JP2005298615A - 高衝撃性ポリカーボネート樹脂組成物及びその組成物からなる成形品 - Google Patents
高衝撃性ポリカーボネート樹脂組成物及びその組成物からなる成形品 Download PDFInfo
- Publication number
- JP2005298615A JP2005298615A JP2004114974A JP2004114974A JP2005298615A JP 2005298615 A JP2005298615 A JP 2005298615A JP 2004114974 A JP2004114974 A JP 2004114974A JP 2004114974 A JP2004114974 A JP 2004114974A JP 2005298615 A JP2005298615 A JP 2005298615A
- Authority
- JP
- Japan
- Prior art keywords
- polycarbonate resin
- weight
- parts
- resin composition
- high impact
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
化学結合したハロゲン原子を0.1〜10重量%含有する芳香族ポリカーボネート樹脂100重量部あたり少なくとも一種のペリノン系染料を0.01〜2重量部配合してなることを特徴とする高衝撃性ポリカーボネート樹脂組成物。
【効果】
本発明の高衝撃性ポリカーボネート樹脂組成物は、色調、加水分解性、引張強度等の物性を損なうことなく耐衝撃性に極めて優れている。したがって、家電材料、OA機器材料、電子・電気材料、自動車材料用途等に極めて有用である。
Description
(1項)化学結合したハロゲン原子を0.1〜10重量%含有する芳香族ポリカーボネート樹脂100重量部あたり少なくとも一種のペリノン系染料を0.01〜2重量部配合してなることを特徴とする高衝撃性ポリカーボネート樹脂組成物。
シ−3,3'−ジメチルジフェニルスルホキシドで例示されるジヒドロキシジアリールスルホキシド類;4,4'−ジヒドロキシジフェニルスルホン、4,4'−ジヒドロキシ−3,3'−ジメチルジフェニルスルホン等で例示されるジヒドロキシジアリールスルホン類;ハイドロキノン、レゾルシン、4,4'−ジヒドロキシジフェニル等があげられる。
A:良好 (染料本来の色相を有し、色が鮮明)
B:普通 (鮮明さにやや欠ける)
○:試験後プレートは白濁せず。
×:試験後プレートは白濁した。
JIS K−7111に基いて、ノッチ0.25mmRで測定した。
ASTM D−638に準じて行なった。
樹脂約1gを精秤し、テトラヒドロフラン25mlに溶解後、蛍光X線分析装置(セイコー社製、SEA2010L型)により測定した。
ビスフェノールA(BPA)を界面法によりホスゲンと重縮合させ、パラ−t−ブチルフェノールで末端封止した。即ち、BPA 15.09kg/時、NaOH 5.49kg/時及び水93.5kg/時を、ハイドロサルファイト0.017kg/時の存在下に、35℃で溶解した後、5℃まで冷却した水相並びに5℃に冷却した塩化メチレン61.9kg/時の有機相を、各々内径6mm、外径8mmのステンレス配管に供給し、同配管内で混合し、さらにホモミキサーを用いて、回転数6000rpmの条件下で乳化し、乳濁液を調製した。
BPAとテトラブロムビスフェノールA(TBBPA)からなる共重合ポリカーボネート樹脂を製造した。即ち、BPA16.0kg/時、NaOH5.97kg/時、及び水101.1kg/時をハイドロサルファイト0.018kg/時の存在下に35℃で溶解した後、25℃まで冷却した塩化メチレン60.5kg/時の有機相を各々内径6mm、外径8mmのステンレス製配管に供給し、同配管内で混合し、さらにホモミキサーを用いて乳化し乳濁液を調製した。
参考例のPC−1、PC−2に表1に示す添加剤を所定量加えタンブラーにて30分混合後、40mm単軸押出機にてシリンダー温度290℃でペレット化し、射出成形機にて、シリンダー温度290℃で3mm厚プレート試験片を作成しシャルピー衝撃強度、引張強度を測定した。その評価結果を表1に示す。
(1)ペリノン系染料:CI Solvent Red 135、三菱化学社製、Diaresin Red HS
(2)アンスラキノン系染料:CI Solvent Red 52、三菱化学社製、Diaresin Red H5B
(3)アンスラキノン系染料:CI Solvent Blue 97、ドイツ国Bayer社製、Macrolex Blue RR
(4)フタロシアニン系染料:C.I.74160、ドイツ国BASF社製、Heliogon Blue
(5)熱安定剤:トリス(2,4−ジ−t−ブチルフェニルホスファイト、旭電化工業社製、アデカスタブ2112
(6)離型剤:グリセリンモノステアレート、理研ビタミン社製、リケマールS100A
Claims (7)
- 化学結合したハロゲン原子を0.1〜10重量%含有する芳香族ポリカーボネート樹脂100重量部あたり少なくとも一種のペリノン系染料を0.01〜2重量部配合してなることを特徴とする高衝撃性ポリカーボネート樹脂組成物。
- 芳香族ポリカーボネート樹脂100重量部あたりアンスラキノン系染料を0.001〜0.5重量部配合してなることを特徴とする請求項1に記載の高衝撃性ポリカーボネート樹脂組成物。
- 熱安定剤として、芳香族ポリカーボネート樹脂100重量部あたり亜リン酸エステル化合物を0.001〜0.5重量部配合してなることを特徴とする請求項1又は2に記載の高衝撃性ポリカーボネート樹脂組成物。
- 離型剤として、芳香族ポリカーボネート樹脂100重量部あたり多価脂肪族アルコールと炭素数10〜22の脂肪酸との部分エステル化合物を0.01〜2重量部配合してなることを特徴とする請求項1〜3のいずれか1項に記載の高衝撃性ポリカーボネート樹脂組成物。
- 請求項1〜6のいずれか1項に記載の高衝撃性ポリカーボネート樹脂組成物からなる成形品。