JP2006129712A - Lowly insect-attracting sheet - Google Patents
Lowly insect-attracting sheet Download PDFInfo
- Publication number
- JP2006129712A JP2006129712A JP2004318935A JP2004318935A JP2006129712A JP 2006129712 A JP2006129712 A JP 2006129712A JP 2004318935 A JP2004318935 A JP 2004318935A JP 2004318935 A JP2004318935 A JP 2004318935A JP 2006129712 A JP2006129712 A JP 2006129712A
- Authority
- JP
- Japan
- Prior art keywords
- light
- light transmittance
- sheet
- maximum absorption
- wavelength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明はシートに関し、詳しくは光源を覆うことにより、この光源に昆虫類が群がることを防止できる低誘虫性のシートに関する。 The present invention relates to a sheet, and more particularly to a sheet having a low susceptibility that can prevent insects from gathering in the light source by covering the light source.
昆虫類には、紫外光に向かって進む走光性があるため、夜間には、かかる波長の光を放射する光源、例えば白色蛍光灯などに誘引されて群がってくる。 Insects have the ability to travel toward ultraviolet light, so they gather at night by being attracted by a light source that emits light of this wavelength, such as a white fluorescent lamp.
光源に昆虫類が誘引されることを防ぐために、昆虫類が最も敏感に反応する波長の光を遮蔽し、これ以外の光、例えば可視光のほとんどは透過する低誘虫性のシートが提案されている。例えば特許文献1〔特開昭55−023921号公報〕には、光線透過率が波長300〜380nmで1%以下、波長420〜700nmで80%以上であるシートが提案されている。同文献で具体的に提案されているシートは、波長400〜410nmの光線透過率が40%〜70%であり、波長420〜700nmに吸収極大ピークがないので(特許文献1の第8頁の第1図)、人間の目には殆ど無色に見え、これを透して見える光源からの光は、自然な色調に見える。
In order to prevent insects from being attracted to the light source, a low-attractive sheet has been proposed that shields light of the wavelength to which insects react most sensitively and transmits most other light, for example, visible light. Yes. For example, Patent Document 1 (JP 55-023921 A) proposes a sheet having a light transmittance of 1% or less at a wavelength of 300 to 380 nm and 80% or more at a wavelength of 420 to 700 nm. The sheet specifically proposed in this document has a light transmittance of 40% to 70% at a wavelength of 400 to 410 nm and no absorption maximum peak at a wavelength of 420 to 700 nm (see
しかし、同文献に具体的に開示されているシートは、波長400〜410nmで40%〜70%もの光線透過率であるため、かかる波長範囲の光にも反応する昆虫類が群がってくるという問題があった。 However, since the sheet disclosed specifically in the same document has a light transmittance of 40% to 70% at a wavelength of 400 to 410 nm, there is a problem that insects that react to light in this wavelength range gather. was there.
かかる問題を解決するものとしては、特許文献2〔特開昭62−278931号公報〕には、波長300〜380nmの光線透過率が1%以下であり、波長400〜480nmの光線透過率が30%以下であり、波長580〜700nmの光線透過率が80%以上であるシートが提案されており、具体的には波長580〜700nmに吸収極大ピークが見られないものが開示されている〔特許文献2の第9頁の第3図〕。かかるシートは、400〜410nmの光線透過率が30%以下であるので、かかる波長範囲の光にも反応する昆虫類が誘引されて群がってくるのを防止することができる。 In order to solve this problem, Patent Document 2 (Japanese Patent Laid-Open No. Sho 62-278931) discloses that the light transmittance at a wavelength of 300 to 380 nm is 1% or less and the light transmittance at a wavelength of 400 to 480 nm is 30%. %, And a light transmittance of a wavelength of 580 to 700 nm is proposed to be 80% or more. Specifically, a sheet having no absorption maximum peak at a wavelength of 580 to 700 nm is disclosed [Patents] FIG. 3 on page 9 of document 2]. Since such a sheet has a light transmittance of 400 to 410 nm of 30% or less, it is possible to prevent insects that also react to light in this wavelength range from being attracted and gathered.
しかし、同文献で具体的に提案されているシートは、人間の目には着色して見え、これを透過してくる光源からの光が不自然な色調に見えてしまうという問題があった。 However, the sheet specifically proposed in this document has a problem in that it appears colored to human eyes, and light from a light source that passes through the sheet looks unnatural.
また、低誘虫性のシートとして、光源を覆う照明カバーなどのように、光を拡散させながら透過させる拡散透過性を有するものも求められている。 In addition, a sheet having low diffusion property that allows light to pass through while diffusing, such as an illumination cover that covers a light source, is also demanded as a low-attractive sheet.
そこで本発明者は、光源を覆うことで、この光源に昆虫類が群がることを防止でき、人間の目には着色していない自然な色調に見え、光源からの光を拡散透過させうるシートを開発するべく鋭意検討した結果、ヘイズが95%以上であり、波長300〜410nmでの光線吸収率を1%以下で、波長450nm〜800nmの光線透過率が40%〜70%であり、この波長範囲に極大吸収波長530〜620nmの吸収極大ピークが有り、この極大吸収波長における光線透過率が、波長450nm〜700nmにおける最大光線透過率の0.86倍以下のシートは、透過光を拡散透過し、昆虫類が群がってくることが無く、また人間の目には殆ど着色していないように見えることを見出し、本発明に至った。 Therefore, the present inventor can prevent insects from gathering in the light source by covering the light source, a sheet that looks natural tones that are not colored to the human eye, and can diffuse and transmit light from the light source. As a result of intensive studies to develop, the haze is 95% or more, the light absorptivity at a wavelength of 300 to 410 nm is 1% or less, and the light transmittance at a wavelength of 450 nm to 800 nm is 40% to 70%. A sheet having an absorption maximum peak with a maximum absorption wavelength of 530 to 620 nm in the range, and a light transmittance at this maximum absorption wavelength of 0.86 times or less of the maximum light transmittance at a wavelength of 450 nm to 700 nm diffuses and transmits the transmitted light. The present inventors have found that insects do not gather and appear to be hardly colored by human eyes.
すなわち本発明は、ヘイズが95%以上であり、
300nm〜410nmの波長範囲(A)で光線透過率(TA)が1%以下であり、
450nm〜800nmの波長範囲(B)で光線透過率(TB)が40%〜70%であり
、
極大吸収波長(λP)が530nm〜620nmである吸収極大ピーク(P)を有し、
前記極大吸収波長(λP)における光線透過率(TP)が、450nm〜700nmの波長範囲(B)における最大光線透過率(TBmax)の0.86倍以下である
ことを特徴とするシートを提供するものである。図1に本発明のシートの一例の光線透過スペクトルを示す。
That is, the present invention has a haze of 95% or more,
Light transmittance in the wavelength range 300nm~410nm (A) (T A) is 1% or less,
In the wavelength range (B) of 450 nm to 800 nm, the light transmittance (T B ) is 40% to 70%,
An absorption maximum peak (P) having a maximum absorption wavelength (λ P ) of 530 nm to 620 nm;
A sheet having a light transmittance (T P ) at the maximum absorption wavelength (λ P ) of 0.86 times or less of a maximum light transmittance (T Bmax ) in a wavelength range (B) of 450 nm to 700 nm. Is to provide. FIG. 1 shows a light transmission spectrum of an example of the sheet of the present invention.
本発明のシートによれば、光源に昆虫類が群がることを防止でき、また、このシートは人間の目には着色していない自然な色調に見える。 According to the sheet of the present invention, insects can be prevented from flocking to the light source, and the sheet looks natural tones that are not colored by human eyes.
本発明のシートは、300nm〜410nmの波長範囲(A)で光線透過率が1%以下であり、理想的には実質的に0である。本発明のシートは、かかる波長範囲(A)での光線透過率(TA)が1%以下であるので、昆虫類が反応する波長範囲(A)の光は十分に遮蔽されている。 The sheet of the present invention has a light transmittance of 1% or less in the wavelength range (A) of 300 nm to 410 nm, and ideally substantially zero. Sheet of the present invention, since the light transmittance at such wavelength range (A) (T A) is less than 1%, the light of wavelength insects reacts range (A) is well shielded.
450nm〜800nmの波長範囲(B)では、光線透過率(TB)が40%〜70%である。かかる光線透過率(TB)が40%未満であると、例えば光源を覆った場合などに十分に可視光を透過することができず、人間の目には暗く見えてしまう傾向にある。 In the wavelength range (B) of 450 nm to 800 nm, the light transmittance (T B ) is 40% to 70%. When the light transmittance (T B ) is less than 40%, for example, when the light source is covered, the visible light cannot be sufficiently transmitted, and the human eye tends to appear dark.
本発明のシートは、吸収極大ピーク(P)を有しており、この吸収極大ピーク(P)は最大吸収波長(λP)が530nm〜620nmである。最大吸収波長(λP)が530nm未満であったり、620nmを超えていると、人間の目には着色して見えることがある。 The sheet of the present invention has an absorption maximum peak (P), and this absorption maximum peak (P) has a maximum absorption wavelength (λ P ) of 530 nm to 620 nm. If the maximum absorption wavelength (λ P ) is less than 530 nm or exceeds 620 nm, it may appear colored to human eyes.
吸収極大ピーク(P)の最大吸収波長(λp)における光線透過率(Tp)は、450nm〜800nmの波長範囲(B)における最大光線透過率(TBmax)の0.86倍以下である。かかる光線透過率(TP)が最大光線透過率(TBmax)の0.86倍を超えていると、人間の目には着色して見えてしまう傾向にあり、好ましくない。なお、450nm〜800nmの波長範囲(B)における光線透過率(TB)は40%〜70%の範囲であるので、極大吸収ピーク(P)の最大吸収波長(λp)における光線透過率(Tp)は、最大光線透過率(TBmax)の0.57倍以上である。 The light transmittance (T p ) at the maximum absorption wavelength (λ p ) of the absorption maximum peak (P) is 0.86 times or less of the maximum light transmittance (T Bmax ) in the wavelength range (B) of 450 nm to 800 nm. . If the light transmittance (T P ) exceeds 0.86 times the maximum light transmittance (T Bmax ), it tends to be colored and seen by human eyes, which is not preferable. Incidentally, the light transmittance in the wavelength range of 450nm~800nm (B) (T B) is so in the range of 40% to 70%, the light transmittance at the maximum absorption wavelength (lambda p) of the maximum absorption peak (P) ( T p ) is 0.57 times or more of the maximum light transmittance (T Bmax ).
かかる本発明のシートとしては、例えば透明樹脂に紫外線吸収剤、着色剤および光拡散剤を含有させた樹脂組成物からなるシートが挙げられる。 Examples of the sheet of the present invention include a sheet made of a resin composition in which a transparent resin contains an ultraviolet absorber, a colorant, and a light diffusing agent.
透明樹脂としては、例えばアクリル樹脂が挙げられる。アクリル樹脂はそれ単独では無色で透明な熱可塑性樹脂として広く用いられているものである。かかるアクリル樹脂としては、例えばメタクリル酸メチル単位の含有量が50質量%以上の重合体が挙げられ、メタクリル酸メチルの単独重合体であってもよいし、メタクリル酸メチルおよびこれと共重合可能な単量体の共重合体であってもよい。 An example of the transparent resin is an acrylic resin. An acrylic resin is widely used as a colorless and transparent thermoplastic resin by itself. Examples of the acrylic resin include a polymer having a methyl methacrylate unit content of 50% by mass or more, and may be a homopolymer of methyl methacrylate, or methyl methacrylate and copolymerizable therewith. A monomer copolymer may also be used.
メタクリル酸メチルと共重合可能な単量体は、分子内にメタクリル酸メチルとラジカル重合可能な二重結合を一つ有する単官能単量体であってもよいし、二つ以上有する多官能単量体であってもよい。単官能単量体としては、例えばアクリル酸メチル、アクリル酸ブチル、アクリル酸2−エチルヘキシル、アクリル酸シクロヘキシルなどのアクリル酸エステル類、メタクリル酸エチル、メタクリル酸2−エチルヘキシル、メタクリル酸シクロヘキシルなどのようなメタクリル酸エステル類、アクリル酸、メタクリル酸、スチレンなどが挙げられる。また、多官能単量体としては、例えばネオペンチルグリコールジメタクリレート、エチレングリコールジメタクリレート、テトラエチレングリコールジメタクリレート、トリメチロールプロパントリメタクリレートなどが挙げられる。これらの単量体は、それぞれ単独で、または2種以上を組み合わせて用いることができる。 The monomer copolymerizable with methyl methacrylate may be a monofunctional monomer having one double bond capable of radical polymerization with methyl methacrylate in the molecule, or a polyfunctional monomer having two or more. It may be a mer. Monofunctional monomers include, for example, acrylic esters such as methyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, cyclohexyl acrylate, ethyl methacrylate, 2-ethylhexyl methacrylate, cyclohexyl methacrylate, and the like. Examples include methacrylic acid esters, acrylic acid, methacrylic acid, and styrene. Examples of the polyfunctional monomer include neopentyl glycol dimethacrylate, ethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, and trimethylolpropane trimethacrylate. These monomers can be used alone or in combination of two or more.
紫外線吸収剤としては、例えば最大吸収波長(λUVmax)が350nm〜370nmである紫外線吸収剤が用いられる。最大吸収波長(λUVmax)が350nm未満の紫外線吸収剤を用いたのでは、410nm以下の光線透過率(TA)を1%以下とするために多量に含有させる必要があり、経済的に不利である。また、370nmを超える紫外線吸収剤であってもよいが、その多くは、波長450nm以上にも吸収があるので、後述する着色剤の使用量が多くなり、シートが黒っぽく見えてしまうため、好ましくない。
As the ultraviolet absorber, for example, an ultraviolet absorber having a maximum absorption wavelength (λ UVmax ) of 350 nm to 370 nm is used. When an ultraviolet absorber having a maximum absorption wavelength (λ UVmax ) of less than 350 nm is used, it is necessary to contain a large amount in order to make the light transmittance (T A ) of 410 nm or less 1% or less, which is economically disadvantageous. It is. Moreover, although the ultraviolet absorber exceeding 370 nm may be sufficient, since many of them also absorb at
最大吸収波長(λUVmax)が350nm〜370nmである紫外線吸収剤としては、例えば2−〔5−クロロ(2H)−ベンゾトリアゾール−2−イル〕−4−メチル−6−(tert−ブチル)フェノール〔最大吸収波長λUVmax=353nm〕、2、4−ジ−tert−ブチル−6−(5−クロロベンゾトリアゾール−2−イル)フェノール〔最大吸収波長λUVmax=353nm〕などが挙げられる。かかる紫外線吸収剤の含有量は、紫外線吸収剤の種類にもよるが、例えばシートの単位面積あたり10g/m2〜100g/m2程度である。 Examples of the ultraviolet absorber having a maximum absorption wavelength (λ UVmax ) of 350 nm to 370 nm include 2- [5-chloro (2H) -benzotriazol-2-yl] -4-methyl-6- (tert-butyl) phenol. [Maximum absorption wavelength λ UVmax = 353 nm], 2,4-di-tert-butyl-6- (5-chlorobenzotriazol-2-yl) phenol [maximum absorption wavelength λ UVmax = 353 nm] and the like. The content of the ultraviolet absorber, depending on the kind of the ultraviolet absorber, such as 2 to 100 g / m 2 approximately 10 g / m per unit area of the sheet.
着色剤としては、最大吸収波長(λVISmax)が530nm〜620nmである着色剤が用いられ、透過光の散乱が少ない点で、染料が好ましく用いられる。かかる染料としては、例えばC.I.ディスパース バイオレット 26(C.I.Disperse Violet 26)〔最大吸収波長λUVmax=540nm、「Sumiplast Bordeaux HBL」(住友化学社)などとして市販されている。〕、
C.I.ディスパース バイオレット 28(C.I.Disperse Violet 28)〔最大吸収波長λVISmax=約550nm、「Sumiplast Violet RR」(住友化学社)、「Diaresin Violet D」(三菱化学社)などとして市販されている。〕、
C.I.ピグメント バイオレット 1(C.I.Pigment Violet 1)〔最大吸収波長λUVmax=560nm、「Rhodamine B」(サンケミカル社)、「Fanal Violet D5480」(BASF社)などとして市販されている。〕、
C.I.ソルベント バイオレット 13(C.I.Solvent Violet 13)〔最大吸収波長λVISmax=約580nm、「Waxoline Purple AS」(ICI社)、「Sumiplast Violet B」(住友化学社)、「Macrolex Violet B」(Bayer社)などとして市販されている。〕、
C.I.ソルベント ブルー 97(C.I.Solvent Blue 97)〔最大吸収波長λUVmax=580〜610nm、「Macrolex Blue RR」(Bayer社)などとして市販されている。〕などが挙げられる。かかる着色剤の含有量は、その種類によって異なるが、例えばシートの単位面積あたり0.001g/m2〜0.02g/m2程度である。
As the colorant, a colorant having a maximum absorption wavelength (λ VISmax ) of 530 nm to 620 nm is used, and a dye is preferably used in terms of less scattered light. Examples of such dyes include C.I. I. Disperse Violet 26 (maximum absorption wavelength λ UVmax = 540 nm, “Sumiplast Bordeaux HBL” (Sumitomo Chemical Co., Ltd.)) ],
C. I. Disperse Violet 28 (maximum absorption wavelength λ VISmax = approximately 550 nm, “Sumiplast Violet RR” (Sumitomo Chemical Co., Ltd.), “Diaresin Violet D” (Mitsubishi Chemical Co., Ltd.)) ],
C. I. Pigment Violet 1 (maximum absorption wavelength λ UVmax = 560 nm, “Rhodamine B” (Sun Chemical), “Final Violet D5480” (BASF), etc. ],
C. I. Solvent Violet 13 (Maximum absorption wavelength λ VISmax = about 580 nm, “Waxoline Purple AS” (ICI), “Sumiplast Violet B” (Sumitomo Chemical), “Macrolex Violet B” (Bayer), etc. It is commercially available. ],
C. I. Solvent Blue 97 (CISolvent Blue 97) [Maximum absorption wavelength λ UVmax = 580 to 610 nm, “Macrolex Blue RR” (Bayer), etc.] And the like. The content of the colorant may vary depending on the type, such as 0.001g / m 2 ~0.02g / m 2 approximately per unit area of the sheet.
光拡散剤としては、例えば酸化チタン、炭酸カルシウム、水酸化アルミニウム、タルクなどの無機微粒子を用いることができる。光拡散剤として、架橋ポリスチレン粒子、架橋アクリル粒子などの有機微粒子を用いることもできる。透明樹脂に対して非相溶性の樹脂を透明樹脂と溶融混練して用いることもでき、この非相溶性の樹脂は、透明樹脂と相分離することにより、光を拡散させる。 As the light diffusing agent, inorganic fine particles such as titanium oxide, calcium carbonate, aluminum hydroxide, and talc can be used. As the light diffusing agent, organic fine particles such as crosslinked polystyrene particles and crosslinked acrylic particles can also be used. A resin that is incompatible with the transparent resin can be used after being melt-kneaded with the transparent resin, and this incompatible resin diffuses light by phase separation with the transparent resin.
光拡散剤の使用量は、450nm〜800nmの波長範囲(B)で光線透過率(TB)およびヘイズが本発明で規定する範囲となるように適宜選択され、光拡散剤の種類、無機微粒子を用いる場合には、その粒子径などにより異なるが、例えばシートの単位面積あたりの含有量で5g/m2〜500g/m2程度である。光拡散剤の使用量が多いと、上記波長範囲(B)での光線透過率(TB)が低くなり、少ないとヘイズが低くなる。 The amount of the light diffusing agent used is appropriately selected so that the light transmittance (T B ) and the haze are within the range specified in the present invention in the wavelength range (B) of 450 nm to 800 nm. when using a varies due its particle size, such as 2 to 500 g / m 2 about 5 g / m at a content per unit area of the sheet. When the amount of the light diffusing agent used is large, the light transmittance (T B ) in the wavelength range ( B ) is low, and when it is small, the haze is low.
かかる樹脂組成物シートは、例えば加熱されて溶融状態にある透明樹脂に紫外線吸収剤、着色剤および光拡散剤を添加して、成形する方法、具体的には押出成形、射出成形などの通常の成形方法で製造することができる。また、押出成形などの方法でペレット化してから、プレス成形法によって熱プレスしてもよい。 Such a resin composition sheet is formed by adding a UV absorber, a colorant and a light diffusing agent to a transparent resin which is heated and in a molten state, for example, an ordinary method such as extrusion molding or injection molding. It can be manufactured by a molding method. Alternatively, the pellets may be pelletized by a method such as extrusion and then hot pressed by a press molding method.
樹脂組成物シートは、単量体またはその部分重合物と紫外線吸収剤、着色剤および光拡散剤とを混合し、得られた混合物を重合セル内で重合させて成形するキャスト重合法によっても製造することができる。単量体としては、メタクリル酸メチルを単独で用いてもよいし、メタクリル酸メチルおよびこれと共重合可能な単量体の混合物であってもよい。混合物は通常、重合開始剤を含有させて用いられる。また通常は、重合後、重合セルからの離型を容易にするために離型剤が添加されて用いられる。 The resin composition sheet is also produced by a cast polymerization method in which a monomer or a partial polymer thereof is mixed with an ultraviolet absorber, a colorant, and a light diffusing agent, and the resulting mixture is polymerized in a polymerization cell. can do. As the monomer, methyl methacrylate may be used alone, or a mixture of methyl methacrylate and a monomer copolymerizable therewith may be used. The mixture is usually used by containing a polymerization initiator. In general, after polymerization, a release agent is added to facilitate release from the polymerization cell.
樹脂シートは、上記と同様の単量体に紫外線吸収剤、着色剤および光拡散剤を混合してから、懸濁重合法、塊状重合法などの方法で重合して樹脂組成物を得、得られた樹脂組成物を押出成形法、射出成形法などの成形法により成形する方法でも製造することができる。 The resin sheet is obtained by mixing a monomer similar to the above with an ultraviolet absorber, a colorant and a light diffusing agent, and then polymerizing by a method such as a suspension polymerization method or a bulk polymerization method to obtain a resin composition. The obtained resin composition can also be produced by a molding method such as an extrusion molding method or an injection molding method.
かかる本発明のシートは、厚みが通常0.1mm〜30mm程度である。 Such a sheet of the present invention usually has a thickness of about 0.1 mm to 30 mm.
本発明のシートは、光線透過率が300nm〜410nmの波長範囲(A)で1%以下であるので、白色蛍光灯などの光源を覆う照明カバーとして用いることで、光源に昆虫類が群がることを防止することができ、人間の目には着色していないよう見えるので、自然な色調の照明光で照明することができる。 Since the sheet of the present invention has a light transmittance of 1% or less in the wavelength range (A) of 300 nm to 410 nm, it can be used as an illumination cover for covering a light source such as a white fluorescent lamp, so that insects gather in the light source. It can be prevented, and since it does not appear to be colored to human eyes, it can be illuminated with illumination light of a natural color tone.
本発明のシートは、内部に光源を有していて、この内部の光源によって照明する内照式の看板の看板材として用いることで、看板材に描かれた装飾の色彩を損なうことなく、昆虫類が群がることを防止することができる。 The sheet of the present invention has a light source inside, and is used as a signboard material for an internally-illuminated signboard illuminated by this internal light source, so that the color of the decoration drawn on the signboard material is not impaired. It is possible to prevent the class from flocking.
本発明のシートを、家屋などの窓材、出入口の間仕切り板などとして用いることで、屋内の照明によって窓際や出入口などに昆虫類が群がることがなく、また日中は自然な色調で太陽光を屋内に採り入れることができる。 By using the sheet of the present invention as a window material of a house, a partition plate of an entrance, etc., indoor lighting prevents insects from gathering at the windows and entrances, and sunlight is emitted in natural colors during the day. Can be taken indoors.
以下、実施例によって本発明をより詳細に説明するが、本発明はかかる実施例によって限定されるものではない。 EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited by this Example.
なお、各実施例で得たシートの光線透過スペクトルは、分光光度計〔日立U−4000型〕を用いて300nm〜800nmの波長範囲で5nm間隔で測定して求めた。
イエローインデックスは(YI)は、同時測定方式分光方式色度計〔日本電色工業(株)製、「SQ−2000」〕を用いて反射法により、JIS Z−8722に記載の方法により、Cの標準光を用いたときの三刺激値(X、Y、Z)を求め、この三刺激値から、JIS Z7105に従って求めた。
ヘイズは、JIS K7136に従い、反射・透過率計〔(株)村上色彩技術研究所製、「HR−100型」〕を用いて測定した。
In addition, the light transmission spectrum of the sheet | seat obtained in each Example was calculated | required by measuring at 5 nm intervals in the wavelength range of 300 nm-800 nm using the spectrophotometer [Hitachi U-4000 type].
The yellow index (YI) is determined by the reflection method using a simultaneous measurement type spectroscopic colorimeter [manufactured by Nippon Denshoku Industries Co., Ltd., “SQ-2000”], by the method described in JIS Z-8722. The tristimulus values (X, Y, Z) when using the standard light were obtained, and the tristimulus values were obtained according to JIS Z7105.
The haze was measured according to JIS K7136 using a reflection / transmittance meter [manufactured by Murakami Color Research Laboratory, "HR-100 type"].
実施例1
メタクリル酸メチル100質量部あたり2,2’−アゾビスイソブチロニトリル(重合開始剤)0.002質量部を混合し、80℃で部分重合させて、重合体含有量5質量%の部分重合物を得た。この部分重合物98.5質量部に、メタクリル酸メチル−スチレン共重合体樹脂(MS樹脂)〔メタクリル酸メチル単位20質量%、スチレン単位80質量%〕1.49質量部を加え、さらに2−〔5−クロロ(2H)−ベンゾトリアゾール−2−イル〕−4−メチル−6−tert−ブチル〕フェノール(紫外線吸収剤)1.5質量部、着色剤〔C.I.ソルベント バイオレット 13、最大吸収波長λVISmax=約580nm、「Waxoline Purple AS」〕0.0002質量部、酸化チタン微粉末〔光拡散剤〕0.042質量部、2,2’−アゾビスイソブチロニトリル(重合開始剤)0.08質量部および離型剤0.05質量部を添加し、減圧下〔絶対圧力で87kPa〕にて30分間脱気した。その後、ガラス板〔厚さ10mm、30cm×30cm〕2枚とと塩化ビニル製ガスケットで構成された重合セル内に注入し、72℃に加熱して同温度で3時間保持したのち、120℃に加熱し同温度で1時間保持して重合させて、厚さ2mmのアクリル樹脂組成物シートを得た。このアクリル樹脂組成物シートは、目視では着色を確認できなかった。このアクリル樹脂組成物シートの光線透過スペクトルを図1に示し、評価結果を第1表に示す。
Example 1
0.002 parts by mass of 2,2′-azobisisobutyronitrile (polymerization initiator) per 100 parts by mass of methyl methacrylate was mixed and partially polymerized at 80 ° C. to obtain a partial polymerization with a polymer content of 5% by mass. I got a thing. To 98.5 parts by mass of this partially polymerized product, 1.49 parts by mass of methyl methacrylate-styrene copolymer resin (MS resin) [
このアクリル樹脂組成物シートは、単位面積あたり紫外線吸収剤を35.7g/m2、着色剤を0.00476g/m2、光拡散剤を36.5g/m2それぞれ含んでいて、ヘイズは99.4%、YIは−3.1である。300nm〜410nmの波長範囲(A)での光線透過率の最大値(TAmax)は0.1%(410nm)であり、450〜800nmの波長範囲(B)での光線透過率の最小値(TBmin)は42.2%、最大値(TBmax)は53.1%である。極大吸収ピークを有し、その極大吸収波長(λp)は約560nm、極大吸収波長における光線透過率(Tp)は42.2%である。極大吸収波長における光線透過率(Tp)は、最大光線透過率(TBmax)の0.79倍である。 The acrylic resin composition sheet, 35.7 g / m 2 and per unit area ultraviolet absorber, colorant 0.00476g / m 2, include a light diffusing agent 36.5 g / m 2, respectively, haze 99 .4% and YI is -3.1. The maximum value (T Amax ) of the light transmittance in the wavelength range (A) of 300 nm to 410 nm is 0.1% (410 nm), and the minimum value of the light transmittance in the wavelength range (B) of 450 to 800 nm ( T Bmin ) is 42.2%, and the maximum value (T Bmax ) is 53.1%. It has a maximum absorption peak, the maximum absorption wavelength (λ p ) is about 560 nm, and the light transmittance (T p ) at the maximum absorption wavelength is 42.2%. The light transmittance (T p ) at the maximum absorption wavelength is 0.79 times the maximum light transmittance (T Bmax ).
このシートを白色蛍光灯の照明カバーとして使用すると、白色蛍光灯からの光は拡散透過されて自然な乳白色に見え、また屋外で使用しても、昆虫類が群がってこない。 When this sheet is used as an illumination cover for a white fluorescent lamp, the light from the white fluorescent lamp is diffused and transmitted to look natural milky white, and insects do not gather even when used outdoors.
実施例2
部分重合物の使用量を97.5質量部とし、紫外線吸収剤の使用量を1.0質量部とした以外は実施例1と同様に操作して、アクリル樹脂組成物シートを得た。このアクリル樹脂組成物シートは、目視では着色を確認できなかった。このアクリル樹脂組成物シートの光線透過スペクトルを図2に示す。評価結果を第1表に示す。
Example 2
An acrylic resin composition sheet was obtained in the same manner as in Example 1 except that the use amount of the partial polymer was 97.5 parts by mass and the use amount of the ultraviolet absorber was 1.0 part by mass. This acrylic resin composition sheet could not be colored visually. The light transmission spectrum of this acrylic resin composition sheet is shown in FIG. The evaluation results are shown in Table 1.
このアクリル樹脂組成物シートは、単位面積あたり紫外線吸収剤を23.8g/m2、着色剤を0.00476g/m2、光拡散剤を36.5g/m2それぞれ含んでいて、ヘイズは99.4%、YIは−6.3である。300nm〜410nmの波長範囲(A)での光線透過率の最大値(TAmax)は0.3%(410nm)、450〜800nmの波長範囲(B)での光線透過率の最小値(TBmin)は42.2%、最大値(TBmax)は53.1%である。極大吸収ピーク(P)を有し、その極大吸収波長(λp)は約560nm、極大吸収波長における光線透過率(Tp)は42.2%である。極大吸収波長における光線透過率(Tp)は、最大光線透過率(TBmax)の0.80倍である。 The acrylic resin composition sheet, 23.8 g / m 2 and per unit area ultraviolet absorber, colorant 0.00476g / m 2, include a light diffusing agent 36.5 g / m 2, respectively, haze 99 .4%, YI is -6.3. The maximum value (T Amax ) of light transmittance in the wavelength range (A) of 300 nm to 410 nm is 0.3% (410 nm), and the minimum value of light transmittance (T Bmin in the wavelength range (B) of 450 to 800 nm. ) Is 42.2%, and the maximum value (T Bmax ) is 53.1%. It has a maximum absorption peak (P), its maximum absorption wavelength (λ p ) is about 560 nm, and its light transmittance (T p ) at the maximum absorption wavelength is 42.2%. The light transmittance (T p ) at the maximum absorption wavelength is 0.80 times the maximum light transmittance (T Bmax ).
このシートを白色蛍光灯の照明カバーとして使用すると、白色蛍光灯からの光は拡散透過されて自然な乳白色に見え、また屋外で使用しても、昆虫類が群がってこない。 When this sheet is used as an illumination cover for a white fluorescent lamp, the light from the white fluorescent lamp is diffused and transmitted to look natural milky white, and insects do not gather even when used outdoors.
実施例3
部分重合物の使用量を97.8質量部とし、紫外線吸収剤の使用量を0.75質量部とした以外は実施例1と同様に操作して、アクリル樹脂組成物シートを得た。このアクリル樹脂組成物シートは、目視では着色を確認できなかった。このアクリル樹脂組成物シートの光線透過スペクトルを図3に示す。評価結果を第1表に示す。
Example 3
An acrylic resin composition sheet was obtained in the same manner as in Example 1 except that the amount of the partially polymerized product was 97.8 parts by mass and the amount of the ultraviolet absorber was 0.75 parts by mass. This acrylic resin composition sheet could not be colored visually. The light transmission spectrum of this acrylic resin composition sheet is shown in FIG. The evaluation results are shown in Table 1.
このアクリル樹脂組成物シートは、単位面積あたり紫外線吸収剤を17.9g/m2、着色剤を0.00476g/m2、光拡散剤を36.5g/m2それぞれ含んでいて、ヘイズは99.4%、YIは−7.4である。300nm〜410nmの波長範囲(A)での光線透過率の最大値(TAmax)は0.8%(410nm)、450〜800nmの波長範囲(B)での光線透過率の最小値(TBmin)は43.4%、最大値(TBmax)は54.1%である。極大吸収ピーク(P)を有し、その極大吸収波長(λp)は約560nm、極大吸収波長における光線透過率(Tp)は43.4%である。極大吸収波長における光線透過率(Tp)は、最大光線透過率(TBmax)の0.80倍である。 The acrylic resin composition sheet, 17.9 g / m 2 and per unit area ultraviolet absorber, colorant 0.00476g / m 2, include a light diffusing agent 36.5 g / m 2, respectively, haze 99 .4% and YI is -7.4. The maximum value (T Amax ) of light transmittance in the wavelength range (A) of 300 nm to 410 nm is 0.8% (410 nm), and the minimum value of light transmittance (T Bmin in the wavelength range (B) of 450 to 800 nm. ) Is 43.4%, and the maximum value (T Bmax ) is 54.1%. It has a maximum absorption peak (P), its maximum absorption wavelength (λ p ) is about 560 nm, and its light transmittance (T p ) at the maximum absorption wavelength is 43.4%. The light transmittance (T p ) at the maximum absorption wavelength is 0.80 times the maximum light transmittance (T Bmax ).
このシートを白色蛍光灯の照明カバーとして使用すると、白色蛍光灯からの光は拡散透過されて自然な乳白色に見え、また屋外で使用しても、昆虫類が群がってこない。 When this sheet is used as an illumination cover for a white fluorescent lamp, the light from the white fluorescent lamp is diffused and transmitted to look natural milky white, and insects do not gather even when used outdoors.
実施例4
部分重合物の使用量を97.5質量部とし、紫外線吸収剤の使用量を1.0質量部とし、着色剤の使用量を0.00015質量部とした以外は実施例1と同様に操作して、アクリル樹脂組成物シートを得た。このアクリル樹脂組成物シートは、目視では着色を確認できなかった。このアクリル樹脂組成物シートの光線透過スペクトルを図4に示す。評価結果を第2表に示す。
Example 4
The same operation as in Example 1 was conducted except that the amount of the partially polymerized product was 97.5 parts by mass, the amount of the ultraviolet absorber used was 1.0 part by mass, and the amount of the colorant used was 0.00015 parts by mass. Thus, an acrylic resin composition sheet was obtained. This acrylic resin composition sheet could not be colored visually. The light transmission spectrum of this acrylic resin composition sheet is shown in FIG. The evaluation results are shown in Table 2.
このアクリル樹脂組成物シートは、単位面積あたり紫外線吸収剤を23.8g/m2、着色剤を0.0036g/m2、光拡散剤を36.5g/m2それぞれ含んでいて、ヘイズは99.2%YIは−2.2である。300nm〜410nmの波長範囲(A)での光線透過率の最大値(TAmax)は0.3%(410nm)、450〜800nmの波長範囲(B)での光線透過率の最小値(TBmin)は44.5%、最大値(TBmax)は54.2%である。極大吸収ピーク(P)を有し、その極大吸収波長(λp)は約560nm、極大吸収波長における光線透過率(Tp)は44.5%である。極大吸収波長における光線透過率(Tp)は、最大光線透過率(TBmax)の0.82倍である。 The acrylic resin composition sheet, 23.8 g / m 2 and per unit area ultraviolet absorber, colorant 0.0036 g / m 2, include a light diffusing agent 36.5 g / m 2, respectively, haze 99 .2% YI is -2.2. The maximum value (T Amax ) of light transmittance in the wavelength range (A) of 300 nm to 410 nm is 0.3% (410 nm), and the minimum value of light transmittance (T Bmin in the wavelength range (B) of 450 to 800 nm. ) Is 44.5%, and the maximum value (T Bmax ) is 54.2%. It has a maximum absorption peak (P), its maximum absorption wavelength (λ p ) is about 560 nm, and its light transmittance (T p ) at the maximum absorption wavelength is 44.5%. The light transmittance (T p ) at the maximum absorption wavelength is 0.82 times the maximum light transmittance (T Bmax ).
このシートを白色蛍光灯の照明カバーとして使用すると、白色蛍光灯からの光は拡散透過されて自然な乳白色に見え、また屋外で使用しても、昆虫類が群がってこない。 When this sheet is used as an illumination cover for a white fluorescent lamp, the light from the white fluorescent lamp is diffused and transmitted to look natural milky white, and insects do not gather even when used outdoors.
実施例5
部分重合物の使用量を98.2質量部とし、MS樹脂の使用量を0.75質量部とし、紫外線吸収剤の使用量を1.1質量部とし、着色剤の使用量を0.00016質量部とし、光拡散剤の使用量を0.021質量部とした以外は実施例1と同様に操作して、アクリル樹脂組成物シートを得た。このアクリル樹脂組成物シートは、目視では着色を確認できなかった。このアクリル樹脂組成物シートの光線透過スペクトルを図5に示す。評価結果を第2表に示す。
Example 5
The amount of partial polymer used is 98.2 parts by mass, the amount of MS resin used is 0.75 parts by mass, the amount of UV absorber used is 1.1 parts by mass, and the amount of colorant used is 0.00016. An acrylic resin composition sheet was obtained in the same manner as in Example 1 except that the amount of the light diffusing agent was 0.021 parts by mass. This acrylic resin composition sheet could not be colored visually. The light transmission spectrum of this acrylic resin composition sheet is shown in FIG. The evaluation results are shown in Table 2.
このアクリル樹脂組成物シートは、単位面積あたり紫外線吸収剤を26.2g/m2、着色剤を0.0036g/m2、光拡散剤を18.4g/m2それぞれ含んでいて、ヘイズは99.3%、YIは−1.7である。300nm〜410nmの波長範囲(A)での光線透過率の最大値(TAmax)は0.6%(410nm)、450〜800nmの波長範囲(B)での光線透過率の最小値(TBmin)は55.9%、最大値(TBmax)は65.9%である。極大吸収ピーク(P)を有し、その極大吸収波長(λp)は約550nm、極大吸収波長における光線透過率(Tp)は55.9%である。極大吸収波長における光線透過率(Tp)は、最大光線透過率(TBmax)の0.85倍である。 The acrylic resin composition sheet, 26.2 g / m 2 and per unit area ultraviolet absorber, colorant 0.0036 g / m 2, include a light diffusing agent 18.4 g / m 2, respectively, haze 99 .3%, YI is -1.7. The maximum value (T Amax ) of light transmittance in the wavelength range (A) of 300 nm to 410 nm is 0.6% (410 nm), and the minimum value of light transmittance (T Bmin in the wavelength range (B) of 450 to 800 nm. ) Is 55.9%, and the maximum value (T Bmax ) is 65.9%. It has a maximum absorption peak (P), its maximum absorption wavelength (λ p ) is about 550 nm, and its light transmittance (T p ) at the maximum absorption wavelength is 55.9%. The light transmittance (T p ) at the maximum absorption wavelength is 0.85 times the maximum light transmittance (T Bmax ).
このシートを白色蛍光灯の照明カバーとして使用すると、白色蛍光灯からの光は拡散透過されて自然な乳白色に見え、また屋外で使用しても、昆虫類が群がってこない。 When this sheet is used as a lighting cover for a white fluorescent lamp, the light from the white fluorescent lamp is diffused and transmitted to look natural milky white, and insects do not gather even when used outdoors.
比較例1
部分重合物の使用量を97.5質量部とし、紫外線吸収剤の使用量を1.0質量部とし、着色剤の使用量を0.00005質量部とした以外は実施例1と同様に操作して、アクリル樹脂組成物シートを得た。このアクリル樹脂組成物シートは、目視でやや黄色に着色していた。このアクリル樹脂組成物シートの光線透過スペクトルを図6に示す。評価結果を第2表に示す。
Comparative Example 1
The same operation as in Example 1 was performed except that the amount of the partially polymerized product was 97.5 parts by mass, the amount of the ultraviolet absorber used was 1.0 part by mass, and the amount of the colorant used was 0.00005 parts by mass. Thus, an acrylic resin composition sheet was obtained. This acrylic resin composition sheet was slightly colored yellow visually. The light transmission spectrum of this acrylic resin composition sheet is shown in FIG. The evaluation results are shown in Table 2.
このアクリル樹脂組成物シートは、単位面積あたり紫外線吸収剤を23.8g/m2、着色剤を0.0012g/m2、光拡散剤を36.5g/m2それぞれ含んでいて、ヘイズは99.4%、YIは6.8である。300nm〜410nmの波長範囲(A)での光線透過率の最大値(TAmax)は0.3%(410nm)、450〜800nmの波長範囲(B)での光線透過率の最小値(TBmin)は46.5%、最大値(TBmax)は53.2%である。極大吸収ピーク(P)を有し、その極大吸収波長(λp)は約540nm、極大吸収波長における光線透過率(Tp)は46.9%である。極大吸収波長における光線透過率(Tp)は、最大光線透過率(TBmax)の0.88倍である。 The acrylic resin composition sheet is, 23.8 g / m 2 and per unit area ultraviolet absorber, colorant 0.0012 g / m 2, include a light diffusing agent 36.5 g / m 2, respectively, haze 99 .4%, YI is 6.8. The maximum value (T Amax ) of light transmittance in the wavelength range (A) of 300 nm to 410 nm is 0.3% (410 nm), and the minimum value of light transmittance (T Bmin in the wavelength range (B) of 450 to 800 nm. ) Is 46.5%, and the maximum value (T Bmax ) is 53.2%. It has a maximum absorption peak (P), its maximum absorption wavelength (λ p ) is about 540 nm, and its light transmittance (T p ) at the maximum absorption wavelength is 46.9%. The light transmittance (T p ) at the maximum absorption wavelength is 0.88 times the maximum light transmittance (T Bmax ).
このシートを白色蛍光灯の照明カバーとして使用すると、昆虫累は群がってこず、白色蛍光灯からの光は拡散透過されるが、白色蛍光灯からの光はやや黄色く見える。
When this sheet is used as an illumination cover for a white fluorescent lamp, the insects do not collect and the light from the white fluorescent lamp diffuses and is transmitted, but the light from the white fluorescent lamp appears slightly yellow.
第 1 表
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
実施例1 実施例2 実施例3
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
部分重合物 (質量部) 98.5 97.5 97.8
MS樹脂 (質量部) 1.49 1.49 1.49
紫外線吸収剤 (質量部) 1.5 1.0 0.75
(g/m2) 35.7 23.8 17.9
着色剤 (質量部) 0.0002 0.0002 0.0002
(g/m2) 0.00476 0.00476 0.00476
光拡散剤 (質量部) 0.042 0.042 0.042
(g/m2) 36.5 36.5 36.5
────────────────────────────────────────
TAmax (%) 0.1 0.3 0.8
TBmin (%) 42.2 42.2 43.4
TBmax (%) 53.1 53.1 53.1
────────────────────────────────────────
吸収極大ピーク
λp (nm) 560 560 560
Tp (%) 42.2 42.2 43.4
Tp/TBmax 0.79 0.79 0.80
────────────────────────────────────────
ヘイズ (%) 99.4 99.4 99.4
YI −3.1 −6.3 −7.4
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
TAmax:300nm〜410nmの波長範囲(A)での光線透過率の最大値
TBmin:450〜700nmの波長範囲(B)での光線透過率の最小値
TBmax:450〜700nmの波長範囲(B)での光線透過率の最大値
λp :極大吸収ピークの極大吸収波長
Tp :極大吸収波長における光線透過率
Table 1
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
Example 1 Example 2 Example 3
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
Partial polymer (parts by mass) 98.5 97.5 97.8
MS resin (parts by weight) 1.49 1.49 1.49
UV absorber (parts by mass) 1.5 1.0 0.75
(g / m 2 ) 35.7 23.8 17.9
Colorant (parts by mass) 0.0002 0.0002 0.0002
(g / m 2 ) 0.00476 0.00476 0.00476
Light diffusing agent (parts by mass) 0.042 0.042 0.042
(g / m 2 ) 36.5 36.5 36.5
────────────────────────────────────────
T Amax (%) 0.1 0.3 0.8
T Bmin (%) 42.2 42.2 43.4
T Bmax (%) 53.1 53.1 53.1
────────────────────────────────────────
Absorption maximum peak λ p (nm) 560 560 560
T p (%) 42.2 42.2 43.4
T p / T Bmax 0.79 0.79 0.80
────────────────────────────────────────
Haze (%) 99.4 99.4 99.4
YI-3.1-6.3-7.4
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
T Amax : Maximum value of light transmittance in the wavelength range (A) of 300 nm to 410 nm T Bmin : Minimum value of light transmittance in the wavelength range (B) of 450 to 700 nm T Bmax : Wavelength range of 450 to 700 nm ( Maximum value of light transmittance in B) λ p : Maximum absorption wavelength of maximum absorption peak T p : Light transmittance at maximum absorption wavelength
第 2 表
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
実施例4 実施例5 比較例1
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
部分重合物 (質量部) 97.5 98.2 97.5
MS樹脂 (質量部) 1.49 0.75 1.49
紫外線吸収剤 (質量部) 1.0 1.1 1.0
(g/m2) 23.8 26.2 23.8
着色剤 (質量部) 0.00015 0.00016 0.00005
(g/m2) 0.00357 0.00390 0.00119
光拡散剤 (質量部) 0.042 0.042 0.042
(g/m2) 36.5 36.5 36.5
────────────────────────────────────────
TAmax (%) 0.3 0.6 0.3
TBmin (%) 44.5 55.9 46.5
TBmax (%) 54.2 65.9 53.2
────────────────────────────────────────
吸収極大ピーク
λp (nm) 560 550 540
Tp (%) 42.5 55.9 46.9
Tp/TBmax 0.82 0.85 0.88
────────────────────────────────────────
ヘイズ (%) 99.2 99.3 99.4
YI −2.2 −1.7 6.8
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
TAmax:300nm〜410nmの波長範囲(A)での光線透過率の最大値
TBmin:450〜700nmの波長範囲(B)での光線透過率の最小値
TBmax:450〜700nmの波長範囲(B)での光線透過率の最大値
λp :極大吸収ピークの極大吸収波長
Tp :極大吸収波長における光線透過率
Table 2
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
Example 4 Example 5 Comparative Example 1
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
Partial polymer (parts by mass) 97.5 98.2 97.5
MS resin (parts by weight) 1.49 0.75 1.49
Ultraviolet absorber (parts by mass) 1.0 1.1 1.0
(g / m 2 ) 23.8 26.2 23.8
Colorant (parts by mass) 0.00015 0.00016 0.00005
(g / m 2 ) 0.00357 0.00390 0.00119
Light diffusing agent (parts by mass) 0.042 0.042 0.042
(g / m 2 ) 36.5 36.5 36.5
────────────────────────────────────────
T Amax (%) 0.3 0.6 0.3
T Bmin (%) 44.5 55.9 46.5
T Bmax (%) 54.2 65.9 53.2
────────────────────────────────────────
Absorption maximum peak λ p (nm) 560 550 540
T p (%) 42.5 55.9 46.9
T p / T Bmax 0.82 0.85 0.88
────────────────────────────────────────
Haze (%) 99.2 99.3 99.4
YI -2.2 -1.7 6.8
━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━━
T Amax : Maximum value of light transmittance in the wavelength range (A) of 300 nm to 410 nm T Bmin : Minimum value of light transmittance in the wavelength range (B) of 450 to 700 nm T Bmax : Wavelength range of 450 to 700 nm ( Maximum value of light transmittance in B) λ p : Maximum absorption wavelength of maximum absorption peak T p : Light transmittance at maximum absorption wavelength
A:300nm〜410nmの波長範囲
B:450nm〜700nmの波長範囲
P:吸収極大ピーク
A: Wavelength range from 300 nm to 410 nm B: Wavelength range from 450 nm to 700 nm P: Maximum absorption peak
Claims (3)