JP2006337593A - Polarizing plate - Google Patents
Polarizing plate Download PDFInfo
- Publication number
- JP2006337593A JP2006337593A JP2005160549A JP2005160549A JP2006337593A JP 2006337593 A JP2006337593 A JP 2006337593A JP 2005160549 A JP2005160549 A JP 2005160549A JP 2005160549 A JP2005160549 A JP 2005160549A JP 2006337593 A JP2006337593 A JP 2006337593A
- Authority
- JP
- Japan
- Prior art keywords
- amylose
- film
- polarizing plate
- dichroic dye
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、褪色しにくく、薄型でも充分な偏光性能を発揮でき、しかも保護フィルムを必要としない偏光板に関する。 The present invention relates to a polarizing plate that does not easily fade, can exhibit sufficient polarization performance even when it is thin, and does not require a protective film.
偏光板は、一定方向の偏波面の光だけを通す材料であり、液晶表示素子においては電界による液晶の配向の変化を可視化させる役割を有する重要な部材である。
液晶表示素子に用いられる偏光板としては、一般に、ポリビニルアルコール（ＰＶＡ）の水溶液を製膜し、これにヨウ素等の二色性染料を吸着させた後一軸延伸したものを偏光子としたものが用いられている（例えば、特許文献１等）。
The polarizing plate is a material that allows only light having a polarization plane in a certain direction to pass therethrough. In a liquid crystal display element, the polarizing plate is an important member having a role of visualizing a change in liquid crystal alignment due to an electric field.
As a polarizing plate used for a liquid crystal display element, generally, a polarizer is prepared by forming an aqueous solution of polyvinyl alcohol (PVA), adsorbing a dichroic dye such as iodine and then uniaxially stretching it. Used (for example, Patent Document 1).
しかしながら、ＰＶＡを用いた偏光子では、ヨウ素等の二色性染料とＰＶＡとの結合力が低く、高湿度下で加熱された場合に二色性染料が抜けて褪色し、偏光性能が低下することがあるという問題があった。また、一般にＰＶＡを用いた偏光子では、一定以上の厚さがなければ充分の偏光性能を発揮することができず、偏光板を薄型化することが困難であるという問題もあった。 However, in a polarizer using PVA, the binding force between a dichroic dye such as iodine and PVA is low, and when heated under high humidity, the dichroic dye is lost and faded, and the polarization performance is deteriorated. There was a problem that there was something. Further, in general, a polarizer using PVA has a problem that it is difficult to make a polarizing plate thin because a sufficient polarizing performance cannot be exhibited unless the thickness exceeds a certain value.
更に、ＰＶＡを用いた偏光板では、ＰＶＡが過乾燥して強度や柔軟性を失わないように、偏光子の少なくとも片面にトリアセチルセルロース等の保護フィルムを貼り合わせる必要があった。このような保護フィルムを貼り合わせる工程は煩雑なうえ、高温、高湿下で長時間放置されたときにＰＶＡが吸湿して、保護フィルムが剥離してしまうことがあるという問題があった。そこで、保護フィルムを必要としない偏光板が待望されていた。
本発明は、上記現状に鑑み、褪色しにくく、薄型でも充分な偏光性能を発揮でき、しかも保護フィルムを必要としない偏光板を提供することを目的とする。 An object of the present invention is to provide a polarizing plate that is difficult to fade, can exhibit sufficient polarization performance even in a thin shape, and does not require a protective film.
本発明は、重量平均分子量１５万〜１５００万、直線性の分子構造を有するアミロースを含有するフィルムを、二色性染料で染色してなる偏光板である。
以下の本発明を詳述する。
The present invention is a polarizing plate obtained by dyeing a film containing amylose having a weight average molecular weight of 150,000 to 15 million and a linear molecular structure with a dichroic dye.
The present invention is described in detail below.
アミロースは、アミロペクチンとともにデンプンを構成する成分として知られており、ブドウ糖が直鎖状に連結してなる高分子である。天然由来のアミロースは分子量分布が広く、また、分岐の多い分子構造であることから、強度等の諸性能の制御が困難であり、また、透明なフィルムが得られないという問題があった。 Amylose is known as a component constituting starch together with amylopectin, and is a polymer in which glucose is linked in a straight chain. Naturally derived amylose has a wide molecular weight distribution and a highly branched molecular structure, so that it is difficult to control various properties such as strength, and a transparent film cannot be obtained.
しかしながら、近年、酵素を用いてアミロースを合成する技術が開発され、この技術によれば、分子量の制御が容易で、しかも、分岐構造が少ない酵素合成アミロースを製造することができる。
本発明者らは、鋭意検討の結果、重量平均分子量が一定の範囲で、直線性の分子構造を有する酵素合成アミロースを含有するフィルムを二色性染料で染色してなるフィルムは、褪色しにくく、薄型でも充分な偏光性能を発揮でき、しかも保護フィルムを必要としないことから、偏光板として好適であることを見出し、本発明を完成するに至った。
これは、重量平均分子量が一定の範囲で、直線性の分子構造を有する酵素合成アミロースを用いれば、成膜が容易であり、かつ、得られたフィルムは極めて延伸性が高く配向しやすい性質を有すること、アミロースのらせん状の主骨格が二色性染料をらせん構造中に包接して二色性染料との高い結合性を発揮すること、ＰＶＡフィルムに比べて乾燥しても柔軟性が高く、保護フィルムで保護しなくても充分な強度を発揮できること等によると考えられる。
なお、本明細書において、直線性の分子構造を有するアミロースとは、らせん構造をなすブドウ糖が直鎖状に連結してなる主鎖を形成しており、分岐が少ないことを意味する。
However, in recent years, a technique for synthesizing amylose using an enzyme has been developed, and according to this technique, an enzyme-synthesized amylose that can be easily controlled in molecular weight and has few branched structures can be produced.
As a result of intensive studies, the present inventors have found that a film obtained by dyeing a film containing an enzymatically synthesized amylose having a linear molecular structure with a dichroic dye within a certain range of weight average molecular weight is less likely to fade. The present invention has been completed by finding that it is suitable as a polarizing plate because it can exhibit sufficient polarizing performance even in a thin shape and does not require a protective film.
This is because, when an enzyme-synthesized amylose having a linear molecular structure with a weight average molecular weight in a certain range is used, film formation is easy, and the obtained film has extremely high stretchability and is easily oriented. Having a helical main skeleton of amylose to include a dichroic dye in the helical structure and exhibiting high binding properties with the dichroic dye; high flexibility even when dried compared to a PVA film This is considered to be due to the fact that sufficient strength can be exhibited without protection with a protective film.
In the present specification, amylose having a linear molecular structure means that a main chain formed by linearly connecting glucose having a helical structure is formed, and there are few branches.
本発明の偏光板は、アミロースを含有するフィルム（以下、アミロースフィルムともいう）からなる。
上記アミロースは、重量平均分子量の下限が１５万、上限が１５００万である。１５万未満であると、低濃度でしか透明な溶液が得られず、濃度を上げた場合には、ゲルや粒子が含有し、透明度が確保できなくなる。１５００万を超えると、ゲル化が激しくなり、透明フィルムが得られなくなる（水等の媒体に溶解して溶液を調製することが困難となり、フィルムの製造が困難となる）。好ましい下限は５０万、好ましい上限は５００万である。なお、重量平均分子量の異なる複数のアミロースを併用してもよい。
The polarizing plate of the present invention comprises a film containing amylose (hereinafter also referred to as amylose film).
The lower limit of the weight average molecular weight of the amylose is 150,000, and the upper limit is 15 million. When the concentration is less than 150,000, a transparent solution can be obtained only at a low concentration. When the concentration is increased, gels and particles are contained, and transparency cannot be ensured. When it exceeds 15 million, gelation becomes intense and a transparent film cannot be obtained (dissolving in a medium such as water makes it difficult to prepare a solution, which makes it difficult to produce a film). A preferable lower limit is 500,000, and a preferable upper limit is 5 million. A plurality of amyloses having different weight average molecular weights may be used in combination.
このような一定の分子量を有し、直線性の分子構造を有するアミロースは、ブドウ糖を原料として、グルコースホスホリラーゼ及びグルカンホスホリラーゼの２種の酵素を作用させることにより製造することができる。 Amylose having such a constant molecular weight and a linear molecular structure can be produced by using glucose as a raw material and acting two enzymes, glucose phosphorylase and glucan phosphorylase.
上記アミロースは、化学的に変性されたものであってもよい。化学的に変性することにより、種々の性能を付与することができる。例えば、アミロースのＯＨ基の一部を光硬化性アクリル末端基に置換する変性を行った場合には、成膜後に光重合により架橋を施して、引張強度や表面の鉛筆硬度等の機械的な性能をより向上させることができる。
また、上記アミロースフィルムを成型後に、適当な架橋剤を作用させることによりアミロースに架橋を施してもよい。上記架橋剤としては特に限定されず、例えば、ホウ酸等が挙げられる。
The amylose may be chemically modified. Various performances can be imparted by chemical modification. For example, when modification is performed by substituting a part of the OH group of amylose with a photocurable acrylic end group, crosslinking is performed by photopolymerization after film formation, and mechanical strength such as tensile strength and surface pencil hardness is obtained. The performance can be further improved.
Further, after molding the amylose film, the amylose may be crosslinked by acting an appropriate crosslinking agent. The crosslinking agent is not particularly limited, and examples thereof include boric acid.
上記アミロースフィルムは、上記アミロースのみからなるものであってもよく、本発明の目的を阻害しない範囲において、アミロース以外の樹脂成分を併用するものであってもよい。このような他の樹脂成分を併用することにより、耐水性や耐候性等を付与したり、他の機能を付与したり、より安価に製造できるようにすることができる。例えば、ＰＶＡを併用した場合には、アミロースとの相溶性にも優れることから、光学性能等に影響することなく高い成型性等を付与することができる。その他、ＴＡＣ、ノルボルネン樹脂、ポリカーボネイト樹脂などが考えられるが、特に限定はされない。 The amylose film may be composed of only the amylose, or may be used in combination with a resin component other than amylose as long as the object of the present invention is not impaired. By using such other resin components in combination, water resistance, weather resistance, etc. can be imparted, other functions can be imparted, and the production can be made at a lower cost. For example, when PVA is used in combination, it is excellent in compatibility with amylose, so that high moldability and the like can be imparted without affecting optical performance and the like. In addition, TAC, norbornene resin, polycarbonate resin, and the like can be considered, but are not particularly limited.
上記アミロースフィルムは、本発明の目的を阻害しない範囲において、紫外線吸収剤、酸化防止剤、帯電防止剤等の従来公知の添加剤を含有してもよい。特に、本発明の偏光板を、トリアセチルセルロース等の保護フィルムと併用せずに用いる場合には、紫外線吸収剤は必須となる。
なお、上記添加剤を含有することにより配向性等が低下する恐れがある場合には、例えば、上記アミロースフィルムを２層構造とし、一方の層にのみ上記配合剤を配合するようにしてもよい。
The amylose film may contain conventionally known additives such as an ultraviolet absorber, an antioxidant, and an antistatic agent as long as the object of the present invention is not impaired. In particular, when the polarizing plate of the present invention is used without being used in combination with a protective film such as triacetyl cellulose, an ultraviolet absorber is essential.
In addition, when there exists a possibility that orientation etc. may fall by containing the said additive, the said amylose film may be made into 2 layer structure, for example, and you may make it mix | blend the said compounding agent only in one layer. .
上記アミロースフィルムを製造する方法としては特に限定されず、例えば、上記アミロースと必要に応じて添加する成分とを水、アルコール等の有機溶剤又はこれらの混合溶媒等に溶解して溶液を調製して、これを流延し、乾燥する方法等が挙げられる。特にアルコール等の有機溶剤を用いる場合には、乾燥に要する時間を短縮できる等の利点がある。 The method for producing the amylose film is not particularly limited. For example, a solution is prepared by dissolving the amylose and components to be added as necessary in water, an organic solvent such as alcohol, or a mixed solvent thereof. The method of casting this and drying is mentioned. In particular, when an organic solvent such as alcohol is used, there is an advantage that the time required for drying can be shortened.
上記アミロースフィルムは、延伸されたものであることが好ましい。延伸されることにより高い配向性が発現し、二色性染料と組み合わせることによって高い偏光性能を発揮できる。
上記延伸を行う場合の倍率としては特に限定されないが、好ましい下限は１．１倍である。１．１倍未満であると、充分な配向性が発現せずに充分な偏光性能が得られないことがある。上限については特に限定されないが、通常は４倍程度の延伸で充分な配向性が得られる。ただし、特に高い配向性が必要な場合は、４倍を超えて延伸してもよい。
The amylose film is preferably stretched. High orientation is exhibited by stretching, and high polarization performance can be exhibited by combining with a dichroic dye.
Although it does not specifically limit as a magnification in the case of performing the said extending | stretching, A preferable minimum is 1.1 times. If it is less than 1.1 times, sufficient orientation may not be exhibited and sufficient polarization performance may not be obtained. Although there is no particular limitation on the upper limit, sufficient orientation is usually obtained by stretching about 4 times. However, when particularly high orientation is required, the film may be stretched more than 4 times.
上記延伸の方法としては特に限定されず、例えば、未延伸のフィルムに加熱しながら応力を加える等の従来公知の方法を用いることができる。
また、本発明の偏光板が、後述するような支持体上に上記アミロースを含有する溶液を塗工、乾燥して、厚さ１〜１０μｍの薄膜を形成してなるである場合には、剪断をかけながら塗布を行う等の方法により配向を行うことも可能である。この場合、配向性を向上させるために、支持体の表面にラビング処理等を施していてもよい。
The stretching method is not particularly limited. For example, a conventionally known method such as applying stress to an unstretched film while heating can be used.
Further, when the polarizing plate of the present invention is formed by coating a solution containing the above amylose on a support as described later and drying to form a thin film having a thickness of 1 to 10 μm, shearing is performed. It is also possible to perform orientation by a method such as coating while applying. In this case, in order to improve the orientation, the surface of the support may be subjected to a rubbing treatment or the like.
上記アミロースフィルムは、プラズマ処理、コロナ処理等の表面改質処理が施されてもよい。このような表面改質処理を施すことにより、液晶表示素子を構成する他の部材との密着性を向上させることができる。 The amylose film may be subjected to surface modification treatment such as plasma treatment or corona treatment. By performing such a surface modification treatment, it is possible to improve adhesion with other members constituting the liquid crystal display element.
本発明の偏光板は、上記アミロースフィルムを二色性染料で染色してなるものである。二色性染料で染色することにより偏光性能を発揮できる。
上記二色性染料としては特に限定されないが、例えば、高い偏光性能を得やすいことからヨウ素が好適である。
The polarizing plate of the present invention is obtained by dyeing the amylose film with a dichroic dye. Polarizing performance can be exhibited by dyeing with a dichroic dye.
Although it does not specifically limit as said dichroic dye, For example, since a high polarization performance is easy to be obtained, an iodine is suitable.
上記アミロースフィルムを二色性染料で染色する方法としては特に限定されず、例えば、上記アミロースフィルムを、ヨウ素とヨウ化カリウムとを含有するヨウ素溶液槽に浸漬する方法（湿式法）；上記アミロースフィルムをヨウ素ガス中に置く方法（乾式法）等が挙げられる。
とりわけ乾式法は、従来のＰＶＡではできなかった方法であり、湿式法に比べて乾燥工程が不要になる等の利点がある。また、乾式法によれば、ガス種および処理雰囲気条件の制御により、含有されるヨウ素の各イオン長さの配合比を制御することが可能であり、得られる偏光板の波長依存性を低減させることができる。
The method for dyeing the amylose film with a dichroic dye is not particularly limited. For example, the method for immersing the amylose film in an iodine solution bath containing iodine and potassium iodide (wet method); And the like (the dry method) and the like are placed in iodine gas.
In particular, the dry method is a method that has not been possible with conventional PVA, and has the advantage that a drying step is not necessary as compared with the wet method. In addition, according to the dry method, it is possible to control the compounding ratio of each ion length of iodine contained by controlling the gas species and the processing atmosphere conditions, and reduce the wavelength dependency of the obtained polarizing plate. be able to.
本発明の偏光板の態様としては、従来のＰＶＡからなる偏光子と同様に厚さ２０〜２５μｍのフィルム状であってもよいし、位相差板等の支持板の表面に、厚さ１〜１０μｍ程度に塗工して乾燥したフィルム（塗工フィルム）であってもよい。本発明の偏光板は、高度な配向性及び包接性を有することから、極めて薄くとも充分な偏光性能を発揮でき、かつ、薄くとも割れ難いことから、このような塗工フィルム状であってもよく、液晶表示素子全体の薄型化にも貢献することができる。 As an aspect of the polarizing plate of the present invention, a film shape having a thickness of 20 to 25 μm may be used in the same manner as a conventional polarizer made of PVA, or a thickness of 1 to It may be a film (coated film) that is applied to a thickness of about 10 μm and dried. Since the polarizing plate of the present invention has a high degree of orientation and inclusion, it can exhibit sufficient polarization performance even if it is extremely thin, and it is difficult to break even if it is thin. In addition, it can contribute to the thinning of the entire liquid crystal display element.
本発明の偏光板は、特に保護フィルムを併用する必要がない。これにより、保護フィルムの貼り合わせ工程を省略することができ、歩留りも向上して、安価に製造することができる。また、保護フィルムに対する位相差補償必要性の問題、保護フィルムの耐久変化による光学特性劣化の問題等、保護フィルムに起因する液晶表示素子の問題点を解決することができる。 The polarizing plate of the present invention does not need to use a protective film in combination. Thereby, the bonding process of a protective film can be skipped, a yield can also be improved and it can manufacture at low cost. In addition, it is possible to solve the problems of the liquid crystal display element caused by the protective film, such as the problem of necessity of phase difference compensation for the protective film and the problem of deterioration of optical characteristics due to the durability change of the protective film.
本発明の偏光板は、ＪＩＳ Ｒ ３１０６に準拠した方法により測定した可視光透過率の好ましい下限が３８％である。３８％未満であると、液晶表示素子の偏光板としての用途には用いることができないことがある。より好ましい下限は４０％である。
本発明の偏光板は、ＪＩＳ Ｋ ６７１４に準拠した方法により測定したヘイズ値の好ましい上限が５％である。５％を超えると、液晶表示素子の偏光板としての用途には用いることができないことがある。より好ましい上限は３％である。
In the polarizing plate of the present invention, the preferable lower limit of the visible light transmittance measured by a method based on JIS R 3106 is 38%. If it is less than 38%, it may not be used as a polarizing plate for a liquid crystal display element. A more preferred lower limit is 40%.
In the polarizing plate of the present invention, the preferable upper limit of the haze value measured by a method based on JIS K 6714 is 5%. If it exceeds 5%, it may not be used as a polarizing plate for a liquid crystal display element. A more preferred upper limit is 3%.
本発明の偏光板は、特定の重量平均分子量、及び、直線性の分子構造を有するアミロースを用いたフィルムを用いることにより、染色した二色性染料が褪色しにくく、高温高湿下に置いた場合でも安定した偏光性能を発揮することができる。また、極めて薄くしても偏光性能を発揮できることから、塗工フィルム状とすることにより、液晶表示素子全体の薄型化に貢献できる。更に、保護フィルムを必要としないことから、容易かつ安価に製造できることに加え、保護フィルムに起因する種々の問題点を解決することができる。 The polarizing plate of the present invention uses a film using amylose having a specific weight average molecular weight and a linear molecular structure, so that the dyed dichroic dye is difficult to fade and is placed under high temperature and high humidity. Even in the case, stable polarization performance can be exhibited. In addition, since the polarizing performance can be exhibited even if it is extremely thin, it is possible to contribute to the thinning of the entire liquid crystal display element by forming a coating film. Furthermore, since a protective film is not required, various problems caused by the protective film can be solved in addition to easy and inexpensive production.
本発明によれば、褪色しにくく、薄型でも充分な偏光性能を発揮でき、しかも保護フィルムを必要としない偏光板を提供することができる。 According to the present invention, it is possible to provide a polarizing plate that is difficult to fade, can exhibit sufficient polarization performance even when it is thin, and does not require a protective film.
以下に実施例を掲げて本発明を更に詳しく説明するが、本発明はこれら実施例のみに限定されるものではない。 Hereinafter, the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these examples.
（実施例１）
（１）酵素合成アミロースの調製
ブドウ糖を原料として、グルコースホスホリラーゼ及びグルカンホスホリラーゼの２種の酵素を作用させることにより酵素合成アミロースを得た。
得られた酵素合成アミロースの重量平均分子量は９０万であった。
Example 1
(1) Preparation of enzyme-synthesized amylose Enzyme-synthesized amylose was obtained by using glucose as a raw material and allowing two enzymes, glucose phosphorylase and glucan phosphorylase to act.
The obtained enzyme-synthesized amylose had a weight average molecular weight of 900,000.
（２）アミロースフィルムの製造
得られた酵素合成アミロースを蒸留水に溶解して、５％アミロース水溶液を調製した。得られたアミロース水溶液を、ガラス上にコーターを用いて塗工した後、室温で１日放置後、８０℃で１時間乾燥して、厚さ２５μｍのアミロースフィルムを得た。
(2) Production of amylose film The obtained enzyme-synthesized amylose was dissolved in distilled water to prepare a 5% amylose aqueous solution. The obtained amylose aqueous solution was coated on a glass using a coater, allowed to stand at room temperature for 1 day, and then dried at 80 ° C. for 1 hour to obtain an amylose film having a thickness of 25 μm.
（３）偏光板の製造
得られたアミロースフィルムを、ヨウ素、ヨウ化カリウム及びホウ酸を溶解した水溶液中に浸漬して、アミロースフィルムをヨウ素で染色した。
次いで、染色アミロースフィルムを６０℃の温度をかけながら２倍延伸して、厚さ１８μｍの偏光板を得た。
(3) Production of polarizing plate The obtained amylose film was immersed in an aqueous solution in which iodine, potassium iodide and boric acid were dissolved, and the amylose film was dyed with iodine.
Next, the dyed amylose film was stretched twice while applying a temperature of 60 ° C. to obtain a polarizing plate having a thickness of 18 μm.
（実施例２）
実施例１で調製したアミロース水溶液を用い、位相差板（積水化学工業株式会社製、エスシーナ位相差フィルム）上にワイヤーバーを用いて剪断塗布した後、６０℃、１０分乾燥して、厚さ５μｍの塗工アミロースフィルム形成させ、塗工アミロース膜付きの位相差板を作製した。得られた塗工アミロース膜付きの位相差板の塗工アミロース膜部分に、ヨウ素、ヨウ化カリウム及びホウ酸を溶解した水溶液を作用させて、アミロースフィルムをヨウ素で染色して、偏光板付き位相差板を得た。
(Example 2)
Using the aqueous amylose solution prepared in Example 1, the film was shear-coated using a wire bar on a retardation plate (Sekisui Chemical Co., Ltd., Essina retardation film), then dried at 60 ° C. for 10 minutes to obtain a thickness. A 5 μm coated amylose film was formed to prepare a retardation plate with a coated amylose film. An aqueous solution in which iodine, potassium iodide and boric acid are dissolved is allowed to act on the coated amylose film portion of the obtained retardation film with a coated amylose film, and the amylose film is dyed with iodine. A phase difference plate was obtained.
実施例１及び２で得られた偏光板について、偏光度を測定したところ９９％、また、ＪＩＳ Ｒ ３１０６に準拠した方法により可視光透過率を測定したところ４０％であった。 About the polarizing plate obtained in Example 1 and 2, when the degree of polarization was measured, it was 99%, and when the visible light transmittance was measured by a method based on JIS R 3106, it was 40%.
本発明によれば、褪色しにくく、薄型でも充分な偏光性能を発揮でき、しかも保護フィルムを必要としない偏光板を提供することができる。 According to the present invention, it is possible to provide a polarizing plate that is difficult to fade, can exhibit sufficient polarization performance even when it is thin, and does not require a protective film.
Claims (4)