JP2007051043A - Method for growing carbon nanotube, method for forming wiring, and wiring - Google Patents
Method for growing carbon nanotube, method for forming wiring, and wiring Download PDFInfo
- Publication number
- JP2007051043A JP2007051043A JP2005239065A JP2005239065A JP2007051043A JP 2007051043 A JP2007051043 A JP 2007051043A JP 2005239065 A JP2005239065 A JP 2005239065A JP 2005239065 A JP2005239065 A JP 2005239065A JP 2007051043 A JP2007051043 A JP 2007051043A
- Authority
- JP
- Japan
- Prior art keywords
- substrate
- carbon nanotube
- gas
- carbon
- nanotubes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、カーボンナノチューブの成長方法、カーボンナノチューブを用いた配線形成方法及びその形成方法により形成された配線に関する。 The present invention relates to a carbon nanotube growth method, a wiring formation method using carbon nanotubes, and a wiring formed by the formation method.
カーボンナノチューブ（以下、ナノチューブという）は、その高電流密度耐性、高熱伝導度、高機械強度という特性から、次世代電子デバイス材料として注目されている。このナノチューブの合成方法としては、アーク放電法やＣＶＤ法があげられ、特に、ＣＶＤ法により基板に対して垂直方向に成長させる技術は、種々提案されている。 Carbon nanotubes (hereinafter referred to as nanotubes) are attracting attention as next-generation electronic device materials because of their high current density resistance, high thermal conductivity, and high mechanical strength. Examples of the method for synthesizing the nanotube include an arc discharge method and a CVD method. In particular, various techniques for growing in a direction perpendicular to the substrate by the CVD method have been proposed.
しかし、配線材料やトランジスタなどのデバイス材料としてナノチューブを用いるためには、基板に対し水平方向に成長させる必要があり、このような水平方向にナノチューブを成長させる方法がいくつか提案されている。例えば、基板上に金属膜を形成してその表面を酸化させて触媒担持膜とし、さらにこの触媒担持膜上に触媒膜を形成して、この触媒膜からナノチューブを基板に対して水平方向に気相成長させる方法が開示されている（例えば、特許文献１参照）。
上記従来技術においては、成長したナノチューブは基板に対して水平に成長するがその方向性はランダムであるため、気相成長させる際に電界・磁界あるいは基板を回転させる際の遠心力などの外場を印加することによってその方向をそろなければならないという問題があった。また、触媒担持膜をパターニングする必要があり、製造プロセスが複雑で、製造コストが高いという問題もあった。 In the above prior art, the grown nanotube grows horizontally with respect to the substrate, but its directionality is random. Therefore, an external field such as an electric field / magnetic field or a centrifugal force when rotating the substrate is used for vapor phase growth. There was a problem that the direction had to be aligned by applying. In addition, it is necessary to pattern the catalyst-carrying film, and the manufacturing process is complicated and the manufacturing cost is high.
そこで、本発明の課題は、かかる従来技術の問題点を解決し、製造プロセスが簡単であって、基板に対し水平方向であってかつ所定の方向にナノチューブを成長させる方法を提供し、さらにこの方法を利用した配線形成方法及び配線を提供することにある。 Therefore, an object of the present invention is to solve the above-mentioned problems of the prior art, provide a method for growing nanotubes in a predetermined direction that is horizontal with respect to the substrate, with a simple manufacturing process. An object of the present invention is to provide a wiring forming method and a wiring using the method.
本発明のカーボンナノチューブの成長方法は、基板上に触媒源を設け、化学気相成長法により触媒源からカーボンナノチューブを基板面に対し水平に成長させる方法において、カーボンナノチューブを基板の表面の原子配列の方位に沿って成長させることを特徴とする。 The carbon nanotube growth method of the present invention is a method in which a catalyst source is provided on a substrate, and the carbon nanotubes are grown horizontally from the catalyst surface from the catalyst source by chemical vapor deposition. It grows along the azimuth | direction.
本発明によれば、基板の表面の原子配列の方位に沿ってナノチューブが成長するので、基板に対し水平方向の所定の方位に、成長したナノチューブの軸方向を揃えることができる。従って、外場を加えることなく、ナノチューブの成長方位を簡単に制御することができる。 According to the present invention, since nanotubes grow along the orientation of the atomic arrangement on the surface of the substrate, the axial direction of the grown nanotubes can be aligned in a predetermined orientation in the horizontal direction with respect to the substrate. Therefore, the growth direction of the nanotube can be easily controlled without adding an external field.
前記基板の少なくとも表面は、所定の対称性の結晶方位を有することが好ましい。このような材料を用いれば、ナノチューブが結晶方位に沿って成長しやすいからである。 It is preferable that at least the surface of the substrate has a predetermined symmetrical crystal orientation. This is because the use of such a material makes it easy for the nanotubes to grow along the crystal orientation.
前記所定の対称性の結晶方位を有する基板は、シリコンまたはガリウム砒素等の半導体、マグネシア又はサファイアからなることが好ましい。 The substrate having the predetermined symmetric crystal orientation is preferably made of a semiconductor such as silicon or gallium arsenide, magnesia or sapphire.
前記基板は、配線形成上、（１００）面又は（１１１）面を有することが好ましい。 The substrate preferably has a (100) plane or a (111) plane in terms of wiring formation.
また、前記基板の表面が、この表面に配置された金属原子によって形成された原子配列、又は、表面に形成された溝や構造物の原子配列を有している場合には、カーボンナノチューブをこれらの原子配列の方位に沿って成長させることも可能である。 Further, when the surface of the substrate has an atomic arrangement formed by metal atoms arranged on the surface, or an atomic arrangement of grooves or structures formed on the surface, the carbon nanotubes are It is also possible to grow along the orientation of the atomic arrangement.
前記化学気相成長法に用いるガスは、原料ガスとしての炭素原子含有ガスと還元ガスとしてのＨ２ガス又はアンモニアガスのいずれか一種のガスとからなることを特徴とする。 The gas used in the chemical vapor deposition method is characterized by comprising a carbon atom-containing gas as a source gas and any one of H 2 gas and ammonia gas as a reducing gas.
この炭素原子含有ガスは、ＣＯガス、ＣＯ２ガス、炭化水素及びアルコール類から選ばれた少なくとも一種のガスであることが好ましい。炭化水素は、飽和炭化水素又は不飽和炭化水素であることが好ましく、飽和炭化水素としてはメタン、不飽和炭化水素としてはエチレン又はアセチレンのいずれかが好ましい。 The carbon atom-containing gas is preferably at least one gas selected from CO gas, CO 2 gas, hydrocarbons and alcohols. The hydrocarbon is preferably a saturated hydrocarbon or an unsaturated hydrocarbon. The saturated hydrocarbon is preferably methane, and the unsaturated hydrocarbon is preferably ethylene or acetylene.
これらのＣＯガス又はＣＯ２ガスの濃度は、２０〜９５vol％であることが好ましい。２０vol％未満である場合には、触媒源からナノチューブが十分に成長できず、９５vol％より大きいと、ガスが自己分解しにくくなるからである。 The concentration of these CO gas or CO 2 gas is preferably 20 to 95 vol%. This is because when the amount is less than 20 vol%, the nanotubes cannot be sufficiently grown from the catalyst source, and when it is greater than 95 vol%, the gas is difficult to self-decompose.
炭化水素の濃度は、２〜２０vol％であることが好ましい。２vol％未満である場合、触媒源からナノチューブが十分に成長できず、２０vol％より大きいとナノチューブ形成装置の内壁がダメージを受けやすくなってしまうからである。 The concentration of the hydrocarbon is preferably 2 to 20 vol%. This is because when the amount is less than 2 vol%, the nanotubes cannot be sufficiently grown from the catalyst source, and when the amount is greater than 20 vol%, the inner wall of the nanotube forming device is easily damaged.
前記化学気相成長法における基板温度は、７００〜１２００℃であることが望ましい。７００℃未満であると、ナノチューブの結晶性が悪くなり、かつ、多層ナノチューブが混在しやすくなるからである。また、１２００℃より高いと、原料ガスが直接分解されて、基板上にアモルファス状のカーボンが混在するからである。 The substrate temperature in the chemical vapor deposition method is preferably 700 to 1200 ° C. This is because if it is lower than 700 ° C., the crystallinity of the nanotubes deteriorates and multi-walled nanotubes are likely to be mixed. Further, when the temperature is higher than 1200 ° C., the raw material gas is directly decomposed, and amorphous carbon is mixed on the substrate.
また、本発明のカーボンナノチューブの成長方法は、基板上に複数の触媒源を基板の原子配列の方位に沿って間隔を空けて設け、上記したカーボンナノチューブの成長方法によってカーボンナノチューブを各触媒源から基板の原子配列の方位に沿って成長させ、隣接する触媒源間をカーボンナノチューブで接続することを特徴とする。 In the carbon nanotube growth method of the present invention, a plurality of catalyst sources are provided on the substrate at intervals along the orientation of the atomic arrangement of the substrate, and the carbon nanotubes are separated from each catalyst source by the carbon nanotube growth method described above. It grows along the orientation of the atomic arrangement of the substrate, and the adjacent catalyst sources are connected by carbon nanotubes.
本発明の配線形成方法は、基板上に触媒源としての複数の電極層を基板の原子配列の方位に間隔を空けて設けて、上記したカーボンナノチューブの成長方法によってカーボンナノチューブを各電極層から基板の原子配列の方位に沿って成長させ、隣接する電極層をカーボンナノチューブで接続することを特徴とする。 In the wiring formation method of the present invention, a plurality of electrode layers as catalyst sources are provided on a substrate at intervals in the direction of the atomic arrangement of the substrate, and the carbon nanotubes are separated from each electrode layer by the above-described carbon nanotube growth method. And the adjacent electrode layers are connected by carbon nanotubes.
さらに、本発明のカーボンナノチューブの別の成長方法は、基板上に触媒源と無機化合物層とを基板の原子配列の方位に沿って間隔を空けて設けて、上記したカーボンナノチューブの成長方法によってカーボンナノチューブを電極層から無機化合物層に向かって基板の原子配列の方位に沿って成長させて、無機化合物層にてカーボンナノチューブの成長をとめることを特徴とする。 Furthermore, another growth method of the carbon nanotube of the present invention is a method in which a catalyst source and an inorganic compound layer are provided on a substrate at an interval along the orientation of the atomic arrangement of the substrate. The nanotube is grown from the electrode layer toward the inorganic compound layer along the orientation of the atomic arrangement of the substrate, and the growth of the carbon nanotube is stopped in the inorganic compound layer.
本発明の配線形成方法は、基板上に触媒源としての電極層と無機化合物層とを基板の原子配列に沿って間隔を空けて設けて、上記したカーボンナノチューブの成長方法によってカーボンナノチューブを電極層から無機化合物層に向かって基板の原子配列に沿って成長させて、無機化合物層にてその成長をとめて配線の終端とすることを特徴とする。 In the wiring forming method of the present invention, an electrode layer serving as a catalyst source and an inorganic compound layer are provided on a substrate at intervals along the atomic arrangement of the substrate, and the carbon nanotube is formed into an electrode layer by the carbon nanotube growth method described above. It grows along the atomic arrangement of the substrate from the substrate toward the inorganic compound layer, and the growth is stopped at the inorganic compound layer to be the end of the wiring.
前記無機化合物層は、金属、合金、炭素のいずれかからなることが好ましい。また、この無機化合物層は、カーボンナノチューブを吸収して炭化物となる金属からなることが好ましい。 The inorganic compound layer is preferably made of any of metal, alloy, and carbon. Moreover, it is preferable that this inorganic compound layer consists of the metal which absorbs a carbon nanotube and becomes a carbide | carbonized_material.
また、本発明の配線は、上記した配線形成方法により形成されたことを特徴とする。 The wiring of the present invention is formed by the above-described wiring forming method.
本発明のナノチューブの成長方法によれば、簡単な製造プロセスでナノチューブの成長方向を制御できるという効果を奏し、この方法により成長したナノチューブを用いて基板に直接ナノチューブを配線することが可能となる。 According to the nanotube growth method of the present invention, it is possible to control the nanotube growth direction with a simple manufacturing process, and the nanotubes grown by this method can be directly wired to the substrate.
本発明のナノチューブの成長方法について、図１を用いて説明する。 The nanotube growth method of the present invention will be described with reference to FIG.
図１（ａ）によれば、１は基板であり、この基板上に触媒源２を形成する。基板１は、所定の対称性の結晶方位を有する材料からなる。 According to FIG. 1A, reference numeral 1 denotes a substrate, on which a catalyst source 2 is formed. The substrate 1 is made of a material having a predetermined symmetric crystal orientation.
この材料としては、例えば、半導体、サファイア、マグネシア又は金属などが挙げられる。半導体としては、Ｓｉ、Ｇｅ、等のＩＶ族元素、ＧａＰ、ＧａＡｓ、ＩｎＰ、ＩｎＡｓ等のＩＩＩ−ＩＶ族化合物、ＺｎＳ、ＺｎＳｅ、ＺｎＴｅ、ＣｄＳ、ＣｄＳｅ、ＣｄＴｅのＩＩ−ＶＩ族化合物、ＰｂＳ、ＰｂＳｅ、ＰｂＴｅ等のＩＶ−ＶＩ族化合物等が挙げられ、好ましくはＳｉ、ＧａＡｓである。金属としては、ＣｒやＡｕがあげられる。また、基板１の表面のみがこれらの所定の対称性の結晶方位を有する材料からなるものであってもよい。 Examples of this material include a semiconductor, sapphire, magnesia, or metal. Examples of the semiconductor include group IV elements such as Si and Ge, group III-IV compounds such as GaP, GaAs, InP, and InAs, group II-VI compounds of ZnS, ZnSe, ZnTe, CdS, CdSe, and CdTe, PbS, and PbSe. IV-VI group compounds such as PbTe and the like, and Si and GaAs are preferable. Examples of the metal include Cr and Au. Further, only the surface of the substrate 1 may be made of a material having these predetermined symmetric crystal orientations.
この基板１は、触媒源を構成する金属又は合金と化学反応しないものであることが重要である。これは、化学反応が起こると、触媒源２の活性を失わせたり、触媒源を消滅させたりするからである。このような基板としては、例えば、ボロンドープされたシリコン基板、Ｃｒ等の単結晶を成長させたシリコン基板若しくは石英基板などが挙げられる。 It is important that the substrate 1 does not chemically react with the metal or alloy constituting the catalyst source. This is because when the chemical reaction occurs, the activity of the catalyst source 2 is lost or the catalyst source is extinguished. Examples of such a substrate include a boron-doped silicon substrate, a silicon substrate on which a single crystal such as Cr is grown, or a quartz substrate.
表面の結晶方位は、特に制限はないが、（１００）面や（１１１）面を有するものが配線形成上好ましい。 The crystal orientation of the surface is not particularly limited, but those having a (100) plane or a (111) plane are preferable for wiring formation.
触媒源２は、遷移金属からなり、特に、コバルト、鉄、ニッケルから選ばれた少なくとも１種の金属またはこれらの金属の少なくとも１種を含む合金からなることが好ましい。触媒源２の形状は、特に制限はなく、例えば、粒子状や、パターン化された膜状であってもよい。 The catalyst source 2 is preferably made of a transition metal, particularly at least one metal selected from cobalt, iron, and nickel, or an alloy containing at least one of these metals. The shape of the catalyst source 2 is not particularly limited, and may be, for example, a particle shape or a patterned film shape.
粒子状の場合、その粒子の直径は、１ｎｍ〜１０ｎｍであればよく、独立して散在していてもよい。ただし、単層ナノチューブを得るためには、その直径が２ｎｍ〜５ｎｍであることが好ましい。パターン化された膜状の触媒源である場合、膜の上面から成長したナノチューブは上面で綿状になってしまい基板に沿って成長することができず、膜の側面から成長したナノチューブが基板に沿って成長する。この側面から成長したナノチューブの直径は、膜厚によって決定されることから、膜の最大厚みが５０ｎｍで、その平均厚みが１〜５０ｎｍであることが好ましく、単層ナノチューブを得るためには１〜５ｎｍであることがより好ましい。５０ｎｍを超えると、アモルファスカーボンやカーボンファイバーが混在するからである。 In the case of particles, the diameter of the particles may be 1 nm to 10 nm, and may be scattered independently. However, in order to obtain single-walled nanotubes, the diameter is preferably 2 nm to 5 nm. In the case of a patterned film-like catalyst source, the nanotubes grown from the top surface of the film become flocculent on the top surface and cannot grow along the substrate, and the nanotubes grown from the side surface of the film grow on the substrate. Grow along. Since the diameter of the nanotube grown from this side is determined by the film thickness, the maximum thickness of the film is preferably 50 nm and the average thickness is preferably 1 to 50 nm. More preferably, it is 5 nm. This is because if it exceeds 50 nm, amorphous carbon and carbon fiber are mixed.
この触媒源２の形成方法は、特に制限されないが、例えば、真空蒸着法、デポジション法、スパッタ法などの公知の方法を用いることができる。 The method for forming the catalyst source 2 is not particularly limited, and known methods such as a vacuum deposition method, a deposition method, and a sputtering method can be used.
触媒源２を膜状に形成する場合、基板に沿う方向のみナノチューブを成長させるには、膜の上面にＣＶＤ法などの公知の方法でＣｒ等のマスクを形成するか、膜を矩形状等にパターニングする際に使用したレジストをそのまま残しておいてもよい。 When the catalyst source 2 is formed in a film shape, in order to grow nanotubes only in the direction along the substrate, a mask such as Cr is formed on the upper surface of the film by a known method such as a CVD method, or the film is formed in a rectangular shape or the like. The resist used for patterning may be left as it is.
上記した触媒源を形成した基板をＣＶＤ装置に搬送し、気相成長を開始する。 The substrate on which the above-described catalyst source is formed is transferred to a CVD apparatus, and vapor phase growth is started.
気相成長において、基板加熱温度は、７００〜１２００℃が好ましく、より好ましくは８００〜１０００℃である。また、このときのＣＶＤ装置内の圧力は、０．２Ｐａ〜大気圧であることが好ましく、より好ましくは大気圧である。 In vapor phase growth, the substrate heating temperature is preferably 700 to 1200 ° C, more preferably 800 to 1000 ° C. Moreover, it is preferable that the pressure in a CVD apparatus at this time is 0.2 Pa-atmospheric pressure, More preferably, it is atmospheric pressure.
原料ガスを導入して、ナノチューブ３を触媒源２から成長させる（図１(ｂ)参照）。原料ガスは、炭素原子を含むガス（例えば、一酸化炭素、二酸化炭素）、ＣＨ４のような炭化水素及びアルコール類のうちの少なくとも１種からなるガスであり、これを不活性ガスで希釈してもよい。この不活性ガスは、窒素ガスや、アルゴン等の希ガスから選ばれた少なくとも１種であればよい。炭化水素は、飽和炭化水素又は不飽和炭化水素であり、飽和炭化水素としては、メタンであることが好ましく、不飽和炭化水素としては、エチレン又はアセチレンであることが好ましい。 The raw material gas is introduced to grow the nanotube 3 from the catalyst source 2 (see FIG. 1B). The source gas is a gas composed of at least one of a gas containing carbon atoms (for example, carbon monoxide, carbon dioxide), a hydrocarbon such as CH 4 and an alcohol, and this is diluted with an inert gas. May be. The inert gas may be at least one selected from nitrogen gas and rare gases such as argon. The hydrocarbon is a saturated hydrocarbon or an unsaturated hydrocarbon. The saturated hydrocarbon is preferably methane, and the unsaturated hydrocarbon is preferably ethylene or acetylene.
また、還元ガスとして、例えばＨ２ガス又はアンモニアガスのいずれか一種のガスを使用することが好ましい。本発明では、炭素原子含有ガスとＨ２ガスとからなる混合ガス、例えば、ＣＯとＨ２ガス、ＣＨ４とＨ２ガスとからなる混合ガスを用いることが好ましく、特に、成長速度の制御が容易であることから、ＣＯとＨ２ガスからなる混合ガスが好ましい。そして、ＣＯとＨ２ガスの混合ガスからなる場合には、ＣＯガス又はＣＯ２の濃度は、２０vol％から９５vol％であり、好ましくは２５vol％〜９０vol％、さらに好ましくは７０vol％〜９０vol％である。また、ＣＨ４とＨ２ガスからなる混合ガスの場合には、ＣＨ４ガスの濃度は２vol％〜２０vol％が好ましい。 Further, as the reducing gas, for example, any one of H 2 gas and ammonia gas is preferably used. In the present invention, it is preferable to use a mixed gas composed of a carbon atom-containing gas and H 2 gas, for example, a mixed gas composed of CO and H 2 gas, or CH 4 and H 2 gas. because it is easy, a mixed gas consisting of CO and H 2 gas is preferable. When comprising a mixed gas of CO and H 2 gas, CO gas or CO 2 concentration is 95 vol% from 20 vol%, preferably 25vol% ~90vol%, more preferably at 70vol% ~90vol% is there. In the case of a mixed gas consisting of CH 4 and H 2 gas, the concentration of CH 4 gas is preferably 2vol% ~20vol%.
この原料ガスを流量５０〜２００ｓｃｃｍで２０〜６０分間導入しつづけて、低速度でナノチューブを成長させると、触媒源から触媒源のない基板上へ基板表面の原子配列の方位に沿って、軸方向を揃えながらナノチューブが成長する。この場合の低速度とは、１〜２０μｍ／ｍｉｎ以下、、好ましくは１−１０μｍ／ｍｉｎ以下、より好ましくは１〜３μｍ／ｍｉｎ以下である。２０μｍ／ｍｉｎを超えるとナノチューブが基板に沿って成長することができず、１μｍ／ｍｉｎ未満であると実用的ではないからである。 When this raw material gas is continuously introduced at a flow rate of 50 to 200 sccm for 20 to 60 minutes and nanotubes are grown at a low speed, an axial direction follows the orientation of the atomic arrangement on the substrate surface from the catalyst source onto the substrate without the catalyst source. Nanotubes grow while aligning. In this case, the low speed is 1 to 20 μm / min or less, preferably 1 to 10 μm / min or less, more preferably 1 to 3 μm / min or less. This is because if it exceeds 20 μm / min, nanotubes cannot grow along the substrate, and if it is less than 1 μm / min, it is not practical.
また、ナノチューブを成長させる前に、Ｈ２ガス等の還元ガスをＣＶＤ装置内に導入し、その還元ガス雰囲気中で、触媒源を設けた基板を圧力１〜２Ｐａ、温度４００〜８００℃で１０〜２０分間加熱し、前処理を行なってもよい。前処理を行なうことで、基板と触媒源とが活性化し、ナノチューブがより成長しやすくなるからである。 Further, before growing the nanotubes, a reducing gas such as H 2 gas is introduced into the CVD apparatus, and the substrate provided with the catalyst source in the reducing gas atmosphere is set at a pressure of 1 to 2 Pa and a temperature of 400 to 800 ° C. Pretreatment may be performed by heating for ~ 20 minutes. This is because by performing the pretreatment, the substrate and the catalyst source are activated, and the nanotubes are more easily grown.
前記触媒源２は、図２（ａ）に示すように、基板１上に所定の間隔をあけて原子配列の方位に沿って隣接して複数設けてもよい。なお、図２において図１と同じ構成要素については同じ参照符号をつけてある。このように触媒源２を設けた場合に、上記の条件下でナノチューブを気相成長させると、基板１の原子配列に沿って各触媒源からナノチューブ３が向かいあって成長するので（図２（ｂ）参照）、基板上で両ナノチューブが接続する（図２（ｃ）参照）。このように、本発明によれば各触媒源間をナノチューブで接続することができるので、この触媒源を電極層とすれば、電極層間を接続するナノチューブを配線として用いることが可能である。 As shown in FIG. 2A, a plurality of the catalyst sources 2 may be provided adjacent to each other along the orientation of the atomic arrangement on the substrate 1 at a predetermined interval. In FIG. 2, the same components as those in FIG. 1 are given the same reference numerals. When the catalyst source 2 is provided in this way, if the nanotubes are grown in a vapor phase under the above conditions, the nanotubes 3 grow from each catalyst source facing each other along the atomic arrangement of the substrate 1 (FIG. 2 ( b)), both nanotubes are connected on the substrate (see FIG. 2C). Thus, according to the present invention, the catalyst sources can be connected by nanotubes. If this catalyst source is an electrode layer, the nanotubes connecting the electrode layers can be used as wiring.
さらに、前記基板上にスパッタ法などの公知の方法で、無機化合物層を設けてナノチューブの成長を止めることもできる。図３（ａ）に示すように、触媒源２と無機化合物層４とを一定の距離を開けて基板１の原子配列の方位に沿って設け、触媒源からナノチューブ３を気相成長させる。なお、図３において図１と同じ構成要素については同じ参照符号をつけてある。 Furthermore, the growth of nanotubes can be stopped by providing an inorganic compound layer on the substrate by a known method such as sputtering. As shown in FIG. 3A, the catalyst source 2 and the inorganic compound layer 4 are provided along the orientation of the atomic arrangement of the substrate 1 with a certain distance therebetween, and the nanotubes 3 are vapor-grown from the catalyst source. In FIG. 3, the same components as those in FIG. 1 are given the same reference numerals.
ナノチューブ３を原子配列の方位に沿って上記した基板温度、成長速度等の条件下で気相成長させると、図３（ｂ）に示すように、無機化合物層４にぶつかってその成長がとまる。このように、触媒源と無機化合物層とを基板上に設ければ、触媒源を電極層とした場合に、電極層から成長した配線としてのナノチューブをこの無機化合物層で終端させることが可能である。この無機化合物層４としては、例えば、Ｗ、Ａｕなどの金属や、金属化合物（例えば、ＴｉＮやＴａＣ）、炭素からなる層であることが好ましい。また、無機化合物層４として、ナノチューブを吸収して炭化物化する金属、ＴａやＴｉを使用すれば、配線形成後にＣＶＤプロセスを実行してもナノチューブが必要以上に成長することはないので好ましい。 When the nanotube 3 is vapor-phase grown along the orientation of the atomic arrangement under the above-described conditions such as the substrate temperature and the growth rate, the nanotube 3 hits the inorganic compound layer 4 and stops growing as shown in FIG. As described above, when the catalyst source and the inorganic compound layer are provided on the substrate, when the catalyst source is an electrode layer, it is possible to terminate the nanotube as the wiring grown from the electrode layer with this inorganic compound layer. is there. The inorganic compound layer 4 is preferably a layer made of a metal such as W or Au, a metal compound (for example, TiN or TaC), or carbon. Further, it is preferable to use a metal such as Ta or Ti that absorbs and carbonizes nanotubes as the inorganic compound layer 4 because the nanotubes do not grow more than necessary even if a CVD process is performed after the wiring is formed.
なお、上記した本発明の実施形態では、ナノチューブの成長条件を最適化することによって、ナノチューブを触媒源から基板表面の原子配列の方位に沿って成長させたが、基板表面に金属原子を並べて、この金属原子に沿ってナノチューブを成長させることも可能である。例えば、基板上に公知の方法によってＡｕからなる金属原子を並べて金属原子列（幅１原子分〜数原子分）を作製する。なお、公知の方法としては、原子レベルの精度で原子をハンドリングできるＳＴＭやＡＦＭ等の装置によって原子を並べる方法、例えば、Ｍ．Ｆ．ＣｒｏｍｍｉｅらがＳｃｉｅｎｃｅ２６２、ｐ２１８−２２０（１９９３）にて開示しているＳＴＭによって銅面上に鉄原子を並べる方法が挙げられる。その後、スパッタ法等によって触媒源を金属原子列に沿ってナノチューブが成長するように形成し、上記した気相成長の条件下で、ナノチューブを金属原子列に沿って成長させることが可能である。この場合には、触媒源から金属原子列の方位に沿ってナノチューブが成長するので、基板や基板表面の原子配列が高い結晶方位を有する必要はない。また、この金属原子の代わりに、ナノスケールの溝や突起物を基板上に設けてもよい。この場合においても、上記の気相成長の要件を満たせば、溝や突起物等の構造物の原子配列の方位に沿って、ナノチューブを成長させることが可能である。 In the embodiment of the present invention described above, the nanotubes were grown from the catalyst source along the orientation of the atomic arrangement on the substrate surface by optimizing the growth conditions of the nanotubes. It is also possible to grow nanotubes along this metal atom. For example, metal atoms made of Au are arranged on a substrate by a known method to produce a metal atom string (for a width of 1 atom to several atoms). As a known method, a method of arranging atoms by an apparatus such as STM or AFM that can handle atoms with atomic level accuracy, for example, M.I. F. There is a method in which iron atoms are arranged on a copper surface by STM disclosed in Science 262, p218-220 (1993). Thereafter, the catalyst source is formed by sputtering or the like so that the nanotubes grow along the metal atom rows, and the nanotubes can be grown along the metal atom rows under the above-described conditions of vapor phase growth. In this case, since the nanotubes grow from the catalyst source along the orientation of the metal atom row, it is not necessary that the atomic arrangement on the substrate or the substrate surface has a high crystal orientation. Further, instead of this metal atom, a nanoscale groove or protrusion may be provided on the substrate. Even in this case, nanotubes can be grown along the orientation of the atomic arrangement of structures such as grooves and protrusions if the above-mentioned requirements for vapor phase growth are satisfied.
以下、実施例によって本発明を詳細に説明する。 Hereinafter, the present invention will be described in detail by way of examples.
本実施例では、原子が直交して配列されている（００１）面上に触媒源を設けて、この触媒源からナノチューブを基板に対し水平方向に成長させた状態を観察した。 In this example, a catalyst source was provided on the (001) plane in which atoms were orthogonally arranged, and a state where nanotubes were grown from the catalyst source in the horizontal direction with respect to the substrate was observed.
まず、片面研磨されたボロンドープのシリコン（００１）単結晶基板（縦２０ｍｍ×横２０ｍｍ×厚み０．７ｍｍ）の研磨面上に、触媒源としてのＦｅ粒子（直径２〜５ｎｍ）を真空蒸着によって散在させて形成した。この（００１）基板表面の原子配列の模式図を図４（ａ）に示す。図４(ａ)に示したように、（００１）面では、シリコン原子が＜１００＞及び＜０１０＞方位に直交して配列している。 First, Fe particles (diameter: 2 to 5 nm) as a catalyst source are scattered on a polished surface of a single-side polished boron-doped silicon (001) single crystal substrate (length 20 mm × width 20 mm × thickness 0.7 mm) by vacuum deposition. Formed. A schematic diagram of the atomic arrangement on the surface of the (001) substrate is shown in FIG. As shown in FIG. 4A, on the (001) plane, silicon atoms are arranged orthogonal to the <100> and <010> orientations.
次いで、この基板を、ランプを熱源とする熱ＣＶＤ装置内の試料ホルダー上に載置した。この基板をＨ２ガス中で前処理を行った後、ＣＶＤ装置内を真空排気して圧力１Ｐａとし、ＣＯとＨ２とからなる混合ガス（混合割合は、ＣＯの割合が９０vol％）をＣＯ／Ｈ２＝９００／１００ｓｃｃｍの流量で導入して大気圧とした。その流量と圧力を維持したまま、１０分間で基板温度を９００℃まで昇温させ、ナノチューブを２０分間気相成長させた。その状態をＳＥＭで観察した。図４（ｂ）にそのＳＥＭ写真を示す。 Next, this substrate was placed on a sample holder in a thermal CVD apparatus using a lamp as a heat source. After pre-treating this substrate in H 2 gas, the inside of the CVD apparatus is evacuated to a pressure of 1 Pa, and a mixed gas composed of CO and H 2 (mixing ratio is 90 vol% of CO) is changed to CO. Introduced at a flow rate of / H 2 = 900/100 sccm to atmospheric pressure. While maintaining the flow rate and pressure, the substrate temperature was raised to 900 ° C. in 10 minutes, and the nanotubes were vapor grown for 20 minutes. The state was observed with SEM. FIG. 4B shows the SEM photograph.
図４（ｂ）に示すように、ナノチューブが、散在している触媒源から＜１００＞、＜０１０＞の各方位に軸方向を揃えて成長しており、点Ａでは２本のナノチューブが角度９０度で交差していた。この結果から、各触媒源からナノチューブが（００１）基板表面の原子配列の方位に沿って成長していたことが分かった。 As shown in FIG. 4 (b), nanotubes are grown from scattered catalyst sources with the axial directions aligned in the <100> and <010> directions, and at point A, the two nanotubes are angular Crossed at 90 degrees. From this result, it was found that nanotubes grew from each catalyst source along the orientation of the atomic arrangement on the (001) substrate surface.
本実施例では、（１１１）面上に触媒源を設け、この触媒源からナノチューブを基板に対し水平に成長させた状態を観察した。 In this example, a catalyst source was provided on the (111) plane, and a state was observed in which nanotubes were grown horizontally from the catalyst source with respect to the substrate.
片面研磨されたボロンドープのシリコン（１１１）単結晶基板（縦２０ｍｍ×横２０ｍｍ×厚み０．７ｍｍ）の研磨面上に、触媒源としてのＦｅ粒子（直径２〜５ｎｍ）を真空蒸着によって散在させて形成した。この（１１１）基板表面の原子配列の模式図を図５（ａ）に示す。図５（ａ）に示したように、（１１１）面では、シリコン原子は＜０１１＞、＜１０１＞、＜１１０＞の各方位に６０度の角度で配列している。 Fe particles (2-5 nm in diameter) as a catalyst source are scattered by vacuum deposition on a polished surface of a boron-doped silicon (111) single crystal substrate (vertical 20 mm × horizontal 20 mm × thickness 0.7 mm) polished on one side. Formed. A schematic diagram of the atomic arrangement on the (111) substrate surface is shown in FIG. As shown in FIG. 5A, on the (111) plane, silicon atoms are arranged at an angle of 60 degrees in each of <011>, <101>, and <110> orientations.
その後、実施例１と同様の方法でこの（１１１）基板上に触媒源からナノチューブを気相成長させ、その状態をＳＥＭで観察した。図５（ｂ）にそのＳＥＭ写真を示す。 Thereafter, nanotubes were vapor-phase grown from the catalyst source on this (111) substrate in the same manner as in Example 1, and the state was observed by SEM. FIG. 5B shows the SEM photograph.
図５（ｂ）によれば、ナノチューブが、散在している各触媒源から基板の原子配列の方位に沿って軸方向を揃えて成長しており、点Ａでは＜０１１＞、＜１０１＞、＜１１０＞の各方位に成長したナノチューブがそれぞれ６０度の角度で交わっていた。このことから、各ナノチューブが触媒源から（１１１）基板の原子配列の方位に成長していたことが分かった。 According to FIG. 5 (b), nanotubes are grown from each of the scattered catalyst sources with the axial direction aligned along the orientation of the atomic arrangement of the substrate, and at point A, <011>, <101>, The nanotubes grown in each <110> direction intersected at an angle of 60 degrees. From this, it was found that each nanotube grew from the catalyst source in the orientation of the atomic arrangement of the (111) substrate.
本実施例では、ナノチューブを気相成長させる際の炭素原子含有ガスの流量を変化することでナノチューブの成長速度を変化させ、その状態を観察した。 In this example, the growth rate of the nanotube was changed by changing the flow rate of the carbon atom-containing gas during the vapor phase growth of the nanotube, and the state was observed.
片面研磨されたボロンドープのシリコン（００１）単結晶基板（縦２０ｍｍ×横２０ｍｍ×厚み０．７ｍｍ）の研磨面上に、触媒源としてのＦｅ粒子（直径２〜５ｎｍ）を真空蒸着によって散在させて形成した。 Fe particles (diameter: 2 to 5 nm) as a catalyst source are dispersed by vacuum deposition on a polished surface of a single-side polished boron-doped silicon (001) single crystal substrate (vertical 20 mm × horizontal 20 mm × thickness 0.7 mm). Formed.
次いで、この基板を、ランプを熱源とする熱ＣＶＤ装置内の試料ホルダー上に載置した。この基板をＨ２ガス中で前処理を行った後、ＣＶＤ装置内を真空排気して圧力１Ｐａとし、ＣＯとＨ２とからなる混合ガス（混合割合は、ＣＯの割合が９０vol％）を成長速度を変更できるように流量を変化させて導入し、大気圧とした。その流量と圧力を維持したまま、１０分間で基板温度を９００℃まで昇温させ、ナノチューブを５〜２０分間気相成長させ、基板に沿って成長するかどうかをＳＥＭで観察した。 Next, this substrate was placed on a sample holder in a thermal CVD apparatus using a lamp as a heat source. After pre-treating this substrate in H 2 gas, the inside of the CVD apparatus is evacuated to a pressure of 1 Pa, and a mixed gas composed of CO and H 2 (mixing ratio is 90 vol% of CO) is grown. Introduced by changing the flow rate so that the speed could be changed to atmospheric pressure. While maintaining the flow rate and pressure, the substrate temperature was raised to 900 ° C. in 10 minutes, and the nanotubes were grown in a vapor phase for 5 to 20 minutes.
成長速度が１００μｍ／ｍｉｎである場合、ナノチューブを基板の結晶方位に沿って成長させることができなかった。成長速度が２０μｍ／ｍｉｎである場合には、散在した触媒源から＜１００＞、＜０１０＞の各方位に軸方向を揃えてナノチューブが成長しているものがいくつか確認できた。成長速度が１０μｍ／ｍｉｎである場合、ナノチューブは、散在している触媒源から＜１００＞、＜０１０＞の各方位に軸方向を揃えて成長しているものが多く、２本のナノチューブが角度９０度で交差しているものもあった。成長速度が３μｍ／ｍｉｎである場合、各ナノチューブが、散在している触媒源から＜１００＞、＜０１０＞の各方位に軸方向を揃えて成長しており、２本のナノチューブが角度９０度で交差しているものもあった。 When the growth rate was 100 μm / min, the nanotubes could not be grown along the crystal orientation of the substrate. When the growth rate was 20 μm / min, it was confirmed that some nanotubes were grown from the dispersed catalyst source with the axial directions aligned in the <100> and <010> directions. When the growth rate is 10 μm / min, the nanotubes are often grown from the scattered catalyst source with the axial direction aligned in the <100> and <010> directions, and the two nanotubes are angled. Some crossed at 90 degrees. When the growth rate is 3 μm / min, each nanotube grows from the scattered catalyst source in the <100> and <010> directions in the same axial direction, and the two nanotubes have an angle of 90 degrees. Some of them crossed.
これにより、結晶方位に沿って成長させるための成長速度は、２０μｍ／ｍｉｎ以下であり、好ましくは１０μｍ／ｍｉｎ以下、より好ましくは３μｍ／ｍｉｎ以下であることが分かった。 Thereby, it was found that the growth rate for growing along the crystal orientation is 20 μm / min or less, preferably 10 μm / min or less, more preferably 3 μm / min or less.
本実施例では、矩形状の触媒源からナノチューブを成長させてその状態を観察した。 In this example, nanotubes were grown from a rectangular catalyst source and the state was observed.
片面研磨されたボロンドープのシリコン（００１）単結晶基板（縦２０ｍｍ×横２０ｍｍ×厚み０．７ｍｍ）の研磨面上に、真空蒸着によって触媒源としてのＦｅ膜を形成した。この膜上にレジストを設けてパターニングし、縦３００μｍ×横５０μｍ×平均厚み５ｎｍのＦｅ層を基板の＜０１０＞方位に長手方向を沿わせるようにして形成した。パターニングする際に用いたレジストはそのまま残し、膜上面にナノチューブが成長しないようにした。 An Fe film as a catalyst source was formed by vacuum deposition on a polished surface of a boron-doped silicon (001) single crystal substrate (vertical 20 mm × horizontal 20 mm × thickness 0.7 mm) polished on one side. A resist was provided on this film and patterned, and an Fe layer having a length of 300 μm × width of 50 μm × average thickness of 5 nm was formed so that the longitudinal direction was along the <010> direction of the substrate. The resist used for patterning was left as it was so that nanotubes did not grow on the top surface of the film.
その後、実施例１と同様の方法で気相成長を行ったところ、ナノチューブは、触媒源の長手方向の側面の幅３００μｍに渡り、＜１００＞方位に軸方向を揃えて１０〜５０μｍの長さで成長した。これらのナノチューブをＳＥＭ及びＴＥＭで確認すると、全て単層ナノチューブであり、直径は１〜２ｎｍであった。 Thereafter, vapor phase growth was performed in the same manner as in Example 1. As a result, the nanotubes had a width of 300 μm on the side surface in the longitudinal direction of the catalyst source and a length of 10 to 50 μm with the axial direction aligned in the <100> direction. I grew up. When these nanotubes were confirmed by SEM and TEM, they were all single-walled nanotubes and had a diameter of 1 to 2 nm.
本実施例では、矩形状の触媒源を基板上に複数設けて、各触媒源からナノチューブが成長する様子を観察した。 In this example, a plurality of rectangular catalyst sources were provided on the substrate, and the growth of nanotubes from each catalyst source was observed.
片面研磨されたボロンドープのシリコン（００１）単結晶基板（縦２０ｍｍ×横２０ｍｍ×厚み０．７ｍｍ）の研磨面上に、真空蒸着によって触媒源としての複数のＦｅ膜を形成した。この膜上にレジストを設けてパターニングし、縦３００μｍ×横５０μｍ×平均厚み５ｎｍのＦｅ層を基板の＜０１０＞、＜１００＞の各方位に長手方向を沿わせるように間隔（５０μｍ）を空けて形成した。パターニングの際に用いたレジストはそのまま残し、膜上面にナノチューブが成長しないようにした。同じ方位に形成した触媒源はそれぞれ対向するように配置した。 A plurality of Fe films as a catalyst source were formed by vacuum deposition on a polished surface of a single-side polished boron-doped silicon (001) single crystal substrate (vertical 20 mm × horizontal 20 mm × thickness 0.7 mm). A resist is provided on this film for patterning, and an Fe layer having a length of 300 μm × width of 50 μm × average thickness of 5 nm is spaced apart (50 μm) so that the longitudinal direction is along each of the <010> and <100> directions of the substrate. Formed. The resist used for patterning was left as it was so that nanotubes did not grow on the top surface of the film. The catalyst sources formed in the same direction were arranged to face each other.
その後、実施例１と同様の方法で気相成長を行った（ただし、成長時間を６０分とした）ところ、ナノチューブは、＜１００＞、＜０１０＞方位に軸方向を揃えてそれぞれ５０〜１００μｍの長さで成長した。これらのナノチューブをＳＥＭ及びＴＥＭで確認すると、全て直径１〜２ｎｍの単層ナノチューブであった。また、対向している触媒源間のナノチューブが互いに接続されている状態も観察された。 Thereafter, vapor phase growth was performed in the same manner as in Example 1 (however, the growth time was set to 60 minutes), and the nanotubes were aligned in the <100> and <010> directions and the axial direction was 50 to 100 μm. Grew in length. When these nanotubes were confirmed by SEM and TEM, they were all single-walled nanotubes having a diameter of 1 to 2 nm. In addition, it was observed that the nanotubes between the facing catalyst sources were connected to each other.
本実施例では、基板上に触媒源と無機化合物からなる層とをそれぞれ設けて、触媒源からナノチューブが成長する状態を観察した。 In this example, a catalyst source and a layer made of an inorganic compound were provided on the substrate, and the state in which nanotubes grew from the catalyst source was observed.
片面研磨されたボロンドープのシリコン（００１）単結晶基板（縦２０ｍｍ×横２０ｍｍ×厚み０．７ｍｍ）の研磨面上に、膜を形成した。この膜上にレジストを設けてパターニングし、縦３００μｍ×横５０μｍ×平均厚み５ｎｍのＦｅ層を基板の＜１００＞方位に長手方向を沿わせて形成した。このＦｅ層と＜０１０＞方位の対向する場所に５０μｍ離してＷ層（縦３００μｍ×横５０μｍ×平均厚み５０ｎｍ）をスパッタ法で形成した。 A film was formed on a polished surface of a single-side polished boron-doped silicon (001) single crystal substrate (vertical 20 mm × horizontal 20 mm × thickness 0.7 mm). A resist was provided on this film and patterned to form a Fe layer having a length of 300 μm × width of 50 μm × average thickness of 5 nm along the <100> direction of the substrate along the longitudinal direction. A W layer (length 300 μm × width 50 μm × average thickness 50 nm) was formed by sputtering at a position 50 μm away from this Fe layer in a location facing the <010> orientation.
その後、実施例１と同様の方法で気相成長を行ったところ、ナノチューブは、触媒源から＜０１０＞方位に軸方向を揃えて幅３００μｍ、長さ５０μｍで成長して、Ｗ層に接触してその成長が止まっていた。これらのナノチューブもＳＥＭ及びＴＥＭで確認すると、直径１〜２ｎｍの単層ナノチューブであった。 Thereafter, vapor phase growth was performed in the same manner as in Example 1. As a result, the nanotubes grew from the catalyst source in the <010> direction with the axial direction aligned to a width of 300 μm and a length of 50 μm, and contacted the W layer. That growth has stopped. When these nanotubes were also confirmed by SEM and TEM, they were single-walled nanotubes having a diameter of 1 to 2 nm.
本発明のナノチューブの成長方法によれば、基板に対して水平方向にその軸方向を揃えてナノチューブを成長させることが可能であり、このナノチューブを用いて基板上に配線することが可能である。従って、本発明は半導体製造分野において利用できる。 According to the nanotube growth method of the present invention, it is possible to grow a nanotube with its axial direction aligned in the horizontal direction with respect to the substrate, and it is possible to wire on the substrate using this nanotube. Therefore, the present invention can be used in the field of semiconductor manufacturing.
１ 基板 ２ 触媒源 ３ ナノチューブ ４ 無機化合物層
DESCRIPTION OF SYMBOLS 1 Substrate 2 Catalyst source 3 Nanotube 4 Inorganic compound layer
Claims (23)