium acetate content 1.0 mass%, volatile content 5. 0 mass%, viscosity (4 mass%, 20 ° C.) 3.1 ± 0.3 CPS], PVA-405 [PVA content 94.0 mass%, saponification degree 81.5 ± 1.5 mol%, sodium acetate contained 1.0 mass%, volatile matter 5.0 mass%, viscosity (4 mass%, 20 ° C.) 4.8 ± 0.4 CPS],

ＰＶＡ−４２０［ＰＶＡ含有率９４．０質量％、鹸化度７９．５±１．５モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％］、ＰＶＡ−６１３［ＰＶＡ含有率９４．０質量％、鹸化度９３．５±１．０モル％、酢酸ナトリウム含有率１．０質量％、揮発分５．０質量％、粘度（４質量％、２０℃）１６．５±２．０ＣＰＳ］、Ｌ−８［ＰＶＡ含有率９６．０質量％、鹸化度７１．０±１．５モル％、酢酸ナトリウム含有率１．０質量％（灰分）、揮発分３．０質量％、粘度（４質量％、２０℃）５．４±０．４ＣＰＳ］（以上、いずれもクラレ(株)製の商品名）などがある。 PVA-420 [PVA content 94.0% by mass, saponification degree 79.5 ± 1.5 mol%, sodium acetate content 1.0% by mass, volatile matter 5.0% by mass], PVA-613 [PVA-containing Rate 94.0% by mass, saponification degree 93.5 ± 1.0 mol%, sodium acetate content 1.0% by mass, volatile matter 5.0% by mass, viscosity (4% by mass, 20 ° C.) 16.5 ± 2.0 CPS], L-8 [PVA content 96.0 mass%, saponification degree 71.0 ± 1.5 mol%, sodium acetate content 1.0 mass% (ash content), volatile content 3.0 mass% Viscosity (4% by mass, 20 ° C.) 5.4 ± 0.4 CPS] (all are trade names manufactured by Kuraray Co., Ltd.).

なお、上記の測定値はＪＩＳ Ｋ−６７２６−１９７７に準じて求めたものである。   In addition, said measured value is calculated | required according to JISK-6726-1977.

変性ポリビニルアルコールについては、長野浩一ら共著，「ポバール」（高分子刊行会発行）に記載のものが用いられる。カチオン、アニオン、−ＳＨ化合物、アルキルチオ化合物、シラノールによる変性がある。   As for the modified polyvinyl alcohol, those described in Koichi Nagano et al., “Poval” (published by Kobunshi Shuppankai) are used. There is modification by cation, anion, -SH compound, alkylthio compound, silanol.

このような変性ポリビニルアルコール（変性ＰＶＡ）としては、ＣポリマーとしてＣ−１１８、Ｃ−３１８、Ｃ−３１８−２Ａ、Ｃ−５０６（以上、いずれもクラレ(株)製の商品名）、ＨＬポリマーとしてＨＬ−１２Ｅ、ＨＬ−１２０３（以上、いずれもクラレ(株)製の商品名）、ＨＭポリマーとしてＨＭ−０３、ＨＭ−Ｎ−０３（以上、いずれもクラレ(株)製の商品名）、ＫポリマーとしてＫＬ−１１８、ＫＬ−３１８、ＫＬ−５０６、ＫＭ−１１８Ｔ、ＫＭ−６１８（以上、いずれもクラレ(株)製の商品名）、ＭポリマーとしてＭ−１１５（クラレ(株)製の商品名）、ＭＰポリマーとしてＭＰ−１０２、ＭＰ−２０２、ＭＰ−２０３（以上、いずれもクラレ(株)製の商品名）、ＭＰＫポリマーとして、ＭＰＫ−１、ＭＰＫ−２、ＭＰＫ−３、ＭＰＫ−４、ＭＰＫ−５、ＭＰＫ−６（以上、いずれもクラレ(株)製の商品名）、ＲポリマーとしてＲ−１１３０、Ｒ−２１０５、Ｒ−２１３０（以上、いずれもクラレ(株)製の商品名）、ＶポリマーとしてＶ−２２５０（クラレ(株)製の商品名）などがある。   As such modified polyvinyl alcohol (modified PVA), C-118, C-318, C-318-2A, C-506 (all are trade names manufactured by Kuraray Co., Ltd.), HL polymer as C polymer. HL-12E, HL-1203 (all are trade names manufactured by Kuraray Co., Ltd.), HM polymer is HM-03, HM-N-03 (all are trade names manufactured by Kuraray Co., Ltd.), KL-118, KL-318, KL-506, KM-118T, KM-618 (all are trade names manufactured by Kuraray Co., Ltd.) as the K polymer, and M-115 (manufactured by Kuraray Co., Ltd.) as the M polymer. (Trade name), MP-102, MP-202, MP-203 (all are trade names manufactured by Kuraray Co., Ltd.) as MP polymers, MPK-1, MPK-2, MPK-3, PK-4, MPK-5, MPK-6 (all are trade names manufactured by Kuraray Co., Ltd.), R polymer as R-1130, R-2105, R-2130 (all are manufactured by Kuraray Co., Ltd.) And V-2250 (trade name, manufactured by Kuraray Co., Ltd.).

ポリビニルアルコールは、その水溶液に添加する微量の溶剤あるいは無機塩類によって粘度調整をしたり粘度安定化させたりすることが可能であって、詳しくは上記文献、長野浩一ら共著，「ポバール」，高分子刊行会発行，144〜154頁記載のものを使用することができる。その代表例としてホウ酸を含有させることで塗布面質を向上させることができ、好ましい。ホウ酸の添加量は、ポリビニルアルコールに対し０．０１〜４０質量％であることが好ましい。   Polyvinyl alcohol can be adjusted in viscosity or stabilized by a small amount of solvent or inorganic salt added to the aqueous solution. For details, refer to the above document, Koichi Nagano et al., “Poval”, Polymer Issued by the publisher, pages 144 to 154 can be used. As a typical example, it is possible to improve the coating surface quality by containing boric acid, which is preferable. The addition amount of boric acid is preferably 0.01 to 40% by mass with respect to polyvinyl alcohol.

好適なバインダーは透明又は半透明で、一般に無色であり、天然樹脂やポリマー及びコポリマー、合成樹脂やポリマー及びコポリマー、その他フィルムを形成する媒体、例えば、ゴム類、ポリビニルアルコール類、ヒドロキシエチルセルロース類、セルロースアセテート類、セルロースアセテートブチレート類、ポリビニルピロリドン類、デンプン、ポリアクリル酸類、ポリメチルメタクリル酸類、ポリ塩化ビニル類、ポリメタクリル酸類、スチレン−無水マレイン酸共重合体類、スチレン−アクリロニトリル共重合体類、スチレン−ブタジエン共重合体類、ポリビニルアセタール類（例えば、ポリビニルホルマール及びポリビニルブチラール）、ポリエステル類、ポリウレタン類、フェノキシ樹脂、ポリ塩化ビニリデン類、ポリエポキシド類、ポリカーボネート類、ポリ酢酸ビニル類、ポリオレフィン類、セルロースエステル類、ポリアミド類であって水溶性のものである。   Suitable binders are transparent or translucent, generally colorless, and are natural resins, polymers and copolymers, synthetic resins, polymers and copolymers, and other film-forming media such as rubbers, polyvinyl alcohols, hydroxyethyl celluloses, cellulose Acetates, cellulose acetate butyrate, polyvinylpyrrolidone, starch, polyacrylic acid, polymethylmethacrylic acid, polyvinyl chloride, polymethacrylic acid, styrene-maleic anhydride copolymers, styrene-acrylonitrile copolymers , Styrene-butadiene copolymers, polyvinyl acetals (eg, polyvinyl formal and polyvinyl butyral), polyesters, polyurethanes, phenoxy resins, polyvinylidene chlorides, polyepoxides , Polycarbonates, polyvinyl acetates, polyolefins, cellulose esters, and polyamides such water-soluble.

本発明においては、水溶性ポリマーがポリビニルアルコール類、ゼラチンが好ましく、ゼラチンが最も好ましい。
受容層における水溶性ポリマーの添加量は、当該受容層全体の１〜２５質量％であることが好ましく、１〜１０質量％であることがより好ましい。 In the present invention, the water-soluble polymer is preferably polyvinyl alcohol or gelatin, and most preferably gelatin.
The addition amount of the water-soluble polymer in the receiving layer is preferably 1 to 25% by mass, and more preferably 1 to 10% by mass with respect to the entire receiving layer.

＜硬膜剤＞
本発明には架橋剤を使用することが好ましい。
架橋剤として本発明に好ましく用いられる硬膜剤は、受像シートの塗設層（例えば、受容層、断熱層、下塗層など）中に添加することができる。
本発明で用いることができる硬膜剤としては、特開平１−２１４８４５号公報１７頁のＨ−１，４，６，８，１４，米国特許第４,６１８,５７３号明細書のカラム１３〜２３の式（VII）〜（XII）で表わされる化合物（Ｈ−１〜５４）、特開平２−２１４８５２号公報８頁右下の式（６）で表わされる化合物（Ｈ−１〜７６），特にＨ−１４、米国特許第３,３２５,２８７号明細書のクレーム１に記載の化合物などが好ましく用いられる。硬膜剤の例としては米国特許第４,６７８,７３９号明細書の第４１欄、同第４,７９１,０４２号、特開昭５９−１１６６５５号、同６２−２４５２６１号、同６１−１８９４２号、特開平４−２１８０４４号の公報または明細書等に記載の硬膜剤が挙げられる。より具体的には、アルデヒド系硬膜剤（ホルムアルデヒドなど）、アジリジン系硬膜剤、エポキシ系硬膜剤、ビニルスルホン系硬膜剤（Ｎ，Ｎ’−エチレン−ビス（ビニルスルホニルアセタミド）エタンなど）、Ｎ−メチロール系硬膜剤（ジメチロール尿素など）、ほう酸、メタほう酸あるいは高分子硬膜剤（特開昭６２−２３４１５７号公報などに記載の化合物）が挙げられる。
好ましくはビニルスルホン系硬膜剤やクロロトリアジン類が挙げられる。
本発明においてさらに好ましい硬膜剤は下記一般式（Ｂ）または（Ｃ）で表される化合物である。
一般式（Ｂ）
(ＣＨ₂＝ＣＨ−ＳＯ₂)n−Ｌ
一般式（Ｃ）
(Ｘ−ＣＨ₂−ＣＨ₂−ＳＯ₂)n−Ｌ
一般式（Ｂ）、（Ｃ）中でＸはハロゲン原子を表し、Ｌはｎ価の有機連結基を表す。一般式（Ｂ）または（Ｃ）で表される化合物が低分子化合物である場合ｎは１ないし４の整数を表す。高分子化合物である場合Ｌはポリマー鎖を含む有機連結基であり、このときｎは１０〜１０００の範囲である。 <Hardener>
In the present invention, it is preferable to use a crosslinking agent.
The hardener preferably used in the present invention as a crosslinking agent can be added to a coating layer (for example, a receiving layer, a heat insulating layer, a subbing layer) of the image receiving sheet.
Examples of the hardening agent that can be used in the present invention include H-1,4,6,8,14 on page 17 of JP-A-1-214845, column 13 to U.S. Pat. No. 4,618,573. 23 compounds (H-1 to 54) represented by formulas (VII) to (XII), compounds (H-1 to 76) represented by formula (6) at the lower right of JP-A-2-214852, page 8, In particular, H-14 and the compounds described in claim 1 of US Pat. No. 3,325,287 are preferably used. Examples of hardeners are US Pat. No. 4,678,739, column 41, US Pat. No. 4,791,042, JP-A-59-116655, JP-A-62-245261, and JP-A-61-18942. And the hardening agent described in JP-A-4-218444 or the specification thereof. More specifically, aldehyde hardeners (formaldehyde, etc.), aziridine hardeners, epoxy hardeners, vinyl sulfone hardeners (N, N′-ethylene-bis (vinylsulfonylacetamide) Ethane), N-methylol hardeners (dimethylolurea, etc.), boric acid, metaboric acid, or polymer hardeners (compounds described in JP-A-62-234157).
Preferably, a vinyl sulfone type hardener and chlorotriazines are used.
More preferable hardeners in the present invention are compounds represented by the following general formula (B) or (C).
General formula (B)
_{(CH 2 = CH-SO 2} ) n-L
General formula (C)
_{(X-CH 2 -CH 2 -SO} 2) n-L
In general formulas (B) and (C), X represents a halogen atom, and L represents an n-valent organic linking group. When the compound represented by formula (B) or (C) is a low molecular compound, n represents an integer of 1 to 4. In the case of a polymer compound, L is an organic linking group containing a polymer chain, and n is in the range of 10 to 1000.

一般式（Ｂ）、（Ｃ）中で、Ｘは好ましくは塩素原子または臭素原子で、臭素原子がより好ましい。ｎは１ないし４の整数であるが、好ましくは２ないし４の整数、より好ましくは２ないし３の整数、最も好ましくは２である。   In the general formulas (B) and (C), X is preferably a chlorine atom or a bromine atom, more preferably a bromine atom. n is an integer of 1 to 4, preferably an integer of 2 to 4, more preferably an integer of 2 to 3, and most preferably 2.

Ｌはｎ価の有機基を表し、好ましくは脂肪族炭化水素基、芳香族炭化水素基またはヘテロ環基であり、これらの基がエーテル結合、エステル結合、アミド結合、スルホンアミド結合、ウレア結合、ウレタン結合等でさらに連結していてもよい。また、これらの基は置換基を有していてもよく、ハロゲン原子、アルキル基、アリール基、ヘテロ環基、ヒドロキシル基、アルコキシ基、アリールオキシ基、アルキルチオ基、アリールチオ基、アシルオキシ基、アルコキシカルボニル基、カルバモイルオキシ基、アシル基、アシルオキシ基、アシルアミノ基、スルホンアミド基、カルバモイル基、スルファモイル基、スルホニル基、ホスホリル基、カルボキシル基、スルホ基等が挙げられ、ハロゲン原子、アルキル基、ヒドロキシ基、アルコキシ基、アリールオキシ基およびアシルオキシ基が好ましい。   L represents an n-valent organic group, preferably an aliphatic hydrocarbon group, an aromatic hydrocarbon group or a heterocyclic group, and these groups are ether bond, ester bond, amide bond, sulfonamide bond, urea bond, It may be further connected with a urethane bond or the like. These groups may have a substituent, such as a halogen atom, alkyl group, aryl group, heterocyclic group, hydroxyl group, alkoxy group, aryloxy group, alkylthio group, arylthio group, acyloxy group, alkoxycarbonyl. Groups, carbamoyloxy groups, acyl groups, acyloxy groups, acylamino groups, sulfonamido groups, carbamoyl groups, sulfamoyl groups, sulfonyl groups, phosphoryl groups, carboxyl groups, sulfo groups, etc., halogen atoms, alkyl groups, hydroxy groups, Alkoxy groups, aryloxy groups and acyloxy groups are preferred.

ビニルスルホン系硬膜剤の具体的な例として下記（ＶＳ−１）〜（ＶＳ−２７）を挙げるが、本発明においては、これらに限定されない。   Specific examples of the vinyl sulfone hardener include the following (VS-1) to (VS-27), but are not limited to these in the present invention.

これらの硬膜剤は、米国特許第４，１７３，４８１号明細書等の記載の方法を参照して得ることができる。
また、クロロトリアジン系硬膜剤としては、少なくとも１個のクロル原子が、２位、４位または６位に置換した１，３，５−トリアジン化合物が好ましい。
塩素原子は、２位、４位または６位に、２個または３個置換したものもがより好ましい。２位、４位または６位に、少なくとも１個の塩素原子が置換して、残りの位置に、塩素原子以外の基が置換してもよく、これらの基としては、水素原子、臭素原子、フッ素原子、沃素原子、アルキル基、アルケニル基、アルキニル基、シクロアルキル基、シクロアルケニル基、アリール基、ヘテロ環基、ヒドロキシ基、ニトロ基、シアノ基、アミノ基、ヒドロキシルアミノ基、アルキルアミノ基、アリールアミノ基、ヘテロ環アミノ基、アシルアミノ基、スルホンアミド基、カルバモイル基、スルファモイル基、スルホ基、カルボキシル基、アルコキシ基、アルケノキシ基、アリールオキシ基、ヘテロ環オキシ基、アシル基、アシルオキシ基、アルキルもしくはアリールスルホニル基、アルキルもしくはアリールスルフィニル基、アルキルもしくはアリールスルホニルオキシ基、メルカプト基、アルキルチオ基、アルケニルチオ基、アリールチオ基、ヘテロ環チオ基、アルキルオキシもしくはアリールオキシカルボニル基などが挙げられる。
クロロトリアジン系硬膜剤の具体的な例は、４，６−ジクロロ−２−ヒドロキシ−１，３，５−トリアジンもしくはこのＮａ塩、２−クロロ−４，６−ジフェノキシトリアジン、２−クロロ−４，６−ビス〔２，４，６−トリメチルフェノキシ〕トリアジン、２−ク
ロロ−４，６−ジグリシドキシ−１，３，５−トリアジン、２−クロロ−４−（ｎ−ブトキシ）−６−グリシドキシ−１，３，５−トリアジン、２−クロロ−４−（２，４，６−トリメチルフェノキシ）−６−グリシドキシ−１，３，５−トリアジン、２−クロロ−４−（２−クロロエトキシ）−６−（２，４，６−トリメチルフェノキシ）１，３，５−トリアジン、２−クロロ−４−（２−ブロモエトキシ）−６−（２，４，６−トリメチルフェノキシ）−１，３，５−トリアジン、２−クロロ−４−（２−ジ−ｎ−ブチルホスファトエトキシ）−６−（２，４，６−トリメチルフェノキシ）−１，３，５−トリアジン、２−クロロ−４−（２−ジ−ｎ−ブチルホスファトエトキシ）−６−（２，６−キシレノキシ）−１，３，５−トリアジン等であるが、本発明においてこれらに限定されない。
このような化合物は、塩化シアヌル（すなわち２，４，６−トリクロロトリアジン）を、複素環上の置換基に対応するヒドロキシ化合物、チオ化合物またはアミノ化合物等と反応させることによって容易に製造できる。 These hardeners can be obtained by referring to the method described in US Pat. No. 4,173,481.
As the chlorotriazine hardener, a 1,3,5-triazine compound in which at least one chloro atom is substituted at the 2-position, 4-position or 6-position is preferable.
More preferred are those in which 2 or 3 chlorine atoms are substituted at the 2nd, 4th or 6th position. At least one chlorine atom may be substituted at the 2-position, 4-position or 6-position, and a group other than a chlorine atom may be substituted at the remaining positions. Examples of these groups include a hydrogen atom, a bromine atom, Fluorine atom, iodine atom, alkyl group, alkenyl group, alkynyl group, cycloalkyl group, cycloalkenyl group, aryl group, heterocyclic group, hydroxy group, nitro group, cyano group, amino group, hydroxylamino group, alkylamino group, Arylamino group, heterocyclic amino group, acylamino group, sulfonamido group, carbamoyl group, sulfamoyl group, sulfo group, carboxyl group, alkoxy group, alkenoxy group, aryloxy group, heterocyclic oxy group, acyl group, acyloxy group, alkyl Or arylsulfonyl group, alkyl or arylsulfinyl group, alkyl Ku is arylsulfonyloxy group, a mercapto group, an alkylthio group, an alkenylthio group, an arylthio group, a heterocyclic thio group, such as alkyloxy or aryloxy carbonyl group.
Specific examples of the chlorotriazine hardener include 4,6-dichloro-2-hydroxy-1,3,5-triazine or its Na salt, 2-chloro-4,6-diphenoxytriazine, 2-chloro. -4,6-bis [2,4,6-trimethylphenoxy] triazine, 2-chloro-4,6-diglycidoxy-1,3,5-triazine, 2-chloro-4- (n-butoxy) -6 Glycidoxy-1,3,5-triazine, 2-chloro-4- (2,4,6-trimethylphenoxy) -6-glycidoxy-1,3,5-triazine, 2-chloro-4- (2-chloroethoxy ) -6- (2,4,6-trimethylphenoxy) 1,3,5-triazine, 2-chloro-4- (2-bromoethoxy) -6- (2,4,6-trimethylphenoxy) -1, 3,5-tri 2-chloro-4- (2-di-n-butylphosphatoethoxy) -6- (2,4,6-trimethylphenoxy) -1,3,5-triazine, 2-chloro-4- (2 -Di-n-butylphosphatoethoxy) -6- (2,6-xylenoxy) -1,3,5-triazine and the like, but not limited thereto.
Such a compound can be easily produced by reacting cyanuric chloride (that is, 2,4,6-trichlorotriazine) with a hydroxy compound, a thio compound or an amino compound corresponding to a substituent on the heterocyclic ring.

これらの硬膜剤は、水溶性ポリマー１ｇあたり０．００１〜１ｇ、好ましくは０．００５〜０．５ｇが用いられる。   These hardeners are used in an amount of 0.001 to 1 g, preferably 0.005 to 0.5 g, per 1 g of water-soluble polymer.

＜乳化物＞
本発明の感熱転写受像シートの受容層には、乳化物を含有することが好ましい。本発明に好ましく用いられる乳化物について、以下に説明する。
滑剤、酸化防止剤などの疎水性添加剤は米国特許第２，３２２，０２７号明細書に記載の方法などの公知の方法により受像シートの層（例えば、受容層、断熱層、下塗層など）中に導入することができる。この場合には、米国特許第４，５５５，４７０号、同第４，５３６，４６６号、同第４，５３６，４６７号、同第４，５８７，２０６号、同第４，５５５，４７６号、同第４，５９９，２９６号、特公平３−６２２５６号の公報または明細書などに記載のような高沸点有機溶媒を、必要に応じて沸点５０℃〜１６０℃の低沸点有機溶媒と併用して用いることができる。またこれら滑剤や酸化防止剤、高沸点有機溶媒などは２種以上併用することができる。 <Emulsions>
The receiving layer of the heat-sensitive transfer image-receiving sheet of the present invention preferably contains an emulsion. The emulsion preferably used in the present invention will be described below.
Hydrophobic additives such as lubricants and antioxidants can be obtained by a known method such as the method described in US Pat. No. 2,322,027, such as a layer of an image receiving sheet (for example, a receiving layer, a heat insulating layer, an undercoat layer, etc.). ) Can be introduced in. In this case, U.S. Pat. Nos. 4,555,470, 4,536,466, 4,536,467, 4,587,206, 4,555,476 No. 4,599,296, JP-B-3-62256, or a high boiling point organic solvent described in the specification or the like, if necessary, in combination with a low boiling point organic solvent having a boiling point of 50 ° C. to 160 ° C. Can be used. These lubricants, antioxidants, high-boiling organic solvents and the like can be used in combination of two or more.

酸化防止剤（以下に本明細書ではラジカル捕捉剤とも称す）としては下記一般式（Ｅ−１）〜（Ｅ−３）のいずれかで表される化合物が好ましく用いられる。   As the antioxidant (hereinafter also referred to as a radical scavenger), a compound represented by any one of the following general formulas (E-1) to (E-3) is preferably used.

Ｒ₄₁は脂肪族基、アリール基、ヘテロ環基、アシル基、脂肪族オキシカルボニル基、アリールオキシカルボニル基、脂肪族スルホニル基、アリールスルホニル基、フォスホリル基または-Ｓｉ(Ｒ₄₇)(Ｒ₄₈)(Ｒ₄₉)を表す。ここで、Ｒ₄₇、Ｒ₄₈及びＲ₄₉は各々独立に脂
肪族基、アリール基、脂肪族オキシ基またはアリールオキシ基を表す。Ｒ₄₂〜Ｒ₄₆は水素原子または置換基を表す。該置換基としては、ハロゲン原子、脂肪族基（アルキル基、アルケニル基、アルキニル基、シクロアルキル基、シクロアルケニル基を包含する）、アリール基、ヘテロ環基、ヒドロキシ基、メルカプト基、脂肪族オキシ基、アリールオキシ基、ヘテロ環オキシ基、脂肪族チオ基、アリールチオ基、ヘテロ環チオ基、アミノ基、脂肪族アミノ基、アリールアミノ基、ヘテロ環アミノ基、アシルアミノ基、スルホンアミド基、シアノ基、ニトロ基、カルバモイル基、スルファモイル基、アシル基、脂肪族オキシカルボニル基、アリールオキシカルボニル基などが挙げられる。Ｒ_a1〜Ｒ_a4は各々独立に、水素原子または脂肪族基（例えばメチル、エチル）を表す。
一般式（Ｅ−１）〜（Ｅ−３）のいずれかで表わされる化合物について、本発明の効果の点での好ましい置換基について述べる。
一般式（Ｅ−１）〜（Ｅ−３）において、Ｒ₄₁は脂肪族基、アシル基、脂肪族オキシカルボニル基、アリールオキシカルボニル基またはフォスホリル基であって、Ｒ₄₂、Ｒ₄₃、Ｒ₄₅及びＲ₄₆は各々独立に、水素原子、脂肪族基、脂肪族オキシ基またはアシルアミノ基である場合が好ましく、Ｒ₄₁は脂肪族基であって、Ｒ₄₂、Ｒ₄₃、Ｒ₄₅及びＲ₄₆は各々独立に、水素原子または脂肪族基である場合はさらに好ましい。
以下に、一般式（Ｅ−１）〜（Ｅ−３）のいずれかで表される好ましい具体例を以下に示すが、本発明はこれらに限定されるものではない。 R ₄₁ is an aliphatic group, aryl group, heterocyclic group, acyl group, aliphatic oxycarbonyl group, aryloxycarbonyl group, aliphatic sulfonyl group, arylsulfonyl group, phosphoryl group, or —Si (R ₄₇ ) (R ₄₈ ). (R ₄₉ ) is represented. Here, R ₄₇ , R ₄₈ and R ₄₉ each independently represents an aliphatic group, an aryl group, an aliphatic oxy group or an aryloxy group. R _{42 to} R ₄₆ represent a hydrogen atom or a substituent. Examples of the substituent include halogen atoms, aliphatic groups (including alkyl groups, alkenyl groups, alkynyl groups, cycloalkyl groups, and cycloalkenyl groups), aryl groups, heterocyclic groups, hydroxy groups, mercapto groups, aliphatic oxy groups. Group, aryloxy group, heterocyclic oxy group, aliphatic thio group, arylthio group, heterocyclic thio group, amino group, aliphatic amino group, arylamino group, heterocyclic amino group, acylamino group, sulfonamide group, cyano group Nitro group, carbamoyl group, sulfamoyl group, acyl group, aliphatic oxycarbonyl group, aryloxycarbonyl group and the like. R _{a1 to} R _a4 each independently represents a hydrogen atom or an aliphatic group (for example, methyl, ethyl).
With respect to the compound represented by any one of the general formulas (E-1) to (E-3), preferred substituents in terms of the effects of the present invention will be described.
In the general formulas (E-1) to (E-3), R ₄₁ is an aliphatic group, an acyl group, an aliphatic oxycarbonyl group, an aryloxycarbonyl group, or a phosphoryl group, and R ₄₂ , R ₄₃ , R ₄₅ And R ₄₆ are each independently preferably a hydrogen atom, an aliphatic group, an aliphatic oxy group or an acylamino group, R ₄₁ is an aliphatic group, and R ₄₂ , R ₄₃ , R ₄₅ and R ₄₆ are It is more preferable that each independently represents a hydrogen atom or an aliphatic group.
Although the preferable specific example represented by either of general formula (E-1)-(E-3) below is shown below, this invention is not limited to these.

酸化防止剤の含有量はポリマーラテックス中の固形分に対して好ましくは、１．０〜７．０質量％、より好ましくは２．５〜５．０質量％である。   The content of the antioxidant is preferably 1.0 to 7.0% by mass, more preferably 2.5 to 5.0% by mass, based on the solid content in the polymer latex.

滑剤としては、例えば、ポリエチレンワックス、アミドワックス、テフロン（登録商標）パウダー等の固形ワックス類；シリコーンオイル、リン酸エステル系化合物、フッ素系界面活性剤、シリコーン系界面活性剤およびその他当該技術分野で公知の離型剤を使用することができ、フッ素系界面活性剤等に代表されるフッ素系化合物、シリコーン系界面活性剤、シリコーンオイル及び／又はその硬化物等のシリコーン系化合物が好ましく用いられる。滑剤の含有量はポリマーラテックス中の固形分に対して好ましくは、１．０〜１０．０質量％、より好ましくは１．５〜２．５質量％である。   Examples of the lubricant include solid waxes such as polyethylene wax, amide wax, and Teflon (registered trademark) powder; silicone oil, phosphate ester compounds, fluorine surfactants, silicone surfactants, and other in the technical field. A known release agent can be used, and a fluorine-based compound represented by a fluorine-based surfactant, a silicone-based surfactant, a silicone oil such as a silicone oil and / or a cured product thereof is preferably used. The content of the lubricant is preferably 1.0 to 10.0% by mass, more preferably 1.5 to 2.5% by mass, based on the solid content in the polymer latex.

滑剤としてのシリコーンオイルとしては、ストレートシリコーンオイル、および変性シリコーンオイルやその硬化物が使用できる。ストレートシリコーンオイルには、ジメチルシリコーンオイル、メチルフェニルシリコーンオイル、メチルハイドロジェンシリコーンオイルがあり、ジメチルシリコーンオイルとしては、ＫＦ９６−１０、ＫＦ９６−１００、ＫＦ９６−１０００、ＫＦ９６Ｈ−１００００、ＫＦ９６Ｈ−１２５００、ＫＦ９６Ｈ−１０００００（いずれも商品名、信越化学工業(株)製）等を挙げられ、ジメチルシリコーンオイルとしては、ＫＦ５０−１００、ＫＦ５４、ＫＦ５６（いずれも商品名、信越化学工業(株)製）等が挙げられる。   As the silicone oil as the lubricant, straight silicone oil, modified silicone oil and its cured product can be used. Straight silicone oils include dimethyl silicone oil, methylphenyl silicone oil, and methyl hydrogen silicone oil. Examples of dimethyl silicone oil include KF96-10, KF96-100, KF96-1000, KF96H-10000, KF96H-12500, and KF96H. -100,000 (all are trade names, manufactured by Shin-Etsu Chemical Co., Ltd.) and the like, and as dimethyl silicone oil, KF50-100, KF54, KF56 (all are trade names, manufactured by Shin-Etsu Chemical Co., Ltd.), etc. Can be mentioned.

変性シリコーンオイルは、反応性シリコーンオイルと非反応性シリコーンオイルに分類
できる。反応性シリコーンオイルには、アミノ変性、エポキシ変性、カルボキシル変性、ヒドロキシ変性、メタクリル変性、メルカプト変性、フェノール変性、片末端反応性・異種官能基変性がある。アミノ変性シリコーンオイルとしては、ＫＦ−３９３、ＫＦ−８５７、ＫＦ−８５８、Ｘ−２２−３６８０、Ｘ−２２−３８０１Ｃ、ＫＦ−８０１０、Ｘ−２２−１６１Ａ、ＫＦ−８０１２（いずれも商品名、信越化学工業(株)製）等が挙げられ、エポキシ変性シリコーンオイルとしては、ＫＦ−１００Ｔ、ＫＦ−１０１、ＫＦ−６０−１６４、ＫＦ−１０３、Ｘ−２２−３４３、Ｘ−２２−３０００Ｔ（いずれも商品名、信越化学工業(株)製）等が挙げられる。カルボキシル変性シリコーンオイルとしては、Ｘ−２２−１６２Ｃ（商品名、信越化学工業(株)製）等が挙げられ、ヒドロキシ変性シリコーンオイルとしては、Ｘ−２２−１６０ＡＳ、ＫＦ−６００１、ＫＦ−６００２、ＫＦ−６００３、Ｘ−２２−１７０ＤＸ、Ｘ−２２−１７６ＤＸ、Ｘ−２２−１７６Ｄ、Ｘ−２２−１７６ＤＦ（いずれも商品名、信越化学工業(株)製）等が挙げられ、メタクリル変性シリコーンオイルとしては、Ｘ−２２−１６４Ａ、Ｘ−２２−１６４Ｃ、Ｘ−２４−８２０１、Ｘ−２２−１７４Ｄ、Ｘ−２２−２４２６（いずれも商品名、信越化学工業(株)製）等が挙げられる。 The modified silicone oil can be classified into a reactive silicone oil and a non-reactive silicone oil. The reactive silicone oil includes amino modification, epoxy modification, carboxyl modification, hydroxy modification, methacryl modification, mercapto modification, phenol modification, one-terminal reactivity and heterofunctional modification. As amino-modified silicone oil, KF-393, KF-857, KF-858, X-22-3680, X-22-3801C, KF-8010, X-22-161A, KF-8012 (all trade names, Shin-Etsu Chemical Co., Ltd.) and the like, and epoxy-modified silicone oils include KF-100T, KF-101, KF-60-164, KF-103, X-22-343, X-22-3000T ( All of them are trade names, manufactured by Shin-Etsu Chemical Co., Ltd.). Examples of the carboxyl-modified silicone oil include X-22-162C (trade name, manufactured by Shin-Etsu Chemical Co., Ltd.). Examples of the hydroxy-modified silicone oil include X-22-160AS, KF-6001, KF-6002, KF-6003, X-22-170DX, X-22-176DX, X-22-176D, X-22-176DF (all trade names, manufactured by Shin-Etsu Chemical Co., Ltd.) X-22-164A, X-22-164C, X-24-8201, X-22-174D, X-22-2426 (all are trade names, manufactured by Shin-Etsu Chemical Co., Ltd.) and the like. .

反応性シリコーンオイルとしては、硬化させて使用することもでき、反応硬化型、光硬化型、触媒硬化型等に分類できる。このなかで反応硬化型のシリコーンオイルが特に好ましく、反応硬化型シリコーンオイルとしては、アミノ変性シリコーンオイルとエポキシ変性シリコーンオイルとを反応硬化させたものが好ましい。また、触媒硬化型あるいは光硬化型シリコーンオイルとしては、ＫＳ−７０５Ｆ−ＰＳ、ＫＳ−７０５Ｆ−ＰＳ−１、ＫＳ−７７０−ＰＬ−３〔触媒硬化型シリコーンオイル：いずれも商品名、信越化学工業(
株)製〕、ＫＳ−７２０、ＫＳ−７７４−ＰＬ−３〔光硬化型シリコーンオイル：いずれ
も商品名、信越化学工業(株)製〕等が挙げられる。これら硬化型シリコーンオイルの添加量は受容層を構成する樹脂の０．５〜３０質量％が好ましい。離型剤は、ポリエステル樹脂１００質量部に対して２〜４質量％、好ましくは２〜３質量％程度使用する。その量が少なすぎると、離型性を確実に確保することができず、また多すぎると保護層が受像シートに転写しなくなってしまう。 The reactive silicone oil can be used after being cured, and can be classified into a reaction curable type, a photo curable type, a catalyst curable type, and the like. Of these, reaction-curable silicone oils are particularly preferable. As the reaction-curable silicone oils, those obtained by reaction-curing amino-modified silicone oil and epoxy-modified silicone oil are preferable. Further, as the catalyst curable type or photo curable type silicone oil, KS-705F-PS, KS-705F-PS-1, KS-770-PL-3 [catalyst curable type silicone oil: all trade names, Shin-Etsu Chemical Co., Ltd. (
Co., Ltd.], KS-720, KS-774-PL-3 [photocured silicone oil: trade names, manufactured by Shin-Etsu Chemical Co., Ltd.], and the like. The addition amount of these curable silicone oils is preferably 0.5 to 30% by mass of the resin constituting the receiving layer. The release agent is used in an amount of 2 to 4% by mass, preferably about 2 to 3% by mass, based on 100 parts by mass of the polyester resin. If the amount is too small, the releasability cannot be ensured, and if the amount is too large, the protective layer will not be transferred to the image receiving sheet.

非反応性シリコーンオイルとしては、ポリエーテル変性、メチルスチリル変性、アルキル変性、高級脂肪酸エステル変性、親水性特殊変性、高級アルコキシ変性、フッ素変性等がある。ポリエーテル変性シリコーン（ＫＦ−６０１２、商品名、信越化学工業(株)製）が挙げられ、メチルスチル変性シリコーンシリコーンオイルとしては、（２４−５１０、ＫＦ４１−４１０、いずれも商品名、信越化学工業(株)製）等が挙げられる。また、下記一般式１〜３のいずれかで表される変性シリコーンも使用することができる。   Non-reactive silicone oils include polyether modification, methylstyryl modification, alkyl modification, higher fatty acid ester modification, hydrophilic special modification, higher alkoxy modification, fluorine modification and the like. Examples include polyether-modified silicone (KF-6012, trade name, manufactured by Shin-Etsu Chemical Co., Ltd.), and methylstil-modified silicone silicone oils (24-510, KF41-410, both trade names, Shin-Etsu Chemical ( Etc.). Moreover, the modified silicone represented by either of the following general formulas 1-3 can also be used.

一般式１中、Ｒは水素原子、またはアリール基、若しくはシクロアルキル基で置換されても良い直鎖または分岐のアルキル基を表す。ｍ、ｎは２０００以下の整数を表し、ａ、ｂは３０以下の整数を表す。   In General Formula 1, R represents a hydrogen atom, an aryl group, or a linear or branched alkyl group that may be substituted with a cycloalkyl group. m and n represent an integer of 2000 or less, and a and b represent an integer of 30 or less.

一般式２中、Ｒは水素原子、またはアリール基、若しくはシクロアルキル基で置換されても良い直鎖または分岐のアルキル基を表す。ｍは２０００以下の整数を表し、ａ、ｂは３０以下の整数を表す。   In General Formula 2, R represents a hydrogen atom, an aryl group, or a linear or branched alkyl group which may be substituted with a cycloalkyl group. m represents an integer of 2000 or less, and a and b represent an integer of 30 or less.

一般式３中、Ｒは水素原子、またはアリール基、若しくはシクロアルキル基で置換されても良い直鎖または分岐のアルキル基を表す。ｍ、ｎは２０００以下の整数を表し、ａ、ｂは３０以下の整数を表す。Ｒ¹は単結合または２価の連結基を表し、Ｅは置換基を有し
てもよいエチレン基を表し、Ｐは置換基を有してもよいプロピレン基を表す。 In General Formula 3, R represents a hydrogen atom, an aryl group, or a linear or branched alkyl group which may be substituted with a cycloalkyl group. m and n represent an integer of 2000 or less, and a and b represent an integer of 30 or less. R ¹ represents a single bond or a divalent linking group, E represents an ethylene group which may have a substituent, and P represents a propylene group which may have a substituent.

上記のようなシリコーンオイルは「シリコーンハンドブック」（日刊工業新聞社刊）に記載されており、硬化型シリコーンオイルの硬化技術として、特開平８−１０８６３６号公報や特開２００２−２６４５４３号公報に記載の技術が好ましく使用できる。   Silicone oils such as those described above are described in “Silicone Handbook” (published by Nikkan Kogyo Shimbun Co., Ltd.), and are described in JP-A-8-108636 and JP-A-2002-264543 as curing technologies for curable silicone oils. The technique can be preferably used.

高沸点有機溶媒としては、フタル酸エステル類（フタル酸ジブチル、フタル酸ジオクチル、フタル酸ジ−２−エチルヘキシル等）、リン酸またはホスホン酸エステル類（リン酸トリフェニル、リン酸トリクレジル、リン酸トリ−２−エチルヘキシル等）、脂肪酸エステル類（コハク酸ジ−２−エチルヘキシル、クエン酸トリブチル等）、安息香酸エステル類（安息香酸２−エチルヘキシル、安息香酸ドデシル等）、アミド類（Ｎ，Ｎ−ジエチルドデカンアミド、Ｎ，Ｎ−ジメチルオレインアミド等）、アルコールまたはフェノール類（イソステアリルアルコール、２，４−ジ−ｔｅｒｔ−アミルフェノール等）、アニリン類（Ｎ，Ｎ−ジブチル−２−ブトキシ−５−ｔｅｒｔ−オクチルアニリン等）、塩素化パラフィン類、炭化水素類（ドデシルベンゼン、ジイソプロピルナフタレン等）、カルボン酸類（２−（２，４−ジ−ｔｅｒｔ−アミルフェノキシ）酪酸等が挙げられる。
好ましくは以下の化合物が用いられる。 High boiling point organic solvents include phthalates (dibutyl phthalate, dioctyl phthalate, di-2-ethylhexyl phthalate, etc.), phosphoric acid or phosphonic esters (triphenyl phosphate, tricresyl phosphate, triphosphate phosphate) 2-ethylhexyl, etc.), fatty acid esters (di-2-ethylhexyl succinate, tributyl citrate, etc.), benzoates (2-ethylhexyl benzoate, dodecyl benzoate, etc.), amides (N, N-diethyl, etc.) Dodecanamide, N, N-dimethyloleamide, etc.), alcohol or phenols (isostearyl alcohol, 2,4-di-tert-amylphenol, etc.), anilines (N, N-dibutyl-2-butoxy-5-) tert-octylaniline, etc.), chlorinated paraffins, hydrocarbons (dode) Rubenzen, diisopropyl naphthalene), carboxylic acids (2- (2,4-di -tert- amylphenoxy) butyric acid, and the like.
The following compounds are preferably used.

また、補助溶媒として沸点が３０℃以上１６０℃以下の有機溶媒（酢酸エチル、酢酸ブチル、メチルエチルケトン、シクロヘキサノン、メチルセロソルブアセテート等）を併用しても良い。高沸点有機溶媒の量は用いられる疎水性添加剤１ｇに対して１０ｇ以下、好ましくは５ｇ以下、より好ましくは１ｇ〜０．１ｇである。また、バインダー１ｇに対して１ミリリットル以下、更には０．５ミリリットル以下、特に０．３ミリリットル以下が適当である。   Further, an organic solvent (such as ethyl acetate, butyl acetate, methyl ethyl ketone, cyclohexanone, or methyl cellosolve acetate) having a boiling point of 30 ° C. or higher and 160 ° C. or lower may be used in combination as an auxiliary solvent. The amount of the high-boiling organic solvent is 10 g or less, preferably 5 g or less, more preferably 1 g to 0.1 g based on 1 g of the hydrophobic additive used. In addition, 1 milliliter or less, further 0.5 milliliter or less, particularly 0.3 milliliter or less is appropriate for 1 g of binder.

特公昭５１−３９８５３号、特開昭５１−５９９４３号の各公報に記載されている重合物による分散法や特開昭６２−３０２４２号公報等に記載されている微粒子分散物にして添加する方法も使用できる。水に実質的に不溶な化合物の場合には、前記方法以外にバインダー中に微粒子にして分散含有させることができる。
疎水性化合物を親水性コロイドに分散する際には、種々の界面活性剤を用いることができる。例えば特開昭５９−１５７６３６号公報の３７〜３８頁に記載の界面活性剤として挙げたものを使うことができる。また、特開平７−５６２６７号、同７−２２８５８９号、***公開特許第１,９３２,２９９Ａ号の公報または明細書に記載のリン酸エステル型界面活性剤も使用することができる。 A dispersion method using a polymer described in JP-B-51-39853 and JP-A-51-59943, or a fine particle dispersion described in JP-A-62-22422, etc. Can also be used. In the case of a compound that is substantially insoluble in water, it can be dispersed and contained as fine particles in a binder other than the above method.
In dispersing the hydrophobic compound in the hydrophilic colloid, various surfactants can be used. For example, the surfactants described in JP-A No. 59-157636, pages 37 to 38 can be used. Further, phosphate ester type surfactants described in JP-A-7-56267, JP-A-7-228589 and West German Patent No. 1,932,299A or the specification can also be used.

＜紫外線吸収剤＞
また、本発明では耐光性を向上するために受容層に紫外線吸収剤が添加してもよい。このとき、紫外線吸収剤を高分子量化することで受容層に固定でき、インクシートへの拡散や加熱による昇華・蒸散などを防ぐことができる。
紫外線吸収剤としては、情報記録分野において広く知られている各種紫外線吸収剤骨格を有する化合物を使用することができる。具体的には、２−ヒドロキシベンゾトリアゾール型紫外線吸収剤、２−ヒドロキシベンゾトリアジン型紫外線吸収剤、２−ヒドロキシベンゾフェノン型紫外線吸収剤骨格を有する化合物を挙げることができる。紫外線吸収能（吸光係数）・安定性の観点では、ベンゾトリアゾール型、トリアジン骨格を有する化合物が好ましく、高分子量化・ラテックス化の観点ではベンゾトリアゾール型、ベンゾフェノン型の骨格を有する化合物が好ましい。具体的には、特開２００４−３６１９３６号公報などに記載された紫外線吸収剤を用いることができる。 <Ultraviolet absorber>
In the present invention, an ultraviolet absorber may be added to the receiving layer in order to improve light resistance. At this time, the UV absorber can be fixed to the receiving layer by increasing the molecular weight, and can be prevented from being diffused into the ink sheet or sublimation / transpiration due to heating.
As the ultraviolet absorber, compounds having various ultraviolet absorber skeletons widely known in the field of information recording can be used. Specific examples include 2-hydroxybenzotriazole type ultraviolet absorbers, 2-hydroxybenzotriazine type ultraviolet absorbers, and compounds having a 2-hydroxybenzophenone type ultraviolet absorber skeleton. A compound having a benzotriazole type or triazine skeleton is preferable from the viewpoint of ultraviolet absorption ability (absorption coefficient) / stability, and a compound having a benzotriazole type or benzophenone type skeleton is preferable from the viewpoint of increasing the molecular weight or forming a latex. Specifically, an ultraviolet absorber described in JP 2004-361936 A can be used.

紫外線吸収剤は、紫外域に吸収をもち、可視領域に吸収端がかからないことが好ましい。具体的には、受容層に添加して感熱転写受像シートを形成したとき、３７０ｎｍの反射濃度がＡｂｓ０．５以上になることが好ましく、３８０ｎｍの反射濃度がＡｂｓ０．５以上になることが更に好ましい。また、４００ｎｍの反射濃度がＡｂｓ０．１以下であることが好ましい。なお、４００ｎｍを超える範囲での反射濃度が高いと画像が黄ばむため好ましくない。   The ultraviolet absorber preferably has absorption in the ultraviolet region and does not have an absorption edge in the visible region. Specifically, when added to the receiving layer to form a thermal transfer image-receiving sheet, the reflection density at 370 nm is preferably Abs 0.5 or more, and the reflection density at 380 nm is more preferably Abs 0.5 or more. . The reflection density at 400 nm is preferably Abs 0.1 or less. A high reflection density in the range exceeding 400 nm is not preferable because the image is yellowed.

本発明では、紫外線吸収剤は高分子量化され、重量平均分子量１００００以上が好ましく、重量平均分子量１０００００以上が更に好ましい。高分子量化する手段としては、紫外線吸収剤をポリマーにグラフトすることが好ましい。主鎖となるポリマーとしては、併用する受容ポリマーより色素の染着性が劣るポリマー骨格を有することが好ましい。また、製膜した際に十分な皮膜強度を有することが好ましい。ポリマー主鎖に対する紫外線吸収剤のグラフト率は、５〜２０質量％が好ましく、８〜１５質量％がより好ましい。   In the present invention, the ultraviolet absorber has a high molecular weight, preferably a weight average molecular weight of 10,000 or more, and more preferably a weight average molecular weight of 100,000 or more. As a means for increasing the molecular weight, it is preferable to graft an ultraviolet absorber onto the polymer. The polymer that becomes the main chain preferably has a polymer skeleton that is inferior in dyeability to the dye used in combination. Moreover, it is preferable to have sufficient film strength when the film is formed. The graft ratio of the ultraviolet absorber to the polymer main chain is preferably 5 to 20% by mass, and more preferably 8 to 15% by mass.

また、紫外線吸収剤をグラフトしたポリマーはラテックス化することが更に好ましい。ラテックス化することにより水分散系の塗布液を塗布製膜することにより受容層を形成することができ、製造コストを軽減することが可能である。ラテックス化する方法は例えば特許第３４５０３３９号明細書などに記載された方法を用いることができる。ラテックス化された紫外線吸収剤としては、例えば一方社油脂工業株式会社製ＵＬＳ−７００、ＵＬＳ−１７００、ＵＬＳ−１３８３ＭＡ、ＵＬＳ−１６３５ＭＨ、ＸＬ−７０１６、ＵＬＳ−９３３ＬＰ、ＵＬＳ−９３５ＬＨ、新中村化学製Ｎｅｗ Ｃｏａｔ ＵＶＡ−１０２５Ｗ、Ｎｅｗ Ｃｏａｔ ＵＶＡ−２０４Ｗ、Ｎｅｗ Ｃｏａｔ ＵＶＡ−４５１２Ｍ（いずれも商品名）など市販の紫外線吸収剤を使用することもできる。
紫外線吸収剤をグラフトしたポリマーをラテックス化する場合、前記の染着性受容ポリマーのラテックスと混合してから塗布することで紫外線吸収剤が均一に分散した受容層を形成することができる。 Moreover, it is more preferable that the polymer grafted with the ultraviolet absorber is made into a latex. The receptor layer can be formed by forming an aqueous dispersion type coating solution into a latex to form a latex, and the manufacturing cost can be reduced. For example, the method described in Japanese Patent No. 3450339 can be used as a method for forming a latex. Examples of the latex-made ultraviolet absorber include ULS-700, ULS-1700, ULS-1383MA, ULS-1635MH, XL-7016, ULS-933LP, ULS-935LH, Shin-Nakamura Chemical Co., Ltd. Commercially available ultraviolet absorbers such as New Coat UVA-1025W, New Coat UVA-204W, and New Coat UVA-4512M (both are trade names) can also be used.
When the polymer to which the ultraviolet absorber is grafted is made into a latex, it is possible to form a receiving layer in which the ultraviolet absorber is uniformly dispersed by mixing with the latex of the above-mentioned dyeable receiving polymer and applying it.

紫外線吸収剤をグラフトしたポリマー又はそのラテックスの添加量は、受容層を形成する染着性受容ポリマーラテックスに対して５〜５０質量部が好ましく、１０〜３０質量部がより好ましい。   The added amount of the polymer grafted with the ultraviolet absorber or the latex thereof is preferably 5 to 50 parts by mass, more preferably 10 to 30 parts by mass with respect to the dyeable accepting polymer latex forming the receptor layer.

＜離型剤＞
また、受容層には、画像形成時に熱転写シートとの熱融着を防ぐために、離型剤を配合することもできる。離型剤は、シリコーンオイル、リン酸エステル系可塑剤フッ素系化合物、及び各種ワックス分散物を用いることができる。特にシリコーンオイル、ワックス分散物が好ましく用いられる。 <Release agent>
In addition, a release agent may be added to the receiving layer in order to prevent thermal fusion with the thermal transfer sheet during image formation. As the mold release agent, silicone oil, phosphate ester plasticizer fluorine compound, and various wax dispersions can be used. In particular, silicone oil and wax dispersion are preferably used.

シリコーンオイルとしては、エポキシ変性、アルキル変性、アミノ変性、カルボキシル変性、アルコール変性、フッ素変性、アルキルアラルキルポリエーテル変性、エポキシ・ポリエーテル変性、ポリエーテル変性等の変性シリコーンオイルが好ましく用いられるが、中でもビニル変性シリコーンオイルとハイドロジェン変性シリコーンオイルとの反応物が良い。離型剤の添加量は、受容ポリマーに対して０．２〜３０質量部が好ましい。   As the silicone oil, modified silicone oils such as epoxy modification, alkyl modification, amino modification, carboxyl modification, alcohol modification, fluorine modification, alkylaralkyl polyether modification, epoxy / polyether modification, and polyether modification are preferably used. A reaction product of vinyl-modified silicone oil and hydrogen-modified silicone oil is preferable. The addition amount of the release agent is preferably 0.2 to 30 parts by mass with respect to the receiving polymer.

ワックス分散物としては、公知の分散物を使用することができる。本発明では、「ワックスとは、常温で固体または半固体のアルキル鎖を持つ有機物」として扱う（「改定 ワックスの性質と応用」（幸書房、１９８９年）の定義に従う）。好ましい化合物の例としては、キャンデリラワックス、カルナウバワックス、ライスワックス、木ロウ、モンタンワックス、オゾケライト、パラフィンワックス、マイクロクリスタリンワックス、ペトロラクタム、フィッシャー・トロプシュワックス、ポリエチレンワックス、モンタンワックス誘導体、パラフィンワックス誘導体、マイクロクリスタリンワックス誘導体、硬化ひまし油、硬化ひまし油誘導体、１２−ヒドロキシステアリン酸、ステアリン酸アミド、無水フタル酸イミド、塩素化炭化水素、その他配合ワックスなどがあげられる。このなかで、カルナウバワックス、モンタンワックス及びその誘導体、パラフィンワックス及びその誘導体、マイクロクリスタリンワックス及びその誘導体、ポリエチレンワックス、ステアリン酸アミドが好ましく、カウナウバワックス、モンダンワックスおよびその誘導体、マイクロクリスタリンワックス、ステアリン酸アミドがより好ましく、モンタンワックス及びその誘導体、マイクロクリスタリンワックスが更に好ましい。
このワックスは融点が２５℃〜１２０℃のものから選ばれ、好ましくは４０℃〜１００℃、更に好ましくは６０℃〜９０℃のものから選ばれる。
ワックスは水分散物が好ましく、更に微粒子化したものがより好ましい。水分散の方法、および微粒子化させる方法は、「改定 ワックスの性質と応用」（幸書房、１９８９年）に記載の方法で達成される。
ワックスの添加量は、受容層全固形量の０．５質量％〜３０質量％であることが好ましく、１質量％〜２０質量％がより好ましく、１．５質量％〜１５質量％が更に好ましい。 A known dispersion can be used as the wax dispersion. In the present invention, “wax is treated as an organic substance having a solid or semi-solid alkyl chain at normal temperature” (according to the definition of “Revised properties and application of wax” (Shoshobo, 1989)). Examples of preferred compounds include candelilla wax, carnauba wax, rice wax, wood wax, montan wax, ozokerite, paraffin wax, microcrystalline wax, petrolactam, Fischer-Tropsch wax, polyethylene wax, montan wax derivatives, paraffin wax. Derivatives, microcrystalline wax derivatives, hardened castor oil, hardened castor oil derivatives, 12-hydroxystearic acid, stearamide, phthalic anhydride, chlorinated hydrocarbons, and other blended waxes. Of these, carnauba wax, montan wax and derivatives thereof, paraffin wax and derivatives thereof, microcrystalline wax and derivatives thereof, polyethylene wax and stearamide are preferred, kaunauba wax, mondan wax and derivatives thereof, and microcrystalline wax. Stearamide is more preferable, and montan wax and derivatives thereof, and microcrystalline wax are more preferable.
This wax is selected from those having a melting point of 25 ° C to 120 ° C, preferably 40 ° C to 100 ° C, more preferably 60 ° C to 90 ° C.
The wax is preferably an aqueous dispersion, and more preferably finely divided. The water dispersion method and the micronization method can be achieved by the methods described in “Revised Wax Properties and Applications” (Sachibo, 1989).
The addition amount of the wax is preferably 0.5% by mass to 30% by mass, more preferably 1% by mass to 20% by mass, and still more preferably 1.5% by mass to 15% by mass of the total solid content of the receiving layer. .

受容層の塗布量は、０．５〜１０ｇ／ｍ²（固形分換算、以下本発明における塗布量は
特に断りのない限り、固形分換算の数値である。）が好ましく、より好ましくは１〜８ｇ／ｍ²、更に好ましくは２〜７ｇ／ｍ²の塗布量が好ましい。受容層の膜厚は１〜２０μｍであることが好ましい。 The coating amount of the receiving layer is preferably 0.5 to 10 g / m ² (in terms of solid content, hereinafter the coating amount in the present invention is a numerical value in terms of solid content unless otherwise specified), and more preferably 1 to 1. 8 g / m ^2, more preferably the coating weight of 2~7g / m ² is preferred. The thickness of the receiving layer is preferably 1 to 20 μm.

（断熱層）
断熱層は、サーマルヘッド等を用いた加熱転写時における熱から支持体を保護する役割を果たす。また、高いクッション性を有するので、基材として紙を用いた場合であっても、印字感度の高い熱転写受像シートを得ることができる。断熱層は１層でも２層以上でも良い。断熱層は、受容層より支持体側に設けられる。 (Insulation layer)
The heat insulating layer serves to protect the support from heat during heat transfer using a thermal head or the like. Moreover, since it has high cushioning properties, a thermal transfer image-receiving sheet with high printing sensitivity can be obtained even when paper is used as the substrate. The heat insulating layer may be one layer or two or more layers. The heat insulating layer is provided on the support side from the receptor layer.

本発明に用いられる受像シートにおいて、断熱層は中空ポリマーを含有することが好ましい。
本発明における中空ポリマーとは粒子内部に独立した気孔を有するポリマー粒子であり、例えば、［１］ポリスチレン、アクリル樹脂、スチレン−アクリル樹脂等により形成された隔壁内部に水などの分散媒が入っており、塗布乾燥後、粒子内の分散媒が粒子外に蒸発して粒子内部が中空となる非発泡型の中空粒子、［２］ブタン、ペンタンなどの低沸点液体を、ポリ塩化ビニリデン、ポリアクリロニトリル、ポリアクリル酸、ポリアクリル酸エステルのいずれか又はそれらの混合物もしくは重合物よりなる樹脂で覆っており、塗工後、加熱により粒子内部の低沸点液体が膨張することにより内部が中空となる発泡型マイクロバルーン、［３］上記の［２］をあらかじめ加熱発泡させて中空ポリマーとしたマイクロバルーンなどが挙げられる。 In the image receiving sheet used in the present invention, the heat insulating layer preferably contains a hollow polymer.
The hollow polymer in the present invention is a polymer particle having independent pores inside the particle. For example, [1] a dispersion medium such as water enters a partition formed by polystyrene, acrylic resin, styrene-acrylic resin or the like. After coating and drying, non-foamed hollow particles in which the dispersion medium in the particles evaporates outside the particles and the inside of the particles becomes hollow, [2] low boiling point liquids such as butane and pentane, polyvinylidene chloride, polyacrylonitrile Foam that is covered with a resin made of polyacrylic acid, polyacrylic acid ester, or a mixture or polymer thereof, and the inside of which is hollowed by the expansion of the low-boiling liquid inside the particles by heating after coating. Type microballoons, and [3] microballoons obtained by heating and foaming the above [2] in advance to form a hollow polymer.

これらの中空ポリマーの粒子サイズは０．１〜２０μｍが好ましく、０．１〜２μｍがより好ましく、０．１〜１μｍが更に好ましく、０.２〜０.８μｍが特に好ましい。サイズが小さすぎると、中空率が下がる傾向があり望まれる断熱性が得られなくなり、サイズが大きすぎると、断熱層の膜厚に対して中空ポリマーの粒子径が大きすぎて平滑な面が得られにくくなり、粗大粒子に起因する塗布故障が発生しやすくなるためである。
中空ポリマーの中空率は、２０〜７０％程度のものが好ましく、２０〜５０％のものがより好ましい。これは、中空率が２０％未満になると十分な断熱性が得られなくなり、中空率が過剰に高くなると、粒子サイズが好ましい範囲では不完全な中空粒子の比率が増えて、十分な膜強度が得られなくなるからである。 The particle size of these hollow polymers is preferably 0.1 to 20 μm, more preferably 0.1 to 2 μm, still more preferably 0.1 to 1 μm, and particularly preferably 0.2 to 0.8 μm. If the size is too small, the hollowness tends to decrease and the desired heat insulating property cannot be obtained.If the size is too large, the particle diameter of the hollow polymer is too large for the film thickness of the heat insulating layer to obtain a smooth surface. This is because it becomes difficult to cause coating failure due to coarse particles.
The hollow ratio of the hollow polymer is preferably about 20 to 70%, more preferably 20 to 50%. This is because when the hollow ratio is less than 20%, sufficient heat insulation cannot be obtained, and when the hollow ratio is excessively high, the ratio of incomplete hollow particles increases within a preferable particle size range, and sufficient film strength is obtained. This is because it cannot be obtained.

本発明での中空ポリマーの中空率とは、透過型電子顕微鏡写真により少なくとも３００個の中空ポリマーの内部空隙の円相当直径と、中空ポリマーの粒子径を各々測定し、それらの数値から以下のように計算して求められる個別中空率（％）を平均して中空ポリマーの中空率（％）とする。   The hollow ratio of the hollow polymer in the present invention is determined by measuring the equivalent circle diameter of the internal voids of at least 300 hollow polymers and the particle diameter of the hollow polymer from transmission electron micrographs. The hollow ratio (%) of the hollow polymer is averaged by calculating the individual hollow ratio (%) obtained by

個別中空率（％）＝（空隙の円相当直径）³／（中空ポリマーの粒子径）³×１００

Individual hollow ratio (%) = (circle equivalent diameter of voids) ³ / (particle diameter of hollow polymer) ³ × 100

中空ポリマーのガラス転移温度（Ｔｇ）は７０℃以上であることが好ましく、１００℃以上であることがより好ましい。中空ポリマーは必要に応じて２種以上混合して使用することができる。   The glass transition temperature (Tg) of the hollow polymer is preferably 70 ° C. or higher, and more preferably 100 ° C. or higher. Two or more types of hollow polymers can be mixed and used as necessary.

このような中空ポリマーは市販されており、前記［１］の具体例としてはローアンドハース社製ローペイク１０５５、大日本インキ社製ボンコートＰＰ−１０００、ＪＳＲ社製ＳＸ８６６（Ｂ）、日本ゼオン社製ニッポールＭＨ５０５５（いずれも商品名）などが挙げられる。前記［２］の具体例としては松本油脂製薬社製のＦ−３０、Ｆ−５０（いずれも商品名）などが挙げられる。前記［３］の具体例としては松本油脂製薬社製のＦ−３０Ｅ、日本フェライト社製エクスパンセル４６１ＤＥ、５５１ＤＥ、５５１ＤＥ２０（いずれも商品名）が挙げられる。これらの中で、前記［１］の系列の中空ポリマーがより好ましく使用できる。   Such hollow polymers are commercially available, and specific examples of the above [1] include Law and Haas Ropaque 1055, Dainippon Ink Boncoat PP-1000, JSR SX866 (B), Nippon Zeon Nippon MH5055 (both are trade names). Specific examples of [2] include F-30 and F-50 (both trade names) manufactured by Matsumoto Yushi Seiyaku Co., Ltd. Specific examples of [3] include F-30E manufactured by Matsumoto Yushi Seiyaku Co., Ltd., EXPANSELL 461DE, 551DE, and 551DE20 (all trade names) manufactured by Nippon Ferrite Co., Ltd. Among these, the hollow polymer of the series [1] can be used more preferably.

中空ポリマーを含む断熱層中にはバインダー樹脂として水分散型樹脂または水溶解型樹脂をバインダーとして含有することが好ましい。本発明で使用されるバインダー樹脂としては、アクリル樹脂、スチレン−アクリル共重合体、ポリスチレン樹脂、ポリビニルアルコール樹脂、酢酸ビニル樹脂、エチレン−酢酸ビニル共重合体、塩化ビニル酢酸ビニル共重合体、スチレンーブタジエン共重合体、ポリ塩化ビニリデン樹脂、セルロース誘導体、カゼイン、デンプン、ゼラチンなどの公知の樹脂を用いることができる。またこれらの樹脂は単独又は混合して用いることができる。   The heat insulating layer containing the hollow polymer preferably contains a water-dispersed resin or a water-soluble resin as a binder resin as a binder resin. Examples of the binder resin used in the present invention include acrylic resins, styrene-acrylic copolymers, polystyrene resins, polyvinyl alcohol resins, vinyl acetate resins, ethylene-vinyl acetate copolymers, vinyl chloride vinyl acetate copolymers, and styrene. Known resins such as butadiene copolymers, polyvinylidene chloride resins, cellulose derivatives, casein, starch, and gelatin can be used. These resins can be used alone or in combination.

断熱層における中空ポリマーの固形分含有量は、バインダー樹脂の固形分含有量を１００質量部としたとき５〜２０００質量部の間であることが好ましく、５〜１０００質量部の間であることがより好ましく、５〜４００質量部の間であることが更に好ましい。また、中空ポリマーの固形分の塗工液に対して占める質量比は、１〜７０質量％が好ましく、１０〜４０質量％がより好ましい。中空ポリマーの比率が少なすぎると十分な断熱性をえることができず、中空ポリマーの比率が多すぎると中空ポリマー同士の結着力が低下し、十分な膜強度が得られず、耐擦過性が悪化する。   The solid content of the hollow polymer in the heat insulating layer is preferably between 5 and 2000 parts by mass, and preferably between 5 and 1000 parts by mass when the solid content of the binder resin is 100 parts by mass. More preferably, it is more preferably between 5 and 400 parts by mass. Moreover, 1-70 mass% is preferable, and, as for the mass ratio which occupies with respect to the coating liquid of the solid content of a hollow polymer, 10-40 mass% is more preferable. If the ratio of the hollow polymer is too small, sufficient heat insulation cannot be obtained, and if the ratio of the hollow polymer is too large, the binding force between the hollow polymers is lowered, sufficient film strength cannot be obtained, and scratch resistance is obtained. Getting worse.

本発明に用いられる受像シートは、断熱層に、中空ポリマー以外に、有機溶剤に耐性の無い樹脂を含まない。有機溶剤に耐性の無い樹脂（色素染着性樹脂）を断熱層に含むと、画像転写後の画像にじみが増大するため好ましくない。これは、断熱層に色素染着性樹脂および中空ポリマーが存在することで、転写後、受容層に染着した色素が、経時で、隣接した断熱層を介して色素の移動が起こるためであると考えられる。
ここで、「有機溶剤に耐性の無い」とは、有機溶剤（メチルエチルケトン、酢酸エチル、ベンゼン、トルエン、キシレンなど）への溶解度が１質量％以下、好ましくは０．５質量％以下であることをいう。例えば前記ポリマーラテックスは、「有機溶剤に耐性の無い樹脂」に含まれる。 The image-receiving sheet used in the present invention does not contain a resin having no resistance to organic solvents in addition to the hollow polymer in the heat insulating layer. If the heat insulating layer contains a resin that is not resistant to organic solvents (pigment dyeing resin), the image bleeding after the image transfer increases, which is not preferable. This is because the dye-stainable resin and the hollow polymer exist in the heat insulating layer, so that the dye dyed on the receiving layer after the transfer moves over time through the adjacent heat-insulating layer. it is conceivable that.
Here, “not resistant to organic solvent” means that the solubility in an organic solvent (methyl ethyl ketone, ethyl acetate, benzene, toluene, xylene, etc.) is 1% by mass or less, preferably 0.5% by mass or less. Say. For example, the polymer latex is included in “resin not resistant to organic solvent”.

また、断熱層は前記の水溶性ポリマーを含有することが好ましい。好ましく用いることができる化合物は前記と同様である。
断熱層における水溶性ポリマーの添加量は、当該断熱層全体の１〜７５質量％であることが好ましく、１〜５０質量％であることがより好ましい。 Moreover, it is preferable that a heat insulation layer contains the said water-soluble polymer. The compounds that can be preferably used are the same as described above.
The amount of the water-soluble polymer added to the heat insulating layer is preferably 1 to 75% by mass and more preferably 1 to 50% by mass with respect to the entire heat insulating layer.

断熱層には、ゼラチンを含むことが好ましい。断熱層のゼラチンの塗工液に占める量は０．５〜１４質量％が好ましく、１〜６質量％が特に好ましい。また、断熱層における前記中空ポリマーの塗布量は１〜１００ｇ／ｍ²が好ましく、５〜２０ｇ／ｍ²がより好ましい。 The heat insulating layer preferably contains gelatin. The amount of the heat insulating layer in the gelatin coating solution is preferably 0.5 to 14% by mass, particularly preferably 1 to 6% by mass. The coating amount of the hollow polymer in the heat insulation layer is preferably ^{1~100g / m 2, 5~20g / m} 2 is more preferable.

また、断熱層に含まれる水溶性ポリマーは、架橋剤により架橋されていることが好ましい。好ましく用いることができる架橋剤およびその使用量の好ましい範囲は前記と同様である。
断熱層中の水溶性ポリマーは、架橋剤の種類によっても異なるが、水溶性ポリマーに対して、０．１〜２０質量％架橋されていることが好ましく、１〜１０質量％架橋されていることがより好ましい。 Moreover, it is preferable that the water-soluble polymer contained in the heat insulation layer is crosslinked by a crosslinking agent. The preferred range of the crosslinking agent that can be preferably used and the amount of use thereof is the same as described above.
Although the water-soluble polymer in the heat insulating layer varies depending on the type of the crosslinking agent, it is preferably 0.1 to 20% by mass crosslinked with respect to the water-soluble polymer, and 1 to 10% by mass crosslinked. Is more preferable.

中空ポリマーを含む断熱層の厚みは５〜５０μｍであることが好ましく、５〜４０μｍであることがより好ましい。   The thickness of the heat insulating layer containing the hollow polymer is preferably 5 to 50 μm, and more preferably 5 to 40 μm.

中空ポリマーを含む断熱層の厚みと、中空ポリマーを含む断熱層の固形塗布量から算出される断熱層の空隙率は、１０〜７０％が好ましく、１５〜６０％が更に好ましい。断熱層の空隙率が１０％未満だと十分な断熱性が得られず、７０％以上だと中空ポリマー同士の結着力が低下し十分な膜強度が得られず、耐擦過性が悪化する。
本発明において断熱層の空隙率、下式（ｂ）にて算出される値Ｖである。 The porosity of the heat insulating layer calculated from the thickness of the heat insulating layer containing the hollow polymer and the solid coating amount of the heat insulating layer containing the hollow polymer is preferably 10 to 70%, and more preferably 15 to 60%. When the porosity of the heat insulating layer is less than 10%, sufficient heat insulating properties cannot be obtained, and when it is 70% or more, the binding force between the hollow polymers is lowered, and sufficient film strength cannot be obtained, and the scratch resistance is deteriorated.
In the present invention, the porosity of the heat insulating layer is a value V calculated by the following equation (b).

上記式（ｂ）において、Ｌは断熱層の膜厚を示し、ｇｉは断熱層を構成する特定の素材ｉの固形塗布量をしめし、ｄｉは特定の素材ｉの比重を示す。ここで、ｄｉが中空ポリマーの比重を示すとき、ｄｉは中空ポリマーの壁材の比重を示す。   In the above formula (b), L represents the film thickness of the heat insulating layer, gi represents the solid coating amount of the specific material i constituting the heat insulating layer, and di represents the specific gravity of the specific material i. Here, when di represents the specific gravity of the hollow polymer, di represents the specific gravity of the wall material of the hollow polymer.

（下地層）
受容層と断熱層との間には下地層が形成されていてもよく、例えば白地調整層、帯電調節層、接着層、プライマー層が形成される。これらの層については、例えば特許第３５８５５９９号公報、特許第２９２５２４４号公報などに記載されたものと同様の構成とすることができる。 (Underlayer)
An undercoat layer may be formed between the receiving layer and the heat insulating layer. For example, a white background adjusting layer, a charge adjusting layer, an adhesive layer, and a primer layer are formed. About these layers, it can be set as the structure similar to what was described, for example in patent 3585599, patent 2925244, etc.

（支持体）
本発明では、従来から公知のどのような支持体でも使用することができるが、耐水性支持体が用いられる。耐水性支持体を用いることで支持体中に水分が吸収されるのを防止して、受容層の経時による性能変化を防止することができる。耐水性支持体としては例えばコート紙やラミネート紙を用いることができる。 (Support)
In the present invention, any conventionally known support can be used, but a water-resistant support is used. By using a water-resistant support, it is possible to prevent moisture from being absorbed into the support, and to prevent a change in performance of the receiving layer over time. As the water-resistant support, for example, coated paper or laminated paper can be used.

−コート紙−
前記コート紙は、原紙等のシートに、各種の樹脂、ゴムラテックス又は高分子材料を片面又は両面に塗工した紙であり、用途に応じて、塗工量が異なる。このようなコート紙としては、例えば、アート紙、キャストコート紙、ヤンキー紙等が挙げられる。 -Coated paper-
The coated paper is a paper obtained by coating various sheets of resin, rubber latex, or polymer material on one side or both sides of a sheet such as a base paper, and the coating amount varies depending on the application. Examples of such coated paper include art paper, cast coated paper, Yankee paper, and the like.

前記原紙等の表面に塗工する樹脂としては、熱可塑性樹脂を使用することが適当である。このような熱可塑性樹脂としては、例えば、以下の（イ）〜（チ）の熱可塑性樹脂を例示することができる。   As the resin applied to the surface of the base paper or the like, it is appropriate to use a thermoplastic resin. Examples of such a thermoplastic resin include the following thermoplastic resins (a) to (h).

（イ）ポリエチレン樹脂、ポリプロピレン樹脂等のポリオレフィン樹脂や、エチレンやプロピレン等のオレフィンと、他のビニルモノマーとの共重合体樹脂や、アクリル樹脂等が挙げられる。
（ロ）エステル結合を有する熱可塑性樹脂である。例えば、ジカルボン酸成分（これらのジカルボン酸成分にはスルホン酸基、カルボキシル基等が置換していてもよい）と、アルコール成分（これらのアルコール成分には水酸基などが置換されていてもよい）との縮合により得られるポリエステル樹脂、ポリメチルメタクリレート、ポリブチルメタクリレート、ポリメチルアクリレート、ポリブチルアクリレート等のポリアクリル酸エステル樹脂又はポリメタクリル酸エステル樹脂、ポリカーボネート樹脂、ポリ酢酸ビニル樹脂、スチレンアクリレート樹脂、スチレン−メタクリル酸エステル共重合体樹脂、ビニルトルエンアクリレート樹脂等が挙げられる。
具体的には、特開昭５９−１０１３９５号公報、同６３−７９７１号公報、同６３−７９７２号公報、同６３−７９７３号公報、同６０−２９４８６２号公報などに記載のものを挙げることができる。
また、市販品としては、東洋紡(株)製のバイロン２９０、バイロン２００、バイロン２８０、バイロン３００、バイロン１０３、バイロンＧＫ−１４０、バイロンＧＫ−１３０；花王(株)製のタフトンＮＥ−３８２、タフトンＵ−５、ＡＴＲ−２００９、ＡＴＲ−２０１０；ユニチカ(株)製のエリーテルＵＥ３５００、ＵＥ３２１０、ＸＡ−８１５３、ＫＺＡ−７０４９、ＫＺＡ−１４４９；日本合成化学(株)製のポリエスターＴＰ−２２０、Ｒ−１８８；星光化学工業(株)製のハイロスシリーズの各種熱可塑性樹脂（いずれも商品名）等が挙げられる。 (A) Polyolefin resins such as polyethylene resins and polypropylene resins, copolymer resins of olefins such as ethylene and propylene and other vinyl monomers, acrylic resins, and the like.
(B) A thermoplastic resin having an ester bond. For example, a dicarboxylic acid component (these dicarboxylic acid components may be substituted with a sulfonic acid group, a carboxyl group, etc.) and an alcohol component (these alcohol components may be substituted with a hydroxyl group, etc.) Polyester resin, polymethyl methacrylate, polybutyl methacrylate, polymethyl acrylate, polybutyl acrylate and other polyacrylate resin or polymethacrylate resin, polycarbonate resin, polyvinyl acetate resin, styrene acrylate resin, styrene -Methacrylic acid ester copolymer resin, vinyl toluene acrylate resin, etc. are mentioned.
Specific examples include those described in JP-A Nos. 59-101395, 63-7971, 63-7972, 63-7773, and 60-294862. it can.
Commercially available products include Byron 290, Byron 200, Byron 280, Byron 300, Byron 103, Byron GK-140, Byron GK-130 manufactured by Toyobo Co., Ltd., Tufton NE-382, Tufton manufactured by Kao Corporation U-5, ATR-2009, ATR-2010; Elitel UE3500, UE3210, XA-8153, KZA-7049, KZA-1449 manufactured by Unitika Ltd. Polyester TP-220, R manufactured by Nippon Synthetic Chemical Co., Ltd. -188; various types of thermoplastic resins of the Hiros series manufactured by Seiko Chemical Industry Co., Ltd. (all trade names).

（ハ）ポリウレタン樹脂等が挙げられる。
（ニ）ポリアミド樹脂、尿素樹脂等が挙げられる。
（ホ）ポリスルホン樹脂等が挙げられる。
（ヘ）ポリ塩化ビニル樹脂、ポリ塩化ビニリデン樹脂、塩化ビニル−酢酸ビニル共重合体樹脂、塩化ビニル−プロピオン酸ビニル共重合体樹脂等が挙げられる。
（ト）ポリビニルブチラール等の、ポリオール樹脂、エチルセルロース樹脂、酢酸セルロース樹脂等のセルロース樹脂等が挙げられる。
（チ）ポリカプロラクトン樹脂、スチレン−無水マレイン酸樹脂、ポリアクリロニトリル樹脂、ポリエーテル樹脂、エポキシ樹脂、フェノール樹脂等が挙げられる。
なお、前記熱可塑性樹脂は、１種単独で使用してもよく、２種以上を併用してもよい。 (C) Polyurethane resin etc. are mentioned.
(D) Polyamide resin, urea resin, etc. are mentioned.
(E) Polysulfone resin and the like.
(F) Polyvinyl chloride resin, polyvinylidene chloride resin, vinyl chloride-vinyl acetate copolymer resin, vinyl chloride-vinyl propionate copolymer resin, and the like.
(G) Cellulose resins, such as polyol resin, ethyl cellulose resin, cellulose acetate resin, etc., such as polyvinyl butyral.
(H) Polycaprolactone resin, styrene-maleic anhydride resin, polyacrylonitrile resin, polyether resin, epoxy resin, phenol resin and the like.
In addition, the said thermoplastic resin may be used individually by 1 type, and may use 2 or more types together.

また、前記熱可塑性樹脂には、増白剤、導電剤、填料、酸化チタン、群青、カーボンブラック等の顔料や染料等を必要に応じて含有させておくことができる。   Further, the thermoplastic resin may contain pigments or dyes such as brighteners, conductive agents, fillers, titanium oxide, ultramarine blue, and carbon black as required.

−ラミネート紙−
前記ラミネート紙は、原紙等のシートに、各種の樹脂、ゴム又は高分子シート又はフィルム等をラミネートした紙である。前記ラミネート材料としては、例えば、ポリオレフィン、ポリ塩化ビニル、ポリエチレンテレフタレート、ポリスチレン、ポリメタクリレート、ポリカーボネート、ポリイミド、トリアセチルセルロース等が挙げられる。これらの樹脂は、１種単独で使用してもよく、２種以上を併用してもよい。 -Laminated paper-
The laminated paper is a paper obtained by laminating various resins, rubber or polymer sheets or films on a sheet such as a base paper. Examples of the laminate material include polyolefin, polyvinyl chloride, polyethylene terephthalate, polystyrene, polymethacrylate, polycarbonate, polyimide, triacetyl cellulose, and the like. These resins may be used alone or in combination of two or more.

前記ポリオレフィンは、一般に低密度ポリエチレンを用いて形成することが多いが、支持体の耐熱性を向上させるために、ポリプロピレン、ポリプロピレンとポリエチレンとのブレンド、高密度ポリエチレン、高密度ポリエチレンと低密度ポリエチレンとのブレンド等を用いるのが好ましい。特に、コストや、ラミネート適性等の点から、高密度ポリエチレンと低密度ポリエチレンとのブレンドを用いるのが最も好ましい。   In general, the polyolefin is often formed using low density polyethylene, but in order to improve the heat resistance of the support, polypropylene, a blend of polypropylene and polyethylene, high density polyethylene, high density polyethylene and low density polyethylene, It is preferable to use a blend of In particular, it is most preferable to use a blend of high-density polyethylene and low-density polyethylene from the viewpoint of cost, suitability for lamination, and the like.

前記高密度ポリエチレンと、前記低密度ポリエチレンとのブレンドは、例えば、ブレンド比率（質量比）１／９〜９／１で用いられる。該ブレンド比率としては、２／８〜８／２が好ましく、３／７〜７／３がより好ましい。該支持体の両面に熱可塑性樹脂層を形成する場合、支持体の裏面は、例えば、高密度ポリエチレン、或いは高密度ポリエチレンと低密度ポリエチレンとのブレンドを用いて形成されるのが好ましい。ポリエチレンの分子量としては、特に制限はないが、メルトインデックスが、高密度ポリエチレン及び低密度ポリエチレンのいずれについても、１．０〜４０ｇ／１０分の間のものであって、押出し適性を有するものが好ましい。
尚、これらのシート又はフィルムには、白色反射性を与える処理を行ってもよい。このような処理方法としては、例えば、これらのシート又はフィルム中に酸化チタンなどの顔料を配合する方法が挙げられる。 The blend of the high density polyethylene and the low density polyethylene is used, for example, in a blend ratio (mass ratio) of 1/9 to 9/1. The blend ratio is preferably 2/8 to 8/2, and more preferably 3/7 to 7/3. When forming a thermoplastic resin layer on both surfaces of the support, the back surface of the support is preferably formed using, for example, high-density polyethylene or a blend of high-density polyethylene and low-density polyethylene. The molecular weight of polyethylene is not particularly limited, but the melt index is 1.0 to 40 g / 10 min for both high-density polyethylene and low-density polyethylene and has extrudability. preferable.
In addition, you may perform the process which gives white reflectivity to these sheets or films. Examples of such a treatment method include a method of blending a pigment such as titanium oxide in these sheets or films.

前記支持体の厚みとしては、２５μｍ〜３００μｍが好ましく、５０μｍ〜２６０μｍがより好ましく、７５μｍ〜２２０μｍが更に好ましい。該支持体の剛度としては、種々のものがその目的に応じて使用することが可能であり、写真画質の電子写真用受像シート用の支持体としては、カラー銀塩写真用の支持体に近いものが好ましい。   The thickness of the support is preferably 25 μm to 300 μm, more preferably 50 μm to 260 μm, and still more preferably 75 μm to 220 μm. Various stiffnesses can be used according to the purpose, and the support for a photographic image receiving sheet for electrophotography is close to a support for color silver halide photography. Those are preferred.

（カール調整層）
支持体がそのまま露出していると環境中の湿度・温度により感熱転写受像シートがカールしてしまうことがあるため、支持体の裏面側にカール調整層を形成することが好ましい。カール調整層は、受像シートのカールを防止するだけでなく防水の役割も果たす。カール調整層には、ポリエチレンラミネートやポリプロピレンラミネート等が用いられる。具体的には、例えば特開昭６１−１１０１３５号公報、特開平６−２０２２９５号公報などに記載されたものと同様にして形成することができる。 (Curl adjustment layer)
If the support is exposed as it is, the heat-sensitive transfer image-receiving sheet may be curled due to the humidity and temperature in the environment. Therefore, it is preferable to form a curl adjusting layer on the back side of the support. The curl adjusting layer not only prevents the image receiving sheet from curling but also serves as a waterproof. For the curl adjusting layer, polyethylene laminate, polypropylene laminate, or the like is used. Specifically, it can be formed in the same manner as described in, for example, JP-A-61-110135 and JP-A-6-202295.

（筆記層・帯電調整層）
筆記層・帯電調整層には、無機酸化物コロイドやイオン性ポリマー等を用いることができる。帯電防止剤として、例えば第四級アンモニウム塩、ポリアミン誘導体等のカチオン系帯電防止剤、アルキルホスフェート等のアニオン系帯電防止剤、脂肪酸エステル等のノニオン系帯電防止剤など任意のものを用いることができる。具体的には、例えば特許第３５８５５８５号明細書などに記載されたものと同様にして形成することができる。 (Writing layer / Charge adjustment layer)
An inorganic oxide colloid, an ionic polymer, or the like can be used for the writing layer and the charge adjusting layer. As the antistatic agent, for example, a cationic antistatic agent such as a quaternary ammonium salt or a polyamine derivative, an anionic antistatic agent such as an alkyl phosphate, or a nonionic antistatic agent such as a fatty acid ester can be used. . Specifically, it can be formed in the same manner as that described in, for example, Japanese Patent No. 3585585.

以下、本発明の感熱転写受像シートの製造方法について説明する。
本発明の感熱転写受像シートは、少なくとも１層の受容層、中間層および断熱層を支持体上に同時重層塗布することで形成することができる。
前記受容層とこれに隣接する層とを同時に塗布して製造することが好ましく、前記隣接する層が断熱層であることがより好ましい。
支持体上に複数の機能の異なる複数の層（気泡層、断熱層、中間層、受容層など）からなる多層構成の受像シートを製造する場合、特開２００４−１０６２８３号、同２００４−１８１８８８号、同２００４−３４５２６７号等の各公報に示されている如く各層を順次塗り重ねていくか、あらかじめ各層を支持体上に塗布したものを張り合わせることにより製造することが知られている。一方、写真業界では例えば複数の層を同時に重層塗布することにより生産性を大幅に向上させることが知られている。例えば特開米国特許第２，７６１，７９１号、同第２，６８１，２３４号、同第３，５０８，９４７号、同第４，４５７，２５６号、同第３，９９３，０１９号、特開昭６３−５４９７５号、特開昭６１−２７８８４８号、同５５−８６５５７号、同５２−３１７２７号、同５５−１４２５６５号、同５０−４３１４０号、同６３−８０８７２号、同５４−５４０２０号、特開平５−１０４０６１号、同５−１２７３０５号、特公昭４９−７０５０号の公報または明細書やEdgar B. Gutoffら著，「Coating and Drying Defects：Troubleshooting Operating Problems」，John Wiley＆Sons社，1995年，101〜103頁などに記載のいわゆるスライド塗布（スライドコーティング法）、カーテン塗布（カーテンコーティング法）といわれる方法が知られている。
本発明では、上記同時重層塗布を多層構成の受像シートの製造に用いることにより、生産性を大幅に向上させると同時に画像欠陥を大幅に減少させることができる。 The method for producing the thermal transfer image receiving sheet of the present invention will be described below.
The heat-sensitive transfer image-receiving sheet of the present invention can be formed by simultaneously applying at least one receiving layer, intermediate layer and heat insulating layer on a support.
It is preferable that the receptor layer and a layer adjacent to the receptor layer are simultaneously applied and manufactured, and it is more preferable that the adjacent layer is a heat insulating layer.
When producing a multi-layer image receiving sheet comprising a plurality of layers having different functions (such as a bubble layer, a heat insulating layer, an intermediate layer, and a receiving layer) on a support, JP-A Nos. 2004-106283 and 2004-181888 are disclosed. In addition, it is known that each layer is sequentially coated as disclosed in each publication such as JP-A 2004-345267, or the layers are previously applied on a support and bonded together. On the other hand, it is known in the photographic industry that productivity is greatly improved, for example, by applying a plurality of layers simultaneously. For example, JP-A Nos. 2,761,791, 2,681,234, 3,508,947, 4,457,256, 3,993,019, Kaisho 63-54975, JP-A-61-278848, 55-86557, 52-31727, 55-142565, 50-43140, 63-80872, 54-54020 JP-A-5-104061, JP-A-5-127305, JP-B-49-7050, or specification, Edgar B. Gutoff et al., "Coating and Drying Defects: Troubleshooting Operating Problems", John Wiley & Sons, 1995. , 101-103, etc., so-called slide coating (slide coating method) and curtain coating (curtain coating method) are known.
In the present invention, the simultaneous multi-layer coating is used for manufacturing a multi-layer image-receiving sheet, whereby productivity can be greatly improved and image defects can be greatly reduced.

本発明においては複数の層は樹脂を主成分として構成される。各層を形成するための塗布液は水分散ラテックスであることが好ましい。各層の塗布液に占めるラテックス状態の樹脂の固形分重量は５〜８０％の範囲が好ましく２０〜６０％の範囲が特に好ましい。上記水分散ラテックスに含まれる樹脂の平均粒子サイズは５μｍ以下であり１μｍ以下が特に好ましい。上記水分散ラテックスは必要に応じて界面活性剤、分散剤、バインダー樹脂など公知の添加剤を含むことができる。
本発明では米国特許２，７６１，７９１号明細書に記載の方法で支持体上に複数の層の積層体を形成した後速やかに固化させる事が好ましい。一例として樹脂により固化する多層構成の場合、支持体上に複数の層を形成した後すばやく温度を上げることが好ましい。またゼラチンなど低温でゲル化するバインダーを含む場合には支持体上に複数の層を形成した後すばやく温度を下げることが好ましい場合もある。
本発明においては多層構成を構成する１層あたりの塗布液の塗布量は１ｇ／ｍ²〜５０
０ｇ／ｍ²の範囲が好ましい。多層構成の層数は２以上で任意に選択できる。受容層は支
持体から最も遠く離れた層として設けられることが好ましい。 In the present invention, the plurality of layers are composed mainly of a resin. The coating solution for forming each layer is preferably water-dispersed latex. The solid content weight of the latex resin in the coating solution of each layer is preferably in the range of 5 to 80%, particularly preferably in the range of 20 to 60%. The average particle size of the resin contained in the water-dispersed latex is 5 μm or less and particularly preferably 1 μm or less. The water-dispersed latex may contain a known additive such as a surfactant, a dispersant, and a binder resin as necessary.
In the present invention, it is preferable to form a laminate of a plurality of layers on a support by the method described in US Pat. No. 2,761,791 and then quickly solidify. As an example, in the case of a multilayer structure solidified by a resin, it is preferable to quickly raise the temperature after forming a plurality of layers on the support. When a binder that gels at a low temperature such as gelatin is included, it may be preferable to quickly lower the temperature after forming a plurality of layers on the support.
In the present invention, the coating amount of the coating solution per layer constituting the multilayer structure is 1 g / m ² to 50.
A range of 0 g / m ² is preferred. The number of layers in the multilayer configuration can be arbitrarily selected as 2 or more. The receiving layer is preferably provided as the layer furthest away from the support.

熱転写画像形成の際に、上述した本発明の感熱転写受像シートと併せて使用される感熱転写シート（インクシート）は支持体上に拡散転写染料を含む色素層を設けたものであり、任意のインクシートを使用することができる。熱転写時の熱エネルギーの付与手段は、従来公知の付与手段のいずれも使用することができ、例えば、サーマルプリンター（例えば、日立製作所製、商品名、ビデオプリンターＶＹ−１００）等の記録装置によって記録時間をコントロールすることにより、５〜１００ｍＪ／ｍｍ²程度の熱エネルギーを付与することによって所期の目的を十分に達成することができる。
また、本発明の感熱転写受像シートは、支持体を適宜選択することにより、熱転写記録可能な枚葉またはロール状の感熱転写受像シート、カード類、透過型原稿作成用シート等の各種用途に適用することもできる。 The thermal transfer sheet (ink sheet) used in combination with the above-described thermal transfer image-receiving sheet of the present invention at the time of thermal transfer image formation is provided with a dye layer containing a diffusion transfer dye on a support. Ink sheets can be used. As the means for applying thermal energy at the time of thermal transfer, any conventionally known means for applying can be used. For example, recording is performed by a recording device such as a thermal printer (for example, product name, video printer VY-100, manufactured by Hitachi, Ltd.). By controlling the time, the intended purpose can be sufficiently achieved by applying thermal energy of about 5 to 100 mJ / mm ² .
The heat-sensitive transfer image-receiving sheet of the present invention can be applied to various uses such as a sheet- or roll-shaped heat-sensitive transfer image-receiving sheet, cards, and transmission-type manuscript preparation sheets capable of thermal transfer recording by appropriately selecting a support. You can also

本発明は、感熱転写記録方式を利用したプリンター、複写機などに利用することができる。   The present invention can be used in printers, copiers and the like using a thermal transfer recording system.

以下、本発明を実施例に基づき更に詳細に説明するが、本発明はこれらに限定されるものではない。なお、実施例中で、部または％とあるのは、特に断りのない限り質量基準である。
実施例１ EXAMPLES Hereinafter, although this invention is demonstrated in detail based on an Example, this invention is not limited to these. In Examples, “part” or “%” is based on mass unless otherwise specified.
Example 1

（インクシートの作製）
厚さ６．０μｍのポリエステルフィルム（ルミラー、商品名、(株)東レ製）を基材フィルムとして用いた。そのフィルム背面側に耐熱スリップ層（厚み１μｍ）を形成し、かつ表面側に下記組成のイエロー、マゼンタ、シアン組成物を、それぞれ単色に塗布（乾膜時の塗布量１ｇ／ｍ²）した。
イエロー組成物
染料（マクロレックスイエロー６Ｇ、商品名、バイエル社製） ５．５質量部
ポリビニルブチラール樹脂 ４．５質量部
（エスレックＢＸ−１、商品名、積水化学工業(株)製）
メチルエチルケトン／トルエン（質量比１／１） ９０質量部
マゼンタ組成物
マゼンタ染料（ディスパーズレッド６０） ５．５質量部
ポリビニルブチラール樹脂 ４．５質量部
（エスレックＢＸ−１、商品名、積水化学工業(株)製）
メチルエチルケトン／トルエン（質量比１／１） ９０質量部
シアン組成物
シアン染料（ソルベントブルー６３） ５．５質量部
ポリビニルブチラール樹脂 ４．５質量部
（エスレックＢＸ−１、商品名、積水化学工業(株)製）
メチルエチルケトン／トルエン（質量比１／１） ９０質量部 (Preparation of ink sheet)
A polyester film having a thickness of 6.0 μm (Lumirror, trade name, manufactured by Toray Industries, Inc.) was used as a base film. A heat-resistant slip layer (thickness 1 μm) was formed on the back side of the film, and yellow, magenta and cyan compositions having the following compositions were applied to the surface side in a single color (coating amount 1 g / m ² during dry film formation).
Yellow composition Dye (Macrolex Yellow 6G, trade name, manufactured by Bayer) 5.5 parts by weight Polyvinyl butyral resin 4.5 parts by weight (ESREC BX-1, trade name, manufactured by Sekisui Chemical Co., Ltd.)
Methyl ethyl ketone / toluene (mass ratio 1/1) 90 parts by mass Magenta composition Magenta dye (Disperse Red 60) 5.5 parts by mass Polyvinyl butyral resin 4.5 parts by mass (ESREC BX-1, trade name, Sekisui Chemical Co., Ltd.) Made by Co., Ltd.)
Methyl ethyl ketone / toluene (mass ratio 1/1) 90 parts by mass Cyan composition Cyan dye (Solvent Blue 63) 5.5 parts by mass Polyvinyl butyral resin 4.5 parts by mass (ESREC BX-1, trade name, Sekisui Chemical Co., Ltd.) ) Made)
90 parts by mass of methyl ethyl ketone / toluene (mass ratio 1/1)

（受層シートの作製）
（支持体の作製）
アカシアからなるＬＢＫＰ（広葉樹晒クラフトパルプ）５０質量部及びアスペンからなるＬＢＫＰ ５０質量部をそれぞれディスクリファイナーによりカナディアンフリーネス３００ｍｌに叩解しパルプスラリーを調製した。
次いで、上記で得られたパルプスラリーに、対パルプ当り、カチオン変性でんぷん（日本ＮＳＣ(株)製ＣＡＴ０３０４Ｌ）１．３％、アニオン性ポリアクリルアミド（星光ＰＭＣ(株)製 ＤＡ４１０４）０．１５％、アルキルケテンダイマー（荒川化学(株)製サイズパインＫ）Ｏ．２９％、エポキシ化ベヘン酸アミド０．２９％、ポリアミドポリアミンエピクロルヒドリン（荒川化学(株)製：アラフィックス１００）０．３２％を加えた後、消泡剤０．１２％を加えた。 (Preparation of layer-receiving sheet)
(Production of support)
50 parts by mass of LBKP (hardwood bleached kraft pulp) made of acacia and 50 parts by mass of LBKP made of aspen were each beaten to 300 ml of Canadian freeness by a disc refiner to prepare a pulp slurry.
Next, to the pulp slurry obtained above, cation modified starch (CAT0304L manufactured by NSC Japan) 1.3%, anionic polyacrylamide (DA4104 manufactured by Seiko PMC Co.) 0.15% per pulp, Alkyl ketene dimer (size pine K manufactured by Arakawa Chemical Co., Ltd.) 29%, 0.29% epoxidized behenamide, 0.32% polyamide polyamine epichlorohydrin (Arakawa Chemical Co., Ltd .: Arafix 100) were added, and then 0.12% of an antifoaming agent was added.

前記のようにして調製したパルプスラリーを長網抄紙機で抄紙し、ウェッブのフェルト面をドラムドライヤーシリンダーにドライヤーカンバスを介して押し当てて乾燥する工程において、ドライヤーカンバスの引張り力を１．６ｋｇ／ｃｍに設定して乾燥を行なった後、サイズプレスにて原紙の両面にポリビニルアルコール（(株)クラレ製：ＫＬ−１１８）を１ｇ／ｍ²塗布して乾燥し、カレンダー処理を行った。なお、原紙の坪量は１５７ｇ／ｍ²で抄造し、厚さ１６０μｍの原紙（基紙）を得た。 In the process of making the pulp slurry prepared as described above with a long paper machine and pressing the felt surface of the web against the drum dryer cylinder through the dryer canvas for drying, the tensile force of the dryer canvas is 1.6 kg / After drying at a setting of cm, 1 g / m ² of polyvinyl alcohol (manufactured by Kuraray Co., Ltd .: KL-118) was applied on both sides of the base paper with a size press and dried, and calendar treatment was performed. The base paper was made with a basis weight of 157 g / m ² to obtain a base paper (base paper) having a thickness of 160 μm.

得られた基紙のワイヤー面（裏面）側に、コロナ放電処理を行なった後、溶融押出機を用いてＭＦＲ（メルトフローレート；以下同様）１６．０ｇ／１０分、密度０．９６ｇ／ｃｍ³の高密度ポリエチレン（ハイドロタルサイト（商品名ＤＨＴ−４Ａ、協和化学工業(株)製）２５０ｐｐｍと、二次酸化防止剤（トリス（２，４−ジ−ｔ−ブチルフェニル）
フォスファイト、商品名：イルガフォス１６８、チバ・スペシャリティ・ケミカルズ(株)製、２００ｐｐｍを含有）と、ＭＦＲ ４．０ｇ／１０分、密度０．９３ｇ／ｃｍ³の低
密度ポリエチレンと、を７５／２５（質量比）の割合で配合した樹脂組成物を、厚さ２１ｇ／ｍ²となるようにコーティングし、マット面からなる熱可塑性樹脂層を形成した（以下、この熱可塑性樹脂層面を「裏面」と称する。）。この裏面側の熱可塑性樹脂層に更にコロナ放電処理を施し、その後、帯電防止剤として、酸化アルミニウム（日産化学工業(株)製の「アルミナゾル１００」）と二酸化ケイ素（日産化学工業(株)製の「スノーテックスＯ」）とを１：２の質量比で水に分散した分散液を、乾燥質量が０．２ｇ／ｍ²となるように塗布した。続いて表面にコロナ処理し１０質量％の酸化チタンを有するＭＦＲ ４．０ｇ／１０分、密度０．９３ｇ／ｍ²の低密度ポリエチレンを２７ｇ／ｍ²になるように溶融押出機を用いてコーティングし、鏡面からなる熱可塑性樹脂層を形成した。 After performing corona discharge treatment on the wire surface (back surface) side of the obtained base paper, MFR (melt flow rate; hereinafter the same) 16.0 g / 10 min, density 0.96 g / cm using a melt extruder. ³ high density polyethylene (hydrotalcite (trade name DHT-4A, manufactured by Kyowa Chemical Industry Co., Ltd.) 250 ppm and secondary antioxidant (Tris (2,4-di-t-butylphenyl))
Phosphite, trade name: Irgaphos 168, manufactured by Ciba Specialty Chemicals Co., Ltd., containing 200 ppm), MFR 4.0 g / 10 min, low density polyethylene of density 0.93 g / cm ³ , 75/25 The resin composition blended at a ratio of (mass ratio) was coated to a thickness of 21 g / m ² to form a thermoplastic resin layer comprising a mat surface (hereinafter, this thermoplastic resin layer surface is referred to as “back surface”). Called). The thermoplastic resin layer on the back side is further subjected to corona discharge treatment, and then, as an antistatic agent, aluminum oxide (“Alumina Sol 100” manufactured by Nissan Chemical Industries, Ltd.) and silicon dioxide (manufactured by Nissan Chemical Industries, Ltd.) Of “Snowtex O”) was dispersed in water at a mass ratio of 1: 2 so that the dry mass was 0.2 g / m ² . Followed by a corona treatment on the surface MFR 4.0 g / 10 min with 10 wt% of titanium oxide, the coating using a melt extruder so that a low density polyethylene having a density of 0.93 g / m ² to 27 g / m ² Then, a thermoplastic resin layer having a mirror surface was formed.

（乳化分散物Ａの調製）
高沸点溶媒（下記のＳＯＬＶ−５）を１３.５ｇ、下記のＥＢ−９を１９ｇ、下記のＢ−４７を９ｇ、および酢酸エチルを２０ｍｌ混合して、得られた溶液を１ｇのドデシルベンゼンスルホン酸ナトリウムを含む２０質量％ゼラチン水溶液２５０ｇ中に高速攪拌乳化機（ディゾルバー）で乳化分散し、水を加えて３８０ｇの乳化物Ａを調製した。 (Preparation of emulsified dispersion A)
13.5 g of a high boiling point solvent (SOLV-5 below), 19 g of EB-9 below, 9 g of B-47 below, and 20 ml of ethyl acetate were mixed with 1 g of dodecylbenzenesulfone. The mixture was emulsified and dispersed in 250 g of a 20% by weight gelatin aqueous solution containing sodium acid with a high-speed stirring emulsifier (dissolver), and water was added to prepare 380 g of Emulsion A.

（感熱転写受像シート１０１（比較例）の作製）
上記のように作成した支持体上に下層から順に下塗層、断熱層、受容層の構成の多層構成塗布物を同時重層塗布した。塗工液の組成と塗布量を以下に示す。 (Preparation of thermal transfer image-receiving sheet 101 (comparative example))
On the support prepared as described above, a multi-layer coating composition composed of an undercoat layer, a heat insulating layer, and a receiving layer was applied simultaneously from the lower layer. The composition and coating amount of the coating solution are shown below.

下塗層塗工液
（組成）
スチレンブタジエンラテックス ９３質量部
（日本エイアンドエル社製 ＳＲ１０３）
ＰＶＡ ８．７％水溶液 ５７質量部
ＮａＯＨでｐＨを８に調節
（塗布量） ２１ｍｌ／ｍ² Undercoat layer coating liquid (composition)
93 parts by mass of styrene-butadiene latex (SR103 manufactured by Nippon A & L Co., Ltd.)
PVA 8.7% aqueous solution 57 parts by mass Adjust pH to 8 with NaOH (application amount) 21 ml / m ²

断熱層塗工液
（組成）
中空ポリマーラテックス ３８質量部
（日本ゼオン(株)製 ＭＨ５０５５）
１６％ゼラチン水溶液 ２６質量部
水 ４質量部
ＮａＯＨでｐＨを８に調節
（塗布量） ４５ｍｌ／ｍ² Heat insulation layer coating liquid (composition)
38 parts by mass of hollow polymer latex (MH5055 manufactured by Nippon Zeon Co., Ltd.)
16% aqueous gelatin solution 26 parts by weight Water 4 parts by weight Adjust pH to 8 with NaOH (coating amount) 45 ml / m ²

受容層塗工液
（組成）
塩ビアクリルラテックス ４４質量部
（日信化学(株)製 ビニブラン９００）
塩ビアクリルラテックス ２７質量部
（日信化学(株)製 ビニブラン２７６）
先に調製した乳化物Ａ ４．２質量部
マイクロクリスタリンワックス ７質量部
（日本製蝋(株)製 ＥＭＵＳＴＡＲ−４２Ｘ）
水 ２４質量部
下記化合物Ａ ０．０５質量部
ＮａＯＨでｐＨを８に調節
（塗布量） １８ｍｌ／ｍ²
化合物Ａ Receiving layer coating liquid (composition)
44 parts by mass of PVC acrylic latex (Nishin Chemical Co., Ltd. Vinibrand 900)
27 parts by weight of vinyl chloride acrylic latex (Viniblanc 276 manufactured by Nissin Chemical Co., Ltd.)
Emulsion A prepared previously 4.2 parts by mass Microcrystalline wax 7 parts by mass (Nippon Wax Co., Ltd. EMUSTAR-42X)
Water 24 parts by mass The following compound A 0.05 part by mass The pH is adjusted to 8 with NaOH (application amount) 18 ml / m ²
Compound A

上記受容層塗布液に、塗布直前に、化合物Ｂ(架橋材)を添加した。化合物Ｂの添加量は、断熱層と受容層中のゼラチンの、合計の質量に対して、３質量％となるように添加した。
化合物Ｂ Compound B (crosslinking material) was added to the receiving layer coating solution immediately before coating. The amount of compound B added was 3% by mass relative to the total mass of gelatin in the heat insulating layer and the receiving layer.
Compound B

（感熱転写受像シート１０２〜１０９（本発明）の作製）
感熱転写受像シート１０１において、受容層に新たに下記マット剤を添加した。なお、添加量は上記受像層塗工液に１.５質量部添加した。この際、マット剤を添加した分だけ水を除去し全体量は変化しないように調液を行った。 (Preparation of thermal transfer image-receiving sheets 102 to 109 (present invention))
In the heat-sensitive transfer image-receiving sheet 101, the following matting agent was newly added to the receiving layer. The amount added was 1.5 parts by mass in the image-receiving layer coating solution. At this time, preparation was performed such that water was removed by the amount of the matting agent added and the total amount did not change.

（画像形成）
インクシートと、感熱転写受像シート１０１〜１１０を装填可能なように加工し、昇華型熱転写プリンターＡＳＫ２０００ (富士写真フィルム(株)社製) を用いて、高速プリントモードで、３５℃７０％の環境下で出力した。感熱転写受像シートは、３５℃７０％の環境下で２時間調湿した後、プリンターに装填した。出力画像は、下記の２種の画像を用いた。
１）高濃度の全面黒画像（黒ベタ画像）
２）各種単色とグレーの、白〜最高濃度までの階調画像
これらの２種の画像を、各々３０枚連続して画像出力した。
なお高速プリントモードでは、１枚目が排出されてから、２枚目が排出されるまでの時間は８秒間であった。 (Image formation)
The ink sheet and the thermal transfer image receiving sheets 101 to 110 are processed so that they can be loaded, and using a sublimation type thermal transfer printer ASK2000 (manufactured by Fuji Photo Film Co., Ltd.) in a high-speed print mode, an environment of 35 ° C. and 70%. Output below. The heat-sensitive transfer image-receiving sheet was conditioned at 35 ° C. and 70% for 2 hours and then loaded into a printer. The following two types of images were used as output images.
1) Full-scale black image with high density (solid black image)
2) Tone images of various single colors and gray, from white to the highest density, 30 images of each of these two types of images were continuously output.
In the high-speed print mode, the time from when the first sheet is discharged to when the second sheet is discharged is 8 seconds.

（離型性）
出力した２画像を用いて、離型性の評価を下記基準で官能評価した。
〔評価ランク〕
◎：全てのプリントに問題は見られない。
○：一部のプリント（全出力枚数の５％）に軽度なスジ状のムラ（スティッキング）が発生している。
△：半数以上のプリントにスティッキングが発生している。
×：ほとんどのプリントにスティッキング、異常転写（インクリボンの染料層ごと転写する現象）など離型性不良による故障が発生する。 (Releasability)
Using the two output images, sensory evaluation was performed based on the following criteria for releasability.
[Evaluation rank]
A: No problem is seen in all prints.
○: Some streaky unevenness (sticking) occurs in some prints (5% of the total number of output sheets).
Δ: Sticking occurs in more than half of the prints.
X: Failure due to poor releasability such as sticking or abnormal transfer (a phenomenon in which the ink layer of the ink ribbon is transferred) occurs in most prints.

（画質粒状）
上記で出力した、「各種単色とグレーの、白〜最高濃度までの階調画像」を用いて、白〜濃度１．０付近までに着目して、以下の官能評価を行った。画質粒状は、特に低濃度部分でより判断しやすいためである。官能評価は、５人以上で行い、最も厳しく評価した人の結果を、評価結果とした。
〔評価ランク〕
◎：粒状が良く、ザラザラ感が感じられない。
○：粒状が感じられ、ややザラザラ感があるが、画像上問題ない。
△：粒状は悪く感じられるが、濃度１．０付近では目立たたず、問題ない。
×：粒状が悪く感じられ、濃度１．０付近でも目立っており、問題有り。 (Granular quality)
The following sensory evaluation was performed by focusing on the range from white to density around 1.0 using the “monochromatic and gray gradation images from white to the maximum density” output above. This is because the image quality granularity is easier to judge, particularly in the low density portion. The sensory evaluation was performed by five or more people, and the result of the person who was most severely evaluated was used as the evaluation result.
[Evaluation rank]
A: Graininess is good and no rough feeling is felt.
○: Graininess is felt and there is a slight roughness, but there is no problem in the image.
Δ: The granularity seems to be bad, but it does not stand out in the vicinity of a density of 1.0, and there is no problem.
X: Graininess is felt bad, and there is a problem even when the density is around 1.0.

上記表２より、マット剤がない試料１０１に対して、本発明の試料１０２〜試料１１０は離型性で良好な結果が得られた。
特に、メラミン樹脂を含有する試料１０７、１０８、１０９が、画像粒状を悪化させず、離型性が良く最も総合性能が良かった。
試料１０３と試料１０４との比較より、同じ有機微粒子マット剤であっても、架橋した有機微粒子の方が、粒状性を悪化させないまま離型性を良化させることが分かった。
試料１０２と試料１０５との比較より、同じ有機微粒子マット剤であっても、ＤＶＢを含む有機微粒子の方が、粒状性を悪化させないまま離型性を良化させることが分かった。
粒径（３．５μｍ→６．５μｍ）に関しては、試料１０５と試料１１０の比較より、ポリ（Ｓｔ／ＤＶＢ＝９０／１０）粒子では、許容範囲内で粒状性を悪化させるのに対し、試料１０８／試料１０９の比較より、メラミン-シリカ樹脂では粒状性は変化しない。これより、有機微粒子の中でも、メラミン-シリカ樹脂が特に好ましいことが分かった。 From Table 2 above, Sample 102 to Sample 110 of the present invention obtained good results with releasability compared to Sample 101 without the matting agent.
In particular, Samples 107, 108, and 109 containing a melamine resin did not deteriorate the image granularity and had good releasability and the best overall performance.
From comparison between Sample 103 and Sample 104, it was found that even with the same organic fine particle matting agent, the crosslinked organic fine particles improve the releasability without deteriorating the granularity.
From comparison between Sample 102 and Sample 105, it was found that even with the same organic fine particle matting agent, organic fine particles containing DVB improve the releasability without deteriorating the granularity.
Regarding the particle size (3.5 μm → 6.5 μm), the comparison between the sample 105 and the sample 110 shows that the poly (St / DVB = 90/10) particles deteriorate the granularity within an allowable range, whereas the sample From the comparison of 108 / sample 109, the granularity does not change with melamine-silica resin. From this, it was found that melamine-silica resin is particularly preferable among the organic fine particles.

実施例２
（感熱転写受像シート２０２〜２０９（本発明）の作製）
実施例１において、粒状性の評価が△、○であった試料（試料１０４、試料１０５、試料１１０）及び最も性能が良かった試料１０８に対して、添加するマット剤量を減らしたサンプルを作製した。具体的には、試料受像層塗工液に加えるマット剤を１５質量部だったものを７．５質量部に変えた以外は実施例１と同様に行った。その結果を下記表３に示す。なお表３には、実施例１の結果を一部併記した。 Example 2
(Preparation of thermal transfer image-receiving sheets 202 to 209 (present invention))
In Example 1, a sample with a reduced amount of matting agent added to a sample (Sample 10 4 , Sample 105, Sample 110) in which the evaluation of granularity was Δ or ◯, and a sample 108 having the best performance. Produced. Specifically, the same procedure as in Example 1 was performed except that the matting agent added to the sample image-receiving layer coating solution was changed to 15 parts by mass to 7.5 parts by mass. The results are shown in Table 3 below. In Table 3, a part of the results of Example 1 is shown.

表３から明らかなように、マット剤を含有しない試料１０１に対して、本発明の試料２０４、２０５、２０８、２１０は離型性で良好な結果が得られた。また、試料１０４と試料２０４、試料１０５と試料２０５、試料１１０と試料２１０との比較から、マット剤添加量を減らすと、離型性は許容範囲内で低下させるが、画質粒状性は向上することが分かる。一方で、試料２０８は、試料１０８と比して、離型性、画質粒状性ともに良く、最も良好な結果が得られた。   As is clear from Table 3, the samples 204, 205, 208, and 210 of the present invention obtained good results with releasability compared to the sample 101 containing no matting agent. Further, from the comparison between Sample 104 and Sample 204, Sample 105 and Sample 205, and Sample 110 and Sample 210, when the amount of the matting agent added is decreased, the releasability is lowered within an allowable range, but the image quality granularity is improved. I understand that. On the other hand, the sample 208 had better releasability and image quality granularity than the sample 108, and the best results were obtained.

Claims (9)

支持体上に、マット剤を含む少なくとも１層の受容層を有し、該マット剤が、粒径１〜１０μｍであって、かつ有機化合物を含有する微粒子であることを特徴とする感熱転写受像シート。   A heat-sensitive transfer image-receiving image having at least one receiving layer containing a matting agent on a support, wherein the matting agent is a fine particle having a particle diameter of 1 to 10 μm and containing an organic compound. Sheet. 前記マット剤のガラス転移温度が９０℃以上であることを特徴とする請求項１に記載の感熱転写受像シート。   The thermal transfer image-receiving sheet according to claim 1, wherein the matting agent has a glass transition temperature of 90 ° C. or higher. 前記マット剤のガラス転移温度が１３０℃以上であることを特徴とする請求項１に記載の感熱転写受像シート。   The thermal transfer image-receiving sheet according to claim 1, wherein the matting agent has a glass transition temperature of 130 ° C or higher. 前記マット剤の分解温度が２００℃以上であることを特徴とする請求項１に記載の感熱転写受像シート。   The thermal transfer image-receiving sheet according to claim 1, wherein a decomposition temperature of the matting agent is 200 ° C or higher. 前記マット剤がメラミン樹脂を含有することを特徴とする請求項１〜４のいずれか１項に記載の感熱転写受像シート。   The thermal transfer image-receiving sheet according to any one of claims 1 to 4, wherein the matting agent contains a melamine resin. 前記受容層と支持体の間に少なくとも１層の中空ポリマーラテックス及び水溶性ポリマーを含有する断熱層を有することを特徴とする請求項１〜５のいずれか１項に記載の感熱転写受像シート。   The heat-sensitive transfer image-receiving sheet according to any one of claims 1 to 5, further comprising a heat-insulating layer containing at least one hollow polymer latex and a water-soluble polymer between the receiving layer and the support. 前記受容層が、少なくとも１種のポリマーラテックスを含有することを特徴とする請求項１〜６のいずれか１項に記載の感熱転写受像シート。   The heat-sensitive transfer image-receiving sheet according to claim 1, wherein the receiving layer contains at least one polymer latex. 請求項１〜７のいずれか１項に記載の感熱転写受像シートの製造工程において、前記受容層とこれに隣接する層とを同時に塗布して製造することを特徴とする感熱転写受像シートの製造方法。   In the manufacturing process of the thermal transfer image receiving sheet of any one of Claims 1-7, manufacture of the thermal transfer image receiving sheet characterized by apply | coating and manufacturing the said receiving layer and the layer adjacent to this simultaneously. Method. 前記隣接層が断熱層であることを特徴とする請求項８に記載の感熱転写受像シートの製造方法。
The method for producing a thermal transfer image-receiving sheet according to claim 8, wherein the adjacent layer is a heat insulating layer.