JP2005347316A - Thermally conductive sheet - Google Patents
Thermally conductive sheet Download PDFInfo
- Publication number
- JP2005347316A JP2005347316A JP2004161900A JP2004161900A JP2005347316A JP 2005347316 A JP2005347316 A JP 2005347316A JP 2004161900 A JP2004161900 A JP 2004161900A JP 2004161900 A JP2004161900 A JP 2004161900A JP 2005347316 A JP2005347316 A JP 2005347316A
- Authority
- JP
- Japan
- Prior art keywords
- organic
- conductive sheet
- inorganic hybrid
- heat
- thermally conductive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、例えば発熱性電子部品等の発熱体と放熱器等との間に介在せしめられる熱伝導性シートに関するものである。 The present invention relates to a heat conductive sheet interposed between a heat generator such as a heat-generating electronic component and a radiator.
電気機器や電子機器の高性能化に伴い、これらの発熱性電子部品の消費電力が高くなっている。そのため発熱性電子部品から発生する熱量も増加傾向にあり、発熱性電子部品から効率良く熱を除去することが、電気機器や電子機器の熱対策上の重要な課題となっている。
そこで、発熱性電子部品を冷却する方法として、一般的に、発熱性電子部品の表面に金属板や放熱器（ヒートシンク）等の放熱体を、熱伝導性シートや、グリースを介して、圧接し、放熱面積を大きくすることが行われている。該熱伝導性シートには、特に高い電気絶縁性、熱伝導性が要求されている。
また該熱伝導性シートには、シート（もしくはテープ）としての機械的強度が求められるため、強度を向上させるためのガラスクロスを内包した熱伝導性シートも提供されている。
With the improvement in performance of electric and electronic devices, the power consumption of these heat generating electronic components is increasing. For this reason, the amount of heat generated from the heat-generating electronic components is also increasing, and efficiently removing heat from the heat-generating electronic components has become an important issue in heat countermeasures for electrical and electronic devices.
Therefore, as a method of cooling the heat-generating electronic component, generally, a heat sink such as a metal plate or a radiator (heat sink) is press-contacted to the surface of the heat-generating electronic component via a heat conductive sheet or grease. In order to increase the heat dissipation area, it has been carried out. The heat conductive sheet is required to have particularly high electrical insulation and heat conductivity.
In addition, since the heat conductive sheet is required to have mechanical strength as a sheet (or tape), a heat conductive sheet including a glass cloth for improving the strength is also provided.
上記熱伝導性シートの材料として、電気絶縁性、耐熱性、柔軟性等の観点より、シリコーンゴムをベースポリマーとする組成物に、熱伝導性充填剤を配合させたものが使用されていた（例えば、特許文献１参照）。このような熱伝導性シートは、電気絶縁性、熱伝導性等に優れ、汎用されている。 As a material for the heat conductive sheet, a composition in which a heat conductive filler is blended with a composition having a silicone rubber as a base polymer has been used from the viewpoint of electrical insulation, heat resistance, flexibility, and the like ( For example, see Patent Document 1). Such a heat conductive sheet is excellent in electrical insulation, heat conductivity and the like, and is widely used.
熱伝導性充填剤を配合したシリコーンゴム組成物からなる熱伝導性シートは、電気絶縁性、熱伝導性に優れるものの、１８０℃以上の高温条件下で長時間連続使用できる耐熱性を有しておらず、問題となっている。
また熱伝導性シートのベースポリマーとして使用するシリコーンポリマーは高温度下において、側鎖のメチル基の酸化による架橋によって架橋点が増加する事により硬度上昇、伸び低下などの物理特性が低下する。またシロキサン結合が解重合を起こしポリマーが切断される事によるシロキサンの低分子化や環状シロキサンが発生し硬度低下、軟化現象が起こり、さまざまな熱劣化現象が発生する。
シリコーンポリマーをベースとした熱伝導性シートは、その表面に粘着性を有する為、粘着防止の為の打ち粉を付ける為、電子機器の組み立て工程やクリーンルームを汚染するという問題がある。
所で、該シリコーンゴム組成物は粘度が高く流動性が悪いので、トランスファー成形法によってシート状に成形されることが多い。トランスファー成形法は、一般的に寸法精度の良い成形品が得られることで知られているが、該シリコーンゴム組成物を使用する場合、該シリコーンゴム組成物の離型性が悪いので、型崩れし易く、熱伝導性シートが変形してしまう場合があり、問題となっている。
A heat conductive sheet made of a silicone rubber composition containing a heat conductive filler is excellent in electrical insulation and heat conductivity, but has heat resistance that can be used continuously for a long time at a high temperature of 180 ° C. or higher. Not a problem.
In addition, the silicone polymer used as the base polymer of the heat conductive sheet is deteriorated in physical properties such as an increase in hardness and a decrease in elongation due to an increase in cross-linking points due to cross-linking by oxidation of the methyl group in the side chain at a high temperature. In addition, the siloxane bond undergoes depolymerization and the polymer is cleaved, so that the molecular weight of the siloxane is reduced and cyclic siloxane is generated, causing a decrease in hardness and a softening phenomenon, and various thermal deterioration phenomena occur.
A heat conductive sheet based on a silicone polymer has adhesiveness on its surface, and thus has a problem of contaminating an electronic device assembly process and a clean room because it is applied with dust to prevent adhesion.
However, since the silicone rubber composition has high viscosity and poor fluidity, it is often formed into a sheet by a transfer molding method. The transfer molding method is generally known to obtain a molded article with good dimensional accuracy. However, when the silicone rubber composition is used, the silicone rubber composition is not releasable, so that it loses its shape. This is a problem because the heat conductive sheet may be deformed.
本発明は上記課題を解決するための手段として、内層と、該内層の両面に形成される外層を有し、該内層は、金属アルコキシドと、片末端または両末端に該金属アルコキシドと反応可能な官能基を有するオルガノポリシロキサンと、熱伝導性フィラーとを含む有機・無機ハイブリッド配合物を、多孔性シートに含浸し、該有機・無機ハイブリッド配合物を加熱硬化せしめてなる層であり、該外層は、該有機・無機ハイブリッド配合物を加熱硬化せしめてなる有機・無機ハイブリッド層である熱伝導性シートを提供するものである。
上記熱伝導性シートは、硬度（ＪＩＳタイプＡ硬度）が２０〜９５であることが望ましい。また上記多孔性シートはガラスクロスであることが望ましい。
また上記熱伝導性フィラーは、金属酸化物および／または金属窒化物および／または金属炭化物の微粒子であることが望ましい。
As a means for solving the above-mentioned problems, the present invention has an inner layer and an outer layer formed on both sides of the inner layer, and the inner layer can react with the metal alkoxide at one or both ends. A layer formed by impregnating a porous sheet with an organic / inorganic hybrid compound containing an organopolysiloxane having a functional group and a thermally conductive filler, and heat-curing the organic / inorganic hybrid compound, the outer layer Provides a heat conductive sheet which is an organic / inorganic hybrid layer obtained by heat-curing the organic / inorganic hybrid blend.
The heat conductive sheet preferably has a hardness (JIS type A hardness) of 20 to 95. The porous sheet is preferably a glass cloth.
The heat conductive filler is preferably fine particles of metal oxide and / or metal nitride and / or metal carbide.
本発明の熱伝導性シートは、熱伝導性、電気絶縁性、耐熱性に優れ、更に、離型性に優れるものである。 The heat conductive sheet of this invention is excellent in heat conductivity, electrical insulation, and heat resistance, and is excellent in releasability.
本発明の熱伝導性シートは、内層と、該内層の両面に形成される外層を有する。該内層は、金属アルコキシドと、片末端または両末端に該金属アルコキシドと反応可能な官能基を有するオルガノポリシロキサンと、熱伝導性フィラーとを含む有機・無機ハイブリッド配合物を、多孔性シートに含浸し、該有機・無機ハイブリッド配合物を加熱硬化せしめてなる層からなる。また該外層は、該有機・無機ハイブリッド配合物を加熱硬化せしめてなる有機・無機ハイブリッド層からなる。以下、本発明の熱伝導性シートについて詳細に説明する。 The heat conductive sheet of this invention has an inner layer and the outer layer formed in both surfaces of this inner layer. The inner layer impregnates a porous sheet with an organic / inorganic hybrid compound containing a metal alkoxide, an organopolysiloxane having a functional group capable of reacting with the metal alkoxide at one or both ends, and a thermally conductive filler. And a layer formed by heat-curing the organic / inorganic hybrid blend. The outer layer is composed of an organic / inorganic hybrid layer obtained by heat-curing the organic / inorganic hybrid blend. Hereinafter, the heat conductive sheet of the present invention will be described in detail.
〔金属アルコキシド〕
本発明で使用される金属アルコキシドの金属の種類としては、ホウ素、アルミニウム、ケイ素、チタン、バナジウム、マンガン、鉄、コバルト、亜鉛、ゲルマニウム、イットリウム、ジルコニウム、ニオブ、ランタン、セリウム、カドミウム、タンタル、タングステン等のアルコキシドが挙げられるが、特に望ましい金属は、チタン、ジルコニウムである。
またアルコキシドの種類としては特に限定されることなく、例えばメトキシド、エトキシド、ｎ−プロポキシド、ｉｓｏ−プロポキシド、ｎ−ブトキシド、ｉｓｏ−ブトキシド、ｓｅｃ−ブトキシド、ｔｅｒｔ−ブトキシド、メトキシエトキシド、エトキシエトキシド等が挙げられる。
上記アルコキシドは、使用するオルガノポリシロキサンとの反応性を適宜検討して選択されるが、一般的に、プロポキシドを使用することが望ましい。
上記金属はアセト酢酸メチル、アセト酢酸エチル、アセト酢酸イソプロピル等のアセト酢酸エステル等の化学修飾剤によって化学修飾されることが望ましい。
[Metal alkoxide]
Metal types of metal alkoxide used in the present invention include boron, aluminum, silicon, titanium, vanadium, manganese, iron, cobalt, zinc, germanium, yttrium, zirconium, niobium, lanthanum, cerium, cadmium, tantalum, tungsten Among them, particularly desirable metals are titanium and zirconium.
The type of alkoxide is not particularly limited. For example, methoxide, ethoxide, n-propoxide, iso-propoxide, n-butoxide, iso-butoxide, sec-butoxide, tert-butoxide, methoxyethoxide, ethoxyethoxy And the like.
The alkoxide is selected by appropriately considering the reactivity with the organopolysiloxane to be used, but it is generally desirable to use propoxide.
The metal is desirably chemically modified with a chemical modifier such as acetoacetate such as methyl acetoacetate, ethyl acetoacetate, and isopropyl acetoacetate.
〔オルガノポリシロキサン〕
本発明で使用されるポリオルガノシロキサンとして、片末端または両末端シラノールポリジメチルシロキサン等の片末端または両末端に金属アルコキシドと反応可能な官能基を有するオルガノポリシロキサン等を使用することが望ましい。
[Organopolysiloxane]
As the polyorganosiloxane used in the present invention, it is desirable to use an organopolysiloxane having a functional group capable of reacting with a metal alkoxide at one or both ends, such as one-end or both-end silanol polydimethylsiloxane.
上記オルガノポリシロキサンとしては、一般に重量平均分子量が４００〜７００００の範囲にあるものが使用される。金属アルコキシドとの反応性の観点から、重量平均分子量が５０００〜４００００の範囲にあるオルガノポリシロキサンが好ましい。
重量平均分子量が上記範囲にあるオルガノポリシロキサンを使用した有機・無機ハイブリッド層は、高温条件下で連続使用しても劣化し難く、熱伝導性、絶縁性等の機能が安定している。
オルガノポリシロキサンの重量平均分子量が５０００未満であると、得られる有機・無機ハイブリッド層は、耐熱耐久性に欠ける。
１５０℃以上の高温条件下では、重量平均分子量が１５０００以上のオルガノポリシロキサンを使用することが望ましい。該オルガノポリシロキサンの重量平均分子量が７００００を超えると、ゾル液の粘度が高くなり過ぎてフィラーの配合が困難になる。
該オルガノポリシロキサンの重量平均分子量が１５０００未満であると、得られる有機・無機ハイブリット材料の耐熱性が劣る。
As the organopolysiloxane, those having a weight average molecular weight in the range of 400 to 70000 are generally used. From the viewpoint of reactivity with the metal alkoxide, an organopolysiloxane having a weight average molecular weight in the range of 5,000 to 40,000 is preferable.
An organic / inorganic hybrid layer using an organopolysiloxane having a weight average molecular weight within the above range hardly deteriorates even when continuously used under high temperature conditions, and functions such as thermal conductivity and insulation are stable.
When the weight average molecular weight of the organopolysiloxane is less than 5000, the resulting organic / inorganic hybrid layer lacks heat resistance and durability.
It is desirable to use an organopolysiloxane having a weight average molecular weight of 15000 or higher under a high temperature condition of 150 ° C. or higher. When the weight average molecular weight of the organopolysiloxane exceeds 70,000, the viscosity of the sol solution becomes too high and it becomes difficult to blend the filler.
When the weight average molecular weight of the organopolysiloxane is less than 15,000, the resulting organic / inorganic hybrid material has poor heat resistance.
該オルガノポリシロキサンの片末端または両末端に存する金属または半金属のアルコキシドと反応可能な官能基とは、例えば以下に示される官能基（化学式１〜化学式１３）である。なお化学式のＲおよびR´は、メチレン、アルキレン、アルキルを示す。 The functional group capable of reacting with the metal or semi-metal alkoxide at one or both ends of the organopolysiloxane is, for example, the following functional groups (Chemical Formula 1 to Chemical Formula 13). In the chemical formula, R and R ′ represent methylene, alkylene, and alkyl.
−Cl、Br等のハロゲン原子
-Halogen atoms such as Cl and Br
また、必要に応じて、上記オルガノポリシロキサンと共に、ジアルキルジアルコキシシランを使用してもよい。
該ジアルキルジアルコキシシランとしては、例えば、ジメチルジメトキシシラン、ジメチルジエトキシシラン、ジメチルジプロポキシシラン、ジメチルジブトキシシラン、ジエチルジメトキシシラン、ジエチルジエトキシシラン、ジエチルジプロポキシシラン、ジエチルジブトキシシラン、ジプロピルジメトキシシラン、ジプロピルジエトキシシラン、ジプロピルジプロポキシシラン、ジプロピルジブトキシシラン、ジフェニルジメトキシシラン、ジフェニルジエトキシシラン、ジフェニルジプロポキシシラン、ジフェニルジブトキシシラン等が挙げられる。
Moreover, you may use a dialkyl dialkoxysilane with the said organopolysiloxane as needed.
Examples of the dialkyl dialkoxysilane include dimethyldimethoxysilane, dimethyldiethoxysilane, dimethyldipropoxysilane, dimethyldibutoxysilane, diethyldimethoxysilane, diethyldiethoxysilane, diethyldipropoxysilane, diethyldibutoxysilane, and dipropyl. Examples include dimethoxysilane, dipropyldiethoxysilane, dipropyldipropoxysilane, dipropyldibutoxysilane, diphenyldimethoxysilane, diphenyldiethoxysilane, diphenyldipropoxysilane, diphenyldibutoxysilane, and the like.
〔熱伝導性フィラー〕
本発明で使用される熱伝導性フィラーとしては、金属酸化物および／または金属窒化物および／または金属炭化物の微粒子であることが望ましい。例えば、酸化アルミニウム、酸化マグネシウム、酸化亜鉛、酸化ニッケル、酸化チタン、酸化ケイ素、酸化バナジウム、酸化銅、酸化鉄、酸化銀等の金属酸化物、または窒化アルミニウム、窒化硼素、炭化ケイ素、窒化ケイ素等の金属窒化物または金属炭化物等がある。
熱伝導性フィラーの粒子形状は、球状およびフレーク状のいずれでもよいが、その平均粒子径は、通常、０．１μｍ〜３００μｍの範囲内であることが望ましい。
熱伝導性フィラーは、金属アルコキシド溶液とオルガノポリシロキサン溶液とを混合して得られるゾル液に添加される。該ゾル液への分散性、物理特性を改善するために、該熱伝導性フィラーにダイレクトブレンド法、インテグラルブレンド法、スラリー法などによって表面処理を施しても良い。表面処理方法としては、例えば、シランカップリング剤による処理方法がある。該シランカップリング剤としては、例えば、Ｎ−ヘキシルトリエトキシシラン、Ｎ−ヘキシルトリメトキシシラン、Ｎ−オクチルトリエトキシシラン、Ｎ−デシルトリメトキシシラン、フェニルトリメトキシシラン、フェニルトリエトキシシラン、ジフェニルジメトキシシラン、ジフェニルジエトキシシラン、市販されているシランカップリング剤等がある。
なお熱伝導性フィラーは、オルガノポリシロキサン溶液に添加しても良い。該熱伝導性フィラーを添加後のオルガノポリシロキサンに、金属アルコキシド溶液を添加してゾル液を調製しても良い。
本発明で使用される熱伝導性フィラーは、粒子径の異なる２種以上の同種または異種の熱伝導性フィラーの混合物として使用することが好ましい。該熱伝導性フィラーの粒子径の差は、３倍以上であることが望ましい。
(Thermal conductive filler)
The thermally conductive filler used in the present invention is desirably fine particles of metal oxide and / or metal nitride and / or metal carbide. For example, aluminum oxide, magnesium oxide, zinc oxide, nickel oxide, titanium oxide, silicon oxide, vanadium oxide, copper oxide, iron oxide, silver oxide, or other metal oxide, or aluminum nitride, boron nitride, silicon carbide, silicon nitride, etc. Metal nitride or metal carbide.
The particle shape of the thermally conductive filler may be either spherical or flaky, but the average particle size is usually preferably in the range of 0.1 μm to 300 μm.
A heat conductive filler is added to the sol liquid obtained by mixing a metal alkoxide solution and an organopolysiloxane solution. In order to improve dispersibility in the sol solution and physical properties, the heat conductive filler may be subjected to a surface treatment by a direct blend method, an integral blend method, a slurry method, or the like. As the surface treatment method, for example, there is a treatment method using a silane coupling agent. Examples of the silane coupling agent include N-hexyltriethoxysilane, N-hexyltrimethoxysilane, N-octyltriethoxysilane, N-decyltrimethoxysilane, phenyltrimethoxysilane, phenyltriethoxysilane, and diphenyldimethoxy. Examples include silane, diphenyldiethoxysilane, and commercially available silane coupling agents.
The heat conductive filler may be added to the organopolysiloxane solution. A sol solution may be prepared by adding a metal alkoxide solution to the organopolysiloxane after addition of the thermally conductive filler.
The heat conductive filler used in the present invention is preferably used as a mixture of two or more kinds of the same or different heat conductive fillers having different particle diameters. The difference in particle diameter of the thermally conductive filler is preferably 3 times or more.
〔多孔性シート〕
本発明で使用される多孔性シートとは、内層に内包されるものであり、該内層ひいては熱伝導性シートを補強するものである。
本発明の多孔性シートとして、例えば、ガラス繊維（ガラスヤーン）、炭素繊維、ポリエステル繊維、ナイロン繊維等の合成樹脂繊維からなる平織（Ｐｌａｉｎ）、綾織（Ｔｗｉｌ）、朱子織（Ｓａｔｉｎ）、からみ織（Ｌｅｎｏ）、摸紗織（Ｍｏｃｋ Ｌｅｎｏ）等の織組織のクロス、ガラスロービングからなる一方向ロービングクロス、バルキーロービングクロス、バイヤスロービング、ハイブリッドロービングクロス等を使用することが出来る。
本発明の多孔性シートとして、特に望ましいのは、熱伝導性に優れるガラスヤーンからなるガラスクロス、ロービングクロスである。なお該多孔性シートは、公知のシランカップリング剤で表面処理されても良い。
本発明において多孔性シートは、通常、０．１％〜７５％、より好ましくは１％〜５０％の空隙率を有することが望ましい。多孔性シートの空隙率が７５％を超えると、得られる熱伝導性シートの強度が不充分となる場合がある。一方、多孔性シートの空隙率が０．１％未満であると得られる熱伝導性シートの熱伝導性が不充分となる場合がある。
好ましい多孔性シートの厚みは、０．０１ｍｍ〜１．００ｍｍ、より好ましくは０．０２ｍｍ〜０．７５ｍｍである。
熱伝導性シートの内層に内包される多孔性シートは、１枚であってもよく、また２枚以上であってもよい。
本発明の多孔性シートは、内層から表出しないように、内層中に、完全に内包されていることが望ましい。内層から多孔性シートが表出すると該内層の表面に凹凸が生じ、得られる熱伝導性シートの表面にも凹凸を生じ、該熱伝導性シートと金属板等の他の部材との密着性が悪くなる。
(Porous sheet)
The porous sheet used in the present invention is included in the inner layer, and reinforces the inner layer and thus the heat conductive sheet.
Examples of the porous sheet of the present invention include plain weave (Twill), satin weave (Satin), and tangle weave made of synthetic resin fibers such as glass fiber (glass yarn), carbon fiber, polyester fiber, and nylon fiber. (Leno), cloth weave (Mock Leno), etc., unidirectional roving cloth made of glass roving, bulky roving cloth, buyer roving cloth, hybrid roving cloth, etc. can be used.
As the porous sheet of the present invention, a glass cloth and a roving cloth made of a glass yarn excellent in thermal conductivity are particularly desirable. The porous sheet may be surface-treated with a known silane coupling agent.
In the present invention, the porous sheet usually has a porosity of 0.1% to 75%, more preferably 1% to 50%. When the porosity of the porous sheet exceeds 75%, the strength of the obtained heat conductive sheet may be insufficient. On the other hand, if the porosity of the porous sheet is less than 0.1%, the thermal conductivity of the obtained thermal conductive sheet may be insufficient.
The thickness of a preferable porous sheet is 0.01 mm to 1.00 mm, more preferably 0.02 mm to 0.75 mm.
The number of porous sheets included in the inner layer of the heat conductive sheet may be one, or two or more.
It is desirable that the porous sheet of the present invention is completely encapsulated in the inner layer so as not to be exposed from the inner layer. When the porous sheet is exposed from the inner layer, the surface of the inner layer is uneven, the surface of the resulting heat conductive sheet is also uneven, and the adhesion between the heat conductive sheet and other members such as a metal plate is improved. Deteriorate.
〔有機・無機ハイブリッド配合物の製造〕
有機・無機ハイブリッド配合物を製造するには、まず、所望の金属アルコキシドの加水分解物を含む金属アルコキシド溶液と、上記オルガノポリシロキサン溶液とを混ぜ合わせ、上記オルガノポリシロキサンの片末端または両末端の金属アルコキシドと反応可能な官能基と金属アルコキシドとの加水分解を伴う縮合反応を行い、有機・無機ハイブリッドゾル液を調製する。
[Manufacture of organic / inorganic hybrid compounds]
In order to produce an organic / inorganic hybrid compound, first, a metal alkoxide solution containing a hydrolyzate of a desired metal alkoxide is mixed with the organopolysiloxane solution, and one or both ends of the organopolysiloxane are mixed. An organic / inorganic hybrid sol solution is prepared by conducting a condensation reaction involving hydrolysis of a functional group capable of reacting with a metal alkoxide and the metal alkoxide.
具体的には、上記オルガノポリシロキサン溶液中に上記金属アルコキシドあるいは、所望なれば上記化学修飾剤によって修飾された金属アルコキシドを滴下する。 Specifically, the metal alkoxide or, if desired, a metal alkoxide modified with the chemical modifier is dropped into the organopolysiloxane solution.
上記オルガノポリシロキサン溶液に使用される溶媒は、オルガノポリシロキサンや金属アルコキシドの溶解度を考慮して選択されるが、一般的に、メタノール、エタノール等のアルコール、アセトン、トルエン、キシレン、テトラヒドロフラン等を使用出来る。 The solvent used in the organopolysiloxane solution is selected in consideration of the solubility of the organopolysiloxane and metal alkoxide, but in general, alcohols such as methanol and ethanol, acetone, toluene, xylene, tetrahydrofuran and the like are used. I can do it.
オルガノポリシロキサン溶液に加えられる金属アルコキシドを化学修飾剤によって化学修飾剤する場合、該化学修飾剤は金属アルコキシド１モルに対して２モル以下の量、望ましくは０．５モル以上１モル以下の量で使用される。 When the metal alkoxide added to the organopolysiloxane solution is chemically modified by a chemical modifier, the amount of the chemical modifier is 2 mol or less, preferably 0.5 mol or more and 1 mol or less, relative to 1 mol of the metal alkoxide. Used in.
上記金属アルコキシドのオルガノポリシロキサンに対する添加量は、通常モル比で１：０．１〜１：３０の範囲とする。
また該金属アルコキシドに対して該オルガノポリシロキサンは８０体積％程度であることが望ましい。
上記比率よりも金属成分が多いと該金属成分が粒塊を形成して、得られる有機・無機ハイブリッド層にうねりや気孔が形成され、またオルガノポリシロキサンが多いと無機成分と有機成分の相乗効果が現れず、有機成分の特性に近づく。
The amount of the metal alkoxide added to the organopolysiloxane is usually in the range of 1: 0.1 to 1:30 in molar ratio.
The organopolysiloxane is preferably about 80% by volume with respect to the metal alkoxide.
When there are more metal components than the above ratio, the metal components form agglomerates, and swells and pores are formed in the resulting organic / inorganic hybrid layer, and when there are many organopolysiloxanes, the synergistic effect of the inorganic and organic components Does not appear and approaches the characteristics of the organic component.
上記有機・無機ハイブリッドゾル液には、前記熱伝導性フィラーが添加、混合され、有機・無機ハイブリッド配合物が得られる。
該熱伝導性フィラーの添加量は、通常、有機・無機ハイブリッドゾル液１００質量部に対し１００〜３０００質量部添加されていることが好ましいが、より好ましくは１００質量部〜２５００質量部である。本発明の有機・無機ハイブリッドゾル液は、フィラー分散性に優れるので、容易に該熱伝導性フィラーを均一に分散させることが出来る。
The above-mentioned organic / inorganic hybrid sol liquid is mixed with the thermally conductive filler to obtain an organic / inorganic hybrid blend.
The amount of the thermally conductive filler added is usually preferably 100 to 3000 parts by mass, more preferably 100 to 2500 parts by mass with respect to 100 parts by mass of the organic / inorganic hybrid sol liquid. Since the organic / inorganic hybrid sol liquid of the present invention is excellent in filler dispersibility, the heat conductive filler can be easily dispersed uniformly.
なお上記有機・無機ハイブリッドゾル液には、該熱伝導性フィラー以外に、所望により、酸化防止剤、紫外線吸収剤、防腐剤、接着付与剤、粘度調節剤等の充填剤を添加しても良い。以上のようにして得られる有機・無機ハイブリッドゾル液は、白濁化することなく、かつポットライフの長いゾル液となる。 In addition to the thermally conductive filler, the organic / inorganic hybrid sol liquid may contain a filler such as an antioxidant, an ultraviolet absorber, an antiseptic, an adhesion-imparting agent, and a viscosity modifier, if desired. . The organic / inorganic hybrid sol solution obtained as described above does not become cloudy and becomes a sol solution having a long pot life.
〔熱伝導性シート〕
本発明の熱伝導性シートの製造方法を以下、説明する。まず上記多孔性シートにサイジングを施して該多孔性シートの空隙を埋める。該サイジングは上記多孔性シートをサイジング液に浸漬含浸して行われる。該サイジング液として、上記有機・無機ハイブリッド配合物を溶剤でサイジングに適当な粘度に希釈した希釈液が使用される。その後、該多孔性シートを常温、常湿で風乾し、所定時間、加熱乾燥すると有機・無機ハイブリッド配合物をＢ−ステージまで硬化させたシート（中間層）が得られる。
次いで、得られた中間層の両面に公知のコーティング法により外層を形成する。該中間層の両面に形成された外層は、該中間層と接合一体化される。まず該中間層の両面に有機・無機ハイブリッド配合物をコーティングする。コーティング後、更にホットプレスして、該中間層の両面に有機・無機ハイブリッド配合物をＢ−ステージまで硬化させた外層を形成するシートが得られる。
該シートを、引き続き、常温、常湿で風乾し、その後所定時間、加熱乾燥して、中間層および外層を共に完全硬化させると、本発明の熱伝導性シートが得られる。
[Thermal conductive sheet]
The manufacturing method of the heat conductive sheet of this invention is demonstrated below. First, the porous sheet is sized to fill the voids in the porous sheet. The sizing is performed by immersing the porous sheet in a sizing solution. As the sizing solution, a diluted solution obtained by diluting the organic / inorganic hybrid compound with a solvent to a viscosity suitable for sizing is used. Thereafter, the porous sheet is air-dried at room temperature and normal humidity, and is heated and dried for a predetermined time to obtain a sheet (intermediate layer) obtained by curing the organic / inorganic hybrid blend to the B-stage.
Subsequently, an outer layer is formed on both surfaces of the obtained intermediate layer by a known coating method. The outer layers formed on both surfaces of the intermediate layer are joined and integrated with the intermediate layer. First, the organic / inorganic hybrid compound is coated on both sides of the intermediate layer. After coating, the sheet is further hot-pressed to obtain a sheet on which an outer layer is formed by curing the organic / inorganic hybrid compound to the B-stage on both sides of the intermediate layer.
The sheet is then air-dried at normal temperature and normal humidity, and then heated and dried for a predetermined time to completely cure both the intermediate layer and the outer layer, whereby the heat conductive sheet of the present invention is obtained.
本発明の熱伝導性シートの厚みは、 ０．０１ｍｍ〜５．０ｍｍであることが望ましく、より望ましくは、０．２ｍｍ〜３．０ｍｍである。 The thickness of the heat conductive sheet of the present invention is desirably 0.01 mm to 5.0 mm, and more desirably 0.2 mm to 3.0 mm.
本発明の熱伝導性シートは、ＪＩＳタイプＡ硬度が２０〜９５であることが望ましく、より望ましい硬度は３５〜９０である。
該熱伝導性シートの硬度が２０〜９５の範囲であると、該熱伝導性シートを発熱性電子部品および放熱器の間に挟持させて使用する場合、該熱伝導性シートは、弾性体であるため該発熱性電子部品および放熱器の表面の形状に併せて変形、追従することが出来、よって高い熱伝導性を発揮することが出来る。
該熱伝導性シートの硬度が２０未満の場合、該熱伝導性シートは発熱性電子部品や放熱器に対する追従性、密着性に優れるものの、充分な強度を確保出来ない。
また該熱伝導性シートの硬度が９５を超えると、該熱伝導性シートは発熱性電子部品や放熱器等に対する追従性、密着性に劣り、充分な熱伝導性を発揮することが出来ない。
As for the heat conductive sheet of this invention, it is desirable that JIS type A hardness is 20-95, and more desirable hardness is 35-90.
When the hardness of the heat conductive sheet is in the range of 20 to 95, when the heat conductive sheet is sandwiched between a heat generating electronic component and a radiator, the heat conductive sheet is an elastic body. Therefore, it can be deformed and tracked in accordance with the shape of the heat generating electronic component and the surface of the radiator, and thus can exhibit high thermal conductivity.
When the hardness of the heat conductive sheet is less than 20, the heat conductive sheet is excellent in followability and adhesion to heat-generating electronic components and radiators, but cannot secure sufficient strength.
On the other hand, when the hardness of the heat conductive sheet exceeds 95, the heat conductive sheet is inferior in followability and adhesion to heat-generating electronic parts and radiators, and cannot exhibit sufficient heat conductivity.
本発明の熱伝導性シートは、一方の外層と、他方の外層が中間層を介して一体化している。一方の外層が、中間層に内包される多孔性シートの空隙を介して他方の外層と架橋しているので、本発明の熱伝導性シートの厚み方向の熱伝導性が損なわれない。
また本発明の熱伝導性シートは、振動等により外層と内層が剥離しない。
また更に、本発明の熱伝導性シートは、内層に多孔性シートを内包しているので該熱伝導性シートの平面方向の伸び性が規制される。
以下、本発明を実施例によって説明する。但し、本発明は以下に示される実施例によって限定されるものではない。
In the heat conductive sheet of the present invention, one outer layer and the other outer layer are integrated via an intermediate layer. Since one outer layer is cross-linked with the other outer layer through the gap of the porous sheet included in the intermediate layer, the thermal conductivity in the thickness direction of the heat conductive sheet of the present invention is not impaired.
Moreover, the heat conductive sheet of this invention does not peel an outer layer and an inner layer by vibration etc.
Furthermore, since the heat conductive sheet of the present invention includes a porous sheet in the inner layer, the extensibility of the heat conductive sheet in the planar direction is restricted.
Hereinafter, the present invention will be described by way of examples. However, this invention is not limited by the Example shown below.
〔実施例１〕
オルガノポリシロキサン（重量平均分子量２００００、ＸＦ３９０５、ＧＥ東芝シリコーン製）１５ｍｏｌを加熱処理し、Ａ液とした。
一方、ジルコニウムプロポキシド１ｍｏｌとアセト酢酸エチル０．５ｍｏｌとを窒素雰囲気下で反応させて、アセト酢酸エチルで化学修飾されたジルコニウムプロポキシドを調製し、Ｂ液とした。Ａ液にＢ液を滴下、混合しゾル液（Ｃ液）を調製した。
該ゾル液（Ｃ液）１００質量部に対し、アルミナ５００質量部を添加、混合して、有機・無機ハイブリッド配合物を得た。
なお該アルミナは、平均粒径３．０μｍ（ＡＬ−３０、昭和電工株式会社製）および４０．０μｍ（ＡＳ−１０、昭和電工株式会社製）の酸化アルミニウムを１：４の質量比で混合したものである。
その後、上記有機・無機ハイブリッド配合物をサイジング液として使用し、多孔性シート（ガラスクロス；ＴＥＸ番手、たて；１１．２、よこ；１１．２、糸密度（本／２５ｍｍ）、たて；６０本、よこ；５９本、５ｇ／ｍ2、空隙率；１５％、厚み；０．０５ｍｍ）を、該サイジング液に浸漬含浸し、その後、１日間風乾し、１００℃で２時間、１２０℃で２時間の条件で加熱乾燥して、有機・無機ハイブリッド配合物をＢ−ステージまで硬化させたシート（中間層）を得た。
一方、３種のゾル液（Ｃ液）１００質量部に対し、アルミナ７５０質量部、１０００質量部および１５００質量部を添加、混合して３種の有機・無機ハイブリッド配合物を調製した。なお使用したアルミナは上記アルミナと同種のアルミナである。
上記シート（中間層）に、上記有機・無機ハイブリッド配合物をコーティング剤として、上記中間層の両面にコーティングし、その後、ホットプレスして該中間層の両面にＢ−ステージまで硬化させた外層を形成するシートを得た。このようにして、組成の異なる３種の有機・無機ハイブリッド配合物を使用して、中間層に外層を形成した３種のシートを得た。
次いで、上記シートを加熱炉において１５０℃で２時間、１８０℃で２時間、２００℃で２時間、２５０℃で２時間、３００℃で２時間の条件下で加熱して、３種の熱伝導性シート（厚み０．３０ｍｍ）を得た。
得られたシートの熱抵抗値および熱伝導率を評価した。熱抵抗値は、ＡＳＴＭ Ｄ５４７０、熱伝導率は、ＪＩＳ Ｒ２６１６に基づき測定した。結果は表１に示した。
また、熱伝導性シートの硬度（ＪＩＳタイプＡ硬度）と、体積固有抵抗（ＪＩＳ Ｋ６２４９）を併せて測定した。なお熱伝導性シートの厚み（試料の厚み）は０．３０ｍｍであった。結果は表１に示した。
[Example 1]
15 mol of organopolysiloxane (weight average molecular weight 20000, XF3905, manufactured by GE Toshiba Silicone) was heat-treated to prepare a solution A.
On the other hand, 1 mol of zirconium propoxide and 0.5 mol of ethyl acetoacetate were reacted in a nitrogen atmosphere to prepare zirconium propoxide chemically modified with ethyl acetoacetate. B liquid was dripped and mixed with A liquid, and the sol liquid (C liquid) was prepared.
500 parts by mass of alumina was added to and mixed with 100 parts by mass of the sol solution (C liquid) to obtain an organic / inorganic hybrid blend.
The alumina was prepared by mixing aluminum oxide having an average particle size of 3.0 μm (AL-30, Showa Denko KK) and 40.0 μm (AS-10, Showa Denko KK) in a mass ratio of 1: 4. Is.
Thereafter, the organic / inorganic hybrid blend was used as a sizing solution, and a porous sheet (glass cloth; TEX count, warp; 11.2, weft; 11.2, yarn density (lines / 25 mm), warp; 60 pieces, weft pieces; 59 pieces, 5 g / m 2 , porosity: 15%, thickness: 0.05 mm) were immersed and impregnated in the sizing solution, and then air-dried for 1 day, at 100 ° C. for 2 hours, 120 ° C. The sheet (intermediate layer) in which the organic / inorganic hybrid blend was cured to the B-stage was obtained by heating and drying under the conditions of 2 hours.
On the other hand, 750 parts by mass, 1000 parts by mass and 1500 parts by mass of alumina were added to and mixed with 100 parts by mass of the three types of sol liquids (C liquids) to prepare three types of organic / inorganic hybrid blends. The alumina used is the same kind of alumina as the above alumina.
On the sheet (intermediate layer), the outer layer was coated on both sides of the intermediate layer using the organic / inorganic hybrid compound as a coating agent, and then hot pressed to cure both sides of the intermediate layer to the B-stage. A sheet to be formed was obtained. In this way, three kinds of sheets having an outer layer formed on the intermediate layer were obtained using three kinds of organic / inorganic hybrid blends having different compositions.
Next, the above sheet is heated in a heating furnace at 150 ° C. for 2 hours, 180 ° C. for 2 hours, 200 ° C. for 2 hours, 250 ° C. for 2 hours, and 300 ° C. for 2 hours. Sheet (thickness 0.30 mm) was obtained.
The obtained sheet was evaluated for thermal resistance and thermal conductivity. The thermal resistance value was measured based on ASTM D5470, and the thermal conductivity was measured based on JIS R2616. The results are shown in Table 1.
Moreover, the hardness (JIS type A hardness) of the heat conductive sheet and the volume resistivity (JIS K6249) were measured together. The thickness of the heat conductive sheet (sample thickness) was 0.30 mm. The results are shown in Table 1.
結果より、何れの熱伝導性シートについて、優れた放熱効果を有することが確かめられた。 From the results, it was confirmed that any heat conductive sheet had an excellent heat dissipation effect.
また上記の熱伝導性シート（シート３）を３００℃×２４０時間の条件で加熱して、耐久性の評価を行った。なお硬度は、ＪＩＳ Ｋ６２５３、伸びおよび引張り強さは、ＪＩＳ Ｋ６２５１に準拠して測定した。 Moreover, durability evaluation was performed by heating said heat conductive sheet (sheet | seat 3) on the conditions of 300 degreeC x 240 hours. The hardness was measured according to JIS K6253, and the elongation and tensile strength were measured according to JIS K6251.
評価の結果、上記条件下では、熱伝導性シートの分解や表面の変質等は起こらなかった。 As a result of the evaluation, the thermal conductive sheet was not decomposed or the surface was not deteriorated under the above conditions.
本発明の熱伝導性シートは、発熱性電子部品と放熱器や、発熱性電子部品と金属製伝熱板との間に介在させて使用する熱伝導性シートや、ＬＣＤ（Liquid Crystal Display）熱圧着用シート等に使用することが出来る。 The heat conductive sheet of the present invention includes a heat conductive electronic component and a radiator, a heat conductive sheet used by being interposed between the heat conductive electronic component and a metal heat transfer plate, or a liquid crystal display (LCD) heat. It can be used for pressure bonding sheets.
Claims (4)