JP2006321864A - Ink composition, inkjet recording method, printed matter, manufacturing method of lithographic printing plate, and lithographic printing plate - Google Patents
Ink composition, inkjet recording method, printed matter, manufacturing method of lithographic printing plate, and lithographic printing plate Download PDFInfo
- Publication number
- JP2006321864A JP2006321864A JP2005144836A JP2005144836A JP2006321864A JP 2006321864 A JP2006321864 A JP 2006321864A JP 2005144836 A JP2005144836 A JP 2005144836A JP 2005144836 A JP2005144836 A JP 2005144836A JP 2006321864 A JP2006321864 A JP 2006321864A
- Authority
- JP
- Japan
- Prior art keywords
- group
- ink composition
- ink
- compound
- examples
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、インクジェット記録用として好適に用いられるインク組成物、インクジェット記録方法、及び、これを用いた印刷物、さらに、該インクを用いて得られる平版印刷版並びに平版印刷版の製造方法に関するものである。詳しくは、放射線の照射に対して、高感度で硬化し、高画質の画像を形成することができ、且つ、保存安定性の良好なインクジェット記録用に好適なインク組成物、インクジェット記録方法、及び、これを用いた印刷物、該インクを用いて得られる平版印刷版並びに平版印刷版の製造方法に関するものである。 The present invention relates to an ink composition suitably used for ink jet recording, an ink jet recording method, a printed material using the ink composition, a lithographic printing plate obtained using the ink, and a method for producing a lithographic printing plate. is there. Specifically, an ink composition, an ink jet recording method, which can be cured with high sensitivity to radiation irradiation, can form a high quality image, and is suitable for ink jet recording with good storage stability, and Further, the present invention relates to a printed matter using the same, a lithographic printing plate obtained using the ink, and a method for producing the lithographic printing plate.
画像データ信号に基づき、紙などの被記録媒体に画像を形成する画像記録方法として、電子写真方式、昇華型及び溶融型熱転写方式、インクジェット方式などがある。電子写真方式は、感光体ドラム上に帯電及び露光により静電潜像を形成するプロセスを必要とし、システムが複雑となり、結果的に製造コストが高価になるなどの問題がある。また熱転写方式は、装置は安価であるが、インクリボンを用いるため、ランニングコストが高くかつ廃材が出るなどの問題がある。一方インクジェット方式は、安価な装置で、且つ必要とされる画像部のみにインクを吐出し被記録媒体上に直接画像形成を行うため、インクを効率良く使用でき、ランニングコストが安い。さらに、騒音が少なく、画像記録方式として優れている。 As an image recording method for forming an image on a recording medium such as paper based on an image data signal, there are an electrophotographic method, a sublimation type and a melt type thermal transfer method, an ink jet method and the like. The electrophotographic system requires a process of forming an electrostatic latent image on a photosensitive drum by charging and exposure, and there is a problem that the system becomes complicated and consequently the manufacturing cost becomes high. In addition, although the thermal transfer method is inexpensive, there are problems such as high running costs and waste materials due to the use of ink ribbons. On the other hand, the ink jet system is an inexpensive apparatus and ejects ink only to a required image portion to form an image directly on a recording medium, so that ink can be used efficiently and running cost is low. Furthermore, there is little noise and it is excellent as an image recording method.
紫外線などの放射線の照射により硬化可能なインク組成物、特にインクジェット記録用インク（放射線硬化型インクジェット記録用インク）は、十分に高い感度及び高画質の提供が求められている。高感度化を達成することにより、放射線に対し高い硬化性が付与され、消費電力低減、放射線発生器への負荷軽減による高寿命化、不十分硬化に基づく低分子物質の発生の防止等、多くの利益が生じる。また、高感度化は、とくにインク組成物、特にインクジェット記録用インクを平版印刷版の画像部として使用した場合、画像部の硬化強度が高まることになり、高耐刷性が得られることになる。 Ink compositions that can be cured by irradiation with radiation such as ultraviolet rays, in particular ink jet recording inks (radiation curable ink jet recording inks), are required to provide sufficiently high sensitivity and high image quality. By achieving high sensitivity, high curability is imparted to radiation, reducing power consumption, extending life by reducing the load on the radiation generator, preventing the generation of low-molecular substances due to insufficient curing, etc. Profits are generated. In addition, when the sensitivity is increased, particularly when an ink composition, in particular, an ink jet recording ink is used as an image portion of a lithographic printing plate, the curing strength of the image portion is increased and high printing durability is obtained. .
このような放射線、例えば、紫外線による硬化型インクジェット方式は、比較的低臭気であり、速乾性、インク吸収性の無い被記録媒体への記録が出来る点で、近年注目されつつあり、ラジカル重合を利用したインクジェット用紫外線硬化型インク組成物が開示されている（例えば、特許文献１〜５参照。）。また、インクジェット記録方法にて通常直接記録することが困難な支持体に対しても、滲みがなく、高感度で、被記録媒体への密着性が高い画像が記録可能で、かつ皮膚刺激性や感作性の少ない安全性が高いインクジェット記録用インクを提供すること等を目的として、特定のラジカル重合型アクリレート化合物群からなる重合性化合物と色材とを含有する組成物が提案されている（例えば、特許文献６、７参照。）。これらのラジカル重合型インクは、硬化速度に優れ、滲みのない画像を形成しうるものの、硬化時の体積収縮により、被記録媒体との密着性が低下するという問題を有していた。 Such a curable ink jet method using radiation, for example, ultraviolet rays has been attracting attention in recent years because it has a relatively low odor, and can be recorded on a recording medium having no quick drying and no ink absorption. An ultraviolet ray curable ink composition for inkjet that is used is disclosed (for example, see Patent Documents 1 to 5). Further, even for a support that is usually difficult to directly record with an ink jet recording method, it is possible to record an image with no blur, high sensitivity, high adhesion to a recording medium, and skin irritation or For the purpose of providing an inkjet recording ink with low sensitization and high safety, a composition containing a polymerizable compound consisting of a specific radical polymerization type acrylate compound group and a coloring material has been proposed ( For example, see Patent Documents 6 and 7.) Although these radical polymerization type inks are excellent in curing speed and can form images without bleeding, they have a problem that adhesion to a recording medium is reduced due to volume shrinkage during curing.
このため、被記録媒体への密着性を向上させる目的で、紫外線硬化時の収縮率が小さいカチオン重合型インク組成物が提案されている（例えば、特許文献８参照。）。但し、これらカチオン重合型インクは、経時で発生した酸に基づく反応により、保存時の安定性が十分ではなく、実用化には大きな障害となっていた。このため、保存安定性を改良する試みとして、塩基性化合物や熱塩基発生剤を添加する技術が提案されている（例えば、特許文献９〜１１参照。）が、塩基性化合物が露光により発生した酸の機能を阻害するためにインクの硬化感度が低下するという新たな問題が発生することがわかった。このため、保存安定性と高感度との両立が切望されている。 For this reason, for the purpose of improving the adhesion to the recording medium, a cationic polymerization type ink composition having a small shrinkage rate upon UV curing has been proposed (for example, see Patent Document 8). However, these cationic polymerization type inks are not sufficiently stable at the time of storage due to the reaction based on the acid generated with the passage of time, which has been a major obstacle to practical use. For this reason, as an attempt to improve the storage stability, a technique of adding a basic compound or a thermal base generator has been proposed (for example, see Patent Documents 9 to 11), but the basic compound was generated by exposure. It has been found that a new problem arises that the curing sensitivity of the ink is lowered due to the inhibition of the acid function. For this reason, both storage stability and high sensitivity are desired.
前記課題を考慮してなされた本発明の目的は、活性放射線の照射により高感度で硬化し、高画質の画像を形成することができ、被記録媒体上への密着性が優れ、保存安定性の良好で、且つ、インクヘッドを長寿命化できるインク組成物、及び、該インク組成物を用いたインクジェット記録方法を提供することにある。
また、本発明の他の目的は、保存安定性に優れ、紫外線の照射により高感度で硬化可能なインク組成物を用いて得られた印刷物、平版印刷版、及び、平版印刷版の作製方法を提供することにある。
The object of the present invention made in consideration of the above problems is that it can be cured with high sensitivity by irradiation with actinic radiation, can form a high-quality image, has excellent adhesion to a recording medium, and has storage stability. It is an object of the present invention to provide an ink composition that can improve the life of the ink head and extend the life of the ink head, and an ink jet recording method using the ink composition.
Another object of the present invention is to provide a printed matter, a lithographic printing plate, and a method for producing the lithographic printing plate, which are obtained using an ink composition that has excellent storage stability and is highly curable by irradiation with ultraviolet rays. It is to provide.
上記目的は、以下の＜１＞、＜８＞及び＜１０＞〜＜１２＞により達成された。好ましい実施態様である＜２＞〜＜７＞及び＜９＞と共に以下に示す。
＜１＞ （ａ）カチオン重合性化合物、（ｂ）放射線の照射により酸を発生する化合物、（ｃ）着色剤、及び、（ｄ）２種以上のアミン化合物を含有することを特徴とするインク組成物、
＜２＞ 共役酸のｐＫａの異なる２種以上のアミン化合物を含有する上記＜１＞に記載のインク組成物、
＜３＞ ２種以上のアミン化合物が、１種以上の弱塩基性アミンと１種以上の強塩基性アミンとの組合わせである上記＜１＞又は＜２＞に記載のインク組成物、
＜４＞ 弱塩基性アミンの共役酸のｐＫａ値が３〜１０であり、強塩基性アミンの共役酸のｐＫａ値が１０より大きい化合物である上記＜３＞に記載のインク組成物、
＜５＞ 着色剤が顔料又は油溶性染料である上記＜１＞〜＜４＞のいずれか１つに記載のインク組成物、
＜６＞ 油溶性染料の酸化電位が１．０Ｖ（ｖｓＳＣＥ）以上である上記＜５＞に記載のインク組成物、
＜７＞ インクジェット記録用である上記＜１＞〜＜６＞のいずれか１つに記載のインク組成物、
＜８＞ （ａ）被記録媒体上にインク組成物を吐出する工程、及び（ｂ）吐出されたインク組成物に活性放射線を照射してインク組成物を硬化する工程、を含むインクジェット記録方法であって、前記インク組成物が上記＜１＞〜＜７＞のいずれか１つに記載のインク組成物であるインクジェット記録方法、
＜９＞ 前記活性放射線が、発光ピーク波長が３５０〜４２０ｎｍの範囲にあり、かつ被記録媒体表面での最高照度が１０〜２，０００ｍＷ／ｃｍ2となる紫外線を発生する発光ダイオードにより照射される紫外線である上記＜８＞に記載のインクジェット記録方法、
＜１０＞ 上記＜８＞又は＜９＞に記載のインクジェット記録方法によって記録された印刷物、
＜１１＞ （ａ）上記＜１＞〜＜７＞のいずれか１つに記載のインク組成物を親水性支持体上に吐出する工程、及び（ｂ）吐出されたインク組成物に活性放射線を照射して、前記インク組成物を硬化させることにより、前記インク組成物が硬化してなる疎水性画像を前記親水性支持体上に形成する工程、を含む平版印刷版の製造方法、
＜１２＞ 上記＜１１＞に記載の平版印刷版の製造方法によって製造された平版印刷版。
The above object was achieved by the following <1>, <8>, and <10> to <12>. It is shown below with <2>-<7> and <9> which are preferable embodiments.
<1> An ink comprising (a) a cationically polymerizable compound, (b) a compound that generates an acid upon irradiation with radiation, (c) a colorant, and (d) two or more amine compounds. Composition,
<2> The ink composition according to the above <1>, which contains two or more amine compounds having different pKa of conjugate acids.
<3> The ink composition according to <1> or <2>, wherein the two or more amine compounds are a combination of one or more weakly basic amines and one or more strongly basic amines.
<4> The ink composition according to <3>, wherein the pKa value of the conjugate acid of the weakly basic amine is 3 to 10, and the pKa value of the conjugate acid of the strongly basic amine is greater than 10.
<5> The ink composition according to any one of <1> to <4>, wherein the colorant is a pigment or an oil-soluble dye.
<6> The ink composition according to <5>, wherein the oxidation potential of the oil-soluble dye is 1.0 V (vs SCE) or more.
<7> The ink composition according to any one of the above <1> to <6>, which is for inkjet recording.
<8> An inkjet recording method comprising: (a) a step of ejecting an ink composition onto a recording medium; and (b) a step of irradiating the ejected ink composition with active radiation to cure the ink composition. An ink jet recording method, wherein the ink composition is the ink composition according to any one of the above items <1> to <7>.
<9> The actinic radiation is irradiated by a light emitting diode that generates ultraviolet rays having an emission peak wavelength in a range of 350 to 420 nm and a maximum illuminance on a recording medium surface of 10 to 2,000 mW / cm 2. The inkjet recording method according to <8>, which is ultraviolet rays;
<10> Printed matter recorded by the inkjet recording method according to <8> or <9> above,
<11> (a) a step of discharging the ink composition according to any one of <1> to <7> above onto a hydrophilic support, and (b) actinic radiation to the discharged ink composition. Irradiating and curing the ink composition to form a hydrophobic image formed by curing the ink composition on the hydrophilic support.
<12> A lithographic printing plate produced by the method for producing a lithographic printing plate as described in <11> above.
本発明によれば、放射線の照射に対して高感度で硬化し、高画質の画像を形成することができ、被記録媒体上への密着性が優れ、保存安定性の良好で、インクヘッドを長寿命化できるインク組成物、及び、該インク組成物を用いたインクジェット記録方法を提供することができる。
また、前記保存安定性に優れ、紫外線の照射により高感度で硬化可能なインク組成物を用いて得られた印刷物は高画質であり、画像部の強度に優れる。同様に本発明のインク組成物を用いることで、高耐刷、高画質の平版印刷版を、デジタルデータに基づき作製することができるという効果を奏する。
According to the present invention, the ink head can be cured with high sensitivity to radiation irradiation, can form a high-quality image, has excellent adhesion to a recording medium, has good storage stability, and has an ink head. It is possible to provide an ink composition capable of extending the life and an ink jet recording method using the ink composition.
Moreover, the printed matter obtained by using the ink composition which is excellent in the storage stability and can be cured with high sensitivity by irradiation with ultraviolet rays has high image quality and excellent image portion strength. Similarly, by using the ink composition of the present invention, it is possible to produce a lithographic printing plate with high printing durability and high image quality based on digital data.
本発明のインク組成物（以下、単に「インク」ともいう。）は、放射線の照射により硬化可能であり、（ａ）カチオン重合性化合物、（ｂ）放射線の照射により酸を発生する化合物、（ｃ）着色剤、及び、（ｄ）２種以上のアミン化合物を含有することを特徴とする。
本発明で言う「放射線」とは、その照射によりインク組成物中において開始種を発生させうるエネルギーを付与することができるものであれば、特に制限はなく、広くα線、γ線、Ｘ線、紫外線、可視光線、電子線などを包含するものである。中でも、硬化感度及び装置の入手容易性の観点からは、紫外線及び電子線が好ましく、特に紫外線が好ましい。従って、本発明のインク組成物としては、放射線として、紫外線を照射することにより硬化可能なインク組成物であることが好ましい。
以下、本発明について詳細に説明する。
The ink composition of the present invention (hereinafter, also simply referred to as “ink”) is curable by irradiation with radiation, (a) a cationically polymerizable compound, (b) a compound that generates an acid upon irradiation with radiation, ( c) a colorant and (d) two or more amine compounds.
The “radiation” referred to in the present invention is not particularly limited as long as it can impart energy capable of generating a starting species in the ink composition by the irradiation, and is broadly α-ray, γ-ray, X-ray. , Ultraviolet rays, visible rays, electron beams, and the like. Among these, from the viewpoints of curing sensitivity and device availability, ultraviolet rays and electron beams are preferable, and ultraviolet rays are particularly preferable. Therefore, the ink composition of the present invention is preferably an ink composition that can be cured by irradiating ultraviolet rays as radiation.
Hereinafter, the present invention will be described in detail.
［（ｄ）２種以上のアミン化合物］
本発明のインク組成物は、２種以上のアミン化合物を含有する。
本発明に用いることのできるアミン化合物としては、２種以上の異なるアミン化合物であればよいが、１種以上の弱塩基性アミン化合物と１種以上の強塩基性アミン化合物とを組合わせて用いることが好ましい。弱塩基性アミン化合物は、インクの硬化感度低下に対する影響が小さく、一方強塩基性化合物は、インク組成物の保存安定性向上の効果が大きい。これらを組合わせることで、インク組成物の保存安定性と高感度を両立することが可能であることを見出し本発明に到達した。ここで弱塩基性アミン化合物としては、共役酸のｐＫａ値が３〜１０、好ましくは４〜７の値を示す化合物であり、強塩基性化合物としては、共役酸のｐＫａ値が１０より大きい値を示す化合物である。
なお、ここで規定するｐＫａ値は、弱電解質の水溶液中での解離定数Ｋａの常用対数に負号を付けたもの、即ち、ｐＫａ＝−ｌｏｇ10Ｋａと定義される。本発明においては、このｐＫａ値は、エタノール／水（７／３）中、ＨＣｌ及びＮａＯＨ標準液による滴定により算出される。
[(D) Two or more amine compounds]
The ink composition of the present invention contains two or more amine compounds.
The amine compound that can be used in the present invention may be two or more different amine compounds, but one or more weakly basic amine compounds and one or more strongly basic amine compounds are used in combination. It is preferable. A weakly basic amine compound has a small effect on a decrease in the curing sensitivity of the ink, while a strongly basic compound has a large effect of improving the storage stability of the ink composition. It has been found that by combining these, it is possible to achieve both storage stability and high sensitivity of the ink composition, and the present invention has been achieved. Here, the weak basic amine compound is a compound having a pKa value of the conjugate acid of 3 to 10, preferably 4 to 7, and the strong basic compound has a pKa value of the conjugate acid of more than 10. It is a compound which shows.
The pKa value defined here is defined as a value obtained by adding a negative sign to the common logarithm of the dissociation constant Ka in an aqueous solution of a weak electrolyte, that is, pKa = −log 10 Ka. In the present invention, this pKa value is calculated by titration with HCl and NaOH standard solutions in ethanol / water (7/3).
また、本発明に用いることのできるアミン化合物は、１級、２級及び３級のアミン化合物のいずれでもよく、分子内に２以上のアミン部位を有していてもよいが、重合性化合物との副反応や変色反応の抑制の観点から、３級のアミン化合物を使用することが好ましい。２種以上用いるアミン化合物それぞれの混合比としては、アミン化合物の総重量に対し、１種のアミン化合物が１０重量％以上であることが好ましく、また、アミン化合物の総重量に対し、１種のアミン化合物が９０重量％以下であることが好ましい。上記の範囲であると、それぞれのアミン化合物の特性が発揮でき、インク組成物が保存安定性に優れ、また硬化感度の低下を抑制できる。 The amine compound that can be used in the present invention may be any of primary, secondary, and tertiary amine compounds, and may have two or more amine sites in the molecule. From the viewpoint of suppressing side reactions and discoloration reactions, tertiary amine compounds are preferably used. As a mixing ratio of each of the two or more amine compounds, one amine compound is preferably 10% by weight or more based on the total weight of the amine compound, and one kind of amine compound is used based on the total weight of the amine compound. The amine compound is preferably 90% by weight or less. Within the above range, the characteristics of each amine compound can be exhibited, the ink composition is excellent in storage stability, and a decrease in curing sensitivity can be suppressed.
本発明で用いることのできるアミン化合物のうち、共役酸のｐＫａが３〜１０の値を示すアミン化合物として具体的には、例えば、２−クロロアニリン、２−ブロモアニリン、４−メチルアニリン、３−クロロアニリン、３，５−ジブロモアニリン、Ｎ−メチルアニリン、Ｎ，Ｎ−ジメチルアニリン、３−ニトロアニリン、２−アミノ安息香酸、４−アミノアゾベンゼン、Ｎ−フェニルアニリン、Ｎ−フェニルグリシンなどのアニリン類；３−クロロピリジン、３−ブロモピリジン、４−ヒドロキシピリジン、３−カルボキシピリジン、２，６−ジメチルピリジン、２，４，６−トリメチルピリジンなどのピリジン類；の他、プロリン、ヒドロキシプロリン、プリン、８−ヒドロキシプリン、Ｎ−メチルピラジン、チアゾール、トリプトファンなどの環状アミン；アルギニン、アスパラギン酸、グルタミン酸、Ｎ−メチルグリシン、Ｎ−プロピルグリシン、ヒスチジン、シスチン、ロイシン、イソロイシン、オルニチン、セリン、トレオニン、メチオニン、アラニン、メトキシアラニンなどの脂肪族アミン類；などが挙げられるが、なかでも好ましいのは、下記式（Ｉ）又は式（II）で表される化合物である。 Among the amine compounds that can be used in the present invention, specific examples of amine compounds having a pKa of a conjugate acid of 3 to 10 include 2-chloroaniline, 2-bromoaniline, 4-methylaniline, 3 -Chloroaniline, 3,5-dibromoaniline, N-methylaniline, N, N-dimethylaniline, 3-nitroaniline, 2-aminobenzoic acid, 4-aminoazobenzene, N-phenylaniline, N-phenylglycine, etc. Anilines; pyridines such as 3-chloropyridine, 3-bromopyridine, 4-hydroxypyridine, 3-carboxypyridine, 2,6-dimethylpyridine, 2,4,6-trimethylpyridine; other proline, hydroxyproline , Purine, 8-hydroxypurine, N-methylpyrazine, thiazole, tryptophan Cyclic amines such as arginine, aspartic acid, glutamic acid, N-methylglycine, N-propylglycine, histidine, cystine, leucine, isoleucine, ornithine, serine, threonine, methionine, alanine, methoxyalanine, etc .; Among them, preferred is a compound represented by the following formula (I) or (II).
式（Ｉ）及び式（II）中、Ｒ1、Ｒ2はそれぞれ独立に水素原子、アルキル基、シクロアルキル基、アラルキル基、またはアリール基を示し、Ａｒ1はアリール基を示す。Ｒ3〜Ｒ5はそれぞれ独立に水素原子、アルキル基、シクロアルキル基、アラルキル基、アリール基、ヒドロキシ基、カルボキシ基、シアノ基、ニトロ基、アシル基、または−Ｎ（Ｒ1）（Ｒ2）基を示す。また式（Ｉ）におけるＲ1とＲ2、式（II）におけるＲ3〜Ｒ5の２つが、互いに結合し、脂肪族環、芳香族環、またはヘテロ環を形成してもよい。 In formula (I) and formula (II), R 1 and R 2 each independently represent a hydrogen atom, an alkyl group, a cycloalkyl group, an aralkyl group, or an aryl group, and Ar 1 represents an aryl group. R 3 to R 5 are each independently a hydrogen atom, alkyl group, cycloalkyl group, aralkyl group, aryl group, hydroxy group, carboxy group, cyano group, nitro group, acyl group, or —N (R 1 ) (R 2 ) Group. Two of R 1 and R 2 in formula (I) and R 3 to R 5 in formula (II) may be bonded to each other to form an aliphatic ring, an aromatic ring, or a hetero ring.
式（Ｉ）及び式（II）において、Ｒ1、Ｒ2、Ｒ3〜Ｒ5としては、炭素数１〜８のアルキル基、炭素数５〜１２の単環又は多環のシクロアルキル基が好ましい。
Ｒ1とＲ2、或いは、Ｒ3〜Ｒ5のうち２つが、互いに結合して環を形成する場合に形成される環としては、例えば、ピロリジン環、ピペリジン環、ピラジン環、１，３−ジアザシクロペンテン環、１，３−ジアザシクロヘキセン環、１，３−ジアザシクロヘプタン環等が挙げられる。
In Formula (I) and Formula (II), R 1 , R 2 , R 3 to R 5 are each an alkyl group having 1 to 8 carbon atoms, a monocyclic or polycyclic cycloalkyl group having 5 to 12 carbon atoms. preferable.
Examples of the ring formed when two of R 1 and R 2 or R 3 to R 5 are bonded to each other to form a ring include, for example, pyrrolidine ring, piperidine ring, pyrazine ring, 1,3- Examples thereof include a diazacyclopentene ring, a 1,3-diazacyclohexene ring, and a 1,3-diazacycloheptane ring.
前記アルキル基としては、好ましくはメチル基、エチル基、プロピル基、ｎ−ブチル基、ｓｅｃ−ブチル基、ヘキシル基、オクチル基、デシル基のような炭素数１〜１０個のものが挙げられる。
シクロアルキル基としては、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、シクロペンチル基、ノルボルニル基のような炭素数３〜１０個のものが挙げられる。
アラルキル基としては、ベンジル基、フェネチル基、ナフチルメチル基のような炭素数７〜１２個のものが挙げられる。
アリール基としては、フェニル基、トリル基、メトキシフェニル基、ナフチル基、アントリル基などのような炭素数６〜１５個のものが挙げられる。
Preferred examples of the alkyl group include those having 1 to 10 carbon atoms such as methyl group, ethyl group, propyl group, n-butyl group, sec-butyl group, hexyl group, octyl group and decyl group.
Examples of the cycloalkyl group include those having 3 to 10 carbon atoms such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cyclopentyl group, and a norbornyl group.
Examples of the aralkyl group include those having 7 to 12 carbon atoms such as a benzyl group, a phenethyl group, and a naphthylmethyl group.
Examples of the aryl group include those having 6 to 15 carbon atoms such as a phenyl group, a tolyl group, a methoxyphenyl group, a naphthyl group, and an anthryl group.
またこれらの基は置換基を有するものであってもよく、ここで導入可能な置換基としては、直鎖、分岐、あるいは環状のアルキル基（メチル基、エチル基、プロピル基、イソプロピル基、ｎ−ブチル基、ｓｅｃ−ブチル基、ｔ−ブチル基、シクロプロピル基、シクロペンチル基、シクロヘキシル基など）、直鎖、分岐、あるいは環状のアルコキシ基（メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ヒドロキシエトキシ基など）、前記アリール基、ハロゲン原子（フッ素原子、塩素原子、ブロモ原子、ヨー素原子）、ヒドロキシ基、カルボキシル基、シアノ基、アシル基（アセチル基、プロパノイル基、ベンゾイル基など）、ニトロ基、アルキルアミノ基、ジアルキルアミノ基（アルキル基は上記と同じもの）、アリールアミノ基（アリール基は前記と同じもの）、−Ｓ−Ｒ0基が挙げられる。ここでＲ0は、上記直鎖、分岐、或いは環状のアルキル基、またはアリール基を表す。特に好ましい置換基としては、ヒドロキシ基（ＯＨ基）、カルボキシル基（ＣＯＯＨ基）などの親水性基が挙げられる。 These groups may have a substituent, and examples of the substituent that can be introduced here include linear, branched, or cyclic alkyl groups (methyl group, ethyl group, propyl group, isopropyl group, n -Butyl group, sec-butyl group, t-butyl group, cyclopropyl group, cyclopentyl group, cyclohexyl group, etc.), linear, branched, or cyclic alkoxy group (methoxy group, ethoxy group, propoxy group, butoxy group, hydroxy) Ethoxy group, etc.), aryl group, halogen atom (fluorine atom, chlorine atom, bromo atom, iodine atom), hydroxy group, carboxyl group, cyano group, acyl group (acetyl group, propanoyl group, benzoyl group, etc.), nitro Group, alkylamino group, dialkylamino group (the alkyl group is the same as above), arylamino group (a Lumpur groups are the same meanings as defined above), - S-R 0 group can be mentioned. Here, R 0 represents the linear, branched or cyclic alkyl group or aryl group. Particularly preferred substituents include hydrophilic groups such as hydroxy groups (OH groups) and carboxyl groups (COOH groups).
共役酸のｐＫａが３〜１０の値を示すアミン化合物としては、以下に示す〔（Ｉ−１）〜（Ｉ−４０）、（II−１）〜（II−２４）〕を用いることが特に好ましい。 As the amine compound having a pKa of the conjugate acid of 3 to 10, it is particularly preferable to use [(I-1) to (I-40), (II-1) to (II-24)] shown below. preferable.
また、本発明で用いることのできるアミン化合物のうち、共役酸のｐＫａが１０より大きな値を示すアミン化合物として具体的には、例えば、脂肪族３級アミン構造を有する化合物や、１，３−ジアザプロペン構造を有する化合物が好ましく、更に好ましくは、下記式（III）、又は、式（IV）で表される化合物である。 Further, among amine compounds that can be used in the present invention, specific examples of amine compounds having a pKa of a conjugate acid greater than 10 include compounds having an aliphatic tertiary amine structure, 1,3- A compound having a diazapropene structure is preferable, and a compound represented by the following formula (III) or formula (IV) is more preferable.
上記式（III）及び上記式（IV）において、Ｒ6〜Ｒ8、Ｒ10〜Ｒ12は、それぞれ独立に、水素原子、アルキル基、シクロアルキル基、又はアラルキル基を示す。また、Ｒ9は、アルキル基、シクロアルキル基、アラルキル基、アリール基、−Ｎ（Ｒ13）（Ｒ14）基、又は−ＯＲ15基を示す。ここで、Ｒ13〜Ｒ15は、それぞれ独立に、水素原子、アルキル基、シクロアルキル基、又はアラルキル基を示す。 In the above formula (III) and the above formula (IV), R 6 to R 8 and R 10 to R 12 each independently represent a hydrogen atom, an alkyl group, a cycloalkyl group, or an aralkyl group. R 9 represents an alkyl group, a cycloalkyl group, an aralkyl group, an aryl group, an —N (R 13 ) (R 14 ) group, or an —OR 15 group. Here, R < 13 > -R < 15 > shows a hydrogen atom, an alkyl group, a cycloalkyl group, or an aralkyl group each independently.
前記アルキル基としては、好ましくは、メチル基、エチル基、プロピル基、ｎ−ブチル基、ｓｅｃ−ブチル基、ヘキシル基、オクチル基、デシル基のような炭素数１〜１０個のものが挙げられる。
前記シクロアルキル基としては、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、シクロペンチル基、ノルボルニル基のような炭素数３〜１０個のものが挙げられる。
前記アラルキル基としては、ベンジル基、フェネチル基、ナフチルメチル基のような炭素数７〜１２個のものが挙げられる。
前記アリール基としては、フェニル基、トリル基、メトキシフェニル基、ナフチル基、アントリル基などのような炭素数６〜１５個のものが挙げられる。
Preferred examples of the alkyl group include those having 1 to 10 carbon atoms such as methyl group, ethyl group, propyl group, n-butyl group, sec-butyl group, hexyl group, octyl group and decyl group. .
Examples of the cycloalkyl group include those having 3 to 10 carbon atoms such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cyclopentyl group, and a norbornyl group.
Examples of the aralkyl group include those having 7 to 12 carbon atoms such as benzyl group, phenethyl group, and naphthylmethyl group.
Examples of the aryl group include those having 6 to 15 carbon atoms such as a phenyl group, a tolyl group, a methoxyphenyl group, a naphthyl group, and an anthryl group.
また、上記式（III）におけるＲ6〜Ｒ8のうち２つ、上記式（IV）におけるＲ9〜Ｒ15のうち２つが、互いに結合し、脂肪族環、芳香族環、又はヘテロ環を形成してもよい。
ここで、上記のようにして形成される環構造としては、例えば、ピロリジン環、ピペリジン環、ピラジン環、１，３−ジアザシクロペンテン環、１，３−ジアザシクロヘキセン環、１，３−ジアザシクロヘプタン環等が挙げられる。
Two of R 6 to R 8 in the above formula (III) and two of R 9 to R 15 in the above formula (IV) are bonded to each other to form an aliphatic ring, an aromatic ring, or a heterocyclic ring. It may be formed.
Here, examples of the ring structure formed as described above include pyrrolidine ring, piperidine ring, pyrazine ring, 1,3-diazacyclopentene ring, 1,3-diazacyclohexene ring, 1,3-dia The cyclocycloheptane ring etc. are mentioned.
上記した各基は、置換基を導入可能な場合には、置換基を更に有してもよい。導入可能な置換基としては、直鎖、分岐、又は環状のアルキル基（例えば、メチル基、エチル基、プロピル基、イソプロピル基、ｎ−ブチル基、ｓｅｃ−ブチル基、ｔ−ブチル基、シクロプロピル基、シクロペンチル基、シクロヘキシル基など）、直鎖、分岐、又は環状のアルコキシ基（例えば、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ヒドロキシエトキシ基など）、アリール基（前記アリール基として挙げられているもの）、ハロゲン原子（フッ素原子、塩素原子、臭素原子、ヨウ素原子）、ヒドロキシ基、カルボキシル基、シアノ基、アシル基（例えば、アセチル基、プロパノイル基、ベンゾイル基など）、ニトロ基、アルキルアミノ基、ジアルキルアミノ基（アルキル部分は上記アルキル基と同義）、アリールアミノ基（アリール部分は前記アリール基と同義）、−Ｓ−Ｒ0基を表す。ここで、Ｒ0は、直鎖、分岐、又は環状のアルキル基、或いはアリール基を表す。 Each group described above may further have a substituent when a substituent can be introduced. Examples of the substituent that can be introduced include linear, branched, or cyclic alkyl groups (for example, methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, sec-butyl group, t-butyl group, cyclopropyl group). Group, cyclopentyl group, cyclohexyl group, etc.), linear, branched, or cyclic alkoxy group (eg, methoxy group, ethoxy group, propoxy group, butoxy group, hydroxyethoxy group, etc.), aryl group (said as the aryl group) ), Halogen atom (fluorine atom, chlorine atom, bromine atom, iodine atom), hydroxy group, carboxyl group, cyano group, acyl group (eg acetyl group, propanoyl group, benzoyl group, etc.), nitro group, alkyl Amino group, dialkylamino group (the alkyl moiety is as defined above), arylamino group Aryl moiety of the aryl group as defined), - represents a S-R 0 group. Here, R 0 represents a linear, branched, or cyclic alkyl group or an aryl group.
式（III）におけるＲ6〜Ｒ8としては、置換基を有してもよいアルキル基、又は、置換基を有してもよいシクロアルキル基が好ましく、炭素数１〜８個のアルキル基、又は、炭素数５〜１２個の単環若しくは多環のシクロアルキル基がより好ましい。
式（IV）におけるＲ9としては、置換基を有してもよいアルキル基、置換基を有してもよいシクロアルキル基、又は−Ｎ（Ｒ13）（Ｒ14）基が好ましく、炭素数１〜６個のアルキル基、又は−Ｎ（Ｒ13）（Ｒ14）基がより好ましい。
式（IV）におけるＲ10〜Ｒ12としては、置換基を有してもよいアルキル基、又は、置換基を有してもよいシクロアルキル基が好ましく、炭素数１〜８個のアルキル基、又は、炭素数５〜１２個の単環若しくは多環のシクロアルキル基がより好ましい。
As R < 6 > -R < 8 > in Formula (III), the alkyl group which may have a substituent, or the cycloalkyl group which may have a substituent is preferable, a C1-C8 alkyl group, Alternatively, a monocyclic or polycyclic cycloalkyl group having 5 to 12 carbon atoms is more preferable.
R 9 in formula (IV) is preferably an alkyl group which may have a substituent, a cycloalkyl group which may have a substituent, or a —N (R 13 ) (R 14 ) group, 1-6 alkyl group, or -N (R 13) (R 14 ) group is more preferable.
As R < 10 > -R < 12 > in Formula (IV), the alkyl group which may have a substituent, or the cycloalkyl group which may have a substituent is preferable, a C1-C8 alkyl group, Alternatively, a monocyclic or polycyclic cycloalkyl group having 5 to 12 carbon atoms is more preferable.
共役酸のｐＫａが１０より大きな値を示すアミン化合物としては、以下に示す〔（III−１）〜（III−２１）、（IV−１）〜（IV−１２）〕を用いることが特に好ましい。 It is particularly preferable to use the following [(III-1) to (III-21), (IV-1) to (IV-12)] as the amine compound in which the pKa of the conjugate acid is greater than 10. .
用いるアミン化合物としては、共役酸のｐＫａが異なる２種以上のアミン化合物を用いることが好ましく、少なくとも１種の共役酸のｐＫａが３〜１０の値を示すアミン化合物と、少なくとも１種の共役酸のｐＫａが１０より大きい値を示すアミン化合物とを組み合わせて用いることがより好ましく、少なくとも１種の式（Ｉ）又は式（II）で表される化合物と少なくとも１種の式（III）又は式（IV）で表される化合物とを組み合わせて用いることがさらに好ましい。
また、用いるアミン化合物としては、２種以上であり、２〜４種であることが好ましく、２〜３種であることがより好ましく、２種であることがさらに好ましく、弱塩基性アミン１種と強塩基性アミン１種とを用いることが特に好ましい。弱塩基性アミン及び強塩基性アミンの好ましい範囲は、上述と同様である。
As the amine compound to be used, it is preferable to use two or more kinds of amine compounds having different pKa values of the conjugate acid, and an amine compound having a pKa value of 3 to 10 of at least one kind of conjugate acid and at least one kind of conjugate acid. It is more preferable to use in combination with an amine compound having a pKa of greater than 10 and at least one compound represented by formula (I) or formula (II) and at least one formula (III) or formula More preferably, it is used in combination with a compound represented by (IV).
Moreover, as an amine compound to be used, it is 2 or more types, It is preferable that it is 2-4 types, It is more preferable that it is 2-3 types, It is further more preferable that they are 2 types, 1 type of weak basic amine And 1 type of strongly basic amine are particularly preferred. The preferred ranges of the weakly basic amine and the strongly basic amine are the same as described above.
インク組成物中の（ｄ）２種以上のアミン化合物の含量は、組成物の全固形分に対し、０．００１〜１０重量％であることが好ましく、０．０１〜７重量％がより好ましく、０．０３〜５重量％がさらに好ましい。なお、本発明でインク組成物中の固形分とは、インク組成物から後述の溶剤等の揮発性成分を除いた成分とする。
また、（ｄ）２種以上のアミン化合物の含量と後述する（ｂ）放射線の照射により酸を発生する化合物との割合は、（ｄ）／（ｂ）のモル比で０．００１〜０．５で用いることが好ましく、０．００５〜０．２であることがより好ましい。
The content of (d) two or more amine compounds in the ink composition is preferably 0.001 to 10% by weight, more preferably 0.01 to 7% by weight, based on the total solid content of the composition. 0.03 to 5% by weight is more preferable. In the present invention, the solid content in the ink composition is a component obtained by removing a volatile component such as a solvent described later from the ink composition.
The ratio of (d) the content of two or more amine compounds to the compound (b) that generates an acid upon irradiation with radiation, which will be described later, is a molar ratio of (d) / (b) of 0.001 to 0.00. 5 is preferable, and 0.005-0.2 is more preferable.
〔（ａ）カチオン重合性化合物〕
本発明に用いることができる（ａ）カチオン重合性化合物は、後述する（ｂ）放射線の照射により酸を発生する化合物から発生する酸により重合反応を開始し、硬化する化合物であれば特に制限はなく、光カチオン重合性モノマーとして知られる各種公知のカチオン重合性のモノマーを使用することができる。カチオン重合性モノマーとしては、例えば、特開平６−９７１４号、特開２００１−３１８９２号、同２００１−４００６８号、同２００１−５５５０７号、同２００１−３１０９３８号、同２００１−３１０９３７号、同２００１−２２０５２６号などの各公報に記載されているエポキシ化合物、ビニルエーテル化合物、オキセタン化合物などが挙げられる。
[(A) Cationic polymerizable compound]
The (a) cationic polymerizable compound that can be used in the present invention is not particularly limited as long as it is a compound that initiates a polymerization reaction with an acid generated from a compound that generates an acid upon irradiation with radiation (b) described later and cures. In addition, various known cationic polymerizable monomers known as photo cationic polymerizable monomers can be used. Examples of the cationic polymerizable monomer include JP-A-6-9714, JP-A-2001-31892, JP-A-2001-40068, JP-A-2001-55507, JP-A-2001-310938, JP-A-2001-310937, and 2001-2001. Examples thereof include epoxy compounds, vinyl ether compounds, oxetane compounds and the like described in each publication such as No. 220526.
エポキシ化合物としては、芳香族エポキシド、脂環式エポキシド、及び、芳香族エポキシドなどが挙げられる。
芳香族エポキシドとしては、少なくとも１個の芳香族核を有する多価フェノールあるいはそのアルキレンオキサイド付加体とエピクロルヒドリンとの反応によって製造されるジ又はポリグリシジルエーテルが挙げられ、例えば、ビスフェノールＡあるいはそのアルキレンオキサイド付加体のジ又はポリグリシジルエーテル、水素添加ビスフェノールＡあるいはそのアルキレンオキサイド付加体のジ又はポリグリシジルエーテル、並びにノボラック型エポキシ樹脂等が挙げられる。ここでアルキレンオキサイドとしては、エチレンオキサイド及びプロピレンオキサイド等が挙げられる。
Examples of the epoxy compound include aromatic epoxides, alicyclic epoxides, and aromatic epoxides.
Aromatic epoxides include di- or polyglycidyl ethers produced by the reaction of polyphenols having at least one aromatic nucleus or their alkylene oxide adducts and epichlorohydrin, such as bisphenol A or its alkylene oxides. Examples thereof include di- or polyglycidyl ethers of adducts, di- or polyglycidyl ethers of hydrogenated bisphenol A or its alkylene oxide adducts, and novolak-type epoxy resins. Here, examples of the alkylene oxide include ethylene oxide and propylene oxide.
脂環式エポキシドとしては、少なくとも１個のシクロへキセン又はシクロペンテン環等のシクロアルカン環を有する化合物を、過酸化水素、過酸等の適当な酸化剤でエポキシ化することによって得られる、シクロヘキセンオキサイド又はシクロペンテンオキサイド含有化合物が好ましく挙げられる。
脂肪族エポキシドとしては、脂肪族多価アルコールあるいはそのアルキレンオキサイド付加体のジ又はポリグリシジルエーテル等があり、その代表例としては、エチレングリコールのジグリシジルエーテル、プロピレングリコールのジグリシジルエーテル又は１，６−ヘキサンジオールのジグリシジルエーテル等のアルキレングリコールのジグリシジルエーテル、グリセリンあるいはそのアルキレンオキサイド付加体のジ又はトリグリシジルエーテル等の多価アルコールのポリグリシジルエーテル、ポリエチレングリコールあるいはそのアルキレンオキサイド付加体のジグリシジルエーテル、ポリプロピレングリコールあるいはそのアルキレンオキサイド付加体のジグリシジルエーテルに代表されるポリアルキレングリコールのジグリシジルエーテル等が挙げられる。ここでアルキレンオキサイドとしては、エチレンオキサイド及びプロピレンオキサイド等が挙げられる。
As the alicyclic epoxide, cyclohexene oxide obtained by epoxidizing a compound having at least one cycloalkane ring such as cyclohexene or cyclopentene ring with a suitable oxidizing agent such as hydrogen peroxide or peracid. Or a cyclopentene oxide containing compound is mentioned preferably.
Examples of aliphatic epoxides include dihydric polyglycidyl ethers of aliphatic polyhydric alcohols or alkylene oxide adducts thereof, and typical examples thereof include diglycidyl ether of ethylene glycol, diglycidyl ether of propylene glycol, or 1,6. -Diglycidyl ether of alkylene glycol such as diglycidyl ether of hexanediol, polyglycidyl ether of polyhydric alcohol such as di- or triglycidyl ether of glycerin or its alkylene oxide adduct, diglycidyl of polyethylene glycol or its alkylene oxide adduct Diglycidyl of polyalkylene glycol represented by diglycidyl ether of ether, polypropylene glycol or its alkylene oxide adduct Ether and the like. Here, examples of the alkylene oxide include ethylene oxide and propylene oxide.
本発明に用いることのできる単官能及び多官能のエポキシ化合物を詳しく例示する。
単官能エポキシ化合物の例としては、例えば、フェニルグリシジルエーテル、ｐ−ｔｅｒｔ−ブチルフェニルグリシジルエーテル、ブチルグリシジルエーテル、２−エチルヘキシルグリシジルエーテル、アリルグリシジルエーテル、１，２−ブチレンオキサイド、１，３−ブタジエンモノオキサイド、１，２−エポキシドデカン、エピクロロヒドリン、１，２−エポキシデカン、スチレンオキサイド、シクロヘキセンオキサイド、３−メタクリロイルオキシメチルシクロヘキセンオキサイド、３−アクリロイルオキシメチルシクロヘキセンオキサイド、３−ビニルシクロヘキセンオキサイド等が挙げられる。
The monofunctional and polyfunctional epoxy compounds that can be used in the present invention are exemplified in detail.
Examples of monofunctional epoxy compounds include, for example, phenyl glycidyl ether, p-tert-butylphenyl glycidyl ether, butyl glycidyl ether, 2-ethylhexyl glycidyl ether, allyl glycidyl ether, 1,2-butylene oxide, 1,3-butadiene. Monooxide, 1,2-epoxydodecane, epichlorohydrin, 1,2-epoxydecane, styrene oxide, cyclohexene oxide, 3-methacryloyloxymethylcyclohexene oxide, 3-acryloyloxymethylcyclohexene oxide, 3-vinylcyclohexene oxide, etc. Is mentioned.
また、多官能エポキシ化合物の例としては、例えば、ビスフェノールＡジグリシジルエーテル、ビスフェノールＦジグリシジルエーテル、ビスフェノールＳジグリシジルエーテル、臭素化ビスフェノールＡジグリシジルエーテル、臭素化ビスフェノールＦジグリシジルエーテル、臭素化ビスフェノールＳジグリシジルエーテル、エポキシノボラック樹脂、水添ビスフェノールＡジグリシジルエーテル、水添ビスフェノールＦジグリシジルエーテル、水添ビスフェノールＳジグリシジルエーテル、３，４−エポキシシクロヘキシルメチル−３’，４’−エポキシシクロヘキサンカルボキシレート、２−（３，４−エポキシシクロヘキシル−５，５−スピロ−３，４−エポキシ）シクロヘキサン−メタ−ジオキサン、ビス（３，４−エポキシシクロヘキシルメチル）アジペート、ビニルシクロヘキセンオキサイド、４−ビニルエポキシシクロヘキサン、ビス（３，４−エポキシ−６−メチルシクロヘキシルメチル）アジペート、３，４−エポキシ−６−メチルシクロヘキシル−３’，４’−エポキシ−６’−メチルシクロヘキサンカルボキシレート、メチレンビス（３，４−エポキシシクロヘキサン）、ジシクロペンタジエンジエポキサイド、エチレングリコールのジ（３，４−エポキシシクロヘキシルメチル）エーテル、エチレンビス（３，４−エポキシシクロヘキサンカルボキシレート）、エポキシヘキサヒドロフタル酸ジオクチル、エポキシヘキサヒドロフタル酸ジ−２−エチルヘキシル、１，４−ブタンジオールジグリシジルエーテル、１，６−ヘキサンジオールジグリシジルエーテル、グリセリントリグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、ポリプロピレングリコールジグリシジルエーテル類、１，１，３−テトラデカジエンジオキサイド、リモネンジオキサイド、１，２，７，８−ジエポキシオクタン、１，２，５，６−ジエポキシシクロオクタン等が挙げられる。 Examples of polyfunctional epoxy compounds include, for example, bisphenol A diglycidyl ether, bisphenol F diglycidyl ether, bisphenol S diglycidyl ether, brominated bisphenol A diglycidyl ether, brominated bisphenol F diglycidyl ether, and brominated bisphenol. S diglycidyl ether, epoxy novolac resin, hydrogenated bisphenol A diglycidyl ether, hydrogenated bisphenol F diglycidyl ether, hydrogenated bisphenol S diglycidyl ether, 3,4-epoxycyclohexylmethyl-3 ′, 4′-epoxycyclohexanecarboxy 2- (3,4-epoxycyclohexyl-5,5-spiro-3,4-epoxy) cyclohexane-meta-dioxane, bis (3,4-epoxy Hexylmethyl) adipate, vinylcyclohexene oxide, 4-vinylepoxycyclohexane, bis (3,4-epoxy-6-methylcyclohexylmethyl) adipate, 3,4-epoxy-6-methylcyclohexyl-3 ', 4'-epoxy- 6'-methylcyclohexanecarboxylate, methylenebis (3,4-epoxycyclohexane), dicyclopentadiene diepoxide, ethylene glycol di (3,4-epoxycyclohexylmethyl) ether, ethylenebis (3,4-epoxycyclohexanecarboxylate) ), Dioctyl epoxyhexahydrophthalate, di-2-ethylhexyl epoxyhexahydrophthalate, 1,4-butanediol diglycidyl ether, 1,6-hexanediol diglycidyl Ether, glycerin triglycidyl ether, trimethylolpropane triglycidyl ether, polyethylene glycol diglycidyl ether, polypropylene glycol diglycidyl ethers, 1,1,3-tetradecadiene dioxide, limonene dioxide, 1,2,7,8 -Diepoxyoctane, 1,2,5,6-diepoxycyclooctane and the like.
これらのエポキシ化合物のなかでも、芳香族エポキシド及び脂環式エポキシドが、硬化速度に優れるという観点から好ましく、特に脂環式エポキシドが好ましい。 Among these epoxy compounds, aromatic epoxides and alicyclic epoxides are preferable from the viewpoint of excellent curing speed, and alicyclic epoxides are particularly preferable.
ビニルエーテル化合物としては、例えばエチレングリコールジビニルエーテル、ジエチレングリコールジビニルエーテル、トリエチレングリコールジビニルエーテル、プロピレングリコールジビニルエーテル、ジプロピレングリコールジビニルエーテル、ブタンジオールジビニルエーテル、ヘキサンジオールジビニルエーテル、シクロヘキサンジメタノールジビニルエーテル、トリメチロールプロパントリビニルエーテル等のジ又はトリビニルエーテル化合物、エチルビニルエーテル、ｎ−ブチルビニルエーテル、イソブチルビニルエーテル、オクタデシルビニルエーテル、シクロヘキシルビニルエーテル、ヒドロキシブチルビニルエーテル、２−エチルヘキシルビニルエーテル、シクロヘキサンジメタノールモノビニルエーテル、ｎ−プロピルビニルエーテル、イソプロピルビニルエーテル、イソプロペニルエーテル−Ｏ−プロピレンカーボネート、ドデシルビニルエーテル、ジエチレングリコールモノビニルエーテル、オクタデシルビニルエーテル等のモノビニルエーテル化合物等が挙げられる。 Examples of the vinyl ether compound include ethylene glycol divinyl ether, diethylene glycol divinyl ether, triethylene glycol divinyl ether, propylene glycol divinyl ether, dipropylene glycol divinyl ether, butanediol divinyl ether, hexanediol divinyl ether, cyclohexanedimethanol divinyl ether, and trimethylol. Di- or trivinyl ether compounds such as propane trivinyl ether, ethyl vinyl ether, n-butyl vinyl ether, isobutyl vinyl ether, octadecyl vinyl ether, cyclohexyl vinyl ether, hydroxybutyl vinyl ether, 2-ethylhexyl vinyl ether, cyclohexane dimethanol monovinyl ether, n-pro Vinyl ether, isopropyl vinyl ether, isopropenyl ether -O- propylene carbonate, dodecyl vinyl ether, diethylene glycol monovinyl ether, and octadecyl vinyl ether.
以下に、単官能ビニルエーテルと多官能ビニルエーテルを詳しく例示する。
単官能ビニルエーテルの例としては、例えば、メチルビニルエーテル、エチルビニルエーテル、プロピルビニルエーテル、ｎ−ブチルビニルエーテル、ｔ−ブチルビニルエーテル、２−エチルヘキシルビニルエーテル、ｎ−ノニルビニルエーテル、ラウリルビニルエーテル、シクロヘキシルビニルエーテル、シクロヘキシルメチルビニルエーテル、４−メチルシクロヘキシルメチルビニルエーテル、ベンジルビニルエーテル、ジシクロペンテニルビニルエーテル、２−ジシクロペンテノキシエチルビニルエーテル、メトキシエチルビニルエーテル、エトキシエチルビニルエーテル、ブトキシエチルビニルエーテル、メトキシエトキシエチルビニルエーテル、エトキシエトキシエチルビニルエーテル、メトキシポリエチレングリコールビニルエーテル、テトラヒドロフルフリルビニルエーテル、２−ヒドロキシエチルビニルエーテル、２−ヒドロキシプロピルビニルエーテル、４−ヒドロキシブチルビニルエーテル、４−ヒドロキシメチルシクロヘキシルメチルビニルエーテル、ジエチレングリコールモノビニルエーテル、ポリエチレングリコールビニルエーテル、クロルエチルビニルエーテル、クロルブチルビニルエーテル、クロルエトキシエチルビニルエーテル、フェニルエチルビニルエーテル、フェノキシポリエチレングリコールビニルエーテル等が挙げられる。
Below, monofunctional vinyl ether and polyfunctional vinyl ether are illustrated in detail.
Examples of monofunctional vinyl ethers include, for example, methyl vinyl ether, ethyl vinyl ether, propyl vinyl ether, n-butyl vinyl ether, t-butyl vinyl ether, 2-ethylhexyl vinyl ether, n-nonyl vinyl ether, lauryl vinyl ether, cyclohexyl vinyl ether, cyclohexyl methyl vinyl ether, 4 -Methylcyclohexyl methyl vinyl ether, benzyl vinyl ether, dicyclopentenyl vinyl ether, 2-dicyclopentenoxyethyl vinyl ether, methoxyethyl vinyl ether, ethoxyethyl vinyl ether, butoxyethyl vinyl ether, methoxyethoxyethyl vinyl ether, ethoxyethoxyethyl vinyl ether, methoxypolyethylene glycol vinyl D Ter, tetrahydrofurfuryl vinyl ether, 2-hydroxyethyl vinyl ether, 2-hydroxypropyl vinyl ether, 4-hydroxybutyl vinyl ether, 4-hydroxymethylcyclohexyl methyl vinyl ether, diethylene glycol monovinyl ether, polyethylene glycol vinyl ether, chloroethyl vinyl ether, chlorobutyl vinyl ether, chloro Examples thereof include ethoxyethyl vinyl ether, phenylethyl vinyl ether, phenoxypolyethylene glycol vinyl ether and the like.
また、多官能ビニルエーテルの例としては、例えば、エチレングリコールジビニルエーテル、ジエチレングリコールジビニルエーテル、ポリエチレングリコールジビニルエーテル、プロピレングリコールジビニルエーテル、ブチレングリコールジビニルエーテル、ヘキサンジオールジビニルエーテル、ビスフェノールＡアルキレンオキサイドジビニルエーテル、ビスフェノールＦアルキレンオキサイドジビニルエーテルなどのジビニルエーテル類；トリメチロールエタントリビニルエーテル、トリメチロールプロパントリビニルエーテル、ジトリメチロールプロパンテトラビニルエーテル、グリセリントリビニルエーテル、ペンタエリスリトールテトラビニルエーテル、ジペンタエリスリトールペンタビニルエーテル、ジペンタエリスリトールヘキサビニルエーテル、エチレンオキサイド付加トリメチロールプロパントリビニルエーテル、プロピレンオキサイド付加トリメチロールプロパントリビニルエーテル、エチレンオキサイド付加ジトリメチロールプロパンテトラビニルエーテル、プロピレンオキサイド付加ジトリメチロールプロパンテトラビニルエーテル、エチレンオキサイド付加ペンタエリスリトールテトラビニルエーテル、プロピレンオキサイド付加ペンタエリスリトールテトラビニルエーテル、エチレンオキサイド付加ジペンタエリスリトールヘキサビニルエーテル、プロピレンオキサイド付加ジペンタエリスリトールヘキサビニルエーテルなどの多官能ビニルエーテル類等が挙げられる。
ビニルエーテル化合物としては、ジ又はトリビニルエーテル化合物が、硬化性、被記録媒体との密着性、形成された画像の表面硬度などの観点から好ましく、特にジビニルエーテル化合物が好ましい。
Examples of polyfunctional vinyl ethers include ethylene glycol divinyl ether, diethylene glycol divinyl ether, polyethylene glycol divinyl ether, propylene glycol divinyl ether, butylene glycol divinyl ether, hexanediol divinyl ether, bisphenol A alkylene oxide divinyl ether, and bisphenol F. Divinyl ethers such as alkylene oxide divinyl ether; trimethylolethane trivinyl ether, trimethylolpropane trivinyl ether, ditrimethylolpropane tetravinyl ether, glycerin trivinyl ether, pentaerythritol tetravinyl ether, dipentaerythritol pentavinyl ether, dipentaerythritol Hexavinyl ether, ethylene oxide-added trimethylolpropane trivinyl ether, propylene oxide-added trimethylolpropane trivinyl ether, ethylene oxide-added ditrimethylolpropane tetravinyl ether, propylene oxide-added ditrimethylolpropane tetravinyl ether, ethylene oxide-added pentaerythritol tetravinyl ether, propylene oxide addition And polyfunctional vinyl ethers such as pentaerythritol tetravinyl ether, ethylene oxide-added dipentaerythritol hexavinyl ether, and propylene oxide-added dipentaerythritol hexavinyl ether.
As the vinyl ether compound, a di- or trivinyl ether compound is preferable from the viewpoints of curability, adhesion to a recording medium, surface hardness of the formed image, and the like, and a divinyl ether compound is particularly preferable.
本発明に使用できるオキセタン化合物は、少なくとも１つのオキセタン環を有する化合物を指し、特開２００１−２２０５２６号、同２００１−３１０９３７号、同２００３−３４１２１７号の各公報に記載される如き、公知のオキセタン化合物を任意に選択して使用できる。
本発明のインク組成物に使用しうるオキセタン環を有する化合物としては、その構造内にオキセタン環を１〜４個有する化合物が好ましい。このような化合物を使用することで、インク組成物の粘度をハンドリング性の良好な範囲に維持することが容易となり、また、硬化後のインクの被記録媒体との高い密着性を得ることができる。
The oxetane compound that can be used in the present invention refers to a compound having at least one oxetane ring, and is known oxetane as described in JP-A Nos. A compound can be arbitrarily selected and used.
The compound having an oxetane ring that can be used in the ink composition of the present invention is preferably a compound having 1 to 4 oxetane rings in the structure. By using such a compound, it becomes easy to maintain the viscosity of the ink composition in a good handling property range, and it is possible to obtain high adhesion of the cured ink to the recording medium. .
分子内に１〜２個のオキセタン環を有する化合物としては、下記式（１）〜（３）で示される化合物等が挙げられる。 Examples of the compound having 1 to 2 oxetane rings in the molecule include compounds represented by the following formulas (1) to (3).
Ｒa1は、水素原子、炭素数１〜６のアルキル基、炭素数１〜６のフルオロアルキル基、アリル基、アリール基、フリル基又はチエニル基を表す。分子内に２つのＲa1が存在する場合、それらは同じであっても異なるものであってもよい。
アルキル基としては、メチル基、エチル基、プロピル基、ブチル基等が挙げられ、フルオロアルキル基としては、これらアルキル基の水素のいずれかがフッ素原子で置換されたものが好ましく挙げられる。
Ｒa2は、水素原子、炭素数１〜６個のアルキル基、炭素数２〜６個のアルケニル基、芳香環を有する基、炭素数２〜６個のアルキルカルボニル基、炭素数２〜６個のアルコキシカルボニル基、炭素数２〜６個のＮ−アルキルカルバモイル基を表す。アルキル基としては、メチル基、エチル基、プロピル基、ブチル基等が挙げられ、アルケニル基としては、１−プロペニル基、２−プロペニル基、２−メチル−１−プロペニル基、２−メチル−２−プロペニル基、１−ブテニル基、２−ブテニル基、３−ブテニル基等が挙げられ、芳香環を有する基としては、フェニル基、ベンジル基、フルオロベンジル基、メトキシベンジル基、フェノキシエチル基等が挙げられる。アルキルカルボニル基としては、エチルカルボニル基、プロピルカルボニル基、ブチルカルボニル基等が、アルキコキシカルボニル基としては、エトキシカルボニル基、プロポキシカルボニル基、ブトキシカルボニル基等が、Ｎ−アルキルカルバモイル基としては、エチルカルバモイル基、プロピルカルバモイル基、ブチルカルバモイル基、ペンチルカルバモイル基等が挙げられる。また、Ｒa2は置換基を有していても良く、置換基としては、１〜６のアルキル基、フッ素原子が挙げられる。
R a1 represents a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, a fluoroalkyl group having 1 to 6 carbon atoms, an allyl group, an aryl group, a furyl group, or a thienyl group. When two R a1 are present in the molecule, they may be the same or different.
Examples of the alkyl group include a methyl group, an ethyl group, a propyl group, and a butyl group. Preferred examples of the fluoroalkyl group include those in which any hydrogen of these alkyl groups is substituted with a fluorine atom.
R a2 is a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, a group having an aromatic ring, an alkylcarbonyl group having 2 to 6 carbon atoms, or 2 to 6 carbon atoms. Represents an alkoxycarbonyl group, and an N-alkylcarbamoyl group having 2 to 6 carbon atoms. Examples of the alkyl group include a methyl group, an ethyl group, a propyl group, and a butyl group. Examples of the alkenyl group include a 1-propenyl group, a 2-propenyl group, a 2-methyl-1-propenyl group, and 2-methyl-2. -Propenyl group, 1-butenyl group, 2-butenyl group, 3-butenyl group and the like. Examples of the group having an aromatic ring include phenyl group, benzyl group, fluorobenzyl group, methoxybenzyl group, phenoxyethyl group and the like. Can be mentioned. As the alkylcarbonyl group, an ethylcarbonyl group, a propylcarbonyl group, a butylcarbonyl group, etc., as an alkoxycarbonyl group, an ethoxycarbonyl group, a propoxycarbonyl group, a butoxycarbonyl group, etc., as an N-alkylcarbamoyl group, Examples thereof include an ethylcarbamoyl group, a propylcarbamoyl group, a butylcarbamoyl group, and a pentylcarbamoyl group. R a2 may have a substituent, and examples of the substituent include an alkyl group of 1 to 6 and a fluorine atom.
Ｒa3は、線状又は分枝状アルキレン基、線状又は分枝状ポリ（アルキレンオキシ）基、線状又は分枝状不飽和炭化水素基、カルボニル基又はカルボニル基を含むアルキレン基、カルボキシル基を含むアルキレン基、カルバモイル基を含むアルキレン基、又は、以下に示す基を表す。アルキレン基としては、例えば、エチレン基、プロピレン基、ブチレン基が挙げられ、ポリ（アルキレンオキシ）基としては、ポリ（エチレンオキシ）基、ポリ（プロピレンオキシ）基等が挙げられる。不飽和炭化水素基としては、プロペニレン基、メチルプロペニレン基、ブテニレン基等が挙げられる。 R a3 is a linear or branched alkylene group, a linear or branched poly (alkyleneoxy) group, a linear or branched unsaturated hydrocarbon group, a carbonyl group or an alkylene group containing a carbonyl group, a carboxyl group Represents an alkylene group containing, an alkylene group containing a carbamoyl group, or a group shown below. Examples of the alkylene group include an ethylene group, a propylene group, and a butylene group. Examples of the poly (alkyleneoxy) group include a poly (ethyleneoxy) group and a poly (propyleneoxy) group. Examples of the unsaturated hydrocarbon group include a propenylene group, a methylpropenylene group, and a butenylene group.
Ｒa3が上記多価基である場合、Ｒa4は、水素原子、炭素数１〜４個のアルキル基、炭素数１〜４個のアルコキシ基、ハロゲン原子、ニトロ基、シアノ基、メルカプト基、低級アルキルカルボキシル基、カルボキシル基、又はカルバモイル基を表す。
Ｒa5は、酸素原子、硫黄原子、メチレン基、ＮＨ、ＳＯ、ＳＯ2、Ｃ（ＣＦ3）2、又は、Ｃ（ＣＨ3）2を表す。
Ｒa6は、炭素数１〜４個のアルキル基、又は、アリール基を表し、ｎは０〜２，０００の整数である。Ｒa7は炭素数１〜４個のアルキル基、アリール基、又は、下記構造を有する１価の基を表す。下記式中、Ｒa8は炭素数１〜４個のアルキル基、又はアリール基であり、ｍは０〜１００の整数である。
When R a3 is the above polyvalent group, R a4 is a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, a halogen atom, a nitro group, a cyano group, a mercapto group, Represents a lower alkyl carboxyl group, a carboxyl group, or a carbamoyl group.
R a5 represents an oxygen atom, a sulfur atom, a methylene group, NH, SO, SO 2 , C (CF 3 ) 2 , or C (CH 3 ) 2 .
R a6 represents an alkyl group having 1 to 4 carbon atoms or an aryl group, and n is an integer of 0 to 2,000. R a7 represents an alkyl group having 1 to 4 carbon atoms, an aryl group, or a monovalent group having the following structure. In the following formula, R a8 is an alkyl group having 1 to 4 carbon atoms or an aryl group, and m is an integer of 0 to 100.
式（１）で表される化合物として、３−エチル−３−ヒドロキシメチルオキセタン（ＯＸＴ−１０１：東亞合成（株）製）、３−エチル−３−（２−エチルヘキシロキシメチル）オキセタン（ＯＸＴ−２１２：東亞合成（株）製）、３−エチル−３−フェノキシメチルオキセタン（ＯＸＴ−２１１：東亞合成（株）製）が挙げられる。式（２）で表される化合物としては、１，４−ビス［（３−エチル−３−オキセタニルメトキシ）メチル］ベンゼン（ＯＸＴ−１２１：東亞合成（株）が挙げられる。また、式（３）で表される化合物としては、ビス（３−エチル−３−オキセタニルメチル）エーテル（ＯＸＴ−２２１：東亞合成（株））が挙げられる。 As a compound represented by the formula (1), 3-ethyl-3-hydroxymethyloxetane (OXT-101: manufactured by Toagosei Co., Ltd.), 3-ethyl-3- (2-ethylhexyloxymethyl) oxetane (OXT) -212: manufactured by Toagosei Co., Ltd.) and 3-ethyl-3-phenoxymethyloxetane (OXT-211: manufactured by Toagosei Co., Ltd.). Examples of the compound represented by the formula (2) include 1,4-bis [(3-ethyl-3-oxetanylmethoxy) methyl] benzene (OXT-121: Toagosei Co., Ltd.). ), Bis (3-ethyl-3-oxetanylmethyl) ether (OXT-221: Toagosei Co., Ltd.) is exemplified.
３〜４個のオキセタン環を有する化合物としては、下記式（４）で示される化合物が挙げられる。 Examples of the compound having 3 to 4 oxetane rings include a compound represented by the following formula (4).
式（４）において、Ｒa1は、前記式（１）におけるのと同義である。また、他か連結基であるＲa9としては、例えば、下記Ａ〜Ｃで示される基等の炭素数１〜１２の分枝状アルキレン基、下記Ｄで示される基等の分枝状ポリ（アルキレンオキシ）基又は下記Ｅで示される基等の分枝状ポリシロキシ基等が挙げられる。ｊは、３又は４である。 In the formula (4), R a1 has the same meaning as in the formula (1). Other examples of Ra 9 as a linking group include branched alkylene groups having 1 to 12 carbon atoms such as groups represented by the following A to C and branched poly ( An alkyleneoxy) group or a branched polysiloxy group such as a group represented by E below. j is 3 or 4.
上記Ａにおいて、Ｒa10はメチル基、エチル基又はプロピル基を表す。また、上記Ｄにおいて、ｐは１〜１０の整数である。 In the above A, R a10 represents a methyl group, an ethyl group or a propyl group. Moreover, in said D, p is an integer of 1-10.
また、本発明に好適に使用しうるオキセタン化合物の別の態様として、側鎖にオキセタン環を有する下記式（５）で示される化合物が挙げられる。 Another embodiment of the oxetane compound that can be suitably used in the present invention includes a compound represented by the following formula (5) having an oxetane ring in the side chain.
式（５）において、Ｒa8は前記式におけるのと同義である。Ｒa11はメチル基、エチル基、プロピル基又はブチル基等の炭素数１〜４のアルキル基又はトリアルキルシリル基であり、ｒは１〜４である。 In the formula (5), R a8 has the same meaning as in the above formula. R a11 is an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, a propyl group, or a butyl group, or a trialkylsilyl group, and r is 1 to 4.
このようなオキセタン環を有する化合物については、前記特開２００３−３４１２１７号公報、段落番号００２１ないし００８４に詳細に記載され、ここに記載の化合物は本発明にも好適に使用しうる。
特開２００４−９１５５６号公報に記載されたオキセタン化合物も本発明に使用することができる。段落番号００２２ないし００５８に詳細に記載されている。
本発明で使用するオキセタン化合物のなかでも、インク組成物の粘度と粘着性の観点から、オキセタン環を１個有する化合物を使用することが好ましい。
Such a compound having an oxetane ring is described in detail in JP-A-2003-341217, paragraphs 0021 to 0084, and the compounds described herein can be suitably used in the present invention.
Oxetane compounds described in JP 2004-91556 A can also be used in the present invention. Details are described in paragraphs 0022 to 0058.
Among the oxetane compounds used in the present invention, it is preferable to use a compound having one oxetane ring from the viewpoint of the viscosity and tackiness of the ink composition.
本発明に用いることのできる（ａ）カチオン重合性化合物は、１種のみを用いても、２種以上を併用してもよいが、インク硬化時の収縮を効果的に抑制するといった観点からは、オキセタン化合物とエポキシ化合物から選ばれる少なくとも１種の化合物と、ビニルエーテル化合物とを併用することが好ましい。
インク組成物中の（ａ）カチオン重合性化合物の含量は、組成物の全固形分に対し、１０〜９５重量％が好ましく適当であり、より好ましくは３０〜９０重量％、更に好ましくは５０〜８５重量％の範囲である。
The cationic polymerizable compound (a) that can be used in the present invention may be used alone or in combination of two or more, but from the viewpoint of effectively suppressing shrinkage during ink curing. It is preferable to use a vinyl ether compound in combination with at least one compound selected from oxetane compounds and epoxy compounds.
The content of the cationic polymerizable compound (a) in the ink composition is preferably 10 to 95% by weight, more preferably 30 to 90% by weight, and still more preferably 50 to 50% by weight based on the total solid content of the composition. It is in the range of 85% by weight.
［（ｂ）放射線の照射により酸を発生する化合物］
本発明のインク組成物は、（ｂ）放射線の照射により酸を発生する化合物（以下、「光酸発生剤」とも称する。）を含有する。
本発明のインク組成物に用いることのできる光酸発生剤としては、光カチオン重合の光開始剤、光ラジカル重合の光開始剤、色素類の光消色剤、光変色剤、あるいはマイクロレジスト等に使用されている光（４００〜２００ｎｍの紫外線、遠紫外線、特に好ましくは、ｇ線、ｈ線、ｉ線、ＫｒＦエキシマレーザー光）、ＡｒＦエキシマレーザー光、電子線、Ｘ線、分子線又はイオンビームなどの照射により酸を発生する化合物を適宜選択して使用することができる。
[(B) Compound generating acid upon irradiation]
The ink composition of the present invention contains (b) a compound that generates an acid upon irradiation with radiation (hereinafter also referred to as a “photoacid generator”).
Examples of the photoacid generator that can be used in the ink composition of the present invention include a photoinitiator for photocationic polymerization, a photoinitiator for radical photopolymerization, a photodecolorant for dyes, a photochromic agent, and a microresist. Light (400-200 nm ultraviolet light, far ultraviolet light, particularly preferably g-line, h-line, i-line, KrF excimer laser light), ArF excimer laser light, electron beam, X-ray, molecular beam or ion A compound that generates an acid upon irradiation with a beam or the like can be appropriately selected and used.
このような光酸発生剤としては、放射線の照射により分解して酸を発生する、ジアゾニウム塩、ホスホニウム塩、スルホニウム塩、ヨードニウム塩などのオニウム塩化合物、イミドスルホネート、オキシムスルホネート、ジアゾジスルホン、ジスルホン、ｏ−ニトロベンジルスルホネート等のスルホネート化合物などを挙げることができる。 Examples of such a photoacid generator include an onium salt compound such as diazonium salt, phosphonium salt, sulfonium salt, iodonium salt, imide sulfonate, oxime sulfonate, diazodisulfone, disulfone, which decomposes upon irradiation with radiation to generate an acid. Examples thereof include sulfonate compounds such as o-nitrobenzyl sulfonate.
また、その他の本発明に用いられる活性光線又は放射線の照射により酸を発生する化合物（光酸発生剤）としては、例えば、Ｓ．Ｉ．Ｓｃｈｌｅｓｉｎｇｅｒ，Ｐｈｏｔｏｇｒ．Ｓｃｉ．Ｅｎｇ．，１８，３８７（１９７４）、Ｔ．Ｓ．Ｂａｌ ｅｔａｌ，Ｐｏｌｙｍｅｒ，２１，４２３（１９８０）等に記載のジアゾニウム塩、米国特許第４，０６９，０５５号、同４，０６９，０５６号、同 Ｒｅ ２７，９９２号、特開平３−１４０１４０号等に記載のアンモニウム塩、Ｄ．Ｃ．Ｎｅｃｋｅｒ ｅｔａｌ，Ｍａｃｒｏｍｏｌｅｃｕｌｅｓ，１７，２４６８（１９８４）、Ｃ．Ｓ．Ｗｅｎ ｅｔａｌ，Ｔｅｈ，Ｐｒｏｃ．Ｃｏｎｆ．Ｒａｄ．Ｃｕｒｉｎｇ ＡＳＩＡ，ｐ４７８ Ｔｏｋｙｏ，Ｏｃｔ（１９８８）、米国特許第４，０６９，０５５ 号、同４，０６９，０５６号等に記載のホスホニウム塩、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔａｌ，Ｍａｃｒｏｍｏｒｅｃｕｌｅｓ，１０（６），１３０７（１９７７）、Ｃｈｅｍ．＆Ｅｎｇ．Ｎｅｗｓ，Ｎｏｖ．２８，ｐ３１（１９８８）、欧州特許第１０４，１４３号、同第３３９，０４９号、同第４１０，２０１号、特開平２−１５０８４８号、特開平２−２９６５１４号等に記載のヨードニウム塩、 Other compounds (photoacid generators) that generate acid upon irradiation with actinic rays or radiation used in the present invention include, for example, S.I. I. Schlesinger, Photogr. Sci. Eng. , 18, 387 (1974), T.A. S. Diazonium salts described in Bal etal, Polymer, 21, 423 (1980), U.S. Pat. Nos. 4,069,055, 4,069,056, Re 27,992, JP-A-3-140140, etc. An ammonium salt according to claim 1, C. Necker et al., Macromolecules, 17, 2468 (1984), C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988), U.S. Pat. Nos. 4,069,055, 4,069,056, and the like; V. Crivello et al, Macromolecules, 10 (6), 1307 (1977), Chem. & Eng. News, Nov. 28, p31 (1988), European Patent Nos. 104,143, 339,049, 410,201, JP-A-2-150848, JP-A-2-296514 and the like,
Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔａｌ，Ｐｏｌｙｍｅｒ Ｊ．１７，７３ （１９８５）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔａｌ．Ｊ．Ｏｒｇ．Ｃｈｅｍ．，４３，３０５５（１９７８）、Ｗ．Ｒ．Ｗａｔｔ ｅｔａｌ，Ｊ．ＰｏｌｙｍｅｒＳｃｉ．，Ｐｏｌｙｍｅｒ Ｃｈｅｍ．Ｅｄ．，２２，１７８９（１９８４）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔａｌ，Ｐｏｌｙｍｅｒ Ｂｕｌｌ．，１４，２７９（１９８５）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔａｌ，Ｍａｃｒｏｍｏｒｅｃｕｌｅｓ，１４（５），１１４１（１９８１）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏｅｔａｌ，Ｊ．ＰｏｌｙｍｅｒＳｃｉ．，Ｐｏｌｙｍｅｒ Ｃｈｅｍ．Ｅｄ．，１７，２８７７（１９７９）、欧州特許第３７０，６９３号、同１６１，８１１号、同４１０，２０１号、同３３９，０４９号、同２３３，５６７号、同２９７，４４３号、同２９７，４４２号、米国特許第３，９０２，１１４号、同４，９３３，３７７号、同４，７６０，０１３号、同４，７３４，４４４号、同２，８３３，８２７号、独国特許第２，９０４，６２６号、同３，６０４，５８０号、同３，６０４，５８１号、特開平７−２８２３７号、同８−２７１０２号等に記載のスルホニウム塩、 J. et al. V. Crivello et al, Polymer J. et al. 17, 73 (1985), J. MoI. V. Crivello et al. J. et al. Org. Chem. 43, 3055 (1978); R. Watt et al. PolymerSci. , Polymer Chem. Ed. , 22, 1789 (1984), J. Am. V. Crivello et al., Polymer Bull. 14, 279 (1985), J. Am. V. Crivello et al, Macromolecules, 14 (5), 1141 (1981), J. MoI. V. Crivello et al. PolymerSci. , Polymer Chem. Ed. 17, 2877 (1979), European Patent Nos. 370,693, 161,811, 410,201, 339,049, 233,567, 297,443, and 297,442. U.S. Pat.Nos. 3,902,114, 4,933,377, 4,760,013, 4,734,444, 2,833,827, German Patent 2, Nos. 904, 626, 3,604, 580, 3,604, 581, JP-A-7-28237, 8-27102, etc.,
Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔａｌ，Ｍａｃｒｏｍｏｒｅｃｕｌｅｓ，１０（６），１３０７（１９７７）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔａｌ，Ｊ．ＰｏｌｙｍｅｒＳｃｉ．，Ｐｏｌｙｍｅｒ Ｃｈｅｍ．Ｅｄ．，１７，１０４７（１９７９）等に記載のセレノニウム塩、Ｃ．Ｓ．Ｗｅｎ ｅｔａｌ，Ｔｅｈ，Ｐｒｏｃ．Ｃｏｎｆ．Ｒａｄ．Ｃｕｒｉｎｇ ＡＳＩＡ，ｐ４７８ Ｔｏｋｙｏ，Ｏｃｔ（１９８８）等に記載のアルソニウム塩等のオニウム塩、米国特許第３，９０５，８１５号、特公昭４６−４６０５号、特開昭４８−３６２８１号、特開昭５５−３２０７０号、特開昭６０−２３９７３６号、特開昭６１−１６９８３５号、特開昭６１−１６９８３７号、特開昭６２−５８２４１号、特開昭６２−２１２４０１号、特開昭６３−７０２４３号、特開昭６３−２９８３３９号等に記載の有機ハロゲン化合物、Ｋ．Ｍｅｉｅｒ ｅｔ ａｌ，Ｊ．Ｒａｄ．Ｃｕｒｉｎｇ，１３（４），２６（１９８６）、Ｔ．Ｐ．Ｇｉｌｌ ｅｔ ａｌ，Ｉｎｏｒｇ．Ｃｈｅｍ．，１９，３００７（１９８０）、Ｄ．Ａｓｔｒｕｃ，Ａｃｃ．Ｃｈｅｍ．Ｒｅｓ．，１９（１２），３７７（１９８６）、特開平２−１６１４４５号等に記載の有機金属／有機ハロゲン化物、 J. et al. V. Crivello et al., Macromolecules, 10 (6), 1307 (1977), J. MoI. V. Crivello et al. PolymerSci. , Polymer Chem. Ed. , 17, 1047 (1979), etc., selenonium salts, C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988) and other onium salts such as arsonium salts, US Pat. No. 3,905,815, Japanese Examined Patent Publication No. 46-4605, Japanese Unexamined Patent Publication No. 48-36281, Japanese Unexamined Patent Publication No. 55-55. -32070, JP-A-60-239736, JP-A-61-169835, JP-A-61-169837, JP-A-62-58241, JP-A-62-212401, JP-A-63-70243 , Organic halogen compounds described in JP-A-63-298339 and the like; Meier et al, J.A. Rad. Curing, 13 (4), 26 (1986), T.A. P. Gill et al, Inorg. Chem. , 19, 3007 (1980), D.M. Astruc, Acc. Chem. Res. , 19 (12), 377 (1986), and organometallic / organic halides described in JP-A-2-161445, etc.
Ｓ．Ｈａｙａｓｅ ｅｔａｌ，Ｊ．Ｐｏｌｙｍｅｒ Ｓｃｉ．，２５，７５３（１９８７）、Ｅ．Ｒｅｉｃｈｍａｎｉｓ ｅｔａｌ，Ｊ．Ｐｈｏｌｙｍｅｒ Ｓｃｉ．，Ｐｏｌｙｍｅｒ Ｃｈｅｍ．Ｅｄ．，２３，１（１９８５）、Ｑ．Ｑ．Ｚｈｕ ｅｔａｌ，Ｊ．Ｐｈｏｔｏｃｈｅｍ．，３６，８５，３９，３１７（１９８７）、Ｂ．Ａｍｉｔ ｅｔａｌ，Ｔｅｔｒａｈｅｄｒｏｎ Ｌｅｔｔ．，（２４）２２０５（１９７３）、Ｄ．Ｈ．Ｒ．Ｂａｒｔｏｎ ｅｔａｌ，Ｊ．Ｃｈｅｍ．Ｓｏｃ．，３５７１（１９６５）、Ｐ．Ｍ．Ｃｏｌｌｉｎｓ ｅｔ ａｌ，Ｊ．Ｃｈｅｍ．Ｓｏｃ．，Ｐｅｒｋｉｎ Ｉ，１６９５（１９７５）、Ｍ．Ｒｕｄｉｎｓｔｅｉｎ ｅｔａｌ，Ｔｅｔｒａｈｅｄｒｏｎ Ｌｅｔｔ．，（１７），１４４５（１９７５）、Ｊ．Ｗ．Ｗａｌｋｅｒ ｅｔａｌ，Ｊ．Ａｍ．Ｃｈｅｍ．Ｓｏｃ．，１１０，７１７０（１９８８）、Ｓ．Ｃ．Ｂｕｓｍａｎ ｅｔａｌ，Ｊ．Ｉｍａｇｉｎｇ Ｔｅｃｈｎｏｌ．，１１（４），１９１（１９８５）、Ｈ．Ｍ．Ｈｏｕｌｉｈａｎ ｅｔａｌ，Ｍａｃｏｒｍｏｌｅｃｕｌｅｓ，２１，２００１（１９８８）、Ｐ．Ｍ．Ｃｏｌｌｉｎｓ ｅｔａｌ，Ｊ．Ｃｈｅｍ．Ｓｏｃ．，Ｃｈｅｍ．Ｃｏｍｍｕｎ．，５３２（１９７２）、Ｓ．Ｈａｙａｓｅ ｅｔａｌ，Ｍａｃｒｏｍｏｌｅｃｕｌｅｓ，１８，１７９９（１９８５）、Ｅ．Ｒｅｉｃｈｍａｎｉｓ ｅｔａｌ，Ｊ．Ｅｌｅｃｔｒｏｃｈｅｍ．Ｓｏｃ．，Ｓｏｌｉｄ Ｓｔａｔｅ Ｓｃｉ．Ｔｅｃｈｎｏｌ．，１３０（６）、Ｆ．Ｍ．Ｈｏｕｌｉｈａｎ ｅｔａｌ，Ｍａｃｒｏｍｏｌｃｕｌｅｓ，２１，２００１（１９８８）、 欧州特許第０２９０，７５０号、同０４６，０８３号、同１５６，５３５号、同２７１，８５１号、同０，３８８，３４３号、米国特許第３，９０１，７１０号、同４，１８１，５３１号、特開昭６０−１９８５３８号、特開昭５３−１３３０２２号等に記載のＯ−ニトロベンジル型保護基を有する光酸発生剤、 S. Hayase et al. Polymer Sci. 25, 753 (1987), E.I. Reichmanis et al. Polymer Sci. , Polymer Chem. Ed. , 23, 1 (1985), Q.M. Q. Zhu etal, J. et al. Photochem. 36, 85, 39, 317 (1987), B.R. Amit etal, Tetrahedron Lett. , (24) 2205 (1973), D.M. H. R. Barton et al. Chem. Soc. , 3571 (1965), p. M.M. Collins et al, J.A. Chem. Soc. Perkin I, 1695 (1975), M .; Rudinstein et al., Tetrahedron Lett. , (17), 1445 (1975), J. MoI. W. Walker et al. Am. Chem. Soc. 110, 7170 (1988), S.A. C. Busman et al. Imaging Technol. 11 (4), 191 (1985), H. et al. M.M. Houlihan et al, Macormolecules, 21, 2001 (1988), p. M.M. Collins et al. Chem. Soc. , Chem. Commun. 532 (1972), S.A. Hayase et al., Macromolecules, 18, 1799 (1985), E.I. Reichmanis et al. Electrochem. Soc. , Solid State Sci. Technol. , 130 (6), F.M. M.M. Houlihan et al, Macromolecules, 21, 2001 (1988), European Patent Nos. 0290,750, 046,083, 156,535, 271,851, 0,388,343, US Patent No. 3 , 901,710, 4,181,531, JP-A-60-198538, JP-A-53-133022 and the like, a photoacid generator having an O-nitrobenzyl type protecting group,
Ｍ．ＴＵＮＯＯＫＡ ｅｔａｌ，Ｐｏｌｙｍｅｒ Ｐｒｅｐｒｉｎｔｓ Ｊａｐａｎ，３５（８）、Ｇ．Ｂｅｒｎｅｒ ｅｔａｌ，Ｊ．Ｒａｄ．Ｃｕｒｉｎｇ，１３（４）、Ｗ．Ｊ．Ｍｉｊｓ ｅｔａｌ，Ｃｏａｔｉｎｇ Ｔｅｃｈｎｏｌ．，５５（６９７），４５（１９８３），Ａｋｚｏ、Ｈ．Ａｄａｃｈｉ ｅｔａｌ，Ｐｏｌｙｍｅｒ Ｐｒｅｐｒｉｎｔｓ，Ｊａｐａｎ，３７（３）、欧州特許第０１９９，６７２号、同８４５１５号、同０４４，１１５号、同第６１８，５６４号、同０１０１，１２２号、米国特許第４，３７１，６０５号、同４，４３１，７７４号、特開昭６４−１８１４３号、特開平２−２４５７５６号、特開平３−１４０１０９号等に記載のイミノスルフォネ−ト等に代表される光分解してスルホン酸を発生する化合物、特開昭６１−１６６５４４号、特開平２−７１２７０号等に記載のジスルホン化合物、特開平３−１０３８５４号、同３−１０３８５６号、同４−２１０９６０号等に記載のジアゾケトスルホン、ジアゾジスルホン化合物を挙げることができる。 M.M. TUNOOKA et al, Polymer Preprints Japan, 35 (8), G.M. Berner et al. Rad. Curing, 13 (4), W.M. J. et al. Mijs et al, Coating Technol. , 55 (697), 45 (1983), Akzo, H .; Adachi et al, Polymer Preprints, Japan, 37 (3), European Patent No. 0199,672, No. 84515, No. 044,115, No. 618,564, No. 0101,122, US Pat. No. 4,371 , 605, 4,431,774, JP-A 64-18143, JP-A-2-245756, JP-A-3-140109, and the like. Compounds generating an acid, disulfone compounds described in JP-A-61-1166544 and JP-A-2-71270, diazo compounds described in JP-A-3-103854, JP-A-3-103856, and JP-A-4-210960 Examples thereof include ketosulfone and diazodisulfone compounds.
また、これらの光により酸を発生する基、あるいは化合物をポリマーの主鎖又は側鎖に導入した化合物、たとえば、Ｍ．Ｅ．Ｗｏｏｄｈｏｕｓｅ ｅｔ ａｌ，Ｊ．Ａｍ．Ｃｈｅｍ．Ｓｏｃ．，１０４，５５８６（１９８２）、Ｓ．Ｐ．Ｐａｐｐａｓ ｅｔ ａｌ，Ｊ．Ｉｍａｇｉｎｇ Ｓｃｉ．，３０（５），２１８（１９８６）、Ｓ．Ｋｏｎｄｏ ｅｔａｌ，Ｍａｋｒｏｍｏｌ．Ｃｈｅｍ．，Ｒａｐｉｄ Ｃｏｍｍｕｎ．，９，６２５（１９８８）、Ｙ．Ｙａｍａｄａ ｅｔａｌ，Ｍａｋｒｏｍｏｌ．Ｃｈｅｍ．，１５２，１５３，１６３（１９７２）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔ ａｌ，Ｊ．ＰｏｌｙｍｅｒＳｃｉ．，Ｐｏｌｙｍｅｒ Ｃｈｅｍ．Ｅｄ．，１７，３８４５（１９７９）、米国特許第３，８４９，１３７号、独国特許第３，９１４，４０７号、特開昭６３−２６６５３号、特開昭５５−１６４８２４号、特開昭６２−６９２６３号、特開昭６３−１４６０３８号、特開昭６３−１６３４５２号、特開昭６２−１５３８５３号、特開昭６３−１４６０２９号等に記載の化合物を用いることができる。たとえば、ジアゾニウム塩、アンモニウム塩、ホスホニウム塩、ヨードニウム塩、スルホニウム塩、セレノニウム塩、アルソニウム塩等のオニウム塩、有機ハロゲン化合物、有機金属／有機ハロゲン化物、ｏ−ニトロベンジル型保護基を有する光酸発生剤、イミノスルフォネート等に代表される光分解してスルホン酸を発生する化合物、ジスルホン化合物、ジアゾケトスルホン、ジアゾジスルホン化合物を挙げることができる。 Further, a group which generates an acid by these light, or a compound in which a compound is introduced into the main chain or side chain of the polymer, for example, M.I. E. Woodhouse et al., J. MoI. Am. Chem. Soc. 104, 5586 (1982), S .; P. Pappas et al. Imaging Sci. , 30 (5), 218 (1986), S .; Kondo et al, Makromol. Chem. , Rapid Commun. , 9, 625 (1988), Y. et al. Yamada et al, Makromol. Chem. 152, 153, 163 (1972), J. Am. V. Crivello et al, J.A. PolymerSci. , Polymer Chem. Ed. 17, 3845 (1979), U.S. Pat. No. 3,849,137, German Patent No. 3,914,407, JP-A 63-26653, JP-A 55-164824, JP-A 62- 69263, JP-A 63-146038, JP-A 63-163452, JP-A 62-153853, JP-A 63-146029, and the like can be used. For example, diazonium salts, ammonium salts, phosphonium salts, iodonium salts, sulfonium salts, selenonium salts, onium salts such as arsonium salts, organic halogen compounds, organic metal / organic halides, photoacid generators having o-nitrobenzyl type protecting groups Examples thereof include a compound capable of generating a sulfonic acid by photolysis represented by an agent, iminosulfonate, and the like, a disulfone compound, a diazoketosulfone, and a diazodisulfone compound.
さらにＶ．Ｎ．Ｒ．Ｐｉｌｌａｉ，Ｓｙｎｔｈｅｓｉｓ，（１），１（１９８０）、Ａ．Ａｂａｄ ｅｔａｌ，Ｔｅｔｒａｈｅｄｒｏｎ Ｌｅｔｔ．，（４７）４５５５（１９７１）、Ｄ．Ｈ．Ｒ．Ｂａｒｔｏｎ ｅｔ ａｌ，Ｊ．Ｃｈｅｍ．Ｓｏｃ．，（Ｃ），３２９（１９７０）、米国特許第３，７７９，７７８号、欧州特許第１２６，７１２号等に記載の光により酸を発生する化合物も使用することができる。 Furthermore, V. N. R. Pillai, Synthesis, (1), 1 (1980), A.M. Abad et al., Tetrahedron Lett. , (47) 4555 (1971), D.M. H. R. Barton et al, J.A. Chem. Soc. , (C), 329 (1970), U.S. Pat. No. 3,779,778, European Patent No. 126,712, and the like, compounds that generate an acid by light can also be used.
本発明に用いることができる光酸発生剤として好ましい化合物として、下記式（ｂ１）、（ｂ２）、（ｂ３）で表される化合物を挙げることができる。 Preferred examples of the photoacid generator that can be used in the present invention include compounds represented by the following formulas (b1), (b2), and (b3).
式（ｂ１）において、Ｒ201、Ｒ202及びＲ203は、各々独立に有機基を表す。
Ｘ-は、非求核性アニオンを表し、好ましくはスルホン酸アニオン、カルボン酸アニオン、ビス（アルキルスルホニル）アミドアニオン、トリス（アルキルスルホニル）メチドアニオン、ＢＦ4 -、ＰＦ6 -、ＳｂＦ6 -や以下に示す基などが挙げられ、好ましくは炭素原子を有する有機アニオンである。
In the formula (b1), R 201 , R 202 and R 203 each independently represents an organic group.
X − represents a non-nucleophilic anion, preferably a sulfonate anion, a carboxylate anion, a bis (alkylsulfonyl) amide anion, a tris (alkylsulfonyl) methide anion, BF 4 − , PF 6 − , SbF 6 − or the following The organic anion which has a carbon atom is preferable.
好ましい有機アニオンとしては下式に示す有機アニオンが挙げられる。 Preferable organic anions include organic anions represented by the following formula.
Ｒｃ1は、有機基を表す。
Ｒｃ1における有機基として炭素数１〜３０のものが挙げられ、好ましくはアルキル基、シクロアルキル基、アリール基、またはこれらの複数が、単結合、−Ｏ−、−ＣＯ2−、−Ｓ−、−ＳＯ3−、−ＳＯ2Ｎ（Ｒｄ1）−などの連結基で連結された基を挙げることができる。
Rc 1 represents an organic group.
Examples of the organic group in Rc 1 include those having 1 to 30 carbon atoms, and preferably an alkyl group, a cycloalkyl group, an aryl group, or a plurality of these are a single bond, —O—, —CO 2 —, —S—. , —SO 3 —, —SO 2 N (Rd 1 ) — and the like.
Ｒｄ1は、水素原子、アルキル基を表す。
Ｒｃ3、Ｒｃ4、Ｒｃ5は、各々独立に、有機基を表す。
Ｒｃ3、Ｒｃ4、Ｒｃ5の有機基として、好ましくはＲｃ1における好ましい有機基と同じものを挙げることができ、最も好ましくは炭素数１〜４のパーフロロアルキル基である。
Ｒｃ3とＲｃ4が結合して環を形成していてもよい。
Ｒｃ3とＲｃ4が結合して形成される基としてはアルキレン基、アリーレン基が挙げられる。好ましくは炭素数２〜４のパーフロロアルキレン基である。
Rd 1 represents a hydrogen atom or an alkyl group.
Rc 3 , Rc 4 and Rc 5 each independently represents an organic group.
Preferred examples of the organic group for Rc 3 , Rc 4 , and Rc 5 include the same organic groups as those for Rc 1 , and most preferably a perfluoroalkyl group having 1 to 4 carbon atoms.
Rc 3 and Rc 4 may combine to form a ring.
Examples of the group formed by combining Rc 3 and Rc 4 include an alkylene group and an arylene group. Preferably, it is a C2-C4 perfluoroalkylene group.
Ｒｃ1、Ｒｃ3〜Ｒｃ5の有機基として、最も好ましくは１位がフッ素原子またはフロロアルキル基で置換されたアルキル基、フッ素原子またはフロロアルキル基で置換されたフェニル基である。フッ素原子またはフロロアルキル基を有することにより、光照射によって発生した酸の酸性度が上がり、感度が向上する。 The organic group of Rc 1 and Rc 3 to Rc 5 is most preferably an alkyl group substituted at the 1-position with a fluorine atom or a fluoroalkyl group, or a phenyl group substituted with a fluorine atom or a fluoroalkyl group. By having a fluorine atom or a fluoroalkyl group, the acidity of the acid generated by light irradiation is increased and the sensitivity is improved.
Ｒ201、Ｒ202及びＲ203としての有機基の炭素数は、一般的に１〜３０、好ましくは１〜２０である。
また、Ｒ201〜Ｒ203のうち２つが結合して環構造を形成してもよく、環内に酸素原子、硫黄原子、エステル結合、アミド結合、カルボニル基を含んでいてもよい。Ｒ201〜Ｒ203の内の２つが結合して形成する基としては、アルキレン基（例えば、ブチレン基、ペンチレン基）を挙げることができる。
The carbon number of the organic group as R 201 , R 202 and R 203 is generally 1-30, preferably 1-20.
Two of R 201 to R 203 may be bonded to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group. The two of the group formed by bonding of the R 201 to R 203, there can be mentioned an alkylene group (e.g., butylene, pentylene).
Ｒ201、Ｒ202及びＲ203としての有機基の具体例としては、後述する化合物（ｂ１−１）、（ｂ１−２）、（ｂ１−３）における対応する基を挙げることができる。 Specific examples of the organic group as R 201 , R 202 and R 203 include corresponding groups in the compounds (b1-1), (b1-2) and (b1-3) described later.
なお、式（ｂ１）で表される構造を複数有する化合物であってもよい。例えば、式（ｂ１）で表される化合物のＲ201〜Ｒ203のうち少なくともひとつが、式（ｂ１）で表される他の化合物におけるＲ201〜Ｒ203の少なくともひとつと直接、又は、連結基を介して結合した構造を有する化合物であってもよい。 In addition, the compound which has two or more structures represented by Formula (b1) may be sufficient. For example, at least one of R 201 to R 203 of a compound represented by the formula (b1) is at least one directly with R 201 to R 203 of another compound represented by formula (b1), or a linking group It may be a compound having a structure bonded via
更に好ましい（ｂ１）成分として、以下に説明する化合物（ｂ１−１）、（ｂ１−２）、及び（ｂ１−３）を挙げることができる。 Further preferred examples of the component (b1) include compounds (b1-1), (b1-2), and (b1-3) described below.
化合物（ｂ１−１）は、上記式（ｂ１）のＲ201〜Ｒ203の少なくとも１つがアリール基である、アリールスルホニム化合物、即ち、アリールスルホニウムをカチオンとする化合物である。 Compound (b1-1) is in which at least one aryl group R 201 to R 203 in formula (b1), arylsulfonium compound, i.e., a compound having arylsulfonium as a cation.
アリールスルホニウム化合物は、Ｒ201〜Ｒ203の全てがアリール基でもよいし、Ｒ201〜Ｒ203の一部がアリール基で、残りがアルキル基、シクロアルキル基でもよい。 In the arylsulfonium compound, all of R 201 to R 203 may be an aryl group, or a part of R 201 to R 203 may be an aryl group, and the rest may be an alkyl group or a cycloalkyl group.
アリールスルホニウム化合物としては、例えば、トリアリールスルホニウム化合物、ジアリールアルキルスルホニウム化合物、アリールジアルキルスルホニウム化合物、ジアリールシクロアルキルスルホニウム化合物、アリールジシクロアルキルスルホニウム化合物等を挙げることができる。 Examples of the arylsulfonium compound include triarylsulfonium compounds, diarylalkylsulfonium compounds, aryldialkylsulfonium compounds, diarylcycloalkylsulfonium compounds, aryldicycloalkylsulfonium compounds, and the like.
アリールスルホニウム化合物のアリール基としてはフェニル基、ナフチル基などのアリール基、インドール残基、ピロール残基、などのヘテロアリール基が好ましく、更に好ましくはフェニル基、インドール残基である。アリールスルホニム化合物が２つ以上のアリール基を有する場合に、２つ以上あるアリール基は同一であっても異なっていてもよい。 The aryl group of the arylsulfonium compound is preferably an aryl group such as a phenyl group or a naphthyl group, or a heteroaryl group such as an indole residue or a pyrrole residue, more preferably a phenyl group or an indole residue. When the arylsulfonium compound has two or more aryl groups, the two or more aryl groups may be the same or different.
アリールスルホニウム化合物が必要に応じて有しているアルキル基としては、炭素数１〜１５の直鎖又は分岐状アルキル基が好ましく、例えば、メチル基、エチル基、プロピル基、ｎ−ブチル基、ｓｅｃ−ブチル基、ｔ−ブチル基等を挙げることができる。
アリールスルホニウム化合物が必要に応じて有しているシクロアルキル基としては、炭素数３〜１５のシクロアルキル基が好ましく、例えば、シクロプロピル基、シクロブチル基、シクロヘキシル基等を挙げることができる。
The alkyl group that the arylsulfonium compound has as necessary is preferably a linear or branched alkyl group having 1 to 15 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an n-butyl group, sec. -A butyl group, a t-butyl group, etc. can be mentioned.
The cycloalkyl group that the arylsulfonium compound has as necessary is preferably a cycloalkyl group having 3 to 15 carbon atoms, and examples thereof include a cyclopropyl group, a cyclobutyl group, and a cyclohexyl group.
Ｒ201〜Ｒ203のアリール基、アルキル基、シクロアルキル基は、アルキル基（例えば炭素数１〜１５）、シクロアルキル基（例えば炭素数３〜１５）、アリール基（例えば炭素数６〜１４）、アルコキシ基（例えば炭素数１〜１５）、ハロゲン原子、水酸基、フェニルチオ基を置換基として有してもよい。好ましい置換基としては、炭素数１〜１２の直鎖又は分岐状アルキル基、炭素数３〜１２のシクロアルキル基、炭素数１〜１２の直鎖、分岐又は環状のアルコキシ基であり、最も好ましくは炭素数１〜４のアルキル基、炭素数１〜４のアルコキシ基である。置換基は、３つのＲ201〜Ｒ203のうち、いずれか１つに置換していてもよいし、３つ全てに置換していてもよい。また、Ｒ201〜Ｒ203がアリール基の場合に、置換基はアリール基のｐ−位に置換していることが好ましい。 Aryl group, alkyl group of R 201 to R 203, cycloalkyl group, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (for example, 6 to 14 carbon atoms) , An alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, or a phenylthio group may be substituted. Preferred substituents are linear or branched alkyl groups having 1 to 12 carbon atoms, cycloalkyl groups having 3 to 12 carbon atoms, and linear, branched or cyclic alkoxy groups having 1 to 12 carbon atoms, and most preferred. Is an alkyl group having 1 to 4 carbon atoms and an alkoxy group having 1 to 4 carbon atoms. Substituents, of the three R 201 to R 203, may be substituted on any one, or may be substituted on all of three. When R 201 to R 203 are an aryl group, the substituent is preferably substituted at the p-position of the aryl group.
次に、化合物（ｂ１−２）について説明する。
化合物（ｂ１−２）は、式（ｂ１）におけるＲ201〜Ｒ203が、各々独立に、芳香環を含有しない有機基を表す場合の化合物である。ここで芳香環とは、ヘテロ原子を含有する芳香族環も包含するものである。
Ｒ201〜Ｒ203としての芳香環を含有しない有機基は、一般的に炭素数１〜３０、好ましくは炭素数１〜２０である。
Ｒ201〜Ｒ203は、各々独立に、好ましくはアルキル基、シクロアルキル基、アリル基、ビニル基であり、より好ましくは直鎖、分岐、環状２−オキソアルキル基、アルコキシカルボニルメチル基、特に好ましくは直鎖、分岐２−オキソアルキル基である。
Next, the compound (b1-2) will be described.
The compound (b1-2) is a compound in the case where R 201 to R 203 in the formula (b1) each independently represents an organic group not containing an aromatic ring. Here, the aromatic ring includes an aromatic ring containing a hetero atom.
The organic group having no aromatic ring as R 201 to R 203 generally has 1 to 30 carbon atoms, preferably 1 to 20 carbon atoms.
R 201 to R 203 each independently, preferably an alkyl group, a cycloalkyl group, an allyl group, a vinyl group, more preferably a linear, branched or cyclic 2-oxoalkyl group, an alkoxycarbonylmethyl group, particularly preferably Is a linear, branched 2-oxoalkyl group.
Ｒ201〜Ｒ203としてのアルキル基は、直鎖状、分岐状のいずれであってもよく、好ましくは、炭素数１〜１０の直鎖又は分岐アルキル基（例えば、メチル基、エチル基、プロピル基、ブチル基、ペンチル基）を挙げることができ、直鎖、分岐２−オキソアルキル基、アルコキシカルボニルメチル基がより好ましい。 The alkyl group as R 201 to R 203 may be linear, may be either branched, preferably a straight-chain or branched alkyl group (e.g., methyl group having 1 to 10 carbon atoms, an ethyl group, a propyl Group, a butyl group, a pentyl group), and a linear, branched 2-oxoalkyl group, and an alkoxycarbonylmethyl group are more preferable.
Ｒ201〜Ｒ203としてのシクロアルキル基は、好ましくは、炭素数３〜１０のシクロアルキル基（シクロペンチル基、シクロヘキシル基、ノルボニル基）を挙げることができ、環状２−オキソアルキル基がより好ましい。 The cycloalkyl group as R 201 to R 203 is preferably a cycloalkyl group having 3 to 10 carbon atoms (a cyclopentyl group, a cyclohexyl group, a norbornyl group) can be exemplified, more preferably a cyclic 2-oxoalkyl group.
Ｒ201〜Ｒ203の直鎖、分岐、環状２−オキソアルキル基としては、好ましくは、上記のアルキル基、シクロアルキル基の２位に＞Ｃ＝Ｏを有する基を挙げることができる。
Ｒ201〜Ｒ203としてのアルコキシカルボニルメチル基におけるアルコキシ基としては、好ましくは炭素数１〜５のアルコキシ基（メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペントキシ基）を挙げることができる。
Ｒ201〜Ｒ203は、ハロゲン原子、アルコキシ基（例えば炭素数１〜５）、水酸基、シアノ基、ニトロ基によって更に置換されていてもよい。
Linear R 201 to R 203, branched, or cyclic 2-oxoalkyl group, preferably, may be mentioned 2-position group having> C = O at the above-described alkyl or cycloalkyl group.
The alkoxy group in the alkoxycarbonylmethyl group as R 201 to R 203, preferably may be mentioned alkoxy groups having 1 to 5 carbon atoms (a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentoxy group).
R 201 to R 203 may be further substituted with a halogen atom, an alkoxy group (eg, having 1 to 5 carbon atoms), a hydroxyl group, a cyano group, or a nitro group.
化合物（ｂ１−３）とは、以下の式（ｂ１−３）で表される化合物であり、フェナシルスルフォニウム塩構造を有する化合物である。 The compound (b1-3) is a compound represented by the following formula (b1-3) and is a compound having a phenacylsulfonium salt structure.
式（ｂ１−３）に於いて、Ｒ1c〜Ｒ5cは、各々独立に、水素原子、アルキル基、シクロアルキル基、アルコキシ基、又はハロゲン原子を表す。
Ｒ6c及びＲ7cは、各々独立に、水素原子、アルキル基又はシクロアルキル基を表す。
Ｒx及びＲyは、各々独立に、アルキル基、シクロアルキル基、アリル基、又はビニル基を表す。
Ｒ1c〜Ｒ5c中のいずれか２つ以上、Ｒ6cとＲ7c、及びＲxとＲyは、それぞれ結合して環構造を形成してもよい。
Ｚｃ-は、非求核性アニオンを表し、式（ｂ１）に於けるＸ-の非求核性アニオンと同様のものを挙げることができる。
In formula (b1-3), R 1c to R 5c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an alkoxy group, or a halogen atom.
R 6c and R 7c each independently represents a hydrogen atom, an alkyl group or a cycloalkyl group.
R x and R y each independently represents an alkyl group, a cycloalkyl group, an allyl group, or a vinyl group.
Any two or more of R 1c to R 5c , R 6c and R 7c , and R x and R y may be bonded to each other to form a ring structure.
Zc − represents a non-nucleophilic anion, and examples thereof include the same as the non-nucleophilic anion of X − in formula (b1).
Ｒ1c〜Ｒ7cとしてのアルキル基は、直鎖状、分岐状のいずれであってもよく、例えば炭素数１〜２０個、好ましくは炭素数１〜１２個の直鎖及び分岐アルキル基（例えば、メチル基、エチル基、直鎖又は分岐プロピル基、直鎖又は分岐ブチル基、直鎖又は分岐ペンチル基）を挙げることができる。 The alkyl group as R 1c to R 7c may be either linear or branched, for example, a linear or branched alkyl group having 1 to 20 carbon atoms, preferably 1 to 12 carbon atoms (for example, Methyl group, ethyl group, linear or branched propyl group, linear or branched butyl group, linear or branched pentyl group).
Ｒ1c〜Ｒ7cのシクロアルキル基として、好ましくは、炭素数３〜８個のシクロアルキル基（例えば、シクロペンチル基、シクロヘキシル基）を挙げることができる。 Preferred examples of the cycloalkyl group represented by R 1c to R 7c include a cycloalkyl group having 3 to 8 carbon atoms (for example, a cyclopentyl group and a cyclohexyl group).
Ｒ1c〜Ｒ5cとしてのアルコキシ基は、直鎖、分岐、環状のいずれであってもよく、例えば炭素数１〜１０のアルコキシ基、好ましくは、炭素数１〜５の直鎖及び分岐アルコキシ基（例えば、メトキシ基、エトキシ基、直鎖又は分岐プロポキシ基、直鎖又は分岐ブトキシ基、直鎖又は分岐ペントキシ基）、炭素数３〜８の環状アルコキシ基（例えば、シクロペンチルオキシ基、シクロヘキシルオキシ基）を挙げることができる。 The alkoxy group as R 1c to R 5c may be linear, branched or cyclic, for example, an alkoxy group having 1 to 10 carbon atoms, preferably a linear or branched alkoxy group having 1 to 5 carbon atoms. (For example, methoxy group, ethoxy group, linear or branched propoxy group, linear or branched butoxy group, linear or branched pentoxy group), C3-C8 cyclic alkoxy group (for example, cyclopentyloxy group, cyclohexyloxy group) ).
Ｒ1c〜Ｒ5c中のいずれか２つ以上、Ｒ6cとＲ7c、及びＲxとＲyが結合して形成する基としては、ブチレン基、ペンチレン基等を挙げることができる。この環構造は、酸素原子、硫黄原子、エステル結合、アミド結合を含んでいてもよい。 Examples of the group formed by combining any two or more of R 1c to R 5c , R 6c and R 7c , and R x and R y include a butylene group and a pentylene group. This ring structure may contain an oxygen atom, a sulfur atom, an ester bond, or an amide bond.
好ましくはＲ1c〜Ｒ5cのうちいずれかが直鎖状若しくは分岐状アルキル基、シクロアルキル基又は直鎖、分岐、環状アルコキシ基であり、更に好ましくはＲ1cからＲ5cの炭素数の和が２〜１５である。これにより、溶剤溶解性がより向上し、保存時にパーティクルの発生が抑制されるので好ましい。 Preferably any one of R 1c to R 5c is a linear or branched alkyl group, a cycloalkyl group, or a linear, branched or cyclic alkoxy group, and more preferably the sum of the carbon number of R 1c to R 5c is 2-15. This is preferable because solvent solubility is further improved and generation of particles is suppressed during storage.
Ｒx及びＲyとしてのアルキル基、シクロアルキル基は、Ｒ1c〜Ｒ7cとしてのアルキル基、シクロアルキル基と同様のものを挙げることができる。
Ｒx及びＲyは、２−オキソアルキル基、アルコキシカルボニルメチル基であることが好ましい。
２−オキソアルキル基は、Ｒ1c〜Ｒ5cとしてのアルキル基、シクロアルキル基の２位に＞Ｃ＝Ｏを有する基を挙げることができる。
アルコキシカルボニルメチル基におけるアルコキシ基については、Ｒ1c〜Ｒ5cとしてのアルコキシ基と同様のものを挙げることができる。
Examples of the alkyl group and cycloalkyl group as R x and R y include the same alkyl groups and cycloalkyl groups as R 1c to R 7c .
R x and R y are preferably a 2-oxoalkyl group or an alkoxycarbonylmethyl group.
Examples of the 2-oxoalkyl group include a group having> C═O at the 2-position of the alkyl group or cycloalkyl group as R 1c to R 5c .
Examples of the alkoxy group in the alkoxycarbonylmethyl group include the same alkoxy groups as R 1c to R 5c .
Ｒx、Ｒyは、好ましくは炭素数４個以上のアルキル基、シクロアルキル基であり、より好ましくは６個以上、更に好ましくは８個以上のアルキル基、シクロアルキル基である。 R x and R y are preferably an alkyl group or cycloalkyl group having 4 or more carbon atoms, more preferably 6 or more, and still more preferably 8 or more alkyl groups or cycloalkyl groups.
式（ｂ２）、（ｂ３）中、Ｒ204〜Ｒ207は、各々独立に、アリール基、アルキル基又はシクロアルキル基を表す。Ｘ-は、非求核性アニオンを表し、式（ｂ１）に於けるＸ-の非求核性アニオンと同様のものを挙げることができる。 Formula (b2), in (b3), R 204 ~R 207 each independently represents an aryl group, an alkyl group or a cycloalkyl group. X − represents a non-nucleophilic anion, and examples thereof include the same non-nucleophilic anion as X − in formula (b1).
Ｒ204〜Ｒ207のアリール基としてはフェニル基、ナフチル基が好ましく、更に好ましくはフェニル基である。
Ｒ204〜Ｒ207としてのアルキル基は、直鎖状、分岐状のいずれであってもよく、好ましくは、炭素数１〜１０の直鎖又は分岐アルキル基（例えば、メチル基、エチル基、プロピル基、ブチル基、ペンチル基）を挙げることができる。Ｒ204〜Ｒ207としてのシクロアルキル基は、好ましくは、炭素数３〜１０のシクロアルキル基（シクロペンチル基、シクロヘキシル基、ノルボニル基）を挙げることができる。
Ｒ204〜Ｒ207が有していてもよい置換基としては、例えば、アルキル基（例えば炭素数１〜１５）、シクロアルキル基（例えば炭素数３〜１５）、アリール基（例えば炭素数６〜１５）、アルコキシ基（例えば炭素数１〜１５）、ハロゲン原子、水酸基、フェニルチオ基等を挙げることができる。
Phenyl group and a naphthyl group are preferred as the aryl group of R 204 to R 207, more preferably a phenyl group.
The alkyl group as R 204 to R 207 may be linear, may be either branched, preferably a straight-chain or branched alkyl group (e.g., methyl group having 1 to 10 carbon atoms, an ethyl group, a propyl Group, butyl group, pentyl group). The cycloalkyl group as R 204 to R 207 is preferably, and a cycloalkyl group having 3 to 10 carbon atoms (e.g., cyclopentyl, cyclohexyl, norbornyl).
The R 204 to R 207 are substituents which may have, for example, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (e.g., 6 carbon atoms 15), alkoxy groups (for example, having 1 to 15 carbon atoms), halogen atoms, hydroxyl groups, phenylthio groups and the like.
使用してもよい活性光線又は放射線の照射により酸を発生する化合物として、更に、下記式（ｂ４）、（ｂ５）、（ｂ６）で表される化合物を挙げることができる。 Examples of the compound that generates an acid upon irradiation with actinic rays or radiation that may be used further include compounds represented by the following formulas (b4), (b5), and (b6).
式（ｂ４）〜（ｂ６）中、Ａｒ3及びＡｒ4は、各々独立に、アリール基を表す。
Ｒ206、Ｒ207及びＲ208は、各々独立に、アルキル基、シクロアルキル基又はアリール基を表す。
Ａは、アルキレン基、アルケニレン基又はアリーレン基を表す。
In formulas (b4) to (b6), Ar 3 and Ar 4 each independently represents an aryl group.
R 206 , R 207 and R 208 each independently represents an alkyl group, a cycloalkyl group or an aryl group.
A represents an alkylene group, an alkenylene group or an arylene group.
前記光酸発生剤のなかでも好ましくものとしては、式（ｂ１）〜（ｂ３）で表される化合物を挙げることができる。
本発明に用いることのできる（ｂ）光酸発生剤の好ましい化合物例〔（ｂ−１）〜（ｂ−９６）〕を以下に挙げるが、本発明はこれらに限定されるものではない。
Preferable examples of the photoacid generator include compounds represented by formulas (b1) to (b3).
Preferred compound examples ((b-1) to (b-96)) of (b) photoacid generator that can be used in the present invention are listed below, but the present invention is not limited thereto.
また、特開２００２−１２２９９４号公報、段落番号〔００２９〕乃至〔００３０〕に記載のオキサゾール誘導体、ｓ−トリアジン誘導体なども好適に用いられる。
特開２００２−１２２９９４号公報、段落番号〔００３７〕乃至〔００６３〕に例示されるオニウム塩化合物、スルホネート系化合物も本発明に好適に使用しうる。
Further, oxazole derivatives and s-triazine derivatives described in JP-A No. 2002-122994, paragraph numbers [0029] to [0030] are also preferably used.
The onium salt compounds and sulfonate compounds exemplified in JP-A-2002-122994, paragraphs [0037] to [0063] can also be suitably used in the present invention.
（ｂ）光酸発生剤は、１種単独で又は２種以上を組み合わせて使用することができる。
インク組成物中の（ｂ）光酸発生剤の含有量は、インク組成物の全固形分換算で、０．１〜２０重量％が好ましく、より好ましくは０．５〜１０重量％、更に好ましくは１〜７重量％である。
(B) A photo-acid generator can be used individually by 1 type or in combination of 2 or more types.
The content of the (b) photoacid generator in the ink composition is preferably 0.1 to 20% by weight, more preferably 0.5 to 10% by weight, and still more preferably, in terms of the total solid content of the ink composition. Is 1-7% by weight.
［（ｃ）着色剤］
本発明のインク組成物は、（ｃ）着色剤を含有する。
本発明に用いることのできる着色剤としては、特に制限はないが、耐候性に優れ、色再現性に富んだ顔料及び油溶性染料が好ましく、溶解性染料等の任意の公知の着色剤から選択して使用することができる。本発明のインク組成物又はインクジェット記録用インク組成物に好適に使用し得る着色剤は、硬化反応である重合反応において重合禁止剤として機能しないことが好ましい。これは、活性放射線による硬化反応の感度を低下させないためである。
[(C) Colorant]
The ink composition of the present invention contains (c) a colorant.
The colorant that can be used in the present invention is not particularly limited, but pigments and oil-soluble dyes that are excellent in weather resistance and excellent in color reproducibility are preferable, and are selected from any known colorant such as a soluble dye. Can be used. The colorant that can be suitably used in the ink composition of the present invention or the ink composition for ink jet recording preferably does not function as a polymerization inhibitor in a polymerization reaction that is a curing reaction. This is because the sensitivity of the curing reaction by actinic radiation is not reduced.
〔顔料〕
顔料としては、特に限定されるものではなく、一般に市販されているすべての有機顔料及び無機顔料、又は顔料を、分散媒として不溶性の樹脂等に分散させたもの、或いは顔料表面に樹脂をグラフト化したもの等を用いることができる。また、樹脂粒子を染料で染色したもの等も用いることができる。
これらの顔料としては、例えば、伊藤征司郎編「顔料の辞典」（２０００年刊）、Ｗ．Ｈｅｒｂｓｔ，Ｋ．Ｈｕｎｇｅｒ「Ｉｎｄｕｓｔｒｉａｌ Ｏｒｇａｎｉｃ Ｐｉｇｍｅｎｔｓ」、特開２００２−１２６０７号公報、特開２００２−１８８０２５号公報、特開２００３−２６９７８号公報、特開２００３−３４２５０３号公報に記載の顔料が挙げられる。
[Pigment]
The pigment is not particularly limited, and all commercially available organic and inorganic pigments or pigments dispersed in an insoluble resin or the like as a dispersion medium, or the resin is grafted onto the pigment surface Can be used. Moreover, what dye | stained the resin particle with dye can be used.
Examples of these pigments include, for example, “Pigment Dictionary” (2000), edited by Seijiro Ito. Herbst, K.M. Hunger “Industrial Organic Pigments”, JP 2002-12607 A, JP 2002-188025 A, JP 2003-26978 A, and JP 2003-342503 A3.
本発明において使用できる有機顔料及び無機顔料の具体例としては、例えば、イエロー色を呈するものとして、Ｃ．Ｉ．ピグメントイエロー１（ファストイエローＧ等），Ｃ．Ｉ．ピグメントイエロー７４の如きモノアゾ顔料、Ｃ．Ｉ．ピグメントイエロー１２（ジスアジイエローＡＡＡ等）、Ｃ．Ｉ．ピグメントイエロー１７の如きジスアゾ顔料、Ｃ．Ｉ．ピグメントイエロー１８０の如き非ベンジジン系のアゾ顔料、Ｃ．Ｉ．ピグメントイエロー１００（タートラジンイエローレーキ等）の如きアゾレーキ顔料、Ｃ．Ｉ．ピグメントイエロー９５（縮合アゾイエローＧＲ等）の如き縮合アゾ顔料、Ｃ．Ｉ．ピグメントイエロー１１５（キノリンイエローレーキ等）の如き酸性染料レーキ顔料、Ｃ．Ｉ．ピグメントイエロー１８（チオフラビンレーキ等）の如き塩基性染料レーキ顔料、フラバントロンイエロー（Ｙ−２４）の如きアントラキノン系顔料、イソインドリノンイエロー３ＲＬＴ（Ｙ−１１０）の如きイソインドリノン顔料、キノフタロンイエロー（Ｙ−１３８）の如きキノフタロン顔料、イソインドリンイエロー（Ｙ−１３９）の如きイソインドリン顔料、Ｃ．Ｉ．ピグメントイエロー１５３（ニッケルニトロソイエロー等）の如きニトロソ顔料、Ｃ．Ｉ．ピグメントイエロー１１７（銅アゾメチンイエロー等）の如き金属錯塩アゾメチン顔料等が挙げられる。 Specific examples of organic pigments and inorganic pigments that can be used in the present invention include C.I. I. Pigment Yellow 1 (Fast Yellow G etc.), C.I. I. A monoazo pigment such as C.I. Pigment Yellow 74; I. Pigment Yellow 12 (disaji yellow AAA, etc.), C.I. I. Disazo pigments such as C.I. Pigment Yellow 17; I. Non-benzidine type azo pigments such as CI Pigment Yellow 180; I. Azo lake pigments such as C.I. Pigment Yellow 100 (eg Tartrazine Yellow Lake); I. Condensed azo pigments such as CI Pigment Yellow 95 (Condensed Azo Yellow GR, etc.); I. Acidic dye lake pigments such as C.I. Pigment Yellow 115 (such as quinoline yellow lake); I. Basic dye lake pigments such as CI Pigment Yellow 18 (Thioflavin Lake, etc.), anthraquinone pigments such as Flavantron Yellow (Y-24), isoindolinone pigments such as Isoindolinone Yellow 3RLT (Y-110), and quinophthalone yellow Quinophthalone pigments such as (Y-138), isoindoline pigments such as isoindoline yellow (Y-139), C.I. I. Nitroso pigments such as C.I. Pigment Yellow 153 (nickel nitroso yellow, etc.); I. And metal complex salt azomethine pigments such as CI Pigment Yellow 117 (copper azomethine yellow, etc.).
赤或いはマゼンタ色を呈するものとして、Ｃ．Ｉ．ピグメントレッド３（トルイジンレッド等）の如きモノアゾ系顔料、Ｃ．Ｉ．ピグメントレッド３８（ピラゾロンレッドＢ等）の如きジスアゾ顔料、Ｃ．Ｉ．ピグメントレッド５３：１（レーキレッドＣ等）やＣ．Ｉ．ピグメントレッド５７：１（ブリリアントカーミン６Ｂ）の如きアゾレーキ顔料、Ｃ．Ｉ．ピグメントレッド１４４（縮合アゾレッドＢＲ等）の如き縮合アゾ顔料、Ｃ．Ｉ．ピグメントレッド１７４（フロキシンＢレーキ等）の如き酸性染料レーキ顔料、Ｃ．Ｉ．ピグメントレッド８１（ローダミン６Ｇ’レーキ等）の如き塩基性染料レーキ顔料、Ｃ．Ｉ．ピグメントレッド１７７（ジアントラキノニルレッド等）の如きアントラキノン系顔料、Ｃ．Ｉ．ピグメントレッド８８（チオインジゴボルドー等）の如きチオインジゴ顔料、Ｃ．Ｉ．ピグメントレッド１９４（ペリノンレッド等）の如きペリノン顔料、Ｃ．Ｉ．ピグメントレッド１４９（ペリレンスカーレット等）の如きペリレン顔料、Ｃ．Ｉ．ピグメントバイオレット１９（無置換キナクリドン）、Ｃ．Ｉ．ピグメントレッド１２２（キナクリドンマゼンタ等）の如きキナクリドン顔料、Ｃ．Ｉ．ピグメントレッド１８０（イソインドリノンレッド２ＢＬＴ等）の如きイソインドリノン顔料、Ｃ．Ｉ．ピグメントレッド８３（マダーレーキ等）の如きアリザリンレーキ顔料等が挙げられる。 C. As a thing which exhibits red or magenta color. I. Monoazo pigments such as CI Pigment Red 3 (Toluidine Red, etc.); I. Disazo pigments such as C.I. Pigment Red 38 (Pyrazolone Red B, etc.); I. Pigment Red 53: 1 (Lake Red C, etc.) and C.I. I. Azo lake pigments such as C.I. Pigment Red 57: 1 (Brilliant Carmine 6B); I. Condensed azo pigments such as C.I. Pigment Red 144 (condensed azo red BR, etc.); I. Acidic dye lake pigments such as C.I. Pigment Red 174 (Phloxine B Lake, etc.); I. Basic dye lake pigments such as C.I. Pigment Red 81 (Rhodamine 6G 'lake, etc.); I. Anthraquinone pigments such as C.I. Pigment Red 177 (eg, dianthraquinonyl red); I. Thioindigo pigments such as C.I. Pigment Red 88 (Thioindigo Bordeaux, etc.); I. Perinone pigments such as C.I. Pigment Red 194 (perinone red, etc.); I. Perylene pigments such as C.I. Pigment Red 149 (perylene scarlet, etc.); I. Pigment violet 19 (unsubstituted quinacridone), C.I. I. Quinacridone pigments such as CI Pigment Red 122 (quinacridone magenta, etc.); I. Isoindolinone pigments such as CI Pigment Red 180 (isoindolinone red 2BLT, etc.); I. And alizarin lake pigments such as CI Pigment Red 83 (Mada Lake, etc.).
青或いはシアン色を呈する顔料として、Ｃ．Ｉ．ピグメントブルー２５（ジアニシジンブルー等）の如きジスアゾ系顔料、Ｃ．Ｉ．ピグメントブルー１５（フタロシアニンブルー等）の如きフタロシアニン顔料、Ｃ．Ｉ．ピグメントブルー２４（ピーコックブルーレーキ等）の如き酸性染料レーキ顔料、Ｃ．Ｉ．ピグメントブルー１（ビクロチアピュアブルーＢＯレーキ等）の如き塩基性染料レーキ顔料、Ｃ．Ｉ．ピグメントブルー６０（インダントロンブルー等）の如きアントラキノン系顔料、Ｃ．Ｉ．ピグメントブルー１８（アルカリブルーＶ−５：１）の如きアルカリブルー顔料等が挙げられる。 As a pigment exhibiting blue or cyan, C.I. I. Disazo pigments such as C.I. Pigment Blue 25 (Dianisidine Blue, etc.); I. Phthalocyanine pigments such as C.I. Pigment Blue 15 (phthalocyanine blue, etc.); I. Acidic dye lake pigments such as C.I. Pigment Blue 24 (Peacock Blue Lake, etc.); I. Basic dye lake pigments such as C.I. Pigment Blue 1 (Viclotia Pure Blue BO Lake, etc.); I. Anthraquinone pigments such as C.I. Pigment Blue 60 (Indantron Blue, etc.); I. And alkali blue pigments such as CI Pigment Blue 18 (Alkali Blue V-5: 1).
緑色を呈する顔料として、Ｃ．Ｉ．ピグメントグリーン７（フタロシアニングリーン）、Ｃ．Ｉ．ピグメントグリーン３６（フタロシアニングリーン）の如きフタロシアニン顔料、Ｃ．Ｉ．ピグメントグリーン８（ニトロソグリーン）等の如きアゾ金属錯体顔料等が挙げられる。
オレンジ色を呈する顔料として、Ｃ．Ｉ．ピグメントオレンジ６６（イソインドリンオレンジ）の如きイソインドリン系顔料、Ｃ．Ｉ．ピグメントオレンジ５１（ジクロロピラントロンオレンジ）の如きアントラキノン系顔料が挙げられる。
As a pigment exhibiting green, C.I. I. Pigment green 7 (phthalocyanine green), C.I. I. Phthalocyanine pigments such as C.I. Pigment Green 36 (phthalocyanine green); I. And azo metal complex pigments such as CI Pigment Green 8 (Nitroso Green).
As a pigment exhibiting orange, C.I. I. An isoindoline pigment such as C.I. Pigment Orange 66 (isoindoline orange); I. And anthraquinone pigments such as CI Pigment Orange 51 (dichloropyrantron orange).
黒色を呈する顔料として、カーボンブラック、チタンブラック、アニリンブラック等が挙げられる。
白色顔料の具体例としては、塩基性炭酸鉛（２ＰｂＣＯ3Ｐｂ（ＯＨ）2、いわゆる、シルバーホワイト）、酸化亜鉛（ＺｎＯ、いわゆる、ジンクホワイト）、酸化チタン（ＴｉＯ2、いわゆる、チタンホワイト）、チタン酸ストロンチウム（ＳｒＴｉＯ3、いわゆる、チタンストロンチウムホワイト）などが利用可能である。
Examples of the black pigment include carbon black, titanium black, and aniline black.
Specific examples of the white pigment include basic lead carbonate (2PbCO 3 Pb (OH) 2 , so-called silver white), zinc oxide (ZnO, so-called zinc white), titanium oxide (TiO 2 , so-called titanium white), Strontium titanate (SrTiO 3 , so-called titanium strontium white) or the like can be used.
ここで、酸化チタンは他の白色顔料と比べて比重が小さく、屈折率が大きく化学的、物理的にも安定であるため、顔料としての隠蔽力や着色力が大きく、更に、酸やアルカリ、その他の環境に対する耐久性にも優れている。したがって、白色顔料としては酸化チタンを利用することが好ましい。もちろん、必要に応じて他の白色顔料（列挙した白色顔料以外であってもよい。）を使用してもよい。 Here, titanium oxide has a smaller specific gravity than other white pigments, a large refractive index, and is chemically and physically stable, so that it has a large hiding power and coloring power as a pigment. Excellent durability against other environments. Therefore, it is preferable to use titanium oxide as the white pigment. Of course, other white pigments (may be other than the listed white pigments) may be used as necessary.
顔料の分散には、例えば、ボールミル、サンドミル、アトライター、ロールミル、ジェットミル、ホモジナイザー、ペイントシェーカー、ニーダー、アジテータ、ヘンシェルミキサ、コロイドミル、超音波ホモジナイザー、パールミル、湿式ジェットミル等の分散装置を用いることができる。
顔料の分散を行う際に分散剤を添加することも可能である。分散剤としては、水酸基含有カルボン酸エステル、長鎖ポリアミノアマイドと高分子量酸エステルの塩、高分子量ポリカルボン酸の塩、高分子量不飽和酸エステル、高分子共重合物、変性ポリアクリレート、脂肪族多価カルボン酸、ナフタレンスルホン酸ホルマリン縮合物、ポリオキシエチレンアルキル燐酸エステル、顔料誘導体等を挙げることができる。また、Ｚｅｎｅｃａ社のＳｏｌｓｐｅｒｓｅシリーズなどの市販の高分子分散剤を用いることも好ましい。
また、分散助剤として、各種顔料に応じたシナージストを用いることも可能である。これらの分散剤及び分散助剤は、顔料１００重量部に対し、１〜５０重量部添加することが好ましい。
For dispersing the pigment, for example, a dispersion device such as a ball mill, a sand mill, an attritor, a roll mill, a jet mill, a homogenizer, a paint shaker, a kneader, an agitator, a Henschel mixer, a colloid mill, an ultrasonic homogenizer, a pearl mill, or a wet jet mill is used. be able to.
It is also possible to add a dispersant when dispersing the pigment. Examples of the dispersant include a hydroxyl group-containing carboxylic acid ester, a salt of a long-chain polyaminoamide and a high molecular weight acid ester, a salt of a high molecular weight polycarboxylic acid, a high molecular weight unsaturated acid ester, a high molecular weight copolymer, a modified polyacrylate, an aliphatic Examples thereof include polyvalent carboxylic acids, naphthalene sulfonic acid formalin condensates, polyoxyethylene alkyl phosphate esters, and pigment derivatives. It is also preferable to use a commercially available polymer dispersant such as the Solsperse series from Zeneca.
Moreover, it is also possible to use a synergist according to various pigments as a dispersion aid. These dispersants and dispersion aids are preferably added in an amount of 1 to 50 parts by weight with respect to 100 parts by weight of the pigment.
インク組成物において、顔料などの諸成分の分散媒としては、溶剤を添加してもよく、また、無溶媒で、低分子量成分である前記（ａ）カチオン重合性化合物を分散媒として用いてもよいが、本発明のインク組成物は、放射線硬化型のインクであり、インクを被記録媒体上に適用後、硬化させるため、無溶剤であることが好ましい。これは、硬化されたインク画像中に、溶剤が残留すると、耐溶剤性が劣化したり、残留する溶剤のＶＯＣ（Ｖｏｌａｔｉｌｅ Ｏｒｇａｎｉｃ Ｃｏｍｐｏｕｎｄ）の問題が生じるためである。このような観点から、分散媒としては、（ａ）カチオン重合性化合物を用い、中でも、最も粘度が低いカチオン重合性モノマーを選択することが分散適性やインク組成物のハンドリング性向上の観点から好ましい。 In the ink composition, as a dispersion medium for various components such as pigments, a solvent may be added, or the solvent-free low molecular weight component (a) cationic polymerizable compound may be used as a dispersion medium. However, the ink composition of the present invention is a radiation curable ink, and is preferably solventless in order to cure the ink after it is applied to a recording medium. This is because if the solvent remains in the cured ink image, the solvent resistance is deteriorated or a VOC (Volatile Organic Compound) problem of the remaining solvent occurs. From such a viewpoint, as the dispersion medium, (a) a cationically polymerizable compound is used, and among them, it is preferable to select a cationically polymerizable monomer having the lowest viscosity in terms of dispersion suitability and handling properties of the ink composition. .
顔料の平均粒径は、０．０２〜０．４μｍにするのが好ましく、０．０２〜０．１μｍとするのが更に好ましく、より好ましくは、０．０２〜０．０７μｍの範囲である。
顔料粒子の平均粒径を上記好ましい範囲となるよう、顔料、分散剤、分散媒体の選定、分散条件、ろ過条件を設定する。この粒径管理によって、ヘッドノズルの詰まりを抑制し、インクの保存安定性、インク透明性及び硬化感度を維持することができる。
The average particle diameter of the pigment is preferably 0.02 to 0.4 μm, more preferably 0.02 to 0.1 μm, and more preferably 0.02 to 0.07 μm.
The selection of pigment, dispersant, dispersion medium, dispersion conditions, and filtration conditions are set so that the average particle diameter of the pigment particles is within the above-mentioned preferable range. By controlling the particle size, clogging of the head nozzle can be suppressed, and ink storage stability, ink transparency, and curing sensitivity can be maintained.
〔染料〕
本発明に用いることのできる染料は、油溶性のものが好ましい。具体的には、２５℃での水への溶解度（水１００ｇに溶解する色素の質量）が１ｇ以下であるものを意味し、好ましくは０．５ｇ以下、より好ましくは０．１ｇ以下である。従って、所謂、水に不溶性の油溶性染料が好ましく用いられる。
〔dye〕
The dye that can be used in the present invention is preferably oil-soluble. Specifically, it means that the solubility in water at 25 ° C. (the mass of the dye dissolved in 100 g of water) is 1 g or less, preferably 0.5 g or less, more preferably 0.1 g or less. Therefore, a so-called water-insoluble oil-soluble dye is preferably used.
本発明に用いることのできる染料は、インク組成物に必要量溶解させるために上記記載の染料母核に対して油溶化基を導入することも好ましい。
油溶化基としては、長鎖、分岐アルキル基、長鎖、分岐アルコキシ基、長鎖、分岐アルキルチオ基、長鎖、分岐アルキルスルホニル基、長鎖、分岐アシルオキシ基、長鎖、分岐アルコキシカルボニル基、長鎖、分岐アシル基、長鎖、分岐アシルアミノ基長鎖、分岐アルキルスルホニルアミノ基、長鎖、分岐アルキルアミノスルホニル基及びこれら長鎖、分岐置換基を含むアリール基、アリールオキシ基、アリールオキシカルボニル基、アリールカルボニルオキシ基、アリールアミノカルボニル基、アリールアミノスルホニル基、アリールスルホニルアミノ基等が挙げられる。
また、カルボン酸、スルホン酸を有する水溶性染料に対して、長鎖、分岐アルコール、アミン、フェノール、アニリン誘導体を用いて油溶化基であるアルコキシカルボニル基、アリールオキシカルボニル基、アルキルアミノスルホニル基、アリールアミノスルホニル基に変換することにより染料を得てもよい。
The dye that can be used in the present invention preferably has an oil-solubilizing group introduced into the above-described dye mother core in order to dissolve the necessary amount in the ink composition.
As the oil-solubilizing group, long chain, branched alkyl group, long chain, branched alkoxy group, long chain, branched alkylthio group, long chain, branched alkylsulfonyl group, long chain, branched acyloxy group, long chain, branched alkoxycarbonyl group, Long chain, branched acyl group, long chain, branched acylamino group long chain, branched alkylsulfonylamino group, long chain, branched alkylaminosulfonyl group and these long chains, aryl groups containing branched substituents, aryloxy groups, aryloxycarbonyl Group, arylcarbonyloxy group, arylaminocarbonyl group, arylaminosulfonyl group, arylsulfonylamino group and the like.
In addition, for water-soluble dyes having carboxylic acid and sulfonic acid, long chain, branched alcohol, amine, phenol, aniline derivatives are used as oil-solubilizing alkoxycarbonyl groups, aryloxycarbonyl groups, alkylaminosulfonyl groups, A dye may be obtained by conversion to an arylaminosulfonyl group.
前記油溶性染料としては、融点が２００℃以下のものが好ましく、融点が１５０℃以下であるものがより好ましく、融点が１００℃以下であるものが更に好ましい。融点が低い油溶性染料を用いることにより、インク組成物中での色素の結晶析出が抑制され、インク組成物の保存安定性が良くなる。
また、退色、特にオゾンなどの酸化性物質に対する耐性や硬化特性を向上させるために、酸化電位が貴である（高い）ことが望ましい。このため、本発明で用いる油溶性染料として、酸化電位が１．０Ｖ（ｖｓＳＣＥ）以上であるものが好ましく用いられる。酸化電位は高いほうが好ましく、酸化電位が１．１Ｖ（ｖｓＳＣＥ）以上のものがより好ましく、１．１５Ｖ（ｖｓＳＣＥ）以上のものが特に好ましい。
The oil-soluble dye preferably has a melting point of 200 ° C. or lower, more preferably has a melting point of 150 ° C. or lower, and still more preferably has a melting point of 100 ° C. or lower. By using an oil-soluble dye having a low melting point, the precipitation of dye crystals in the ink composition is suppressed, and the storage stability of the ink composition is improved.
Further, it is desirable that the oxidation potential is noble (high) in order to improve fading, particularly resistance to oxidizing substances such as ozone and curing characteristics. For this reason, as the oil-soluble dye used in the present invention, those having an oxidation potential of 1.0 V (vs SCE) or more are preferably used. The oxidation potential is preferably higher, the oxidation potential is more preferably 1.1 V (vs SCE) or more, and particularly preferably 1.15 V (vs SCE) or more.
イエロー色の染料としては、特開２００４−２５０４８３号公報の記載の一般式（Ｙ−Ｉ）で表される構造の化合物が好ましい。
特に好ましい染料は、特開２００４−２５０４８３号公報の段落番号［００３４］に記載されている一般式（Ｙ−II）〜（Ｙ−ＩＶ）で表される染料であり、具体例として特開２００４−２５０４８３号公報の段落番号［００６０］から［００７１］に記載の化合物が挙げられる。尚、該公報記載の一般式（Ｙ−Ｉ）の油溶性染料はイエローのみでなく、ブラックインク、レッドインクなどのいかなる色のインクに用いてもよい。
As the yellow dye, a compound having a structure represented by the general formula (Y-I) described in JP-A No. 2004-250483 is preferable.
Particularly preferred dyes are dyes represented by general formulas (Y-II) to (Y-IV) described in paragraph [0034] of JP-A No. 2004-250483. And the compounds described in paragraph numbers [0060] to [0071] of JP-A-250483. The oil-soluble dye of the general formula (Y-I) described in the publication may be used not only for yellow but also for inks of any color such as black ink and red ink.
マゼンタ色の染料としては、特開２００２−１１４９３０号公報に記載の一般式（３）、（４）で表される構造の化合物が好ましく、具体例としては、特開２００２−１１４９３０号公報の段落［００５４］〜［００７３］に記載の化合物が挙げられる。
特に好ましい染料は、特開２００２−１２１４１４号公報の段落番号［００８４］から［０１２２］に記載されている一般式（Ｍ−１）〜（Ｍ−２）で表されるアゾ染料であり、具体例として特開２００２−１２１４１４号公報の段落番号［０１２３］から［０１３２］に記載の化合物が挙げられる。尚、該公報記載の一般式（３）、（４）、（Ｍ−１）〜（Ｍ−２）の油溶性染料はマゼンタのみでなく、ブラックインク、レッドインクなどのいかなる色のインクに用いてもよい。
The magenta dye is preferably a compound having a structure represented by the general formulas (3) and (4) described in JP-A No. 2002-114930. Specific examples include paragraphs of JP-A No. 2002-114930. Examples include the compounds described in [0054] to [0073].
Particularly preferred dyes are azo dyes represented by the general formulas (M-1) to (M-2) described in paragraph numbers [0084] to [0122] of JP-A No. 2002-121414, and specific examples Examples thereof include compounds described in paragraph numbers [0123] to [0132] of JP-A No. 2002-121414. The oil-soluble dyes represented by the general formulas (3), (4) and (M-1) to (M-2) described in the publication are used not only for magenta but also for any color ink such as black ink and red ink. May be.
シアン色の染料としては、特開２００１−１８１５４７号公報に記載の式（Ｉ）〜（ＩＶ）で表される染料、特開２００２−１２１４１４号公報の段落番号［００６３］から［００７８］に記載されている一般式（ＩＶ−１）〜（ＩＶ−４）で表される染料が好ましいものとして挙げられ、具体例として特開２００１−１８１５４７号公報の段落番号［００５２］から［００６６］、特開２００２−１２１４１４号公報の段落番号［００７９］から［００８１］に記載の化合物が挙げられる。
特に好ましい染料は、特開２００２−１２１４１４号公報の段落番号［０１３３］から［０１９６］に記載されている一般式（Ｃ−Ｉ）、（Ｃ−II）で表されるフタロシアニン染料であり、更に一般式（Ｃ−II）で表されるフタロシアニン染料が好ましい。この具体例としては、特開２００２−１２１４１４号公報の段落番号［０１９８］から［０２０１］に記載の化合物が挙げられる。尚、前記式（Ｉ）〜（ＩＶ）、（ＩＶ−１）〜（ＩＶ−４）、（Ｃ−Ｉ）、（Ｃ−II）の油溶性染料はシアンのみでなく、ブラックインクやグリーンインクなどのいかなる色のインクに用いてもよい。
Examples of the cyan dye include dyes represented by formulas (I) to (IV) described in JP-A No. 2001-181547, and paragraphs [0063] to [0078] of JP-A No. 2002-121414. The dyes represented by the general formulas (IV-1) to (IV-4) described above are preferred, and specific examples include paragraph numbers [0052] to [0066] of JP-A No. 2001-181547. Examples thereof include the compounds described in paragraph Nos. [0079] to [0081] of Kai 2002-121414.
Particularly preferred dyes are phthalocyanine dyes represented by general formulas (CI) and (C-II) described in paragraphs [0133] to [0196] of JP-A No. 2002-121414, A phthalocyanine dye represented by formula (C-II) is preferred. Specific examples thereof include the compounds described in JP-A No. 2002-121414, paragraph numbers [0198] to [0201]. The oil-soluble dyes of the formulas (I) to (IV), (IV-1) to (IV-4), (CI) and (C-II) are not only cyan but also black ink or green ink. The ink may be used for any color ink.
−酸化電位−
本発明における染料の酸化電位の値（Ｅｏｘ）は、当業者が容易に測定することができる。この方法に関しては、例えばＰ．Ｄｅｌａｈａｙ著“Ｎｅｗ Ｉｎｓｔｒｕｍｅｎｔａｌ Ｍｅｔｈｏｄｓ ｉｎ Ｅｌｅｃｔｒｏｃｈｅｍｉｓｔｒｙ”（１９５４年，Ｉｎｔｅｒｓｃｉｅｎｃｅ Ｐｕｂｌｉｓｈｅｒｓ社刊）や、Ａ．Ｊ．Ｂａｒｄ他著“Ｅｌｅｃｔｒｏｃｈｅｍｉｃａｌ Ｍｅｔｈｏｄｓ”（１９８０年、Ｊｏｈｎ Ｗｉｌｅｙ ＆ Ｓｏｎｓ社刊）、藤嶋昭他著“電気化学測定法”（１９８４年 技報堂出版社刊）に記載されている。
具体的に酸化電位は、過塩素酸ナトリウムや過塩素酸テトラプロピルアンモニウムといった支持電解質を含むジメチルホルムアミドやアセトニトリルのような溶媒中に、被験試料を１×１０-2〜１×１０-6モル／リットル溶解して、サイクリックボルタンメトリーや直流ポーラログラフィー装置により、作用極として炭素（ＧＣ）を、対極として回転白金電極を用いて酸化側（貴側）に掃引したときの酸化波を直線で近似して、この直線と残余電流・電位直線との交点と、直線と飽和電流直線との交点（又はピーク電位値を通る縦軸に平行な直線との交点）とで作られる線分の中間電位値をＳＣＥ（飽和カロメル電極）に対する値として測定する。この値は、液間電位差や試料溶液の液抵抗などの影響で、数１０ミルボルト程度偏位することがあるが、標準試料（例えばハイドロキノン）を入れて電位の再現性を保証することができる。また、用いる支持電解質や溶媒は、被験試料の酸化電位や溶解性により適当なものを選ぶことができる。用いることができる支持電解質や溶媒については藤嶋昭他著“電気化学測定法”（１９８４年 技報堂出版社刊）１０１〜１１８ページに記載がある。
-Oxidation potential-
The oxidation potential value (Eox) of the dye in the present invention can be easily measured by those skilled in the art. Regarding this method, for example Delahay, “New Instrumental Methods in Electrochemistry” (1954, published by Interscience Publishers); J. et al. "Electrochemical Methods" by Bard et al. (1980, published by John Wiley & Sons) and Akira Fujishima et al., "Electrochemical Measurement Methods" (published by Gihodo Publishing Co., Ltd., 1984).
Specifically, the oxidation potential is 1 × 10 −2 to 1 × 10 −6 mol / min in a solvent such as dimethylformamide or acetonitrile containing a supporting electrolyte such as sodium perchlorate or tetrapropylammonium perchlorate. Approximate the oxidization wave in a straight line by dissolving 1 liter and sweeping to the oxidation side (noble side) using carbon (GC) as the working electrode and rotating platinum electrode as the counter electrode by cyclic voltammetry and DC polarography equipment Then, the intermediate potential of the line segment formed by the intersection of this straight line and the residual current / potential line and the intersection of the straight line and the saturation current line (or the intersection of the straight line parallel to the vertical axis passing through the peak potential value) Values are measured as values for SCE (saturated calomel electrode). Although this value may be deviated by several tens of mil volts due to the influence of the liquid potential difference or the liquid resistance of the sample solution, the reproducibility of the potential can be guaranteed by inserting a standard sample (for example, hydroquinone). The supporting electrolyte and solvent to be used can be selected appropriately depending on the oxidation potential and solubility of the test sample. The supporting electrolytes and solvents that can be used are described in Akira Fujishima et al.
以下に、本発明で使用しうる染料の具体例を示すが、本発明に用いられる染料は、下記の具体例に限定されるものでない。 Specific examples of the dye that can be used in the present invention are shown below, but the dye used in the present invention is not limited to the following specific examples.
これらの着色剤はインク組成物中、固形分換算で１〜２０重量％添加されることが好ましく、２〜１０重量％がより好ましい。 These colorants are preferably added in an amount of 1 to 20% by weight in terms of solid content in the ink composition, and more preferably 2 to 10% by weight.
［その他の成分］
以下に、必要に応じて本発明のインク組成物に用いることのできる種々の添加剤について述べる。
[Other ingredients]
The various additives that can be used in the ink composition of the present invention as necessary are described below.
〔紫外線吸収剤〕
本発明においては、得られる画像の耐候性向上、退色防止の観点から、紫外線吸収剤を用いることができる。
紫外線吸収剤としては、例えば、特開昭５８−１８５６７７号公報、同６１−１９０５３７号公報、特開平２−７８２号公報、同５−１９７０７５号公報、同９−３４０５７号公報等に記載されたベンゾトリアゾール系化合物、特開昭４６−２７８４号公報、特開平５−１９４４８３号公報、米国特許第３２１４４６３号等に記載されたベンゾフェノン系化合物、特公昭４８−３０４９２号公報、同５６−２１１４１号公報、特開平１０−８８１０６号公報等に記載された桂皮酸系化合物、特開平４−２９８５０３号公報、同８−５３４２７号公報、同８−２３９３６８号公報、同１０−１８２６２１号公報、特表平８−５０１２９１号公報等に記載されたトリアジン系化合物、リサーチディスクロージャーＮｏ．２４２３９号に記載された化合物やスチルベン系、ベンズオキサゾール系化合物に代表される紫外線を吸収して蛍光を発する化合物、いわゆる蛍光増白剤、などが挙げられる。
添加量は目的に応じて適宜選択されるが、一般的には、固形分換算で０．５〜１５重量％であることが好ましい。
[Ultraviolet absorber]
In the present invention, an ultraviolet absorber can be used from the viewpoint of improving the weather resistance of the obtained image and preventing discoloration.
Examples of the ultraviolet absorber are described in JP-A-58-185679, JP-A-61-190537, JP-A-2-782, JP-A-5-97075, JP-A-9-34057, and the like. Benzotriazole compounds, benzophenone compounds described in JP-A No. 46-2784, JP-A No. 5-194433, US Pat. No. 3,214,463, etc., JP-B Nos. 48-30492 and 56-21141 Cinnamic acid compounds described in JP-A-10-88106, JP-A-4-298503, JP-A-8-53427, JP-A-8-239368, JP-A-10-182621, JP The triazine compounds described in JP-A-8-501291, Research Disclosure No. Examples thereof include compounds described in No. 24239, compounds that emit ultraviolet light by absorbing ultraviolet rays typified by stilbene and benzoxazole compounds, so-called fluorescent brighteners, and the like.
The addition amount is appropriately selected according to the purpose, but generally it is preferably 0.5 to 15% by weight in terms of solid content.
〔増感剤〕
本発明のインク組成物には、光酸発生剤の酸発生効率の向上、感光波長の長波長化の目的で、必要に応じ、増感剤を添加してもよい。増感剤としては、光酸発生剤に対し、電子移動機構又はエネルギー移動機構で増感させるものであれば、何れでもよい。好ましくは、アントラセン、９，１０−ジアルコキシアントラセン、ピレン、ペリレンなどの芳香族多縮環化合物、アセトフェノン、ベンゾフェノン、チオキサントン、ミヒラーケトンなどの芳香族ケトン化合物、フェノチアジン、Ｎ−アリールオキサゾリジノンなどのヘテロ環化合物が挙げられる。添加量は目的に応じて適宜選択されるが、（ｂ）光酸発生剤に対し０．０１〜１モル％で用いることが好ましく、０．１〜０．５モル％がより好ましい。
[Sensitizer]
If necessary, a sensitizer may be added to the ink composition of the present invention for the purpose of improving the acid generation efficiency of the photoacid generator and increasing the photosensitive wavelength. Any sensitizer may be used as long as the photoacid generator is sensitized by an electron transfer mechanism or an energy transfer mechanism. Preferably, aromatic polycondensed compounds such as anthracene, 9,10-dialkoxyanthracene, pyrene and perylene, aromatic ketone compounds such as acetophenone, benzophenone, thioxanthone and Michlerketone, and heterocyclic compounds such as phenothiazine and N-aryloxazolidinone Is mentioned. Although the addition amount is appropriately selected according to the purpose, it is preferably used in an amount of 0.01 to 1 mol%, more preferably 0.1 to 0.5 mol% with respect to (b) the photoacid generator.
〔酸化防止剤〕
インク組成物の安定性向上のため、酸化防止剤を添加することができる。酸化防止剤としては、ヨーロッパ公開特許、同第２２３７３９号公報、同３０９４０１号公報、同第３０９４０２号公報、同第３１０５５１号公報、同第３１０５５２号公報、同第４５９４１６号公報、ドイツ公開特許第３４３５４４３号公報、特開昭５４−４８５３５号公報、同６２−２６２０４７号公報、同６３−１１３５３６号公報、同６３−１６３３５１号公報、特開平２−２６２６５４号公報、特開平２−７１２６２号公報、特開平３−１２１４４９号公報、特開平５−６１１６６号公報、特開平５−１１９４４９号公報、米国特許第４８１４２６２号明細書、米国特許第４９８０２７５号明細書等に記載のものを挙げることができる。
添加量は目的に応じて適宜選択されるが、固形分換算で０．１〜８重量％であることが好ましい。
〔Antioxidant〕
An antioxidant can be added to improve the stability of the ink composition. Examples of the antioxidant include European Published Patent No. 223739, No. 309401, No. 309402, No. 310551, No. 310552, No. 4594416, German Published Patent No. 3435443. JP, 54-85535, 62-262417, 63-113536, 63-163351, JP-A-2-262654, JP-A-2-71262, Examples thereof include those described in Kaihei 3-121449, JP-A-5-61166, JP-A-5-119449, US Pat. No. 4,814,262, US Pat. No. 4,980,275, and the like.
Although the addition amount is appropriately selected according to the purpose, it is preferably 0.1 to 8% by weight in terms of solid content.
〔褪色防止剤〕
本発明のインク組成物には、各種の有機系及び金属錯体系の褪色防止剤を使用することができる。前記有機系の褪色防止剤としては、ハイドロキノン類、アルコキシフェノール類、ジアルコキシフェノール類、フェノール類、アニリン類、アミン類、インダン類、クロマン類、アルコキシアニリン類、ヘテロ環類、などが挙げられる。前記金属錯体系の褪色防止剤としては、ニッケル錯体、亜鉛錯体、などが挙げられ、具体的には、リサーチディスクロージャーＮｏ．１７６４３の第ＶIIのＩ〜Ｊ項、同Ｎｏ．１５１６２、同Ｎｏ．１８７１６の６５０頁左欄、同Ｎｏ．３６５４４の５２７頁、同Ｎｏ．３０７１０５の８７２頁、同Ｎｏ．１５１６２に引用された特許に記載された化合物や、特開昭６２−２１５２７２号公報の１２７頁〜１３７頁に記載された代表的化合物の一般式及び化合物例に含まれる化合物を使用することができる。
添加量は目的に応じて適宜選択されるが、固形分換算で０．１〜８重量％であることが好ましい。
[Anti-fading agent]
In the ink composition of the present invention, various organic and metal complex anti-fading agents can be used. Examples of the organic anti-fading agent include hydroquinones, alkoxyphenols, dialkoxyphenols, phenols, anilines, amines, indanes, chromans, alkoxyanilines, and heterocycles. Examples of the metal complex anti-fading agent include nickel complexes and zinc complexes. No. 17643, VII, I to J, No. 15162, ibid. No. 18716, page 650, left column, ibid. No. 36544, page 527, ibid. No. 307105, page 872, ibid. The compounds described in the patent cited in No. 15162 and the compounds included in the general formulas and compound examples of representative compounds described in JP-A-62-215272, pages 127 to 137 can be used. .
Although the addition amount is appropriately selected according to the purpose, it is preferably 0.1 to 8% by weight in terms of solid content.
〔導電性塩類〕
本発明のインク組成物には、吐出物性の制御を目的として、チオシアン酸カリウム、硝酸リチウム、チオシアン酸アンモニウム、ジメチルアミン塩酸塩などの導電性塩類を添加することができる。
[Conductive salts]
Conductive salts such as potassium thiocyanate, lithium nitrate, ammonium thiocyanate, and dimethylamine hydrochloride can be added to the ink composition of the present invention for the purpose of controlling ejection properties.
〔溶剤〕
本発明のインク組成物には、被記録媒体との密着性を改良するため、極微量の有機溶剤を添加することも有効である。
溶剤としては、例えば、アセトン、メチルエチルケトン、ジエチルケトン等のケトン系溶剤、メタノール、エタノール、２−プロパノール、１−プロパノール、１−ブタノール、ｔｅｒｔ−ブタノール等のアルコール系溶剤、クロロホルム、塩化メチレン等の塩素系溶剤、ベンゼン、トルエン等の芳香族系溶剤、酢酸エチル、酢酸ブチル、酢酸イソプロピルなどのエステル系溶剤、ジエチルエーテル、テトラヒドロフラン、ジオキサン等のエーテル系溶剤、エチレングリコールモノメチルエーテル、エチレングリコールジメチルエーテル等のグリコールエーテル系溶剤、などが挙げられる。
この場合、耐溶剤性やＶＯＣの問題が起こらない範囲での添加が有効であり、その量はインク組成物全体に対し０．１〜５重量％が好ましく、より好ましくは０．１〜３重量％の範囲である。
〔solvent〕
In order to improve the adhesion to the recording medium, it is also effective to add a very small amount of an organic solvent to the ink composition of the present invention.
Examples of the solvent include ketone solvents such as acetone, methyl ethyl ketone, and diethyl ketone, alcohol solvents such as methanol, ethanol, 2-propanol, 1-propanol, 1-butanol, and tert-butanol, and chlorine such as chloroform and methylene chloride. Solvents, aromatic solvents such as benzene and toluene, ester solvents such as ethyl acetate, butyl acetate and isopropyl acetate, ether solvents such as diethyl ether, tetrahydrofuran and dioxane, glycols such as ethylene glycol monomethyl ether and ethylene glycol dimethyl ether And ether solvents.
In this case, it is effective to add the solvent within the range that does not cause the problem of solvent resistance and VOC, and the amount is preferably 0.1 to 5% by weight, more preferably 0.1 to 3% by weight based on the whole ink composition. % Range.
〔高分子化合物〕
本発明のインク組成物には、膜物性を調整するため、各種高分子化合物を添加することができる。高分子化合物としては、アクリル系重合体、ポリビニルブチラール樹脂、ポリウレタン樹脂、ポリアミド樹脂、ポリエステル樹脂、エポキシ樹脂、フェノール樹脂、ポリカーボネート樹脂、ポリビニルブチラール樹脂、ポリビニルホルマール樹脂、シェラック、ビニル系樹脂、アクリル系樹脂、ゴム系樹脂、ワックス類、その他の天然樹脂等が使用できる。また、これらは２種以上併用してもかまわない。これらのうち、アクリル系のモノマーの共重合によって得られるビニル系共重合が好ましい。更に、高分子結合材の共重合組成として、「カルボキシル基含有モノマー」、「メタクリル酸アルキルエステル」、又は「アクリル酸アルキルエステル」を構造単位として含む共重合体も好ましく用いられる。
[Polymer compound]
Various polymer compounds can be added to the ink composition of the present invention in order to adjust film physical properties. Examples of polymer compounds include acrylic polymers, polyvinyl butyral resins, polyurethane resins, polyamide resins, polyester resins, epoxy resins, phenol resins, polycarbonate resins, polyvinyl butyral resins, polyvinyl formal resins, shellacs, vinyl resins, acrylic resins. Rubber resins, waxes and other natural resins can be used. Two or more of these may be used in combination. Of these, vinyl copolymer obtained by copolymerization of acrylic monomers is preferred. Furthermore, a copolymer containing “carboxyl group-containing monomer”, “methacrylic acid alkyl ester”, or “acrylic acid alkyl ester” as a structural unit is also preferably used as the copolymer composition of the polymer binder.
〔界面活性剤〕
本発明のインク組成物には、界面活性剤を添加してもよい。
界面活性剤としては、特開昭６２−１７３４６３号、同６２−１８３４５７号の各公報に記載されたものが挙げられる。例えば、ジアルキルスルホコハク酸塩類、アルキルナフタレンスルホン酸塩類、脂肪酸塩類等のアニオン性界面活性剤、ポリオキシエチレンアルキルエーテル類、ポリオキシエチレンアルキルアリルエーテル類、アセチレングリコール類、ポリオキシエチレン・ポリオキシプロピレンブロックコポリマー類等のノニオン性界面活性剤、アルキルアミン塩類、第４級アンモニウム塩類等のカチオン性界面活性剤が挙げられる。なお、前記界面活性剤の代わりに有機フルオロ化合物を用いてもよい。前記有機フルオロ化合物は、疎水性であることが好ましい。前記有機フルオロ化合物としては、例えば、フッ素系界面活性剤、オイル状フッ素系化合物（例、フッ素油）及び固体状フッ素化合物樹脂（例、四フッ化エチレン樹脂）が含まれ、特公昭５７−９０５３号（第８〜１７欄）、特開昭６２−１３５８２６号の各公報に記載されたものが挙げられる。
[Surfactant]
A surfactant may be added to the ink composition of the present invention.
Examples of the surfactant include those described in JP-A Nos. 62-173463 and 62-183457. For example, anionic surfactants such as dialkyl sulfosuccinates, alkyl naphthalene sulfonates, fatty acid salts, polyoxyethylene alkyl ethers, polyoxyethylene alkyl allyl ethers, acetylene glycols, polyoxyethylene / polyoxypropylene blocks Nonionic surfactants such as copolymers, and cationic surfactants such as alkylamine salts and quaternary ammonium salts. An organic fluoro compound may be used in place of the surfactant. The organic fluoro compound is preferably hydrophobic. Examples of the organic fluoro compounds include fluorine surfactants, oily fluorine compounds (eg, fluorine oil) and solid fluorine compound resins (eg, tetrafluoroethylene resin). No. (columns 8 to 17) and those described in JP-A Nos. 62-135826.
この他にも、必要に応じて、例えば、レベリング添加剤、マット剤、膜物性を調整するためのワックス類、ポリオレフィンやＰＥＴ等の被記録媒体への密着性を改善するために、重合を阻害しないタッキファイヤーなどを含有させることができる。
タッキファイヤーとしては、具体的には、特開２００１−４９２００号公報の５〜６ｐに記載されている高分子量の粘着性ポリマー（例えば、（メタ）アクリル酸と炭素数１〜２０のアルキル基を有するアルコールとのエステル、（メタ）アクリル酸と炭素数３〜１４の脂環属アルコールとのエステル、（メタ）アクリル酸と炭素数６〜１４の芳香属アルコールとのエステルからなる共重合物）や、重合性不飽和結合を有する低分子量粘着付与性樹脂などである。
In addition to this, if necessary, for example, leveling additives, matting agents, waxes for adjusting film physical properties, polymerization to inhibit the adhesion to recording media such as polyolefin and PET, and the like, The tackifier which does not do can be contained.
As the tackifier, specifically, a high molecular weight adhesive polymer described in JP-A-2001-49200, 5-6p (for example, (meth) acrylic acid and an alkyl group having 1 to 20 carbon atoms). An ester with an alcohol having, an ester of (meth) acrylic acid with an alicyclic alcohol having 3 to 14 carbon atoms, a copolymer comprising an ester of (meth) acrylic acid with an aromatic alcohol having 6 to 14 carbon atoms) And a low molecular weight tackifying resin having a polymerizable unsaturated bond.
［インク組成物の好ましい物性］
本発明のインク組成物は、吐出性を考慮し、吐出時の温度において（例えば、２５〜８０℃、好ましくは２５〜５０℃）、インク粘度が５〜３０ｍＰａ・ｓであることが好ましく、更に好ましくは７〜１５ｍＰａ・ｓであり、上記範囲になるように適宜組成比を調整し決定することが好ましい。なお、２５〜３０℃でのインク粘度は、好ましくは８〜３００ｍＰａ・ｓ、より好ましくは１０〜１００ｍＰａ・ｓである。本発明のインク組成物は、粘度が上記範囲になるように適宜組成比を調整することが好ましい。室温での粘度を高く設定した場合、多孔質な被記録媒体を用いた場合でも、被記録媒体中へのインク浸透を回避し、未硬化モノマーの低減、臭気低減が可能となる。更にインク液滴着弾時のインクの滲みを抑えることができ、その結果として画質が改善される利点を有する。室温での粘度を低く設定した場合、インク吐出時の加温が不要、または加温温度を比較的低温に設定できるため、インクジェット装置に対する負荷が小さくなるとともに、使用できるインクジェットヘッドの範囲が広がる利点を有する。
[Preferred physical properties of ink composition]
The ink composition of the present invention preferably has an ink viscosity of 5 to 30 mPa · s at a temperature at the time of ejection (for example, 25 to 80 ° C., preferably 25 to 50 ° C.) in consideration of ejection properties. The pressure is preferably 7 to 15 mPa · s, and is preferably determined by adjusting the composition ratio as appropriate so as to be in the above range. The ink viscosity at 25 to 30 ° C. is preferably 8 to 300 mPa · s, more preferably 10 to 100 mPa · s. It is preferable that the composition ratio of the ink composition of the present invention is appropriately adjusted so that the viscosity is in the above range. When the viscosity at room temperature is set high, ink penetration into the recording medium can be avoided even when a porous recording medium is used, and uncured monomers can be reduced and odors can be reduced. Furthermore, ink bleeding at the time of ink droplet landing can be suppressed, and as a result, the image quality is improved. When the viscosity at room temperature is set low, heating during ink ejection is unnecessary, or the heating temperature can be set to a relatively low temperature, which reduces the load on the inkjet device and increases the range of usable inkjet heads. Have
本発明のインク組成物の表面張力は、好ましくは２０〜３０ｍＮ／ｍ、更に好ましくは２３〜２８ｍＮ／ｍである。ポリオレフィン、ＰＥＴ、コート紙、非コート紙など様々な被記録媒体へ記録する場合、滲み及び浸透の観点から、２０ｍＮ／ｍ以上が好ましく、濡れ性の点はで３０ｍＮ／ｍ以下が好ましい。 The surface tension of the ink composition of the present invention is preferably 20 to 30 mN / m, more preferably 23 to 28 mN / m. When recording on various recording media such as polyolefin, PET, coated paper, and non-coated paper, 20 mN / m or more is preferable from the viewpoint of bleeding and penetration, and the wettability is preferably 30 mN / m or less.
このようにして調製された本発明のインク組成物は、インクジェット記録用インクとして好適に用いられる。インクジェット記録用インクとして用いる場合には、インク組成物をインクジェットプリンターにより被記録媒体に射出し、その後、射出されたインク組成物に放射線を照射して硬化して記録を行う。
このインクにより得られた印刷物は、画像部が紫外線などの放射線照射により硬化しており、画像部の強度に優れるため、インクによる画像形成以外にも、例えば、平版印刷版のインク受容層（画像部）の形成など、種々の用途に使用しうる。
The ink composition of the present invention thus prepared is suitably used as an ink for inkjet recording. When used as an ink for ink jet recording, the ink composition is ejected onto a recording medium by an ink jet printer, and then the ejected ink composition is irradiated with radiation and cured to perform recording.
In the printed matter obtained with this ink, the image portion is cured by irradiation with radiation such as ultraviolet rays, and the strength of the image portion is excellent. Therefore, in addition to image formation with ink, for example, an ink receiving layer (image image of a lithographic printing plate) Part), and can be used for various purposes.
［インクジェット記録方法およびインクジェット記録装置］
次に、本発明に好適に採用され得るインクジェット記録方法およびインクジェット記録装置について、以下説明する。
[Inkjet recording method and inkjet recording apparatus]
Next, an ink jet recording method and an ink jet recording apparatus that can be suitably employed in the present invention will be described below.
本発明のインクジェット記録方法は、（ａ）被記録媒体上にインク組成物を吐出する工程、及び、（ｂ）吐出されたインク組成物に放射線を照射してインク組成物を硬化する工程を含むインクジェット記録方法であって、本発明のインク組成物を用いるインクジェット記録方法である。
また、本発明の印刷物は、前記インクジェット記録方法によって記録された印刷物である。
インクジェット記録方法においては、上記インク組成物を４０〜８０℃に加熱して、インク組成物の粘度を５〜１０ｍＰａ・ｓに下げた後、吐出することが好ましく、この方法を用いることにより高い吐出安定性を実現することができる。一般に、放射線硬化型インク組成物では、概して水性インクより粘度が高いため、印字時の温度変動による粘度変動幅が大きい。このインク組成物の粘度変動は、そのまま液滴サイズ、液滴吐出速度に対して大きな影響を与え、これにより画質劣化を引き起こすため、印字時のインク組成物温度はできるだけ一定に保つことが必要である。インク組成物温度の制御幅は設定温度±５℃とすることが好ましく、より好ましくは設定温度±２℃、更に好ましくは設定温度±１℃である。
The inkjet recording method of the present invention includes (a) a step of ejecting an ink composition onto a recording medium, and (b) a step of curing the ink composition by irradiating the ejected ink composition with radiation. An ink jet recording method using the ink composition of the present invention.
The printed matter of the present invention is a printed matter recorded by the inkjet recording method.
In the ink jet recording method, it is preferable that the ink composition is heated to 40 to 80 ° C. and the viscosity of the ink composition is lowered to 5 to 10 mPa · s and then discharged. Stability can be achieved. In general, radiation curable ink compositions generally have a higher viscosity than aqueous inks, so that the viscosity fluctuation range due to temperature fluctuations during printing is large. This viscosity variation of the ink composition directly affects the droplet size and the droplet discharge speed as it is, which causes image quality deterioration. Therefore, it is necessary to keep the temperature of the ink composition during printing as constant as possible. is there. The control range of the ink composition temperature is preferably set temperature ± 5 ° C., more preferably set temperature ± 2 ° C., and further preferably set temperature ± 1 ° C.
インクジェット記録装置には、インク組成物温度の安定化手段を備えることが一つの特徴であり、一定温度にする部位はインクタンク（中間タンクがある場合は中間タンク）からノズル吐出面までの配管系、部材の全てが対象となる。 One feature of the ink jet recording apparatus is that it includes a means for stabilizing the temperature of the ink composition, and the portion to be kept at a constant temperature is a piping system from an ink tank (an intermediate tank if an intermediate tank is present) to the nozzle ejection surface. All of the members are targeted.
温度コントロールの方法としては、特に制約はないが、例えば、温度センサーを各配管部位に複数設け、インク組成物流量、環境温度に応じた加熱制御をすることが好ましい。また、加熱するヘッドユニットは、装置本体を外気からの温度の影響を受けないよう、熱的に遮断もしくは断熱されていることが好ましい。加熱に要するプリンター立上げ時間を短縮するため、あるいは熱エネルギーのロスを低減するために、他部位との断熱を行うとともに、加熱ユニット全体の熱容量を小さくすることが好ましい。 The temperature control method is not particularly limited, but for example, it is preferable to provide a plurality of temperature sensors in each piping portion and perform heating control according to the ink composition flow rate and the environmental temperature. Moreover, it is preferable that the head unit to be heated is thermally shielded or insulated so that the apparatus main body is not affected by the temperature from the outside air. In order to shorten the printer start-up time required for heating or to reduce the loss of thermal energy, it is preferable to insulate from other parts and reduce the heat capacity of the entire heating unit.
次に放射線の照射条件について述べる。基本的な照射方法は、特開昭６０−１３２７６７号公報に開示されている。具体的には、ヘッドユニットの両側に光源を設け、シャトル方式でヘッドと光源を走査する。照射は、インク着弾後、一定時間をおいて行われることになる。更に、駆動を伴わない別光源によって硬化を完了させる。ＷＯ９９／５４４１５号では、照射方法として、光ファイバーを用いた方法やコリメートされた光源をヘッドユニット側面に設けた鏡面に当て、記録部へＵＶ光を照射する方法が開示されている。本発明においては、これらの照射方法を用いることが可能である。
ここで、使用される放射線としては、α線、γ線、電子線、Ｘ線、紫外線、可視光又は赤外光などが使用され得る。活性放射線のピーク波長は、増感色素の吸収特性にもよるが、例えば、２００〜６００ｎｍ、好ましくは、３００〜４５０ｎｍ、より好ましくは、３５０〜４５０ｎｍであることが適当である。また、本発明では、重合開始系は、低出力の活性放射線であっても十分な感度を有するものである。従って、活性放射線の出力は、例えば、２，０００ｍＪ／ｃｍ2以下、好ましくは、１０〜２，０００ｍＪ／ｃｍ2、より好ましくは、２０〜１，０００ｍＪ／ｃｍ2、さらに好ましくは、５０〜８００ｍＪ／ｃｍ2の照射エネルギーであることが適当である。また、活性放射線は、露光面照度が、例えば、１０〜２，０００ｍＷ／ｃｍ2、好ましくは、２０〜１，０００ｍＷ／ｃｍ2で照射されることが適当である。
Next, radiation conditions will be described. A basic irradiation method is disclosed in JP-A-60-132767. Specifically, a light source is provided on both sides of the head unit, and the head and the light source are scanned by a shuttle method. Irradiation is performed after a certain period of time after ink landing. Further, the curing is completed by another light source that is not driven. In WO99 / 54415, as an irradiation method, a method using an optical fiber or a method in which a collimated light source is applied to a mirror surface provided on the side surface of the head unit to irradiate the recording unit with UV light is disclosed. In the present invention, these irradiation methods can be used.
Here, α-rays, γ-rays, electron beams, X-rays, ultraviolet rays, visible light, infrared light, or the like can be used as the radiation used. The peak wavelength of the actinic radiation is, for example, from 200 to 600 nm, preferably from 300 to 450 nm, more preferably from 350 to 450 nm, although it depends on the absorption characteristics of the sensitizing dye. In the present invention, the polymerization initiation system has sufficient sensitivity even with a low-power active radiation. Thus, the output of the actinic radiation is, for example, 2,000 mJ / cm 2 or less, preferably, 10 to 2,000 mJ / cm 2, more preferably, 20 to 1,000 mJ / cm 2, more preferably, 50 to 800 mJ An irradiation energy of / cm 2 is appropriate. The active radiation, the illumination intensity on the exposed surface is, for example, 10 to 2,000 mW / cm 2, preferably, it is suitable to be irradiated at 20 to 1,000 mW / cm 2.
また本発明では、インク組成物を一定温度に加温するとともに、着弾から照射までの時間を０．０１〜０．５秒とすることが望ましく、好ましくは０．０１〜０．３秒、更に好ましくは０．０１〜０．１５秒後に放射線を照射することである。このように着弾から照射までの時間を極短時間に制御することにより、着弾インクが硬化前に滲むことを防止するこが可能となる。また、多孔質な被記録媒体に対しても光源の届かない深部までインク組成物が浸透する前に露光することができる為、未反応モノマーの残留を抑えられ、その結果として臭気を低減することができる。上記説明したインクジェット記録方法と本発明のインク組成物とを併せて用いることにより、大きな相乗効果をもたらすことになる。特に、２５℃におけるインク粘度が８〜５００ｍＰａ・ｓのインク組成物を用いると大きな効果を得ることが出来る。このような記録方法を取ることで、表面の濡れ性が異なる様々な被記録媒体に対しても、着弾したインクのドット径を一定に保つことが出来、画質が向上する。なお、カラー画像を得るためには、明度の低い色から順に重ねていくことが好ましい。明度の低いインクを重ねると、下部のインクまで照射線が到達しにくく、硬化感度の阻害、残留モノマーの増加および臭気の発生、密着性の劣化が生じやすい。また、照射は、全色を射出してまとめて露光することが可能だが、１色毎に露光するほうが、硬化促進の観点で好ましい。 In the present invention, the ink composition is heated to a constant temperature, and the time from landing to irradiation is desirably 0.01 to 0.5 seconds, preferably 0.01 to 0.3 seconds, and more preferably The irradiation is preferably performed after 0.01 to 0.15 seconds. Thus, by controlling the time from landing to irradiation to an extremely short time, it is possible to prevent the landing ink from bleeding before being cured. In addition, since the ink composition can be exposed to a porous recording medium before reaching the deep part where the light source does not reach, residual unreacted monomer can be suppressed, and as a result, odor can be reduced. Can do. By using the inkjet recording method described above and the ink composition of the present invention in combination, a great synergistic effect is brought about. In particular, when an ink composition having an ink viscosity of 8 to 500 mPa · s at 25 ° C. is used, a great effect can be obtained. By adopting such a recording method, the dot diameter of the landed ink can be kept constant even on various recording media having different surface wettability, and the image quality is improved. In addition, in order to obtain a color image, it is preferable to superimpose in order from the color with the lowest brightness. When inks with low lightness are stacked, it is difficult for the irradiation rays to reach the lower ink, and inhibition of curing sensitivity, increase of residual monomers, generation of odor, and deterioration of adhesion tend to occur. Irradiation can be performed by injecting all colors and exposing them together, but exposure for each color is preferable from the viewpoint of curing acceleration.
本発明に用いられるインクジェット記録装置としては、特に制限はなく、市販のインクジェット記録装置が使用できる。即ち、本発明においては、市販のインクジェット記録装置を用いて被記録媒体へ記録することができる。
本発明で用いることのできるインクジェット記録装置としては、例えば、インク供給系、温度センサー、活性放射線源を含む。
インク供給系は、例えば、本発明の上記インク組成物を含む元タンク、供給配管、インクジェットヘッド直前のインク供給タンク、フィルター、ピエゾ型のインクジェットヘッドからなる。ピエゾ型のインクジェットヘッドは、１〜１００ｐｌ、好ましくは、８〜３０ｐｌのマルチサイズドットを例えば、３２０×３２０〜４，０００×４，０００ｄｐｉ、好ましくは、４００×４００〜１，６００×１，６００ｄｐｉ、より好ましくは、７２０×７２０ｄｐｉの解像度で吐出できるよう駆動することができる。なお、本発明でいうｄｐｉとは、２．５４ｃｍ当たりのドット数を表す。
上述したように、放射線硬化型インクは、吐出されるインクを一定温度にすることが望ましいことから、インク供給タンクからインクジェットヘッド部分までは、断熱及び加温を行うことができる。温度コントロールの方法としては、特に制約はないが、例えば、温度センサーを各配管部位に複数設け、インク流量、環境温度に応じた加熱制御をすることが好ましい。温度センサーは、インク供給タンク及びインクジェットヘッドのノズル付近に設けることができる。また、加熱するヘッドユニットは、装置本体を外気からの温度の影響を受けないよう、熱的に遮断若しくは断熱されていることが好ましい。加熱に要するプリンター立上げ時間を短縮するため、あるいは熱エネルギーのロスを低減するために、他部位との断熱を行うとともに、加熱ユニット全体の熱容量を小さくすることが好ましい。
活性放射線源としては、水銀ランプやガス・固体レーザー等が主に利用されており、紫外線光硬化型インクジェットには、水銀ランプ、メタルハライドランプが広く知られている。しかしながら、現在環境保護の観点から水銀フリー化が強く望まれており、ＧａＮ系半導体紫外発光デバイスへの置き換えは産業的、環境的にも非常に有用である。更にＬＥＤ（ＵＶ−ＬＥＤ），ＬＤ（ＵＶ−ＬＤ）は小型、高寿命、高効率、低コストであり、光硬化型インクジェット用光源として期待されている。
また、発光ダイオード（ＬＥＤ）及びレーザーダイオード（ＬＤ）を活性放射線源として用いることが可能である。特に、紫外線源を要する場合、紫外ＬＥＤ及び紫外ＬＤを使用することができる。例えば、日亜化学（株）は、主放出スペクトルが３６５ｎｍと４２０ｎｍとの間の波長を有する紫色ＬＥＤを上市している。更に一層短い波長が必要とされる場合、米国特許番号第６，０８４，２５０号明細書は、３００ｎｍと３７０ｎｍとの間に中心付けされた活性放射線を放出し得るＬＥＤを開示している。また、他の紫外ＬＥＤも、入手可能であり、異なる紫外線帯域の放射を照射することができる。本発明で特に好ましい活性放射線源は、ＵＶ−ＬＥＤであり、特に好ましくは、３５０〜４２０ｎｍにピーク波長を有するＵＶ−ＬＥＤである。
また、ＬＥＤの被記録媒体上での最高照度は１０〜２，０００ｍＷ／ｃｍ2であることが好ましく、２０〜１，０００ｍＷ／ｃｍ2であることがより好ましく、特に好ましくは５０〜８００ｍＷ／ｃｍ2である。
There is no restriction | limiting in particular as an inkjet recording device used for this invention, A commercially available inkjet recording device can be used. That is, in the present invention, recording can be performed on a recording medium using a commercially available inkjet recording apparatus.
Examples of the ink jet recording apparatus that can be used in the present invention include an ink supply system, a temperature sensor, and an actinic radiation source.
The ink supply system includes, for example, an original tank containing the ink composition of the present invention, a supply pipe, an ink supply tank immediately before the inkjet head, a filter, and a piezo-type inkjet head. The piezo-type inkjet head has a multi-size dot of 1 to 100 pl, preferably 8 to 30 pl, for example, 320 × 320 to 4,000 × 4,000 dpi, preferably 400 × 400 to 1,600 × 1,600 dpi. More preferably, it can be driven so as to discharge at a resolution of 720 × 720 dpi. In the present invention, dpi represents the number of dots per 2.54 cm.
As described above, since it is desirable that the radiation curable ink has a constant temperature for the ejected ink, heat insulation and heating can be performed from the ink supply tank to the inkjet head portion. The temperature control method is not particularly limited, but for example, it is preferable to provide a plurality of temperature sensors in each piping portion and perform heating control according to the ink flow rate and the environmental temperature. The temperature sensor can be provided near the ink supply tank and the nozzle of the inkjet head. Moreover, it is preferable that the head unit to be heated is thermally shielded or insulated so that the apparatus main body is not affected by the temperature from the outside air. In order to shorten the printer start-up time required for heating or to reduce the loss of thermal energy, it is preferable to insulate from other parts and reduce the heat capacity of the entire heating unit.
As active radiation sources, mercury lamps, gas / solid lasers, and the like are mainly used, and mercury lamps and metal halide lamps are widely known as ultraviolet light curable ink jets. However, from the viewpoint of environmental protection, mercury-free is strongly desired, and replacement with a GaN-based semiconductor ultraviolet light-emitting device is very useful industrially and environmentally. Furthermore, LED (UV-LED) and LD (UV-LD) are small, have a long life, have high efficiency, and are low in cost, and are expected as light sources for photocurable ink jets.
Further, a light emitting diode (LED) and a laser diode (LD) can be used as the active radiation source. In particular, when an ultraviolet light source is required, an ultraviolet LED and an ultraviolet LD can be used. For example, Nichia Corporation has launched a purple LED whose main emission spectrum has a wavelength between 365 nm and 420 nm. When even shorter wavelengths are required, US Pat. No. 6,084,250 discloses an LED that can emit actinic radiation centered between 300 nm and 370 nm. Other ultraviolet LEDs are also available and can emit radiation in different ultraviolet bands. The actinic radiation source particularly preferred in the present invention is a UV-LED, particularly preferably a UV-LED having a peak wavelength at 350 to 420 nm.
It is preferable that maximum illumination intensity of the LED on a recording medium is 10 to 2,000 mW / cm 2, more preferably 20 to 1,000 mW / cm 2, particularly preferably 50 to 800 mW / cm 2 .
〔被記録媒体〕
本発明のインク組成物を適用しうる被記録媒体としては、特に制限はなく、通常の非コート紙、コート紙などの紙類、いわゆる軟包装に用いられる各種非吸収性樹脂材料あるいは、それをフィルム状に成形した樹脂フィルムを用いることができ、各種プラスチックフィルムとしては、例えば、ＰＥＴフィルム、ＯＰＳフィルム、ＯＰＰフィルム、ＯＮｙフィルム、ＰＶＣフィルム、ＰＥフィルム、ＴＡＣフィルム等を挙げることができる。その他、被記録媒体材料として使用しうるプラスチックとしては、ポリカーボネート、アクリル樹脂、ＡＢＳ、ポリアセタール、ＰＶＡ、ゴム類などが挙げられる。また、金属類や、ガラス類も被記録媒体として使用可能である。
本発明のインク組成物は、硬化時の熱収縮が少なく、基材（被記録媒体）との密着性に優れるため、インクの硬化収縮、硬化反応時の発熱などにより、フィルムのカール、変形が生じやすいフィルム、例えば、熱でシュリンク可能な、ＰＥＴフィルム、ＯＰＳフィルム、ＯＰＰフィルム、ＯＮｙフィルム、ＰＶＣフィルムなどにおいても、高精細な画像を形成しうるという利点を有する。
[Recording medium]
The recording medium to which the ink composition of the present invention can be applied is not particularly limited, and various non-absorbing resin materials used for ordinary non-coated paper, coated paper, and so on, so-called soft packaging, or the like. A resin film formed into a film can be used, and examples of the various plastic films include PET film, OPS film, OPP film, ONy film, PVC film, PE film, and TAC film. In addition, examples of the plastic that can be used as a recording medium material include polycarbonate, acrylic resin, ABS, polyacetal, PVA, and rubbers. Metals and glasses can also be used as the recording medium.
The ink composition of the present invention has little heat shrinkage at the time of curing and excellent adhesion to the substrate (recording medium), so that the film curls and deforms due to the ink shrinkage and heat generation during the curing reaction. Films that tend to occur, for example, heat-shrinkable PET films, OPS films, OPP films, ONy films, PVC films, etc., have the advantage that high-definition images can be formed.
［平版印刷版］
本発明のインク組成物の好適な応用例として、平版印刷版への使用が挙げられる。
本発明の平版印刷版の製造方法は、（ａ）本発明のインク組成物を親水性支持体上に吐出する工程、及び、（ｂ）吐出されたインク組成物に放射線を照射して、前記インク組成物を硬化させることにより、前記インク組成物が硬化してなる疎水性画像を前記親水性支持体上に形成する工程を含む。
また、本発明の平版印刷版は、前記平版印刷版の製造方法によって製造された平版印刷版である。
本発明のインク組成物を、インクジェット記録装置などを用いて、親水性支持体上に吐出した後、放射線を照射してインクを硬化させ疎水性画像を形成することで、親水性支持体表面に画像様に疎水性のインク受容性領域が形成される。ここに、インクと水性成分を供給すると、水性成分が親水性支持体の露出している領域に保持され、インクが疎水性画像に保持されて、そのまま印刷工程を実施することができる。
本発明のインク組成物は放射線照射により優れた硬化性を示すことから、これを応用した本発明の平版印刷版は耐刷性に優れた画像部を有することになる。また、画像部を形成するのにインクジェット記録装置を用いて、デジタルデータにより直接、高精細な平版印刷版の画像部を形成することができる。
平版印刷版の製造に用いられるインク組成物は、前記した本発明のインク組成物をそのまま適用すればよい。
[Lithographic printing plate]
A preferable application example of the ink composition of the present invention is use in a lithographic printing plate.
The method for producing a lithographic printing plate of the present invention comprises (a) a step of discharging the ink composition of the present invention onto a hydrophilic support, and (b) irradiating the discharged ink composition with radiation, The method includes a step of forming a hydrophobic image formed by curing the ink composition on the hydrophilic support by curing the ink composition.
The lithographic printing plate of the present invention is a lithographic printing plate produced by the method for producing a lithographic printing plate.
After discharging the ink composition of the present invention onto a hydrophilic support using an ink jet recording apparatus or the like, the ink is cured by irradiating with radiation to form a hydrophobic image on the surface of the hydrophilic support. An image-like hydrophobic ink-receiving area is formed. When the ink and the aqueous component are supplied here, the aqueous component is held in the exposed region of the hydrophilic support, the ink is held in the hydrophobic image, and the printing process can be performed as it is.
Since the ink composition of the present invention exhibits excellent curability upon irradiation with radiation, the lithographic printing plate of the present invention to which the ink composition is applied has an image portion having excellent printing durability. In addition, an inkjet recording apparatus can be used to form an image portion, and a high-definition lithographic printing plate image portion can be formed directly from digital data.
The ink composition of the present invention described above may be applied as it is to the ink composition used for the production of a lithographic printing plate.
〔支持体〕
本発明の平版印刷版を作製するにあたって好ましく使用される支持体について説明する。
本発明の平版印刷版に用いられる支持体は、特に限定されず、寸度的に安定な板状の支持体であればよい。支持体を構成する材料が表面親水性を有するものであれば、そのまま用いてもよく、また、支持体を構成する板状材料の表面に親水化処理を行って用いてもよい。
支持体を構成する材料としては、例えば、紙、プラスチック（例えば、ポリエチレン、ポリプロピレン、ポリスチレン等）がラミネートされた紙、金属板（例えば、アルミニウム、亜鉛、銅等）、プラスチックフィルム（例えば、二酢酸セルロース、三酢酸セルロース、プロピオン酸セルロース、酪酸セルロース、酢酸酪酸セルロース、硝酸セルロース、ポリエチレンテレフタレート、ポリエチレン、ポリスチレン、ポリプロピレン、ポリカーボネート、ポリビニルアセタール等）、上述した金属がラミネートされまたは蒸着された紙またはプラスチックフィルム等が挙げられる。好ましい支持体としては、ポリエステルフィルムおよびアルミニウム板が挙げられる。なかでも、寸法安定性がよく、比較的安価であるアルミニウム板が好ましい。
[Support]
The support preferably used for preparing the planographic printing plate of the present invention will be described.
The support used for the lithographic printing plate of the present invention is not particularly limited as long as it is a dimensionally stable plate-like support. If the material constituting the support has surface hydrophilicity, it may be used as it is, or the surface of the plate-like material constituting the support may be subjected to a hydrophilic treatment.
Examples of the material constituting the support include paper, paper laminated with plastic (eg, polyethylene, polypropylene, polystyrene, etc.), metal plate (eg, aluminum, zinc, copper, etc.), and plastic film (eg, diacetic acid). Cellulose, cellulose triacetate, cellulose propionate, cellulose butyrate, cellulose acetate butyrate, cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.), paper or plastic film laminated or vapor-deposited with the above metals Etc. Preferable supports include a polyester film and an aluminum plate. Among these, an aluminum plate that has good dimensional stability and is relatively inexpensive is preferable.
アルミニウム板は、純アルミニウム板、アルミニウムを主成分とし、微量の異元素を含む合金板、または、アルミニウムもしくはアルミニウム合金の薄膜にプラスチックがラミネートされているものである。アルミニウム合金に含まれる異元素には、ケイ素、鉄、マンガン、銅、マグネシウム、クロム、亜鉛、ビスマス、ニッケル、チタン等が挙げられる。合金中の異元素の含有量は１０重量％以下であるのが好ましい。本発明においては、純アルミニウム板が好ましいが、完全に純粋なアルミニウムは精錬技術上製造が困難であるので、わずかに異元素を含有するものでもよい。アルミニウム板は、その組成が特定されるものではなく、公知公用の素材のものを適宜利用することができる。 The aluminum plate is a pure aluminum plate, an alloy plate containing aluminum as a main component and containing a trace amount of foreign elements, or a plastic laminated on a thin film of aluminum or an aluminum alloy. Examples of the foreign element contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of foreign elements in the alloy is preferably 10% by weight or less. In the present invention, a pure aluminum plate is preferable, but completely pure aluminum is difficult to manufacture in terms of refining technology, and therefore may contain a slightly different element. The composition of the aluminum plate is not specified, and a publicly known material can be used as appropriate.
支持体の厚さは０．１〜０．６ｍｍであるのが好ましく、０．１５〜０．４ｍｍであるのがより好ましい。 The thickness of the support is preferably from 0.1 to 0.6 mm, more preferably from 0.15 to 0.4 mm.
アルミニウム板を使用するに先立ち、粗面化処理、陽極酸化処理等の表面処理を施すのが好ましい。表面処理により、親水性の向上および画像記録層と支持体との密着性の確保が容易になる。アルミニウム板を粗面化処理するに先立ち、所望により、表面の圧延油を除去するための界面活性剤、有機溶剤、アルカリ性水溶液等による脱脂処理が行われる。 Prior to using the aluminum plate, it is preferable to perform a surface treatment such as roughening treatment or anodizing treatment. By the surface treatment, it is easy to improve hydrophilicity and secure adhesion between the image recording layer and the support. Prior to roughening the aluminum plate, a degreasing treatment with a surfactant, an organic solvent, an alkaline aqueous solution or the like for removing rolling oil on the surface is performed as desired.
アルミニウム板表面の粗面化処理は、種々の方法により行われるが、例えば、機械的粗面化処理、電気化学的粗面化処理（電気化学的に表面を溶解させる粗面化処理）、化学的粗面化処理（化学的に表面を選択溶解させる粗面化処理）が挙げられる。
機械的粗面化処理の方法としては、ボール研磨法、ブラシ研磨法、ブラスト研磨法、バフ研磨法等の公知の方法を用いることができる。また、アルミニウムの圧延段階において凹凸を設けたロールで凹凸形状を転写する転写法も用いてもかまわない。
電気化学的粗面化処理の方法としては、例えば、塩酸、硝酸等の酸を含有する電解液中で交流または直流により行う方法が挙げられる。また、特開昭５４−６３９０２号公報に記載されているような混合酸を用いる方法も挙げられる。
The surface roughening treatment of the aluminum plate is performed by various methods. For example, mechanical surface roughening treatment, electrochemical surface roughening treatment (surface roughening treatment for dissolving the surface electrochemically), chemical treatment, etc. Surface roughening treatment (roughening treatment that chemically selectively dissolves the surface).
As a method for the mechanical surface roughening treatment, a known method such as a ball polishing method, a brush polishing method, a blast polishing method, or a buff polishing method can be used. Also, a transfer method in which the uneven shape is transferred with a roll provided with unevenness in the aluminum rolling step may be used.
Examples of the electrochemical surface roughening treatment include a method in which an alternating current or a direct current is used in an electrolytic solution containing an acid such as hydrochloric acid or nitric acid. Another example is a method using a mixed acid as described in JP-A-54-63902.
粗面化処理されたアルミニウム板は、必要に応じて、水酸化カリウム、水酸化ナトリウム等の水溶液を用いてアルカリエッチング処理を施され、更に、中和処理された後、所望により、耐摩耗性を高めるために陽極酸化処理を施される。 The surface-roughened aluminum plate is subjected to an alkali etching treatment using an aqueous solution of potassium hydroxide, sodium hydroxide or the like, if necessary, further neutralized, and if desired, wear resistant. In order to increase the anodic oxidation treatment.
アルミニウム板の陽極酸化処理に用いられる電解質としては、多孔質酸化皮膜を形成させる種々の電解質の使用が可能である。一般的には、硫酸、塩酸、シュウ酸、クロム酸またはそれらの混酸が用いられる。それらの電解質の濃度は電解質の種類によって適宜決められる。
陽極酸化処理の条件は、用いられる電解質により種々変わるので一概に特定することはできないが、一般的には、電解質濃度１〜８０重量％溶液、液温５〜７０℃、電流密度５〜６０Ａ／ｄｍ2、電圧１〜１００Ｖ、電解時間１０秒〜５分であるのが好ましい。形成される陽極酸化皮膜の量は、１．０〜５．０ｇ／ｍ2であるのが好ましく、１．５〜４．０ｇ／ｍ2であるのがより好ましい。この範囲で、良好な耐刷性と平版印刷版の非画像部の良好な耐傷性が得られるので好ましい。
As an electrolyte used for anodizing treatment of an aluminum plate, various electrolytes that form a porous oxide film can be used. In general, sulfuric acid, hydrochloric acid, oxalic acid, chromic acid or a mixed acid thereof is used. The concentration of these electrolytes is appropriately determined depending on the type of electrolyte.
The conditions for anodizing treatment vary depending on the electrolyte used, and thus cannot be specified in general. In general, however, an electrolyte concentration of 1 to 80% by weight solution, a liquid temperature of 5 to 70 ° C., a current density of 5 to 60 A / dm 2 , voltage 1 to 100 V, and electrolysis time 10 seconds to 5 minutes are preferable. The amount of the anodized film formed is preferably from 1.0 to 5.0 g / m 2, and more preferably 1.5 to 4.0 g / m 2. Within this range, good printing durability and good scratch resistance of the non-image area of the lithographic printing plate can be obtained, which is preferable.
本発明で用いられる支持体としては、上記のような表面処理をされ陽極酸化皮膜を有する基板をそのまま用いても良いが、上層との接着性、親水性、汚れ難さ、断熱性などをの一層改良のため、必要に応じて、特開２００１−２５３１８１号や特開２００１−３２２３６５号に記載されている陽極酸化皮膜のマイクロポアの拡大処理や封孔処理、および親水性化合物を含有する水溶液に浸漬する表面親水化処理などを適宜選択して行うことができる。もちろんこれら拡大処理、封孔処理は、これらに記載のものに限られたものではなく従来公知の何れも方法も行うことができる。 As a support used in the present invention, a substrate that has been surface-treated as described above and has an anodized film may be used as it is, but it has adhesion to the upper layer, hydrophilicity, resistance to contamination, heat insulation, etc. For further improvement, if necessary, an aqueous solution containing an anodized film micropore expansion treatment or sealing treatment described in JP-A Nos. 2001-253181 and 2001-322365, and a hydrophilic compound It is possible to appropriately select and perform surface hydrophilization treatment that is immersed in the substrate. Of course, these enlargement processing and sealing processing are not limited to those described above, and any conventionally known method can be performed.
〔封孔処理〕
封孔処理としては、蒸気封孔のほかフッ化ジルコン酸の単独処理、フッ化ナトリウムによる処理など無機フッ素化合物を含有する水溶液による封孔処理、塩化リチウムを添加した蒸気封孔、熱水による封孔処理でも可能である。
なかでも、無機フッ素化合物を含有する水溶液による封孔処理、水蒸気による封孔処理および熱水による封孔処理が好ましい。
[Sealing treatment]
Sealing treatment includes vapor sealing, single treatment with zirconic fluoride, treatment with aqueous solution containing inorganic fluorine compounds such as treatment with sodium fluoride, vapor sealing with addition of lithium chloride, sealing with hot water. Hole processing is also possible.
Of these, sealing treatment with an aqueous solution containing an inorganic fluorine compound, sealing treatment with water vapor, and sealing treatment with hot water are preferable.
〔親水化処理〕
本発明に用いられる親水化処理としては、米国特許第２，７１４，０６６号、同第３，１８１，４６１号、同第３，２８０，７３４号および同第３，９０２，７３４号の各明細書に記載されているようなアルカリ金属シリケート法がある。この方法においては、支持体をケイ酸ナトリウムなどの水溶液で浸漬処理し、または電解処理する。そのほかに、特公昭３６−２２０６３号公報に記載されているフッ化ジルコン酸カリウムで処理する方法、米国特許第３，２７６，８６８号、同第４，１５３，４６１号および同第４，６８９，２７２号の各明細書に記載されているようなポリビニルホスホン酸で処理する方法などが挙げられる。
[Hydrophilic treatment]
Examples of the hydrophilization treatment used in the present invention include US Pat. Nos. 2,714,066, 3,181,461, 3,280,734 and 3,902,734. There is an alkali metal silicate method as described in the book. In this method, the support is immersed in an aqueous solution such as sodium silicate or electrolytically treated. In addition, the treatment with potassium zirconate fluoride described in JP-B 36-22063, U.S. Pat. Nos. 3,276,868, 4,153,461 and 4,689, And a method of treating with polyvinyl phosphonic acid as described in each specification of No. 272.
本発明に用いることのできる支持体は、中心線平均粗さが０．１０〜１．２μｍであるのが好ましい。この範囲であると、画像記録層との良好な密着性、良好な耐刷性と良好な汚れ難さが得られ好ましい。 The support that can be used in the present invention preferably has a center line average roughness of 0.10 to 1.2 μm. Within this range, good adhesion to the image recording layer, good printing durability and good stain resistance can be obtained.
以下に実施例及び比較例を示し、本発明をより具体的に説明する。但し、本発明はこれらの実施例によって限定されるものではない。 Hereinafter, the present invention will be described in more detail with reference to examples and comparative examples. However, the present invention is not limited to these examples.
〔アミン化合物の各物性値の測定方法〕
用いたアミン化合物の共役酸のｐＫａについて、公知文献等によりその値が明らかになっていないものは、エタノール／水（７／３）中、ＨＣｌ及びＮａＯＨ標準液による滴定により求めた。
[Methods for measuring physical properties of amine compounds]
About the pKa of the conjugate acid of the amine compound used, those whose values were not clarified by known literatures and the like were determined by titration with HCl and NaOH standard solutions in ethanol / water (7/3).
〔実施例１〕
《顔料分散物の調製》
下記に記載の方法に従って、イエロー、マゼンタ、シアン及びブラックの各顔料分散物１を調製した。なお、分散条件は、各顔料粒子の平均粒径が０．２〜０．３μｍの範囲となるように、公知の分散装置を用いて、分散条件を適宜調整して行、次いで加熱下でフィルター濾過を行って調製した。
（イエロー顔料分散物１）
・Ｃ．Ｉ．ピグメントイエロー１３ ２０重量部
・高分子分散剤（Ｚｅｎｅｃａ社製 Ｓｏｌｓｐｅｒｓｅシリーズ）２０重量部
・ジエチレングリコールジビニルエーテル（ＢＡＳＦ社製） ６０重量部
（マゼンタ顔料分散物１）
・Ｃ．Ｉ．ピグメントレッド５７：１ ２０重量部
・高分子分散剤（Ｚｅｎｅｃａ社製 Ｓｏｌｓｐｅｒｓｅシリーズ）２０重量部
・ジエチレングリコールジビニルエーテル（ＢＡＳＦ社製） ６０重量部
（シアン顔料分散物１）
・Ｃ．Ｉ．ピグメントブルー１５：３ ２０重量部
・高分子分散剤（Ｚｅｎｅｃａ社製 Ｓｏｌｓｐｅｒｓｅシリーズ）２０重量部
・ジエチレングリコールジビニルエーテル（ＢＡＳＦ社製） ６０重量部
（ブラック顔料分散物１）
・Ｃ．Ｉ．ピグメントブラック７ ２０重量部
・高分子分散剤（Ｚｅｎｅｃａ社製 Ｓｏｌｓｐｅｒｓｅシリーズ）２０重量部
・ジエチレングリコールジビニルエーテル（ＢＡＳＦ社製） ６０重量部
[Example 1]
<< Preparation of pigment dispersion >>
According to the method described below, yellow, magenta, cyan and black pigment dispersions 1 were prepared. The dispersion conditions are adjusted appropriately using a known dispersion device so that the average particle diameter of each pigment particle is in the range of 0.2 to 0.3 μm, and then filtered under heating. Prepared by filtration.
(Yellow pigment dispersion 1)
・ C. I. Pigment Yellow 13 20 parts by weight, polymer dispersant (Solsperse series manufactured by Zeneca) 20 parts by weight, diethylene glycol divinyl ether (manufactured by BASF) 60 parts by weight (magenta pigment dispersion 1)
・ C. I. Pigment Red 57: 1 20 parts by weight, polymer dispersant (Solsperse series manufactured by Zeneca) 20 parts by weight, diethylene glycol divinyl ether (manufactured by BASF) 60 parts by weight (cyan pigment dispersion 1)
・ C. I. Pigment Blue 15: 3 20 parts by weight / polymer dispersing agent (Solsperse series manufactured by Zeneca) 20 parts by weight / diethylene glycol divinyl ether (manufactured by BASF) 60 parts by weight (black pigment dispersion 1)
・ C. I. 20 parts by weight of Pigment Black 7 20 parts by weight of polymer dispersant (Solsperse series manufactured by Zeneca) 60 parts by weight of diethylene glycol divinyl ether (manufactured by BASF)
《インクの調製》
下記の成分を混合し、フィルターによって濾過して、各色のインク１とした。
（イエローインク１）
・（ａ）カチオン重合性化合物
セロキサイド２０２１（エポキシ化合物：ダイセルＵＣＢ（株）製） ３５重量部
ＯＸＴ−２２１（オキセタン化合物：東亞合成（株）製） ５５重量部
・（ｂ）光酸発生剤
化合物例（ｂ−２７）／（ｂ−３２）＝１／２ ５重量部
・（ｃ）着色剤（前記顔料分散物）
イエロー顔料分散物１ ５重量部
・（ｄ）２種以上のアミン化合物
アミン化合物例（Ｉ−５：ｐＫａ値＝４．６） ０．０３重量部
アミン化合物例（III−３：ｐＫａ値＝１０．８） ０．０３重量部
（マゼンタインク１）
・（ａ）カチオン重合性化合物
セロキサイド２０２１（エポキシ化合物：ダイセルＵＣＢ（株）製） ３５重量部
ＯＸＴ−２２１（オキセタン化合物：東亞合成（株）製） ５５重量部
・（ｂ）光酸発生剤
化合物例（ｂ−３） ５重量部
・（ｃ）着色剤（前記顔料分散物）
マゼンタ顔料分散物１ ５重量部
・（ｄ）２種以上のアミン化合物
アミン化合物例（Ｉ−５：ｐＫａ値＝４．６） ０．０３重量部
アミン化合物例（III−３：ｐＫａ値＝１０．８） ０．０３重量部
（シアンインク１）
・（ａ）カチオン重合性化合物
セロキサイド２０２１（エポキシ化合物：ダイセルＵＣＢ（株）製） ３５重量部
ＯＸＴ−２２１（オキセタン化合物：東亞合成（株）製） ５５重量部
・（ｂ）光酸発生剤
化合物例（ｂ−７５） ５重量部
・（ｃ）着色剤（前記顔料分散物）
シアン顔料分散物１ ５重量部
・（ｄ）２種以上のアミン化合物
アミン化合物例（Ｉ−５：ｐＫａ値＝４．６） ０．０３重量部
アミン化合物例（III−３：ｐＫａ値＝１０．８） ０．０３重量部
（ブラックインク１）
・（ａ）カチオン重合性化合物
セロキサイド２０２１（エポキシ化合物：ダイセルＵＣＢ（株）製） ３５重量部
ＯＸＴ−２２１（オキセタン化合物：東亞合成（株）製） ５５重量部
・（ｂ）光酸発生剤
化合物例（ｂ−１０） ５重量部
・（ｃ）着色剤（前記顔料分散物）
ブラック顔料分散物１ ５重量部
・（ｄ）２種以上のアミン化合物
アミン化合物例（Ｉ−５：ｐＫａ値＝４．６） ０．０３重量部
アミン化合物例（III−３：ｐＫａ値＝１０．８） ０．０３重量部
・増感剤
９，１０−ジメトキシアントラセン ０．５重量部
<Preparation of ink>
The following components were mixed and filtered through a filter to obtain ink 1 of each color.
(Yellow ink 1)
-(A) Cationic polymerizable compound Celoxide 2021 (epoxy compound: manufactured by Daicel UCB) 35 parts by weight OXT-221 (Oxetane compound: manufactured by Toagosei Co., Ltd.) 55 parts by weight-(b) Photoacid generator Compound Example (b-27) / (b-32) = 1/2 5 parts by weight (c) Colorant (pigment dispersion)
Yellow pigment dispersion 1 5 parts by weight (d) Two or more types of amine compounds Examples of amine compounds (I-5: pKa value = 4.6) 0.03 parts by weight Examples of amine compounds (III-3: pKa value = 10) .8) 0.03 part by weight (magenta ink 1)
-(A) Cationic polymerizable compound Celoxide 2021 (epoxy compound: manufactured by Daicel UCB) 35 parts by weight OXT-221 (Oxetane compound: manufactured by Toagosei Co., Ltd.) 55 parts by weight-(b) Photoacid generator Compound Example (b-3) 5 parts by weight / (c) Colorant (pigment dispersion)
Magenta Pigment Dispersion 1 5 parts by weight (d) Two or more types of amine compounds Amine compound examples (I-5: pKa value = 4.6) 0.03 parts by weight Amine compound examples (III-3: pKa value = 10) .8) 0.03 part by weight (cyan ink 1)
-(A) Cationic polymerizable compound Celoxide 2021 (epoxy compound: manufactured by Daicel UCB) 35 parts by weight OXT-221 (Oxetane compound: manufactured by Toagosei Co., Ltd.) 55 parts by weight-(b) Photoacid generator Compound Example (b-75) 5 parts by weight. (C) Colorant (pigment dispersion)
Cyan Pigment Dispersion 1 5 parts by weight. (D) Two or more types of amine compounds Amine compound examples (I-5: pKa value = 4.6) 0.03 parts by weight Amine compound examples (III-3: pKa value = 10) .8) 0.03 part by weight (black ink 1)
-(A) Cationic polymerizable compound Celoxide 2021 (epoxy compound: manufactured by Daicel UCB) 35 parts by weight OXT-221 (Oxetane compound: manufactured by Toagosei Co., Ltd.) 55 parts by weight-(b) Photoacid generator Compound Example (b-10) 5 parts by weight / (c) Colorant (pigment dispersion)
Black Pigment Dispersion 1 5 parts by weight. (D) Two or more kinds of amine compounds Amine compound examples (I-5: pKa value = 4.6) 0.03 parts by weight Amine compound examples (III-3: pKa value = 10) .8) 0.03 part by weight / sensitizer 9,10-dimethoxyanthracene 0.5 part by weight
《インクジェット画像記録》（多色画像の評価）
次に、ピエゾ型インクジェットノズルを有する市販のインクジェット記録装置を用いて、被記録媒体への記録を行った。インク供給系は、元タンク、供給配管、インクジェットヘッド直前のインク供給タンク、フィルター、ピエゾ型のインクジェットヘッドから成り、インク供給タンクからインクジェットヘッド部分までを断熱および加温を行った。温度センサーは、インク供給タンクおよびインクジェットヘッドのノズル付近にそれぞれ設け、ノズル部分が常に４０℃±２℃となるよう、温度制御を行った。ピエゾ型のインクジェットヘッドは、８〜３０ｐｌのマルチサイズドットを７２０×７２０ｄｐｉの解像度で射出できるよう駆動した。着弾後はＵＶ−Ａ光を露光面照度１００ｍＷ／ｃｍ2、に集光し、被記録媒体上にインク着弾した０．１秒後に照射が始まるよう露光系、主走査速度及び射出周波数を調整した。また、露光時間を可変とし、露光エネルギーを照射した。なお、本発明でいうｄｐｉとは、２．５４ｃｍ当たりのドット数を表す。
<Inkjet image recording> (Evaluation of multicolor images)
Next, recording on a recording medium was performed using a commercially available inkjet recording apparatus having a piezoelectric inkjet nozzle. The ink supply system was composed of an original tank, a supply pipe, an ink supply tank immediately before the inkjet head, a filter, and a piezo-type inkjet head, and heat insulation and heating were performed from the ink supply tank to the inkjet head portion. Temperature sensors were provided near the ink supply tank and the nozzles of the inkjet head, respectively, and temperature control was performed so that the nozzle portions were always 40 ° C. ± 2 ° C. The piezo-type inkjet head was driven so that 8 to 30 pl multi-size dots could be ejected at a resolution of 720 × 720 dpi. After landing, UV-A light is condensed to an exposure surface illuminance of 100 mW / cm 2 , and the exposure system, main scanning speed and ejection frequency are adjusted so that irradiation starts 0.1 seconds after ink landing on the recording medium. . Further, the exposure time was variable, and exposure energy was irradiated. In the present invention, dpi represents the number of dots per 2.54 cm.
上記調製した各色インクを用い、環境温度２５℃にて、ブラック→シアン→マゼンタ→イエローの順に射出、１色毎に紫外線を照射した。触診で粘着性が無くなる様、完全に硬化するエネルギーとして、１色あたりのトータル露光エネルギーが一律３００ｍＪ／ｃｍ2で露光した。被記録媒体としては、砂目立てしたアルミニウム支持体、印刷適性を持たせた表面処理済みの透明二軸延伸ポリプロピレンフィルム、軟質塩化ビニルシート、キャストコート紙、市販の再生紙に各カラー画像を記録したところ、いずれもドットの滲みの無い高解像度の画像が得られた。更に、上質紙においてもインクが裏周りすることなく、十分にインクが硬化し、未反応モノマーによる臭気が殆どしなかった。また、フィルムに記録したインクには十分な可とう性があり、折り曲げてもインクにクラックが入ることは無く、セロハンテープ剥離による密着性テストにおいても問題無かった。 Each color ink prepared above was ejected in the order of black → cyan → magenta → yellow at an ambient temperature of 25 ° C. and irradiated with ultraviolet rays for each color. In order to eliminate tackiness by palpation, the exposure was performed with a total exposure energy per color of 300 mJ / cm 2 as the energy for complete curing. As recording media, each color image was recorded on a grained aluminum support, a transparent biaxially stretched polypropylene film having a printability, a soft vinyl chloride sheet, cast coated paper, and commercially available recycled paper. However, in both cases, a high-resolution image without dot bleeding was obtained. Furthermore, even on high-quality paper, the ink was sufficiently cured without causing the ink to turn around, and there was almost no odor due to unreacted monomers. Further, the ink recorded on the film had sufficient flexibility, and the ink did not crack even when it was bent, and there was no problem in the adhesion test by cellophane tape peeling.
［実施例２〜８、比較例１及び２］
《インクの調製》
（マゼンタインク２〜１２）
・（ａ）カチオン重合性化合物 ９０重量部
・（ｂ）光酸発生剤 ５重量部
・（ｃ）着色剤（前記マゼンタ顔料分散物１） ５重量部
・（ｄ）２種以上のアミン化合物 それぞれ化合物１種につき０．０３重量部
・必要に応じ増感剤 ０．５重量部
実施例２〜８（マゼンタインク２〜８）、比較例１及び２（マゼンタインク９及び１０）に使用した各成分の化合物は、下記表１に示す。また、使用したアミン化合物のｐＫａ値については、同じく下記表１に示す。
[Examples 2 to 8, Comparative Examples 1 and 2]
<Preparation of ink>
(Magenta ink 2-12)
-(A) 90 parts by weight of a cationic polymerizable compound-(b) 5 parts by weight of a photoacid generator-(c) 5 parts by weight of a colorant (the magenta pigment dispersion 1)-(d) two or more amine compounds, respectively 0.03 part by weight per compound, 0.5 part by weight of sensitizer as required Each of the compounds used in Examples 2 to 8 (magenta inks 2 to 8) and Comparative Examples 1 and 2 (magenta inks 9 and 10) The component compounds are shown in Table 1 below. The pKa value of the amine compound used is also shown in Table 1 below.
なお、下記表１に記載のカチオン重合性化合物、及び、増感剤の詳細は以下の通りである。
カチオン重合性化合物（１）：セロキサイド２０２１（エポキシ：ダイセルＵＣＢ（株）製）／ＯＸＴ−２２１（オキセタン：東亞合成（株）製）＝３５／５５混合物
カチオン重合性化合物（２）：セロキサイド３０００（エポキシ：ダイセルＵＣＢ（株）製）／ＯＸＴ−２１１（オキセタン：東亞合成（株）製）＝５０／４０混合物
カチオン重合性化合物（３）：ビスフェノールＡ−ジグリシジルエーテル／ＯＸＴ−２２１（オキセタン：東亞合成（株）製）＝４０／５０混合物
カチオン重合性化合物（４）：セロキサイド２０２１（エポキシ：ダイセルＵＣＢ（株）製）／ＯＸＴ−１０１（オキセタン：東亞合成（株）製）＝５５／３５混合物
増感剤（５）：９，１０−ジメトキシアントラセン
増感剤（６）：ピレン
なお、比較例２では、オクチルアミン（ｐＫａ値＝７）を添加した。
The details of the cationically polymerizable compounds and sensitizers listed in Table 1 below are as follows.
Cationic polymerizable compound (1): Celoxide 2021 (epoxy: manufactured by Daicel UCB Co., Ltd.) / OXT-221 (Oxetane: manufactured by Toagosei Co., Ltd.) = 35/55 mixture Cationic polymerizable compound (2): Celoxide 3000 ( Epoxy: Daicel UCB Co., Ltd./OXT-211 (Oxetane: Toagosei Co., Ltd.) = 50/40 mixture Cationic polymerizable compound (3): Bisphenol A-diglycidyl ether / OXT-221 (Oxetane: Tojo) Synthetic Co., Ltd.) = 40/50 mixture Cationic polymerizable compound (4): Celoxide 2021 (Epoxy: Daicel UCB Co., Ltd.) / OXT-101 (Oxetane: Toagosei Co., Ltd.) = 55/35 mixture Sensitizer (5): 9,10-dimethoxyanthracene Sensitizer (6): Pyrene In addition, Comparative Example 2 It was added octylamine (pKa value = 7).
（実施例９）
Ｃ．Ｉ．ピグメントレッド５７：１の代わりに、油溶性染料として下記の化合物Ｍ−１（酸化電位＋１．４０Ｖ）を用いた以外は、マゼンタインク１と同様に調製し、マゼンタインク１１とした。
Example 9
C. I. Magenta ink 11 was prepared in the same manner as magenta ink 1 except that the following compound M-1 (oxidation potential +1.40 V) was used as the oil-soluble dye instead of Pigment Red 57: 1.
（実施例１０）
Ｃ．Ｉ．ピグメントレッド５７：１の代わりに、油溶性染料として下記の化合物Ｍ−２（酸化電位＋０．７０Ｖ）を用いた以外は、マゼンタインク１と同様に調製し、マゼンタインク１２とした。
(Example 10)
C. I. Magenta ink 12 was prepared in the same manner as Magenta ink 1 except that the following compound M-2 (oxidation potential +0.70 V) was used as the oil-soluble dye instead of Pigment Red 57: 1.
〔インクジェット画像記録〕（単色画像評価）
以上のようにして調製したマゼンタインク２〜１１を用いて、実施例１に記載の方法と同様にして、マゼンタ画像を作製した。
１．インクジェット画像の評価
次いで、各形成した画像について、下記に記載の方法に準じて、硬化に必要な感度、市販の再生紙における浸透性、砂目立てしたアルミニウム支持体でのインク滲み、密着性、耐刷性、保存安定性の評価を行った。
２．硬化感度の測定
紫外線照射後の画像面において、粘着感の無くなる露光エネルギー量（ｍＪ／ｃｍ2）を硬化感度と定義した。数値が小さいものほど高感度であることを表す。
３．保存安定性の評価
作製したインクを７５％ＲＨ、６０℃で３日保存した後、射出温度でのインク粘度を測定し、インク粘度の増加分を、保存後／保存前の粘度比で表した。粘度が変化せず１．０に近いほうが保存安定性良好であり、１．５を超えると射出時に目詰まりを起こす場合があり好ましくない。
[Inkjet image recording] (single color image evaluation)
Using the magenta inks 2 to 11 prepared as described above, magenta images were produced in the same manner as in the method described in Example 1.
1. Evaluation of Inkjet Image Next, for each formed image, the sensitivity required for curing, penetrability in commercially available recycled paper, ink bleeding on a grained aluminum support, adhesion, and resistance according to the method described below. The printability and storage stability were evaluated.
2. Measurement of Curing Sensitivity The amount of exposure energy (mJ / cm 2 ) that eliminates stickiness on the image surface after UV irradiation was defined as curing sensitivity. The smaller the value, the higher the sensitivity.
3. Evaluation of storage stability After the prepared ink was stored at 75% RH and 60 ° C. for 3 days, the ink viscosity at the injection temperature was measured, and the increase in the ink viscosity was expressed as the viscosity ratio after storage / before storage. . If the viscosity does not change and is close to 1.0, the storage stability is good, and if it exceeds 1.5, clogging may occur at the time of injection, which is not preferable.
４．市販の再生紙に対する浸透性評価
市販の再生紙に対し印字した画像について、下記の基準に従い浸透性の評価を行った。
○：殆ど浸透せず、残留モノマー臭もしない
△：僅かに浸透し、残留モノマー臭も僅かに認められる
×：明らかにインクが裏面側に浸透し、残留モノマー臭も強い
５．砂目立てしたアルミニウム支持体におけるインク滲み評価
砂目立てしたアルミニウム支持体上に印字した画像について、下記の基準に従いインク滲みの評価を行った。
○：隣接するドット間の滲みが無い
△：僅かにドットが滲む
×：ドットが滲み、明らかに画像がぼやける
６．砂目立てしたアルミニウム支持体における密着性の評価
上記作製した印字画像について、全く印字面に傷をつけない試料と、ＪＩＳ Ｋ ５４００に準拠して、印字面上に１ｍｍ間隔で縦、横に１１本の切れ目をいれ、１ｍｍ角の碁盤目を１００個作った試料を作製し、各印字面上にセロハンテープを貼り付け、９０度の角度で素早く剥がし、剥がれずに残った印字画像あるいは碁盤目の状況について、下記の基準に則り評価した。
○：碁盤目テストでも、印字画像の剥がれが全く認められない
△：碁盤目テストでは若干のインク剥がれが認められるが、インク面に傷をつけなければ剥がれは殆ど認められない
×：両条件共に、簡単にセロハンテープでの剥がれが認められる
4). Permeability evaluation with respect to commercially available recycled paper For images printed on commercially available recycled paper, the permeability was evaluated according to the following criteria.
○: Almost no penetration and no residual monomer odor Δ: Slight penetration and slight residual monomer odor X: Clearly the ink penetrates the back side and the residual monomer odor is strong. Evaluation of Ink Bleeding on Grained Aluminum Support An image printed on a grained aluminum support was evaluated for ink bleeding according to the following criteria.
○: No blur between adjacent dots Δ: Slightly blur dots ×: Dot blurs and the image is clearly blurred Evaluation of Adhesiveness on Grained Aluminum Support Samples of the printed image produced above and 11 samples vertically and horizontally at 1 mm intervals on the printed surface in accordance with JIS K 5400 and a sample that does not scratch the printed surface at all. Make 100 samples of 1 mm square grids, paste cellophane tape on each printing surface, quickly peel off at a 90 degree angle, and print images remaining without peeling or grids The situation was evaluated according to the following criteria.
○: No peeling of the printed image is observed even in the cross cut test. Δ: Some peeling of the ink is recognized in the cross cut test, but almost no peeling is observed unless the ink surface is scratched. Easy to peel off with cellophane tape
〔平版印刷版としての評価〕
上記で作製した砂目立てしたアルミニウム支持体上に本発明のインク組成物で印字し、画像形成した。これを平版印刷版として評価した。
ａ．画像の評価
本発明のインク組成物により作製した平版印刷版を、ハイデルＫＯＲ−Ｄ機に掛け、インク〔枚葉用ＶＡＬＵＥＳ−Ｇ紅（大日本インク（株）製）〕と湿し水〔Ｅｃｏｌｉｔｙ２（富士写真フイルム（株）製）〕とを供給して印刷を行った。１００枚印刷後の印刷物を目視で以下の基準により評価した。
○：画像部の白ヌケ、及び、非画像部の汚れのない画像が得られた。
△：画像部に僅かな白ヌケ、及び／又は、非画像部に僅かな汚れが観察された。
×：画像部の白ヌケ、及び／又は、非画像部の汚れが観察され、実用上問題のあるレベルであった。
ｂ．耐刷性の評価
そのまま印刷を継続し、刷了枚数を耐刷性の指標として相対比較した（比較例１を１００とした）。数値が大きいものほど高耐刷であり好ましい。
これらの評価結果を表１に示す。
[Evaluation as a planographic printing plate]
An image was formed by printing with the ink composition of the present invention on the grained aluminum support prepared above. This was evaluated as a lithographic printing plate.
a. Evaluation of Image A lithographic printing plate produced from the ink composition of the present invention was placed on a Heidel KOR-D machine, and ink [VALUES-G Beni for Sheetfed (Dainippon Ink Co., Ltd.)] and fountain solution [Ecolity 2 (Manufactured by Fuji Photo Film Co., Ltd.)]. The printed matter after printing 100 sheets was visually evaluated according to the following criteria.
◯: An image free from white spots in the image area and a non-image area stain was obtained.
Δ: Slight white spots in the image area and / or slight stains in the non-image area were observed.
X: White spots in the image area and / or stains in the non-image area were observed, and there was a problem in practical use.
b. Evaluation of printing durability Printing was continued as it was, and a relative comparison was made by using the number of printed sheets as an index of printing durability (Comparative Example 1 was taken as 100). A larger numerical value is preferable because it has a higher printing durability.
These evaluation results are shown in Table 1.
（実施例１１）
マゼンタインク１を用いて、Integration Technology社製メタルハライドランプVzero085の代わりに、紫外発光ダイオード（ＵＶ−ＬＥＤ）を用いた以外は、実施例１に記載の方法と同様にして、マゼンタ画像を作製した。
本実施例でＵＶ−ＬＥＤは、日亜化学製NCCU033を用いた。前記ＬＥＤは１チップから波長３６５ｎｍの紫外光を出力するものであって、約５００ｍＡの電流を通電することにより、チップから約１００ｍＷの光が発光される。これを７ｍｍ間隔に複数個配列し、被記録媒体（以下、メディアとも言う。）表面で０．３Ｗ／ｃｍ2のパワーが得られる。打滴後露光されるまでの時間、及び露光時間はメディアの搬送速度及びヘッドとＬＥＤの搬送方向の距離により変更可能である。本実施例では着弾後、約０．５秒後に露光される。
メディアとの距離及び搬送速度の設定に応じて、メディア上の露光エネルギーを０．０１〜１５Ｊ／ｃｍ2の間で調整することができる。
その結果、触診で粘着性が無くなる様、完全に硬化するエネルギーとしては、２５０ｍＪ／ｃｍ2であった。被記録媒体としては、砂目立てしたアルミニウム支持体、印刷適性を持たせた表面処理済みの透明二軸延伸ポリプロピレンフィルム、軟質塩化ビニルシート、キャストコート紙、市販の再生紙に各カラー画像を記録したところ、いずれもドットの滲みの無い高解像度の画像が得られた。更に、上質紙においてもインクが裏周りすることなく、十分にインクが硬化し、未反応モノマーによる臭気が殆どしなかった。また、フィルムに記録したインクには十分な可とう性があり、折り曲げてもインクにクラックが入ることは無く、セロテープ（登録商標）剥離による密着性テストにおいても問題無かった。
ピエゾ型インクジェットヘッドＣＡ３（東芝テック社製）を使用し、３０分間連続突出させた後、ノズルの状態を確認したところ、目詰りを生じたノズルはなく問題はなかった。またインクに、ピエゾ型インクジェットヘッドＣＡ３（東芝テック社製）を一部浸し、５０℃にて１週間経時させた後、浸した金属部分の腐食（変色）を調べたところ、変色は見られず、全く問題なかった。
(Example 11)
A magenta image was produced using the magenta ink 1 in the same manner as described in Example 1 except that an ultraviolet light emitting diode (UV-LED) was used instead of the metal halide lamp Vzero085 manufactured by Integration Technology.
In this example, NCCU033 manufactured by Nichia Chemical was used as the UV-LED. The LED outputs ultraviolet light having a wavelength of 365 nm from one chip. When a current of about 500 mA is applied, light of about 100 mW is emitted from the chip. A plurality of these are arranged at intervals of 7 mm, and a power of 0.3 W / cm 2 can be obtained on the surface of a recording medium (hereinafter also referred to as a medium). The exposure time after the droplet ejection and the exposure time can be changed according to the transport speed of the medium and the distance between the head and the LED in the transport direction. In this embodiment, the exposure is performed about 0.5 seconds after landing.
Depending on the setting of the distance to the medium and the conveyance speed, the exposure energy on the medium can be adjusted between 0.01 and 15 J / cm 2 .
As a result, the energy for complete curing was 250 mJ / cm 2 so that the tackiness disappeared by palpation. As recording media, each color image was recorded on a grained aluminum support, a transparent biaxially stretched polypropylene film having a printability, a soft vinyl chloride sheet, cast coated paper, and commercially available recycled paper. However, in both cases, a high-resolution image without dot bleeding was obtained. Furthermore, even on high-quality paper, the ink was sufficiently cured without causing the ink to turn around, and there was almost no odor due to unreacted monomers. Further, the ink recorded on the film had sufficient flexibility, and the ink was not cracked even when it was bent, and there was no problem in the adhesion test by peeling the cello tape (registered trademark).
Using a piezo ink jet head CA3 (manufactured by TOSHIBA TEC Corp.) and continuously projecting for 30 minutes, the state of the nozzles was confirmed. As a result, there was no problem with clogged nozzles. In addition, a part of the piezo ink jet head CA3 (manufactured by TOSHIBA TEC) was immersed in the ink, and after aging for one week at 50 ° C., when the corrosion (discoloration) of the immersed metal part was examined, no discoloration was found. There was no problem at all.
上記結果より、各実施例のインク組成物は、放射線の照射に対して高感度で硬化し、紙への画像形成性においても高画質の画像を形成することができ、保存安定性も良好であった。このように、本発明においては、硬化感度、非浸透性支持体上での滲み抑制と、インクの保存安定性の両立が達成されたことがわかる。
一方、（ｄ）２種以上のアミン化合物を含まない比較例１、２のインク組成物は、保存安定性に問題があり、且つ、再生紙への浸透性、アルミ支持体での滲み、硬化感度のいずれもやや劣ることがわかった。
また、本発明のインク組成物により画像形成した平版印刷版は、高画質の画像形成が可能であり、耐刷性も良好であることがわかった。
From the above results, the ink composition of each example is cured with high sensitivity to radiation irradiation, can form a high-quality image in terms of image formation on paper, and has good storage stability. there were. Thus, in the present invention, it can be seen that both curing sensitivity, suppression of bleeding on a non-permeable support and storage stability of ink have been achieved.
On the other hand, (d) the ink compositions of Comparative Examples 1 and 2, which do not contain two or more amine compounds, have problems in storage stability, and are permeable to recycled paper, bleeding on an aluminum support, and curing. All of the sensitivity was found to be slightly inferior.
Further, it was found that the lithographic printing plate on which an image was formed with the ink composition of the present invention can form a high quality image and has good printing durability.
Claims (12)
（ｂ）放射線の照射により酸を発生する化合物、
（ｃ）着色剤、及び、
（ｄ）２種以上のアミン化合物
を含有することを特徴とする
インク組成物。 (A) a cationically polymerizable compound,
(B) a compound that generates an acid upon irradiation with radiation,
(C) a colorant, and
(D) An ink composition comprising two or more amine compounds.
（ｂ）吐出されたインク組成物に活性放射線を照射してインク組成物を硬化する工程、
を含むインクジェット記録方法であって、
前記インク組成物が請求項１乃至請求項７のいずれか１項に記載のインク組成物である
インクジェット記録方法。 (A) a step of discharging the ink composition onto a recording medium; and (b) a step of irradiating the discharged ink composition with active radiation to cure the ink composition.
An inkjet recording method comprising:
The inkjet recording method, wherein the ink composition is the ink composition according to any one of claims 1 to 7.
（ｂ）吐出されたインク組成物に活性放射線を照射して、前記インク組成物を硬化させることにより、前記インク組成物が硬化してなる疎水性画像を前記親水性支持体上に形成する工程、
を含む平版印刷版の製造方法。 (A) a step of discharging the ink composition according to any one of claims 1 to 7 onto a hydrophilic support; and (b) irradiating the discharged ink composition with actinic radiation, Forming the hydrophobic image formed by curing the ink composition on the hydrophilic support by curing the ink composition;
A method for producing a lithographic printing plate comprising