JP2006124264A - Calcium oxide dispersion liquid and its manufacturing method - Google Patents
Calcium oxide dispersion liquid and its manufacturing method Download PDFInfo
- Publication number
- JP2006124264A JP2006124264A JP2005102719A JP2005102719A JP2006124264A JP 2006124264 A JP2006124264 A JP 2006124264A JP 2005102719 A JP2005102719 A JP 2005102719A JP 2005102719 A JP2005102719 A JP 2005102719A JP 2006124264 A JP2006124264 A JP 2006124264A
- Authority
- JP
- Japan
- Prior art keywords
- calcium oxide
- calcium
- dispersion
- dispersion medium
- alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
本発明は酸化カルシウム微粒子の分散液およびその製造方法に関する。詳しくは粒子径が小さく、均一に分散された高濃度酸化カルシウムの分散液およびその製造方法に関する。 The present invention relates to a dispersion of calcium oxide fine particles and a method for producing the same. Specifically, the present invention relates to a dispersion of high-concentration calcium oxide having a small particle size and uniformly dispersed, and a method for producing the same.
酸化カルシウムは吸湿性が高く、吸湿材、脱水剤として有用である。酸化カルシウムを吸湿材、脱水剤として利用する場合、高活性であることが要求される。そのため粒子は広い表面積を持つナノ粒子であること、脱水作用という面では不活性である水酸化カルシウム、炭酸カルシウムを極力含まないことが望ましい。さらに、酸化カルシウムをナノ粒子化することにより光透過性を有するペーストの製造が可能である。また、取り扱いの面から均一な分散液状での供給が望まれる。 Calcium oxide has high hygroscopicity and is useful as a hygroscopic material and a dehydrating agent. When calcium oxide is used as a hygroscopic material or a dehydrating agent, high activity is required. Therefore, it is desirable that the particles should be nanoparticles having a large surface area and should contain as little calcium hydroxide and calcium carbonate as possible in terms of dehydration. Furthermore, it is possible to produce a paste having optical transparency by making calcium oxide into nanoparticles. In addition, supply in a uniform dispersed liquid is desired from the viewpoint of handling.
従来、酸化カルシウムは石灰石を１２００℃程度に加熱して分解することで製造されてきた。しかし、高温により粒子径が大きく成長し、互いに焼結し硬い物質が生成する。このため、この方法による生成物を粉砕してナノ粒子化するには莫大なエネルギーと時間がかかる。しかし、吸湿材、脱水剤として用いる酸化カルシウムを製造する際には、酸化カルシウムの吸湿を抑制する必要があり、時間がかかる処理は不適切である。また、従来の酸化カルシウムの合成法では粒子径の非常に小さい粒子を、不活性物を含まず分散液にすることは困難であった。また、酸化カルシウムの粒径が細かいほどスラリーの粘度は上昇するため、酸化カルシウムナノ粒子の高濃度スラリーの製造は従来の技術では不可能であった。 Conventionally, calcium oxide has been produced by heating and decomposing limestone to about 1200 ° C. However, the particle size grows greatly at high temperatures and sinters to produce a hard substance. For this reason, it takes enormous energy and time to pulverize the product by this method into nanoparticles. However, when manufacturing calcium oxide used as a hygroscopic material and a dehydrating agent, it is necessary to suppress the moisture absorption of calcium oxide, and a time-consuming treatment is inappropriate. In addition, it has been difficult for conventional calcium oxide synthesis methods to make particles having a very small particle size into a dispersion containing no inert substances. Further, since the viscosity of the slurry increases as the particle size of calcium oxide is finer, it is impossible to produce a high concentration slurry of calcium oxide nanoparticles by the conventional technique.
本発明は、粒子径が小さく高純度の酸化カルシウムが均一に分散された酸化カルシウム分散液およびその製造方法を提供することを課題としている。 An object of the present invention is to provide a calcium oxide dispersion in which high-purity calcium oxide having a small particle size is uniformly dispersed and a method for producing the same.
本発明者らは先に有機金属β−ジケトン錯体の気相酸化によるナノ粒子金属酸化物の合成法を開発している。本手法を用いメジアン粒子径が２００ｎｍ以下の一次粒子を合成することが可能である。この粒子は凝集体で存在するため、凝集を解砕するために５０μｍの微小ビーズを用い、分散媒として最適な分散媒（アルコール等）を用いることで、均一で微小粒子の酸化カルシウム分散液を調整することを可能とした。分散媒の種類によって分散性は全く異なり、双極子モーメント、粘度などの観点から選択、あるいは選択した溶媒の最適な混合をすることにより安定な酸化カルシウムナノ粒子の分散液を製造しうることを見出した。
また、不活性ガス雰囲気下、短時間処理により酸化カルシウムの不活性化を抑制できることを可能とした。
The present inventors have previously developed a method for synthesizing nanoparticulate metal oxides by gas phase oxidation of organometallic β-diketone complexes. Using this technique, primary particles having a median particle diameter of 200 nm or less can be synthesized. Since these particles exist as aggregates, 50 μm microbeads are used to break up the agglomeration, and an optimal dispersion medium (alcohol or the like) is used as a dispersion medium. It was possible to adjust. It was found that the dispersibility is completely different depending on the type of dispersion medium, and it is possible to produce a stable dispersion of calcium oxide nanoparticles by selecting from the viewpoint of dipole moment, viscosity, etc., or by optimally mixing the selected solvent. It was.
In addition, the inactivation of calcium oxide can be suppressed by a short time treatment under an inert gas atmosphere.
すなわち、本発明は基本的に以下の〔１〕〜〔２２〕の発明からなる。
〔１〕メジアン粒径（体積基準）が１〜２００ｎｍ、最大粒子径が１０〜１０００ｎｍの範囲にある酸化カルシウム微粒子および有機分散媒を含むことを特徴とする酸化カルシウム分散液。
That is, the present invention basically comprises the following inventions [1] to [22].
[1] A calcium oxide dispersion comprising calcium oxide fine particles and an organic dispersion medium having a median particle size (volume basis) of 1 to 200 nm and a maximum particle size of 10 to 1000 nm.
〔２〕上記酸化カルシウム分散液中の酸化カルシウム濃度が１０〜５０（質量）％であることを特徴とする〔１〕に記載の酸化カルシウム分散液。
〔３〕水分量が１，０００ｐｐｍ（質量）未満である有機分散媒を原料として得られたものであることを特徴とする〔１〕または〔２〕に記載の酸化カルシウム分散液。
[2] The calcium oxide dispersion according to [1], wherein the calcium oxide concentration in the calcium oxide dispersion is 10 to 50 (mass)%.
[3] The calcium oxide dispersion according to [1] or [2], which is obtained using an organic dispersion medium having a water content of less than 1,000 ppm (mass) as a raw material.
〔４〕上記酸化カルシウム微粒子が、カルシウム錯体を気化し、気相中で酸化して得られたものであることを特徴とする〔１〕〜〔３〕のいずれか１項に記載の酸化カルシウム分散液。 [4] The calcium oxide according to any one of [1] to [3], wherein the calcium oxide fine particles are obtained by vaporizing a calcium complex and oxidizing in a gas phase. Dispersion.
〔５〕上記酸化カルシウム微粒子が、カルシウム錯体を気化し、気相中で酸化した後、焼成処理して得られたものであることを特徴とする〔１〕〜〔３〕のいずれか１項に記載の酸化カルシウム分散液。 [5] Any one of [1] to [3], wherein the calcium oxide fine particles are obtained by vaporizing a calcium complex, oxidizing the gas in a gas phase, and performing a baking treatment. Calcium oxide dispersion described in 1.
〔６〕上記カルシウム錯体が、カルシウムとβ−ジケトン化合物との錯体であることを特徴とする〔４〕または〔５〕に記載の酸化カルシウム分散液。
〔７〕上記酸化カルシウム微粒子が、水酸化カルシウムの含有量が５質量％未満、炭酸カルシウムの含有量が１質量％未満であることを特徴とする〔１〕〜〔６〕のいずれかに記載の酸化カルシウム分散液。
[6] The calcium oxide dispersion liquid according to [4] or [5], wherein the calcium complex is a complex of calcium and a β-diketone compound.
[7] The calcium oxide fine particles have a calcium hydroxide content of less than 5% by mass and a calcium carbonate content of less than 1% by mass, according to any one of [1] to [6] Calcium oxide dispersion.
〔８〕上記有機分散媒がアルコール、ニトリル化合物、アミド化合物および多価アルコール誘導体のいずれかであることを特徴とする〔１〕〜〔７〕のいずれかに記載の酸化カルシウム分散液。 [8] The calcium oxide dispersion liquid according to any one of [1] to [7], wherein the organic dispersion medium is any one of an alcohol, a nitrile compound, an amide compound, and a polyhydric alcohol derivative.
〔９〕上記アルコールが炭素数３以上のアルコールであることを特徴とする〔８〕に記載の酸化カルシウム分散液。
〔１０〕上記有機分散媒が２価アルコール誘導体であることを特徴とする請求項８に記載の酸化カルシウム分散液。
[9] The calcium oxide dispersion according to [8], wherein the alcohol is an alcohol having 3 or more carbon atoms.
[10] The calcium oxide dispersion according to claim 8, wherein the organic dispersion medium is a dihydric alcohol derivative.
〔１１〕上記有機分散媒が、アセトニトリル、１−ブタノール、１−ヘキサノール、１−メトキシ−２−プロパノールのいずれかであることを特徴とする〔１〕〜〔７〕のいずれかに記載の酸化カルシウム分散液。 [11] The oxidation according to any one of [1] to [7], wherein the organic dispersion medium is any one of acetonitrile, 1-butanol, 1-hexanol, and 1-methoxy-2-propanol. Calcium dispersion.
〔１２〕上記有機分散媒が混合分散媒であることを特徴とする〔１〕〜〔７〕のいずれかに記載の酸化カルシウム分散液。
〔１３〕上記有機分散媒がニトリル化合物とアルコールの混合分散媒、芳香族化合物とアルコールの混合分散媒、芳香族化合物とアミン化合物の混合分散媒、エステルとアルコールの混合分散媒、アミド化合物とアルコールの混合分散媒、芳香族化合物とニトリル化合物の混合分散媒および多価アルコール誘導体とアミン化合物の混合分散媒のいずれかであることを特徴とする〔１２〕に記載の酸化カルシウム分散液。
[12] The calcium oxide dispersion according to any one of [1] to [7], wherein the organic dispersion medium is a mixed dispersion medium.
[13] The organic dispersion medium is a mixed dispersion medium of a nitrile compound and an alcohol, a mixed dispersion medium of an aromatic compound and an alcohol, a mixed dispersion medium of an aromatic compound and an amine compound, a mixed dispersion medium of an ester and an alcohol, an amide compound and an alcohol The calcium oxide dispersion liquid according to [12], characterized in that any one of a mixed dispersion medium, an aromatic compound and a nitrile compound, and a mixed dispersion medium of a polyhydric alcohol derivative and an amine compound.
〔１４〕上記混合分散媒が、トルエンとアルコール、酢酸ブチルとアルコール、ＮＮ−ジメチルアセトアミドとアルコール、ジエチレングリコールジメチルエーテルとモノエタノールアミン、ジエチレングリコールジメチルエーテルとジエタノールアミン、ジエチレングリコールジメチルエーテルとトリエタノールアミンの組み合わせのいずれかであることを特徴とする〔１２〕に記載の酸化カルシウム分散液。 [14] The mixed dispersion medium is any combination of toluene and alcohol, butyl acetate and alcohol, NN-dimethylacetamide and alcohol, diethylene glycol dimethyl ether and monoethanolamine, diethylene glycol dimethyl ether and diethanolamine, diethylene glycol dimethyl ether and triethanolamine. The calcium oxide dispersion liquid according to [12], which is characterized in that
〔１５〕分散剤を含むことを特徴とする〔１〕〜〔１４〕のいずれかに記載の酸化カルシウム分散液。
〔１６〕上記分散剤がノニオン系界面活性剤から選ばれる1種以上の化合物であること
を特徴とする〔１５〕に記載の酸化カルシウム分散液。
[15] The calcium oxide dispersion according to any one of [1] to [14], which contains a dispersant.
[16] The calcium oxide dispersion according to [15], wherein the dispersant is one or more compounds selected from nonionic surfactants.
〔１７〕上記ノニオン系界面活性剤が水酸基を有するものであることを特徴とする〔１
６〕に記載の酸化カルシウム分散液。
〔１８〕上記ノニオン系界面活性剤がポリプロピレンオキシド付加グリセリンである事を特徴とする〔１６〕に記載の酸化カルシウム分散液。
[17] The nonionic surfactant has a hydroxyl group [1]
6]. Calcium oxide dispersion liquid.
[18] The calcium oxide dispersion according to [16], wherein the nonionic surfactant is polypropylene oxide-added glycerin.
〔１９〕上記有機分散媒が粘性率３．０ｍＰａ・ｓ（２０℃）以下であることを特徴とする〔１〕〜〔１８〕のいずれかに記載の酸化カルシウム分散液。
〔２０〕酸化カルシウムの微粒子と有機分散媒と直径５〜２００μｍのビーズとを容器に充填し、これらを攪拌することにより〔１〕〜〔１９〕のいずれかに記載の酸化カルシウム分散液を製造することを特徴とする酸化カルシウム分散液の製造方法。
[19] The calcium oxide dispersion liquid according to any one of [1] to [18], wherein the organic dispersion medium has a viscosity of 3.0 mPa · s (20 ° C.) or less.
[20] A calcium oxide dispersion liquid according to any one of [1] to [19] is produced by filling a container with calcium oxide fine particles, an organic dispersion medium, and beads having a diameter of 5 to 200 μm and stirring them. A method for producing a calcium oxide dispersion liquid.
〔２１〕上記攪拌を水分含有量が１０ｐｐｍ（ｍｏｌ）以下の不活性ガス雰囲気下で行うことを特徴とする〔２０〕に記載の酸化カルシウム分散液の製造方法。
〔２２〕容器に充填する有機分散媒の水分量が１,０００ｐｐｍ（質量）未満であるこ
とを特徴とする〔２０〕または〔２１〕に記載の酸化カルシウム分散液の製造方法。
[21] The method for producing a calcium oxide dispersion as described in [20], wherein the stirring is performed in an inert gas atmosphere having a water content of 10 ppm (mol) or less.
[22] The method for producing a calcium oxide dispersion according to [20] or [21], wherein the water content of the organic dispersion medium filled in the container is less than 1,000 ppm (mass).
本発明に係る酸化カルシウム分散液は、脱水性の面で不活性物である水酸化カルシウム、炭酸カルシウムをほとんど含まず酸化カルシウム純度が高いので、吸湿材、脱水剤として非常に有用である。また、酸化カルシウムの粒子が微小で、表面積が大きいため、吸湿材としての性能が高い。また、塗布して膜として使用すると高い透明性の膜が得られる。さらに、酸化カルシウム微粒子を高濃度で分散できるため、コスト面でも非常に有利である。これらの特長の故、本発明の酸化カルシウム分散液は、精密機器、電子材料（有機ＥＬ、ＥＬＤなど。）への適用が可能となる。 The calcium oxide dispersion according to the present invention is very useful as a hygroscopic material and a dehydrating agent because it contains almost no inert calcium hydroxide and calcium carbonate in terms of dehydration and has high calcium oxide purity. Further, since the calcium oxide particles are minute and have a large surface area, the performance as a hygroscopic material is high. Also, when applied and used as a film, a highly transparent film can be obtained. Furthermore, since the calcium oxide fine particles can be dispersed at a high concentration, it is very advantageous in terms of cost. Because of these features, the calcium oxide dispersion of the present invention can be applied to precision instruments and electronic materials (organic EL, ELD, etc.).
本発明に係る酸化カルシウム分散液の製造方法は、上記のような優れた性質を有する酸化カルシウム分散液を効率よく製造することができる。 The method for producing a calcium oxide dispersion according to the present invention can efficiently produce a calcium oxide dispersion having excellent properties as described above.
以下、本発明に係る酸化カルシウム分散液およびその製造方法について詳細に説明する。
［酸化カルシウム分散液］
本発明に係る酸化カルシウム分散液は、少なくとも酸化カルシウム微粒子と有機分散媒を含んでいる。
Hereinafter, the calcium oxide dispersion and the method for producing the same according to the present invention will be described in detail.
[Calcium oxide dispersion]
The calcium oxide dispersion according to the present invention contains at least calcium oxide fine particles and an organic dispersion medium.
酸化カルシウム微粒子は、メジアン粒子径（体積累積分率（粒子の密度が一定なら質量積分率でも同じ値となる）が５０％となる粒子径：Ｄ50）が１〜２００ｎｍ、好ましくは５〜１５０ｎｍ、より好ましくは１０〜１００ｎｍであり、最大粒子径が１０〜１０００ｎｍ、より好ましくは１５〜５００ｎｍ、さらに好ましくは２０〜２５０ｎｍ、特に好ましくは５０〜１５０ｎｍである。粒子径が大きい場合、微細加工が不可能となり、光透過性も悪くなる等の問題が発生し、また表面積が小さくなり吸湿効率が下がるので好ましくない。 The calcium oxide fine particles have a median particle diameter (particle diameter (D 50 ) at which the volume cumulative fraction (the same value is obtained even when the particle density is constant) is 50%): 1 to 200 nm, preferably 5 to 150 nm. More preferably, it is 10-100 nm, and the maximum particle diameter is 10-1000 nm, More preferably, it is 15-500 nm, More preferably, it is 20-250 nm, Most preferably, it is 50-150 nm. When the particle size is large, fine processing becomes impossible and problems such as poor light transmission occur, and the surface area becomes small and the hygroscopic efficiency decreases.
なお、メジアン粒子径および最大粒子径は、酸化カルシウム分散液を必要に応じて分散媒と同じ有機分散媒により希釈してレーザードップラー法により測定する。メジアン粒子径および最大粒子径の測定は、例えば日機装株式会社製のNanotrac UPA-EX150や同社のMicrotrac UPA-150により行うことができる。 The median particle size and the maximum particle size are measured by a laser Doppler method after diluting the calcium oxide dispersion with the same organic dispersion medium as the dispersion medium as necessary. The median particle size and the maximum particle size can be measured, for example, by Nanotrac UPA-EX150 manufactured by Nikkiso Co., Ltd. or Microtrac UPA-150 manufactured by the same company.
有機分散媒としては特に制限はないが、アルコール、ニトリル化合物、アミド化合物、多価アルコール誘導体等の有機溶媒およびこれらの混合溶媒、並びに芳香族化合物とアルコールの混合分散媒、芳香族化合物とアミン化合物の混合分散媒、エステルとアルコール
の混合分散媒、芳香族化合物とニトリル化合物の混合分散媒、２価アルコール誘導体とアミン化合物の混合分散媒が好ましい。また、静電反発による凝集抑制効果を期待する場合はプロトン性溶媒であることが好ましい。
Although there is no restriction | limiting in particular as an organic dispersion medium, Organic solvents, such as alcohol, a nitrile compound, an amide compound, a polyhydric alcohol derivative, and these mixed solvents, and a mixed dispersion medium of an aromatic compound and alcohol, an aromatic compound, and an amine compound And a mixed dispersion medium of an ester and an alcohol, a mixed dispersion medium of an aromatic compound and a nitrile compound, and a mixed dispersion medium of a dihydric alcohol derivative and an amine compound. Moreover, when expecting the aggregation inhibitory effect by electrostatic repulsion, it is preferable that it is a protic solvent.
アルコールとしては、メタノール、エタノール、プロパノール、イソプロパノール、ブタノール、ペンタノール、ヘキサノール、ヘプタノール、オクタノール、シクロペンタノール、シクロヘキサノールなどの炭素数１〜１０のものが挙げられ、特に炭素数３以上のアルコールは再凝集抑制効果が高く、吸湿性も低いため好ましい。なかでも１−ブタノールが特に好ましい。 Examples of the alcohol include those having 1 to 10 carbon atoms such as methanol, ethanol, propanol, isopropanol, butanol, pentanol, hexanol, heptanol, octanol, cyclopentanol and cyclohexanol. A reaggregation suppressing effect is high and hygroscopicity is low, which is preferable. Of these, 1-butanol is particularly preferable.
ニトリル化合物はシアノ基（−ＣＮ）を有する有機溶媒であり、具体的にはアセトニトリル、スクシノニトリル、プロピオニトリル、ブチロニトリル、アクリロニトリル、アジポニトリル、ベンゾニトリルなどの炭素数１〜１０の化合物が挙げられる。なかでもアセトニトリルが特に好ましい。 A nitrile compound is an organic solvent having a cyano group (—CN), and specific examples include compounds having 1 to 10 carbon atoms such as acetonitrile, succinonitrile, propionitrile, butyronitrile, acrylonitrile, adiponitrile, and benzonitrile. . Of these, acetonitrile is particularly preferred.
アミド化合物はアミド基を有する有機溶媒であり、具体的にはホルムアミド、Ｎ−メチルホルムアミド、Ｎ,Ｎ−ジメチルホルムアミド、Ｎ,Ｎ−ジエチルホルムアミド、アセトアミド、Ｎ−メチルアセトアミド、Ｎ,Ｎ−ジメチルアセトアミド、Ｎ,Ｎ−ジエチルアセトアミド、Ｎ−メチルプロピオンアミドなどが挙げられる。 An amide compound is an organic solvent having an amide group, specifically, formamide, N-methylformamide, N, N-dimethylformamide, N, N-diethylformamide, acetamide, N-methylacetamide, N, N-dimethylacetamide N, N-diethylacetamide, N-methylpropionamide and the like.
多価アルコール誘導体は、多価アルコールの、モノエーテル、ジエーテル、モノエステル、ジエステルが好ましい。
多価アルコール誘導体としては、１−メトキシ−２−プロパノール、１−エトキシ−２−プロパノール、１−ブトキシ−２−プロパノール、ジエチレングリコールエチルメチルエーテル、ジエチレングリコールジエチルエーテル、ジエチレングリコールジブチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノエチルエーテルアセタート、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテルアセタート、ジエチレングリコールモノメチルエーテル、エチレングリコールジアセタート、エチレングリコールジエチルエーテル、エチレングリコールジブチルエーテル、エチレングリコールジメチルエーテル、エチレングリコールモノアセタート、エチレングリコールモノイソプロピルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノエチルエーテルアセタート、エチレングリコールモノブチルエーテル、エチレングリコールモノブチルエーテルアセタート、エチレングリコールモノヘキシルエーテル、エチレングリコールモノメチルエーテル、エチレングリコールモノメチルエーテルアセタート、エチレングリコールモノメトキシメチルエーテルなどの２価アルコールの誘導体；グリセリンモノアセタート、グリセリンジアセタート、グリセリントリアセタート、グリセリンジアルキルエーテル（例えば、１,２−ジメチルグリセリン、１,３−ジメチルグリセリン、１,３−ジエチルグ
リセリン）などの３価以上の多価アルコール誘導体などが挙げられる。なかでも１−メトキシ−２−プロパノールが特に好ましい。
The polyhydric alcohol derivative is preferably a monoether, diether, monoester or diester of polyhydric alcohol.
As polyhydric alcohol derivatives, 1-methoxy-2-propanol, 1-ethoxy-2-propanol, 1-butoxy-2-propanol, diethylene glycol ethyl methyl ether, diethylene glycol diethyl ether, diethylene glycol dibutyl ether, diethylene glycol dimethyl ether, diethylene glycol monoethyl Ether, diethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether, diethylene glycol monobutyl ether acetate, diethylene glycol monomethyl ether, ethylene glycol diacetate, ethylene glycol diethyl ether, ethylene glycol dibutyl ether, ethylene glycol dimethyl ether, ethylene glycol monoacetate Tar, ethylene glycol monoisopropyl ether, ethylene glycol monoethyl ether, ethylene glycol monoethyl ether acetate, ethylene glycol monobutyl ether, ethylene glycol monobutyl ether acetate, ethylene glycol monohexyl ether, ethylene glycol monomethyl ether, ethylene glycol monomethyl ether acetate Derivatives of dihydric alcohols such as tartrate, ethylene glycol monomethoxymethyl ether; glycerin monoacetate, glycerin diacetate, glycerin triacetate, glycerin dialkyl ether (eg 1,2-dimethylglycerin, 1,3-dimethylglycerin) 1,3-diethylglycerin) and the like trivalent or higher polyhydric alcohol derivatives It is. Of these, 1-methoxy-2-propanol is particularly preferable.
本発明の酸化カルシウム分散液に使用する有機分散媒を２種類以上の有機分散媒を混合分散媒にすることで、より高濃度の酸化カルシウムの製造が可能になる。以下に好ましい混合分散媒の例を挙げる。 By using the organic dispersion medium used in the calcium oxide dispersion of the present invention as a mixed dispersion medium of two or more kinds of organic dispersion media, it becomes possible to produce calcium oxide with a higher concentration. Examples of preferred mixed dispersion media are given below.
＜ニトリル化合物とアルコールの混合分散媒＞
混合分散媒に使用するニトリル化合物、アルコールは前記のものを使用できる。
組み合わせとしては、アセトニトリルとアルコール（特に１−ブタノール、１−ヘキサノール）が好ましい。
混合分散媒に対するアルコールの割合は０．００５〜５０％（質量）であることが好まし
く、さらに好ましくは０．０１〜１０％、もっとも好ましくは０．０１〜０．５％である。
<Mixed dispersion medium of nitrile compound and alcohol>
The nitrile compounds and alcohols used for the mixed dispersion medium can be those described above.
As a combination, acetonitrile and alcohol (especially 1-butanol and 1-hexanol) are preferable.
The ratio of alcohol to the mixed dispersion medium is preferably 0.005 to 50% (mass), more preferably 0.01 to 10%, and most preferably 0.01 to 0.5%.
さらに、この混合分散媒に第三の溶媒成分を加えても良い。第三成分としてはアミン化合物などが挙げられる。アミン化合物としては、モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、モノエチルアミン、ジエチルアミン、トリエチルアミン、エチレンジアミンなどが挙げられる。 Furthermore, a third solvent component may be added to the mixed dispersion medium. Examples of the third component include amine compounds. Examples of the amine compound include monoethanolamine, diethanolamine, triethanolamine, monoethylamine, diethylamine, triethylamine, and ethylenediamine.
＜芳香族化合物とアルコールの混合分散媒＞
芳香族化合物としては、具体的にはベンゼン、トルエン、キシレン、エチルベンゼンが挙げられる。アルコールとしては前記のものが使用できる。組み合わせとしては、トルエンと１−ヘキサノール、キシレンと１−ヘキサノール、エチルベンゼンと１−ヘキサノールが好ましい。
<Mixed dispersion medium of aromatic compound and alcohol>
Specific examples of the aromatic compound include benzene, toluene, xylene, and ethylbenzene. As the alcohol, those described above can be used. Preferred combinations are toluene and 1-hexanol, xylene and 1-hexanol, and ethylbenzene and 1-hexanol.
混合分散媒に対するアルコールの割合は０．００５〜５０％（質量）であることが好ましく、さらに好ましくは０．０１〜１０％、もっとも好ましくは０．０１〜０．５％である。
さらに、この混合分散媒に第三成分を加えても良い。第三成分としては前記のアミン化合物などが挙げられる。
The ratio of alcohol to the mixed dispersion medium is preferably 0.005 to 50% (mass), more preferably 0.01 to 10%, and most preferably 0.01 to 0.5%.
Further, a third component may be added to the mixed dispersion medium. Examples of the third component include the amine compounds described above.
＜芳香族化合物とアミン化合物の混合分散媒＞
芳香族化合物は前記のものが使用できる。アミン化合物としては、モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、モノエチルアミン、ジエチルアミン、トリエチルアミン、エチレンジアミンなどが挙げられる。組み合わせとしては、キシレンとモノエタノールアミンが好ましい。
混合分散媒に対するアミン化合物の割合は０．００５〜５０％（質量）であることが好ましく、さらに好ましくは０．０１〜１０％、もっとも好ましくは０．０１〜５％である。
<Mixed dispersion medium of aromatic compound and amine compound>
The above-mentioned aromatic compounds can be used. Examples of the amine compound include monoethanolamine, diethanolamine, triethanolamine, monoethylamine, diethylamine, triethylamine, and ethylenediamine. As a combination, xylene and monoethanolamine are preferable.
The ratio of the amine compound to the mixed dispersion medium is preferably 0.005 to 50% (mass), more preferably 0.01 to 10%, and most preferably 0.01 to 5%.
＜エステルとアルコールの混合分散媒＞
エステルとしては、ギ酸エチル、ギ酸プロピル、ギ酸ブチル、酢酸メチル、酢酸エチル、酢酸プロピル、酢酸ブチル、酢酸ペンチル、ピバリン酸メチル、ピバリン酸エチル等が好ましい。アルコールは前記のものが使用できる。組み合わせとしては酢酸ブチルと１−ブタノール、酢酸ブチルと１−ヘキサノール、ピバリン酸アルキルと１−ヘキサノールが好ましい。
<Ester and alcohol mixed dispersion medium>
As the ester, ethyl formate, propyl formate, butyl formate, methyl acetate, ethyl acetate, propyl acetate, butyl acetate, pentyl acetate, methyl pivalate, ethyl pivalate and the like are preferable. The above-mentioned alcohol can be used. Preferred combinations are butyl acetate and 1-butanol, butyl acetate and 1-hexanol, alkyl pivalate and 1-hexanol.
さらに、この混合分散媒に第三成分を加えても良い。第三成分としては前記アミン化合物などが挙げられる。
混合分散媒に対するアルコールの割合は０．００５〜５０％（質量）であることが好ましく、さらに好ましくは０．０１〜１０％、もっとも好ましくは０．０１〜０．５％である。
Further, a third component may be added to the mixed dispersion medium. Examples of the third component include the amine compounds.
The ratio of alcohol to the mixed dispersion medium is preferably 0.005 to 50% (mass), more preferably 0.01 to 10%, and most preferably 0.01 to 0.5%.
＜アミド化合物とアルコールの混合分散媒＞
アミド化合物およびアルコールは前記のものが使用できる。組み合わせとしてはＮ,Ｎ
−ジメチルホルムアミドとアルコール（特に１−ブタノール、１−ヘキサノール）、Ｎ,
Ｎ−ジメチルアセトアミドとアルコール（特に１−ブタノール、１−ヘキサノール）が好ましい。さらに、この混合分散媒に第三成分を加えても良い。第三成分としてはアミン化合物などが挙げられる。
混合分散媒に対するアルコールの割合は０．００５〜５０％（質量）であることが好ましく、さらに好ましくは０．０１〜１０％、もっとも好ましくは０．０１〜０．５％である。
<Mixed dispersion medium of amide compound and alcohol>
The amide compounds and alcohols described above can be used. N, N as a combination
-Dimethylformamide and alcohol (especially 1-butanol, 1-hexanol), N,
N-dimethylacetamide and alcohol (especially 1-butanol and 1-hexanol) are preferred. Further, a third component may be added to the mixed dispersion medium. Examples of the third component include amine compounds.
The ratio of alcohol to the mixed dispersion medium is preferably 0.005 to 50% (mass), more preferably 0.01 to 10%, and most preferably 0.01 to 0.5%.
＜芳香族化合物とニトリル化合物の混合分散媒＞
芳香族化合物およびニトリル化合物は前記のものが使用できる。さらに、この混合分散媒に第三成分を加えても良い。第三成分としてはアミン化合物などが挙げられる。
混合分散媒に対するニトリル化合物の割合は０．００５〜５０％（質量）であることが好ましく、さらに好ましくは０．０１〜１０％、もっとも好ましくは０．０１〜０．５％である。
<Mixed dispersion medium of aromatic compound and nitrile compound>
The above-mentioned aromatic compounds and nitrile compounds can be used. Further, a third component may be added to the mixed dispersion medium. Examples of the third component include amine compounds.
The ratio of the nitrile compound to the mixed dispersion medium is preferably 0.005 to 50% (mass), more preferably 0.01 to 10%, and most preferably 0.01 to 0.5%.
＜多価アルコール誘導体とアミン化合物の混合分散媒＞
多価アルコール誘導体およびアミン化合物は前記のものが使用できる。組み合わせとしてはジエチレングリコールジメチルエーテルとアミン化合物（特にモノエタノールアミン、ジエタノールアミン、トリエタノールアミンなど水酸基を有するもの）が好ましい。さらに、この混合分散媒に第三成分を加えても良い。
<Mixed dispersion medium of polyhydric alcohol derivative and amine compound>
As the polyhydric alcohol derivative and the amine compound, those described above can be used. As a combination, diethylene glycol dimethyl ether and an amine compound (especially those having a hydroxyl group such as monoethanolamine, diethanolamine, triethanolamine) are preferable. Further, a third component may be added to the mixed dispersion medium.
混合分散媒に対するアミン化合物の割合が０．００５〜５０％（質量）であることが好ましく、さらに好ましくは０．０１〜１０％、さらに好ましくは０．０１〜５％である。
本発明に係る酸化カルシウム分散液は分散剤が添加されていると、流動性や安定性が更に向上するため、分散粒径を更に小さくする事が出来るためにより好ましい。添加する分散剤には特に制限は無いが、ノニオン系界面活性剤が好適に使用され、これらの化合物の中でも特に水酸基を有するものが好ましい。
The ratio of the amine compound to the mixed dispersion medium is preferably 0.005 to 50% (mass), more preferably 0.01 to 10%, and still more preferably 0.01 to 5%.
The calcium oxide dispersion according to the present invention is more preferably added with a dispersant because the fluidity and stability are further improved, and the dispersed particle size can be further reduced. Although there is no restriction | limiting in particular in the dispersing agent to add, Nonionic surfactant is used suitably and the thing which has a hydroxyl group especially among these compounds is preferable.
ノニオン系界面活性剤としては、例えばポリオキシエチレンアルキルエーテル、ポリオキシエチレン２級アルコールエーテル、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレン、ポリオキシプロピレンブロックコポリマー、ポリオキシエチレンポリオキシプロピレンアルキルエーテル、ポリプロピレンオキシド付加グリセリンなどのエーテル型の界面活性剤や、ポリオキシエチレングリセリン脂肪酸エステル、ポリオキシエチレンヒマシ油および硬化ヒマシ油、ポリオキシエチレンソルビタン脂肪酸エステルなどのエステルエーテル型の界面活性剤などが挙げられる。これらの中で特に好ましくはポリプロピレンオキシド付加グリセリンが挙げられる。 Nonionic surfactants include, for example, polyoxyethylene alkyl ether, polyoxyethylene secondary alcohol ether, polyoxyethylene alkylphenyl ether, polyoxyethylene, polyoxypropylene block copolymer, polyoxyethylene polyoxypropylene alkyl ether, polypropylene Examples include ether type surfactants such as oxide-added glycerin, and ester ether type surfactants such as polyoxyethylene glycerin fatty acid ester, polyoxyethylene castor oil and hydrogenated castor oil, and polyoxyethylene sorbitan fatty acid ester. Of these, polypropylene oxide-added glycerin is particularly preferable.
添加する量は選択する化合物に依存するが、酸化カルシウムに対して０．１〜１０質量％の範囲で調整することが好ましい。
分散剤はビーズミルで酸化カルシウムを分散媒に分散させる前の分散媒に添加しても良いし、ビーズミルで分散させた後の分散液に添加しても良いが、ビーズミルで分散させる前に添加した方が更に流動性や安定性が向上するために好ましい。
The amount to be added depends on the compound to be selected, but is preferably adjusted in the range of 0.1 to 10% by mass with respect to calcium oxide.
The dispersant may be added to the dispersion medium before the calcium oxide is dispersed in the dispersion medium by the bead mill, or may be added to the dispersion liquid after being dispersed by the bead mill, but is added before being dispersed by the bead mill. This is preferable because the fluidity and stability are further improved.
本発明で原料として用いられる有機分散媒は、水分量が少ないことが好ましく、酸化カルシウムと混合する前の水分量は通常１，０００ｐｐｍ（質量）未満、好ましくは５００ｐｐｍ、より好ましくは１００ｐｐｍ（質量）、さらに好ましくは１０ｐｐｍ（質量）、特に好ましくは５ｐｐｍ（質量）未満である。水分量が上記範囲にあると、酸化カルシウム分散液は、水酸化カルシウム分量が増加することがなく、着色や増粘の問題が発生することがないため好ましい。このような水分量が少ない有機分散媒は、モレキュラーシーブや酸化カルシウムで脱水することにより得ることができる。 The organic dispersion medium used as a raw material in the present invention preferably has a small amount of water, and the amount of water before mixing with calcium oxide is usually less than 1,000 ppm (mass), preferably 500 ppm, more preferably 100 ppm (mass). More preferably, it is less than 10 ppm (mass), particularly preferably less than 5 ppm (mass). When the water content is in the above range, the calcium oxide dispersion is preferable because the calcium hydroxide content does not increase and the problem of coloring and thickening does not occur. Such an organic dispersion medium having a small amount of water can be obtained by dehydration with molecular sieve or calcium oxide.
なお、有機分散媒の水分含量は、カール・フィッシャー法による電量滴定式水分測定装置、例えば三菱化学社製ＣＡ−０６を用いて測定される。
本発明に係る酸化カルシウム分散液は、酸化カルシウムの濃度が好ましくは１０〜５０質量％、さらに好ましくは２０〜５０質量％、より好ましくは２５〜５０質量％、もっとも好ましくは３０〜５０質量％である。酸化カルシウムの濃度が上記範囲より小さいと、吸湿効果を得るための酸化カルシウムを準備するのに大量の分散媒が必要となる。また、
上記範囲より大きいと、分散液の粘度が上昇し取り扱いが困難になる。
分散液中の酸化カルシウムの濃度は、分散液の調製時には仕込み量から計算することができ、分散液を調製した後は以下の（ａ）、（ｂ）の方法などにより確認することができる。
In addition, the water content of the organic dispersion medium is measured using a coulometric titration-type water measuring device by the Karl Fischer method, for example, CA-06 manufactured by Mitsubishi Chemical Corporation.
In the calcium oxide dispersion according to the present invention, the concentration of calcium oxide is preferably 10 to 50% by mass, more preferably 20 to 50% by mass, more preferably 25 to 50% by mass, and most preferably 30 to 50% by mass. is there. When the concentration of calcium oxide is smaller than the above range, a large amount of dispersion medium is required to prepare calcium oxide for obtaining a hygroscopic effect. Also,
When it is larger than the above range, the viscosity of the dispersion increases and handling becomes difficult.
The concentration of calcium oxide in the dispersion can be calculated from the charged amount when the dispersion is prepared, and can be confirmed by the following methods (a) and (b) after the dispersion is prepared.
（ａ）例えば、減圧下ロータリーエバポレーターで分散媒を留去、分散液を大気雰囲気下で２００℃まで加熱、などの方法により、分散液から分散媒を除去する。次に、得られた残渣を、塩酸、硫酸などの酸で溶解し純水で希釈した後、原子吸光測定装置（例えば、セイコーインスツルメンツ社製 原子吸光分光光度計ＳＡＳ−７５００Ａ）やＩＣＰ測定装置（例えば、セイコーインスツルメンツ社製 ＩＣＰ質量分析装置ＳＰＱ−９０００）でカルシウム濃度を測定し、分散液の酸化カルシウム濃度を計算により求める。 (A) For example, the dispersion medium is removed from the dispersion liquid by a method such as distilling off the dispersion medium with a rotary evaporator under reduced pressure and heating the dispersion liquid to 200 ° C. in an air atmosphere. Next, the obtained residue is dissolved in an acid such as hydrochloric acid or sulfuric acid and diluted with pure water, and then an atomic absorption measurement apparatus (for example, atomic absorption spectrophotometer SAS-7500A manufactured by Seiko Instruments Inc.) or an ICP measurement apparatus ( For example, the calcium concentration is measured with an Seiko Instruments ICP mass spectrometer SPQ-9000), and the calcium oxide concentration of the dispersion is calculated.
（ｂ）上記（ａ）法と同様にして、分散液から分散媒を除去する。次に、熱天秤装置（例えば、セイコーインスツルメンツ社製 ＴＧ／ＤＴＡ６２００型）で大気圧下１０００℃まで昇温し、残渣である酸化カルシウムの重量を測定し、分散液の酸化カルシウム濃度を計算する。 (B) The dispersion medium is removed from the dispersion in the same manner as in the method (a). Next, the temperature is raised to 1000 ° C. under atmospheric pressure using a thermobalance device (for example, TG / DTA6200 type manufactured by Seiko Instruments Inc.), the weight of calcium oxide as a residue is measured, and the calcium oxide concentration of the dispersion is calculated.
本発明に係る酸化カルシウム分散液は、酸化カルシウム微粒子の水酸化カルシウムの含有量が５質量％未満、好ましくは１質量％未満であり、炭酸カルシウムの含有量が１質量％未満、好ましくは０．５質量％未満である。水酸化カルシウムの含有量および炭酸カルシウムの含有量が上記範囲内にあると、脱水性の面で不活性物である水酸化カルシウム、炭酸カルシウムをほとんど含まないので、吸湿材、脱水剤としての性能が優れる。 In the calcium oxide dispersion according to the present invention, the content of calcium hydroxide in the calcium oxide fine particles is less than 5% by mass, preferably less than 1% by mass, and the content of calcium carbonate is less than 1% by mass, preferably 0.8%. It is less than 5% by mass. When the calcium hydroxide content and calcium carbonate content are within the above ranges, it contains almost no calcium hydroxide and calcium carbonate, which are inert in terms of dehydration, so it can be used as a hygroscopic material and dehydrating agent. Is excellent.
水酸化カルシウムおよび炭酸カルシウムの含有量は、熱天秤装置により測定される。３００℃前後で現れる水酸化カルシウムの脱水による重量減少から水酸化カルシウム量を計算し、７００℃前後で現れる炭酸カルシウムの脱炭酸による重量減少から炭酸カルシウム量を計算する。
分散媒の粘度は、高濃度の微粒子酸化カルシウム分散液を製造するには小さい方が良く、３．０ｍＰａ・ｓ（２０℃）以下が好ましく、１．０ｍＰａ・ｓ（２０℃）以下がより好ましい。なお、混合分散媒である場合には、混合分散媒の粘度が上記範囲であることが好ましい。
The content of calcium hydroxide and calcium carbonate is measured by a thermobalance device. The amount of calcium hydroxide is calculated from the weight reduction due to dehydration of calcium hydroxide appearing around 300 ° C., and the amount of calcium carbonate is calculated from the weight reduction due to decarboxylation of calcium carbonate appearing around 700 ° C.
The viscosity of the dispersion medium is preferably small for producing a high-concentration fine particle calcium oxide dispersion, preferably 3.0 mPa · s (20 ° C.) or less, more preferably 1.0 mPa · s (20 ° C.) or less. . In the case of a mixed dispersion medium, the viscosity of the mixed dispersion medium is preferably in the above range.
［酸化カルシウム分散液の製造方法］
通常、ミクロンサイズ以上の酸化カルシウム粒子をさらに粉砕し、メジアン粒子径を２００ｎｍ以下にすることは困難である。そこで、分散媒に分散させる前の酸化カルシウムのメジアン粒子径は２００ｎｍ以下であることが好ましい。
[Method for producing calcium oxide dispersion]
Usually, it is difficult to further pulverize calcium oxide particles of micron size or more and to reduce the median particle diameter to 200 nm or less. Therefore, the median particle diameter of calcium oxide before being dispersed in the dispersion medium is preferably 200 nm or less.
このような粒子径の酸化カルシウム微粒子は例えば、まずカルシウムとβ−ジケトン化合物との錯体（β−ジケトン／カルシウム錯体）、カルシウムアルコキシドなどのカルシウム錯体を気化させ、次にこの気体状のカルシウム錯体を酸化性物質の存在下で燃焼させることにより酸化カルシウム微粒子を得ることができる。 For example, the calcium oxide fine particles having such a particle size first vaporize a calcium complex such as a complex of calcium and a β-diketone compound (β-diketone / calcium complex) or calcium alkoxide, and then convert the gaseous calcium complex to Calcium oxide fine particles can be obtained by burning in the presence of an oxidizing substance.
また、酸化カルシウム微粒子は、β−ジケトン／カルシウム錯体の溶液（アルコールなどを溶媒とする）を気化させ、気体状のβ−ジケトン／カルシウム錯体を含む蒸気と、気体状の酸化性物質（空気など）とを混合し、得られた混合物を加熱して該気体状のβ−ジケトン／カルシウム錯体を燃焼させて得ることもできる。 Further, the calcium oxide fine particles vaporize a solution of β-diketone / calcium complex (using alcohol or the like as a solvent), vapor containing a gaseous β-diketone / calcium complex, and a gaseous oxidizing substance (such as air). And the resulting mixture is heated to burn the gaseous β-diketone / calcium complex.
本発明で用いられるβ−ジケトン／カルシウム錯体としては、２,２,６,６−テトラメ
チルヘプタン−３,５−ジオン（ＤＰＭ・Ｈ）、２,６−ジメチル−３,５−ヘプタンジオ
ン（ＤＭＨＤ・Ｈ）または２,４−ペンタンジオン（ａｃａｃ・Ｈ）のカルシウム錯体が
好ましく、具体的には例えばＣａ(ＤＰＭ)2、Ｃａ(ＤＭＨＤ)2、Ｃａ(ａｃａｃ)2および
これらのｎ水塩（ｎは１以上の数）が挙げられる。なお、ａｃａｃ等はａｃａｃ・Ｈ等からＨ+が脱離して配位子となった状態を示す。
As the β-diketone / calcium complex used in the present invention, 2,2,6,6-tetramethylheptane-3,5-dione (DPM · H), 2,6-dimethyl-3,5-heptanedione ( DMHD · H) or a calcium complex of 2,4-pentanedione (acac · H), such as Ca (DPM) 2 , Ca (DMHD) 2 , Ca (acac) 2 and their n-hydrates. (N is a number of 1 or more). Acac and the like indicate a state where H + is eliminated from acac · H and the like to form a ligand.
本発明で用いられるカルシウムアルコキシドとしては、カルシウムのメトキシド、エトキシド、ｎ−プロポキシド、ｉ−プロポキシド、ｎ−ブトキシド、ｓｅｃ−ブトキシド、ｔｅｒｔ−ブトキシド、ｔ−アミロキシドなどが好ましく、具体的には例えばジメトキシカルシウム、ジエトキシカルシウム、ジ−ｉ−プロポキシカルシウム等が挙げられる。
これらのカルシウム錯体は、２種以上組み合わせて用いることもできる。
As the calcium alkoxide used in the present invention, calcium methoxide, ethoxide, n-propoxide, i-propoxide, n-butoxide, sec-butoxide, tert-butoxide, t-amyloxide and the like are preferable. Examples include dimethoxy calcium, diethoxy calcium, di-i-propoxy calcium and the like.
These calcium complexes can be used in combination of two or more.
気体状のカルシウム錯体としては、固体または液体状のカルシウム錯体を加熱して気化させたもの、カルシウム錯体の溶液を加熱して気化させたもの、これらの混合物などが挙げられる。 Examples of the gaseous calcium complex include those obtained by heating and vaporizing a solid or liquid calcium complex, those obtained by heating and vaporizing a calcium complex solution, and mixtures thereof.
気体状のカルシウム錯体は、１種のカルシウム錯体の蒸気であっても、２種以上のカルシウム錯体の混合蒸気であってもよい。２種以上のカルシウム錯体の混合蒸気は、２種以上のカルシウム錯体を混合してから気化させたものでもよいし、気化させてから混合したものでも良い。 The gaseous calcium complex may be a vapor of one kind of calcium complex or a mixed vapor of two or more kinds of calcium complexes. The mixed vapor of two or more calcium complexes may be vaporized after mixing two or more calcium complexes, or may be mixed after vaporization.
カルシウム錯体としてアルコキシドを使用する場合は、アルコキシドが加水分解することがあるため、気化前に分解して収率が低くなったり、配管が閉塞したりするなどの問題が発生する場合がある。したがって、アルコキシドを有機溶媒の溶液として安定化させて気化することも好ましい。 When an alkoxide is used as the calcium complex, the alkoxide may be hydrolyzed, so that problems such as decomposition before vaporization and a decrease in yield and blockage of piping may occur. Therefore, it is also preferable to stabilize and vaporize the alkoxide as an organic solvent solution.
気体状のカルシウム錯体が、カルシウム錯体の溶液を加熱して気化させたものである場合には、１種のカルシウム錯体の蒸気を含むものであっても、２種以上のカルシウム錯体の蒸気を含むものであってもよい。２種以上のカルシウム錯体の蒸気を含む場合には、異なるカルシウム錯体を含む２以上の溶液から気化させたものを混合したものであってもよいし、２種以上のカルシウム錯体を含む溶液から気化させたものであってもよい。 When the gaseous calcium complex is obtained by heating and vaporizing a calcium complex solution, it contains two or more calcium complex vapors, even if it contains one calcium complex vapor. It may be a thing. In the case of containing two or more kinds of calcium complex vapors, it may be a mixture of two or more solutions containing different calcium complexes, or may be vaporized from a solution containing two or more kinds of calcium complexes. It may be made.
ここでカルシウム錯体の溶液に用いられる溶媒としては、メチルアルコール、エチルアルコール、プロピルアルコール、ブチルアルコール、テトラヒドロフラン、ジメチルスルホキサイド、ジメチルホルムアミド、ヘキサン、シクロヘキサン、メチルシクロヘキサン、ジオキサン、アセトン、酢酸エチル、酢酸ブチル、メチルイソブチリルケトン、ジエチルエーテル、ｔ−ブチルメチルエーテル、アセチルアセトン、ジイソブチリルメタン、ジピバロイルメタンなどから選ばれる少なくとも１種の溶媒が挙げられる。これらの溶媒は、１種単独で、または２種以上組み合わせて用いることができる。また、溶液の濃度は特に限定されない。 Solvents used in the calcium complex solution are methyl alcohol, ethyl alcohol, propyl alcohol, butyl alcohol, tetrahydrofuran, dimethyl sulfoxide, dimethylformamide, hexane, cyclohexane, methylcyclohexane, dioxane, acetone, ethyl acetate, acetic acid. Examples thereof include at least one solvent selected from butyl, methyl isobutyryl ketone, diethyl ether, t-butyl methyl ether, acetylacetone, diisobutyrylmethane, dipivaloylmethane, and the like. These solvents can be used alone or in combination of two or more. Further, the concentration of the solution is not particularly limited.
本発明では、気体状のカルシウム錯体のキャリアとして、窒素、アルゴンなどの不活性ガスを用いることができる。
本発明で用いられる酸化性物質としては、酸素、酸素と他の気体、例えば窒素、アルゴンなど不活性ガスとを任意の割合で混合した混合ガス、空気、水、亜酸化窒素などが挙げられる。これら酸化性物質は単独で使用しても２種類以上を組み合わせて使用しても良い。
In the present invention, an inert gas such as nitrogen or argon can be used as a carrier for the gaseous calcium complex.
Examples of the oxidizing substance used in the present invention include oxygen, a mixed gas obtained by mixing oxygen and an inert gas such as nitrogen and argon at an arbitrary ratio, air, water, nitrous oxide, and the like. These oxidizing substances may be used alone or in combination of two or more.
気体状のカルシウム錯体と酸化性物質とは、カルシウム錯体を燃焼させる前に、それぞれカルシウム錯体が分解する温度未満の温度に予熱してもよいし、気体状のカルシウム錯体と酸化性物質とを混合した後に、カルシウム錯体が分解する温度未満の温度に予熱してもよい。また、気体状のカルシウム錯体と酸化性物質とは、燃焼させる前に混合してもよ
いし、気体状のカルシウム錯体をカルシウム錯体が分解する温度以上の温度に加熱した後、酸化性物質中に放出して、酸化性物質と混合しながら燃焼させてもよい。また、カルシウム錯体が液体状のもの、あるいは有機溶媒に溶解した溶液状のものである場合は液体状のまま酸化性物質と混合しても良い。
The gaseous calcium complex and the oxidizing substance may be preheated to a temperature below the temperature at which the calcium complex decomposes before the calcium complex is burned, or the gaseous calcium complex and the oxidizing substance are mixed. Then, it may be preheated to a temperature below the temperature at which the calcium complex decomposes. Further, the gaseous calcium complex and the oxidizing substance may be mixed before burning, or after heating the gaseous calcium complex to a temperature higher than the temperature at which the calcium complex decomposes, It may be released and burned with mixing with an oxidizing substance. Further, when the calcium complex is in a liquid form or in a solution form dissolved in an organic solvent, it may be mixed with an oxidizing substance while remaining in a liquid form.
カルシウム錯体と酸化性物質の混合は、完全混合状態になるような条件で混合するのが望ましい。
気体状のカルシウム錯体と酸化性物質とは、混合した後燃焼させることが好ましい。燃焼させるには、着火源を用いてもよいし、発火点以上の温度に加熱してもよい。
It is desirable that the calcium complex and the oxidizing substance are mixed under conditions such that they are in a completely mixed state.
The gaseous calcium complex and the oxidizing substance are preferably mixed and then burned. In order to burn, an ignition source may be used, or it may be heated to a temperature above the ignition point.
混合が不十分でカルシウム錯体が完全に燃焼しない場合は、炭化物や水分等の未反応物の残存や、反応時間の長時間化による微粒子の融着などが生じる為、品質や粒径が安定せず、得られる粒子径も概して大きくなるという問題がある。 If mixing is insufficient and the calcium complex does not burn completely, unreacted substances such as carbides and moisture remain, and fusion of fine particles due to longer reaction time may occur, resulting in stable quality and particle size. In addition, there is a problem that the particle size obtained is generally large.
気体状のカルシウム錯体またはカルシウム錯体を溶解した溶液を気化したものを酸化性物質と混合したあとの混合気体は、カルシウム錯体の濃度が爆発範囲に入っていることが好ましい。範囲外の場合は燃焼が安定せず、好ましくない。カルシウム錯体の蒸気圧が低く、爆発範囲に到達しない場合には助燃剤を使用することが好ましい。助燃剤に特に制限は無いが、例えばカルシウム錯体を溶解した溶液を使用する場合は、この溶液の溶媒を助燃剤とすることが出来る。 It is preferable that the concentration of the calcium complex is in the explosive range in the mixed gas after mixing the gaseous calcium complex or the vaporized solution of the calcium complex with the oxidizing substance. When it is out of the range, combustion is not stable, which is not preferable. When the vapor pressure of the calcium complex is low and the explosive range is not reached, it is preferable to use a combustion aid. Although there is no restriction | limiting in particular in a combustor, For example, when using the solution which melt | dissolved the calcium complex, the solvent of this solution can be used as a combustor.
酸化性物質は、カルシウム錯体として固体または液体状のカルシウム錯体を加熱して気化させたものを用いる場合にはカルシウム錯体を完全酸化するのに必要な酸素量、気体状のカルシウム錯体としてカルシウム錯体の溶液を加熱して気化させたものを用いる場合には、カルシウム錯体および溶媒を完全酸化するのに必要な酸素量の０．５倍〜４０倍モル、好ましくは１〜３０倍モル、より好ましくは１〜２０倍モルとなる量で用いられる。酸素量が少なすぎると未反応の原料により生成した酸化カルシウム微粒子が凝集する場合がある。多すぎると有機物濃度が爆発限界以下となり燃焼が安定せず好ましくない。 In the case of using an oxidized substance obtained by heating and vaporizing a solid or liquid calcium complex as the calcium complex, the amount of oxygen necessary to completely oxidize the calcium complex, and the calcium complex as a gaseous calcium complex. When using a solution vaporized by heating, 0.5 to 40 times mol, preferably 1 to 30 times mol of oxygen necessary for complete oxidation of the calcium complex and the solvent, more preferably It is used in an amount of 1 to 20 moles. If the amount of oxygen is too small, calcium oxide fine particles generated from unreacted raw materials may aggregate. If the amount is too large, the concentration of organic substances is below the explosion limit, and combustion is not stable, which is not preferable.
本発明における燃焼温度は４００℃以上が好ましく、特に５００〜１５００℃の範囲が好ましい。燃焼温度が低い場合は未反応原料や不完全燃焼による有機成分の残存などが有り好ましくない。燃焼温度が高すぎる場合は装置材質の劣化による装置寿命の低下やコンタミネーションなどの問題があり好ましくない。 The combustion temperature in the present invention is preferably 400 ° C. or higher, and particularly preferably in the range of 500 to 1500 ° C. When the combustion temperature is low, there are unreacted raw materials and residual organic components due to incomplete combustion. If the combustion temperature is too high, there are problems such as a reduction in device life due to deterioration of the device material and contamination, which is not preferable.
このようにして得られる酸化カルシウム微粒子のメジアン粒径（体積基準）は１〜２００ｎｍである。
上述したような方法で酸化カルシウム微粒子を製造するより具体的な方法としては、例えば図１に示すような装置で行う方法がある。図１は、本発明で用いられる酸化カルシウム微粒子の製造方法に用いられる製造装置の一例を示す説明図である。
The median particle size (volume basis) of the calcium oxide fine particles thus obtained is 1 to 200 nm.
As a more specific method for producing the calcium oxide fine particles by the method as described above, for example, there is a method using an apparatus as shown in FIG. FIG. 1 is an explanatory view showing an example of a production apparatus used in the method for producing calcium oxide fine particles used in the present invention.
β−ジケトン／カルシウム錯体の溶液２は、定量ポンプ４を通じて定量的に加熱気化器６に供給され、ここで気化される。また、加熱気化器６で気化された気体状のβ−ジケトン／カルシウム錯体を含む蒸気は、キャリアガスがマスフローコントローラ４を通じて定量的に加熱気化器６に供給されることにより、定量的に管状加熱炉７入り口の同軸ノズルに供給される。酸化性物質（空気など）１は、マスフローコントローラ３を通じて定量的に予熱器５に供給され、予熱された酸化性物質１は、定量的に管状加熱炉７入り口の同軸ノズルに供給される。この同軸ノズルから供給された、気化したβ−ジケトン／カルシウム錯体と酸化性物質は管状加熱炉７内で急激に混合され、燃焼（酸化反応）して、酸化カルシウムの微粒子となる。生成した酸化カルシウムの微粒子は、捕集器８で捕集される。 The β-diketone / calcium complex solution 2 is quantitatively supplied to the heating vaporizer 6 through the metering pump 4 and vaporized there. Further, the vapor containing the gaseous β-diketone / calcium complex vaporized by the heating vaporizer 6 is quantitatively heated by supplying the carrier gas quantitatively to the heating vaporizer 6 through the mass flow controller 4. It is supplied to the coaxial nozzle at the entrance of the furnace 7. The oxidizing substance (air etc.) 1 is quantitatively supplied to the preheater 5 through the mass flow controller 3, and the preheated oxidizing substance 1 is quantitatively supplied to the coaxial nozzle at the entrance of the tubular heating furnace 7. The vaporized β-diketone / calcium complex and the oxidizing substance supplied from the coaxial nozzle are rapidly mixed in the tubular heating furnace 7 and burned (oxidation reaction) to form calcium oxide fine particles. The generated calcium oxide fine particles are collected by the collector 8.
このカルシウム酸化物の微粒子は、通常不純物として水酸化カルシウム（（Ｃａ(ＯＨ)2）や炭酸カルシウム（ＣａＣＯ3）を含有する。そのため、これらの不純物を酸化カルシウムに変換するため、５００℃以上１０００℃以下の条件で焼成処理を行うことが好ましい。なお、本発明では、酸化カルシウムの微粒子に含有されるＣａ(ＯＨ)2、ＣａＣＯ3をＣａＯに変換する処理を焼成処理という。 The calcium oxide fine particles usually contain calcium hydroxide ((Ca (OH) 2 ) or calcium carbonate (CaCO 3 ) as impurities, and therefore, in order to convert these impurities into calcium oxide, 500 ° C. or more and 1000 ° C. It is preferable to perform the baking treatment at a temperature not higher than ° C. In the present invention, the treatment for converting Ca (OH) 2 and CaCO 3 contained in the fine particles of calcium oxide into CaO is referred to as a baking treatment.
なお、酸化カルシウムは非常に吸湿性が高いため、上記の操作中に、わずかな水分などにより、酸化カルシウム（ＣａＯ）が水酸化カルシウム（Ｃａ(ＯＨ)2）や炭酸カルシウ
ム（ＣａＣＯ3）となり、酸化カルシウムの不純物となることがある。このため生成した
酸化カルシウムの微粒子の取り出し等の操作は、水分の非常に少ない雰囲気下（例えば乾燥窒素のグローブボックス内）、例えば水分含量が１０ｐｐｍ（ｍｏｌ）以下の雰囲気で行うことが好ましい。
In addition, since calcium oxide is very hygroscopic, calcium oxide (CaO) becomes calcium hydroxide (Ca (OH) 2 ) or calcium carbonate (CaCO 3 ) due to a slight amount of moisture during the above operation. May become an impurity of calcium oxide. For this reason, it is preferable to perform operations such as taking out the generated calcium oxide fine particles in an atmosphere with a very low moisture content (for example, in a dry nitrogen glove box), for example, in an atmosphere having a moisture content of 10 ppm (mol) or less.
本発明に係る酸化カルシウム分散液は、上記の方法により製造した酸化カルシウムの微粒を上記有機分散媒に分散することにより調製することができる。
なお、上記の方法で得られた酸化カルシウム微粒子は一次粒子が凝集していることがある。この凝集体の解砕には、ビーズミルやジェットミル用いる方法等多種ある。しかし、ナノ粒子の解砕を行うためは、ビーズミルが好ましい。使用するビーズのサイズは、微小であるほど解砕の分散速度の向上と到達粒径の低下が可能なので、直径が５〜２００μｍ、特に１０〜１００μｍのビーズを使用するのが特に好ましい。また、ビーズの素材は、耐摩耗性、酸化カルシウムへの不純物の混入を最小限とする等の観点からジルコニア製であることが好ましい。
The calcium oxide dispersion according to the present invention can be prepared by dispersing calcium oxide fine particles produced by the above method in the organic dispersion medium.
Note that the primary particles of the calcium oxide fine particles obtained by the above method may be aggregated. There are various methods such as a method using a bead mill or a jet mill for crushing the aggregate. However, a bead mill is preferred for crushing the nanoparticles. The smaller the bead size used, the higher the dispersal rate of crushing and the lowering of the final particle size, so it is particularly preferable to use beads having a diameter of 5 to 200 μm, particularly 10 to 100 μm. Further, the material of the beads is preferably made of zirconia from the viewpoints of wear resistance and minimizing the mixing of impurities into calcium oxide.
この解砕操作時に、有機分散媒を加えておくと、凝集体の解砕と同時に分散液を製造することができる。
ビーズミルを用いて解砕と同時に分散液を製造する方法として具体的には、上述した方法により製造した酸化カルシウムの微粒子と上記有機分散媒と上記ビーズとを容器に充填し、これらを攪拌する。このときのビーズの充填率は、好ましくは８５〜９５％であり、酸化カルシウムの微粒子は、酸化カルシウムの微粒子と有機分散媒との合計量を１００質量％としたときに、好ましくは１〜５０質量％となるような量で使用する。また、攪拌時間は所望するメジアン粒径により適宜決定されるが、通常１０分〜５時間程度である。
If an organic dispersion medium is added during the crushing operation, a dispersion can be produced simultaneously with the crushing of the aggregates.
Specifically, as a method of producing a dispersion simultaneously with crushing using a bead mill, a container is filled with the fine particles of calcium oxide produced by the method described above, the organic dispersion medium, and the beads, and these are stirred. The filling rate of the beads at this time is preferably 85 to 95%, and the calcium oxide fine particles are preferably 1 to 50 when the total amount of the calcium oxide fine particles and the organic dispersion medium is 100% by mass. Use in such an amount that the mass%. The stirring time is appropriately determined depending on the desired median particle size, but is usually about 10 minutes to 5 hours.
解砕、分散操作時の雰囲気は、酸化カルシウムが気相からの吸湿するのを抑制するため、不活性ガス雰囲気が好ましい。不活性ガスとしては、例えばヘリウム、アルゴン等の希ガスや、窒素などが挙げられる。使用する不活性ガスの水分量は１０ｐｐｍ（ｍｏｌ）以下が好ましい。水分量が多い場合、分散処理中に分散液が吸湿し、水酸化カルシウムの増加、粘度上昇、着色等の問題があり好ましくない。
また、ビーズミルを用いて解砕と同時に分散液を製造する際に、プレ分散として、超音波や自転公転ミキサーなどで分散液に酸化カルシウムを予め分散しておいても良い。
The atmosphere during the crushing and dispersing operation is preferably an inert gas atmosphere in order to prevent calcium oxide from absorbing moisture from the gas phase. Examples of the inert gas include noble gases such as helium and argon, and nitrogen. The water content of the inert gas used is preferably 10 ppm (mol) or less. When the amount of water is large, the dispersion liquid absorbs moisture during the dispersion treatment, and there are problems such as an increase in calcium hydroxide, an increase in viscosity, and coloring.
Moreover, when manufacturing a dispersion simultaneously with crushing using a bead mill, you may disperse | distribute calcium oxide to a dispersion liquid beforehand as a pre-dispersion with an ultrasonic wave, a rotation revolution mixer, etc.
上述した方法により酸化カルシウム微粒が均一に分散された分散液が得られる。なお、本発明において「酸化カルシウム微粒が均一に分散された分散液」とは、後述する分散液の流動性および安定性の試験において評価がいずれも「○」であるものをいう。 By the method described above, a dispersion liquid in which calcium oxide fine particles are uniformly dispersed is obtained. In the present invention, the “dispersion in which calcium oxide fine particles are uniformly dispersed” means that the evaluation is “◯” in the fluidity and stability tests of the dispersion described later.
［実施例］
以下、実施例に基づいて本発明をさらに具体的に説明するが、本発明はこれら実施例に限定されるものではない。
[Example]
EXAMPLES Hereinafter, although this invention is demonstrated further more concretely based on an Example, this invention is not limited to these Examples.
＜分析方法＞
＜メジアン粒径、最大粒径＞
粒度分布計：日機装社製、Ｍｉｃｒｏｔｒａｃ ＵＰＡ−１５０型を用いて測定した。
<Analysis method>
<Median particle size, maximum particle size>
Particle size distribution meter: Measured using a Microtrac UPA-150 model manufactured by Nikkiso Co., Ltd.
測定条件 溶媒：分散媒に用いた溶媒で１００倍希釈
＜ＢＥＴ表面積＞
装置社名：ＱＵＡＮＴＡ ＣＨＲＯＭＥ社製 Ｃｈｅｍ ＢＥＴ−３０００
＜水酸化カルシウム、炭酸カルシウム量＞
熱天秤での方法
熱天秤：セイコーインスツルメンツ社製 ＴＧ／ＤＴＡ６２００型
測定温度範囲：３０〜１０００℃ 昇温１０℃／ｍｉｎ
Ｎ2雰囲気、２００ｍｌ／ｍｉｎ
水酸化カルシウム量は、３００℃前後で現れる水酸化カルシウムの脱水による重量減少から計算により求めた。
Measurement conditions Solvent: 100-fold dilution with solvent used as dispersion medium <BET surface area>
Device company name: Chem BET-3000 manufactured by QUANTA CHROME
<Calcium hydroxide and calcium carbonate content>
Method using a thermobalance Thermobalance: TG / DTA6200 type, manufactured by Seiko Instruments Inc. Measurement temperature range: 30 to 1000 ° C Temperature increase 10 ° C / min
N 2 atmosphere, 200 ml / min
The amount of calcium hydroxide was calculated from the weight loss due to dehydration of calcium hydroxide appearing around 300 ° C.
炭酸カルシウム量は、７００℃前後で現れる炭酸カルシウムの脱炭酸による重量減少から計算により求めた。
＜製造例１＞
図１に示すような装置を用いて酸化カルシウム微粒子を製造した。
２５０℃に加熱した気化器（６）にＣａ（ＤＰＭ）2 ３００ｇ（昭和電工製）およびメタノール ７００ｇの混合溶液を４ｍｌ／ｍｉｎの流速で導入、気化した。空気（１）を４
０ｌ／ｍｉｎの量で予熱器（５）へ流し２５０℃に加熱した。気体状のＣａ（ＤＰＭ）2
およびメタノールと、空気とを管状電気炉（７）入り口の同軸ノズルへ供給した。管状電気炉（７）での燃焼温度を９５０℃とした。燃焼時間は１秒であり、供給した空気中の酸素量はＣａ（ＤＰＭ）2およびメタノールを完全酸化するのに必要な酸素量の１．５倍モ
ルの量であった。その結果捕集器（８）に捕集された酸化カルシウム微粒子の収率は９０％であった。得られた酸化カルシウム微粒子のメジアン粒径は３０ｎｍであった。微粒子の写真を図−２に示す。
The amount of calcium carbonate was calculated from the weight loss due to decarboxylation of calcium carbonate that appears at around 700 ° C.
<Production Example 1>
Calcium oxide fine particles were produced using an apparatus as shown in FIG.
A mixed solution of 300 g of Ca (DPM) 2 (manufactured by Showa Denko) and 700 g of methanol was introduced into the vaporizer (6) heated to 250 ° C. at a flow rate of 4 ml / min and vaporized. Air (1) is 4
It was poured into the preheater (5) at an amount of 0 l / min and heated to 250 ° C. Gaseous Ca (DPM) 2
And methanol and air were supplied to the coaxial nozzle at the entrance of the tubular electric furnace (7). The combustion temperature in the tubular electric furnace (7) was 950 ° C. The combustion time was 1 second, and the amount of oxygen in the supplied air was 1.5 times the amount of oxygen necessary for complete oxidation of Ca (DPM) 2 and methanol. As a result, the yield of calcium oxide fine particles collected in the collector (8) was 90%. The obtained calcium oxide fine particles had a median particle size of 30 nm. A photograph of the fine particles is shown in FIG.
得られた微粒子は炭酸カルシウム、水酸化カルシウムを不純物として含有する。これら不純物を除去するため、空気雰囲気下５５０℃、５時間アニール処理したあと、さらに５８０℃、３時間アニール処理した。生成酸化カルシウム粒子はＢＥＴ表面積が２０ｍ2／
ｇであり、これは算術平均粒子径で８８ｎｍに相当する。熱天秤装置（セイコーインスツルメンツ社製 ＴＧ／ＤＴＡ６２００）を用い熱重量測定により水酸化カルシウム、炭酸カルシウムの含量を測定した結果、それぞれ１質量％未満であった。
The obtained fine particles contain calcium carbonate and calcium hydroxide as impurities. In order to remove these impurities, after annealing at 550 ° C. for 5 hours in an air atmosphere, annealing was further performed at 580 ° C. for 3 hours. The generated calcium oxide particles have a BET surface area of 20 m 2 /
g, which corresponds to an arithmetic average particle size of 88 nm. As a result of measuring the content of calcium hydroxide and calcium carbonate by thermogravimetry using a thermobalance device (TG / DTA6200 manufactured by Seiko Instruments Inc.), each was less than 1% by mass.
＜実施例１＞
製造例１で得た酸化カルシウム粒子を５６ｇと水分量９ｐｐｍ（質量）の１−ブタノール５０４ｇを混合し、超音波処理に１時間付し、均一な懸濁液を得た。この懸濁液を、直径５０μｍの酸化ジルコニウムビーズを入れたビーズミル（コトブキ技研製、ＵＡＭ−０１５）で窒素雰囲気下（水分８ｐｐｍ（ｍｏｌ））２時間処理し、１０質量％の酸化カルシウム分散液を得た。粒度分布は１００倍希釈後、粒度分布計で測定し、メジアン粒径８４ｎｍ、最大粒子径４００ｎｍであった。水酸化カルシウム含量は５質量％未満、炭酸カルシウムの含量は１質量％未満であった。
<Example 1>
56 g of calcium oxide particles obtained in Production Example 1 and 504 g of 1-butanol having a water content of 9 ppm (mass) were mixed and subjected to ultrasonic treatment for 1 hour to obtain a uniform suspension. This suspension was treated for 2 hours in a nitrogen atmosphere (moisture 8 ppm (mol)) in a bead mill (manufactured by Kotobuki Giken, UAM-015) containing zirconium oxide beads having a diameter of 50 μm, and a 10 mass% calcium oxide dispersion was obtained. Obtained. The particle size distribution was 100 times diluted and then measured with a particle size distribution meter. The median particle size was 84 nm and the maximum particle size was 400 nm. The calcium hydroxide content was less than 5% by mass, and the calcium carbonate content was less than 1% by mass.
＜比較例１＞
製造例１で得た酸化カルシウム粒子５ｇと水分量８ｐｐｍ（質量）の１−ブタノールを９５ｇを混合し超音波処理に１時間付し、均一な懸濁液を得た。この懸濁液の粒度分布を粒度分布計（日機装製、Ｍｉｃｒｏｔｒａｃ ＵＰＡ−１５０）で測定した結果、メジアン径３４０ｎｍ、最大粒子径１３７０ｎｍであった。
<Comparative Example 1>
5 g of calcium oxide particles obtained in Production Example 1 and 95 g of 1-butanol having a water content of 8 ppm (mass) were mixed and subjected to ultrasonic treatment for 1 hour to obtain a uniform suspension. The particle size distribution of this suspension was measured with a particle size distribution meter (manufactured by Nikkiso, Microtrac UPA-150), and as a result, the median diameter was 340 nm and the maximum particle diameter was 1370 nm.
＜実施例２〜１３＞
分散媒の種類と酸化カルシウム濃度を変更して実施例２〜１３を行った。
製造例１の２回目のアニール処理を７００℃、１時間とした以外は製造例１と同じ方法で製造して得られたＢＥＴ表面積が１８ｍ2／ｇ（算術平均粒子径で１００ｎｍに相当）
の酸化カルシウム粒子と表１に記載の分散媒の合計：３１２ｇを表１に記載の酸化カルシウム濃度となるように混合し、超音波処理に１時間付し、均一な懸濁液を得た。使用した混合分散媒の水分量はいずれも１０００ｐｐｍ以下であった。この懸濁液を、直径５０μｍの酸化ジルコニウムビーズを入れたビーズミルで窒素雰囲気下（水分８ｐｐｍ（ｍｏｌ））２時間処理し、表１に記載の濃度の酸化カルシウム分散液を得た。粒度分布は１００倍希釈後、粒度分布計で測定し、メジアン粒径、最大粒子径の値を得た。水酸化カルシウム含量はいずれも５％未満、炭酸カルシウムの含量は１％未満であった。
分散媒の種類、酸化カルシウム濃度および結果は表１に示した。
<Examples 2 to 13>
Examples 2 to 13 were performed by changing the type of the dispersion medium and the calcium oxide concentration.
A BET surface area of 18 m 2 / g obtained by the same method as in Production Example 1 except that the second annealing treatment in Production Example 1 was performed at 700 ° C. for 1 hour (corresponding to an arithmetic average particle diameter of 100 nm).
312 g of the calcium oxide particles and the dispersion medium described in Table 1 were mixed so as to have the calcium oxide concentration described in Table 1, and subjected to ultrasonic treatment for 1 hour to obtain a uniform suspension. The water content of the mixed dispersion medium used was 1000 ppm or less. This suspension was treated with a bead mill containing zirconium oxide beads having a diameter of 50 μm in a nitrogen atmosphere (water content 8 ppm (mol)) for 2 hours to obtain a calcium oxide dispersion having the concentrations shown in Table 1. The particle size distribution was diluted 100 times and then measured with a particle size distribution meter to obtain median particle size and maximum particle size values. The calcium hydroxide content was less than 5%, and the calcium carbonate content was less than 1%.
The type of dispersion medium, calcium oxide concentration and results are shown in Table 1.
実施例２の分散液を室温下７日間静置した後、再度粒度分布を測定した。その結果、メジアン径９０ｎｍ、最大粒子径４００ｎｍであり、得られた分散液は非常に安定であることがわかった。 After allowing the dispersion of Example 2 to stand at room temperature for 7 days, the particle size distribution was measured again. As a result, it was found that the median diameter was 90 nm and the maximum particle diameter was 400 nm, and the obtained dispersion was very stable.
比較例１に比べ、実施例１〜１３の分散液のメジアン径、最大粒子径は小さくビーズミルによる２次凝集の解砕が起こったと考えられる。
また、分散処理時に窒素雰囲気下とすることで、酸化カルシウムの吸湿が十分に抑えられた。
＜実施例１４＞
ビーズミルで処理する前に、分散媒−２としてジエタノールアミンを０．９ｇ、分散剤として旭電化工業（株）製ＧＬ−１００を３．７ｇ懸濁液に添加した他は実施例１３と同様にして酸化カルシウム分散液を製造したところ、メジアン径６０ｎｍ、最大粒子径２４０ｎｍの値を得た。更にこの分散液を室温下７日間静置した後、再度粒度分布を測定した結果、メジアン径６０ｎｍ、最大粒子径２４０ｎｍと全く値は変化しておらず、得られた分散液は非常に安定であることがわかった。
Compared to Comparative Example 1, the median diameter and the maximum particle diameter of the dispersions of Examples 1 to 13 are small, and it is considered that secondary agglomeration by the bead mill occurred.
Moreover, the moisture absorption of calcium oxide was sufficiently suppressed by setting it as nitrogen atmosphere at the time of a dispersion process.
<Example 14>
Before the treatment with the bead mill, 0.9 g of diethanolamine as dispersion medium-2 and 3.7 g of Asahi Denka Kogyo Co., Ltd. GL-100 were added to the suspension as in the same manner as in Example 13. When a calcium oxide dispersion was produced, a median diameter of 60 nm and a maximum particle diameter of 240 nm were obtained. Further, the dispersion was allowed to stand at room temperature for 7 days, and the particle size distribution was measured again. As a result, the median diameter was 60 nm and the maximum particle diameter was 240 nm, and the obtained dispersion was very stable. I found out.
酸化カルシウム濃度：分散液中の酸化カルシウム濃度を示す。
分散媒−１：分散媒−１の種類と濃度（総分散媒中の分散媒−１の濃度）を示す。
分散媒−２：分散媒−２の種類と濃度（総分散媒中の分散媒−２の濃度）を示す。
Calcium oxide concentration: Indicates the calcium oxide concentration in the dispersion.
Dispersion medium-1: Indicates the type and concentration of dispersion medium-1 (concentration of dispersion medium-1 in the total dispersion medium).
Dispersion medium-2: Indicates the type and concentration of dispersion medium-2 (concentration of dispersion medium-2 in the total dispersion medium).
分散媒略号：ＤＭＦ＝Ｎ,Ｎ−ジメチルホルムアミド
ＤＭＡＣ＝Ｎ,Ｎ−ジメチルアセトアミド
Ｄｉｇｌｙｍｅ＝ジエチレングリコールジメチルエーテル
ＰＧＭＥ＝１−メトキシ−２−プロパノール（プロピレングリコールモノメチルエーテル）
メジアン粒径：分散液中の酸化カルシウムのメジアン粒径（体積基準）を示す。カッコ内は最大粒径を示す。
Dispersion medium abbreviation: DMF = N, N-dimethylformamide
DMAC = N, N-dimethylacetamide
Diglyme = Diethylene glycol dimethyl ether
PGME = 1-methoxy-2-propanol (propylene glycol monomethyl ether)
Median particle size: median particle size (volume basis) of calcium oxide in the dispersion. The maximum particle size is shown in parentheses.
流動性：分散液の流動性を示す。１８０ｍｌ蓋付き透明ガラス容器５０ｍｍφに分散液を５０ｍｌ入れ、素早く９０度倒した際の流動性を観察。測定は室温で行った。
○ … 容器と同時に分散液も倒れる。
△ … 容器を倒した後分散液はゆっくり倒れる。
× … 容器を倒しても分散液は倒れない。
Fluidity: Indicates the fluidity of the dispersion. Put 50ml of dispersion in a transparent glass container 50mmφ with 180ml lid and observe the fluidity when quickly tilted 90 degrees. The measurement was performed at room temperature.
○… The dispersion falls down at the same time as the container.
Δ: The dispersion falls slowly after the container is tilted.
×… The dispersion does not fall even if the container is tilted.
安定性：１８０ｍｌの蓋付き透明ガラス容器５０ｍｍφに分散液を５０ｍｌ入れ、これを１週間室温保管し、分散液を観察。
○ … 変化無し。
△ … 透明な上澄みが観察される。
× … 沈殿が観察される。
Stability: 50 ml of the dispersion was put into a 180 ml transparent glass container with a lid of 50 mmφ and stored at room temperature for 1 week, and the dispersion was observed.
○… No change.
Δ: A transparent supernatant is observed.
×: Precipitation is observed.
１ … 酸化性物質
２ … 溶液
３ … マスフローコントロラー
４ … 定量ポンプ
５ … 予熱器
６ … 気化器
７ … 管状加熱炉
８ … 捕集器
DESCRIPTION OF SYMBOLS 1 ... Oxidizing substance 2 ... Solution 3 ... Mass flow controller 4 ... Metering pump 5 ... Preheater 6 ... Vaporizer 7 ... Tubular heating furnace 8 ... Collector
Claims (22)
ルアセトアミドとアルコール、ジエチレングリコールジメチルエーテルとモノエタノールアミン、ジエチレングリコールジメチルエーテルとジエタノールアミン、ジエチレングリコールジメチルエーテルとトリエタノールアミンの組み合わせのいずれかであることを特徴とする請求項１２に記載の酸化カルシウム分散液。 The mixed dispersion medium is any combination of toluene and alcohol, butyl acetate and alcohol, N, N-dimethylacetamide and alcohol, diethylene glycol dimethyl ether and monoethanolamine, diethylene glycol dimethyl ether and diethanolamine, diethylene glycol dimethyl ether and triethanolamine. The calcium oxide dispersion according to claim 12.
する請求項１５に記載の酸化カルシウム分散液。 The calcium oxide dispersion according to claim 15, wherein the dispersant is one or more compounds selected from nonionic surfactants.
とする請求項２０または２１に記載の酸化カルシウム分散液の製造方法。 The method for producing a calcium oxide dispersion according to claim 20 or 21, wherein the water content of the organic dispersion medium filled in the container is less than 1,000 ppm (mass).