JP2006106235A - Method and apparatus for manufacturing toner - Google Patents
Method and apparatus for manufacturing toner Download PDFInfo
- Publication number
- JP2006106235A JP2006106235A JP2004290948A JP2004290948A JP2006106235A JP 2006106235 A JP2006106235 A JP 2006106235A JP 2004290948 A JP2004290948 A JP 2004290948A JP 2004290948 A JP2004290948 A JP 2004290948A JP 2006106235 A JP2006106235 A JP 2006106235A
- Authority
- JP
- Japan
- Prior art keywords
- toner
- raw material
- toner raw
- melt
- cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、複数の成分が溶融混合されたトナー原料からトナー粒子を作製するトナーの製造方法、及び、当該トナーの製造方法を実施するためのトナーの製造装置に関する。 The present invention relates to a toner production method for producing toner particles from a toner raw material in which a plurality of components are melt-mixed, and a toner production apparatus for carrying out the toner production method.
トナーの製造方法として、一般的に、溶融混練機等を用いて、先ずバインダ樹脂、着色剤（顔料、染料）、ワックス等の複数の成分からなるトナー原料を各成分が均一に分散するように溶融混合させ、その後冷却されたトナー原料の混合物を機械的な粉砕手段を用い、粗粉砕及び微粉砕により所望の粒度のトナー粒子に粉砕する方法が実施されている。
この従来のトナー製造方法において、溶融混合物が混練機外に吐き出された後、比較的短い時間（例えば、５秒〜１０秒）のうちにワックスの融点よりも低い温度での圧延冷却を開始させることにより、溶融混合物中のワックスが冷却過程で再凝集して分散径が大きくなることを防止する技術が提案されている（特許文献１参照）。
As a toner production method, generally, using a melt kneader or the like, first, a toner raw material composed of a plurality of components such as a binder resin, a colorant (pigment, dye), and a wax is dispersed uniformly. A method in which a mixture of melted and then cooled toner raw materials is pulverized into toner particles having a desired particle size by coarse pulverization and fine pulverization using mechanical pulverization means.
In this conventional toner manufacturing method, after the molten mixture is discharged out of the kneader, rolling cooling is started at a temperature lower than the melting point of the wax within a relatively short time (for example, 5 seconds to 10 seconds). Thus, a technique for preventing the wax in the molten mixture from re-aggregating in the cooling process and increasing the dispersion diameter has been proposed (see Patent Document 1).
特許文献１に記載のトナーの製造方法によれば、溶融混合物におけるワックスの凝集をある程度抑制する効果は期待できるが、溶融混合の終了（混練機出口）から冷却開始までに最少でも５秒の時間差があること、及び、圧延冷却では溶融混合物の細部（圧延物の内部）に冷却作用が及びにくいことから、必ずしも十分な再凝集防止効果が得られない可能性がある。 According to the toner production method described in Patent Document 1, an effect of suppressing the aggregation of wax in the molten mixture to some extent can be expected, but a time difference of at least 5 seconds from the end of the melt mixing (kneader exit) to the start of cooling. In addition, there is a possibility that a sufficient re-aggregation preventing effect cannot always be obtained due to the fact that the cooling action does not easily reach the details of the molten mixture (inside the rolled product) by rolling cooling.
本発明は、上記実情に鑑みてなされたものであり、その目的は、溶融混合されたトナー原料の各成分の再凝集を有効に防止して、トナー原料の各成分が均一に分散されたトナー粒子を製造することができるトナーの製造方法、及び、該製造方法に適したトナーの製造装置を提供することにある。 The present invention has been made in view of the above circumstances, and an object of the present invention is to effectively prevent re-aggregation of each component of the melt-mixed toner material, and toner in which each component of the toner material is uniformly dispersed It is an object of the present invention to provide a toner manufacturing method capable of manufacturing particles and a toner manufacturing apparatus suitable for the manufacturing method.
上記目的を達成するための本発明に係るトナーの製造方法の第一特徴構成は、複数の成分からなるトナー原料を溶融混合する溶融混合工程と、前記溶融混合工程で得られた前記トナー原料の溶融混合物を微細化するとともに冷却する微細化冷却工程と、前記微細化冷却工程で微細化及び冷却された前記トナー原料の混合物を粉砕してトナー粒子を作製する粉砕工程とを有する点にある。 In order to achieve the above object, a first characteristic configuration of a toner production method according to the present invention includes a melt mixing step of melting and mixing a toner raw material comprising a plurality of components, and the toner raw material obtained in the melt mixing step. The present invention is characterized in that it has a micronization cooling process for micronizing and cooling the molten mixture, and a pulverization process for producing toner particles by pulverizing the mixture of the toner raw materials refined and cooled in the micronization cooling process.
すなわち、溶融混合工程において複数の成分からなるトナー原料の各成分が均一に分散するように溶融混合された後、微細化冷却工程において上記トナー原料の溶融混合物が微細化されるとともに冷却されるため、溶融混合物の微細化された各部分即ち溶融混合物の細部に対して冷却作用が及ぶ。その結果、トナー原料の溶融混合物が細部に亘って急冷されるのでトナー原料の各成分の再凝集が防止され、均一な分散状態を維持したトナー原料の微細化された混合物が得られる。そして、このトナー原料の微細化された混合物を粉砕工程において粉砕することにより、各成分が均一に分散された所望の粒度のトナー粒子が作製される。
従って、溶融混合されたトナー原料の各成分の再凝集を有効に防止して、トナー原料の各成分が均一に分散されたトナー粒子を製造することができるトナーの製造方法が提供される。
That is, after the toner raw material composed of a plurality of components is melt-mixed in the melt-mixing step so as to be uniformly dispersed, the toner raw-material melt mixture is refined and cooled in the miniaturization cooling step. , The cooling action is effected on each refined part of the molten mixture, ie the details of the molten mixture. As a result, since the molten mixture of the toner raw material is rapidly cooled in detail, re-aggregation of each component of the toner raw material is prevented, and a finely mixed mixture of the toner raw material maintaining a uniform dispersion state can be obtained. Then, the finely divided mixture of the toner raw material is pulverized in a pulverizing step, thereby producing toner particles having a desired particle size in which each component is uniformly dispersed.
Accordingly, there is provided a toner manufacturing method capable of effectively preventing reaggregation of each component of the melted and mixed toner material and manufacturing toner particles in which each component of the toner material is uniformly dispersed.
同第二特徴構成は、上記第一特徴構成において、前記微細化冷却工程では、前記トナー原料の溶融混合物を繊維状に形成して微細化する点にある。
すなわち、前記微細化冷却工程において前記トナー原料の溶融混合物を繊維状に形成することで連続的に効率良く微細化することができ、粉砕工程では、長い繊維状の溶融混合物を切断作用等により粉砕するので、粉砕効率が高くなる。
従って、トナーの製造方法の好適な実施形態が提供される。
The second feature configuration is that, in the first feature configuration, in the miniaturization cooling step, the molten mixture of the toner raw material is formed into a fiber and refined.
That is, the molten mixture of the toner raw material is formed into a fiber shape in the micronization cooling step so that it can be continuously and efficiently miniaturized. In the pulverization step, the long fibrous melt mixture is pulverized by a cutting action or the like. Therefore, the pulverization efficiency is increased.
Accordingly, a preferred embodiment of a toner manufacturing method is provided.
同第三特徴構成は、上記第一又は第二特徴構成において、前記微細化冷却工程では、前記トナー原料の微細化された溶融混合物に冷風を吹き付けて冷却する点にある。
すなわち、所望の温度の冷風を送風手段等を用いて吹き付けることで、トナー原料の微細化された溶融混合物を表面から迅速に冷却することができる。
従って、トナーの製造方法の好適な実施形態が提供される。
The third characteristic configuration is that, in the first or second characteristic configuration, in the miniaturization cooling step, cooling is performed by blowing cold air to the miniaturized molten mixture of the toner raw material.
That is, by blowing cool air at a desired temperature using a blower or the like, the molten mixture of the toner raw material can be rapidly cooled from the surface.
Accordingly, a preferred embodiment of a toner manufacturing method is provided.
また本発明に係るトナーの製造装置の第一特徴構成は、複数の成分からなるトナー原料を溶融混合する溶融混合部と、前記トナー原料の溶融混合物を微細化する微細化部と、微細化された前記トナー原料の溶融混合物を冷却する冷却部と、微細化及び冷却された前記トナー原料の混合物を粉砕する粉砕部とを備えた点にある。 The first characteristic configuration of the toner manufacturing apparatus according to the present invention includes a melt mixing unit that melts and mixes toner raw materials composed of a plurality of components, and a miniaturization unit that refines the molten mixture of toner raw materials. And a pulverizing section for pulverizing the refined and cooled mixture of the toner raw materials.
すなわち、複数の成分からなるトナー原料の各成分が溶融混合部によって溶融混合され、そのトナー原料の溶融混合物が微細化部によって微細化されるとともに冷却部によって冷却され、そのトナー原料の微細化及び冷却された混合物が粉砕部によって粉砕され、所望の粒度のトナー粒子が作製される。
従って、上記トナーの製造方法を実施するのに適したトナーの製造装置を提供される。
That is, each component of the toner raw material composed of a plurality of components is melt-mixed by the melt mixing section, and the molten mixture of the toner raw material is refined by the miniaturization section and cooled by the cooling section. The cooled mixture is pulverized by the pulverization unit to produce toner particles having a desired particle size.
Therefore, a toner manufacturing apparatus suitable for carrying out the toner manufacturing method is provided.
同第二特徴構成は、上記第一特徴構成において、前記微細化部が、前記トナー原料の溶融混合物を押出して繊維状に形成するノズルで構成されている点にある。
すなわち、微細化部を構成するノズルによってトナー原料の溶融混合物を押出して繊維状に形成することで、連続的に効率良く微細化することができる。
従って、トナーの製造装置の好適な実施形態が提供される。
The second characteristic configuration is that, in the first characteristic configuration, the miniaturization part is configured by a nozzle that extrudes a molten mixture of the toner raw material to form a fiber.
That is, it is possible to continuously and efficiently miniaturize by extruding the molten mixture of the toner raw material into a fiber by the nozzle constituting the miniaturization part.
Accordingly, a preferred embodiment of the toner manufacturing apparatus is provided.
同第三特徴構成は、上記第二特徴構成において、前記ノズルが、複数並置されている点にある。
すなわち、複数の並置したノズルからトナー原料の溶融混合物が押し出されて繊維状に形成される。その結果、トナー原料の多量の溶融混合物を同時に繊維状に形成することができる。
従って、処理効率に優れたトナーの製造装置の好適な実施形態が提供される。
The third feature configuration is that a plurality of the nozzles are juxtaposed in the second feature configuration.
That is, a molten mixture of toner raw materials is extruded from a plurality of juxtaposed nozzles to form a fiber. As a result, a large amount of a molten mixture of toner raw materials can be formed into fibers simultaneously.
Therefore, a preferred embodiment of a toner production apparatus having excellent processing efficiency is provided.
同第四特徴構成は、上記第一から第三特徴構成のいずれかにおいて、前記溶融混合部が、可動式の混練部材によって前記トナー原料を混練する混練機と、当該混練機の後段でかつ前記微細化部の前段に位置した静止型ミキサーとを備えている点にある。
すなわち、複数の成分からなるトナー原料は、先ず混練機において可動する混練部材から強い力を受けて十分に溶融混練された後、混練機の後段で微細化部の前段に位置した静止型ミキサーにおいて混合作用を受けてから微細化部に送られるので、混練機によって得られるトナー原料の溶融混合物を静止型ミキサーによって良好な溶融混合状態を維持しつつ微細化部に送ることができる。
従って、トナー原料の各成分が均一に分散されたトナー粒子の製造に一層適したトナーの製造装置の好適な実施形態が提供される。
In the fourth feature configuration, in any one of the first to third feature configurations, the melt mixing unit includes a kneader in which the toner raw material is kneaded by a movable kneading member, a rear stage of the kneader, and the It is in the point provided with the stationary mixer located in the front | former stage of the refinement | miniaturization part.
That is, a toner material composed of a plurality of components is first melted and kneaded sufficiently by receiving a strong force from a movable kneading member in a kneading machine, and then in a stationary mixer located in a stage downstream of the kneading machine and before the miniaturization unit. Since it is sent to the miniaturization section after receiving the mixing action, the molten mixture of the toner raw materials obtained by the kneader can be sent to the miniaturization section while maintaining a good melt mixing state by the static mixer.
Therefore, a preferred embodiment of a toner production apparatus more suitable for producing toner particles in which the respective components of the toner raw material are uniformly dispersed is provided.
同第五特徴構成は、上記第一から第四特徴構成のいずれかにおいて、前記溶融混合部が、前記トナー原料のうちの所定成分を除いた各成分を溶融混合した後、当該混合物に対して前記トナー原料の所定成分を加えて溶融混合させるよう構成されている点にある。
すなわち、複数の成分からなるトナー原料のうち所定成分を除いた各成分を溶融混合させた後で当該トナー原料の所定成分を加えて溶融混合するので、例えば、長時間の溶融混合によって特性が変化もしくは劣化するような成分については、後混合により溶融混合の時間を短くして、特性の変化や劣化を抑制することができ、また、短時間で他の成分と溶融混合するような成分については、後混合により無駄な混合エネルギーの消費を抑えることができる。
従って、トナー原料の各成分の特性に合わせて溶融混合部における各成分の投入構成を適切に設定できるトナーの製造装置の好適な実施形態が提供される。
According to the fifth feature configuration, in any one of the first to fourth feature configurations, the melt mixing unit melts and mixes each component excluding the predetermined component of the toner raw material, and then mixes the mixture. A predetermined component of the toner raw material is added and melt-mixed.
That is, each component of the toner raw material composed of a plurality of components excluding the predetermined component is melt-mixed and then the predetermined component of the toner raw material is added and melt-mixed. Or, for components that deteriorate, the time of melt mixing can be shortened by post-mixing to suppress changes in characteristics and deterioration, and for components that melt and mix with other components in a short time In addition, wasteful mixing energy consumption can be suppressed by post-mixing.
Therefore, a preferred embodiment of a toner manufacturing apparatus is provided in which the input configuration of each component in the melt mixing unit can be appropriately set in accordance with the characteristics of each component of the toner raw material.
本発明に係るトナーの製造方法及び製造装置の実施形態について、図面に基づいて説明する。 Embodiments of a toner manufacturing method and a manufacturing apparatus according to the present invention will be described with reference to the drawings.
本発明のトナーの製造方法は、図１に示すように、バインダ樹脂、着色剤、ワックス等の複数の成分からなるトナー原料を溶融混合する溶融混合工程と、溶融混合工程で得られたトナー原料の溶融混合物を微細化するとともに冷却する微細化冷却工程と、微細化冷却工程で微細化及び冷却されたトナー原料の混合物を粉砕してトナー粒子を作製する粉砕工程とを有する。そして、上記微細化冷却工程では、トナー原料の溶融混合物を繊維状に形成して微細化するとともに、当該トナー原料の微細化された溶融混合物に冷風を吹き付けて冷却する。尚、上記粉砕工程では、実際には分級機能を備えた粉砕機等を用いて粉砕物を分級し、所望の粒度のトナー粒子を得るようにしている。また、上記のように繊維状のトナー原料を粉砕して作製されるトナー粒子は柱状（円柱状など）に形成されるので、粉砕工程の前や後に、適宜流動性向上剤等を外添する外添処理や球形化処理等を施す。 As shown in FIG. 1, the toner production method of the present invention comprises a melt mixing step of melting and mixing a toner material composed of a plurality of components such as a binder resin, a colorant, and a wax, and a toner material obtained in the melt mixing step. And a pulverization step of pulverizing the mixture of the toner raw material refined and cooled in the micronization cooling step to produce toner particles. In the fine cooling process, the molten mixture of the toner raw material is formed into a fiber shape and refined, and cooled by blowing cold air on the miniaturized molten mixture of the toner raw material. In the above pulverization step, the pulverized product is actually classified using a pulverizer having a classification function to obtain toner particles having a desired particle size. Further, since the toner particles prepared by pulverizing the fibrous toner raw material as described above are formed in a columnar shape (such as a columnar shape), a fluidity improver or the like is appropriately externally added before or after the pulverization step. External addition processing, spheroidization processing, etc. are performed.
次に、本発明のトナー製造装置は、図２に示すように、上記複数の成分からなるトナー原料を溶融混合する溶融混合部１０と、前記トナー原料の溶融混合物を微細化する微細化部２０と、微細化された前記トナー原料の溶融混合物を冷却する冷却部３０と、微細化及び冷却された前記トナー原料の混合物を粉砕する粉砕部４０とを備えている。
そして、図１のトナーの製造方法と対応させると、上記溶融混合部１０によって、溶融混合工程が実行され、上記微細化部２０と冷却部３０によって、微細化冷却工程が実行され、上記粉砕部４０によって粉砕工程が実行される。
Next, as shown in FIG. 2, the toner manufacturing apparatus of the present invention includes a melting and mixing unit 10 that melts and mixes the toner materials composed of the plurality of components, and a refining unit 20 that refines the molten mixture of toner materials. A cooling unit 30 that cools the molten mixture of the toner material that has been refined, and a pulverization unit 40 that crushes the mixture of the toner material that has been refined and cooled.
Then, in correspondence with the toner manufacturing method of FIG. 1, the melt mixing unit 10 performs a melt mixing process, the micronization unit 20 and the cooling unit 30 perform a micronization cooling process, and the pulverization unit By 40, the grinding step is executed.
具体的には、混合装置（例えば、ホソカワミクロン（株）製サイクロミックス）９、ホッパ１Ａ付で内部に回転スクリュー１５を有する一軸型エクストルーダー１、静止型ミキサ２、静止型ミキサ２の出口から分岐した多段の分配流路３Ａを有する流路構造体３などが設けられ、一軸型エクストルーダー１の出口と静止型ミキサ２の入口の間にはモータ５で駆動されるギアポンプ４が配置されている。なお、分配流路３Ａの最終段の各流路出口に対応させて、押出し用のノズル６が複数並置されて設けられている。また、一軸型エクストルーダー１、ギアポンプ４、静止型ミキサ２、流路構造体３には、図示は省略するが、トナー原料をバインダ樹脂の融点以上の高温、例えば１３０℃〜２４０℃程度に加熱して低粘度にするためのヒータを備えている。 Specifically, the mixing device (for example, Hosokawa Micron Co., Ltd. cyclomix) 9, a uniaxial extruder 1 with a hopper 1 A and a rotating screw 15 inside, a static mixer 2, branching from the outlet of the static mixer 2 A flow path structure 3 having a multistage distribution flow path 3A is provided, and a gear pump 4 driven by a motor 5 is disposed between the outlet of the uniaxial extruder 1 and the inlet of the stationary mixer 2. . Note that a plurality of extrusion nozzles 6 are provided side by side so as to correspond to the respective channel outlets in the final stage of the distribution channel 3A. Although not shown in the uniaxial extruder 1, the gear pump 4, the static mixer 2, and the flow path structure 3, the toner material is heated to a temperature higher than the melting point of the binder resin, for example, about 130 ° C to 240 ° C. And a heater for reducing the viscosity.
上記装置において、前記トナー原料は、ホッパ１Ａから一軸型エクストルーダー１内に投入されると、ヒータによって加熱されて溶融状態となり混合されながら出口側に送られる。一軸型エクストルーダー１から送り出されたトナー原料の溶融混合物は、ギアポンプ４で圧力及び押し出し量を調整された後、静止型ミキサ２内の流路と多段の分配流路３Ａを通流する間に混合が促進され、トナー原料の各成分が均一に細かく分散した状態になる。そして、複数のノズル６から下向きに繊維状に押し出されるとともに図示しない延伸用エアー吹き出し装置から吹き出す熱風によって延伸されたトナー原料の溶融混合物が、送風機７から冷風を吹き付けられて冷却される。なお、下方に落下したトナー原料の繊維状物は受け容器８内に回収され、所定量ごとに粉砕機４０に投入されて粉砕処理される。 In the above apparatus, when the toner raw material is put into the uniaxial extruder 1 from the hopper 1A, it is heated by a heater to be in a molten state and fed to the outlet side while being mixed. The molten mixture of toner raw materials fed from the uniaxial extruder 1 is adjusted in pressure and extrusion amount by the gear pump 4 and then flows through the flow path in the static mixer 2 and the multistage distribution flow path 3A. Mixing is promoted, and each component of the toner raw material is uniformly and finely dispersed. Then, the molten mixture of the toner raw material which is extruded downward from the plurality of nozzles 6 and is stretched by hot air blown from a drawing air blowing device (not shown) is cooled by blowing cold air from the blower 7. The fibrous material of the toner raw material that has fallen downward is collected in the receiving container 8, and is fed into the pulverizer 40 every predetermined amount for pulverization.
尚、上記静止型ミキサ２は、公知の静止型ミキサを使用することができ、具体的には、図２に示すように、螺旋状の流路を形成するように捩られた曲面を有する羽根体１４が、トナー原料の流れ方向に沿って隣接するもの同士で螺旋の捩れ角度を反転させながら複数個（図２の例では３個）設けられた構造である。 As the static mixer 2, a known static mixer can be used. Specifically, as shown in FIG. 2, a blade having a curved surface twisted so as to form a spiral flow path. A plurality of bodies 14 (three in the example shown in FIG. 2) are provided while adjacent to each other along the flow direction of the toner material while reversing the twist angle of the spiral.
以上より、溶融混合部１０が、一軸型エクストルーダー１、静止型ミキサ２及び流路構造体３によって構成される。また、微細化部２０が、前記トナー原料の溶融混合物を押し出して繊維状に形成する前記ノズル６と延伸用エアー吹き出し装置によって構成され、冷却部３０が、冷風を吹き付ける上記送風機７で構成される。さらに、粉砕機４０が粉砕部４０に対応する。即ち、溶融混合部１０が、可動式の混練部材（具体的には、回転スクリュー１５）によって前記トナー原料を混練する混練機としての一軸型エクストルーダー１と、当該混練機（一軸型エクストルーダー１）の後段でかつ前記微細化部２０の前段に位置した静止型ミキサー２とを備えている。 As described above, the melt mixing unit 10 is constituted by the uniaxial extruder 1, the static mixer 2, and the flow path structure 3. Further, the miniaturization unit 20 is configured by the nozzle 6 that extrudes the molten mixture of the toner raw material to form a fiber and the stretching air blowing device, and the cooling unit 30 is configured by the blower 7 that blows cold air. . Further, the pulverizer 40 corresponds to the pulverization unit 40. That is, the melt mixing unit 10 is a uniaxial extruder 1 as a kneader for kneading the toner raw material by a movable kneading member (specifically, a rotary screw 15), and the kneading machine (uniaxial extruder 1). ) And the stationary mixer 2 positioned in the preceding stage of the miniaturization unit 20.
上記粉砕機４０は、例えば、ホソカワミクロン（株）製ＡＣＭパルペライザで構成される。具体的には、図３に示すように、下方に気体導入口４１を設け上方に気体及び粉体の排出口４２を設けた本体４３の内部を筒状部材４４によって外側の粉砕室Ａと内側の分級室Ｂとに区分し、粉砕室Ａが粉砕部材４５を備えた回転体４５Ａを内蔵するとともに下方側で前記気体導入口４１に連通し、分級室Ｂが粗粉と微粉を分級して微粉のみを通過させる分級機構４６を経由して前記排出口４２に連通している。尚、原料（トナー原料の繊維状物）は本体４３の横側部に設けた投入口４３Ａから粉砕室Ａに投入する。また、排出口４２は図示しないバグフィルタ内蔵の集塵機を通して外部に向けて吸引排気されている。上記回転体４５Ａは上下軸心周りに回転自在であり、回転体４５Ａの外周部に、縦型ハンマータイプの前記粉砕部材４５が粉砕室Ａの内壁部に装着されたライナ４７と間隙を隔てる状態で複数取付けられている。そして、上記粉砕室Ａにおいて原料が粉砕部材４５から機械的衝撃力を受けて粉砕される。 The pulverizer 40 is composed of an ACM pulverizer manufactured by Hosokawa Micron Corporation, for example. Specifically, as shown in FIG. 3, the inside of a main body 43 provided with a gas inlet 41 on the lower side and a gas and powder outlet 42 on the upper side is connected to the outer grinding chamber A and the inner side by a cylindrical member 44. And the pulverizing chamber A contains a rotating body 45A provided with a pulverizing member 45 and communicates with the gas inlet 41 on the lower side, and the classifying chamber B classifies coarse powder and fine powder. It communicates with the discharge port 42 via a classification mechanism 46 that allows only fine powder to pass through. The raw material (the fibrous material of the toner raw material) is fed into the pulverizing chamber A through a charging port 43A provided on the side of the main body 43. The discharge port 42 is sucked and exhausted to the outside through a dust collector with a bag filter (not shown). The rotating body 45A is rotatable about the vertical axis, and the vertical hammer type pulverizing member 45 is separated from the liner 47 mounted on the inner wall of the pulverizing chamber A at the outer periphery of the rotating body 45A. Several are installed in. In the crushing chamber A, the raw material is crushed by receiving a mechanical impact force from the crushing member 45.
上記分級機構４６は、上下軸心周りに回転自在な回転体４８の外周部に複数の分級羽根４９を立設させた構造であり、粉砕物に作用する分級室Ｂから排出口４２に向かう気流の搬送力と回転体４８によって付与される遠心力の差によって微粉と粗粉を分離する。即ち、粉砕室Ａから分級室Ｂに流入した粉砕物のうち、気流による搬送力の方が大きく作用する微粉は分級羽根４９を通過して排出口４２から排出され、遠心力の方が大きく作用する粗粉は分級羽根４９を通過せずに筒状部材４４の下方から粉砕室Ａに戻る。 The classifying mechanism 46 has a structure in which a plurality of classifying blades 49 are erected on the outer peripheral portion of a rotating body 48 that is rotatable around a vertical axis, and an air flow from the classifying chamber B acting on the pulverized material toward the discharge port 42. The fine powder and the coarse powder are separated by the difference between the conveying force and the centrifugal force applied by the rotating body 48. That is, among the pulverized material that flows into the classification chamber B from the pulverization chamber A, the fine powder having a larger conveying force due to the airflow passes through the classification blade 49 and is discharged from the discharge port 42, and the centrifugal force has a larger effect. The coarse powder to be returned returns to the crushing chamber A from below the cylindrical member 44 without passing through the classification blade 49.
図４に、トナー粒子１２中においてワックス粒子１１が良好に分散されてワックス粒子１１の分散径が小さい状態（イ）と、ワックス粒子１１が再凝集して分散性が悪くなり、ワックス粒子１１の分散径が大きくなった状態（ロ）の例を模式的に示す。そして、ワックス粒子１１の分散性が悪いトナー粒子１２は、ワックス粒子部分で割れ易いため、現像剤としての耐久性が劣る不利がある。 FIG. 4 shows that the wax particles 11 are well dispersed in the toner particles 12 and the dispersion diameter of the wax particles 11 is small (A), and the wax particles 11 are re-agglomerated to deteriorate the dispersibility. An example of a state (B) in which the dispersion diameter is increased is schematically shown. The toner particles 12 having a low dispersibility of the wax particles 11 are liable to break at the wax particle portion, and thus have a disadvantage that the durability as a developer is inferior.
図５は、トナー粒子中における顔料の分散性が良い場合と分散性が悪い場合とで、トナー粒子の光透過率特性が違ってくることを示すデータの一例である。分散性が良好な場合は透過率が高くなるのに対し、分散性が不良の場合は透過率が低くなる。特にカラー用トナーの場合には、各色のトナーが転写材上に層状に重なって状態で形成されるので、トナーの透過率が低いと下側の層の色が上方に現れず、カラー画像として良好な色再現範囲が得られない不都合が生じる。 FIG. 5 is an example of data indicating that the light transmittance characteristics of the toner particles differ depending on whether the dispersibility of the pigment in the toner particles is good or not. When the dispersibility is good, the transmittance is high, whereas when the dispersibility is poor, the transmittance is low. In particular, in the case of color toners, toner of each color is formed in a layered state on the transfer material. Therefore, when the toner transmittance is low, the color of the lower layer does not appear upward, and a color image is obtained. There arises a disadvantage that a good color reproduction range cannot be obtained.
〔別実施形態〕
上記実施形態では、微細化冷却工程や微細化部２０において、トナー原料の溶融混合物を微細化する手段として、繊維状に押出し形成するノズル６で構成したが、微細化手段はかかる繊維状に形成する手段に限定されるものではない。例えば、トナー原料の溶融混合物を微細な切片状に形成する手段でもよい。
[Another embodiment]
In the above-described embodiment, the finer cooling step and the finer portion 20 are configured by the nozzle 6 that is extruded into a fiber shape as a means for refining the molten mixture of the toner raw material. It is not limited to the means to do. For example, a means for forming a molten mixture of toner raw materials into fine slices may be used.
上記実施形態では、微細化冷却工程や冷却部３０において、微細化（繊維状化）したトナー原料の溶融混合物を冷却する手段として、冷風を吹き付ける送風機７で構成したが、ノズル６から押し出すときの押出し速度が非常に高速である（例えば、４０ｍ／ｓｅｃ）ので、上記のような送風機を設けなくても、押出した周囲の温度条件を常温又は低温条件に維持することによって冷却させることも可能である。 In the above embodiment, the blower 7 that blows cold air is used as a means for cooling the melted mixture of the toner material that has been made fine (fibrous) in the fine cooling process or the cooling unit 30. Since the extrusion speed is very high (for example, 40 m / sec), it is possible to cool by maintaining the temperature condition around the extruded temperature at room temperature or low temperature without providing a blower as described above. is there.
上記実施形態では、粉砕工程や粉砕部４０において、微細化（繊維状化）したトナー原料の混合物をいったん容器８に一定量回収してから、粉砕機４０に投入するように構成したが、微細化（繊維状化）したトナー原料の混合物を連続的に粉砕機４０に投入するように構成することも可能である。 In the above embodiment, the toner material mixture that has been refined (fibridized) is once collected in the container 8 in the crushing step or crushing unit 40 and then put into the crusher 40. It is also possible to configure such that the mixture of the toner raw materials (fibridized) is continuously fed into the pulverizer 40.
上記実施形態では、溶融混合部１０を、トナー原料の各成分を最初から一緒に溶融混合するよう構成したが、トナー原料のうちの所定成分を除いた各成分を溶融混合した後、当該混合物に対して前記トナー原料の所定成分を溶融混合させるよう構成してもよい。ここで、後で混合する成分としては、バインダ樹脂以外のワックス、顔料・染料等の着色剤、荷電制御剤、シリカ等の粉砕助剤など適宜選択することができる。
溶融混合部１０で上記所定成分を後混合する位置は、混練機（一軸型エクストルーダー１）の出口箇所から静止型ミキサー２の入口箇所までの範囲、静止型ミキサー２の内部流路、静止型ミキサー２の出口箇所から流路構造体３の入口箇所までの範囲、流路構造体３の内部流路３Ａにおいて任意の位置に設定できる。図６には、ワックスを除いたトナー原料の各成分を一軸型エクストルーダー１で溶融混合した後、ワックスを静止型ミキサー２の入口箇所から混合する例を示している。図６中、１６はワックス用の溶融装置、１７はワックス用のギアポンプである。
In the above embodiment, the melt mixing unit 10 is configured to melt and mix the components of the toner raw material together from the beginning. However, after melt mixing the components of the toner raw material excluding the predetermined components, the mixture is added to the mixture. On the other hand, a predetermined component of the toner raw material may be melted and mixed. Here, as components to be mixed later, waxes other than the binder resin, colorants such as pigments and dyes, charge control agents, and grinding aids such as silica can be appropriately selected.
The position where the predetermined component is post-mixed in the melt mixing unit 10 is a range from the exit location of the kneader (uniaxial extruder 1) to the entrance location of the static mixer 2, the internal flow path of the static mixer 2, the static type The range from the outlet location of the mixer 2 to the inlet location of the flow path structure 3 and the internal flow path 3A of the flow path structure 3 can be set at an arbitrary position. FIG. 6 shows an example in which each component of the toner raw material excluding the wax is melt-mixed by the uniaxial extruder 1 and then the wax is mixed from the inlet portion of the stationary mixer 2. In FIG. 6, 16 is a melting apparatus for wax, and 17 is a gear pump for wax.
なお、溶融混合工程や溶融混合部１０において使用される溶融混合用の装置は上記実施形態で用いた装置に限らず、各種の装置が使用できる。 In addition, the apparatus for melt mixing used in the melt mixing process or the melt mixing unit 10 is not limited to the apparatus used in the above embodiment, and various apparatuses can be used.
次に、本発明に係るトナーの製造方法の実施例について、カラー用の４色のトナー（ブラック、シアン、マゼンタ、イエロー）を例にして説明する。 Next, an example of a toner manufacturing method according to the present invention will be described by taking four color toners (black, cyan, magenta, yellow) as an example.
（ブラックトナー）
ポリエステル樹脂（Ｔｇ：６４℃、流出開始温度（島津製作所製フローテスタにより測定、以下同様）：１１９℃）１００重量部、カーボンブラック１０重量部、サリチル酸亜鉛塩３重量部、及びカルナウバワックス５重量部を、前記混合装置９で予備混合した後、一軸型エクストルーダー１に供給して溶融し、ギアポンプ４で圧力調整した後（ギアポンプ後段で約４．２ＭＰａ）、温度１５０℃の溶融状態で静止型ミキサ２に押し出し供給した。そして、静止型ミキサ２での溶融混合を経て、孔径３００μｍのノズル６から押し出しつつ熱風により線径５．０μｍとなるように延伸したのち冷却して、微粒子前駆体繊維を得た。尚、このときの繊維の生成速度は、押し出し量と繊維径から約４０ｍ／ｓｅｃと算出された。
(Black toner)
100 parts by weight of a polyester resin (Tg: 64 ° C., starting temperature (measured with a flow tester manufactured by Shimadzu Corp., hereinafter the same): 119 ° C.), 10 parts by weight of carbon black, 3 parts by weight of zinc salicylate, and 5 parts by weight of carnauba wax The parts are premixed by the mixing device 9 and then supplied to the uniaxial extruder 1 to be melted and the pressure is adjusted by the gear pump 4 (about 4.2 MPa at the rear stage of the gear pump), and then in a molten state at a temperature of 150 ° C. The extrusion was supplied to the mold mixer 2. Then, after being melt-mixed in the static mixer 2, it was stretched to a wire diameter of 5.0 μm with hot air while being extruded from a nozzle 6 having a pore diameter of 300 μm, and then cooled to obtain fine particle precursor fibers. The fiber generation rate at this time was calculated to be about 40 m / sec from the extrusion amount and the fiber diameter.
さらに、上記微粒子前駆体繊維を、前記分級機内蔵型粉砕機（ＡＣＭパルペライザ）で粉砕及び分級処理し、その結果、体積平均径６．４μｍ、個数平均径５．３μｍで、体積基準における１２μｍ以上の粒子の割合が１．４％、１６μｍ以上の粒子の割合が０％、個数基準における５μｍ未満の微粉粒子の割合が１１．２％の粒度分布のトナー用粒子を得た。 Further, the fine particle precursor fiber was pulverized and classified by the classifier built-in type pulverizer (ACM pulverizer). As a result, the volume average diameter was 6.4 μm, the number average diameter was 5.3 μm, and the volume standard was 12 μm or more. Toner particles having a particle size distribution of 1.4%, a particle size of 16 μm or more of 0%, and a fine particle size of less than 5 μm on the number basis was 11.2%.
次いで、上記トナー用粒子１００重量部、ステアリン酸亜鉛（平均粒子径０．３μｍ）０．０２重量部、シリカ（比表面積から算出した粒子径１２ｎｍ）０．７５重量部、及びシリカ（比表面積から算出した粒子径３０ｎｍ）０．７５重量部を、圧縮剪断型混合機（例えば、ホソカワミクロン（株）製メカノフュージョン、以下同様）により攪拌混合して、ブラック現像剤を得た。 Next, 100 parts by weight of the toner particles, 0.02 parts by weight of zinc stearate (average particle diameter 0.3 μm), 0.75 parts by weight of silica (particle diameter 12 nm calculated from the specific surface area), and silica (from the specific surface area). A black developer was obtained by stirring and mixing 0.75 parts by weight of a calculated particle diameter of 30 nm using a compression shear mixer (for example, Mechanofusion manufactured by Hosokawa Micron Corporation, the same applies hereinafter).
（シアントナー）
ポリエステル樹脂（Ｔｇ：６４℃、流出開始温度：１１９℃）１００重量部、銅フタロシアニン系顔料５重量部、レシチン３重量部、及びカルナウバワックス５重量部を、実施例１と同様の条件で混合、溶融、ノズルからの押し出し等の工程を経て、線径５．０μｍの微粒子前駆体繊維を得た。さらに、この微粒子前駆体繊維を、実施例１と同様に前記分級機内蔵型粉砕機で粉砕して、体積平均径６．５μｍ、個数平均径５．６μｍで、体積基準における１２μｍ以上の粒子の割合が１．５％、１６μｍ以上の粒子の割合が０％、個数基準における５μｍ未満の微粉粒子の割合が１０．２％の粒度分布のトナー用粒子を得た。次いで、上記トナー用粒子に対して、実施例１と同じ条件で、ステアリン酸亜鉛及びシリカを混合して、前記圧縮剪断型混合機により攪拌混合して、シアン現像剤を得た。
(Cyan toner)
100 parts by weight of a polyester resin (Tg: 64 ° C., outflow start temperature: 119 ° C.), 5 parts by weight of copper phthalocyanine pigment, 3 parts by weight of lecithin, and 5 parts by weight of carnauba wax are mixed under the same conditions as in Example 1. Through a process such as melting, extrusion from a nozzle, etc., a fine particle precursor fiber having a wire diameter of 5.0 μm was obtained. Further, this fine particle precursor fiber was pulverized by the above-mentioned classifier built-in type pulverizer in the same manner as in Example 1 to obtain particles having a volume average diameter of 6.5 μm, a number average diameter of 5.6 μm, and 12 μm or more on a volume basis. Toner particles having a particle size distribution with a ratio of 1.5%, a ratio of particles of 16 μm or more of 0%, and a ratio of fine powder particles of less than 5 μm based on the number of 10.2% were obtained. Next, zinc stearate and silica were mixed with the toner particles under the same conditions as in Example 1, and the mixture was stirred and mixed by the compression shear mixer to obtain a cyan developer.
（マゼンタトナー）
ポリエステル樹脂（Ｔｇ：６４℃、流出開始温度：１１９℃）１００重量部、キナクリドン系顔料５重量部、レシチン３重量部、及びカルナウバワックス５重量部を、実施例１と同様の条件で混合、溶融、ノズルからの押し出し等の工程を経て、線径５．０μｍの微粒子前駆体繊維を得た。さらに、この微粒子前駆体繊維を、実施例１と同様に前記分級機内蔵型粉砕機で粉砕して、体積平均径６．５μｍ、個数平均径５．５μｍで、体積基準における１２μｍ以上の粒子の割合が１．４％、１６μｍ以上の粒子の割合が０％、個数基準における５μｍ未満の微粉粒子の割合が１０．４％の粒度分布のトナー用粒子を得た。次いで、上記トナー用粒子に対して、実施例１と同じ条件で、ステアリン酸亜鉛及びシリカを混合して、前記圧縮剪断型混合機により攪拌混合して、マゼンタ現像剤を得た。
(Magenta toner)
100 parts by weight of a polyester resin (Tg: 64 ° C., outflow start temperature: 119 ° C.), 5 parts by weight of a quinacridone pigment, 3 parts by weight of lecithin, and 5 parts by weight of carnauba wax are mixed under the same conditions as in Example 1. Through steps such as melting and extrusion from a nozzle, fine particle precursor fibers having a wire diameter of 5.0 μm were obtained. Further, this fine particle precursor fiber was pulverized by the above-mentioned classifier built-in type pulverizer in the same manner as in Example 1 to obtain particles having a volume average diameter of 6.5 μm, a number average diameter of 5.5 μm, and 12 μm or more in volume standard. Toner particles having a particle size distribution of 1.4%, a ratio of particles of 16 μm or more of 0%, and a ratio of fine powder particles of less than 5 μm based on the number of 10.4% were obtained. Next, zinc stearate and silica were mixed with the toner particles under the same conditions as in Example 1 and stirred and mixed with the compression shear mixer to obtain a magenta developer.
（イエロートナー）
ポリエステル樹脂（Ｔｇ：６４℃、流出開始温度：１１９℃）１００重量部、ジスアゾ系顔料５重量部、レシチン３重量部、及びカルナウバワックス５重量部を、実施例１と同様の条件で混合、溶融、ノズルからの押し出し等の工程を経て、線径５．０μｍの微粒子前駆体繊維を得た。さらに、この微粒子前駆体繊維を、実施例１と同様に前記分級機内蔵型粉砕機で粉砕して、体積平均径６．６μｍ、個数平均径５．７μｍで、体積基準における１２μｍ以上の粒子の割合が１．６％、１６μｍ以上の粒子の割合が０％、個数基準における５μｍ未満の微粉粒子の割合が９．４％の粒度分布のトナー用粒子を得た。次いで、上記トナー用粒子に対して、実施例１と同じ条件で、ステアリン酸亜鉛及びシリカを混合して、前記圧縮剪断型混合機により攪拌混合して、イエロー現像剤を得た。
(Yellow toner)
100 parts by weight of a polyester resin (Tg: 64 ° C., outflow start temperature: 119 ° C.), 5 parts by weight of a disazo pigment, 3 parts by weight of lecithin, and 5 parts by weight of carnauba wax are mixed under the same conditions as in Example 1. Through steps such as melting and extrusion from a nozzle, fine particle precursor fibers having a wire diameter of 5.0 μm were obtained. Further, this fine particle precursor fiber was pulverized by the above-mentioned classifier built-in type pulverizer in the same manner as in Example 1 to obtain particles having a volume average diameter of 6.6 μm, a number average diameter of 5.7 μm, and 12 μm or more on a volume basis. Toner particles having a particle size distribution of 1.6%, a ratio of particles of 16 μm or more being 0%, and a ratio of fine powder particles of less than 5 μm based on the number of 9.4% were obtained. Next, zinc stearate and silica were mixed with the toner particles under the same conditions as in Example 1 and stirred and mixed with the compression shear mixer to obtain a yellow developer.
次に、上記のようにして得た各色の現像剤粒子における原料の分散状態を観察した。例えば、シアンの現像剤粒子について、金属コーティングを施してから、エポキシ樹脂に包埋し、切断した後、切断面を四酸化ルテニウムで染色し、さらに超箔切片を作製して現像剤粒子断面の試験サンプルとした。この超箔切片をＴＥＭにより観察すると、シアン顔料は均一に分散しており、大きなシアン顔料の粒は観察されなかった。また、カルナウバワックスは、約０．３μｍ程度の粒に微分散していること確認できた。その他の色の現像剤粒子についても、同様に、顔料、ワックスの良好な分散が確認できた。 Next, the dispersion state of the raw materials in the developer particles of each color obtained as described above was observed. For example, for cyan developer particles, after metal coating, embedding in epoxy resin and cutting, the cut surface is dyed with ruthenium tetroxide, and an ultra-foil slice is prepared to produce a cross-section of the developer particles. A test sample was obtained. When this super foil section was observed with a TEM, the cyan pigment was uniformly dispersed and no large cyan pigment particles were observed. Moreover, it was confirmed that the carnauba wax was finely dispersed in about 0.3 μm grains. Similarly, good dispersion of pigments and waxes could be confirmed for the developer particles of other colors.
最後に、上記のようにして得た４色の現像剤粒子について、画像装置（セイコーエプソン株式会社製プリンタＬＰ−７０００Ｃ）を用いて画像評価を行った。その結果、得られた画像は、画像濃度が高く安定しており、濃淡コントロール（階調）も良好で、かつ、解像度が高くシャープであった。また、地汚れや転写時のちり（飛点）等もなかった。尚、このことから、ＴＥＭでは観察できなかったが、荷電制御剤（サリチル酸亜鉛、レシチン）の分散が良好であったことが裏付けられる。
また、耐久試験（例えば、１万枚画像出し条件）を行ったときの帯電量の変化について、４色の各現像剤とも初期帯電量（通常、２０〜３０μＣ／ｇ）に対して±７．５μＣ／ｇ程度の範囲内に収まっており、帯電安定性についても良好な結果を得ている。
Finally, the four color developer particles obtained as described above were subjected to image evaluation using an image device (printer LP-7000C manufactured by Seiko Epson Corporation). As a result, the obtained image had a high and stable image density, a good density control (gradation), a high resolution, and a sharp image. Moreover, there were no background stains or dust at the time of transfer. In addition, although this was not able to be observed with TEM, this confirms that the dispersion of the charge control agent (zinc salicylate, lecithin) was good.
In addition, with respect to changes in the charge amount when a durability test (for example, 10,000 sheet image output conditions) is performed, each of the four color developers is ± 7.% relative to the initial charge amount (usually 20 to 30 μC / g). It is within the range of about 5 μC / g, and good results are obtained with respect to charging stability.
本発明に係るトナーの製造方法及び製造装置は、トナー成分の均一化の要求が大きい例えばカラー用、高画質用などの現像トナーの製造に広く適用できる。 The toner production method and production apparatus according to the present invention can be widely applied to the production of developing toners, for example, for color and high image quality, which have a high demand for uniform toner components.
１ 一軸型エクストルーダー
２ 静止型ミキサー
３ 流路構造体
３Ａ 流路
４ ギアポンプ
５ モータ
６ ノズル
７ 送風機
８ 容器
９ 混合装置
１０ 溶融混合部
１１ ワックス粒子
１２ トナー粒子
１４ 羽根体
１５ 混練部材
１６ 溶融装置
１７ ギアポンプ
２０ 微細化部
３０ 冷却部
４０ 粉砕部（粉砕機）
４１ 気体導入口
４２ 排出口
４３ 本体
４４ 筒状部材
４５ 粉砕部材
４５Ａ 回転体
４６ 分級機構
４７ ライナ
４８ 回転体
４９ 分級羽根
DESCRIPTION OF SYMBOLS 1 Uniaxial extruder 2 Static mixer 3 Flow path structure 3A Flow path 4 Gear pump 5 Motor 6 Nozzle 7 Blower 8 Container 9 Mixing device 10 Melt mixing part 11 Wax particle 12 Toner particle 14 Blade body 15 Kneading member 16 Melting device 17 Gear pump 20 Refinement section 30 Cooling section 40 Crushing section (pulverizer)
41 Gas introduction port 42 Discharge port 43 Main body 44 Cylindrical member 45 Grinding member 45A Rotating body 46 Classification mechanism 47 Liner 48 Rotating body 49 Classification blade
Claims (8)
前記溶融混合工程で得られた前記トナー原料の溶融混合物を微細化するとともに冷却する微細化冷却工程と、
前記微細化冷却工程で微細化及び冷却された前記トナー原料の混合物を粉砕してトナー粒子を作製する粉砕工程とを有するトナーの製造方法。 A melt mixing step of melt-mixing a toner material composed of a plurality of components;
A refined cooling step of refining and cooling the molten mixture of the toner raw material obtained in the melt mixing step;
And a pulverization step of pulverizing the mixture of the toner raw materials refined and cooled in the micronization cooling step to produce toner particles.
前記トナー原料の溶融混合物を微細化する微細化部と、
微細化された前記トナー原料の溶融混合物を冷却する冷却部と、
微細化及び冷却された前記トナー原料の混合物を粉砕する粉砕部とを備えたトナーの製造装置。 A melt mixing section for melting and mixing toner raw materials comprising a plurality of components;
A refining section for refining the molten mixture of the toner raw material;
A cooling unit that cools the molten mixture of the toner raw material that has been refined;
And a pulverizing unit for pulverizing the refined and cooled mixture of the toner raw materials.
The melt mixing unit is configured to melt and mix each component of the toner raw material excluding the predetermined component, and then melt and mix the predetermined component of the toner raw material into the mixture. The toner manufacturing apparatus according to claim 1.