JP2006151718A - Plugging material for molten metal tapping hole - Google Patents
Plugging material for molten metal tapping hole Download PDFInfo
- Publication number
- JP2006151718A JP2006151718A JP2004342640A JP2004342640A JP2006151718A JP 2006151718 A JP2006151718 A JP 2006151718A JP 2004342640 A JP2004342640 A JP 2004342640A JP 2004342640 A JP2004342640 A JP 2004342640A JP 2006151718 A JP2006151718 A JP 2006151718A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- coal tar
- plugging material
- molten metal
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、溶融金属出湯口用閉塞材に関する。 The present invention relates to a plug for a molten metal outlet.
溶融金属出湯口用閉塞材の特に重要な特性として、出銑孔用の閉塞材を例にすると（１）マッドガンによる高炉出銑口への充填を容易に行うことができる押出性を有し、かつ出銑口開孔時の被掘削性が良好なこと；（２）充填後の閉塞材が短時間で硬化し、出銑時の溶銑及びスラグの摩耗損傷に耐え得ること；（３）使用時の溶銑及びスラグによる化学的侵食に耐え、出銑口径の拡大が小さく、安定した出銑が長時間維持できる耐食性を有すること、が挙げられる。 As a particularly important characteristic of the plugging material for the molten metal pouring gate, taking the plugging material for the pouring hole as an example, (1) having extrudability that can be easily filled into the blast furnace pouring port with a mud gun, And excavability is good when opening the taphole; (2) The plugging material after filling hardens in a short time and can withstand the hot metal and slag wear damage at the time of tapout; (3) Use It is resistant to chemical erosion caused by hot metal and slag at the time, has a small increase in the diameter of the slag and has a corrosion resistance that can maintain a stable slag for a long time.
これらの特性を満たすものとしてバインダーにコールタールを用いた閉塞材が挙げられる。例えば特許文献１には、粒度調整したＺｒＯ２とＣ粉末とを、それぞれ１５〜９０重量部（質量部）と１０〜３５重量部（質量部）との割合で含有せしめ、更に金属粉末を添加してなる高炉出銑口充填材（請求項１）が開示されており、更に、特許文献１の［００２０］段落においては、タールの配合量が外掛で２０〜２０．５重量部（質量部）の比較例及び実施例が例示されている。 An example of a material that satisfies these characteristics is a plugging material that uses coal tar as a binder. For example, Patent Document 1 contains ZrO 2 and C powder whose particle sizes are adjusted in a ratio of 15 to 90 parts by weight (parts by mass) and 10 to 35 parts by weight (parts by mass), respectively, and further adds metal powder. A blast furnace outlet filling material (Claim 1) is disclosed, and in paragraph [0020] of Patent Document 1, the tar content is 20 to 20.5 parts by weight (mass parts). ) Comparative examples and examples are illustrated.
また、特許文献２には、ロー石、カイアナイト、アルミナ、コークス、炭化珪素、窒化珪素鉄及び粘土を主原料とした配合物に結合剤としてタールを用いた高炉出銑口マッドにおいて、前記ロー石の一部又は全部を粒径４５μｍ以下の微細粒とし、その配合量を５〜１５重量％（質量％）としたことを特徴とする高炉出銑口のマッド（請求項１）；及びロー石、カイアナイト、アルミナ、コークス、炭化珪素、窒化珪素鉄及び粘土を主原料とした配合物に結合剤としてタールを用いた高炉出銑口マッドにおいて、カイアナイトが５〜１５重量％（質量％）、粘土が５重量％（質量％）以下、前記ロー石が粒径４５μｍ以下の微細粒５〜１５重量％（質量％）と粒径４５μｍ超の粗粒３〜１０重量％（質量％）としたことを特徴とする高炉出銑口のマッド（請求項２）が開示されている。また、特許文献２の［０００４］段落には、タールを外掛で１７〜２２重量％（質量％）添加することが好ましい旨の記載もある。 Patent Document 2 discloses a blast furnace outlet mud using tar as a binder in a blend mainly composed of rholite, kyanite, alumina, coke, silicon carbide, silicon nitride iron and clay. Blast furnace outlet mud characterized in that a part or all of the fine particles are fine particles having a particle size of 45 μm or less, and the blending amount thereof is 5 to 15 wt% (mass%); In a blast furnace outlet mud using tar as a binder in a blend mainly composed of kyanite, alumina, coke, silicon carbide, iron silicon nitride and clay, kyanite is 5 to 15% by weight (mass%), clay Is 5% by weight (mass%) or less, the rholite is 5-15% by weight (mass%) of fine particles having a particle diameter of 45 μm or less, and 3-10% by weight (mass%) of coarse particles having a particle diameter of more than 45 μm. Blast furnace outlet featuring Mad (Claim 2) is disclosed. Further, paragraph [0004] of Patent Document 2 also describes that it is preferable to add 17 to 22% by weight (mass%) of tar as an outer portion.
しかし、結合剤として使用されているコールタール（タール）は、有害物質と言われているベンゾ［ａ］ピレンが約１％程度含まれており、作業環境に問題を生ずることがある。海外では、その使用が禁止されている国も存在している。コールタールに替わるバインダーとしてはフェノール樹脂のようなレジンバインダーあるいは石油系タール等が考えられるが、コールタールを使用した閉塞材と比較すると明らかに耐用が劣っており、更に、価格面でも数倍のコストアップとなっている。 However, coal tar (tar) used as a binder contains about 1% of benzo [a] pyrene, which is said to be a harmful substance, and may cause problems in the working environment. Overseas, there are countries where their use is prohibited. Resin binders such as phenolic resins or petroleum-based tars can be considered as binders to replace coal tar, but the durability is clearly inferior compared to plugging materials using coal tar, and the price is several times higher. Cost is up.
例えば、特許文献３には、慣用のマッド材用耐火物骨材に、焼結材として機能性微粒子状フェノール樹脂を１〜８重量％（質量％）及びＡｌ−Ｓｉ系合金粉末を１〜１２重量％（質量％）または金属Ａｌ粉末及び金属Ｓｉ粉末を合計量で１〜１２重量％（質量％）、及び焼結用バインダーとしてノボラック型フェノール樹脂８〜２０重量％（質量％）添加、配合することを特徴とするマッド材が開示されている。 For example, in Patent Document 3, 1 to 8 wt% (mass%) of functional fine particle phenol resin and 1 to 12 Al—Si alloy powder as a sintered material are added to a conventional refractory aggregate for a mud material. 1% to 12% by weight (mass%) of the total amount of metal Al powder and metal Si powder, and 8-20% by weight (mass%) of novolac type phenolic resin as a binder for sintering A mud material characterized in that is disclosed.
また、特許文献４には、アルミナ、ボーキサイト、スピネル、ロー石、シャモット、炭化珪素、黒鉛、粘土等の耐火性組成物１００重量部（質量部）に対し、結合材としてアントラセンオイル５〜１５重量部（質量部）とホウ酸１〜７重量部（質量部）を添加混練したことを特徴とする出銑孔充填材が開示されている。 Patent Document 4 discloses that anthracene oil is used in an amount of 5 to 15 wt.% As a binder with respect to 100 wt. Parts (mass portion) of a refractory composition such as alumina, bauxite, spinel, rholite, chamotte, silicon carbide, graphite, and clay. A filling hole filling material characterized by adding and kneading a part (mass part) and 1 to 7 parts by weight (mass part) of boric acid is disclosed.
更に、特許文献５には、アルミナ、ロウ石、シャモット、炭化珪素等の耐火物骨材と、コークス、黒鉛等の炭素質原料と、カオリン、ベントナイト等の耐火粘土と、バインダーとを配合した出銑口用マッド材において、このバインダーが、石炭粒子とコールタール中の沸点１００℃〜４５０℃の成分との混合物であることを特徴とする出銑口用マッド材（請求項１）；コールタール中の沸点１００℃〜４５０℃の成分がナフタリン吸収油、タール吸収油、アントラセン油、脱晶アントラセン油、ベンゼン、トルエン、キシレン、フェノール類のうちの１種以上である請求項１記載の出銑口用マッド材（請求項２）を開示している。 Further, Patent Document 5 discloses a combination of a refractory aggregate such as alumina, wax, chamotte and silicon carbide, a carbonaceous raw material such as coke and graphite, a refractory clay such as kaolin and bentonite, and a binder. In the mud material for sheds, the binder is a mixture of coal particles and components having a boiling point of 100 ° C to 450 ° C in coal tar (claim 1); coal tar 2. The output of claim 1, wherein the component having a boiling point of 100 ° C. to 450 ° C. is at least one of naphthalene absorption oil, tar absorption oil, anthracene oil, decrystallized anthracene oil, benzene, toluene, xylene, and phenols. An oral mud material (Claim 2) is disclosed.
特許文献１に記載されたマッド材（閉塞材）は、発煙、悪臭の軽減、早期強度の発現と焼成時間の短縮が図られ、出銑口の充填作業の環境改善と作業時間の短縮等の改善がなされたものであるが、ノボラック型フェノール樹脂を使用した閉塞材は、コールタールを用いた閉塞材に比べて、発煙、悪臭の軽減等の作業環境の改善には効果的であるものの、出銑時間が劣るという問題点がある。また、価格面では、コールタールの３〜５倍程度のものが一般的であり、コールタールと同等の価格のものは開発されていないのが現状である。 The mud material (occlusion material) described in Patent Document 1 is designed to reduce smoke generation, malodor, develop early strength and shorten firing time, improve the environment for filling work at the spout, reduce work time, etc. Although the improvement was made, the plugging material using novolac type phenolic resin is more effective in improving the working environment such as smoke generation and odor reduction compared to the plugging material using coal tar. There is a problem that the spawn time is poor. Also, in terms of price, those that are about 3 to 5 times the cost of coal tar are common, and those that have the same price as coal tar have not been developed.
また、特許文献４に記載された出銑孔充填材（閉塞材）は、有害物質と言われているベンゾ［ａ］ピレン含有量の少ないアントラセンオイルをバインダーとして使用した閉塞材であるが、アントラセンオイルは粘性が低いために、閉塞材に求められる特性としての粘りが不足し、マッドガンによる安定した閉塞が困難になるという問題点がある。 Further, the filling hole filling material (occlusion material) described in Patent Document 4 is an occlusion material using anthracene oil having a low benzo [a] pyrene content, which is said to be a harmful substance, as a binder. Since oil has a low viscosity, there is a problem that the viscosity as a characteristic required for the plugging material is insufficient, and it is difficult to stably block with a mud gun.
更に、特許文献５に記載された出銑口用マッド材（閉塞材）は、バインダーとして石炭粒子とコールタール中の沸点１００℃〜４５０℃の成分との混合物を使用するものであり、この閉塞材は、早強性及び耐食性（高温強度）に優れ、しかも焼き付きを起こすことなく、安価で熱的安定性の良好な閉塞材を提供できるものであるが、有害物質成分や環境問題については考慮されていない。 Further, the tap mud material (blocking material) described in Patent Document 5 uses a mixture of coal particles and a component having a boiling point of 100 ° C. to 450 ° C. in coal tar as a binder. The material is excellent in early strength and corrosion resistance (high-temperature strength), and can provide a low-cost and good thermal stability closure material without causing seizure. It has not been.
従って、本発明の目的は、有害物質の少ないバインダーを使用することで作業環境を改善することができ、且つ従来のバインダーを使用した閉塞材よりも優れた耐用性を有する溶融金属出湯口用閉塞材を提供することにある。 Therefore, the object of the present invention is to improve the working environment by using a binder with less harmful substances, and to have a better durability than a plugging material using a conventional binder. To provide materials.
即ち、本発明の溶融金属出湯口用閉塞材は、ロー石、アルミナ、炭化珪素、窒化珪素、コークス及び粘土質原料からなる群から選択される２種または３種以上の耐火性原料１００質量部に対して、ベンゾ［ａ］ピレン含有量が０．０５質量％以下で、且つフリーフェノール含有量が０．５質量％以下である成分調整コールタールをバインダーとして外掛で１０〜２０質量％配合してなることを特徴とする。 That is, the closing material for the molten metal tap of the present invention is 100 parts by mass of two or more refractory raw materials selected from the group consisting of rholite, alumina, silicon carbide, silicon nitride, coke and clayey raw materials. In contrast, a component-adjusted coal tar having a benzo [a] pyrene content of 0.05% by mass or less and a free phenol content of 0.5% by mass or less is blended as an external component in an amount of 10 to 20% by mass. It is characterized by.
本発明の溶融金属出湯口用閉塞材によれば、バインダーとしてベンゾ［ａ］ピレン含有量が０．０５質量％以下で、且つフリーフェノール含有量が０．５質量％以下である成分調整コールタールを使用することにより、従来のコールタールをバインダーとする閉塞材よりも優れた耐用性を提供できると共に、コールタールに起因する環境問題を解決することができるという効果を奏するものである。 According to the plugging material for a molten metal outlet of the present invention, the component-adjusted coal tar having a benzo [a] pyrene content of 0.05% by mass or less and a free phenol content of 0.5% by mass or less as a binder. By using this, it is possible to provide durability that is superior to that of a conventional sealing material using coal tar as a binder and to solve the environmental problems caused by coal tar.
溶融金属出湯口用閉塞材は、一般にコールタールをバインダーとして耐火骨材に外掛で２０重量％程度添加、配合されているが、通常のコールタールには、有害物質と言われているベンゾ［ａ］ピレンが約１質量％程度含まれており、作業環境に影響を及ぼす恐れがあることは前述の通りである。また、コールタール代替のバインダーでは、充分な耐用性を得ることはできない。そこで、コールタールを起源としてベンゾ［ａ］ピレンの含有量を削減したバインダーを使用し、その他の特性を保持させることが有効であると考えられる。 The molten metal outlet plugging material is generally added and blended to the refractory aggregate with coal tar as a binder and about 20% by weight. However, benzo [a As described above, pyrene is contained in an amount of about 1% by mass and may affect the working environment. In addition, with a binder replacing coal tar, sufficient durability cannot be obtained. Therefore, it is considered effective to use a binder having a reduced content of benzo [a] pyrene originating from coal tar to maintain other characteristics.
そこで、本発明の溶融金属出湯口用閉塞材では、ベンゾ［ａ］ピレン含有量が０．０５質量％以下と通常のコールタールの５／１００以下であり、且つフリーフェノール含有量が０．５質量％以下である成分調整コールタールをバインダーとして使用するものである。なお、ベンゾ［ａ］ピレンは上述の通り有害物質と言われている成分であり、その含有量は少なければ少ない程好ましい。 Accordingly, in the plugging material for a molten metal tap according to the present invention, the benzo [a] pyrene content is 0.05% by mass or less, 5/100 or less of normal coal tar, and the free phenol content is 0.5%. The component-adjusted coal tar having a mass% or less is used as a binder. Benzo [a] pyrene is a component that is said to be a harmful substance as described above, and its content is preferably as small as possible.
なお、レジンバインダーとして使用されるノボラック型フェノール樹脂には、通常約１質量％程度のフリーフェノールが含まれているが、このフリーフェノールも有害物質と言われている成分であり、その含有量は少ない程好ましく、本発明に使用する成分調整コールタールでは、フリーフェノールの含有量は０．５質量％以下であることが好ましい。 In addition, the novolak type phenol resin used as the resin binder usually contains about 1% by mass of free phenol. This free phenol is also a component that is said to be a harmful substance, and its content is The smaller the content, the better. In the component-adjusted coal tar used in the present invention, the content of free phenol is preferably 0.5% by mass or less.
上述のようなベンゾ［ａ］ピレン含有量が０．０５質量％以下で、且つフリーフェノール含有量が０．５質量％以下の成分調整コールタールとしては、例えばRUTGERS社製CARBORES T60、CARBORES T170等を使用することができる。成分調整コールタールの添加量は、後述の耐火性原料１００質量部に対して外掛で１０〜２０質量％、好ましくは１０〜１５質量％の範囲内である。成分調整コールタールの添加量が１０質量％未満であると、バインダーとしての結合性及び充填時のスベリ性を維持することが困難となるために好ましくない。また、成分調整コールタールの添加量が２０質量％を超えると、揮発成分が増大し、加熱後の気孔率が高く、耐用性の低下を招くために好ましくない。なお、成分調整コールタールといえどもベンゾ［ａ］ピレンやフリーフェノールを全く含まないものではなく、例えばベンゾ［ａ］ピレンを０．０５質量％以下程度、フリーフェノールを０．５質量％以下程度の量で含有するために、ベンゾ［ａ］ピレン並びにフリーフェノールの量を極力抑えるためにも、成分調整コールタールの添加量は、上記範囲内で必要最低限とすることが好ましい。 Examples of the component-adjusted coal tar having a benzo [a] pyrene content of 0.05% by mass or less and a free phenol content of 0.5% by mass or less as described above include CARBORES T60 and CARBORES T170 manufactured by RUTGERS. Can be used. The amount of the component-adjusted coal tar is 10 to 20% by mass, preferably 10 to 15% by mass, based on 100 parts by mass of the refractory raw material described later. When the amount of the component-adjusted coal tar is less than 10% by mass, it is not preferable because it becomes difficult to maintain the binding property as a binder and the smoothness during filling. Moreover, when the addition amount of a component adjustment coal tar exceeds 20 mass%, a volatile component will increase, the porosity after a heating will be high, and it will lead to a fall of durability, and is unpreferable. The component-adjusted coal tar does not contain benzo [a] pyrene or free phenol at all. For example, benzo [a] pyrene is about 0.05% by mass or less, and free phenol is about 0.5% by mass or less. Therefore, in order to suppress the amounts of benzo [a] pyrene and free phenol as much as possible, the amount of the component-adjusted coal tar is preferably set to the minimum necessary within the above range.
本発明の溶融金属出湯口用閉塞材に使用される耐火性原料は、特に限定されるものではなく、慣用、公知の材質を使用することができ、例えばロー石、アルミナ、炭化珪素、窒化珪素、コークス、粘土質原料等を例示することができる。これらの耐火性原料は、２種または３種以上を併用することができる。 The refractory raw material used for the closing material for the molten metal outlet of the present invention is not particularly limited, and conventional and known materials can be used, for example, rholite, alumina, silicon carbide, silicon nitride Coke, clayey raw materials and the like can be exemplified. These refractory raw materials can be used in combination of two or more.
以下に実施例及び比較例を挙げて本発明の溶融金属出湯口用閉塞材を更に説明する。
表１に示す配合割合で耐火性原料の配合物を作成し、得られた配合物を約５分間混練し、６０℃に保温したバインダーを添加して約１時間混練した。バインダーの添加量は、押し出し抵抗測定（マーシャル試験）による総荷重が約３５０ｋｇｆとなるように調整した。
この押し出し抵抗圧力は、図１に示す形状のステンレン製試料ホルダー（Ｌ１＝９ｃｍ、Ｌ２＝６ｃｍ、Ｌ３＝２６ｃｍ、Ｌ４＝１２ｃｍ、Ｌ５＝２ｃｍ）に、６０℃で保温した練り土を充填し、図２に示す試料押し出し用面板（Ａ）、試料ホルダー（Ｂ）、台座（Ｃ）及びシリンダーヘッド（Ｄ）から構成される測定装置を用いて、シリンダーヘッド（Ｄ）の押し出し速度を１０ｍｍ／秒とした時の押し出し抵抗を試料押し出し用面板（Ａ）に掛かる総荷重として測定したものである。
また、保形性は、ＪＩＳ Ｋ２５２４に規定されている針入度試験機を使用し、図３に記載する形状及び寸法を有する針が５秒間に侵入する長さを測定したものである。保形性は稠度測定により７０（１／１０ｍｍ）以下となるように調整した。
そして、約５ＭＰａの成形圧で４０×４０×１６０ｍｍに成形し、１３５０℃で３時間にわたり還元加熱後の供試体について曲げ強さ及び見掛気孔率の測定を行った。
Hereinafter, the plugging material for the molten metal tap according to the present invention will be further described with reference to examples and comparative examples.
Formulations of refractory raw materials were prepared at the blending ratios shown in Table 1, and the resulting blends were kneaded for about 5 minutes, and a binder kept at 60 ° C. was added and kneaded for about 1 hour. The addition amount of the binder was adjusted so that the total load by the extrusion resistance measurement (Marshall test) was about 350 kgf.
This extrusion resistance pressure is filled with a clay sample held at 60 ° C. in a stainless steel sample holder (L1 = 9 cm, L2 = 6 cm, L3 = 26 cm, L4 = 12 cm, L5 = 2 cm) having the shape shown in FIG. The extrusion speed of the cylinder head (D) is set to 10 mm / second using a measuring device composed of the sample extrusion face plate (A), sample holder (B), pedestal (C) and cylinder head (D) shown in FIG. The extruding resistance is measured as the total load applied to the sample extruding face plate (A).
Further, the shape retention property is obtained by measuring the length of penetration of a needle having the shape and dimensions shown in FIG. 3 in 5 seconds using a penetration tester defined in JIS K2524. The shape retention was adjusted to 70 (1/10 mm) or less by measuring the consistency.
And it shape | molded to 40x40x160mm with the shaping | molding pressure of about 5 MPa, and measured the bending strength and the apparent porosity about the test piece after reduction heating at 1350 degreeC for 3 hours.
表１において、成分調整コールタールは、ベンゾ［ａ］ピレン含有量０．０３質量％及びフリーフェノール含有量０．１質量％品である。また、無水コールタールは、ベンゾ［ａ］ピレン含有量１質量％及びフリーフェノール含有量０．１質量％品である。更に、ノボラック型フェノール樹脂は、フリーフェノール含有量６質量％品である。 In Table 1, the component-adjusted coal tar is a product having a benzo [a] pyrene content of 0.03% by mass and a free phenol content of 0.1% by mass. The anhydrous coal tar is a product having a benzo [a] pyrene content of 1% by mass and a free phenol content of 0.1% by mass. Furthermore, the novolac type phenol resin has a free phenol content of 6% by mass.
また、表１において、曲げ強さは、成形圧５ＭＰａで４０×４０×１６０ｍｍに成形し、８００℃で３時間または１５００℃で３時間還元焼成することによって得た供試体について測定した値である。
更に、耐食性試験は、回転アーク炉侵食試験法により、銑鉄と高炉スラグを侵食剤として使用し、還元雰囲気、１５５０℃で１０時間にわたり試験を行った後、供試体を切断し、侵食寸法を測定し、比較品１の侵食寸法を１００とした時の侵食寸法を指数化して溶損指数としたものである。溶損指数は小さい程、耐食性が良いことを示す。
Further, in Table 1, the bending strength is a value measured for a specimen obtained by molding to 40 × 40 × 160 mm at a molding pressure of 5 MPa and reducing and firing at 800 ° C. for 3 hours or 1500 ° C. for 3 hours. .
Furthermore, the corrosion resistance test was conducted using a rotating arc furnace erosion test method using pig iron and blast furnace slag as an erodant, tested in a reducing atmosphere at 1550 ° C for 10 hours, then cutting the specimen and measuring the erosion dimensions. The erosion dimension when the erosion dimension of the comparative product 1 is 100 is indexed to obtain a erosion index. The smaller the melting index, the better the corrosion resistance.
バインダーの添加量は、本発明品と比較品１ではほぼ同じ量を必要とした。また、本発明品は比較品１と比較して曲げ強さで８００℃加熱後で同等、１５００℃加熱後では高い結果を得た。また、見掛気孔率は、本発明品では比較品１よりも低い値を示した。更に、耐食性試験における溶損指数も本発明品は比較品１より小さい値を示しており、成分調整コールタールは、無水コールタールと比較して耐用性に優れていることが判る。
比較品２、比較品３は、本発明品及び比較品１に比べ曲げ強さが極めて低く、見掛気孔率も高い値を示した。このことにより、石油系タールあるいはノボラック型フェノール樹脂のようなバインダーは、ベンゾ［ａ］ピレンのような有害物質と言われている成分は含まれないものの成分調整コールタールや無水コールタールと同等の耐用性を得ることはできなかった。
上記結果から、成分調整コールタールは、無水コールタールのような従来使用されているバインダーよりも有効であることが判る。
The amount of binder added was almost the same for the product of the present invention and the comparative product 1. Further, the product of the present invention had a bending strength equivalent to that after heating at 800 ° C. and higher results after heating at 1500 ° C. than the comparative product 1. The apparent porosity of the product of the present invention was lower than that of Comparative Product 1. Further, the melt loss index in the corrosion resistance test shows that the product of the present invention has a value smaller than that of the comparative product 1, and it can be seen that the component-adjusted coal tar is superior in durability compared to anhydrous coal tar.
The comparative product 2 and the comparative product 3 had extremely low bending strength and a high apparent porosity as compared with the product of the present invention and the comparative product 1. As a result, binders such as petroleum-based tars or novolak-type phenol resins do not contain components that are said to be harmful substances such as benzo [a] pyrene, but are equivalent to component-adjusted coal tar and anhydrous coal tar. The service life could not be obtained.
From the above results, it can be seen that component-adjusted coal tar is more effective than conventionally used binders such as anhydrous coal tar.
本発明の溶融金属出湯口用閉塞材は、出銑口等の閉塞材として好適に使用できるものである。 The plugging material for the molten metal outlet of the present invention can be suitably used as a plugging material such as a tap.
Ａ 試料押し出し用面板
Ｂ 試料ホルダー
Ｃ 台座
Ｄ シリンダーヘッド
A Sample faceplate B Sample holder C Base D Cylinder head
Claims (1)