JP2007161804A - Epoxy resin composition for sealing and electronic part device - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To obtain a non-halogen and non-antimony epoxy resin composition for sealing having good flame retardancy without reducing reliability in characteristics such as moldability, reflow resistance, moisture resistance and high temperature released characteristics and the like and provide electronic parts devices equipped with elements sealed with the same. <P>SOLUTION: The epoxy resin composition for sealing comprises (A) an epoxy resin and (B) a curing agent and contains (C) a compound expressed by general formula (I) as (B) the curing agent. In the formula (I), R<SP>1</SP>is selected from H, OH, a 1-8C alkyl and a 1-6C alkoxy and all R<SP>1</SP>s may be the same or different; R<SP>2</SP>and R<SP>3</SP>are each selected from H and a 1-6C alkyl and all of them may be the same or different; n expresses 1-20 integer; m expresses 1-3 integer. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、封止用エポキシ樹脂組成物及びこの組成物で封止した素子を備えた電子部品装置に関する。   The present invention relates to an epoxy resin composition for sealing and an electronic component device provided with an element sealed with this composition.

従来から、トランジスタ、ＩＣ等の電子部品装置の素子封止の分野では生産性、コスト等の面から樹脂封止が主流となり、エポキシ樹脂成形材料が広く用いられている。この理由としては、エポキシ樹脂が電気特性、耐湿性、耐熱性、機械特性、インサート品との接着性などの諸特性にバランスがとれているためである。これらの封止用エポキシ樹脂成形材料の難燃化は主にテトラブロモビスフェノールＡのジグリシジルエーテル等のブロム化樹脂と酸化アンチモンの組合せにより行われている。   Conventionally, in the field of element sealing of electronic component devices such as transistors and ICs, resin sealing has been the mainstream in terms of productivity and cost, and epoxy resin molding materials have been widely used. This is because epoxy resins are balanced in various properties such as electrical properties, moisture resistance, heat resistance, mechanical properties, and adhesiveness with inserts. The flame-retardant of these sealing epoxy resin molding materials is mainly performed by a combination of a brominated resin such as diglycidyl ether of tetrabromobisphenol A and antimony oxide.

近年、環境保護の観点からＲｏＨＳ、ＷＥＥＥ等、臭素系化合物に関する法規制の動きがあり、封止用エポキシ樹脂成形材料についてもノンハロゲン化（ノンブロム化）及びノンアンチモン化の要求が出てきている。また、プラスチック封止ＩＣの高温放置特性にブロム化合物が悪影響を及ぼすことが知られており、この観点からもブロム化樹脂量の低減が望まれている。   In recent years, there has been a movement of laws and regulations relating to brominated compounds such as RoHS and WEEE from the viewpoint of environmental protection, and there has been a demand for non-halogenation (non-bromination) and non-antimony formation for epoxy resin molding materials for sealing. In addition, it is known that a bromo compound has an adverse effect on the high temperature storage characteristics of a plastic encapsulated IC. From this viewpoint, reduction of the amount of bromo resin is desired.

そこで、ブロム化樹脂や酸化アンチモンを用いずに難燃化を達成する手法としては、赤リンを用いる方法（例えば特許文献１参照。）、リン酸エステル化合物を用いる方法（例えば特許文献２参照。）、ホスファゼン化合物を用いる方法（例えば特許文献３参照。）、金属水酸化物を用いる方法（例えば特許文献４参照。）、金属水酸化物と金属酸化物を併用する方法（例えば特許文献５参照。）、フェロセン等のシクロペンタジエニル化合物（例えば特許文献６参照。）、アセチルアセトナート銅（例えば非特許文献１参照。）等の有機金属化合物を用いる方法などのハロゲン、アンチモン以外の難燃剤を用いる方法、充填剤の割合を高くする方法（例えば特許文献７参照。）、また最近では、難燃性の高い樹脂を使用する方法（例えば特許文献８参照。）等が試みられている。   Therefore, as a method for achieving flame retardancy without using brominated resin or antimony oxide, a method using red phosphorus (for example, see Patent Document 1) and a method using a phosphoric ester compound (for example, see Patent Document 2). ), A method using a phosphazene compound (for example, see Patent Document 3), a method using a metal hydroxide (for example, see Patent Document 4), and a method for using a metal hydroxide and a metal oxide in combination (for example, see Patent Document 5). ), Cyclopentadienyl compounds such as ferrocene (see, for example, Patent Document 6), flame retardants other than halogen and antimony, such as methods using organometallic compounds such as acetylacetonate copper (see, for example, Non-Patent Document 1). , A method of increasing the ratio of the filler (see, for example, Patent Document 7), and recently, a method of using a highly flame-retardant resin (for example, special References 8.), And the like have been attempted.

特開平９−２２７７６５号公報JP-A-9-227765 特開平９−２３５４４９号公報JP 9-235449 A 特開平８−２２５７１４号公報JP-A-8-225714 特開平９−２４１４８３号公報Japanese Patent Laid-Open No. 9-241383 特開平９−１００３３７号公報Japanese Patent Laid-Open No. 9-130037 特開平１１−２６９３４９号公報JP-A-11-269349 特開平７−８２３４３号公報JP 7-82343 A 特開平１１−１４０２７７号公報JP-A-11-140277 加藤寛、機能材料、１１（６）、３４（１９９１）Hiroshi Kato, Functional Materials, 11 (6), 34 (1991)

しかしながら、封止用エポキシ樹脂成形材料に赤リンを用いた場合は耐湿性の低下の問題、リン酸エステル化合物やホスファゼン化合物を用いた場合は可塑化による成形性の低下や耐湿性の低下の問題、金属水酸化物を用いた場合は流動性や金型離型性の低下の問題、金属酸化物を用いた場合や、充填剤の割合を高くした場合は流動性の低下の問題がそれぞれある。また、アセチルアセトナート銅等の有機金属化合物を用いた場合は、硬化反応を阻害し成形性が低下する問題がある。さらにはこれまで発明された難燃性の高い樹脂を使用する方法では、難燃性が電子部品装置の材料に求められるＵＬ−９４ Ｖ−０を十分に満足するものではなかった。   However, when red phosphorus is used as the epoxy resin molding material for sealing, there is a problem of reduced moisture resistance, and when a phosphoric ester compound or phosphazene compound is used, there is a problem of reduced moldability or reduced moisture resistance due to plasticization. When using metal hydroxides, there are problems of lowering fluidity and mold releasability, and when using metal oxides or increasing the proportion of filler, there are problems of lowering fluidity. . Further, when an organometallic compound such as acetylacetonate copper is used, there is a problem that the curing reaction is inhibited and the moldability is lowered. Furthermore, the method using a highly flame-retardant resin invented so far does not sufficiently satisfy UL-94 V-0, which is required for materials of electronic component devices.

以上のようにこれらノンハロゲン、ノンアンチモン系の難燃剤、充填剤の割合を高くする方法及び難燃性の高い樹脂を使用する方法では、いずれの場合もブロム化樹脂と酸化アンチモンを併用した封止用エポキシ樹脂成形材料と同等の成形性、信頼性及び難燃性を得るに至っていない。   As described above, in the method of increasing the proportion of these non-halogen, non-antimony flame retardants and fillers and the method using a highly flame-retardant resin, sealing using both a brominated resin and antimony oxide is used in both cases. The moldability, reliability, and flame retardancy equivalent to the epoxy resin molding materials for use have not been achieved.

本発明はかかる状況に鑑みなされたもので、ノンハロゲンかつノンアンチモンで、成形性、耐リフロー性、耐湿性及び高温放置特性等の信頼性を低下させずに難燃性が良好な封止用エポキシ樹脂材料、及びこれにより封止した素子を備えた電子部品装置を提供しようとするものである。   The present invention has been made in view of such circumstances, and is an epoxy for sealing that is non-halogen and non-antimony and has good flame retardancy without reducing reliability such as moldability, reflow resistance, moisture resistance, and high-temperature storage properties. An object of the present invention is to provide an electronic component device including a resin material and an element sealed thereby.

本発明者らは上記の課題を解決するために鋭意検討を重ねた結果、特定の化合物を配合した封止用エポキシ樹脂組成物により上記の目的を達成しうることを見い出し、本発明を完成するに至った。   As a result of intensive studies to solve the above-mentioned problems, the present inventors have found that the above object can be achieved by an epoxy resin composition for sealing containing a specific compound, thereby completing the present invention. It came to.

本願は以下の発明に関する。
（１）（Ａ）エポキシ樹脂、（Ｂ）硬化剤を含有し、（Ｂ）硬化剤として（Ｃ）下記一般式（Ｉ）で示される化合物を含有する封止用エポキシ樹脂組成物。 The present application relates to the following inventions.
(1) An epoxy resin composition for sealing containing (A) an epoxy resin, (B) a curing agent, and (B) a compound represented by the following general formula (I) as (B) the curing agent.

（一般式（Ｉ）中のＲ¹は水素原子、水酸基、炭素数１〜８のアルキル基、炭素数１〜６のアルコキシ基から選ばれ、全てが同一でも異なっていてもよい。Ｒ²、Ｒ³は水素原子、炭素数１〜６のアルキル基から選ばれ、全てが同一でも異なっていてもよい。ｎは１〜２０の整数を示し、ｍは１〜３の整数を示す。）

(R ¹ in the general formula (I) is selected from a hydrogen atom, a hydroxyl group, an alkyl group having 1 to 8 carbon atoms, and an alkoxy group having 1 to 6 carbon atoms, all of which may be the same or different. R ² , R ³ is selected from a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, all of which may be the same or different, n represents an integer of 1 to 20, and m represents an integer of 1 to 3.

（２）一般式（Ｉ）で示される化合物（Ｃ）中のｍが１または２である上記（１）記載の封止用エポキシ樹脂組成物。
（３）（Ａ）エポキシ樹脂がビフェニル型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、スチルベン型エポキシ樹脂、硫黄原子含有エポキシ樹脂、ノボラック型エポキシ樹脂、ジシクロペンタジエン型エポキシ樹脂、ナフタレン型エポキシ樹脂、トリフェニルメタン型エポキシ樹脂、ビフェニレン型エポキシ樹脂及びナフトール・アラルキル型フェノール樹脂のうち少なくとも１種を含有する上記（１）又は（２）記載の封止用エポキシ樹脂組成物。
（４）（Ｃ）一般式（Ｉ）で示される化合物を、（Ａ）エポキシ樹脂中に４０〜１００質量％含む上記（１）〜（３）いずれかに記載の封止用エポキシ樹脂組成物。
（５）（Ｃ）一般式（Ｉ）で示される化合物を、（Ａ）エポキシ樹脂中に６０〜１００質量％含む上記（１）〜（３）いずれかに記載の封止用エポキシ樹脂組成物。
（６）（Ｂ）硬化剤がビフェニル型フェノール樹脂、アラルキル型フェノール樹脂、ジシクロペンタジエン型フェノール樹脂、トリフェニルメタン型フェノール樹脂及びノボラック型フェノール樹脂のうち少なくとも１種を含有する上記（１）〜（５）いずれかに記載の封止用エポキシ樹脂組成物。
（７）さらに（Ｄ）硬化促進剤を含有する上記（１）〜（６）いずれかに記載の封止用エポキシ樹脂組成物。
（８）（Ｄ）硬化促進剤がトリフェニルホスフィンである上記（７）記載の封止用エポキシ樹脂組成物。
（９）（Ｄ）硬化促進剤が第三ホスフィン化合物とキノン化合物との付加物である上記（７）記載の封止用エポキシ樹脂組成物。
（１０）さらに（Ｅ）無機充填剤を含有する上記（１）〜（９）いずれかに記載の封止用エポキシ樹脂組成物。
（１１）（Ｅ）無機充填剤の含有量が封止用エポキシ樹脂組成物中６０〜９５質量％である上記（１０）記載の封止用エポキシ樹脂組成物。
（１２）（Ｅ）無機充填剤の含有量が封止用エポキシ樹脂組成物中７０〜９０質量％である上記（１０）記載の封止用エポキシ樹脂組成物。
（１３）さらに（Ｆ）カップリング剤を含有する上記（１）〜（１２）いずれかに記載の封止用エポキシ樹脂組成物。
（１４）（Ｆ）カップリング剤が２級アミノ基を有するシランカップリング剤を含有する上記（１３）記載の封止用エポキシ樹脂組成物。
（１５）２級アミノ基を有するシランカップリング剤が下記一般式（ＩＩ）で示される化合物を含有する上記（１４）記載の封止用エポキシ樹脂組成物。 (2) The epoxy resin composition for sealing according to the above (1), wherein m in the compound (C) represented by the general formula (I) is 1 or 2.
(3) (A) Epoxy resin is biphenyl type epoxy resin, bisphenol F type epoxy resin, stilbene type epoxy resin, sulfur atom-containing epoxy resin, novolac type epoxy resin, dicyclopentadiene type epoxy resin, naphthalene type epoxy resin, triphenyl The sealing epoxy resin composition according to the above (1) or (2), which contains at least one of a methane type epoxy resin, a biphenylene type epoxy resin, and a naphthol / aralkyl type phenol resin.
(4) (C) The epoxy resin composition for sealing according to any one of the above (1) to (3), wherein the compound represented by the general formula (I) is contained in 40 to 100% by mass in the (A) epoxy resin. .
(5) (C) The epoxy resin composition for sealing according to any one of (1) to (3), wherein the compound represented by the general formula (I) is contained in 60 to 100% by mass in the (A) epoxy resin. .
(6) (B) The above (1) to (B), wherein the curing agent contains at least one of biphenyl type phenol resin, aralkyl type phenol resin, dicyclopentadiene type phenol resin, triphenylmethane type phenol resin and novolac type phenol resin. (5) The epoxy resin composition for sealing according to any one of the above.
(7) The epoxy resin composition for sealing according to any one of (1) to (6), further comprising (D) a curing accelerator.
(8) The epoxy resin composition for sealing according to the above (7), wherein (D) the curing accelerator is triphenylphosphine.
(9) The epoxy resin composition for sealing according to (7), wherein (D) the curing accelerator is an adduct of a third phosphine compound and a quinone compound.
(10) The sealing epoxy resin composition according to any one of (1) to (9), further comprising (E) an inorganic filler.
(11) The epoxy resin composition for sealing according to the above (10), wherein the content of (E) inorganic filler is 60 to 95% by mass in the epoxy resin composition for sealing.
(12) The epoxy resin composition for sealing according to the above (10), wherein the content of the inorganic filler (E) is 70 to 90% by mass in the epoxy resin composition for sealing.
(13) The sealing epoxy resin composition according to any one of (1) to (12), further comprising (F) a coupling agent.
(14) The epoxy resin composition for sealing according to (13), wherein the (F) coupling agent contains a silane coupling agent having a secondary amino group.
(15) The epoxy resin composition for sealing according to (14), wherein the silane coupling agent having a secondary amino group contains a compound represented by the following general formula (II).

（ここで、Ｒ^１は水素原子、炭素数１〜６のアルキル基及び炭素数１〜２のアルコキシ基から選ばれ、Ｒ^２は炭素数１〜６のアルキル基及びフェニル基から選ばれ、Ｒ^３はメチル基又はエチル基を示し、ｎは１〜６の整数を示し、ｍは１〜３の整数を示す。）

(Where R ¹ is selected from a hydrogen atom, an alkyl group having 1 to 6 carbon atoms and an alkoxy group having 1 to ² carbon atoms, R ² is selected from an alkyl group having 1 to 6 carbon atoms and a phenyl group; ³ represents a methyl group or an ethyl group, n represents an integer of 1 to 6, and m represents an integer of 1 to ^3. )

（１６）上記（１）〜（１５）のいずれかに記載の封止用エポキシ樹脂組成物で封止された素子を備えた電子部品装置。 (16) An electronic component device including an element sealed with the sealing epoxy resin composition according to any one of (1) to (15).

本発明による封止用エポキシ樹脂組成物は難燃性が良好な電子部品装置等の製品を得ることができ、その工業的価値は大である。   The epoxy resin composition for sealing according to the present invention can provide products such as electronic component devices having good flame retardancy, and its industrial value is great.

本発明において用いられる（Ａ）エポキシ樹脂は従来公知のエポキシ樹脂を使用することができる。使用可能なエポキシ樹脂としては、たとえば、フェノールノボラック型エポキシ樹脂、オルソクレゾールノボラック型エポキシ樹脂、トリフェニルメタン骨格を有するエポキシ樹脂をはじめとするフェノール、クレゾール、キシレノール、レゾルシン、カテコール、ビスフェノールＡ、ビスフェノールＦ等のフェノール類及び／又はα−ナフトール、β−ナフトール、ジヒドロキシナフタレン等のナフトール類とホルムアルデヒド、アセトアルデヒド、プロピオンアルデヒド、ベンズアルデヒド、サリチルアルデヒド等のアルデヒド基を有する化合物とを酸性触媒下で縮合又は共縮合させて得られるノボラック樹脂をエポキシ化したもの。ビスフェノールＡ、ビスフェノールＦ、ビスフェノールＳ、アルキル置換又は非置換のビフェノール等のジグリシジルエーテル。スチルベン型エポキシ樹脂、ハイドロキノン型エポキシ樹脂、フタル酸、ダイマー酸等の多塩基酸とエピクロルヒドリンの反応により得られるグリシジルエステル型エポキシ樹脂、ジアミノジフェニルメタン、イソシアヌル酸等のポリアミンとエピクロルヒドリンの反応により得られるグリシジルアミン型エポキシ樹脂、ジシクロペンタジエンとフェノール類の共縮合樹脂のエポキシ化物、ナフタレン環を有するエポキシ樹脂、キシリレン骨格、ビフェニレン骨格を含有するフェノール・アラルキル樹脂、ナフトール・アラルキル樹脂等のアラルキル型フェノール樹脂のエポキシ化物、トリメチロールプロパン型エポキシ樹脂、テルペン変性エポキシ樹脂、オレフィン結合を過酢酸等の過酸で酸化して得られる線状脂肪族エポキシ樹脂、脂環族エポキシ樹脂、硫黄原子含有エポキシ樹脂などが挙げられ、これらを単独で用いても２種以上を組み合わせて併用して用いてもよい。   A conventionally well-known epoxy resin can be used for the (A) epoxy resin used in this invention. Usable epoxy resins include, for example, phenol novolac type epoxy resins, orthocresol novolac type epoxy resins, epoxy resins having a triphenylmethane skeleton, phenol, cresol, xylenol, resorcin, catechol, bisphenol A, bisphenol F And / or naphthols such as α-naphthol, β-naphthol and dihydroxynaphthalene and compounds having an aldehyde group such as formaldehyde, acetaldehyde, propionaldehyde, benzaldehyde and salicylaldehyde in an acidic catalyst. Epoxidized novolac resin obtained by the process. Diglycidyl ethers such as bisphenol A, bisphenol F, bisphenol S, alkyl-substituted or unsubstituted biphenol. Stilbene type epoxy resin, hydroquinone type epoxy resin, glycidyl ester type epoxy resin obtained by reaction of polybasic acid such as phthalic acid and dimer acid and epichlorohydrin, diaminodiphenylmethane, isocyanuric acid etc. glycidylamine obtained by reaction of epichlorohydrin Type epoxy resin, epoxidized product of co-condensation resin of dicyclopentadiene and phenol, epoxy resin having naphthalene ring, xylylene skeleton, phenol / aralkyl resin containing biphenylene skeleton, epoxy of aralkyl type phenol resin such as naphthol / aralkyl resin , Trimethylolpropane type epoxy resin, terpene modified epoxy resin, linear aliphatic epoxy resin obtained by oxidizing olefinic bond with peracid such as peracetic acid, alicyclic ring Epoxy resins, include such sulfur-containing epoxy resins may be used in combination or in combination of two or more with these alone.

なかでも、流動性及び耐リフロー性の観点からはビフェニル型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、スチルベン型エポキシ樹脂及び硫黄原子含有エポキシ樹脂が好ましく、硬化性の観点からはノボラック型エポキシ樹脂が好ましく、低吸湿性の観点からはジシクロペンタジエン型エポキシ樹脂が好ましく、耐熱性及び低反り性の観点からはナフタレン型エポキシ樹脂及びトリフェニルメタン型エポキシ樹脂が好ましく、難燃性の観点からはビフェニレン型エポキシ樹脂及びナフトール・アラルキル型エポキシ樹脂が好ましい。これらのエポキシ樹脂の少なくとも１種を含有していることが好ましい。   Among them, biphenyl type epoxy resin, bisphenol F type epoxy resin, stilbene type epoxy resin and sulfur atom-containing epoxy resin are preferable from the viewpoint of fluidity and reflow resistance, and novolac type epoxy resin is preferable from the viewpoint of curability, From the viewpoint of low hygroscopicity, dicyclopentadiene type epoxy resin is preferable. From the viewpoint of heat resistance and low warpage, naphthalene type epoxy resin and triphenylmethane type epoxy resin are preferable. From the viewpoint of flame retardancy, biphenylene type epoxy resin is preferable. Resins and naphthol / aralkyl epoxy resins are preferred. It is preferable to contain at least one of these epoxy resins.

ビフェニル型エポキシ樹脂としてはたとえば下記一般式（ＩＩＩ）で示されるエポキシ樹脂等が挙げられ、ビスフェノールＦ型エポキシ樹脂としてはたとえば下記一般式（ＩＶ）で示されるエポキシ樹脂等が挙げられ、スチルベン型エポキシ樹脂としてはたとえば下記一般式（Ｖ）で示されるエポキシ樹脂等が挙げられ、硫黄原子含有エポキシ樹脂としてはたとえば下記一般式（ＶＩ）で示されるエポキシ樹脂等が挙げられる。   Examples of the biphenyl type epoxy resin include an epoxy resin represented by the following general formula (III). Examples of the bisphenol F type epoxy resin include an epoxy resin represented by the following general formula (IV), and a stilbene type epoxy resin. Examples of the resin include an epoxy resin represented by the following general formula (V), and examples of the sulfur atom-containing epoxy resin include an epoxy resin represented by the following general formula (VI).

（ここで、Ｒ^１〜Ｒ^８は水素原子及び炭素数１〜１０の置換又は非置換の一価の炭化水素基から選ばれ、全てが同一でも異なっていてもよい。ｎは０〜３の整数を示す。）

(Here, R ^{1 to} R ⁸ are selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, all of which may be the same or different. N is 0 to 3). Indicates an integer.)

（ここで、Ｒ^１〜Ｒ^８は水素原子、炭素数１〜１０のアルキル基、炭素数１〜１０のアルコキシル基、炭素数６〜１０のアリール基、及び炭素数６〜１０のアラルキル基から選ばれ、全てが同一でも異なっていてもよい。ｎは０〜３の整数を示す。）

(Here, R ^{1 to} R ⁸ are a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, an alkoxyl group having 1 to 10 carbon atoms, an aryl group having 6 to 10 carbon atoms, and an aralkyl group having 6 to 10 carbon atoms. All may be the same or different, and n represents an integer of 0 to 3.)

（ここで、Ｒ^１〜Ｒ^８は水素原子及び炭素数１〜５の置換又は非置換の一価の炭化水素基から選ばれ、全てが同一でも異なっていてもよい。ｎは０〜１０の整数を示す。）

(Here, R ^{1 to} R ⁸ are selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 5 carbon atoms, and all may be the same or different. N is 0 to 10. Indicates an integer.)

（ここで、Ｒ^１〜Ｒ^８は水素原子、置換又は非置換の炭素数１〜１０のアルキル基及び置換又は非置換の炭素数１〜１０のアルコキシ基から選ばれ、全てが同一でも異なっていてもよい。ｎは０〜３の整数を示す。）

(Here, R ^{1 to} R ⁸ are selected from a hydrogen atom, a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, and a substituted or unsubstituted alkoxy group having 1 to 10 carbon atoms, all of which are the same or different. (N represents an integer of 0 to 3.)

上記一般式（ＩＩＩ）で示されるビフェニル型エポキシ樹脂としては、たとえば、４，４´−ビス（２，３−エポキシプロポキシ）ビフェニル又は４，４´−ビス（２，３−エポキシプロポキシ）−３，３´，５，５´−テトラメチルビフェニルを主成分とするエポキシ樹脂、エピクロルヒドリンと４，４´−ビフェノール又は４，４´−（３，３´，５，５´−テトラメチル）ビフェノールとを反応させて得られるエポキシ樹脂等が挙げられる。なかでも４，４´−ビス（２，３−エポキシプロポキシ）−３，３´，５，５´−テトラメチルビフェニルを主成分とするエポキシ樹脂が好ましい。このような化合物としてはＹＸ−４０００（ジャパンエポキシレジン株式会社製商品名）等が市販品として入手可能である。   Examples of the biphenyl type epoxy resin represented by the general formula (III) include 4,4′-bis (2,3-epoxypropoxy) biphenyl or 4,4′-bis (2,3-epoxypropoxy) -3. , 3 ', 5,5'-tetramethylbiphenyl as the main component, epichlorohydrin and 4,4'-biphenol or 4,4'-(3,3 ', 5,5'-tetramethyl) biphenol An epoxy resin obtained by reacting is used. Among these, an epoxy resin mainly composed of 4,4′-bis (2,3-epoxypropoxy) -3,3 ′, 5,5′-tetramethylbiphenyl is preferable. As such a compound, YX-4000 (trade name, manufactured by Japan Epoxy Resin Co., Ltd.) and the like are commercially available.

上記一般式（ＩＶ）で示されるビスフェノールＦ型エポキシ樹脂としては、例えば、Ｒ^１、Ｒ^３、Ｒ^６及びＲ^８がメチル基で、Ｒ^２、Ｒ^４、Ｒ^５及びＲ^７が水素原子であり、ｎ＝０を主成分とするＹＳＬＶ−８０ＸＹ（東都化成株式会社製商品名）等が市販品として入手可能である。 Examples of the bisphenol F-type epoxy resin represented by the general formula (IV) include, for example, R ¹ , R ³ , R ⁶ and R ⁸ are methyl groups, and R ² , R ⁴ , R ⁵ and R ⁷ are hydrogen atoms. Yes, YSLV-80XY (trade name, manufactured by Toto Kasei Co., Ltd.) having n = 0 as a main component is commercially available.

上記一般式（Ｖ）で示されるスチルベン型エポキシ樹脂は、原料であるスチルベン系フェノール類とエピクロルヒドリンとを塩基性物質存在下で反応させて得ることができる。この原料であるスチルベン系フェノール類としては、たとえば３−ｔｅｒｔ−ブチル−４，４′−ジヒドロキシ−３′，５，５′−トリメチルスチルベン、３−ｔｅｒｔ−ブチル−４，４′−ジヒドロキシ−３′，５′，６−トリメチルスチルベン、４，４´−ジヒドロキシ−３，３´，５，５´−テトラメチルスチルベン、４，４´−ジヒドロキシ−３，３´−ジ−ｔｅｒｔ−ブチル−５，５´−ジメチルスチルベン、４，４´−ジヒドロキシ−３，３´−ジ−ｔｅｒｔ−ブチル−６，６´−ジメチルスチルベン等が挙げられ、なかでも３−ｔｅｒｔ−ブチル−４，４′−ジヒドロキシ−３′，５，５′−トリメチルスチルベン、及び４，４´−ジヒドロキシ−３，３´，５，５´−テトラメチルスチルベンが好ましい。これらのスチルベン型フェノール類は単独で用いても２種以上を組み合わせて用いてもよい。   The stilbene type epoxy resin represented by the general formula (V) can be obtained by reacting a stilbene phenol as a raw material with epichlorohydrin in the presence of a basic substance. Examples of the raw material stilbene phenols include 3-tert-butyl-4,4′-dihydroxy-3 ′, 5,5′-trimethylstilbene, 3-tert-butyl-4,4′-dihydroxy-3. ', 5', 6-trimethylstilbene, 4,4'-dihydroxy-3,3 ', 5,5'-tetramethylstilbene, 4,4'-dihydroxy-3,3'-di-tert-butyl-5 , 5'-dimethylstilbene, 4,4'-dihydroxy-3,3'-di-tert-butyl-6,6'-dimethylstilbene, among others, 3-tert-butyl-4,4'- Dihydroxy-3 ', 5,5'-trimethylstilbene and 4,4'-dihydroxy-3,3', 5,5'-tetramethylstilbene are preferred. These stilbene type phenols may be used alone or in combination of two or more.

上記一般式（ＶＩ）で示される硫黄原子含有エポキシ樹脂のなかでも、Ｒ^２、Ｒ^３、Ｒ^６及びＲ^７が水素原子で、Ｒ^１、Ｒ^４、Ｒ^５及びＲ^８がアルキル基であるエポキシ樹脂が好ましく、Ｒ^２、Ｒ^３、Ｒ^６及びＲ^７が水素原子で、Ｒ^１及びＲ^８がｔｅｒｔ−ブチル基で、Ｒ^４及びＲ^５がメチル基であるエポキシ樹脂がより好ましい。このような化合物としては、ＹＳＬＶ−１２０ＴＥ（東都化成株式会社製商品名）等が市販品として入手可能である。これらのエポキシ樹脂はいずれか１種を単独で併用に用いても２種以上を組合わせて併用に用いてもよい。 Among the sulfur atom-containing epoxy resins represented by the general formula (VI), R ² , R ³ , R ⁶ and R ⁷ are hydrogen atoms, and R ¹ , R ⁴ , R ⁵ and R ⁸ are alkyl groups. An epoxy resin is preferred, and an epoxy resin in which R ² , R ³ , R ⁶ and R ⁷ are hydrogen atoms, R ¹ and R ⁸ are tert-butyl groups, and R ⁴ and R ⁵ are methyl groups is more preferred. As such a compound, YSLV-120TE (trade name, manufactured by Tohto Kasei Co., Ltd.) and the like are available as commercial products. Any one of these epoxy resins may be used alone or in combination of two or more.

ノボラック型エポキシ樹脂としては、たとえば下記一般式（ＶＩＩ）で示されるエポキシ樹脂等が挙げられる。   Examples of the novolac type epoxy resin include an epoxy resin represented by the following general formula (VII).

（ここで、Ｒは水素原子及び炭素数１〜１０の置換又は非置換の一価の炭化水素基から選ばれ、ｎは０〜１０の整数を示す。）

(Here, R is selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, and n represents an integer of 0 to 10.)

上記一般式（ＶＩＩ）で示されるノボラック型エポキシ樹脂は、ノボラック型フェノール樹脂にエピクロルヒドリンを反応させることによって容易に得られる。なかでも、一般式（ＶＩＩ）中のＲとしては、メチル基、エチル基、プロピル基、ブチル基、イソプロピル基、イソブチル基等の炭素数１〜１０のアルキル基、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基等の炭素数１〜１０のアルコキシル基が好ましく、水素原子又はメチル基がより好ましい。ｎは０〜３の整数が好ましい。上記一般式（ＶＩＩ）で示されるノボラック型エポキシ樹脂のなかでも、オルトクレゾールノボラック型エポキシ樹脂が好ましい。このような化合物としてはＥＯＣＮ−１０２０（日本化薬株式会社製商品名）等が市販品として入手可能である。   The novolak-type epoxy resin represented by the general formula (VII) can be easily obtained by reacting novolak-type phenol resin with epichlorohydrin. Especially, as R in general formula (VII), it is a C1-C10 alkyl group, such as a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, an isobutyl group, a methoxy group, an ethoxy group, a propoxy group. C1-C10 alkoxyl groups, such as a butoxy group, are preferable, and a hydrogen atom or a methyl group is more preferable. n is preferably an integer of 0 to 3. Among the novolak type epoxy resins represented by the general formula (VII), orthocresol novolak type epoxy resins are preferable. As such a compound, EOCN-1020 (trade name, manufactured by Nippon Kayaku Co., Ltd.) and the like are commercially available.

ジシクロペンタジエン型エポキシ樹脂としては、たとえば下記一般式（ＶＩＩＩ）で示されるエポキシ樹脂等が挙げられる。   Examples of the dicyclopentadiene type epoxy resin include an epoxy resin represented by the following general formula (VIII).

（ここで、Ｒ^１及びＲ^２は水素原子及び炭素数１〜１０の置換又は非置換の一価の炭化水素基からそれぞれ独立して選ばれ、ｎは０〜１０の整数を示し、ｍは０〜６の整数を示す。）

Wherein R ¹ and R ² are each independently selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, n is an integer of 0 to 10, and m is Represents an integer of 0 to 6.)

上記式（ＶＩＩＩ）中のＲ^１としては、たとえば、水素原子、メチル基、エチル基、プロピル基、ブチル基、イソプロピル基、ｔｅｒｔ−ブチル基等のアルキル基、ビニル基、アリル基、ブテニル基等のアルケニル基、ハロゲン化アルキル基、アミノ基置換アルキル基、メルカプト基置換アルキル基などの炭素数１〜５の置換又は非置換の一価の炭化水素基が挙げられ、なかでもメチル基、エチル基等のアルキル基及び水素原子が好ましく、メチル基及び水素原子がより好ましい。Ｒ^２としては、たとえば、水素原子、メチル基、エチル基、プロピル基、ブチル基、イソプロピル基、ｔｅｒｔ−ブチル基等のアルキル基、ビニル基、アリル基、ブテニル基等のアルケニル基、ハロゲン化アルキル基、アミノ基置換アルキル基、メルカプト基置換アルキル基などの炭素数１〜５の置換又は非置換の一価の炭化水素基が挙げられ、なかでも水素原子が好ましい。このような化合物としてはＨＰ−７２００（大日本インキ化学工業株式会社製商品名）等が市販品として入手可能である。 R ¹ in the above formula (VIII) is, for example, a hydrogen atom, an alkyl group such as a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, or a tert-butyl group, a vinyl group, an allyl group, or a butenyl group. C1-C5 substituted or unsubstituted monovalent hydrocarbon groups such as alkenyl groups, halogenated alkyl groups, amino group-substituted alkyl groups, mercapto group-substituted alkyl groups, and the like. Among them, methyl groups, ethyl groups Alkyl groups and hydrogen atoms such as methyl groups and hydrogen atoms are more preferable. Examples of R ² include a hydrogen atom, an alkyl group such as a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, and a tert-butyl group, an alkenyl group such as a vinyl group, an allyl group, and a butenyl group, and an alkyl halide. Examples thereof include substituted or unsubstituted monovalent hydrocarbon groups having 1 to 5 carbon atoms such as a group, an amino group-substituted alkyl group, and a mercapto group-substituted alkyl group, and among them, a hydrogen atom is preferable. As such a compound, HP-7200 (trade name, manufactured by Dainippon Ink and Chemicals, Inc.) is available as a commercial product.

ナフタレン型エポキシ樹脂としてはたとえば下記一般式（ＩＸ）で示されるエポキシ樹脂等が挙げられ、トリフェニルメタン型エポキシ樹脂としてはたとえば下記一般式（Ｘ）で示されるエポキシ樹脂等が挙げられる。   Examples of the naphthalene type epoxy resin include an epoxy resin represented by the following general formula (IX), and examples of the triphenylmethane type epoxy resin include an epoxy resin represented by the following general formula (X).

（ここで、Ｒ^１〜Ｒ^３は水素原子及び置換又は非置換の炭素数１〜１２の一価の炭化水素基から選ばれ、それぞれ全てが同一でも異なっていてもよい。ｐは１又は０で、ｌ、ｍはそれぞれ０〜１１の整数であって、（ｌ＋ｍ）が１〜１１の整数でかつ（ｌ＋ｐ）が１〜１２の整数となるよう選ばれる。ｉは０〜３の整数、ｊは０〜２の整数、ｋは０〜４の整数を示す。）

(Here, R ^{1 to} R ³ are selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 12 carbon atoms, all of which may be the same or different. P is 1 or 0. And l and m are each an integer of 0 to 11, wherein (l + m) is an integer of 1 to 11 and (l + p) is an integer of 1 to 12. i is an integer of 0 to 3, j represents an integer of 0 to 2, and k represents an integer of 0 to 4.)

上記一般式（ＩＸ）で示されるナフタレン型エポキシ樹脂としては、ｌ個の構成単位及びｍ個の構成単位をランダムに含むランダム共重合体、交互に含む交互共重合体、規則的に含む共重合体、ブロック状に含むブロック共重合体が挙げられ、これらのいずれか１種を単独で用いても、２種以上を組み合わせて用いてもよい。Ｒ^１、Ｒ^２が水素原子で、Ｒ^３がメチル基である上記化合物としては、ＮＣ−７０００（日本化薬株式会社製商品名）等が市販品として入手可能である。 The naphthalene type epoxy resin represented by the general formula (IX) includes a random copolymer containing 1 constituent unit and m constituent units at random, an alternating copolymer containing alternating units, and a copolymer containing regularly. Examples thereof include block copolymers which are included in a combined or block form, and any one of these may be used alone, or two or more may be used in combination. As the above compound in which R ¹ and R ² are hydrogen atoms and R ³ is a methyl group, NC-7000 (trade name, manufactured by Nippon Kayaku Co., Ltd.) is commercially available.

（ここで、Ｒは水素原子及び炭素数１〜１０の置換又は非置換の一価の炭化水素基から選ばれ、ｎは１〜１０の整数を示す。）

(Here, R is selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, and n represents an integer of 1 to 10.)

Ｒが水素原子である上記化合物としてはＥ−１０３２（ジャパンエポキシレジン株式会社製商品名）等が市販品として入手可能である。   As said compound whose R is a hydrogen atom, E-1032 (Japan Epoxy Resin Co., Ltd. brand name) etc. can be obtained as a commercial item.

ビフェニレン型エポキシ樹脂としてはたとえば下記一般式（ＸＩ）で示されるエポキシ樹脂等が挙げられ、ナフトール・アラルキル型エポキシ樹脂としてはたとえば下記一般式（ＸＩＩ）で示されるエポキシ樹脂等が挙げられる。   Examples of the biphenylene type epoxy resin include an epoxy resin represented by the following general formula (XI), and examples of the naphthol / aralkyl type epoxy resin include an epoxy resin represented by the following general formula (XII).

（上記式中のＲ^１〜Ｒ^９は全てが同一でも異なっていてもよく、水素原子、メチル基、エチル基、プロピル基、ブチル基、イソプロピル基、イソブチル基等の炭素数１〜１０のアルキル基、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基等の炭素数１〜１０のアルコキシル基、フェニル基、トリル基、キシリル基等の炭素数６〜１０のアリール基、及び、ベンジル基、フェネチル基等の炭素数６〜１０のアラルキル基から選ばれ、なかでも水素原子とメチル基が好ましい。ｎは０〜１０の整数を示す。）

(R ^{1 to} R ⁹ in the above formula may all be the same or different and are alkyls having 1 to 10 carbon atoms such as hydrogen atom, methyl group, ethyl group, propyl group, butyl group, isopropyl group, isobutyl group, etc. Group, methoxy group, ethoxy group, propoxy group, butoxy group, etc., C1-C10 alkoxyl group, phenyl group, tolyl group, xylyl group, etc. aryl group, benzyl group, phenethyl group Selected from aralkyl groups having 6 to 10 carbon atoms such as hydrogen atom and methyl group, and n represents an integer of 0 to 10.)

（ここで、Ｒ^１〜Ｒ^３は水素原子及び置換又は非置換の炭素数１〜１２の一価の炭化水素基から選ばれ、それぞれ全てが同一でも異なっていてもよい。ｎは１〜１０の整数を示す。）

(Here, R ^{1 to} R ³ are selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 12 carbon atoms, all of which may be the same or different. N is 1 to 10). Indicates an integer.)

ビフェニレン型エポキシ樹脂としてはＮＣ−３０００（日本化薬株式会社製商品名）が市販品として入手可能である。またナフトール・アラルキル型エポキシ樹脂としてはＥＳＮ−１７５等（東都化成株式会社製商品名）が市販品として入手可能である。これらのエポキシ樹脂はいずれか１種を単独で用いても両者を組合わせて用いてもよい。   As a biphenylene type epoxy resin, NC-3000 (trade name, manufactured by Nippon Kayaku Co., Ltd.) is commercially available. As naphthol / aralkyl type epoxy resins, ESN-175 (trade name, manufactured by Tohto Kasei Co., Ltd.) is commercially available. These epoxy resins may be used alone or in combination.

また（Ａ）エポキシ樹脂として下記構造式（ＸＩＩＩ）のエポキシ樹脂も使用することができる。   Moreover, the epoxy resin of following structural formula (XIII) can also be used as (A) epoxy resin.

（一般式（ＸＩＩＩ）中のＲ^１は、置換又は非置換の炭素数１〜１２の炭化水素基及び置換又は非置換の炭素数１〜１２のアルコキシ基から選ばれ、全てが同一でも異なっていてもよい。ｎは０〜４の整数を示す。またＲ^２は、置換又は非置換の炭素数１〜１２の炭化水素基及び置換又は非置換の炭素数１〜１２のアルコキシ基から選ばれ、全てが同一でも異なっていてもよい。ｍは０〜２の整数を示す。）

(R ¹ in the general formula (XIII) is selected from a substituted or unsubstituted hydrocarbon group having 1 to 12 carbon atoms and a substituted or unsubstituted alkoxy group having 1 to 12 carbon atoms, all of which are the same or different. N represents an integer of 0 to 4. R ² is selected from a substituted or unsubstituted hydrocarbon group having 1 to 12 carbon atoms and a substituted or unsubstituted alkoxy group having 1 to 12 carbon atoms. All may be the same or different, and m represents an integer of 0 to 2.)

上記一般式（ＸＩＩＩ）で示されるエポキシ樹脂としては、たとえば下記一般式（ＸＩＶ）〜（ＸＸＸＩＩ）で示されるエポキシ樹脂等が挙げられる。   Examples of the epoxy resin represented by the general formula (XIII) include epoxy resins represented by the following general formulas (XIV) to (XXXII).

なかでも、難燃性、成形性の観点からは上記一般式（ＸＩＶ）で示されるエポキシ樹脂が好ましい。このような化合物としてはＹＬ−７１７２（ジャパンエポキシレジン社製商品名）等が入手可能である。 Especially, the epoxy resin shown by the said general formula (XIV) is preferable from a viewpoint of a flame retardance and a moldability. As such a compound, YL-7172 (trade name of Japan Epoxy Resin Co., Ltd.) and the like are available.

また下記一般式（ＸＸＸＩＩＩ）で示される化合物を使用することもできる。   Moreover, the compound shown by the following general formula (XXXIII) can also be used.

（一般式（ＸＸＸＩＩＩ）中のＲ¹は水素原子、水酸基、炭素数１〜８のアルキル基、炭素数１〜６のアルコキシ基から選ばれ、全てが同一でも異なっていてもよい。Ｒ²、Ｒ³は水素原子、炭素数１〜６のアルキル基から選ばれ、全てが同一でも異なっていてもよい。ｎは１〜２０の整数を示し、ｍは１〜３の整数を示す。）

(R ¹ in the general formula (XXXIII) is selected from a hydrogen atom, a hydroxyl group, an alkyl group having 1 to 8 carbon atoms, and an alkoxy group having 1 to 6 carbon atoms, all of which may be the same or different. R ² , R ³ is selected from a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, all of which may be the same or different, n represents an integer of 1 to 20, and m represents an integer of 1 to 3.

一般式（ＸＸＸＩＩＩ）中のｍは１〜２であることが難燃性、硬化性の観点から好ましい。   M in the general formula (XXXIII) is preferably 1 or 2 from the viewpoint of flame retardancy and curability.

一般式（ＸＸＸＩＩＩ）で示される化合物はインドール類と架橋剤を酸触媒下で反応させた後、エピハロヒドリン化合物と反応させることにより得られる。インドール類の置換基Ｒ¹としては水素原子、水酸基、メトキシ基、エトキシ基、ビニルエーテル基、イソプロポキシ基、アリルオキシ基、プロパルギルエーテル基、ブトキシ基、フェノキシ基、メチル基、エチル基、ビニル基、エチン基、ｎ−プロピル基、イソプロピル基、アリル基、プロパルギル基、ブチル基、ｎ−アミル基、ｓｅｃ−アミル基、ｔｅｒｔ−アミル基、シクロヘキシル基、フェニル基、ベンジル基等が挙げられる。好ましくは水素原子、炭素数１〜３のアルキル基であり、より好ましくは水素原子である。架橋剤と反応させて得られる下記一般式（ａ）の架橋基としてはｐ−キシリレン基、ｍ−キシリレン基、１，４−ビスエチリデンフェニル基、１，３−ビスエチリデンフェニレン基、１，４−ビスイソプロピリデンフェニレン基、１，３−イソプロピリデンフェニレン基、４，４’−ビスメチレンビフェニル基、３，４’−ビスメチレンビフェニル基、３，３’−ビスメチレンビフェニル基、４，４’−ビスエチリデンビフェニル基、３，４’−ビスエチリデンビフェニル基、３，３’−ビスエチリデンビフェニル基、４，４’−ビスイソプロピリデンビフェニル基、３，４’−ビスイソプロピリデンビフェニル基、３，３’−ビスイソプロピリデンビフェニル基が挙げられる。また架橋剤としてホルムアルデヒド、アセトアルデヒド、プロピルアルデヒド、ブチルアルデヒド、アミルアルデヒド、ベンズアルデヒド、アセトン等のアルデヒド類、ケトン類を併用してもよい。ｎは１〜２０の整数を示すが、好ましくは１〜５である。酸触媒としては塩酸、硫酸、燐酸、蟻酸、シュウ酸、トリフルオロ酢酸、ｐ-トルエンスルホン酸、ジメチル硫酸、ジエチル硫酸、塩化亜鉛、塩化アルミニウム、塩化鉄、三フッ化ホウ素酸、イオン交換樹脂、活性白土、シリカアルミナ、ゼオライト等が挙げられる。 The compound represented by the general formula (XXXIII) is obtained by reacting an indole with a crosslinking agent in the presence of an acid catalyst and then reacting with an epihalohydrin compound. The indole substituent R ¹ includes a hydrogen atom, hydroxyl group, methoxy group, ethoxy group, vinyl ether group, isopropoxy group, allyloxy group, propargyl ether group, butoxy group, phenoxy group, methyl group, ethyl group, vinyl group, ethyne. Group, n-propyl group, isopropyl group, allyl group, propargyl group, butyl group, n-amyl group, sec-amyl group, tert-amyl group, cyclohexyl group, phenyl group, benzyl group and the like. Preferably they are a hydrogen atom and a C1-C3 alkyl group, More preferably, it is a hydrogen atom. As a crosslinking group of the following general formula (a) obtained by reacting with a crosslinking agent, p-xylylene group, m-xylylene group, 1,4-bisethylidenephenyl group, 1,3-bisethylidenephenylene group, 1,4 -Bisisopropylidenephenylene group, 1,3-isopropylidenephenylene group, 4,4'-bismethylenebiphenyl group, 3,4'-bismethylenebiphenyl group, 3,3'-bismethylenebiphenyl group, 4,4 ' -Bisethylidenebiphenyl group, 3,4'-bisethylidenebiphenyl group, 3,3'-bisethylidenebiphenyl group, 4,4'-bisisopropylidenebiphenyl group, 3,4'-bisisopropylidenebiphenyl group, 3, A 3′-bisisopropylidenebiphenyl group may be mentioned. Moreover, you may use together aldehydes and ketones, such as formaldehyde, acetaldehyde, propyl aldehyde, butyraldehyde, amyl aldehyde, benzaldehyde, acetone, as a crosslinking agent. n represents an integer of 1 to 20, preferably 1 to 5. Acid catalysts include hydrochloric acid, sulfuric acid, phosphoric acid, formic acid, oxalic acid, trifluoroacetic acid, p-toluenesulfonic acid, dimethyl sulfate, diethyl sulfate, zinc chloride, aluminum chloride, iron chloride, boron trifluoride, ion exchange resin, Examples include activated clay, silica alumina, and zeolite.

（一般式（ａ）中のＲ²、Ｒ³は水素原子、炭素数１〜６のアルキル基から選ばれ、全てが同一でも異なっていてもよい。ｍは１〜３の整数を示す。）
一般式（ＸＸＸＩＩＩ）で示される化合物としてはＥＮＰ−８０（東都化成株式会社製）等が入手可能である。

(R ² and R ³ in the general formula (a) are selected from a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, all of which may be the same or different. M represents an integer of 1 to 3)
As the compound represented by the general formula (XXXIII), ENP-80 (manufactured by Toto Kasei Co., Ltd.) and the like are available.

一般式（ＸＸＸＩＩＩ）で示される化合物の軟化点は４０〜２００℃、好ましくは５０〜１６０℃、さらに好ましくは６０〜１２０℃である。４０℃未満の場合、硬化性が低下し、２００℃を超える場合は流動性が低下する傾向にある。ここで軟化点とはＪＩＳ−Ｋ−６９１１の環球法に基づき測定される軟化点を示す。   The softening point of the compound represented by the general formula (XXXIII) is 40 to 200 ° C, preferably 50 to 160 ° C, and more preferably 60 to 120 ° C. When the temperature is lower than 40 ° C, the curability is lowered, and when it exceeds 200 ° C, the fluidity tends to be lowered. Here, the softening point indicates a softening point measured based on the ring and ball method of JIS-K-6911.

上記エポキシ樹脂を各々の観点で性能を発揮するためには、その配合量は、エポキシ樹脂全量に対して３０質量％以上とすることが好ましく、５０質量％以上がより好ましく、６０質量％以上とすることがさらに好ましい。   In order to exhibit the performance of the epoxy resin from each viewpoint, the blending amount is preferably 30% by mass or more, more preferably 50% by mass or more, and more preferably 60% by mass or more with respect to the total amount of the epoxy resin. More preferably.

本発明において用いられる（Ｂ）硬化剤は（Ｃ）下記一般式（Ｉ）で示される化合物を含むことを特徴とする。   The (B) curing agent used in the present invention is characterized by containing (C) a compound represented by the following general formula (I).

（一般式（Ｉ）中のＲ¹は水素原子、水酸基、炭素数１〜８のアルキル基、炭素数１〜６のアルコキシ基から選ばれ、全てが同一でも異なっていてもよい。Ｒ²、Ｒ³は水素原子、炭素数１〜６のアルキル基から選ばれ、全てが同一でも異なっていてもよい。ｎは１〜２０の整数を示し、ｍは１〜３の整数を示す。）
（Ｃ）一般式（Ｉ）中のｍは１〜２であることが難燃性、硬化性の観点から好ましい。

(R ¹ in the general formula (I) is selected from a hydrogen atom, a hydroxyl group, an alkyl group having 1 to 8 carbon atoms, and an alkoxy group having 1 to 6 carbon atoms, all of which may be the same or different. R ² , R ³ is selected from a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, all of which may be the same or different, n represents an integer of 1 to 20, and m represents an integer of 1 to 3.
(C) m in the general formula (I) is preferably 1 or 2 from the viewpoint of flame retardancy and curability.

（Ｃ）一般式（Ｉ）で示される化合物はインドール類と架橋剤を酸触媒下で反応させることにより得られる。インドール類の置換基Ｒ¹としては水素原子、水酸基、メトキシ基、エトキシ基、ビニルエーテル基、イソプロポキシ基、アリルオキシ基、プロパルギルエーテル基、ブトキシ基、フェノキシ基、メチル基、エチル基、ビニル基、エチン基、ｎ−プロピル基、イソプロピル基、アリル基、プロパルギル基、ブチル基、ｎ−アミル基、ｓｅｃ−アミル基、ｔｅｒｔ−アミル基、シクロヘキシル基、フェニル基、ベンジル基等が挙げられる。好ましくは水素原子、炭素数１〜３のアルキル基であり、より好ましくは水素原子である。架橋剤と反応させて得られる下記一般式（ａ）の架橋基としてはｐ−キシリレン基、ｍ−キシリレン基、１，４−ビスエチリデンフェニル基、１，３−ビスエチリデンフェニレン基、１，４−ビスイソプロピリデンフェニレン基、１，３−イソプロピリデンフェニレン基、４，４’−ビスメチレンビフェニル基、３，４’−ビスメチレンビフェニル基、３，３’−ビスメチレンビフェニル基、４，４’−ビスエチリデンビフェニル基、３，４’−ビスエチリデンビフェニル基、３，３’−ビスエチリデンビフェニル基、４，４’−ビスイソプロピリデンビフェニル基、３，４’−ビスイソプロピリデンビフェニル基、３，３’−ビスイソプロピリデンビフェニル基が挙げられる。また架橋剤としてホルムアルデヒド、アセトアルデヒド、プロピルアルデヒド、ブチルアルデヒド、アミルアルデヒド、ベンズアルデヒド、アセトン等のアルデヒド類、ケトン類を併用してもよい。ｎは１〜２０の整数を示すが、好ましくは１〜５である。酸触媒としては塩酸、硫酸、燐酸、蟻酸、シュウ酸、トリフルオロ酢酸、ｐ-トルエンスルホン酸、ジメチル硫酸、ジエチル硫酸、塩化亜鉛、塩化アルミニウム、塩化鉄、三フッ化ホウ素酸、イオン交換樹脂、活性白土、シリカアルミナ、ゼオライト等が挙げられる。 (C) The compound represented by the general formula (I) can be obtained by reacting an indole with a crosslinking agent in the presence of an acid catalyst. The indole substituent R ¹ includes a hydrogen atom, hydroxyl group, methoxy group, ethoxy group, vinyl ether group, isopropoxy group, allyloxy group, propargyl ether group, butoxy group, phenoxy group, methyl group, ethyl group, vinyl group, ethyne. Group, n-propyl group, isopropyl group, allyl group, propargyl group, butyl group, n-amyl group, sec-amyl group, tert-amyl group, cyclohexyl group, phenyl group, benzyl group and the like. Preferably they are a hydrogen atom and a C1-C3 alkyl group, More preferably, it is a hydrogen atom. As a crosslinking group of the following general formula (a) obtained by reacting with a crosslinking agent, p-xylylene group, m-xylylene group, 1,4-bisethylidenephenyl group, 1,3-bisethylidenephenylene group, 1,4 -Bisisopropylidenephenylene group, 1,3-isopropylidenephenylene group, 4,4'-bismethylenebiphenyl group, 3,4'-bismethylenebiphenyl group, 3,3'-bismethylenebiphenyl group, 4,4 ' -Bisethylidenebiphenyl group, 3,4'-bisethylidenebiphenyl group, 3,3'-bisethylidenebiphenyl group, 4,4'-bisisopropylidenebiphenyl group, 3,4'-bisisopropylidenebiphenyl group, 3, A 3′-bisisopropylidenebiphenyl group may be mentioned. Moreover, you may use together aldehydes and ketones, such as formaldehyde, acetaldehyde, propyl aldehyde, butyraldehyde, amyl aldehyde, benzaldehyde, acetone, as a crosslinking agent. n represents an integer of 1 to 20, preferably 1 to 5. Acid catalysts include hydrochloric acid, sulfuric acid, phosphoric acid, formic acid, oxalic acid, trifluoroacetic acid, p-toluenesulfonic acid, dimethyl sulfate, diethyl sulfate, zinc chloride, aluminum chloride, iron chloride, boron trifluoride, ion exchange resin, Examples include activated clay, silica alumina, and zeolite.

（一般式（ａ）中のＲ²、Ｒ³は水素原子、炭素数１〜６のアルキル基から選ばれ、全てが同一でも異なっていてもよい。ｍは１〜３の整数を示す。）

(R ² and R ³ in the general formula (a) are selected from a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, all of which may be the same or different. M represents an integer of 1 to 3)

（Ｃ）下記一般式（Ｉ）で示される化合物としてはＮＰ−８０（東都化成株式会社製）等が入手可能である。   (C) As a compound represented by the following general formula (I), NP-80 (manufactured by Toto Kasei Co., Ltd.) and the like are available.

（Ｃ）一般式（Ｉ）で示される化合物の軟化点は４０〜２００℃、好ましくは５０〜１６０℃、さらに好ましくは６０〜１２０℃である。４０℃未満の場合、硬化性が低下し、２００℃を超える場合は流動性が低下する傾向にある。ここで軟化点とはＪＩＳ−Ｋ−６９１１の環球法に基づき測定される軟化点を示す。   (C) The softening point of the compound represented by the general formula (I) is 40 to 200 ° C, preferably 50 to 160 ° C, more preferably 60 to 120 ° C. When the temperature is lower than 40 ° C, the curability is lowered, and when it exceeds 200 ° C, the fluidity tends to be lowered. Here, the softening point indicates a softening point measured based on the ring and ball method of JIS-K-6911.

（Ｃ）一般式（Ｉ）で示される化合物の配合量は、（Ｂ）硬化剤全量に対して４０〜１００質量％が好ましく、６０〜１００質量％がさらに好ましい。４０質量％未満であると難燃性が低下する傾向にある。 (C) 40-100 mass% is preferable with respect to (B) hardening | curing agent whole quantity, and, as for the compounding quantity of the compound shown by general formula (I), 60-100 mass% is more preferable. If it is less than 40% by mass, the flame retardancy tends to decrease.

本発明には従来公知の硬化剤を併用することができる。併用可能な硬化剤としては、封止用エポキシ樹脂組成物に一般に使用されているもので特に制限はないが、たとえば、フェノール、クレゾール、レゾルシン、カテコール、ビスフェノールＡ、ビスフェノールＦ、フェニルフェノール、アミノフェノール等のフェノール類及び／又はα−ナフトール、β−ナフトール、ジヒドロキシナフタレン等のナフトール類とホルムアルデヒド、ベンズアルデヒド、サリチルアルデヒド等のアルデヒド基を有する化合物とを酸性触媒下で縮合又は共縮合させて得られるノボラック型フェノール樹脂、フェノール類及び／又はナフトール類とジメトキシパラキシレン又はビス（メトキシメチル）ビフェニルから合成されるフェノール・アラルキル樹脂、ビフェニレン型フェノール・アラルキル樹脂、ナフトール・アラルキル樹脂等のアラルキル型フェノール樹脂、フェノール類及び／又はナフトール類とジシクロペンタジエンから共重合により合成される、ジシクロペンタジエン型フェノールノボラック樹脂、ジシクロペンタジエン型ナフトールノボラック樹脂等のジシクロペンタジエン型フェノール樹脂、トリフェニルメタン型フェノール樹脂、テルペン変性フェノール樹脂、パラキシリレン及び／又はメタキシリレン変性フェノール樹脂、メラミン変性フェノール樹脂、シクロペンタジエン変性フェノール樹脂、これら２種以上を共重合して得たフェノール樹脂などが挙げられる。これらを単独で用いても２種以上を組み合わせて用いてもよい。 A conventionally well-known hardening | curing agent can be used together in this invention. Curing agents that can be used in combination are generally used in sealing epoxy resin compositions and are not particularly limited. For example, phenol, cresol, resorcin, catechol, bisphenol A, bisphenol F, phenylphenol, aminophenol Novolaks obtained by condensation or cocondensation of phenols such as naphthols such as α-naphthol, β-naphthol, and dihydroxynaphthalene with compounds having an aldehyde group such as formaldehyde, benzaldehyde, salicylaldehyde, etc. in the presence of an acidic catalyst Type phenolic resin, phenol / aralkyl resin, biphenylene type phenol / aralkyl resin, naphthol synthesized from phenol and / or naphthol and dimethoxyparaxylene or bis (methoxymethyl) biphenyl・ Dicyclopentadiene type such as dicyclopentadiene type phenol novolac resin, dicyclopentadiene type naphthol novolac resin, synthesized by copolymerization from aralkyl type phenol resin such as aralkyl resin, phenols and / or naphthols and dicyclopentadiene Phenol resin, triphenylmethane type phenol resin, terpene modified phenol resin, paraxylylene and / or metaxylylene modified phenol resin, melamine modified phenol resin, cyclopentadiene modified phenol resin, phenol resin obtained by copolymerizing these two or more, etc. Can be mentioned. These may be used alone or in combination of two or more.

なかでも、難燃性、成形性の観点からは下記一般式（ＸＸＸＩＶ）で示されるフェノール・アラルキル樹脂が好ましい   Among these, from the viewpoint of flame retardancy and moldability, a phenol / aralkyl resin represented by the following general formula (XXXIV) is preferable.

（ここで、Ｒは水素原子及び炭素数１〜１０の置換又は非置換の一価の炭化水素基から選ばれ、ｎは０〜１０の整数を示す。）

(Here, R is selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, and n represents an integer of 0 to 10.)

一般式（ＸＸＸＩＶ）中のＲが水素原子で、ｎの平均値が０〜８であるフェノール・アラルキル樹脂がより好ましい。具体例としては、ｐ−キシリレン型フェノール・アラルキル樹脂、ｍ−キシリレン型フェノール・アラルキル樹脂等が挙げられる。このような化合物としてはＸＬＣ（三井化学株式会社製商品名）等が市販品として入手可能である。これらのアラルキル型フェノール樹脂を用いる場合、その配合量は、その性能を発揮するために硬化剤全量に対して３０質量％以上とすることが好ましく、５０質量％以上がより好ましい。   A phenol / aralkyl resin in which R in the general formula (XXXIV) is a hydrogen atom and the average value of n is 0 to 8 is more preferable. Specific examples include p-xylylene type phenol / aralkyl resins, m-xylylene type phenol / aralkyl resins, and the like. As such a compound, XLC (trade name, manufactured by Mitsui Chemicals, Inc.) is available as a commercial product. When using these aralkyl type phenol resins, the blending amount is preferably 30% by mass or more, more preferably 50% by mass or more, based on the total amount of the curing agent in order to exhibit the performance.

ナフトール・アラルキル樹脂としては、たとえば下記一般式（ＸＸＸＶ）で示されるフェノール樹脂等が挙げられる。   Examples of the naphthol / aralkyl resin include a phenol resin represented by the following general formula (XXXV).

上記一般式（ＸＸＸＶ）で示されるナフトール・アラルキル樹脂としては、たとえばＲ^１、Ｒ^２が全て水素原子である化合物等が挙げられ、このような化合物としては、ＳＮ−１７０（新日鐵化学株式会社製商品名）が市販品として入手可能である。 Examples of the naphthol-aralkyl resin represented by the general formula (XXXV) include compounds in which R ¹ and R ² are all hydrogen atoms, and examples of such compounds include SN-170 (Nippon Steel Chemical Co., Ltd.). Company name) is available as a commercial product.

ジシクロペンタジエン型フェノール樹脂としては、たとえば下記一般式（ＸＸＸＶＩ）で示されるフェノール樹脂等が挙げられる。   Examples of the dicyclopentadiene type phenol resin include a phenol resin represented by the following general formula (XXXVI).

（ここで、Ｒ^１及びＲ^２は水素原子及び炭素数１〜１０の置換又は非置換の一価の炭化水素基からそれぞれ独立して選ばれ、ｎは０〜１０の整数を示し、ｍは０〜６の整数を示す。）

Wherein R ¹ and R ² are each independently selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, n is an integer of 0 to 10, and m is Represents an integer of 0 to 6.)

Ｒ^１及びＲ^２が水素原子である上記化合物としてはＤＰＰ（新日本石油化学株式会社製商品名）等が市販品として入手可能である。 As said compound whose R < ¹ > and R < ² > is a hydrogen atom, DPP (New Nippon Petrochemical Co., Ltd. brand name) etc. are available as a commercial item.

トリフェニルメタン型フェノール樹脂としては、たとえば下記一般式（ＸＸＸＶＩＩ）で示されるフェノール樹脂等が挙げられる。   Examples of the triphenylmethane type phenol resin include a phenol resin represented by the following general formula (XXXVII).

（ここで、Ｒは水素原子及び炭素数１〜１０の置換又は非置換の一価の炭化水素基から選ばれ、ｎは１〜１０の整数を示す。）

(Here, R is selected from a hydrogen atom and a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, and n represents an integer of 1 to 10.)

Ｒが水素原子である上記化合物としては、ＭＥＨ−７５００（明和化成株式会社製商品名）等が市販品として入手可能である。   As the above compound in which R is a hydrogen atom, MEH-7500 (trade name, manufactured by Meiwa Kasei Co., Ltd.) and the like are commercially available.

ノボラック型フェノール樹脂としては、たとえばフェノールノボラック樹脂、クレゾールノボラック樹脂、ナフトールノボラック樹脂等が挙げられ、なかでもフェノールノボラック樹脂が好ましい。   Examples of the novolak type phenol resin include a phenol novolak resin, a cresol novolak resin, a naphthol novolak resin, and the like. Among these, a phenol novolak resin is preferable.

ビフェニレン型フェノール・アラルキル樹脂としては、たとえば下記一般式（ＸＸＸＶＩＩＩ）で示されるフェノール樹脂等が挙げられる。   Examples of the biphenylene type phenol-aralkyl resin include a phenol resin represented by the following general formula (XXXVIII).

上記式（ＸＸＸＶＩＩＩ）中のＲ^１〜Ｒ^９は全てが同一でも異なっていてもよく、水素原子、メチル基、エチル基、プロピル基、ブチル基、イソプロピル基、イソブチル基等の炭素数１〜１０のアルキル基、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基等の炭素数１〜１０のアルコキシル基、フェニル基、トリル基、キシリル基等の炭素数６〜１０のアリール基、及び、ベンジル基、フェネチル基等の炭素数６〜１０のアラルキル基から選ばれ、なかでも水素原子とメチル基が好ましい。ｎは０〜１０の整数を示す。 R ^{1 to} R ⁹ in the above formula (XXXVIII) may all be the same or different and have 1 to 10 carbon atoms such as a hydrogen atom, a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, and an isobutyl group. An alkyl group, a methoxy group, an ethoxy group, a propoxy group, a butoxy group or the like, an alkoxyl group having 1 to 10 carbon atoms, a phenyl group, a tolyl group, an aryl group having 6 to 10 carbon atoms such as a xylyl group, and a benzyl group, It is selected from aralkyl groups having 6 to 10 carbon atoms such as phenethyl group, and among them, a hydrogen atom and a methyl group are preferable. n represents an integer of 0 to 10.

上記一般式（ＸＸＸＶＩＩＩ）で示されるビフェニレン型フェノール・アラルキル樹脂としては、たとえばＲ^１〜Ｒ^９が全て水素原子である化合物等が挙げられ、なかでも溶融粘度の観点から、ｎが１以上の縮合体を５０重量％以上含む縮合体の混合物が好ましい。このような化合物としては、ＭＥＨ−７８５１（明和化成株式会社製商品名）が市販品として入手可能である。 Examples of the biphenylene type phenol / aralkyl resin represented by the general formula (XXXVIII) include compounds in which R ^{1 to} R ⁹ are all hydrogen atoms, and in particular, from the viewpoint of melt viscosity, n is a condensation of 1 or more. A mixture of condensates containing 50% by weight or more of the body is preferred. As such a compound, MEH-7851 (trade name, manufactured by Meiwa Kasei Co., Ltd.) is commercially available.

上記のアラルキル型フェノール樹脂、ナフトール・アラルキル樹脂、ジシクロペンタジエン型フェノール樹脂、トリフェニルメタン型フェノール樹脂、ノボラック型フェノール樹脂、ビフェニレン型フェノール・アラルキル樹脂は、いずれか１種を単独で用いても２種以上を組合わせて用いてもよい。   The above aralkyl-type phenol resin, naphthol-aralkyl resin, dicyclopentadiene-type phenol resin, triphenylmethane-type phenol resin, novolac-type phenol resin, biphenylene-type phenol-aralkyl resin can be used alone or in combination. You may use combining a seed | species or more.

併用する上記エポキシ樹脂の中では特にノボラック型エフェノール樹脂が硬化性の観点から好ましく、アラルキル型フェノール樹脂が流動性、耐リフロー性の観点から好ましい   Among the epoxy resins used in combination, the novolak type phenolic resin is preferable from the viewpoint of curability, and the aralkyl type phenolic resin is preferable from the viewpoint of fluidity and reflow resistance.

本発明の封止用エポキシ樹脂組成物には難燃性を向上させる観点から、アセナフチレンを含有してもよい。アセナフチレンはアセナフテンを脱水素して得ることができるが、市販品を用いてもよい。また、アセナフチレンの重合物又はアセナフチレンと他の芳香族オレフィンとの重合物として用いることもできる。アセナフチレンの重合物又はアセナフチレンと他の芳香族オレフィンとの重合物を得る方法としては、ラジカル重合、カチオン重合、アニオン重合等が挙げられる。また、重合に際しては従来公知の触媒を用いることができるが、触媒を用いずに熱だけで行うこともできる。この際、重合温度は８０〜１６０℃が好ましく、９０〜１５０℃がより好ましい。得られるアセナフチレンの重合物又はアセナフチレンと他の芳香族オレフィンとの重合物の軟化点は、６０〜１５０℃が好ましく、７０〜１３０℃がより好ましい。６０℃より低いと成形時の染み出しにより成形性が低下する傾向にあり、１５０℃より高いと樹脂との相溶性が低下する傾向にある。   From the viewpoint of improving flame retardancy, the sealing epoxy resin composition of the present invention may contain acenaphthylene. Although acenaphthylene can be obtained by dehydrogenating acenaphthene, a commercially available product may be used. Further, it can be used as a polymer of acenaphthylene or a polymer of acenaphthylene and other aromatic olefins. Examples of a method for obtaining a polymer of acenaphthylene or a polymer of acenaphthylene and another aromatic olefin include radical polymerization, cationic polymerization, and anionic polymerization. In the polymerization, a conventionally known catalyst can be used, but it can also be carried out only by heat without using a catalyst. At this time, the polymerization temperature is preferably 80 to 160 ° C, more preferably 90 to 150 ° C. 60-150 degreeC is preferable and, as for the softening point of the polymer of the polymer of acenaphthylene obtained or acenaphthylene and another aromatic olefin, 70-130 degreeC is more preferable. When the temperature is lower than 60 ° C., the moldability tends to decrease due to oozing during molding, and when the temperature is higher than 150 ° C., the compatibility with the resin tends to decrease.

アセナフチレンと共重合させる他の芳香族オレフィンとしては、スチレン、α−メチルスチレン、インデン、ベンゾチオフェン、ベンゾフラン、ビニルナフタレン、ビニルビフェニル又はそれらのアルキル置換体等が挙げられる。また、上記した芳香族オレフィン以外に本発明の効果に支障の無い範囲で脂肪族オレフィンを併用することもできる。脂肪族オレフィンとしては、（メタ）アクリル酸及びそれらのエステル、無水マレイン酸、無水イタコン酸、フマル酸及びそれらのエステル等が挙げられる。これら脂肪族オレフィンの使用量は重合モノマー全量に対して２０重量％以下が好ましく、９重量％以下がより好ましい。   Examples of other aromatic olefins to be copolymerized with acenaphthylene include styrene, α-methylstyrene, indene, benzothiophene, benzofuran, vinylnaphthalene, vinylbiphenyl, and alkyl-substituted products thereof. In addition to the above-mentioned aromatic olefins, aliphatic olefins can be used in combination as long as the effects of the present invention are not hindered. Examples of the aliphatic olefin include (meth) acrylic acid and esters thereof, maleic anhydride, itaconic anhydride, fumaric acid and esters thereof. The amount of these aliphatic olefins used is preferably 20% by weight or less, more preferably 9% by weight or less, based on the total amount of the polymerization monomers.

さらに、アセナフチレンとして、（Ｂ）硬化剤の一部又は全部と予備混合されたアセナフチレンを含有することもできる。（Ｂ）硬化剤の一部又は全部と、アセナフチレン、アセナフチレンの重合物及びアセナフチレンと他の芳香族オレフィンとの重合物の１種以上とを予備混合したものを用いてもよい。予備混合の方法としては、（Ｂ）及びアセナフチレン成分をそれぞれ微細に粉砕し固体状態のままミキサー等で混合する方法、両成分を溶解する溶媒に均一に溶解させた後溶媒を除去する方法、（Ｂ）及び／又はアセナフチレン成分の軟化点以上の温度で両者を溶融混合する方法等で行うことができるが、均一な混合物が得られて不純物の混入が少ない溶融混合法が好ましい。溶融混合は、（Ｂ）及び／又はアセナフチレン成分の軟化点以上の温度であれば制限はないが、１００〜２５０℃が好ましく、１２０〜２００℃がより好ましい。また、溶融混合は両者が均一に混合すれば混合時間に制限はないが、１〜２０時間が好ましく、２〜１５時間がより好ましい。   Furthermore, as acenaphthylene, the acenaphthylene premixed with a part or all of (B) hardening | curing agent can also be contained. (B) A premixed mixture of a part or all of the curing agent and one or more of acenaphthylene, a polymer of acenaphthylene, and a polymer of acenaphthylene and another aromatic olefin may be used. As a premixing method, (B) and the acenaphthylene component are each finely pulverized and mixed with a mixer or the like in a solid state, a method in which both components are uniformly dissolved in a solvent that dissolves both components, and then the solvent is removed. B) and / or a method in which both are melt mixed at a temperature equal to or higher than the softening point of the acenaphthylene component, etc., but a melt mixing method in which a uniform mixture is obtained and impurities are less mixed is preferable. The melt mixing is not limited as long as the temperature is equal to or higher than the softening point of (B) and / or the acenaphthylene component, but is preferably 100 to 250 ° C, more preferably 120 to 200 ° C. Moreover, although melt mixing will not have a restriction | limiting in mixing time if both are mixed uniformly, 1 to 20 hours are preferable and 2 to 15 hours are more preferable.

（Ｂ）硬化剤とアセナフチレンを予備混合する場合、混合中にアセナフチレン成分が重合もしくは（Ｂ）硬化剤と反応しても構わない。本発明の封止用エポキシ樹脂組成物中には、アセナフチレン成分の分散性に起因する難燃性向上の観点から前述の予備混合物（アセナフチレン変性硬化剤）が（Ｂ）硬化剤中に９０重量％以上含まれることが好ましい。
アセナフチレン変性硬化剤中に含まれるアセナフチレン及び／又はアセナフチレンを含む芳香族オレフィンの重合物の量は５〜４０重量％が好ましく、８〜２５重量％がより好ましい。５重量％より少ないと難燃性が低下する傾向があり、４０重量％より多いと成形性が低下する傾向がある。本発明のエポキシ樹脂組成物中に含まれるアセナフチレン構造の含有率は、難燃性と成形性の観点からは０．１〜５重量％が好ましく、０．３〜３重量％がより好ましい。０．１重量％より少ないと難燃性に劣る傾向にあり、５重量％より多いと成形性が低下する傾向にある。 When the (B) curing agent and acenaphthylene are premixed, the acenaphthylene component may be polymerized or reacted with the (B) curing agent during mixing. In the epoxy resin composition for sealing of the present invention, from the viewpoint of improving flame retardancy due to dispersibility of the acenaphthylene component, the above-mentioned premix (acenaphthylene-modified curing agent) is 90% by weight in the (B) curing agent. It is preferable to be contained above.
The amount of acenaphthylene and / or aromatic olefin polymer containing acenaphthylene contained in the acenaphthylene-modified curing agent is preferably 5 to 40% by weight, and more preferably 8 to 25% by weight. If the amount is less than 5% by weight, the flame retardancy tends to decrease, and if it exceeds 40% by weight, the moldability tends to decrease. The content of the acenaphthylene structure contained in the epoxy resin composition of the present invention is preferably 0.1 to 5% by weight and more preferably 0.3 to 3% by weight from the viewpoints of flame retardancy and moldability. If it is less than 0.1% by weight, it tends to be inferior in flame retardancy, and if it is more than 5% by weight, moldability tends to be lowered.

（Ａ）エポキシ樹脂と（Ｂ）硬化剤との当量比、すなわち、エポキシ樹脂中のエポキシ基数に対する硬化剤中の水酸基数の比（硬化剤中の水酸基数／エポキシ樹脂中のエポキシ基数）は、特に制限はないが、それぞれの未反応分を少なく抑えるために０．５〜２の範囲に設定されることが好ましく、０．６〜１．３がより好ましい。成形性及び耐リフロー性に優れる封止用エポキシ樹脂組成物を得るためには０．８〜１．２の範囲に設定されることがさらに好ましい。   The equivalent ratio of (A) epoxy resin and (B) curing agent, that is, the ratio of the number of hydroxyl groups in the curing agent to the number of epoxy groups in the epoxy resin (number of hydroxyl groups in the curing agent / number of epoxy groups in the epoxy resin) is: Although there is no restriction | limiting in particular, In order to suppress each unreacted part small, it is preferable to set to the range of 0.5-2, and 0.6-1.3 are more preferable. In order to obtain a sealing epoxy resin composition excellent in moldability and reflow resistance, it is more preferably set in the range of 0.8 to 1.2.

本発明の封止用エポキシ樹脂組成物には、（Ａ）エポキシ樹脂と（Ｂ）硬化剤の反応を促進させるために必要に応じて（Ｄ）硬化促進剤を用いることができる。（Ｄ）硬化促進剤は、封止用エポキシ樹脂組成物に一般に使用されているもので特に制限はないが、たとえば、１，８−ジアザ−ビシクロ（５，４，０）ウンデセン−７、１，５−ジアザ−ビシクロ（４，３，０）ノネン、５、６−ジブチルアミノ−１，８−ジアザ−ビシクロ（５，４，０）ウンデセン−７等のシクロアミジン化合物及びこれらの化合物に無水マレイン酸、１，４−ベンゾキノン、２，５−トルキノン、１，４−ナフトキノン、２，３−ジメチルベンゾキノン、２，６−ジメチルベンゾキノン、２，３−ジメトキシ−５−メチル−１，４−ベンゾキノン、２，３−ジメトキシ−１，４−ベンゾキノン、フェニル−１，４−ベンゾキノン等のキノン化合物、ジアゾフェニルメタン、フェノール樹脂等のπ結合をもつ化合物を付加してなる分子内分極を有する化合物、ベンジルジメチルアミン、トリエタノールアミン、ジメチルアミノエタノール、トリス（ジメチルアミノメチル）フェノール等の３級アミン類及びこれらの誘導体、２−メチルイミダゾール、２−フェニルイミダゾール、２−フェニル−４−メチルイミダゾール等のイミダゾール類及びこれらの誘導体、トリブチルホスフィン、メチルジフェニルホスフィン、トリフェニルホスフィン、トリス（４−メチルフェニル）ホスフィン、ジフェニルホスフィン、フェニルホスフィン等のホスフィン化合物及びこれらのホスフィン化合物に無水マレイン酸、上記キノン化合物、ジアゾフェニルメタン、フェノール樹脂等のπ結合をもつ化合物を付加してなる分子内分極を有するリン化合物、テトラフェニルホスホニウムテトラフェニルボレート、トリフェニルホスフィンテトラフェニルボレート、２−エチル−４−メチルイミダゾールテトラフェニルボレート、Ｎ−メチルモルホリンテトラフェニルボレート等のテトラフェニルボロン塩及びこれらの誘導体などが挙げられ、これらを単独で用いても２種以上を組み合わせて用いてもよい。   In the sealing epoxy resin composition of the present invention, a (D) curing accelerator can be used as necessary to promote the reaction between the (A) epoxy resin and the (B) curing agent. (D) Although a hardening accelerator is generally used for the epoxy resin composition for sealing and is not particularly limited, for example, 1,8-diaza-bicyclo (5,4,0) undecene-7, 1 , 5-diaza-bicyclo (4,3,0) nonene, cycloamidine compounds such as 5,6-dibutylamino-1,8-diaza-bicyclo (5,4,0) undecene-7 and these compounds Maleic acid, 1,4-benzoquinone, 2,5-toluquinone, 1,4-naphthoquinone, 2,3-dimethylbenzoquinone, 2,6-dimethylbenzoquinone, 2,3-dimethoxy-5-methyl-1,4-benzoquinone , Quinone compounds such as 2,3-dimethoxy-1,4-benzoquinone and phenyl-1,4-benzoquinone, and compounds having a π bond such as diazophenylmethane and phenol resin. A compound having intramolecular polarization, tertiary amines such as benzyldimethylamine, triethanolamine, dimethylaminoethanol, tris (dimethylaminomethyl) phenol, and derivatives thereof, 2-methylimidazole, 2-phenylimidazole, Imidazoles such as 2-phenyl-4-methylimidazole and derivatives thereof, phosphine compounds such as tributylphosphine, methyldiphenylphosphine, triphenylphosphine, tris (4-methylphenyl) phosphine, diphenylphosphine, and phenylphosphine, and these phosphines Phosphorus compound having intramolecular polarization, tetraphenylphosphoric acid, which is obtained by adding a compound having a π bond such as maleic anhydride, the above quinone compound, diazophenylmethane, or phenol resin to the compound. And tetraphenyl boron salts such as um tetraphenyl borate, triphenylphosphine tetraphenyl borate, 2-ethyl-4-methylimidazole tetraphenyl borate, N-methylmorpholine tetraphenyl borate, and derivatives thereof. You may use it, or may use it in combination of 2 or more types.

なかでも、難燃性、硬化性の観点からは、トリフェニルホスフィンが好ましく、難燃性、硬化性、流動性及び離型性の観点からは第三ホスフィン化合物とキノン化合物との付加物が好ましい。第三ホスフィン化合物としては、特に限定するものではないが、トリシクロヘキシルホスフィン、トリブチルホスフィン、ジブチルフェニルホスフィン、ブチルジフェニルホスフィン、エチルジフェニルホスフィン、トリフェニルホスフィン、トリス（４−メチルフェニル）ホスフィン、トリス（４−エチルフェニル）ホスフィン、トリス（４−プロピルフェニル）ホスフィン、トリス（４−ブチルフェニル）ホスフィン、トリス（イソプロピルフェニル）ホスフィン、トリス（ｔ−ブチルフェニル）ホスフィン、トリス（２，４−ジメチルフェニル）ホスフィン、トリス（２，６−ジメチルフェニル）ホスフィン、トリス（２，４，６−トリメチルフェニル）ホスフィン、トリス（２，６−ジメチル−４−エトキシフェニル）ホスフィン、トリス（４−メトキシフェニル）ホスフィン、トリス（４−エトキシフェニル）ホスフィンなどのアルキル基、アリール基を有する第三ホスフィン化合物が好ましい。またキノン化合物としてはｏ−ベンゾキノン、ｐ−ベンゾキノン、ジフェノキノン、１，４−ナフトキノン、アントラキノン等があげられ、なかでも耐湿性、保存安定性の観点からｐ−ベンゾキノンが好ましい。トリス（４−メチルフェニル）ホスフィンとｐ−ベンゾキノンとの付加物が離型性の観点からより好ましい。   Of these, triphenylphosphine is preferable from the viewpoint of flame retardancy and curability, and an adduct of a third phosphine compound and a quinone compound is preferable from the viewpoint of flame retardancy, curability, fluidity, and mold release. . Although it does not specifically limit as a tertiary phosphine compound, Tricyclohexyl phosphine, tributyl phosphine, dibutyl phenyl phosphine, butyl diphenyl phosphine, ethyl diphenyl phosphine, triphenyl phosphine, tris (4-methylphenyl) phosphine, tris (4 -Ethylphenyl) phosphine, tris (4-propylphenyl) phosphine, tris (4-butylphenyl) phosphine, tris (isopropylphenyl) phosphine, tris (t-butylphenyl) phosphine, tris (2,4-dimethylphenyl) phosphine , Tris (2,6-dimethylphenyl) phosphine, tris (2,4,6-trimethylphenyl) phosphine, tris (2,6-dimethyl-4-ethoxyphenyl) phosphine, Squirrel (4-methoxyphenyl) phosphine, alkyl groups such as tris (4-ethoxyphenyl) phosphine, tertiary phosphine compounds having an aryl group are preferable. Examples of the quinone compound include o-benzoquinone, p-benzoquinone, diphenoquinone, 1,4-naphthoquinone, anthraquinone and the like. Among these, p-benzoquinone is preferable from the viewpoint of moisture resistance and storage stability. An adduct of tris (4-methylphenyl) phosphine and p-benzoquinone is more preferable from the viewpoint of releasability.

（Ｄ）硬化促進剤の配合量は、硬化促進効果が達成される量であれば特に制限されるものではないが、封止用エポキシ樹脂組成物に対して０．００５〜２重量％が好ましく、０．０１〜０．５重量％がより好ましい。０．００５重量％未満では短時間での硬化性に劣る傾向があり、２重量％を超えると硬化速度が速すぎて良好な成形品を得ることが困難になる傾向がある。   (D) The blending amount of the curing accelerator is not particularly limited as long as the curing acceleration effect is achieved, but is preferably 0.005 to 2% by weight based on the epoxy resin composition for sealing. 0.01 to 0.5% by weight is more preferable. If it is less than 0.005% by weight, the curability in a short time tends to be inferior, and if it exceeds 2% by weight, the curing rate tends to be too high and it tends to be difficult to obtain a good molded product.

本発明では必要に応じて（Ｅ）無機充填剤を配合することができる。無機充填剤は、吸湿性、線膨張係数低減、熱伝導性向上及び強度向上の効果があり、たとえば、溶融シリカ、結晶シリカ、アルミナ、ジルコン、珪酸カルシウム、炭酸カルシウム、チタン酸カリウム、炭化珪素、窒化珪素、窒化アルミ、窒化ホウ素、ベリリア、ジルコニア、ジルコン、フォステライト、ステアタイト、スピネル、ムライト、チタニア等の粉体、又はこれらを球形化したビーズ、ガラス繊維等が挙げられる。さらに、難燃効果のある無機充填剤としては水酸化アルミニウム、水酸化マグネシウム、複合金属水酸化物、硼酸亜鉛、モリブデン酸亜鉛などが挙げられる。ここで、ホウ酸亜鉛としてはＦＢ−２９０、ＦＢ−５００（Ｕ．Ｓ．Ｂｏｒａｘ社製）、ＦＲＺ−５００Ｃ（水澤化学社製）等が、モリブデン酸亜鉛としてはＫＥＭＧＡＲＤ９１１Ｂ、９１１Ｃ、１１００（Ｓｈｅｒｗｉｎ−Ｗｉｌｌｉａｍｓ社製）等が各々市販品として入手可能である。   In this invention, (E) inorganic filler can be mix | blended as needed. The inorganic filler has the effects of hygroscopicity, linear expansion coefficient reduction, thermal conductivity improvement and strength improvement, for example, fused silica, crystalline silica, alumina, zircon, calcium silicate, calcium carbonate, potassium titanate, silicon carbide, Examples thereof include powders such as silicon nitride, aluminum nitride, boron nitride, beryllia, zirconia, zircon, fosterite, steatite, spinel, mullite, and titania, or beads and glass fibers obtained by spheroidizing these. Furthermore, examples of the inorganic filler having a flame retardant effect include aluminum hydroxide, magnesium hydroxide, composite metal hydroxide, zinc borate, and zinc molybdate. Here, as the zinc borate, FB-290, FB-500 (manufactured by US Borax), FRZ-500C (manufactured by Mizusawa Chemical Co., Ltd.) and the like, and as the zinc molybdate, KEGGARD 911B, 911C, 1100 (Sherwin- (Made by Williams) etc. are each available as a commercial item.

これらの無機充填剤は単独で用いても２種以上を組み合わせて用いてもよい。なかでも、充填性、線膨張係数の低減の観点からは溶融シリカが、高熱伝導性の観点からはアルミナが好ましく、無機充填剤の形状は充填性及び金型摩耗性の点から球形が好ましい。   These inorganic fillers may be used alone or in combination of two or more. Of these, fused silica is preferable from the viewpoint of filling property and linear expansion coefficient, and alumina is preferable from the viewpoint of high thermal conductivity, and the shape of the inorganic filler is preferably spherical from the viewpoint of filling property and mold wear.

無機充填剤の配合量は、難燃性、成形性、吸湿性、線膨張係数低減、強度向上及び耐リフロー性の観点から、封止用エポキシ樹脂組成物に対して５０質量％以上が好ましく、６０〜９５質量％が難燃性の観点からより好ましく、７０〜９０質量％がさらに好ましい。６０質量％未満では難燃性及び耐リフロー性が低下する傾向があり、９５質量％を超えると流動性が不足する傾向があり、また難燃性も低下する傾向にある。   The blending amount of the inorganic filler is preferably 50% by mass or more based on the epoxy resin composition for sealing, from the viewpoints of flame retardancy, moldability, hygroscopicity, linear expansion coefficient reduction, strength improvement and reflow resistance, 60-95 mass% is more preferable from a flame-retardant viewpoint, and 70-90 mass% is further more preferable. If the amount is less than 60% by mass, the flame retardancy and the reflow resistance tend to be lowered. If the amount exceeds 95% by mass, the fluidity tends to be insufficient, and the flame retardancy tends to be lowered.

（Ｅ）無機充填剤を用いる場合、本発明の封止用エポキシ樹脂組成物には、樹脂成分と充項剤との接着性を高めるために、（Ｆ）カップリング剤をさらに配合することが好ましい。（Ｆ）カップリング剤としては、封止用エポキシ樹脂組成物に一般に使用されているもので特に制限はないが、たとえば、１級及び／又は２級及び／又は３級アミノ基を有するシラン化合物、エポキシシラン、メルカプトシラン、アルキルシラン、ウレイドシラン、ビニルシラン等の各種シラン系化合物、チタン系化合物、アルミニウムキレート類、アルミニウム／ジルコニウム系化合物等が挙げられる。これらを例示すると、ビニルトリクロロシラン、ビニルトリエトキシシラン、ビニルトリス（β−メトキシエトキシ）シラン、γ−メタクリロキシプロピルトリメトキシシラン、β−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルメチルジメトキシシラン、ビニルトリアセトキシシラン、γ−メルカプトプロピルトリメトキシシラン、γ−アミノプロピルトリメトキシシラン、γ−アミノプロピルメチルジメトキシシラン、γ−アミノプロピルトリエトキシシラン、γ−アミノプロピルメチルジエトキシシラン、γ−アニリノプロピルトリメトキシシラン、γ−アニリノプロピルトリエトキシシラン、γ−（Ｎ，Ｎ−ジメチル）アミノプロピルトリメトキシシラン、γ−（Ｎ，Ｎ−ジエチル）アミノプロピルトリメトキシシラン、γ−（Ｎ，Ｎ−ジブチル）アミノプロピルトリメトキシシラン、γ−（Ｎ−メチル）アニリノプロピルトリメトキシシラン、γ−（Ｎ−エチル）アニリノプロピルトリメトキシシラン、γ−（Ｎ，Ｎ−ジメチル）アミノプロピルトリエトキシシラン、γ−（Ｎ，Ｎ−ジエチル）アミノプロピルトリエトキシシラン、γ−（Ｎ，Ｎ−ジブチル）アミノプロピルトリエトキシシラン、γ−（Ｎ−メチル）アニリノプロピルトリエトキシシラン、γ−（Ｎ−エチル）アニリノプロピルトリエトキシシラン、γ−（Ｎ，Ｎ−ジメチル）アミノプロピルメチルジメトキシシラン、γ−（Ｎ，Ｎ−ジエチル）アミノプロピルメチルジメトキシシラン、γ−（Ｎ，Ｎ−ジブチル）アミノプロピルメチルジメトキシシラン、γ−（Ｎ−メチル）アニリノプロピルメチルジメトキシシラン、γ−（Ｎ−エチル）アニリノプロピルメチルジメトキシシラン、Ｎ−（トリメトキシシリルプロピル）エチレンジアミン、Ｎ−（ジメトキシメチルシリルイソプロピル）エチレンジアミン、メチルトリメトキシシラン、ジメチルジメトキシシラン、メチルトリエトキシシラン、γ−クロロプロピルトリメトキシシラン、ヘキサメチルジシラン、ビニルトリメトキシシラン、γ−メルカプトプロピルメチルジメトキシシラン等のシラン系カップリング剤、イソプロピルトリイソステアロイルチタネート、イソプロピルトリス（ジオクチルパイロホスフェート）チタネート、イソプロピルトリ（Ｎ−アミノエチル−アミノエチル）チタネート、テトラオクチルビス（ジトリデシルホスファイト）チタネート、テトラ（２，２−ジアリルオキシメチル−１−ブチル）ビス（ジトリデシル）ホスファイトチタネート、ビス（ジオクチルパイロホスフェート）オキシアセテートチタネート、ビス（ジオクチルパイロホスフェート）エチレンチタネート、イソプロピルトリオクタノイルチタネート、イソプロピルジメタクリルイソステアロイルチタネート、イソプロピルトリドデシルベンゼンスルホニルチタネート、イソプロピルイソステアロイルジアクリルチタネート、イソプロピルトリ（ジオクチルホスフェート）チタネート、イソプロピルトリクミルフェニルチタネート、テトライソプロピルビス（ジオクチルホスファイト）チタネート等のチタネート系カップリング剤などが挙げられ、これらの１種を単独で用いても２種類以上を組み合わせて用いてもよい。   (E) When an inorganic filler is used, the sealing epoxy resin composition of the present invention may further contain (F) a coupling agent in order to enhance the adhesion between the resin component and the filler. preferable. (F) The coupling agent is generally used in an epoxy resin composition for sealing and is not particularly limited. For example, a silane compound having a primary and / or secondary and / or tertiary amino group And various silane compounds such as epoxy silane, mercapto silane, alkyl silane, ureido silane, and vinyl silane, titanium compounds, aluminum chelates, and aluminum / zirconium compounds. Examples of these are vinyltrichlorosilane, vinyltriethoxysilane, vinyltris (β-methoxyethoxy) silane, γ-methacryloxypropyltrimethoxysilane, β- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, γ-glycol. Sidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldimethoxysilane, vinyltriacetoxysilane, γ-mercaptopropyltrimethoxysilane, γ-aminopropyltrimethoxysilane, γ-aminopropylmethyldimethoxysilane, γ-aminopropyl Triethoxysilane, γ-aminopropylmethyldiethoxysilane, γ-anilinopropyltrimethoxysilane, γ-anilinopropyltriethoxysilane, γ- (N, N-dimethyl) aminopropyltrimethoxy Silane, γ- (N, N-diethyl) aminopropyltrimethoxysilane, γ- (N, N-dibutyl) aminopropyltrimethoxysilane, γ- (N-methyl) anilinopropyltrimethoxysilane, γ- (N -Ethyl) anilinopropyltrimethoxysilane, γ- (N, N-dimethyl) aminopropyltriethoxysilane, γ- (N, N-diethyl) aminopropyltriethoxysilane, γ- (N, N-dibutyl) amino Propyltriethoxysilane, γ- (N-methyl) anilinopropyltriethoxysilane, γ- (N-ethyl) anilinopropyltriethoxysilane, γ- (N, N-dimethyl) aminopropylmethyldimethoxysilane, γ- (N, N-diethyl) aminopropylmethyldimethoxysilane, γ- (N, N-dibutyl) aminopropy Rumethyldimethoxysilane, γ- (N-methyl) anilinopropylmethyldimethoxysilane, γ- (N-ethyl) anilinopropylmethyldimethoxysilane, N- (trimethoxysilylpropyl) ethylenediamine, N- (dimethoxymethylsilylisopropyl) ) Silane coupling agents such as ethylenediamine, methyltrimethoxysilane, dimethyldimethoxysilane, methyltriethoxysilane, γ-chloropropyltrimethoxysilane, hexamethyldisilane, vinyltrimethoxysilane, γ-mercaptopropylmethyldimethoxysilane, isopropyl Triisostearoyl titanate, isopropyl tris (dioctyl pyrophosphate) titanate, isopropyl tri (N-aminoethyl-aminoethyl) titanate, tetraoctane Rubis (ditridecyl phosphite) titanate, tetra (2,2-diallyloxymethyl-1-butyl) bis (ditridecyl) phosphite titanate, bis (dioctyl pyrophosphate) oxyacetate titanate, bis (dioctyl pyrophosphate) ethylene titanate, Isopropyltrioctanoyl titanate, isopropyldimethacrylisostearoyl titanate, isopropyltridodecylbenzenesulfonyl titanate, isopropylisostearoyl diacryl titanate, isopropyltri (dioctylphosphate) titanate, isopropyltricumylphenyl titanate, tetraisopropylbis (dioctylphosphite) titanate And titanate coupling agents such as A seed may be used independently or may be used in combination of 2 or more types.

なかでも流動性、難燃性の観点からは２級アミノ基を有するシランカップリング剤が好ましい。２級アミノ基を有するシランカップリング剤は分子内に２級アミノ基を有するシラン化合物であれば特に制限はないが、たとえば、γ−アニリノプロピルトリメトキシシラン、γ−アニリノプロピルトリエトキシシラン、γ−アニリノプロピルメチルジメトキシシラン、γ−アニリノプロピルメチルジエトキシシラン、γ−アニリノプロピルエチルジエトキシシラン、γ−アニリノプロピルエチルジメトキシシラン、γ−アニリノメチルトリメトキシシラン、γ−アニリノメチルトリエトキシシラン、γ−アニリノメチルメチルジメトキシシラン、γ−アニリノメチルメチルジエトキシシラン、γ−アニリノメチルエチルジエトキシシラン、γ−アニリノメチルエチルジメトキシシラン、Ｎ−（ｐ−メトキシフェニル）−γ−アミノプロピルトリメトキシシラン、Ｎ−（ｐ−メトキシフェニル）−γ−アミノプロピルトリエトキシシラン、Ｎ−（ｐ−メトキシフェニル）−γ−アミノプロピルメチルジメトキシシラン、Ｎ−（ｐ−メトキシフェニル）−γ−アミノプロピルメチルジエトキシシラン、Ｎ−（ｐ−メトキシフェニル）−γ−アミノプロピルエチルジエトキシシラン、Ｎ−（ｐ−メトキシフェニル）−γ−アミノプロピルエチルジメトキシシラン、γ−（Ｎ−メチル）アミノプロピルトリメトキシシラン、γ−（Ｎ−エチル）アミノプロピルトリメトキシシラン、γ−（Ｎ−ブチル）アミノプロピルトリメトキシシラン、γ−（Ｎ−ベンジル）アミノプロピルトリメトキシシラン、γ−（Ｎ−メチル）アミノプロピルトリエトキシシラン、γ−（Ｎ−エチル）アミノプロピルトリエトキシシラン、γ−（Ｎ−ブチル）アミノプロピルトリエトキシシラン、γ−（Ｎ−ベンジル）アミノプロピルトリエトキシシラン、γ−（Ｎ−メチル）アミノプロピルメチルジメトキシシラン、γ−（Ｎ−エチル）アミノプロピルメチルジメトキシシラン、γ−（Ｎ−ブチル）アミノプロピルメチルジメトキシシラン、γ−（Ｎ−ベンジル）アミノプロピルメチルジメトキシシラン、Ｎ−β−（アミノエチル）−γ−アミノプロピルトリメトキシシラン、γ−（β−アミノエチル）アミノプロピルトリメトキシシラン、Ｎ−β−（Ｎ−ビニルベンジルアミノエチル）−γ−アミノプロピルトリメトキシシラン等が挙げられる。なかでも下記一般式（ＩＩ）で示されるアミノシランカップリング剤が特に好ましい。   Of these, a silane coupling agent having a secondary amino group is preferred from the viewpoint of fluidity and flame retardancy. The silane coupling agent having a secondary amino group is not particularly limited as long as it is a silane compound having a secondary amino group in the molecule. For example, γ-anilinopropyltrimethoxysilane, γ-anilinopropyltriethoxysilane Γ-anilinopropylmethyldimethoxysilane, γ-anilinopropylmethyldiethoxysilane, γ-anilinopropylethyldiethoxysilane, γ-anilinopropylethyldimethoxysilane, γ-anilinomethyltrimethoxysilane, γ- Anilinomethyltriethoxysilane, γ-anilinomethylmethyldimethoxysilane, γ-anilinomethylmethyldiethoxysilane, γ-anilinomethylethyldiethoxysilane, γ-anilinomethylethyldimethoxysilane, N- (p- Methoxyphenyl) -γ-aminopropyltrimeth Sisilane, N- (p-methoxyphenyl) -γ-aminopropyltriethoxysilane, N- (p-methoxyphenyl) -γ-aminopropylmethyldimethoxysilane, N- (p-methoxyphenyl) -γ-aminopropylmethyl Diethoxysilane, N- (p-methoxyphenyl) -γ-aminopropylethyldiethoxysilane, N- (p-methoxyphenyl) -γ-aminopropylethyldimethoxysilane, γ- (N-methyl) aminopropyltrimethoxy Silane, γ- (N-ethyl) aminopropyltrimethoxysilane, γ- (N-butyl) aminopropyltrimethoxysilane, γ- (N-benzyl) aminopropyltrimethoxysilane, γ- (N-methyl) aminopropyl Triethoxysilane, γ- (N-ethyl) aminopropyltriethoxy Lan, γ- (N-butyl) aminopropyltriethoxysilane, γ- (N-benzyl) aminopropyltriethoxysilane, γ- (N-methyl) aminopropylmethyldimethoxysilane, γ- (N-ethyl) aminopropyl Methyldimethoxysilane, γ- (N-butyl) aminopropylmethyldimethoxysilane, γ- (N-benzyl) aminopropylmethyldimethoxysilane, N-β- (aminoethyl) -γ-aminopropyltrimethoxysilane, γ- ( β-aminoethyl) aminopropyltrimethoxysilane, N-β- (N-vinylbenzylaminoethyl) -γ-aminopropyltrimethoxysilane and the like. Of these, aminosilane coupling agents represented by the following general formula (II) are particularly preferred.

（ここで、Ｒ^１は水素原子、炭素数１〜６のアルキル基及び炭素数１〜２のアルコキシ基から選ばれ、Ｒ^２は炭素数１〜６のアルキル基及びフェニル基から選ばれ、Ｒ^３はメチル基又はエチル基を示し、ｎは１〜６の整数を示し、ｍは１〜３の整数を示す。）

(Where R ¹ is selected from a hydrogen atom, an alkyl group having 1 to 6 carbon atoms and an alkoxy group having 1 to ² carbon atoms, R ² is selected from an alkyl group having 1 to 6 carbon atoms and a phenyl group; ³ represents a methyl group or an ethyl group, n represents an integer of 1 to 6, and m represents an integer of 1 to ^3. )

カップリング剤の全配合量は、封止用エポキシ樹脂組成物に対して０．０３７〜４．７５質量％であることが好ましく、０．０５〜５質量％であることがより好ましく、０．１〜２．５質量％であることがさらに好ましい。０．０３７質量％未満ではフレームとの接着性が低下する傾向があり、４．７５質量％を超えるとパッケージの成形性が低下する傾向がある。   The total blending amount of the coupling agent is preferably 0.037 to 4.75% by mass, more preferably 0.05 to 5% by mass with respect to the epoxy resin composition for sealing. More preferably, it is 1-2.5 mass%. If it is less than 0.037% by mass, the adhesion to the frame tends to be lowered, and if it exceeds 4.75% by mass, the moldability of the package tends to be lowered.

本発明の封止用エポキシ樹脂組成物には、さらに難燃性を向上する目的で従来公知のノンハロゲン、ノンアンチモンの難燃剤を必要に応じて配合することができる。たとえば、赤リン、酸化亜鉛等の無機化合物とフェノール樹脂等の熱硬化性樹脂で被覆された赤リン及びリン酸エステル、ホスフィンオキサイド等のリン化合物、メラミン、メラミン誘導体、メラミン変性フェノール樹脂、トリアジン環を有する化合物、シアヌル酸誘導体、イソシアヌル酸誘導体等の窒素含有化合物、シクロホスファゼン等のリン及び窒素含有化合物、水酸化アルミニウム、水酸化マグネシウム、複合金属水酸化物、酸化亜鉛、錫酸亜鉛、硼酸亜鉛、酸化鉄、酸化モリブデン、モリブデン酸亜鉛、ジシクロペンタジエニル鉄等の金属元素を含む化合物などが挙げられ、これらの１種を単独で用いても２種以上を組合わせて用いてもよい。   In the sealing epoxy resin composition of the present invention, conventionally known non-halogen and non-antimony flame retardants can be blended as needed for the purpose of further improving the flame retardancy. For example, red phosphorus coated with inorganic compounds such as red phosphorus and zinc oxide and thermosetting resins such as phenolic resins, phosphorus compounds such as phosphate esters and phosphine oxides, melamine, melamine derivatives, melamine-modified phenolic resins, triazine rings , Nitrogen-containing compounds such as cyanuric acid derivatives and isocyanuric acid derivatives, phosphorus and nitrogen-containing compounds such as cyclophosphazenes, aluminum hydroxide, magnesium hydroxide, composite metal hydroxides, zinc oxide, zinc stannate, zinc borate , Compounds containing metal elements such as iron oxide, molybdenum oxide, zinc molybdate, dicyclopentadienyl iron, and the like. These may be used alone or in combination of two or more. .

なかでも流動性の観点からは、リン酸エステル、ホスフィンオキサイド及びシクロホスファゼンが好ましい。リン酸エステルはリン酸とアルコール化合物又はフェノール化合物のエステル化合物であれば特に制限はないが、例えばトリメチルホスフェート、トリエチルホスフェート、トリフェニルホスフェート、トリクレジルホスフェート、トリキシレニルホスフェート、クレジルジフェニルホスフェート、キシレニルジフェニルホスフェート、トリス（２，６ジメチルフェニル）ホスフェート及び芳香族縮合リン酸エステル等が挙げられる。なかでも耐加水分解性の観点からは、下記一般式（ＸＸＸＩＸ）で示される芳香族縮合リン酸エステルが好ましい。   Of these, phosphate ester, phosphine oxide and cyclophosphazene are preferable from the viewpoint of fluidity. The phosphate ester is not particularly limited as long as it is an ester compound of phosphoric acid and an alcohol compound or a phenol compound. For example, trimethyl phosphate, triethyl phosphate, triphenyl phosphate, tricresyl phosphate, trixylenyl phosphate, cresyl diphenyl phosphate, Examples include xylenyl diphenyl phosphate, tris (2,6 dimethylphenyl) phosphate, and aromatic condensed phosphate ester. Among these, from the viewpoint of hydrolysis resistance, an aromatic condensed phosphate represented by the following general formula (XXXIX) is preferable.

上記式（ＸＸＸＩＸ）のリン酸エステルを例示すると、下記構造式（ＸＸＸＸ）〜（ＸＸＸＸＩＶ）で示されるリン酸エステル等が挙げられる。   When the phosphoric acid ester of the said formula (XXXIX) is illustrated, the phosphoric acid ester shown by the following structural formula (XXXX)-(XXXXIV) etc. will be mentioned.

これらリン酸エステルの添加量は、充填剤を除く他の全配合成分に対して、燐原子の量で０．２〜３．０重量％の範囲内であることが好ましい。０．２重量％より少ない場合は難燃効果が低くなる傾向がある。３．０重量％を超えた場合は成形性、耐湿性の低下や、成形時にこれらのリン酸エステルがしみ出し、外観を阻害する場合がある。   It is preferable that the addition amount of these phosphate ester exists in the range of 0.2-3.0 weight% in the quantity of a phosphorus atom with respect to all the other compounding components except a filler. When it is less than 0.2% by weight, the flame retardancy tends to be low. If it exceeds 3.0% by weight, the formability and moisture resistance may be deteriorated, and these phosphate esters may ooze out during molding, thereby impairing the appearance.

ホスフィンオキサイドを難燃剤として用いる場合、ホスフィンオキサイドとしては下記一般式（ＸＸＸＸＶ）で示される化合物が好ましい。   When phosphine oxide is used as a flame retardant, the phosphine oxide is preferably a compound represented by the following general formula (XXXXV).

（ここで、Ｒ^１、Ｒ^２及びＲ^３は炭素数１〜１０の置換又は非置換のアルキル基、アリール基、アラルキル基及び水素原子を示し、すべて同一でも異なってもよい。ただしすべてが水素原子である場合を除く。）

(Here, R ¹ , R ² and R ³ represent a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, an aryl group, an aralkyl group and a hydrogen atom, which may all be the same or different. Except when it is an atom.)

上記一般式（ＸＸＸＸＶ）で示されるリン化合物の中でも、耐加水分解性の観点からはＲ^１〜Ｒ^３が置換又は非置換のアリール基であることが好ましく、特に好ましくはフェニル基である。 Among the phosphorus compounds represented by the above general formula (XXXXV), R ^{1 to} R ³ are preferably a substituted or unsubstituted aryl group, particularly preferably a phenyl group, from the viewpoint of hydrolysis resistance.

ホスフィンオキサイドの配合量は封止用エポキシ樹脂組成物に対してリン原子の量が０．０１〜０．２質量％であることが必要である。好ましくは０．０２〜０．１質量％であり、さらに好ましくは０．０３〜０．０８質量％である。０．０１質量％未満であると難燃性が低下し、０．２質量％を超えると成形性、耐湿性が低下する。   The compounding quantity of phosphine oxide needs that the quantity of phosphorus atoms is 0.01-0.2 mass% with respect to the epoxy resin composition for sealing. Preferably it is 0.02-0.1 mass%, More preferably, it is 0.03-0.08 mass%. If it is less than 0.01% by mass, the flame retardancy is lowered, and if it exceeds 0.2% by mass, the moldability and moisture resistance are lowered.

シクロホスファゼンとしては主鎖骨格中に次式（ＸＸＸＸＶＩ）及び／又は次式（ＸＸＸＸＶＩＩ）を繰り返し単位として含む環状ホスファゼン化合物、あるいはホスファゼン環中の燐原子に対する置換位置が異なる次式（ＸＸＸＸＶＩＩＩ）及び／又は次式（ＸＸＸＸＩＸ）を繰り返し単位として含む化合物等が挙げられる。   Cyclophosphazenes include cyclic phosphazene compounds containing the following formula (XXXXVI) and / or the following formula (XXXXVII) as a repeating unit in the main chain skeleton, or the following formulas (XXXXVIII) and / or different substitution positions for phosphorus atoms in the phosphazene ring. Alternatively, a compound containing the following formula (XXXIX) as a repeating unit can be given.

ここで、式（ＸＸＸＸＶＩ）及び式（ＸＸＸＶＩＩＩ）中のｍは１〜１０の整数で、Ｒ^１〜Ｒ^４は置換基を有しても良い炭素数１〜１２のアルキル基、アリール基及び水酸基から選ばれ、全て同一でも異なっていても良い。Ａは炭素数１〜４のアルキレン基又はアリレン基を示す。式（ＸＸＸＸＶＩＩ）及び式（ＸＸＸＸＩＸ）中のｎは１〜１０の整数で、Ｒ^５〜Ｒ^８は置換基を有しても良い炭素数１〜１２のアルキル基又はアリール基から選ばれ、全て同一でも異なっていても良く、Ａは炭素数１〜４のアルキレン基又はアリレン基を示す。また、式中ｍ個のＲ^１、Ｒ^２、Ｒ^３、Ｒ^４はｍ個全てが同一でも異なっていても良く、ｎ個のＲ^５、Ｒ^６、Ｒ^７、Ｒ^８はｎ個全てが同一でも異なっていても良い。
上記式（ＸＸＸＸＶＩ）〜式（ＸＸＸＸＩＸ）において、Ｒ^１〜Ｒ^８で示される置換基を有しても良い炭素数１〜１２のアルキル基又はアリール基としては特に制限はないが、例えばメチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｓｅｃ−ブチル基、ｔｅｒｔ−ブチル基等のアルキル基、フェニル基、１−ナフチル基、２−ナフチル基等のアリール基、ｏ−トリル基、ｍ−トリル基、ｐ−トリル基、２，３−キシリル基、２，４−キシリル基、ｏ−クメニル基、ｍ−クメニル基、ｐ−クメニル基、メシチル基等のアルキル基置換アリール基、ベンジル基、フェネチル基等のアリール基置換アルキル基などが挙げられ、さらにこれらに置換する置換基としては、アルキル基、アルコキシル基、アリール基、水酸基、アミノ基、エポキシ基、ビニル基、ヒドロキシアルキル基、アルキルアミノ基等が挙げられる。 Here, m in the formula (XXXXVI) and the formula (XXXVIII) is an integer of 1 to 10, and R ^{1 to} R ⁴ are alkyl groups, aryl groups, and hydroxyl groups having 1 to 12 carbon atoms that may have a substituent. And all may be the same or different. A represents an alkylene group having 1 to 4 carbon atoms or an arylene group. N in Formula (XXXXVII) and Formula (XXXXIX) is an integer of 1 to 10, and R ^{5 to} R ⁸ are selected from an alkyl group or aryl group having 1 to 12 carbon atoms that may have a substituent, and all They may be the same or different, and A represents an alkylene group having 1 to 4 carbon atoms or an arylene group. In the formula, m R ¹ , R ² , R ³ and R ⁴ may all be the same or different, and n R ⁵ , R ⁶ , R ⁷ and R ⁸ are all n. It may be the same or different.
In the above formulas (XXXXVI) to (XXXXIX), the alkyl group or aryl group having 1 to 12 carbon atoms which may have a substituent represented by R ^{1 to} R ⁸ is not particularly limited. Alkyl groups such as ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, sec-butyl group and tert-butyl group, aryl groups such as phenyl group, 1-naphthyl group and 2-naphthyl group, o-tolyl Group, m-tolyl group, p-tolyl group, 2,3-xylyl group, 2,4-xylyl group, o-cumenyl group, m-cumenyl group, p-cumenyl group, mesityl group, etc. , Aryl groups substituted alkyl groups such as benzyl group and phenethyl group, etc., and substituents substituted therewith include alkyl groups, alkoxyl groups, aryl groups, water Group, an amino group, an epoxy group, a vinyl group, a hydroxyalkyl group, an alkylamino group, and the like.

これらの中で、エポキシ樹脂組成物の耐熱性、耐湿性の観点からはアリール基が好ましく、より好ましくはフェニル基もしくはヒドロキシフェニル基である。   Among these, from the viewpoint of heat resistance and moisture resistance of the epoxy resin composition, an aryl group is preferable, and a phenyl group or a hydroxyphenyl group is more preferable.

また、上記式（ＸＸＸＸＶＩ）〜式（ＸＸＸＸＩＸ）中のＡで示される炭素数１〜４のアルキレン基又はアリレン基としては特に制限はないが、例えばメチレン基、エチレン基、プロピレン基、イソプロピレン基、ブチレン基、イソブチレン基、フェニレン基、トリレン基、キシリレン基、ナフチレン基等が挙げられ、エポキシ樹脂組成物の耐熱性、耐湿性の観点からはアリレン基が好ましく、中でもフェニレン基がより好ましい。   Further, the alkylene group or arylene group having 1 to 4 carbon atoms represented by A in the above formulas (XXXXVI) to (XXXXIX) is not particularly limited, but for example, a methylene group, an ethylene group, a propylene group, an isopropylene group. , Butylene group, isobutylene group, phenylene group, tolylene group, xylylene group, naphthylene group, and the like. From the viewpoint of heat resistance and moisture resistance of the epoxy resin composition, an arylene group is preferable, and a phenylene group is more preferable.

環状ホスファゼン化合物は、上記式（ＸＸＸＸＶＩ）〜式（ＸＸＸＸＩＸ）のいずれかの重合物、上記式（ＸＸＸＸＶＩ）と上記式（ＸＸＸＸＶＩＩ）との共重合物、又は上記式（ＸＸＸＸＶＩＩＩ）と上記式（ＸＸＸＸＩＸ）との共重合物であるが、共重合物の場合、ランダム共重合物でも、ブロック共重合物でも、交互共重合物のいずれでも良い。その共重合モル比ｍ／ｎは特に限定するものではないが、エポキシ樹脂硬化物の耐熱性や強度向上の観点から１／０〜１／４が好ましく、１／０〜１／１．５がより好ましい。また、重合度ｍ＋ｎは１〜２０であり、好ましくは２〜８、より好ましくは３〜６である。   The cyclic phosphazene compound is a polymer of any one of the above formulas (XXXXVI) to (XXXXIX), a copolymer of the above formula (XXXXVI) and the above formula (XXXXVII), or the above formula (XXXXVIII) and the above formula (XXXXIX). In the case of a copolymer, it may be a random copolymer, a block copolymer or an alternating copolymer. The copolymerization molar ratio m / n is not particularly limited, but is preferably 1/0 to 1/4 from the viewpoint of heat resistance and strength improvement of the cured epoxy resin, and 1/0 to 1 / 1.5. More preferred. Moreover, polymerization degree m + n is 1-20, Preferably it is 2-8, More preferably, it is 3-6.

環状ホスファゼン化合物として好ましいものを例示すると、次式（ＸＸＸＸＸ）の重合物、次式（ＸＸＸＸＸＩ）の共重合物等が挙げられる。   Preferred examples of the cyclic phosphazene compound include a polymer of the following formula (XXXX), a copolymer of the following formula (XXXXXX), and the like.

（ここで、式（ＸＸＸＸＸ）中のｍは、０〜９の整数で、Ｒ^１〜Ｒ^４はそれぞれ独立に水素又は水酸基を示す。）

(Here, m in the formula (XXXX) is an integer of 0 to 9, and R ^{1 to} R ⁴ each independently represent hydrogen or a hydroxyl group.)

ここで、上記式（ＸＸＸＸＸＩ）中のｍ、ｎは、０〜９の整数で、Ｒ^１〜Ｒ^４はそれぞれ独立に水素または水酸基から選ばれ、Ｒ^５〜Ｒ^８はそれぞれ独立に水素または水酸基から選ばれる。また、上記式（ＸＸＸＸＸＩ）で示される環状ホスファゼン化合物は、次に示すｍ個の繰り返し単位（ａ）とｎ個の繰り返し単位（ｂ）を交互に含むもの、ブロック状に含むもの、ランダムに含むもののいずれであってもかまわないが、ランダムに含むものが好ましい。 Here, m and n in the above formula (XXXXXXI) are integers of 0 to 9, R ^{1 to} R ⁴ are each independently selected from hydrogen or a hydroxyl group, and R ^{5 to} R ⁸ are each independently hydrogen or a hydroxyl group. Chosen from. In addition, the cyclic phosphazene compound represented by the above formula (XXXXXXI) includes the following m repeating units (a) and n repeating units (b) alternately, including blocks, or randomly including Any of these may be used, but those randomly included are preferred.

中でも、上記式（ＸＸＸＸＸ）でｍが３〜６の重合体を主成分とするものや、上記式（ＸＸＸＸＸＩでＲ^５〜Ｒ^８が全て水素又は１つが水酸基であり、ｍ／ｎが１／２〜１／３で、ｍ＋ｎが３〜６の共重合体を主成分とするものが好ましい。また、市販のホスファゼン化合物としては、ＳＰＥ−１００（大塚化学製商品名）が入手可能である。 Among them, a polymer having m of 3 to 6 as a main component in the above formula (XXXX), or R ^{5 to} R ⁸ in the above formula (XXXXI) are all hydrogen or one is a hydroxyl group, and m / n is 1 / The main component is preferably a copolymer having 2 to 1/3 and m + n of 3 to 6. As a commercially available phosphazene compound, SPE-100 (trade name, manufactured by Otsuka Chemical) is available.

複合金属水酸化物を難燃剤として用いる場合、複合金属水酸化物は下記組成式（ＸＸＸＸＸＩＩ）で示される化合物が好ましい。   When the composite metal hydroxide is used as a flame retardant, the composite metal hydroxide is preferably a compound represented by the following composition formula (XXXXII).

（ここで、Ｍ^１、Ｍ^２及びＭ^３は互いに異なる金属元素を示し、ａ、ｂ、ｃ、ｄ、ｅ、ｆ、ｐ、ｑ及びｍは正の数、ｒは０又は正の数を示す。）

(Here, M ¹ , M ² and M ³ represent different metal elements, a, b, c, d, e, f, p, q and m are positive numbers, and r is 0 or a positive number. Show.)

なかでも、上記組成式（ＸＸＸＸＸＩＩ）中のｒが０である化合物、すなわち、下記組成式（ＸＸＸＸＸＩＩＩ）で示される化合物がさらに好ましい。   Among these, a compound in which r in the composition formula (XXXXII) is 0, that is, a compound represented by the following composition formula (XXXXIII) is more preferable.

（ここで、Ｍ^１及びＭ^２は互いに異なる金属元素を示し、ａ、ｂ、ｃ、ｄ、ｍ、ｎ及びｌは正の数を示す。）

(Here, M ¹ and M ² represent different metal elements, and a, b, c, d, m, n, and l represent positive numbers.)

上記組成式（ＸＸＸＸＸＩＩ）及び（ＸＸＸＸＸＩＩＩ）中のＭ^１、Ｍ^２及びＭ^３は互いに異なる金属元素であれば特に制限はないが、難燃性の観点からは、Ｍ^１とＭ^２が同一とならないようにＭ^１が第３周期の金属元素、ＩＩＡ族のアルカリ土類金属元素、ＩＶＢ族、ＩＩＢ族、ＶＩＩＩ族、ＩＢ族、ＩＩＩＡ族及びＩＶＡ族に属する金属元素から選ばれ、Ｍ^２がＩＩＩＢ〜ＩＩＢ族の遷移金属元素から選ばれることが好ましく、Ｍ^１がマグネシウム、カルシウム、アルミニウム、スズ、チタン、鉄、コバルト、ニッケル、銅及び亜鉛から選ばれ、Ｍ^２が鉄、コバルト、ニッケル、銅及び亜鉛から選ばれることがより好ましい。流動性の観点からは、Ｍ^１がマグネシウム、Ｍ^２が亜鉛又はニッケルであることが好ましく、Ｍ^１がマグネシウムでＭ^２が亜鉛であることがより好ましい。 M ¹ , M ² and M ³ in the above composition formulas (XXXXII) and (XXXXIII) are not particularly limited as long as they are different metal elements, but from the viewpoint of flame retardancy, M ¹ and M ² are the same. M ¹ is selected from metal elements belonging to the third period metal element, Group IIA alkaline earth metal element, Group IVB, Group IIB, Group VIII, Group IB, Group IIIA and Group IVA, and M ² Preferably, the transition metal element is selected from Group IIIB to IIB, M ¹ is selected from magnesium, calcium, aluminum, tin, titanium, iron, cobalt, nickel, copper and zinc, and M ² is iron, cobalt, nickel, More preferably, it is selected from copper and zinc. From the viewpoint of fluidity, M ¹ is preferably magnesium and M ² is preferably zinc or nickel, more preferably M ¹ is magnesium and M ² is zinc.

上記組成式（ＸＸＸＸＸＩＩ）中のｐ、ｑ、ｒのモル比は本発明の効果が得られれば特に制限はないが、ｒ＝０で、ｐ及びｑのモル比ｐ／ｑが９９／１〜５０／５０であることが好ましい。すなわち、上記組成式（ＸＸＸＸＸＩＩＩ）中のｍ及びｎのモル比ｍ／ｎが９９／１〜５０／５０であることが好ましい。   The molar ratio of p, q, and r in the composition formula (XXXXII) is not particularly limited as long as the effects of the present invention can be obtained. However, when r = 0, the molar ratio p / q of p and q is 99/1 to Preferably it is 50/50. That is, the molar ratio m / n between m and n in the composition formula (XXXXIII) is preferably 99/1 to 50/50.

市販品としては、例えば、上記組成式（ＸＸＸＸＸＩＩＩ）のＭ^１がマグネシウム、Ｍ^２が亜鉛で、ｍが７、ｎが３、ｌが１０で、ａ、ｂ、ｃ及びｄが１である水酸化マグネシウム・水酸化亜鉛固溶体複合金属水酸化物（タテホ化学工業株式会社製商品名エコーマグＺ−１０）を使用できる。なお、金属元素とは半金属元素といわれるものも含めるものとし、非金属元素を除く全ての元素をさす。 Examples of commercially available products include water in which M ^{1 in the} composition formula (XXXXIII) is magnesium, M ² is zinc, m is 7, n is 3, l is 10, and a, b, c, and d are 1. Magnesium oxide / zinc hydroxide solid solution composite metal hydroxide (trade name Echo Mug Z-10, manufactured by Tateho Chemical Co., Ltd.) can be used. In addition, what is called a metalloid element also includes what is called a metal element, and refers to all elements except a nonmetallic element.

なお、金属元素の分類は、典型元素をＡ亜族、遷移元素をＢ亜族とする長周期型の周期率表（出典：共立出版株式会社発行「化学大辞典４」１９８７年２月１５日縮刷版第３０刷）に基づいて行った。   In addition, the classification of metal elements is a long-period type periodic rate table in which the typical element is the A subgroup and the transition element is the B subgroup (Source: Kyoritsu Shuppan Co., Ltd., “Chemical Dictionary 4”, February 15, 1987) (Reduced plate 30th printing).

複合金属水酸化物の形状は特に制限はないが、流動性、充填性の観点からは、平板状より、適度の厚みを有する多面体形状が好ましい。複合金属水酸化物は、金属水酸化物と比較して多面体状の結晶が得られやすい。   The shape of the composite metal hydroxide is not particularly limited, but from the viewpoint of fluidity and filling properties, a polyhedral shape having an appropriate thickness is preferable to a flat plate shape. Compared to metal hydroxides, complex metal hydroxides tend to give polyhedral crystals.

複合金属水酸化物の配合量は特に制限はないが、封止用エポキシ樹脂組成物に対して０．５〜２０質量％が好ましく、０．７〜１５質量％がより好ましく、１．４〜１２質量％がさらに好ましい。０．５質量％未満では難燃性が不十分となる傾向があり、２０質量％を超えると流動性及び耐リフロー性が低下する傾向がある。   Although the compounding quantity of a composite metal hydroxide does not have a restriction | limiting in particular, 0.5-20 mass% is preferable with respect to the epoxy resin composition for sealing, 0.7-15 mass% is more preferable, 1.4- 12 mass% is more preferable. If it is less than 0.5% by mass, the flame retardancy tends to be insufficient, and if it exceeds 20% by mass, the fluidity and reflow resistance tend to be lowered.

トリアジン環を有する化合物としては、フェノール性水酸基を有する化合物とトリアジン誘導体とアルデヒド基を有する化合物を共縮重合させたものが、難燃性、銅フレームとの接着性の観点から好ましい。フェノール性水酸基を有する化合物としては、フェノール、クレゾール、キシレノール、エチルフェノール、ブチルフェノール、ノニルフェノール、オクチルフェノール等のアルキルフェノール類、レゾルシン、カテコール、ビスフェノールＡ、ビスフェノールＦ、ビスフェノールＳ等の多価フェノール類、フェニルフェノール、アミノフェノール、又はα−ナフトール、β−ナフトール、ジヒドロキシナフタレン等のナフトール類あるいはこれらのフェノール性水酸基を有する化合物とホルムアルデヒド等のアルデヒド基を有する化合物とを酸性触媒下で縮合又は共縮合させて得られる樹脂等がある。中でも、成形性の観点からはフェノール、クレゾール、あるいはこれらとホルムアルデヒドとの共縮重合物が好ましい。また、トリアジン誘導体としては分子中にトリアジン核を有するものであれば特に限定はなく、メラミン、ベンゾグアナミン、アセトグアナミン等のグアナミン誘導体、シアヌル酸、メチルシアヌレート等のシアヌル酸誘導体が挙げられ、１種類のみまたは２種類以上の併用も可能である。中でも、成形性、信頼性の観点からはメラミン、ベンゾグアナミン等のグアナミン誘導体が好ましい。また、アルデヒド基を有する化合物としては、例えば、ホルマリン、パラホルムアルデヒド等が挙げられる。 As the compound having a triazine ring, a compound obtained by co-condensation polymerization of a compound having a phenolic hydroxyl group, a triazine derivative and a compound having an aldehyde group is preferable from the viewpoint of flame retardancy and adhesiveness to a copper frame. Examples of the compound having a phenolic hydroxyl group include alkylphenols such as phenol, cresol, xylenol, ethylphenol, butylphenol, nonylphenol, octylphenol, polyphenols such as resorcin, catechol, bisphenol A, bisphenol F, bisphenol S, phenylphenol, It is obtained by condensation or cocondensation of aminophenol, naphthols such as α-naphthol, β-naphthol, dihydroxynaphthalene or the like, or a compound having these phenolic hydroxyl groups and a compound having an aldehyde group such as formaldehyde under an acidic catalyst. There are resins. Of these, phenol, cresol, or a copolycondensation product of these with formaldehyde is preferable from the viewpoint of moldability. The triazine derivative is not particularly limited as long as it has a triazine nucleus in the molecule, and examples thereof include guanamine derivatives such as melamine, benzoguanamine and acetoguanamine, and cyanuric acid derivatives such as cyanuric acid and methyl cyanurate. Only two or more types can be used in combination. Of these, guanamine derivatives such as melamine and benzoguanamine are preferable from the viewpoints of moldability and reliability. Examples of the compound having an aldehyde group include formalin and paraformaldehyde.

フェノール性水酸基を有する化合物に対するアルデヒド基を有する化合物の配合量は、モル比（アルデヒド基を有する化合物（モル）／フェノール性水酸基を有する化合物（モル））で０．０５〜０．９になるようにすることが好ましく、０．１〜０．８とするのがより好ましい。０．０５未満ではフェノール性水酸基に対するアルデヒド基を有する化合物の反応が起こりにくく、未反応フェノールが残りやすく、生産性が悪く、０．９を超えると合成中ゲル化しやすくなる。   The compounding amount of the compound having an aldehyde group with respect to the compound having a phenolic hydroxyl group is 0.05 to 0.9 in a molar ratio (compound having an aldehyde group (mol) / compound having a phenolic hydroxyl group (mol)). It is preferable to set it to 0.1 to 0.8. If it is less than 0.05, the reaction of the compound having an aldehyde group with respect to the phenolic hydroxyl group hardly occurs, unreacted phenol tends to remain, the productivity is poor, and if it exceeds 0.9, gelation tends to occur during synthesis.

フェノール性水酸基を有する化合物に対するトリアジン誘導体の配合量は１〜３０重量％とするのが好ましく、さらには５〜２０重量％とするのがより好ましい。１重量％未満では難燃性に乏しく、３０重量％を超えると軟化点が高くなり、組成物作製時の混練性が低下する。トリアジン誘導体に対するアルデヒド基を有する化合物の配合量（モル比）は特に制限はない。   The blending amount of the triazine derivative with respect to the compound having a phenolic hydroxyl group is preferably 1 to 30% by weight, and more preferably 5 to 20% by weight. If it is less than 1% by weight, the flame retardancy is poor, and if it exceeds 30% by weight, the softening point becomes high and the kneadability at the time of preparing the composition is lowered. The compounding amount (molar ratio) of the compound having an aldehyde group with respect to the triazine derivative is not particularly limited.

フェノール性水酸基を有する化合物とトリアジン誘導体とアルデヒド基を有する化合物との共縮重合物の合成時の反応温度は特に制限はないが、６０〜１２０℃で行うのが好ましい。また反応のｐＨは３〜９が好ましく、４〜８がさらに好ましい。ｐＨが３未満では合成中に樹脂がゲル化し易く、９より高いとフェノール樹脂とトリアジン誘導体とアルデヒド基を有する化合物との共縮重合が起こりにくくなり、製造した樹脂の窒素含有量が低くなる。   The reaction temperature at the time of synthesizing a copolycondensation product of a compound having a phenolic hydroxyl group, a triazine derivative and a compound having an aldehyde group is not particularly limited, but is preferably 60 to 120 ° C. Moreover, 3-9 are preferable and, as for pH of reaction, 4-8 are more preferable. If the pH is less than 3, the resin tends to gel during synthesis, and if it is higher than 9, copolycondensation of the phenol resin, triazine derivative and compound having an aldehyde group hardly occurs, and the produced resin has a low nitrogen content.

必要に応じてフェノール性水酸基を有する化合物にアルデヒド基を有する化合物、トリアジン誘導体を反応させた後、常圧または減圧下での加熱蒸留等で、未反応のフェノール化合物及びアルデヒド基を有する化合物等を除去することができる。この時未反応フェノール化合物の残存量が３％以下であることが好ましい。３％を超える場合は成形性が低下しがちである。   If necessary, after reacting a compound having a phenolic hydroxyl group with a compound having an aldehyde group, a triazine derivative, heating distillation under normal pressure or reduced pressure, etc., an unreacted phenol compound and a compound having an aldehyde group, etc. Can be removed. At this time, the residual amount of the unreacted phenol compound is preferably 3% or less. If it exceeds 3%, the moldability tends to decrease.

また得られた共縮重合物の軟化点は４０〜１５０℃であることが好ましい。４０℃未満であるとブロッキングしやすく、１５０℃を超える場合は組成物の混練性が低下する。このフェノール性水酸基を有する化合物とトリアジン誘導体とアルデヒド基を有する化合物との共縮重合物を例示するならば、下記構造式（ＸＸＸＸＸＩＶ）〜（ＸＸＸＸＸＩＸ）のものが挙げられる。   Moreover, it is preferable that the softening point of the obtained copolycondensation product is 40-150 degreeC. When it is less than 40 ° C., it is easy to block, and when it exceeds 150 ° C., the kneadability of the composition is lowered. Examples of the copolycondensation product of a compound having a phenolic hydroxyl group, a triazine derivative, and a compound having an aldehyde group include those represented by the following structural formulas (XXXXIV) to (XXXXIX).

フェノール性水酸基を有する化合物とトリアジン誘導体とアルデヒド基を有する化合物との共縮重合物の数平均分子量は５００〜１０００であることが好ましく、５５０〜８００がさらに好ましい。５００未満であると成形性、耐リフロークラック性が低下し、１０００を超える場合は流動性が低下しがちである。また重量平均分子量は１５００〜１００００であることが好ましく、１７００〜７０００がさらに好ましい。１５００未満であると耐リフロークラック性が低下し、１００００を超える場合は流動性が低下しがちである。さらに、このフェノール性水酸基を有する化合物とトリアジン誘導体とアルデヒド基を有する化合物との共縮重合物の分子量分布Ｍｗ／Ｍｎは２．０〜１０．０であることが好ましく、３．０〜６．０がさらに好ましい。２．０未満であると耐リフロークラック性が低下し、１０．０を超える場合は流動性が低下しがちである。   The number average molecular weight of the copolycondensation product of a compound having a phenolic hydroxyl group, a triazine derivative and a compound having an aldehyde group is preferably 500 to 1,000, and more preferably 550 to 800. If it is less than 500, moldability and reflow crack resistance are lowered, and if it exceeds 1000, fluidity tends to be lowered. The weight average molecular weight is preferably 1500 to 10,000, and more preferably 1700 to 7000. When it is less than 1500, the reflow crack resistance is lowered, and when it exceeds 10,000, the fluidity tends to be lowered. Furthermore, the molecular weight distribution Mw / Mn of the copolycondensation product of the compound having a phenolic hydroxyl group, the triazine derivative and the compound having an aldehyde group is preferably 2.0 to 10.0, and preferably 3.0 to 6. 0 is more preferable. When it is less than 2.0, the reflow crack resistance is lowered, and when it exceeds 10.0, the fluidity tends to be lowered.

上記共縮重合物の中でもフェノール樹脂とトリアジン誘導体とアルデヒド基を有する化合物との共重縮合物であることが、耐リフロー性の観点からより好ましい。ここで用いられるフェノール樹脂としては組成物で一般に使用されているもので特に限定はなく、例えば、フェノール、クレゾール、キシレノール、エチルフェノール、ブチルフェノール、ノニルフェノール、オクチルフェノール等のアルキルフェノール類、レゾルシン、カテコール、ビスフェノールＡ、ビスフェノールＦ、ビスフェノールＳ等の多価フェノール類、α−ナフトール、β−ナフトール、ジヒドロキシナフタレン等のナフトール類又はフェニルフェノール、アミノフェノール等のフェノール誘導体とホルムアルデヒド等のアルデヒド基を有する化合物とを酸性触媒下で縮合又は共縮合させて得られる樹脂等がある。中でも、成形性の観点からはフェノールとホルムアルデヒドとの重縮合物であるフェノール・ノボラック樹脂が好ましい。   Among the copolycondensation products, a copolycondensation product of a phenol resin, a triazine derivative and a compound having an aldehyde group is more preferable from the viewpoint of reflow resistance. The phenol resin used here is not particularly limited as it is generally used in the composition, for example, phenol, cresol, xylenol, ethylphenol, butylphenol, nonylphenol, alkylphenols such as octylphenol, resorcin, catechol, bisphenol A. Acid catalysts for polyhydric phenols such as bisphenol F and bisphenol S, naphthols such as α-naphthol, β-naphthol and dihydroxynaphthalene or phenol derivatives such as phenylphenol and aminophenol and compounds having an aldehyde group such as formaldehyde There are resins obtained by condensation or cocondensation below. Among these, from the viewpoint of moldability, a phenol novolak resin which is a polycondensate of phenol and formaldehyde is preferable.

フェノール樹脂は上記に列挙したようなものであれば、特にその合成方法は限定するものではないが、下記に示す方法により合成したものを用いた場合、その分子量、分子量分布を本発明で記載する好ましい範囲のものとして合成可能であるという点で、好適である。すなわち、フェノール樹脂を合成する際、フェノール誘導体とアルデヒド基を有する化合物の使用割合は、フェノール誘導体１モルに対してアルデヒド基を有する化合物が０．０１〜２．０モルとすることが好ましく、０．０５〜１．０モルとすることがより好ましい。０．０１モル未満では、反応が不十分となり、分子量が上がらず、成形性、耐熱性、耐水性、難燃性、強度等が低下する傾向があり、２．０モルを超えると、分子量が大きくなりすぎて、混練性が低下する傾向がある。   The synthesis method of the phenol resin is not particularly limited as long as it is enumerated above, but when it is synthesized by the method shown below, its molecular weight and molecular weight distribution are described in the present invention. It is preferable in that it can be synthesized as a preferred range. That is, when synthesizing a phenol resin, the proportion of the compound having a phenol derivative and an aldehyde group is preferably 0.01 to 2.0 mol of the compound having an aldehyde group with respect to 1 mol of the phenol derivative. It is more preferable to set it as 0.05-1.0 mol. If the amount is less than 0.01 mol, the reaction becomes insufficient, the molecular weight does not increase, and the moldability, heat resistance, water resistance, flame retardancy, strength, etc. tend to decrease. It tends to be too large and the kneadability tends to decrease.

この反応温度は、８０〜２２０℃とすることが好ましく、１００〜１８０℃とすることがより好ましい。８０℃未満では、反応性が不充分となり、分子量が小さく、成形性が低下する傾向があり、２５０℃を越えるとフェノール樹脂を合成する際に、生産設備的に不利となる傾向がある。反応時間は、１〜３０時間程度とするのが好ましい。   This reaction temperature is preferably 80 to 220 ° C, more preferably 100 to 180 ° C. If the temperature is less than 80 ° C., the reactivity becomes insufficient, the molecular weight tends to be small, and the moldability tends to decrease. If the temperature exceeds 250 ° C., the production equipment tends to be disadvantageous when the phenol resin is synthesized. The reaction time is preferably about 1 to 30 hours.

また、必要に応じてトリメチルアミン、トリエチルアミン等のアミン系触媒、ｐ−トルエンスルホン酸、蓚酸等の酸触媒、水酸化ナトリウム、アンモニア等のアルカリ触媒などを、フェノール誘導体１モルに対して、０．００００１〜０．０１モル程度使用してもよい。また、反応系のＰＨは、１〜１０程度とするのが好ましい。   If necessary, an amine catalyst such as trimethylamine or triethylamine, an acid catalyst such as p-toluenesulfonic acid or oxalic acid, an alkali catalyst such as sodium hydroxide or ammonia, etc. may be added to 0.00001 with respect to 1 mol of the phenol derivative. About 0.01 mol may be used. The pH of the reaction system is preferably about 1 to 10.

このようにして、フェノール誘導体及びアルデヒド基を有する化合物を反応させた後、必要に応じて、未反応のフェノール誘導体、アルデヒド基を有する化合物、水等を加熱減圧下に除去することができるが、その条件は、温度が８０〜２２０℃、望ましくは１００〜１８０℃、圧力が１００ｍｍＨｇ以下、望ましくは６０ｍｍＨｇ以下、時間が０．５〜１０時間とすることが好ましい。   In this way, after reacting the phenol derivative and the compound having an aldehyde group, if necessary, the unreacted phenol derivative, the compound having an aldehyde group, water and the like can be removed under heating and reduced pressure. It is preferable that the temperature is 80 to 220 ° C., desirably 100 to 180 ° C., the pressure is 100 mmHg or less, desirably 60 mmHg or less, and the time is 0.5 to 10 hours.

フェノール樹脂に、トリアジン誘導体及びアルデヒド基を有する化合物を添加し、反応させる際のトリアジン誘導体及びアルデヒド基を有する化合物の使用割合は、フェノール誘導体とアルデヒド基を有する化合物との重縮合物（フェノール樹脂）（未反応のフェノール誘導体、アルデヒド基を有する化合物、水等を加熱減圧下に除去したもの、あるいは前記除去を行っていないもの（この場合は、未反応フェノールも重縮合物の重量に含むこととする））１００ｇ対して、トリアジン誘導体を３〜５０ｇとすることが好ましく、４〜３０ｇとすることがより好ましい。また、アルデヒド基を有する化合物は、重縮合物（フェノール樹脂）１００ｇ対して、５〜１００ｇとすることが好ましく、６〜５０ｇとすることがより好ましい。トリアジン誘導体（ｂ）及びアルデヒド基を有する化合物を上記のような範囲とすることで、最終的に得られる重縮合物の分子量分布、窒素含有量を所望の範囲に容易に調整することができる。   The proportion of the triazine derivative and the compound having an aldehyde group used in the reaction by adding a triazine derivative and a compound having an aldehyde group to the phenol resin is the polycondensate of the phenol derivative and the compound having an aldehyde group (phenol resin). (Unreacted phenol derivative, compound having an aldehyde group, water removed under heating or reduced pressure, or not removed (in this case, unreacted phenol is included in the weight of the polycondensate) 3) The triazine derivative is preferably 3 to 50 g and more preferably 4 to 30 g with respect to 100 g. Moreover, it is preferable to set it as 5-100g with respect to 100g of polycondensates (phenol resin), and, as for the compound which has an aldehyde group, it is more preferable to set it as 6-50g. By setting the triazine derivative (b) and the compound having an aldehyde group in the above ranges, the molecular weight distribution and nitrogen content of the finally obtained polycondensate can be easily adjusted to a desired range.

反応温度は、５０〜２５０℃とすることが好ましく、８０〜１７０℃とすることがより好ましい。５０℃未満では、反応が不充分となり、分子量が上がらず、成形性、耐熱性、耐水性、難燃性、強度等が低下する傾向があり、２５０℃を越えると合成する際に、生産設備的に不利となる傾向がある。反応時間は、１〜３０時間程度とするのが好ましい。   The reaction temperature is preferably 50 to 250 ° C, more preferably 80 to 170 ° C. If the temperature is lower than 50 ° C, the reaction becomes insufficient, the molecular weight does not increase, and the moldability, heat resistance, water resistance, flame retardancy, strength, etc. tend to decrease. Tend to be disadvantageous. The reaction time is preferably about 1 to 30 hours.

また、必要に応じてトリメチルアミン、トリエチルアミン等のアミン系触媒、蓚酸等の酸触媒を、フェノール誘導体１モルに対して、０．００００１〜０．０１モル程度使用してもよい。   Moreover, you may use about 0.00001-0.01 mol of amine catalysts, such as a trimethylamine and a triethylamine, and acid catalysts, such as an oxalic acid, with respect to 1 mol of phenol derivatives as needed.

また、反応系のｐＨは、１〜１０程度とするのが好ましい。フェノール誘導体とアルデヒド基を有する化合物との重縮合物（フェノール樹脂）と、トリアジン誘導体及びアルデヒド基を有する化合物との反応の後、未反応のフェノール誘導体、アルデヒド基を有する化合物、水等を加熱減圧下に除去することができるが、その条件は、温度が８０〜１８０℃、圧力が１００ｍｍＨｇ以下、望ましくは６０ｍｍＨｇ以下、時間が０．５〜１０時間とすることが好ましい。合成に用いるトリアジン誘導体としては分子中にトリアジン核を有する化合物であれば特に限定はなく、メラミン、ベンゾグアナミン、アセトグアナミン等のグアナミン誘導体、シアヌル酸、メチルシアヌレート等のシアヌル酸誘導体等が挙げられ、１種類のみまたは２種類以上の併用も可能である。中でも、成形性、信頼性の観点からはメラミン、ベンゾグアナミン等のグアナミン誘導体が好ましい。また、アルデヒド基を有する化合物（ｃ）としては、例えば、ホルムアルデヒド、ホルマリン、パラホルムアルデヒド等が挙げられる。   The pH of the reaction system is preferably about 1 to 10. After reaction of a polycondensate (phenol resin) of a phenol derivative and a compound having an aldehyde group with a triazine derivative and a compound having an aldehyde group, the unreacted phenol derivative, the compound having an aldehyde group, water, etc. are heated under reduced pressure. The conditions are preferably that the temperature is 80 to 180 ° C., the pressure is 100 mmHg or less, desirably 60 mmHg or less, and the time is 0.5 to 10 hours. The triazine derivative used for the synthesis is not particularly limited as long as it is a compound having a triazine nucleus in the molecule, and examples thereof include guanamine derivatives such as melamine, benzoguanamine and acetoguanamine, cyanuric acid derivatives such as cyanuric acid and methyl cyanurate, Only one type or a combination of two or more types is possible. Of these, guanamine derivatives such as melamine and benzoguanamine are preferable from the viewpoints of moldability and reliability. Moreover, as a compound (c) which has an aldehyde group, formaldehyde, formalin, paraformaldehyde, etc. are mentioned, for example.

また本発明ではケイ素含有重合物を含有してもよい。ケイ素含有重合物としては下記の結合（ｃ）及び（ｄ）を有し、末端がＲ^１、水酸基及びアルコキシ基から選ばれた官能基であり、エポキシ当量が５００〜４０００であれば特に制限はないが、このような重合物として例えば分岐状ポリシロキサンなどが挙げられる。 In the present invention, a silicon-containing polymer may be contained. The silicon-containing polymer has the following bonds (c) and (d), the terminal is a functional group selected from R ¹ , a hydroxyl group and an alkoxy group, and the epoxy equivalent is 500 to 4000. There is no such polymer, but examples include branched polysiloxane.

（ここで、Ｒ^１は炭素数１〜１２の置換または非置換の１価の炭化水素基から選ばれ、ケイ素含有重合物中の全Ｒ^１はすべてが同一でも異なっていてもよい。Ｘはエポキシ基を含む１価の有機基を示す。）

(Here, R ¹ is selected from substituted or unsubstituted monovalent hydrocarbon groups having 1 to 12 carbon atoms, and all R ¹ in the silicon-containing polymer may be the same or different. X is Indicates a monovalent organic group containing an epoxy group.)

上記一般式（ｃ）及び（ｄ）中のＲ^１としてはメチル基、エチル基、プロピル基、ブチル基、イソプロピル基、イソブチル基、ｔ−ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、２−エチルヘキシル基等のアルキル基、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基等のアルケニル基、フェニル基、トリル基、キシリル基、ナフチル基、ビフェニル基等のアリール基、ベンジル基、フェネチル基等のアラルキル基等が挙げられ、なかでもメチル基又はフェニル基が好ましい。 R ¹ in the general formulas (c) and (d) is a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, an isobutyl group, a t-butyl group, a pentyl group, a hexyl group, a heptyl group, or an octyl group. , Alkyl groups such as 2-ethylhexyl group, alkenyl groups such as vinyl group, allyl group, butenyl group, pentenyl group, hexenyl group, phenyl group, tolyl group, xylyl group, naphthyl group, biphenyl group, benzyl group And an aralkyl group such as a phenethyl group. Among them, a methyl group or a phenyl group is preferable.

また、上記一般式（ｃ）中のＸとしては２，３−エポキシプロピル基、３，４−エポキシブチル基、４，５−エポキシペンチル基、２−グリシドキシエチル基、３−グリシドキシプロピル基、４−グリシドキシブチル基、２−（３，４−エポキシシクロヘキシル）エチル基、３−（３，４−エポキシシクロヘキシル）プロピル基等が挙げられ、中でも３−グリシドキシプロピル基が好ましい。   X in the general formula (c) is 2,3-epoxypropyl group, 3,4-epoxybutyl group, 4,5-epoxypentyl group, 2-glycidoxyethyl group, 3-glycidoxy Propyl group, 4-glycidoxybutyl group, 2- (3,4-epoxycyclohexyl) ethyl group, 3- (3,4-epoxycyclohexyl) propyl group and the like, among which 3-glycidoxypropyl group is mentioned. preferable.

また、ケイ素含有重合物の末端は重合物の保存安定性の点から前述のＲ^１、水酸基及びアルコキシ基のいずれかである必要がある。この場合のアルコキシ基としては、メトキシ基、エトキシ基、プロプキシ基、ブトキシ基が挙げられる。さらに、ケイ素含有重合物のエポキシ当量は、５００〜４０００の範囲であることが必要であり、好ましくは１０００〜２５００である。５００より小さいと封止用エポキシ樹脂組成物の流動性が低下する傾向にあり、４０００より大きいと硬化物表面に染み出しやすく、成形不良を起こし易い傾向にある。ケイ素含有重合物はさらに下記の結合（ｅ）を有することが得られる封止用エポキシ樹脂組成物の流動性と低反り性の両立の観点から好ましい。 Further, the terminal of the silicon-containing polymer needs to be any one of the aforementioned R ¹ , hydroxyl group and alkoxy group from the viewpoint of storage stability of the polymer. In this case, examples of the alkoxy group include a methoxy group, an ethoxy group, a propoxy group, and a butoxy group. Furthermore, the epoxy equivalent of the silicon-containing polymer is required to be in the range of 500 to 4000, preferably 1000 to 2500. If it is less than 500, the fluidity of the epoxy resin composition for sealing tends to decrease, and if it is more than 4000, it tends to ooze out on the surface of the cured product and tends to cause molding defects. The silicon-containing polymer is further preferable from the viewpoint of coexistence of fluidity and low warpage of the sealing epoxy resin composition obtained to have the following bond (e).

（ここで、Ｒ^１はケイ素含有重合物中の全Ｒ^１に対して炭素数１〜１２の置換又は非置換の１価の炭化水素基から選ばれ、ケイ素含有重合物中の全Ｒ^１はすべてが同一でも異なっていてもよい。）

(Here, R ¹ is selected from substituted or unsubstituted monovalent hydrocarbon groups having 1 to 12 carbon atoms with respect to all R ¹ in the silicon-containing polymer, and all R ¹ in the silicon-containing polymer is All may be the same or different.)

上記一般式（ｅ）中のＲ^１としてはメチル基、エチル基、プロピル基、ブチル基、イソプロピル基、イソブチル基、ｔ−ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、２−エチルヘキシル基等のアルキル基、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基等のアルケニル基、フェニル基、トリル基、キシリル基、ナフチル基、ビフェニル基等のアリール基、ベンジル基、フェネチル基等のアラルキル基等が挙げられ、なかでもメチル基またはフェニル基が好ましい。 R ¹ in the general formula (e) is methyl, ethyl, propyl, butyl, isopropyl, isobutyl, t-butyl, pentyl, hexyl, heptyl, octyl, 2-ethylhexyl. Alkyl groups such as vinyl groups, vinyl groups, allyl groups, butenyl groups, pentenyl groups, hexenyl groups and other alkenyl groups, phenyl groups, tolyl groups, xylyl groups, naphthyl groups, biphenyl groups and other aryl groups, benzyl groups, phenethyl groups, etc. And a methyl group or a phenyl group is preferable.

このようなケイ素含有重合物の軟化点は４０℃〜１２０℃に設定されることが好ましく、５０℃〜１００℃に設定されることがより好ましい。４０℃より低いと得られる封止用エポキシ樹脂組成物の硬化物の機械強度が低下する傾向にあり、１２０℃より高いと封止用エポキシ樹脂組成物中へのケイ素含有重合物の分散性が低下する傾向にある。ケイ素含有重合物の軟化点を調整する方法としては、ケイ素含有重合物の分子量、構成結合単位（例えば（ｃ）〜（ｅ）含有比率等）、ケイ素原子に結合する有機基の種類を設定することで可能であるが、特に封止用エポキシ樹脂組成物へのケイ素含有重合物の分散性及び得られる封止用エポキシ樹脂組成物の流動性の観点からケイ素含有重合物中のアリール基の含有量を設定して軟化点を調整することが好ましい。この場合のアリール基とは、フェニル基、トリル基、キシリル基、ナフチル基、ビフェニル基等が挙げられ、フェニル基がより好ましい。ケイ素含有重合物中のケイ素原子に結合した一価の有機基中のフェニル基の含有量を６０モル％〜９９モル％、好ましくは７０モル％〜８５モル％に設定することで所望の軟化点を有するケイ素含有重合物を得ることができる。   The softening point of such a silicon-containing polymer is preferably set to 40 ° C to 120 ° C, and more preferably set to 50 ° C to 100 ° C. When the temperature is lower than 40 ° C., the mechanical strength of the cured epoxy resin composition obtained tends to decrease. When the temperature is higher than 120 ° C., the dispersibility of the silicon-containing polymer in the epoxy resin composition for sealing is low. It tends to decrease. As a method for adjusting the softening point of the silicon-containing polymer, the molecular weight of the silicon-containing polymer, the constituent bond units (for example, (c) to (e) content ratio, etc.), and the type of organic group bonded to the silicon atom are set. In view of the dispersibility of the silicon-containing polymer in the epoxy resin composition for sealing and the fluidity of the resulting epoxy resin composition for sealing, the inclusion of aryl groups in the silicon-containing polymer It is preferable to adjust the softening point by setting the amount. Examples of the aryl group in this case include a phenyl group, a tolyl group, a xylyl group, a naphthyl group, and a biphenyl group, and a phenyl group is more preferable. The desired softening point is set by setting the content of the phenyl group in the monovalent organic group bonded to the silicon atom in the silicon-containing polymer to 60 mol% to 99 mol%, preferably 70 mol% to 85 mol%. A silicon-containing polymer having the following can be obtained.

ケイ素含有重合物の重量平均分子量（Ｍｗ）は、ゲルパーミュエーションクロマトグラフィー（ＧＰＣ）で測定し標準ポリスチレン検量線を用いて換算した値で、１０００〜３００００、好ましくは２０００〜２００００、さらに好ましくは３０００〜１００００である。また。ケイ素含有重合物は、ランダム共重合体であることが好ましい。   The weight average molecular weight (Mw) of the silicon-containing polymer is a value measured by gel permeation chromatography (GPC) and converted using a standard polystyrene calibration curve, and is 1000 to 30000, preferably 2000 to 20000, more preferably. 3000 to 10000. Also. The silicon-containing polymer is preferably a random copolymer.

このようなケイ素含有重合物は以下に示す製造方法により得ることができるが、市販品としては東レ・ダウコーニング・シリコーン株式会社製商品名ＡＹ４２−１１９として入手可能である。   Such a silicon-containing polymer can be obtained by the production method shown below, but a commercially available product is available under the trade name AY42-119 manufactured by Toray Dow Corning Silicone Co., Ltd.

ケイ素含有重合物の製造方法は、特に制限なく公知の方法で製造することができる。例えば、加水分解縮合反応により上記（ｃ）〜（ｅ）単位を形成し得るオルガノクロロシラン、オルガノアルコキシシラン、シロキサン、あるいはそれらの部分加水分解縮合物を原料及び反応生成物を溶解可能な有機溶剤と原料のすべての加水分解性基を加水分解可能な量の水との混合溶液中に混合し、加水分解縮合反応させて得ることができる。この際、封止用エポキシ樹脂組成物中に不純物として含有される塩素量を低減させるためにオルガノアルコキシシラン及び／またはシロキサンを原料とすることが好ましい。この場合、反応を促進する触媒として、酸、塩基、有機金属化合物を添加することが好ましい。   The production method of the silicon-containing polymer can be produced by a known method without any particular limitation. For example, organochlorosilane, organoalkoxysilane, siloxane, or their partial hydrolysis-condensation products that can form the above units (c) to (e) by a hydrolysis-condensation reaction, and an organic solvent capable of dissolving raw materials and reaction products It can be obtained by mixing all the hydrolyzable groups of the raw material in a mixed solution with a hydrolyzable amount of water and subjecting it to a hydrolytic condensation reaction. At this time, in order to reduce the amount of chlorine contained as an impurity in the epoxy resin composition for sealing, organoalkoxysilane and / or siloxane is preferably used as a raw material. In this case, it is preferable to add an acid, a base, or an organometallic compound as a catalyst for promoting the reaction.

（Ａ）ケイ素含有重合物の原料となるオルガノアルコキシシラン及び／またはシロキサンとしては、メチルトリメトキシシラン、メチルトリエトキシシラン、エチルトリメトキシシラン、エチルトリエトキシシラン、ビニルトリメトキシシラン、ビニルトリエトキシシラン、フェニルトリメトキシシラン、フェニルトエトキシシラン、ジメチルジメトキシシラン、メチルフェニルジメトキシシラン、メチルビニルジメトキシシラン、フェニルビニルジメトキシシラン、ジフェニルジメトキシシラン、メチルフェニルジエトキシシラン、メチルビニルジエトキシシラン、フェニルビニルジエトキシシラン、ジフェニルジエトキシシラン、ジメチルジエトキシシラン、テトラメトキシシラン、テトラエトキシシラン、ジメトキシジエトキシシラン、３−グリシドキシプロピルトリメトキシシラン、３−グリシドキシプロピルトリエトキシシラン、３−グリシドキシプロピル（メチル）ジメトキシシラン、３−グリシドキシプロピル（メチル）ジエトキシシラン、３−グリシドキシプロピル（フェニル）ジメトキシシラン、３−グリシドキシプロピル（フェニル）ジエトキシシラン、２−（３，４−エポキシシクロヘキシル）エチル（メチル）ジメトキシシラン、２−（３，４−エポキシシクロヘキシル）エチル（メチル）ジエトキシシラン、２−（３，４−エポキシシクロヘキシル）エチル（フェニル）ジメトキシシラン、２−（３，４−エポキシシクロヘキシル）エチル（フェニル）ジエトキシシラン、およびこれらの加水分解縮合物等が挙げられる。   (A) The organoalkoxysilane and / or siloxane used as a raw material for the silicon-containing polymer are methyltrimethoxysilane, methyltriethoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane. , Phenyltrimethoxysilane, phenyltoethoxysilane, dimethyldimethoxysilane, methylphenyldimethoxysilane, methylvinyldimethoxysilane, phenylvinyldimethoxysilane, diphenyldimethoxysilane, methylphenyldiethoxysilane, methylvinyldiethoxysilane, phenylvinyldiethoxy Silane, diphenyldiethoxysilane, dimethyldiethoxysilane, tetramethoxysilane, tetraethoxysilane, dimethoxydiethoxysilane 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropyl (methyl) dimethoxysilane, 3-glycidoxypropyl (methyl) diethoxysilane, 3-glycidoxy Propyl (phenyl) dimethoxysilane, 3-glycidoxypropyl (phenyl) diethoxysilane, 2- (3,4-epoxycyclohexyl) ethyl (methyl) dimethoxysilane, 2- (3,4-epoxycyclohexyl) ethyl (methyl) ) Diethoxysilane, 2- (3,4-epoxycyclohexyl) ethyl (phenyl) dimethoxysilane, 2- (3,4-epoxycyclohexyl) ethyl (phenyl) diethoxysilane, and their hydrolysis condensates. It is done.

ケイ素含有重合物の含有量は封止用エポキシ樹脂組成物全体の０．２重量％〜１．５重量％が好ましく、０．３重量％〜１．３重量％がさらに好ましい。０．２重量％より少ないと（Ａ）ケイ素含有重合物の添加効果が見られず、１．５重量％より多いと得られる封止用エポキシ樹脂組成物の熱時硬度が低下する傾向にある。   The content of the silicon-containing polymer is preferably 0.2% by weight to 1.5% by weight, and more preferably 0.3% by weight to 1.3% by weight, based on the entire epoxy resin composition for sealing. When the amount is less than 0.2% by weight, the effect of addition of the (A) silicon-containing polymer is not observed, and when the amount is more than 1.5% by weight, the hot hardness of the resulting epoxy resin composition for sealing tends to decrease. .

また、本発明では必要に応じて下記組成式（ＸＸＸＸＸＸ）で表される化合物及び／又は下記組成式（ＸＸＸＸＸＸＩ）で表される化合物をＩＣ等の半導体素子の耐湿性及び高温放置特性を向上させる観点から含有することができる。   In addition, in the present invention, the compound represented by the following composition formula (XXXXXXX) and / or the compound represented by the following composition formula (XXXXXXI) is improved as necessary in the moisture resistance and high-temperature storage characteristics of a semiconductor element such as an IC. It can be contained from the viewpoint.

（０＜Ｘ≦０．５、ｍは正の数）

(0 <X ≦ 0.5, m is a positive number)

（０．９≦ｘ≦１．１ ０．６≦ｙ≦０．８ ０．２≦ｚ≦０．４）

(0.9 ≦ x ≦ 1.1 0.6 ≦ y ≦ 0.8 0.2 ≦ z ≦ 0.4)

なお、上記式（ＸＸＸＸＸＸ）の化合物は市販品として協和化学工業株式会社製商品名ＤＨＴ−４Ａとして入手可能である。また、上記式（ＸＸＸＸＸＸＩ）の化合物は市販品として東亜合成株式会社製商品名ＩＸＥ５００として入手可能である。また必要に応じてその他の陰イオン交換体を添加することもできる。陰イオン交換体としては特に制限はなく、従来公知のものを用いることができるが、たとえば、マグネシウム、アルミニウム、チタン、ジルコニウム、アンチモン等から選ばれる元素の含水酸化物等が挙げられ、これらを単独又は２種以上を組み合わせて用いることができる。   In addition, the compound of the said formula (XXXXXXX) is available as a commercial item as Kyowa Chemical Industry Co., Ltd. brand name DHT-4A. In addition, the compound of the above formula (XXXXXXI) is commercially available as trade name IXE500 manufactured by Toa Gosei Co., Ltd. Further, other anion exchangers can be added as necessary. The anion exchanger is not particularly limited, and conventionally known anion exchangers can be used. Examples thereof include hydrated oxides of elements selected from magnesium, aluminum, titanium, zirconium, antimony, and the like. Alternatively, two or more kinds can be used in combination.

さらに、本発明の封止用エポキシ樹脂組成物には、その他の添加剤として、高級脂肪酸、高級脂肪酸金属塩、エステル系ワックス、ポリオレフィン系ワックス、ポリエチレン、酸化ポリエチレン等の離型剤、カーボンブラック等の着色剤、シリコーンオイルやシリコーンゴム粉末等の応力緩和剤などを必要に応じて配合することができる。   Furthermore, in the sealing epoxy resin composition of the present invention, as other additives, higher fatty acids, higher fatty acid metal salts, ester waxes, polyolefin waxes, polyethylene, release agents such as polyethylene oxide, carbon black, etc. If necessary, a color relaxation agent such as silicone oil or silicone rubber powder can be added.

本発明の封止用エポキシ樹脂組成物は、難燃性の観点から（Ａ）エポキシ樹脂と（Ｂ）硬化剤を予め溶融混合して用いることが好ましい。溶融混合する方法は特に制限は無いが、両者あるいは一方が溶融する温度以上に加熱して、攪拌し、均一になるまで混合する。この際、ゲル化しないよう、ＧＰＣ（ゲルパーミエーションクロマトグラフィー）、ＦＴ−ＩＲ等を使用して反応性を確認し、最適な条件を設定することが好ましい。（Ａ）エポキシ樹脂として上記一般式（Ｉ）の化合物を、（Ｂ）硬化剤として上記一般式（ＩＩ）の化合物を使用する際は８０〜１２０℃、好ましくは９０〜１２０℃で１０〜６０分、好ましくは２０〜４０分攪拌溶融混合することが好ましい。   The sealing epoxy resin composition of the present invention is preferably used by previously melt-mixing (A) an epoxy resin and (B) a curing agent from the viewpoint of flame retardancy. The method of melt mixing is not particularly limited, but it is heated to a temperature at which both or one of them is melted, stirred and mixed until uniform. At this time, it is preferable to set the optimum conditions by confirming the reactivity using GPC (gel permeation chromatography), FT-IR or the like so as not to gel. (A) When using the compound of the said general formula (I) as an epoxy resin, and (B) the compound of the said general formula (II) as a hardening | curing agent, 80-120 degreeC, Preferably it is 10-60 at 90-120 degreeC. Minutes, preferably 20 to 40 minutes.

本発明の封止用エポキシ樹脂組成物は、各種原材料を均一に分散混合できるのであれば、いかなる手法を用いても調製できるが、一般的な手法として、所定の配合量の原材料をミキサー等によって十分混合した後、ミキシングロール、押出機、らいかい機、プラネタリミキサ等によって混合又は溶融混練した後、冷却し、必要に応じて脱泡、粉砕する方法等を挙げることができる。また、必要に応じて成形条件に合うような寸法及び重量でタブレット化してもよい。   The epoxy resin composition for sealing of the present invention can be prepared by any method as long as various raw materials can be uniformly dispersed and mixed. As a general method, a raw material having a predetermined blending amount is mixed with a mixer or the like. Examples thereof include a method of mixing or melt-kneading with a mixing roll, an extruder, a raking machine, a planetary mixer and the like after sufficiently mixing, cooling, and defoaming and pulverizing as necessary. Moreover, you may tablet into the dimension and weight which meet molding conditions as needed.

本発明の封止用エポキシ樹脂組成物を封止材として用いて、半導体装置等の電子部品装置を封止する方法としては、低圧トランスファ成形法が最も一般的であるが、インジェクション成形法、圧縮成形法等も挙げられる。ディスペンス方式、注型方式、印刷方式等を用いてもよい。   As a method for sealing an electronic component device such as a semiconductor device using the sealing epoxy resin composition of the present invention as a sealing material, the low pressure transfer molding method is the most common, but the injection molding method, compression A molding method etc. are also mentioned. A dispensing method, a casting method, a printing method, or the like may be used.

本発明で得られる封止用エポキシ樹脂組成物により封止した素子を備えた本発明の電子部品装置としては、リードフレーム、配線済みのテープキャリア、配線板、ガラス、シリコンウエハ等の支持部材や実装基板に、半導体チップ、トランジスタ、ダイオード、サイリスタ等の能動素子、コンデンサ、抵抗体、コイル等の受動素子等の素子を搭載し、必要な部分を本発明の封止用エポキシ樹脂組成物で封止した、電子部品装置等が挙げられる。   As an electronic component device of the present invention provided with an element sealed with the epoxy resin composition for sealing obtained in the present invention, a lead frame, a wired tape carrier, a wiring board, glass, a support member such as a silicon wafer, An active element such as a semiconductor chip, a transistor, a diode, or a thyristor, or a passive element such as a capacitor, resistor, or coil is mounted on the mounting substrate, and necessary portions are sealed with the epoxy resin composition for sealing of the present invention. An electronic component device or the like that has stopped.

ここで、実装基板としては特に制限するものではなく、たとえば、有機基板、有機フィルム、セラミック基板、ガラス基板等のインターポーザ基板、液晶用ガラス基板、ＭＣＭ（Ｍｕｌｔｉ Ｃｈｉｐ Ｍｏｄｕｌｅ）用基板、ハイブリットＩＣ用基板等が挙げられる。   Here, the mounting substrate is not particularly limited. For example, an organic substrate, an organic film, a ceramic substrate, an interposer substrate such as a glass substrate, a liquid crystal glass substrate, an MCM (Multi Chip Module) substrate, and a hybrid IC substrate. Etc.

このような素子を備えた電子部品装置としては、たとえば半導体装置が挙げられ、具体的には、リードフレーム（アイランド、タブ）上に半導体チップ等の素子を固定し、ボンディングパッド等の素子の端子部とリード部をワイヤボンディングやバンプで接続した後、本発明の封止用エポキシ樹脂組成物を用いてトランスファ成形などにより封止してなる、ＤＩＰ（Ｄｕａｌ Ｉｎｌｉｎｅ Ｐａｃｋａｇｅ）、ＰＬＣＣ（Ｐｌａｓｔｉｃ Ｌｅａｄｅｄ Ｃｈｉｐ Ｃａｒｒｉｅｒ）、ＱＦＰ（Ｑｕａｄ Ｆｌａｔ Ｐａｃｋａｇｅ）、ＳＯＰ（Ｓｍａｌｌ Ｏｕｔｌｉｎｅ Ｐａｃｋａｇｅ）、ＳＯＪ（Ｓｍａｌｌ Ｏｕｔｌｉｎｅ Ｊ−ｌｅａｄ ｐａｃｋａｇｅ）、ＴＳＯＰ（Ｔｈｉｎ Ｓｍａｌｌ Ｏｕｔｌｉｎｅ Ｐａｃｋａｇｅ）、ＴＱＦＰ（Ｔｈｉｎ Ｑｕａｄ Ｆｌａｔ Ｐａｃｋａｇｅ）等の樹脂封止型ＩＣ、テープキャリアにリードボンディングした半導体チップを、本発明の封止用エポキシ樹脂組成物で封止したＴＣＰ（Ｔａｐｅ Ｃａｒｒｉｅｒ Ｐａｃｋａｇｅ）、配線板やガラス上に形成した配線に、ワイヤボンディング、フリップチップボンディング、はんだ等で接続した半導体チップを、本発明の封止用エポキシ樹脂組成物で封止したＣＯＢ（Ｃｈｉｐ Ｏｎ Ｂｏａｒｄ）、ＣＯＧ（Ｃｈｉｐ Ｏｎ Ｇｌａｓｓ）等のベアチップ実装した半導体装置、配線板やガラス上に形成した配線に、ワイヤボンディング、フリップチップボンディング、はんだ等で接続した半導体チップ、トランジスタ、ダイオード、サイリスタ等の能動素子及び／又はコンデンサ、抵抗体、コイル等の受動素子を、本発明の封止用エポキシ樹脂組成物で封止したハイブリッドＩＣ、ＭＣＭ（Ｍｕｌｔｉ Ｃｈｉｐ Ｍｏｄｕｌｅ）マザーボード接続用の端子を形成したインターポーザ基板に半導体チップを搭載し、バンプまたはワイヤボンディングにより半導体チップとインターポーザ基板に形成された配線を接続した後、本発明の封止用エポキシ樹脂組成物で半導体チップ搭載側を封止したＢＧＡ（Ｂａｌｌ Ｇｒｉｄ Ａｒｒａｙ）、ＣＳＰ（Ｃｈｉｐ Ｓｉｚｅ Ｐａｃｋａｇｅ）、ＭＣＰ（Ｍｕｌｔｉ Ｃｈｉｐ Ｐａｃｋａｇｅ）などが挙げられる。また、これらの半導体装置は、実装基板上に素子が２個以上重なった形で搭載されたスタックド（積層）型パッケージであっても、２個以上の素子を一度に封止用エポキシ樹脂組成物で封止した一括モールド型パッケージであってもよい。   An example of an electronic component device provided with such an element is a semiconductor device. Specifically, an element such as a semiconductor chip is fixed on a lead frame (island, tab) and a terminal of an element such as a bonding pad. The lead part and the lead part are connected by wire bonding or bump, and then sealed by transfer molding using the sealing epoxy resin composition of the present invention, DIP (Dual Inline Package), PLCC (Plastic Leaded Chip Carrier). ), QFP (Quad Flat Package), SOP (Small Outline Package), SOJ (Small Outline J-lead package), TSOP (Thin Small Outline Package), TQ TCP (Tape Carrier Package), a wiring board or glass in which a semiconductor chip lead-bonded to a resin carrier type IC such as P (Thin Quad Flat Package) or a tape carrier is sealed with the epoxy resin composition for sealing of the present invention COB (Chip On Board), COG (Chip On Glass), in which a semiconductor chip connected to the wiring formed above by wire bonding, flip chip bonding, solder or the like is sealed with the sealing epoxy resin composition of the present invention. Active devices such as semiconductor chips, transistors, diodes, thyristors and / or capacitors, resistors connected to semiconductor devices mounted on bare chips, etc., wiring formed on wiring boards and glass, wire bonding, flip chip bonding, solder, etc. A semiconductor chip is mounted on an interposer substrate on which a hybrid IC in which a passive element such as a body and a coil is sealed with the sealing epoxy resin composition of the present invention and a terminal for connecting an MCM (Multi Chip Module) motherboard is formed, and bumps Alternatively, after connecting the semiconductor chip and the wiring formed on the interposer substrate by wire bonding, the semiconductor chip mounting side is sealed with the sealing epoxy resin composition of the present invention, BGA (Ball Grid Array), CSP (Chip Size Package) ), MCP (Multi Chip Package), and the like. In addition, even if these semiconductor devices are stacked type packages in which two or more elements are stacked on a mounting substrate, the epoxy resin composition for sealing two or more elements at a time It may be a batch mold type package sealed with.

次に実施例により本発明を説明するが、本発明の範囲はこれらの実施例に限定されるものではない。
（実施例１〜２８、比較例１〜１０）
エポキシ樹脂として、エポキシ当量１９０、軟化点６５℃のｏ−クレゾールノボラック型エポキシ樹脂（東都化成株式会社製商品名ＹＤＣＮ−５００）（エポキシ樹脂１）、エポキシ当量１９６、融点１０６℃のビフェニル型エポキシ樹脂（ジャパンエポキシレジン株式会社製商品名エピコートＹＸ−４０００Ｈ）（エポキシ樹脂２）、エポキシ当量２４５、融点１１０℃の硫黄原子含有エポキシ樹脂（東都化成株式会社製商品名ＹＳＬＶ−１２０ＴＥ）（エポキシ樹脂３）、エポキシ当量２７３、軟化点５８℃のビフェニレン型エポキシ樹脂（日本化薬株式会社製商品名ＮＣ−３０００）（エポキシ樹脂４）及びエポキシ当量３１６、軟化点７２℃の一般式（Ｉ）で示され、ｍが２である化合物（東都化成株式会社製商品名ＥＮＰ−８０）（エポキシ樹脂５）、硬化剤として水酸基当量２１９、軟化点８０℃の一般式（Ｉ）で示され、ｍが２である化合物（東都化成株式会社製商品名ＮＰ−８０）（硬化剤１）、軟化点８０℃、水酸基当量１０６のフェノールノボラック樹脂（明和化成株式会社製商品名Ｈ−１）（硬化剤２）、軟化点７０℃、水酸基当量１７５のフェノール・アラルキル樹脂（三井化学株式会社製商品名ミレックスＸＬＣ−３Ｌ）（硬化剤３）及び軟化点８０℃、水酸基当量１９９のビフェニレン型フェノール樹脂（明和化成株式会社製商品名ＭＥＨ−７８５１）（硬化剤４）、硬化促進剤としてトリフェニルホスフィン（硬化促進剤１）、トリフェニルホスフィンと１，４−ベンゾキノンの付加物（硬化促進剤２）、カップリング剤としてγ−グリシドキシプロピルトリメトキシシラン（エポキシシラン）、２級アミノ基を含有するシランカップリング剤（γ−アニリノプロピルトリメトキシシラン）（アニリノシラン）、難燃剤として芳香族縮合リン酸エステル（大八化学製商品名ＰＸ−２００）、トリフェニルホスフィンオキサイド、シクロホスファゼン（大塚化学株式会社製商品名ＳＰＥ−１００）、水酸化マグネシウム・水酸化亜鉛固溶体複合金属水酸化物（タテホ化学工業株式会社製商品名エコーマグＺ−１０）、三酸化アンチモン及びエポキシ当量３９７、軟化点６９℃、臭素含量４９質量％のビスフェノールＡ型臭素化エポキシ樹脂（東都化成株式会社製ＹＤＢ−４００）、無機充填剤として平均粒径１４．５μｍ、比表面積２．８ｍ^２／ｇの球状溶融シリカ、その他の添加剤としてカルナバワックス（クラリアント社製）及びカーボンブラック（三菱化学株式会社製商品名ＭＡ−１００）をそれぞれ表１〜表４に示す質量部で配合し、混練温度８０℃、混練時間１０分の条件でロール混練を行い、実施例１〜２８、比較例１〜１０を作製した。なお表中の空欄は配合無しを表す。 EXAMPLES Next, although an Example demonstrates this invention, the scope of the present invention is not limited to these Examples.
(Examples 1-28, Comparative Examples 1-10)
As an epoxy resin, an epoxy equivalent of 190 and an o-cresol novolac type epoxy resin having a softening point of 65 ° C. (trade name YDCN-500 manufactured by Toto Kasei Co., Ltd.) (epoxy resin 1), an epoxy equivalent of 196 and a biphenyl type epoxy resin having a melting point of 106 ° C. (Trade name Epicoat YX-4000H manufactured by Japan Epoxy Resin Co., Ltd.) (epoxy resin 2), epoxy equivalent 245, sulfur atom-containing epoxy resin having a melting point of 110 ° C. (trade name YSLV-120TE manufactured by Toto Kasei Co., Ltd.) (epoxy resin 3) , Epoxy equivalent 273, biphenylene type epoxy resin having a softening point of 58 ° C. (Nippon Kayaku Co., Ltd., trade name NC-3000) (epoxy resin 4) and epoxy equivalent 316 having a softening point of 72 ° C. , Compound wherein m is 2 (trade name ENP-80 manufactured by Toto Kasei Co., Ltd.) Epoxy resin 5), a compound represented by general formula (I) having a hydroxyl group equivalent of 219 and a softening point of 80 ° C. as a curing agent, and m is 2 (trade name NP-80 manufactured by Toto Kasei Co., Ltd.) (curing agent 1), Phenol novolak resin having a softening point of 80 ° C. and a hydroxyl equivalent weight of 106 (product name H-1 manufactured by Meiwa Kasei Co., Ltd.) (curing agent 2), phenol aralkyl resin having a softening point of 70 ° C. and a hydroxyl equivalent weight of 175 (product of Mitsui Chemicals, Inc.) Name Millex XLC-3L) (curing agent 3), biphenylene type phenol resin having a softening point of 80 ° C. and a hydroxyl group equivalent of 199 (trade name MEH-7851 manufactured by Meiwa Kasei Co., Ltd.) (curing agent 4), and triphenylphosphine as a curing accelerator (Curing Accelerator 1), adduct of triphenylphosphine and 1,4-benzoquinone (Curing Accelerator 2), and γ-glycidoxypro as a coupling agent Pyrtrimethoxysilane (epoxysilane), secondary amino group-containing silane coupling agent (γ-anilinopropyltrimethoxysilane) (anilinosilane), aromatic condensed phosphate ester as a flame retardant (trade name, manufactured by Daihachi Chemical) PX-200), triphenylphosphine oxide, cyclophosphazene (trade name SPE-100, manufactured by Otsuka Chemical Co., Ltd.), magnesium hydroxide / zinc hydroxide solid solution composite metal hydroxide (trade name Echo Mag Z-, manufactured by Tateho Chemical Industry Co., Ltd.) 10), antimony trioxide and epoxy equivalent 397, softening point 69 ° C., bisphenol A brominated epoxy resin having a bromine content of 49% by mass (YDB-400 manufactured by Tohto Kasei Co., Ltd.), average particle size 14.5 μm as an inorganic filler spherical fused silica having a specific surface area of 2.8 m ² / g, mosquitoes as other additives Nava wax (manufactured by Clariant) and carbon black (trade name MA-100, manufactured by Mitsubishi Chemical Corporation) are blended in parts by mass shown in Tables 1 to 4, respectively, and roll kneaded at a kneading temperature of 80 ° C. and a kneading time of 10 minutes. And Examples 1 to 28 and Comparative Examples 1 to 10 were produced. Note that the blank in the table indicates no blending.

作製した実施例１〜２８、比較例１〜１０の封止用エポキシ樹脂組成物の特性を、次の各試験により求めた。結果を表５〜表８に示す。
（１）スパイラルフロー
ＥＭＭＩ−１−６６に準じたスパイラルフロー測定用金型を用いて、封止用エポキシ樹脂組成物をトランスファ成形機により、金型温度１８０℃、成形圧力６．９ＭＰａ、硬化時間９０秒の条件で成形し、流動距離（ｃｍ）を求めた。 The characteristics of the produced epoxy resin compositions for sealing of Examples 1 to 28 and Comparative Examples 1 to 10 were determined by the following tests. The results are shown in Tables 5-8.
(1) Spiral flow Using a spiral flow measurement mold in accordance with EMMI-1-66, a sealing epoxy resin composition was molded by a transfer molding machine at a mold temperature of 180 ° C., a molding pressure of 6.9 MPa, and a curing time. Molding was performed for 90 seconds, and the flow distance (cm) was determined.

（２）熱時硬度
封止用エポキシ樹脂組成物を上記（１）の成形条件で直径５０ｍｍ×厚さ３ｍｍの円板に成形し、成形後直ちにショアＤ型硬度計を用いて測定した。 (2) Hardness upon heating The sealing epoxy resin composition was molded into a disc having a diameter of 50 mm and a thickness of 3 mm under the molding conditions of (1), and measured immediately after molding using a Shore D hardness meter.

（３）難燃性
厚さ１／１６インチの試験片を成形する金型を用いて、封止用エポキシ樹脂組成物を上記（１）の成形条件で成形して、さらに１８０℃で５時間後硬化を行い、ＵＬ−９４試験法に従って難燃性を評価した。 (3) Flame retardancy Using a mold for molding a test piece having a thickness of 1/16 inch, the epoxy resin composition for sealing was molded under the molding conditions of (1) above, and further at 180 ° C. for 5 hours. Post-curing was performed and flame retardancy was evaluated according to the UL-94 test method.

（４）耐リフロー性
８ｍｍ×１０ｍｍ×０．４ｍｍのシリコンチップを搭載した外形寸法２０ｍｍ×１４ｍｍ×２ｍｍの８０ピンフラットパッケージ（ＱＦＰ）（リードフレーム材質：銅合金、リード先端銀メッキ処理品）を、封止用エポキシ樹脂組成物を用いて上記（３）の条件で成形、後硬化して作製し、８５℃、８５％ＲＨの条件で加湿して所定時間毎に２４０℃、１０秒の条件でリフロー処理を行い、クラックの有無を観察し、試験パッケージ数（５個）に対するクラック発生パッケージ数で評価した。 (4) Reflow resistance An 80-pin flat package (QFP) (lead frame material: copper alloy, lead tip silver-plated product) with an external dimension of 20 mm x 14 mm x 2 mm mounted with an 8 mm x 10 mm x 0.4 mm silicon chip. Then, molding and post-curing using the epoxy resin composition for sealing under the conditions of (3) above, humidifying under conditions of 85 ° C. and 85% RH, and conditions of 240 ° C. and 10 seconds every predetermined time Then, reflow treatment was performed, the presence or absence of cracks was observed, and the number of crack generation packages with respect to the number of test packages (5) was evaluated.

（５）耐湿性
５μｍ厚の酸化膜上に線幅１０μｍ、厚さ１μｍのアルミ配線を施した６ｍｍ×６ｍｍ×０．４ｍｍのテスト用シリコンチップを搭載した外形寸法２０ｍｍ×１４ｍｍ×２．７ｍｍの８０ピンフラットパッケージ（ＱＦＰ）を、封止用エポキシ樹脂組成物を用いて上記（３）の条件で成形、後硬化して作製し、前処理を行った後、加湿して所定時間毎にアルミ配線腐食による断線不良を調べ、試験パッケージ数（１０個）に対する不良パッケージ数で評価した。 (5) Moisture resistance External dimensions of 20 mm x 14 mm x 2.7 mm mounted with a 6 mm x 6 mm x 0.4 mm test silicon chip on which an aluminum wiring with a line width of 10 µm and a thickness of 1 µm is mounted on a 5 µm thick oxide film An 80-pin flat package (QFP) is molded and post-cured using the epoxy resin composition for sealing under the above conditions (3), pre-treated, humidified, and aluminum is added every predetermined time. The disconnection failure due to wiring corrosion was examined, and the number of defective packages relative to the number of test packages (10) was evaluated.

なお、前処理は８５℃、８５％ＲＨ、７２時間の条件でフラットパッケージを加湿後、２１５℃、９０秒間のベーパーフェーズリフロー処理を行った。その後の加湿は０．２ＭＰａ、１２１℃の条件で行った。   In addition, after pre-humidifying the flat package on conditions of 85 degreeC and 85% RH for 72 hours, the vapor phase reflow process for 215 degreeC and 90 second was performed. Subsequent humidification was performed under conditions of 0.2 MPa and 121 ° C.

（６）高温放置特性
５μｍ厚の酸化膜上に線幅１０μｍ、厚さ１μｍのアルミ配線を施した５ｍｍ×９ｍｍ×０．４ｍｍのテスト用シリコンチップを、部分銀メッキを施した４２アロイのリードフレーム上に銀ペーストを用いて搭載し、サーモニック型ワイヤボンダにより、２００℃でチップのボンディングパッドとインナリードをＡｕ線にて接続した１６ピン型ＤＩＰ（Ｄｕａｌ Ｉｎｌｉｎｅ Ｐａｃｋａｇｅ）を、封止用エポキシ樹脂組成物を用いて上記（３）の条件で成形、後硬化して作製して、２００℃の高温槽中に保管し、所定時間毎に取り出して導通試験を行い、試験パッケージ数（１０個）に対する導通不良パッケージ数で、高温放置特性を評価した。 (6) High-temperature storage characteristics 42 mm lead made of 5 mm x 9 mm x 0.4 mm test silicon chip with aluminum wiring with line width of 10 μm and thickness of 1 μm on 5 μm thick oxide film, with partial silver plating A 16-pin DIP (Dual Inline Package), which is mounted on the frame using silver paste and connected to the chip's bonding pads and inner leads with Au wire at 200 ° C by a thermonic wire bonder, is used as an epoxy resin for sealing Molded and post-cured using the composition under the condition (3) above, stored in a high-temperature bath at 200 ° C., taken out every predetermined time, conducted a continuity test, and the number of test packages (10) The high temperature storage characteristics were evaluated based on the number of poorly conductive packages.

本発明の上記一般式（Ｉ）で示される化合物を配合していない比較例１〜５は難燃性に劣っており、ＵＬ−９４ Ｖ−０を達成していない。また上記一般式（Ｉ）で示される化合物を配合せず、各種難燃剤を配合した比較例６〜１０の内、比較例７〜９は耐湿性が劣っている。また比較例１０は流動性に劣っている。さらに比較例６はＶ−０を達成しているものの、高温放置特性が劣っている。   The comparative examples 1-5 which are not mix | blending the compound shown by the said general formula (I) of this invention are inferior in a flame retardance, and have not achieved UL-94 V-0. Moreover, the comparative examples 7-9 are inferior in moisture resistance among the comparative examples 6-10 which mix | blended the compound shown by the said general formula (I), and mix | blended various flame retardants. Further, Comparative Example 10 is inferior in fluidity. Further, although Comparative Example 6 achieved V-0, the high-temperature storage characteristics were inferior.

これに対し、上記一般式（Ｉ）で示される化合物を含んだ実施例１〜２８は全てＵＬ−９４ Ｖ−０を達成し、難燃性が良好で、また成形性も良好である。さらには耐リフロー性に優れ、耐湿性及び高温放置といった信頼性にも優れている。

On the other hand, Examples 1 to 28 including the compound represented by the general formula (I) all achieve UL-94 V-0, have good flame retardancy and good moldability. Furthermore, it is excellent in reflow resistance, and is excellent in reliability such as moisture resistance and high temperature storage.

Claims (16)

（Ａ）エポキシ樹脂、（Ｂ）硬化剤を含有し、（Ｂ）硬化剤として（Ｃ）下記一般式（Ｉ）で示される化合物を含有する封止用エポキシ樹脂組成物。

（一般式（Ｉ）中のＲ^１は水素原子、水酸基、炭素数１〜８のアルキル基、炭素数１〜６のアルコキシ基から選ばれ、全てが同一でも異なっていてもよい。Ｒ^２、Ｒ^３は水素原子、炭素数１〜６のアルキル基から選ばれ、全てが同一でも異なっていてもよい。ｎは１〜２０の整数を示し、ｍは１〜３の整数を示す。） An epoxy resin composition for sealing containing (A) an epoxy resin, (B) a curing agent, and (B) a compound represented by the following general formula (I) as a curing agent.

(R ¹ in the general formula (I) is selected from a hydrogen atom, a hydroxyl group, an alkyl group having 1 to 8 carbon atoms, and an alkoxy group having 1 to 6 carbon atoms, all of which may be the same or different. R ² , R ³ is selected from a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, all of which may be the same or different, n represents an integer of 1 to 20, and m represents an integer of 1 to ^3. ) 一般式（Ｉ）で示される化合物（Ｃ）中のｍが、１または２である請求項１記載の封止用エポキシ樹脂組成物。   The epoxy resin composition for sealing according to claim 1, wherein m in the compound (C) represented by the general formula (I) is 1 or 2. （Ａ）エポキシ樹脂が、ビフェニル型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、スチルベン型エポキシ樹脂、硫黄原子含有エポキシ樹脂、ノボラック型エポキシ樹脂、ジシクロペンタジエン型エポキシ樹脂、ナフタレン型エポキシ樹脂、トリフェニルメタン型エポキシ樹脂、ビフェニレン型エポキシ樹脂及びナフトール・アラルキル型フェノール樹脂のうち少なくとも１種を含有する請求項１又は２記載の封止用エポキシ樹脂組成物。   (A) Epoxy resin is biphenyl type epoxy resin, bisphenol F type epoxy resin, stilbene type epoxy resin, sulfur atom-containing epoxy resin, novolac type epoxy resin, dicyclopentadiene type epoxy resin, naphthalene type epoxy resin, triphenylmethane type The epoxy resin composition for sealing according to claim 1 or 2, comprising at least one of an epoxy resin, a biphenylene type epoxy resin, and a naphthol / aralkyl type phenol resin. （Ｃ）一般式（Ｉ）で示される化合物を、（Ｂ）硬化剤中に４０〜１００質量％含む請求項１〜３いずれかに記載の封止用エポキシ樹脂組成物。   (C) The epoxy resin composition for sealing in any one of Claims 1-3 which contains 40-100 mass% of compounds shown by general formula (I) in (B) hardening | curing agent. （Ｃ）一般式（Ｉ）で示される化合物を、（Ｂ）硬化剤中に６０〜１００質量％含む請求項１〜３いずれかに記載の封止用エポキシ樹脂組成物。   (C) The epoxy resin composition for sealing in any one of Claims 1-3 which contains 60-100 mass% of compounds shown by general formula (I) in (B) hardening | curing agent. （Ｂ）硬化剤がビフェニル型フェノール樹脂、アラルキル型フェノール樹脂、ジシクロペンタジエン型フェノール樹脂、トリフェニルメタン型フェノール樹脂及びノボラック型フェノール樹脂のうち少なくとも１種を含有する請求項１〜５いずれかに記載の封止用エポキシ樹脂組成物。   (B) The curing agent contains at least one of biphenyl type phenolic resin, aralkyl type phenolic resin, dicyclopentadiene type phenolic resin, triphenylmethane type phenolic resin and novolac type phenolic resin. The epoxy resin composition for sealing as described. さらに（Ｄ）硬化促進剤を含有する請求項１〜６いずれかに記載の封止用エポキシ樹脂組成物。   Furthermore, the epoxy resin composition for sealing in any one of Claims 1-6 containing (D) hardening accelerator. （Ｄ）硬化促進剤がトリフェニルホスフィンである請求項７記載の封止用エポキシ樹脂組成物。   (D) The epoxy resin composition for sealing according to claim 7, wherein the curing accelerator is triphenylphosphine. （Ｄ）硬化促進剤が第三ホスフィン化合物とキノン化合物との付加物である請求項７記載の封止用エポキシ樹脂組成物。   The epoxy resin composition for sealing according to claim 7, wherein (D) the curing accelerator is an adduct of a third phosphine compound and a quinone compound. さらに（Ｅ）無機充填剤を含有する請求項１〜９いずれかに記載の封止用エポキシ樹脂組成物。   Furthermore, the epoxy resin composition for sealing in any one of Claims 1-9 containing (E) inorganic filler. （Ｅ）無機充填剤の含有量が、封止用エポキシ樹脂組成物中６０〜９５質量％である請求項１０記載の封止用エポキシ樹脂組成物。   (E) The epoxy resin composition for sealing according to claim 10, wherein the content of the inorganic filler is 60 to 95% by mass in the epoxy resin composition for sealing. （Ｅ）無機充填剤の含有量が、封止用エポキシ樹脂組成物中７０〜９０質量％である請求項１０記載の封止用エポキシ樹脂組成物。   (E) The epoxy resin composition for sealing according to claim 10, wherein the content of the inorganic filler is 70 to 90% by mass in the epoxy resin composition for sealing. さらに（Ｆ）カップリング剤を含有する請求項１〜１２いずれかに記載の封止用エポキシ樹脂組成物。   Furthermore, the epoxy resin composition for sealing in any one of Claims 1-12 containing a coupling agent (F). （Ｆ）カップリング剤が２級アミノ基を有するシランカップリング剤を含有する請求項１３記載の封止用エポキシ樹脂組成物。   The epoxy resin composition for sealing according to claim 13, wherein the coupling agent (F) contains a silane coupling agent having a secondary amino group. ２級アミノ基を有するシランカップリング剤が下記一般式（ＩＩ）で示される化合物を含有する請求項１４記載の封止用エポキシ樹脂組成物。

（ここで、Ｒ^１は水素原子、炭素数１〜６のアルキル基及び炭素数１〜２のアルコキシ基から選ばれ、Ｒ^２は炭素数１〜６のアルキル基及びフェニル基から選ばれ、Ｒ^３はメチル基又はエチル基を示し、ｎは１〜６の整数を示し、ｍは１〜３の整数を示す。） The epoxy resin composition for sealing according to claim 14, wherein the silane coupling agent having a secondary amino group contains a compound represented by the following general formula (II).

(Where R ¹ is selected from a hydrogen atom, an alkyl group having 1 to 6 carbon atoms and an alkoxy group having 1 to ² carbon atoms, R ² is selected from an alkyl group having 1 to 6 carbon atoms and a phenyl group; ³ represents a methyl group or an ethyl group, n represents an integer of 1 to 6, and m represents an integer of 1 to ^3. ) 請求項１〜１５のいずれかに記載の封止用エポキシ樹脂組成物で封止された素子を備えた電子部品装置。

The electronic component apparatus provided with the element sealed with the epoxy resin composition for sealing in any one of Claims 1-15.