JP2006040572A - Positive active material for aqueous lithium secondary battery and aqueous lithium secondary battery - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a positive active material for an aqueous lithium secondary battery and the aqueous lithium secondary battery containing no expensive Co, displaying high discharge capacity, and having excellent charge discharge cycle characteristics. <P>SOLUTION: The aqueous lithium secondary battery 1 has a positive electrode 2 containing a positive active material, a negative electrode 3 containing a negative active material, and an aqueous electrolyte prepared by dissolving a lithium salt in water, and the positive active material for the aqueous lithium secondary battery is provided. The positive active material has a layer structure compound represented by general formula: Li<SB>t</SB>Ni<SB>x</SB>Mn<SB>y</SB>M<SB>z</SB>O<SB>2</SB>as the main component. Wherein, 0.9≤t≤1.2; 0.4≤x≤0.55; 0.4≤y≤0.55; 0≤z≤0.2; M is at least one element selected from Mg, Al, Fe, Ti, Ga, Cu, V, and Nb. The negative active material has a substance having lower occlusion potential and release potential than the compound represented by the general formula as the main component. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

本発明は、電解液として、リチウム塩を水に溶解してなる水溶液電解液を有する水系リチウム二次電池用の正極活物質、及び該正極活物質を用いた水系リチウム二次電池に関する。   The present invention relates to a positive electrode active material for an aqueous lithium secondary battery having an aqueous electrolyte solution obtained by dissolving a lithium salt in water as an electrolytic solution, and an aqueous lithium secondary battery using the positive electrode active material.

電解液の溶媒として有機系溶媒を用いた非水系のリチウム二次電池は、高電圧でエネルギー密度が高く、また小型・軽量化が図れることから、パソコンや携帯電話等の携帯情報端末等を中心に情報通信機器の分野で実用が進み、広く一般に普及するに至っている。また他の分野では、環境問題、資源問題から電気自動車の開発が急がれる中、このようなリチウム二次電池を電気自動車用電源として用いることが検討されている。   Non-aqueous lithium secondary batteries that use organic solvents as the solvent for the electrolyte solution are high voltage, high energy density, and can be reduced in size and weight, so they are mainly used in personal information terminals such as personal computers and mobile phones. In practical use in the field of information communication equipment, it has been widely spread. In other fields, the development of electric vehicles has been urgently promoted due to environmental issues and resource issues, and the use of such lithium secondary batteries as power sources for electric vehicles has been studied.

一般に、非水系のリチウム二次電池は、正極活物質としてリチウム遷移金属複合酸化物を、負極活物質として炭素材料を用い、非水電解液として有機溶媒にリチウム塩を溶解した電解液を用いて構成されている。
具体的には、正極活物質としては、例えばＬｉＣｏＯ₂、ＬｉＮｉＯ₂、及びＬｉＭｎ₂Ｏ₄等が用いられており、これらの活物質は、金属Ｌｉに対して３．５〜４．３Ｖの電位範囲で使用される。また、負極活物質としては炭素材料等が用いられており、１〜０．１Ｖ程度の電位範囲で使用される。非水系のリチウム二次電池は、このような正極活物質と負極活物質とを組み合わせることにより、単セルにおいて３〜４Ｖ級の高い起電力を発揮できる。 Generally, a non-aqueous lithium secondary battery uses a lithium transition metal composite oxide as a positive electrode active material, a carbon material as a negative electrode active material, and an electrolyte solution in which a lithium salt is dissolved in an organic solvent as a non-aqueous electrolyte solution. It is configured.
Specifically, for example, LiCoO ₂ , LiNiO ₂ , LiMn ₂ O _{4 and the} like are used as the positive electrode active material, and these active materials have a potential of 3.5 to 4.3 V with respect to the metal Li. Used in range. Moreover, a carbon material etc. are used as a negative electrode active material, and it is used in the electric potential range of about 1-0.1V. A non-aqueous lithium secondary battery can exhibit a high electromotive force of 3 to 4 V class in a single cell by combining such a positive electrode active material and a negative electrode active material.

しかし、非水系のリチウム二次電池には、次のような問題が指摘されている。
即ち、非水系のリチウム二次電池は、電解液として有機溶媒等の非水系電解液を含有しているため、常に引火や爆発の危険性を有している。過充電状態や高温環境下にされされた状態においては、特にその危険性が高い。
二次電池は、エネルギーを電気化学的に蓄え放出する装置である。したがって、電気化学的に蓄えたエネルギーが、例えば正極と負極との短絡等の何らかのきっかけで、急激に熱エネルギーに変換されてしまったときに、内部に可燃性の有機溶媒がある場合には、必然的に引火、爆発を引き起こすおそれがある。
このような問題は、特に電気自動車やハイブリッド車等のように大型の電池を必要とする用途においては致命的である。また、自動車用電源として用いると、使用温度や充放電サイクルの面でも過酷な条件で使用されることとなり、引火や爆発の危険性がより高くなると考えられている。 However, the following problems have been pointed out for non-aqueous lithium secondary batteries.
That is, since the nonaqueous lithium secondary battery contains a nonaqueous electrolytic solution such as an organic solvent as an electrolytic solution, there is always a risk of ignition or explosion. The danger is particularly high in an overcharged state or a state where the battery is subjected to a high temperature environment.
Secondary batteries are devices that store and release energy electrochemically. Therefore, when the energy stored electrochemically has been suddenly converted into thermal energy due to, for example, a short circuit between the positive electrode and the negative electrode, when there is a flammable organic solvent inside, There is a risk of fire and explosion.
Such a problem is particularly fatal in applications that require large batteries, such as electric vehicles and hybrid vehicles. Further, when used as a power source for automobiles, it is used under severe conditions in terms of operating temperature and charge / discharge cycle, and it is considered that the risk of ignition and explosion becomes higher.

ところで、非水系のリチウム二次電池は、電解液に水を使用しないため、水の電気分解反応に縛られることがなく、約４Ｖという高電圧の起電力を発揮することができる。その反面、電池内に水分が存在すれば、電気分解に伴ってガスが発生したり、リチウムとの反応により充放電サイクル特性が低下したり、また、副反応により充放電効率が低下したり、電池構成材料が腐食したりする等という様々な問題を引き起こすおそれがある。
そのため、非水系のリチウム二次電池においては、その製造工程において徹底したドライ環境を維持する必要があり、水分を完全に除去するために特殊な設備と多大な労力を要している。そのため、製造コストが高くなってしまうという問題がある。この観点からも、特に電気自動車用の二次電池をにらんだ将来の量産化に対応し難いという問題があった。 By the way, since the non-aqueous lithium secondary battery does not use water as an electrolyte, it is not restricted by the electrolysis reaction of water and can exhibit an electromotive force of a high voltage of about 4V. On the other hand, if moisture is present in the battery, gas is generated with electrolysis, charge / discharge cycle characteristics are reduced due to reaction with lithium, and charge / discharge efficiency is reduced due to side reactions, There is a risk of causing various problems such as corrosion of battery constituent materials.
Therefore, in a non-aqueous lithium secondary battery, it is necessary to maintain a thorough dry environment in the manufacturing process, and special equipment and a great deal of labor are required to completely remove moisture. Therefore, there exists a problem that manufacturing cost will become high. From this point of view as well, there is a problem that it is difficult to cope with mass production in the future with a view to secondary batteries for electric vehicles.

一方、電解液として水溶液を用いた水系リチウム二次電池がある。この水系リチウム二次電池は、上述の非水系リチウム二次電池が有する問題に対して非常に有利であると予測される。
即ち、水系リチウム二次電池は、電解液に有機溶媒を含有していないため、基本的には燃えることはない。また、製造工程においてドライ環境を必要としないため、製造にかかるコストを大幅に減少することができる。さらに、一般的に水溶液電解液は非水系電解液に比べて導電性が高いため、水系リチウム二次電池は、非水系のリチウム二次電池に比べて内部抵抗が低くなるという利点がある。 On the other hand, there is an aqueous lithium secondary battery using an aqueous solution as an electrolytic solution. This aqueous lithium secondary battery is expected to be very advantageous for the problems of the non-aqueous lithium secondary battery described above.
That is, the water-based lithium secondary battery does not basically burn because it does not contain an organic solvent in the electrolytic solution. In addition, since a dry environment is not required in the manufacturing process, manufacturing costs can be significantly reduced. Furthermore, since aqueous electrolytes generally have higher conductivity than non-aqueous electrolytes, aqueous lithium secondary batteries have the advantage of lower internal resistance than non-aqueous lithium secondary batteries.

しかし、水系リチウム二次電池は、水の電気分解反応が起こらない電位範囲での使用が求められる。そのため、水系リチウム二次電池は、非水系のリチウム二次電池と比較して起電力が小さくなる。水の電気分解電位から計算すると１．２Ｖ程度が限界であるが、実際には電気分解によりガスが発生するためには過電圧が必要であることから、２Ｖ程度が限界となる。このことは、水系リチウム二次電池は、高エネルギー密度、即ち軽くて小さいことを重視する携帯機器等の用途には向かないが、比較的コストを重視し、大型の電池が用いられる電気自動車やハイブリッド電気自動車、ひいては家庭用分散電源等の用途に適することが予想されている。   However, water-based lithium secondary batteries are required to be used in a potential range where no water electrolysis reaction occurs. Therefore, the electromotive force of the aqueous lithium secondary battery is smaller than that of the non-aqueous lithium secondary battery. When calculated from the electrolysis potential of water, the limit is about 1.2 V. However, in actuality, an overvoltage is necessary to generate gas by electrolysis, so about 2 V is the limit. This is because water-based lithium secondary batteries are not suitable for applications such as portable devices that emphasize high energy density, that is, light and small. It is expected to be suitable for applications such as hybrid electric vehicles and eventually household distributed power supplies.

水系リチウム二次電池を構成する上で重要なことは、水溶液中で安定で、かつ水の電気分解により酸素や水素を発生しない電位範囲において、可逆的に大量のリチウムを吸蔵及び脱離できる活物質、つまり特定の電位範囲において大きな容量を発揮できる活物質を用いる点にある。
また、電解液としては、中性からアルカリ性の電解液を用いることが望まれている。活物質として主として用いられる酸化物系の電極材料は、一般に酸性の水溶液中では安定性に乏しく、また、酸性電解液中の多量のＨ⁺イオンは、純粋なＬｉ⁺イオンのロッキングチェア反応を阻害するおそれがあるからである。 What is important for the construction of an aqueous lithium secondary battery is that it is stable in an aqueous solution and has an activity capable of reversibly occluding and desorbing a large amount of lithium in a potential range where oxygen and hydrogen are not generated by electrolysis of water. The substance is that an active material that can exhibit a large capacity in a specific potential range is used.
Further, it is desired to use a neutral to alkaline electrolyte as the electrolyte. Oxide-based electrode materials that are mainly used as active materials generally have poor stability in acidic aqueous solutions, and a large amount of H ⁺ ions in acidic electrolytes inhibit the rocking chair reaction of pure Li ⁺ ions. It is because there is a possibility of doing.

中性、即ちｐＨ＝７の電解液を用いた場合には、水の分解電圧は、水素発生電位が２．６２Ｖ、酸素発生電位が３．８５Ｖである。また、強アルカリ性、即ちｐＨ＝１４の電解液を用いた場合には、水の分解電圧は水素発生電位が２．２１Ｖ、酸素発生電位が３．４４Ｖである。
したがって、正極活物質としては、最低限３．８５Ｖ（ｐＨ＝７）までにより多くのＬｉが引き抜ける材料が望まれている。負極活物質としては、２．２１Ｖ（ｐＨ＝１４）までにより多くのＬｉが挿入できる材料が望まれている。ガス発生過電圧が存在するため、実際にはこの範囲外の電位においても使用可能ではあるが、自己放電や高温での使用を考えるとできるだけこの範囲内の電位で使用することが望まれる。 When a neutral, ie, pH = 7 electrolyte is used, the water decomposition voltage is 2.62V for hydrogen generation potential and 3.85V for oxygen generation potential. In addition, when a strong alkaline, that is, pH = 14 electrolytic solution is used, the water decomposition voltage has a hydrogen generation potential of 2.21 V and an oxygen generation potential of 3.44 V.
Therefore, as the positive electrode active material, a material from which more Li can be pulled out to a minimum of 3.85 V (pH = 7) is desired. As the negative electrode active material, a material into which more Li can be inserted up to 2.21 V (pH = 14) is desired. Since a gas generation overvoltage exists, it can be used even at a potential outside this range. However, considering self-discharge and use at a high temperature, it is desirable to use the potential within this range as much as possible.

現在までに、水系リチウム二次電池としては、正極活物質として、Ｌｉ−Ｍｎ酸化物、Ｌｉ−Ｎｉ酸化物、Ｌｉ−Ｃｏ酸化物等を含有し、負極活物質としてＬｉ−Ｍｎ酸化物、ＶＯ₂、ＬｉＶ₃Ｏ₈等を含有するものが提案されている（特許文献１及び２参照）。 To date, water-based lithium secondary batteries include Li—Mn oxide, Li—Ni oxide, Li—Co oxide and the like as the positive electrode active material, and Li—Mn oxide, VO as the negative electrode active material. ₂ and those containing LiV ₃ O ₈ have been proposed (see Patent Documents 1 and 2).

しかしながら、このような活物質は、放電容量や水溶液電解液中での安定性が未だ不充分であった。そのため、従来の水系リチウム二次電池は、容量が小さく、充放電を繰り返し行うことにより容量劣化が起こりやすいという問題があった。それ故、現状の水系リチウム二次電池は、未だアイデア段階を抜けておらず、従来の非水系のリチウム二次電池等に取って代わる程の実用性を備えるには至っていない。   However, such active materials still have insufficient discharge capacity and stability in aqueous electrolyte solutions. Therefore, the conventional water-based lithium secondary battery has a problem that the capacity is small and the capacity is easily deteriorated by repeated charging and discharging. Therefore, the current aqueous lithium secondary battery has not yet gone through the idea stage, and has not yet been practical enough to replace the conventional non-aqueous lithium secondary battery.

また、Ｌｉ−Ｃｏ酸化物等のようにＣｏを含む活物質は、高い放電容量を発揮できる一方で、高価なＣｏを含有するため、製造コストが増大するという問題がある。そのため、Ｃｏを含む活物質を水系リチウム二次電池に用いると、安価に製造できるという水系リチウム二次電池の利点が損なわれてしまう。したがって、Ｃｏを含む活物質は、電気自動車やハイブリッド電気自動車、及び家庭用分散電源等のように、特に水系リチウム二次電池の適用が望まれている用途に適していないという問題があった。   In addition, an active material containing Co, such as Li—Co oxide, can exhibit a high discharge capacity, but has a problem that manufacturing cost increases because it contains expensive Co. Therefore, when an active material containing Co is used for an aqueous lithium secondary battery, the advantage of the aqueous lithium secondary battery that it can be manufactured at low cost is impaired. Therefore, there has been a problem that an active material containing Co is not suitable for use in which application of a water-based lithium secondary battery is desired, such as an electric vehicle, a hybrid electric vehicle, and a household distributed power source.

特表平９−５０８４９０号公報JP-T-9-508490 特開２０００−７７０７３号公報JP 2000-77073 A

本発明はかかる従来の問題点に鑑みてなされたものであって、高価なＣｏを含まず、高い放電容量を発揮できると共に、充放電サイクル特性に優れた水系リチウム二次電池用正極活物質及び水系リチウム二次電池を提供しようとするものである。   The present invention was made in view of such conventional problems, and does not contain expensive Co, can exhibit a high discharge capacity, and has a positive electrode active material for an aqueous lithium secondary battery excellent in charge / discharge cycle characteristics, and The present invention intends to provide an aqueous lithium secondary battery.

第１の発明は、リチウム塩を水に溶解してなる水溶液電解液を有する水系リチウム二次電池用の正極活物質であって、
上記正極活物質は、一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂（０．９≦ｔ≦１．２、０．４≦ｘ≦０．５５、０．４≦ｙ≦０．５５、０≦ｚ≦０．２、Ｍは、Ｍｇ、Ａｌ、Ｆｅ、Ｔｉ、Ｇａ、Ｃｕ、Ｖ、及びＮｂから選ばれる１種以上）で表される層状構造の化合物を主成分とすることを特徴とする水系リチウム二次電池用正極活物質にある（請求項１）。 A first invention is a positive electrode active material for an aqueous lithium secondary battery having an aqueous electrolyte obtained by dissolving a lithium salt in water,
The positive electrode active material is represented by the general formula _{Li t Ni x Mn y M z} O 2 (0.9 ≦ t ≦ 1.2,0.4 ≦ x ≦ 0.55,0.4 ≦ y ≦ 0.55,0 ≦ z ≦ 0.2, M is mainly composed of a compound having a layered structure represented by one or more selected from Mg, Al, Fe, Ti, Ga, Cu, V, and Nb) The positive electrode active material for an aqueous lithium secondary battery is (Claim 1).

上記第１の発明の水系リチウム二次電池用正極活物質においては、上記一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂で表される層状構造の化合物を主成分としている。そして上記一般式で表される化合物は、その組成中に高価なＣｏを含んでおらず、比較的安価なＭｎを多く含んでいるため、低コストに製造することができる。そのため、電気自動車やハイブリッド電気自動車、及び家庭用分散電源等のように、量産化が要求される用途にも適用することができる。 In the positive electrode active material for aqueous lithium secondary battery of the first invention, are mainly composed of a compound of layered structure represented by the general formula _{Li t Ni x Mn y M z} O 2. And since the compound represented by the said general formula does not contain expensive Co in the composition and contains many comparatively cheap Mn, it can be manufactured at low cost. Therefore, the present invention can also be applied to uses that require mass production, such as electric vehicles, hybrid electric vehicles, and home-use distributed power supplies.

また、上記一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂で表される層状構造の化合物は、Ｌｉ以外の主要構成金属元素がＭｎのみで構成される層状ＬｉＭｎＯ₂やスピネル型ＬｉＭｎ₂Ｏ₄等に比べて、水の電気分解が起こらない電位範囲内でより多くの可逆容量を有している。そのため、上記正極活物質は、水系リチウム二次電池に用いたとき、高い放電容量を発揮することができる。さらに充放電を繰り返し行ったときの容量の劣化を防止することができ、充放電初期における高い放電容量を維持することができる。また、上記正極活物質は、水溶液電解液中においても安定であるため、水系リチウム二次電池の正極活物質として好適である。 Further, the compounds of the general formula _{Li t Ni x Mn y M z} O 2 represented by a layered structure, the layered LiMnO ₂ or spinel formed main constituent metal element other than Li are only Mn LiMn ₂ O _4, etc. Compared to the above, it has more reversible capacity within a potential range where electrolysis of water does not occur. Therefore, the positive electrode active material can exhibit a high discharge capacity when used in an aqueous lithium secondary battery. Furthermore, the capacity | capacitance deterioration when charging / discharging is performed repeatedly can be prevented, and the high discharge capacity in the initial stage of charging / discharging can be maintained. Moreover, since the said positive electrode active material is stable also in aqueous solution electrolyte solution, it is suitable as a positive electrode active material of a water-system lithium secondary battery.

このように、上記第１の発明によれば、高価なＣｏを含まず、高い放電容量を発揮できると共に、充放電サイクル特性に優れた水系リチウム二次電池用正極活物質及び水系リチウム二次電池を提供することができる。   Thus, according to the first aspect of the present invention, the positive electrode active material for an aqueous lithium secondary battery and the aqueous lithium secondary battery that do not contain expensive Co, can exhibit a high discharge capacity, and are excellent in charge / discharge cycle characteristics. Can be provided.

第２の発明は、正極活物質を含有する正極と、負極活物質を含有する負極と、リチウム塩を水に溶解してなる水溶液電解液とを有する水系リチウム二次電池において、
上記正極活物質は、一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂（０．９≦ｔ≦１．２、０．４≦ｘ≦０．５５、０．４≦ｙ≦０．５５、０≦ｚ≦０．２、Ｍは、Ｍｇ、Ａｌ、Ｆｅ、Ｔｉ、Ｇａ、Ｃｕ、Ｖ、及びＮｂから選ばれる１種以上）で表される層状構造の化合物を主成分とし、
上記負極活物質は、上記一般式で表される化合物よりも、リチウムの吸蔵・脱離電位が低い物質を主成分とすることを特徴とする水系リチウム二次電池にある（請求項２）。 A second invention is an aqueous lithium secondary battery having a positive electrode containing a positive electrode active material, a negative electrode containing a negative electrode active material, and an aqueous electrolyte obtained by dissolving a lithium salt in water.
The positive electrode active material is represented by the general formula _{Li t Ni x Mn y M z} O 2 (0.9 ≦ t ≦ 1.2,0.4 ≦ x ≦ 0.55,0.4 ≦ y ≦ 0.55,0 ≦ z ≦ 0.2, M is mainly composed of a compound having a layered structure represented by (one or more selected from Mg, Al, Fe, Ti, Ga, Cu, V, and Nb),
The negative electrode active material is an aqueous lithium secondary battery characterized in that a main component is a substance having a lower lithium insertion / extraction potential than the compound represented by the general formula (claim 2).

上記第２の発明の水系リチウム二次電池において最も注目すべき点は、上記水系リチウム二次電池は、一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂で表される層状構造の化合物を上記正極活物質の主成分としている点にある。
即ち、上記水系リチウム二次電池は、上記第１の発明の正極活物質を含有している。そのため、上記水系リチウム二次電池は、低コストで製造できると共に、従来の水系リチウム二次電池に比べて高い放電容量を示すことができる。また、上記水系リチウム二次電池においては、充放電によるサイクル劣化を抑制することができる。 The second most noteworthy in water based lithium secondary battery of the invention, the aqueous lithium secondary battery is represented by the general formula _{Li t Ni x Mn y M z} O 2 in the positive electrode of a compound of layered structure represented The main component of the active material is.
That is, the aqueous lithium secondary battery contains the positive electrode active material of the first invention. Therefore, the water based lithium secondary battery can be manufactured at a low cost, and can exhibit a higher discharge capacity than a conventional water based lithium secondary battery. Moreover, in the said water-system lithium secondary battery, cycle deterioration by charging / discharging can be suppressed.

このように、上記第２の発明によれば、高価なＣｏを含まず、高い放電容量を発揮できると共に、充放電サイクル特性に優れた水系リチウム二次電池を提供することができる。   As described above, according to the second aspect of the invention, it is possible to provide an aqueous lithium secondary battery that does not contain expensive Co, can exhibit a high discharge capacity, and is excellent in charge / discharge cycle characteristics.

次に、本発明の実施の形態について説明する。
本発明において、上記正極活物質は、一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂（０．９≦ｔ≦１．２、０．４≦ｘ≦０．５５、０．４≦ｙ≦０．５５、０≦ｚ≦０．２、Ｍは、Ｍｇ、Ａｌ、Ｆｅ、Ｔｉ、Ｇａ、Ｃｕ、Ｖ、及びＮｂから選ばれる１種以上）で表される層状構造の化合物を主成分とする。
上記一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂において、ｔ、ｘ、及びｙの値が上記の範囲を外れる場合には、上記正極活物質を用いて水系リチウム二次電池を構成したときに、その放電容量や充放電サイクル特性が劣化するおそれがある。 Next, an embodiment of the present invention will be described.
In the present invention, the cathode active material is represented by the general formula _{Li t Ni x Mn y M z} O 2 (0.9 ≦ t ≦ 1.2,0.4 ≦ x ≦ 0.55,0.4 ≦ y ≦ 0 .55, 0 ≦ z ≦ 0.2, M is mainly composed of a compound having a layered structure represented by one or more selected from Mg, Al, Fe, Ti, Ga, Cu, V, and Nb) .
In the general formula _{Li t Ni x Mn y M z} O 2, t, x, and if the value of y is outside the range described above, when configuring an aqueous lithium secondary battery using the positive electrode active material The discharge capacity and charge / discharge cycle characteristics may be deteriorated.

また、一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂において、Ｍは任意の成分である。Ｍは、Ｍｇ、Ａｌ、Ｆｅ、Ｔｉ、Ｇａ、Ｃｕ、Ｖ、及びＮｂから選ばれる１種以上である。ｚ＝０の場合には、上記一般式は、Ｌｉ_tＮｉ_xＭｎ_yＯ₂で表される。
上記正極活物質においては、Ｍを含有することもできるが、Ｍを含有しなくとも、優れた放電容量及び充放電サイクル特性を発揮することができる。 In the general formula _{Li t Ni x Mn y M z} O 2, M is an optional component. M is at least one selected from Mg, Al, Fe, Ti, Ga, Cu, V, and Nb. In the case of z = 0, the above formula is represented by _{Li t Ni x Mn y O 2} .
The positive electrode active material can contain M, but even when M is not contained, excellent discharge capacity and charge / discharge cycle characteristics can be exhibited.

上記一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂において、ｚは、０＜ｚ≦０．２であることが好ましい。
この場合には、上記一般式において、Ｍが必須成分となり、この場合には、上記正極活物質は、より優れた放電容量及び充放電サイクル特性を発揮することができる。
ｚが０．２を超える場合には、上記一般紙記で表される化合物の層状構造が不安定になったり、上記一般式で表される化合物がもはや層状構造をとれなくなったりするおそれがある。そのためこの場合には、上記正極活物質の充放電特性が低下するおそれがある。 In the general formula _{Li t Ni x Mn y M z} O 2, z is preferably 0 <z ≦ 0.2.
In this case, in the above general formula, M is an essential component, and in this case, the positive electrode active material can exhibit more excellent discharge capacity and charge / discharge cycle characteristics.
If z exceeds 0.2, the layered structure of the compound represented by the above general paper may become unstable, or the compound represented by the above general formula may no longer have a layered structure. . Therefore, in this case, the charge / discharge characteristics of the positive electrode active material may be deteriorated.

また、上記一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂で表される化合物としては、Ｍの種類や、ｔ、ｘ、ｙ、及びｚの範囲を変えることにより、種々のものが存在する。上記水系リチウム二次電池においては、これらのうち１種類を正極活物質として正極に用いることもできるが、２種以上を混合して用いることもできる。さらに、上記一般式で表される層状構造の化合物と公知の正極活物質とを混合したものを用いることもできる。 The compound represented by the general formula _{Li t Ni x Mn y M z} O 2, the type and the M, t, x, by changing the range of y, and z, there are various things. In the aqueous lithium secondary battery, one of these can be used as the positive electrode active material for the positive electrode, but two or more can be mixed and used. Furthermore, what mixed the compound of the layered structure represented with the said general formula and a well-known positive electrode active material can also be used.

上記正極活物質は、例えば、共沈法を用いてＮｉ、Ｍｎ、及びＭの混合水酸化物を作製し、該混合水酸化物を焼成することにより、ＮｉとＭｎとＭとの酸化物固溶体を作製し、該酸化物固溶体とＬｉＯＨとを焼成すること等により作製することができる。
焼成においては、粒成長が進むと特性が悪くなるため、できるだけ単一相になり、充分な結晶化が起こる最低の温度で焼成を行うことが好ましい。 The positive electrode active material is prepared by, for example, preparing a mixed hydroxide of Ni, Mn, and M using a coprecipitation method, and firing the mixed hydroxide, thereby forming an oxide solid solution of Ni, Mn, and M. And the oxide solid solution and LiOH are fired.
In firing, since the characteristics deteriorate as grain growth proceeds, it is preferable to perform firing at the lowest temperature at which a single phase is obtained and sufficient crystallization occurs.

また、上記第２の発明の水系リチウム二次電池において、上記負極活物質は、上記一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂で表される化合物よりも、リチウムの吸蔵・脱離電位が低い物質を主成分とする。
このような物質としては、例えばＬｉＶ₂Ｏ₄、ＬｉＶ₃Ｏ₈、Ｌｉ_1.5Ｖ₃Ｏ_y（７≦ｙ≦８）等のリチウムバナジウム複合酸化物、Ｌｉ₄Ｔｉ₅Ｏ₁₂等のリチウムチタン複合酸化物、鉄酸化物、及び鉄水酸化物等がある。 Further, the aqueous lithium secondary battery of the second invention, the negative electrode active material, than the compound represented by the general formula _{Li t Ni x Mn y M z} O 2, the absorption and desorption potential of lithium Mainly low substances.
Examples of such materials include lithium vanadium composite oxides such as LiV ₂ O ₄ , LiV ₃ O ₈ , Li _1.5 V ₃ O _y (7 ≦ y ≦ 8), and lithium titanium composites such as Li ₄ Ti ₅ O _12. There are oxides, iron oxides, iron hydroxides, and the like.

また、上記水系リチウム二次電池は、電解液としてリチウム塩を水に溶解してなる水溶液電解液を有する。
このようなリチウム塩としては、例えばＬｉＮＯ₃、ＬｉＯＨ、ＬｉＣｌ、及びＬｉ₂Ｓ等がある。これらのリチウム塩は、それぞれ単独で用いることもできるが、２種以上を併用することもできる。 Moreover, the said water-system lithium secondary battery has aqueous solution electrolyte solution formed by melt | dissolving lithium salt in water as electrolyte solution.
Examples of such a lithium salt include LiNO ₃ , LiOH, LiCl, and Li ₂ S. These lithium salts can be used alone or in combination of two or more.

次に、上記水溶液電解液のｐＨは、６〜１０であることが好ましい（請求項３）。
上記水溶液電解液のｐＨが６未満の場合には、上記一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂で表される化合物が不安定となり、電池の容量や充放電サイクル特性が低下するおそれがある。一方、ｐＨが１０を超える場合には、水の電気分解電位、即ち水素発生電位及び酸素発生電位がそれぞれ２．２１Ｖ及び３．４４Ｖまで低下する。そのため、正極や負極で酸素や水素が発生し易くなるおそれがある。 Next, the pH of the aqueous electrolyte solution is preferably 6 to 10. (Claim 3)
If the pH of the aqueous electrolyte solution is less than 6, the compound represented by the general formula _{Li t Ni x Mn y M z} O 2 becomes unstable, it may decrease the capacity and charge-discharge cycle characteristics of the battery is there. On the other hand, when the pH exceeds 10, the electrolysis potential of water, that is, the hydrogen generation potential and the oxygen generation potential are decreased to 2.21 V and 3.44 V, respectively. Therefore, oxygen and hydrogen may be easily generated at the positive electrode and the negative electrode.

また、上記水系リチウム二次電池においては、例えばリチウムを吸蔵・放出する正極及び負極と、これらの間に狭装されるセパレータと、正極及び負極間でリチウムを移動させる水溶液電解液などを主要構成要素として構成することができる。   The above-mentioned aqueous lithium secondary battery mainly includes, for example, a positive electrode and a negative electrode that store and release lithium, a separator that is sandwiched between them, and an aqueous electrolyte that moves lithium between the positive electrode and the negative electrode. Can be configured as an element.

上記水系リチウム二次電池において、正極は、例えば上記正極活物質に導電材及び結着材を混合し、必要に応じて適当な溶剤を加えてペースト状の正極合材としたものを成形し、必要に応じて電極密度を高めるべく圧縮して形成することができる。
導電材は、正極の電気伝導性を確保するためのものであり、例えばカーボンブラック、アセチレンブラック、黒鉛等の炭素物質粉末状体の１種又は２種以上を混合したものを用いることができる。 In the aqueous lithium secondary battery, the positive electrode is formed, for example, by mixing a conductive material and a binder with the positive electrode active material, and adding a suitable solvent as necessary to form a paste-like positive electrode mixture, If necessary, it can be compressed to increase the electrode density.
The conductive material is for ensuring the electrical conductivity of the positive electrode, and for example, a material obtained by mixing one or more carbon material powders such as carbon black, acetylene black, and graphite can be used.

結着材は、活物質粒子及び導電材粒子を繋ぎ止める役割を果たすものであり、例えばポリテトラフルオロエチレン、ポリフッ化ビニリデン、フッ素ゴム等の含フッ素樹脂、或いはポリプロピレン、ポリエチレン、ポリエチレンテレフタレート等の熱可塑性樹脂、若しくはポリアクリロニトリル系高分子等を用いることができる。
これら活物質、導電材、結着材を分散させる溶剤としては、例えばＮ−メチル−２−ピロリドン等の有機溶剤を用いることができる。 The binder serves to bind the active material particles and the conductive material particles. For example, a fluorine-containing resin such as polytetrafluoroethylene, polyvinylidene fluoride, or fluororubber, or heat such as polypropylene, polyethylene, or polyethylene terephthalate. A plastic resin, a polyacrylonitrile-based polymer, or the like can be used.
As a solvent for dispersing these active material, conductive material, and binder, for example, an organic solvent such as N-methyl-2-pyrrolidone can be used.

負極は、上記正極と同様に、例えば上記負極活物質に導電材や結着材を混合し、必要に応じて適当な溶媒を加えてペースト状にした負極合材を成形し、その後必要に応じてプレスして形成することができる。   As with the positive electrode, for example, the negative electrode active material is mixed with a conductive material or a binder, and if necessary, an appropriate solvent is added to form a paste-like negative electrode mixture. And press to form.

また、正極及び負極に狭装させるセパレータは、正極と負極とを分離し電解液を保持するものであり、例えばセルロース、ポリエチレン、及びポリプロピレン等の薄い微多孔膜を用いることができる。   In addition, the separator to be narrowly attached to the positive electrode and the negative electrode separates the positive electrode and the negative electrode and holds the electrolytic solution. For example, a thin microporous film such as cellulose, polyethylene, or polypropylene can be used.

また、上記水系リチウム二次電池の形状としては、例えばコイン型、円筒型、角型等がある。正極、負極、セパレータ及び水溶液電解液等を収容する電池ケースとしては、これらの形状に対応したものを用いることができる。   Examples of the shape of the water based lithium secondary battery include a coin shape, a cylindrical shape, and a square shape. As the battery case that accommodates the positive electrode, the negative electrode, the separator, the aqueous electrolyte, and the like, those corresponding to these shapes can be used.

（実施例１）
次に、本発明の実施例につき、図１及び図２を用いて説明する。
本例は、正極活物質及び該正極活物質を用いて水系リチウム二次電池を作製し、該水系リチウム二次電池の放電容量及び充放電サイクル特性を評価する例である。 Example 1
Next, an embodiment of the present invention will be described with reference to FIGS.
In this example, an aqueous lithium secondary battery is produced using a positive electrode active material and the positive electrode active material, and the discharge capacity and charge / discharge cycle characteristics of the aqueous lithium secondary battery are evaluated.

本例においては、正極活物質はＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂で表される層状構造の化合物で表される層状構造の化合物を主成分とする。
図１に示すごとく、本例の水系リチウム二次電池１は、正極活物質を含有する正極２と、負極活物質を含有する負極３と、リチウム塩を水に溶解してなる水溶液電解液とを有する。正極活物質は、上記のごとく、ＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂で表される層状構造の化合物を主成分とする。負極活物質は、ＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂よりも、リチウムの吸蔵・脱離電位が低い物質、即ちＬｉ_1.5Ｖ₃Ｏ_y（７≦ｙ≦８）を主成分とする。水溶液電解液は、リチウム塩としてのＬｉＮＯ₃を水に溶解してなる。 In this example, the positive electrode active material is mainly composed of a compound having a layered structure represented by a compound having a layered structure represented by LiNi _1/2 Mn _1/2 O ₂ .
As shown in FIG. 1, the aqueous lithium secondary battery 1 of this example includes a positive electrode 2 containing a positive electrode active material, a negative electrode 3 containing a negative electrode active material, and an aqueous electrolyte obtained by dissolving a lithium salt in water. Have As described above, the positive electrode active material is mainly composed of a compound having a layered structure represented by LiNi _1/2 Mn _1/2 O ₂ . The negative electrode active material is mainly composed of a material having a lower lithium insertion / desorption potential than LiNi _1/2 Mn _1/2 O ₂ , that is, Li _1.5 V ₃ O _y (7 ≦ y ≦ 8). The aqueous electrolyte solution is obtained by dissolving LiNO ₃ as a lithium salt in water.

水系リチウム二次電池１においては、ＣＲ２０１６型の電池ケース１１中に、正極２及び負極３と共に、これらの間に狭装させた状態でセパレータ４が配置されている。また、電池ケース１１内には、水溶液電解液が注入されている。電池ケース１１内の端部には、ガスケット５が配置されており、電池ケース１１は封口板１２により密閉されている。   In the water based lithium secondary battery 1, a separator 4 is disposed in a CR2016 type battery case 11 together with a positive electrode 2 and a negative electrode 3 in a state of being sandwiched between them. An aqueous electrolyte solution is injected into the battery case 11. A gasket 5 is disposed at an end in the battery case 11, and the battery case 11 is sealed with a sealing plate 12.

次に、本例の水系リチウム二次電池の作製方法につき、説明する。
まず、下記のようにして、正極活物質として、ＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂で表される層状構造の化合物を合成する。
ＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂の合成にあたっては、所謂共沈法を用いたＮｉ、Ｍｎの混合水酸化物の作製、焼成によるＮｉ、Ｍｎの酸化物固溶体の作製、及び該酸化物固溶体とＬｉＯＨとの焼成という三段階の反応を経て合成した。 Next, a manufacturing method of the water based lithium secondary battery of this example will be described.
First, a compound having a layered structure represented by LiNi _1/2 Mn _1/2 O ₂ is synthesized as a positive electrode active material as described below.
In the synthesis of LiNi _1/2 Mn _1/2 O ₂ , production of mixed hydroxides of Ni and Mn using a so-called coprecipitation method, production of Ni and Mn oxide solid solutions by firing, and the oxide solid solutions It was synthesized through a three-stage reaction of baking with LiOH.

具体的には、まず、硝酸ニッケル（II）・六水和物（Ｎｉ(ＮＯ₃)₂・６Ｈ₂Ｏ）と、酢酸マンガン（II）・無水（Ｃ₄Ｈ₆ＭｎＯ₄）とを、ＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂という組成になるような化学量論比にしたがって水に溶かして水溶液を作製した。このとき、水溶液中における各元素（Ｎｉ及びＭｎ）の濃度が１ｍｏｌ／Ｌとなるように調整した。
次いで、この水溶液のｐＨが８になるまで１０％アンモニア水を滴下し、Ｎｉ及びＭｎの混合水酸化物を得た。得られた混合水酸化物を充分に洗浄し、乾燥させた。 Specifically, first, nickel nitrate (II) .hexahydrate (Ni (NO ₃ ) ₂ .6H ₂ O), manganese acetate (II) .anhydrous (C ₄ H ₆ MnO ₄ ), LiNi _An aqueous solution was prepared by dissolving in water according to a stoichiometric ratio such that the composition was _1/2 Mn _1/2 O ₂ . At this time, the concentration of each element (Ni and Mn) in the aqueous solution was adjusted to 1 mol / L.
Next, 10% aqueous ammonia was added dropwise until the pH of the aqueous solution reached 8, to obtain a mixed hydroxide of Ni and Mn. The resulting mixed hydroxide was thoroughly washed and dried.

次に、この混合水酸化物を、窒素気流中で、温度４００℃にて仮焼した。これによりＮｉ及びＭｎの酸化物固溶体を得た。
続いて、水酸化リチウム・一水和物（ＬｉＯＨ・Ｈ₂Ｏ）をＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂という組成の化学量論比にしたがって水に溶かし、さらに上記にて得られた酸化物固溶体を加えて混合した。混合は、ボールミルを用いて１２時間行った。乾燥後、混合物を空気中にて、温度１５０℃で１時間加熱し、その後、さらに温度１０００℃にて１２時間焼成した。このようにして、ＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂で表される層状構造の化合物を作製した。これを正極活物質とする。 Next, this mixed hydroxide was calcined at a temperature of 400 ° C. in a nitrogen stream. Thereby, an oxide solid solution of Ni and Mn was obtained.
Subsequently, lithium hydroxide monohydrate (LiOH.H ₂ O) was dissolved in water according to the stoichiometric ratio of the composition LiNi _1/2 Mn _1/2 O ₂ , and the oxidation obtained above The solid solution was added and mixed. Mixing was performed for 12 hours using a ball mill. After drying, the mixture was heated in air at a temperature of 150 ° C. for 1 hour, and then calcined at a temperature of 1000 ° C. for 12 hours. In this way, a compound having a layered structure represented by LiNi _1/2 Mn _1/2 O ₂ was produced. This is a positive electrode active material.

次に、以下のようにして負極活物質としてのＬｉ_1.5Ｖ₃Ｏ_y（７≦ｙ≦８）を作製した。
まず、炭酸リチウム（Ｌｉ₂ＣＯ₃）１．６８８ｇと、五酸化バナジウム（Ｖ₂Ｏ₅）８．３１２ｇとを準備し、これらの混合物１０ｇを自動乳鉢で２時間混合した。次いで、混合物をアルゴン気流中で、４．３３℃／ｍｉｎの昇温速度で６８０℃まで昇温し、１２時間保持した。その後、４．３３℃／ｍｉｎの速度で冷却した。このようにして、Ｌｉ_1.5Ｖ₃Ｏ_y（７≦ｙ≦８）を作製した。これを負極活物質とする。 Next, Li _1.5 V ₃ O _y (7 ≦ y ≦ 8) as a negative electrode active material was produced as follows.
First, 1.688 g of lithium carbonate (Li ₂ CO ₃ ) and 8.31 g of vanadium pentoxide (V ₂ O ₅ ) were prepared, and 10 g of these mixtures were mixed in an automatic mortar for 2 hours. Next, the mixture was heated to 680 ° C. at a temperature increase rate of 4.33 ° C./min in an argon stream and held for 12 hours. Thereafter, it was cooled at a rate of 4.33 ° C./min. In this way, Li _1.5 V ₃ O _y (7 ≦ y ≦ 8) was produced. This is defined as a negative electrode active material.

次に、上記正極活物質及び負極活物質を用いて、水系リチウム二次電池を作製する。
具体的には、まず、正極活物質としてのＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂を７０重量部、導電剤としてのカーボンブラックを２５重量部、及び結着材としてのポリテトラフルオロエチレン（ＰＴＦＥ）を５重量部混合し、正極合材を作製した。
また、負極活物質としてのＬｉ_1.5Ｖ₃Ｏ_y（７≦ｙ≦８）を７０重量部、導電剤としてのカーボンブラックを２５重量部、及び結着材としてのポリテトラフルオロエチレン（ＰＴＦＥ）を５重量部混合し、負極合材を作製した。 Next, an aqueous lithium secondary battery is manufactured using the positive electrode active material and the negative electrode active material.
Specifically, first, 70 parts by weight of LiNi _1/2 Mn _1/2 O ₂ as a positive electrode active material, 25 parts by weight of carbon black as a conductive agent, and polytetrafluoroethylene (PTFE as a binder) ) Was mixed to prepare a positive electrode mixture.
Further, Li _1.5 V ₃ O _y (7 ≦ y ≦ 8) as a negative electrode active material is 70 parts by weight, carbon black as a conductive agent is 25 parts by weight, and polytetrafluoroethylene (PTFE) as a binder is used. 5 parts by weight was mixed to prepare a negative electrode mixture.

次に、図１に示すごとく、ＣＲ２０１６型のコインセル用の電池ケース１１を準備し、予め電池ケース１１の内側に溶接したメッシュ上に正極合材を約０．６ｔｏｎ／ｃｍ²で圧着して正極２を形成した。この正極２と同様にして、メッシュ上に負極合材を約０．６ｔｏｎ／ｃｍ²で圧着して負極３を形成した。
正極２及び負極３は、厚さ２５μｍのセルロース系のセパレータ４を介して、電池ケース１１内に配置した。 Next, as shown in FIG. 1, a battery case 11 for a CR2016 type coin cell is prepared, and a positive electrode mixture is pressure-bonded at about 0.6 ton / cm ² on a mesh previously welded to the inside of the battery case 11. 2 was formed. In the same manner as this positive electrode 2, the negative electrode mixture was pressed onto the mesh at about 0.6 ton / cm ² to form the negative electrode 3.
The positive electrode 2 and the negative electrode 3 were disposed in the battery case 11 via a cellulose separator 4 having a thickness of 25 μm.

次いで、電池ケース１１内にガスケット５を配置し、さらに電池ケース１１内に水溶液電解液を適量注入し含浸させた。本例においては、水溶液電解液としては、３ＭのＬｉＮＯ₃水溶液（ｐＨ≒７）を用いた。
次に、電池ケース１１の開口部に封口板１２を配置し、電池ケース１１の端部をかしめ加工することにより、電池ケース１１を密封して、水系リチウム二次電池１を作製した。これを電池Ｅ１とする。 Next, the gasket 5 was placed in the battery case 11, and an appropriate amount of an aqueous electrolyte solution was injected into the battery case 11 and impregnated. In this example, a 3M LiNO ₃ aqueous solution (pH≈7) was used as the aqueous electrolyte.
Next, the sealing plate 12 was disposed in the opening of the battery case 11, and the end of the battery case 11 was caulked to seal the battery case 11, thereby producing the aqueous lithium secondary battery 1. This is referred to as a battery E1.

また、本例においては、電池Ｅ１の優れた特性を明らかにするため、正極活物質として層状構造のＬｉＭｎＯ₂、又は層状岩塩型構造のＬｉＮｉ_0.8Ｃｏ_0.2Ｏ₂をそれぞれ有する２種類の水系リチウム二次電池（電池Ｃ１及び電池Ｃ２）を作製した。 Further, in this example, in order to clarify the excellent characteristics of the battery E1, two types of aqueous lithium secondary batteries each having LiMnO _{2 having} a layered structure or LiNi _0.8 Co _0.2 O ₂ having a layered rock salt structure as a positive electrode active material are used. Secondary batteries (battery C1 and battery C2) were produced.

具体的には、まず、２種類の正極活物質（ＬｉＭｎＯ₂、ＬｉＮｉ_0.8Ｃｏ_0.2Ｏ₂）を準備した。
層状構造のＬｉＭｎＯ₂の作製にあたっては、まず８０ｍｌのイオン交換水に６．２９ｇの水酸化リチウム一水和物を溶かし、さらに二酸化マンガンを２．６１ｇ加え、超音波分散を３０分間行った。リチウムとマンガンのモル比は５：１であった。その混合物をフッ素樹脂で内張されたオートクレーブ内で２００℃の水熱条件下で７日間反応させた。容器内の沈殿物を濾過し、その後水洗し、１２０℃で乾燥させて、層状構造（空間群Ｒ３−ｍ）のＬｉＭｎＯ₂を得た。
また、層状岩塩型構造ＬｉＮｉ_0.8Ｃｏ_0.2Ｏ₂は、Ｌｉ、Ｎｉ、及びＣｏの金属塩から液相法で合成することにより作製した。 Specifically, first, two types of positive electrode active materials (LiMnO ₂ and LiNi _0.8 Co _0.2 O ₂ ) were prepared.
In producing LiMnO _{2 having} a layered structure, 6.29 g of lithium hydroxide monohydrate was first dissolved in 80 ml of ion exchange water, and 2.61 g of manganese dioxide was further added, followed by ultrasonic dispersion for 30 minutes. The molar ratio of lithium to manganese was 5: 1. The mixture was reacted in an autoclave lined with a fluororesin under hydrothermal conditions at 200 ° C. for 7 days. The precipitate in the container was filtered, then washed with water, and dried at 120 ° C. to obtain LiMnO ₂ having a layered structure (space group R3-m).
The layered rock salt structure LiNi _0.8 Co _0.2 O ₂ was prepared by synthesizing from a metal salt of Li, Ni, and Co by a liquid phase method.

次に、これら２種類の正極活物質を用いて、上記電池Ｅ１と同様にして２種類の水系リチウム二次電池を作製した。これらを電池Ｃ１及び電池Ｃ２とする。
電池Ｃ１は、正極活物質として層状構造のＬｉＭｎＯ₂を含有する点を除いては、上記電池Ｅ１と同様のものである。
電池Ｃ２は、正極活物質として層状岩塩型構造のＬｉＮｉ_0.8Ｃｏ_0.2Ｏ₂を含有する点を除いては、上記電池Ｅ１と同様のものである。 Next, using these two types of positive electrode active materials, two types of aqueous lithium secondary batteries were produced in the same manner as the battery E1. Let these be the battery C1 and the battery C2.
The battery C1 is the same as the battery E1 except that it includes LiMnO ₂ having a layered structure as a positive electrode active material.
The battery C2 is the same as the battery E1 except that it includes LiNi _0.8 Co _0.2 O ₂ having a layered rock salt structure as a positive electrode active material.

次に、上記のようにして作製した３種類の水系リチウム二次電池（電池Ｅ１、電池Ｃ１及び電池Ｃ２）について、充放電サイクル特性を調べた（充放電サイクル試験）。
充放電サイクル試験は、各電池について、温度６０℃の条件下で、電流密度０．５ｍＡ／ｃｍ²の定電流にて電池電圧１．２Ｖまで充電し、その後電流密度０．５ｍＡ／ｃｍ²の定電流にて電池電圧０．１Ｖまで放電する充放電を１サイクルとし、このサイクルを１０サイクル繰り返すことにより行った。各充放電サイクルにおいては、１．２Ｖまで充電した後、及び０．１Ｖまで放電した後に、充電休止時間及び放電休止時間をそれぞれ１分間ずつ設けた。そして、各サイクル毎に、各電池（電池Ｅ１、電池Ｃ１、電池Ｃ２）の放電容量を測定した。 Next, charge / discharge cycle characteristics were examined for the three types of aqueous lithium secondary batteries (battery E1, battery C1, and battery C2) produced as described above (charge / discharge cycle test).
In the charge / discharge cycle test, each battery was charged to a battery voltage of 1.2 V at a constant current of a current density of 0.5 mA / cm ² under a temperature of 60 ° C., and then a current density of 0.5 mA / cm ² . Charging / discharging at a constant current up to a battery voltage of 0.1 V was taken as one cycle, and this cycle was repeated 10 times. In each charging / discharging cycle, after charging to 1.2V and discharging to 0.1V, a charging suspension time and a discharging suspension time were provided for 1 minute each. And the discharge capacity of each battery (battery E1, battery C1, battery C2) was measured for every cycle.

放電容量は、各サイクル毎の放電電流値（ｍＡ）を測定し、この放電電流値に放電に要した時間（ｈｒ）を乗じて得られた値を、電池内の正極活物質の重量（ｇ）で除することにより算出した。
その結果を図２に示す。 The discharge capacity is determined by measuring the discharge current value (mA) for each cycle, and multiplying this discharge current value by the time (hr) required for discharge to obtain the weight of the positive electrode active material in the battery (g ).
The result is shown in FIG.

図２において、横軸はサイクル数（回）を示し、縦軸は放電容量（ｍＡｈ／ｇ）を示すものである。同図には、正極活物質としてＬｉＮｉ_1/2Ｍｎ_1/2Ｏ₂を用いて構成した電池を電池Ｅ１とし、ＬｉＭｎＯ₂を用いて構成した電池を電池Ｃ１として表し、ＬｉＮｉ_0.8Ｃｏ_0.2Ｏ₂を用いて構成した電池を電池Ｃ２として表した。
また、電池Ｅ１、電池Ｃ１、及び電池Ｃ２の初期充電容量及び初期放電容量を下記の表１に示す。初期充電容量及び初期放電容量は、各電池の１回目の充電容量及び放電容量を示すものである。また、充電容量は、充電電流値（ｍＡ）を測定し、この充電電流値に充電に要した時間（ｈｒ）を乗じて得られた値を、電池内の正極活物質の重量（ｇ）で除することにより算出した。 In FIG. 2, the horizontal axis indicates the number of cycles (times), and the vertical axis indicates the discharge capacity (mAh / g). In the figure, a battery configured using LiNi _1/2 Mn _1/2 O ₂ as a positive electrode active material is referred to as a battery E1, a battery configured using LiMnO ₂ is referred to as a battery C1, and LiNi _0.8 Co _0.2 O _2. A battery constituted by using was represented as a battery C2.
The initial charge capacity and initial discharge capacity of the battery E1, the battery C1, and the battery C2 are shown in Table 1 below. The initial charge capacity and the initial discharge capacity indicate the first charge capacity and discharge capacity of each battery. Further, the charge capacity is obtained by measuring the charge current value (mA) and multiplying the charge current value by the time (hr) required for charging, as the weight (g) of the positive electrode active material in the battery. It was calculated by dividing.

表１より知られるごとく、電池Ｅ１は、電池Ｃ１及び電池Ｃ２に比べて初期充電容量は小さいものの、大きな初期放電容量を発揮できることがわかる。
また、図２から知られるごとく、電池Ｃ２は、３サイクル目まで放電容量が増加し、その後低下するという特異な特性を示したが、電池Ｅ、電池Ｃ１、及び電池Ｃ２は、いずれもほぼ同程度の放電容量の低下率を示した。しかし、電池Ｅは、電池Ｃ１及び電池Ｃ２に比べて、初期放電容量が顕著に高く、充放電サイクルを繰り返した後においてもこの高い放電容量を維持し、電池Ｃ１及び電池Ｃ２に比べて高い放電容量を発揮できることがわかる。 As is known from Table 1, it can be seen that the battery E1 can exhibit a large initial discharge capacity although the initial charge capacity is smaller than those of the battery C1 and the battery C2.
In addition, as is known from FIG. 2, the battery C2 exhibited a unique characteristic that the discharge capacity increased until the third cycle and then decreased, but all of the battery E, the battery C1, and the battery C2 are substantially the same. The rate of decrease in discharge capacity was shown. However, the battery E has a remarkably high initial discharge capacity compared to the batteries C1 and C2, and maintains this high discharge capacity even after repeating the charge / discharge cycle, and the discharge is higher than that of the batteries C1 and C2. It turns out that capacity can be demonstrated.

このように、本例の電池Ｅ１は、従来の水系リチウム二次電池に比べて、高い容量を発揮できると共に、優れた充放電サイクル特性を発揮できることがわかる。また、電池Ｅ１は、正極活物質の組成中に高価なＣｏを含んでおらず、安価に製造することができる。   Thus, it turns out that the battery E1 of this example can exhibit a high capacity | capacitance compared with the conventional water-system lithium secondary battery, and can exhibit the outstanding charging / discharging cycling characteristics. Further, the battery E1 does not contain expensive Co in the composition of the positive electrode active material, and can be manufactured at a low cost.

実施例１にかかる、水系リチウム二次電池の構成を示す説明図。BRIEF DESCRIPTION OF THE DRAWINGS Explanatory drawing which shows the structure of the water-system lithium secondary battery concerning Example 1. FIG. 実施例１にかかかる、３種類の水系リチウム二次電池（電池Ｅ１、電池Ｃ１、電池Ｃ２）の充放電サイクル特性を示す線図。The diagram which shows the charging / discharging cycle characteristic of three types of water based lithium secondary batteries (battery E1, battery C1, battery C2) concerning Example 1. FIG.

符号の説明Explanation of symbols

１ 水系リチウム二次電池
２ 正極
３ 負極 1 Water-based lithium secondary battery 2 Positive electrode 3 Negative electrode

Claims (3)

リチウム塩を水に溶解してなる水溶液電解液を有する水系リチウム二次電池用の正極活物質であって、
上記正極活物質は、一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂（０．９≦ｔ≦１．２、０．４≦ｘ≦０．５５、０．４≦ｙ≦０．５５、０≦ｚ≦０．２、Ｍは、Ｍｇ、Ａｌ、Ｆｅ、Ｔｉ、Ｇａ、Ｃｕ、Ｖ、及びＮｂから選ばれる１種以上）で表される層状構造の化合物を主成分とすることを特徴とする水系リチウム二次電池用正極活物質。 A positive electrode active material for an aqueous lithium secondary battery having an aqueous electrolyte obtained by dissolving a lithium salt in water,
The positive electrode active material is represented by the general formula _{Li t Ni x Mn y M z} O 2 (0.9 ≦ t ≦ 1.2,0.4 ≦ x ≦ 0.55,0.4 ≦ y ≦ 0.55,0 ≦ z ≦ 0.2, M is mainly composed of a compound having a layered structure represented by one or more selected from Mg, Al, Fe, Ti, Ga, Cu, V, and Nb) A positive electrode active material for an aqueous lithium secondary battery. 正極活物質を含有する正極と、負極活物質を含有する負極と、リチウム塩を水に溶解してなる水溶液電解液とを有する水系リチウム二次電池において、
上記正極活物質は、一般式Ｌｉ_tＮｉ_xＭｎ_yＭ_zＯ₂（０．９≦ｔ≦１．２、０．４≦ｘ≦０．５５、０．４≦ｙ≦０．５５、０≦ｚ≦０．２、Ｍは、Ｍｇ、Ａｌ、Ｆｅ、Ｔｉ、Ｇａ、Ｃｕ、Ｖ、及びＮｂから選ばれる１種以上）で表される層状構造の化合物を主成分とし、
上記負極活物質は、上記一般式で表される化合物よりも、リチウムの吸蔵・脱離電位が低い物質を主成分とすることを特徴とする水系リチウム二次電池。 In an aqueous lithium secondary battery having a positive electrode containing a positive electrode active material, a negative electrode containing a negative electrode active material, and an aqueous electrolyte obtained by dissolving a lithium salt in water,
The positive electrode active material is represented by the general formula _{Li t Ni x Mn y M z} O 2 (0.9 ≦ t ≦ 1.2,0.4 ≦ x ≦ 0.55,0.4 ≦ y ≦ 0.55,0 ≦ z ≦ 0.2, M is mainly composed of a compound having a layered structure represented by (one or more selected from Mg, Al, Fe, Ti, Ga, Cu, V, and Nb),
The water-based lithium secondary battery, wherein the negative electrode active material contains a substance having a lower lithium insertion / extraction potential than the compound represented by the general formula. 請求項２において、上記水溶液電解液のｐＨは、６〜１０であることを特徴とする水系リチウム二次電池。   The aqueous lithium secondary battery according to claim 2, wherein the aqueous electrolyte solution has a pH of 6 to 10.