JP2006099923A - クリーニングテープ - Google Patents
クリーニングテープ Download PDFInfo
- Publication number
- JP2006099923A JP2006099923A JP2004288215A JP2004288215A JP2006099923A JP 2006099923 A JP2006099923 A JP 2006099923A JP 2004288215 A JP2004288215 A JP 2004288215A JP 2004288215 A JP2004288215 A JP 2004288215A JP 2006099923 A JP2006099923 A JP 2006099923A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- magnetic
- cleaning
- head
- cleaning tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】 支持体上の少なくとも一方の面に粉体および結合剤を含む塗布層を設け、前記塗布層と磁気ヘッドとを接触させるクリーニングテープであって、前記塗布層の中心線平均粗さRaが5〜25nmであり、かつ前記塗布層表面に25nm以上の高さの突起が60〜1700個/105μm2存在することを特徴とするクリーニングテープ。
【選択図】 なし
Description
1)支持体上の少なくとも一方の面に粉体および結合剤を含む塗布層を設け、前記塗布層と磁気ヘッドとを接触させるクリーニングテープであって、前記塗布層の中心線平均粗さRaが5〜25nmであり、かつ前記塗布層表面に25nm以上の高さの突起が60〜1700個/105μm2存在することを特徴とするクリーニングテープ。
2)前記塗布層が、前記支持体上に設けられた非磁性層と、前記非磁性層上に設けられた磁性層とを有することを特徴とする上記1)に記載のクリーニングテープ。
さらに本発明のクリーニングテープでは、塗布層として、支持体上に非磁性層を設け、さらにその上に磁性層を設けることで、クリーニング効果を増大させることができる。また上層を磁性層にしたため、必要に応じて情報記録も同時に行える。
本発明のクリーニングテープは、支持体上の少なくとも一方の面に粉体および結合剤を含む塗布層が設けられている。この塗布層の中心線平均粗さ(Ra)は、5〜25nmである必要がある。好ましくは10〜20nm、さらに好ましくは12〜18nmである。Raが5nmより小さいと充分なクリーニング効果が得られず、25nmを超えるとヘッド磨耗が増大するという不具合が生じる。
対物レンズ:20倍、中間レンズ:1.0倍、測定範囲:345μm×257μmで円筒補正、傾き補正後にRaを算出する。
支持体上に設けられる塗布層は微粒子無機粉末のような粉体を結合剤で分散したものを主に用いる。前記微粒子無機粉末は非磁性物でも磁性粒子でも構わない。塗布層は単層、若しくは複数の層で構成される。塗布層はMRヘッドに接触する面に形成する。
塗布層を設ける目的は、支持体にない機能を必要に応じて付与するためのもので、例えば、研磨粒子としての非磁性粒子をMRヘッドに接触する面に含有させてクリーニング効果をもたせる、導電性粒子を含有させて帯電防止機能を持たせる、磁性体を含有させて磁気信号を記録することなどが挙げられる。
塗布層はさらに潤滑剤を含むことにより、摩擦係数を制御することが可能である。好ましい塗布層としては、データーテープと同様の磁性層、若しくは、非磁性層を単独に、あるいは非磁性層(下層)上に磁性層(上層)を塗布した2層構成のものをMRヘッドに接触する側に設け、反対側にカーボンブラックを主体としたバックコート(バック層)を設ける。
塗布層の厚みは、単層、若しくは複数層の合計が0.1〜5.0μmが好ましく、0.5〜3.0μmが更に好ましい。支持体の厚みは、3〜25μmが好ましく、6〜20μmが更に好ましい。非磁性層上に磁性層を設けた構成の場合は、非磁性層厚み0.5〜4.5μm、好ましくは0.5〜2.5μm、磁性層厚みは0.03〜0.2μm、好ましくは0.05〜0.15μm、より好ましくは0.05〜0.10μmである。
カッピングは、以下により測定される値である。
テープを1m切り出し、測定環境(23℃、50%RH)に24時間保持する。長手方向中央部300mmを切り出し、塗布層を上にした状態(磁性層を設けた場合は磁性層を上にした状態)で平板上に3時間静置する。しかるのち、前記300mmの中央部100mm長のテープ幅(W2)をコンパレータで測定する。さらに同じサンプルにスライドグラスをかぶせた時のテープ幅(W1)を測定する。
カッピングは、次式の近似式にて求められる値を言う。
カッピング=(W2/2)tan(S1/2)
ただし、S=10×{1−(1.2W2/W1−0.2)1/2}
上記表面電気抵抗を所定に制御する手段としては、カーボンブラックなどの導電性粉末を例えば下層、上層及びバック層の少なくとも1層に添加することが挙げられる。例えば、各々の層の結合剤100質量部に対してカーボンブラックを1〜20質量部添加することが挙げられる。
以下、上記磁気テープをクリーニングテープとしたものについて、詳述する。
<磁性層および非磁性層の結合剤等>
磁性層、非磁性層に使用される結合剤としては従来公知の熱可塑性樹脂、熱硬化性樹脂、反応型樹脂やこれらの混合物が使用される。熱可塑性樹脂としては、ガラス転移温度が−100〜150℃、数平均分子量が1000〜200000、好ましくは10000〜100000、重合度が約50〜1000程度のものが使用される。
ポリウレタン樹脂中の水酸基の含有量は、1分子あたり3〜20個であるのが好ましく、より好ましくは1分子あたり4〜5個である。1分子あたり3個未満であるとポリイソシアネート硬化剤との反応性が低下するために、塗膜強度と耐久性が低下しやすい。また、20個より多いと、溶剤への溶解性と分散性が低下しやすい。ポリウレタン樹脂中の水酸基の含有量を調整するために、ポリウレタン樹脂の合成に際し、水酸基が3官能以上の化合物を用いることができる。具体的には、トリメチロールエタン、トリメチロールプロパン、無水トリメリット酸、グリセリン、ペンタエリスリトール、ヘキサントリオール、特公平6−64726号に記載されるポリエステルポリオールを原料とする2塩基酸と該化合物をグリコール成分として得られる3官能以上水酸基を有する分岐ポリエステル、ポリエーテルエステル等が挙げられる。好ましいのは3官能のものであり、4官能以上になると反応過程においてゲル化しやすくなる。
磁性層に使用する強磁性粉末としては、α−Feを主成分とする強磁性合金粉末、磁性酸化鉄、六方晶フェライト等が用いられるが、α―Feを主成分とする強磁性合金粉末が特に好ましい。強磁性粉末の平均粒子サイズは針状の場合、長軸長が20〜200nm、好ましくは30〜150nm、より好ましくは30〜100nmである。板状粒子の場合は板径が15〜50nm、好ましくは20〜45nmである。これらの強磁性粉末には所定の原子以外にAl、Si、S、Sc、Ca、Ti、V、Cr、Cu、Y、Mo、Rh、Pd、Ag、Sn、Sb、Te、Ba、Ta、W、Re、Au、Hg、Pb、Bi、La、Ce、Pr、Nd、P、Co、Mn、Zn、Ni、Sr、Bなどの原子を含んでもかまわない。特に、Al、Si、Ca、Y、Ba、La、Nd、Co、Ni、Bの少なくとも1つをα−Fe以外に含むことが好ましく、Co、Y、Alの少なくとも一つを含むことがさらに好ましい。
このような非磁性粒子としては、α化率90%以上のα−アルミナ、β−アルミナ、炭化ケイ素、酸化クロム、酸化セリウム、α−酸化鉄、コランダム、人造ダイアモンド、窒化珪素、炭化珪素、チタンカーバイト、酸化チタン、二酸化珪素、窒化ホウ素などの公知の材料が単独または組合せで使用される。また、これらの非磁性粒子どうしの複合体(非磁性粒子を他の非磁性粒子で表面処理したもの)を使用してもよい。これらの非磁性粒子には主成分以外の化合物または元素が含まれる場合もあるが主成分が90%以上であれば効果にかわりはない。タップ密度は0.3〜2g/cc、含水率は0.1〜5重量%、pHは2〜11、比表面積は1〜30m2 /g、が好ましい。本発明に用いられる非磁性粒子の形状は針状、球状、サイコロ状、のいずれでも良いが、形状の一部に角を有するものが研磨性が高く好ましい。
本発明に用いられる非磁性粒子の具体的な例としては、住友化学社製:AKP−20、AKP−30、AKP−50、HIT−50、日本化学工業社製:G5、G7、S−1、戸田工業社製:TF−100、TF−140、100ED、140EDなどがあげられる。本発明に用いられる非磁性粒子は磁性層のほかに、非磁性層にも種類、量および組合せを変えて添加することもできる。これらの非磁性粒子はあらかじめ結合剤で分散処理したのち磁性塗料中に添加してもかまわない。
非磁性粒子の添加量は、強磁性粉末に対して5〜30質量%、好ましくは10〜20質量%である。
また、非磁性粒子の平均粒径は、磁性層の厚みを考慮して決定するのが好ましい。これにより、非磁性粒子が磁性層表面に最適な高さの凸部を形成し、クリーニング効果が増大する。例えば、磁性層の厚みに対し、非磁性粒子の平均粒径は、50〜200%の範囲が好ましい。
非磁性層に用いられる無機粉末は、非磁性粉末であり、例えば、金属酸化物、金属炭酸塩、金属硫酸塩、金属窒化物、金属炭化物、金属硫化物、等の無機質化合物から選択することができる。非磁性層にカーボンブラックを混合させて公知の効果である表面電気抵抗Rsを下げること、光透過率を小さくすることができるとともに、所望のマイクロビッカース硬度を得る事ができる。また、下層にカーボンブラックを含ませることで潤滑剤貯蔵の効果をもたらすことも可能である。カーボンブラックの種類はゴム用ファーネス、ゴム用サーマル、カラー用ブラック、アセチレンブラック、等を用いることができる。下層のカーボンブラックは所望する効果によって、上記のような特性を最適化すべきであり、併用することでより効果が得られることがある。また非磁性層には有機質粉末を目的に応じて、添加することもできる。非磁性層の潤滑剤、分散剤、添加剤、溶剤、分散方法その他は磁性層に関する公知技術が適用できる。
磁性層、非磁性層等に使用される添加剤としては、ヘッド研磨効果、潤滑効果、帯電防止効果、分散効果、可塑効果などをもつものが使用される。具体的にはWO98/35345号等に記載のものが挙げられる。
潤滑剤としては、例えば、炭素数10〜24の一塩基性脂肪酸、およびこれらの金属塩(Li、Na、K、Cuなど)または炭素数10〜24の一塩基性脂肪酸と炭素数2〜12の一価、二価、三価、四価、五価、六価アルコールのいずれか一つとからなるモノ脂肪酸エステルまたはジ脂肪酸エステルまたはトリ脂肪酸エステル、アルキレンオキシド重合物のモノアルキルエーテルの脂肪酸エステル、炭素数8〜22の脂肪酸アミドなどが使用できる。上記脂肪酸及びアルコールは、不飽和結合を含んでも、また分岐していてもかまわない。
これらの具体例としては脂肪酸では、カプリン酸、カプリル酸、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、ベヘン酸、オレイン酸、エライジン酸、リノール酸、リノレン酸、イソステアリン酸、などが挙げられる。エステル類ではブチルステアレート、オクチルステアレート、アミルステアレート、イソオクチルステアレート、ブチルミリステート、オクチルミリステート、ブトキシエチルステアレート、ブトキシジエチルステアレート、2−エチルヘキシルステアレート、2−オクチルドデシルパルミテート、2−ヘキシルドデシルパルミテート、イソヘキサデシルステアレート、オレイルオレエート、ドデシルステアレート、トリデシルステアレート、エルカ酸オレイル、ネオペンチルグリコールジデカノエート、エチレングリコールジオレイル等が挙げられる。
バック層には、カーボンブラックと無機粉末が含有されていることが好ましい。結合剤、各種添加剤は、磁性層や非磁性層の処方が適用される。バック層の厚みは、0.1〜1.0μmが好ましく、0.4〜0.6μmが更に好ましい。
磁気テープに用いられる支持体は、非磁性可撓性支持体であることが好ましく、ポリエチレンテレフタレート、ポリエチレンナフタレート等のポリエステル類、ポリオレフィン類、セルローストリアセテート、ポリカーボネート、芳香族又は脂肪族ポリアミド、ポリイミド、ポリアミドイミド、ポリスルフォン、ポリアラミド、ポリベンゾオキサゾールなどの公知のフィルムが使用できる。中でもポリエチレンテレフタレートフィルム又はポリイミドフィルムを用いるのが好ましい。これらの支持体にはあらかじめコロナ放電処理、プラズマ処理、易接着処理、熱処理、除塵処理などを行ってもよい。支持体は、長さ方向の弾性率が3.5〜20GPa、幅方向の弾性率が3.5〜20GPa、好ましくは長さ方向及び幅方向共に弾性率が4〜15GPaとするのが好適である。なお、支持体に含まれるフィラー量を調節して、本発明で規定する突起数を制御できることは前述のとおりであり、例えばフィラーとしては、SiO2、CaCO3等が挙げられ、その添加量は、例えば樹脂に対して0.1〜3質量%である。
磁性層と非磁性層は、上記成分を溶媒に溶解乃至分散して各々の塗料を作製し、支持体(ウェブ)上に順じ塗布することにより作製できる。非磁性層が湿潤状態にあるうち磁性層を塗布するウエット・オン・ウエット方式でも非磁性層が乾燥した上に塗布するウエット・オン・ドライ方式でもよい。塗布乾燥されたウェブは適宜配向処理、カレンダ処理、スリットが施される。
[実施例1]
実施例中の「部」の表示は「質量部」を示す。
<塗布液の作製>
上層用塗料組成
強磁性金属粉末 100部
抗磁力Hc:191kA/m(2400Oe)
BET法による比表面積:62m2/g
結晶子サイズ:110Å
飽和磁化量σs:117A・m2/kg
平均長軸長:45nm
平均針状比:5
pH:9.3
Co/Fe:25原子%
Al/Fe:7原子%
Y/Fe:12原子%
塩化ビニル系共重合体(日本ゼオン社製MR−110) 10部
(−SO3Na含有量:5×10-6eq/g、重合度:350、
エポキシ基(モノマー単位で3.5質量%)
ポリエステルポリウレタン樹脂 10部
(ネオペンチルグリコール/カプロラクトンポリオール/MDI
=0.9/2.6/1(質量比)、
−SO3Na基:1×10-4eq/g含有)
αアルミナ(平均粒径:0.2μm) 10部
カーボンブラック(平均粒径:0.10μm) 1部
ブチルステアレート 1.5部
ステアリン酸 0.5部
メチルエチルケトン 150部
シクロヘキサノン 50部
トルエン 40部
非磁性粉末 針状α酸化鉄 80部
BET法による比表面積:58m2/g
平均長軸長:0.15μm
平均針状比:7.5
カーボンブラック 20部
平均一次粒子径:16nm
DBP吸油量:80ml/100g
pH:8.0
BET法による比表面積:250m2/g
塩化ビニル系共重合体 12部
日本ゼオン製MR−110
ポリエステルポリウレタン樹脂 5部
(ネオペンチルグリコール/カプロラクトンポリオール/MDI
=0.9/2.6/1(質量比)、
−SO3Na基:1×10-4eq/g含有)
ブチルステアレート 1.06部
ステアリン酸 1.18部
メチルエチルケトン 150部
シクロヘキサノン 50部
トルエン 40部
微粒子カーボンブラック 100部
(平均粒子径:40nm)
粗粒子カーボンブラック 100部
(平均粒子径:90nm)
αアルミナ(硬質無機粉末) 5部
(平均粒子径:200nm、モース硬度:9)
ニトロセルロース樹脂 90部
ポリウレタン樹脂 50部
ポリエステル樹脂 5部
分散剤:オレイン酸銅 5部
銅フタロシアニン 5部
硫酸バリウム(沈降性) 5部
(BF−1、平均粒子径:50nm、モース硬度:3、堺化学工業(株)製)
メチルエチルケトン 800部
トルエン 800部
得られた上層用塗料、下層用塗料を、ポリエチレンテレフタレート(PET)支持体A(厚さ:14.5μm、長さ(MD)方向のヤング率:500Kg/mm2(4.9GPa)、巾(TD)方法のヤング率:500Kg/mm2(4.9GPa)、上層塗布面の中心線平均表面粗さRa:35nm、バック面側Ra:36nm)上に上層、下層の乾燥後の厚みがそれぞれ0.1μm、1.4μmとなるよう同時重層塗布した。次いで、上層がまだ湿潤状態にあるうちに300mTの磁力をもつコバルト磁石と150mTの磁力をもつソレノイドを用いて配向処理を行った。その後、乾燥させることにより上層を形成した。
その後、支持体の他方の側(上層とは反対側)に、上記バック層用塗料を乾燥後の厚さが、0.5μmとなるように塗布し、乾燥してバック層を形成した。支持体の一方の面に上層そして他方の面にバック層がそれぞれ設けられたクリーニングテープ用のロールを得た。更に、加熱処理後のロールを加熱金属ロールと熱硬化性樹脂を芯金に被覆した弾性ロールから構成されるカレンダー処理機(温度:90℃、線圧:300Kg/cm(294kN/m))に通してカレンダー処理を行った。
得られたロールを50℃48時間、加熱処理を行った。その後1/2インチ幅に裁断してクリーニングテープを作製した。
支持体Aに対して支持体のフィラーの練り込み量を増加させて突起数を増加させた支持体Bを使用した以外は実施例1と同一条件でクリーニングテープを作製した。
支持体Aに対して支持体のフィラーの練り込み量を減少させて突起数を減少させた支持体Cを使用した以外は実施例1と同一条件でクリーニングテープを作製した。
実施例2に対してカレンダー処理を変更した以外は実施例2と同一条件でクリーニングテープを作製した。
実施例1に対して支持体Dを使用した以外は実施例1と同一条件でクリーニングテープを作製した。
得られた1/2吋巾のクリーニングテープをUltrium−2カートリッジに300m巻き込んだ。
上記試料を以下により評価し、表2に示した。
[クリーニングテープカートリッジの評価]
得られたクリーニングテープカートリッジを下記の測定条件に従って評価した。
(1)クリーニング力:富士写真フイルム(株)製Ultrium−2磁気テープカートリッジAを、MRヘッドを有するIBM社製Ultrium−2ドライブにセットし、記録波長0.4μmの信号を記録・再生させ、そのときの再生出力を0chと7ch(ヘッドモジュールの最上部と最下部)で測定する(初期出力)。しかる後にヘッド汚れ発生用カートリッジBを1往復走行させてヘッド汚れを発生させ、前記の記録済みUltrium−2磁気テープカートリッジAを再生させ出力を測定する(クリーニング前出力)。
次に本発明のクリーニングテープカートリッジCを1往復走行させた後、前記カートリッジAを再生させて出力を測定する(クリーニング後出力)。初期出力とクリーニング後出力の比(dB換算)をクリーニング力とした(0dBが理想:−1dB以上が許容範囲)。
前記クリーニングテープ用の組成物のうち磁性層中の研磨剤を添加しないものを作製して、Ra5nm、厚み6.8μmのPENベース上に非磁性層・磁性層・バック層を塗布後、前記クリーニングテープと同様の工程でカレンダー・裁断して、Ultrium−2カートリッジに609m巻き込んだ磁気テープカートリッジ。
(2)ヘッド摩耗:IBM社製Ultrium−2ドライブを用い、23℃70%RHで10分間、当該クリーニングテープを走行させ、その前後のMRヘッドの高さをAFMで測定し、ヘッド摩耗を算出した。(50nm/10分が許容範囲)
これに対し、比較例1のクリーニングテープは、突起数が本発明の範囲を超えているため、ヘッド摩耗が増大している。また、比較例2のクリーニングテープは、クリーニング力が極端に低下していることが分かる。
Claims (2)
- 支持体上の少なくとも一方の面に粉体および結合剤を含む塗布層を設け、前記塗布層と磁気ヘッドとを接触させるクリーニングテープであって、前記塗布層の中心線平均粗さRaが5〜25nmであり、かつ前記塗布層表面に25nm以上の高さの突起が60〜1700個/105μm2存在することを特徴とするクリーニングテープ。
- 前記塗布層が、前記支持体上に設けられた非磁性層と、前記非磁性層上に設けられた磁性層とを有することを特徴とする請求項1に記載のクリーニングテープ。