JP2005335099A - Functional transfer sheet and transfer laminate - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a functional transfer sheet capable of efficiently imparting various functional properties to the necessary place of a desired article material effectively and simply at low cost, and a transfer laminate using it. <P>SOLUTION: The functional transfer sheet is constituted by forming a release layer (2) on one side of a base film (1), forming a functional urethane resin layer (3) on the surface of the release layer (2) and forming a vapor deposition layer (5) on the functional urethane resin layer (3). The functional transfer sheet is transferred to a base material so that the functional urethane resin layer (3) becomes the outermost surface layer of a product to constitute the functional transfer laminate. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

本発明は、各種の機能を有する物品を形成するための転写シートおよび転写積層体に関するものである。   The present invention relates to a transfer sheet and a transfer laminate for forming articles having various functions.

近年、各種の機能性を有する商品が、健康促進や、清潔志向、交通安全志向の高まりに反映して提案され、開発されている。そのひとつとして、健康促進を図るマイナスイオンを生成するマイナスイオン生成物質としてトルマリン（電気石）あるいはモナズ石などのイオンセラミックが知られており、またトルマリンやイオンセラミックは遠赤外線を発生することも知られている。そして、マイナスイオンや遠赤外線を人体に作用させて健康促進を図るために、マイナスイオン生成物質を衣服に付着させたり、あるいはマイナスイオン生成物質を含む樹脂組成物で成形品を形成したりすることが行われている。例えば、剥離シートの剥離層の表面にトルマリン粉末やイオンセラミック粉末を含む樹脂組成物を含有する印刷層を形成し、さらにその上に接着層を形成した転写シートが開示されている（特許文献１）。   In recent years, products having various functionalities have been proposed and developed to reflect health promotion, increased cleanliness and traffic safety. As one of them, tourmaline (ionite) or ion ceramics such as monazite are known as negative ion-generating substances that generate negative ions that promote health. It is also known that tourmaline and ion ceramics generate far-infrared rays. It has been. In order to promote health by applying negative ions or far-infrared rays to the human body, the negative ion generating substance is attached to clothes or a molded product is formed from a resin composition containing the negative ion generating substance. Has been done. For example, a transfer sheet is disclosed in which a printed layer containing a resin composition containing tourmaline powder or ionic ceramic powder is formed on the surface of the release layer of the release sheet, and an adhesive layer is further formed thereon (Patent Document 1). ).

また、清潔志向の高まりから多くの抗菌製品が開発されている。この抗菌製品に抗菌性能を持たせるには、一般に抗菌剤を添加した塗料を用いて当該製品の全面に均一に塗布する方法が採られている。抗菌剤としては、ゼオライト系、リン酸ジルコニウム系、チタニア系、ガラス系、リン酸カルシウム系、セラミック系、二酸化ケイ素系などの無機系抗菌剤、また第四級アンモニウム塩系、ハロジアリル尿素系、グアニジン系、フェノール系、脂肪酸エステル系、ベンゾイミダゾール系などの有機系抗菌剤が、プラスチック、ゴムなどへの抗菌性付与の目的で使用されている。また、亜鉛系無機抗菌剤微粒子および有機系抗菌剤を使用した転写材を用いることも報告されている（特許文献２）。   In addition, many antibacterial products have been developed due to the increasing awareness of cleanliness. In order to impart antibacterial performance to this antibacterial product, generally, a method of uniformly coating the entire surface of the product using a paint added with an antibacterial agent is employed. Antibacterial agents include zeolite, zirconium phosphate, titania, glass, calcium phosphate, ceramic, silicon dioxide, and other inorganic antibacterials, quaternary ammonium salts, halodiallyl ureas, guanidines, Organic antibacterial agents such as phenols, fatty acid esters, and benzimidazoles are used for the purpose of imparting antibacterial properties to plastics and rubbers. It has also been reported that a transfer material using zinc-based inorganic antibacterial fine particles and an organic antibacterial agent is used (Patent Document 2).

また、交通安全志向に基づく再帰反射性転写シートは、通学服、トレーニングウェア、ジョギングウェア、シューズなどに転写されると、転写積層体が自動車のヘッドライト照射に対する再帰反射性を有することになり、薄暮や夜間に交通事故に遭遇する危険性を未然に回避できることが報告されている（特許文献３）。
また、蓄光性物質を付与した蓄光シートは光を吸収して励起し、暗闇で１〜２時間発光することが知られており、安全シート（非常口の表示など）や広告、ディプレー用などに使用されている。 In addition, when the retroreflective transfer sheet based on traffic safety orientation is transferred to school clothes, training wear, jogging wear, shoes, etc., the transfer laminate will have retroreflective properties for automobile headlight irradiation, It has been reported that the danger of encountering a traffic accident at dusk or at night can be avoided in advance (Patent Document 3).
In addition, it is known that a phosphorescent sheet with a phosphorescent substance absorbs light, excites it, and emits light in the dark for 1-2 hours. It is used for safety sheets (emergency exit display, etc.), advertisements, and displays. Has been.

特開２００３−１１８２９６号公報JP 2003-118296 A 特開平８−１５７６２８号公報JP-A-8-157628 特開平１０−１９３８８７号公報Japanese Patent Laid-Open No. 10-193877

しかし、上記特開２００３−１１８２９６号公報の転写シートでは既存の衣服やその他の物品にマイナスイオン生成物質を付着させることはできるが、転写体の最表面に剥離層の樹脂が残存することからマイナスイオンの生成が少なく、その効果が低くなるという問題があった。   However, the transfer sheet disclosed in Japanese Patent Application Laid-Open No. 2003-118296 allows a negative ion generating substance to adhere to existing clothes and other articles, but it is minus because the resin of the release layer remains on the outermost surface of the transfer body. There was a problem that the production of ions was small and the effect was low.

また、上記特開平８−１５７６２８号公報の透明抗菌抗カビ性保護層は、膜厚が０. ５〜１０μｍ程度の範囲であり、抗菌剤の含有量も少なく、安定した抗菌性が得られず、また転写時の剥離性においても、作業安定性に欠ける等の問題があった。   Further, the transparent antibacterial and antifungal protective layer of the above-mentioned JP-A-8-157628 has a film thickness in the range of about 0.5 to 10 μm, has a small content of antibacterial agent, and stable antibacterial properties cannot be obtained. Also, there are problems such as lack of work stability in the peelability at the time of transfer.

さらに、上記特開平１０−１９３８８７号公報の再帰反射性転写シートでは、再帰反射のための透明球列の下方に蓄光顔料を含む残光発生層が存在しているが、自動車のヘッドライト照射に対する再帰反射性が充分でないという問題があった。
さらに、従来の蓄光性シートでは、暗闇で発光はするが、暗く、少し離れてしまうと発光していることがわかりにくくなり、蓄光性が充分ではないという問題があった。 Further, in the retroreflective transfer sheet of JP-A-10-193877, there is an afterglow generation layer containing a phosphorescent pigment below the transparent sphere array for retroreflection. There was a problem that the retroreflectivity was not sufficient.
Furthermore, the conventional phosphorescent sheet emits light in the dark, but it is difficult to recognize that the light is emitted when it is dark and slightly separated, and there is a problem that the phosphorescent property is not sufficient.

本発明は、上記の如き従来技術が有する問題点を効率的に解決するためになされたものであって、その目的は所望物品の必要箇所に効果的かつ簡便に低コストで各種の機能性を効率的に素材に与えることができる機能性転写シート、およびそれを用いる転写積層体を提供することにある。   The present invention has been made in order to efficiently solve the problems of the prior art as described above, and its purpose is to provide various functionalities effectively and simply at a required cost of a desired article at a low cost. It is an object to provide a functional transfer sheet that can be efficiently applied to a material, and a transfer laminate using the functional transfer sheet.

上記本発明の目的は、例えば、下記の如き手段により解決される。
すなわち、ベースフィルム（１）の片面上にリリース層（２）を形成し、リリース層の面上に機能性ウレタン樹脂層（３）を形成し、さらに機能性ウレタン樹脂層（３）の面上に蒸着層（５）を形成したことを特徴とする機能性転写シート。 The object of the present invention is solved by, for example, the following means.
That is, the release layer (2) is formed on one surface of the base film (1), the functional urethane resin layer (3) is formed on the surface of the release layer, and further on the surface of the functional urethane resin layer (3). A functional transfer sheet having a vapor-deposited layer (5) formed thereon.

機能性ウレタン樹脂層（３）がマイナスイオン発生物質、抗菌性物質、再帰反射性物質および蓄光性物質から選ばれる少なくとも１種類を含有することを特徴とする上記機能性転写シート。   The functional transfer sheet, wherein the functional urethane resin layer (3) contains at least one selected from a negative ion generating substance, an antibacterial substance, a retroreflective substance, and a phosphorescent substance.

蒸着層（５）の面上に、接着層(6) を形成したことを特徴とする上記機能性転写シート。   The functional transfer sheet as described above, wherein an adhesive layer (6) is formed on the surface of the vapor deposition layer (5).

機能性ウレタン樹脂層（３）と蒸着層（５）の間に保護層（４）を形成したことを特徴とする上記機能性転写シート。   The functional transfer sheet, wherein a protective layer (4) is formed between the functional urethane resin layer (3) and the vapor deposition layer (5).

ベースフィルム（１）のリリース層（２）を形成した面とは反対の面上に、離型層(7)
を形成したことを特徴とする上記機能性転写シート。 On the side of the base film (1) opposite to the side on which the release layer (2) is formed, the release layer (7)
The functional transfer sheet as described above, wherein

上記機能性転写シートを基材に転写した機能性転写積層体であって、機能性ウレタン樹脂層（３）が製品最表層になっていることを特徴とする機能性転写積層体。   A functional transfer laminate obtained by transferring the functional transfer sheet to a substrate, wherein the functional urethane resin layer (3) is the outermost layer of the product.

本発明の機能性転写シートを布地、織物、合成皮革、金属、木材、樹脂等の各種の素材で形成された物品表面に転写して得られる転写積層体は、機能性ウレタン樹脂層（３）と蒸着層（５）が形成されているため、蒸着層（５）の物理的性質、化学的性質によって機能性ウレタン樹脂層（３）の各種機能をより効率的に発現することができ、よって本発明によれば健康促進、抗菌性、再帰反射性、蓄光性等の各種機能により優れた積層体を得ることができる。   The transfer laminate obtained by transferring the functional transfer sheet of the present invention to the surface of an article formed of various materials such as fabric, woven fabric, synthetic leather, metal, wood, resin, etc. has a functional urethane resin layer (3). Since the vapor-deposited layer (5) is formed, various functions of the functional urethane resin layer (3) can be expressed more efficiently by the physical and chemical properties of the vapor-deposited layer (5). According to the present invention, a laminate excellent in various functions such as health promotion, antibacterial properties, retroreflective properties, and luminous properties can be obtained.

さらには薄膜の樹脂系リリース層（２）が形成されているため、転写後に機能性ウレタン樹脂層（３）が製品最表層となることで、従来品よりも効率的に各種機能を発現させることができ、かつ、リリース層（２）と機能性ウレタン樹脂層（３）が容易に剥離できるものであるため、優れた作業性をも兼ね備えた機能性転写シートおよび転写積層体を提供できる。
上記のことから、本発明の機能性転写シートのリリース層（２）は、支持体であるベースフィルム（１）とは強固に密着し、転写時に機能性ウレタン樹脂層（３）と容易に剥離することができる薄膜の樹脂層であることがより好ましい。 Furthermore, since a thin resin-based release layer (2) is formed, the functional urethane resin layer (3) becomes the outermost layer of the product after transfer, so that various functions can be expressed more efficiently than conventional products. In addition, since the release layer (2) and the functional urethane resin layer (3) can be easily separated, a functional transfer sheet and a transfer laminate having excellent workability can be provided.
From the above, the release layer (2) of the functional transfer sheet of the present invention is firmly adhered to the base film (1) as a support, and is easily peeled off from the functional urethane resin layer (3) during transfer. It is more preferable that the resin layer is a thin resin layer.

本発明の機能性転写シートに用いるベースフィルム（１）としては、特に制限はなく、充分な自己保持性を有する通常の転写シートに用いられるものであればいずれも用いることができる。例えば、ポリエチレンテレフタレートフィルム、ポリプロピレンフィルム、ポリエチレンフィルム、ポリアミドフィルム、ポリアミドイミドフィルム、ポリカーボネートフィルム、ポリスチレンフィルム、ポリ塩化ビニルフィルムなどの合成樹脂フィルムやセルロースアセテートフィルムなどの人造樹脂フィルム、セロハン紙、グラシン紙などの洋紙、和紙などのフィルム状物、あるいはこれらの複合フィルム状物もしくは複合シート状物などが挙げられる。加工面にコロナ処理、アンカーコート等の処理を施したフィルムを用いることもできる。   There is no restriction | limiting in particular as a base film (1) used for the functional transfer sheet of this invention, Any can be used if it is used for the normal transfer sheet which has sufficient self-holding property. For example, polyethylene terephthalate film, polypropylene film, polyethylene film, polyamide film, polyamideimide film, polycarbonate film, polystyrene film, synthetic resin film such as polyvinyl chloride film, artificial resin film such as cellulose acetate film, cellophane paper, glassine paper, etc. And film-like materials such as Japanese paper and Japanese paper, or composite film-like materials or composite sheet-like materials thereof. A film having a processed surface such as corona treatment or anchor coating can also be used.

ベースフィルム（１）の厚さとしては、特に制限はなく、通常４〜１００μｍの範囲、好ましくは９〜７５μｍの範囲、より好ましくは２５〜５０μｍの範囲であるのが、しわや亀裂などのない機能性転写シートの製造ができる点から好ましい。   There is no restriction | limiting in particular as thickness of a base film (1), Usually, it is the range of 4-100 micrometers, Preferably it is the range of 9-75 micrometers, More preferably, it is the range of 25-50 micrometers, but there is no wrinkle or a crack. This is preferable because a functional transfer sheet can be produced.

本発明の機能性転写シートにおいて、リリース層（２）は、転写時の剥離がリリース層（２）と機能性ウレタン樹脂層（３）の間の界面で生じるものであることが必要である。ただし、本発明の転写積層体において、機能性ウレタン樹脂層（３）が製品最表面になるということは、必ずしも最表層の１００％が機能性ウレタン樹脂層（３）である必要は無く、各機能性を劣化させない程度であればリリース層（２）の一部が部分的に製品最表層に残存していてもよいことを意味する。   In the functional transfer sheet of the present invention, the release layer (2) needs to be peeled off during transfer at the interface between the release layer (2) and the functional urethane resin layer (3). However, in the transfer laminate of the present invention, the functional urethane resin layer (3) is the outermost surface of the product, which means that 100% of the outermost layer does not necessarily need to be the functional urethane resin layer (3). This means that a part of the release layer (2) may partially remain on the outermost layer of the product as long as the functionality is not deteriorated.

リリース層（２）に用いる樹脂としては、例えば、メラミン系樹脂、尿素系樹脂、尿素−メラミン系樹脂、ウレタン系樹脂、アクリル系樹脂、フッ素系樹脂、シリコーン系樹脂、ベンゾグアナミン系樹脂またはセルロース系樹脂の単独またはそれらの２種以上の混合物を主成分としたものが挙げられる。好ましくは、メラミン系樹脂、尿素系樹脂、尿素−メラミン系樹脂が挙げられる。リリース層（２）は、これらの樹脂を有機溶剤に溶解させて得た塗料をグラビア印刷法、スクリーン印刷法、オフセット印刷法などの通常の印刷法で前記ベースフィルム（１）の上に塗布し、乾燥させ、もしくは熱硬化性樹脂、紫外線硬化性樹脂、電子線硬化性樹脂、放射線硬化性樹脂などの硬化性塗膜の場合には硬化させて形成される。リリース層（２）の厚さとしては、特に制限はなく、通常０．０５〜２μｍ程度の範囲から適宜選択して採用される。０．０５μｍ未満の場合、剥離しにくくなることがある。また、２μｍを超えると剥離しやすく、転写前に箔の脱離が起こったり、またはベースフィルム（１）とリリース層（２）の間で剥離したりすることになり、安定した各種機能が得られないことがある。   Examples of the resin used for the release layer (2) include melamine resins, urea resins, urea-melamine resins, urethane resins, acrylic resins, fluorine resins, silicone resins, benzoguanamine resins, and cellulose resins. Or a mixture of two or more of them as a main component. Preferably, melamine resin, urea resin, and urea-melamine resin are used. The release layer (2) is obtained by applying a paint obtained by dissolving these resins in an organic solvent onto the base film (1) by a normal printing method such as gravure printing, screen printing, or offset printing. In the case of a curable coating such as a thermosetting resin, an ultraviolet curable resin, an electron beam curable resin, or a radiation curable resin, it is formed by curing. There is no restriction | limiting in particular as thickness of a release layer (2), Usually, it selects from the range of about 0.05-2 micrometers suitably, and is employ | adopted. If it is less than 0.05 μm, it may be difficult to peel off. Also, if it exceeds 2 μm, it will be easy to peel off, and the foil will be detached before transfer, or it will peel off between the base film (1) and the release layer (2), and various stable functions can be obtained. It may not be possible.

本発明の機能性転写シートにおいて、機能性ウレタン樹脂層（３）に用いるベース樹脂としては、転写時の剥離がリリース層（２）と機能性ウレタン樹脂層（３）との界面で生じることが必要であり、耐光性が良好で通常の転写箔に用いられるものであればいずれも用いることができる。例えば、ウレタン系樹脂、ウレタン−アクリル系樹脂などを単独でまたはそれらの２種以上を混合して用いることができる。   In the functional transfer sheet of the present invention, as the base resin used for the functional urethane resin layer (3), peeling during transfer may occur at the interface between the release layer (2) and the functional urethane resin layer (3). Any one can be used as long as it is necessary and has good light resistance and can be used for a normal transfer foil. For example, urethane resin, urethane-acrylic resin, etc. can be used alone or in admixture of two or more thereof.

マイナスイオン発生物質としては、特に制限がなく、トルマリン、モナズ石、化石サンゴなどを用いることができ、これらの物質を単独でまたは２種以上を混合して用いることができる。抗菌性物質としては、銀や銅およびこれらのものをゼオライト等に担持させたものをはじめ、第４級アンモニウム塩、ビリジン系化合物、ポリカルボン酸塩、キトサン、ヒノキチオール、ヨモギ抽出物などを単独でまたはそれらの２種以上を混合して用いることができる。
再帰反射性物質としては、ガラス製やプラスチック製のビーズなどを単独でまたは２種以上を混合して用いることができる。
蓄光性物質としては、ＺｎＳ：Ｃｕ、ＣａＳｒＳ：Ｂｉ、ＺｎＣｄＳ：Ｃｕ等の硫化物系蓄光系蛍光体、特開平７−１１２５０号公報に記載されている蓄光剤などを単独でまたは２種以上の混合物として用いることができる。 The negative ion generating substance is not particularly limited, and tourmaline, monazite, fossil coral and the like can be used, and these substances can be used alone or in admixture of two or more. Antibacterial substances such as silver, copper and those supported on zeolite, quaternary ammonium salts, pyridine compounds, polycarboxylates, chitosan, hinokitiol, mugwort extract, etc. alone Alternatively, two or more of them can be mixed and used.
As the retroreflective material, glass or plastic beads can be used alone or in admixture of two or more.
Examples of the phosphorescent substance include sulfide-based phosphorescent phosphors such as ZnS: Cu, CaSrS: Bi, and ZnCdS: Cu, phosphorescent agents described in JP-A-7-11250, and the like. It can be used as a mixture.

機能性ウレタン樹脂層（３）中のマイナスイオン発生物質の含有量は、機能性ウレタン樹脂層中の樹脂固形分１００質量部に対して通常５〜１００質量部の範囲、好ましくは１０〜４０質量部の範囲である。マイナスイオン発生物質の量が上記範囲を超えると、機能性ウレタン樹脂層の膜強度が低下することがある。また、上記範囲未満では十分な機能発現効果が得られないことがある。
機能性ウレタン樹脂層（３）中の抗菌性物質の含有量は、機能性ウレタン樹脂層中の樹脂固形分１００質量部に対して通常０．０５〜３０質量部の範囲、好ましくは０．５〜５質量部の範囲である。抗菌性物質の量が上記範囲を超えても、機能発現効果はそれ以上はそれほど向上せず、コスト対比機能発現効果が低下することがある。また、上記範囲未満では十分な機能発現効果が得られないことがある。
機能性ウレタン樹脂層（３）中の再帰反射性物質としてのビーズの含有量は、機能性ウレタン樹脂層中の樹脂固形分１００質量部に対して通常１００〜２０００質量部の範囲、好ましくは５００〜１０００質量部の範囲である。再帰反射性物質としてのビーズの量が上記範囲を超えると、機能性ウレタン樹脂層の膜強度が低下することがある。また、上記範囲未満では十分な機能発現効果が得られないことがある。
機能性ウレタン樹脂層（３）中の蓄光性物質の含有量は、機能性ウレタン樹脂層中の樹脂固形分１００質量部に対して通常１０〜１０００質量部の範囲、好ましくは２５０〜６００質量部の範囲である。蓄光性物質の量が上記範囲を超えると、機能性ウレタン樹脂層の膜強度が低下することがある。また、上記範囲未満では十分な機能発現効果が得られないことがある。 The content of the negative ion generating substance in the functional urethane resin layer (3) is usually in the range of 5 to 100 parts by mass, preferably 10 to 40 parts by mass with respect to 100 parts by mass of the resin solid content in the functional urethane resin layer. Part range. When the amount of the negative ion generating substance exceeds the above range, the film strength of the functional urethane resin layer may be lowered. Moreover, if it is less than the said range, sufficient function expression effect may not be acquired.
The content of the antibacterial substance in the functional urethane resin layer (3) is usually in the range of 0.05 to 30 parts by mass, preferably 0.5 to 100 parts by mass of the resin solid content in the functional urethane resin layer. It is the range of -5 mass parts. Even when the amount of the antibacterial substance exceeds the above range, the function expression effect is not improved so much, and the function expression effect for cost may be reduced. Moreover, if it is less than the said range, sufficient function expression effect may not be acquired.
The content of the beads as a retroreflective substance in the functional urethane resin layer (3) is usually in the range of 100 to 2000 parts by mass, preferably 500 with respect to 100 parts by mass of the resin solid content in the functional urethane resin layer. It is the range of -1000 mass parts. When the amount of the beads as the retroreflective material exceeds the above range, the film strength of the functional urethane resin layer may be lowered. Moreover, if it is less than the said range, sufficient function expression effect may not be acquired.
Content of the luminous substance in a functional urethane resin layer (3) is the range of 10-1000 mass parts normally with respect to 100 mass parts of resin solid content in a functional urethane resin layer, Preferably it is 250-600 mass parts Range. When the amount of the luminous substance exceeds the above range, the film strength of the functional urethane resin layer may be lowered. Moreover, if it is less than the said range, sufficient function expression effect may not be acquired.

本発明の機能性転写シートにおいて用いる機能性ウレタン樹脂層（３）は、例えば、前記機能性ウレタン樹脂層（３）を形成するベース樹脂に前記特定のマイナスイオン発生物質、抗菌性物質、再帰反射性物質および蓄光性物質の少なくとも１種類を特定の含有量で配合し、有機溶剤に分散溶解させて得た塗料を、グラビア印刷法、スクリーン印刷法、オフセット印刷法などの通常の印刷法により、前記ベースフィルム（１）上にリリース層（２）を介して塗布し、乾燥させ、もしくは熱硬化性樹脂、紫外線硬化性樹脂、電子線硬化性樹脂、放射線硬化性樹脂などの硬化性塗膜の場合には硬化させて形成することができる。機能性ウレタン樹脂層（３）の厚さとしては、特に制限はなく、通常１０〜５０μｍ程度の範囲から適宜選択して採用される。この厚さが１０μｍ未満の場合には十分な機能発現効果や保護効果が得られず、また５０μｍより厚くしても機能発現効果や保護効果はそれ以上はそれほど向上せず、コスト対比機能発現効果が低下することがある。   The functional urethane resin layer (3) used in the functional transfer sheet of the present invention is, for example, a base resin that forms the functional urethane resin layer (3), the specific negative ion generating substance, the antibacterial substance, and the retroreflection. A paint obtained by blending at least one of a luminescent substance and a phosphorescent substance with a specific content and dispersing and dissolving in an organic solvent is obtained by a normal printing method such as a gravure printing method, a screen printing method, an offset printing method, It is applied to the base film (1) through a release layer (2) and dried, or a curable coating film such as a thermosetting resin, an ultraviolet curable resin, an electron beam curable resin, or a radiation curable resin. In some cases, it can be cured. There is no restriction | limiting in particular as thickness of a functional urethane resin layer (3), Usually, it selects from a range of about 10-50 micrometers suitably, and is employ | adopted. If this thickness is less than 10 μm, sufficient function manifesting effect and protective effect cannot be obtained, and even if it is thicker than 50 μm, the function manifesting effect and protective effect are not improved so much, and the function manifesting effect for cost comparison May decrease.

本発明の機能性転写シートにおいて、機能性ウレタン樹脂層（３）と蒸着層（５）との密着性が不十分な場合には、必要に応じて、保護層（４）を形成することができる。
保護層（４）に用いる樹脂としては、機能性ウレタン樹脂層（３）との密着性、蒸着層（５）形成時における耐熱性および蒸着層（５）との密着性を与えるものであるのがよく、例えば、ポリエステル系樹脂、メラミン系樹脂、尿素系樹脂、尿素−メラミン系樹脂、ウレタン系樹脂、アクリル系樹脂、ニトロセルロース系樹脂の単独またはそれらの２種以上の混合物を主成分としたものが挙げられる。保護層（４）は、これらの樹脂を有機溶剤に溶解させて得た塗料をグラビア印刷法、スクリーン印刷法、オフセット印刷法などの通常の印刷法で前記機能性ウレタン樹脂層（３）の上に塗布し、乾燥させ、もしくは熱硬化性樹脂、紫外線硬化性樹脂、電子線硬化性樹脂、放射線硬化性樹脂などの硬化性塗膜の場合には硬化させて形成される。保護層（４）の厚さとしては、特に制限はなく、通常０．０５〜１０μｍ程度の範囲から、好ましくは０．５〜５μｍ程度の範囲から適宜選択して採用される。この厚さが０．０５μｍ未満の場合、機能性ウレタン樹脂層（３）との密着性が悪くなることがある。また、１０μｍを超えても密着性等の物性のさらなる向上は見られず、コスト高になることがある。また保護層（４）は、必要に応じて、染料や顔料を添加して着色されてもよい。 In the functional transfer sheet of the present invention, if the adhesion between the functional urethane resin layer (3) and the vapor deposition layer (5) is insufficient, a protective layer (4) can be formed as necessary. it can.
As the resin used for the protective layer (4), it provides adhesion to the functional urethane resin layer (3), heat resistance when forming the vapor deposition layer (5), and adhesion to the vapor deposition layer (5). For example, a polyester resin, a melamine resin, a urea resin, a urea-melamine resin, a urethane resin, an acrylic resin, a nitrocellulose resin alone or a mixture of two or more thereof is used as a main component. Things. The protective layer (4) is formed on the functional urethane resin layer (3) by a normal printing method such as a gravure printing method, a screen printing method or an offset printing method using a paint obtained by dissolving these resins in an organic solvent. In the case of a curable coating such as a thermosetting resin, an ultraviolet curable resin, an electron beam curable resin, or a radiation curable resin, it is formed by curing. There is no restriction | limiting in particular as thickness of a protective layer (4), Usually, it selects from the range of about 0.05-10 micrometers, Preferably it selects from the range of about 0.5-5 micrometers suitably, and is employ | adopted. When this thickness is less than 0.05 μm, the adhesion with the functional urethane resin layer (3) may deteriorate. Moreover, even if it exceeds 10 micrometers, the further improvement of physical properties, such as adhesiveness, is not seen, but cost may become high. The protective layer (4) may be colored by adding a dye or a pigment as necessary.

本発明の機能性転写シートにおいて、蒸着層（５）に用いる蒸着材料は、通常の転写シートに用いられる金属およびその合金、金属化合物などから適宜選択して採用される。例えば、アルミニウム、クロム、ニッケル、チタン、錫、金、銀、銅、白金、亜鉛、珪素などの蒸着可能な金属の単体、それらの合金、あるいはそれらの各種化合物などから機能性ウレタン樹脂層に含有される機能性成分に応じて適宜選択して採用される。   In the functional transfer sheet of the present invention, the vapor deposition material used for the vapor deposition layer (5) is appropriately selected from the metals used in ordinary transfer sheets, alloys thereof, metal compounds, and the like. For example, contained in functional urethane resin layers from simple metals that can be deposited such as aluminum, chromium, nickel, titanium, tin, gold, silver, copper, platinum, zinc, and silicon, alloys thereof, or various compounds thereof Depending on the functional component to be used, it is appropriately selected and employed.

蒸着層（５）は、前記蒸着材料を真空蒸着法、スパッタリング法、イオンプレーティング法などの通常の薄膜形成方法により形成される。蒸着層（５）の厚さには、特に制限はなく、金属光沢効果、ハーフミラー効果などの所望の目的に合せて適宜の厚さが選択され、採用される。   The vapor deposition layer (5) is formed by an ordinary thin film forming method such as a vacuum vapor deposition method, a sputtering method, or an ion plating method using the vapor deposition material. There is no restriction | limiting in particular in the thickness of a vapor deposition layer (5), Appropriate thickness is selected and employ | adopted according to desired objectives, such as a metallic luster effect and a half mirror effect.

本発明の機能性転写シートには、必要に応じて、接着層（６）を形成することができる。接着層（６）に用いる樹脂としては、特に制限はなく、通常の転写材に用いられる樹脂から適宜選択して用いることができる。例えば、ポリエステル−イソシアネート系、ウレタン系、アクリル系、酢酸ビニル系、塩化ビニル系、スチレンーブタジエン系、塩化ビニル酢酸ビニル系、エチレンー酢酸ビニル系、ポリエステル系、塩化ゴム系、塩素化ポリプロピレン系など有機溶剤型樹脂、エマルジョン系樹脂の単独またはそれらの２種以上の混合物を主成分とする樹脂から基材に対して適宜選択して採用される。   An adhesive layer (6) can be formed on the functional transfer sheet of the present invention as necessary. There is no restriction | limiting in particular as resin used for a contact bonding layer (6), It can select suitably from resin used for a normal transfer material, and can use it. For example, polyester-isocyanate-based, urethane-based, acrylic-based, vinyl acetate-based, vinyl chloride-based, styrene-butadiene-based, vinyl chloride-vinyl acetate-based, ethylene-vinyl acetate-based, polyester-based, chlorinated rubber-based, chlorinated polypropylene-based, etc. A solvent type resin, an emulsion resin alone or a resin mainly composed of a mixture of two or more thereof is appropriately selected for the substrate.

接着層（６）は、前記樹脂を有機溶剤や水で希釈して得た塗液を、グラビア印刷法、スクリーン印刷法、オフセット印刷法により、前記蒸着層(5) 上に塗布し、乾燥させて形成される。接着層（６）の厚さは、特に制限はなく、通常０．３〜２０μｍ程度の範囲から基材の表面状態などに応じて適宜選択して採用される。   For the adhesive layer (6), a coating solution obtained by diluting the resin with an organic solvent or water is applied onto the vapor deposition layer (5) by a gravure printing method, a screen printing method, or an offset printing method, and dried. Formed. There is no restriction | limiting in particular in the thickness of an adhesive layer (6), Usually, it selects from a range of about 0.3-20 micrometers suitably according to the surface state of a base material, etc. and is employ | adopted.

本発明の機能性転写シートには、必要に応じて、離型層（７）を形成することができる。離型層（７）に用いる樹脂としては、特に制限はなく、通常の転写材に用いられる樹脂から適宜選択して用いることができる。例えば、シリコーン系、フッ素系、ワックス系樹脂の単独またはそれらの２種以上の混合物を主成分とする樹脂から適宜選択して採用される。   A release layer (7) can be formed on the functional transfer sheet of the present invention as necessary. There is no restriction | limiting in particular as resin used for a mold release layer (7), It can select from the resin used for a normal transfer material suitably, and can use it. For example, a silicone-based resin, a fluorine-based resin, or a wax-based resin alone or a resin mainly composed of a mixture of two or more thereof can be selected and used.

離型層（７）は、前記樹脂を有機溶剤や水で希釈して得た塗液を、グラビア印刷法、スクリーン印刷法、オフセット印刷法により、前記ベースフィルム（１）のリリース層（２）を形成した面とは反対の面に塗布し、乾燥させて形成される。離型層（７）の厚さは、特に制限はなく、通常０．０５〜１μｍ程度の範囲で適宜選択して採用される。   The release layer (7) is a release layer (2) of the base film (1) obtained by diluting the resin with an organic solvent or water by gravure printing, screen printing, or offset printing. It is formed by applying to a surface opposite to the surface on which the film is formed and drying. There is no restriction | limiting in particular in the thickness of a mold release layer (7), Usually, it selects and employ | adopts suitably in the range of about 0.05-1 micrometer.

機能性転写積層体の被転写物となる基材としては、特に制限は無く、あらゆる物品のプラスチック成形品、プラスチック、繊維布帛、紙、木材、無機系素材等のあらゆる基材、内外装建材、自動車内外装用成形部品、雑貨、化粧品容器・キャップ、汎用パッケージ、弱電製品、高級襖、欄間、木工品、レザー、工芸品、民芸品等を用いることができる。   The base material to be transferred of the functional transfer laminate is not particularly limited, and is any plastic molded product of any article, plastic, fiber cloth, paper, wood, inorganic base materials, interior / exterior building materials, Molded parts for interior and exterior of automobiles, miscellaneous goods, cosmetic containers / caps, general-purpose packages, light electrical appliances, high-grade bags, bamma, woodwork, leather, crafts, folkcrafts, etc. can be used.

機能性転写積層体の転写法としては特に制限は無く、ロール転写、アップダウン転写、ブロー転写、インモールド転写等の公知の転写方法により簡単に転写を行うことができる。   There is no restriction | limiting in particular as a transfer method of a functional transfer laminated body, It can transfer simply by well-known transfer methods, such as roll transfer, up-down transfer, blow transfer, and in-mold transfer.

以下に実施例および比較例を挙げ、本発明をさらに説明する。なお、例中の部は質量部である。   The present invention will be further described below with reference to examples and comparative examples. In addition, the part in an example is a mass part.

実施例１
（マイナスイオン生成）
厚さ３８μｍの２軸延伸ポリエチレンテレフタレートフィルム上にメラミン樹脂２部、メチルエチルケトン４９部、トルエン４９部からなる溶液をグラビアコーティング法にて塗布し、乾燥して厚さ０．１μｍのリリース層を形成した。このリリース層上に
ウレタン樹脂（固形分３０％） １００部、
マイナスイオン発生物質（モナズ石） ６部、
メチルエチルケトン ３０部、および
トルエン ２０部
からなる塗液をグラビアコーテイング法にて塗布し、乾燥して厚さ１５μｍの機能性ウレタン樹脂層を形成した。この機能性ウレタン樹脂層上にポリエステル樹脂５０部、ポリイソシアネート樹脂１０部、メチルエチルケトン２０部およびトルエン２０部からなる溶液をグラビアコーティング法にて塗布し、乾燥して厚さ１μｍの保護層を形成した。さらに、連続真空蒸着法により４５０Åのアルミニウム蒸着層を形成し、ポリウレタン樹脂５０部、ポリイソシアネート樹脂５部および酢酸エチル４５部からなる接着剤溶液をグラビアコーティング法にて塗布し、乾燥して厚さ６μｍの接着層を形成して、本発明の機能性転写シートを得た。さらに、この機能性転写シートを用い、ロール転写機にて８０℃で合成皮革に転写を行って本発明の転写積層体を得た。 Example 1
(Negative ion generation)
A solution comprising 2 parts of melamine resin, 49 parts of methyl ethyl ketone and 49 parts of toluene was applied on a biaxially stretched polyethylene terephthalate film having a thickness of 38 μm by a gravure coating method and dried to form a release layer having a thickness of 0.1 μm. . On this release layer, 100 parts of urethane resin (solid content 30%),
Anion generator (monazite) 6 parts,
A coating solution comprising 30 parts of methyl ethyl ketone and 20 parts of toluene was applied by a gravure coating method and dried to form a functional urethane resin layer having a thickness of 15 μm. On this functional urethane resin layer, a solution comprising 50 parts of polyester resin, 10 parts of polyisocyanate resin, 20 parts of methyl ethyl ketone and 20 parts of toluene was applied by a gravure coating method and dried to form a protective layer having a thickness of 1 μm. . Further, an aluminum vapor deposition layer of 450 mm is formed by a continuous vacuum vapor deposition method, and an adhesive solution consisting of 50 parts of polyurethane resin, 5 parts of polyisocyanate resin and 45 parts of ethyl acetate is applied by a gravure coating method and dried to a thickness. A 6 μm adhesive layer was formed to obtain a functional transfer sheet of the present invention. Furthermore, using this functional transfer sheet, transfer was performed on synthetic leather at 80 ° C. with a roll transfer machine to obtain a transfer laminate of the present invention.

実施例２
（抗菌性）
厚さ３８μｍの２軸延伸ポリエチレンテレフタレートフィルム上にメラミン樹脂２部、メチルエチルケトン４９部、トルエン４９部からなる溶液をグラビアコーティング法にて塗布し、乾燥して厚さ０．１μｍのリリース層を形成した。このリリース層上に
ウレタン樹脂（固形分２０％） １００部、
銀担持ゼオライト ０．５部、
トルエン ２０部、および
メチルエチルケトン ３０部
からなる塗液をグラビアコーティング法にて塗布し、乾燥して厚さ１５μｍの機能性ウレタン樹脂層を形成した。この機能性ウレタン樹脂層上にポリエステル樹脂５０部、ポリイソシアネート樹脂１０部、メチルエチルケトン２０部、トルエン２０部からなる溶液をグラビアコーティング法にて塗布し、乾燥して厚さ１μｍの保護層を形成した。さらに、連続真空蒸着法により４５０Åのアルミニウム蒸着層を形成し、ポリウレタン樹脂５０部、ポリイソシアネート樹脂５部、酢酸エチル４５部からなる接着剤溶液をグラビアコーティング法にて塗布し、乾燥して厚さ６μｍの接着層を形成して、本発明の機能性転写シートを得た。さらに、ロール転写機にて８０℃で合成皮革に転写し、本発明の転写積層体を得た。 Example 2
(Antibacterial)
A solution comprising 2 parts of melamine resin, 49 parts of methyl ethyl ketone and 49 parts of toluene was applied on a biaxially stretched polyethylene terephthalate film having a thickness of 38 μm by a gravure coating method and dried to form a release layer having a thickness of 0.1 μm. . 100 parts of urethane resin (solid content 20%) on this release layer,
0.5 parts of silver supported zeolite,
A coating solution comprising 20 parts of toluene and 30 parts of methyl ethyl ketone was applied by a gravure coating method and dried to form a functional urethane resin layer having a thickness of 15 μm. A solution comprising 50 parts of a polyester resin, 10 parts of a polyisocyanate resin, 20 parts of methyl ethyl ketone, and 20 parts of toluene was applied on the functional urethane resin layer by a gravure coating method, and dried to form a protective layer having a thickness of 1 μm. . Further, an aluminum vapor deposition layer of 450 mm is formed by a continuous vacuum vapor deposition method, and an adhesive solution consisting of 50 parts of polyurethane resin, 5 parts of polyisocyanate resin, and 45 parts of ethyl acetate is applied by gravure coating, and dried to a thickness. A 6 μm adhesive layer was formed to obtain a functional transfer sheet of the present invention. Furthermore, it transferred to the synthetic leather at 80 ° C. with a roll transfer machine to obtain the transfer laminate of the present invention.

実施例３
（再帰反射性）
厚さ３８μｍの２軸延伸ポリエチレンテレフタレートフィルム上にメラミン樹脂２部、メチルエチルケトン４９部、トルエン４９部からなる溶液をグラビアコーティング法にて塗布し、乾燥して厚さ０．１μｍのリリース層を形成した。このリリース層の上に
ウレタン樹脂（固形分２０％） １００部、
ガラズビーズ １００部、
メチルエチルケトン ３０部、および
トルエン ２０部
からなる塗液をグラビアコーティング法にて塗布し、乾燥して厚さ５０μｍの機能性ウレタン樹脂層を形成した。この機能性ウレタン樹脂層上にポリエステル樹脂５０部、ポリイソシアネート樹脂１０部、メチルエチルケトン２０部、トルエン２０部からなる溶液をグラビアコーティング法にて塗布し、乾燥して厚さ１μｍの保護層を形成した。さらに、連続真空蒸着法により４５０Åのアルミニウム蒸着層を形成し、ポリウレタン樹脂５０部、ポリイソシアネート樹脂５部、酢酸エチル４５部からなる接着剤溶液をグラビアコーティング法にて塗布し、乾燥して厚さ６μｍの接着層を形成して、本発明の機能性転写シートを得た。さらに、ロール転写機にて８０℃で合成皮革に転写し、本発明の転写積層体を得た。 Example 3
(Retroreflective)
A solution comprising 2 parts of melamine resin, 49 parts of methyl ethyl ketone and 49 parts of toluene was applied on a biaxially stretched polyethylene terephthalate film having a thickness of 38 μm by a gravure coating method and dried to form a release layer having a thickness of 0.1 μm. . On this release layer, 100 parts of urethane resin (solid content 20%),
100 parts of glass beads,
A coating solution composed of 30 parts of methyl ethyl ketone and 20 parts of toluene was applied by a gravure coating method and dried to form a functional urethane resin layer having a thickness of 50 μm. A solution comprising 50 parts of a polyester resin, 10 parts of a polyisocyanate resin, 20 parts of methyl ethyl ketone, and 20 parts of toluene was applied on the functional urethane resin layer by a gravure coating method, and dried to form a protective layer having a thickness of 1 μm. . Further, an aluminum vapor deposition layer of 450 mm is formed by a continuous vacuum vapor deposition method, and an adhesive solution consisting of 50 parts of polyurethane resin, 5 parts of polyisocyanate resin, and 45 parts of ethyl acetate is applied by gravure coating, and dried to a thickness. A 6 μm adhesive layer was formed to obtain a functional transfer sheet of the present invention. Furthermore, it transferred to the synthetic leather at 80 ° C. with a roll transfer machine to obtain the transfer laminate of the present invention.

実施例４
（蓄光性）
厚さ３８μｍの２軸延伸ポリエチレンテレフタレートフィルム上にメラミン樹脂２部、メチルエチルケトン４９部、トルエン４９部からなる溶液をグラビアコーティング法にて塗布し、乾燥して厚さ０．１μｍのリリース層を形成した。このリリース層上に
ウレタン樹脂（固形分２０％） １００部、
アルミン酸ストロンチウム系蓄光剤 ５０部、
メチルエチルケトン ３０部、および
トルエン ２０部
からなる塗液をグラビアコーティング法にて塗布し、乾燥して厚さ５０μｍの機能性ウレタン樹脂層を形成した。この機能性ウレタン樹脂層上にポリエステル樹脂５０部、ポリイソシアネート樹脂１０部、メチルエチルケトン２０部、トルエン２０部からなる溶液をグラビアコーティング法にて塗布し、乾燥して厚さ１μｍの保護層を形成した。さらに、連続真空蒸着法により４５０Åのアルミニウム蒸着層を形成し、ポリウレタン樹脂５０部、ポリイソシアネート樹脂５部、酢酸エチル４５部からなる接着剤をグラビアコーティング法にて塗布し、乾燥して厚さ６μｍの接着層を形成して、本発明の機能性転写シートを得た。さらに、ロール転写機にて８０℃で合成皮革に転写し、本発明の転写積層体を得た。 Example 4
(Luminescent)
A solution comprising 2 parts of melamine resin, 49 parts of methyl ethyl ketone and 49 parts of toluene was applied on a biaxially stretched polyethylene terephthalate film having a thickness of 38 μm by a gravure coating method and dried to form a release layer having a thickness of 0.1 μm. . 100 parts of urethane resin (solid content 20%) on this release layer,
50 parts of strontium aluminate phosphorescent agent,
A coating solution composed of 30 parts of methyl ethyl ketone and 20 parts of toluene was applied by a gravure coating method and dried to form a functional urethane resin layer having a thickness of 50 μm. A solution comprising 50 parts of a polyester resin, 10 parts of a polyisocyanate resin, 20 parts of methyl ethyl ketone, and 20 parts of toluene was applied on the functional urethane resin layer by a gravure coating method, and dried to form a protective layer having a thickness of 1 μm. . Furthermore, an aluminum vapor deposition layer having a thickness of 450 mm is formed by a continuous vacuum vapor deposition method, and an adhesive composed of 50 parts of polyurethane resin, 5 parts of polyisocyanate resin, and 45 parts of ethyl acetate is applied by a gravure coating method and dried to a thickness of 6 μm. Thus, the functional transfer sheet of the present invention was obtained. Furthermore, it transferred to the synthetic leather at 80 ° C. with a roll transfer machine to obtain the transfer laminate of the present invention.

比較例１
厚さ３８μｍの２軸延伸ポリエチレンテレフタレートフィルム上に、フッ素樹脂を用いて乾燥膜厚が１０μｍになるように塗布して剥離層を形成した。この剥離層上にアクリル樹脂、トルマリン粉末からなる配合塗料を乾燥膜厚が１００μｍになるように塗布してマイナスイオン生成層を形成した。さらに、ポリウレタン系接着剤を乾燥膜厚が１００μｍになるように塗布して接着層を形成し、マイナスイオン生成転写シートを得た。さらに、ロール転写機にて８０℃で合成皮革に転写し、比較例のマイナスイオン生成転写積層体を得た。 Comparative Example 1
On a biaxially stretched polyethylene terephthalate film having a thickness of 38 μm, a release layer was formed by applying a dry film thickness of 10 μm using a fluororesin. On the release layer, a blended paint composed of acrylic resin and tourmaline powder was applied so that the dry film thickness was 100 μm to form a negative ion generation layer. Further, an adhesive layer was formed by applying a polyurethane adhesive so that the dry film thickness was 100 μm, and a negative ion generation transfer sheet was obtained. Furthermore, it transferred to the synthetic leather at 80 ° C. with a roll transfer machine to obtain a negative ion generation transfer laminate of a comparative example.

比較例２
実施例１の構成から蒸着層を除いた以外は実施例１と同様にして転写積層体を得た。 Comparative Example 2
A transfer laminate was obtained in the same manner as in Example 1 except that the vapor deposition layer was removed from the configuration of Example 1.

比較例３
市販のビーズシート( 商品名: スパークライトＴＲ、ユニチカ製) にポリウレタン樹脂２０重量％、ポリエステル樹脂２重量％、イソシアネート樹脂３重量％、黄色系の蓄光顔料７５重量％からなるペースト状の経時架橋性インクを１００メッシュのスクリーン版によって所定の模様にスクリーン印刷で形成した。さらに、通常の赤色顔料、次いで青色顔料を添加したインクで２回スクリーン印刷を行い、全体で厚さ６〜３０μｍの残光発生層を形成した。次に、ポリウレタン樹脂４０重量％、ポリアミド樹脂６０重量％からなり、ペースト状の熱可塑性インクを７０メッシュのスクリーン版を用いてスクリーン印刷して厚さ６０〜１００μｍの接着層を形成し、再帰反射性転写シートを得た。さらに、ロール転写機にて８０℃で合成皮革に転写し、比較例の再帰反射性転写積層体を得た。 Comparative Example 3
A commercially available bead sheet (trade name: Sparklite TR, manufactured by Unitika), 20% by weight of polyurethane resin, 2% by weight of polyester resin, 3% by weight of isocyanate resin, and 75% by weight of a yellow phosphorescent pigment. The ink was formed into a predetermined pattern by screen printing with a 100-mesh screen plate. Furthermore, screen printing was performed twice with an ink added with a normal red pigment and then a blue pigment to form an afterglow generating layer having a thickness of 6 to 30 μm as a whole. Next, 40% by weight polyurethane resin and 60% by weight polyamide resin were used, and a paste-like thermoplastic ink was screen-printed using a 70-mesh screen plate to form an adhesive layer having a thickness of 60 to 100 μm. A transfer sheet was obtained. Furthermore, it transferred to the synthetic leather at 80 ° C. with a roll transfer machine to obtain a retroreflective transfer laminate of a comparative example.

比較例４
実施例３の構成から蒸着層を除いた以外は実施例３と同様にして転写積層体を得た。 Comparative Example 4
A transfer laminate was obtained in the same manner as in Example 3 except that the vapor deposition layer was removed from the configuration of Example 3.

比較例５
実施例４の構成から蒸着層を除いた以外は実施例４と同様にして蓄光性転写積層体を得た。 Comparative Example 5
A phosphorescent transfer laminate was obtained in the same manner as in Example 4 except that the vapor deposition layer was removed from the configuration of Example 4.

実施例１および比較例１、２で得られた転写積層体のマイナスイオン放出量を測定した結果を表１に示す。   Table 1 shows the results of measuring the amount of negative ions released from the transfer laminates obtained in Example 1 and Comparative Examples 1 and 2.

（１）マイナスイオン放出量の測定方法
イオン測定器としてＩＣ−１０００（有限会社ユニバーサル企画）を用い、試料をＡ４サイズに切り取り、Ａ４サイズの台紙に貼り付け、これを角柱状にし、イオン測定器の吸入口に取り付け、マイナスのレンジにて測定を行った。試料となる角柱は、その長辺が柱の外周となるように作成した。また、マイナスイオンが発生した場合には、−とし、それに続いてマイナスイオン発生数の測定値を記した。逆に、プラスイオンが発生した場合には、＋とし、それに続いてプラスイオン発生数の測定値を記した。 (1) Method for measuring the amount of negative ions released IC-1000 (Universal Planning Co., Ltd.) is used as an ion measuring instrument, and the sample is cut into A4 size and pasted on an A4 size mount. It was attached to the suction port and measured in the negative range. The rectangular column used as a sample was prepared so that the long side was the outer periphery of the column. In addition, when negative ions were generated, − was given, followed by the measured value of the number of negative ions generated. On the contrary, when positive ions were generated, it was set as +, and subsequently, the measured value of the number of positive ions generated was recorded.

実施例２で得られた転写積層体の転写作業性および抗菌性の評価をした結果を表２に示す。   Table 2 shows the results of evaluating transfer workability and antibacterial properties of the transfer laminate obtained in Example 2.

（２）転写作業性の評価方法
得られた抗菌性転写シートをロール転写機にて８０℃で合成皮革に転写し、本発明の抗菌性転写積層体を得た時の転写作業性を評価した。
○：箔離れが良く、作業性が良好であった。
△：箔離れがやや硬く、作業性に支障があった。
×：箔離れが硬く、作業性が悪かった。 (2) Evaluation method of transfer workability The obtained antibacterial transfer sheet was transferred to a synthetic leather at 80 ° C. with a roll transfer machine to evaluate the transfer workability when the antibacterial transfer laminate of the present invention was obtained. .
○: Foil separation was good and workability was good.
(Triangle | delta): The foil separation was a little hard and there was a problem in workability.
X: The foil separation was hard and the workability was poor.

（３）抗菌性の評価方法
ＪＩＳ Ｌ１９０２ 菌液吸収法（殺菌活性値）にて評価を行った。 (3) Evaluation method of antibacterial property It evaluated by JISL1902 bacterial solution absorption method (bactericidal activity value).

実施例３および比較例３、４で得られた転写積層体の再帰反射性の評価結果を表３に示す。   Table 3 shows the retroreflectivity evaluation results of the transfer laminates obtained in Example 3 and Comparative Examples 3 and 4.

（４）再帰反射性の評価方法
ＪＩＳ Ｚ９１１７の反射性能測定法に準じた簡易な反射測定を実施した。すなわち、暗室中で、１００Ｗタングステン電球を被測定物からの距離１０ｍの位置に置き、光の入射角を０．２°、反射光の観測角度を２°にして、その時の輝度を目視により比較判定した。 (4) Evaluation method of retroreflectivity Simple reflection measurement according to the reflection performance measurement method of JIS Z9117 was performed. In other words, in a dark room, a 100W tungsten bulb is placed at a distance of 10 m from the object to be measured, the incident angle of light is 0.2 °, the observation angle of reflected light is 2 °, and the brightness at that time is compared visually. Judged.

実施例４および比較例５で得られた転写積層体の蓄光性の評価結果を表４に示す。   Table 4 shows the evaluation results of the luminous properties of the transfer laminates obtained in Example 4 and Comparative Example 5.

（５）蓄光性の評価方法
５０ｍｍ×５０ｍｍの試料を準備し、予め暗所に放置して残光を消去する。次に、Ｄ６５標準光源により２００ルクスの照度で１０分間照射し、光の照射を中止した直後の蓄光性を目視にて評価した。 (5) Evaluation method of luminous property A sample of 50 mm × 50 mm is prepared and left in a dark place in advance to erase afterglow. Next, the D65 standard light source was irradiated for 10 minutes at an illuminance of 200 lux, and the phosphorescence immediately after stopping the light irradiation was evaluated visually.

上記表１に示したように、実施例１においては、マイナスイオン放出量が多く、効率的で良好である。比較例１、２においては、マイナスイオン放出量が本発明の実施例１に比較して劣る。実施例１は、蒸着層が形成されているため、電気的性質、物理的性質、化学的性質によってマイナスイオン生成の発生効率が向上していると推測できる。一方、比較例１では、転写最表面に剥離層が残存していることも推測できる。すなわち、本発明の機能性転写積層体は、比較例のマイナスイオン生成性転写積層体に比べて、マイナスイオン放出量が著しく優れていることがわかる。   As shown in Table 1 above, in Example 1, the negative ion release amount is large, which is efficient and good. In Comparative Examples 1 and 2, the negative ion release amount is inferior to that of Example 1 of the present invention. In Example 1, since the vapor deposition layer is formed, it can be presumed that the generation efficiency of negative ions is improved by the electrical property, the physical property, and the chemical property. On the other hand, in Comparative Example 1, it can also be estimated that the release layer remains on the outermost transfer surface. That is, it can be seen that the functional transfer laminate of the present invention is significantly superior in the amount of negative ions released compared to the negative ion-generating transfer laminate of the comparative example.

上記表２に示したように、実施例２においてはリリース層と機能性ウレタン樹脂層の剥離性が優れており、転写作業性が良い。また、機能性ウレタン樹脂層が機能性転写積層体の製品最表層になるので、効率的な優れた抗菌性を示す。   As shown in Table 2 above, in Example 2, the release layer and the functional urethane resin layer have excellent peelability, and transfer workability is good. In addition, since the functional urethane resin layer is the outermost product layer of the functional transfer laminate, it exhibits efficient and excellent antibacterial properties.

上記表３に示したように、実施例３においては、再帰反射性が高く、効率的で良好である。比較例３においては、残光発生層によるものであるため、蓄光時間は長いが再帰反射性が十分でない。比較例４は、ガラスビーズのみの反射であるため、十分な再帰反射性が得られない。すなわち、本発明の機能性転写積層体は、比較例３、４の再帰反射性転写積層体に比べて、光照射に対する再帰反射性が鮮明で、著しく優れていることがわかる。   As shown in Table 3 above, in Example 3, the retroreflectivity is high, which is efficient and good. In Comparative Example 3, since it is due to the afterglow generation layer, the light accumulation time is long, but the retroreflective property is not sufficient. Since the comparative example 4 is reflection of only glass beads, sufficient retroreflectivity cannot be obtained. That is, it can be seen that the functional transfer laminate of the present invention has a clear and remarkably excellent retroreflectivity with respect to light irradiation as compared with the retroreflective transfer laminates of Comparative Examples 3 and 4.

上記表４に示したように、実施例４においては、暗室において明るく発光し、目立っていたが、比較例５の蓄光性転写積層体では暗かった。したがって、暗室等での表示物に実施例４の機能性転写積層体を用いた場合、表示が明確に確認できるが、比較例５の蓄光性転写積層体では表示物そのものがどこにあるのか発見し難かった。   As shown in Table 4 above, in Example 4, the light emitted brightly in the dark room and was conspicuous, but in the phosphorescent transfer laminate of Comparative Example 5, it was dark. Therefore, when the functional transfer laminate of Example 4 is used for a display in a dark room or the like, the display can be clearly confirmed. However, in the phosphorescent transfer laminate of Comparative Example 5, it was discovered where the display itself is. It was difficult.

上記に開示された実施の形態および実施例はすべての点で例示であって制限的なものではないと考えられるべきである。本発明の範囲は、上記した説明ではなくて特許請求の範囲によって示され、特許請求の範囲と均等の意味および範囲内でのすべての変更を含むことが意図される。   The embodiments and examples disclosed above should be considered as illustrative in all points and not restrictive. The scope of the present invention is defined by the terms of the claims, rather than the description above, and is intended to include any modifications within the scope and meaning equivalent to the terms of the claims.

本発明の機能性転写シートによれば、革製品や布地製品、織物製品はもちろんのこと、プラスチック成形品、プラスチック、紙、木材、無機系素材等あらゆる基材、内外装建材、自動車内外装用成形部品、雑貨、化粧品容器キャップ、汎用パッケージ、弱電製品、高級襖、欄間、木工品、工芸品民芸品等の各種素材で形成された物品表面に対して転写を行うことができ、所望物品の必要箇所に効果的かつ簡便に低コストで均質な各種機能を付与させることができるので、本発明は産業上極めて有用である。   According to the functional transfer sheet of the present invention, not only leather products, fabric products, and textile products, but also plastic molded products, plastics, paper, wood, inorganic materials, and other base materials, interior / exterior building materials, automotive interior / exterior molded parts , Miscellaneous goods, cosmetic container caps, general-purpose packages, light electrical appliances, luxury bags, bamma, woodwork, crafts, crafts, etc. Thus, the present invention can be imparted with various functions that are effective and simple and low-cost and homogeneous, so that the present invention is extremely useful industrially.

本発明の機能性転写シートの実施形態の一例を示す概略断面図である。It is a schematic sectional drawing which shows an example of embodiment of the functional transfer sheet of this invention. 本発明の転写積層体の実施形態の一例を示す概略断面図である。It is a schematic sectional drawing which shows an example of embodiment of the transfer laminated body of this invention.

符号の説明Explanation of symbols

１ ベースフィルム（１）
２ リリース層（２）
３ 機能性ウレタン樹脂層（３）
４ 保護層（４）
５ 蒸着層（５）
６ 接着層（６）
７ 離型層（７）
８ 基材（８） 1 Base film (1)
2 Release layer (2)
3 Functional urethane resin layer (3)
4 Protective layer (4)
5 Deposition layer (5)
6 Adhesive layer (6)
7 Release layer (7)
8 Base material (8)

Claims (6)

ベースフィルム（１）の片面上にリリース層（２）を形成し、リリース層（２）の面上に機能性ウレタン樹脂層（３）を形成し、さらに機能性ウレタン樹脂層（３）の面上に蒸着層（５）を形成したことを特徴とする機能性転写シート。   The release layer (2) is formed on one surface of the base film (1), the functional urethane resin layer (3) is formed on the surface of the release layer (2), and the surface of the functional urethane resin layer (3) is further formed. A functional transfer sheet having a vapor deposition layer (5) formed thereon. 機能性ウレタン樹脂層(3) がマイナスイオン発生物質、抗菌性物質、再帰反射性物質および蓄光性物質から選ばれる少なくとも１種類を含有することを特徴とする請求項１記載の機能性転写シート。   The functional transfer sheet according to claim 1, wherein the functional urethane resin layer (3) contains at least one selected from a negative ion generating substance, an antibacterial substance, a retroreflective substance, and a phosphorescent substance. 蒸着層（５）の面上に、接着層（６）を形成したことを特徴とする請求項１または２記載の機能性転写シート。   The functional transfer sheet according to claim 1 or 2, wherein an adhesive layer (6) is formed on the surface of the vapor deposition layer (5). 機能性ウレタン樹脂層（３）と蒸着層（５）の間に保護層（４）を形成したことを特徴とする請求項１〜３のいずれかに記載の機能性転写シート。   The functional transfer sheet according to any one of claims 1 to 3, wherein a protective layer (4) is formed between the functional urethane resin layer (3) and the vapor deposition layer (5). ベースフィルム（１）のリリース層（２）を形成した面とは反対の面上に、離型層（７）を形成したことを特徴とする請求項１〜４のいずれかに記載の機能性転写シート。   The functionality according to any one of claims 1 to 4, wherein a release layer (7) is formed on the surface opposite to the surface on which the release layer (2) of the base film (1) is formed. Transfer sheet. 請求項１〜５のいずれかに記載した機能性転写シートを基材に転写した機能性転写積層体であって、機能性ウレタン樹脂層（３）が製品最表面になっていることを特徴とする機能性転写積層体。   A functional transfer laminate obtained by transferring the functional transfer sheet according to any one of claims 1 to 5 to a substrate, wherein the functional urethane resin layer (3) is the outermost surface of the product. Functional transfer laminate.